Evaporation mask, framed deposition mask, method for manufacturing an evaporation mask, method for manufacturing an organic device, and method for manufacturing an evaporation mask with a frame

Abstract

To provide a vapor deposition mask capable of improving fineness, a vapor deposition mask with a frame, a vapor deposition mask manufacturing method, an organic device manufacturing method, and a method for manufacturing a vapor deposition mask with a frame.SOLUTION: A vapor deposition mask according to this disclosure comprises a mask substrate 15 including silicon, a mask layer 20 having a first face 20a and a second face 20b positioned on a side opposite to the first face and opposed to the mask substrate, and a through hole 40 penetrating through the mask layer. The mask substrate includes a substrate opening 16. When seen from a plane view, the through hole is positioned in the substrate opening. The mask layer has a mask body layer serving as a first face, and a mask intermediate layer positioned between the mask body layer and the mask substrate. The mask body layer includes a metallic material.SELECTED DRAWING: Figure 3

Description

[Technical field]

[0001] The present disclosure relates to a deposition mask, a framed deposition mask, a method for manufacturing a deposition mask, a method for manufacturing an organic device, and a framed deposition mask. [Background technology]

[0002] Display devices used in portable devices such as smartphones and tablets are preferably high definition, with a pixel density of, for example, 400 ppi or more. There is also an increasing demand for portable devices to support ultra-high definition (UHD), and in this case, the pixel density of the display device is preferably, for example, 800 ppi or more.

[0003] Among display devices, organic EL display devices, as an example of an organic device, have been attracting attention due to their good responsiveness, low power consumption, and high contrast. As a method for forming pixels of an organic EL display device, a method for forming pixels in a desired pattern using a deposition mask in which through-holes arranged in a desired pattern are formed is known. Specifically, first, a deposition mask is combined with a deposition substrate for an organic EL display device. Then, a deposition material containing an organic material is deposited on the deposition substrate by passing it through the through-holes of the deposition mask. This allows a deposition layer containing the deposition material (or a light-emitting layer of an organic EL display device) to be formed as pixels on the deposition substrate in the same pattern as the through-holes of the deposition mask (see, for example, Patent Documents 1 to 3).

[0004] As an example of a method for manufacturing such a deposition mask, a method is known in which through holes are formed in a metal plate by etching using a photolithography technique. [Prior art documents] [Patent documents]

[0005] [Patent Document 1] Patent No. 5382259 [Patent Document 2] Korean Patent No. 10-1812772 [Patent Document 3] JP 2010-116579 A Summary of the Invention [Problem to be solved by the invention]

[0006] An object of the present disclosure is to provide a deposition mask capable of improving definition, a framed deposition mask, a method for manufacturing a deposition mask, a method for manufacturing an organic device, and a method for manufacturing a framed deposition mask. [Means for solving the problem]

[0007] The deposition mask according to the present disclosure includes a mask substrate containing silicon, a mask layer having a first surface and a second surface located on the opposite side to the first surface and facing the mask substrate, and a through-hole penetrating the mask layer. The mask substrate has a substrate opening. In a plan view, the through-hole is located within the substrate opening. The mask layer has a mask body layer forming the first surface, and a mask intermediate layer located between the mask body layer and the mask substrate. The mask body layer contains a metal material.

[0008] A framed deposition mask according to the present disclosure includes the deposition mask described above and a frame that supports a mask substrate of the deposition mask.

[0009] The method for manufacturing a deposition mask according to the present disclosure includes a substrate preparation step of preparing a mask substrate containing silicon, a mask layer formation step, a substrate opening formation step, and a through hole formation step. In the mask layer formation step, a mask layer having a first surface and a second surface located on the opposite side to the first surface and facing the mask substrate is formed on the mask substrate. In the substrate opening formation step, a substrate opening is formed on the mask substrate. In the through hole formation step, a through hole penetrating the mask layer is formed. In a plan view, the through hole is located within the substrate opening. The mask layer formation step includes a mask intermediate layer formation step of forming a mask intermediate layer on a surface of the mask substrate facing the mask layer, and a mask main body layer formation step of forming a mask main body layer on a surface of the mask intermediate layer opposite to the mask substrate. The mask main body layer includes a metal material.

[0010] The method for manufacturing a deposition mask according to the present disclosure includes a substrate preparation step of preparing a mask substrate containing silicon, a mask layer formation step, a substrate opening formation step, and a mask layer opening formation step. In the mask layer formation step, a mask layer having a first surface and a second surface located on the opposite side to the first surface and facing the mask substrate is formed on the mask substrate. In the substrate opening formation step, a substrate opening is formed on the mask substrate. In the mask layer opening formation step, a mask layer opening is formed in the mask layer along the substrate opening in a plan view. The mask layer formation step includes a mask intermediate layer formation step of forming a mask intermediate layer on a surface of the mask substrate facing the mask layer, and a mask main layer formation step of forming a mask main layer on a surface of the mask intermediate layer opposite to the mask substrate and forming a through hole penetrating the mask main layer. In the mask layer opening formation step, the mask layer opening is formed in the mask intermediate layer. In a plan view, the through hole is located in the substrate opening. The mask main layer includes a metal material.

[0011] The method for manufacturing an organic EL device according to the present disclosure includes a deposition mask preparation step of preparing a deposition mask by the above-mentioned deposition mask manufacturing method, a bonding step, and a deposition step. In the bonding step, a first surface of the metal layer of the deposition mask is bonded to a deposition substrate. In the deposition step, a deposition material is deposited on the deposition substrate through the through-holes of the deposition mask to form a deposition layer.

[0012] The method for manufacturing a framed deposition mask according to the present disclosure includes a deposition mask preparation step of preparing a deposition mask by the above-described deposition mask manufacturing method, and a frame attachment step of attaching a frame to a mask substrate of the deposition mask. Effect of the Invention

[0013] According to the present disclosure, the definition can be improved. [Brief description of the drawings]

[0014] [Figure 1] FIG. 1 illustrates a deposition apparatus including a deposition mask according to an embodiment of the present disclosure. [Diagram 2] FIG. 2 is a plan view illustrating a deposition mask according to an embodiment of the present disclosure. [Diagram 3] FIG. 3 is a diagram showing a cross section taken along line AA in FIG. 2. [Figure 4] FIG. 3 is a partially enlarged plan view of the deposition mask of FIG. [Figure 5A] 5 is a partially enlarged plan view showing a through-hole group of the deposition mask in FIG. 4. [Figure 5B] 5B is a partially enlarged plan view showing a modified example of the through-hole group in FIG. 5A. FIG. [Figure 6] 1A to 1C are diagrams illustrating a substrate preparation step in a deposition mask manufacturing method according to an embodiment of the present disclosure. [Figure 7] 6A to 6C are diagrams illustrating a second metal layer forming step in the deposition mask manufacturing method according to the embodiment of the present disclosure. [Figure 8] 5A to 5C are diagrams illustrating a first metal layer forming step in the deposition mask manufacturing method according to the embodiment of the present disclosure. [Figure 9] 11A to 11C are diagrams illustrating a resist layer forming step in a substrate opening forming step in the method for manufacturing a deposition mask according to the embodiment of the present disclosure. [Figure 10] 11A to 11C are diagrams illustrating a substrate etching step in a substrate opening forming step in the manufacturing method of a deposition mask according to an embodiment of the present disclosure. [Figure 11A] 11 is a diagram showing a step of forming a first recess in the substrate etching step of FIG. 10. FIG. [Figure 11B] 11 is a diagram showing a step of forming a first protective layer in the substrate etching step of FIG. 10. FIG. [Figure 11C] 11 is a diagram showing a step of forming a second recess in the substrate etching step of FIG. 10. FIG. [Figure 11D] 11 is a diagram showing a step of forming a second protective layer in the substrate etching step of FIG. 10. FIG. [Figure 11E] 11 is a diagram showing a step of forming a fourth recess in the substrate etching step of FIG. 10. FIG. [Figure 12] 11A to 11C are diagrams illustrating a resist layer removing step in a substrate opening forming step in the deposition mask manufacturing method according to the embodiment of the present disclosure. [Figure 13A] 10A and 10B are diagrams illustrating a state in which a metal layer is irradiated with laser light in a through-hole forming step in the method for manufacturing a deposition mask according to an embodiment of the present disclosure. [Figure 13B] FIG. 13B is a diagram showing a modification of FIG. 13A. [Figure 13C] FIG. 13C is a schematic diagram showing the laser light generating device of FIG. 13B. [Figure 14] 10A to 10C are diagrams illustrating a state in which through holes are formed in a through hole forming step in the deposition mask manufacturing method according to the embodiment of the present disclosure. [Figure 15A] FIG. 2 is a plan view showing an example of an organic EL display device produced using a deposition mask in an embodiment of the present disclosure, the plan view showing an organic layer deposited in a deposition process. [Figure 15B] 15B is a cross-sectional view of the organic EL display device of FIG. 15A as viewed from the BB direction. [Figure 16]4 is a schematic cross-sectional view showing a modification of the deposition mask shown in FIG. [Figure 17] 17A to 17C are diagrams illustrating a resist layer forming step as a method for manufacturing the deposition mask shown in FIG. 16. [Figure 18] 17A to 17C are diagrams illustrating a first metal layer forming step as a method for manufacturing the deposition mask shown in FIG. 16. [Figure 19] 17A to 17C are diagrams illustrating a resist layer removing step as part of the method for producing the deposition mask shown in FIG. 16. [Figure 20] 17A to 17C are diagrams illustrating a substrate opening forming step as a method for manufacturing the deposition mask shown in FIG. 16. [Figure 21] 17A to 17C are diagrams illustrating a mask layer opening forming step as a method for manufacturing the deposition mask shown in FIG. 16. [Figure 22A] 4 is a schematic cross-sectional view showing a modification of the deposition mask shown in FIG. [Figure 22B] 4 is a schematic cross-sectional view showing another modified example of the deposition mask shown in FIG. [Figure 23] 3 is a plan view showing a modified example of the deposition mask shown in FIG. 2. [Figure 24] 5 is a partially enlarged plan view showing a modification of the deposition mask shown in FIG. [Diagram 25] 3 is a plan view showing a modified example of the deposition mask shown in FIG. 2. [Figure 26] FIG. 26 is a diagram showing a cross section taken along line CC in FIG. 25. [Figure 27] FIG. 26 is a plan view showing a modified example of the deposition mask shown in FIG. [Figure 28] FIG. 26 is a plan view showing a modified example of the deposition mask shown in FIG. [Figure 29] 11 is an enlarged plan view showing a modified example of a substrate opening of a deposition mask according to an embodiment of the present disclosure. FIG. [Diagram 30] 13 is an enlarged plan view showing another modified example of a substrate opening of a deposition mask according to an embodiment of the present disclosure. FIG. [Diagram 31] 13 is an enlarged plan view showing another modified example of a substrate opening of a deposition mask according to an embodiment of the present disclosure. FIG. [Diagram 32] FIG. 26 is a plan view showing a modified example of the deposition mask shown in FIG. [Diagram 33] FIG. 33 is a diagram showing a cross section taken along line DD in FIG. 32. [Diagram 34] 4 is a schematic cross-sectional view showing another modified example of the deposition mask shown in FIG. [Diagram 35] FIG. 26 is a plan view showing another modified example of the deposition mask shown in FIG. [Diagram 36] 36 is a diagram showing a schematic cross section taken along line EE in FIG. 35. FIG. [Figure 37] FIG. 26 is a plan view showing another modified example of the deposition mask shown in FIG. [Figure 38] FIG. 38 is a diagram showing a cross section taken along line FF in FIG. 37. [Figure 39] 39A to 39C are diagrams illustrating an insulating layer forming step as a method for manufacturing the deposition mask shown in FIG. 38. [Diagram 40] 39A to 39C are diagrams illustrating an insulating opening forming step as a method for manufacturing the deposition mask shown in FIG. 38. [Diagram 41] 39 is a diagram showing a first metal layer forming step as a manufacturing method of the deposition mask shown in FIG. 38. FIG. [Diagram 42] 39A to 39C are diagrams illustrating a polishing step as a method for manufacturing the deposition mask shown in FIG. 38. [Diagram 43] 39 is a diagram showing a first mask protective layer forming step as a manufacturing method of the deposition mask shown in FIG. 38. FIG. [Diagram 44] 39A to 39C are diagrams illustrating an insulating layer removing step as part of the method for manufacturing the deposition mask shown in FIG. 38. [Diagram 45] 39 is a diagram showing a second mask protective layer forming step as part of a method for manufacturing the deposition mask shown in FIG. 38. FIG. [Diagram 46] 39A to 39C are diagrams illustrating a substrate opening forming step as a manufacturing method for the deposition mask shown in FIG. 38. [Figure 47] 39A to 39C are diagrams illustrating a mask layer opening forming step as a manufacturing method for the deposition mask shown in FIG. 38. [Figure 48] 39 is a diagram showing a second protective layer removing step as part of the method for manufacturing the deposition mask shown in FIG. 38. FIG. [Figure 49]11 is an enlarged plan view showing a modification of the first metal layer of the deposition mask according to the embodiment of the present disclosure. FIG. [Figure 50] FIG. 26 is a plan view showing another modified example of the deposition mask shown in FIG. [Figure 51] FIG. 51 is a schematic cross-sectional view taken along line GG in FIG. 50. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0015] In this specification and drawings, unless otherwise specified, terms meaning a material serving as the basis of a certain configuration, such as "substrate," "base material," "plate," "sheet," and "film," are not to be distinguished from one another solely on the basis of differences in name.

[0016] In this specification and drawings, unless otherwise specified, terms that specify shapes, geometric conditions, and the extent thereof, such as "parallel" and "orthogonal," and values ​​of lengths and angles, are not to be bound by strict meanings, but are to be interpreted within a range within which similar functions can be expected.

[0017] In this specification and drawings, unless otherwise specified, when a certain component, region, or other component is described as being "on" or "under", "upper" or "lower", or "above" or "below" another component, region, or other component, this includes the case where the component is directly in contact with the other component. It also includes the case where another component is included between the component and the other component, that is, the case where the components are indirectly in contact. Furthermore, unless otherwise specified, the terms "on", "upper side", "upper", or "lower", or "lower", "lower side", and "lower" may be used in the up-down direction.

[0018] In this specification and drawings, unless otherwise specified, the state in which the face of element A is "facing" the face of element B includes not only the case in which the face of element A is in contact with the face of element B, but also the case in which element C is located between the faces of element A and element B. In other words, the term "facing" is a term that indicates the orientation of two faces.

[0019] In this specification and drawings, unless otherwise specified, the same or similar parts or parts having similar functions are denoted by the same or similar symbols, and repeated explanations may be omitted. In addition, the dimensional ratios of the drawings may differ from the actual ratios for the convenience of explanation, and some components may be omitted from the drawings.

[0020] In this specification and drawings, unless otherwise specified, the present invention may be combined with other embodiments or modified examples to the extent that no contradiction occurs. In addition, other embodiments may be combined with each other, or other embodiments may be combined with modified examples to the extent that no contradiction occurs. In addition, modified examples may be combined with each other to the extent that no contradiction occurs.

[0021] In this specification and drawings, unless otherwise specified, when a plurality of steps are disclosed in a method such as a manufacturing method, other steps that are not disclosed may be performed between the disclosed steps. In addition, the order of the disclosed steps is arbitrary within the range that does not cause contradictions.

[0022] In this specification and drawings, unless otherwise specified, a numerical range expressed by the symbol "~" includes the numerical values ​​before and after the symbol "~". For example, the numerical range defined by the expression "34 to 38 mass%" is the same as the numerical range defined by the expression "34 mass% or more and 38 mass% or less".

[0023] In this specification and the drawings, unless otherwise specified, an embodiment of this specification will be described by taking an example related to a deposition mask used for patterning an organic material in a desired pattern on a substrate when manufacturing an organic device, and a manufacturing method thereof. However, this embodiment is not limited to such an application, and can be applied to deposition masks used for various purposes.

[0024] Hereinafter, an embodiment of the present disclosure will be described in detail with reference to the drawings. The embodiment described below is an example of an embodiment of the present disclosure, and the present disclosure is not to be interpreted as being limited to only these embodiments.

[0025] A first aspect of the present disclosure is a method for manufacturing a semiconductor device comprising: a mask substrate comprising silicon; a mask layer having a first surface and a second surface located opposite to the first surface and facing the mask substrate; a through hole penetrating the mask layer; the mask substrate has a substrate opening; In a plan view, the through hole is located within the substrate opening, the mask layer includes a mask body layer forming the first surface, and a mask intermediate layer located between the mask body layer and the mask substrate; a deposition mask, wherein the mask body layer contains a metal material; It is.

[0026] As a second aspect of the present disclosure, in the deposition mask according to the first aspect described above, The thickness of the mask intermediate layer is smaller than the thickness of the mask body layer. This may be done.

[0027] As a third aspect of the present disclosure, in the deposition mask according to the first or second aspect described above, the mask intermediate layer includes a substrate side layer including gold, aluminum, chromium, nickel, titanium, titanium nitride, an aluminum alloy including neodymium, silicon oxide, or silicon dioxide; the substrate side layer is in contact with the mask body layer and is in contact with the mask substrate; This may be done.

[0028] As a fourth aspect of the present disclosure, in the deposition mask according to the first or second aspect described above, the mask intermediate layer includes a body-side layer facing the mask body layer and a substrate-side layer facing the mask substrate, The body side layer and the substrate side layer are made of different metal materials. This may be done.

[0029] As a fifth aspect of the present disclosure, in the deposition mask according to the fourth aspect described above, The substrate side layer includes gold, aluminum, chromium, nickel, titanium, titanium nitride, aluminum alloy containing neodymium, silicon oxide, or silicon dioxide; This may be done.

[0030] As a sixth aspect of the present disclosure, in the deposition mask according to the fourth or fifth aspect described above, The body side layer includes titanium, copper, nickel, or gold. This may be done.

[0031] As a seventh aspect of the present disclosure, in a deposition mask according to each of the fourth aspect to the sixth aspect described above, the mask intermediate layer includes an intermediate layer located between the substrate side layer and the body side layer, The intermediate layer is made of a metal material different from that of the main body side layer and the substrate side layer. This may be done.

[0032] As an eighth aspect of the present disclosure, in the deposition mask according to the seventh aspect described above, The intermediate layer comprises titanium, titanium nitride, aluminum, an aluminum alloy containing neodymium, silicon oxide, silicon dioxide, nickel, copper, chromium or gold; This may be done.

[0033] As a ninth aspect of the present disclosure, in a deposition mask according to each of the first aspect to the eighth aspect described above, the metal material of the mask body layer is a magnetic metal material; This may be done.

[0034] As a tenth aspect of the present disclosure, in a deposition mask according to each of the first aspect to the ninth aspect described above, the mask substrate has a substrate body defining the substrate opening; the mask intermediate layer includes a body region located between the mask body layer and the substrate body, and an opening region located within the substrate opening in a plan view, The through-hole penetrates the mask body layer and the opening region. This may be done.

[0035] As an eleventh aspect of the present disclosure, in the deposition mask according to the tenth aspect described above, an opening dimension of the through hole in the second surface in a predetermined direction is larger than an opening dimension of the through hole in the first surface in the predetermined direction; This may be done.

[0036] As a twelfth aspect of the present disclosure, in a deposition mask according to each of the first aspect to the ninth aspect described above, the mask substrate has a substrate body defining the substrate opening; the mask intermediate layer includes a body region portion located between the mask body layer and the substrate body, and a mask layer opening formed along the substrate opening in a plan view, The through-hole penetrates the mask body layer. This may be done.

[0037] As a thirteenth aspect of the present disclosure, in the deposition mask according to the twelfth aspect described above, an opening dimension in a predetermined direction of the through hole in a surface of the mask body layer facing the mask substrate is larger than an opening dimension in the predetermined direction of the through hole in the first surface; This may be done.

[0038] As a fourteenth aspect of the present disclosure, in a deposition mask according to each of the first aspect to the thirteenth aspect described above, the mask layer has two or more of the through holes, In a plan view, two or more of the through holes are located within the substrate opening. This may be done.

[0039] As a fifteenth aspect of the present disclosure, in the deposition mask according to the fourteenth aspect described above, the mask layer has two or more through hole groups each composed of two or more of the through holes, In a plan view, two or more of the through hole groups are located within the substrate opening. This may be done.

[0040] As a sixteenth aspect of the present disclosure, in the deposition mask according to the fourteenth aspect described above, the mask substrate has two or more of the substrate openings; the mask layer has two or more through hole groups each composed of two or more of the through holes, In plan view, two or more of the through-hole groups may be located within each of the substrate openings.

[0041] As a seventeenth aspect of the present disclosure, in the deposition mask according to the fourteenth aspect described above, the mask substrate has two or more of the substrate openings; the mask layer has two or more through hole groups each composed of two or more of the through holes, In a plan view, one of the through hole groups is located within each of the substrate openings. This may be done.

[0042] As an eighteenth aspect of the present disclosure, in a deposition mask according to each of the first aspect to the seventeenth aspect described above, The substrate opening is formed in a rectangular shape in a plan view, A curved portion is provided at each of four corners of the outline of the substrate opening in a plan view. This may be done.

[0043] As a nineteenth aspect of the present disclosure, in a deposition mask according to each of the first to ninth aspects described above, a first alignment mark is provided on a surface of the mask substrate opposite to the mask layer; This may be done.

[0044] As a twentieth aspect of the present disclosure, in the deposition mask according to the nineteenth aspect described above, the mask substrate has a substrate body that defines the substrate opening, and an inner protrusion that protrudes inward from the substrate body in a plan view, the first alignment mark is located on the inner protrusion; This may be done.

[0045] As a 21st aspect of the present disclosure, in the deposition mask according to the 19th aspect or the 20th aspect, a second alignment mark is provided at a position closer to the through hole than the first alignment mark; This may be done.

[0046] As a 22nd aspect of the present disclosure, in the deposition mask according to the 21st aspect described above, the mask layer has two or more of the through holes, two or more through hole groups each composed of the two or more through holes, and mask bars provided between adjacent ones of the through hole groups, the second alignment mark is located on the mask rail; This may be done.

[0047] As a 23rd aspect of the present disclosure, in the deposition mask according to the 22nd aspect described above, the mask bars include first mask bars and second mask bars extending in directions perpendicular to each other in a plan view, the second alignment mark is located at an intersection where the first mask bar and the second mask bar intersect. This may be done.

[0048] As a 24th aspect of the present disclosure, in a deposition mask according to each of the first to 23rd aspects described above, In a plan view, an outer edge of the mask body layer is located inside an outer edge of the mask intermediate layer. This may be done.

[0049] As a 25th aspect of the present disclosure, in the deposition mask according to each of the first to 24th aspects described above, the mask body layer includes two or more body islands; a groove penetrating the mask body layer is located between two adjacent body islands; This may be done.

[0050] As a 26th aspect of the present disclosure, in a deposition mask according to each of the first to 25th aspects described above, the mask layer has a mask insulating layer forming the first surface; the mask body layer includes two or more body islands; the mask insulating layer is located between two adjacent body islands; This may be done.

[0051] As a 27th aspect of the present disclosure, in a deposition mask according to each of the first to 26th aspects described above, the mask layer has two or more through hole groups each composed of two or more of the through holes, the mask layer has a mask insulating layer forming the first surface; the mask insulating layer is located between two adjacent groups of the through holes; This may be done.

[0052] As a 28th aspect of the present disclosure, in a deposition mask according to each of the first to 27th aspects described above, the mask body layer includes a dummy body island located at a position not overlapping with the substrate opening in a plan view; This may be done.

[0053] A twenty-ninth aspect of the present disclosure is a method for producing a semiconductor device comprising the steps of: A deposition mask according to any one of the first to twenty-eighth aspects described above; a frame supporting the mask substrate of the deposition mask; It is.

[0054] A thirtieth aspect of the present disclosure is a method for producing a semiconductor device comprising the steps of: a substrate preparation step of preparing a mask substrate comprising silicon; a mask layer forming step of forming a mask layer on the mask substrate, the mask layer having a first surface and a second surface located on the opposite side to the first surface and facing the mask substrate; a substrate aperture forming step of forming a substrate aperture in the mask substrate; and forming a through hole penetrating the mask layer, In a plan view, the through hole is located within the substrate opening, the mask layer forming step includes a mask intermediate layer forming step of forming a mask intermediate layer on a surface of the mask substrate facing the mask layer, and a mask main body layer forming step of forming a mask main body layer on a surface of the mask intermediate layer opposite to the mask substrate, A method for manufacturing a deposition mask, wherein the mask body layer contains a metal material; It is.

[0055] As a 31st aspect of the present disclosure, in the method for producing a deposition mask according to the 30th aspect described above, In the through hole forming step, the through hole is formed by irradiating the mask layer with a laser light. This may be done.

[0056] As a thirty-second aspect of the present disclosure, in the method for producing a deposition mask according to the thirty-first aspect described above, the through hole forming step is carried out after the substrate opening forming step, the laser light is irradiated onto the second surface of the mask layer through the substrate opening; This may be done.

[0057] As a 33rd aspect of the present disclosure, in the method for producing a deposition mask according to the 31st aspect or the 33rd aspect, The laser light is a femtosecond laser light. This may be done.

[0058] As a 34th aspect of the present disclosure, in the method for manufacturing a deposition mask according to each of the 31st aspect to the 32nd aspect, In the through hole forming step, the laser light is irradiated onto the mask layer through a mask hole of a photomask corresponding to the through hole. This may be done.

[0059] As a 35th aspect of the present disclosure, in the method for producing a deposition mask according to the 34th aspect, the photomask has a plurality of the mask holes; In the through hole forming step, the laser light is irradiated onto the mask layer through a plurality of the mask holes of the photomask. This may be done.

[0060] As a 36th aspect of the present disclosure, in a method for manufacturing a deposition mask according to each of the 30th aspect to the 35th aspect, the mask substrate has a substrate body defining the substrate opening; the mask intermediate layer includes a body region located between the mask body layer and the substrate body, and an opening region located within the substrate opening in a plan view, In the through hole forming step, the through hole is formed so as to penetrate the mask body layer and the opening region. This may be done.

[0061] As a 37th aspect of the present disclosure, in the method for manufacturing a deposition mask according to the 36th aspect described above, an opening dimension of the through hole in the second surface in a predetermined direction is larger than an opening dimension of the through hole in the first surface in the predetermined direction; This may be done.

[0062] As a 38th aspect of the present disclosure, in a method for manufacturing a deposition mask according to each of the 30th aspect to the 35th aspect, a mask layer opening forming step of forming a mask layer opening in the mask intermediate layer along the substrate opening in a plan view after the substrate opening forming step; In the through hole forming step, the through hole is formed so as to penetrate the mask body layer. This may be done.

[0063] As a thirty-ninth aspect of the present disclosure, in the method for producing a deposition mask according to the thirty-eighth aspect, an opening dimension in a predetermined direction of the through hole in a surface of the mask body layer facing the mask substrate is larger than an opening dimension in the predetermined direction of the through hole in the first surface; This may be done.

