Cushioning bodies and shoe insoles comprising elastomeric materials and methods for forming same

Abstract

To provide a shock absorber and a shock absorber material including an elastomeric material.SOLUTION: An insole for a shoe includes an insole body of elastomeric material having a first major surface and a second major surface opposite the first major surface. A distance between the first major surface and the second major surface is between about 1 mm and about 10 mm. The elastomeric material defines a plurality of voids extending through the elastomeric material from the first major surface to the second major surface. Each void has a dimension between about 1 mm and about 3 mm in a plane parallel to at least one of the first major surface and the second major surface. A minimum distance between adjacent voids is between about 0.5 mm and about 3 mm. A shoe insole includes such a shock absorber. A method of forming an insole for a shoe includes providing an elastomeric material within a mold to form an insole body of elastomeric material.SELECTED DRAWING: Figure 2

Description

[Technical Field]

[0001] Priority claim This application claims the benefit of the filing date of U.S. patent application Ser. No. 15 / 700,786, filed Sep. 11, 2017, for "Cushions and Shoe Insoles Comprising Elastomeric Material and Methods of Forming Same."

[0002] FIELD OF THE DISCLOSURE Embodiments of the present disclosure generally relate to cushioning and cushioning materials that include elastomeric materials. [Background technology]

[0003] Cushioning materials have a variety of uses, including mattresses, seating surfaces, shoe inserts, packaging, and medical devices. Cushioning materials can be formulated and / or configured to reduce peak pressures on the cushioned object, thereby increasing human or animal comfort and protecting the object from damage. Cushioning materials can be formed from materials that deflect or deform under load, such as polyethylene or polyurethane foam (e.g., textured foam), vinyl, rubber, springs, natural or synthetic fibers, and flexible containers filled with fluids. Different cushioning materials can have different responses to a given pressure, and some materials may be better suited for different applications. Cushioning materials may also be used in combination with one another to achieve selected properties.

[0004] For example, the cushioning material may include a foam layer covered with a layer of a thermosetting elastomeric gel, such as a polyurethane gel or a silicone gel. Because polyurethane gels and silicone gels are generally structurally weak and / or sticky, the cushioning material may include a film, such as a thin thermoplastic polyurethane film, covering the gel. The film can enhance the strength of the gel and, because the film generally adheres to the gel but is not sticky itself, can prevent other materials from sticking to the gel.

[0005] Gels can be used for cushioning and / or temperature management. Gels can provide cushioning because they can hydrostatically flow to the shape of the object being cushioned and tend to cushion pressure peaks. Gels can also reduce shear stress. Gels can have high thermal mass and / or thermal conductivity and therefore can be used for heating (such as in hot packs for sore muscles), cooling (such as in cold packs for sprains or for a cooling sensation when lying on a mattress or pillow), or maintaining a given temperature (such as in mattresses used in warm or cool rooms). For example, the gel can be fused to the top of a mattress core, or a film can cover the gel. As another example, the gel can be used as the top layer of a gel-on-foam wheelchair cushion.

[0006] Conventional gel layers, with or without a plastic film, can act as a barrier to gases (e.g., air, steam, or other gases). This barrier can cause difficulties, such as discomfort, when body heat and / or sweat accumulate between the user's body and the gel layer. Even when a breathable material (such as a cover containing foam or batting fibers) is placed between the cushioned object and the gel, gas can only move laterally through the breathable material. Because gas cannot pass through the plastic film or gel, the plastic film or gel inhibits the gas from flowing out of the cushioned object. When the weight of the cushioned object compresses the breathable material, the lateral gas flow path can become more constricted. Summary of the Invention

[0007] In some embodiments, a shoe insole includes a body including an elastomeric material having a first major surface and a second major surface opposite the first major surface. The distance between the first major surface and the second major surface is about 1 mm to about 10 mm. The elastomeric material defines a plurality of voids extending through the elastomeric material from the first major surface to the second major surface. Each void of the plurality of voids has a dimension of about 1 mm to about 3 mm in a plane parallel to at least one of the first major surface and the second major surface. The minimum distance between adjacent voids of the plurality of voids is about 0.5 mm to about 3 mm.

[0008] In some embodiments, a method of forming a shoe insole includes providing an elastomeric material into a mold to form an insole body of the elastomeric material having a first major surface and a second major surface opposite the first major surface. The distance between the first major surface and the second major surface is about 1 mm to about 10 mm. The mold portion occupies a plurality of voids that extend through the elastomeric material from the first major surface to the second major surface. Each void of the plurality of voids has a dimension of about 1 mm to about 3 mm in a plane parallel to at least one of the first major surface and the second major surface. The minimum distance between adjacent voids of the plurality of voids is about 0.5 mm to about 3 mm.

[0009] In certain embodiments, a shoe includes an insole body having a non-gel component and a gel component adjacent to the non-gel component. The gel component includes a body of elastomeric material having a first major surface and a second major surface opposite the first major surface. The distance between the first major surface and the second major surface is about 1 mm to about 10 mm. The gel component defines a plurality of voids that extend through the gel component from the first major surface to the second major surface. Each void of the plurality of voids has a dimension of about 1 mm to about 3 mm in a plane parallel to at least one of the first major surface and the second major surface. The minimum distance between adjacent voids of the plurality of voids is about 0.5 mm to about 3 mm. [Brief explanation of the drawings]

[0010] [Figure 1] 1 is a schematic diagram showing a main surface of a cushioning element. [Figure 2] 2 is a simplified cross-sectional view of the cushioning element shown in FIG. 1. [Figure 3] 2 is an enlarged view of a portion of the cushioning element of FIG. 1. [Figure 4] 2 is a simplified cross-sectional view showing how the cushioning element of FIG. 1 can be formed in a mold. [Figure 5] 2 is a simplified cross-sectional view showing how the cushioning element of FIG. 1 can be formed in a mold. [Figure 6] 2 is a simplified cross-sectional view showing how the cushioning element of FIG. 1 can be formed in a mold. [Figure 7] 10A-10C are simplified cross-sectional views illustrating how a cushioning element can buckle. [Figure 8] 10A-10C are simplified cross-sectional views illustrating how a cushioning element may be inflated. [Figure 9] 1 is a schematic diagram showing a shoe insole. [Figure 10] 10 shows a more detailed cross-section of a portion of the insole of FIG. 9. [Figure 11] 1 is a schematic diagram showing an insert for a shoe insole. [Figure 12] 1 is a graph showing test data obtained from various conventional insoles. [Figure 13] 1 is a graph showing test data obtained from various conventional insoles. [Figure 14] 1 is a graph showing test data obtained from various conventional insoles. [Figure 15] 1 is a graph showing test data obtained from insoles containing gel. [Figure 16] 1 is a graph showing test data obtained from insoles containing gel. DETAILED DESCRIPTION OF THE INVENTION

[0011] As used herein, the term "cushioning element" means and includes any deformable device intended for use in cushioning one body from another. As a non-limiting example, a cushioning element (e.g., a seat cushion) may be a device that cushions another object that may come into contact with the human body. Includes materials intended for use in cushioning a human body from the body (e.g., chair seats).

