Abstract

In one embodiment, a multifunctional material system is provided, comprising a variable permeability layer, a desiccant-containing layer, and a vapor-permeable support layer. The variable permeability layer can have a vapor permeability that increases with increasing relative humidity. The desiccant-containing layer can be adjacent to the variable permeability layer. A vapor-permeable support layer can be disposed adjacent to at least one of the variable permeability layer and the desiccant-containing layer. When the relative humidity is higher adjacent to the variable permeability layer than the desiccant layer, water migrates in a first direction from the variable permeability layer to the desiccant layer. When the relative humidity is higher adjacent to the desiccant-containing layer than the variable permeability layer, water migrates in an opposing second direction from the desiccant-containing layer to the variable permeability layer. The water migration rate in the first direction is higher than in the second direction when the humidity gradient is reversed.

Description

[Technical field]

[0001] This application claims the benefit of U.S. Provisional Patent Application No. 62 / 725,446, entitled “Construction Materials Incorporating A Multifunctional Subsystem For Passive Heat And Water Management In Building Envelopes,” filed August 31, 2019, which is incorporated herein by reference in its entirety. [Background technology]

[0002] It is desirable for an enclosure, such as a building, to have characteristics such as energy efficiency, comfort, and durability at an affordable cost. However, conflicts can arise when attempting to achieve these characteristics simultaneously. As an example, a building's energy efficiency can be improved by using insulation and increasing the building's airtightness. However, moisture control becomes a greater concern. In particular, achieving a high R-value (a measure of resistance to heat transfer) through the insulation and airtightness of the enclosure can result in a reduced permeability to water vapor, increasing the risk of condensation, moisture damage, and mold. Thus, as energy efficiency increases, durability and comfort can often decrease. Summary of the Invention

[0003] Various techniques have been developed to improve moisture control. In one aspect, the membrane of a "smart" vapor retarder exhibits a permeability to water vapor that varies with relative humidity. As an example, the permeability of the membrane increases rapidly with increasing relative humidity, allowing the wall to dry out as water penetrates, while the permeability of the membrane decreases with decreasing relative humidity, slowing the diffusion of water vapor into the wall. However, even smart vapor retarders allow a finite amount of water to enter the wall when the relative humidity increases outside, since diffusion causes water vapor to move in the direction of decreasing humidity. When the relative humidity decreases, the amount of time required to remove water vapor from the wall is approximately the same as the amount of time water vapor was added to the wall. That is, when the magnitude of the relative humidity gradient across the wall is reversed, the smart vapor retarder exhibits time symmetry with respect to the ingress and egress of water vapor. It can therefore be seen that the smart vapor retarder does not have a mechanism to preferentially suppress the ingress of water vapor compared to the egress of water vapor when the relative humidity conditions are reversed.

[0004] Desiccant-based systems are another moisture control technology in current technology. Desiccant systems remove water directly from the air by adsorbing water onto the surface of a desiccant material. When the desiccant material is heated, the adsorbed water is driven off the surface of the desiccant material. This process restores the desiccant's ability to dehumidify the air. In contrast, existing HVAC systems remove water from the air by first cooling the air below the dew point and then reheating the air to the desired temperature. HVAC systems require power to both cool and heat the air during operation, making them significantly less energy efficient than existing HVAC systems for moisture control. However, while desiccant-based dehumidification systems are more energy efficient than existing HVAC systems, they still consume energy to generate the heat required for desiccant regeneration.

[0005] It can be understood that improving the energy efficiency of buildings often significantly increases construction costs. Generally, installing additional layers for air, moisture and temperature control significantly increases labor costs. Therefore, multifunctional building materials that can simultaneously regulate the infiltration and discharge of water vapor, store and release heat, and humidify and dehumidify can improve the heat retention and humidity control performance of buildings, and improve energy efficiency while reducing labor costs for construction. Furthermore, multifunctional materials that can both humidify and dehumidify without moving mechanical parts and without using electricity can further improve efficiency.

[0006] The embodiments of the present disclosure provide a multifunctional material system that addresses these challenges. The first function of the multifunctional material system is the storage and release of thermal energy, similar to that of a phase change material (PCM). In general, PCMs can regulate temperature by absorbing latent heat when the ambient temperature rises above a phase transition temperature, or by releasing latent heat when the ambient temperature falls below a phase transition temperature. Existing PCMs can phase change between liquid and solid states, as in the case of paraffin, and between hydrated and anhydrous states, as in the case of salt hydrates. The multifunctional material system can adsorb or release heat as water transitions between gaseous and condensed states on the material surface (e.g., the boiling / condensation lines of the water phase diagram). This PCM-like behavior can improve energy efficiency by reducing the energy demand of HVAC systems by an amount equal to the latent heat transferred.

[0007] The second function of the multifunctional material system is the storage and release of water vapor as a humidity buffer. Humidity buffering, also called moisture buffering, characterizes the ability of a material to moderate changes in relative humidity by absorbing and releasing water vapor from the surrounding air. Humidity is an important determinant of human comfort, and most people prefer environments with a relative humidity of about 35% to 60%. Extremely high humidity creates conditions in which mold, mildew, and dust mites can grow. Extremely low humidity levels can cause dry eyes and skin, increase the risk of respiratory problems, or increase the risk of catching a cold or flu.

[0008] The third function of the multifunctional material system is to bias the diffusive flow of water vapor in the direction of the desiccant layer, like a water vapor diode, also known as a one-way water vapor valve. That is, diffusive flow of water vapor is permitted in the "open" direction of the water vapor diode, and diffusive flow is inhibited in the "closed" direction of the water vapor diode. This function of the multifunctional material system inhibits the ingress of water vapor from the environment outside the enclosure while allowing the egress of water vapor from the environment inside the enclosure.

[0009] When used in a building envelope, embodiments of the disclosed multi-functional material can reduce installation costs compared to installing a separate membrane layer in the building envelope. Additionally, in alternative embodiments, the disclosed multi-functional material can omit either the variably permeable layer or the desiccant layer. Such modified multi-functional materials can optimize subsets of performance benefits for different areas of a building, such as bathrooms and kitchens, where humidity control or water vapor transport is a primary concern.

[0010] In one embodiment, a multifunctional material system is provided, which can include a variable permeability layer, a desiccant-containing layer, and a vapor-permeable support layer. The variable permeability layer can have a vapor permeability that increases with increasing relative humidity. The desiccant-containing layer can be adjacent to the variable permeability layer. The vapor-permeable support layer can be disposed adjacent to at least one of the variable permeability layer and the desiccant-containing layer. When the relative humidity is higher adjacent to the variable permeability layer than the desiccant layer, water moves in a first direction from the variable permeability layer to the desiccant layer. When the relative humidity is higher adjacent to the desiccant-containing layer than the variable permeability layer, water moves in an opposite second direction from the desiccant-containing layer to the variable permeability layer. The water movement rate in the first direction is higher than in the second direction when the humidity gradient is reversed.

[0011] In another embodiment, the vapor permeable layer is interposed between the desiccant-containing layer and the variably permeable layer. In another embodiment, the permeability of the variably permeable layer increases approximately exponentially with increasing relative humidity.

[0012] In another embodiment, the desiccant-containing layer is substantially homogeneous. In another embodiment, the desiccant-containing layer is a composite material that includes desiccant particles embedded in a matrix.

