Catalyst manufacturing method and propylene manufacturing method

Abstract

To provide a method for producing a catalyst for the production of propylene, making it possible to produce propylene from ethanol in high yield, while suppressing the formation of by-products, and a method for producing propylene.SOLUTION: A method for producing a catalyst includes: a supporting step for causing a compound of at least one metal M selected from the group consisting of metals of Group 1 and 2 elements and rare earth elements to be supported on zirconium oxide, to obtain a support mixture; and a firing step for firing the support mixture at 650°C or higher to obtain a catalyst.SELECTED DRAWING: None

Description

[Technical Field]

[0001] The present invention relates to a method for producing a catalyst and a method for producing propylene. [Background technology]

[0002] In recent years, concerns about climate change and the depletion and rising prices of fossil fuel resources have led to a demand for technologies to produce basic chemicals from sustainable raw materials. Propylene is one of the most representative basic chemicals, and is used in large quantities as a raw material for chemical products such as acrylic acid and acrolein, and for resins such as polypropylene. Ethanol can also be produced from biomass and is a sustainable raw material. Therefore, research is being conducted on methods to produce propylene from ethanol as one method of producing basic chemicals from sustainable raw materials.

[0003] For example, Patent Document 1 discloses a catalyst containing a zirconium oxide component and a metal element such as lithium as a catalyst for producing an olefin compound such as propylene from an alcohol compound with high efficiency. Non-Patent Document 1 discloses an yttrium-modified zirconia catalyst obtained by coprecipitation as a catalyst for obtaining propylene from ethanol with high selectivity. [Prior art documents] [Patent documents]

[0004] [Patent Document 1] Japanese Patent Application Laid-Open No. 2012-254447 [Non-patent literature]

[0005] [Non-Patent Document 1] W.Xia et al., “Highly selective catalytic conversion of ethanol to propylene over yttrium-modified zirconia catalyst”, Catalysis Communications, Vol.90, pp 10-13(2017) Summary of the Invention [Problem to be solved by the invention]

[0006] When producing propylene from ethanol as a raw material, the use of conventional porous oxide catalysts has the problem of easily producing large amounts of by-products such as olefins and alkanes with large carbon numbers. Furthermore, when a solid oxide catalyst such as zirconium oxide is used, the by-production of olefins and alkanes with a large carbon number is suppressed, but acetone and the like are produced as by-products, and the yield of propylene is insufficient. Therefore, there has been a demand for a catalyst and a production method that can suppress the production of the above-mentioned by-products and improve the propylene yield. Therefore, an object of the present disclosure is to provide a method for producing a catalyst for producing propylene, which can produce propylene from ethanol in a high yield while suppressing the production of by-products, and a technique related to a method for producing propylene. [Means for solving the problem]

[0007] As a result of intensive research into solving the above-mentioned problems, the present inventors discovered that the above-mentioned problems can be solved by supporting a specific metal on zirconium oxide, calcining the resulting catalyst under specific conditions, and using the catalyst in the production of propylene, thereby completing the invention.

[0008] That is, one aspect of the present disclosure can provide a technology related to a catalyst production method, which includes a supporting step of supporting a compound of at least one metal M selected from the group consisting of metals of Group 1 elements, metals of Group 2 elements, and metals of rare earth elements on zirconium oxide to obtain a supported mixture, and a calcining step of calcining the supported mixture at 650°C or higher to obtain a catalyst. [Effects of the Invention]

[0009] According to one aspect of the present disclosure, it is possible to provide a method for producing a catalyst for propylene production, which can produce propylene from ethanol in a high yield while suppressing the production of by-products, and a method for producing propylene. DETAILED DESCRIPTION OF THE INVENTION

[0010] The present disclosure relates to a technology for producing a catalyst, which includes a supporting step of supporting a compound of at least one metal M selected from the group consisting of metals of Group 1 elements, metals of Group 2 elements, and metals of rare earth elements on zirconium oxide to obtain a supported mixture, and a calcining step of calcining the supported mixture at 650°C or higher to obtain a catalyst. The present disclosure will be described in detail below.

