Sheet manufacturing method and sheet manufacturing apparatus

Abstract

To provide a sheet manufacturing method and a sheet manufacturing device for manufacturing a sheet suitable for repeated recycling.SOLUTION: A sheet manufacturing method includes a web forming process for forming web by dryly accumulating fibers, a moisture giving process for giving moisture to the web W, and a heat compression process for simultaneously compressing and externally heating the web W imparted with the moisture. Moisture content of the web W imparted with the moisture in the moisture giving process is 12% by mass or higher. Compression degree of the web W before and after the heat compression process is 1 / 7 or less.SELECTED DRAWING: Figure 2

Description

[Technical Field]

[0001] The present invention relates to a sheet manufacturing method and a sheet manufacturing apparatus. [Background technology]

[0002] Conventionally, sheet manufacturing apparatuses have been known that manufacture new sheets using raw materials such as waste paper, etc. Patent Document 1 discloses that the sheet manufacturing apparatus adds moisture to the web so that the moisture content of the web is 8% of the web's mass, and that when the web is heated, it may be compressed so that the thickness becomes about 1 / 5 to 1 / 100 of the thickness of the web. [Prior art documents] [Patent documents]

[0003] [Patent Document 1] Japanese Patent Application Laid-Open No. 2015-203163 Summary of the Invention [Problem to be solved by the invention]

[0004] However, when a high-strength sheet is manufactured by the sheet manufacturing apparatus of Patent Document 1, the manufactured sheet is sometimes not suitable for repeated recycling. [Means for solving the problem]

[0005] The sheet manufacturing method includes a web forming step of dry-depositing fibers to form a web, a moisture imparting step of imparting moisture to the web, and a compression heating step of compressing and simultaneously heating the moisture-imparted web from the outside, wherein the moisture content of the moisture-imparted web in the moisture imparting step is 12% by mass or more, and the degree of compression of the web before and after the compression heating step is 1 / 7 or less.

[0006] The sheet manufacturing apparatus includes a web forming section that dry-deposits fibers to form a web, a moisture imparting section that imparts moisture to the web, and a compression heating section that compresses the moisture-imparted web while simultaneously heating it from the outside, wherein the moisture content of the moisture-imparted web in the moisture imparting section is 12% by mass or more, and the degree of compression of the web before and after the compression heating section is 1 / 7 or less. [Brief explanation of the drawings]

[0007] [Figure 1] FIG. 1 is a diagram schematically illustrating a sheet manufacturing apparatus according to a first embodiment. [Figure 2] 1 is a flowchart illustrating a sheet manufacturing method. [Figure 3] FIG. 10 is a diagram showing the sheet creation conditions and evaluation results. [Figure 4] FIG. 10 is a diagram schematically illustrating a sheet manufacturing apparatus according to a second embodiment. DETAILED DESCRIPTION OF THE INVENTION

[0008] 1. First embodiment Hereinafter, embodiments of the present invention will be described. The embodiments described below are examples of the present invention. The present invention is not limited to the following embodiments, and includes various modified forms that are implemented within the scope of the present invention. Note that not all of the configurations described below are necessarily essential configurations of the present invention.

[0009] The sheet manufacturing method according to the present embodiment includes a web forming step of dry-depositing fibers to form a web, a moisture imparting step of imparting moisture to the web, and a compression and heating step of compressing and simultaneously externally heating the moisture-imparted web. Hereinafter, an example of a sheet manufacturing apparatus capable of implementing the sheet manufacturing method according to the present embodiment will first be described, and then the sheet manufacturing method will be described.

[0010] 1-1. Sheet manufacturing equipment FIG. 1 is a diagram schematically illustrating a sheet manufacturing apparatus 100 according to the present embodiment. A sheet manufacturing apparatus 100, which is an example of a sheet manufacturing apparatus capable of carrying out the sheet manufacturing method of the present embodiment, will be described with reference to FIG.

[0011] As shown in FIG. 1, the sheet manufacturing apparatus 100 includes, for example, a supply section 10, a crushing section 12, a defibrating section 20, a sorting section 40, a first web forming section 45, a rotating body 49, a mixing section 50, a deposition section 60, a second web forming section 70, a sheet forming section 80, and a cutting section 90.

[0012] The supply unit 10 supplies raw material to the crushing unit 12. The supply unit 10 is, for example, an automatic feeding unit for continuously feeding raw material into the crushing unit 12. The raw material supplied by the supply unit 10 is, for example, a fiber-containing material such as waste paper or a pulp sheet.

[0013] The crushing unit 12 shreds the raw material supplied by the supply unit 10 into small pieces in air, such as the atmosphere. The small pieces have a shape and size of, for example, several centimeters square. In this embodiment, the crushing unit 12 has crushing blades 14, which can shred the input raw material. A shredder, for example, is used as the crushing unit 12. The raw material shredded by the crushing unit 12 is received in a hopper 1 and then transferred to the defibrating unit 20 via a pipe 2.

[0014] The defibrating unit 20 defibrates the raw material cut by the crushing unit 12. Here, "defibrating" refers to unraveling raw material made up of multiple fibers bonded together into individual fibers. The defibrating unit 20 also has the function of separating substances such as resin particles, ink, toner, and anti-bleed agents adhering to the raw material from the fibers.

[0015] The material that has passed through the defibrating unit 20 is called the "defibrated material." In addition to the defibrated material fibers, the "defibrated material" may also contain additives such as resin particles that have separated from the fibers when the fibers are defibrated, colorants such as ink and toner, and anti-bleeding agents and paper strength agents. The shape of the defibrated material is string-like. The defibrated material may exist in a state where it is not entangled with other defibrated fibers, i.e., in an independent state, or it may exist in a state where it is entangled with other defibrated material and forms clumps, i.e., in a clump-like state.

[0016] The defibrator unit 20 performs defibration in a dry manner. Here, the term "dry" refers to performing processes such as defibration in air, such as in the atmosphere, rather than in a liquid. An impeller mill, for example, is used as the defibrator unit 20. The defibrator unit 20 has the function of generating an airflow that sucks in the raw material and discharges the defibrated material. This allows the defibrator unit 20 to suck in the raw material together with the airflow from the inlet 22 using the airflow it generates, defibrate the material, and transport the defibrated material to the outlet 24. The defibrated material that has passed through the defibrator unit 20 is transferred to the sorting unit 40 via pipe 3. The airflow for transporting the defibrated material from the defibrator unit 20 to the sorting unit 40 may be the airflow generated by the defibrator unit 20, or it may be possible to provide an airflow generating device such as a blower and use that airflow.

