Carbide alloy and cutting tool using same

Abstract

A cemented carbide alloy comprising a plurality of tungsten carbide particles and a binder phase, the cemented carbide alloy containing a total of 80 volume % or more of the tungsten carbide particles and the binder phase, the cemented carbide alloy containing 0.1 volume % or more and 20 volume % or less of the binder phase, the cemented carbide alloy containing at least one first element selected from the group consisting of titanium, tantalum, niobium, zirconium, hafnium and molybdenum, the cemented carbide alloy containing a total of 0.01 atomic % or more and 10.0 atomic % or less of the first element, the binder phase containing 50 mass % or more of cobalt, and the first element not segregating in a first interface region between adjacent tungsten carbide particles.

Description

[Technical field]

[0001] The present disclosure relates to a cemented carbide and a cutting tool using the same. [Background technology]

[0002] 2. Description of the Related Art Cemented carbide having tungsten carbide (WC) particles and a binder phase mainly composed of cobalt or the like has been used as a material for cutting tools (Patent Documents 1 and 2). [Prior art documents] [Patent documents]

[0003] [Patent Document 1] JP 2016-098393 A [Patent Document 2] JP 2021-110010 A Summary of the Invention

[0004] The present disclosure provides a cemented carbide comprising a plurality of tungsten carbide particles and a binder phase, The cemented carbide contains 80% by volume or more of the tungsten carbide particles and the binder phase in total, The cemented carbide contains the binder phase in an amount of 0.1% by volume or more and 20% by volume or less, The cemented carbide comprises at least one first element selected from the group consisting of titanium, tantalum, niobium, zirconium, hafnium and molybdenum; The cemented carbide contains the first element in a total amount of 0.01 atomic % or more and 10.0 atomic % or less, The binder phase contains 50% by mass or more of cobalt, The cemented carbide is a hard alloy in which the first element does not segregate in a first interface region between adjacent tungsten carbide particles. [Brief description of the drawings]

[0005] [Figure 1] FIG. 1 is a schematic cross-sectional view of a cemented carbide according to a first embodiment. [Diagram 2] FIG. 2 is a diagram for explaining a method for confirming that the first element is not segregated in the first interface region, and shows a first graph. [Diagram 3] FIG. 3 is a schematic diagram of a cutting tool according to the second embodiment. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0006] [Problem that this disclosure aims to solve] In recent years, with the expansion of 5G (fifth generation mobile communication system), the amount of information being transmitted has increased, and printed circuit boards are required to have even higher heat resistance. To improve the heat resistance of printed circuit boards, technologies have been developed to improve the heat resistance of the resin and glass filler that make up printed circuit boards. However, this has also made printed circuit boards more difficult to cut. Even when used as materials for cutting tools for drilling holes in such printed circuit boards, there is a demand for cemented carbide that can extend the life of the tools.

[0007] Therefore, an object of the present disclosure is to provide a cemented carbide alloy and a cutting tool having the same that enable a longer tool life, particularly when used as a material for cutting tools for drilling holes in printed circuit boards.

[0008] [Effects of this disclosure] According to the present disclosure, it is possible to provide a cemented carbide alloy and a cutting tool having the same that enable a longer tool life, particularly when used as a material for cutting tools for drilling holes in printed circuit boards.

[0009] [Description of the embodiments of the present disclosure] First, the embodiments of the present disclosure will be listed and described. (1) The present disclosure provides a cemented carbide comprising a plurality of tungsten carbide particles and a binder phase, The cemented carbide contains 80% by volume or more of the tungsten carbide particles and the binder phase in total, The cemented carbide contains the binder phase in an amount of 0.1% by volume or more and 20% by volume or less, The cemented carbide comprises at least one first element selected from the group consisting of titanium, tantalum, niobium, zirconium, hafnium and molybdenum; The cemented carbide contains the first element in a total amount of 0.01 atomic % or more and 10.0 atomic % or less, The binder phase contains 50% by mass or more of cobalt, The cemented carbide is a hard alloy in which the first element does not segregate in a first interface region between adjacent tungsten carbide particles.

[0010] According to the present disclosure, it is possible to provide a cemented carbide alloy and a cutting tool having the same that enable a longer tool life, particularly when used as a material for cutting tools for drilling holes in printed circuit boards.