[0013] In another embodiment, the desiccant-containing layer includes a first layer having a matrix formed from a vapor-permeable binder and a second layer having a matrix formed from a variable permeability binder, where the first layer is the variable permeability layer.

[0014] In another embodiment, at least a portion of the desiccant-containing layer is formed from a desiccant material, which may be at least one of silica gel, zeolite, calcium oxide (CaO), calcium sulfate (CaSO), lithium chloride (LiCl), clay, or activated carbon.

[0015] In another embodiment, the vapor permeable layer is formed from polylactic acid (PLA), polytetrafluoroethylene, silicone, natural rubber, synthetic rubber, polystyrene, polymethylpentene (PMP), polycarbonate (PC), polyurethane (PU), or polymethylmethacrylate (PMMA).

[0016] In another embodiment, the variably permeable layer is formed from a polyamide or polyvinyl alcohol (PVA). As an example, the polyamide can be nylon. In one embodiment, a wall assembly is provided, the wall assembly including a wall cavity, an insulating material, and a multi-functional material system. The wall cavity can define a first surface adjacent to the interior of the building and a second surface adjacent to the exterior of the building. The insulating material can be disposed within at least a portion of the wall cavity. In one embodiment, the multi-functional material system can include a variable permeability layer, a desiccant-containing layer, and a vapor-permeable support layer. The variable permeability layer can have a vapor permeability that increases with increasing relative humidity. The desiccant-containing layer can be adjacent to the variable permeability layer. The vapor-permeable support layer can be disposed adjacent to at least one of the variable permeability layer and the desiccant-containing layer. When the relative humidity is higher adjacent to the variable permeability layer than the desiccant layer, water migrates in a first direction from the variable permeability layer to the desiccant layer. When the relative humidity is higher adjacent to the desiccant-containing layer than the variable permeability layer, water migrates in an opposite second direction from the desiccant-containing layer to the variable permeability layer. The rate of water movement in the first direction is higher than in the second direction when the humidity gradient is reversed. The multifunctional material system can be disposed on at least one of the first surface and the second surface of the wall cavity.

[0017] In one embodiment, a multifunctional material assembly is provided, the multifunctional material assembly can include a substrate and a multifunctional material system. In one embodiment, the multifunctional material system can include a variable permeability layer, a desiccant-containing layer, and a vapor-permeable support layer. The variable permeability layer can have a vapor permeability that increases with increasing relative humidity. The desiccant-containing layer can be adjacent to the variable permeability layer. The vapor-permeable support layer can be disposed adjacent to at least one of the variable permeability layer and the desiccant-containing layer. When the relative humidity is higher adjacent to the variable permeability layer than the desiccant layer, water moves in a first direction from the variable permeability layer to the desiccant layer. When the relative humidity is higher adjacent to the desiccant-containing layer than the variable permeability layer, water moves in an opposite second direction from the desiccant-containing layer to the variable permeability layer. The water movement rate in the first direction is higher than in the second direction when the humidity gradient is reversed. The multifunctional material system can be disposed on at least one of the first surface and the second surface of the wall cavity. At least one layer of the multifunctional material system can be disposed on a surface of the substrate.

[0018] In another embodiment, the assembly may further include an adhesive layer interposed between the substrate and the layer of the multifunctional material system. In another embodiment, the adhesive layer is a variably permeable layer.

[0019] In another embodiment, the substrate is oriented strand board (OSB), insulation, gypsum board, cement board, stucco, drywall, underlayment, roofing, coating, or a building membrane. In another embodiment, the variably permeable layer is disposed on a first surface of the substrate and the desiccant-containing layer is disposed on a second surface of the substrate opposite the first surface of the substrate.

[0020] In another embodiment, the multifunctional material assembly includes a desiccant-containing layer formed from a matrix of substrate and desiccant particles embedded in the substrate, with a variably permeable layer disposed on a surface of the desiccant layer.

[0021] In one embodiment, a multifunctional material assembly is provided, the multifunctional material assembly including a pocketed structure, a plurality of desiccant particles, and a variable permeability layer. The pocketed structure can define one or more pockets having an open side. The plurality of desiccant particles can be disposed within each of the one or more pockets (e.g., occupying at least a portion of a volume of each pocket). The variable permeability layer can have a vapor permeability that increases with increasing relative humidity. Additionally, the variable permeability layer can overlie the open side of each of the one or more pockets.

[0022] The multifunctional material assembly may also include a substrate. The variably permeable layer may be secured to the substrate. [Brief description of the drawings]

[0023] [Figure 1] FIG. 1 illustrates one exemplary embodiment of an operating environment including a multi-functional material structure having a variably permeable layer and a desiccant layer. [Diagram 2] FIG. 13 shows a plot of water vapor transmission rate as a function of humidity for selected vapor retarder wall cavities. [Diagram 3] 1 is a plot of adsorption isotherms for various desiccant materials, including silica gel. [Figure 4a] 2 is a plot showing measurements of water flux and net water transfer across the multifunctional material system of FIG. 1. [Figure 4b] 2 is a plot showing a theoretical simulation of water flux and pure water transfer through the multifunctional material system of FIG. 1. [Figure 5a] FIG. 1 illustrates one exemplary embodiment of a multi-functional material system including a variably permeable layer and a desiccant layer. [Figure 5b] FIG. 1 illustrates one exemplary embodiment of a multi-functional material system including a desiccant layer in the form of a composite. [Figure 6] FIG. 1 illustrates one exemplary embodiment of a multifunctional material system including one or more vapor permeable support layers. [Figure 7a]FIG. 1 illustrates one exemplary embodiment of a multifunctional material system including a desiccant bed having two layers. [Figure 7b] FIG. 1 illustrates one exemplary embodiment of a multifunctional material system in the form of a composite having a gradient of desiccant concentration across its thickness. [Figure 8] FIG. 1 illustrates one exemplary embodiment of a multi-functional material adhered to a substrate. [Figure 9] FIG. 1 illustrates another exemplary embodiment of a multifunctional material adhered to a substrate. [Figure 10] FIG. 10 illustrates another exemplary embodiment of a multi-functional material adhered to a substrate, with a vapor retarder and a desiccant layer disposed on opposite sides of the substrate. [Figure 11] FIG. 1 illustrates another exemplary embodiment of a multifunctional material adhered to one surface of a substrate, where the desiccant layer of the multifunctional material system includes desiccant particles embedded in a matrix formed from the substrate material. [Figure 12] FIG. 13 illustrates another exemplary embodiment of a multi-functional material that includes a desiccant layer in the form of a pocketed structure having pockets that contain desiccant particles. [Figure 13] FIG. 13 shows the multi-functional material of FIG. 12 adhered to a substrate. [Figure 14] FIG. 1 illustrates another exemplary embodiment of a smart wall panel including a multifunctional material system having a variably permeable layer wrapped around the edges of the panel and a vapor-tight seal formed adjacent to and between the smart wall panel. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0024] It should be noted that the drawings are not necessarily to scale: the drawings are intended to depict only typical aspects of the subject matter disclosed herein, and therefore should not be construed as limiting the scope of the present disclosure.

[0025] Discussed herein are embodiments of a multifunctional material system and corresponding methods of manufacture and use as a building material, although embodiments of the present disclosure may be employed in other applications without limitation.