[0017] The sorting unit 40 introduces the defibrated material defibrated by the defibrator unit 20 from an inlet 42 and sorts it by fiber length. The sorting unit 40 has, for example, a drum unit 41 and a housing unit 43 that houses the drum unit 41. The drum unit 41 is, for example, a sieve. The drum unit 41 has a mesh and can separate fibers or particles smaller than the mesh opening size, i.e., a first sorted material that passes through the mesh, from fibers, undefibrated pieces, and lumps larger than the mesh opening size, i.e., a second sorted material that does not pass through the mesh. For example, the first sorted material is transferred to the deposition unit 60 via pipe 7. The second sorted material is returned to the defibrator unit 20 from a discharge outlet 44 via pipe 8. Specifically, the drum unit 41 is a cylindrical sieve that is rotated by a motor. The mesh of the drum portion 41 may be, for example, a wire mesh, an expanded metal made by stretching a metal plate with slits, or a punched metal made by forming holes in a metal plate with a press or the like.

[0018] The first web forming unit 45 conveys the first sorted material that has passed through the sorting unit 40 to the pipe 7. The first web forming unit 45 has, for example, a mesh belt 46, a tension roller 47, and a suction mechanism 48.

[0019] The suction mechanism 48 can suck the first sorted material that has passed through the openings of the sorting unit 40 and been dispersed into the air onto the mesh belt 46. The first sorted material is deposited on the moving mesh belt 46 to form a web V. The basic configurations of the mesh belt 46, tension roller 47, and suction mechanism 48 are similar to those of the mesh belt 72, tension roller 74, and suction mechanism 76 of the second web forming unit 70, which will be described later.

[0020] The web V is formed into a soft, puffy state containing a lot of air by passing through the sorting unit 40 and the first web forming unit 45. The web V deposited on the mesh belt 46 is fed into the pipe 7 and transported to the deposition unit 60.

[0021] The rotating body 49 can cut the web V. In this embodiment, the rotating body 49 has a base 49a and protrusions 49b protruding from the base 49a. The protrusions 49b have, for example, a plate-like shape. In this embodiment, four protrusions 49b are provided, and the four protrusions 49b are provided at equal intervals. By rotating the base 49a in the direction R, the protrusions 49b can rotate around the base 49a as an axis. By cutting the web V with the rotating body 49, it is possible to reduce, for example, fluctuations in the amount of defibrated material supplied to the accumulation section 60 per unit time.

[0022] The rotating body 49 is provided near the first web forming unit 45. In this embodiment, the rotating body 49 is provided near the tension roller 47a located downstream in the path of the web V. The rotating body 49 is provided at a position where the protrusions 49b can come into contact with the web V but do not come into contact with the mesh belt 46 on which the web V is deposited. This makes it possible to prevent the mesh belt 46 from being worn by the protrusions 49b. The shortest distance between the protrusions 49b and the mesh belt 46 is, for example, 0.05 mm or more and 0.5 mm or less. This is the distance at which the web V can be cut without damaging the mesh belt 46.

[0023] The mixing section 50 mixes, for example, the first sorted material that has passed through the sorting section 40 with an additive. The mixing section 50 has, for example, an additive supply section 52 that supplies the additive, a pipe 54 that transports the first sorted material and the additive, and a blower 56. In this embodiment, the additive is supplied from the additive supply section 52 to the pipe 54 via a hopper 9. The pipe 54 is in communication with the pipe 7.

[0024] In the mixing section 50, an air current is generated by a blower 56, and the first sorted material and the additives can be transported while being mixed in the pipe 54. The mechanism for mixing the first sorted material and the additives is not particularly limited, and may be one that uses a blade that rotates at high speed to mix the materials, or one that uses the rotation of a container, such as a V-type mixer.

[0025] The additive supply unit 52 may be a screw feeder as shown in FIG. 1 or a disk feeder (not shown).

[0026] The additive supplied from the additive supply unit 52 is not particularly limited, but may include, for example, a material for binding multiple fibers. When the sheet manufacturing method of the present embodiment is applied, the additive includes starch or dextrin. Starch and dextrin will be described later.

[0027] The additives supplied from the additive supply unit 52 may contain, depending on the type of sheet to be produced, a colorant for coloring the fibers, an agglomeration inhibitor for inhibiting agglomeration of the fibers and additives, and a flame retardant for making the fibers less flammable. Furthermore, when producing a sheet without using additives, the mixing unit 50 need not be provided. The mixture that has passed through the mixing unit 50 is transferred to the deposition unit 60 via a pipe 54.

[0028] The depositing unit 60 introduces the mixture that has passed through the mixing unit 50 from an inlet 62, loosens the tangled defibrated material, and drops it down while dispersing it in the air. This allows the depositing unit 60 to deposit the mixture uniformly in the second web forming unit 70.

[0029] The deposition unit 60 has, for example, a drum unit 61 and a housing unit 63 that houses the drum unit 61. A rotating cylindrical sieve is used as the drum unit 61. The drum unit 61 has a mesh and causes fibers or particles that are smaller than the mesh size and are contained in the mixture that has passed through the mixing unit 50 to fall. The configuration of the drum unit 61 is the same as the configuration of the drum unit 41, for example.

[0030] The "sieve" of the drum unit 61 does not have to have the function of separating out a specific object. In other words, the "sieve" used as the drum unit 61 means one equipped with a mesh, and the drum unit 61 may allow all of the mixture introduced into the drum unit 61 to fall.

[0031] The second web forming unit 70 accumulates the material that has passed through the accumulation unit 60 to form a web W. The second web forming unit 70 has, for example, a mesh belt 72, a tension roller 74, and a suction mechanism 76.

[0032] Materials that have passed through the openings of the accumulation section 60 are deposited on the mesh belt 72. The mesh belt 72 is stretched by tension rollers 74 and is configured to prevent materials from passing through but allow air to pass through. The mesh belt 72 moves as the tension rollers 74 rotate. As the mesh belt 72 moves continuously, materials that have passed through the accumulation section 60 continuously fall and accumulate, forming a web W on the mesh belt 72.