[0011] (2) In the above (1), the total content of the first elements in the cemented carbide may be 0.1 atomic % or more and 5 atomic % or less, thereby further improving the tool life.

[0012] (3) In the above (1) or (2), the cemented carbide may contain 18 volume % or less of the binder phase, which further improves the tool life.

[0013] (4) In any one of the above (1) to (3), when the adjacent tungsten carbide particles are a first tungsten carbide particle and a second tungsten carbide particle, the first tungsten carbide particle and the second tungsten carbide particle form a first interface, The first interface region is composed of a first A region within 1.2 nm from the first interface to the first tungsten carbide particle side, and a first B region within 1.2 nm from the first interface to the second tungsten carbide particle side.

[0014] (5) A cutting tool according to the present disclosure is a cutting tool having a cutting edge made of the cemented carbide according to any one of (1) to (4) above.

[0015] The cutting tools of the present disclosure can have long tool life, especially when used in drilling holes in printed circuit boards.

[0016] [Details of the embodiment of the present disclosure] Specific examples of the cemented carbide and cutting tool of the present disclosure will be described below with reference to the drawings. In the drawings of the present disclosure, the same reference numerals represent the same or corresponding parts. Furthermore, dimensional relationships such as length, width, thickness, and depth have been appropriately changed for clarity and simplification of the drawings, and do not necessarily represent actual dimensional relationships.

[0017] In this disclosure, the expression "A to B" means the upper and lower limits of a range (i.e., A or more and B or less). When no unit is specified for A and a unit is specified only for B, the unit of A and the unit of B are the same.

[0018] In the present disclosure, when a compound or the like is represented by a chemical formula, unless the atomic ratio is particularly limited, it is intended to include any conventionally known atomic ratio, and should not necessarily be limited to only those within the stoichiometric range.

[0019] In the present disclosure, when one or more numerical values ​​are described as the lower limit and the upper limit of a numerical range, a combination of any one numerical value described as the lower limit and any one numerical value described as the upper limit is also disclosed. For example, when a1 or more, b1 or more, and c1 or more are described as the lower limit, and a2 or less, b2 or less, and c2 or less are described as the upper limit, a1 or more and a2 or less, a1 or more and b2 or less, a1 or more and c2 or less, b1 or more and a2 or less, b1 or more and b2 or less, b1 or more and c2 or less, c1 or more and a2 or less, c1 or more and b2 or less, and c1 or more and c2 or less are disclosed.

[0020] [Embodiment 1: Carbide] The cemented carbide according to one embodiment of the present disclosure (hereinafter also referred to as "embodiment 1") is A cemented carbide comprising a plurality of tungsten carbide particles and a binder phase, The cemented carbide contains 80% by volume or more of the tungsten carbide particles and the binder phase in total, The cemented carbide contains 0.1% by volume or more and 20% by volume or less of the binder phase, The cemented carbide comprises at least one first element selected from the group consisting of titanium, tantalum, niobium, zirconium, hafnium and molybdenum; The cemented carbide contains the first element in a total amount of 0.01 atomic % or more and 10.0 atomic % or less, The binder phase contains at least 50% by mass of cobalt, The cemented carbide is a cemented carbide in which the first element does not segregate in a first interface region between adjacent tungsten carbide particles.

[0021] The cemented carbide of embodiment 1 can provide a cemented carbide that enables a tool to have a long life, particularly when used as a material for a cutting tool for drilling holes in printed circuit boards, and a cutting tool including the same. The reason for this is not clear, but is presumed to be as follows.

[0022] The cemented carbide of the first embodiment includes a plurality of tungsten carbide particles (hereinafter also referred to as "WC particles") and a binder phase, and the total content of the WC particles and the binder phase in the cemented carbide is 80 volume % or more. As a result, the cemented carbide has high hardness and strength, and a cutting tool using the cemented carbide can have excellent wear resistance and breakage resistance.

[0023] The cemented carbide of the first embodiment contains a binder phase of 0.1% by volume or more and 20% by volume or less, and the binder phase contains 50% by mass or more of cobalt. This allows the cemented carbide to have high hardness and strength, and a cutting tool using the cemented carbide to have excellent wear resistance and breakage resistance.