[0012] As used herein, the term "elastomeric polymer" means and includes a polymer that can recover its original size and shape after being deformed. In other words, an elastomeric polymer is a polymer that has elastic or viscoelastic properties. Elastomeric polymers may also be referred to in the art as "elastomers." Elastomeric polymers include, but are not limited to, homopolymers (polymers with a single repeating chemical unit) and copolymers (polymers with two or more chemical units).

[0013] As used herein, the term "elastomeric block copolymer" means and includes elastomeric polymers having groups or blocks of homopolymers linked together, such as AB diblock copolymers and ABA triblock copolymers. AB diblock copolymers have two distinct blocks of homopolymer. ABA triblock copolymers have two blocks of a single homopolymer (A), each linked to a single block of a different homopolymer (B).

[0014] As used herein, the term "plasticizer" means and includes a substance added to another material (e.g., an elastomeric polymer) to increase the material's processability. For example, a plasticizer may increase the flexibility, softness, or extensibility of a material. Plasticizers include, but are not limited to, hydrocarbon fluids such as mineral oil. Hydrocarbon plasticizers can be aromatic or aliphatic.

[0015] As used herein, the term "elastomeric material" refers to and includes elastomeric polymers and mixtures of elastomeric polymers with plasticizers and / or other materials. Elastomeric materials are elastic (i.e., capable of recovering size and shape after deformation). Elastomeric materials include, but are not limited to, materials referred to in the art as "elastomeric gels," "gelatinous elastomers," or simply "gels."

[0016] As used herein, any relational terms such as "first," "second," "top," "bottom," etc. are used for clarity and convenience in understanding the disclosure and accompanying drawings, and do not imply or depend on any particular configuration, orientation, or order unless the context clearly indicates otherwise.

[0017] As used herein, the term "and / or" means and includes any and all combinations of one or more of the associated listed items.

[0018] The figures shown herein are not actual illustrations of particular materials or devices, but merely idealized representations used to explain embodiments of the present disclosure. Elements common between figures may retain the same numerical designations.

[0019] The present disclosure describes cushioning elements that include a gel (i.e., an elastomeric material) with voids that extend through the gel. In response to an applied force, the gel can be configured to deform by expanding before the gel can buckle. Buckling occurs when the shape of the support member changes suddenly. When the support member buckles, the load on the cushioned object is reduced. The load on the cushioned object, if any, can be transferred to other support members. Buckling is generally described in U.S. Pat. No. 7,730,566, issued June 8, 2010, entitled "Multi-walled Gelastic Material," and U.S. Pat. No. 8,919,750, issued December 30, 2014, entitled "Cushioning Elements Comprising Buckling Walls and Methods of Forming Such Cushioning Walls." "Bulging Elements," the entire disclosures of each of which are incorporated herein by reference. Bulging includes outward deformation of the material, typically in all directions perpendicular to the applied force. Bulging is generally described in U.S. Pat. No. 3,997,151, issued Dec. 14, 1976, for "Modular Cushioning Pad." Cushioning elements that deform by buckling and bulging may be referred to as "semi-buckled, semi-bulged."

[0020] Figure 7 shows cushioning element members 2, 4, 6, and 8 buckling when a force is applied (i.e., relative to the top and bottom of members 2, 4, 6, and 8 in the orientation of Figure 7). For example, member 2 is shown buckling approximately in half. Member 4 is shown buckling at multiple points such that the central portion of member 4 folds over on itself. Members 6 and 8 are shown buckling outward in opposite directions from each other. In other embodiments, the members may buckle toward each other.

[0021] Figure 8 shows cushioning member 10 expanding when a force is applied (i.e., relative to the top and bottom of member 10 in the orientation of Figure 8). The cross section of member 10 increases in the center as the height of the material decreases. Cushioning elements disclosed herein may exhibit the expanding characteristic. Such cushioning elements may provide sufficient resistance to withstand relatively high levels of force exerted in a concentrated area.

[0022] FIG. 1 is a schematic diagram showing a major surface (e.g., top or bottom) of cushioning element 102. FIG. 2 is a simplified cross-sectional view of cushioning element 102. FIG. 3 is an enlarged view showing a portion 103 of cushioning element 102. Cushioning element 102 includes gel 105 that defines a void 104 that extends through cushioning element 102 from a first major surface 106, referred to for simplicity as top surface 106, to a second major surface 108, referred to for simplicity as bottom surface 108. Cushioning element 102 can be in any orientation, with top surface 106 and bottom surface 108 needing to be placed at the top and bottom, respectively.

[0023] Gel 105 may be formed, for example, as described in U.S. Pat. No. 5,994,450, issued Nov. 30, 1999, entitled "Gelatinous Elastomer and Methods of Making and Using," the disclosure of each of which is incorporated herein by reference in its entirety. "The Same and Articles Made Therefrom," U.S. Patent No. 7,964,664, issued June 21, 2011, "Gel with Wide Distribution of MW in Mid-Block," U.S. Patent No. 4,369,284, issued January 18, 1983, "Thermoplastic Elastomer Gelatinous Compositions," U.S. Patent No. 8,919,750, issued December 30, 2014, "Cushioning Elements Comprising Buckling Walls and Methods The gel 105 may be a gel or elastomeric material such as those described in "The Art of Forming Such Cushioning Elements." The gel 105 may include an elastomeric polymer and a plasticizer. The gel 105 may be a gelatinous elastomer, a thermoplastic elastomer, a natural rubber, a synthetic elastomer, a blend of natural and synthetic elastomers, or the like.