[0033] The suction mechanism 76 is provided below the mesh belt 72. The suction mechanism 76 can generate a downward airflow. The suction mechanism 76 can suck the mixture dispersed in the air by the deposition unit 60 onto the mesh belt 72. This can increase the discharge speed from the deposition unit 60. Furthermore, the suction mechanism 76 can form a downflow in the falling path of the mixture, preventing the defibrated material and additives from becoming entangled during the fall.

[0034] As described above, by passing through the deposition section 60 and the second web forming section 70, the web W is formed in a soft, puffy state containing a lot of air.

[0035] The deposited web W is moistened while being transported to the sheet forming unit 80. The moisture is imparted by a moisture imparting unit 78. The moisture imparting unit 78 imparts moisture to the web W so that the web W has a predetermined moisture content. The moisture imparting unit 78 can be configured using, for example, steam, mist, a shower, an inkjet, or the like. Of these, it is more preferable for the moisture imparting unit 78 to impart moisture to the web W using steam or mist, as this allows moisture to be imparted to the web W with good uniformity.

[0036] In this embodiment, a suction mechanism 79 is provided at a position facing the moisture applicator 78 with the web W interposed therebetween. The suction mechanism 79 can generate a downward airflow. The suction mechanism 79 allows moisture generated from the moisture applicator 78 to pass through the web W and be sucked in. This allows moisture to be applied more uniformly in the thickness direction of the web W. In this embodiment, moisture is applied from the moisture applicator 78 to the web W on the mesh belt 72, but the moisture applicator 78 may be provided not on the mesh belt 72 but at a position before the web W is transported to the sheet forming unit 80. The web W to which moisture has been added by the moisture adding unit 78 is transported to the sheet forming unit 80.

[0037] The sheet forming unit 80 compresses and heats the web W accumulated on the mesh belt 72 to form a sheet S. In the sheet forming unit 80, heat and pressure are applied to the mixture of defibrated material and additives that has been mixed, accumulated, and moistened. In the sheet forming unit 80, the moisture evaporates after the temperature rises, and the thickness of the web W decreases, increasing the density.

[0038] The temperature of the water and starch or dextrin increases due to heat, and the density increases due to pressure, causing the starch or dextrin to gelatinize. Then, as the water evaporates, multiple fibers become entangled and bonded via the gelatinized starch or dextrin. This allows for the formation of a sheet S with good mechanical strength. Furthermore, the water evaporates due to heat, and the density increases due to pressure, causing hydrogen bonds to form between multiple fibers. This allows for the formation of a sheet S with even better mechanical strength.

[0039] The sheet forming unit 80 has a compression heating unit 84 that compresses and heats the web W. The compression heating unit 84 is configured using, for example, a compression heating roller. In this embodiment, the compression heating unit 84 is configured using a pair of compression heating rollers 86. The number of compression heating rollers 86 is not particularly limited. The compression heating unit 84 can compress and heat the web W simultaneously.

[0040] The cutting unit 90 cuts the sheet S formed by the sheet forming unit 80. In this embodiment, the cutting unit 90 has a first cutting unit 92 that cuts the sheet S in a direction intersecting the conveying direction of the sheet S, and a second cutting unit 94 that cuts the sheet S in a direction parallel to the conveying direction. The second cutting unit 94 cuts the sheet S that has passed through the first cutting unit 92, for example. In this way, a single sheet S of a predetermined size is formed. The cut single sheet S is discharged to a discharge receiving portion 96.

[0041] 1-2. Sheet manufacturing method FIG. 2 is a flowchart illustrating the sheet manufacturing method. The sheet manufacturing method according to this embodiment will be described with reference to FIG. The sheet manufacturing method of the present embodiment can be performed, for example, using the above-described sheet manufacturing apparatus 100. Hereinafter, a description will be given of the sheet manufacturing method performed using the above-described sheet manufacturing apparatus 100. The sheet S manufactured by the sheet manufacturing apparatus 100 is a sheet containing at least fibers, and in the present embodiment, starch or dextrin.

[0042] In the web forming step, the web W may not contain starch or dextrin. In this case, in the compression and heating step described below, the sheet S is formed by hydrogen bonding between the fibers.

[0043] As shown in Fig. 2, the sheet manufacturing method according to this embodiment includes a web forming step (step S11), a moisture imparting step (step S12), and a compression and heating step (step S13). In the web forming step (step S11), a mixture containing fibers and starch or dextrin is dry-deposited to form a web. In the moisture imparting step (step S12), moisture is imparted to the web W. In the compression and heating step (step S13), the moisture imparted web W is compressed and heated.

[0044] 1-2-1. Fiber The fibers are not particularly limited, and a wide variety of fiber materials can be used. Examples of fibers include natural fibers (animal fibers, plant fibers), chemical fibers (organic fibers, inorganic fibers, and organic-inorganic composite fibers), etc. More specifically, examples of fibers include fibers made from cellulose, silk, wool, cotton, hemp, kenaf, flax, ramie, jute, Manila hemp, sisal, coniferous trees, broad-leaved trees, etc. Furthermore, when using these fibers, they may be used alone or in appropriate mixtures, or may be used as regenerated fibers that have been purified, etc.

[0045] Examples of raw materials for the fibers include pulp, waste paper, and old cloth. The fibers may be subjected to various surface treatments. The fiber material may be a pure substance, or may be a material containing multiple components such as impurities and other components. Defibrated materials obtained by dry-defibrating waste paper, pulp sheets, and the like may also be used as the fibers.

[0046] The length of the fiber is not particularly limited, but the length of an independent fiber along the longitudinal direction of the fiber is preferably 1 μm or more and 5 mm or less, more preferably 2 μm or more and 3 mm or less, and even more preferably 3 μm or more and 2 mm or less.

[0047] The sheet manufacturing method of the present embodiment includes a moisture addition step (step S12), and therefore, using fibers capable of forming hydrogen bonds can increase the mechanical strength of the formed sheet S. An example of such fibers is cellulose.

[0048] The fiber content in the sheet S is preferably 50% by mass or more and 99.9% by mass or less, more preferably 60% by mass or more and 99% by mass or less, and even more preferably 70% by mass or more and 99% by mass or less. Such a content can be achieved by blending when forming the mixture.

