Blank, manufacturing method of structural member, and structural member

Abstract

A blank (20) comprises a plurality of steel sheets. The plurality of steel sheets are arranged and joined so as to have an annular shape in a plan view of the blank (20). The plurality of steel sheets include steel sheets (21, 22). An edge portion of a first steel sheet (21) and an edge portion of a second steel sheet (22) form an overlap portion (241). Among the plurality of steel sheets, the steel sheet that constitutes a part of the blank (20) having a minimum plate thickness (tmin) is a plated steel sheet. A maximum plate thickness (tmax) of the blank (20) is in the overlap portion (241). The emissivity of surfaces (216, 226) of the steel sheets (21, 22), respectively, positioned outside the overlap portion (241) is greater than the emissivity of at least one of the other surfaces of the plurality of steel sheets.

Description

[Technical field]

[0001] The present disclosure relates to a blank for hot stamping. The present disclosure also relates to a method for manufacturing a structural member using the blank, and to the structural member. [Background technology]

[0002] Structures such as the body of an automobile are formed by a plurality of structural members. The structural members are manufactured, for example, by press forming a blank. In order to ensure high strength and good dimensional accuracy, the structural members are sometimes manufactured by a press forming method called hot stamping. Hot stamping is a technique in which a blank, which is a steel plate, is heated to a temperature in the austenite range, and then the blank is press formed using a die, and the blank is held in the die and quenched by removing heat (rapid cooling).

[0003] Patent Document 1 discloses a steel sheet (blank) for hot stamping. The steel sheet of Patent Document 1 has a surface treatment film having an emissivity of 60% or more at a wavelength of 8.0 μm at 25° C., covering the entire surface of at least one surface. According to Patent Document 1, the surface of the steel sheet to which the surface treatment film is applied has an increased emissivity, and the heat transfer effect by radiation is large. Therefore, when the steel sheet is heated during hot stamping, the steel sheet is heated to the A temperature at which the metal structure transforms into the austenite phase. c3 The temperature is quickly raised to a temperature equal to or higher than the heating point. Patent Document 1 describes that this makes it possible to shorten the heating time and improve the productivity of hot stamped members.

[0004] Patent Document 2 discloses a method for manufacturing an automobile body side structural frame from a plurality of blanks. In Patent Document 2, a composite blank is formed by joining a plurality of blanks, and the composite blank is press-formed to manufacture the body side structural frame. Patent Document 2 also describes hot forming (hot stamping) the composite blank. [Prior art documents] [Patent documents]

[0005] [Patent Document 1] International Publication No. 2022 / 215229 [Patent Document 2] Special Publication No. 2021-528248 Summary of the Invention [Problem to be solved by the invention]

[0006] In recent years, in order to simplify the manufacturing process of structures, it has been considered to integrate two or more components from the blank stage. Patent Document 2 discloses, for example, that a composite blank having an annular shape in a plan view is subjected to hot stamping to form an annular body side structural frame in which pillars, rockers, etc. are integrated. Patent Document 2 describes that adjacent steel plates in a composite blank are overlapped and joined by spot welding. In this way, when a composite blank includes an overlapping portion, it is difficult to ensure a process window in the manufacturing of a structural member. Specifically, during hot stamping, the blank is heated until its microstructure is austenitized. However, the overlapping portion formed by partial overlapping of steel plates has a larger plate thickness than the non-overlapping portion, and is therefore difficult to heat. For example, when the steel sheet having the smallest sheet thickness in the blank is a plated steel sheet, while the overlap part having the largest sheet thickness in the blank is heated to ensure its strength by hot stamping, the alloying of the plating layer in the thinnest plated steel sheet that was heated first may proceed excessively, causing the diffusion layer to thicken and reducing or losing the corrosion resistance (rust prevention) of the plating layer. Therefore, when an overlap part exists in the blank, it is difficult to ensure the process window of the heating conditions. In addition, the heating speed of the overlap part having the largest sheet thickness in the blank may become a bottleneck, which may reduce the productivity of the structural member.

[0007] An object of the present disclosure is to provide a blank for hot stamping capable of manufacturing a structural component that combines the strength of the overlap portion having the maximum plate thickness with the rust prevention function of the portion having the minimum plate thickness. [Means for solving the problem]

[0008] A blank for hot stamping according to the present disclosure includes a plurality of steel sheets. The plurality of steel sheets are arranged and joined to have an annular shape in a plan view of the blank. The plurality of steel sheets include a first steel sheet and a second steel sheet. The second steel sheet has an end portion. The end portion of the second steel sheet is overlapped and joined to the end portion of the first steel sheet to form an overlap portion together with the end portion of the first steel sheet. Among the plurality of steel sheets, a steel sheet constituting a portion having a minimum sheet thickness in the blank is a plated steel sheet having a base steel sheet and a plating layer provided on the base steel sheet. The overlap portion has a maximum sheet thickness in the blank. The emissivity of a surface located outside the overlap portion in each of the first steel sheet and the second steel sheet is greater than the emissivity of at least one of the other surfaces in the plurality of steel sheets. Effect of the Invention

[0009] According to the hot stamping blank of the present disclosure, it is possible to manufacture a structural component that combines the strength of the overlap portion having the maximum plate thickness with the rust prevention function of the portion having the minimum plate thickness. [Brief description of the drawings]

[0010] [Figure 1] FIG. 1 is a plan view of a structural member according to an embodiment. [Diagram 2] FIG. 2 is a cross-sectional view taken along line II-II of FIG. [Figure 3A] FIG. 3A is a schematic diagram for explaining the method for manufacturing a structural member according to the embodiment, and is a diagram showing a blank according to the embodiment. [Figure 3B] FIG. 3B is a schematic diagram for explaining the manufacturing method of a structural member according to the embodiment, and is a diagram showing a blank according to the embodiment. [Figure 3C]FIG. 3C is a schematic diagram for explaining the manufacturing method of a structural member according to the embodiment, and shows a blank according to the embodiment. [Figure 3D] FIG. 3D is a schematic diagram for explaining the manufacturing method of a structural member according to the embodiment, and shows a blank according to the embodiment. [Figure 3E] FIG. 3E is a schematic diagram for explaining a manufacturing method of a structural member according to an embodiment. [Figure 3F] FIG. 3F is a schematic diagram for explaining a manufacturing method of a structural member according to an embodiment. [Figure 3G] FIG. 3G is a schematic diagram for explaining the manufacturing method of the structural member according to the embodiment. [Figure 4] FIG. 4 is a cross-sectional view of a structural member manufactured by the manufacturing method according to the embodiment. [Diagram 5] FIG. 5 is a plan view of a structural member according to a modified example of the above embodiment. [Figure 6A] FIG. 6A is a diagram showing a division pattern of a structural member in the first embodiment. [Figure 6B] FIG. 6B is a diagram showing another division pattern of the structural member in the first embodiment. [Figure 6C] FIG. 6C is a diagram showing still another division pattern of the structural member in the first embodiment. [Figure 6D] FIG. 6D is a diagram showing still another division pattern of the structural member in the first embodiment. [Figure 6E] FIG. 6E is a diagram showing still another division pattern of the structural member in the first embodiment. [Figure 6F] FIG. 6F is a diagram showing still another division pattern of the structural member in the first embodiment. [Figure 6G] FIG. 6G is a diagram showing still another division pattern of the structural member in the first embodiment. [Figure 7A] FIG. 7A is a diagram showing a division pattern of a structural member in the second embodiment. [Figure 7B] FIG. 7B is a diagram showing another division pattern of the structural member in the second embodiment. [Figure 7C] FIG. 7C is a diagram showing still another division pattern of the structural member in the second embodiment. [Figure 7D] FIG. 7D is a diagram showing still another division pattern of the structural member in the second embodiment. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0011] A blank for hot stamping according to an embodiment includes a plurality of steel sheets. The plurality of steel sheets are arranged and joined to have an annular shape in a plan view of the blank. The plurality of steel sheets include a first steel sheet and a second steel sheet. The second steel sheet has an end portion. The end portion of the second steel sheet is overlapped and joined to the end portion of the first steel sheet to form an overlap portion together with the end portion of the first steel sheet. Of the plurality of steel sheets, a steel sheet constituting a portion having a minimum sheet thickness in the blank is a plated steel sheet having a base steel sheet and a plating layer provided on the base steel sheet. The overlap portion has a maximum sheet thickness in the blank. The emissivity of a surface located outside the overlap portion in each of the first steel sheet and the second steel sheet is greater than the emissivity of at least one of the other surfaces in the plurality of steel sheets (first configuration).

[0012] In the blank according to the first configuration, the end of the first steel sheet and the end of the second steel sheet form an overlap portion having the maximum sheet thickness in the blank. The emissivity of the surface located outside the overlap portion in each of the first steel sheet and the second steel sheet is larger than the emissivity of at least one other surface in the blank. That is, in the blank, the emissivity of both outer surfaces of the overlap portion is relatively high. As a result, when the blank is heated during hot stamping, the heating rate of the overlap portion can be increased, and the heating time of the overlap portion can be shortened. Therefore, the heating of the blank required for hot stamping can be completed before the alloying of the plating layer in the steel sheet with the minimum sheet thickness, which has been heated in advance, progresses excessively and the diffusion layer becomes thick. As a result, the strength of the overlap portion with the maximum sheet thickness can be ensured by hot stamping, and the corrosion resistance (rust resistance) of the steel sheet with the minimum sheet thickness can be ensured.

[0013] Thus, the blank according to the first configuration makes it possible to manufacture a structural member that has both the strength of the overlap portion having the maximum plate thickness and the rust prevention function of the portion having the minimum plate thickness. That is, the blank can increase the heating rate of the overlap portion having the maximum plate thickness, and as a result, it is easy to ensure the process window of the heating conditions in the manufacture of the structural member. In addition, by increasing the heating rate of the overlap portion, the heating time of the blank for hot stamping can be shortened, and the productivity of the structural member can be improved. Furthermore, by shortening the heating time of the blank, energy consumption in the manufacture of the structural member is suppressed, and the amount of greenhouse gas generated when the blank is heated for hot stamping can be reduced.