[0064] A fortieth aspect of the present disclosure is a method for producing ... composition comprising the steps of: a substrate preparation step of preparing a mask substrate comprising silicon; a mask layer forming step of forming a mask layer on the mask substrate, the mask layer having a first surface and a second surface located on the opposite side to the first surface and facing the mask substrate; a substrate aperture forming step of forming a substrate aperture in the mask substrate; a mask layer opening forming step of forming a mask layer opening in the mask layer along the substrate opening in a plan view, the mask layer forming step includes a mask intermediate layer forming step of forming a mask intermediate layer on a surface of the mask substrate facing the mask layer, and a mask main body layer forming step of forming a mask main body layer on a surface of the mask intermediate layer opposite to the mask substrate and forming a through hole penetrating the mask main body layer, In the mask layer opening forming step, the mask layer opening is formed in the mask intermediate layer, In a plan view, the through hole is located within the substrate opening, The mask body layer includes a metal material. A method for manufacturing a deposition mask, It is.

[0065] As a 41st aspect of the present disclosure, in the method for producing a deposition mask according to the above-mentioned 40th aspect, In the mask body layer forming step, a resist layer is formed in a pattern corresponding to the through hole on a surface of the mask intermediate layer opposite to the mask substrate. This may be done.

[0066] As a 42nd aspect of the present disclosure, in the method for producing a deposition mask according to the above-mentioned 40th aspect or the above-mentioned 41st aspect, an opening dimension in a predetermined direction of the through hole in a surface of the mask body layer facing the mask substrate is larger than an opening dimension in the predetermined direction of the through hole in the first surface; This may be done.

[0067] As a 43rd aspect of the present disclosure, in the method for manufacturing a deposition mask according to each of the 40th aspect to the 42nd aspect, in the mask body layer forming step, a mask insulating layer is formed in a pattern corresponding to the through hole on a surface of the mask intermediate layer opposite to the mask substrate, the mask body layer includes two or more body islands; the mask insulating layer is located between two adjacent body islands; This may be done.

[0068] As a 44th aspect of the present disclosure, in the method for producing a deposition mask according to each of the 30th aspect to the 43rd aspect, the metal material of the mask body layer is a magnetic metal material; This may be done.

[0069] As a 45th aspect of the present disclosure, in the method for manufacturing a deposition mask according to each of the 30th aspect to the 44th aspect, The thickness of the mask intermediate layer is smaller than the thickness of the mask body layer. This may be done.

[0070] As a 46th aspect of the present disclosure, in the method for manufacturing a deposition mask according to each of the 30th aspect to the 45th aspect, The substrate opening forming step includes a resist layer forming step of forming a resist layer having a resist opening on a surface of the mask substrate opposite to the mask layer, and a substrate etching step of etching the mask substrate through the resist opening to form the substrate opening. This may be done.

[0071] As a 47th aspect of the present disclosure, in the method for producing a deposition mask according to the 46th aspect described above, the mask intermediate layer includes a substrate side layer including a material that can ensure adhesion to the mask substrate and is resistant to an etching medium used in the substrate etching step; This may be done.

[0072] As a 48th aspect of the present disclosure, in the method for producing a deposition mask according to the 47th aspect, the mask intermediate layer includes a body side layer facing the mask body layer and including a material capable of ensuring adhesion with the mask body layer; This may be done.

[0073] As a 49th aspect of the present disclosure, in the method for producing a deposition mask according to the 48th aspect, In the mask layer forming step, the mask body layer is formed by a plating process, The mask intermediate layer is located between the substrate side layer and the body side layer. an intermediate layer including a material capable of protecting the substrate side layer from a plating solution for forming the mask body layer; This may be done.

[0074] As a 50th aspect of the present disclosure, in the method for producing a deposition mask according to the 47th aspect, The substrate side layer may be in contact with the mask body layer and also in contact with the mask substrate.

[0075] As a 51st aspect of the present disclosure, in a method for manufacturing a deposition mask according to each of the 30th aspect to the 50th aspect, In the mask layer forming step, the mask intermediate layer is formed by a sputtering process. This may be done.

[0076] As a 52nd aspect of the present disclosure, in a method for manufacturing a deposition mask according to each of the 30th aspect to the 50th aspect, In the mask layer forming step, the mask intermediate layer may be formed by a vapor deposition process.

[0077] As a 53rd aspect of the present disclosure, in a method for manufacturing a deposition mask according to each of the 30th aspect to the 52nd aspect, the mask layer has two or more of the through holes, In a plan view, two or more of the through holes are located within the substrate opening. This may be done.

[0078] As a 54th aspect of the present disclosure, in the method for producing a deposition mask according to the 53rd aspect described above, the mask layer has two or more through hole groups each composed of two or more of the through holes, When viewed in a plan view, two or more of the through hole groups are located within the substrate opening. This may be done.

[0079] As a 55th aspect of the present disclosure, in the method for producing a deposition mask according to the 53rd aspect described above, the mask substrate has two or more of the substrate openings; the mask layer has two or more through hole groups each composed of two or more of the through holes, In plan view, two or more of the through-hole groups may be located within each of the substrate openings.

[0080] As a 56th aspect of the present disclosure, in the method for producing a deposition mask according to the 53rd aspect described above, the mask substrate has two or more of the substrate openings; the mask layer has two or more through hole groups each composed of two or more of the through holes, In a plan view, one of the through hole groups is located within each of the substrate openings. This may be done.

[0081] As a 57th aspect of the present disclosure, in a method for manufacturing a deposition mask according to each of the 30th aspect to the 56th aspect, The substrate opening is formed in a rectangular shape in a plan view, A curved portion is provided at each of four corners of the outline of the substrate opening in a plan view. This may be done.

[0082] As a 58th aspect of the present disclosure, in a method for manufacturing a deposition mask according to each of the 30th aspect to the 57th aspect, forming a first alignment mark on a surface of the mask substrate opposite to the mask layer; This may be done.

[0083] As a fifty-ninth aspect of the present disclosure, in the method for producing a deposition mask according to the fifty-eighth aspect described above, the mask substrate has a substrate body that defines the substrate opening, and an inner protrusion that protrudes inward from the substrate body in a plan view, the first alignment mark is located on the inner protrusion; This may be done.

[0084] As a 60th aspect of the present disclosure, in the method for producing a deposition mask according to the 58th aspect or the 59th aspect, forming a second alignment mark at a position closer to the through hole than the first alignment mark; This may be done.

[0085] As a 61st aspect of the present disclosure, in the method for producing a deposition mask according to the 60th aspect described above, the mask layer has two or more of the through holes, two or more through hole groups each composed of the two or more through holes, and mask bars provided between adjacent ones of the through hole groups, the second alignment mark is located on the mask rail; This may be done.

[0086] As a 62nd aspect of the present disclosure, in the method for producing a deposition mask according to the 61st aspect described above, the mask bars include first and second mask bars extending in directions perpendicular to each other in a plan view, the second alignment mark is located at an intersection where the first mask bar and the second mask bar intersect. This may be done.

[0087] As a 63rd aspect of the present disclosure, in a method for manufacturing a deposition mask according to each of the 30th aspect to the 62nd aspect, In a plan view, an outer edge of the mask body layer is located inside an outer edge of the mask intermediate layer. This may be done.

[0088] As a 64th aspect of the present disclosure, in a method for manufacturing a deposition mask according to each of the 30th aspect to the 63rd aspect, the mask body layer includes two or more body islands; a groove penetrating the mask body layer is located between two adjacent body islands; This may be done.

[0089] As a 65th aspect of the present disclosure, in a method for manufacturing a deposition mask according to each of the 30th aspect to the 64th aspect, the mask layer has two or more through hole groups each composed of two or more of the through holes, the mask layer has a mask insulating layer forming the first surface; The mask insulating layer may be located between two adjacent groups of the through holes.

[0090] As a 66th aspect of the present disclosure, in a method for manufacturing a deposition mask according to each of the 30th aspect to the 65th aspect, the mask body layer includes a dummy body island located at a position not overlapping with the substrate opening in a plan view; This may be done.

[0091] Each of the 30th to 66th aspects may be a deposition mask manufactured by the deposition mask manufacturing method of each of the 30th to 66th aspects.

[0092] A sixty-seventh aspect of the present disclosure is a method for producing a semiconductor device comprising the steps of: a deposition mask preparation step of preparing the deposition mask by the deposition mask manufacturing method according to any one of the 30th to 66th aspects; a bonding step of bonding the first surface of the mask layer of the deposition mask to a deposition substrate; a deposition step of depositing a deposition material onto the deposition substrate through the through-holes of the deposition mask to form a deposition layer; It is.

[0093] The above-mentioned sixty-seventh aspect may be an organic device manufactured by the method for manufacturing an organic device of the sixty-seventh aspect.

[0094] A sixty-eighth aspect of the present disclosure is a method for producing a semiconductor device comprising the steps of: a deposition mask preparation step of preparing the deposition mask by the deposition mask manufacturing method according to any one of the 30th to 66th aspects; a frame attachment step of attaching a frame to the mask substrate of the deposition mask; It is.

[0095] The above-mentioned sixty-eighth aspect may be a framed deposition mask manufactured by the method for manufacturing a framed deposition mask of the sixty-eighth aspect.

[0096] Hereinafter, an embodiment of the present disclosure will be described in detail with reference to the drawings. The embodiment described below is an example of an embodiment of the present disclosure, and the present disclosure is not limited to only these embodiments.

[0097] First, a deposition apparatus 80 for performing a deposition process for depositing a deposition material on a target object will be described with reference to FIG. 1. As shown in FIG. 1, the deposition apparatus 80 may include a deposition source (e.g., a crucible 81), a heater 83, and a deposition mask 10. The deposition apparatus 80 may further include an exhaust means (not shown). The exhaust means can reduce the pressure inside the deposition apparatus 80 to a vacuum atmosphere. The crucible 81 is provided inside the deposition apparatus 80 and configured to accommodate a deposition material 82 such as an organic light-emitting material. The heater 83 is configured to heat the crucible 81. By heating the crucible 81 in a vacuum atmosphere, the deposition material 82 evaporates.

[0098] The deposition mask 10 is disposed in the deposition apparatus 80 so as to face the crucible 81. The deposition mask 10 may be disposed above the crucible 81. A deposition substrate 110 is disposed so as to face the deposition mask 10. The deposition substrate 110 is an object to which the deposition material 82 is to be attached. The deposition substrate 110 may be disposed above the deposition mask 10. The deposition material flying from the crucible 81 passes through through-holes 40 of the deposition mask 10, which will be described later, and is attached to the deposition substrate 110.

[0099] As shown in FIG. 1, the deposition apparatus 80 may include a magnet 85 arranged on the surface of the deposition substrate 110 opposite to the deposition mask 10. The deposition mask 10 can be attracted toward the magnet 85 by the magnetic force of the magnet 85, and the deposition mask 10 can be attached to the deposition substrate 110. This can suppress the occurrence of a shadow (described later) in the deposition process. This can improve the shape accuracy and position accuracy of a deposition layer (or organic layers 130A, 130B, and 130C of an organic device 100 described later, see FIGS. 15A and 15B) formed by the deposition material 82 attached to the deposition substrate 110. A cooling plate (not shown) for cooling the deposition substrate 110 during deposition may be interposed between the deposition substrate 110 and the magnet 85.

[0100] Next, the deposition mask 10 according to the present embodiment will be described in more detail with reference to FIGS. 1 to 5B.

[0101] 1 to 3, the deposition mask 10 may include a mask layer 20 provided with through-holes 40 described later, and a mask substrate 15 supporting the mask layer 20. The mask substrate 15 may be located on a second surface 20b of the mask layer 20 described later.

[0102] As shown in FIG. 2, the deposition mask 10 according to the present embodiment may have a planar shape similar to that of a silicon wafer used in semiconductor manufacturing when viewed in a direction perpendicular to a first surface 20a described later (hereinafter referred to as a planar view). In this case, both the mask layer 20 and the mask substrate 15 may have a shape similar to that of a silicon wafer. The silicon wafer may have a planar shape (see FIG. 2) in which a part of a circle is linearly cut out, called an orientation flat, like a general wafer shape. Alternatively, the silicon wafer may have a planar shape in which a part of a circle is concavely cut out, called a notch.

[0103] As shown in Fig. 3, the mask substrate 15 may have a first substrate surface 15a facing the mask layer 20 and a second substrate surface 15b located on the opposite side to the first substrate surface 15a. The mask layer 20 (more specifically, the substrate-side layer 26 described later) may be attached or fixed to the first substrate surface 15a. The mask layer 20 and the mask substrate 15 may be inseparably attached to each other by a layer (for example, a second metal layer 22 described later) formed by sputtering the mask layer 20 or vapor deposition processing described later. Fig. 3 is a schematic diagram of the cross section taken along the line AA in Fig. 2, and the number of through-hole groups 30 and the number of through-holes 40 are reduced to make the drawing easier to understand.

[0104] As shown in FIG. 2 and FIG. 3, the mask substrate 15 may have a substrate opening 16 exposing the through-hole 40 of the mask layer 20. The substrate opening 16 extends from the first substrate surface 15a to the second substrate surface 15b and penetrates the mask substrate 15. In a plan view, the through-hole 40 may be located in the substrate opening 16, or a plurality of through-holes 40 may be located. In one embodiment, the mask substrate 15 may have a frame shape in a plan view. As shown in FIG. 2, the mask substrate 15 may have a substrate frame 17 that is located outside the through-hole group 30 and has a planar shape that follows the outer edge 15c of the mask substrate 15. This substrate frame 17 is an example of a substrate main body. The substrate opening 16 may be defined inside the substrate frame 17. As shown in FIG. 2, the substrate opening 16 may have a contour similar to the outer edge 15c of the mask substrate 15 in a plan view, or may have a circular contour.

[0105] The diameter of the mask substrate 15 is not particularly limited, but may be, for example, 150 mm (6 inches), 200 mm (8 inches), 300 mm (12 inches), or 450 mm (18 inches).

[0106] The thickness H1 of the mask substrate 15 is not particularly limited, but may be 0.625 mm when the diameter is 150 mm, 0.725 mm when the diameter is 200 mm, or 0.775 mm when the diameter is 300 mm.

[0107] The mask substrate 15 may contain silicon. For example, when a glass substrate is used as the deposition substrate 110, the thermal expansion coefficient of the mask substrate 15 can be adjusted to a value equal to or close to that of the glass substrate. During the deposition process, the shape accuracy and position accuracy of the organic layers 130A, 130B, and 130C formed on the deposition substrate 110 may be reduced due to the difference in thermal expansion coefficient between the deposition mask 10 including the mask layer 20 and the deposition substrate 110. Hereinafter, this reduction may be referred to as a reduction in accuracy. The reduction in accuracy can be suppressed by adjusting the thermal expansion coefficient of the mask substrate 15 to a value equal to or close to that of the glass substrate. Furthermore, when a silicon substrate is used as the deposition substrate 110, the mask substrate 15 can be made of the same material as or the same material as the deposition substrate 110. In this case, the difference between the thermal expansion coefficient of the mask substrate 15 and the thermal expansion coefficient of the deposition substrate 110 can be reduced. Furthermore, the thermal expansion coefficient of the mask substrate 15 and the thermal expansion coefficient of the deposition substrate 110 can be made equal. This can further suppress the reduction in accuracy.

[0108] 3, the mask layer 20 may have a first surface 20a and a second surface 20b located on the opposite side to the first surface 20a and facing the mask substrate 15. The first surface 20a may be a surface to which the deposition substrate 110 comes into close contact during deposition. The second surface 20b may be attached to the mask substrate 15.

[0109] The thickness H2 of the mask layer 20 may be, for example, 2 μm or more, 3 μm or more, 4 μm or more, or 5 μm or more. By setting the thickness H2 to 2 μm or more, the mechanical strength of the mask layer 20 can be ensured and deformation or damage during handling can be suppressed. The thickness H2 may be, for example, 6 μm or less, 7 μm or less, 8 μm or less, or 9 μm or less. By setting the thickness H2 to 9 μm or less, the occurrence of a shadow can be suppressed. The range of the thickness H2 may be determined by a first group consisting of 2 μm, 3 μm, 4 μm, and 5 μm, and / or a second group consisting of 6 μm, 7 μm, 8 μm, and 9 μm. The range of the thickness H2 may be determined by a combination of any one of the values ​​included in the first group described above and any one of the values ​​included in the second group described above. The range of the thickness H2 may be determined by a combination of any two of the values ​​included in the first group described above. The range of thickness H2 may be defined by a combination of any two of the values ​​included in the second group described above.For example, it may be 2 μm or more and 9 μm or less, 2 μm or more and 8 μm or less, 2 μm or more and 7 μm or less, 2 μm or more and 6 μm or less, 2 μm or more and 5 μm or less, 2 μm or more and 4 μm or less, 2 μm or more and 3 μm or less, 3 μm or more and 9 μm or less, 3 μm or more and 8 μm or less, 3 μm or more and 7 μm or less, 3 μm or more and 6 μm or less, 3 μm or more and 5 μm or less, 3 μm or more and 4 μm or less, or 4 μm or more and 9 μm or less. Alternatively, it may be 4 μm or more and 8 μm or less, 4 μm or more and 7 μm or less, 4 μm or more and 6 μm or less, 4 μm or more and 5 μm or less, 5 μm or more and 9 μm or less, 5 μm or more and 8 μm or less, 5 μm or more and 7 μm or less, 5 μm or more and 6 μm or more and 9 μm or less, 6 μm or more and 8 μm or less, 6 μm or more and 7 μm or less, 7 μm or more and 9 μm or less, 7 μm or more and 8 μm or less, or 8 μm or more and 9 μm or less.

[0110] In one embodiment, the mask layer 20 may have a first metal layer 21 located on the first surface 20a side and a second metal layer 22 located on the second surface 20b side of the first metal layer 21. The first metal layer 21 may be a layer forming the first surface 20a. The first metal layer 21 is an example of a mask body layer and may be referred to as a metal body layer. The first metal layer 21 may be attached to and laminated on the second metal layer 22. The second metal layer 22 is an example of a mask intermediate layer and may be referred to as a metal intermediate layer. The second metal layer 22 is located between the first metal layer 21 and the mask substrate 15. The thickness H4 of the second metal layer 22 may be smaller than the thickness H3 of the first metal layer 21. The first metal layer 21 may be formed by a plating process as described later. The second metal layer 22 may be formed by a sputtering process as described later.

[0111] The second metal layer 22 may include a body region 22a located between the first metal layer 21 and the substrate frame 17, and an opening region 22b located within the substrate opening 16 in a plan view. In the example shown in Fig. 3, the second metal layer 22 is formed on the entire surface of the first metal layer 21 facing the mask substrate 15. Both the body region 22a and the opening region 22b may be composed of a body-side layer 25, a substrate-side layer 26, and an intermediate layer 27, which will be described later.

[0112] As shown in FIG. 3, in a plan view, at least a part of the outer edge 21c of the first metal layer 21 may be located at a position overlapping the outer edge 22c of the second metal layer 22. The outer edge 21c of the first metal layer 21 may be located at a position overlapping the outer edge 22c of the second metal layer 22 as a whole. The outer edge of the body-side layer 25, the outer edge of the substrate-side layer 26, and the outer edge of the intermediate layer 27 described below may overlap in a plan view to form the outer edge 22c of the second metal layer 22. In a plan view, at least a part of the outer edge 21c of the first metal layer 21 and at least a part of the outer edge 22c of the second metal layer 22 may be located at a position overlapping the outer edge 15c of the mask substrate 15 described above. The outer edge 21c of the first metal layer 21 and the outer edge 22c of the second metal layer 22 may be located at a position overlapping the outer edge 15c of the mask substrate 15 as a whole.

[0113] The second metal layer 22 may include a body-side layer 25 located on the first metal layer 21 side, and a substrate-side layer 26 located on the mask substrate 15 side of the body-side layer 25. The body-side layer 25 may be located on the first metal layer 21 side of the substrate-side layer 26. The body-side layer 25 may face the first metal layer 21. The substrate-side layer 26 may face the mask substrate 15. The surface of the substrate-side layer 26 facing the mask substrate 15 may constitute the second surface 20b described above. An intermediate layer 27 may be located between the body-side layer 25 and the substrate-side layer 26. The second metal layer 22 may have a three-layer structure.

[0114] The materials constituting the body-side layer 25, the substrate-side layer 26, and the intermediate layer 27 may be different from each other. The body-side layer 25, the substrate-side layer 26, and the intermediate layer 27 may be made of different metal materials. The body-side layer 25, the substrate-side layer 26, and the intermediate layer 27 may be configured as layers having specific purposes. The body-side layer 25 may be, for example, a layer capable of ensuring adhesion to the first metal layer 21. The substrate-side layer 26 may be, for example, a layer capable of ensuring adhesion to the mask substrate 15. The substrate-side layer 26 may also be a layer having resistance to an etching medium used in a substrate etching step described later. More specifically, the substrate-side layer 26 may be a layer capable of suppressing erosion by the etching medium. The intermediate layer 27 may be, for example, a layer capable of protecting the substrate-side layer 26 from a plating solution used in a first metal layer forming step. More specifically, when the body-side layer 25 is made of copper as described later and the thickness H5 (described later) of the body-side layer 25 is thin, the body-side layer 25 may be formed in a porous state. In this case, since the plating solution can reach the intermediate layer 27 through the body-side layer 25, the intermediate layer 27 may be resistant to the plating solution. For example, when the body-side layer 25 is made of copper and the board-side layer 26 is made of an aluminum alloy containing neodymium, the intermediate layer 27 may be a layer that can ensure adhesion between the body-side layer 25 and the board-side layer 26.

[0115] The thickness H3 of the first metal layer 21 may be, for example, 0.5 μm or more, 1.0 μm or more, 1.5 μm or more, or 2.0 μm or more. By setting the thickness H3 to 0.5 μm or more, mechanical strength can be ensured, deformation or breakage during handling can be suppressed, and defects such as pinholes can be suppressed. In addition, the thickness H3 may be, for example, 10.0 μm or less, 15.0 μm or less, 20.0 μm or less, or 25.0 μm or less. By setting the thickness H3 to 25.0 μm or less, the occurrence of shadows can be suppressed. The range of the thickness H3 may be determined by a first group consisting of 0.5 μm, 1.0 μm, 1.5 μm, and 2.0 μm, and / or a second group consisting of 10.0 μm, 15.0 μm, 20.0 μm, and 25.0 μm. The range of thickness H3 may be determined by a combination of any one of the values ​​included in the above-mentioned first group and any one of the values ​​included in the above-mentioned second group. The range of thickness H3 may be determined by a combination of any two of the values ​​included in the above-mentioned first group. The range of thickness H3 may be determined by a combination of any two of the values ​​included in the above-mentioned second group.For example, it may be 0.5 μm or more and 25.0 μm or less, 0.5 μm or more and 20.0 μm or less, 0.5 μm or more and 15.0 μm or less, 0.5 μm or more and 10.0 μm or less, 0.5 μm or more and 2.0 μm or less, 0.5 μm or more and 1.5 μm or less, 0.5 μm or more and 1.0 μm or less, 1.0 μm or more and 25.0 μm or less, 1.0 μm or more and 20.0 μm or less, 1.0 μm or more and 15.0 μm or less, 1.0 μm or more and 10.0 μm or less, 1.0 μm or more and 2.0 μm or less, 1.0 μm or more and 1.5 μm or less, 1.5 μm or more and 25.0 μm or less, It may be 1.5 μm or more and 15.0 μm or less, 1.5 μm or more and 10.0 μm or less, 1.5 μm or more and 2.0 μm or less, 2.0 μm or more and 25.0 μm or less, 2.0 μm or more and 20.0 μm or less, 2.0 μm or more and 15.0 μm or less, 2.0 μm or more and 10.0 μm or less, 10.0 μm or more and 25.0 μm or less, 10.0 μm or more and 20.0 μm or less, 10.0 μm or more and 15.0 μm or less, 15.0 μm or more and 25.0 μm or less, 15.0 μm or more and 20.0 μm or less, or 20.0 μm or more and 25.0 μm or less.

[0116] Alternatively, the thickness H3 of the first metal layer 21 may be, for example, 3.2 μm or more, 3.4 μm or more, 3.6 μm or more, or 3.8 μm or more. By setting the thickness H3 to 3.2 μm or more, the first metal layer 21 that can ensure mechanical strength and suppress deformation or damage during handling can be stably formed by a plating process described later. In addition, the thickness H3 may be, for example, 4.2 μm or less, 4.4 μm or less, 4.6 μm or less, or 4.8 μm or less. By setting the thickness H3 to 4.8 μm or less, the first metal layer 21 can be efficiently formed. The range of the thickness H3 may be determined by a first group consisting of 3.2 μm, 3.4 μm, 3.6 μm, and 3.8 μm, and / or a second group consisting of 4.2 μm, 4.4 μm, 4.6 μm, and 4.8 μm. The range of thickness H3 may be determined by a combination of any one of the values ​​included in the above-mentioned first group and any one of the values ​​included in the above-mentioned second group. The range of thickness H3 may be determined by a combination of any two of the values ​​included in the above-mentioned first group. The range of thickness H3 may be determined by a combination of any two of the values ​​included in the above-mentioned second group.For example, it may be 3.2 μm or more and 4.8 μm or less, 3.2 μm or more and 4.6 μm or less, 3.2 μm or more and 4.4 μm or less, 3.2 μm or more and 4.2 μm or less, 3.2 μm or more and 3.8 μm or less, 3.2 μm or more and 3.6 μm or less, 3.2 μm or more and 3.4 μm or less, 3.4 μm or more and 4.8 μm or less, 3.4 μm or more and 4.6 μm or less, 3.4 μm or more and 4.4 μm or less, 3.4 μm or more and 4.2 μm or less, 3.4 μm or more and 3.8 μm or less, 3.4 μm or more and 3.6 μm or less, or 3.6 μm or more and 4.8 μm or less. Alternatively, it may be 3.6 μm or more and 4.6 μm or less, 3.6 μm or more and 4.4 μm or less, 3.6 μm or more and 4.2 μm or less, 3.6 μm or more and 3.8 μm or less, 3.8 μm or more and 4.8 μm or less, 3.8 μm or more and 4.6 μm or less, 3.8 μm or more and 4.4 μm or less, 3.8 μm or more and 4.2 μm or less, 4.2 μm or more and 4.8 μm or less, 4.2 μm or more and 4.6 μm or less, 4.2 μm or more and 4.4 μm or less, 4.4 μm or more and 4.8 μm or less, 4.4 μm or more and 4.6 μm or less, or 4.6 μm or more and 4.8 μm or less.