[0049] 1-2-2. Starch, dextrin Starch and dextrin are water-soluble polysaccharides that dissolve in water, warm water, or hot water. Starch is a polymer formed by the polymerization of multiple α-glucose molecules through glycosidic bonds. Starch may be linear or branched. Starch derived from various plants can be used. Examples of starch sources include grains such as corn, wheat, and rice; beans such as broad beans, mung beans, and adzuki beans; tubers such as potatoes, sweet potatoes, and tapioca; wild plants such as dogtooth violets, bracken, and kudzu; and palm trees such as sago palm.

[0050] Furthermore, processed starch or modified starch may be used as the starch. Examples of processed starch include acetylated adipic acid cross-linked starch, acetylated starch, oxidized starch, sodium octenyl succinate starch, hydroxypropyl starch, hydroxypropylated phosphate cross-linked starch, phosphated starch, phosphate esterified phosphate cross-linked starch, urea phosphate esterified starch, sodium starch glycolate, and high-amylose corn starch. Examples of modified starch include pregelatinized starch, dextrin, lauryl polyglucose, cationized starch, thermoplastic starch, and carbamate starch. Dextrin obtained by processing or modifying starch can be suitably used.

[0051] In the sheet manufacturing method, starch or dextrin is used, and after adding moisture, it is compressed and heated, which causes at least one of gelatinization of the starch or dextrin and hydrogen bonding between the fibers, thereby giving the sheet S sufficient strength.

[0052] The starch or dextrin content in the sheet S is preferably 0.1% by mass or more and 50% by mass or less, more preferably 1% by mass or more and 40% by mass or less, and even more preferably 1% by mass or more and 30% by mass or less. Such a content can be achieved by blending when forming the mixture.

[0053] 1-2-3. Web forming process In the web formation process (step S11), a mixture containing fibers and, in this embodiment, starch or dextrin is dry-deposited to form a web. The fibers are defibrated material defibrated by the defibrator unit 20, the starch or dextrin is supplied from the additive supply unit 52, and the mixture is formed by the mixer unit 50. Then, the mixture is dry-deposited by the depositing unit 60 and the second web forming unit 70 to form the web W.

[0054] 1-2-4. Moisture addition process In the moisture imparting step (step S12), moisture is imparted to the web W formed in the web forming step. In this embodiment, moisture can be imparted to the web W by the moisture imparting unit 78.

[0055] The amount of moisture added in the moisture-adding step can be controlled by the moisture content of the web W. The moisture content of the web W to which moisture has been added in the moisture-adding step is preferably 12% by mass or more and 50% by mass or less, more preferably 13% by mass or more and 40% by mass or less, and even more preferably 14% by mass or more and 25% by mass or less. When the amount of moisture added is within this range, a sheet S with excellent strength can be produced while suppressing the amount of energy, such as electricity, required to heat and dry the web W.

[0056] Furthermore, in the moisture imparting step, it is preferable to impart water vapor or mist to the web W. In this way, moisture can be imparted more uniformly to the web W, and the sheet S can be produced with a simpler device configuration.

[0057] 1-2-5. Compression and heating process In the compression and heating step (step S13), the web W to which moisture has been added in the moisture adding step is compressed and simultaneously heated from the outside (surface) of the web W. In the compression and heating step, compression and heating are performed simultaneously. In this embodiment, this compression and heating step is performed by the sheet forming unit 80.

[0058] As described above, the sheet forming unit 80 includes a pair of compressing and heating rollers 86 as the compressing and heating unit 84. The sheet forming unit 80 (compressing and heating unit 84) compresses and heats the web W by sandwiching the web W, which has been accumulated on the mesh belt 72 and to which moisture has been added in the moisture adding unit 78 so that the web W has a predetermined moisture content, between the pair of compressing and heating rollers 86 while rotating, to form a sheet S.

[0059] In the compression and heating process, the web W is compressed to a predetermined degree, thereby reducing the thickness of the web W after the compression and heating process compared to before the compression and heating process, and increasing the density of the web W.

[0060] The compression degree refers to the ratio of compression before and after the compression heating step. The compression degree is expressed by the following formula (1): In this embodiment, however, the compression degree is expressed as a fraction. Compression degree = Web thickness after compression and heating process / Web thickness before compression and heating process (1)

[0061] Here, the "thickness of the web before the compression and heating process" corresponds to the "before" in "before and after the compression and heating process" and refers to the thickness of the web W immediately after moisture is added in the moisture adding section 78 of the sheet manufacturing apparatus 100. Furthermore, the "thickness of the web W after the compression and heating process" corresponds to the "after" in "before and after the compression and heating process" and refers to the thickness of the web W immediately after compression and heating in the compression and heating section 84 of the sheet manufacturing apparatus 100.

[0062] In this embodiment, the degree of compression is preferably 1 / 18 to 1 / 7, more preferably 1 / 18 to 1 / 10, and even more preferably 1 / 16 to 1 / 12. Note that "more than" and "less than" refer to the magnitude of a fraction. In this specification, the degree of compression may be expressed as "high" or "low," but it should be noted that the higher the degree of compression, the smaller the fraction, and the lower the degree of compression, the larger the fraction. The degree of compression can be adjusted by adjusting the nip pressure of the compression heating roller 86.

[0063] By compressing the web W to a degree of compression within this range, a sheet S with good strength can be produced and fiber deterioration can be suppressed, so that the produced sheet S can be used again as raw material to produce a sheet S with good strength again.

[0064] In the compression and heating step, the web W is heated to a predetermined temperature, thereby forming hydrogen bonds between the fibers and providing the sheet S with sufficient strength.

[0065] The pair of compression heating rollers 86 are provided with a heating element (not shown) such as a halogen heater at the center, and are capable of maintaining the surface temperature of the compression heating rollers 86 at a predetermined temperature. Therefore, in this embodiment, the compression heating rollers 86 heat the web W from the outside (surface) of the web W, thereby evaporating the moisture contained in the web W.

[0066] In this embodiment, the heating temperature of the web W in the compression and heating step is 100° C. or less. In the compression and heating step, the web W is heated to a temperature of preferably 60° C. or more and 100° C. or less, more preferably 65° C. or more and 98° C. or less, and even more preferably 70° C. or more and 96° C. or less. The heating temperature can be adjusted by adjusting the drive voltage of the heating member of the compression and heating roller 86.