[0026] FIG. 1 illustrates one exemplary embodiment 100 of an operating environment in the form of a wall assembly 102. The wall assembly 102 includes a wall cavity 104 that defines a first or inner surface 104a adjacent to an interior environment 106 and a second or outer surface 104b adjacent to an exterior environment 110. In general, the interior environment 106 can be the space enclosed by the wall assembly 102 that is conditioned, while the exterior environment 110 is an unconditioned space. Thus, when a multifunctional material system 114 is installed on the inner surface 104a of the wall assembly 102, the interior environment 106 can be the interior of a room of a building, and the exterior environment can be the exterior of the building. However, it can be understood that embodiments of the multifunctional material system can also be used in a wall assembly that separates two interior rooms, one of which is conditioned and the other of which is not (e.g., a stairwell or other unconditioned space). In either case, a desiccant layer can be located closest to the unconditioned space / environment.

[0027] The wall assembly 102 may further include an insulating material 112 disposed within at least a portion of the wall cavity 104 (e.g., between the first surface 104a and the second surface 104b). The wall assembly 102 may further include a multi-functional material system 114. As shown, the multi-functional material is disposed on the inner surface 104a. However, in alternative embodiments, the multi-functional material system may be disposed on or adjacent to opposing surfaces of the wall cavity (e.g., adjacent to the outer surface), or on or adjacent to both the inner and outer surfaces.

[0028] The multifunctional material system 114 may include a variable permeability layer 114a of thickness T and a desiccant-containing layer 114b of thickness L. The variable permeability layer 114a may also be referred to herein as a vapor retarder or vapor barrier. As discussed in more detail below, the desiccant-containing layer 114b may be substantially entirely composed of a desiccant material or may be composed of a composite material including a desiccant material embedded in a matrix. However, for simplicity, the desiccant-containing layer 114b is referred to herein as a desiccant layer. The desiccant layer 114b is disposed adjacent to the variable permeability layer 114a. As also discussed in more detail below, the desiccant layer may be in contact with the side of the variable permeability layer or may be separated from the side of the variable permeability layer by one or more intervening layers.

[0029] Examples of materials from which the variable permeability layer 114a is formed include polyamides (e.g., nylon), polyvinyl alcohol (PVA), and various polyions. Examples of desiccant materials from which the desiccant layer 114b is formed include one or more of silica gel, zeolite, calcium oxide (CaO2), calcium sulfate (CASO4), lithium chloride (LiCl), clay, or activated carbon. The thickness L of the desiccant layer 114b may be selected from the range of about 0.05 mm to about 20 mm. The thickness T of the variable permeability layer 114a may be selected from the range of about 0.001 mm to about 0.01.

[0030] In embodiments where the desiccant material has a porous structure, the pore size may range from about 0.4 nm to about 100 μm. In other embodiments, the pore size may be about 0.04 nm. In further embodiments, the pore size may be about 100 μm.

[0031] The pore size of the porous desiccant material may also vary with position within the desiccant layer 114b. As an example, the pore size may decrease approaching a selected side of the desiccant layer 114b (e.g., the side of the desiccant layer 114b closest to the external environment 110).

[0032] The multifunctional material system 114 can be configured to perform a variety of functions, alone or in any combination. In one aspect, the multifunctional material system 114 functions as a vapor diode by allowing water to move in a first direction from the side of the variably permeable layer 114a to the side of the desiccant layer 114b at a significantly higher rate than if the humidity gradient were reversed and water vapor were pursued in the opposite direction. In another aspect, the multifunctional material system 114 regulates temperature similar to a phase change material, except that in this context, the phase change is between the adsorbed water in the desiccant layer 114b and water vapor. In a further aspect, the multifunctional material system 114 regulates relative humidity by adsorbing more water vapor when humidity increases and releasing water vapor when humidity decreases. These functions improve the energy efficiency, durability, and comfort of buildings. The physical principles of these functions, and an estimate of the magnitude of their effect, are discussed in detail below. [Vapor diode function] The embodiment of the vapor diode function works as follows: When humidity is high on the side of the variable permeability layer 114a, the permeability to water vapor, also called the permeability coefficient, increases. The desiccant layer 114b has a relatively high permeability and relatively easily adsorbs the water received from the variable permeability layer 114a. The water received by the side of the desiccant layer 114b then evaporates into the air adjacent to the desiccant layer 114b. Conversely, when humidity is high on the side of the desiccant layer 114b, the desiccant layer 114b absorbs and separates the water before it reaches the variable permeability layer 114a. In this way, the relative humidity of the variable permeability layer 114a, and therefore the permeability of the variable permeability layer 114a, remains low. Over the humidity fluctuation cycle, there is a net transfer (e.g., pumping) of water throughout the multifunctional material system 114. This correction function, which does not currently exist in building materials, can be used to pump water out of the wall cavity 104, thereby improving durability.

[0033] The functionality of the vapor diode relies on both the nonlinear and asymmetric properties of vapor transport in the multifunctional material system 114. The nonlinearity is provided by the variable permeability layer 114a, whose permeability rises exponentially with relative humidity RH. Figure 2 shows the RH-dependent permeability coefficient of a smart vapor retarder made from a polyamide material (MemBrain, Certaindeed). It can be observed that the permeability coefficient varies by two orders of magnitude.

[0034] The asymmetry is provided by the desiccant layer 114b, which separates water from only one side of the variably permeable layer 114a (e.g., the side of the variably permeable layer 114a closest to the desiccant layer 114b). Figure 3 shows plots of adsorption isotherms (adsorption as a function of relative humidity at constant temperature) for silica gel, a non-toxic nanoporous mineral, as well as CaO, clay, molecular sieve, CASO4. Silica gel adsorbs water roughly proportional to the relative humidity RH of the surrounding air, and has the capacity to hold up to about 37% of its dry weight in water. Water diffuses relatively slowly inside the silica gel, which results in a delay between the humidity change on one side of the silica gel layer and the time when the water content begins to equilibrate on the other side. The diffusion constant D SG =2x10 -11 m 2 s -1 and the thickness of the desiccant layer L is L 2 / 2D SG The lag time, which scales as , characterizes the time it takes for the silica gel to separate water from the vapor barrier, allowing the structure to modify vapor transport. As an example, for 1 mm of silica gel, the lag time is about 7 hours, which is long enough to modify diurnal (daily) humidity fluctuations. For 2 mm of silica gel, the lag time is about 115 days or more, suggesting that annual humidity cycles can be modified as well.

[0035] Variations in relative humidity occur most noticeably with temperature changes. RH and temperature are inversely related, since the ability of air to hold water vapor increases with temperature. As an example, assume air with a fixed moisture content that starts at 23°C and 40% relative humidity. As the air is warmed to 28°C, the relative humidity drops to 29.7%. As the air is cooled to 18°C, the relative humidity rises to 54.5%. These changes can be evaluated using a psychrometric chart or the Magnus formula. Over the same 10°C temperature range, the permeability coefficient of the smart vapor barrier would change by about a factor of 7, according to Figure 2, and the silica gel would be expected to exchange about 13% of its dry mass in water, according to Figure 3. Both are significant effects.