[0117] The thickness H4 of the second metal layer 22 may be, for example, 100 nm or more, 200 nm or more, 300 nm or more, or 400 nm or more. By setting the thickness H4 to 100 nm or more, the second metal layer 22 can be stably formed by a sputtering process described later. In addition, the thickness H4 may be, for example, 800 nm or less, 1000 nm or less, 1200 nm or less, or 1500 nm or less. By setting the thickness H4 to 1500 nm or less, the second metal layer 22 can be efficiently formed. The range of the thickness H4 may be determined by a first group consisting of 100 nm, 200 nm, 300 nm, and 400 nm, and / or a second group consisting of 800 nm, 1000 nm, 1200 nm, and 1500 nm. The range of the thickness H4 may be determined by a combination of any one of the values ​​included in the first group described above and any one of the values ​​included in the second group described above. The range of thickness H4 may be determined by any combination of two values ​​included in the first group described above. The range of thickness H4 may be determined by any combination of two values ​​included in the second group described above.For example, it may be 100 nm or more and 1500 nm or less, 100 nm or more and 1200 nm or less, 100 nm or more and 1000 nm or less, 100 nm or more and 800 nm or less, 100 nm or more and 400 nm or less, 100 nm or more and 300 nm or less, 100 nm or more and 200 nm or less, 200 nm or more and 1500 nm or less, 200 nm or more and 1200 nm or less, 200 nm or more and 1000 nm or less, 200 nm or more and 800 nm or less, 200 nm or more and 400 nm or less, 200 nm or more and 300 nm or less, 300 nm or more and 1500 nm or less, 00nm or more and 1200nm or less, 300nm or more and 1000nm or less, 300nm or more and 800nm ​​or less, 300nm or more and 400nm or less, 400nm or more and 1500nm or less, 400nm or more and 1200nm or less, 400nm or more and 1000nm or less, 400nm or more and 800nm ​​or less, 800nm ​​or more and 1500nm or less, 800nm ​​or more and 1200nm or less, 800nm ​​or more and 1000nm or less, 1000nm or more and 1500nm or less, 1000nm or more and 1200nm or less, or 1200nm or more and 1500nm or less.

[0118] Alternatively, the thickness H4 of the second metal layer 22 may be, for example, 100 nm or more, 200 nm or more, 300 nm or more, or 400 nm or more. By setting the thickness H4 to 100 nm or more, the second metal layer 22 can be stably formed by a sputtering process described later. In addition, the thickness H4 may be, for example, 500 nm or less, 600 nm or less, 700 nm or less, or 800 nm or less. By setting the thickness H4 to 800 nm or less, the second metal layer 22 can be formed more efficiently. The range of the thickness H4 may be determined by a first group consisting of 100 nm, 200 nm, 300 nm, and 400 nm, and / or a second group consisting of 500 nm, 600 nm, 700 nm, and 800 nm. The range of the thickness H4 may be determined by a combination of any one of the values ​​included in the first group described above and any one of the values ​​included in the second group described above. The range of thickness H4 may be determined by any combination of two values ​​included in the first group described above. The range of thickness H4 may be determined by any combination of two values ​​included in the second group described above.For example, it may be 100 nm or more and 800 nm or less, 100 nm or more and 700 nm or less, 100 nm or more and 600 nm or less, 100 nm or more and 500 nm or less, 100 nm or more and 400 nm or less, 100 nm or more and 300 nm or less, 100 nm or more and 200 nm or less, 200 nm or more and 800 nm or less, 200 nm or more and 700 nm or less, 200 nm or more and 600 nm or less, 200 nm or more and 500 nm or less, 200 nm or more and 400 nm or less, 200 nm or more and 300 nm or more and 300 nm or more and 800 nm or less. Alternatively, it may be 300 nm or more and 700 nm or less, 300 nm or more and 600 nm or less, 300 nm or more and 500 nm or less, 300 nm or more and 400 nm or less, 400 nm or more and 800 nm or less, 400 nm or more and 700 nm or less, 400 nm or more and 600 nm or less, 400 nm or more and 500 nm or less, 500 nm or more and 800 nm or less, 500 nm or more and 700 nm or less, 500 nm or more and 600 nm or less, 600 nm or more and 800 nm or less, 600 nm or more and 700 nm or less, or 700 nm or more and 800 nm or less.

[0119] The thickness H5 of the body side layer 25 may be, for example, 180 nm or more, 185 nm or more, 190 nm or more, or 195 nm or more. By setting the thickness H5 to 180 nm or more, the body side layer 25 can be stably formed by the sputtering process described later. Furthermore, the thickness H5 may be, for example, 800 nm or less, 1000 nm or less, 1200 nm or less, or 1500 nm or less. By setting the thickness H5 to 1500 nm or less, the body side layer 25 can be efficiently formed by the sputtering process described later. The range of the thickness H5 may be determined by a first group consisting of 180 nm, 185 nm, 190 nm, and 195 nm, and / or a second group consisting of 800 nm, 1000 nm, 1200 nm, and 1500 nm. The range of thickness H5 may be determined by a combination of any one of the values ​​included in the first group described above and any one of the values ​​included in the second group described above. The range of thickness H5 may be determined by a combination of any two of the values ​​included in the first group described above. The range of thickness H5 may be determined by a combination of any two of the values ​​included in the second group described above.For example, it may be 180 nm or more and 1500 nm or less, 180 nm or more and 1200 nm or less, 180 nm or more and 1000 nm or less, 180 nm or more and 800 nm or less, 180 nm or more and 195 nm or less, 180 nm or more and 190 nm or less, 180 nm or more and 185 nm or less, 185 nm or more and 1500 nm or less, 185 nm or more and 1200 nm or less, 185 nm or more and 1000 nm or less, 185 nm or more and 800 nm or less, 185 nm or more and 195 nm or less, 185 nm or more and 190 nm or less, 190 nm or more and 1500 nm or less, It may be 90 nm or more and 1200 nm or less, 190 nm or more and 1000 nm or less, 190 nm or more and 800 nm or less, 190 nm or more and 195 nm or less, 195 nm or more and 1500 nm or less, 195 nm or more and 1200 nm or less, 195 nm or more and 1000 nm or less, 195 nm or more and 800 nm or less, 800 nm or more and 1500 nm or less, 800 nm or more and 1200 nm or less, 800 nm or more and 1000 nm or less, 1000 nm or more and 1500 nm or less, 1000 nm or more and 1200 nm or less, or 1200 nm or more and 1500 nm or less.

[0120] Alternatively, the thickness H5 of the body-side layer 25 may be, for example, 180 nm or more, 185 nm or more, 190 nm or more, or 195 nm or more. By setting the thickness H5 to 180 nm or more, the body-side layer 25 can be stably formed by the sputtering process described later. Furthermore, the thickness H5 may be, for example, 205 nm or less, 210 nm or less, 215 nm or less, or 220 nm or less. By setting the thickness H5 to 220 nm or less, the body-side layer 25 can be formed more efficiently by the sputtering process described later. The range of the thickness H5 may be determined by a first group consisting of 180 nm, 185 nm, 190 nm, and 195 nm, and / or a second group consisting of 205 nm, 210 nm, 215 nm, and 220 nm. The range of the thickness H5 may be determined by a combination of any one of the values ​​included in the first group described above and any one of the values ​​included in the second group described above. The range of thickness H5 may be determined by any combination of two values ​​included in the first group described above. The range of thickness H5 may be determined by any combination of two values ​​included in the second group described above.For example, it may be 180 nm or more and 220 nm or less, 180 nm or more and 215 nm or less, 180 nm or more and 210 nm or less, 180 nm or more and 205 nm or less, 180 nm or more and 195 nm or less, 180 nm or more and 190 nm or less, 180 nm or more and 185 nm or less, 185 nm or more and 220 nm or less, 185 nm or more and 215 nm or less, 185 nm or more and 210 nm or less, 185 nm or more and 205 nm or less, 185 nm or more and 195 nm or less, 185 nm or more and 190 nm or less, or 190 nm or more and 220 nm or less. Alternatively, it may be 190 nm or more and 215 nm or less, or 190 nm or more and 210 nm or less, or 190 nm or more and 205 nm or less, or 190 nm or more and 195 nm or less, or 195 nm or more and 220 nm or less, or 195 nm or more and 215 nm or less, or 195 nm or more and 210 nm or less, or 195 nm or more and 205 nm or less, or 205 nm or more and 220 nm or less, or 205 nm or more and 215 nm or less, or 205 nm or more and 210 nm or less, or 210 nm or more and 220 nm or less, or 210 nm or more and 215 nm or less.

[0121] The thickness H6 of the substrate-side layer 26 may be, for example, 90 nm or more, 92 nm or more, 94 nm or more, or 96 nm or more. By setting the thickness H6 to 90 nm or more, the substrate-side layer 26 can be stably formed by the sputtering process described later. Also, the thickness H6 may be, for example, 104 nm or less, 106 nm or less, 108 nm or less, or 110 nm or less. By setting the thickness H6 to 110 nm or less, the substrate-side layer 26 can be efficiently formed. The range of the thickness H6 may be determined by a first group consisting of 90 nm, 92 nm, 94 nm, and 96 nm, and / or a second group consisting of 104 nm, 106 nm, 108 nm, and 110 nm. The range of the thickness H6 may be determined by a combination of any one of the values ​​included in the first group described above and any one of the values ​​included in the second group described above. The range of thickness H6 may be determined by any combination of two values ​​included in the first group described above. The range of thickness H6 may be determined by any combination of two values ​​included in the second group described above.For example, it may be 90 nm or more and 110 nm or less, 90 nm or more and 108 nm or less, 90 nm or more and 106 nm or less, 90 nm or more and 104 nm or less, 90 nm or more and 96 nm or less, 90 nm or more and 94 nm or less, 90 nm or more and 92 nm or less, 92 nm or more and 110 nm or less, 92 nm or more and 108 nm or less, 92 nm or more and 106 nm or less, 92 nm or more and 104 nm or less, 92 nm or more and 96 nm or less, 92 nm or more and 94 nm or less, 94 nm or more and 110 nm or less, 94 nm or more and 95 nm or less, 95 nm or more and 110 ... m may be 94 nm or more and 106 nm or less, may be 94 nm or more and 104 nm or less, may be 94 nm or more and 96 nm or less, may be 96 nm or more and 110 nm or less, may be 96 nm or more and 108 nm or less, may be 96 nm or more and 106 nm or less, may be 96 nm or more and 104 nm or less, may be 104 nm or more and 110 nm or less, may be 104 nm or more and 108 nm or less, may be 104 nm or more and 106 nm or less, may be 106 nm or more and 110 nm or less, may be 106 nm or more and 108 nm or less, may be 108 nm or more and 110 nm or less.

[0122] The thickness H7 of the intermediate layer 27 may be, for example, 45 nm or more, 50 nm or more, 55 nm or more, or 65 nm or more. By setting the thickness H7 to 45 nm or more, the intermediate layer 27 can be stably formed by the sputtering process described later. In addition, the thickness H7 may be, for example, 80 nm or less, 90 nm or less, 100 nm or less, or 110 nm or less. By setting the thickness H7 to 110 nm or less, the intermediate layer 27 can be efficiently formed. The range of the thickness H7 may be determined by a first group consisting of 45 nm, 50 nm, 55 nm, and 65 nm, and / or a second group consisting of 80 nm, 90 nm, 100 nm, and 110 nm. The range of the thickness H7 may be determined by a combination of any one of the values ​​included in the first group described above and any one of the values ​​included in the second group described above. The range of the thickness H7 may be determined by a combination of any two of the values ​​included in the first group described above. The range of thickness H7 may be defined by a combination of any two of the values ​​included in the second group mentioned above.For example, it may be 45 nm or more and 110 nm or less, 45 nm or more and 100 nm or less, 45 nm or more and 90 nm or less, 45 nm or more and 80 nm or less, 45 nm or more and 65 nm or less, 45 nm or more and 55 nm or less, 45 nm or more and 50 nm or less, 50 nm or more and 110 nm or less, 50 nm or more and 100 nm or less, 50 nm or more and 90 nm or less, 50 nm or more and 80 nm or less, 50 nm or more and 65 nm or less, 50 nm or more and 55 nm or less, or 55 nm or more and 110 nm or less, It may be 55nm or more and 100nm or less, may be 55nm or more and 90nm or less, may be 55nm or more and 80nm or less, may be 55nm or more and 65nm or less, may be 65nm or more and 110nm or less, may be 65nm or more and 100nm or less, may be 65nm or more and 90nm or less, may be 65nm or more and 80nm or less, may be 80nm or more and 110nm or less, may be 80nm or more and 100nm or less, may be 80nm or more and 90nm or less, may be 90nm or more and 110nm or less, may be 90nm or more and 100nm or less, may be 100nm or more and 110nm or less.

[0123] Alternatively, the thickness H7 of the intermediate layer 27 may be, for example, 45 nm or more, 46 nm or more, 47 nm or more, or 48 nm or more. By setting the thickness H7 to 45 nm or more, the intermediate layer 27 can be stably formed by the sputtering process described later. Furthermore, the thickness H7 may be, for example, 52 nm or less, 53 nm or less, 54 nm or less, or 55 nm or less. By setting the thickness H7 to 55 nm or less, the intermediate layer 27 can be efficiently formed. The range of the thickness H7 may be determined by a first group consisting of 45 nm, 46 nm, 47 nm, and 48 nm, and / or a second group consisting of 52 nm, 53 nm, 54 nm, and 55 nm. The range of the thickness H7 may be determined by a combination of any one of the values ​​included in the first group described above and any one of the values ​​included in the second group described above. The range of the thickness H7 may be determined by a combination of any two of the values ​​included in the first group described above. The range of thickness H7 may be defined by a combination of any two of the values ​​included in the second group mentioned above.For example, it may be 45 nm or more and 55 nm or less, 45 nm or more and 54 nm or less, 45 nm or more and 53 nm or less, 45 nm or more and 52 nm or less, 45 nm or more and 48 nm or less, 45 nm or more and 47 nm or less, 45 nm or more and 46 nm or less, 46 nm or more and 55 nm or less, 46 nm or more and 54 nm or less, 46 nm or more and 53 nm or less, 46 nm or more and 52 nm or less, 46 nm or more and 48 nm or less, 46 nm or more and 47 nm or less, or 47 nm or more and 55 nm or less. Alternatively, it may be 47 nm or more and 54 nm or less, 47 nm or more and 53 nm or less, 47 nm or more and 52 nm or less, 47 nm or more and 48 nm or less, 48 ​​nm or more and 55 nm or less, 48 ​​nm or more and 54 nm or less, 48 ​​nm or more and 53 nm or less, 48 ​​nm or more and 52 nm or less, 52 nm or more and 55 nm or less, 52 nm or more and 54 nm or less, 52 nm or more and 53 nm or less, 53 nm or more and 55 nm or less, 53 nm or more and 54 nm or less, or 54 nm or more and 55 nm or less.

[0124] The first metal layer 21 may include a metal material. The metal material may be a magnetic metal material. For example, an iron alloy containing nickel may be used as a material constituting the first metal layer 21. The iron alloy may further contain cobalt in addition to nickel. For example, an iron alloy containing nickel and cobalt in total of 30% by mass or more and 54% by mass or less and a cobalt content of 0% by mass or more and 6% by mass or less may be used as a material for the first metal layer 21. For the iron alloy containing nickel, an Invar material containing 34% by mass or more and 38% by mass or less of nickel, or a low thermal expansion Fe-Ni-based plating alloy containing 38% by mass or more and 54% by mass or less of nickel may be used. For the iron alloy containing nickel and cobalt, a Super Invar material containing 30% by mass or more and 34% by mass or less of nickel and further containing cobalt may be used. By using such an iron alloy, the thermal expansion coefficient of the first metal layer 21 can be reduced. For example, when a glass substrate is used as the deposition substrate 110, the thermal expansion coefficient of the mask layer 20 can be adjusted to a value equal to or close to that of the glass substrate, thereby making it possible to suppress deterioration in accuracy.

[0125] As the material constituting the first metal layer 21, instead of the above-mentioned iron alloy containing nickel, for example, nickel or a nickel alloy containing cobalt may be used. When a nickel alloy containing cobalt is used, a nickel alloy containing 8 mass % or more and 10 mass % or less of cobalt may be used as the material of the first metal layer 21. When such nickel or nickel alloy is used, it is possible to suppress decomposition of the plating solution used in the first metal layer forming step described below, and the stability of the plating solution can be improved.

[0126] The material constituting the body side layer 25 is not particularly limited as long as it can ensure adhesion with the first metal layer 21. The material constituting the body side layer 25 may be a material that can function as a seed layer when the first metal layer 21 is formed by electrolytic plating or electroless plating. When electrolytic plating is performed, the material constituting the body side layer 25 may be a material with low electrical resistance or a material that is resistant to plating solution. For example, when electrolytic plating is performed, the body side layer 25 may contain titanium (Ti), copper (Cu), nickel (Ni) or gold (Au). When electroless plating is performed, the material constituting the body side layer 25 may be a material that has catalyst adsorption ability or a material that is resistant to plating solution. For example, when electroless plating is performed, the body side layer 25 may contain silicon oxide (SiO), silicon dioxide (SiO2), siloxane (SiOR2), zinc (Zn), titanium (Ti), copper (Cu) or nickel (Ni).

[0127] The material constituting the substrate-side layer 26 is not particularly limited as long as it can secure adhesion to the mask substrate 15 and can suppress erosion by an etching medium used in the substrate etching process described later. For example, the substrate-side layer 26 may contain gold (Au), aluminum (Al), chromium (Cr), nickel (Ni), titanium (Ti), titanium nitride (TiN), aluminum alloy containing neodymium (Al-Nd), silicon oxide (SiO) or silicon dioxide (SiO2). When the substrate-side layer 26 is made of an aluminum alloy containing neodymium, an aluminum alloy containing neodymium in an amount of 0.5 atomic % or more and 2 atomic % or less may be used. Here, the atomic % is obtained by performing a compositional analysis of the substrate-side layer 26 using the XPS method. The XPS method is a method for obtaining information on the types and amounts of constituent elements in a region within a range of several nm from the surface of a sample by irradiating the sample with X-rays and measuring the energy distribution of photoelectrons emitted from the sample. In this case, the abundance of each constituent element is proportional to the peak area value calculated by integrating the area of ​​the peak corresponding to each constituent element in the spectrum measured by X-ray photoelectron spectroscopy. Therefore, first, the peak area value corresponding to each constituent element is calculated. Next, the total value of the peak area values ​​of each constituent element is calculated, and then the peak area value of the target constituent element is divided by the total value and multiplied by 100 to calculate the atomic % of the target constituent element. The relationship between the abundance of the constituent element and the peak area value may differ for each constituent element depending on the sensitivity to X-rays, etc. In this case, the peak area value of each constituent element may be multiplied by a relative sensitivity coefficient for correcting the difference in sensitivity to calculate a corrected peak area value, and then the above-mentioned total value and atomic % may be calculated.

[0128] The material constituting the intermediate layer 27 is not particularly limited as long as it is a material that can ensure adhesion between the main body side layer 25 and the substrate side layer 26 and can protect the substrate side layer 26 from the plating solution used in the first metal layer formation process. The material constituting the intermediate layer 27 may be a material that has a thermal expansion coefficient between the thermal expansion coefficient of the main body side layer 25 and the thermal expansion coefficient of the substrate side layer 26. The material constituting the intermediate layer 27 may be a material that has a surface free energy between the surface free energy of the main body side layer 25 and the surface free energy of the substrate side layer 26. For example, the intermediate layer 27 may contain titanium (Ti), titanium nitride (TiN), aluminum (Al), aluminum alloy containing neodymium (Al-Nd), silicon oxide (SiO), silicon dioxide (SiO2), nickel (Ni), copper (Cu), chromium (Cr), or gold (Au).

[0129] The mask layer 20 may have a through hole 40. The mask layer 20 may have two or more through holes 40. The through hole 40 may penetrate the mask layer 20. In this embodiment, the through hole 40 extends from the first surface 20a to the second surface 20b and penetrates the mask layer 20. In this case, the through hole 40 may penetrate the first metal layer 21 and the second metal layer 22.

[0130] The opening dimension of the through hole 40 in a predetermined direction (for example, a first direction D11 or a second direction D12 described later) in the second surface 20b may be larger than the opening dimension of the through hole 40 in the predetermined direction in the first surface 20a. In one embodiment, the cross-sectional opening of the through hole 40 in a direction parallel to the first surface 20a may gradually increase from the first surface 20a to the second surface 20b. In other words, the cross-sectional area of ​​each through hole 40 in a cross section parallel to the first surface 20a at each position along the normal direction of the mask layer 20 may gradually increase from the first surface 20a to the second surface 20b. In this case, the through hole 40 may have a wall surface 41 formed so as to move away from the central axis CL of the through hole 40 from the first surface 20a to the second surface 20b. FIG. 3 shows an example in which the wall surface 41 of the through-hole 40 is inclined linearly with respect to the central axis CL so as to move away from the central axis CL from the first surface 20a to the second surface 20b.

[0131] As shown in FIG. 2 and FIG. 4, the through holes 40 may form two or more through hole groups 30. Each through hole group 30 is located in the substrate opening 16 of the mask substrate 15 in a plan view. That is, the through hole group 30 (or the effective area 23 described later) may be located in the substrate opening 16, or multiple through hole groups 30 (or multiple effective areas 23) may be located. Furthermore, all the through hole groups 30 may be located in one substrate opening 16. As shown in FIG. 4, each through hole group 30 may be configured such that two or more through holes 40 form a group. The through hole group 30 is used as a term meaning a collection of multiple through holes 40 arranged regularly. The through hole 40 on the outer edge of one through hole group 30 is the through hole 40 located at the outermost position among the multiple through holes 40 arranged regularly in the same manner. Outside the through hole 40 located at the outermost position in one through hole group 30, there may not be any through hole 40 that is similarly regularly arranged and intended to pass the deposition material 82.

[0132] As shown in FIG. 2 and FIG. 4, mask bars 28a and 28b may be provided between adjacent through-hole groups 30. The mask bars 28a and 28b may not have through-holes 40 intended for the passage of the deposition material 82. The mask bars 28a and 28b may include a first mask bar 28a and a second mask bar 28b extending in directions perpendicular to each other. The first mask bar 28a may extend in the second direction D12, and the second mask bar 28b may extend in the first direction D11. A plurality of first mask bars 28a may be arranged in the first direction D11. A plurality of second mask bars 28b may be arranged in the second direction D12. The first mask bar 28a and the second mask bar 28b intersect at an intersection 29. The mask bars 28a and 28b may have through-holes or recesses (neither of which are shown) for other purposes arranged therein. These through holes and recesses for other uses may be arranged without the regularity of the arrangement of the through holes 40, and may not be considered to belong to the through hole group 30. The mask bars 28a, 28b may form part of the peripheral region 24 described later.

[0133] As shown in FIG. 4, the through hole groups 30 may be arranged at a predetermined interval (at a predetermined pitch). The through hole groups 30 may be arranged at a predetermined interval in the first direction D11 and at a predetermined interval in the second direction D12. The through hole groups 30 may be arranged in the first direction D11 via the first mask bars 28a, and arranged in the second direction D12 via the second mask bars 28b. The arrangement pitch of the through hole groups 30 may be different in the first direction D11 and the second direction D12, or may be equal. FIG. 4 shows an example in which the arrangement pitch in the first direction D11 and the arrangement pitch in the second direction D12 are equal. As shown in FIG. 4, the through hole groups 30 may be arranged in parallel. That is, the through hole groups 30 constituting one row along the first direction D11 and the through hole groups 30 constituting another row adjacent to the row in the second direction D12 may be aligned in the second direction D12.

[0134] In FIG. 4, the distance between adjacent through-hole groups 30 in the first direction D11 is indicated by C1. The distance C1 corresponds to the width of the first mask rail 28a. The distance between adjacent through-hole groups 30 in the second direction D12 is indicated by C2. The distance C2 corresponds to the width of the second mask rail 28b. Although the distance C1 and the distance C2 may be different, the example shown in FIG. 4 shows an example in which the distance C1 and the distance C2 are equal. The distances C1 and C2 may be set according to the width of a dicing saw used to cut the deposition substrate 110 (see FIG. 15A) on which a plurality of organic devices 100 including organic layers 130A, 130B, 130C, etc. are deposited into individual organic devices 100. The deposition substrate 110 may be cut by single sawing, which divides the deposition substrate 110 into areas between adjacent organic devices 100 in a single cut. Single sawing can efficiently divide the deposition substrate 110 in that the deposition substrate 110 can be divided by one cutting. Single sawing may be applied when the distances C1 and C2 are relatively small. When single sawing is applied, the distances C1 and C2 may be set to be equal or close to the width of the dicing saw. Instead of single sawing, the deposition substrate 110 may be cut by double sawing, in which the deposition substrate 110 is divided by cutting twice in the region between the adjacent organic devices 100. For example, two cuts are performed, one at a position along the edge of one organic device 100 and the other at a position along the edge of the other organic device 100. Such double sawing may be applied when the distances C1 and C2 are relatively large or the width of the dicing saw is relatively small. When double sawing is applied, the cutting time of the deposition substrate 110 can be shortened by applying double sawing with a small width.

[0135] The distances C1 and C2 may be, for example, 30 μm or more, 50 μm or more, 100 μm or more, or 150 μm or more. By setting the distances C1 and C2 to 30 μm or more, a cutting width for cutting the deposition substrate 110 by single sawing using a dicing saw can be secured, and the strength of the deposition mask 10 can be improved. Moreover, the distances C1 and C2 may be, for example, 240 μm or less, 260 μm or less, 280 μm or less, or 300 μm or less. By setting the distances C1 and C2 to 300 μm or less, the surface attachment efficiency to the deposition substrate 110 can be improved. The ranges of the distances C1 and C2 may be determined by a first group consisting of 30 μm, 50 μm, 100 μm, and 150 μm, and / or a second group consisting of 240 μm, 260 μm, 280 μm, and 300 μm. The ranges of the distances C1 and C2 may be determined by a combination of any one of the values ​​included in the first group and any one of the values ​​included in the second group. The ranges of the distances C1 and C2 may be determined by a combination of any two of the values ​​included in the first group. The ranges of the distances C1 and C2 may be determined by a combination of any two of the values ​​included in the second group.For example, it may be 30 μm or more and 300 μm or less, 30 μm or more and 280 μm or less, 30 μm or more and 260 μm or less, 30 μm or more and 240 μm or less, 30 μm or more and 150 μm or less, 30 μm or more and 100 μm or less, 30 μm or more and 50 μm or less, 50 μm or more and 300 μm or less, 50 μm or more and 280 μm or less, 50 μm or more and 260 μm or less, 50 μm or more and 240 μm or less, 50 μm or more and 150 μm or less, 50 μm or more and 100 μm or less, 100 μm or more and 300 μm or less, 100 μm or more and 100 μm or more and 280 μm or less, or may be 100 μm or more and 260 μm or less, or may be 100 μm or more and 240 μm or less, or may be 100 μm or more and 150 μm or less, or may be 150 μm or more and 300 μm or less, or may be 150 μm or more and 280 μm or less, or may be 150 μm or more and 260 μm or less, or may be 150 μm or more and 240 μm or less, or may be 240 μm or more and 300 μm or less, or may be 240 μm or more and 280 μm or less, or may be 240 μm or more and 260 μm or less, or may be 260 μm or more and 300 μm or less, or may be 260 μm or more and 280 μm or less, or may be 280 μm or more and 300 μm or less.