[0014] In the first configuration, each of the plurality of steel sheets may be a plated steel sheet. The plated steel sheet has a base steel sheet and a plating layer provided on the base steel sheet (second configuration).

[0015] In the second configuration, each steel sheet included in the blank is a plated steel sheet. In this case, when the blank is formed into a structural member by hot stamping, the generation of oxide scale can be suppressed. Therefore, after hot stamping, it is not necessary to subject the structural member to a process for removing oxide scale, such as a shot blasting process. Therefore, the productivity of the structural member can be improved.

[0016] In the second configuration, the plating layer may be an aluminum-based plating layer (third configuration).

[0017] In the case where each steel sheet is a plated steel sheet having an aluminum-based plating layer as in the third configuration, when the blank is heated during hot stamping, a difference in the heating rate is likely to occur between the overlapping portion having the maximum sheet thickness and the steel sheet having the minimum sheet thickness. Since the aluminum-based plating layer is close to white, it is likely to reflect heat energy and inhibit the heating of the overlapping portion. However, even if each steel sheet is a plated steel sheet having an aluminum-based plating layer, by increasing the emissivity of both outer surfaces of the overlapping portion, the heating of the overlapping portion can be promoted when the blank is heated during hot stamping, and the heating time of the overlapping portion can be shortened. As a result, the corrosion resistance of the steel sheet having the minimum sheet thickness can be ensured, and the productivity of the structural member manufactured from the blank can be improved.

[0018] In any of the first to third configurations, the surfaces of the first and second steel plates located outside the overlapping portion may be coated with a coating, for example, the coating having an emissivity of 60% or more at 25°C and a wavelength of 8.0 μm (fourth configuration).

[0019] In any of the first to third configurations, the surfaces of the first and second steel plates located outside the overlapping portion may be coated with a coating, which is a coating containing carbon black, one or more oxides selected from the group consisting of Zr oxide, Zn oxide, and Ti oxide, and 0 to 0.30 g / m 2The carbon black and oxide may be present dispersedly throughout the coating. The carbon black content in the coating may be X CB (g / m 2 ), the oxide content is X Oxide (g / m 2 ), then X CB and X Oxide It is preferable that the following formula (1) (see Patent Document 1) is satisfied (fifth configuration). 118.9≦24280 / {6700 / (100+76×X CB )+18000 / (130+65×X Oxide )}≦332.0 (1)

[0020] In any one of the first to fifth configurations, the plurality of steel plates may include two or more steel plates having different plate thicknesses. In this case, the plate thickness of the overlapping portion is set to t max The thickness of the steel plate constituting the part with the smallest thickness in the blank is t min Then, t max / t min It is preferable that the ratio is ≦3.2 (sixth configuration).

[0021] When two or more steel sheets with different thicknesses are included in a blank, the difference in thickness between the overlap portion and the steel sheet constituting the portion with the smallest thickness in the blank becomes larger compared to when all the steel sheets included in the blank have the same thickness. If the difference in thickness is excessive, when manufacturing a structural component from a blank by hot stamping, the temperature rise in the overlap portion becomes slower compared to the steel sheet constituting the portion with the smallest thickness in the blank, and it tends to be more difficult to ensure the process window of the heating conditions. Therefore, in the sixth configuration, the thickness t of the overlap portion is max and the minimum plate thickness t min Ratio to:t max / t minis set to 3.2 or less. As a result, even if a blank contains two or more steel sheets with different thicknesses, it becomes easier to complete heating of the thickest overlapping portion before alloying of the coating layer of the thinnest steel sheet progresses excessively, and the process window of the heating conditions is more easily secured.

[0022] A method for manufacturing a structural component according to an embodiment includes the steps of preparing a blank according to any one of the first to sixth configurations, heating a plurality of steel plates contained in the blank to a temperature equal to or higher than the austenite transformation completion temperature, and using a die to form the heated blank into a structural component that is annular in plan view and quenching it (seventh configuration).

[0023] A structural member according to an embodiment includes a member body and a coating. The member body is formed by a plurality of steel plates joined together and has an annular shape in a plan view. The plurality of steel plates include a first steel plate and a second steel plate. The second steel plate has an end portion. The end portion of the second steel plate is overlapped and joined to the end portion of the first steel plate to form an overlap portion together with the end portion of the first steel plate. The coating is provided on a surface of each of the first steel plate and the second steel plate that is positioned outside the overlap portion. The coating contains at least one oxide selected from the group consisting of Zr oxide, Zn oxide, and Ti oxide in an amount of 0.001 g / m 2 Contains the above (eighth configuration).

[0024] The structural member according to the embodiment comprises a member body and a coating. The member body is formed by a plurality of steel plates joined together and has an annular shape in a plan view. The plurality of steel plates include a first steel plate and a second steel plate. The second steel plate has an end portion. The end portion of the second steel plate is overlapped and joined to the end portion of the first steel plate to form an overlap portion together with the end portion of the first steel plate. The coating is provided on a surface of each of the first steel plate and the second steel plate that is positioned outside the overlap portion. The coating contains carbon black at 0.500 g / m 2 Contains the following (ninth configuration).

[0025] In the eighth or ninth configuration, the structural member may be a door ring part of an automobile. In this case, the member body may include a front pillar, a center pillar, and a rocker connecting the front pillar and the center pillar (tenth configuration).

[0026] Hereinafter, an embodiment of the present disclosure will be described with reference to the drawings. In each drawing, the same or corresponding components are denoted by the same reference numerals, and the same description will not be repeated.

[0027] [Structural Members] 1 is a diagram (plan view) of a structural member 10 according to this embodiment, viewed from above in a state in which the structural member 10 is placed on a horizontal surface. The structural member 10 is used, for example, in the body of an automobile. The structural member 10 is typically a door ring part of an automobile. In this embodiment, an example in which the structural member 10 is a door ring part will be described.

[0028] The structural member 10 is a hot stamped member. That is, the structural member 10 is formed by hot stamping (hot press processing) a blank made of a plurality of steel plates. The structural member 10 includes a member body 11. The member body 11 has an annular shape in a plan view of the structural member 10. The member body 11 includes a front pillar 111, a center pillar 112, and a rocker 113. When the structural member 10 is assembled to the body of an automobile, the center pillar 112 is disposed behind the front pillar 111. The center pillar 112 extends generally in the up-down direction of the vehicle body. The front pillar 111 extends toward the center pillar 112. When the structural member 10 is assembled to the body of an automobile, the rocker 113 is disposed below the front pillar 111 and the center pillar 112. The rocker 113 connects the front pillar 111 and the center pillar 112.

[0029] In this embodiment, the member body 11 is formed of a plurality of steel plates 21, 22, and 23 joined together. In the example of FIG. 1, the front pillar 111 is mainly formed of the steel plates 21 and 23. The center pillar 112 is mainly formed of the steel plate 22. The rocker 113 is formed of the steel plates 22 and 23.

[0030] FIG. 2 is a cross-sectional view taken along the line II-II in FIG. 1. FIG. 2 shows a cross section of the structural member 10 cut along the thickness direction at the position of the steel plate 21. As shown in FIG. 2, the steel plate 21 has an open cross section. The steel plate 21 has, for example, a roughly hat-shaped cross section in the cross section of the structural member 10. More specifically, the steel plate 21 includes a top plate 211, vertical walls 212 and 213, and flanges 214 and 215. The vertical wall 212 is disposed on the opposite side of the vertical wall 213 with respect to the top plate 211. In the cross section of the structural member 10, one ends of the vertical walls 212 and 213 are connected by the top plate 211. In the cross section of the structural member 10, the other ends of the vertical walls 212 and 213 are connected to flanges 214 and 215, respectively. The flanges 214 and 215 protrude from the vertical walls 212 and 213 to the outside of the structural member 10.

[0031] In the structural member 10, the width W of the steel plate 21, i.e., the portion located above the front pillar 111 (FIG. 1), may be 15 mm or more and 300 mm or less. The height H of the steel plate 21, i.e., the portion located above the front pillar 111, may be 10 mm or more and 150 mm or less. The width W is the distance from the end of the R on the vertical wall 212 side of the corner portion between the top plate 211 and the vertical wall 212 to the end of the R on the vertical wall 213 side of the corner portion between the top plate 211 and the vertical wall 213 in the cross section of the structural member 10. The height H is the distance from the top plate 211 to the flanges 214, 215 in the plate thickness direction of the top plate 211.

[0032] Although not shown in the drawings, the other steel plates 22, 23 have an open cross section like the steel plate 21. The steel plates 22, 23 can also have, for example, a generally hat-shaped cross section in the cross section of the structural member 10. The width of the portion of the steel plate 22 that corresponds to the center pillar 112 (FIG. 1) may be 15 mm or more and 300 mm or less. The height of the portion of the steel plate 22 that corresponds to the center pillar 112 may be 10 mm or more and 150 mm or less. The width of the portion of the steel plate 23 that corresponds to the lower part of the front pillar 111 (FIG. 1) may be, for example, 30 mm or more and 750 mm or less. The height of the portion of the steel plate 23 that corresponds to the lower part of the front pillar 111 may be 25 mm or more and 150 mm or less. The width of the portion of the steel plate 23 that corresponds to the locker 113 (FIG. 1) may be, for example, 30 mm or more and 300 mm or less. The height of the portion of the steel plate 23 that corresponds to the locker 113 may be 25 mm or more and 150 mm or less.

[0033] The size of the structural member 10, which is annular in plan view, is, for example, 1.0 m or more. The size of the structural member 10 may be, for example, 4.0 m or less. The size of the structural member 10 is the length of a line segment connecting any two points on the outer periphery of the structural member 10 that are farthest apart when the structural member 10 is placed on a horizontal surface and viewed in the vertical direction.