[0067] By heating the web W at a heating temperature within this range, hydrogen bonds can be formed between the fibers more effectively. Furthermore, when the web W contains starch or dextrin, the starch or dextrin promotes gelatinization, and as moisture evaporates, multiple fibers can be bound together via the gelatinized starch or dextrin. This allows the sheet S to have sufficient strength.

[0068] The compression heating time is preferably 0.5 seconds or more, more preferably 0.6 seconds or more, and even more preferably 0.8 seconds or more as a lower limit, and is preferably 10 seconds or less, more preferably 8 seconds or less, and even more preferably 6 seconds or less as an upper limit.

[0069] The compression heating time refers to the time elapsed from the moment a given portion of the web W comes into contact with the compression heating roller 86 to the moment that portion of the web W leaves the contact. The compression heating time can be adjusted by adjusting the rotation speed of the compression heating roller 86. By compressing and heating the web W within this range of compression heating time, productivity can be improved. Furthermore, moisture can be sufficiently and uniformly permeated into the web, further improving the quality of the sheet S when it is repeatedly recycled.

[0070] In this embodiment, by configuring the compression heating unit 84 as a compression heating roller 86, it is possible to form the sheet S while continuously transporting the web W, compared to when the compression heating unit 84 is configured as a flat press device. Furthermore, when a flat press device is used, a buffer unit is required to temporarily slacken the transported web W while pressing. In other words, when the compression heating roller 86 is used, it is possible to improve manufacturing efficiency and reduce the size of the entire configuration of the sheet manufacturing apparatus 100, compared to when a flat press device is used.

[0071] 1-2-6. Other processes In addition to the above-mentioned steps, the sheet manufacturing method of the present embodiment may also include, for example, a defibrating step, a sorting step, a cutting step, etc. These steps can be easily performed by the above-mentioned sheet manufacturing apparatus 100 using the defibrating unit 20, sorting unit 40, first web forming unit 45, rotating body 49, cutting unit 90, etc.

[0072] 1-3.Effects The sheet manufacturing method of this embodiment includes a web forming step of dry-depositing fibers to form a web W, a moisture imparting step of imparting moisture to the web W, and a compression heating step of compressing and externally heating the moisture-imparted web W. The moisture-imparted web W has a moisture content of 12% by mass or more, and the degree of compression of the web W before and after the compression heating step is 1 / 7 or less. Therefore, in the sheet manufacturing method of the present embodiment, the web W to which moisture has been added is compressed, thereby increasing the density of the web W and allowing the added moisture to penetrate into the interior of the web W in the thickness direction. At this time, by keeping the compression degree to 1 / 7 or less, moisture can be sufficiently penetrated throughout the entire thickness direction of the web W. As a result, hydrogen bonds can be formed between the fibers throughout the entire thickness direction of the web W, resulting in a sheet S with excellent strength.

[0073] When compressing the web W to a compression degree of 1 / 7 or less, if the moisture content of the web W is 12% by mass or more, the fibers become flexible and the pressure required for compression can be reduced. As a result, not only is the manufacturing method simpler, but fiber degradation during compression can be suppressed. By suppressing fiber degradation, even when the manufactured sheet S is defibrated and the resulting fiber is used as raw material to manufacture a new sheet S, the sheet S will have excellent strength.

[0074] When a web W having a moisture content of 12% by mass or more is compressed so that the degree of compression is 1 / 7 or less, the web W can be heated at the same time to cause the moisture to penetrate into the interior of the web W in the thickness direction and to dry the web W, thereby promoting the formation of hydrogen bonds. Furthermore, a web W having a moisture content of 12% by mass or more is prone to breaking and sticking to members it comes into contact with, but by heating such a web W from the outside (surface) when compressing it, the moisture on the surface of the web W can be dried and the web W can be compressed while being prevented from sticking to the compression member (compression heating roller 86).

[0075] In the sheet manufacturing method of the present embodiment, if the degree of compression of the web W before and after the compression and heating step is 1 / 18 or more, deterioration of the fibers during compression can be further suppressed.

[0076] In the sheet manufacturing method of this embodiment, if the moisture content of the moistened web W is 40% by mass or less, when the web W is compressed to a compression degree of 1 / 7 or less, it is possible to prevent the moisture content of the web W from becoming uneven due to the moisture being squeezed out.

[0077] In the sheet manufacturing method of this embodiment, if the heating temperature of the web W in the compression heating process is 60°C or higher and 100°C or lower, hydrogen bonds can be formed between the fibers more effectively, and the sheet S can be given sufficient strength.

[0078] In the sheet manufacturing method of the present embodiment, if the compression and heating time in the compression and heating step is 0.5 seconds or more, moisture can be sufficiently penetrated into the web W. As a result, the quality during repeated recycling can be further improved, and the strength of the sheet S can be further improved.

[0079] In the sheet manufacturing method of the present embodiment, the web W contains starch or dextrin, which can further improve the strength of the sheet S.

[0080] The sheet manufacturing apparatus 100 of this embodiment includes a web forming unit (second web forming unit 70) that dry-deposits fibers to form the web W, a moisture imparting unit 78 that imparts moisture to the web W, and a compression heating unit 84 that compresses and externally heats the moisture-imparted web W. In the sheet manufacturing apparatus 100, the moisture imparted to the web W in the moisture imparting unit 78 has a moisture content of 12% by mass or more, and the degree of compression of the web W before and after the compression heating unit 84 is 1 / 7 or less. Therefore, the sheet manufacturing apparatus 100 of the present embodiment can suppress deterioration of the fibers during compression by the compression heating section 84. Therefore, it is possible to manufacture a sheet S that is excellent in strength and suitable for repeated recycling.

[0081] 1-4. Examples and Comparative Examples The present invention will be explained in more detail below with reference to examples, but the present invention is not limited to these examples.

[0082] 1-4-1. Creating a sheet FIG. 3 is a diagram showing the conditions for producing the sheet and the evaluation results. 3 shows the production conditions and evaluation results when sheets were produced under varying production conditions using an apparatus corresponding to the above-mentioned sheet manufacturing apparatus 100. The sheets were produced by dry piling up defibrated material to form a web, adding moisture to the web, and then compressing and heating the moistened web with a pair of compression and heating rollers to produce the sheets. The web was compressed and heated simultaneously.