[0136] As shown in FIG. 4 and FIG. 5A, in one through-hole group 30, the multiple through holes 40 may be arranged at a predetermined interval or at a predetermined pitch. The through holes 40 may be arranged at a predetermined pitch (reference symbol C3 shown in FIG. 5A) in the first direction D11 and at a predetermined pitch (reference symbol C4 shown in FIG. 5A) in the second direction D12. The arrangement pitches C3 and C4 of the through holes 40 may be different in the first direction D11 and the second direction D12, or may be equal. FIG. 5A shows an example in which the arrangement pitch C3 in the first direction D11 and the arrangement pitch C4 in the second direction D12 are equal. As shown in FIG. 5A, the through holes 40 may be arranged in parallel. That is, each through hole 40 constituting one row along the first direction D11 and each through hole 40 constituting another row adjacent to the row in the second direction D12 may be aligned in the second direction D12. The arrangement pitches C3 and C4 of the through holes 40 may be determined according to the pixel density of the display device or the projection device, for example, as follows. - If the pixel density is 600ppi or more: pitch is 42.3μm or less - If the pixel density is 1200ppi or more: pitch is 21.2μm or less - If the pixel density is 3000ppi or more: pitch is 8.5μm or less - If the pixel density is 5000ppi or more: pitch is 5.1μm or less A display device or projection device with a pixel density of 600 ppi may be used to display images or videos at a distance of about 15 cm from the eyeball, and may be used, for example, in a smartphone. A display device or projection device with a pixel density of 1200 ppi may be used to display images or videos at a distance of about 8 cm from the eyeball, and may be used, for example, to display or project images or videos for expressing virtual reality (so-called VR). A display device or projection device with a pixel density of 3000 ppi may be used to display images or videos at a distance of about 3 cm from the eyeball, and may be used, for example, to display or project images or videos for expressing augmented reality (so-called AR). A display device or projection device with a pixel density of 5000 ppi may be used to display images or videos at a distance of about 2 cm from the eyeball, and may be used, for example, to display or project images or videos for expressing augmented reality.

[0137] The through holes 40 in one through hole group 30 may be arranged in a staggered manner as shown in FIG. 5B, instead of being arranged in parallel. That is, each through hole 40 constituting one row along the first direction D11 and each through hole 40 constituting another row adjacent to the row in the second direction D12 may not be aligned in the second direction D12. In the example shown in FIG. 5B, each through hole 40 constituting one row and each through hole 40 constituting the other adjacent row are arranged with a shift in the first direction D11, and the shift amount is half the arrangement pitch C3 in the first direction. However, the present disclosure is not limited to this, and the shift amount is not limited to half the arrangement pitch C3. In addition, FIG. 5B shows an example in which two rows of through holes 40 adjacent to each other in the second direction D12 are arranged with a shift in the first direction D11, but two rows of through holes 40 adjacent to each other in the first direction D11 may be arranged with a shift in the second direction D12.

[0138] As shown in FIG. 5A, the through-hole 40 may have a substantially rectangular contour in a plan view. In this case, the four corners of the contour of the through-hole 40 may be curved. The shape of the contour may be arbitrarily determined according to the shape of the pixel. For example, the contour may have another polygonal shape such as a hexagon or an octagon, or may have a circular shape. The contour shape may be a combination of a plurality of shapes. The through-holes 40 may have contour shapes different from each other. The opening dimension of the through-hole 40 in the first direction D11 may be a dimension between two intersections where a straight line (corresponding to a first intermediate line ML1 described later in FIG. 5A) extending in the first direction D11 through the center point O of the opening intersects with the contour of the opening. The opening dimension of the through-hole 40 in the second direction D12 may be a dimension between two intersections where a straight line (corresponding to a second intermediate line ML2 described later in FIG. 5A) extending in the second direction D12 through the center point O of the opening intersects with the contour of the opening. The center point O of the opening of the through hole 40 in the first surface 20a and the second surface 20b may be an intersection point of the first intermediate line ML1 and the second intermediate line ML2. The first intermediate line ML1 may be a line that extends in the first direction D11 and is equidistant from two lines that circumscribe the contour of the opening. The second intermediate line ML2 may be a line that extends in the second direction D12 and is equidistant from two lines that circumscribe the contour of the opening. When the through hole 40 has a polygonal contour having an even number of vertices, the opening dimension of the through hole 40 may be the distance between a pair of opposing sides of the polygon, as shown in FIG. 5A.

[0139] In FIG. 5A, the opening dimension of the through hole 40 on the first surface 20a of the mask layer 20 is indicated by the symbol S1. The opening dimension of the through hole 40 on the second surface 20b of the mask layer 20 is indicated by the symbol S2. The opening dimension S2 is larger than the opening dimension S1. In FIG. 5A, the planar shape of the through hole 40 is a square, so that the opening dimension of the through hole 40 in the first direction D11 and the opening dimension of the through hole 40 in the second direction D12 are equal. Representatively, the dimensions of the through hole 40 in the second direction D12 are indicated by the symbols S1 and S2. The symbol S3 indicates the distance between the adjacent through holes 40 on the first surface 20a.

[0140] The dimensions S1, S2, and S3 may be determined according to the pixel density of the display device or the projection device, for example, as shown in Table 1 below. [Table 1]

[0141] As shown in FIG. 3, the wall surface 41 of the through hole 40 described above may be inclined with respect to the first surface 20a of the mask layer 20 at an angle θ1.

[0142] The angle θ1 may be, for example, 60° or more, 65° or more, 70° or more, or 75° or more. By setting the angle θ1 to 60° or more, the arrangement pitches C3 and C4 of the through holes 40 can be reduced, as described later. The angle θ1 may be, for example, 80° or less, 83° or less, 85° or less, or 90° or less. By setting the angle θ1 to 90° or less, the occurrence of a shadow can be suppressed. The range of the angle θ1 may be determined by a first group consisting of 60°, 65°, 70°, and 75°, and / or a second group consisting of 80°, 83°, 85°, and 90°. The range of the angle θ1 may be determined by a combination of any one of the values ​​included in the first group described above and any one of the values ​​included in the second group described above. The range of the angle θ1 may be determined by a combination of any two of the values ​​included in the first group described above. The range of the angle θ1 may be determined by a combination of any two of the values ​​included in the second group described above. For example, the range may be 60° or more and 90° or less, 60° or more and 85° or less, 60° or more and 83° or less, 60° or more and 80° or less, 60° or more and 75° or less, 60° or more and 70° or less, 60° or more and 65° or less, 65° or more and 90° or less, 65° or more and 85° or less, 65° or more and 83° or less, 65° or more and 80° or less, 65° or more and 75° or less, 65° or more and 70° or less, or 70° or more and 90° or less. Alternatively, the angle may be 70° or more and 85° or less, 70° or more and 83° or less, 70° or more and 80° or less, 70° or more and 75° or less, 75° or more and 90° or less, 75° or more and 85° or less, 75° or more and 83° or less, 75° or more and 80° or less, 80° or more and 90° or less, 80° or more and 85° or less, 80° or more and 83° or less, 83° or more and 90° or less, 83° or more and 85° or less, or 85° or more and 90° or less.

[0143] The technical meaning of the angle θ1 will be described below. The directional components of the deposition material 82 flying in the deposition process in which the deposition material 82 is deposited on the deposition substrate 110 using the deposition mask 10 will be described. Depending on the configuration of the crucible 81 shown in FIG. 1, the deposition material 82 may include a component flying along a direction inclined with respect to the thickness direction D2 of the deposition mask 10 in addition to a component flying from the deposition source (crucible 81) toward the deposition substrate 110 along the thickness direction D2 of the deposition mask 10. In this case, a part of the deposition material 82 flying along the inclined direction adheres to the second surface 20b of the mask layer 20 or the wall surface 41 of the through hole 40 before reaching the deposition substrate 110. For this reason, the thickness of the deposition layer (or organic layers 130A, 130B, and 130C described later) formed on the deposition substrate 110 tends to be thinner as it approaches the wall surface 41 of the through hole 40. Such a phenomenon in which the deposition material 82 is prevented from adhering to the deposition substrate 110 by the wall surface 41 of the through-hole 40 is also called a shadow. Possible measures to suppress the occurrence of the shadow include reducing the angle θ1 and reducing the thickness H2 of the mask layer 20.

[0144] Reducing the angle θ1 means that the opening of the through holes 40 on the second surface 20b becomes larger. In this case, the wall surfaces 41 of the through holes 40 adjacent to each other on the second surface 20b are connected, and the second surface 20b does not exist between these through holes 40. That is, the material between the through holes 40 adjacent to each other on the second surface 20b is removed by the laser light irradiation during the through hole forming process described later. Therefore, the angle θ1 does not need to be too small. In this case, the arrangement pitches C3 and C4 of the through holes 40 can be reduced while ensuring the mechanical strength of the mask layer 20.

[0145] To prevent the angle θ1 from being too small, the thickness H2 of the mask layer 20 may be reduced. This can prevent the occurrence of shadows. However, simply reducing the thickness H2 means a decrease in the mechanical strength of the mask layer 20. For this reason, the thickness H2 does not need to be made too small. In this case, the mechanical strength of the mask layer 20 can be ensured.

[0146] Therefore, in this embodiment, the angle θ1 is relatively large, for example, 60° or more. This angle θ1 is larger than that of a conventional deposition mask, for example, 50° or less. Therefore, the wall surface 41 of the through hole 40 can be formed in a shape nearly perpendicular to the first surface 20a and the second surface 20b of the mask layer 20, and the material of the mask layer 20 can remain around the through hole 40. Therefore, the mechanical strength of the mask layer 20 can be improved. In addition, by making the angle θ1 large, the arrangement pitches C3 and C4 of the through holes 40 can be made small.

[0147] Thus, the angle θ1 of the deposition mask 10 according to the present embodiment is 60° or more and 90° or less. Therefore, the deposition mask 10 according to the present embodiment may be used in a deposition apparatus 80 including a crucible 81 having a deposition angle of 90° or close to 90° (for example, 60° or more and 90° or less), or may be used in a surface deposition type deposition apparatus (not shown). In a deposition apparatus 80 including a crucible 81 as shown in FIG. 1, the deposition material 82 may contain a component that flies along a direction inclined with respect to the thickness direction D2. In contrast, in a surface deposition type deposition apparatus, a deposition source disposed below the deposition substrate 110 has a planar spread so as to face the deposition mask 10. This allows the deposition material 82 to fly to the deposition substrate 110 along the thickness direction D2. Therefore, the deposition material 82 can fly evenly in each of the first direction D11 and the second direction D12. The deposition angle is 90° or close to 90°.

[0148] Incidentally, one through-hole group 30 may be referred to as one effective area 23. The area located around the effective area 23 may be referred to as a surrounding area 24. In this case, the surrounding area 24 surrounds a plurality of effective areas 23.

[0149] When a display device such as an organic device 100 (described later) is produced using the deposition mask 10, one effective area 23 corresponds to the display area of ​​one organic device 100. Therefore, by using the deposition mask 10 shown in FIG. 2, a plurality of organic devices 100 can be deposited on a single deposition substrate 110. This type of deposition is also called multi-surface deposition. One effective area 23 may correspond to the display areas of a plurality of organic devices 100.

[0150] The effective area 23 may have a substantially rectangular outline in plan view, as shown in FIG. 4, for example. The outline of the effective area 23 may be defined by a line tangent to the outermost through-hole 40 of the corresponding through-hole group 30 from the outside. More specifically, the outline of the effective area 23 may be defined by a line tangent to the opening of the through-hole 40. In the example shown in FIG. 4, the through-holes 40 are arranged in parallel, so that the outline of the effective area 23 is a substantially rectangular outline. Although not shown, each effective area 23 may have an outline of various shapes depending on the shape of the display area of ​​the organic device 100. For example, each effective area 23 may have a circular outline.

[0151] 2 and 3, the mask substrate 15 may be provided with a first alignment mark 45 for aligning with the deposition substrate 110. The first alignment mark 45 may be disposed at any position as long as the through-hole 40 of the deposition mask 10 and the deposition substrate 110 can be aligned. For example, as shown in FIG. 2 and FIG. 3, the first alignment mark 45 may be formed on the substrate frame 17 of the second substrate surface 15b of the mask substrate 15. When the deposition substrate 110 has optical transparency, which means a property of transmitting visible light, the first alignment mark 45 provided on the mask substrate 15 can be visually recognized through the deposition substrate 110, and the deposition substrate 110 and the through-hole 40 of the deposition mask 10 can be easily aligned. When the deposition substrate 110 does not have optical transparency, the first alignment mark 45 may be visually recognized by irradiating infrared light through the deposition substrate 110, for example. 2, the planar shape of the first alignment mark 45 is shown as a circle, but is not limited thereto and may be any shape such as a rectangle, a cross, etc. Also, the first alignment mark 45 may be formed in a concave shape by etching the second substrate surface 15b of the mask substrate 15 in a substrate etching step to be described later.

[0152] 3 and 4, a second alignment mark 46 for aligning with the deposition substrate 110 may be provided on the first surface 20a of the mask layer 20. The second alignment mark 46 may be disposed at any position as long as the through-hole 40 of the deposition mask 10 and the deposition substrate 110 can be aligned. For example, the second alignment mark 46 may be disposed at a position closer to the through-hole 40 than the first alignment mark 45. For example, as shown in FIG. 3 and FIG. 4, the second alignment mark 46 may be formed in the substrate opening 16 of the mask substrate 15 on the first surface 20a of the mask layer 20 in a plan view. For example, the second alignment mark 46 may be located on the mask rails 28a and 28b formed between the adjacent through-hole groups 30. For example, the second alignment mark 46 may be located at the intersection 29 where the first mask rail 28a and the second mask rail 28b intersect. 4, the second alignment marks 46 are provided at each intersection 29 where each first mask bar 28a and each second mask bar 28b intersect. In other words, the second alignment marks 46 are arranged on each first mask bar 28a, and the second alignment marks 46 are arranged on each second mask bar 28b. In this case, the second alignment marks 46 are arranged at positions corresponding to each corner of each through hole group 30.

[0153] When the deposition substrate 110 has optical transparency for visible light, the second alignment mark 46 provided on the mask layer 20 can be visually recognized through the deposition substrate 110, and the deposition substrate 110 and the through-hole 40 of the deposition mask 10 can be easily aligned. When the deposition substrate 110 does not have optical transparency, for example, the second alignment mark 46 may be visually recognized by irradiating infrared light through the deposition substrate 110. The planar shape of the second alignment mark 46 is shown as a circular shape in FIG. 4 as an example, but is not limited thereto, and may be formed into any shape, such as a rectangular shape or a cross shape. In addition, the second alignment mark 46 may be formed in a concave shape by, for example, irradiating the first surface 20a of the first metal layer 21 with a laser beam. However, the present disclosure is not limited thereto, and the second alignment mark 46 may be formed in a concave shape by, for example, etching the first surface 20a of the first metal layer 21. Alternatively, the first metal layer 21 may be formed to have the second alignment mark 46 by, for example, a plating process in the first metal layer formation step. In this case, the first metal layer 21 may be formed by a plating process in a state where a resist (not shown) is formed at a position corresponding to the second alignment mark 46 on the surface of the second metal layer 22 opposite to the mask substrate 15. This makes it possible to form the second alignment mark 46 penetrating the first metal layer 21.

[0154] Next, a method for manufacturing the deposition mask 10 having such a configuration will be described with reference to Figs. 6 to 14. Here, an example will be described in which the mask substrate 15 is a silicon substrate. The method for manufacturing the deposition mask 10 according to the present embodiment may include a substrate preparation step, a mask layer formation step, a substrate opening formation step, and a through-hole formation step. In Figs. 13 and 14, the number of through-holes 40 is reduced compared to Fig. 3 in order to make the drawings easier to understand.

[0155] 6, a mask substrate 15 having a first substrate surface 15a and a second substrate surface 15b may be prepared in a substrate preparation step. For example, a silicon wafer having a surface orientation of (110) and having the first substrate surface 15a and the second substrate surface 15b polished to a mirror finish may be used as the mask substrate 15.

[0156] After the substrate preparation step, a mask layer 20 having a first surface 20a and a second surface 20b may be formed on the mask substrate 15 as a mask layer formation step. The second surface 20b of the mask layer 20 faces the mask substrate 15 and adheres to the first substrate surface 15a of the mask substrate 15. In the mask layer formation step according to the present embodiment, first, a second metal layer formation step of forming the second metal layer 22 is performed, and then a first metal layer formation step of forming the first metal layer 21 is performed. The first metal layer formation step is an example of a mask main body layer formation step, and the second metal layer formation step is an example of a mask intermediate layer formation step.

[0157] 7, in the second metal layer formation step, a second metal layer 22 is formed on the first substrate surface 15a of the mask substrate 15. More specifically, the second metal layer 22 including a body-side layer 25, a substrate-side layer 26, and an intermediate layer 27 is formed on the mask substrate 15.

[0158] First, the substrate-side layer 26 is formed. The substrate-side layer 26 may be formed on the entire first substrate surface 15a of the mask substrate 15. The substrate-side layer 26 may be formed, for example, by a sputtering process using a sputtering target made of the material of the substrate-side layer 26. The formed substrate-side layer 26 is attached to the mask substrate 15.

[0159] Subsequently, the intermediate layer 27 is formed on the substrate-side layer 26. The intermediate layer 27 may be formed on the entire surface of the substrate-side layer 26. The intermediate layer 27 may be formed, for example, by a sputtering process using a sputtering target made of the material of the intermediate layer 27 (for example, titanium). The formed intermediate layer 27 is attached to the substrate-side layer 26.

[0160] Next, the body side layer 25 is formed on the intermediate layer 27. The body side layer 25 may be formed on the entire surface of the intermediate layer 27. The body side layer 25 may be formed, for example, by a sputtering process using a sputtering target made of the material of the body side layer 25 (for example, copper). The formed body side layer 25 is attached to the intermediate layer 27.

[0161] In this manner, the second metal layer 22 including the body-side layer 25, the substrate-side layer 26 and the intermediate layer 27 is applied to the mask substrate 15.

[0162] In the first metal layer forming step, as shown in FIG. 8, the first metal layer 21 is formed on the surface of the second metal layer 22 opposite to the mask substrate 15. More specifically, the first metal layer 21 is formed on the body-side layer 25. The first metal layer 21 may be formed by, for example, a plating process. Here, the first metal layer 21 is formed by an electrolytic plating process using the second metal layer 22 as a power supply electrode. More specifically, a plating solution is supplied to the surface of the body-side layer 25 opposite to the mask substrate 15. For example, the mask substrate 15 on which the second metal layer 22 is formed is immersed in a plating tank filled with a plating solution. The body-side layer 25 of the second metal layer 22 described above functions as a power supply electrode for plating. As a result, the components of the plating solution are precipitated on the surface of the body-side layer 25 opposite to the mask substrate 15 to form the first metal layer 21. The first metal layer 21 may be formed on the entire surface of the body-side layer 25 opposite to the mask substrate 15. In this manner, the first metal layer 21 is attached to the body side layer 25 .

[0163] The components of the plating solution used are appropriately determined according to the characteristics required for the first metal layer 21. For example, when the first metal layer 21 is made of an iron alloy containing nickel, a mixed solution of a solution containing a nickel compound and a solution containing an iron compound may be used as the plating solution. For example, a mixed solution of a solution containing nickel sulfamate or nickel bromide and a solution containing ferrous sulfamate may be used. Also, when the first metal layer 21 is made of nickel, a solution containing a nickel compound may be used as the plating solution. For example, a nickel sulfamate solution may be used. Also, when the first metal layer 21 is made of a nickel alloy containing cobalt, a mixed solution of a solution containing a nickel compound and a solution containing a cobalt compound may be used as the plating solution. For example, a cobalt sulfamate solution may be used. Each of the above-mentioned plating solutions may contain various additives. As the additives, for example, a pH buffer such as boric acid, or additives such as malonic acid or saccharin may be included.

[0164] After the first metal layer 21 is formed, the first metal layer 21 may be annealed (fired). This allows the first metal layer 21 formed by the plating process to be recrystallized, and the thermal expansion coefficient of the first metal layer 21 to be reduced. That is, in general, even if a rolled material produced by a rolling process and a plated material produced by a plating process have the same material components, the thermal expansion coefficient of the plated material tends to be higher than the thermal expansion coefficient of the rolled material. For this reason, the first metal layer 21 may be recrystallized to reduce the thermal expansion coefficient of the first metal layer 21. During such annealing, the first metal layer 21 may be heated, for example, at a temperature of 600° C. for 5 minutes.

[0165] In the first metal layer forming step, the specific method of plating is not particularly limited as long as the first metal layer 21 can be formed. For example, electroless plating may be performed instead of electrolytic plating. When electroless plating is performed, since there is no electrode as in electrolytic plating, the thickness of the first metal layer 21 formed by electroless plating can be made uniform. When electroless plating is performed, a catalyst layer (not shown) may be provided on the surface of the second metal layer 22 opposite to the mask substrate 15. Even when electrolytic plating is performed, a similar catalyst layer may be provided on the second metal layer 22.

[0166] After the mask layer forming step, a substrate opening 16 exposing the second surface 20b of the mask layer 20 may be formed in the mask substrate 15 as a substrate opening forming step. In the substrate opening forming step according to the present embodiment, a resist layer forming step, a substrate etching step, and a resist layer removing step are performed in this order.

[0167] In the resist layer forming step, as shown in FIG. 9, a resist layer 50 is formed on the second substrate surface 15b of the mask substrate 15. The resist layer 50 has resist openings 51 corresponding to the substrate openings 16. More specifically, first, a liquid resist is applied to the second substrate surface 15b of the mask substrate 15 by a spinner, and then dried and hardened to form the resist layer 50. The resist layer 50 may be formed on the entire second substrate surface 15b. Then, the resist layer 50 is patterned by a photolithography process. For example, when the resist layer 50 is a negative resist, an exposure mask (not shown) that does not irradiate light to the portions of the resist layer 50 corresponding to the resist openings 51 is placed on the resist layer 50. Then, the resist layer 50 is exposed through this exposure mask. Then, the exposed resist layer 50 is developed, and the unexposed portions of the resist layer 50 are removed to form the resist openings 51. After development, the resist layer 50 may be heated to improve the adhesion of the resist layer 50 to the mask substrate 15. For example, a novolac-based resist may be used as the negative resist. A positive resist may be used as the resist layer 50. Alternatively, a dry film resist may be attached to the mask substrate 15 as the resist layer 50.

[0168] The thickness H8 of the resist layer 50 may be, for example, 0.1 μm or more, 0.5 μm or more, 1.0 μm or more, or 1.5 μm or more. By setting the thickness H8 to 0.1 μm or more, it is possible to suppress etching of the portion covered by the resist layer 50 in the substrate etching process described later. In addition, the thickness H8 may be, for example, 20.0 μm or less, 30.0 μm or less, 40.0 μm or less, or 50.0 μm or less. By setting the thickness H8 to 50.0 μm or less, it is possible to ensure availability in the case of a dry film resist, and it is possible to efficiently form the resist layer 50 in the case of a liquid resist. The range of the thickness H8 may be determined by a first group consisting of 0.1 μm, 0.5 μm, 1.0 μm, and 1.5 μm, and / or a second group consisting of 20.0 μm, 30.0 μm, 40.0 μm, and 50.0 μm. The range of thickness H8 may be determined by a combination of any one of the values ​​included in the first group described above and any one of the values ​​included in the second group described above. The range of thickness H8 may be determined by a combination of any two of the values ​​included in the first group described above. The range of thickness H8 may be determined by a combination of any two of the values ​​included in the second group described above.For example, it may be 0.1 μm or more and 50.0 μm or less, 0.1 μm or more and 40.0 μm or less, 0.1 μm or more and 30.0 μm or less, 0.1 μm or more and 20.0 μm or less, 0.1 μm or more and 1.5 μm or less, 0.1 μm or more and 1.0 μm or less, 0.1 μm or more and 0.5 μm or more and 50.0 μm or less, 0.5 μm or more and 40.0 μm or less, 0.5 μm or more and 30.0 μm or less, 0.5 μm or more and 20.0 μm or less, 0.5 μm or more and 1.5 μm or less, 0.5 μm or more and 1.0 μm or less, 1.0 μm or more and 50.0 μm or less, 1.0 It may be 1.0 μm or more and 30.0 μm or less, 1.0 μm or more and 20.0 μm or less, 1.0 μm or more and 1.5 μm or less, 1.5 μm or more and 50.0 μm or less, 1.5 μm or more and 40.0 μm or less, 1.5 μm or more and 30.0 μm or less, 1.5 μm or more and 20.0 μm or less, 20.0 μm or more and 50.0 μm or less, 20.0 μm or more and 40.0 μm or less, 20.0 μm or more and 30.0 μm or less, 30.0 μm or more and 50.0 μm or less, 30.0 μm or more and 40.0 μm or less, or 40.0 μm or more and 50.0 μm or less.

[0169] Alternatively, the thickness H8 of the resist layer 50 may be, for example, 0.1 μm or more, 0.2 μm or more, 0.3 μm or more, or 0.4 μm or more. By setting the thickness H8 to 0.1 μm or more, it is possible to suppress etching of the portion covered by the resist layer 50 in the substrate etching process described later. Also, H8 may be, for example, 0.6 μm or less, 0.7 μm or less, 0.8 μm or less, or 0.9 μm or less. By setting the thickness H8 to 0.9 μm or less, in the case of a dry film resist, availability can be further ensured, and in the case of a liquid resist, the resist layer 50 can be formed more efficiently. The range of H8 may be determined by a first group consisting of 0.1 μm, 0.2 μm, 0.3 μm, and 0.4 μm, and / or a second group consisting of 0.6 μm, 0.7 μm, 0.8 μm, and 0.9 μm. The range of H8 may be defined by a combination of any one of the values ​​included in the first group described above and any one of the values ​​included in the second group described above. The range of H8 may be defined by a combination of any two of the values ​​included in the first group described above. The range of H8 may be defined by a combination of any two of the values ​​included in the second group described above.For example, it may be 0.1 μm or more and 0.9 μm or less, 0.1 μm or more and 0.8 μm or less, 0.1 μm or more and 0.7 μm or less, 0.1 μm or more and 0.6 μm or less, 0.1 μm or more and 0.4 μm or less, 0.1 μm or more and 0.3 μm or less, 0.1 μm or more and 0.2 μm or less, 0.2 μm or more and 0.9 μm or less, 0.2 μm or more and 0.8 μm or less, 0.2 μm or more and 0.7 μm or less, 0.2 μm or more and 0.6 μm or less, 0.2 μm or more and 0.4 μm or less, 0.2 μm or more and 0.3 μm or less, or 0.3 μm or more and 0.9 μm or less. Alternatively, the thickness may be 0.3 μm or more and 0.8 μm or less, 0.3 μm or more and 0.7 μm or less, 0.3 μm or more and 0.6 μm or less, 0.3 μm or more and 0.4 μm or less, 0.4 μm or more and 0.9 μm or less, 0.4 μm or more and 0.8 μm or less, 0.4 μm or more and 0.7 μm or less, 0.4 μm or more and 0.6 μm or less, 0.6 μm or more and 0.9 μm or less, 0.6 μm or more and 0.8 μm or less, 0.6 μm or more and 0.7 μm or less, 0.7 μm or more and 0.9 μm or less, 0.7 μm or more and 0.8 μm or less, or 0.8 μm or more and 0.9 μm or less.