[0011] [Catalyst manufacturing method] The method for producing a catalyst of the present disclosure includes a supporting step of supporting a compound of at least one metal M selected from the group consisting of metals of Group 1 elements, metals of Group 2 elements, and metals of rare earth elements on zirconium oxide to obtain a supported mixture, and a calcining step of calcining the supported mixture at 650°C or higher to obtain a catalyst.

[0012] <Supporting process> The supporting step in the catalyst production method of the present disclosure is a step of supporting a compound of at least one metal M selected from the group consisting of metals of Group 1 elements, metals of Group 2 elements, and metals of rare earth elements on zirconium oxide to obtain a supported mixture. By supporting the metal M on zirconium oxide, the vicinity of the surface of the zirconium oxide, which acts as a catalyst, can be efficiently modified to enhance activity.

[0013] (Compound of at least one metal M selected from the group consisting of metals of Group 1 elements, metals of Group 2 elements, and metals of rare earth elements) The metal M of the compound of metal M used in this step is at least one metal selected from the group consisting of metals of Group 1 elements, metals of Group 2 elements, and metals of rare earth elements. The metals of Group 1 elements are alkali metals, and specific examples include lithium, sodium, potassium, rubidium, cesium, and francium. The metals of Group 2 elements are alkaline earth metals, and specific examples include beryllium, magnesium, calcium, strontium, barium and radium, with calcium being preferred among these. Specific examples of rare earth metals include scandium, yttrium, and lanthanoids. Among these, at least one selected from the group consisting of yttrium and lanthanoids is preferred, with yttrium being more preferred. Here, lanthanoid is a general term for 15 metallic elements, specifically lanthanum, cerium, praseodymium, neodymium, promethium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, thulium, ytterbium, and lutetium. As described above, the metal M is preferably at least one selected from the group consisting of calcium, yttrium, and lanthanoids, more preferably at least one selected from the group consisting of calcium and yttrium, and even more preferably calcium.

[0014] The compound of metal M may be a salt of metal M, a hydroxide of metal M, an alkoxide of metal M, or an oxide of metal M, and is preferably at least one selected from the group consisting of a salt of metal M and an alkoxide of metal M. The salts include inorganic salts and organic salts, with inorganic salts being preferred. Examples of inorganic salts include nitrates, sulfates, phosphates, and hydrochlorides, with nitrates being preferred. Examples of organic salts include carboxylates, sulfonates, and organic phosphates, with carboxylates being preferred and acetates being more preferred. As described above, the compound of metal M is preferably at least one selected from the group consisting of nitrate of metal M, acetate of metal M, and alkoxide of metal M, and more preferably nitrate of metal M.

[0015] (zirconium oxide) The zirconium oxide used in this step has a particle shape, supports the metal M, and serves as a catalyst for producing propylene having the above-mentioned effects. A small amount of hafnium, a small amount of silica, etc. may be contained within a range that does not affect the effect of the catalyst production method of the present disclosure.

[0016] (Supporting method) The supporting method in this step is not particularly limited, but is preferably at least one selected from the group consisting of an impregnation method and an adsorption method, and more preferably an impregnation method.

[0017] The impregnation method is a method in which a compound of metal M is dissolved in a solvent to prepare a solution of the compound of metal M, the solution is mixed with zirconium oxide, and the solvent is removed to support the compound of metal M on zirconium oxide, thereby obtaining a supported mixture.

[0018] In addition to the compound of metal M, a compound of a metal other than metal M may be used within a range that does not impair the effects of the manufacturing method of the present disclosure. As the compound of a metal other than metal M, a zirconium compound is preferred. That is, the solution of the compound of metal M preferably contains a zirconium compound. That is, a preferred supporting method in this step is a method in which the compound of metal M and the zirconium compound are dissolved in a solvent to obtain a solution of the compound of metal M and the zirconium compound, the solution is mixed with zirconium oxide, and the solvent is removed to support the compound of metal M and the zirconium compound on the zirconium oxide, thereby obtaining a supported mixture.

