Solid electrolytic capacitor and method for manufacturing the same

Abstract

The purpose of the present invention is to provide: a solid electrolytic capacitor including both a solid electrolyte and an electrolyte solution between electrode foils, wherein a rise in ESR can be sufficiently suppressed for a long time and for which a long life can be realized; and a method for manufacturing the same. To achieve the foregoing, this solid electrolytic capacitor (1) includes an amine represented by general formula (1) as the base component of an electrolyte solution 2g). In the formula, R1 represents hydrogen, an alkyl group, a hydroxyalkyl group, or an alkoxyalkyl group.　R2, R3, R4, and R5 each independently represent hydrogen, an alkyl group, a hydroxy group, a hydroxyalkyl group, an alkoxy group, or an alkoxyalkyl group.　The ends of R2 and R3 may join to form a ring.　The ends of R4 and R5 may join to form a ring.

Description

[Technical Field]

[0001] The present invention relates to a solid electrolytic capacitor and a method for manufacturing the same. [Background technology]

[0002] While an "electrolytic capacitor" has an electrolyte solution introduced between an anode foil, which has an oxide film or the like formed as a dielectric layer, and a cathode foil, a "solid electrolytic capacitor" is known in which a solid electrolyte containing a conductive polymer is introduced between the electrode foils (see Patent Document 1: Japanese Patent Application Publication No. 2008-109069).

[0003] Solid electrolytic capacitors generally have superior temperature stability and low equivalent series resistance (ESR) compared to electrolytic capacitors. Furthermore, as exemplified in Patent Document 1, there are also known types in which an electrolyte solution is introduced between the electrode foils in addition to the solid electrolyte to improve functionality. Hereinafter, the term "solid electrolytic capacitor" in this application refers to a solid electrolytic capacitor in which an electrolyte solution is introduced between the electrode foils along with the solid electrolyte. [Prior art documents] [Patent Documents]

[0004] [Patent Document 1] Japanese Patent Publication No. 2008-109069 [Patent Document 2] International Publication No. 2017 / 017947 [Overview of the project] [Problems that the invention aims to solve]

[0005] Conventionally, in an electrolytic capacitor, an amine such as triethylamine may be used as the base component of the solute of the electrolytic solution. On the other hand, in a solid electrolytic capacitor, when an amine having a relatively large acid dissociation constant (pKa) of the conjugate acid as used in an electrolytic capacitor is used as the base component of the solute of the electrolytic solution, dedoping of the dopant of the conductive polymer occurs and the solid electrolyte deteriorates. As a result, there arises a problem that the ESR increases. In contrast, Patent Document 2 describes a solid electrolytic capacitor in which the acid component of the solute of the electrolytic solution is contained in excess. According to this, dedoping of the dopant of the conductive polymer can be suppressed, and an increase in the ESR can be suppressed to a certain extent. However, when the acid component in the electrolytic solution is excessive, the conductivity decreases, and when the pH is too low, there is a risk of adversely affecting the films of the respective electrode foils.

Means for Solving the Problems

[0006] The present invention has been made in view of the above circumstances, and an object thereof is to provide a solid electrolytic capacitor and a method for manufacturing the same, which can sufficiently suppress an increase in ESR over a long period of time and can achieve a long life in a solid electrolytic capacitor including a solid electrolyte and an electrolytic solution between electrode foils.

[0007] The present invention solves the above problems by the solution means described below as one embodiment.

[0008] The solid electrolytic capacitor according to the present invention includes an anode foil on which a dielectric layer is formed and a cathode foil, and is a solid electrolytic capacitor including a solid electrolyte and an electrolytic solution in a gap between the anode foil and the cathode foil. The electrolytic solution includes a solvent and a solute, and the solute includes an acid component and a base component. The solvent comprises a polyol compound, and the number of hydroxyl groups X in the polyol compound satisfies the requirement X ≥ (Y / 200) (where Y represents the molecular weight of the polyol compound). The base component includes an amine represented by the general formula (1). In the above general formula (1), the R , Each of these independently represents hydrogen, an alkyl group, an alkoxy group, or an alkoxyalkyl group. , , the R , 4 , R represents hydrogen, alkyl group, or alkoxyalkyl group, and R , 2 , , ,

[0007] , , , and R , 5 , , the R , 3 , In the above general formula (1), the R , 1 , The solvent comprises a polyol compound, and the number of hydroxyl groups X in the polyol compound satisfies the requirement X ≥ (Y / 200) (where Y represents the molecular weight of the polyol compound). ,

[0008] , R represents hydrogen, alkyl group, or alkoxyalkyl group, and R 2 , the R 3 , the R 4 and R 5 Each of these independently represents hydrogen, an alkyl group, an alkoxy group, or an alkoxyalkyl group. It is characterized by this.