[0083] As shown in Figure 3, the production conditions were varied, including the amount of water added (moisture content), the degree of web compression, and the compression time. Sample No. 10 also used starch as a binder. However, the other samples did not use binders such as resin, starch, or dextrin. The basis weight of all samples was approximately 85 g / m². 2 The sheet temperature was about 85° C. The moisture content (moisture content) was measured using an “MX-50” manufactured by A&D.

[0084] Furthermore, thickness A is the thickness of the web before the compression and heating process, and thickness B is the thickness of the web after the compression and heating process. Therefore, the compression degree was calculated using the above-mentioned formula (1).

[0085] 1-4-2.Evaluation conditions The sheets prepared as described above were evaluated for strength, density, water dripping during compression, and repetitive regeneration.

[0086] 1-4-2-1. Strength In the present example, strength refers to tensile strength index. Tensile strength index was calculated by cutting a 10 mm wide x 50 mm long sheet piece from the prepared sheet as a test piece and using the following formula (2). Tensile strength index was evaluated by a tensile test. The test equipment used was an "AGS-X500N" manufactured by Shimadzu Corporation. The tensile speed was 1 mm / s. Specific tensile strength (N m / g) = Maximum tensile load (N) / Specimen width (mm) / Specimen basis weight (g / cm 2 )……(2)

[0087] The evaluation criteria for tensile index (N·m / g) are as follows: A: 12 or more, B: 8 or more but less than 12, C: less than 8.

[0088] 1-4-2-2. Density In the present example, the density was calculated by cutting a test piece of 30 mm wide x 200 mm long from the prepared sheet, measuring the thickness and mass of the test piece, and then calculating the density using the following formula (3). The thickness was measured at five equally spaced locations along the longitudinal direction of the prepared test piece using a micrometer, and the average value was calculated. Density = mass / (thickness x 3 x 20)...(3)

[0089] Density (g / cm 3 The evaluation criteria for ) are as follows: A: 0.6 or more, B: 0.45 or more but less than 0.6, C: less than 0.45.

[0090] 1-4-2-3. Water dripping during compression In this example, dripping of water during compression was visually confirmed during compression.

[0091] The evaluation criteria for water dripping during compression are as follows: A: No dripping occurred, B: Dripping occurred.

[0092] 1-4-2-4. Repeat playback In this example, the repeated recycling involved papermaking using recycled paper as raw material, and the strength was measured after repeating this process twice. In other words, papermaking was performed three times in total. The method for measuring the strength of the repeatedly recycled sheets was as described above. The strength ratio between the once recycled RC1 and the three times recycled RC3 (strength of the three times recycled RC3 / strength of the once recycled RC1) was calculated. In the following explanation, the once recycled will be abbreviated as RC1 and the three times recycled as RC3.

[0093] The evaluation criteria for repeated playback are as follows: A: Ratio is 0.9 or more, B: Ratio is 0.8 or more but less than 0.9, C: Ratio is less than 0.8. However, even if the ratio is "A" or "B", if the strength of RC1 is "C", it will be judged as x (in the comparative example, it will be marked as "A'" or "B'" and the judgement will be x).

[0094] 1-4-3.Evaluation results 3 shows the evaluation results of the sheets of Sample Nos. 1 to 10. Sheets Nos. 1, 4, 5, 7, 8, 9, and 10 are sheets according to the examples, and sheets Nos. 2, 3, and 6 are sheets according to the comparative examples.

[0095] As shown in Figure 3, sheet No. 1 had the appropriate moisture content and degree of compression, and was good in strength and density, with a grade of "B." Because the degree of compression was lower than that of sheet No. 5, it received an "A" for water dripping during compression and an even better "A" for the strength ratio after repeated recycling.

[0096] The No. 2 sheet had a low compression rate of 1 / 5, which meant that moisture was not distributed evenly in the thickness direction, and its density was low at "C," resulting in a low strength of "C." Water dripping during compression was rated "A." The strength ratio after repeated recycling was good at "B'," but RC3 also had low strength like RC1 (the strength of RC1 was rated "C").

[0097] The thickness A of sheet No. 3 is 800 μm, while the thickness A of the other samples is 1800 μm. This is because the sheet was slightly compressed before adding moisture. The final density was good at "B", but the degree of compression before and after adding moisture was low at 1 / 5, so moisture did not spread evenly in the thickness direction. Because it was compressed twice, the density was good at "B", but the strength was low at "C" because moisture did not spread evenly. Water dripping during compression was "A". The strength ratio after repeated recycling was good at "B'", but RC3 had low strength like RC1 (the strength of RC1 was "C").

[0098] Sheet No. 4 was compressed a little higher at 1 / 16, and had higher density and strength than sample No. 1. All evaluation items were rated "A," which was very good, and the evaluation results were better than sheets Nos. 1, 5, 6, 8 to 10.

[0099] Sheet No. 5 had an appropriate moisture content and a slightly higher degree of compression, with the necessary moisture distributed throughout the thickness, making the fibers sufficiently flexible. Its strength, density, and water dripping during compression were all very good, rated "A," and its strength ratio after repeated recycling was also good, rated "B."

[0100] The same pressure as No. 1 was applied to sheet No. 6, but because the moisture content was insufficient at 10% by mass, moisture was not distributed throughout the thickness, resulting in a low strength rating of "C." The strength ratio after repeated recycling was good at "B'," but RC3 also had low strength, just like RC1 (the strength of RC1 was rated "C").

[0101] The same pressure was applied to sheet No. 7 as No. 1, but because it had a higher moisture content of 30% by mass, it was compressed to a higher degree than No. 1, resulting in even higher density and strength than No. 1. Specifically, it received an "A" rating in all evaluation items, a very favorable evaluation result.

[0102] Sheet No. 8 received a "B" for water dripping during compression, indicating a poor evaluation due to the occurrence of water dripping during compression. Other than that, it was in good condition. The same pressure as No. 1 was applied, but the moisture content was higher at 50% by mass, resulting in a higher degree of compression compared to No. 1. This resulted in an even higher density ("A") and strength ("A") than No. 1, which was a good result. Furthermore, the strength ratio after repeated recycling was also good, at "A."

[0103] The compression time of sheet No. 9 was shorter than the other samples at 0.3 seconds, which resulted in slightly poorer moisture uniformity in the thickness direction and a slightly inferior strength ratio when repeatedly recycled. Specifically, the strength, density, and strength ratio when repeatedly recycled were all good, rated "B," but the water dripping during compression was rated "A."