[0019] The zirconium compound includes zirconyl nitrate, zirconium salts, zirconium hydroxides, zirconium alkoxides, zirconium oxides, etc., and is preferably at least one selected from the group consisting of zirconyl nitrate, zirconium salts, and zirconium alkoxides. The salts include inorganic salts and organic salts, with inorganic salts being preferred. Examples of inorganic salts include sulfates, phosphates, and hydrochlorides. Examples of organic salts include carboxylates, sulfonates, and organic phosphates, with carboxylates being preferred and acetates being more preferred. As described above, the zirconium compound is preferably at least one selected from the group consisting of zirconyl nitrate, zirconium acetate, and zirconium alkoxide, and more preferably zirconyl nitrate.

[0020] The molar ratio (M / Zr) of the compound of metal M to the compound of zirconium in the solution is preferably 100 / 1 to 2 / 1, more preferably 30 / 1 to 3 / 1, and even more preferably 20 / 1 to 5 / 1. The molar ratios are calculated in terms of metals, i.e., the molar ratios are the ratio of the number of moles of metal M (element) to the number of moles of zirconium (element) contained in each compound. By supporting zirconium compounds on zirconium oxide in addition to compounds of metal M, it is possible to further suppress the generation of by-products and improve the olefin yield. The reason for this is unclear, but it is thought to be because the crystal structure of zirconium oxide changes from monoclinic to tetragonal, increasing the number of surface oxygen vacancies, which are thought to be important active sites.

[0021] Furthermore, in addition to the compound of metal M and the compound of zirconium, compounds of other metals may be used to the extent that the effects of the production method of the present disclosure are not impaired. For example, the compound of other metal may be added to the solution of the compound of metal M or the solution containing the compound of metal M and the compound of zirconium, and then supported on zirconium oxide.

[0022] The solvent in the solution is preferably a hydrophilic solvent, more preferably water, in which the compound of metal M can be dissolved or dispersed well. In other words, the solution is preferably an aqueous solution. The concentration of the compound of metal M in the solution is not particularly limited as long as it is a concentration that allows uniform support on zirconium oxide, but is preferably 0.005 to 5 mol %, more preferably 0.01 to 1 mol %.

[0023] The amount of the solution relative to the zirconium oxide is not particularly limited as long as it is an amount that allows uniform support on the zirconium oxide, but is preferably 0.25 to 15 times by mass, more preferably 0.25 to 10 times by mass, and even more preferably 0.25 to 5 times by mass relative to the zirconium oxide. The molar ratio (M / Zr) of the compound of metal M to zirconium oxide is preferably 0.001 / 1 to 0.5 / 1, and more preferably 0.005 / 1 to 0.15 / 1. The molar ratio is calculated on a metal basis, i.e., the molar ratio is the ratio of the number of moles of metal M (element) contained in the compound of metal M to the number of moles of zirconium (element) contained in zirconium oxide.

[0024] The method for removing the solvent is not limited, and the solvent may be removed by heating, by reducing the pressure, or by a combination of these. When water is used as the solvent, the temperature for removing water is preferably 20 to 150°C, and under reduced pressure, it is preferably 20 to 100°C, more preferably 20 to 80°C. Under normal pressure (atmospheric pressure), it is preferably 105 to 150°C. A more preferred method is to remove the solvent under reduced pressure at 20 to 80°C until the amount of solvent is 10% by mass or less of the total supported mixture, and then remove the solvent under normal pressure (atmospheric pressure) at 105 to 150°C until the amount of solvent is 5% by mass or less of the total supported mixture.

[0025] <Firing process> The calcination step in the catalyst production method of the present disclosure is a step in which the supported mixture obtained in the previous step is calcined at 650° C. or higher to obtain a catalyst. In the catalyst production method of the present disclosure, by calcining the supported mixture at a high temperature of 650°C or higher, a catalyst for propylene production can be obtained that can produce propylene with a high yield and also suppress the production of by-products. Although it is unclear why the catalyst manufacturing method of the present disclosure can produce a catalyst with such effects, it is thought that this is because the metal M and zirconium form a solid solution on the catalyst surface, resulting in a significant increase in active sites and a change in charge density.