[0034] [Manufacturing methods for structural components] 3A to 3G, a method for manufacturing the structural member 10 will be described below. The method for manufacturing the structural member 10 according to this embodiment includes the steps of preparing a blank 20, heating the blank 20, and forming the heated blank 20 into the structural member 10.

[0035] (preparation process) 3A, in the preparation step, a blank 20 having a shape obtained by developing the structural member 10 is prepared. The blank 20 includes a plurality of steel plates 21, 22, and 23. The steel plates 21, 22, and 23 are arranged and joined so as to have an annular shape in a plan view of the blank 20.

[0036] 3B, 3C, and 3D are cross-sectional views of the blank 20 showing the joints of the steel plates 21, 22, and 23. FIG. 3B, FIG. 3C, and FIG. 3D are cross-sectional views taken along lines IIIB-IIIB, IIIC-IIIC, and IIID-IIID in FIG. 3A, respectively. Referring to FIG. 3B and FIG. 3C, the steel plate 21 is lapped and joined to each of the steel plates 22 and 23. That is, the end of the steel plate 22 is lapped and joined to the end of the steel plate 21 to form an overlapping portion 241 together with the end of the steel plate 21. Similarly, the end of the steel plate 23 is lapped and joined to the end of the steel plate 21 to form an overlapping portion 242 together with the end of the steel plate 21. Referring to FIG. 3D, the steel plate 22 is lapped and joined to the steel plate 23 in addition to the steel plate 21. An end portion of the steel plate 22 is overlapped and joined to an end portion of the steel plate 23 to form an overlap portion 243 together with the end portion of the steel plate 23. The steel plates 21, 22, and 23 are joined by, for example, spot welding or laser welding.

[0037] 3B to 3D, the steel plate 21 has a plate thickness t1. The steel plate 22 has a plate thickness t2. The steel plate 23 has a plate thickness t3. In this embodiment, the plate thickness t1 of the steel plate 21 and the plate thickness t2 of the steel plate 22 are greater than the plate thickness t3 of the steel plate 23. Therefore, the overlap portion 241 of the steel plates 21 and 22 has a maximum plate thickness t max The thickness t of the overlap portion 241 max is larger than the plate thickness of the overlap portion 242 between the steel plates 21 and 23 and the plate thickness of the overlap portion 243 between the steel plates 22 and 23.

[0038] In this embodiment, the sheet thickness t3 of the steel sheet 23 is the smallest among the multiple steel sheets 21, 22, and 23 included in the blank 20. Therefore, the steel sheet 23 has the smallest sheet thickness t min That is, the portion of the steel plate 23 that is not overlapped with the other steel plates 21 and 22 constitutes a portion having a minimum plate thickness t min The thickness t3 of the steel plate 23 is the minimum thickness t min It is.

[0039] In the present embodiment, when the steel plates 21, 22, and 23 have different plate thicknesses t1, t2, and t3, the maximum plate thickness t max and minimum plate thickness t min Ratio of:t max / t min is greater than 2.0. In this case, the maximum plate thickness t max and minimum plate thickness t min For example, t max / t min <4.0. Maximum plate thickness t max and minimum plate thickness t min t max / t min It is preferable that the maximum plate thickness t satisfies ≦3.2. max and minimum plate thickness t min t max / t min ≧2.5. Maximum plate thickness t max For example, the plate thickness t is 4.2 mm or less. max may be 1.6 mm or more.

[0040] The steel plates 21 and 22 have a maximum plate thickness t max The blank 20 has an overlapping portion 241 having a width of 100 mm and a thickness of 100 mm. The emissivity of the surfaces 216, 226 located outside the overlapping portion 241 in each of the steel plates 21, 22 is higher than the emissivity of at least one of the other surfaces of the steel plates 21, 22, 23 included in the blank 20. That is, the emissivity of the surfaces 216, 226 located outside the overlapping portion 241 in the steel plates 21, 22 is higher than the emissivity of the surfaces 217, 227 located inside the overlapping portion 241 in the steel plates 21, 22 and / or the emissivity of one or both surfaces of the other steel plate 23. The surfaces 216, 226 located outside the overlapping portion 241 in each of the steel plates 21, 22 are defined as surfaces having a maximum plate thickness t maxIn this embodiment, the emissivity of the surfaces 216, 226 located outside the overlap portion 241 in the steel plates 21, 22 is greater than the emissivity of the surfaces 217, 227 located inside the overlap portion 241. In addition, the emissivity of the surfaces 216, 226 located outside the overlap portion 241 in the steel plates 21, 22 is greater than the emissivity of the surfaces 217, 227 located inside the overlap portion 241 in the steel plates 21, 22 when the sheet thickness is a minimum min The emissivity at 25°C is greater than the emissivity at both sides of the steel plate 23 constituting the portion having the overlapping portion 241. For example, the emissivity at 25°C at a wavelength of 8.0 μm is 60% or more at the surfaces 216, 226 of the steel plates 21, 22. The emissivity at 25°C at a wavelength of 8.0 μm of the surfaces 216, 226 of the steel plates 21, 22 is more preferably 70% or more, and even more preferably 80% or more. The emissivity at 25°C at a wavelength of 8.0 μm of at least one surface other than the surfaces 216, 226 of the steel plates 21, 22, 23 included in the blank 20 may be less than 60%. The difference in emissivity at 25°C at a wavelength of 8.0 μm between the surfaces 216, 226 on both outer sides of the overlapping portion 241 and at least one surface other than the surfaces 216, 226 is preferably greater than 5%, more preferably greater than 10%, and even more preferably greater than 20%. The emissivity can be measured in accordance with JIS R 1801 (2002). In this case, a sample taken from the steel plate to be measured is placed in a Fourier transform infrared spectrophotometer, and the radiation intensity at a wavelength of 8.0 μm is measured at 25° C. to calculate the emissivity. Alternatively, it is also possible to use a radiation thermometer set to a measurement wavelength of 8.0 μm to measure the radiation intensity of a site of interest at 25° C., and calculate the emissivity from the ratio to the radiation intensity of a black body.

[0041] In this embodiment, the entire surface 216 of the steel plate 21 opposite the steel plate 22 is covered with the coating 25. Also, the entire surface 226 of the steel plate 22 opposite the steel plate 21 is covered with the coating 25. On the other hand, the steel plate 23 is not provided with the coating 25. As a result, the emissivity of both outer surfaces of the overlap portion 241 is higher than the emissivity of the surface of the steel plate 23.

[0042] The coating 25 is, for example, a black coating. The coating 25 may be a carbon-based surface treatment coating (a coating containing carbon (C)). For example, the lightness L * Value (CIE 1976 Lightness Index L as specified in JIS Z8781-4 (2013) * ) is 60 or less, the coating 25 can be determined to be black. The emissivity of the coating 25 at a wavelength of 8.0 μm at 25° C. is 60% or more, preferably 70% or more, and more preferably 80% or more. That is, the emissivity of the surfaces 216, 226 of the steel sheets 21, 22 to which the coating 25 is applied at a wavelength of 8.0 μm at 25° C. is 60% or more, preferably 70% or more, and more preferably 80% or more. The coating 25 may have an emissivity of 60% or more at a wavelength of 8.0 μm at 700° C. For example, the surface treatment coating described in Patent Document 1 can be used as the coating 25. Specifically, the coating 25 can contain carbon black and one or more oxides selected from the group consisting of Zr oxide, Zn oxide, and Ti oxide. The coating 25 may or may not contain silica. That is, the silica content of the coating 25 is 0 g / m 2 The silica content of the coating 25 is 0.30 g / m 2 The silica content may be 0.10 g / m or less. 2 or less, more preferably 0.05 g / m 2 The following is the result.

[0043] The carbon black and the oxide can be present dispersedly throughout the surface of the coating 25 perpendicular to the thickness direction of the steel sheet 21. CB (g / m 2 ), Zr oxide, Zn oxide, and Ti oxide, and the content of one or more oxides (metal oxides) selected from the group consisting of Zr oxide, Zn oxide, and Ti oxide is X Oxide (g / m 2 ), then X CB and X Oxide It is preferable that the following formula (1) is satisfied. 118.9≦24280 / {6700 / (100+76×X CB )+18000 / (130+65×X Oxide )}≦332.0 (1)

[0044] In formula (1), the middle formula is 24280 / {6700 / (100+76×X CB )+18000 / (130+65×X Oxide )} is preferably 119.0 or more, more preferably 170.0 or more, and even more preferably 220.0 or more. The value calculated by the middle formula is preferably 330.0 or less, more preferably 310.0 or less, and even more preferably 300.0 or less.

[0045] The dispersion state of the carbon black and the metal oxide in the coating 25 can be confirmed by performing a surface analysis of the coating 25 for elements derived from the carbon black (e.g., C) and elements derived from the oxide (Zr, Zn, and Ti) using an electron probe micro analyzer (EPMA). CB can be measured by a cross-sectional analysis of the coating 25 using a transmission electron microscope (TEM). That is, a cross-sectional analysis of the coating 25 is performed by TEM-EDS analysis in an area of ​​a predetermined size (thickness of the coating 25 × 5 μm), and the thickness of the coating 25 and the area ratio of particles having a carbon content of 70 mass % or more in that area are measured. The density of carbon black is expressed as ρ (ton / m 3 ), the film thickness is d (μm), and the area ratio is a (%). The value expressed by ρ×d×a is the carbon black content X CB (g / m 2 ) The oxide content X Oxide can be obtained by performing elemental analysis on the surface of the coating 25 using an X-ray fluorescence analyzer (ZSX Primus, manufactured by RIGAKU Corporation) and quantifying the amounts of metallic Zr, metallic Zn, and metallic Ti.