[0036] Measurements of water transport across a prototype multifunctional material system formed as a variable permeability layer in MemBrain (Certainteed) and a desiccant layer formed from silica gel particles were performed. A porous highly permeable plastic film (on the order of millimeters, e.g., about 1-10 mm for the MemBrain) was used to hold the silica gel particles. The multifunctional material system was subjected to a humidity gradient by using it to cover a wide-mouthed cup of water, exposing one side to about 100% RH and the other side to a laboratory environment of about 50% RH. The RH gradient was varied periodically by inverting the structure every day and exposing the other side to water vapor. The masses of the cup and the multifunctional material system, respectively, were measured at regular intervals to determine the transfer of water across the vapor barrier to the silica gel. Figure 4(a) shows a plot of the measured water flux and pure water transfer to the desiccant side as a function of time. The water flux from the MemBrain side to the silica gel side was more than twice as large as the flux in the reverse direction over the entire cycle. Water: about 0.5g -2 day -1 To put this result in context, if the surrounding area is 200 m 2 For a moderately sized home, this pumping rate would remove approximately 0.1 L per day from the walls.

[0037] Water transport was theoretically modeled using the finite difference method. Specifically, MATLAB® was employed to model the diffusion of water throughout the prototype multifunctional material system. The simulation was performed assuming a 75 μm thick polyamide layer as the variable permeability layer and a 200 μm thick silica gel layer as the desiccant layer. The relative humidity was sinusoidally varied on both sides of the simulated multifunctional material system with an amplitude of 20% and a period of 48 hours, for an average RH of 50%. Both sides were out of phase.

[0038] FIG. 4(b) shows a plot of the simulated water flux through the prototype multifunctional material system, as well as the cumulative mass of water accumulating on the desiccant layer side. The water flux from the variable permeability layer side (polyamide side) to the desiccant layer side was twice as large as the peak flux in the reverse direction over the entire cycle. Water was approximately 0.1 gm -2 day -1 The water accumulated on the desiccant layer at an average rate of

[0039] It can be seen that the pumping effect provided by the function of the vapor diode works even if the humidity fluctuations on both sides are in phase, i.e., there is no change in humidity. The only requirement for pumping is that the humidity fluctuates periodically. As an example, when the humidity is high on both sides of the multifunctional material system 114, water vapor diffuses from both sides to the desiccant layer 114b (e.g., via the adjacent air and the variable permeability layer 114a) at a high transport rate through the variable permeability layer 114a. The distribution of water in the desiccant layer 114b can slowly equilibrate (e.g., if the desiccant layer 114b is about 1 mm thick, the time required for complete equilibration can be several hours). Then, when the humidity on both sides of the multifunctional material system 114 is low, the water vapor diffuses out of the multifunctional material system 114 from both sides of the variable permeability layer 114a and the side of the desiccant layer 114b. However, the rate of diffusion through the variable permeability layer 114a is significantly slower than the rate at which water vapor enters. This unequal rate of water entering and leaving through the variable permeability layer 114a results in a net movement (pumping) of water in the direction of the desiccant layer 114b. [Phase change function] An increase in temperature causes the RH to decrease and water to evaporate from the desiccant layer 114b. Conversely, a decrease in temperature causes the RH to increase and the desiccant layer 114b to absorb water. In these two processes, the latent heat absorbed regulates the temperature and the latent heat released reduces the demand on the HVAC system. This principle is the same as phase change materials, except that the ambient water is the phase changing substance.

[0040] For every gram of water evaporated, about 2500 J is absorbed from the environment. This means the sum of the latent heat of boiling and small surface binding energy. As an example, the latent heat density of silica gel may be about 925 kJ / kg. However, in practice, only a part of this latent heat is available. In general, the desiccant layer 114b is never completely dry or completely filled with water under normal operating conditions.

[0041] A more realistic estimate of the latent heat density can be based on the same 10°C temperature change already considered and the fact that the adsorption isotherm in Figure 3 does not change significantly with temperature. The total water adsorbed or released by the silica gel desiccant over this temperature increase is expected to be about 13% of the dry mass. This corresponds to a latent heat density of about 325 kJ / kg. In comparison, the latent heat densities of commercially available phase change materials range from 120 kJ / kg to 220 kJ / kg. It can be seen that the desiccant material can be engineered to release the same latent heat over a narrower temperature range; that is, the adsorption isotherm needs to be steeper in the relevant RH range.

[0042] At a cost of about $1 / kg, silica gel is a relatively inexpensive desiccant material. It is capable of providing latent heat at about 320 kJ / $. Commercially available PCMs cost much more, with the cheaper ones selling for about 36 kJ / $ (based on 120 kJ / kg and $1.5 / lb ($3.3 / kg)). Additionally, its density ρ SG =1280kgm -3 If so, a 1mm layer of silica gel will have a mass of 1.28 kgm -2 m and has an areal mass of approximately 416 kJm -2 In comparison, commercial gypsum boards using PCMs (e.g., National Gypsum ThermalCORE) provide 250 kJm -2 It is. [Humidity buffer function] A silica gel desiccant with a thickness of 1 mm has a maximum capacity of about 450 g of water per square meter of wall. However, more realistically, this value is about 150 gm -2 , which is closer to the amount of water exchanged between the wall and the interior environment under normal conditions. In a medium sized home, the multifunctional material system 114 can absorb or release approximately 30 L of water. This can significantly improve comfort, reduce the energy demands of the HVAC system, and even eliminate the need for powered humidifiers or dehumidifiers.

[0043] Finally, it is important to note that there is a common misconception that silica gel is a hazardous material. This is due to the familiar words "Do not eat" on the white silica gel packets found in packaging (e.g. shoe boxes). However, silica gel itself is not toxic. Instead, the warning is placed on it because the silica gel beads often contain cobalt(II) chloride, which is carcinogenic. Cobalt(II) chloride acts as a moisture indicator by changing color from blue to pink as the moisture content increases. There is no need for cobalt(II) chloride in construction materials, so the use of silica gel desiccant does not pose any obvious safety concerns. [Function Control] The requirements and relative importance of the three functions of the multifunctional material system 114 may depend on the location of the building envelope in which the multifunctional material system 114 is used and the climate in which the building is located. In one aspect, the ability of the multifunctional material system 114 to regulate humidity may be more desirable inside a building than on the exterior. In another aspect, the vapor diode function may be more desirable in humid climates than in dry climates. Methods are available to adjust manufacturing or material parameters to control the performance characteristics of the multifunctional material system 114. This allows the performance of different building materials incorporating the multifunctional material system 114 to be optimized for specific applications.

[0044] The time scale over which the multifunctional material system 114 corrects humidity fluctuations is set by the time scale for water to diffuse through the desiccant layer 114b to reach a steady-state concentration. For a continuous desiccant layer 114b of thickness L, that time scale t is given by:

[0045]

number

[0046]

number

[0047] The ability of the multifunctional material system 114 to regulate temperature, the latent heat, is proportional to the amount of water exchanged between the condensed and vapor phases. Assuming sufficient time for equilibration, the latent heat that can be stored in or released from the continuous desiccant layer 114b is proportional to the thickness. However, assuming only a finite amount of time t, the portion of the desiccant layer 114b where the water concentration changes significantly has a finite thickness of:

[0048]

number

[0049] As mentioned above, the effective amount of latent heat available in the multifunctional material system 114 can be increased by providing the desiccant layer 114b in the form of a composite, the matrix having a high water vapor diffusivity. The desiccant particles must be small enough to equilibrate the water content within about 12 hours. Because water vapor can diffuse more quickly through the matrix, the latent heat content available from such a desiccant layer 114b increases with thickness and exceeds the following value:

[0050]

number

[0051]

number

[0052] Additionally, the ability of the multifunctional material system 114 to regulate humidity is proportional to the amount of water it can exchange between the condensed and vapor phases. The same strategies described above may be used to adjust this ability.