[0026] The calcination temperature in this step is 650°C or higher, preferably 700°C or higher. Also, it is preferably 1000°C or lower, more preferably 900°C or lower. In other words, this step is preferably a calcination step in which the supported mixture is calcined at 700°C or higher to obtain a catalyst, or preferably a calcination step in which the supported mixture is calcined at 1000°C or lower to obtain a catalyst, more preferably a calcination step in which the supported mixture is calcined at 900°C or lower to obtain a catalyst. By calcining at 650°C or higher, the catalytic activity is improved as described above, and by calcining at 1000°C or lower, the decrease in the specific surface area can be suppressed.

[0027] The calcination in this step is preferably carried out in the presence of oxygen, but the entire step may be carried out in the presence of oxygen, or the calcination may be carried out in the presence of oxygen in the early stage of the calcination to convert the metal M into an oxide, and then the temperature may be raised to 650°C or higher in an inert gas atmosphere. The calcination in this step may be carried out in a pure oxygen atmosphere or in a mixed gas atmosphere of oxygen and an inert gas. Of these, the calcination is preferably carried out in a pure oxygen atmosphere or an air atmosphere, and more preferably in an air atmosphere. By carrying out the calcination in an air atmosphere, the compound of metal M and the zirconium compound supported on the zirconium oxide can be efficiently and simply converted into oxides.

[0028] The calcination time in this step may be adjusted appropriately depending on the calcination temperature and the type of metal M, but is preferably 0.1 to 100 hours, more preferably 0.5 to 50 hours, and even more preferably 1 to 20 hours.

[0029] The catalyst obtained in the calcination step may be used as it is for the production of propylene, but it is preferable to prepare it into a shape suitable for the propylene production equipment by subjecting it to pulverization, granulation, molding, etc.

[0030] The molar ratio (M / Zr) of metal M to zirconium in the catalyst obtained by this production method is preferably 0.001 / 1 to 0.5 / 1, and more preferably 0.005 / 1 to 0.15 / 1. This molar ratio is calculated on a metal basis. In other words, the molar ratio is the ratio of the number of moles of metal M (element) contained in the catalyst to the number of moles of zirconium (element) contained in the catalyst. Furthermore, in the supporting step, the ratios of the metal M compound, the zirconium compound optionally contained in the solution, and zirconium oxide used can be adjusted to achieve the desired molar ratio. The molar ratio (M / Zr) of the metal M to zirconium in the catalyst can be determined by ICP emission spectrometry, specifically by the method described in the Examples.

[0031] The BET specific surface area of ​​the catalyst obtained by this production method is preferably 10 to 150 m 2 / g, more preferably 15 to 100m2 / g, more preferably 25 to 80m 2 / g. Furthermore, the catalyst obtained by the production method of the present disclosure is preferably a catalyst for producing propylene, which is used to produce propylene from ethanol.

[0032] <Catalyst> The catalyst obtained by this production method is preferably the catalyst shown below. The catalyst comprises zirconium oxide and an oxide of at least one metal M selected from the group consisting of metals of Group 1 elements, metals of Group 2 elements, and metals of rare earth elements. Specifically, the catalyst comprises zirconium oxide supported with an oxide of at least one metal M selected from the group consisting of metals of Group 1 elements, metals of Group 2 elements, and metals of rare earth elements. Preferably, the catalyst comprises zirconium oxide supported with an oxide of at least one metal M selected from the group consisting of metals of Group 1 elements, metals of Group 2 elements, and metals of rare earth elements.

[0033] The preferred range of the metal M is as described above. The molar ratio (M / Zr) of metal M to zirconium in the catalyst is preferably 0.001 / 1 to 0.5 / 1, and more preferably 0.005 / 1 to 0.15 / 1. This molar ratio is calculated on a metal basis. In other words, the molar ratio is the ratio of the number of moles of metal M (element) contained in the catalyst to the number of moles of zirconium (element) contained in the catalyst. In addition, in the supporting step of the production method, the ratios of the metal M compound, the zirconium compound optionally contained in the solution, and zirconium oxide used can be adjusted to achieve the desired molar ratio. The molar ratio (M / Zr) of the metal M to zirconium in the catalyst can be determined by ICP emission spectrometry, specifically by the method described in the Examples.