[0024] The cemented carbide of the first embodiment contains at least one first element selected from the group consisting of titanium, tantalum, niobium, zirconium, hafnium, and molybdenum, and the cemented carbide contains the first element in a total amount of 0.01 atomic % to 10.0 atomic %. This improves the heat resistance and reactivity resistance of the cemented carbide.

[0025] In the cemented carbide of the first embodiment, the first element is not segregated in the first interface region between adjacent tungsten carbide particles. This improves the interface strength between the tungsten carbide particles in the cemented carbide, and prevents the tungsten carbide particles from falling off during cutting. Therefore, the cutting tool using the cemented carbide as a material can have a long tool life. Furthermore, the hole position accuracy of the cutting tool is improved.

[0026] <Composition of cemented carbide> As shown in FIG. 1, the cemented carbide 3 of the first embodiment includes a plurality of tungsten carbide particles 1 (hereinafter also referred to as "WC particles") and a binder phase 2, and the total content of the WC particles and the binder phase of the cemented carbide 3 is 80% by volume or more. The lower limit of the total content of the WC particles and the binder phase of the cemented carbide may be 82% by volume or more, 84% by volume or more, 85% by volume or more, or 86% by volume or more. The upper limit of the total content of the WC particles and the binder phase of the cemented carbide may be 100% by volume or less. From the viewpoint of manufacturing, the upper limit of the total content of the WC particles and the binder phase of the cemented carbide may be 99% by volume or less, or 98% by volume or less. The total content of the WC particles and the binder phase of the cemented carbide may be 80% by volume or more and 100% by volume or less, 82% by volume or more and 100% by volume or less, or 84% by volume or more and 100% by volume or less.

[0027] The cemented carbide of the first embodiment may be composed of a plurality of tungsten carbide particles and a binder phase. The cemented carbide of the present embodiment may include other phases in addition to the tungsten carbide particles and the binder phase. The other phases may include carbides, nitrides, or carbonitrides containing at least one first element selected from the group consisting of titanium (Ti), tantalum (Ta), niobium (Nb), zirconium (Zr), hafnium (Hf), and molybdenum (Mo). The compositions of the other phases may be, for example, TiCN, TaC, NbC, ZrC, HfC, or Mo2C.

[0028] The cemented carbide of the first embodiment may be composed of tungsten carbide particles, a binder phase, and other phases. The content of the other phases in the cemented carbide is acceptable within a range that does not impair the effects of the present disclosure. For example, the content of the other phases in the cemented carbide may be more than 0 vol% and less than 20 vol%, more than 0 vol% and less than 18 vol%, or more than 0 vol% and less than 16 vol%. In this case, the total content of the WC particles and the binder phase in the cemented carbide may be 80 vol% or more and less than 100 vol%, 82 vol% or more and less than 100 vol%, or 84 vol% or more and less than 100 vol%.

[0029] The cemented carbide of the first embodiment may contain impurities. Examples of the impurities include iron (Fe), calcium (Ca), silicon (Si), and sulfur (S). The content of impurities in the cemented carbide is acceptable within a range that does not impair the effects of the present disclosure. For example, the content of impurities in the cemented carbide is preferably 0% by mass or more and less than 0.1% by mass. The content of impurities in the cemented carbide is measured by ICP optical emission spectroscopy (measuring device: Shimadzu Corporation "ICPS-8100" (trademark)).

[0030] The lower limit of the content of tungsten carbide particles in the cemented carbide of embodiment 1 may be 60 volume% or more, 62 volume% or more, 64 volume% or more, or 68 volume% or more. The upper limit of the content of tungsten carbide particles in the cemented carbide may be 99.9 volume% or less, 99.2 volume% or less, 99 volume% or less, 98 volume% or less, 97 volume% or less, or 90 volume% or less. The content of tungsten carbide particles in the cemented carbide may be 60 volume% or more and 99.9 volume% or less, 60 volume% or more and 99.2 volume% or less, 64 volume% or more and 97 volume% or less, or 68 volume% or more and 90 volume% or less.