[0046] Carbon black content in film 25 X CB is 0.030g / m 2 It is preferable that the content is 0.100 g / m or more. 2 It is more preferable that the content is equal to or more than X. CB is set within a range that satisfies formula (1), but is preferably 0.800 g / m 2 or less, more preferably 0.600 g / m 2 The following is the result.

[0047] Coating 25 may contain 5.0% or more of carbon black by volume, and preferably 8.0% or more of carbon black by volume. Coating 25 may contain 40.0% or less of carbon black by volume, and preferably 30.0% or less of carbon black by volume.

[0048] Metal oxide content in film 25 X Oxide is 0.030g / m 2 It is preferable that the content is 0.060 g / m or more. 2 It is more preferable that the content is equal to or more than X. Oxide is set within a range that satisfies formula (1), but is preferably 0.500 g / m 2 More preferably, it is 0.300 g / m or less. 2 The following is the result.

[0049] Coating 25 may contain 1.0 or more volume percent of metal oxide. Coating 25 may also contain 30.0 or less volume percent of metal oxide, and preferably contains 25.0 or less volume percent of metal oxide.

[0050] Carbon black content X CB (g / m 2 ) and metal oxide content X Oxide (g / m 2 ) ratio: X Oxide / X CB is preferably 0.20 or more and 200.00 or less. Oxide / X CBis more preferably 0.40 or more and 10.00 or less, and further preferably 0.60 or more and 5.00 or less.

[0051] In addition to the carbon black and metal oxides described above, the coating 25 can contain various binder components and additives.

[0052] The binder component is preferably a water-dispersible or water-soluble resin. The content of the binder component is preferably 40% by volume or more with respect to the total volume of the film 25. As the binder component selected from the water-dispersible or water-soluble resins, various known resins exhibiting water dispersibility or water solubility can be used. Examples of such resins exhibiting water dispersibility or water solubility include polyurethane resins, polyester resins, acrylic resins, epoxy resins, fluororesins, polyamide resins, polyolefin resins, and polymer compounds obtained by hydrolysis and condensation polymerization of silane coupling agents. The binder component is more preferably one or more selected from the group consisting of polyester resins, polyurethane resins, polyolefin resins, acrylic resins, epoxy resins, fluororesins, and polyamide resins. When a polyurethane resin is used as the binder component, the polyurethane resin is preferably a polyether-based polyurethane resin.

[0053] The additives include, for example, a leveling agent, a water-soluble solvent, a metal stabilizer, and an etching inhibitor. The leveling agent is, for example, a nonionic or cationic surfactant. Examples of the nonionic or cationic surfactant include polyethylene oxide or polypropylene oxide adducts and acetylene glycol compounds. Examples of the water-soluble solvent include alcohols such as ethanol, isopropyl alcohol, t-butyl alcohol, and propylene glycol, cellosolves such as ethylene glycol monobutyl ether and ethylene glycol monoethyl ether, esters such as ethyl acetate and butyl acetate, and ketones such as acetone, methyl ethyl ketone, and methyl isobutyl ketone. Examples of the metal stabilizer include chelate compounds such as EDTA (ethylenediaminetetraacetic acid) and DTPA (diethylenetriaminepentaacetic acid). Examples of the etching inhibitor include amine compounds such as ethylenediamine, triethylenepentamine, guanidine, and pyrimidine.

[0054] The coating 25 can be formed by applying an organic or inorganic treatment liquid containing, for example, carbon black and a metal oxide to the entire surface 216, 226 of the steel sheets 21, 22, and then drying the volatile components in the treatment liquid. The treatment liquid can be applied to the surface 216, 226 of the steel sheets 21, 22 by, for example, a roll coater, a curtain coater, or an inkjet. In the case of an inkjet, the thickness of the coating 25 can be changed continuously. The thickness of the coating 25 is, for example, 0.5 μm or more and 5.0 μm or less. The thickness of the coating 25 is preferably 1.0 μm or more and 3.0 μm or less. The thickness of the coating 25 is negligibly small compared to the sheet thicknesses t1, t2 of the steel sheets 21, 22. Therefore, the sheet thicknesses of the steel sheets 21, 22 measured including the coating 25 can be treated as the sheet thicknesses t1, t2, respectively.

[0055] Minimum thickness t in blank 20 minThe steel sheet 23 having the above-mentioned characteristics is a plated steel sheet. In this case, the steel sheet 23 has a base steel sheet 23a and a plated layer 23b. The type of the base steel sheet 23a is not particularly limited. The plated layer 23b is provided on the base steel sheet 23a. The plated layer 23b covers the entire or almost the entire both sides of the base steel sheet 23a. The plated layer 23b is a metal plated layer. The plated layer 23b may be, for example, a hot-dip aluminum plating, a hot-dip galvanizing, an alloyed hot-dip galvanizing, or an electrolytic galvanizing. As the steel sheet 23, a known aluminum-plated steel sheet, a galvanized steel sheet, or the like can be used. The sheet thickness t of the steel sheet 23 min is the combined thickness of the base steel sheet 23a and the plating layer 23b.

[0056] The steel sheets 21 and 22 may be known plated steel sheets, similar to the steel sheet 23. That is, the steel sheet 21 may have a base steel sheet 21a and a plating layer 21b provided on the base steel sheet 21a. The steel sheet 22 may have a base steel sheet 22a and a plating layer 22b provided on the base steel sheet 22a. The type of the base steel sheets 21a and 22a is not particularly limited. The plating layers 21b and 22b cover the entire or almost the entire both sides of the base steel sheets 21a and 22a, respectively. The plating layers 21b and 22b are metal plating layers. As the plating layers 21b and 22b, the same plating layers as those exemplified for the steel sheet 23 may be used. That is, the steel sheets 21 and 22 may be aluminum-plated steel sheets or zinc-plated steel sheets, similar to the steel sheet 23. When the steel sheet 21 is a plated steel sheet, the sheet thickness t1 of the steel sheet 21 is the combined sheet thickness of the base steel sheet 21a and the plated layer 21b. Similarly, when the steel sheet 22 is a plated steel sheet, the sheet thickness t2 of the steel sheet 22 is the combined sheet thickness of the base steel sheet 22a and the plated layer 22b.

[0057] The plating layers 21b, 22b, and 23b are typically plating layers mainly composed of aluminum (aluminum-based plating layers). The configuration of the aluminum-based plating layers is not particularly limited. Known aluminum-based plating layers can be used as the plating layers 21b, 22b, and 23b.

[0058] The steel sheets 21, 22, and 23 may each be a plated steel sheet of the same type as the other steel sheets, or may be a plated steel sheet of a different type from the other steel sheets. The steel sheets 21 and 22 may be steel sheets (bare materials) that do not have the plated layers 21b and 22b on their surfaces. When two or more of the steel sheets 21, 22, and 23 are plated steel sheets, the coating weight of each steel sheet may be the same as or different from the other steel sheets.

[0059] (Heating process) The prepared blank 20 is formed into a structural member 10 (FIGS. 1 and 2) by hot stamping. During the hot stamping, the blank 20 is subjected to a heating step. Referring to FIG. 3E, in the heating step, the blank 20 is heated by, for example, a heating furnace 30. The plurality of steel plates 21, 22, and 23 included in the blank 20 are heated to an austenite transformation completion temperature (A c3 The steel plates 21, 22, 23 are heated to, for example, 900° C. or higher. This causes the microstructures of the steel plates 21, 22, 23 to be transformed, for example, entirely or almost entirely into an austenite phase.

[0060] (molding process) Referring to Fig. 3F, in the forming process, the heated blank 20 is formed into a structural member 10 (Figs. 1 and 2) having an annular shape in plan view using a die 40 and quenched. The blank 20 heated in the heating process is removed from the heating furnace 30 (Fig. 3E) and transported to the die 40. The die 40 is attached to a known pressing device. The die 40 includes, for example, a punch 41 and a die 42. The blank 20 is disposed between the punch 41 and the die 42.

[0061] 3G, after the blank 20 is placed between the punch 41 and the die 42, the die 42 approaches relatively to the punch 41. The blank 20 is clamped (pressed) by the punch 41 and the die 42, and formed into a shape along the forming surfaces of the punch 41 and the die 42. The blank 20 is held while being clamped by the punch 41 and the die 42. The blank 20 is cooled (quenched) by the die 40, and its microstructure is transformed into martensite. In this way, the structural member 10 can be manufactured from the blank 20.

[0062] FIG. 4 is a cross-sectional view of the structural member 10 after hot stamping. FIG. 4 shows a cross-section of the structural member 10 at the position of the steel plate 21 (FIGS. 3B and 3C) to which the black coating 25 was applied at the stage of the blank 20. This structural member 10 includes a member body 11 and a coating 12. The coating 12 is provided on the steel plate 21. The black coating 25 (FIGS. 3B and 3C) applied to the steel plate 21 in the blank 20 becomes the coating 12 through hot stamping. Although not shown, the black coating 25 (FIGS. 3B and 3D) applied to the steel plate 22 in the blank 20 becomes the coating 12 through hot stamping. The coating 12 is provided on the surfaces 216, 226 (FIG. 3B) located outside the overlap portion 241 in each of the steel plates 21, 22. If the coating 25 before hot stamping contains carbon black, this carbon black will be almost completely removed by the high temperature heating during hot stamping, but may remain on the member body 11. If the coating 25 before hot stamping satisfies the above formula (1), the coating 12 after hot stamping may not contain carbon black or may contain less than 0.500 g / m 2 In some cases, the coating 12 after hot stamping contains carbon black. In the case where the coating 12 contains carbon black, the carbon black content in the coating 12 is 0 g / m 2 In addition, when the coating 26 before hot stamping satisfies the above formula (1), the coating 12 after hot stamping satisfies the central formula: 24280 / {6700 / (100+76×X CB )+18000 / (130+65×X Oxide)} is, for example, between 120.0 and 150.0.