[0104] Compared to No. 1, sheet No. 10 uses starch as a binder, resulting in improved strength (rated "A"). Specifically, the density was "B," and both the water dripping during compression and the strength ratio after repeated regeneration were rated "A."

[0105] 2. Second embodiment The sheet manufacturing method according to this embodiment is basically the same as the sheet manufacturing method according to the first embodiment. In the sheet manufacturing method according to this embodiment, the configuration of the sheet forming unit 30 (see FIG. 4) in the sheet manufacturing apparatus 100A when performing the compression and heating process is different from the configuration of the sheet forming unit 80 in the first embodiment. Furthermore, by adopting this different sheet forming unit 30, the configurations on the upstream side and downstream side in the conveying direction are slightly different. Therefore, the following mainly describes the configuration of the sheet manufacturing apparatus 100A, which is an example for implementing the sheet manufacturing method according to this embodiment, that is different from the sheet manufacturing apparatus 100 in the first embodiment.

[0106] 2-1. Sheet manufacturing equipment FIG. 4 is a diagram schematically illustrating a sheet manufacturing apparatus 100A according to the present embodiment. 4 shows the configuration downstream of the depositing unit 60 in order to show the configuration parts that are different from the sheet manufacturing apparatus 100 of the first embodiment. A sheet manufacturing apparatus 100A of this embodiment will be described with reference to FIG.

[0107] As described above, the sheet manufacturing apparatus 100A of this embodiment differs from the sheet manufacturing apparatus 100 of the first embodiment in the configuration of the sheet forming unit 30 (compression heating unit 31). In the sheet manufacturing apparatus 100A of this embodiment, the sheet forming unit 30 is disposed downstream of the second web forming unit 70 and the moisture imparting unit 78. The sheet forming unit 30 produces the sheet S by sandwiching the web W, which has been formed in the second web forming unit 70 and has been imparted moisture in the moisture imparting unit 78, between flat press devices and compressing and heating the web W.

[0108] The sheet forming unit 30 has a compression heating unit 31 as a flat-plate press device that compresses and heats the web W. In this embodiment, the compression heating unit 31 has a lower mold portion 33 and an upper mold portion 34 arranged opposite each other. A flat plate 35 made of metal such as aluminum or copper is provided on each of the opposing surfaces of the lower mold portion 33 and the upper mold portion 34. The flat plate 35 is equipped with, for example, a car heater and is configured to be able to heat to a desired temperature. The lower mold portion 33 and the upper mold portion 34 are moved relative to each other using any press mechanism such as a hydraulic press, air press, or mechanical press, and the web W is sandwiched between the lower mold portion 33 and the upper mold portion 34 and compressed and heated.

[0109] 2-2. Sheet manufacturing method The sheet manufacturing method of this embodiment is the same as the sheet manufacturing method of the first embodiment, except for the specific method of the compression and heating step using the compression and heating unit 31 of this embodiment.

[0110] 2-2-1. Compression and heating process In the compression and heating step, the web W to which moisture has been added in the moisture adding step is compressed and heated from the outside (surface) at the same time, as in the first embodiment. In the compression and heating step, compression and heating are performed simultaneously by the sheet forming unit 30.

[0111] As described above, the sheet forming unit 30 includes the lower mold portion 33 and the upper mold portion 34 as the compression heating unit 31. In this embodiment, the compression heating unit 31 is configured such that the upper mold portion 34 moves up and down relative to the lower mold portion 33. The sheet forming unit 30 (compression heating unit 31) sandwiches the web W, which has been accumulated on the mesh belt 72 and has been moistened by the moisture imparting unit 78 to a predetermined moisture content, between the lower mold portion 33 and the upper mold portion 34, and compresses and heats the web W to a predetermined compression degree, at a predetermined heating temperature, and for a predetermined compression and heating time. Therefore, the compression heating unit 31 heats the web W from the outside (surface) of the web W.

[0112] As the heating means of the compression heating unit 31, any heating element such as an oil heater, a sheath heater, or the like can be used. If necessary, a Teflon (registered trademark) sheet may be wrapped around the surface of the flat plate 35. In this case, when the web W is compressed and heated, for example, it is possible to prevent the molten resin fibers from adhering to the flat plate 35, thereby preventing damage to the web W. In the compression heating step, the compression degree, heating temperature, compression heating time, etc. by the compression heating unit 31 are the same as those in the first embodiment.

[0113] As in the first embodiment, the degree of compression is expressed by formula (1). The "thickness of the web W before the compression and heating process" refers to the thickness of the web W immediately after moisture is added by the moisture adding section 78 of the sheet manufacturing apparatus 100A. The "thickness of the web W after the compression and heating process" refers to the thickness of the web W immediately after compression and heating by the compression and heating section 31 of the sheet manufacturing apparatus 100A.

[0114] In addition, the compression heating time in the compression heating section 31 refers to the elapsed time from the moment when the area of ​​the web W to be compressed and heated moves to a position between the lower mold section 33 and the upper mold section 34 and the web W is sandwiched (contacts) between the lower mold section 33 and the upper mold section 34 to the moment when the web W separates from the lower mold section 33 and the upper mold section 34.

[0115] 2-2-2.Other different configurations The sheet manufacturing apparatus 100A is provided with a first conveying section 150 that conveys the web W located in the sheet forming section 30. The first conveying section 150 of this embodiment is disposed downstream of the sheet forming section 30 in the conveying direction of the web W. The first conveying section 150 has a pair of rollers 151.

[0116] In this embodiment, a second conveying section 160 is disposed upstream of the sheet forming section 30 in the conveying direction of the web W. The second conveying section 160 is an auxiliary conveying section that assists the first conveying section 150, and conveys the web W together with the first conveying section 150. The second conveying section 160 has a pair of rollers 161.

[0117] A buffer section 200 is disposed upstream of the sheet forming section 30 in the conveying direction of the web W. In this embodiment, the buffer section 200 is disposed between the second web forming section 70 and the second conveying section 160. The buffer section 200 has a moving roller 210 that pushes the web W while moving along the moving direction of the sheet forming section 30 (the moving direction of the upper mold section 34).