[0009]

Chemical formula

[0010] Thus, the present invention is characterized in that the base component of the solute of the electrolyte contains a cyclic oxygen-containing amine. According to this, by containing hydrophilic oxygen atoms, it is possible to make it difficult for the amine to approach the hydrophobic conductive polymer exemplified by PEDOT-PSS or the like. Therefore, it is possible to suppress the dedoping of the dopant by the amine. In addition, due to the cyclic molecular structure, the conductivity in the electrolyte can be made higher than that of the chain-type amine. As a result, the increase in ESR can be suppressed sufficiently over a long period of time, and the long life of the capacitor can be realized.

[0011] Further, it is preferable that the solvent contains a polyol compound. Since the polyol compound has low volatility, it has high electrolyte retention performance, can maintain its function over a long period of time, and can suppress the deterioration of the conductive polymer. In addition, it has a strong solvation effect, solvates with the cations of the base, makes it difficult to approach the conductive polymer, and can suppress the dedoping of the dopant. Since the solvation effect is stronger for a solvent having more hydroxy groups with respect to its molecular weight, a polyol compound satisfying the requirement of X≧(Y / 200) (where Y represents the molecular weight of the polyol compound) can be more preferably applied.

[0012] Furthermore, it is preferable that the acid dissociation constant (pKa) of the conjugate acid of the amine is 12.0 or less. A low acid dissociation constant (pKa) of the conjugate acid of the amine indicates low nucleophilicity, which suppresses excessive dissociation of the basic component and makes it difficult for it to approach the conductive polymer. Therefore, dopant dedoping can be suppressed.

[0013] In the above general formula (1), the R 1 R represents hydrogen, alkyl group, or alkoxyalkyl group, and R 2 , the R 3 , the R 4 and R 5 Preferably, each of these independently represents hydrogen, an alkyl group, an alkoxy group, or an alkoxyalkyl group. This prevents esterification with acidic components in the electrolyte, such as carboxylic acids, by not containing a hydroxyl group. Therefore, a predetermined conductivity can be maintained for a longer period of time.

[0014] The present invention relates to a method for manufacturing a solid electrolytic capacitor, comprising an anode foil on which a dielectric layer is formed and a cathode foil, wherein a solid electrolyte and an electrolyte solution are included in the gap between the anode foil and the cathode foil, characterized in that the solid electrolyte is introduced into the gap between the anode foil and the cathode foil, the electrolyte solution is introduced afterward, and the basic component of the solute of the electrolyte solution contains an amine represented by general formula (1).

[0015] [ka] (In the formula, R 1 represents hydrogen, alkyl group, hydroxyalkyl group, or alkoxyalkyl group. R 2 , R 3 , R 4 and R 5 Each of these independently represents hydrogen, alkyl group, hydroxyl group, hydroxyalkyl group, alkoxy group, or alkoxyalkyl group. R2 and R 3 The ends of these elements may join together to form a ring. R 4 and R 5 The ends of these two elements may join together to form a ring.

[0016] Thus, the present invention is characterized by including a cyclic oxygen-containing amine in the basic component of the solute of the electrolyte. This makes it difficult for the amine to approach hydrophobic conductive polymers, such as PEDOT-PSS, due to the presence of hydrophilic oxygen atoms. Therefore, dedoping of dopants by the amine can be suppressed. Furthermore, the cyclic molecular structure allows for higher conductivity in the electrolyte compared to chain-type amines. As a result, the increase in ESR can be suppressed over a long period and sufficiently, leading to a longer capacitor lifespan. [Effects of the Invention]

[0017] According to the present invention, the rise in ESR can be suppressed sufficiently over a long period of time, thereby achieving a longer lifespan for the capacitor. [Brief explanation of the drawing]

[0018] [Figure 1] Figure 1 is a schematic cross-sectional view showing the main part of a capacitor element in a solid electrolytic capacitor according to an embodiment of the present invention. [Figure 2] Figure 2 is a partial cross-sectional view showing an example of a solid electrolytic capacitor equipped with the capacitor elements shown in Figure 1. [Figure 3] Figure 3 shows the manufacturing process of the capacitor element shown in Figure 1, with a separator sandwiched between the anode foil and the cathode foil, and the two being wound together. [Modes for carrying out the invention]

[0019] Embodiments of the present invention will be described in detail below with reference to the drawings. In this embodiment, a wound-type solid electrolytic capacitor 1 (hereinafter sometimes referred to as "capacitor 1") will be used as an example, but the form of capacitor 1 is not limited, and for example, a multilayer type may also be used.

[0020] (Capacitor element) Figure 1 is a schematic cross-sectional view showing the main part of the capacitor element 2 in the solid electrolytic capacitor 1 according to this embodiment. The capacitor element 2 comprises an anode foil 2a, a cathode foil 2b, and a separator 2c interposed between the anode foil 2a and the cathode foil 2b. The anode foil 2a and cathode foil 2b are made of valve metals such as aluminum, tantalum, and niobium, as an example. An oxide film 2d as a dielectric layer is formed on the surface of the anode foil 2a, which has been roughened by etching, by chemical conversion treatment (hereinafter, the ease of formation of this oxide film 2d may be referred to as "chemical conversion properties"). An oxide film 2e is formed on the surface of the cathode foil 2b, which has been roughened by etching, by natural oxidation. By roughening the electrode foils 2a and 2b, etch pits (depressions) are formed, increasing the specific surface area and thereby increasing the capacitance. As an example, separator 2c may be made of cellulose fibers that are chemically compatible with conductive polymers or hydrophilic polymers, or synthetic resins such as nylon, polypropylene (PP), polyethylene (PE), polyethylene terephthalate (PET), or polyphenylene sulfide (PPS) that have excellent heat resistance.