[0063] When the coating 25 (FIGS. 3B and 3C) before hot stamping satisfies the above formula (1), the coating 12 after hot stamping contains one or more oxides (metal oxides) selected from the group consisting of Zr oxide, Zn oxide, and Ti oxide at a concentration of, for example, 0 g / m 2 More preferably, 0.001 g / m 2 The metal oxide content of the coating 12 is, for example, 0.500 g / m 2 In this way, when the metal oxide remains on the structural member 10, that is, when the coating 12 is 0 g / m 2 In the case where the coating 25 before hot stamping satisfies the above formula (1), the coating 12 after hot stamping has a metal oxide content of 0 to 0.30 g / m or more, which is more preferable because it improves the corrosion resistance of the structural member 10. 2 Contains silica.

[0064] The carbon black content, metal oxide content, and silica content in the coating 12 can be measured in the same manner as the coating 25 at the blank 20 stage. Specifically, the vehicle body part is disassembled to obtain a ring-shaped structural member 10, and an analysis sample is obtained from this structural member 10, for example, by laser cutting or the like. For example, an analysis sample is obtained from each of the multiple steel plates included in the structural member 10. The analysis sample is obtained from the center or its vicinity of the top plate of each steel plate having an open cross section. The obtained analysis sample is adjusted by polishing the cross section to the outside of the heat-affected zone during laser cutting, etc., to prepare a sample for coating analysis. By performing surface analysis of the coating 12 for elements derived from carbon black (e.g., C) and elements derived from oxides (Zr, Zn, and Ti) using EPMA for this sample, the dispersion state of carbon black and metal oxide in the coating 12 can be confirmed. Since the coating 12 is present on the front side and / or back side of the structural member 10 depending on the part of the structural member 10, the front side and back side of the analysis sample are analyzed.

[0065] In many cases, the outermost layer of the structural member 10 is, for example, an electrodeposition coating film. In that case, the coating layer that is below the electrodeposition coating film layer and above the alloyed metal plating layer is analyzed. The carbon black content X of the coating 12 is CB can be measured by a cross-sectional analysis of the coating 25 using a TEM. That is, a cross-sectional analysis of the coating 12 is performed by TEM-EDS analysis in an area of ​​a predetermined size (thickness of the coating 12 × 5 μm), and the thickness of the coating 12 and the area ratio of particles with a carbon content of 70 mass % or more in that area are measured. The density of carbon black is expressed as ρ (ton / m 3 ), the film thickness is d (μm), and the area ratio is a (%). The value expressed by ρ×d×a is the carbon black content X CB (g / m 2 ) The oxide content X Oxide can be determined by performing elemental analysis of the coating layer that is located below the electrodeposition coating layer and above the alloyed metal plating layer using the above-mentioned X-ray fluorescence analyzer, and quantifying the amounts of metallic Zr, metallic Zn, and metallic Ti.

[0066] After the forming process (hot stamping), the steel plate 21 may have a tensile strength of, for example, 0.5 GPa or more, and preferably has a tensile strength of 1.0 GPa or more. Similarly, after the forming process (hot stamping), the steel plates 22 and 23 (FIG. 1) may have a tensile strength of, for example, 0.5 GPa or more, and preferably has a tensile strength of 1.0 GPa or more. At least one of the steel plates 21, 22, and 23 may have a tensile strength of 1.5 GPa or more after the forming process. The tensile strength of each of the steel plates 21, 22, and 23 may be the same as or different from the tensile strength of the other steel plates.

[0067] [effect] When the blank 20 is heated during hot stamping, the minimum sheet thickness t minIn the steel sheet 23 having the above structure, iron diffuses from the base steel sheet 23a to the plating layer 23b to form a diffusion layer. The diffusion layer becomes thicker as the heating time of the blank 20 becomes longer, which may reduce the corrosion resistance or weldability of the steel sheet 23 due to the plating layer 23b. In order to ensure the corrosion resistance and weldability of the steel sheet 23, it is preferable that the thickness of the diffusion layer is kept below a predetermined value. For example, when the steel sheet 23 has a plating layer 23b with a coating weight of 50 to 80 g / m 2 In the case of a steel sheet having a thickness of about 40 to 50 g / m2, the thickness of the diffusion layer is preferably 15 μm or less. 2 In the case of a thin steel sheet, the thickness of the diffusion layer is preferably 10 μm or less. max The emissivity of the surfaces 216, 226 of the steel sheets 21, 22 located outside the overlap portion 241 having the emissivity of 100% or more is greater than the emissivity of at least one of the other surfaces of the steel sheets 21, 22, 23. That is, the surfaces 216, 217 on both outer sides of the overlap portion 241 of the steel sheets 21, 22 are treated to increase the emissivity. As a result, when the blank 20 is heated during hot stamping, the heating rate of the overlap portion 241 can be increased, and the heating time of the overlap portion 241 can be shortened. Therefore, in the thinnest steel sheet 23, which has been heated first, the alloying of the plating layer 23b progresses excessively, and the heating of the blank 20 can be terminated before the diffusion layer grows to a thickness exceeding a predetermined thickness. As a result, the maximum sheet thickness t max The strength of the overlap portion 241 having the minimum plate thickness t min This ensures the corrosion resistance (rust prevention) of the steel plate 23. Furthermore, by suppressing the thickness of the diffusion layer, the weldability of the steel plate 23 is easily ensured.

[0068] In this way, according to the blank 20 of this embodiment, the maximum plate thickness t maxTherefore, it is possible to heat the entire blank 20 to a temperature required for hot stamping before the alloying of the plating layer 23b of the thinnest steel sheet 23 progresses excessively, and the process window of the heating conditions in the manufacture of the structural member 10 can be secured. max The strength of the overlap portion 241 and the minimum plate thickness t min It is possible to manufacture a structural member 10 that has both a rust prevention function at the position of the steel plate 23. Also, by increasing the temperature rise rate of the overlap portion 241, the heating time of the blank 20 can be shortened, thereby improving the productivity of the structural member 10. Furthermore, by shortening the heating time of the blank 20, energy consumption in manufacturing the structural member 10 is suppressed, and the amount of greenhouse gases generated during heating can be reduced.

[0069] In this embodiment, the steel sheets 21, 22, and 23 included in the blank 20 may all be plated steel sheets. In this case, when the blank 20 is formed into the structural member 10 by hot stamping, the generation of oxide scale can be suppressed. Therefore, after hot stamping, it is not necessary to subject the structural member 10 to a process for removing oxide scale, such as a shot blasting process. Therefore, the productivity of the structural member 10 can be improved.

[0070] For example, when the plating layers 21b, 22b, and 23b of the steel sheets 21, 22, and 23 are aluminum-based plating layers, the maximum sheet thickness t max The overlap portion 241 has a minimum plate thickness t minA difference in temperature rise rate is likely to occur between the thin steel sheet 23 and the steel sheet 23 having an aluminum-based plating layer. Since the aluminum-based plating layer is white, it is likely to reflect heat energy and inhibit the temperature rise of the overlap portion 241. However, in the blank 20 according to the present embodiment, the surfaces 216, 226 of the steel sheets 21, 22 arranged on both outer sides of the overlap portion 241 are treated to increase the emissivity. Therefore, even if the steel sheets 21, 22 forming the overlap portion 241 are plated steel sheets having an aluminum-based plating layer, the temperature rise of the overlap portion 241 in the heating process can be promoted and the heating time of the overlap portion 241 can be shortened. Therefore, the corrosion resistance and weldability of the thin steel sheet 23 can be ensured, and the productivity of the structural member 10 can be improved.

[0071] In this embodiment, in the heating process, first, the blank 20 is heated to a minimum thickness t min The steel plate 23 having a maximum plate thickness t reaches the austenite temperature range, and then the portions having a thinner plate thickness reach the austenite temperature range in order. max In the present embodiment, when the steel plates 21, 22, and 23 included in the blank 20 have different thicknesses, the overlap portion 241 having the minimum thickness t min and maximum plate thickness t max If the difference between the thickness t and the thickness t is too large, min For a steel plate 23 having a plate thickness t max The temperature rise of the overlap portion 241 having the minimum plate thickness t min and maximum plate thickness t max Ratio to:t max / t min is preferably 3.2 or less. As a result, even if there is a difference in sheet thickness between the steel sheets 21, 22, and 23, the overlap portion 241 can be sufficiently heated until the phase transformation to austenite is completed before the alloying of the plating layer 23b of the thinnest steel sheet 23 progresses and the diffusion layer becomes thicker and loses corrosion resistance. This makes it easier to ensure a process window in the manufacture of the structural member 10.

[0072] In this embodiment, in order to increase the emissivity of the overlap portion 241, a coating 25 can be applied to the surfaces 216, 226 of the steel plates 21, 22 opposite the mating steel plate. The emissivity of the coating 25 (at a temperature of 25°C and a wavelength of 8.0 μm) is, for example, 60% or more. This allows the overlap portion 241 to be efficiently radiated and heats up, making it easier to increase the temperature rise rate of the overlap portion 241 in the heating process.

[0073] In this embodiment, the coating 25 is made of carbon black, one or more oxides selected from the group consisting of Zr oxide, Zn oxide, and Ti oxide, and a carbon black powder having a density of 0 to 0.30 g / m 2 The following silica and carbon black content X may be contained. CB (g / m 2 ), and oxide content X Oxide (g / m 2 ) preferably satisfies the above formula (1). As described in Patent Document 1, formula (1) is a function of the ratio (%) of the increase in the temperature rise rate (°C / s) and the carbon black content X CB and oxide content X Oxide and (1). Formula (1) expresses that carbon black mainly functions as a heat absorbing material in the range up to 700°C, and oxide mainly functions as a heat absorbing material in the range of 700°C or higher. When coating 25 satisfies formula (1), the emissivity at a wavelength of 8.0 μm at 25°C for both outer surfaces 216, 226 of overlap portion 241 to which coating 25 is applied tends to be 60% or more.