[0031] The cemented carbide of the first embodiment contains a binder phase of 0.1 volume % or more and 20 volume % or less. The lower limit of the binder phase content of the cemented carbide is 0.1 volume % or more, may be 0.4 volume % or more, 1 volume % or more, 1.5 volume % or more, 2 volume % or more, 3 volume % or more, or 8 volume % or more, from the viewpoint of improving toughness. The upper limit of the binder phase content of the cemented carbide is 20 volume % or less, may be 18 volume % or less, may be 16 volume % or less, or may be 15 volume % or less, from the viewpoint of improving hardness. The binder phase content of the cemented carbide may be 0.1 volume % or more and 18 volume % or less, may be 0.4 volume % or more and 18 volume % or less, may be 1.5 volume % or more and 16 volume % or less, or may be 8 volume % or more and 14 volume % or less. When the content of the binder phase in the cemented carbide is 18 volume % or less, the hardness and wear resistance of the cemented carbide are further improved, and therefore the tool life of a cutting tool using the cemented carbide as a material is further improved. The Rockwell hardness (HRC) of the cemented carbide of this embodiment may be, for example, 90 to 95, or 91 to 95.

[0032] The method for measuring the content (volume %) of tungsten carbide particles in the cemented carbide and the content (volume %) of the binder phase in the cemented carbide is as follows.

[0033] (A1) An arbitrary position of the cemented carbide is cut out to expose a cross section, which is then mirror-finished using a cross-section polisher (manufactured by JEOL Ltd.).

[0034] (B1) The mirror-finished surface of the cemented carbide is analyzed using a scanning electron microscope-energy dispersive X-ray spectroscopy (SEM-EDX) (apparatus: Carl Zeiss Gemini450 (trademark)) to identify the elements contained in the cemented carbide.

[0035] (C1) The mirror-finished surface of the cemented carbide is photographed with a scanning electron microscope (SEM) to obtain a backscattered electron image. The photographed area is set to the center of the cross section of the cemented carbide, that is, a position that does not include areas with properties that are clearly different from the bulk part, such as the surface area of ​​the cemented carbide (a position where the entire photographed area is the bulk part of the cemented carbide). The observation magnification is 5000x. The measurement conditions are an acceleration voltage of 3kV, a current value of 2nA, and a working distance (WD) of 5mm.

[0036] (D1) The photographed region of (C1) above is analyzed using an energy dispersive X-ray analyzer attached to a SEM (SEM-EDX), the distribution of the elements identified in (B1) above in the photographed region is identified, and an element mapping image is obtained.

[0037] (E1) The backscattered electron image obtained in (C1) above is imported into a computer and binarized using image analysis software (OpenCV, SciPy). In the binarized image, tungsten carbide particles are shown in white, and the bond phase is shown in gray to black. Note that the binarization threshold changes depending on the contrast, so it is set for each image.

[0038] (F1) By superimposing the element mapping image obtained in (D1) above and the image after the binarization process obtained in (E1) above, the respective regions of the tungsten carbide particles and the binder phase are identified on the image after the binarization process. Specifically, the regions shown in white in the image after the binarization process and in which tungsten (W) and carbon (C) exist in the element mapping image correspond to the regions of the tungsten carbide particles. The regions shown in gray to black in the image after the binarization process and in which cobalt (Co) exists in the element mapping image correspond to the regions of the binder phase.

[0039] (G1) A rectangular measurement field of view of 24.9 μm × 18.8 μm is set in the image after the binarization process. Using the image analysis software, the area percentages of the tungsten carbide particles and the binder phase are measured with the area of ​​the entire measurement field as the denominator.

[0040] (H1) The measurement of (G1) above is carried out in five different non-overlapping measurement fields. In this specification, the average of the area percentages of tungsten carbide particles in the five measurement fields corresponds to the content (volume %) of tungsten carbide particles in the cemented carbide, and the average of the area percentages of the binder phase in the five measurement fields corresponds to the content (volume %) of the binder phase in the cemented carbide.

[0041] If the cemented carbide contains other phases in addition to the WC particles and the binder phase, the content of the other phases in the cemented carbide can be obtained by subtracting the content (volume %) of the tungsten carbide particles and the content (volume %) of the binder phase measured by the above procedure from the total cemented carbide (100 volume %).

[0042] As far as the applicant has measured, as long as measurements are performed on the same sample, the cut-out location of the cemented carbide cross section, the photographing area described in (C1) above, and the measurement field of view described in (G1) above can be arbitrarily set, and even if the tungsten carbide particle content and the binder phase content of the cemented carbide are measured multiple times according to the above procedure, there is little variation in the measurement results, and it has been confirmed that the cut-out location of the cemented carbide cross section, the photographing area, and the measurement field of view can be arbitrarily set without being arbitrary.