[0034] The BET specific surface area of ​​the catalyst is preferably 10 to 150 m 2 / g, more preferably 15 to 100m 2 / g, more preferably 25 to 80m2 / g. The catalyst is preferably a catalyst for producing propylene, which is used to produce propylene from ethanol.

[0035] [Propylene production method] The propylene production method of the present disclosure is a method of obtaining propylene by contacting the catalyst obtained by the production method with ethanol in a reactor. Specifically, the propylene production method of the present disclosure is a method of obtaining propylene by contacting the catalyst obtained by a production method including a supporting step of supporting a compound of at least one metal M selected from metals of Group 1 elements, metals of Group 2 elements, and rare earth metals on zirconium oxide to obtain a supported mixture, and a calcining step of calcining the supported mixture at 650°C or higher to obtain a catalyst.

[0036] The ethanol used in the propylene production method of the present disclosure is not particularly limited, but preferably, ethanol derived from biological resources (biomass) (bioethanol) is used. By contacting bioethanol with the catalyst of the present disclosure, propylene can be produced without increasing the carbon dioxide concentration in the environment, unlike ethanol obtained from fossil fuels. According to the propylene production method of the present disclosure, propylene can be obtained in high yield, and the product may contain ethylene or may be a mixture of propylene and ethylene. As described above, propylene is useful not only as a raw material for resins such as polypropylene, but also as a raw material for chemicals such as acrylic acid and acrolein.

[0037] In the propylene production method of the present disclosure, the method for contacting ethanol with the catalyst is not particularly limited, and may simply involve introducing ethanol into a reactor filled with the catalyst. Examples of the reactor include a fixed-bed reactor, a fluidized-bed reactor, a batch reactor, and a semi-batch reactor. From the viewpoint of propylene productivity, a fixed-bed reactor or a fluidized-bed reactor is preferred, and a fixed-bed reactor is more preferred.

[0038] The state of the raw material ethanol is not particularly limited, but from the viewpoints of increasing the efficiency of propylene production and facilitating the reaction, it is preferably in a gaseous state during the reaction. Furthermore, when gaseous ethanol is brought into contact with the catalyst in the reactor, the ethanol may be combined with other components and supplied to the reactor. Examples of other components include nitrogen, water vapor, hydrogen, carbon monoxide, carbon dioxide, all or part of the product recovered from the reactor outlet, and inert carrier gases such as nitrogen that are substantially unreactive with the raw material alcohol and the propylene produced.

[0039] The reaction temperature in the propylene production method of the present disclosure is not particularly limited, but is preferably 300 to 700° C., and more preferably 350 to 600° C. By carrying out the reaction within this temperature range, the propylene yield can be improved. [Example]

[0040] Next, the present disclosure will be described in more detail using examples, but the technology of the present disclosure is not limited to these examples in any way.

[0041] The catalysts obtained by the production of the catalysts shown in the Examples and Comparative Examples were analyzed and evaluated as follows. (1) Molar ratio of metal M to zirconium in the catalyst (M / Zr) The molar ratio (M / Zr) of metal M to zirconium in the catalysts of the examples and comparative examples was measured as follows. The catalysts obtained in the examples and comparative examples were dissolved by the alkali fusion method, and then the amounts of calcium and zirconium were quantified using an ICP optical emission spectrometer Agilent 5100 (Agilent Technologies) to calculate the molar ratios. The measurement wavelengths in the ICP optical emission spectroscopic analysis were 396.847 nm for Ca and 343.823 nm for Zr.

[0042] (2) BET specific surface area of ​​the catalyst The specific surface area of ​​the catalysts in the examples and comparative examples was measured by the BET single-point method using a catalyst analyzer, Belcat A (manufactured by Microtrac-Bell). As a pretreatment, 0.5 g of the catalyst crushed into powder was heat-treated at 400°C for 30 minutes while flowing He at a flow rate of 30 mL / min, and then the measurement was performed.