[0021] Furthermore, the capacitor element 2 contains a solid electrolyte 2f and an electrolyte solution 2g in the gap between the anode foil 2a and the cathode foil 2b, excluding the separator 2c. However, a portion of the solid electrolyte 2f may be embedded in the separator 2c, or a portion of the electrolyte solution 2g may be impregnated within it. The solid electrolyte 2f is configured to function as a cathode that substantially forms the opposite electrode of the anode foil 2a by contacting the dielectric layer (oxide film 2d) formed on the roughened anode foil 2a. The distribution of the solid electrolyte 2f is not limited, and it may be formed in a columnar, network, or layered manner in the gap between the electrode foils 2a and 2b.

[0022] The solid electrolyte 2f contains a conductive polymer. The conductive polymer is, for example, a π-conjugated polymer and may contain a dopant that exhibits or improves conductivity. In other words, the conductive polymer includes polymers that have insulating or semiconducting properties that can exhibit conductivity through doping. Examples of conductive polymers include "poly(3,4-ethylenedioxythiophene)" (PEDOT), "tetracyanoquinodimethane" (TCNQ), "polypyrrole" (PPy), "polyaniline" (PANI), and "polythiophene" (PT). These conductive polymers contain dopants such as polystyrene sulfonic acid (PSS), toluene sulfonic acid, alkylbenzene sulfonic acid, and naphthalene sulfonic acid as appropriate to have a predetermined conductivity. As an example of the conductive polymer contained in the solid electrolyte 2f, "poly(3,4-ethylenedioxythiophene)" (PEDOT), so-called "PEDOT-PSS," which is doped with polystyrene sulfonic acid (PSS), is preferably applied. The electronic conductivity of conductive polymers is orders of magnitude higher than that of ionic conductivity. Therefore, solid electrolytic capacitor 1 can achieve lower ESR than electrolytic capacitors and also exhibits superior temperature stability.

[0023] Furthermore, the conductive polymer is formed in the form of nanometer-order size (1 nm or larger). In Figure 1, the solid electrolyte 2f represents the conductive polymer particles. As shown in this figure, it is preferable that the conductive polymer particles penetrate the etch pits of the anode foil 2a and make extensive contact with the dielectric layer (oxide film 2d). From this viewpoint, it is preferable that the average particle size of the conductive polymer compound is 300 nm or less, more preferably 200 nm or less, and even more preferably 100 nm or less. Note that the conductive polymer compound referred to here includes conductive polymer particles that contain a dopant and exist integrally with the dopant.

[0024] Methods for introducing such conductive polymers between electrode foils 2a and 2b include introducing monomers, dopants, oxidizing agents, polymerization catalysts, etc., and synthesizing conductive polymers by oxidative polymerization of monomers within the capacitor element 2; and introducing a pre-polymerized and doped conductive polymer dispersion or a self-doped conductive polymer solution, drying it, and removing the dispersion medium or solvent such as water. Of these, the method using dispersions or solutions is preferable because polymerization reactions that have a certain adverse effect on the characteristics of capacitor 1 do not occur in the capacitor element 2, and residues from the polymerization reaction (e.g., oxidizing agents, etc.) that also have a certain adverse effect on the characteristics of capacitor 1 do not remain in the capacitor element 2, thereby allowing the rated voltage of capacitor 1 to be increased.

[0025] The solid electrolyte 2f may contain any additives other than the conductive polymer compound. These additives are stabilizers, reaction inhibitors, etc., introduced together with the conductive polymer or monomer for purposes such as improving or complementing the conductive properties of the conductive polymer or repairing defects in the oxide film 2d. Specifically, examples include glycerin, diglycerin, polyglycerin, etc., which are introduced into the aqueous dispersion of the conductive polymer.

[0026] Furthermore, the electrolyte 2g is introduced into the void between the electrode foils 2a and 2b, either surrounding the solid electrolyte 2f as described above or filling the gaps in the solid electrolyte 2f. The electrolyte 2g in this application is, for example, a fluid liquid component, but may also be a viscous component. The electrolyte 2g may completely fill the void between the electrode foils 2a and 2b, excluding the separator 2c and the solid electrolyte 2f, but it may not completely fill the void, and a predetermined space may exist between the electrode foils 2a and 2b.