[0024] The gel 105 can include ABA triblock copolymers such as styrene ethylene propylene styrene (SEPS), styrene ethylene butylene styrene (SEBS), and styrene ethylene ethylene propylene styrene (SEEPS). For example, ABA triblock copolymers are currently commercially available from Kuraray America, Inc. (Houston, TX) under the tradename SEPTON® 4055 and from Kraton Polymers, LLC (Houston, TX) under the tradenames KRATON® E1830, KRATON® G1650, and KRATON® G1651. In these examples, the "A" block is styrene. The "B" block is a rubber (e.g., butadiene, isoprene, etc.) or hydrogenated rubber (e.g., ethylene / propylene, ethylene / butylene, etc.) that can be plasticized with mineral oil or other hydrocarbon fluids. The gel 105 may be a styrene-based copolymer, such as ethylene, ethylene / ethylene / propylene, etc. The gel 105 may comprise an elastomeric polymer other than a styrenic copolymer, such as a non-styrene elastomeric polymer that is thermoplastic in nature, or that can be solvated with a plasticizer, or that is a multi-component thermoset elastomer.

[0025] Gel 105 may include one or more plasticizers, such as a hydrocarbon fluid. For example, gel 105 may include an aromatic-free food-grade white paraffinic mineral oil, such as those sold under the trade names BLANDOL® and CARNATION® by Sonneborn, Inc. (Mahwah, NJ).

[0026] In some embodiments, gel 105 may have a plasticizer to polymer ratio of about 0.1:1 to about 50:1 by weight. For example, gel 105 may have a plasticizer to polymer ratio of about 1:1 to about 30:1 by weight, or even about 1.5:1 to about 10:1 by weight. In further embodiments, gel 105 may have a plasticizer to polymer ratio of about 4:1 by weight.

[0027] The gel 105 may have one or more fillers (e.g., lightweight microspheres). The fillers may affect the thermal properties, density, processing, etc. of the gel 105. For example, hollow microspheres (e.g., hollow glass microspheres or hollow acrylic microspheres) may reduce the thermal conductivity of the gel 105 by acting as insulators because such hollow microspheres (e.g., hollow glass microspheres or hollow acrylic microspheres) may have a lower thermal conductivity than the plasticizer or polymer. As another example, metal particles (e.g., aluminum, copper, etc.) may increase the thermal conductivity of the resulting gel 105 because such particles may have a higher thermal conductivity than the plasticizer or polymer. Microspheres filled with wax or another phase change material (i.e., a material formulated to undergo a phase change near the temperature at which the buffer element will be used) may provide temperature stability (i.e., due to the heat of fusion of the phase change) at or near the phase change temperature of the wax or other phase change material within the microsphere. The phase change material may have a melting point of about 20°C to about 45°C.

[0028] The gel 105 may also include an antioxidant, which may reduce the effects of thermal degradation during processing or improve long-term stability. Antioxidants include pentaerythritol tetrakis(3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate, available from BASF Corp. (Iselin, NJ) as IRGANOX® 1010 or from Everspring Corp. USA (Los Angeles, CA) as EVERNOX®-10; octadecyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate, available from BASF Corp. as IRGANOX® 1076 or from Everspring Chemical as EVERNOX® 76; and octadecyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate, available from BASF Corp. (Iselin, NJ) ... Examples of antioxidants include tris(2,4-di-tert-butylphenyl) phosphite, available commercially from Chemical Industries, Ltd. as EVERFOS™ 168. One or more antioxidants may be combined in a single formulation of the elastomeric material. The use of antioxidants in mixtures of plasticizers and polymers is described in columns 25 and 26 of U.S. Pat. No. 5,994,450, previously incorporated by reference. The gel 105 may contain up to about 5% by weight of antioxidant. For example, the gel 105 may contain from about 0.10% to about 1.0% by weight of antioxidant.

[0029] In some embodiments, the gel 105 may include a resin. The resin may be selected to modify the elastomeric material to slow the rebound of the cushioning element 102 after deformation. The resin, if present, may be a hydrogenated pure elastomeric resin, such as that available under the trade name REGALREZ® from Eastman Chemical Company (Kingsport, TN). The resin, when present, may function as a tackifier, increasing the tackiness of the surface of the gel 105.

[0030] In some embodiments, the gel 105 may include a pigment or combination of pigments. The pigments may be aesthetic and / or functional. That is, the pigments may provide the cushioning element 102 with an appearance that is appealing to consumers. Additionally, a cushioning element 102 with a dark color may absorb radiation differently than a cushioning element 102 with a light color.

[0031] Gel 105 may include any type of gelatinous elastomer. For example, the elastomeric material may include a melt blend of 1 part by weight of a styrene-ethylene-ethylene-propylene-styrene (SEEPS) elastomeric triblock copolymer (e.g., SEPTON® 4055) and 4 parts by weight of a 70-weight straight-cut white paraffinic mineral oil (e.g., CARNATION® white mineral oil), and optionally pigments, antioxidants, and / or other additives.

[0032] The gel 105 may include a material that can return to its original shape after deformation and can be elastically stretched. The gel 105 may feel rubbery, but may conform to the shape of an object that applies a deformation pressure better than conventional rubber materials and may have a lower durometer hardness than conventional rubber materials. For example, the gel 105 may have a hardness on the Shore A scale of less than about 50, from about 0.1 to about 50, or less than about 5.

[0033] In an undeformed state, cushioning element 102 can have a thickness of about 1 mm to about 10 mm. That is, the distance between top surface 106 and bottom surface 108 can be about 1 mm to about 10 mm. In some embodiments, cushioning element 102 can have a thickness of about 1.5 mm to about 7 mm, or about 2 mm to about 3 mm.

[0034] 1 as being cylindrical (i.e., having a circular cross-section in the plane of the top surface 106 and bottom surface 108), the void 104 may have any selected shape. For example, the void 104 may have a cross-section that is triangular, square, rectangular, trapezoidal, diamond-shaped, hexagonal, quadrilateral with octagonal cross-section, etc.

[0035] As shown in FIG. 3, in an undeformed state, the void 104 may have a maximum dimension x in the plane of the top surface 106 and the bottom surface 108. For a cylindrical void 104, the maximum dimension x is the diameter. For other shapes, the maximum dimension x may be the length of a side, the length of a diagonal, etc. The maximum dimension x may be from about 1 mm to about 3 mm, such as from about 1.5 mm to about 2.5 mm. In some embodiments, the maximum dimension x may be about 2 mm.

[0036] 3, in the undeformed state, the voids 104 may be separated by gel 105 such that the minimum distance y between adjacent voids 104 is between about 0.5 mm and about 3 mm, such as between about 0.8 mm and 1.5 mm. For example, the minimum distance y may be about 1.2 mm.

[0037] Distance x+y is the center-to-center distance between adjacent voids 104, which may be about 1.5 mm to about 6 mm, such as about 2.0 mm to 4.0 mm. For example, distance x+y may be about 3.0 mm. The ratio of x to thickness may be selected to be low enough so that the gel 105 does not buckle when force is applied to the cushioning element 102. That is, a thicker cushioning element 102 may require a relatively thick wall to prevent buckling.