[0043] (3) Propylene yield and reaction conversion In the production of propylene shown in the Examples and Comparative Examples, the gas discharged from the outlet of the reaction tube was analyzed by gas chromatography, and the propylene yield and reaction conversion were calculated according to the following equations. (Propylene yield (mol%-C)) = (number of moles of carbon in the product) / (number of moles of carbon in the raw material compound used in the reaction) × 100 (Conversion rate (mol%-C)) = [1 - (number of moles of carbon in the raw material compound remaining after the reaction) / (number of moles of carbon in the raw material compound used in the reaction)] × 100

[0044] [Catalyst production] Examples 1 and 2 and Comparative Example 1 The catalyst was prepared by impregnation method. 8.6 g of calcium nitrate tetrahydrate was dissolved in 30 g of distilled water to obtain a solution (Solution A). Next, 45 g of cylindrical monoclinic zirconium oxide (RSC-HP manufactured by Daiichi Kigenso Kagaku Kogyo Co., Ltd.) and Solution A were placed in a glass recovery flask. The mixture was dried under reduced pressure at 60°C for 4 hours using a rotary evaporator, then continued to dry in the air at 110°C for 12 hours, and then calcined for 3 hours at the temperature shown in Table 1 (600-900°C) to obtain the catalyst CaO-ZrO2. The catalyst CaO-ZrO2 was crushed in an agate mortar and sized to 0.25-0.5 mm before being used in the production of propylene.

[0045] Example 3 14.7 g of calcium nitrate tetrahydrate and 2.2 g of zirconyl nitrate dihydrate were dissolved in 30 g of distilled water to obtain a solution (Solution B). Next, 45.5 g of cylindrical monoclinic zirconium oxide (RSC-HP manufactured by Daiichi Kigenso Kagaku Kogyo Co., Ltd.) and Solution B were placed in a glass recovery flask. The mixture was dried under reduced pressure at 60°C for 4 hours using a rotary evaporator, then continued to dry in the air at 110°C for 12 hours, and then calcined at 800°C for 3 hours to obtain the catalyst CaO-ZrO2. The catalyst CaO-ZrO2 was crushed in an agate mortar, sized to 0.25-0.5 mm, and used in the production of propylene.

[0046] [Production of propylene] Examples 4 to 6 and Comparative Example 2 A fixed-bed flow reactor was used. 1.0 g of the catalyst particles obtained in Examples 1 to 3 and Comparative Example 1 was packed into a glass-lined stainless steel reaction tube, and a 50 mol% aqueous ethanol solution was supplied to the reaction tube at a rate of 0.02 mL / min (liquid) while nitrogen was circulated at 0.5 MPaG at a flow rate of 12 mL / min, and the reaction was carried out at 450°C. The gas discharged from the outlet of the reaction tube was analyzed by gas chromatography to determine the yield and conversion rate.

[0047] [Table 1]

[0048] As shown in Table 1, by using the catalysts of the examples, propylene can be produced from ethanol in high yield and the production of by-products can be suppressed. It can also be seen that the conversion rate from the raw material ethanol is excellent. As such, it can be seen that the catalysts obtained by the production methods of the examples can produce propylene from ethanol in high yield and can also suppress the production of by-products.

Claims

1. A method for producing a catalyst for producing propylene, which is used to produce propylene from ethanol, comprising: A method for producing a catalyst for propylene production, comprising: a supporting step of supporting a compound of at least one metal M selected from the group consisting of calcium, yttrium, and lanthanoids on zirconium oxide to obtain a supported mixture; and a calcining step of calcining the supported mixture at a temperature of 700°C or higher and 1,000°C or lower to obtain the catalyst.

2. 2. The method for producing a catalyst for propylene production according to claim 1, wherein the catalyst has a BET specific surface area of ​​10 to 150 m 2 / g.

3. The method for producing a catalyst for producing propylene according to claim 1, wherein the molar ratio (M / Zr) of the metal M to zirconium in the catalyst is 0.001 / 1 to 0.5 / 1.

4. 4. The method for producing a catalyst for propylene production according to claim 1, wherein the compound of the metal M is at least one selected from the group consisting of a nitrate of the metal M, an acetate of the metal M, and an alkoxide of the metal M.

5. A method for producing propylene, comprising contacting the catalyst obtained by the method for producing propylene according to any one of claims 1 to 4 with ethanol in a reactor to obtain propylene.