[0043] <Tungsten carbide particles> In the first embodiment, the tungsten carbide particles include at least one of "pure WC particles (including WC containing no impurity elements and WC containing impurity elements below the detection limit)" and "WC particles containing impurity elements intentionally or unavoidably, as long as the effect of the present disclosure is not impaired." The content of impurities in the tungsten carbide particles (when two or more elements are included as impurities, the total concentration of the elements) is less than 0.1% by mass. The content of impurities in the tungsten carbide particles is measured by ICP emission spectrometry.

[0044] In the first embodiment, the average particle size of the tungsten carbide particles is not particularly limited. The average particle size of the tungsten carbide particles can be, for example, 0.1 μm or more and 3.5 μm or less. It has been confirmed that the cemented carbide of the first embodiment can have a long tool life regardless of the average particle size of the tungsten carbide particles.

[0045] <Binded phase> In the first embodiment, the binder phase contains 50% by mass or more of cobalt. This can impart excellent toughness to the cemented carbide. The lower limit of the cobalt content of the binder phase may be 52% by mass or more, 60% by mass or more, 66% by mass or more, or 70% by mass or more. The upper limit of the cobalt content of the binder phase may be 100% by mass or less, less than 100% by mass, 95% by mass or less, 93% by mass or less, or 90% by mass or less. The cobalt content of the binder phase may be 50% by mass or more and less than 100% by mass, 60% by mass or more and 95% by mass or less, or 70% by mass or more and 90% by mass or less.

[0046] The method for measuring the cobalt content of the binder phase is as follows. Using the same methods as (A1) to (F1) for measuring the tungsten carbide particle content, binder phase content, and hard phase particle content of the above-mentioned cemented carbide, the region in which the binder phase exists is identified on the image after the binarization process. The region in which the binder phase exists is analyzed using SEM-EDX to measure the cobalt content of the binder phase.

[0047] As far as the applicant has measured, as long as the same sample is measured, even if the cut-out portion of the cross section of the cemented carbide and the photographed area described in (C1) above are arbitrarily set and the cobalt content of the binder phase is measured multiple times according to the above procedure, there is little variation in the measurement results, and it has been confirmed that arbitrarily setting the cut-out portion of the cross section of the cemented carbide and the photographed area is not arbitrary.

[0048] In the first embodiment, the binder phase may contain at least one first element selected from the group consisting of titanium, tantalum, niobium, zirconium, hafnium, and molybdenum in addition to cobalt. The binder phase may contain at least one second element selected from the group consisting of nickel (Ni), chromium (Cr), iron (Fe), aluminum (Al), ruthenium (Ru), and rhenium (Re) in addition to cobalt and the first element. The binder phase may contain cobalt, the first element, and a second element. The binder phase may contain cobalt, the first element, the second element, and inevitable impurities. Examples of the inevitable impurities include manganese (Mn), magnesium (Mg), calcium (Ca), and sulfur (S).

[0049] <1st element> The cemented carbide of the first embodiment includes at least one first element selected from the group consisting of titanium, tantalum, niobium, zirconium, hafnium, and molybdenum, and the cemented carbide includes the first element in a total amount of 0.01 atomic % or more and 10 atomic % or less. The lower limit of the content of the first element in the cemented carbide is 0.01 atomic % or more, may be 0.03 atomic % or more, may be 0.1 atomic % or more, may be 0.8 atomic % or more, may be 1 atomic % or more, may be 2 atomic % or more, or may be 2.3 atomic % or more, from the viewpoint of improving the tool life. The upper limit of the content of the first element in the cemented carbide is 10.0 atomic % or less, may be 9 atomic % or less, may be 8.2 atomic % or less, may be 8 atomic % or less, may be 7.7 atomic % or less, or may be 5 atomic % or less, from the viewpoint of maintaining the strength. The content of the first element in the cemented carbide may be 0.1 atomic % or more and 5 atomic % or less.

[0050] The content of the first element in the cemented carbide based on the atomic number is measured by ICP (Inductively Coupled Plasma) optical emission spectrometry (measuring device: Shimadzu Corporation's "ICPS-8100" (trademark)).