[0170] In the substrate etching process, as shown in FIG. 10, the mask substrate 15 is etched through the resist opening 51 to form the substrate opening 16. As a result, a part of the second surface 20b of the mask layer 20 is exposed in the substrate opening 16. The etching process of the mask substrate 15 may be a dry etching process using an etching gas. The etching gas is an example of an etching medium. In this case, the mask substrate 15 may be etched by using an etching gas such as DEEP-RIE, ICP (Inductively Coupled Plasma), SF6 gas, CF-based gas, or chlorine-based gas. When the dry etching process is performed, the etching rate can be increased and the wall surface of the substrate opening 16 can be formed substantially perpendicular to the first substrate surface 15a. When the substrate side layer 26 is formed of a material that can suppress erosion by the etching medium, it functions as a stopper layer that stops the etching. The etching process of the mask substrate 15 may be a wet etching process using an etching liquid. The etching liquid is an example of an etching medium. For example, the mask substrate 15 may be immersed in an etching solution of 35% by weight potassium hydroxide at 80° C. for a predetermined time. The portion of the mask substrate 15 that is exposed from the resist layer 50 may be anisotropically etched depending on the plane orientation (or crystal orientation).

[0171] The substrate etching step will be described in more detail. Here, an example in which the substrate opening 16 shown in FIG. 3 is formed by so-called deep RIE (deep reactive ion etching) will be described with reference to FIG. 11A to FIG. 11E. FIG. 11A to FIG. 11E are partial enlarged cross-sectional views that typically show the substrate opening 16 shown in FIG. 3.

[0172] First, as shown in FIG. 11A, a portion of the resist layer 50 exposed by the resist opening 51 is anisotropically etched. As a result, a first recess 16a1 is formed on the second substrate surface 15b. The first recess 16a1 includes a wall surface 16b1 extending from the resist opening 51 toward the first substrate surface 15a, and an end surface 16c1. The wall surface 16b1 is formed so as to widen toward the first substrate surface 15a. That is, as shown in FIG. 11A, the angle θ2 between the wall surface 16b1 and the first substrate surface 15a can be slightly larger than 90°.

[0173] In anisotropic dry etching, plasma of an etching gas is generated inside a deposition chamber (not shown) in which the mask substrate 15 is placed, and the plasma is irradiated onto the second substrate surface 15b of the mask substrate 15. The above-mentioned etching gas may be used as the etching gas for generating the plasma. Etching not only progresses in the thickness direction of the mask substrate 15, but also progresses slightly in the direction along the second substrate surface 15b. However, by setting the etching time to be short, the progress of etching in the direction along the second substrate surface 15b can be suppressed.

[0174] After the first recess 16a1 is formed, a first protective layer 16d1 is formed on the wall surface 16b1 and the end surface 16c1 of the first recess 16a1 as shown in Fig. 11B. This first protective layer 16d1 is formed on the wall surface 16b1 and the end surface 16c1 by supplying a raw material gas such as C4F8 gas to the first recess 16a1.

[0175] After the first protective layer 16d1 is formed, the first recess 16a1 is anisotropically dry etched as shown in FIG. 11C. As a result, a portion of the first protective layer 16d1 located on the end surface 16c1 is removed to form the second recess 16a2. More specifically, the end surface 16c1 of the first recess 16a1 is anisotropically dry etched in the same manner as in the process of forming the first recess 16a1 to form the second recess 16a2 connected to the first recess 16a1. At this time, like the wall surface 16b1 of the first recess 16a1 described above, the wall surface 16b2 of the second recess 16a2 is also formed so as to expand toward the first substrate surface 15a.

[0176] The first protective layer 16d1 formed on the wall surface 16b1 of the first recess 16a1 may or may not be removed by anisotropic dry etching for forming the second recess 16a2. Even if the first protective layer 16d1 is removed, the wall surface 16b1 of the first recess 16a1 can be prevented from being eroded by etching until the first protective layer 16d1 is removed. Furthermore, if the first protective layer 16d1 remains without being removed, the wall surface 16b of the first recess 16a1 can be further prevented from being eroded by etching. Even if the first protective layer 16d1 is not removed, the first protective layer 16d1 may be partially removed by etching.

[0177] 11D, a second protective layer 16d2 is formed on the wall surface 16b2 and the end surface 16c2 of the second recess 16a2. The second protective layer 16d2 can be formed in the same manner as the first protective layer 16d1.

[0178] As shown in FIG. 11E, the formation of such recesses and the formation of the protective layer are repeated many times until the etching of the mask substrate 15 reaches the substrate-side layer 26. In FIG. 11E, for the sake of simplicity, an example is shown in which a third recess 16a3 including a wall surface 16b3 and a fourth recess 16a4 including a wall surface 16b4 are formed following the second recess 16a2. The fourth recess 16a4 reaches the substrate-side layer 26 that functions as an etching stopper layer. The substrate-side layer 26 according to this embodiment is formed of a material that can suppress erosion by the etching gas. Therefore, the substrate-side layer 26 can function as an etching stopper layer and remains without being etched. A third protective layer 16d3 is formed on the wall surface 16b3, but no protective layer is formed on the wall surface 16b4.

[0179] Thereafter, the protective layers 16d1-16d3 remaining on the wall surfaces 16b1-16b3 of the recesses 16a1-16a3 are removed using a treatment liquid. The treatment liquid may be, for example, hydrofluoroether (HFE). The protective layers 16d1-16d3 may be immersed in the treatment liquid at room temperature (for example, about 25°C) to 70°C for 30 minutes. The treatment liquid may be used without diluting the original solution.

[0180] In this manner, the substrate opening 16 is formed in the mask substrate 15 as shown in FIG. 10. The wall surface of the substrate opening 16 is composed of the wall surfaces 16b1-16b4 of the recesses 16a1-16a4. The time of dry etching for forming the recesses 16a1-16a4 may be shortened to increase the number of times the formation of the recesses 16a1-16a4 and the formation of the protective film are repeated. In this case, the wall surface of the substrate opening 16 composed of the wall surfaces 16b1-16b4 of the recesses 16a1-16a4 can be formed substantially perpendicular to the second substrate surface 15b. In addition, a minute step may occur between the wall surfaces 16b1-16b4 of the recesses 16a1-16a4 adjacent to each other, but this step can be reduced by reducing the thickness of the protective layers 16d1-16d3 described above. In this case, in the cross section shown in FIG. 10, the wall surface of the substrate opening 16 can be formed to be a straight line substantially perpendicular to the first substrate surface 15a.

[0181] In the substrate etching step, a step of forming the first alignment mark 45 shown in Figures 2 and 3 may be performed. That is, the first alignment mark 45 may be formed in the substrate etching step.

[0182] 12, in the resist layer removing step, the resist layer 50 is removed from the mask substrate 15. For example, the resist layer 50 may be removed from the mask substrate 15 by using an alkaline stripping liquid.

[0183] In this manner, a mask substrate 15 having a substrate opening 16 formed therein is obtained, as shown in FIG.

[0184] The substrate opening forming step is not limited to the above-mentioned steps. For example, in the substrate opening forming step, a resistant layer (not shown), such as a silicon oxide layer, a silicon nitride layer, or a silicon carbide layer, may be formed on the second substrate surface 15b of the mask substrate 15. In this case, a resistant layer opening may be formed in the resistant layer, and then the mask substrate 15 may be etched through the resistant layer opening. The resistant layer opening may be formed by forming a resist layer having a resist opening in the resistant layer using a photolithography process, and etching the resistant layer through the resist opening. Then, the mask substrate 15 may be etched through the resistant layer opening to form the substrate opening 16. After the substrate opening 16 is formed, the resistant layer may be removed.

[0185] After the substrate opening forming step, a through hole forming step may be performed in which a plurality of through holes 40 are formed in the mask layer 20 so as to be exposed to the substrate opening 16. The through holes 40 may be formed by irradiating the mask layer 20 with laser light L. The through holes 40 may be formed so as to penetrate the first metal layer 21 and the opening region 22b.

[0186] For example, as shown in FIG. 13A, the through holes 40 may be formed one by one by irradiating the laser light L.

[0187] More specifically, first, the mask substrate 15 and the mask layer 20 obtained as described above are placed on a moving stage 60, as shown in FIG. 13A.

[0188] Subsequently, a large number of through holes 40 may be formed by repeating the formation of the through holes 40 and the movement of the moving stage 60. In this case, the irradiation head H does not need to be moved.

[0189] For example, the position where the through hole 40 is to be formed (the center of the through hole 40) is made to face the irradiation head H. Next, the laser light L is irradiated onto the second surface 20b of the mask layer 20 through the substrate opening 16 in a direction from the mask substrate 15 toward the first metal layer 21. As a result, the material of the portion of the mask layer 20 irradiated with the laser light L is sublimated and removed, and the through hole 40 is formed as shown in FIG. 13A. In FIG. 13A, the material of each of the layers 25 to 27 of the first metal layer 21 and the second metal layer 22 constituting the mask layer 20 is removed. In this case, the wall surface 41 of the through hole 40 tends to be formed perpendicular to the second surface 20b. However, depending on the intensity and pulse width of the laser light L and the thickness of the mask layer 20, the wall surface 41 of the through hole 40 may be inclined as shown in FIG. 13A.

[0190] The laser light L irradiated to the mask layer 20 may be femtosecond laser light. The femtosecond laser light is a pulsed laser light with a short pulse width, and can output high-intensity laser light with a short pulse width. The femtosecond laser light can irradiate the mask layer 20 with high-output laser light L in a short time. Therefore, the material molecules can be evaporated in a short time to form the through-holes 40. In this case, it is possible to suppress the formation of burrs on the first surface 20a of the mask layer 20. Burrs are protrusions that occur by processing a metal material. The output of such femtosecond laser light L may be, for example, 5 W or more and 100 W or less. The pulse width of the laser light L may be, for example, 1 fs or more and 10 ns or less. The wavelength of the laser light L may be, for example, 250 nm or more and 1100 nm or less, and may be, for example, 513 nm, which is a green laser. The oscillation frequency of the laser light L may be, for example, 1 Hz or more and 10 MHz or less. As an example, when laser light L is directly irradiated onto mask layer 20 having a thickness H2 of 4 μm without using a photomask 65 described later to form one through hole 40, the pulse width of the laser light L may be 260 fs. In this case, the wavelength of the laser light L may be 513 nm. The number of times of irradiation with laser light L to form one through hole 40 may be one time, or one through hole 40 may be formed by irradiating the laser light L multiple times.

[0191] After one through hole 40 is formed, the irradiation of the laser light L is stopped. Then, the moving stage 60 is moved so that the position where the next through hole 40 is to be formed (the center of the through hole 40) faces the irradiation head H. Then, the laser light L is irradiated in the same manner as described above. By repeating this process, a large number of through holes 40 are formed in the deposition mask 10 according to this embodiment.

[0192] As described above, when the through-hole 40 is formed by irradiating the laser light L, the irradiation head H may be moved without moving the moving stage 60.

[0193] The method of forming the through holes 40 is not limited to this. For example, as shown in Fig. 13B, a plurality of through holes 40 may be formed in parallel by irradiating a laser beam L. For example, as shown in Figs. 13B and 13C, the laser beam L may be irradiated from a laser beam generating device 61.

[0194] The laser light generating device 61 shown in FIG. 13C includes a laser light generating source 62, a first lens 63, a second lens 64 (also referred to as a collimator lens), a photomask 65, a third lens 66 (also referred to as a condenser lens), and a mirror 67. The laser light L generated from the laser light generating source 62 is expanded by the first lens 63 and collimated by the second lens 64. The collimated laser light L passes through a mask hole 65a of the photomask 65 and is condensed by the third lens 66. The condensed laser light L is reflected by the mirror 67 to change direction, and is irradiated onto the second surface 20b of the mask layer 20. Although simplified in FIG. 13C, the laser light L passing through the photomask 65 and the third lens 66 becomes a patterned light corresponding to the through-hole 40 as shown in FIG. 13B.

[0195] The photomask 65 has a plurality of mask holes 65a at positions corresponding to the plurality of through holes 40. In the example shown in FIG. 13B, a single through hole 40 is formed by the laser light L passing through one mask hole 65a. In this case, one mask hole 65a may be assigned to one through hole 40. The photomask 65 may include a light-transmitting substrate such as glass, and a layer on the substrate in which a metal material such as chromium is formed in a pattern, the layer having the above-mentioned mask holes 65a. In FIG. 13C, the above-mentioned substrate is omitted to simplify the drawing.

[0196] Then, the moving stage 60 may be moved to adjust the irradiation position of the laser light L. If the laser light generating device 61 is movable, the laser light generating device 61 may be moved.

[0197] Next, the second surface 20b of the mask layer 20 is irradiated with laser light L from the laser light generating device 61. As a result, the material of the mask layer 20 at the portions irradiated with the laser light L is sublimated and removed, and as shown in FIG. 13B, the plurality of through holes 40 are formed in parallel. Each through hole 40 is formed by the laser light L passing through one assigned mask hole 65a. The number of times of irradiation of the laser light L to form each through hole 40 may be one, or each through hole 40 may be formed by irradiation multiple times. In addition, the photomask 65 is not limited to being used when forming the plurality of through holes 40 in parallel, but may be used when forming the through holes 40 one by one by passing the laser light L through one mask hole 65a. In this case, the through holes 40 are formed one by one by irradiation of the laser light L.

[0198] A plurality of mask holes 65a may be assigned to one through hole 40. In this case, a mask hole 65a having a relatively large planar shape may be arranged in the center of the through hole 40. Furthermore, mask holes 65a having a relatively small planar shape may be arranged around it. The planar shape of the mask hole 65a may gradually become smaller from the center of the through hole 40 toward the outside. Such a pattern of mask holes 65a may be called a halftone pattern or a gradation pattern. That is, a mask hole 65a having a relatively large planar shape may be assigned to the center of the through hole 40, and mask holes 65a having a relatively small planar shape may be assigned around the mask hole 65a. In this case, the laser light L that passes through the large mask hole 65a in the center is irradiated to the mask layer 20 with a relatively high intensity. Therefore, a hole penetrating the mask layer 20 can be formed by the laser light L that passes through the mask hole 65a. The laser light L that passes through the small mask holes 65a in the periphery is irradiated to the mask layer 20 with a relatively low intensity. Therefore, at the position irradiated with the laser light L that has passed through the mask hole 65a, material is removed in a concave shape without penetrating the mask layer 20. By gradually reducing the planar shape of the mask hole 65a assigned to one through hole 40 from the center toward the outside, a plurality of through holes 40 with inclined wall surfaces 41 as shown in FIG.

[0199] 13B, an example has been described in which a plurality of through holes 40 are formed in parallel by irradiating the laser light L using the photomask 65. However, the present disclosure is not limited to this, and the through holes 40 may be formed one by one by irradiating the laser light L through a plurality of mask holes 65a of the photomask 65. That is, when a plurality of mask holes 65a are assigned to one through hole 40, the laser light L may be irradiated only to these mask holes 65a. In this case, the through holes 40 having inclined wall surfaces 41 can be formed one by one.

[0200] 3 and 4 may be performed in the through-hole forming step. That is, the deposition mask 10 is turned upside down so that the first surface 20a faces the irradiation head H. Then, the first surface 20a of the first metal layer 21 may be irradiated with laser light to form the concave second alignment mark 46.

[0201] In this manner, the deposition mask 10 according to the present embodiment as shown in FIG. 14 is obtained.

[0202] As described above, the first metal layer 21 according to this embodiment is formed by plating. In this case, stress acting in a direction of shrinking in plan view remains in the first metal layer 21. As a result, even if the temperature of the first metal layer 21 rises and the first metal layer 21 thermally expands, for example, during deposition, the positional accuracy of the through-holes 40 can be maintained as long as the above-mentioned stress remains. This can be said to be equivalent to a state in which a general deposition mask made by itself through etching or plating is stretched over a frame.

[0203] Next, a method for manufacturing an organic EL display device using the deposition mask 10 according to the present embodiment will be described with reference to FIGS. 1, 15A, and 15B.

[0204] The components and display region of the organic device 100 will be described in detail. FIG. 15A is a plan view showing an example of the organic device 100, showing an organic layer deposited in a deposition process. FIG. 15B is a cross-sectional view of the organic device 100 of FIG. 15A taken along line BB. FIG. 15A is a plan view showing an organic layer deposited in a deposition process, omitting a second electrode 140 (described later) formed after the deposition process. An example of the organic device 100 is an organic EL display device. The organic device 100 includes a light-emitting layer formed on a deposition substrate 110 (described later) by using the deposition mask 10 according to the present embodiment described above. One organic device 100 may correspond to one display region.

[0205] 15A and 15B, the organic device 100 includes a deposition substrate 110 and an element 115 disposed on the deposition substrate 110. The element 115 may include a first electrode 120, an organic layer 130 disposed on the first electrode 120, and a second electrode 140 disposed on the organic layer 130.

[0206] The organic device 100 may include an insulating layer 160 located between two adjacent first electrodes 120 in a plan view. The insulating layer 160 may include, for example, polyimide. The insulating layer 160 may overlap ends of the first electrodes 120.

[0207] The organic device 100 may be of an active matrix type. For example, although not shown, the organic device 100 may include a switch electrically connected to each of the multiple elements 115. The switch is, for example, a transistor. The switch can control ON / OFF of a voltage or a current to the corresponding element 115.

[0208] The deposition substrate 110 may have a first surface 110a on which the first electrode 120 is formed, and a second surface 110b located on the opposite side to the first surface 110a. The deposition substrate 110 may be a plate-like member having insulating properties. The deposition substrate 110 may have optical transparency that allows visible light to pass through.

[0209] When the deposition substrate 110 has a predetermined light transmittance, the light transmittance of the deposition substrate 110 may be a light transmittance that can transmit light emitted from the organic layer 130 for display. For example, the transmittance of the deposition substrate 110 in the visible light region may be 80% or more, or 90% or more. The transmittance of the deposition substrate 110 can be measured by a test method for total light transmittance of plastic-transparent materials conforming to JIS K7361-1.

[0210] The deposition substrate 110 may or may not be flexible. The deposition substrate 110 can be appropriately selected depending on the application of the organic device 100.

[0211] The deposition substrate 110 may include, for example, silicon and may be, for example, a silicon substrate. Alternatively, the deposition substrate 110 may include, for example, glass and may be, for example, a glass substrate. Furthermore, the material of the deposition substrate 110 may be, for example, a rigid material having no flexibility, such as quartz glass, Pyrex (registered trademark) glass, or a synthetic quartz plate. Alternatively, the material of the deposition substrate 110 may be, for example, a flexible material having flexibility, such as a resin film (for example, a polyimide film or a liquid crystal polymer), an optical resin plate, or thin glass. Furthermore, the deposition substrate 110 may be a laminate having a barrier layer on one or both sides of a resin film.

[0212] When the deposition substrate 110 is made of a material other than a silicon substrate, the thickness of the deposition substrate 110 can be appropriately selected depending on the material used for the deposition substrate 110 and the application of the organic device 100. In this case, the thickness of the deposition substrate 110 may be, for example, 0.005 mm or more. Alternatively, the thickness of the deposition substrate 110 may be 5 mm or less.

[0213] The element 115 is configured to realize some function by applying a voltage between the first electrode 120 and the second electrode 140, or by causing a current to flow between the first electrode 120 and the second electrode 140. For example, when the element 115 is a pixel of an organic EL display device, the element 115 can emit light that constitutes an image.

[0214] The first electrode 120 includes a material having electrical conductivity. For example, the first electrode 120 includes a metal, a metal oxide having electrical conductivity, or other inorganic material having electrical conductivity. The first electrode 120 may include a metal oxide having optical transparency and electrical conductivity, such as indium tin oxide.

[0215] The material constituting the first electrode 120 may be a metal such as Au, Cr, Mo, Ag, or Mg. Alternatively, the material constituting the first electrode 120 may be an inorganic oxide such as indium tin oxide called ITO, indium zinc oxide called IZO, or zinc oxide or indium oxide. The material constituting the first electrode 120 may be a conductive polymer such as metal-doped polythiophene. These conductive materials may be used alone or in combination of two or more. When two or more types are used, layers made of each material may be laminated on the conductive material. In addition, the conductive material may be an alloy containing two or more types of materials. For example, the conductive material may be a magnesium alloy such as MgAg.

[0216] The organic layer 130 includes an organic material. When a current is passed through the organic layer 130, the organic layer 130 can perform some function. Passing a current means that a voltage is applied to the organic layer 130 or that a current flows through the organic layer 130. The organic layer 130 may include a light-emitting layer that emits light when a current is passed through it, or a layer whose light transmittance or refractive index changes when a current is passed through it. The organic layer 130 may include an organic semiconductor material.

[0217] As shown in FIG. 15B, the organic layer 130 may include a first organic layer 130A and a second organic layer 130B. Also, as shown in FIG. 15A, the organic layer 130 may further include a third organic layer 130C. The first organic layer 130A, the second organic layer 130B, and the third organic layer 130C are, for example, a red light-emitting layer, a blue light-emitting layer, and a green light-emitting layer. In the following description, when describing a configuration common to the first organic layer 130A, the second organic layer 130B, and the third organic layer 130C among the configurations of the organic layer, the term and symbol "organic layer 130" are used.

[0218] The laminated structure including the first electrode 120, the first organic layer 130A, and the second electrode 140 is also referred to as the first element 115A. The laminated structure including the first electrode 120, the second organic layer 130B, and the second electrode 140 is also referred to as the second element 115B. The laminated structure including the first electrode 120, the third organic layer 130C, and the second electrode 140 is also referred to as the third element 115C. When the organic device 100 is an organic EL display device, the first element 115A, the second element 115B, and the third element 115C are each a subpixel.

[0219] In the following description, when describing a configuration common to the first element 115A, the second element 115B, and the third element 115C, the term and symbol "element 115" are used. In a plan view such as FIG. 15A, the outline of element 115 may be the outline of organic layer 130 that overlaps with first electrode 120 and second electrode 140 in plan view. In the case where organic device 100 includes insulating layer 160, the outline of element 115 may be the outline of organic layer 130 that overlaps with first electrode 120 and second electrode 140 in plan view but does not overlap with insulating layer 160.

[0220] The arrangement of the first element 115A, the second element 115B, and the third element 115C will be described. As shown in Fig. 15A, the first element 115A, the second element 115B, and the third element 115C may be aligned along the element first direction F1. The first element 115A, the second element 115B, and the third element 115C may be aligned along the element second direction F2.

[0221] When a voltage is applied between the first electrode 120 and the second electrode 140, the organic layer 130 located therebetween is driven. When the organic layer 130 is an emitting layer, light is emitted from the organic layer 130 and extracted to the outside from the second electrode 140 side or the first electrode 120 side.

[0222] When the organic layer 130 includes a light-emitting layer that emits light when a current is applied, the organic layer 130 may further include a hole injection layer, a hole transport layer, an electron transport layer, an electron injection layer, and the like.

[0223] For example, when the first electrode 120 is an anode, the organic layer 130 may have a hole injection transport layer between the light emitting layer and the first electrode 120. The hole injection transport layer may be a hole injection layer having a hole injection function, a hole transport layer having a hole transport function, or a layer having both a hole injection function and a hole transport function. The hole injection transport layer may be a layer in which a hole injection layer and a hole transport layer are laminated.

[0224] When the second electrode 140 is a cathode, the organic layer 130 may have an electron injection transport layer between the light emitting layer and the second electrode 140. The electron injection transport layer may be an electron injection layer having an electron injection function, an electron transport layer having an electron transport function, or a layer having both the electron injection function and the electron transport function. The electron injection transport layer may be a layer in which an electron injection layer and an electron transport layer are laminated.

[0225] The light-emitting layer includes a light-emitting material and may include an additive to improve leveling properties.

[0226] The light-emitting material may be a known material, such as a dye-based material, a metal complex-based material, or a polymer-based material.

[0227] The thickness of the light-emitting layer is not particularly limited as long as it can provide a place for recombination of electrons and holes and can exhibit the function of emitting light. The thickness of the light-emitting layer may be, for example, 1 nm or more. The thickness of the light-emitting layer may be 500 nm or less.

[0228] The second electrode 140 includes a material having electrical conductivity, such as a metal. The second electrode 140 is formed on the organic layer 130 by a deposition method using a mask, which will be described later. The material constituting the second electrode 140 may be platinum, gold, silver, copper, iron, tin, chromium, aluminum, indium, lithium, sodium, potassium, calcium, magnesium, chromium, carbon, or the like. These conductive materials may be used alone or in combination of two or more. When two or more types are used, layers made of each material may be laminated on the conductive material. In addition, the conductive material may be an alloy containing two or more types of materials. For example, the conductive material may be a magnesium alloy such as MgAg, an aluminum alloy such as AlLi, AlCa, AlMg, an alloy of alkali metals and alkaline earth metals, or the like.

[0229] As shown in FIG. 15B, the organic device 100 may include a sealing layer (not shown) that covers elements on the deposition substrate 110, such as the organic layers 130A, 130B, and 130C. The sealing layer can prevent water vapor and the like from the outside of the organic device 100 from entering the inside of the organic device 100. This can prevent the organic layers 130A, 130B, and 130C from deteriorating due to moisture. The sealing layer may include, for example, a layer made of an organic material. The organic material may have a refractive index equal to or close to that of the organic layers 130A, 130B, and 130C in order to prevent refraction of light in the sealing layer. The organic material may be sealed with, for example, an inorganic material such as silicon nitride (SiN). In this case, the sealing layer may have a laminated structure in which a layer of an organic material and a layer of an inorganic material are laminated. A planarization layer (not shown) may be interposed between the second electrode 140 and the sealing layer. The planarization layer may be a layer for filling in the irregularities of elements on the deposition substrate 110 and improving the adhesion of the encapsulation layer.

[0230] The manufacturing method for such an organic device 100 may include a step of attaching a deposition material 82 to a deposition substrate 110 using a deposition mask 10 to form organic layers 130A, 130B, and 130C. More specifically, the manufacturing method for the organic EL display device according to the present embodiment may include a deposition mask preparation step, an alignment step, a bonding step, a deposition step, and a cutting step.

[0231] First, in a deposition mask preparation step, the deposition mask 10 described above may be prepared.

[0232] After the deposition mask preparation step, the deposition mask 10 is aligned with respect to the deposition substrate 110 in an alignment step. In the alignment step, the positions of the through holes 40 of the deposition mask 10 with respect to the deposition substrate 110 are confirmed. At this time, the positions of the through holes 40 of the deposition mask 10 with respect to the deposition substrate 110 may be adjusted. For example, a first alignment mark 45 provided on the substrate frame 17 of the mask substrate 15 is aligned with a corresponding substrate alignment mark 111 (see FIG. 3) of the deposition substrate 110. In addition, a second alignment mark 46 provided on the mask rails 28a and 28b of the mask layer 20 is aligned with a corresponding alignment mark (not shown) of the deposition substrate 110. For example, the deposition substrate 110 may be roughly aligned with the through holes 40 using the first alignment mark 45, and then the deposition substrate 110 may be finely aligned with the through holes 40 using the second alignment mark 46. This allows the positions of the through-holes 40 of the deposition mask 10 relative to the deposition substrate 110 to be adjusted with high precision.

[0233] After the alignment step, a bonding step may be performed in which the first surface 20a of the mask layer 20 of the deposition mask 10 is bonded to the deposition substrate 110. More specifically, in the deposition apparatus 80, the first surface 20a of the mask layer 20 of the deposition mask 10 is bonded to the first surface 110a (see FIG. 3 ) of the deposition substrate 110 in an aligned state. At this time, the deposition substrate 110 is interposed between the deposition mask 10 and a magnet 85, and the deposition mask 10 is attracted to the deposition substrate 110 by the magnetic force of the magnet 85. As a result, the deposition substrate 110 is bonded to the first surface 20a of the deposition mask 10.