[0053] The permeability coefficient of the variable permeability layer 114a is inversely proportional to its thickness. Thus, by fabricating the variable permeability layer 114a of an appropriate thickness, the RH-dependent permeability coefficient curve can be scaled by a desired factor. Control of the overall permeability coefficient is important because it affects how effectively the multifunctional material system 114 can utilize humidity fluctuations to pump water vapor. This is also important because it must be possible to make the potential drying capacity of the wall assembly high, and therefore the permeability in at least one direction high. For example, in cold climates, wall assemblies are often designed to be dry on the outside, and the building envelope used as an air and weather barrier on the outside of the substrate has a high permeability to water vapor. Replacing the building envelope with the multifunctional material system 114 can improve the performance of the envelope without sacrificing the potential drying capacity, if the variable permeability layer 114a is fabricated to have a sufficiently high permeability coefficient under humid conditions. That is, if the wall cavity 104 is dry, a relatively low permeability coefficient is not an issue.

[0054] The microstructure and properties of the desiccant material can be engineered to control the performance of the multifunctional material system 114. As one example, the pore size distribution and the hydrophilicity of the surface of the desiccant material affect the shape of the adsorption isotherm. Nanoporous materials with relatively hydrophobic surfaces will adsorb little or no water until the critical humidity value of air is exceeded. At this point, it is energetically favorable for liquid water to condense inside the narrowest constriction of the pores. This effect is controlled by capillary action and is therefore manifested at higher humidity values ​​in larger pores. As another example, different desiccant materials preferentially adsorb water vapor in a range of RH indicated by the steepness of the slope of the adsorption isotherm (FIG. 3). A particular material can be selected because it effectively buffers RH in a particular range of interest, or multiple desiccant materials can be combined to tailor the range in which the mixture can efficiently buffer RH. Thus, the material or microstructure (e.g., pore size) can be selected to most effectively buffer relative humidity within a selected range of RH values ​​(e.g., the slope of the adsorption isotherm is greatest within a selected RH range). [Exemplary multifunctional material architectures] The above-described embodiments of the multifunctional material system 114 architecture can be realized as free-standing membranes. Figure 5A shows a multifunctional material system 500 including a variably permeable layer 114a bonded to a desiccant layer 114b. As shown, the desiccant layer 114b can be substantially homogenous.

[0055] FIG. 5B illustrates another embodiment of the multifunctional material system 500 in the form of a multifunctional material system 550. As shown, the multifunctional material system 550 includes a variably permeable layer 114a and a desiccant layer 114b in the form of a composite desiccant layer 554 including a first component and a second component. By way of example, the first component can be a matrix 556 and the second component can be a desiccant material 560 embedded within the matrix 556. The geometry of the desiccant material 560 can vary. In one aspect, the desiccant material 560 can take the form of a plurality of desiccant particles embedded within the matrix 556. In certain embodiments, the desiccant particles can be approximately uniform in size (e.g., diameter) and shape. In other embodiments, the desiccant particles can have a size distribution (e.g., approximately normal distribution, binary distribution, etc.). By way of example, the desiccant particle size can range from about 0.05 mm to about 5 mm.

[0056] The matrix 556 of the composite desiccant layer 552 may be formed from a material that is highly permeable to water vapor. In one embodiment, a material with a permeability of more than 5 US perms (e.g., more than 10 perms) may be considered a vapor permeable material. Examples of the matrix 556 may include binders, foams (e.g., insulation), netting, fiber mats, filaments, fabrics, cloth, drywall, underlayment, sheathing, and structural insulated panels (SIPs). Examples of binder materials may include polylactic acid (PLA), polytetrafluoroethylene (e.g., colloidal polytetrafluoroethylene), polyurethane (thermoplastic or foamed), silicone, natural rubber, synthetic rubber, polymethylpentene (PMP), polystyrene (PS), polycarbonate (PC), polyvinyl alcohol (PVA), or polymethylmethacrylate (PMMA). Other polymers and resins are also contemplated.

[0057] The desiccant material 560 in the matrix 556 may be formed from any of the desiccant materials described above in the context of the desiccant layer 114b. Examples of desiccant materials may include one or more of silica gel, zeolite, calcium oxide (CaO2), calcium sulfate (CASO4), lithium chloride (LiCl), clay, or activated carbon. Combinations of two or more different desiccant materials are also contemplated.

[0058] In further embodiments, the multifunctional material system 114 can be modified to include one or more vapor-permeable layers (e.g., layers that are highly permeable to water vapor). In certain embodiments, these vapor-permeable layers can provide mechanical support to the multifunctional material system 114 without fundamentally altering its function. In other aspects, the vapor-permeable materials forming the vapor-permeable layers can be materials with a permeability greater than 10 US perms, and the vapor-impermeable materials can be materials with a permeability less than 0.1 US perms. Examples of materials forming the vapor-permeable layers can include fabrics, netting, fiber mats, porous materials, silicone, natural rubber, synthetic rubber, polystyrene (e.g., high impact polystyrene (HIPS)), polymethylpentene (PMP), polycarbonate (PC), polyurethane (PU), and polymethylmethacrylate (PMMA).

[0059] FIG. 6 illustrates another embodiment of the multifunctional material system 114 in the form of a multifunctional material system 600. The multifunctional material system 600 is similar to the multifunctional material system 500 with the addition of a vapor permeable layer 602 for support. As shown in FIG. 6, the vapor permeable layers 602 are disposed on both sides of the desiccant layer 114b, and the variable permeability layer 114a is disposed on one side of the vapor permeable layer 602 closest to the interior environment 106. However, in alternative embodiments, one or more vapor permeable layers may be employed on both sides of the desiccant layer. In further embodiments, the location of the vapor permeable layer and the location of the variable permeability layer may be swapped. That is, the vapor permeable layer(s) may be disposed in contact with the variable permeability layer, the desiccant layer, or both. In other embodiments, the vapor permeable layer may be configured to provide functionality such as water repellency. Additionally, it can be understood that any embodiment of the multifunctional material system disclosed herein may include one or more of the vapor permeable layers, if desired, although not shown.

[0060] Embodiments of the vapor-permeable layer 602 can take on a variety of configurations. In one aspect, the mechanical properties of the vapor-permeable layer 602 can be tailored within a particular range. Examples of mechanical properties can include stiffness (e.g., having a modulus of elasticity greater than a predetermined value), flexibility (e.g., having a modulus of elasticity lower than a predetermined value or a yield stress less than a predetermined value), impact resistance (e.g., having a hardness greater than a predetermined value), acoustic absorption (e.g., acoustic attenuation greater than a predetermined value), tear resistance (e.g., having a fracture toughness greater than a predetermined value), strength (e.g., having a tensile strength greater than a predetermined value), or peel resistance (e.g., having a peel strength greater than a predetermined value).

[0061] In further embodiments, the desiccant layer 114b can include two or more layers. FIG. 7a illustrates another embodiment of the multifunctional material system 114 in the form of a multifunctional material system 700. As illustrated, the desiccant layer 114b includes a first desiccant layer 702 and a second desiccant layer 704. The first desiccant layer 702 and the second desiccant layer 704 can be composites including a matrix and a desiccant material (e.g., desiccant material 560) embedded therein, as described above. In certain embodiments, the matrix can function as a binder to hold the embedded desiccant material. As an example, the first desiccant layer 702 can include a matrix formed from materials such as those described above with respect to the variably permeable layer 114a. The second desiccant layer can include a matrix formed from the same materials as those described above with respect to the vapor permeable layer 602. Thus, the matrix of the first desiccant layer 702 can perform the function of the variably permeable layer 114a, as described above.