[0051] In the cemented carbide of embodiment 1, the first element is not segregated in the first interface region between the adjacent tungsten carbide particles, which improves the interface strength between the tungsten carbide particles, and the cemented carbide can have excellent wear resistance and breakage resistance.

[0052] In the present disclosure, a method for confirming that the first element is not segregated in the first interface region between adjacent tungsten carbide particles of the cemented carbide will be described with reference to FIG.

[0053] The cemented carbide is sliced ​​to a thickness of 30 to 100 nm using an argon ion slicer ("Cryo Ion Slicer IB-09060BCIS" (trademark) manufactured by JEOL Ltd.) under conditions of an acceleration voltage of 6 kV and finishing of 2 kV, to prepare a measurement sample. Next, the measurement sample is observed at 200,000 times magnification using a TEM (Transmission Electron Microscopy) ("JEM-ARM300F2" (trademark) manufactured by JEOL Ltd.) under conditions of an acceleration voltage of 200 V to obtain a first image (not shown).

[0054] In the first image, the tungsten carbide particles are observed as white regions, the binder phase is observed as black regions, and the interface is observed as black regions. In the first image, the interface between the tungsten carbide particles is arbitrarily selected. In the present disclosure, the adjacent tungsten carbide particles that form the interface are also referred to as the first tungsten carbide particle and the second tungsten carbide particle.

[0055] Next, the selected interface is positioned so as to pass through the vicinity of the center of the image, and the observation magnification is adjusted so that the field of view size is 5 nm x 5 nm, and a second image is obtained (not shown). In the second image, the extension direction of the interface is confirmed. Line analysis is performed perpendicular to the extension direction and in a direction from the first tungsten carbide particle to the second tungsten carbide particle to obtain a graph (hereinafter also referred to as the first graph) measuring the distribution of cobalt, tungsten, and the first element. When the cemented carbide contains two or more kinds of the first element, the distribution of each element is measured. Here, the direction perpendicular to the extension direction of the interface means the direction along a straight line intersecting the tangent of the extension direction at an angle of 90° ± 5°. The measurement conditions for obtaining the second image are an acceleration voltage of 200 kV, a camera length of 10 cm, a pixel count of 128 x 128 pixels, and a dwell time of 0.02 to 3 s / pixel.

[0056] Fig. 2 is an example of the first graph. In Fig. 2, the horizontal axis (X axis) indicates the distance (nm) from the measurement start point, and the vertical axis (Y axis) indicates the NET intensity (unitless). In the cemented carbide shown in Fig. 2, the first element is tantalum (Ta).

[0057] In the first graph, the position of the cobalt peak is identified. In this disclosure, the position of the cobalt peak is referred to as the first interface. The first interface is formed by a first tungsten carbide particle and a second tungsten carbide particle adjacent to each other. In the first graph of FIG. 2, the position of the first interface is 4.15 nm on the X-axis.

[0058] In the first graph, a first A region is identified that is located within 1.20 nm from the first interface to the first tungsten carbide particle side, and a first B region is identified that is located within 1.20 nm from the first interface to the second tungsten carbide particle side. In the present disclosure, the region consisting of the first A region and the first B region is the first interface region. In the first graph of FIG. 2, the position of the first interface region is 2.95 to 5.35 nm on the X-axis.

[0059] In the first graph, a second A region is identified in which the distance from the first interface to the first tungsten carbide particle side is 1.50 nm or more and 3.50 nm or less, and a second B region is identified in which the distance from the first interface to the second tungsten carbide particle side is 1.50 nm or more and 3.50 nm or less. In the first graph of Fig. 2, the position of the second A region is 0.65 to 2.65 nm on the X axis, and the position of the second B region is 5.65 to 7.65 nm on the X axis.

[0060] Based on the first graph, the average B of the NET strength in the baseline region consisting of the second A region and the second B region of the first element is calculated. In the first graph, the maximum value A of the NET strength in the first interface region of the first element is measured. When the ratio A / B of the maximum value A to the average B is less than 3, it is confirmed that the first element is not segregated in the first interface region between adjacent tungsten carbide particles of the cemented carbide. In the first graph of FIG. 2, the average B of the NET strength in the baseline region consisting of the second A region and the second B region of tantalum (first element) is 78.7 (the average NET strength in the second A region is 97.6, and the average NET strength in the second B region is 59.7), and the maximum value A of the NET strength in the first interface region of tantalum (first element) is 112.6. In the cemented carbide shown in FIG. 2, A / B is 1.43, so it is confirmed that the first element is not segregated in the first interface region between adjacent tungsten carbide particles of the cemented carbide.