[0038] In an undeformed state, each void 104 has a top surface 106 and a bottom surface 108, respectively. 1 and 3, the voids 104 may have a longitudinal axis perpendicular to the top surface 106 and / or the bottom surface 108. For example, if the voids 104 have a circular cross-section, the voids 104 may be right cylindrical, as shown in Figures 1 and 3. The voids 104 may each have a uniform cross-sectional area in each plane parallel to the top surface 106 and / or the bottom surface 108 when the cushioning element 102 is in an undeformed state.

[0039] When cushioning element 102 is in an undeformed state, the volume of void 104 (i.e., volume 108 between top surface 106 and bottom surface) can be about 25% to about 40% of the total volume of cushioning element 102. For example, the volume of void 104 can be about 30% to about 35% of the total volume of cushioning element 102.

[0040] The thickness of the cushioning element 102, the maximum dimension x of the voids 104, and the minimum distance y between adjacent voids 104 may be selected so that when a force perpendicular to the top surface 106 (or a force having a component perpendicular to the top surface) is applied to the cushioning element 102, a portion of the gel 105 will swell and deform or collapse voids 104 near the applied force before the top surface 106 bottoms out against the bottom surface 108. The voids 104 may be large enough to allow the gel 105 to swell, but may be too small for the gel 105 to buckle. Thus, the load on the cushioning element 102 (when the object being cushioned is a person or other animal) can be spread over a larger area, reducing maximum pressure and increasing comfort.

[0041] In some embodiments, cushioning element 102 may include a non-gel material secured to gel 105. For example, as shown in FIG. 2, cushioning element 102 may include material 110, such as fabric, foam, or a polymer sheet. Material 110 may be secured to gel 105 by an adhesive, or may be melt-bonded or friction-secured in place. In certain embodiments, gel 105 may be secured to material 110 by overmolding, without the two materials being physically interlocked.

[0042] cushioning element 102 may be, by way of non-limiting example, a shoe insole; a shoe midsole; a sock liner; a footbed of any kind; a wrist rest; a bathroom mat, such as for use near a shower, bathtub, or sink (often referred to as a bath mat); a mat for use near a toilet; a mat for use near a kitchen sink (often referred to as a kitchen mat); a standing mat (often referred to as an anti-fatigue mat) for a cashier or clerk in a retail store or a machinist or other mechanical worker in a manufacturing industry; a seat cushion; a yoga mat; a mat for kneeling during prayer or religious acts or ceremonies mats for use when kneeling (often known as prayer mats); landing mats for sporting events such as gymnastics or track and field; carpet pads; flooring; area rugs, pads and mats; cushions for kneeling or sitting; seat cushions; personal exercise pads; pads for use while weightlifting; martial arts mats; wearable impact pads for sports and martial arts; martial arts pads for punching and kicking; mats to prevent bodily injury if the body falls from a bed; mats for use on horses while traveling in a horse box; and may be used as cushions for shipping sensitive electronic components.

[0043] Cushioning element 102 may be formed in a mold configured and adapted to receive gel material (e.g., a liquid form of gel 105 or a precursor to gel 105) and form the gel material in the shape of cushioning element 102. For example, as shown in FIG. 4, if the cushioning element 102 to be formed includes material 110 bonded to gel 105, material 110 may be disposed between sections 202, 204 of mold 206. Section 202 may have a complementary shape such that material 110 conforms to the shape of mold 206 when sections 202, 204 are pressed together, as shown in FIG. 5. Mold 206 may include walls and surfaces configured to define voids 104 of cushioning element 102 shown in FIGS. 1-3.

[0044] To form the cushioning element 102, a gel material may be provided within the mold 206. For example, the gel 105 may be formed by heating the ABA triblock copolymer and any other components, as described above, and injecting the gel material into the mold 206. Injection molding is described, for example, in U.S. Pat. No. 9,446,542, "Small Footprint Apparatus, Method, and Tooling for Molding Large Thermoplastic Parts," issued September 20, 2016, the entire disclosure of which is incorporated by reference. When the mold 206 contains the material 110, the molten gel may at least partially penetrate the material 110 (e.g., penetrate between the fibers of a fabric or penetrate into the pores of a porous material). In some embodiments, the molten gel may completely penetrate the material 110 such that the molten gel can flow across the material 110 through the mold 206.

[0045] In some embodiments, pressure may be used to aid in the penetration of the gel material into the mold 206, including the fibers and / or pores of the material 110, and / or to aid in overmolding adhesion and to mold the component into a selected edge shape. The mold 206 may be used to shape the gel material into the desired final shape of the gel sections or gel pattern, as well as the overall shape of the final cushioning element 102. For example, sections 202, 204 may define flat interiors with beveled edges. In some embodiments, the gel may be molded in such a manner that the molten gel is provided to the mold 206 on the same side of the material 110 as it will be after cooling. In other embodiments, the molten gel may be provided to the mold 206 in such a manner that it passes through the material 110 and into mold cavities on the other side of the material 110; this passage may be enabled in part by pores in the material 110 or by tearing or otherwise splitting the material 110. In some embodiments, an injection molding process may be used to force the gel under pressure into the mold cavities and into the pores of material 110, or against material 110 during overmolding.

[0046] As the gel cools, it may bond to material 110. After the gel cools, cushioning element 102 may be removed from mold 206 by separating sections 202, 204 of mold 206, as shown in FIG. 6. For example, separating sections 202, 204 may leave cushioning element 102 attached to one section 202. Cushioning element 102 may then be removed from section 202, as shown in FIG.

[0047] In some embodiments, a precursor of gel 105 formulated to react upon exposure to heat, pressure, humidity, etc. may be provided to mold 206, and gel 105 may be formed within mold 206. For example, the precursor may include a curing agent such that the precursor cures without exposure to heat, pressure, humidity, etc. The precursor may react to form crosslinks between polymer chains. The precursor may be pourable so that mold 206 can be easily filled with the elastomeric precursor prior to curing.