[0062] In an alternative embodiment, a single layer of the multifunctional material system 114 can provide the functionality of the desiccant layer 114b and the variably permeable layer 114a. FIG. 7b illustrates the multifunctional material system 114 in the form of a multifunctional material system 750, which includes a composite desiccant layer 752 including a matrix formed from a material as described above with respect to the variably permeable layer 114a and a desiccant material 560 embedded therein. The concentration (e.g., volume fraction) of the desiccant material 560 can vary throughout the thickness. As an example, the concentration of the desiccant material 560 in the first portion 754 of the multifunctional material system 750 can be a relatively low value, and the concentration of the desiccant material 506 in the second portion 756 of the multifunctional material system 750 can be a relatively low value. In one particular embodiment, the concentration of the desiccant material 560 in the high concentration portion 756 can be about three times the concentration of the desiccant material 560 in the low concentration portion 754. So configured, the low concentration portion 754 of the multifunctional material system 750 can effectively function as the variably permeable layer 114a, and the high concentration portion 756 of the multifunctional material system 750 can effectively function as the desiccant layer 114b. The thickness of the low concentration portion 754 can be in the range of about 0.001 mm to about 0.1 mm, and the thickness of the high concentration portion 756 can be in the range of about 0.05 mm to about 20 mm. As further shown in FIG. 7, the multifunctional material system can optionally include a vapor permeable layer 602 adhered to one or both sides of the composite desiccant layer 752.

[0063] In certain embodiments, the multifunctional material system 114 may be incorporated into a building in the form of a separate membrane, such as a vapor barrier or building envelope. In other embodiments, it may be desirable to add multifunctionality to the building envelope without increasing the complexity of the building envelope. Thus, the multifunctional material system may also be integrated with one or more elements of the building envelope, such as cladding, underlayment, roofing, insulation, interior panels, etc.

[0064] As an example, the multifunctional material system 114 may be employed to form a functionalized building material. As shown in FIG. 8, a multifunctional material assembly 800 is formed by affixing any embodiment of the multifunctional material system 114 discussed herein to a substrate 802.

[0065] In certain embodiments, the multifunctional material system 114 can be secured to the substrate 802 by a vapor permeable adhesive 804. The permeability of the vapor permeable adhesive 804 can be selected from a range of 5 to 100 perms. Examples of vapor permeable adhesives include polyvinyl alcohol and rubber cement. Examples of substrates are vapor permeable and can include oriented strand board (OSB), insulation (e.g., rigid foam insulation), gypsum board, cement board, stucco, drywall, underlayment, roofing, sheathing, or building membranes, or another building material. So configured, all three functions of the multifunctional material system 114 can operate if the substrate 802 and adhesive 804 are permeable to water vapor.

[0066] In configurations where at least one of the substrate or adhesive is relatively impermeable to water vapor and acts as a vapor barrier (e.g., having a permeability of less than 0.01 perms), the multifunctional material system may no longer function as a vapor diode, although temperature and humidity regulation functions may be retained.

[0067] In alternative embodiments, the adhesive may be omitted and other mechanisms may be employed to secure the substrate to the multifunctional material system. In one aspect, nails, screws, or other fastening mechanisms may be employed. In another aspect, there may be a boundary between the substrate and the multifunctional material system (e.g., the variably permeable layer). Within the boundary, the variably permeable layer may expand within the substrate and mechanically lock thereto, the substrate may expand within the variably permeable layer and mechanically lock thereto, or a combination thereof may occur.

[0068] In a further alternative embodiment, the functions of the adhesive 804 and the variably permeable layer 114a can be combined into a single layer. FIG. 9 shows an embodiment of a multifunctional material assembly 800 in the form of a multifunctional material assembly 900 including a substrate 802, a desiccant layer 114b, and a variably permeable adhesive layer 902. The variably permeable adhesive layer 902 is interposed between the substrate 802 and the desiccant layer 114b and configured to attach the desiccant layer 114b to the substrate 802. The variably permeable adhesive is further configured to provide the functionality of a variably permeable layer, as described above. Examples of variably permeable adhesives include polyvinyl alcohol (PVA) and rubber cement. Combining multiple functions (adhesive and variably permeable) into the variably permeable adhesive layer 902 can reduce the number of layers required to achieve all three functions of the multifunctional material system 114 in the multifunctional material assembly 900. This simplification can reduce the manufacturing cost of the multifunctional material assembly 900.

[0069] In further embodiments of the multifunctional material assembly 800, the variably permeable layer 114a and the desiccant layer 114b may be separated from each other by one or more intervening layers. FIG. 10 illustrates another embodiment of the multifunctional material assembly 800 in the form of a multifunctional material assembly 1000. As shown, the substrate 802 is interposed between the variably permeable layer 114a and the desiccant layer 114b. Thus, the variably permeable layer 114a and the desiccant layer 114b are located on opposite sides of the substrate 802. When configured in this manner, the functionality of the multifunctional material system 114 can be maintained when the substrate 802 is permeable to water vapor. Optionally, one or more vapor permeable layers 602 may be interposed between the variably permeable layer 114a and the desiccant layer 114b.

[0070] FIG. 11 shows the multi-functional material assembly 800 in the form of a multi-functional material assembly 1100 including a composite desiccant layer 1102 in which the desiccant material 560 is embedded in a matrix formed from the material of the substrate 802. A variably permeable layer 114a is further attached to one side of the composite desiccant layer 1120. As previously mentioned, the substrate can be formed from materials including oriented strand board (OSB), insulation (e.g., rigid foam insulation), gypsum board, cement board, stucco, drywall, underlayment, roofing, sheathing, or building membrane. By combining the functionality of the desiccant material 560 with the additional functionality of the substrate 802, the number of layers required to achieve all three functions of the multi-functional material system 114 and the functionality of the substrate 802 can be reduced. This simplification can reduce the manufacturing cost of the multi-functional material assembly 1100.

[0071] An embodiment of the multifunctional material system 114 may employ additional architectures. FIG. 12 illustrates another embodiment of the multifunctional material system 114 in the form of a pocketed multifunctional material system 1200. The pocketed multifunctional material system 1200 includes a pocketed frame 1202 that defines one or more pockets 1204. The desiccant material 560 (e.g., desiccant particles) may occupy at least a portion of the volume of the pockets 1204. As shown in FIG. 12, the pocketed frame 1202 defines one or more pockets 1204 that include an opening 1206 at one end. The variably permeable layer 114a may be positioned to extend across the opening(s) 1206 of the pocket(s) 1204.

[0072] In one particular embodiment, the pocket 1204 contains only the desiccant material 560. That is, there is no binder or adhesive. Thus, the walls of the pocket 1204 (e.g., the pocketed frame 1202 and the variably permeable layer 114a) simply serve to retain the desiccant material 560 within the pocket 1204.