[0234] After the adhesion step, the deposition material 82 may be deposited on the first electrode 120 formed on the deposition substrate 110 through the through holes 40 of the deposition mask 10 to form the organic layers 130A, 130B, and 130C as a deposition step (see FIG. 15B). The organic layers 130A, 130B, and 130C are formed on the corresponding hole transport layers. More specifically, the pressure inside the deposition device 80 is reduced to a vacuum atmosphere. Then, the deposition material 82 is evaporated and caused to fly to the hole transport layer. The flown deposition material 82 passes through each of the through holes 40 of the deposition mask 10 and adheres to the desired hole transport layer. As a result, the organic layers 130A, 130B, and 130C are formed on the first electrode 120 and the insulating layer 160 in a pattern corresponding to the pattern of the through holes 40.

[0235] Here, the organic layers 130A, 130B, and 130C are formed so as to straddle the first electrode 120 and the insulating layer 160 adjacent to the first electrode 120. Although not shown, the organic layers 130A, 130B, and 130C adjacent to each other on the insulating layer 160 may overlap each other.

[0236] As described above, in this embodiment, the through-holes 40 are arranged in a predetermined pattern in each effective area 23. When displaying using a plurality of colors, a deposition mask 10 having through-holes 40 formed in a pattern corresponding to the organic layers 130A, 130B, and 130C of each color is prepared. In each deposition mask 10, a deposition material 82 of each color is attached to a corresponding hole transport layer. Thereby, for example, a red organic light-emitting material, a green organic light-emitting material, and a blue organic light-emitting material can be deposited on one deposition substrate 110, and the organic layers 130A, 130B, and 130C can be formed, respectively.

[0237] After the organic layers 130A, 130B, and 130C are formed, an electron transport layer and an electron injection layer are formed on the organic layers 130A, 130B, and 130C. Then, the second electrode 140 is formed. The second electrode 140 is formed so as to cover each of the organic layers 130A, 130B, and 130C, and is formed on the organic layers 130A, 130B, and 130C so as to straddle the first electrode 120 and the insulating layer 160 adjacent to the first electrode 120. For example, the second electrode 140 may be continuously formed so as to straddle two organic layers 130A, 130B, and 130C adjacent to each other in a plan view.

[0238] The above-mentioned planarization layer and sealing layer are formed on the formed second electrode 140. In this manner, elements such as the organic layers 130A, 130B, and 130C provided on the deposition substrate 110 are sealed with the sealing layer.

[0239] After the deposition process, in a cutting process, the deposition substrate 110 is cut into individual organic devices 100. In this case, for example, the deposition substrate 110 is cut using a dicing saw between adjacent organic devices 100. Depending on the distance between adjacent organic devices 100 and the width of the dicing saw, the deposition substrate 110 may be cut by applying single sawing or double sawing.

[0240] In this manner, the organic device 100 is obtained in which the organic layers 130A, 130B, and 130C of each color are formed on the deposition substrate 110.

[0241] As described above, according to the present embodiment, the deposition mask 10 includes the mask layer 20 having the through-holes 40 and the mask substrate 15 located on the second surface 20b of the mask layer 20. Since the mask substrate 15 is located on the mask layer 20, the strength of the deposition mask 10 can be improved, and the deposition mask 10 can be in close contact with the deposition substrate 110 in this state. As a result, the shape accuracy and position accuracy of the through-holes 40 in the mask layer 20 can be maintained at the shape accuracy and position accuracy at the time when the through-holes 40 are formed, and the definition of the through-holes 40 can be improved. The through-holes 40 can also be made highly precise. In addition, the deposition material 82 can be attached to the deposition substrate 110 in a state where the shape accuracy and position accuracy of the through-holes 40 are improved. Therefore, the definition of the organic layers 130A, 130B, and 130C of the organic device 100 can be improved. In this case, the pixels constituted by the elements including the organic layers 130A, 130B, and 130C can also be made highly precise.

[0242] According to the present embodiment, the mask substrate 15 contains silicon. When the deposition substrate 110 is a silicon substrate, the mask substrate 15 can be made of the same material as or similar to the deposition substrate 110. This can reduce the difference between the thermal expansion coefficient of the mask substrate 15 and the thermal expansion coefficient of the deposition substrate 110. This can suppress a decrease in accuracy. Here, for example, when the pixel density of the organic device 100 is high, it is required to improve the shape accuracy and position accuracy of the through-hole 40. Since the mask substrate 15 according to the present embodiment contains silicon, the difference in the thermal expansion coefficient from the deposition substrate 110 can be reduced as described above. This can suppress the position of the through-hole 40 from being shifted relative to the deposition substrate 110 even when the deposition mask 10 aligned with high accuracy relative to the deposition substrate 110 thermally expands. This can improve the shape accuracy and position accuracy of the organic layers 130A, 130B, and 130C formed on the deposition substrate 110. As a result, the organic device 100 including the high-definition organic layers 130A, 130B, and 130C can be easily manufactured.

[0243] According to this embodiment, the second surface 20b of the mask layer 20 is attached to the mask substrate 15. This can further improve the strength of the deposition mask 10. Here, when the mask layer 20 is produced separately from the mask substrate 15, the mask layer 20 is stretched on a frame such as the mask substrate 15 while applying tension, and then fixed by welding or the like. However, in the deposition mask 10 according to this embodiment, the mask layer 20 is attached to the mask substrate 15, so such stretching is not necessary. This can maintain the shape accuracy and position accuracy of the through-hole 40 of the mask layer 20 attached to the mask substrate 15 at the shape accuracy and position accuracy at the time when the through-hole 40 is formed. This can further improve the definition of the through-hole 40.

[0244] According to the present embodiment, the mask layer 20 includes the first metal layer 21 forming the first surface 20a and the second metal layer 22 located between the first metal layer 21 and the mask substrate 15. This allows the second metal layer 22 to be configured as a layer having a specific purpose. For example, the second metal layer 22 can be formed of a material that can ensure adhesion between the first metal layer 21 and the mask substrate 15. In this case, the deposition mask 10 can be attached to the mask substrate 15, and the strength of the deposition mask 10 can be further improved. Alternatively, the second metal layer 22 can be formed of a material that is resistant to the etching medium used in the substrate etching process. In this case, the first metal layer 21 can be prevented from being etched by the etching medium in the substrate etching process.

[0245] Also, according to this embodiment, the thickness of the second metal layer 22 forming the second surface 20b of the mask layer 20 is smaller than the thickness of the first metal layer 21 forming the first surface 20a. This allows the second metal layer 22 to be configured as a layer having a specific purpose. That is, when the second metal layer 22 is configured as a layer having a specific purpose, it may be difficult to reduce the thermal expansion coefficient. For example, the purpose of the second metal layer 22 may be to ensure adhesion with the first metal layer 21, to ensure adhesion with the mask substrate 15, to suppress erosion by an etching medium used in the substrate etching process, or to protect the substrate side layer 26 from a plating solution containing a material that constitutes the first metal layer 21. The material for achieving such a purpose may have a large thermal expansion coefficient. However, even in this case, the influence of the thermal expansion of the second metal layer 22 can be suppressed by reducing the thickness of the second metal layer 22. This allows the accuracy to be suppressed from decreasing.

[0246] According to the present embodiment, the first metal layer 21 contains a metal material. As a result, the through-holes 40 can be formed in the mask layer 20 made of a metal material. As a result, when the deposition mask 10 is washed after the deposition process of forming the organic layers 130A, 130B, and 130C on the deposition substrate 110, the layer in which the through-holes 40 are located can be prevented from absorbing the washing liquid. As a result, the through-holes 40 can be prevented from being displaced and from being deformed. As a result, the definition of the through-holes 40 in the deposition mask 10 after washing can be improved. In addition, when the first metal layer 21 contains a magnetic metal material, the deposition mask 10 can be brought into close contact with the deposition substrate 110 by using the magnet 85. In this case, the deposition mask 10 can be attracted toward the magnet 85 by a magnetic force, and the adhesion between the deposition mask 10 and the deposition substrate 110 can be improved. As a result, the definition of the organic layers 130A, 130B, and 130C of the organic device 100 can be improved.

[0247] Moreover, according to this embodiment, the second metal layer 22 includes a main body region 22a located between the first metal layer 21 and the substrate frame 17, and an opening region 22b located within the substrate opening 16 in a plan view. This allows the second metal layer 22 to be configured as an etching stopper layer in the substrate etching process. Furthermore, the through hole 40 penetrates the first metal layer 21 and the opening region 22b. This makes it unnecessary to remove the opening region 22b. Furthermore, since the second metal layer 22 includes the opening region 22b, the strength of the deposition mask 10 can be improved.

[0248] Moreover, according to the present embodiment, the opening dimension of the through-hole 40 in a predetermined direction in the second surface 20b is larger than the opening dimension of the through-hole 40 in the first surface 20a in the predetermined direction. This makes it possible to suppress the occurrence of shadows when the deposition substrate 110 is brought into close contact with the first surface 20a during deposition. This makes it possible to improve the shape accuracy and positional accuracy of the organic layers 130A, 130B, and 130C formed by the deposition material 82 attached to the deposition substrate 110, and thus improve the definition of the organic device 100.

[0249] Moreover, according to this embodiment, two or more through holes 40 are located in the substrate opening 16 of the mask substrate 15. This makes it possible to suppress the mask substrate 15 from generating a shadow during deposition. This makes it possible to improve the shape accuracy and position accuracy of the organic layers 130A, 130B, and 130C formed by the deposition material 82 attached to the deposition substrate 110, thereby improving the definition of the organic device 100. Furthermore, according to this embodiment, since a plurality of through hole groups 30 are located in the substrate opening 16, the generation of a shadow can be further suppressed.

[0250] According to the present embodiment, the first alignment mark 45 is provided on the surface of the mask substrate 15 opposite to the mask layer 20. Thus, in an alignment step of aligning the deposition mask 10 with respect to the deposition substrate 110, the deposition mask 10 and the deposition substrate 110 can be aligned using the first alignment mark 45. Because the first alignment mark 45 is provided on the mask substrate 15, the deposition mask 10 can be aligned overall with the deposition substrate 110.

[0251] According to the present embodiment, the second alignment mark 46 is provided at a position closer to the through-hole 40 than the first alignment mark 45. As a result, in a positioning step of aligning the deposition mask 10 with respect to the deposition substrate 110, the deposition mask 10 and the deposition substrate 110 can be aligned using the second alignment mark 46. Since the second alignment mark 46 is provided at a position closer to the through-hole 40 than the first alignment mark 45, the alignment accuracy between the deposition mask 10 and the deposition substrate 110 can be improved. Since the second alignment mark 46 is provided on the first surface 20a of the mask layer 20, the second alignment mark 46 can be viewed through the deposition substrate 110 even when the first metal layer 21 does not have optical transparency.

[0252] Moreover, according to this embodiment, the second alignment mark 46 is located on the mask bars 28a, 28b provided between the adjacent through-hole groups 30. This allows the second alignment mark 46 to be located closer to the through-hole 40. This further improves the alignment accuracy between the deposition mask 10 and the deposition substrate 110. Also, according to this embodiment, the second alignment mark 46 is located at the intersection 29 where the first mask bar 28a and the second mask bar 28b intersect. This allows the through holes 40 of adjacent through-hole groups 30 to be aligned efficiently.

[0253] Moreover, according to the present embodiment, the through holes 40 are formed by irradiating the mask layer 20 with the laser light L. This makes it possible to improve the shape accuracy and position accuracy of the through holes 40. As a result, the definition of the deposition mask 10 can be improved.

[0254] According to the present embodiment, after the substrate opening 16 is formed, the laser light L is irradiated onto the second surface 20b of the mask layer 20 through the substrate opening 16. This allows the opening dimension of the through hole 40 in a predetermined direction on the second surface 20b to be easily made larger than the opening dimension of the through hole 40 in the predetermined direction on the first surface 20a. This allows the through hole 40 that can suppress the occurrence of a shadow to be easily formed when the deposition substrate 110 is brought into close contact with the first surface 20a during deposition. This allows the shape accuracy and position accuracy of the organic layers 130A, 130B, and 130C formed by the deposition material 82 attached to the deposition substrate 110 to be improved, and the definition of the organic device 100 to be improved.

[0255] According to the present embodiment, the laser light L is femtosecond laser light. This allows high-intensity laser light with a short pulse width to be output to the mask layer 20. This makes it possible to suppress the formation of burrs on the first surface 20a of the mask layer 20, and improve the adhesion to the deposition substrate 110. This makes it possible to improve the shape accuracy and position accuracy of the organic layers 130A, 130B, and 130C formed by the deposition material 82 attached to the deposition substrate 110, and improve the definition of the organic device 100.

[0256] Various modifications can be made to the embodiment described above. Below, the modified examples will be described with reference to the drawings as necessary. In the following description and the drawings used in the following description, the same reference numerals as those used for the corresponding parts in the embodiment described above will be used for parts that can be configured in the same manner as the embodiment described above, and duplicated descriptions will be omitted. In addition, if it is clear that the effects obtained in the embodiment described above can also be obtained in the modified examples, the description may be omitted.

[0257] Next, a first modified example will be described.

[0258] In the above-described embodiment, an example has been described in which the second metal layer 22 includes a main body region 22a located between the first metal layer 21 and the substrate frame 17, and an opening region 22b located within the substrate opening 16 in a plan view. However, the present disclosure is not limited to this.

[0259] For example, as shown in Fig. 16, the second metal layer 22 may include a body region 22a and a mask layer opening 22d formed along the substrate opening 16 in a plan view. The mask layer opening 22d may penetrate the body side layer 25, the substrate side layer 26, and the intermediate layer 27. The mask layer opening 22d may have the same planar shape as the substrate opening 16. In the example shown in Fig. 16, the through hole 40 penetrates the first metal layer 21. That is, the through hole 40 extends from the first surface 20a to the surface of the first metal layer 21 facing the mask substrate 15 and penetrates the first metal layer 21.

[0260] The opening dimension of the through hole 40 in a predetermined direction (for example, the first direction D11 or the second direction D12) on the surface of the first metal layer 21 facing the mask substrate 15 may be larger than the opening dimension of the through hole 40 in the predetermined direction on the first surface 20a. In one embodiment, the cross-sectional opening of the through hole 40 in a direction parallel to the first surface 20a may gradually increase from the first surface 20a toward the surface of the first metal layer 21 facing the mask substrate 15. In other words, the cross-sectional area of ​​each through hole 40 in a cross section parallel to the first surface 20a at each position along the normal direction of the mask layer 20 may gradually increase from the first surface 20a toward the surface of the first metal layer 21 facing the mask substrate 15. In this case, the through hole 40 may have a wall surface 41 formed so as to move away from the central axis CL of the through hole 40 from the first surface 20a toward the surface of the first metal layer 21 facing the mask substrate 15. 16 shows an example in which the wall surface 41 of the through hole 40 is inclined linearly with respect to the central axis CL so as to move away from the central axis CL from the first surface 20a toward the surface of the first metal layer 21 facing the mask substrate 15. For example, the opening dimension of the through hole 40 on the first surface 20a of the mask layer 20 may be S1 shown in FIG. 5A. The opening dimension of the through hole 40 on the surface of the first metal layer 21 facing the mask substrate 15 may be S2 shown in FIG. 5A.

[0261] The mask layer opening 22d shown in FIG. 16 may be formed in the second metal layer 22 as a mask layer opening forming step after the substrate opening forming step. The mask layer opening 22d may be formed by etching the second metal layer 22. More specifically, the second metal layer 22 is etched to remove a region of the second metal layer 22 corresponding to the substrate opening 16. In this manner, the mask layer opening 22d may be formed. For example, N-methylpyrrolidone (NMP) may be used as the etching solution. For example, the second metal layer 22 may be immersed in an etching solution at room temperature or higher and 70° C. or lower for 20 minutes. N-methylpyrrolidone may be used without diluting the original solution. Also, the body side layer 25, the substrate side layer 26, and the intermediate layer 27 may be removed by separate etching solutions.

[0262] The through-hole forming step may be performed after the mask layer opening forming step. In this case, in the through-hole forming step, the mask layer opening 22d is formed in the second metal layer 22. For this reason, the laser light L is irradiated onto the surface of the first metal layer 21 facing the mask substrate 15 through the substrate opening 16 and the mask layer opening 22d. As a result, the through-hole 40 penetrating the first metal layer 21 is formed in the first metal layer 21.

[0263] In this manner, according to the first modification, since the second metal layer 22 includes the mask layer opening 22d, it is possible to reduce the thickness of the portion of the mask layer 20 where the through hole 40 is formed, and therefore it is possible to suppress the occurrence of a shadow.

[0264] Next, a second modified example will be described.

[0265] In the above-described first modified example, an example has been described in which the through holes 40 are formed by irradiating the first metal layer 21 with the laser light L. However, the present disclosure is not limited to this. For example, the through holes 40 may be formed when the first metal layer 21 is plated in the first metal layer forming step.

[0266] The method for manufacturing the deposition mask 10 according to this modification may include a substrate preparation step, a mask layer formation step, a substrate opening formation step, and a mask layer opening formation step. In the mask layer formation step, first, a second metal layer formation step is performed, followed by a resist layer formation step, and then a first metal layer formation step. In the first metal layer formation step, a through hole formation step may be performed. After the first metal layer formation step, a resist layer removal step is performed.

[0267] 17, in the resist layer forming step, a resist layer 55 is formed on the second metal layer 22. The resist layer 55 is formed in a pattern corresponding to the through-holes 40.

[0268] More specifically, first, a liquid resist is applied to the surface of the body-side layer 25 opposite the mask substrate 15 by a spinner. The liquid resist is then heated to dry and harden. This forms a resist layer 55. The resist layer 55 may be formed entirely on the body-side layer 25. The heat treatment of the liquid resist may be performed, for example, at a temperature of 90° C. for 90 seconds.

[0269] Next, the resist layer 55 is patterned by photolithography to have a plurality of resist lands 56 formed at positions corresponding to the through holes 40. For example, when the resist layer 55 is a positive resist, an exposure mask (not shown) that does not irradiate light to the portions of the resist layer 55 corresponding to the through holes 40 is placed on the resist layer 55. The resist layer 55 is then exposed through the exposure mask. An i-line stepper exposure device may be used for the exposure. The exposure time may be 420 ms. In this case, in the region irradiated with light, the amount of light irradiation may be reduced by adjusting the focus during exposure near the periphery of the region. As a result, the wall surface 57 of the resist land 56 is formed to be inclined after development. As shown in FIG. 17, the wall surface 57 of the resist land 56 may be inclined at an angle θ3 with respect to the second surface 20b of the mask layer 20. The angle θ3 of the wall surface 57 may be the same as the angle θ1 shown in FIG. That is, the through hole 40 is formed to follow the wall surface 57. In this case, the wall surface 41 of the through hole 40 has the same angle θ1 as that shown in Fig. 3. For example, when the angle θ3 is 70°, the angle θ1 of the wall surface 41 may be 70°.

[0270] Thereafter, the exposed resist layer 55 is developed. This removes the exposed portions of the resist layer 55. Therefore, as shown in FIG. 17, the resist layer 55 is formed in a pattern having a plurality of resist lands 56 arranged at positions corresponding to the through holes 40.

[0271] After development, the resist layer 55 may be heated, thereby improving the adhesion of the resist layer 55 to the body-side layer 25. The heat treatment of the resist layer 55 may be performed at a temperature of 110° C. for 90 seconds, for example.

[0272] For example, iP5700 manufactured by Tokyo Ohka Kogyo Co., Ltd. may be used as the positive resist. However, a negative resist may be used as the resist layer 55. Also, a dry film resist may be attached to the main body side layer 25 as the resist layer 55.

[0273] The thickness H9 of the resist layer 55 may be greater than the thickness H3 of the first metal layer 21 that is formed in the subsequent first metal layer forming step.

[0274] The thickness H9 of the resist layer 55 may be, for example, 4.0 μm or more, 4.4 μm or more, 4.8 μm or more, or 5.2 μm or more. By setting the thickness H9 to 4.0 μm or more, a thickness greater than the thickness of the first metal layer 21 can be ensured in the first metal layer forming step, and the through hole 40 penetrating the first metal layer 21 can be formed. In addition, the thickness H9 may be, for example, 5.8 μm or less, 6.2 μm or less, 6.6 μm or less, or 7.0 μm or less. By setting the thickness H9 to 7.0 μm or less, availability can be ensured in the case of a dry film resist, and the resist layer 55 can be efficiently formed in the case of a liquid resist. The range of thickness H9 may be defined by a first group consisting of 4.0 μm, 4.4 μm, 4.8 μm and 5.2 μm and / or a second group consisting of 5.8 μm, 6.2 μm, 6.6 μm and 7.0 μm. The range of thickness H9 may be defined by a combination of any one of the values ​​included in the above-mentioned first group with any one of the values ​​included in the above-mentioned second group. The range of thickness H9 may be defined by a combination of any two of the values ​​included in the above-mentioned first group. The range of thickness H9 may be defined by a combination of any two of the values ​​included in the above-mentioned second group.For example, it may be 4.0 μm or more and 7.0 μm or less, 4.0 μm or more and 6.6 μm or less, 4.0 μm or more and 6.2 μm or less, 4.0 μm or more and 5.8 μm or less, 4.0 μm or more and 5.2 μm or less, 4.0 μm or more and 4.8 μm or less, 4.0 μm or more and 4.4 μm or less, 4.4 μm or more and 7.0 μm or less, 4.4 μm or more and 6.6 μm or less, 4.4 μm or more and 6.2 μm or less, 4.4 μm or more and 5.8 μm or less, 4.4 μm or more and 5.2 μm or less, 4.4 μm or more and 4.8 μm or less, or 4.8 μm or more and 7.0 μm or less. Alternatively, it may be 4.8 μm or more and 6.6 μm or less, 4.8 μm or more and 6.2 μm or less, 4.8 μm or more and 5.8 μm or less, 4.8 μm or more and 5.2 μm or less, 5.2 μm or more and 7.0 μm or less, 5.2 μm or more and 6.6 μm or less, 5.2 μm or more and 6.2 μm or less, 5.2 μm or more and 5.8 μm or less, 5.8 μm or more and 7.0 μm or less, 5.8 μm or more and 6.6 μm or less, 5.8 μm or more and 6.2 μm or less, 6.2 μm or more and 7.0 μm or less, 6.2 μm or more and 6.6 μm or less, or 6.6 μm or more and 7.0 μm or less.

[0275] In the first metal layer forming step, as shown in FIG. 18, the first metal layer 21 is formed on the surface of the second metal layer 22 opposite to the mask substrate 15. The first metal layer 21 may be formed by plating in the same manner as the first metal layer forming step shown in FIG. 8. In this case, since the resist layer 55 is formed on the surface of the second metal layer 22 opposite to the mask substrate 15, the components of the plating solution are precipitated in the portion of the body side layer 25 where the resist land 56 of the resist layer 55 is not formed. The components precipitated in this manner form the first metal layer 21. The first metal layer 21 thus formed has a through hole 40 formed therein. That is, the through hole 40 is formed in the first metal layer forming step. The first metal layer 21 may be annealed as described above.

[0276] In the resist layer removing step, as shown in FIG. 19, the resist layer 55 is removed. For example, an alkaline stripping liquid may be used to remove the resist land 56 of the resist layer 55 from the second metal layer 22. After the resist layer 55 is removed, the first metal layer 21 may be polished by chemical mechanical polishing as shown in FIG. 42, which will be described later. In this case, the uniformity of the thickness H3 of the first metal layer 21 can be improved. This can improve the accuracy of the opening dimension S1 (see FIG. 5A) of the through hole 40, and the shape accuracy of the through hole 40 can be improved.

[0277] After the mask layer formation step, as a substrate opening formation step, substrate openings 16 are formed in mask substrate 15 as shown in Fig. 20. The substrate opening formation step shown in Fig. 20 may be performed in the same manner as the substrate opening formation step shown in Figs. 9 to 12.

[0278] After the substrate opening forming step, as shown in FIG. 21, a mask layer opening 22d is formed in the second metal layer 22 as a mask layer opening forming step. For example, a portion of the second metal layer 22 located in the substrate opening 16 in a plan view may be removed by etching. This allows the mask layer opening 22d to be formed. More specifically, the mask layer opening 22d is formed by etching the body side layer 25, the substrate side layer 26, and the intermediate layer 27. The etching solution used in the mask layer opening forming step may be an etching solution that can etch the second metal layer 22 while preventing the first metal layer 21 from being etched. For example, an aluminum mixed acid etching solution may be used as such an etching solution. The body side layer 25, the substrate side layer 26, and the intermediate layer 27 may be immersed in an aluminum mixed acid etching solution at room temperature, for example. For example, when the thickness of each layer 25 to 27 is 100 nm, each layer 25 to 27 may be immersed in the aluminum mixed acid etching solution for 2 minutes. The mixed acid aluminum etching solution may be used without diluting the original solution. For example, the mixed acid aluminum etching solution manufactured by Kanto Chemical Industry Co., Ltd. under the trade name "Mixed Acid Al Etching Solution" may be used as the mixed acid aluminum etching solution.

[0279] In this manner, the through-holes 40 are exposed from the substrate openings 16. In this manner, the deposition mask 10 according to this modified example is obtained.

[0280] In this way, according to the second modification, the through holes 40 can be formed regardless of the type of material of the first metal layer 21. That is, depending on the type of material of the first metal layer 21, such as nickel, laser processing using the laser light L may be difficult. However, the resist layer 55 formed in a pattern corresponding to the through holes 40 allows the through holes 40 to be formed in the first metal layer 21 formed by plating. Therefore, the through holes 40 can be formed regardless of the type of material of the first metal layer 21.

[0281] Next, a third modified example will be described.

[0282] In the above-described embodiment, an example has been described in which the second metal layer 22 includes the body-side layer 25, the substrate-side layer 26, and the intermediate layer 27. However, the present disclosure is not limited to this.

[0283] For example, as shown in Fig. 22A, the second metal layer 22 may include a body-side layer 25 and a substrate-side layer 26, but may not include an intermediate layer 27. The second metal layer 22 may have a two-layer structure. The body-side layer 25 and the substrate-side layer 26 may be configured as layers having specific purposes. In this case, the body-side layer 25 and the substrate-side layer 26 may be in direct contact with each other.

[0284] The body-side layer 25 shown in FIG. 22A may contain a material capable of ensuring adhesion with the first metal layer 21, and may contain, for example, copper. The substrate-side layer 26 may contain a material capable of ensuring adhesion with the mask substrate 15 and suppressing erosion by the etching medium used in the substrate etching step, and may contain, for example, an aluminum alloy containing neodymium. For example, if the substrate-side layer 26 has resistance to the plating solution for forming the first metal layer 21, the body-side layer 25 and the substrate-side layer 26 may be made of such a material. Also, for example, even if the substrate-side layer 26 does not have resistance to the plating solution, the body-side layer 25 and the substrate-side layer 26 may be made of such a material, as long as they have a thickness that can remain in the first metal layer forming step.