[0074] The carbon black and oxides can be dispersed throughout the entire surface of the coating 25 that is perpendicular to the thickness direction of the steel sheet 21. This makes it easier to uniformize the emissivity of the surfaces 216, 226 of the steel sheets 21, 22 located on both outer sides of the overlap portion 241. Therefore, the thickest overlap portion 241 can be heated quickly and uniformly in the heating process.

[0075] However, the configuration of the coating 25 is not limited to this. The coating 25 may be a substantially black coating in order to increase the emissivity of both outer surfaces 216, 226 of the overlapping portion 241 compared to an untreated case. For example, the coating 25 may contain graphite or soot instead of or in addition to carbon black. Alternatively, the coating 25 may contain an acicular compound having a hexagonal crystal structure with an aspect ratio of 4 to 50 inclusive in order to increase the emissivity of both outer surfaces 216, 226 of the overlapping portion 241 inclusive. The compound having a hexagonal crystal structure is typically graphite (C), but may also be lanthanum silicate, magnesium diboride, beryllium oxide (beryllia), zinc oxide, β-quartz, goethite (NiS), wurtzite (ZnS), or the like.

[0076] Although the embodiments of the present disclosure have been described above, the present disclosure is not limited to the above-described embodiments, and various modifications are possible without departing from the spirit of the present disclosure.

[0077] In the above embodiment, the minimum plate thickness t min The emissivity of both surfaces of the steel plate 23 having the minimum thickness t is smaller than the emissivity of the surfaces 216, 226 located outside the overlap portion 241 of the steel plates 21, 22. That is, the steel plate 23 is not provided with the coating 25 as in the overlap portion 241. However, min In the steel plate 23 having the overlapping portion 241, the emissivity of at least one of the surfaces may be substantially equal to the emissivity of the surfaces 216, 226 located outside the overlapping portion 241. For example, one or both surfaces of the steel plate 23 may be covered with the same coating 25 as the overlapping portion 241. However, from the viewpoint of ensuring a process window, it is preferable that the black coating 25 is not provided on at least one of the surfaces of the steel plate 23. That is, the emissivity of the surfaces 216, 226 located outside the overlapping portion 241 in each of the steel plates 21, 22 is the minimum at the plate thickness t min It is preferable that the emissivity of the steel plate 23 is larger than that of at least one surface of the steel plate 23 having the emissivity of 1000 nm or more.

[0078] In the above embodiment, in the steel plates 21 and 22, the emissivity of the surfaces 217 and 227 located inside the overlap portion 241 is smaller than the emissivity of the surfaces 216 and 226 located outside the overlap portion 241. That is, in the steel plates 21 and 22, the surfaces 217 and 227 located inside the overlap portion 241 are not provided with the coating 25. However, in the steel plate 21, the surface 217 located inside the overlap portion 241 may be covered with the coating 25. Similarly, in the steel plate 22, the surface 227 located inside the overlap portion 241 may be covered with the coating 25. However, from the viewpoint of uniformly heating the blank 20 during hot stamping, it is preferable that in each of the steel plates 21 and 22, the surfaces 216 and 226 outside the overlap portion 241 are substantially covered with the black coating 25, and the surfaces 217 and 227 located inside the overlap portion 241 are not covered with the coating 25. When both surfaces 216, 217 of the steel plate 21 are covered with the coating 25, the heating of the portion of the steel plate 21 that is not overlapped with the steel plate 22 progresses, the diffusion layer becomes thick, and it may be difficult to ensure the corrosion resistance and weldability of the steel plate 21. Similarly, when both surfaces 226, 227 of the steel plate 22 are covered with the coating 25, the heating of the portion of the steel plate 22 that is not overlapped with the steel plate 21 progresses, the diffusion layer becomes thick, and the corrosion resistance and weldability of the steel plate 22 may be deteriorated. Therefore, in order to more easily ensure good corrosion resistance and weldability, it is preferable that the coating 25 is provided on the surfaces 216, 226 located outside the overlap portion 241 of the steel plates 21, 22, while the coating 25 is not provided on the surfaces 217, 227 located inside the overlap portion 241.

[0079] In the above embodiment, the presence of the substantially black coating 25 reduces the maximum plate thickness t maxThe emissivity of both outer surfaces 216, 226 of the overlap portion 241 having the coating 25 is higher than the emissivity of one or more other surfaces of the steel plates 21, 22, 23. However, the method of increasing the emissivity of a selected portion of the blank 20 is not limited to the coating 25. For example, the emissivity of the selected portion can be increased more than that of the other portions by increasing the surface roughness of the selected portion compared to the surface roughness of the other portions.

[0080] In the above embodiment, the steel plates 21, 22, and 23 included in the blank 20 may each be a single layer or multiple layers. That is, the steel plates 21, 22, and 23 may each be a single steel plate or a plate material formed by overlapping a plurality of steel plates.

[0081] In the above embodiment, the ends of the steel plates 21 and 22 are overlapped and joined to each other to form an overlap portion 241. Similarly, the ends of the steel plates 21 and 23 are overlapped and joined to each other to form an overlap portion 242. Furthermore, the ends of the steel plates 22 and 23 are overlapped and joined to each other to form an overlap portion 243. However, it is sufficient that the blank 20 includes at least one overlap portion. That is, the steel plate 23 does not necessarily have to be overlapped and joined to the steel plates 21 and 22. The steel plate 23 may be butt-joined to one or both of the steel plates 21 and 22.

[0082] In the above embodiment, the blank 20 includes three steel plates 21, 22, and 23. However, the number of steel plates included in the blank 20 is not limited to this. The blank 20 may be composed of two steel plates, or may include four or more steel plates. The blank 20, which is annular in plan view, typically includes three or more steel plates. The maximum plate thickness t of the steel plates included in the blank 20 is maxThe steel sheets 21, 22 forming the overlap portion 241 having the above structure are treated to increase the emissivity on the surfaces 216, 226 located outside the overlap portion 241. The other steel sheets may or may not be treated to increase the emissivity. The blank 20 may include one or more steel sheets that have not been treated to increase the emissivity on one or both sides.

[0083] In the blank 20 according to the above embodiment, the minimum plate thickness t min The steel plates 21 and 22, which are different from the steel plate 23 constituting the portion having the maximum plate thickness t max However, the steel plate 21 or the steel plate 22 forming the overlap portion 241 has a minimum plate thickness t min The steel plate may have the following structure.

[0084] In the above embodiment, the maximum plate thickness t max However, in the blank 20, there is only one overlap portion 241 having a maximum sheet thickness t max There may be multiple overlapping parts having the maximum plate thickness t max Preferably, all overlapping portions having an emissivity enhancing treatment are provided on both outer surfaces.

[0085] In the blank 20 according to the above embodiment, the multiple steel plates 21, 22, 23 have different plate thicknesses. However, two or more of the steel plates included in the blank 20 may have the same plate thickness, or all of the steel plates may have the same plate thickness. When all of the steel plates included in the blank 20 have the same plate thickness, the portion of each steel plate that does not form the overlap portion has the minimum plate thickness t min Each overlap portion has a maximum plate thickness t max In this case, the maximum plate thickness t maxThe emissivity of both outer surfaces of the overlapping portion is greater than the emissivity of at least one of the other surfaces. When the thicknesses of the steel plates included in the blank 20 are all the same, t max / t min is 2.0.

[0086] In the above embodiment, the die 40 used for hot stamping the blank 20 includes a punch 41 and a die 42. However, the configuration of the die 40 is not limited to the example described in the above embodiment. The die 40 may further include, for example, a pad and a blank holder.

[0087] In the above embodiment, the main body 11 of the structural member 10 includes a front pillar 111, a center pillar 112, and a rocker 113. However, the member main body 11 can further include other components. For example, as shown in FIG. 5, the member main body 11 can further include a rear pillar 114. The structural member 10 according to the above embodiment is a door ring part (single door ring part) having a single ring shape. On the other hand, the structural member shown in FIG. 5 is a door ring part (double door ring part) having a double ring shape. When manufacturing a double door ring part, the blank that is the material for the part also has a double ring shape. EXAMPLES

[0088] The present disclosure will be described in more detail below with reference to examples, although the present disclosure is not limited to the following examples.

[0089] [First Example] In order to confirm the effects of this disclosure, a CAE analysis was performed on the press forming (hot stamping) of a structural member, which is a single door ring part, using commercially available software (AUTOFORM R.10, manufactured by AUTOFORM) while changing the type (material type) and thickness of the steel plate contained in the structural member, as well as the division pattern of the structural member.

[0090] The steel plates used in this analysis are shown in Table 1.

[0091] [Table 1]

[0092] In Table 1, the material type is listed in the following order: plating type, tensile strength, and application (hot stamping). Regarding the coating specifications, the black coating is a black coating containing carbon black and metal oxide. "Black coating - one side" means that one entire side of the steel sheet is covered with a black coating. "Black coating - both sides" means that both entire sides of the steel sheet are covered with a black coating.

[0093] The division patterns of the structural members are shown in Figures 6A to 6G. Figures 6A to 6G show the number of steel plates (materials) included in the structural members that are single door ring parts, and the positions of the joints between the steel plates in the structural members. In Figures 6A to 6G, each steel plate is given a number in parentheses.

[0094] The analysis conditions and results for division patterns 1 and 2 shown in Figures 6A and 6B are shown in Table 2. In Figures 6A and 6B, the structural member is formed of three materials (1) to (3). Each of materials (1) to (3) is overlapped and joined with the adjacent material.