[0061] In a cemented carbide, first images are arbitrarily obtained from five mutually non-overlapping fields, and the above-mentioned analysis is repeatedly performed based on each of the first images. If segregation of the first element is not confirmed in the first interface region in four or more fields, it is determined that the first element is not segregated in the first interface region between adjacent tungsten carbide particles in the cemented carbide.

[0062] As far as the applicant has measured, it has been confirmed that, as long as the same sample is measured, the cut-out portion of the cross section of the cemented carbide is arbitrarily set, the first image is arbitrarily obtained on the cross section, and the presence or absence of segregation of the first element in the first interface region is confirmed multiple times according to the above procedure by changing the region of the line analysis, with almost no variation in the results of the presence or absence of segregation of the first element in the first interface region. Therefore, as long as the above-mentioned method for confirming the segregation of the first element is performed on the cemented carbide and it is confirmed that the first element is not segregated in the first interface region, it is inferred that the interfacial strength between the tungsten carbide particles of the cemented carbide is improved.

[0063] In the cemented carbide of the present disclosure, the first element can be present in the other phases mentioned above or in cobalt.

[0064] <Method of manufacturing cemented carbide> The cemented carbide of this embodiment can be manufactured by carrying out the steps of preparing raw material powder, mixing, molding, sintering, and cooling in the above order. Each step will be described below.

[0065] <Preparation process> The preparation step is a step of preparing raw material powders of materials constituting the cemented carbide material. Examples of the raw material powders include tungsten carbide powder (hereinafter also referred to as "WC powder"), cobalt (Co) powder, and powder containing a first metal element. Examples of the powder containing a first metal element include titanium carbonitride (TiCN) powder, tantalum carbide (TaC) powder, niobium carbide (NbC) powder, zirconium carbide (ZrC) powder, hafnium carbide (HfC) powder, molybdenum carbide (Mo2C) powder, and the like. These raw material powders can be commercially available. The average particle size of these raw material powders is not particularly limited, and can be, for example, 0.1 to 3.0 μm. The average particle size of the raw material powders means the average particle size measured by the FSSS (Fisher Sub-Sieve Sizer) method. The average particle size is measured using a "Sub-Sieve Sizer Model 95" (trademark) manufactured by Fisher Scientific. The particle size distribution of the WC powder is measured using a particle size distribution measuring device manufactured by Microtrac (product name: MT3300EX).

[0066] <Mixing process> The mixing step is a step of mixing the raw material powders prepared in the preparation step in a predetermined ratio. A mixed powder in which the raw material powders are mixed is obtained by the mixing step. The mixing ratio of the raw material powders is appropriately adjusted depending on the composition of the target cemented carbide.

[0067] The raw material powders can be mixed by a conventionally known mixing method such as an attritor, a ball mill, or a bead mill. Conventional known conditions can also be used for the mixing conditions. For example, the mixing time can be, for example, 2 hours or more and 20 hours or less.

[0068] After the mixing step, the mixed powder may be granulated as necessary. By granulating the mixed powder, it becomes easier to fill the mixed powder into a die or a mold during the molding step described below. For granulation, a known granulation method can be applied, and for example, a commercially available granulator such as a spray dryer can be used.

[0069] <Forming process> The molding step is a step of forming the mixed powder obtained in the mixing step into a shape for a cutting tool (e.g., a round bar shape) to obtain a molded body. The molding method and molding conditions in the molding step are not particularly limited and may be general methods and conditions.

[0070] <Sintering process> The sintering process is a process in which the compact obtained through the molding process is sintered by a sintering HIP (Hot Isostatic Pressing) process, which can perform sintering and pressing simultaneously, to obtain a cemented carbide intermediate.