[0027] The electrolyte 2g primarily serves to improve or complement the conductivity of the conductive polymer and to repair defects in the oxide film 2d. In other words, the electrolyte 2g has a similar function to the additives in the solid electrolyte 2f, but while the additives are introduced into the capacitor element 2 together with the conductive polymer and monomers, the electrolyte 2g can be introduced after the solid electrolyte 2f has been introduced, as described later. As a result, the electrolyte 2g can exist in the void between the electrode foils 2a and 2b, surrounding the solid electrolyte 2f or filling the gaps in the solid electrolyte 2f. However, a mixed phase of the two may be formed at the boundary between the solid electrolyte 2f and the electrolyte 2g.

[0028] The electrolyte (2 g) contains a solvent and a solute. The solute contains at least one salt, that is, at least one acidic component and at least one basic component. The acidic component may be an organic acid, an inorganic acid, or a compound thereof. Examples of organic acids include carboxylic acids, phenols, sulfonic acids, etc. Examples of carboxylic acids include formic acid, phthalic acid, isophthalic acid, terephthalic acid, salicylic acid, sulfosalicylic acid, maleic acid, adipic acid, benzoic acid, toluic acid, enanthic acid, malonic acid, 1,6-decanedicarboxylic acid, 1,7-octanedicarboxylic acid, azelaic acid, resorcinic acid, phloroglucic acid, gallic acid, citric acid, etc. Examples of inorganic acids include boric acid, phosphoric acid, phosphorous acid, hypophosphorous acid, carbonic acid, silicic acid, etc. Examples of compound compounds of organic and inorganic acids include borodisalicylic acid, borodisuoic acid, borodiglycolic acid, etc. These may be present individually or in combination of two or more types. The acidic components in 2g of these electrolytes have the function of repairing the oxide film 2d by forming a new oxide film (re-formation) in the area of ​​defect when a predetermined voltage is applied, thereby improving the formation properties of the capacitor 1.

[0029] On the other hand, this embodiment is characterized by containing an amine represented by the following general formula (1) as the base.

[0030] [ka] (In the formula, R 1 represents hydrogen, alkyl group, hydroxyalkyl group, or alkoxyalkyl group. R 2 , R 3 , R 4 and R 5 Each of these independently represents hydrogen, alkyl group, hydroxyl group, hydroxyalkyl group, alkoxy group, or alkoxyalkyl group. R 2 and R 3 The ends of these elements may join together to form a ring. R 4 and R 5 The ends of these two elements may join together to form a ring.

[0031] The amine represented by the above general formula (1) is a heterocyclic amine having a structure in which one of the opposite carbon atoms of cyclohexane is replaced with nitrogen and the other with oxygen, and in addition to the carbon that forms the six-membered ring, the nitrogen is R 1 They are bonded together. In addition, each of the four carbons has hydrogen (not shown in general formula (1)) and R, in addition to the carbon, nitrogen, or oxygen that form the six-membered ring. 2 , R 3 , R 4 or R 5 One of the following is bonded to R. Here, in the amine, 2 , R 3 , R 4 and R 5 Of hydrogen, alkyl, hydroxyl group, hydroxyalkyl group, alkoxy group, and alkoxyalkyl group, it is preferable that all of them be hydrogen, from the viewpoint of reducing the influence of steric hindrance on capacitor characteristics. On the other hand, R 1 , R 2 , R 3 , R 4 or R 5However, if each is an alkyl group or contains an alkyl group, preferably a lower alkyl group having 1 to 4 carbon atoms is preferred, and more preferably a methyl group or an ethyl group is preferred. When there are fewer carbon atoms, such as with lower alkyl groups, the viscosity decreases, making it easier to impregnate into etch pits and gaps in conductive polymers, and also providing excellent handling properties.

[0032] Examples of amines represented by general formula (1) include morpholine, 4-methylmorpholine, 4-ethylmorpholine, 4-(2-hydroxyethyl)morpholine, 2-hydroxymethylmorpholine, and cis-2,6-dimethylmorpholine. These may be included individually or in combination of two or more.

[0033] In other words, the amine represented by general formula (1) is characterized by being cyclic, unlike the chain-type amines exemplified by ethanolamine, diethanolamine, N-methyldiethanolamine, etc. Furthermore, the amine represented by general formula (1) is an oxygen-containing amine, unlike the alkyl-substituted amines exemplified by pentylamine, piperidine, N-tert-butylethylamine, dipropylamine, dimethylbutylamine, tributylamine, cyclohexylamine, etc. In this embodiment, the amine salt is characterized by being included in the solute.

[0034] According to this, by containing hydrophilic oxygen atoms, it is possible to make it difficult for amines to approach hydrophobic conductive polymers such as PEDOT-PSS. Therefore, dedoping of dopants by amines can be suppressed. In addition, because the molecular structure is cyclic, the conductivity in the electrolyte can be increased compared to chain-type amines. As a result, as will be described later, even when a high-temperature load of 1000 hours is applied in a 135°C atmosphere while applying the rated voltage, the increase in ESR can be sufficiently suppressed, and the lifespan of capacitor 1 can be extended (see Examples).

[0035] Furthermore, since the amine represented by general formula (1) has a relatively high boiling point, it is possible to improve the heat resistance of capacitor 1. In addition, it is possible to improve the chemical properties of capacitor 1 by exhibiting an oxide film 2d repair effect together with the acid component in the electrolyte.