[0073] The pocketed frame 1202 may be formed from a material that is permeable to water vapor. By way of example, the pocketed frame 1202 may be formed from the same materials as those described above with respect to the vapor permeable layer 602 (e.g., one or more of polylactic acid (PLA), natural rubber, synthetic rubber, polymethylpentene (PMP), polystyrene (PS), polycarbonate (PC), polydimethylsiloxane (PDM), or wood). In an alternative embodiment, the permeability of the pocketed structure may be achieved by forming the pocketed structure using a material that includes a plurality of pores. By way of example, the pocketed structure may be formed from a mesh with openings smaller than the diameter of the desiccant particles. Further examples of materials from which the pocketed structure may be formed include one or more of a fabric, a fiber mat, an open cell foam, or a perforated plastic.

[0074] Figure 13 shows the multifunctional material system 1200 of Figure 12 secured to a substrate 802 to form a multifunctional material assembly 1300. As shown, a variably permeable adhesive layer 902 is interposed between the substrate 802 and the pocketed frame 1202; however, in alternative embodiments, other fastening mechanisms may be employed. Optionally, one or more vapor permeable layers may be provided (e.g., facing the substrate) to support the pocketed structure.

[0075] A building typically includes a building envelope that separates conditioned and unconditioned spaces. The building envelope may provide air, water, heat, light, and / or noise conduction resistance. It may be desirable for the building envelope to be substantially continuous in order to provide the desired conduction resistance, i.e., gaps present in the building envelope do not significantly affect the desired conduction resistance.

[0076] As mentioned above, the embodiments of the multi-function material assembly 800 discussed herein can be employed as a building envelope. In situations where the substrate 802 is a relatively flexible material, the multi-function material assembly 800 can be wrapped around the building frame. If such a flexible multi-function assembly is wrapped in a substantially overlapping manner, gaps can be avoided.

[0077] In situations where the substrate 802 is a relatively rigid material, embodiments of the multifunctional material assembly 800 may be formed as panels. The panels may be secured to a building frame to provide a building envelope. However, it may be appreciated that gaps and seams may exist between adjacent panels of the multifunctional material assembly 800. These gaps, if not addressed, may allow water vapor to bypass the multifunctional material system 114.

[0078] To address potential issues of gaps between panels of the multifunctional material assemblies 800, they may be employed as a building envelope. FIG. 14 illustrates a portion of a building envelope 1400 including a plurality of the multifunctional material assemblies 800 in the form of a multifunctional material panel 1402. As illustrated, the multifunctional material panel 1402 includes a core 1404 and a variably permeable layer 114a extending around three sides of the core 1404 and along a portion of the fourth side to form a lip 1406. The side of the core 1404 that is not completely covered by the variably permeable layer 114a may face the environment to be conditioned (e.g., the exterior environment 110), while the opposite side of the core 1404 that is covered by the variably permeable layer 114a may face the environment to be conditioned (e.g., the interior environment 106). The core 1404 may include a substrate 802 and a desiccant layer 114b. In one embodiment, the substrate 802 and the desiccant layer 114b may be separate layers. In another embodiment, the core may be in the form of a composite desiccant layer 1102 in which the desiccant material 560 is embedded within the matrix of the substrate 802.

[0079] A sealing material can be applied to form a substantially vapor-tight seal 1410 along the gaps 1412 between adjacent multifunctional material panels 1402. The sealing material can be any material that substantially inhibits the conduction of water vapor.

[0080] In the case of a cut-to-size functional material panel 1402, a new lip can be provided along the cut edge along with the variably permeable layer 114a. Additionally, a damaged multifunctional material panel 1402 can be spliced ​​together with other parts of the multifunctional material panel 1402 after sealing its edges and the edges of the gap 1412.

[0081] The sealing material can employ a variety of configurations. In one aspect, the sealing material can be an adhesive vapor barrier tape that is substantially impermeable to water vapor. The lip is present to ensure that the adhesive vapor barrier tape seals against the variably permeable layer 114a. Instead of, or in addition to, the adhesive vapor barrier tape, a vapor impermeable liquid sealant can be employed to form the seal 1410. In such an embodiment, the lip can be omitted.

[0082] Also provided is a method of manufacturing a multifunctional material assembly for use as a building material. In one operation, a substrate 802 is provided. As discussed above, embodiments of the substrate are vapor permeable and may include oriented strand board (OSB), insulation (e.g., rigid foam insulation), gypsum board, cement board, stucco, drywall, underlayment, roofing, cladding, or building membrane, or another building material.

[0083] Layers of the multifunctional material system can be deposited (e.g., by diffusion or spray coating) onto or incorporated into a substrate to form a multifunctional material assembly. In embodiments where the multifunctional material system includes multiple layers, the layers can be deposited sequentially. In certain embodiments, the multifunctional material assembly can be prepared remotely and secured to the building frame. In other embodiments, the substrate can be attached to the building frame, and then the multifunctional material system can be deposited sequentially onto the substrate.

[0084] Embodiments of the vapor permeable layer and the variably permeable layer can be deposited from an aqueous solution, and when the deposited aqueous solution of the layer dries, it can adhere to an underlying layer (e.g., a substrate, the other of the variably permeable layer or the vapor permeable layer, a desiccant layer, etc.) to provide a substantially continuous film of the vapor permeable layer or the variably permeable layer.

[0085] The embodiment of the desiccant layer can be made in various ways. In one aspect, the desiccant layer can be deposited from a slurry containing a binder and desiccant particles. The desiccant particles can be one or more of silica gel, zeolite, calcium oxide (CaO2), calcium sulfate (CASO4), lithium chloride (LiCl), clay, or activated carbon. Examples of binders can include polylactic acid (PLA), polytetrafluoroethylene (e.g., colloidal polytetrafluoroethylene), polyurethane (thermoplastic or foamed), silicone, natural rubber, synthetic rubber, polymethylpentene (PMP), polystyrene, polycarbonate (PC), polyvinyl alcohol (PVA), or polymethylmethacrylate (PMMA). Other polymers and resins are also contemplated.

[0086] In embodiments of the composite desiccant layer in which the matrix is ​​a foam (e.g., polyurethane foam), the foam may be formed from a reaction of two or more components that release gas. The foam matrix may be heated to dryness or may be self-heated by the reaction of two or more components. The deposited composite desiccant layer, when dried, may be adhered to a substrate to provide a substantially continuous film of the composite desiccant layer.

[0087] Alternative embodiments of the composite desiccant layer can be extruded continuously. In one aspect, the desiccant layer can be extruded from a mixture of thermoplastic polymer and desiccant particles. The desiccant particles can be one or more of silica gel, zeolite, calcium oxide (CaO2), calcium sulfate (CASO4), lithium chloride (LiCl), clay, or activated carbon. Examples of thermoplastic resins can include natural rubber, synthetic rubber, polylactic acid (PLA), polystyrene (e.g., high impact polystyrene [HIPS]), polymethylpentene (PMP), polycarbonate (PC), polyurethane (PU), polymethylmethacrylate (PMMA), or polyvinyl alcohol (PVA).

[0088] Exemplary technical effects of the methods, systems, and devices described herein include, by way of non-limiting example, a reduction in the average humidity inside the wall cavity due to the water vapor pumping effect, and a resulting reduction in the risk of one or more of mold, rot, mildew, and dust mites. Further exemplary technical effects include a stabilization of the relative humidity inside the enclosure, and the associated improvement in comfort and air quality. Additional exemplary technical effects include a stabilization of the interior temperature, and a reduction in the energy intensity of heating and cooling when the multifunctional membrane is located inside the enclosure. Other technical effects include a further reduction in the energy intensity of heating and cooling when the multifunctional material system is located outside, so that water collected from the environment at night can be used to evaporate and cool the exterior surface during the day. Further technical effects include a reduction in the risk of water condensation inside the wall, as a result of dampening the humidity swing inside the wall cavity.