[0285] 22A may contain a material capable of protecting the substrate-side layer 26 from the plating solution used in the first metal layer forming step, for example, titanium. The substrate-side layer 26 may contain a material capable of ensuring adhesion to the mask substrate 15 and suppressing erosion by the etching medium used in the substrate etching step, for example, an aluminum alloy containing neodymium. For example, as long as the substrate-side layer 25 can ensure adhesion to the first metal layer 21, the substrate-side layer 25 and the substrate-side layer 26 may be made of such a material.

[0286] 22A may contain a material that ensures adhesion to the first metal layer 21, for example, copper. The substrate-side layer 26 may contain a material that is resistant to the plating solution used in the first metal formation step, for example, titanium. For example, as long as the substrate-side layer 26 is made of a material that ensures adhesion to the mask substrate 15 and can suppress erosion by the etching medium used in the substrate etching step, the substrate-side layer 25 and the substrate-side layer 26 may be made of such a material.

[0287] Also, as shown in FIG. 22B, the second metal layer 22 may be composed of a single metal layer. The single metal layer may be composed of a material having adhesion to the first metal layer 21, adhesion to the mask substrate 15, resistance to the etching medium, and resistance to the plating solution. In this case, the second metal layer 22 may be composed of a material similar to the above-mentioned substrate-side layer 26. In other words, the second metal layer 22 may be composed of only the above-mentioned substrate-side layer 26. In this case, the substrate-side layer 26 is in direct contact with the first metal layer 21 and is in direct contact with the mask substrate 15. In this case, the thickness H10 of the substrate-side layer 26 is formed to a desired thickness H10 as shown in FIG. 22B, thereby suppressing adhesion to the first metal layer 21, adhesion to the mask substrate 15, and erosion by the etching medium. If the thickness H10 can be ensured, the substrate-side layer 26 may be formed by a sputtering process, or may be formed by a deposition process as described later.

[0288] In this case, the thickness H10 of the substrate-side layer 26 may be, for example, 0.6 μm or more, 0.8 μm or more, 1.0 μm or more, or 1.2 μm or more. By setting the thickness H10 to 0.6 μm or more, it is possible to suppress erosion by the etching medium used in the substrate etching process and ensure resistance to the plating solution. Therefore, the body-side layer 25 and the intermediate layer 27 can be omitted. In addition, the thickness H10 may be, for example, 1.4 μm or less, 1.6 μm or less, 1.8 μm or less, or 2.0 μm or less. By setting the thickness H10 to 2.0 μm or less, the substrate-side layer 26 can be efficiently formed by the sputtering process. The range of thickness H10 may be determined by a first group consisting of 0.6 μm, 0.8 μm, 1.0 μm, and 1.2 μm, and / or a second group consisting of 1.4 μm, 1.6 μm, 1.8 μm, and 2.0 μm. The range of thickness H10 may be determined by a combination of any one of the values ​​included in the above-mentioned first group and any one of the values ​​included in the above-mentioned second group. The range of thickness H10 may be determined by a combination of any two of the values ​​included in the above-mentioned first group. The range of thickness H10 may be determined by a combination of any two of the values ​​included in the above-mentioned second group.For example, it may be 0.6 μm or more and 2.0 μm or less, 0.6 μm or more and 1.8 μm or less, 0.6 μm or more and 1.6 μm or less, 0.6 μm or more and 1.4 μm or less, 0.6 μm or more and 1.2 μm or less, 0.6 μm or more and 1.0 μm or less, 0.6 μm or more and 0.8 μm or less, 0.8 μm or more and 2.0 μm or less, 0.8 μm or more and 1.8 μm or less, 0.8 μm or more and 1.6 μm or less, 0.8 μm or more and 1.4 μm or less, 0.8 μm or more and 1.2 μm or less, 0.8 μm or more and 1.0 μm or less, or 1.0 μm or more and 2.0 μm or less. Alternatively, the thickness may be 1.0 μm or more and 1.8 μm or less, 1.0 μm or more and 1.6 μm or less, 1.0 μm or more and 1.4 μm or less, 1.0 μm or more and 1.2 μm or less, 1.2 μm or more and 2.0 μm or less, 1.2 μm or more and 1.8 μm or less, 1.2 μm or more and 1.6 μm or less, 1.2 μm or more and 1.4 μm or less, 1.4 μm or more and 2.0 μm or less, 1.4 μm or more and 1.8 μm or less, 1.4 μm or more and 1.6 μm or less, 1.6 μm or more and 2.0 μm or less, 1.6 μm or more and 1.8 μm or less, or 1.8 μm or more and 2.0 μm or less.

[0289] Next, a fourth modified example will be described.

[0290] In the above-described embodiment, an example has been described in which the second metal layer 22 is formed on the mask substrate 15 by a sputtering process. However, the present disclosure is not limited to this, and the body-side layer 25, the substrate-side layer 26, and the intermediate layer 27 may each be formed by a deposition process such as physical vapor deposition (PVD) or chemical vapor deposition (CVD).

[0291] Next, a fifth modified example will be described.

[0292] In the above-described embodiment, an example in which the through-hole forming step is performed after the substrate opening forming step has been described. However, the present disclosure is not limited to this, and the through-hole forming step may be performed before the substrate opening forming step. In this case, the laser light L may be irradiated onto the first surface 20a of the mask layer 20. The wall surface 41 of the through-hole 40 may be formed perpendicular to the first surface 20a (the above-described angle θ is 90°). Such a deposition mask 10 may be used in the above-described surface deposition type deposition apparatus.

[0293] Next, a sixth modified example will be described.

[0294] In the above-described embodiment, an example has been described in which the first metal layer 21 of the mask layer 20 is formed by plating. However, the present disclosure is not limited to this. For example, the first metal layer 21 may be formed on and attached to the second metal layer 22 by sputtering. In this case, a metal layer similar to the above-described substrate-side layer 26 may be provided as the second metal layer between the first metal layer 21 formed by sputtering and the mask substrate 15.

[0295] Next, a seventh modified example will be described.

[0296] In the above-described embodiment, an example in which the through-hole 40 is formed by irradiating the first metal layer 21 and the second metal layer 22 with the laser light L has been described. However, the present disclosure is not limited to this, and the through-hole 40 may be formed by etching the first metal layer 21 and the second metal layer 22. In this case, for example, the through-hole 40 penetrating the mask layer 20 may be formed by etching an area not covered by a patterned resist (not shown). In the case of wet etching, for example, a solution containing a ferric chloride solution and hydrochloric acid may be used as the etching solution. The temperature of the etching solution is, for example, 25° C. or more and 80° C. or less. In the case of dry etching, methane gas (CH4), carbon dioxide gas (CO2), or the like may be used as the etching gas.

[0297] Next, an eighth modified example will be described.

[0298] In the above-described embodiment, an example has been described in which the first alignment mark 45 for aligning with the deposition substrate 110 is provided on the substrate frame 17 of the mask substrate 15. However, the present disclosure is not limited to this. For example, as shown in FIG. 23, the mask substrate 15 may include an inner protrusion 19 extending inward from the substrate frame 17 in a plan view, and the first alignment mark 45 may be located on the inner protrusion 19. The inner protrusion 19 may include a sidewall 19a facing the adjacent through-hole groups 30 in the first direction D11 and a sidewall 19b facing the adjacent through-hole groups 30 in the second direction D12. In a plan view, the sidewall 19a may extend in the second direction D12, and the sidewall 19b may extend in the first direction D11. By providing the first alignment mark 45 on the inner protrusion 19, the first alignment mark 45 can be disposed at a position close to the through-hole group 30, and the alignment accuracy of the through-holes 40 can be improved.

[0299] Next, a ninth modified example will be described.

[0300] In the above-described embodiment, an example has been described in which the second alignment mark 46 for aligning with the deposition substrate 110 is provided at each intersection 29 where the first mask rail 28a and the second mask rail 28b of the mask layer 20 intersect. However, the present disclosure is not limited to this, and as shown in FIG. 24, the second alignment mark 46 does not have to be provided at all intersections 29. For example, the second alignment mark 46 may be arranged for each of a plurality of through-hole groups 30 in the first direction D11. In FIG. 24, the second alignment mark 46 is arranged for each of two through-hole groups 30 in each of the first direction D11 and the second direction D12. More specifically, the second alignment mark 46 may be arranged on one of two first mask rails 28a adjacent to each other in the first direction D11, and the second alignment mark 46 may not be arranged on the other. The second alignment mark 46 may be arranged on one of two second mask bars 28b adjacent to each other in the second direction D12, and the second alignment mark 46 may not be arranged on the other. In this case, the second alignment mark 46 is arranged at a position corresponding to the corner of the four through-hole groups 30.

[0301] Although not shown, the second alignment mark 46 may be provided on the substrate crosspieces 18a and 18b (see FIGS. 25 and 26) of the mask substrate 15, described later, instead of the mask layer 20. When the second alignment mark 46 is formed in a concave shape, it may be formed on the second substrate surface 15b of the substrate crosspieces 18a and 18b. In this case, the second alignment mark 46 can be visually recognized through the deposition substrate 110 and the mask layer 20 by irradiating infrared light. The second alignment mark 46 may be disposed at a position similar to the second alignment mark 46 shown in FIG. 3 in a plan view, or may be disposed at a position similar to the second alignment mark 46 shown in FIG. 24, and is arbitrary. Such a concave second alignment mark 46 may be formed by etching the second substrate surface 15b on the substrate crosspieces 18a and 18b in a substrate etching process.

[0302] Next, a tenth modified example will be described.

[0303] In the above-described embodiment, an example in which all the through-hole groups 30 are located within one substrate opening 16 of the mask substrate 15 has been described. However, the present disclosure is not limited to this, and the mask substrate 15 may have a plurality of substrate openings 16. For example, as shown in FIG. 25 and FIG. 26, substrate crosspieces 18a, 18b may be provided between adjacent substrate openings 16. The substrate crosspieces 18a, 18b may include a first substrate crosspiece 18a arranged in a first direction D11 and a second substrate crosspiece 18b arranged in a second direction D12. The first substrate crosspiece 18a may extend in the second direction D12. The first substrate crosspiece 18a may overlap the first mask crosspiece 28a described above in a plan view. The second substrate crosspiece 18b may extend in the first direction D11. The second substrate crosspiece 18b may overlap the second mask crosspiece 28b described above in a plan view. FIG. 26 is a diagram that shows a schematic cross section taken along line CC in FIG. 25, and in order to make the drawing easier to understand, the number of through-hole groups 30 and the number of through-holes 40 are reduced.

[0304] In the example shown in FIG. 25 and FIG. 26, one corresponding through-hole group 30 (or effective area 23) is located in each board opening 16. The board opening 16 shown in FIG. 25 and FIG. 26 may have a shape that follows the outline of one corresponding through-hole group 30 (or corresponding effective area 23). The board crosspieces 18a, 18b are connected to the board frame 17 and are located between the adjacent through-hole groups 30 in a plan view. FIG. 26 shows the first board crosspiece 18a, which extends in a direction perpendicular to the paper surface. Both ends of the first board crosspiece 18a are continuously connected to the board frame 17. Although not shown in FIG. 26, the second board crosspiece 18b extends in the left-right direction in FIG. 26. Both ends of the second board crosspiece 18b are continuously connected to the board frame 17. In this way, in plan view, a plurality of board openings 16 are defined by first board rails 18a extending in the second direction D12 and second board rails 18b extending in the first direction D11.

[0305] In the example shown in Fig. 25, the substrate opening 16 has a substantially rectangular contour in a plan view. Here, the four corners of the contour of the substrate opening 16 may be formed by directly intersecting a side 16f (see Fig. 27) that extends in the first direction D11 and a side 16g that extends in the second direction D12, which form the contour of the substrate opening 16. However, a contour of a slight curved shape that is formed unintentionally may be interposed between these sides. However, the present disclosure is not limited to this.

[0306] For example, as shown in Fig. 27, the board opening 16 may have curved portions 16e at the four corners of the outline of the board opening 16, which is substantially rectangular in plan view. The curved portions 16e are portions that connect, in a curved manner, a side 16f extending in the first direction D11 and a side 16g extending in the second direction D12 of the outline of the board opening 16. The curved portions 16e may be intentionally formed to have a curved outline. The curved portions 16e may be formed, for example, in an arc shape. Such curved portions 16e may be included in the board openings 16 shown in Figs. 29 to 31.

[0307] The radius R of the curved portion 16e shown in FIG. 27 may be, for example, 0.3 mm or more, 0.6 mm or more, 0.9 mm or more, or 1.2 mm or more. By setting the radius R to 0.3 mm or more, it is possible to suppress the concentration of stress at the four corners of the board opening 16. In addition, the radius R may be, for example, 1.5 mm or less, 2.0 mm or less, 2.5 mm or less, or 3.0 mm or less. By setting the radius R to 3.0 mm or less, it is possible to suppress the number of through holes 40 that can be arranged in the board opening 16 from being limited. The range of the radius R may be determined by a first group consisting of 0.3 mm, 0.6 mm, 0.9 mm, and 1.2 mm, and / or a second group consisting of 1.5 mm, 2.0 mm, 2.5 mm, and 3.0 mm. The range of the radius R may be determined by a combination of any one of the values ​​included in the first group described above and any one of the values ​​included in the second group described above. The range of the radius R may be determined by a combination of any two of the values ​​included in the first group described above. The range of the radius R may be determined by a combination of any two of the values ​​included in the second group described above.For example, it may be 0.3 mm or more and 3.0 mm or less, 0.3 mm or more and 2.5 mm or less, 0.3 mm or more and 2.0 mm or less, 0.3 mm or more and 1.5 mm or less, 0.3 mm or more and 1.2 mm or less, 0.3 mm or more and 0.9 mm or less, 0.3 mm or more and 0.6 mm or less, 0.6 mm or more and 3.0 mm or less, 0.6 mm or more and 2.5 mm or less, 0.6 mm or more and 2.0 mm or less, 0.6 mm or more and 1.5 mm or less, 0.6 mm or more and 1.2 mm or less, 0.6 mm or more and 0.9 mm or less, or 0.9 mm or more and 3.0 mm or less. Alternatively, the thickness may be 0.9 mm or more and 2.5 mm or less, 0.9 mm or more and 2.0 mm or less, 0.9 mm or more and 1.5 mm or less, 0.9 mm or more and 1.2 mm or less, 1.2 mm or more and 3.0 mm or less, 1.2 mm or more and 2.5 mm or less, 1.2 mm or more and 2.0 mm or less, 1.2 mm or more and 1.5 mm or less, 1.5 mm or more and 3.0 mm or less, 1.5 mm or more and 2.5 mm or less, 1.5 mm or more and 2.0 mm or less, 2.0 mm or more and 3.0 mm or less, 2.0 mm or more and 2.5 mm or less, or 2.5 mm or more and 3.0 mm or less.

[0308] Furthermore, the substrate opening 16 may have a circular outline in plan view as shown in Fig. 28. In the substrate etching step shown in Fig. 10, the portions of the mask substrate 15 corresponding to the substrate crosspieces 18a, 18b are left unetched, thereby forming the substrate crosspieces 18a, 18b.

[0309] Since the mask substrate 15 has a plurality of substrate openings 16 in this manner, the mask layer 20 can be supported by the material of the mask substrate 15 (substrate crosspieces 18a, 18b) remaining between the substrate openings 16. This makes it possible to improve the mechanical strength of the deposition mask 10.

[0310] In addition, when the mask substrate 15 has a plurality of substrate openings 16, as shown in FIG. 25 to FIG. 27, it is not limited to one through hole group 30 being located in one substrate opening 16. For example, as shown in FIG. 29, two or more through hole groups 30 (or effective areas 23) may be located in one substrate opening 16. FIG. 29 shows an example in which four through hole groups 30 are located in one substrate opening 16. Alternatively, it is not limited to all of the through holes 40 constituting one through hole group 30 being located in one substrate opening 16. For example, one through hole group 30 may straddle two or more substrate openings 16 in a plan view. For example, as shown in FIG. 30, one through hole 40 may be located in one substrate opening 16. In the example shown in FIG. 30, a substrate opening 16 is provided for each through hole 40. Also, as shown in FIG. 31, two or more through holes 40 may be located in one substrate opening 16. In the example shown in FIG. 31, two through holes 40 are positioned within one substrate opening 16. In the example shown in FIG.

[0311] Next, an eleventh modified example will be described.

[0312] In the above-described embodiment, an example has been described in which the deposition mask 10 includes the mask layer 20 and the mask substrate 15. However, the present disclosure is not limited to this. For example, as shown in Figs. 32 and 33, the mask substrate 15 may be supported by a frame 201. In this case, the deposition mask 10 and the frame 201 may form a framed deposition mask 200.

[0313] More specifically, the framed deposition mask 200 includes a deposition mask 10 and a frame 201 that supports the mask substrate 15 of the deposition mask 10. The frame 201 may be attached to the mask substrate 15 of the deposition mask 10 so that it can be held when handling the deposition mask 10, for example, when moving the deposition mask 10. This allows the deposition mask 10 to be handled while holding the frame 201, and damage to the deposition mask 10 can be suppressed. As a result, the handling of the deposition mask 10 can be improved.

[0314] The frame 201 may include a first frame surface 201a and a second frame surface 201b. The first frame surface 201a faces the mask substrate 15 and faces a second substrate surface 15b of the mask substrate 15. The second frame surface 201b is located on the opposite side to the first frame surface 201a. The first frame surface 201a is connected to the substrate frame 17 of the mask substrate 15. In a plan view, the frame 201 does not overlap the substrate opening 16. In a plan view, at least a part of the frame 201 extends outward beyond the outer edge 15c of the mask substrate 15. This forms an area for gripping the frame 201 when handling the deposition mask 10. In the example shown in FIG. 32, the frame 201 extends outward as a whole beyond the outer edge 15c of the mask substrate 15.

[0315] The frame 201 may include a glass material or a metal material. The glass material may be quartz glass, borosilicate glass, alkali-free glass, soda glass, or the like. The metal material may be an invar material, aluminum, or stainless steel such as SUS430 or SUS304. By using such a material for the frame 201, the rigidity of the frame 201 can be made higher than that of the mask substrate 15. The frame 201 may include a silicon or resin material. The material of the frame 201 may be determined so that the frame 201 has a required rigidity, taking into consideration the gripping force of an operator or a robot hand handling the framed deposition mask 200.

[0316] The thermal expansion coefficient of the frame 201 may be equal to or close to the thermal expansion coefficient of the mask substrate 15. This allows the frame 201 and the mask substrate 15 to have approximately the same elongation rate when the framed deposition mask 200 is heated. As a result, damage to the mask substrate 15 can be suppressed. In addition, the positional accuracy of the through-holes 40 can be improved, and the deposition accuracy can be improved. More specifically, the absolute value of the difference between the thermal expansion coefficient of the frame 201 and the thermal expansion coefficient of the mask substrate 15 may be 15 ppm / °C or less, 10 ppm / °C or less, or 5.0 ppm / °C or less. The material of the frame 201 may be a material with high thermal conductivity. In this case, the deposition mask 10 can be efficiently cooled.

[0317] In the illustrated example, the frame 201 is formed in an annular shape. The frame 201 can be formed in an annular shape at a portion located outside the outer edge 15c of the mask substrate 15 in a plan view. This can effectively prevent the substrate frame 17 of the mask substrate 15 from being damaged when the deposition mask 10 is handled. More specifically, a frame opening 202 is formed in the center of the frame 201, extending from the first frame surface 201a to the second frame surface 201b and penetrating the frame 201. In the illustrated example, the planar shape of the frame opening 202 is similar to the planar shape of the outer edge 15c of the mask substrate 15. In the illustrated example, the mask substrate 15 includes the above-mentioned first substrate rail 18a and second substrate rail 18b in the same manner as in the examples shown in FIGS. 25 and 26, and a plurality of substrate openings 16 are defined by the substrate rails 18a and 18b. In a plan view, the frame opening 202 overlaps with the first board rail 18a and the second board rail 18b of the mask board 15.

[0318] The outer edge 201c of the frame 201 may have any planar shape. In the illustrated example, the outer edge 201c of the frame 201 is formed in a rectangular shape when seen in a plan view, but may be formed in another polygonal shape, a circular shape, or the like.

[0319] In the above-described eleventh modified example, the mask substrate 15 of the deposition mask 10 according to the tenth modified example shown in FIGS. 25 and 26 is supported by the frame 201. However, the present disclosure is not limited to this. The mask substrate 15 of the deposition mask 10 shown in FIG. 3 may be supported by the frame 201, or the mask substrate 15 of the deposition mask 10 shown in other modified examples may be supported by the frame 201. For example, the mask layer opening 22d may not be formed in the second metal layer 22 shown in FIG. 33, and the second metal layer 22 may include the opening region 22b (see FIG. 3).

[0320] Next, a twelfth modified example will be described.

[0321] In the above-described embodiment, an example has been described in which the outer edge 21c of the first metal layer 21 is located at a position overlapping the outer edge 22c of the second metal layer 22 in a plan view. However, the present disclosure is not limited to this. For example, as shown in FIG. 34, the outer edge 21c of the first metal layer 21 may be located inside the outer edge 22c of the second metal layer 22. In other words, the second metal layer 22 extends outward beyond the outer edge 21c of the first metal layer 21 and is exposed. This allows the first metal layer 21 and the second metal layer 22 to form a step, and the thickness H3 of the first metal layer 21 (see FIG. 3) can be easily measured. In a plan view, a part of the second metal layer 22 may extend outward beyond the outer edge 21c of the first metal layer 21. In this case, a step can be formed in a part of the outer edge 21c of the first metal layer 21 in a plan view. However, in a plan view, the second metal layer 22 may entirely extend outward beyond the outer edge 21c of the first metal layer 21. In this case, a step can be formed around the entire periphery of the outer edge 21c of the first metal layer 21 in a plan view.

[0322] In the first metal layer forming step of forming such a first metal layer 21, a resist layer (not shown) may be formed in advance on the surface of the second metal layer 22 opposite to the mask substrate 15. This resist layer is located in a region close to the outer edge 22c of the second metal layer 22. This allows the first metal layer 21 including the outer edge 21c described above to be formed.

[0323] In this manner, the outer edge 21c of the first metal layer 21 is located inside the outer edge 22c of the second metal layer 22, so that the thickness H3 of the first metal layer 21 can be easily measured.

[0324] In the above-described twelfth modified example, an example has been described in which the outer edge 21c of the first metal layer 21 of the deposition mask 10 according to the tenth modified example shown in FIGS. 25 and 26 is located inside the outer edge 22c of the second metal layer 22. However, the present disclosure is not limited to this. For example, the outer edge 21c of the first metal layer 21 of the deposition mask 10 shown in FIG. 3 may be located inside the outer edge 22c of the second metal layer 22, and the outer edge 21c of the first metal layer 21 of the deposition mask 10 shown in another modified example may be located inside the outer edge 22c of the second metal layer 22. For example, the mask layer opening 22d may not be formed in the second metal layer 22 shown in FIG. 34, and the second metal layer 22 may include the opening region portion 22b (see FIG. 3).

[0325] Next, a thirteenth modified example will be described.

[0326] In the above-described embodiment, an example has been described in which the mask bars 28a, 28b of the first metal layer 21 are formed on the first board bar 18a and the second board bar 18b of the mask substrate 15. However, the present disclosure is not limited to this. For example, as shown in Figs. 35 and 36, metal grooves 210a, 210b may be formed in the mask bars 28a, 28b of the first metal layer 21. The metal grooves 210a, 210b may penetrate the first metal layer 21. The metal grooves 210a, 210b do not have to be formed in the second metal layer 22.

[0327] As shown in FIG. 35 and FIG. 36, a plurality of first metal grooves 210a and a plurality of second metal grooves 210b may be formed in the first metal layer 21. The first metal groove 210a may be formed in the first mask rail 28a and may be located at a position overlapping the first substrate rail 18a in a plan view. The first metal groove 210a may extend in the second direction D12 or may be arranged in the first direction D11. The second metal groove 210b may be formed in the second mask rail 28b and may be located at a position overlapping the second substrate rail 18b in a plan view. The second metal groove 210b may extend in the first direction D11 or may be arranged in the second direction D12.

[0328] In the example shown in FIG. 35 and FIG. 36, the first metal layer 21 may include a plurality of metal islands 211. The metal island 211 is an example of a main body island. The metal island 211 may be partitioned by the first metal groove 210a and the second metal groove 210b. The metal island 211 may be formed for each through hole group 30 (or the effective area 23). One through hole group 30 may be formed in one metal island 211. Alternatively, two or more through hole groups 30 may be located in one metal island 211. The metal island 211 may be formed in a rectangular shape in a plan view. In the example shown in FIG. 35, a plurality of metal islands 211 are formed on the second metal layer 22. The first metal layer 21 may not be formed further outside the metal island 211 located at the outermost position in a plan view among the plurality of metal islands 211. In this case, the second metal layer 22 is exposed, and the first metal layer 21 and the second metal layer 22 form a step similar to that in FIG.

[0329] The metal grooves 210a, 210b may be formed by etching the first metal layer 21. Alternatively, the metal grooves 210a, 210b may be formed by irradiating the first metal layer 21 with laser light.

[0330] In this manner, the metal grooves 210a and 210b are formed in the first metal layer 21, thereby dividing the first metal layer 21. Therefore, warping occurring in the first metal layer 21 can be divided, and warping of the deposition mask 10 can be suppressed.

[0331] In the above-mentioned thirteenth modified example, an example in which the metal grooves 210a, 210b are formed in the first metal layer 21 of the deposition mask 10 according to the tenth modified example shown in FIG. 25 and FIG. 26 has been described. However, the present disclosure is not limited to this. For example, the metal grooves 210a, 210b may be formed in the first metal layer 21 of the deposition mask 10 shown in FIG. 3, or the metal grooves 210a, 210b may be formed in the first metal layer 21 of the deposition mask 10 shown in other modified examples. For example, the mask layer opening 22d may not be formed in the second metal layer 22 shown in FIG. 36, and the second metal layer 22 may include the opening region portion 22b (see FIG. 3).

[0332] Next, a fourteenth modified example will be described.

[0333] In the above-mentioned thirteenth modification, an example has been described in which the metal grooves 210a, 210b are formed in the first metal layer 21. However, the present disclosure is not limited to this. For example, as shown in Figs. 37 and 38, a mask insulating layer 220 may be formed in the metal grooves 210a, 210b.

[0334] More specifically, the mask layer 20 of the deposition mask 10 shown in FIGS. 37 and 38 may include a mask insulating layer 220. The mask insulating layer 220 is located on the first surface 20a side of the mask layer 20. The mask insulating layer 220 may be a layer forming the first surface 20a. The mask insulating layer 220 may be located between two adjacent metal islands 211. In other words, the mask insulating layer 220 may be located between two adjacent through-hole groups 30 (or effective areas 23). The mask insulating layer 220 may penetrate the first metal layer 21.

[0335] More specifically, the mask insulating layer 220 is formed in each of the first metal grooves 210a of the first metal layer 21, and is also formed in each of the second metal grooves 210b. In other words, the mask insulating layer 220 is formed between the two adjacent metal islands 211 described above. The mask insulating layer 220 is also formed outside the metal island 211 that is located at the outermost position in a plan view among the multiple metal islands 211. In this way, the mask insulating layer 220 is formed around the metal island 211. The mask insulating layer 220 may be formed continuously without being divided.