[0036] Furthermore, among the amines according to this embodiment, amines that do not contain a hydroxyl group can be more preferably applied. That is, in general formula (1), R 1 R represents hydrogen, alkyl group, or alkoxyalkyl group, 2 , R 3 , R 4 and R 5 Preferably, each of these elements independently represents hydrogen, an alkyl group, an alkoxy group, or an alkoxyalkyl group. This prevents esterification with acidic components in the electrolyte, such as carboxylic acids. Therefore, it becomes possible to maintain a predetermined conductivity for a longer period of time.

[0037] Furthermore, if the acid dissociation constant (pKa) of the conjugate acid of the basic component is high, it becomes more likely to dissociate excessively into the base, making it easier to approach the conductive polymer. For this reason, among the amines according to this embodiment, amines with a conjugate acid acid dissociation constant (pKa) of 12.0 or less can be more preferably applied, amines with a conjugate acid acid dissociation constant (pKa) of 10.0 or less can be even more preferably applied, and amines with a conjugate acid acid dissociation constant (pKa) of 9.0 or less can be even more preferably applied. As an example, the pKa of cis-2,6-dimethylmorpholine is 9.04 ± 0.60 (predicted value), which is 10 or less. Also, the pKa of morpholine is 8.33, the pKa of 4-methylmorpholine is 7.38, and the pKa of 4-ethylmorpholine is 7.67 (all at 25 [℃]), all of which are 9 or less. Because these amines have low nucleophilicity, excessive dissociation of the basic component is suppressed, making it difficult for them to approach the conductive polymer. Therefore, dopant dedoping can be suppressed.

[0038] Furthermore, examples of solvents for 2g of electrolyte include polyol compounds such as ethylene glycol, diethylene glycol, triethylene glycol, tetraethylene glycol, pentaethylene glycol, glycerin, and diglycerin, as well as GBL (γ-butyrolactone), sulfolane, 3-methylsulfolane, 2,4-dimethylsulfolane, and dimethylformamide. These may be present individually or in combination of two or more. Of these, polyol compounds are preferred.

[0039] In this application, polyol compounds refer to polyhydric alcohols having two or more hydroxyl groups (-OH) in their molecules. Due to their low volatility, polyol compounds have high retention capacity for 2g of electrolyte, maintaining their function over a long period and suppressing the degradation of conductive polymers. Furthermore, they exhibit strong solvation properties, solvating with the cations of basic components and making it difficult for them to approach conductive polymers, thereby suppressing dopant dedoping. The solvation effect is stronger the more hydroxyl groups a solvent has relative to its molecular weight. Therefore, polyol compounds satisfying the requirement that the number of hydroxyl groups X is X≧(Y / 200) (where Y represents the molecular weight of the polyol compound) can be more suitably applied, polyol compounds satisfying the requirement that the number of hydroxyl groups X is X≧(Y / 150) (where Y represents the molecular weight of the polyol compound) can be even more suitably applied, and polyol compounds satisfying the requirement that the number of hydroxyl groups X is X≧(Y / 100) (where Y represents the molecular weight of the polyol compound) can be even more suitably applied.

[0040] For example, ethylene glycol (structural formula: HO-CH2-CH2-OH) has two hydroxyl groups (-OH) (X is 2) and a molecular weight of 62.07. Therefore, Y / 200 is 0.31, Y / 150 is 0.41, and Y / 100 is 0.62, satisfying all the requirements of X≧(Y / 200), X≧(Y / 150), and X≧(Y / 100). Similarly, diethylene glycol (number of hydroxyl groups: 2, molecular weight: 106.12), triethylene glycol (number of hydroxyl groups: 2, molecular weight: 150.17), tetraethylene glycol (number of hydroxyl groups: 2, molecular weight: 194.23), glycerin (number of hydroxyl groups: 3, molecular weight: 92.09), diglycerin (number of hydroxyl groups: 4, molecular weight: 166.17), etc., all satisfy the requirements X≧(Y / 200), X≧(Y / 150), and X≧(Y / 100). Also, pentaethylene glycol (number of hydroxyl groups: 2, molecular weight: 238.28), etc., satisfy the requirements X≧(Y / 200) and X≧(Y / 150).

[0041] These polyol compounds exhibit stronger solvation properties and can further suppress dopant dedoping. Therefore, it is particularly preferable that the solvent consists of these polyol compounds, or that the solvent be a mixture of the polyol compound and other substances, or polyethylene glycol (structural formula: HO-(CH2-CH2-O) n In the case of a polymer such as -H, with 2 hydroxyl groups, in which multiple types of polyol compounds are present, it is particularly preferable to include these polyol compounds. As an example, in this case, including 30 [mass%] or more of the total solvent is sufficient to achieve the objective and sufficiently suppress dopant dedoping. Furthermore, including 50 [mass%] or more of the total solvent can further sufficiently suppress dopant dedoping.