[0089] Certain exemplary embodiments have been described to provide a general understanding of the principles of the structure, function, manufacture, and use of the systems, devices, and methods discussed herein. One or more of these embodiments are illustrated in the accompanying drawings. Those skilled in the art will appreciate that the systems, devices, and methods specifically described herein and illustrated in the accompanying drawings are non-limiting exemplary embodiments, and the scope of the present invention is defined only by the claims. Features illustrated and described in connection with one exemplary embodiment may be combined with features of other embodiments. Such modifications and variations are intended to be within the scope of the present invention. Furthermore, in this disclosure, similarly named components of an embodiment generally have similar features, and therefore, in a particular embodiment, each feature of each similarly named component is not necessarily described in full detail.

[0090] Approximate language used in this application throughout the specification and claims may be applied to modify any quantitative expression that may vary within acceptable limits without causing a change in the basic function involved. Thus, values ​​modified by the terms "about", "approximately", and "substantially" are not limited to the precise values ​​specified. In at least some cases, the approximation language may correspond to the precision of the instrument for measuring the value. Throughout the specification and claims, range limitations can be combined and / or mutually modified, and such ranges are specified and include all subranges contained therein, unless the context or language dictates otherwise.

[0091] Those skilled in the art will appreciate further features and advantages of the present invention based on the above-described embodiments. Accordingly, the present application is not to be limited by what has been particularly shown and described, except as specified in the appended claims. All publications and references cited herein are expressly incorporated by reference.

Claims

1. 1. A multifunctional material system comprising: a variable permeability layer that exhibits increased vapor permeability with increasing relative humidity; a desiccant-containing layer adjacent to the variably permeable layer; a vapor permeable layer disposed adjacent to at least one of the variably permeable layer and the desiccant containing layer; Equipped with when the relative humidity is higher adjacent to the variable permeability layer than the desiccant containing layer, water or water vapor moves in a first direction from the variable permeability layer to the desiccant containing layer, and when the relative humidity is higher adjacent to the desiccant containing layer than the variable permeability layer, water or water vapor moves in an opposing second direction from the desiccant containing layer to the variable permeability layer, the rate of water or water vapor movement in the first direction being greater than the rate of water or water vapor movement in the second direction; The desiccant-containing layer is a composite material including desiccant particles embedded in a matrix. Multifunctional material systems.

2. 1. A multifunctional material system comprising: a variable permeability layer that exhibits increased vapor permeability with increasing relative humidity; a desiccant-containing layer adjacent to the variably permeable layer; a vapor permeable layer disposed adjacent to at least one of the variably permeable layer and the desiccant containing layer; Equipped with when the relative humidity is higher adjacent to the variable permeability layer than the desiccant containing layer, water or water vapor moves in a first direction from the variable permeability layer to the desiccant containing layer, and when the relative humidity is higher adjacent to the desiccant containing layer than the variable permeability layer, water or water vapor moves in an opposing second direction from the desiccant containing layer to the variable permeability layer, the rate of water or water vapor movement in the first direction being greater than the rate of water or water vapor movement in the second direction; the desiccant-containing layer includes a first layer having a matrix formed from a variable permeability binder and a second layer having a matrix formed from a vapor-permeable binder, the first layer being the variable permeability layer; Multifunctional material systems.

3. 1. A multifunctional material system comprising: a variable permeability layer that exhibits increased vapor permeability with increasing relative humidity; a desiccant-containing layer adjacent to the variably permeable layer; a vapor permeable layer disposed adjacent to at least one of the variably permeable layer and the desiccant containing layer; Equipped with when the relative humidity is higher adjacent to the variable permeability layer than the desiccant containing layer, water or water vapor moves in a first direction from the variable permeability layer to the desiccant containing layer, and when the relative humidity is higher adjacent to the desiccant containing layer than the variable permeability layer, water or water vapor moves in an opposing second direction from the desiccant containing layer to the variable permeability layer, the rate of water or water vapor movement in the first direction being greater than the rate of water or water vapor movement in the second direction; The desiccant-containing layer is formed from a desiccant material having a porous structure, and the pore size in the porous structure decreases from a side of the desiccant-containing layer closer to the variable permeability layer to a side of the desiccant-containing layer farther from the variable permeability layer. Multifunctional material systems.

4. 4. The system of claim 1, wherein the vapor permeable layer is interposed between the desiccant-containing layer and the variably permeable layer.

5. 4. The system of claim 1, wherein the permeability of the variably permeable layer increases approximately exponentially with increasing relative humidity.

6. 3. The system of claim 1 or 2, wherein the desiccant-containing layer is substantially homogeneous.

7. At least a portion of the desiccant-containing layer is formed from a desiccant material, and the desiccant material may be silica gel, zeolite, calcium oxide (CaO ２ ), calcium sulfate (CaSO ４ 3. The system of claim 1 or 2, wherein the catalyst is at least one of lithium chloride (LiCl), clay, or activated carbon.

8. 4. The system of claim 1, wherein the vapor permeable layer is formed from polylactic acid (PLA), polytetrafluoroethylene, silicone, natural rubber, synthetic rubber, polystyrene, polymethylpentene (PMP), polycarbonate (PC), polyurethane (PU), or polymethylmethacrylate (PMMA).

9. The system of claim 1 , wherein the variably permeable layer is formed from polyamide or polyvinyl alcohol (PVA).

10. The system of claim 9 , wherein the polyamide is nylon.

11. 1. A wall assembly comprising: a wall cavity defining a first surface adjacent an interior of the building and a second surface adjacent an exterior of the building; an insulating material disposed within at least a portion of the wall cavity; A multifunctional material system according to claim 1 disposed on at least one of the first surface and the second surface of the wall cavity; A wall assembly comprising:

12. A substrate; A multifunctional material system; Equipped with The multifunctional material system comprises: a variable permeability layer that exhibits increased vapor permeability with increasing relative humidity; a desiccant-containing layer adjacent to the variably permeable layer; Including, all layers of the multifunctional material system are disposed on a surface of the substrate, or at least one layer of the multifunctional material system is included in the substrate and at least one layer of the multifunctional material system is disposed on the surface of the substrate; further comprising an adhesive layer interposed between the substrate and the layer of the multifunctional material system; the adhesive layer is the variable permeability layer; Multifunctional material assembly.

13. 13. The multi-functional material assembly of claim 12, wherein the substrate is oriented strand board (OSB), insulation, gypsum board, cement board, stucco, drywall, underlayment, roofing, coating, or architectural membrane.

14. A substrate; A multifunctional material system; Equipped with The multifunctional material system comprises: a variable permeability layer that exhibits increased vapor permeability with increasing relative humidity; a desiccant-containing layer adjacent to the variably permeable layer; Including, The variably permeable layer is disposed on a first surface of the substrate and the desiccant-containing layer is disposed on a second surface of the substrate opposite the first surface of the substrate.

15. A substrate; A multifunctional material system; Equipped with The multifunctional material system comprises: a variable permeability layer that exhibits increased vapor permeability with increasing relative humidity; a desiccant-containing layer adjacent to the variably permeable layer; Including, the desiccant-containing layer is formed from a matrix of the substrate and desiccant particles embedded in the substrate; The variably permeable layer is disposed on a surface of the desiccant-containing layer.