[0118] The moving roller 210 is configured to move in the sheet forming unit 30 while sandwiching the web W. The moving roller 210 is configured to push the web W with a substantially constant weight. In this embodiment, the moving roller 210 is configured to push the web W by its own weight. This applies a force of a substantially constant magnitude to the web W in a substantially constant direction downward in the vertical direction. By continuously applying a substantially constant tension to the web W, the web W is prevented from stagnation in the transport path, and bending of the stagnant web W can be suppressed.

[0119] In the compression heating unit 31 of this embodiment, the flat plate 35 presses the web W while the transport of the web W is stopped, so the web W is not pulled in the transport direction during pressing, as compared to when a compression heating roller is used. Therefore, the directionality of the fibers constituting the web W does not emerge. Therefore, a sheet S having no anisotropy can be produced, and the properties of the sheet S, such as rigidity and bending strength, can be improved. According to the sheet manufacturing method and the sheet manufacturing apparatus 100A of the present embodiment, the same effects as those of the first embodiment can be achieved.

[0120] The present invention includes configurations that are substantially the same as the configurations described in the embodiments, for example, configurations with the same functions, methods, and results, or configurations with the same purpose and effects. The present invention also includes configurations that replace non-essential parts of the configurations described in the embodiments. The present invention also includes configurations that achieve the same effects or purposes as the configurations described in the embodiments. The present invention also includes configurations that add publicly known technology to the configurations described in the embodiments.

[0121] The following can be derived from the above-described embodiment.

[0122] The sheet manufacturing method of this embodiment includes a web forming step of dry-depositing fibers to form a web, a moisture imparting step of imparting moisture to the web, and a compression and heating step of compressing and externally heating the moisture imparted web. In the sheet manufacturing method, the moisture imparted web in the moisture imparting step has a moisture content of 12% by mass or more, and the degree of compression of the web before and after the compression and heating step is 1 / 7 or less. This sheet manufacturing method can suppress deterioration of fibers during compression in the compression and heating step, thereby producing a sheet that is excellent in strength and suitable for repeated recycling.

[0123] In the sheet manufacturing method of the present embodiment, the degree of compression of the web before and after the compression and heating step is 1 / 18 or more. According to this sheet manufacturing method, deterioration of the fibers during compression can be further suppressed.

[0124] In the sheet manufacturing method of the present embodiment, the moisture-imparted web has a moisture content of 40% by mass or less. According to this sheet manufacturing method, by setting the moisture content of the web to 40% by mass or less, when the web is compressed to a compression degree of 1 / 7 or less, it is possible to prevent the moisture content of the web from becoming uneven due to the moisture being squeezed out.

[0125] In the sheet manufacturing method of the present embodiment, the heating temperature of the web in the compression and heating step is 60°C or higher and 100°C or lower. According to this sheet manufacturing method, hydrogen bonds can be formed between the fibers more effectively, and the sheet can have sufficient strength.

[0126] In the sheet manufacturing method of the present embodiment, the compression and heating time in the compression and heating step is 0.5 seconds or more. According to this sheet manufacturing method, the compression and heating time is 0.5 seconds or more, which allows sufficient moisture to penetrate into the web, thereby further improving the quality during repeated recycling and further improving the strength of the sheet.

[0127] In the sheet manufacturing method of the present embodiment, the web contains starch or dextrin. According to this sheet manufacturing method, the strength of the sheet can be further improved.

[0128] The sheet manufacturing apparatus of this embodiment includes a web forming unit (second web forming unit) that dry-deposits fibers to form a web, a moisture imparting unit that imparts moisture to the web, and a compression heating unit that compresses and externally heats the moisture-imparted web. In the sheet manufacturing apparatus, the moisture-imparted web has a moisture content of 12% by mass or more, and the degree of compression of the web before and after the compression heating unit is 1 / 7 or less. This sheet manufacturing apparatus can suppress deterioration of fibers during compression in the compression heating section, thereby manufacturing a sheet that is excellent in strength and suitable for repeated recycling. [Explanation of symbols]

[0129] 1...hopper, 2,3,7,8...pipe, 9...hopper, 10...supply section, 12...crushing section, 14...crushing blade, 20...defibration section, 22...inlet, 24...discharge outlet, 40...sorting section, 41...drum section, 42...inlet, 43...housing section, 44...discharge outlet, 45...first web forming section, 46...mesh belt, 47, 47a...tension roller, 48...suction mechanism, 49...rotating body, 49a...base section, 49b...projection section, 50...mixing section, 52...additive supply section, 54...pipe, 56...blower, 60...accumulation section, 61... Drum section, 62...inlet, 63...housing section, 70...second web forming section, 72...mesh belt, 74...tension roller, 76...suction mechanism, 78...moisture application section, 79...suction mechanism, 80...sheet forming section, 84...compression heating section, 86...compression heating roller, 90...cutting section, 92...first cutting section, 94...second cutting section, 96...discharge receiving section, 100...sheet manufacturing apparatus, 30...sheet forming section, 31...compression heating section, 33...lower mold section, 34...upper mold section, 35...flat plate, 100A...sheet manufacturing apparatus.

Claims

1. A defibration process for dry defibrating waste paper or pulp sheets to obtain defibrated material; a web forming step of dry-stacking the defibrated material to form a web; a moisture imparting step of imparting moisture to the web; a compression and heating step of compressing and simultaneously heating the moisture-added web from the outside; and The moisture content of the web to which moisture has been added in the moisture adding step is 20% by mass or more. 、 The degree of compression of the web before and after the compression and heating step is 1 / 13 or less. A sheet manufacturing method.

2. The sheet manufacturing method according to claim 1, The moisture content of the web to which moisture has been added is 40% by mass or less. Manufacturing method.

3. The sheet manufacturing method according to claim 1 or 2, The heating temperature of the web in the compression and heating step is 60°C or higher and 100°C or lower. A sheet manufacturing method characterized by the above.

4. The sheet manufacturing method according to any one of claims 1 to 3, a compression heating time of 0.5 seconds or more in the compression heating step; Manufacturing method.

5. A defibrating unit that dry-defibrates waste paper or pulp sheets to obtain defibrated material; a web forming unit that dry-deposits the defibrated material to form a web; a moisture applying unit that applies moisture to the web; a compression and heating section that compresses and simultaneously heats the moisture-added web from the outside; , including the moisture content of the web to which moisture has been added in the moisture adding section is 20% by mass or more, The degree of compression of the web before and after the compression heating section is 1 / 13 or less. Sheet manufacturing equipment.

Images