[0042] In addition, the void between electrode foils 2a and 2b may contain any additive along with the electrolyte 2g. This additive is introduced along with the electrolyte 2g as needed after the solid electrolyte 2f has been introduced. Specifically, examples include compounds having a nitro group, such as nitrophenol, nitrobenzoic acid, nitroacetophenone, nitroanisole, and nitrobenzyl alcohol, which are added to absorb hydrogen gas generated by recombination reactions and improve pressure resistance and heat resistance. This additive can exist in a manner similar to the electrolyte, surrounding the solid electrolyte 2f or filling the gaps in the solid electrolyte 2f.

[0043] (Solid electrolytic capacitor) Next, Figure 2 is a partial cross-sectional view showing an example of a solid electrolytic capacitor 1 equipped with the aforementioned capacitor element 2. The solid electrolytic capacitor 1 according to this embodiment is a wound-type capacitor 1 and comprises a capacitor element 2, a first lead terminal 3 joined to the anode foil 2a of the capacitor element 2, a second lead terminal 4 joined to the cathode foil 2b of the capacitor element 2, a case 5 in which the capacitor element 2 is housed, and a sealing body 6 that seals the opening of the case 5 in which the capacitor element 2 is housed.

[0044] Case 5 is a bottomed cylindrical shape and is made of a metal such as aluminum, for example. The sealing body 6 is roughly cylindrical in shape to match the inner circumference of case 5 and has through holes through which the lead terminals 3 and 4 pass and which fit at predetermined locations. This configuration allows the lead terminals 3 and 4, which are connected to the capacitor element 2, to be pulled out of the capacitor 1 through the through holes when case 5 is sealed by the sealing body 6. The sealing body 6 is preferably made of a material that is insulating, has high airtightness to prevent leakage or scattering of substances to the outside of case 5 and entry of foreign matter into case 5, has appropriate elasticity to ensure tight contact with case 5 and lead terminals 3 and 4, and can maintain these properties even at high and low temperatures. Examples of applicable materials include rubber compositions such as isobutylene-isoprene rubber, butyl rubber, ethylene propylene rubber, and fluororubber, as well as other elastomer materials.

[0045] The solid electrolytic capacitor 1 according to this embodiment can be manufactured by known methods exemplified in Japanese Patent Application Publication No. 2020-119916, except that the electrolyte 2g according to this embodiment is used. In general terms, as an example, metal foils roughened by etching are used for the anode foil 2a and cathode foil 2b. First, the anode foil 2a is immersed in a predetermined chemical conversion solution bath and a predetermined voltage is applied to form an oxide film 2d. Next, as shown in Figure 3, a separator 2c is placed between the anode foil 2a to which the first lead terminal 3 is joined and the cathode foil 2b to which the second lead terminal 4 is joined, and these are wound together to form a cylindrical capacitor element 2. Next, the wound capacitor element 2 is immersed in a predetermined chemical solution (for example, an aqueous solution of ammonium adipate, etc.), and a predetermined voltage is applied (for example, 100[V], 5[min]) to form a new oxide film 2d in the defective areas of the oxide film 2d that occurred during the joining and winding of the first lead terminal 3, thereby repairing the defective areas.

[0046] Next, a solid electrolyte 2f containing a conductive polymer is introduced. As mentioned above, methods for introducing the conductive polymer include polymerizing and synthesizing the conductive polymer within the capacitor element 2, or introducing a conductive polymer dispersion or a self-doped conductive polymer solution to remove the dispersion medium and solvent. Specifically, when introducing a conductive polymer dispersion, as an example, the capacitor element 2 is immersed in a predetermined dispersion tank containing a conductive polymer dispersion with appropriate additives. After a certain period of time, the capacitor element 2 is removed, and the dispersion medium is removed by heat treatment or the like. By repeating this operation multiple times, the solid electrolyte 2f can be introduced between the electrode foils 2a and 2b within the capacitor element 2.

[0047] The concentration of the conductive polymer in the dispersion and the number of times the above operation is performed are adjusted as appropriate. As an example, it is preferable to set the concentration of the conductive polymer in the dispersion to about 0.1 [vol%] to 10 [vol%]. By setting the concentration to 0.1 [vol%] or higher, the predetermined capacitor 1 characteristics can be achieved. More preferably, 1 [vol%] or higher is preferable, and even more preferably, 2 [vol%] or higher is preferable. Furthermore, by setting the concentration to 10 [vol%] or lower, the conductive polymer can be homogeneously dispersed in the dispersion. More preferably, 7 [vol%] or lower is preferable, and even more preferably, 3 [vol%] or lower is preferable.

[0048] Next, 2 g of electrolyte and, if necessary, additives are introduced. As an example, the capacitor element 2 is immersed for a certain period of time in a 2 g electrolyte tank containing 2 g of electrolyte with appropriate additives added. This allows the 2 g of electrolyte and additives to impregnate the electrode foils 2a and 2b. The concentration of the 2 g of electrolyte is adjusted as appropriate by adding a predetermined amount of water to the 2 g of electrolyte. The solute base component of the 2 g of electrolyte contains the amine according to this embodiment, represented by the general formula (1) described above. A commercially available amine can be used.