[0048] In other embodiments, the gel 105 may be reversibly heated and cooled. In such embodiments, gel 105 may be provided in the mold 206 in excess of the amount needed to form the cushioning element 102. The gel 105 may be cooled, and the cushioning element 102 and excess material may be removed from the mold 206. The excess material may be separated from the cushioning element 102, remelted, and reused (e.g., by re-injecting the gel 105 into the mold 206) to form another cushioning element 102. A gel 105 that can be reversibly heated and cooled may be advantageously used because the excess material is not wasted. Thus, the cushioning element 102 may be formed at a relatively lower average material cost than a cushioning element formed from a material that cannot be reused. Furthermore, if the gel material can be forced into and extruded through the mold 206 without concern for wasting excess gel material, the cushioning element 102 may be formed with higher quality. That is, by flowing the gel material through the mold 206 This may help ensure that the gel material fills the entire mold 206 without leaving behind air bubbles (which tend to form additional voids that would cause the cushioning element 102 to have different properties). Also, cushioning element 102 may be formed with fewer processing steps compared to conventional cushioning elements, such as by eliminating the need to separately place and bond material 110 to gel 105 after its formation.

[0049] In some embodiments, material 110 is provided in a roll, and material 110 can be moved as or after injection molding shots are performed. Gel 105 can be configured to be applied without gaps between shots. In certain embodiments, there can be gel-on-gel or overmolding, such that gel 105 is continuous on material 110 in the roll direction. For example, a continuous carpet pad or continuous carpet with an integral gel pad can be made in this manner.

[0050] For example, material 110 may be trimmed to form a mat by cutting the perimeter of gel 105. Piping or other binding or sewing may be used to "trim" the edges of the mat, or they may be left cut. The cut in material 110 may be away from the edge of gel 105, around the periphery of gel 105, or through part of gel 105, etc. If the cut is a short distance from gel 105, a sewing needle may not need to penetrate gel 105, and it may be easier to sew the piping. In another embodiment, no fabric or non-gel material is applied between the plates in the molding process; instead, the molten gel fills the holes, cools in mold 206, and is removed from mold 206 as a semi-inflated, semi-buckled gel without any other material.

[0051] The overall shape of the mold 206 can advantageously provide benefits and aesthetics. For example, the mold 206 can be used to create the cushioning element 102 as a flat shoe insole with vertical edges, but if the edges are chamfered or shaped so that they do not terminate abruptly at a surface corresponding to the mold opening direction, it may be more aesthetically pleasing and more comfortable for the user. The force of the molding pressure can form the material 110 into a desired shape, which may be part of the shape of the mold cavity, and solidifying the gel 105 can maintain the material 110 in the general shape it had when the mold 206 opened. A flat bevel at 45 degrees or other angle may be used, or a bevel with a curved surface or any other edge shape may be used. The cushioning element 102 need not be flat but may be shaped for any selected use. For example, the cushioning element 102 may include a raised arch support, a heel cup, or another contour to accommodate a person's foot. Because injection molding (as opposed to gel injection casting) can be molded into nearly infinite shapes, and because the material 110 is forced from its original flat shape to conform to the shape of the mold and maintains that shape due to permanent stretching during molding and / or shaping of the gel 105 after solidification, the cushioning element 102 formed as described above need not be flat on any side, but may have approximately any selected edge shape.

[0052] In some embodiments, it has been a surprising result that the molten gel may be inserted into the mold 206 on the side of the material 110 (often fabric) opposite the side where the gel 105 may be present. The molten gel may also be injected onto the side of the material 110 where the gel 105 may be present in the final product. In either case, the molding pressure may be sufficient to partially or completely infiltrate the pores of the material 110 directly adjacent the gel 105 of the cushioning element 102.

[0053] In some embodiments, material 110 may be a laminated non-gel component having an outer material (e.g., a non-porous material) laminated to an inner material (e.g., a material that is sufficiently porous for the gel to infiltrate and interlock with, or a material that the gel can overmold). Such laminated materials may be formed by any selected method, including adhesive bonding, thermal bonding, welding, etc. In certain embodiments, the outer material may be more porous than the inner material.

[0054] In some applications, it may be necessary to cover both sides of the gel 105 of the cushioning element 102 with a non-gel material, such as foam or cloth. For example, a shoe insole may benefit from a bottom scrim layer (i.e., reinforcement) to maintain the shape of the insole and adhere the insole to a surface such as the outsole or midsole of the shoe. The shoe insole may also benefit from a cloth covering the top of the gel 105 to provide moisture wicking, protect the gel 105 from dirt or other undesirable substances that may adhere to it, and improve the user's experience when putting on and taking off a shoe with the gel inside (e.g., because the gel may adhere too tightly to socks). To achieve a layer covering both sides of the gel 105, one or both sides of the gel 105 may be laminated using pressure and heat, or one or both sides may be glued together during the molding process.

[0055] In some embodiments, if the gel 105 is adhered to another surface, such as a midsole or outsole, the cushioning element 102 may be glued completely or only in convenient locations. For example, if the cushioning element 102 has a stiff scrim on one side to help it maintain its shape, gluing the cushioning element 102 in one location (e.g., the heel of an insole) may be sufficient to hold the cushioning element 102 in place. This may provide a simplified and cheaper manufacturing process by reducing the amount of adhesive or other glue needed and controlling the surface area covered by adhesive.

[0056] FIG. 9 is a schematic diagram illustrating a shoe insole 302. The insole 302 includes cushioning elements 304, 306, which may include the gel material described above. The cushioning elements 304, 306 may be secured within a non-gel component 308. The non-gel component 308 of the insole 302 may include, for example, polyethylene-vinyl acetate (EVA) or foam. The cushioning elements 304, 306 may be patched throughout the insole 302, such as in the heel region, arch region, or other selected portions of the insole 302. For example, the non-gel component 308 may laterally surround each of the cushioning elements 304, 306. In other embodiments, the insole may consist essentially of the gel cushioning elements without lateral non-gel components (with or without covers above or below the gel cushioning elements). FIG. 10 shows a more detailed cross-section of a portion of the insole 302. The cushioning element 304 is shown in the center portion of the insole 302 so that it can support a majority of the load (i.e., force) on a foot placed on the insole. The edges of the insole 302 may be tapered to fit the shoe and can support a relatively small portion of the load under normal use. To secure the cushioning elements 304, 306 to the non-gel component 308, the cushioning elements 304, 306 may be bonded using an adhesive such as a pressure-sensitive adhesive. In some embodiments, a cover material such as a fabric liner may be glued onto the top of the cushioning elements 304, 306 and secured to the non-gel component 308 surrounding the cushioning elements 304, 306.