[0336] The thickness H11 of the mask insulating layer 220 may be the same as the above-mentioned thickness H3 (see FIG. 3) of the first metal layer 21, or the difference between the thickness H11 and the thickness H3 may be 1.0 μm or less.

[0337] The mask insulating layer 220 may have a different property with respect to stress from the first metal layer 21. For example, when the first metal layer 21 applies a tensile stress to the mask substrate 15, the mask insulating layer 220 may be configured to apply a compressive stress to the mask substrate 15. In this case, the mask insulating layer 220 can at least partially cancel the force that the first metal layer 21 applies to the mask substrate 15. For this reason, it is possible to suppress the occurrence of warping of the deposition mask 10. The material of the mask insulating layer 220 may have insulating properties. For example, the mask insulating layer 220 may contain an oxide having insulating properties. The oxide may be, for example, silicon oxide or silicon dioxide.

[0338] Next, a method for manufacturing the deposition mask 10 shown in FIGS. 37 and 38 will be described.

[0339] First, the mask substrate 15 having the second metal layer 22 formed thereon is prepared by the second metal layer forming step shown in FIG.

[0340] 39, in an insulating layer forming step, a mask insulating layer 220 is formed on the second metal layer 22. The mask insulating layer 220 may be formed on the entire surface of the second metal layer 22 opposite to the mask substrate 15. The mask insulating layer 220 may be formed by chemical vapor deposition. For example, the mask insulating layer 220 is formed by chemical vapor deposition using tetraethyl silicate Si(OC2H5)4 as a raw material. Tetraethyl silicate is also called TEOS.

[0341] After the insulating layer forming step, as shown in FIG. 40, a plurality of insulating openings 221 are formed in the mask insulating layer 220 as an insulating opening forming step. The insulating openings 221 may be aligned in the first direction D11 and the second direction D12. The insulating openings 221 have an outline corresponding to the metal island 211 of the first metal layer 21 in a plan view. The planar shape of the outline of the insulating opening 221 may be rectangular. Although not shown, the four corners of the outline of the insulating opening 221 may be curved. The outline of the insulating opening 221 may be other shapes such as a circle. The outline of the insulating opening 221 may be configured to surround the outline of the substrate opening 16 to be formed in a later step. The planar shape of the outline of the insulating opening 221 may be similar to the planar shape of the outline of the substrate opening 16.

[0342] The mask insulating layer 220 may include an insulating frame 222 having a planar shape that follows the outer edge 220c of the mask insulating layer 220, and insulating bars 223a, 223b that define the contour of the insulating opening 221. The insulating frame 222 is an example of an insulating main body. The insulating opening 221 may be defined inside the insulating frame 222.

[0343] The insulating bars 223a, 223b may include a first insulating bar 223a arranged in the first direction D11 and a second insulating bar 223b arranged in the second direction D12. The first insulating bar 223a may extend in the second direction D12. The first insulating bar 223a may overlap the first board bar 18a described above in a plan view. The second insulating bar 223b may extend in the first direction D11. The second insulating bar 223b may overlap the second board bar 18b described above in a plan view. The insulating bars 223a, 223b may penetrate the first metal layer 21.

[0344] The insulating bars 223a and 223b are connected to the insulating frame 222. In plan view, the insulating bars 223a and 223b are located between adjacent insulating openings 221. FIG. 38 shows the first insulating bar 223a, which extends in a direction perpendicular to the paper surface. Both ends of the first insulating bar 223a are continuously connected to the insulating frame 222. Although not shown in FIG. 38, the second insulating bar 223b extends in the left-right direction in FIG. 38. Both ends of the second insulating bar 223b are continuously connected to the insulating frame 222. In this way, a plurality of insulating openings 221 are defined by the first insulating bar 223a extending in the second direction D12 and the second insulating bar 223b extending in the first direction D11 in plan view.

[0345] As shown in FIG. 40, the mask insulating layer 220 may include a plurality of insulating islands 224 located within the insulating openings 221. The above-mentioned through holes 40 of the mask layer 20 are formed at the positions of the insulating islands 224. The method of forming the insulating openings 221 in the mask insulating layer 220 is not particularly limited. For example, the insulating openings 221 may be formed by dry etching using an etching gas. The dry etching may be reactive ion etching.

[0346] After the insulating layer forming step, as shown in FIG. 41, the first metal layer 21 is formed in the insulating opening 221 as a first metal layer forming step. More specifically, the first metal layer 21 is formed on the surface of the second metal layer 22 opposite to the mask substrate 15. The first metal layer 21 may be formed by plating in the same manner as the first metal layer forming step shown in FIG. 8 and FIG. 18. In this case, components of a plating solution are precipitated in a portion of the insulating opening 221 of the mask insulating layer 220 where the insulating island 224 is not formed. The components precipitated in this manner form the metal island 211 of the first metal layer 21 on the second metal layer 22. The through hole 40 is formed in the metal island 211 formed in this manner so as to correspond to the insulating island 224. That is, the through hole 40 is formed in the first metal layer forming step. The metal island 211 of the first metal layer 21 may protrude upward from the insulating opening 221 in the thickness direction D2 of the mask layer 20.

[0347] After the first metal layer 21 is formed, the first metal layer 21 may be annealed in the same manner as the first metal layer forming step shown in FIG.

[0348] After the first metal layer forming step, the first metal layer 21 may be polished by chemical mechanical polishing as shown in Fig. 42 as a polishing step. The polishing step may be performed until the polishing surface of the polishing tool reaches the surface of the mask insulating layer 220 opposite to the second metal layer 22 in the thickness direction D2. This allows the surface of the first metal layer 21 opposite to the second metal layer 22 to be positioned on the same plane as the surface of the mask insulating layer 220 opposite to the second metal layer 22. The uniformity of the thickness H3 of the first metal layer 21 can be improved, and the flatness of the first surface 20a of the mask layer 20 can be improved.

[0349] After the polishing step, a part of the mask insulating layer 220 is removed as an insulating layer removing step. In the insulating layer removing step, a first mask protective layer 225 may be formed to cover the insulating frame 222 and the insulating bars 223a, 223b of the mask insulating layer 220 as a first mask protective layer forming step, as shown in FIG. 43. The first mask protective layer 225 may not cover the insulating islands 224. The first mask protective layer 225 may not cover the first metal layer 21 surrounding the multiple insulating islands 224.

[0350] The first mask protective layer 225 may be resistant to an etching solution for removing the mask insulating layer 220. For example, when the etching solution contains buffered hydrofluoric acid, the first mask protective layer 225 may contain a resin resistant to hydrofluoric acid. For example, the first mask protective layer 225 may contain a photoresist resistant to hydrofluoric acid. The photoresist may contain polyimide or the like. The buffered hydrofluoric acid solution may be a solution containing hydrofluoric acid and ammonium fluoride.

[0351] Next, in the insulating layer removal step, the mask insulating layer 220 is immersed in an etching solution such as a buffered hydrofluoric acid solution. This removes a plurality of insulating islands 224 that are not covered by the first mask protective layer 225, as shown in Fig. 44. Thereafter, the first mask protective layer 225 may be removed.

[0352] After the insulating layer removing step, a substrate opening 16 is formed in the mask substrate 15 as a substrate opening forming step. In the substrate opening forming step, as shown in Fig. 45, a resist layer 50 may be formed on the second substrate surface 15b of the mask substrate 15 in the same manner as in the resist layer forming step shown in Fig. 9. As shown in Fig. 45, a second mask protective layer 226 that covers the first metal layer 21 and the mask insulating layer 220 may be formed as a second mask protective layer forming step.

[0353] Subsequently, as a substrate opening forming step, as shown in FIG. 46, the mask substrate 15 may be etched in the same manner as in the substrate etching step shown in FIG. 10 to form a substrate opening 16.

[0354] After the substrate opening forming step, as a mask layer opening forming step, mask layer openings 22d are formed in second metal layer 22 as shown in Fig. 47. In the mask layer opening forming step, second metal layer 22 may be etched to form mask layer openings 22d in the same manner as in the mask layer opening forming step shown in Fig. 21.

[0355] After the mask layer opening formation step, as a second protective layer removal step, the resist layer 50 and the second mask protective layer 226 may be removed as shown in FIG.

[0356] In this manner, the deposition mask 10 shown in FIGS. 37 and 38 is obtained.

[0357] The first metal layer 21 may be formed on the mask substrate 15 in an environment that is higher than room temperature. For example, a plating step or an annealing step is performed in an environment that is higher than room temperature. When the temperatures of the mask substrate 15 and the first metal layer 21 drop to room temperature, the mask substrate 15 and the first metal layer 21 shrink. When the thermal expansion coefficient of the first metal layer 21 is larger than that of the mask substrate 15, the amount of shrinkage of the first metal layer 21 is larger than the amount of shrinkage of the mask substrate 15. Therefore, the first metal layer 21 applies a tensile stress to the mask substrate 15.

[0358] The mask insulating layer 220 is formed on the mask substrate 15 in an environment that is higher than room temperature. For example, a chemical vapor deposition process is performed in an environment that is higher than room temperature. When the temperatures of the mask substrate 15 and the mask insulating layer 220 are lowered to room temperature, the mask substrate 15 and the mask insulating layer 220 shrink. When the thermal expansion coefficient of the mask insulating layer 220 is smaller than that of the mask substrate 15, the amount of shrinkage of the mask insulating layer 220 is smaller than that of the mask substrate 15. Therefore, the mask insulating layer 220 applies a compressive stress to the mask substrate 15.

[0359] 37 and 38, a first metal layer 21 and a mask insulating layer 220 are formed on a mask substrate 15. Therefore, the compressive stress applied to the mask substrate 15 by the mask insulating layer 220 can at least partially cancel out the tensile stress applied to the mask substrate 15 by the first metal layer 21. As a result, warping of the deposition mask 10 can be suppressed.

[0360] In the first metal layer forming step shown in Fig. 41 described above, the first metal layer 21 may be formed by a process other than plating. For example, the first metal layer 21 may be formed by a physical film formation method. The physical film formation method may be a sputtering method, a vapor deposition method, an ion plating method, or the like. In the physical film formation step, the first metal layer 21 may be formed not only in the insulating opening 221 but also on the insulating frame 222 of the mask insulating layer 220 and on the insulating rails 223a and 223b.

[0361] An oxide film may be formed on the first substrate surface 15a and the second substrate surface 15b of the mask substrate 15 prepared before the insulating layer forming step shown in Fig. 39 described above. The oxide film may be formed by subjecting the mask substrate 15 to a thermal oxidation treatment. The thermal oxidation treatment is a treatment in which the first substrate surface 15a and the second substrate surface 15b of the mask substrate 15 are oxidized by heating the mask substrate 15. The oxide film formed on the second substrate surface 15b may be removed after the first metal layer forming step.

[0362] Next, a fifteenth modified example will be described.

[0363] In the above-mentioned fourteenth modification, an example has been described in which the mask insulating layer 220 includes the first insulating bar 223a and the second insulating bar 223b. However, the present disclosure is not limited to this. For example, as shown in FIG. 49, the mask insulating layer 220 does not have to include the first insulating bar 223a and the second insulating bar 223b. The mask insulating layer 220 does not have to include the insulating frame 222, or may include the insulating frame 222.

[0364] More specifically, as shown in FIG. 49, the first metal layer 21 may have a crosspiece through hole 42 located on the board crosspieces 18a, 18b of the mask substrate 15. The crosspiece through hole 42 does not have to overlap with the board opening 16 of the mask substrate 15 in a plan view. The crosspiece through hole 42 may be located between two adjacent through hole groups 30 (or effective areas 23). The crosspiece through hole 42 may be configured similarly to the through hole 40. The crosspiece through hole 42 may penetrate the first metal layer 21.

[0365] The mask insulating layer 220 may include a plurality of insulating batten islands 227 located in the corresponding batten through holes 42 described above. The insulating batten islands 227 may be embedded in the batten through holes 42. The insulating batten islands 227 may be located between two adjacent metal islands 211. The insulating batten islands 227 may penetrate the first metal layer 21.

[0366] The insulating rail island 227 is formed at a position corresponding to the substrate rails 18a, 18b of the mask substrate 15 in the insulating layer forming step shown in FIG. 40 described above. The insulating rail island 227 may have a shape similar to that of the insulating island 224 described above. In the first mask protective layer forming step shown in FIG. 43, a first mask protective layer 225 is formed on the insulating rail island 227. Thereafter, the steps shown in FIGS. 44 to 48 are performed to obtain the deposition mask 10 on which the insulating rail islands 227 located on the substrate rails 18a, 18b are formed.

[0367] In this modification, the first metal layer 21 has crosspiece through holes 42 located on the substrate crosspieces 18a, 18b of the mask substrate 15. This allows the region between two adjacent through hole groups 30 in the first metal layer 21 to be formed in the same structure as the first metal layer 21 in the through hole group 30 (or the effective region 23). This allows the uniformity of the structure of the first metal layer 21 to be improved. As a result, the uniformity of the plating power supply current can be improved, and the uniformity of the thickness H3 of the first metal layer 21 can be improved. In the polishing process described above, the uniformity of the chemical mechanical polishing of the first metal layer 21 can be improved.

[0368] Next, a sixteenth modified example will be described.

[0369] In the above-described fourteenth modification, an example has been described in which the first metal layer 21 includes a plurality of metal islands 211. However, the present disclosure is not limited to this. For example, as shown in Figs. 50 and 51, the first metal layer 21 may include a dummy metal island 230.

[0370] More specifically, in the example shown in FIG. 50 and FIG. 51, the first metal layer 21 includes a plurality of metal islands 211 and a plurality of dummy metal islands 230. The through holes 40 located in the metal islands 211 overlap the substrate openings 16. The dummy metal islands 230 are an example of dummy body islands. In a plan view, the dummy metal islands 230 are located between the metal islands 211 and the outer edge 15c of the mask substrate 15. The dummy metal islands 230 may be located at positions that do not overlap the substrate openings 16 of the mask substrate 15 in a plan view. The dummy metal islands 230 may overlap the substrate frame 17 of the mask substrate 15.

[0371] A dummy through hole 43 penetrating the first metal layer 21 may be formed in the dummy metal island 230. The dummy through hole 43 does not need to overlap the substrate opening 16 of the mask substrate 15 in a plan view, and may overlap the substrate frame 17.

[0372] The dummy metal island 230 may be separated from the adjacent metal island 211 in a plan view. A mask insulating layer 220 may be located between the dummy metal island 230 and the metal island 211. However, the dummy metal island 230 and the metal island 211 adjacent to each other may be connected to each other or may be formed continuously.

[0373] When the first metal layer 21 is polished by chemical mechanical polishing as in the above-described polishing step shown in Fig. 42, the thickness H3 of the first metal layer 21 after polishing may vary depending on the position. For example, when a plurality of metal islands 211 are formed on the mask substrate 15, the thickness of the metal island 211 close to the outer edge 15c of the mask substrate 15 may be greater than the thickness of the metal island 211 close to the center point of the mask substrate 15. In other words, the metal island 211 close to the outer edge 15c of the mask substrate 15 may not be polished sufficiently.

[0374] In this modification, the dummy metal island 230 is located outside the metal island 211 in a plan view. As a result, an insufficiently polished region is more likely to occur in the dummy metal island 230 than in the metal island 211. Therefore, according to this modification, it is possible to prevent the metal island 211 from being insufficiently polished. In addition, in the above-mentioned first metal layer forming step, the first metal layer 21 can be formed even in a region of the mask substrate 15 that overlaps with the substrate frame 17. Therefore, the first metal layer 21 can be formed in a wide region on the surface of the second metal layer 22 opposite to the mask substrate 15. In this case, it is possible to improve the uniformity of the plating power supply current and improve the uniformity of the thickness H3 of the first metal layer 21. In the above-mentioned polishing step, it is possible to improve the uniformity of the chemical mechanical polishing of the first metal layer 21.

[0375] Although several modified examples of the embodiment have been described above, it is of course possible to apply a plurality of modified examples in appropriate combination.

Claims

1. a mask substrate comprising silicon; a mask layer having a first surface and a second surface located opposite to the first surface and facing the mask substrate; a through hole penetrating the mask layer; the mask substrate has a substrate opening; In a plan view, the through hole is located within the substrate opening, the mask layer includes a mask body layer forming the first surface, and a mask intermediate layer located between the mask body layer and the mask substrate; the mask body layer includes a metal material; the mask layer has a mask insulating layer forming the first surface; the mask body layer includes two or more body islands; The mask insulating layer is located between two adjacent body islands.

2. The deposition mask according to claim 1 , wherein a thickness of the mask intermediate layer is smaller than a thickness of the mask body layer.

3. the mask intermediate layer includes a substrate side layer including gold, aluminum, chromium, nickel, titanium, titanium nitride, an aluminum alloy including neodymium, silicon oxide, or silicon dioxide; The deposition mask according to claim 1 , wherein the substrate side layer is in contact with the mask body layer and is in contact with the mask substrate.

4. the mask intermediate layer includes a body-side layer facing the mask body layer and a substrate-side layer facing the mask substrate, The deposition mask according to claim 1 , wherein the body side layer and the substrate side layer are made of different materials.

5. 5. The deposition mask according to claim 4, wherein the substrate side layer contains gold, aluminum, chromium, nickel, titanium, titanium nitride, an aluminum alloy containing neodymium, silicon oxide, or silicon dioxide.

6. The deposition mask according to claim 4 , wherein the body side layer contains titanium, copper, nickel, or gold.

7. the mask intermediate layer includes an intermediate layer located between the substrate side layer and the body side layer, The deposition mask according to claim 4 , wherein the intermediate layer is made of a material different from that of the main body side layer and the substrate side layer.

8. The deposition mask according to claim 7 , wherein the intermediate layer contains titanium, titanium nitride, aluminum, an aluminum alloy containing neodymium, silicon oxide, silicon dioxide, nickel, copper, chromium, or gold.

9. The deposition mask according to claim 1 , wherein the metal material of the mask body layer is a magnetic metal material.

10. the mask substrate has a substrate body defining the substrate opening; the mask intermediate layer includes a body region located between the mask body layer and the substrate body, and an opening region located within the substrate opening in a plan view, The deposition mask according to claim 1 , wherein the through-hole penetrates the mask body layer and the opening region.

11. The deposition mask according to claim 10 , wherein an opening dimension of the through hole in the predetermined direction in the second surface is larger than an opening dimension of the through hole in the predetermined direction in the first surface.

12. the mask substrate has a substrate body defining the substrate opening; the mask intermediate layer includes a body region portion located between the mask body layer and the substrate body, and a mask layer opening formed along the substrate opening in a plan view, The deposition mask according to claim 1 , wherein the through-hole penetrates the mask body layer.

13. The deposition mask according to claim 12 , wherein an opening dimension in a predetermined direction of the through hole in a surface of the mask body layer facing the mask substrate is larger than an opening dimension in the predetermined direction of the through hole in the first surface.

14. the mask layer has two or more of the through holes, The deposition mask according to claim 1 , wherein two or more of the through holes are located within the substrate opening in a plan view.

15. the mask layer has two or more through hole groups each composed of two or more of the through holes, The deposition mask according to claim 14 , wherein two or more of the through hole groups are located within the substrate opening in a plan view.

16. the mask substrate has two or more of the substrate openings; the mask layer has two or more through hole groups each composed of two or more of the through holes, The deposition mask according to claim 14 , wherein two or more of the through-hole groups are located in each of the substrate openings in a plan view.

17. the mask substrate has two or more of the substrate openings; the mask layer has two or more through hole groups each composed of two or more of the through holes, The deposition mask according to claim 14 , wherein one group of through holes is located in each of the substrate openings in a plan view.

18. The substrate opening is formed in a rectangular shape in a plan view, The deposition mask according to claim 1 , wherein curved portions are provided at four corners of a contour of the substrate opening in a plan view.

19. The deposition mask according to claim 1 , further comprising a first alignment mark provided on a surface of the mask substrate opposite to the mask layer.

20. the mask substrate has a substrate body that defines the substrate opening, and an inner protrusion that protrudes inward from the substrate body in a plan view, The deposition mask of claim 19 , wherein the first alignment mark is located on the inner protrusion.

21. The deposition mask according to claim 19 , wherein a second alignment mark is provided at a position closer to the through hole than the first alignment mark.

22. the mask layer has two or more of the through holes, two or more through hole groups each composed of the two or more through holes, and mask bars provided between adjacent ones of the through hole groups, The deposition mask according to claim 21 , wherein the second alignment mark is located on the mask rail.

23. the mask bars include first mask bars and second mask bars extending in directions perpendicular to each other in a plan view, The deposition mask according to claim 22 , wherein the second alignment mark is located at an intersection between the first mask bar and the second mask bar.

24. the mask body layer includes two or more body islands; The deposition mask according to claim 1 or 2, wherein a groove penetrating the mask body layer is located between two adjacent body islands.

25. The deposition mask according to claim 1 , wherein the mask body layer includes a dummy body island located at a position not overlapping with the substrate opening in a plan view.

26. The deposition mask according to claim 1 or 2; a frame supporting the mask substrate of the deposition mask.

27. a substrate preparation step of preparing a mask substrate comprising silicon; a mask layer forming step of forming a mask layer on the mask substrate, the mask layer having a first surface and a second surface located on the opposite side to the first surface and facing the mask substrate; a substrate aperture forming step of forming a substrate aperture in the mask substrate; a mask layer opening forming step of forming a mask layer opening in the mask layer along the substrate opening in a plan view, the mask layer forming step includes a mask intermediate layer forming step of forming a mask intermediate layer on a surface of the mask substrate facing the mask layer, and a mask main body layer forming step of forming a mask main body layer on a surface of the mask intermediate layer opposite to the mask substrate and forming a through hole penetrating the mask main body layer, In the mask layer opening forming step, the mask layer opening is formed in the mask intermediate layer, In a plan view, the through hole is located within the substrate opening, the mask body layer includes a metal material; In the mask body layer forming step, a mask insulating layer is formed in a pattern corresponding to the through hole on a surface of the mask intermediate layer opposite to the mask substrate, the mask body layer includes two or more body islands; The method for manufacturing a deposition mask, wherein the mask insulating layer is located between two adjacent body islands.

28. 28. The method for producing a deposition mask according to claim 27, wherein in the mask body layer forming step, a resist layer is formed in a pattern corresponding to the through hole on a surface of the mask intermediate layer opposite to the mask substrate.

29. 29 . The method for manufacturing a deposition mask according to claim 27 , wherein an opening dimension in a predetermined direction of the through hole in a surface of the mask body layer facing the mask substrate is larger than an opening dimension in the predetermined direction of the through hole in the first surface.

30. The method for manufacturing a deposition mask according to claim 27 or 28, wherein the metal material of the mask body layer is a magnetic metal material.

31. The method for manufacturing a deposition mask according to claim 27 or 28, wherein a thickness of the mask intermediate layer is smaller than a thickness of the mask main body layer.

32. 29. The method for manufacturing a deposition mask according to claim 27 or 28, wherein the substrate opening forming step includes: a resist layer forming step of forming a resist layer having resist openings on a surface of the mask substrate opposite to the mask layer; and a substrate etching step of etching the mask substrate through the resist openings to form the substrate openings.

33. 33. The method for manufacturing a deposition mask according to claim 32, wherein the mask intermediate layer includes a substrate-side layer including a material that can ensure adhesion to the mask substrate and has resistance to an etching medium used in the substrate etching step.

34. The method for manufacturing a deposition mask according to claim 33 , wherein the mask intermediate layer includes a body side layer facing the mask body layer and including a material capable of ensuring adhesion with the mask body layer.

35. In the mask layer forming step, the mask body layer is formed by a plating process, 35. The method for manufacturing a deposition mask according to claim 34, wherein the mask intermediate layer includes an intermediate layer located between the substrate side layer and the body side layer, the intermediate layer including a material capable of protecting the substrate side layer from a plating solution used to form the mask body layer.

36. The method for manufacturing a deposition mask according to claim 33 , wherein the substrate side layer is in contact with the mask body layer and is in contact with the mask substrate.

37. The method for producing a deposition mask according to claim 27 or 28, wherein in the mask layer forming step, the mask intermediate layer is formed by a sputtering process.

38. The method for producing a deposition mask according to claim 27 or 28, wherein in the mask layer forming step, the mask intermediate layer is formed by a deposition process.

39. the mask layer has two or more of the through holes, The method for manufacturing a deposition mask according to claim 27 or 28, wherein two or more of the through holes are located within the substrate opening in a plan view.

40. the mask layer has two or more through hole groups each composed of two or more of the through holes, The method for manufacturing a deposition mask according to claim 39 , wherein two or more of the through hole groups are located within the substrate opening in a plan view.

41. the mask substrate has two or more of the substrate openings; the mask layer has two or more through hole groups each composed of two or more of the through holes, The method for manufacturing a deposition mask according to claim 39 , wherein two or more of the through hole groups are located in each of the substrate openings in a plan view.

42. the mask substrate has two or more of the substrate openings; the mask layer has two or more through hole groups each composed of two or more of the through holes, The method for manufacturing a deposition mask according to claim 39 , wherein one group of through holes is located in each of the substrate openings in a plan view.

43. The substrate opening is formed in a rectangular shape in a plan view, The method for manufacturing a deposition mask according to claim 27 or 28, wherein curved portions are provided at four corners of a contour of the substrate opening in a plan view.

44. The method for manufacturing a deposition mask according to claim 27 or 28, further comprising forming a first alignment mark on a surface of the mask substrate opposite to the mask layer.

45. the mask substrate has a substrate body that defines the substrate opening, and an inner protrusion that protrudes inward from the substrate body in a plan view, The method for manufacturing a deposition mask according to claim 44 , wherein the first alignment mark is located in the inner protrusion.

46. The method for manufacturing a deposition mask according to claim 44 , further comprising forming a second alignment mark at a position closer to the through hole than the first alignment mark.

47. the mask layer has two or more of the through holes, two or more through hole groups each composed of the two or more through holes, and mask bars provided between adjacent ones of the through hole groups, The method for manufacturing a deposition mask according to claim 46 , wherein the second alignment mark is located on the mask bar.

48. the mask bars include first mask bars and second mask bars extending in directions perpendicular to each other in a plan view, The method for manufacturing a deposition mask according to claim 47 , wherein the second alignment mark is located at an intersection where the first mask bar and the second mask bar intersect.

49. The method for manufacturing a deposition mask according to claim 27 or 28, wherein an outer edge of the mask body layer is located more inward than an outer edge of the mask intermediate layer in a plan view.

50. the mask body layer includes two or more body islands; The method for manufacturing a deposition mask according to claim 27 or 28, wherein a groove penetrating the mask body layer is located between two adjacent body islands.

51. The method for manufacturing a deposition mask according to claim 27 or 28, wherein the mask body layer includes a dummy body island located at a position not overlapping with the substrate opening in a plan view.

52. a deposition mask preparation step of preparing the deposition mask by the deposition mask manufacturing method according to claim 27 or 28; a bonding step of bonding the first surface of the mask layer of the deposition mask to a deposition substrate; and a vapor deposition step of depositing a vapor deposition material onto the vapor deposition substrate through the through-holes of the vapor deposition mask to form a vapor deposition layer.

53. a deposition mask preparation step of preparing the deposition mask by the deposition mask manufacturing method according to claim 27 or 28; and a frame attaching step of attaching a frame to the mask substrate of the deposition mask.

Images