[0049] Next, the lead terminals 3 and 4 are passed through the through-holes of the sealing body 6 and fitted into the predetermined positions. After housing the capacitor element 2 in the case 5, the opening of the case 5 is sealed with the sealing body 6. This sealing can be done, for example, by crimping. After that, the case 5 is covered with an outer sleeve as appropriate. A predetermined voltage is also applied to repair the oxide film 2d. The solid electrolytic capacitor 1 can be manufactured by following these steps. However, these steps are just one example, and the order may be changed. [Examples]

[0050] [Test 1] A solid electrolytic capacitor with a rated voltage of 25[V] was manufactured using the same method as described in the embodiments above. However, aluminum foil was used for the anode and cathode foils. For the conductive polymer, poly(3,4-ethylenedioxythiophene) (PEDOT) doped with polystyrene sulfonic acid (PSS) was used, and an aqueous dispersion of PEDOT-PSS was introduced between the electrode foils. For the electrolyte, an electrolyte prepared with the formulations shown in Table 1 was used. Specifically, in all examples, diethylene glycol was used as the solvent and phthalic acid as the acid component of the solute. Furthermore, for the base component of the solute, morpholine was used in Example 1, 4-(2-hydroxyethyl)morpholine in Example 2, and 2-hydroxymethylmorpholine in Example 3, while triethylamine was used in Comparative Example 1. In all examples, the number of moles of the base component in the electrolyte was kept approximately constant (0.0367~0.0374). Note that the term "number of moles" here refers to the value obtained by dividing the relative quantity [parts by mass] by the molecular weight (the same applies hereafter).

[0051] [Table 1]

[0052] For each example of solid electrolytic capacitor, a high-temperature load test was conducted to evaluate its long-term reliability. The capacitor was subjected to a rated voltage of 25[V] and held at 135[°C] for 1000 hours. Capacitance and dielectric loss tangent (tanδ) at 120[Hz], ESR at 10[kHz] and 100[kHz], and leakage current (LC) at 25[V] for 1 minute were measured before and after the test. The results are shown in Table 2. Note that ΔC in the table represents the rate of change in capacitance (ΔC = (Capacitance after test - Capacitance before test) / Capacitance before test × 100).

[0053] [Table 2]

[0054] As shown in Table 2, before applying a load, there was almost no difference in the performance (measured values) of the capacitors between Examples 1, 2, and 3 and Comparative Example 1. However, after applying a load, the performance of the capacitor in Comparative Example 1 was significantly worse compared to Examples 1, 2, and 3. In contrast, in Examples 1, 2, and 3, the decrease in capacitance, the increase in dielectric loss tangent, and the increase in ESR were all suppressed, and the leakage current was kept to a low value of 10.0 to 11.8 [μA]. From this, it was shown that by using morpholine (Example 1), 4-(2-hydroxyethyl)morpholine (Example 2), or 2-hydroxymethylmorpholine (Example 3) as the basic component of the solute in the electrolyte, heat resistance is improved, degradation is suppressed, and the lifespan of the capacitor characteristics can be extended.

[0055] [Exam 2] Solid electrolytic capacitors with a rated voltage of 25[V] were manufactured using the same method as in Test 1. However, the manufacturing conditions were set to a slightly lower initial capacitance compared to Test 1. In this test, the electrolyte was prepared with the formulations shown in Table 3, and in all cases, diethylene glycol was used as the solvent and phthalic acid as the solute acid component. Furthermore, regarding the solute base component, Example 4 used morpholine (moles: 0.0373), Example 5 used morpholine (moles: 0.0746), and Example 6 used 4-ethylmorpholine (moles: 0.0747). On the other hand, Comparative Example 2 used triethylamine (moles: 0.0751), and Comparative Example 3 used diethanolamine (moles: 0.0751). In all examples except Example 4, the number of moles of the base component in the electrolyte was kept approximately constant (0.0746~0.0751). Other conditions were the same as in Test 1.

[0056] [Table 3]

[0057] For each example of solid electrolytic capacitor, a high-temperature load test was performed in the same manner as in Test 1 to evaluate its long-term reliability. The results are shown in Table 4.

[0058] [Table 4]

[0059] As shown in Table 4, before applying a load, there was almost no difference in the performance (measured values) of the capacitors between Examples 4, 5, and 6 and Comparative Examples 2 and 3. However, after applying a load, the performance of the capacitors in Comparative Examples 2 and 3 deteriorated significantly compared to Examples 4, 5, and 6. In contrast, in Examples 4, 5, and 6, the decrease in capacitance, the increase in dielectric loss tangent, and the increase in ESR were all suppressed, and the leakage current was kept to a low value of 7.2 to 8.1 [μA]. From this, it was confirmed, as in Test 1, that by using morpholine (Examples 4 and 5) or 4-ethylmorpholine (Example 6) as the basic component of the solute in the electrolyte, heat resistance is improved, degradation is suppressed, and the lifespan of the capacitor characteristics can be extended.