[0095] [Table 2]

[0096] In Table 2, the "910℃ reaching time" is the time required for the material to reach the minimum thickness t min The material with the above properties is heated to 910℃ (A c3 "Heating completion time" is the time required for the part of the blank that has the slowest temperature rise to reach 910°C from the start of heating the blank until it is ready for hot stamping. "Process window (PW)" is the time required for the part of the blank that has the slowest temperature rise to reach 910°C from the start of heating the blank until it is ready for hot stamping. minThis is the value obtained by adding the allowable heating time (245 seconds) after a material with this characteristic reaches 910°C to the time it takes to reach 910°C, minus the time it takes to complete heating. The larger this value, the wider the process window of heating conditions is for hot stamping structural components.

[0097] With reference to Table 2 and FIG. 6A, in Example 1, the material (1) and the material (2) have a maximum plate thickness t max = 2.8 mm, and a black coating is applied to the surface located outside the overlap portion in each of the raw materials (1) and (2). On the other hand, a black coating is not applied to the surface located inside the overlap portion in each of the raw materials (1) and (2). In Example 1, the raw material (3) has a minimum plate thickness t min = 1.2 mm, and a black coating is applied to only one side of the blank (3). In Comparative Example 1, which has the same combination of material type and plate thickness as Example 1, a black coating is not applied to any of the blanks (1) to (3). In Example 1, a black coating is arranged on both outsides of the thickest overlap portion, which promotes temperature rise in this overlap portion and significantly shortens the heating completion time of the blank compared to Comparative Example 1. In Example 1, although the time to reach 910°C was faster than in Comparative Example 1 because a black coating was applied to the thinnest blank (3), the process window was expanded by nearly 60 seconds compared to Comparative Example 1.

[0098] Referring to Table 2 and FIG. 6B, in Example 3, the material (1) and the material (3) have the maximum plate thickness t max = 3.4 mm, and a black coating is applied to the surface located outside the overlap portion in each of the raw materials (1) and (3). On the other hand, a black coating is not applied to the surface located inside the overlap portion in each of the raw materials (1) and (3). In Example 3, the raw material (2) has a minimum plate thickness t min= 1.2 mm, and a black coating is applied to only one side of the blank (2). In Comparative Example 2, which has the same combination of material type and plate thickness as Example 3, a black coating is not applied to any of the blanks (1) to (3). In Example 3, a black coating is arranged on both outsides of the thickest overlap part, which promotes temperature rise in this overlap part, and the blank heating completion time is significantly shortened compared to Comparative Example 2. In Example 3, a black coating is applied to the thinnest blank (2), so the time to reach 910°C is faster than in Comparative Example 2, but the process window is expanded by 70 seconds or more compared to Comparative Example 2. In Comparative Example 2, the process window of the heating conditions disappears (negative).

[0099] In Example 2, the material (2) and the material (3) have a maximum plate thickness t max = 2.9 mm, and a black coating is applied to the surface located outside the overlap portion in each of the raw materials (2) and (3). On the other hand, a black coating is not applied to the surface located inside the overlap portion in each of the raw materials (2) and (3). In Example 2, the raw material (1) has a minimum plate thickness t min = 1.2 mm. It was also confirmed that the process window was sufficiently secured in this Example 2.

[0100] The analysis conditions and results for division patterns 3 and 4 shown in Figures 6C and 6D are shown in Table 3. In Figures 6C and 6D, the structural member is formed of four materials (1) to (4). Each of the materials (1) to (4) is overlapped and joined with the adjacent material.

[0101] [Table 3]

[0102] In Examples 4 to 10 in Table 3, as in Examples 1 to 3 (Table 2), at least the maximum plate thickness t maxA black coating is disposed on both outer surfaces of the overlapping portion having the black coating. Therefore, the process window of the heating conditions was sufficiently secured for Examples 4 to 10. When each Example is compared with the corresponding Comparative Example, it is found that the process window is expanded.

[0103] For example, in Example 8, the material (1) and the material (3) have a maximum plate thickness t max = 4.0 mm, and a black coating is applied to the surface located outside the overlap in each of the raw materials (1) and (3) (Table 3 and FIG. 6D). On the other hand, in Comparative Example 4, the combination of material type and plate thickness is the same as in Example 8, but a black coating is not applied to any of the materials, including the overlap. In Example 8, the temperature rise in the overlap is promoted, and the time to complete heating of the blank is significantly shortened compared to Comparative Example 4. In Example 8, the process window is expanded by more than 100 seconds compared to Comparative Example 4. In Comparative Example 4, the process window of the heating conditions disappears (negative).

[0104] For example, in Example 9, the materials (1) and (3), and the materials (3) and (4) each have a maximum plate thickness t max = 2.6 mm, and a black coating is applied to the surface located outside the overlap in each of the materials (1), (3), and (4) (Table 3 and FIG. 6D). On the other hand, in Comparative Example 7, the combination of material type and plate thickness is the same as in Example 9, but the materials (1) and (3) forming the overlap are not provided with a black coating. In Example 9, the temperature rise in the overlap is promoted, and the blank heating completion time is significantly shortened compared to Comparative Example 7. In Example 9, the process window is expanded by 80 seconds or more compared to Comparative Example 7. In Comparative Example 7, a black coating is applied to both sides of the thinnest material (4), and the time to reach 910 ° C is slightly faster than in Example 9 by a little more than 10 seconds, but in Example 9, the blank heating completion time is shortened by 70 seconds or more compared to Comparative Example 7, so it can be said that the process window is expanded compared to Comparative Example 7 even when the difference in the time to reach 910 ° C is taken into account.

[0105] The analysis conditions and results for division patterns 5 and 6 shown in Figures 6E and 6F are shown in Table 4. In Figures 6E and 6F, the structural member is formed from five materials (1) to (5). Each of the materials (1) to (5) is overlapped and joined with the adjacent material.

[0106] [Table 4]

[0107] In Examples 11 to 16 in Table 4, as in Examples 1 to 10 (Tables 2 and 3), at least the maximum plate thickness t max A black coating is arranged on both outer surfaces of the overlapping portion having the black coating. Therefore, the process window of the heating conditions was sufficiently secured for Examples 11 to 16. When each Example is compared with the corresponding Comparative Example, it is found that the process window is expanded.

[0108] For example, in Example 13, the material (1) and the material (2) have a maximum plate thickness t max = 3.2 mm, and a black coating is applied to the surface located outside the overlap in each of the raw materials (1) and (2) (Table 4 and FIG. 6F). On the other hand, in Comparative Example 9, the combination of material type and plate thickness is the same as in Example 13, but a black coating is not applied to any of the materials, including the overlap. In Example 13, the temperature rise in the overlap is promoted, and the time to complete heating of the blank is significantly shortened compared to Comparative Example 9. In Example 13, the process window is expanded by 90 seconds or more compared to Comparative Example 9. In Comparative Example 9, the process window of the heating conditions disappears (negative).

[0109] For example, in Example 15, the material (1) and the material (3) have a maximum plate thickness t maxAn overlap portion having a thickness t = 3.0 mm is formed, and a black coating is applied to the surface located outside the overlap portion in each of the raw materials (1) and (3) (Table 4 and FIG. 6F). In Example 15, the raw materials (3) and (4) have a maximum plate thickness t max = 3.0 mm, and a black coating is applied to the surface located outside the overlap in each of the raw materials (3) and (4). On the other hand, in Comparative Example 11, the combination of material type and plate thickness is the same as in Example 15, but a black coating is not applied to any of the materials, including the overlap. In Example 15, the temperature rise in the overlap is promoted, and the time to complete heating of the blank is significantly shortened compared to Comparative Example 11. In Example 15, the process window is expanded by 60 seconds or more compared to Comparative Example 11.

[0110] [Second Example] Regarding the press forming (hot stamping) of the structural members that are double door ring parts, an analysis similar to that in the first embodiment was carried out while changing the material type and plate thickness contained in the structural members, as well as the division pattern of the structural members.

[0111] As in the first embodiment, the steel plates used as materials were selected from those shown in Table 1. The division pattern of the structural members is as shown in Figs. 7A to 7D. Figs. 7A to 7D show the number of steel plates (materials) included in the structural members that are double door ring components, and the positions of the joints between the steel plates in the structural members. In Figs. 7A to 7D, each steel plate used as material is given a number in parentheses.

[0112] The analysis conditions and results for division patterns 8 and 9 shown in Figures 7A and 7B are shown in Table 5. In Figures 7A and 7B, the structural member is formed of six materials (1) to (6). Each of the materials (1) to (6) is overlapped and joined with the adjacent material.

[0113] [Table 5]

[0114] Referring to Table 5, in Examples 17 to 19, the materials (1) and (3) had the maximum plate thickness t max = 3.4 mm, and a black coating is applied to the surfaces of materials (1) and (3) located outside the overlapping portion. On the other hand, in Comparative Examples 12 and 13, no black coating is applied to any of materials (1) to (6) including the overlapping portion.

[0115] From Table 5, in Examples 17 to 19, the maximum plate thickness t max The temperature rise in the overlapping portion was promoted, and the time to complete heating of the blank was significantly shortened compared to Comparative Examples 12 and 13. As a result, in Examples 17 to 19, the process window of the heating conditions was significantly expanded compared to Comparative Examples 12 and 13.

[0116] The analysis conditions and results for division patterns 10 and 11 shown in Figures 7C and 7D are shown in Table 6. In Figures 7C and 7D, the structural member is formed from seven pieces of material (1) to (7). Each of the materials (1) to (7) is overlapped and joined with the adjacent material.

[0117] [Table 6]

[0118] Referring to Table 6, in Examples 20 to 22, the materials (1) and (3) had the maximum plate thickness t max = 3.4 mm, and a black coating is applied to the surfaces of materials (1) and (3) located outside the overlapping portion. On the other hand, in Comparative Examples 14 and 15, no black coating is applied to any of materials (1) to (7) including the overlapping portion.

[0119] From Table 6, in Examples 20 to 22, the maximum plate thickness t maxThe temperature rise in the overlapping portion was promoted, and the time to complete heating of the blank was significantly shortened compared to Comparative Examples 14 and 15. As a result, in Examples 20 to 22, the process window of the heating conditions was significantly expanded compared to Comparative Examples 14 and 15.