[0057] FIG. 11 is a schematic diagram illustrating an insert 402 for a shoe insole 404. The insert 402 may be configured to be placed within a slot or pocket 406 within the insole 404. The insert 402 may be modular, allowing different inserts 402' to be used instead of or in addition to the insert 402. The inserts 402, 402' may be selected to have different thicknesses or different cushioning characteristics. The shape or cushioning characteristics of the insole 404 may be changed by replacing one insert 402, 402' (or a group of inserts) with another. Thus, the insole 404 may be modified to accommodate different users or different uses (e.g., walking vs. running). Additionally, users may try different inserts 402, 402' depending on their leisure time and may change between different inserts 402, 402' as needed to find a comfortable fit.

[0058] The inserts 402, 402' may be made partially or entirely of gel, as described above. In some embodiments, the inserts 402, 402' are inserted into the pockets 406. A portion of the insole 404 near the pocket 406 may also be made of gel so that the inserts 402, 402′ tend to stick to the walls of the pocket 406 when inserted. The stickiness of the gel may prevent the inserts 402, 402′ from slipping out of the pocket 406 once the inserts 402 are placed in the shoe. Additionally, the flexibility of the gel may allow the pocket 406 to effectively accommodate inserts 402, 402′ of different sizes. One benefit of an insole 404 with modular inserts 402, 402′ is that manufacturers and retailers can limit the number of unique packages (SKUs, or stock-keeping units), because a single package with multiple inserts 402, 402′ can accommodate a wider variety of users than a single, one-piece insole. [Example]

[0059] Comparative Example 1: Conventional insole Figures 12-16 show test data obtained from various insoles having a thickness of approximately 3 mm. To obtain the data shown in Figures 12-14, three different commercially available memory foam insoles were tested to measure the amount of force the insoles could support as a function of compression depth. The force was measured at 0.75 in. 2 (4.84cm 2 ) area. In both cases, an inflection point appears in the curve, indicating buckling of the material and a relatively sudden change in the feel of the insole.

[0060] Example 2: Formation and Use of the Mold A mold was created by machining holes into a lower plate (see, for example, the lower section 204 of mold 206 shown in FIG. 4). A top plate was created that, when attached to the lower plate, completed the overall shape of the gel component and formed a hole for the gel (see, for example, the upper section 202 of mold 206 shown in FIG. 4). A mixture of 1 part by weight SEPTON® 4055 SEEPS polymer and 3 parts by weight Carnation Oil (a 70% by weight undiluted white paraffinic mineral oil) was combined with 0.25% by weight IRGANOX® 1070 antioxidant (available from BASF Corp., Iselin, NJ), 0.25% by weight IRGAFOS® 168 antioxidant (available from BASF Corp.), and 0.25% by weight Horizon Blue aluminum lake pigment (available from Day-Glo Color Corp., Cleveland, OH). The mixture was passed through a heated extruder to melt-blend the materials and then pumped into a piston heated above the melting temperature of the gel. The fabric was inserted between two temperature-controlled plates, which were closed onto the fabric (see Figure 5). The heated piston was connected to a heated tube connected to a heated sprue-and-runner system on one of the plates, forcing the gel into the holes in the lower plate. The piston was driven forward, causing the molten gel to fill the holes and penetrate the fabric under pressure.

[0061] After the molten gel filled the mold cavity and soaked into the fabric, the gel was allowed to cool. The plates were separated (see Figure 6) and the fabric with the cast gel was lifted from the mold.

[0062] Example 3: Gel cushioning insole An insole was formed having dimensions similar to those tested in Example 1. Using a mold as described in Example 2, an insole was formed with gel material approximately 3 mm thick. The gel material had a cylindrical void approximately 2 mm in diameter with a minimum distance y of approximately 1.2 mm (see FIG. 3). This void constituted approximately 33% of the volume of the insole in its undeformed state. This insole was subjected to the same testing as described in Example 1. The data shown in FIG. 15 appear to have no inflection points. Therefore, it appears that the gel material of the insole expands, limiting the effects of potential buckling.

[0063] Example 4: Gel cushioning insole An insole was formed and tested as described in Example 3, except that the gel material was approximately 13 mm thick. The data shown in Figure 16 shows an inflection point, indicating that the gel material buckled. Without being bound by any particular theory, it appears that the thickness of the material, in combination with other dimensions and properties of the gel, determines whether or not the gel material buckles. To avoid a sudden change in the force applied to the insole user due to buckling, the thickness of the insole can be selected to be below the threshold at which the inflection point appears.

[0064] Again, without being bound by any particular theory, the insole of Example 3 appears to have no inflection points because the voids in the gel allow the gel spaces to expand in different directions. In contrast, if the gel is stiff and compressed, there is no place for it to deform when force is applied. Thus, such a gel may feel stiff and ill-fitting despite its soft and flexible nature. In Example 3, the gel can expand outward, but the walls of the internal voids can also expand into the surrounding voids, thereby providing space for the gel to deform and allowing for better cushioning. Such internal deformation can also occur when the gel is compressed by an external boundary. Traditional formed gels, or gels molded into voids (e.g., hollow cylinders or gels with gaps between gel segments or embossed into geometric patterns), can be effective in cushioning and may be less expensive than stiff gels because less gel material can be used, but they may not provide adequate force deflection when pressure is applied over a small surface area. To achieve adequate force deflection for small pressure points, the voids may be selected to be small enough and the walls thick enough that they cannot buckle before bulging into adjacent voids.

[0065] Buckling alone may be undesirable because the user will feel a sudden change in pressure when the material collapses. Additionally, buckling of the material may bottom out upon collapse. Expanding materials may provide benefits such as pressure equalization, vibration damping, and shock absorption.

[0066] One property of a solid mass of gel (i.e., no voids) that may be desirable in some products is that it may prevent residue, dirt, water / liquid, or other substances from entering the gel component. This effect can be achieved with the voided gel materials described herein, at least in part, by adding a solid gel "skin" to the interface between the gel and non-gel components, where the skin may be integrally formed with the remainder of the gel. In such cases, the skin may be part of the entire gel component that is connected to or overmolded with the non-gel component.

[0067] In some embodiments, molding a semi-buckled, semi-bulging gel, or any other gel configuration with an internal space or void, creates a pattern on the exterior of adjacent non-gel components. For example, a semi-buckled, semi-bulging gel with a round hole can create an aesthetically desirable design pattern that enhances the brand or appearance of the shoe in which it is placed.

[0068] In some embodiments, the edges of non-gel components may be encapsulated in the gel, such as at the border of the gel, even after trimming to final product dimensions. This may be aesthetically desirable and may have functional benefits (e.g., as described above with respect to skins). The gel may pass through or around the edges of the fabric and then be trimmed, or the fabric may be trimmed prior to molding and precisely positioned in the mold by placing pins or other means.