[0060] Furthermore, when comparing Example 4 and Example 5, in which the basic component of the solute in the electrolyte was morpholine and the amount of morpholine added was varied, Example 4, which was added at 0.0373 moles, showed better capacitor characteristics after loading than Example 5, which was added at 0.0746 moles, and in particular, the increase in ESR was significantly suppressed. This indicates that by optimally setting the amount of each amine added according to this embodiment, it is possible to further extend the lifespan.

[0061] [Exam 3] Solid electrolytic capacitors with a rated voltage of 25[V] were manufactured using the same method as in Test 1. However, the manufacturing conditions were set to slightly lower the initial capacitance compared to Test 1 (similar to Test 2). In this test, the electrolyte was prepared with the formulations shown in Table 5, and in all cases, the acidic component of the solute was phthalic acid and the basic component of the solute was 4-ethylmorpholine. The solvents used were polyethylene glycol in Example 7, diethylene glycol in Example 8, ethylene glycol in Example 9, glycerin in Example 10, and diglycerin in Example 11. In all cases, the number of moles of the basic component in the electrolyte was kept constant (0.0660) (note that the molecular weight of polyethylene glycol (approximately 200) in Table 5 represents the weight-average molecular weight (Mw)). Other conditions were the same as in Test 1.

[0062] Furthermore, the solvents in Examples 8, 9, 10, and 11 are all protic solvents, which are polyol compounds, and satisfy the aforementioned requirement regarding the number of hydroxyl groups (X ≥ (Y / 100), where X is the number of hydroxyl groups in the compound and Y is the molecular weight of the compound). In addition, the polyethylene glycol with Mw:200 in Example 7 also contains triethylene glycol, tetraethylene glycol, etc., which similarly satisfy the aforementioned requirement regarding the number of hydroxyl groups.

[0063] [Table 5]

[0064] For each example of solid electrolytic capacitor, a high-temperature load test was performed in the same manner as in Test 1 to evaluate its long-term reliability. The results are shown in Table 6.

[0065] [Table 6]

[0066] As shown in Table 6, in Examples 7, 8, 9, 10, and 11 after applying a load, the decrease in capacitance, the increase in dielectric loss tangent, and the increase in ESR were all suppressed, and the leakage current was kept to a low value of 6.1 to 8.4 [μA]. From this, it was shown that when the basic component of the solute in the electrolyte is the amine according to this embodiment, polyol compounds can be suitably applied as the solvent, and among these, solvents having a large number of hydroxyl groups relative to their molecular weight can be suitably applied.

[0067] Furthermore, the present invention is not limited to the embodiments described above, and can be modified in various ways without departing from the scope of the present invention.

Claims

1. It comprises an anode foil on which a dielectric layer is formed, and a cathode foil, A solid electrolytic capacitor comprising a solid electrolyte and an electrolyte solution in the gap between the anode foil and the cathode foil, The electrolyte comprises a solvent and a solute. The solute comprises an acidic component and a basic component. The solvent comprises a polyol compound. The number of hydroxyl groups X in the polyol compound satisfies the requirement X ≥ (Y / 200) (where Y represents the molecular weight of the polyol compound), The aforementioned base component includes an amine represented by general formula (1), In the above general formula (1), The R1 represents hydrogen, an alkyl group, or an alkoxyalkyl group. The R2, R3, R4, and R5 each independently represent hydrogen, an alkyl group, an alkoxy group, or an alkoxyalkyl group. A solid electrolytic capacitor characterized by the following features. 【Chemistry 1】 (In the formula, R １ represents hydrogen, alkyl group, hydroxyalkyl group, or alkoxyalkyl group. R ２ , R ３ , R ４ and R ５ Each of these independently represents hydrogen, alkyl group, hydroxyl group, hydroxyalkyl group, alkoxy group, or alkoxyalkyl group. R ２ and R ３ The ends of these two elements may join together to form a ring. R ４ and R ５ The ends thereof may be joined to form a ring.

2. The acid dissociation constant pKa of the conjugate acid of the amine is 12.0 or less. A solid electrolytic capacitor according to claim 1, characterized by the above.

3. It comprises an anode foil on which a dielectric layer is formed, and a cathode foil, A method for manufacturing a solid electrolytic capacitor, comprising a solid electrolyte and an electrolyte solution in the gap between the anode foil and the cathode foil, After introducing the solid electrolyte into the gap between the anode foil and the cathode foil, the electrolyte solution is introduced. The basic component of the solute in the aforementioned electrolyte is an amine represented by general formula (1). A method for manufacturing solid electrolytic capacitors characterized by the following. 【Chemistry 2】 (In the formula, R １ represents hydrogen, alkyl group, hydroxyalkyl group, or alkoxyalkyl group. R ２ , R ３ , R ４ and R ５ Each of these independently represents hydrogen, alkyl group, hydroxyl group, hydroxyalkyl group, alkoxy group, or alkoxyalkyl group. R ２ and R ３ The ends of these two elements may join together to form a ring. R ４ and R ５ The ends of these two elements may join together to form a ring.