[0120] [Third Example] Regarding press forming (hot stamping) of structural members that are single door ring parts, the maximum plate thickness t max and minimum plate thickness t min To check the effect of the difference between t max / t min The analysis conditions and results are shown in Table 7.

[0121] [Table 7]

[0122] The division pattern in Test Examples 1 and 3 is division pattern 7 shown in FIG. 6G. The division pattern in Test Example 2 and Reference Example is division pattern 5 shown in FIG. 6E. In Test Examples 1 to 3 and Reference Example, each material forms an overlap portion at the joint with the other material. In all of Test Examples 1 to 3, the maximum plate thickness t max A black coating is applied to both outer surfaces of the overlapping portion having the overlapping portions. In each of Test Examples 1 to 3, each of the raw materials (1) to (5) has a difference in sheet thickness between itself and one or more other raw materials. On the other hand, in the Reference Example, the raw materials (1) to (5) all have the same sheet thickness. In the Reference Example, a black coating is not applied to any of the raw materials (1) to (5) including the overlapping portions.

[0123] In the reference example, there is no difference in thickness between materials (1) to (5), so the minimum thickness t min Maximum thickness t for (thickness of materials (1) to (5)) max (Thickness of overlapping part) ratio: t max / t min is 2.0. In the reference example, the maximum plate thickness t max and minimum plate thickness t min Difference from (tmax / t min ) is not large, so it is possible to secure a certain process window for the heating conditions without increasing the emissivity of both outer surfaces of the overlapping part. On the other hand, when there is a difference in thickness between the materials (1) to (5), the maximum thickness t max and minimum plate thickness t min Difference from (t max / t min ) exceeds 2.0. In this case, the effect of increasing the emissivity of both outer surfaces of the overlap portion (by providing a black coating) is likely to be significantly achieved.

[0124] From Table 7, the maximum plate thickness t max When a black coating is applied to both outer surfaces of the overlapping portion having t max / t min It can be seen that even when t exceeds 2.0, the heating completion time is unlikely to be long, and the process window can be secured (Test Examples 1 and 2). max / t min Although the process window was secured, the t max / t min In Test Example 3 where the value exceeded 4.0, the process window was negative.

[0125] According to the results of this analysis, when there is a difference in thickness between materials, t max / t min It is preferable that t≦3.2. If there is a difference in thickness between the materials, max / t min >2.0, but t max / t min It may be ≧2.5.

[0126] The productivity of the structural members and the greenhouse gas generation ratio were evaluated for Test Examples 1 to 3. The rust prevention performance of the structural members was also evaluated for Test Examples 1 to 3. The evaluation results are shown in Table 8.

[0127] [Table 8]

[0128] As shown in Table 8, in Test Examples 1 and 2, the time to complete heating of the blank was shorter than in Test Example 3, and therefore the productivity of the structural components was improved compared to Test Example 3. Furthermore, in Test Examples 1 and 2, the time to complete heating of the blank was shorter than in Test Example 3, and the amount of energy consumed in manufacturing the structural components was reduced, so the greenhouse gas generation rate during manufacturing was also reduced. "Productivity" in Table 8 is the number of blanks (structural components) that can be heat-treated in a heating furnace per minute. "Greenhouse gas generation rate" is the ratio of greenhouse gas generation rate to Test Example 3. The amount of greenhouse gases generated in the heating process was calculated by setting the power consumption of the multi-stage electric heating furnace for hot stamp blank heating at 450 kWh per hour, the furnace temperature at 920 °C, the daily operating time at 15 hours, and the heating and waiting time in the heating furnace at 3 hours, assuming the production of parts with the productivity shown in Table 8, allocating it to the power consumption per structural part, and multiplying it by the greenhouse gas intensity per kWh of the average electricity in Japan in 2018 (from the LCA database AIST IDEAv3.2). Other greenhouse gas emissions (other than the heating process) during the manufacture of structural parts were calculated using the method described in the public literature on LCA calculations for automotive parts (Masahiro Kubo, et al., “Evaluation of Greenhouse Gas Emissions in the Life Cycle of Steel Lightweight Vehicle Bodies and Parts”, Proceedings of the Spring Meeting Academic Lectures, Society of Automotive Engineers of Japan, 2022).

[0129] In Test Examples 1 and 2, the blank heating completion time was shortened compared to Test Example 3, so that the alloying of the thinnest plating layer of the material did not proceed excessively during heating of the blank, and the deterioration of the rust prevention performance (corrosion resistance) of the material was suppressed. In Test Examples 1 and 2, it was possible to maintain high rust prevention performance compared to Test Example 3. The rust prevention performance was evaluated by cutting out corrosion evaluation test pieces (evaluation samples) from the overlap part and other parts of the hot stamped structural member, adopting cycle conditions close to the actual environment specified in the accelerated corrosion test method (VDA233-102) of the German Association of the Automotive Industry (VDA), and conducting a combined cycle test (CCT). In Table 8, the rust prevention performance of all evaluation samples obtained from multiple parts of the structural member is evaluated as good without any problems, and is indicated by "○", and the rust prevention performance of even one of the evaluation samples is evaluated as poor is indicated by "×".

[0130] Test Example 3 was evaluated as being low in comparison with Test Examples 1 and 2. However, as explained in the first to third examples, the maximum plate thickness t max By increasing the emissivity of the surfaces on both sides of the overlap, it is possible to accelerate the temperature rise of the overlap and shorten the heating completion time. max Since the emissivity of both outer surfaces of the overlapping portion is increased, it is estimated that, compared to a case in which the combination of material type and plate thickness is the same as in Test Example 3 but the treatment to increase the emissivity is not applied to the both outer surfaces of the overlapping portion, the time to complete heating of the blank is shorter, and the productivity, greenhouse gas generation rate, and rust prevention performance are improved. [Explanation of symbols]

[0131] 10: Structural members 11: Main body of material 111: Front pillar 112: Center pillar 113: Locker 12: Film 20:Blank 21: Steel plate (first steel plate) 22: Steel plate (second steel plate) 23: Steel plate 21a, 22a, 23a: Base steel plate 21b, 22b, 23b: plating layer 241, 242, 243: Overlapped section 25: Membrane 40: Mold

Claims

1. A blank for hot stamping, The blank includes a plurality of steel plates that are arranged and joined to have an annular shape in a plan view, The plurality of steel plates include A first steel plate; A second steel plate having an end portion that is overlapped and joined to an end portion of the first steel plate to form an overlap portion together with the end portion of the first steel plate; Including, Among the plurality of steel sheets, a steel sheet constituting a portion having a minimum sheet thickness in the blank is a plated steel sheet having a base steel sheet and a plating layer provided on the base steel sheet, The overlap portion has a maximum plate thickness in the blank, A blank, wherein the emissivity of a surface of each of the first steel plate and the second steel plate located outside the overlap portion is greater than the emissivity of at least one of the other surfaces of the plurality of steel plates.

2. 2. The blank of claim 1, A blank, wherein each of the plurality of steel sheets is a plated steel sheet having a base steel sheet and a plating layer provided on the base steel sheet.

3. 3. The blank of claim 2, The blank, wherein the plating layer is an aluminum-based plating layer.

4. 2. The blank of claim 1, A blank, wherein the surfaces of each of the first steel plate and the second steel plate positioned outside the overlap portion are covered with a coating having an emissivity of 60% or more at a wavelength of 8.0 μm at 25° C.

5. 2. The blank of claim 1, A surface of each of the first steel plate and the second steel plate positioned outside the overlap portion is covered with a coating, The coating comprises carbon black, one or more oxides selected from the group consisting of Zr oxide, Zn oxide, and Ti oxide, and a weight ratio of 0 to 0.30 g / m ２ and silica, The content of the carbon black in the coating is X ＣＢ (g / m ２ ), the content of the oxide is X Ｏｘｉｄｅ (g / m ２ ) and then X ＣＢ and X Ｏｘｉｄｅ A blank satisfies the following formula (1): 118.9≦24280 / {6700 / (100+76×X ＣＢ )+18000 / (130+65×X Ｏｘｉｄｅ )}≦332.0 (1)

6. 2. The blank of claim 1, The plurality of steel plates includes two or more steel plates having different plate thicknesses, The thickness of the overlapping portion is t ｍａｘ The thickness of the steel plate constituting the part having the smallest thickness in the blank is t ｍｉｎ Then, t ｍａｘ / t ｍｉｎ ≦3.2, blank.

7. A method for manufacturing a structural member, comprising the steps of: Providing a blank according to any one of claims 1 to 6; Heating the plurality of steel plates included in the blank to an austenite transformation completion temperature or higher; forming the heated blank into an annular structural member in a plan view using a die and quenching the blank; A manufacturing method comprising:

8. A structural member, A member body including a first steel plate and a second steel plate having an end portion that is overlapped and joined to an end portion of the first steel plate to form an overlap portion together with the end portion of the first steel plate, the member body being formed by a plurality of steel plates joined to each other and having an annular shape in a plan view; a first steel plate and a second steel plate, the first steel plate and the second steel plate being provided on a surface located outside the overlap portion ... ２ A coating containing the above, A structural member comprising:

9. A structural member, A member body including a first steel plate and a second steel plate having an end portion that is overlapped and joined to an end portion of the first steel plate to form an overlap portion together with the end portion of the first steel plate, the member body being formed by a plurality of steel plates joined to each other and having an annular shape in a plan view; a carbon black layer having a thickness of 0.500 g / m2 and a thickness of 0.500 g / m2, the carbon black layer being provided on a surface located outside the overlap portion of each of the first steel plate and the second steel plate; ２ A coating containing the following: A structural member comprising:

10. A structural member according to claim 8 or 9, The structural member is a door ring part of an automobile, The member body is a structural member including a front pillar, a center pillar, and a rocker connecting the front pillar and the center pillar.

Images