[0069] The gel components may be wholly or partially waterproof, water resistant, and / or hand or machine washable with or without soap / detergent.

[0070] The gel components may be of any color, and the gel may be colorless and transparent, with or without dyes and / or may be effectively pigmentable.

[0071] The gel component may have members that extend across the voids within the gel (e.g., parallel to the generally flat, upstanding surface of the insole). For example, there may be crossbeams running diagonally from corner to corner that are no thicker than the height of the hollow post; these gel crossbeams may function to reinforce or stabilize the insole, reducing the tendency of the gel to deform unidirectionally under pressure, which may cause irritation to a person's foot. In some embodiments, the skins described above may also effectively function to reinforce the insole laterally and may be considered laterally extending members as described in this paragraph.

[0072] Further non-limiting exemplary embodiments of the present disclosure are described below.

[0073] Embodiment 1: A shoe insole comprising an insole body comprising an elastomeric material having a first major surface and a second major surface opposite the first major surface. The distance between the first major surface and the second major surface is about 1 mm to about 10 mm. The elastomeric material defines a plurality of voids that penetrate the elastomeric material from the first major surface to the second major surface. Each void of the plurality of voids has a dimension of about 1 mm to about 3 mm in a plane parallel to at least one of the first major surface and the second major surface. The minimum distance between adjacent voids of the plurality of voids is about 0.5 mm to about 3 mm.

[0074] Embodiment 2: An insole as described in embodiment 1, wherein when a force is applied to the insole body in a direction perpendicular to the first major surface, a portion of the elastomeric material expands and collapses voids in the vicinity of the applied force before the first major surface bottoms out against the second major surface.

[0075] Embodiment 3: An insole according to embodiment 1 or embodiment 2, wherein the elastomeric material is attached to another component having a material composition different from that of the elastomeric material.

[0076] Embodiment 4: An insole according to embodiment 3, wherein the body of elastomeric material is attached to another component by adhesive.

[0077] Embodiment 5: An insole according to embodiment 3, wherein the elastomeric material is melt bonded to another component.

[0078] Embodiment 6: An insole according to any one of embodiments 3 to 5, wherein the other component comprises fabric.

[0079] Embodiment 7: An insole according to any one of embodiments 1 to 6, wherein each of the plurality of voids has a major axis perpendicular to each of the first main surface and the second main surface.

[0080] Embodiment 8: An insole described in any one of embodiments 1 to 7, wherein when the cushioning body is in an undeformed state, each of the multiple voids has a uniform cross-sectional area in each plane parallel to each of the first main surface and the second main surface.

[0081] Embodiment 9: The insole according to any one of embodiments 1 to 8, wherein the volume of the void is about 25% to about 40% of the volume between the first main surface and the second main surface.

[0082] Embodiment 10: The insole according to any one of embodiments 1 to 9, wherein the distance between the first main surface and the second main surface is about 2 mm to about 3 mm.

[0083] Embodiment 11: An embodiment in which each void of the plurality of voids has a dimension of about 1.5 mm to about 2.5 mm in a plane parallel to at least one of the first major surface and the second major surface. The insole according to any one of aspects 1 to 10.

[0084] Embodiment 12: An insole according to any one of embodiments 1 to 11, wherein the minimum distance between adjacent voids among the plurality of voids is about 0.8 mm to about 1.5 mm.

[0085] Embodiment 13: An insole described in any one of embodiments 1 to 12, wherein the elastomeric material comprises an ABA triblock copolymer.

[0086] Embodiment 14: An insole according to embodiment 13, wherein the elastomeric material further comprises a plasticizer.

[0087] Embodiment 15: The insole of embodiment 14, wherein the ratio of the weight of the plasticizer to the weight of the triblock copolymer is from about 0.1 to about 50.

[0088] Embodiment 16: A shoe comprising the insole according to any one of embodiments 1 to 15.

[0089] Embodiment 17: The shoe described in embodiment 16, wherein the elastomeric material is disposed within a pocket within the insole body.

[0090] Embodiment 18: A shoe according to embodiment 16 or embodiment 17, wherein the insole body further comprises a non-gel component adjacent to the elastomeric material.

[0091] Embodiment 19: A shoe described in any one of embodiments 16 to 18, wherein the non-gel component comprises polyethylene-vinyl acetate.

[0092] Embodiment 20: A shoe according to any one of embodiments 16 to 19, wherein the non-gel component comprises a foam.

[0093] Embodiment 21: A shoe according to any one of embodiments 16 to 20, further comprising a fabric over the non-gel component and the elastomeric material.

[0094] Embodiment 22: A shoe described in any one of embodiments 16 to 21, further comprising a scrim layer beneath the non-gel component and the elastomeric material.

[0095] Embodiment 23: A method of forming a shoe insole, comprising providing an elastomeric material into a mold to form an insole body comprising the elastomeric material having a first major surface and a second major surface opposite the first major surface. The distance between the first major surface and the second major surface is about 1 mm to about 10 mm. The mold portion occupies a plurality of voids that extend through the elastomeric material from the first major surface to the second major surface. Each void of the plurality of voids has a dimension, in a plane parallel to at least one of the first major surface and the second major surface, of about 1 mm to about 3 mm. The minimum distance between adjacent voids of the plurality of voids is about 0.5 mm to about 3 mm.

[0096] Embodiment 24: The method of embodiment 23, wherein providing the elastomeric material in the mold comprises injection molding the elastomeric material in the mold.

[0097] Embodiment 25: The method of embodiment 23 or embodiment 24, further comprising at least partially impregnating the fabric with an elastomeric material.

[0098] Embodiment 26: The method of any one of embodiments 23-25, further comprising solidifying the elastomeric material in a mold.

[0099] Embodiment 27: The method of any one of embodiments 23-26, further comprising melting at least a portion of the solidified elastomeric material and recycling the molten elastomeric material.

[0100] Embodiment 28: A shoe including an insole body including a non-gel component and a gel component adjacent to the non-gel component. The gel component includes a body of elastomeric material having a first major surface and a second major surface opposite the first major surface. The distance between the first major surface and the second major surface is about 1 mm to about 10 mm. The gel component defines a plurality of voids extending through the gel component from the first major surface to the second major surface. Each void of the plurality of voids has a dimension of about 1 mm to about 3 mm in a plane parallel to at least one of the first major surface and the second major surface. The minimum distance between adjacent voids of the plurality of voids is about 0.5 mm to about 3 mm.

[0101] Embodiment 29: The shoe insole of embodiment 28, wherein the gel component is disposed within a pocket within the body containing the non-gel component.

[0102] Embodiment 30: A shoe insole according to embodiment 28 or embodiment 29, wherein the non-gel component comprises polyethylene-vinyl acetate.

[0103] Embodiment 31: A shoe insole according to any one of embodiments 28 to 30, wherein the non-gel component comprises a foam.

[0104] Embodiment 32: The shoe insole of any one of embodiments 28 to 31, further comprising a fabric over the non-gel component and the gel component.

[0105] Embodiment 33: The shoe insole of any one of embodiments 28-32, further comprising a scrim layer beneath the non-gel component and the gel component.

[0106] Embodiment 34: A cushioning element comprising a body of elastomeric material having a first major surface and a second major surface opposite the first major surface. The distance between the first major surface and the second major surface is about 1 mm to about 10 mm. The elastomeric material defines a plurality of voids extending therethrough from the first major surface to the second major surface. Each void of the plurality of voids has a dimension, in a plane parallel to at least one of the first major surface and the second major surface, of about 1 mm to about 3 mm. The minimum distance between adjacent voids of the plurality of voids is about 0.5 mm to about 3 mm.

[0107] Embodiment 35: A cushioning element including a body of elastomeric material having a first major surface and a second major surface opposite the first major surface. The elastomeric material defines a plurality of voids extending therethrough from the first major surface to the second major surface. When a force is applied to the cushioning element, the elastomeric material expands to at least partially fill some of the voids but does not buckle.

[0108] While the present invention has been described herein with reference to certain illustrated embodiments, those skilled in the art will recognize and understand that it is not so limited. Rather, numerous additions, deletions, and modifications to the illustrated embodiments may be made without departing from the scope of the invention as claimed below, including its legal equivalents. In addition, features of one embodiment may be combined with features of another embodiment and still fall within the scope of the invention as contemplated by the inventors. Furthermore, embodiments of the present disclosure have utility with a variety of different cushion types and configurations.

Claims

1. A shoe insole, a substantially non-gel component; 1. A gel component having a first major surface and a second major surface opposite the first major surface, the gel component comprising a single layer of elastomeric material including a plasticizer, the elastomeric material defines a plurality of voids extending through the single layer from the first major surface to the second major surface; when the gel component is in an undeformed state, each void of the plurality of voids has a uniform cross-sectional area in each plane parallel to each of the first major surface and the second major surface; the elastomeric material of the single layer is designed to swell into voids of the single layer in the vicinity of a load applied to the gel component in a direction perpendicular to the first major surface; The swelling is a distance across each gap of the plurality of gaps measured in a plane parallel to at least one of the first major surface and the second major surface; a distance between adjacent voids of the plurality of voids; a thickness of the elastomeric material that allows the elastomeric material to expand into adjacent voids; and the force of the load on the gel component; and a gel component resulting from the gel component is disposed within a pocket within the substantially non-gel component; At least a portion of the pocket is made of the same elastomeric material as the gel component and is in at least partial contact with the gel component disposed within the pocket. Insole.

2. The elastomeric material is attached to another component having a material composition different from that of the elastomeric material. The insole according to claim 1.

3. a collective volume of the plurality of voids is about 25% to about 40% of a total volume between the first major surface and the second major surface; The insole of claim 1.

4. the distance between the first major surface and the second major surface is about 2 mm to about 3 mm; The insole according to claim 1.

5. the distance across each gap of the plurality of gaps is about 1.5 mm to about 2.5 mm, measured in a plane parallel to at least one of the first major surface and the second major surface; The insole according to claim 1.

6. the distance between adjacent voids of the plurality of voids is between about 0.8 mm and about 1.5 mm; The insole of claim 1.

7. the elastomeric material comprises an A-B-A triblock copolymer, and the ratio of the weight of the plasticizer to the weight of the triblock copolymer is from about 0.1 to about 50; The insole of claim 1.

8. A substantially non-gel component; a gel component adjacent to the non-gel component, the gel component includes a single layer of elastomeric material having a first major surface and a second major surface opposite the first major surface and including a plasticizer; the gel component defines a plurality of voids extending through the single layer of elastomeric material from the first major surface to the second major surface; when the gel component is in an undeformed state, each void of the plurality of voids has a uniform cross-sectional area in each plane parallel to each of the first major surface and the second major surface; the elastomeric material of the single layer is designed to swell into voids of the single layer in the vicinity of a load applied to the gel component in a direction perpendicular to the first major surface; The swelling is a distance across each gap of the plurality of gaps measured in a plane parallel to at least one of the first major surface and the second major surface; a distance between adjacent voids of the plurality of voids; a thickness of the elastomeric material that allows the elastomeric material to expand into adjacent voids; and the force of the load on the gel component; a gel component resulting from Including, insole, the gel component is disposed within a pocket within the substantially non-gel component; At least a portion of the pocket is made of the same elastomeric material as the gel component and is in at least partial contact with the gel component disposed within the pocket. shoes.

9. the non-gel component is formed from polyethylene-vinyl acetate; The shoe according to claim 8.

10. The non-gel component comprises a foam The shoe according to claim 8.

11. further comprising a fabric over the non-gel component and the gel component. The shoe according to claim 8.

12. further comprising a scrim layer beneath the non-gel component and the gel component. The shoe according to claim 8.

13. A shoe insole, a substantially non-gel component; a gel component having a first major surface and a second major surface opposite the first major surface, the gel component including a single layer of an elastomeric material, the elastomeric material being an A-B-A triblock copolymer having a plasticizer extending therethrough; a plurality of voids extending through the single layer from the first major surface to the second major surface; Including, when the gel component is in an undeformed state, each void of the plurality of voids has a uniform cross-sectional area in each plane parallel to each of the first major surface and the second major surface; the elastomeric material of the single layer is designed to swell into voids of the single layer in the vicinity of a load applied to the gel component in a direction perpendicular to the first major surface; The swelling is a distance across each gap of the plurality of gaps measured in a plane parallel to at least one of the first major surface and the second major surface; a distance between adjacent voids of the plurality of voids; a thickness of the elastomeric material that allows the elastomeric material to expand into adjacent voids; and the force of the load on the gel component; arises from the gel component is disposed within a pocket within the substantially non-gel component; At least a portion of the pocket is made of the same elastomeric material as the gel component and is in at least partial contact with the gel component disposed within the pocket. Insole.

14. the elastomeric material is attached to another component having a material composition different from that of the elastomeric material; 14. The insole of claim 13.

15. a collective volume of the plurality of voids is about 25% to about 40% of a total volume between the first major surface and the second major surface; 14. The insole of claim 13.