[0071] The sintering process can include a first sintering process and a second sintering process. First, in the first sintering process, the sintering temperature is kept at 1300°C and the sintering pressure is kept at 7MPa for 240 minutes. Next, in the second sintering process, the temperature is raised to 1360°C while maintaining the sintering pressure at 7MPa, and the carbide intermediate is kept at 1360°C for 15 minutes to obtain the carbide intermediate.

[0072] The atmosphere during sintering is not particularly limited, but for example, an N2 gas atmosphere or an inert gas atmosphere such as Ar can be used.

[0073] <Cooling process> The cooling step is a step of cooling the cemented carbide intermediate body after the sintering step. For example, the cemented carbide intermediate body can be quenched in Ar gas under a pressure condition of 100 to 400 MPaG to obtain a cemented carbide.

[0074] <Features of the method for manufacturing the cemented carbide according to this embodiment> The sintering temperature of 1300°C in the first sintering step is lower than that of a general cemented carbide. Furthermore, the sintering time of 240 minutes in the first sintering step is longer than that of a general cemented carbide, which is 30 to 60 minutes. It is presumed that this advances the diffusion and rearrangement of atoms during sintering, and that the cemented carbide of the present disclosure can be obtained in which the first element is not segregated in the first interface region between adjacent tungsten carbide particles. The fact that the cemented carbide of the present disclosure can be realized under such sintering conditions is something that the present inventors have newly discovered as a result of intensive research. Note that the sintering temperature and sintering time in the first sintering step would not have been adopted by those skilled in the art because they would reduce production efficiency.

[0075] [Embodiment 2: Cutting tool] The cutting tool of this embodiment includes a cutting edge made of the cemented carbide of embodiment 1. In this disclosure, the cutting edge means a part involved in cutting. More specifically, the cutting edge means a region surrounded by a cutting edge ridge and a virtual surface that is 2 mm away from the cutting edge ridge toward the cemented carbide side.

[0076] Examples of cutting tools include cutting tools, drills, end mills, indexable cutting tips for milling, indexable cutting tips for turning, metal saws, gear cutting tools, reamers, taps, etc. In particular, as shown in Fig. 3, the cutting tool 10 of this embodiment can exhibit excellent effects in the case of a small diameter drill for processing printed circuit boards. The cutting edge 11 of the cutting tool 10 shown in Fig. 3 is made of the cemented carbide of the first embodiment.

[0077] The cemented carbide of the present embodiment may constitute the entirety of these tools, or may constitute a part of them. Here, "constitute a part" refers to a mode in which the cemented carbide of the present embodiment is brazed to a predetermined position of any substrate to form a cutting edge.

[0078] The cutting tool of this embodiment may further include a hard film covering at least a part of the surface of the substrate made of cemented carbide. The hard film may be made of, for example, diamond-like carbon or diamond.

[0079] The cutting tool of this embodiment can be obtained by forming the cemented carbide of embodiment 1 into a desired shape. EXAMPLES

[0080] The present embodiment will be described in more detail with reference to examples, although the present embodiment is not limited to these examples.

[0081] [Preparation of cemented carbide] Each sample of cemented carbide was prepared according to the following procedure.

[0082] WC powder (average particle size 0.3 μm), Co powder (average particle size 1.0 μm), TiCN powder (average particle size 1.0 μm), TaC powder (average particle size 1.0 μm), NbC powder (average particle size 1.0 μm), ZrC powder (average particle size 1.0 μm), HfC powder (average particle size 1.0 μm), and Mo2C powder (average particle size 1.0 μm) were prepared in the ratios shown in the "raw powder" column of Table 1, and mixed to obtain a mixed powder. For example, in sample 1, WC powder, Co powder, and TiCN powder were prepared in a mass ratio of 81.8:11.7:6.5, and mixed to obtain a mixed powder. In all samples, mixing was performed for 10 hours using an attritor.

[0083] [Table 1]

[0084] Next, the mixed powder was press-molded to produce a round bar-shaped compact. Next, the compact was subjected to a first sintering step in Ar gas. The temperature, pressure, and time in the first sintering step are as shown in the "First sintering step" column of Table 2. Next, while maintaining the pressure, the temperature was changed to 1360°C, and a second sintering step was performed to obtain a cemented carbide intermediate. The holding time in the second sintering step is as shown in the "Second sintering step" column of Table 2. Next, the cemented carbide intermediate was quenched in Ar gas under a pressure of 200 MPaG to obtain each sample of cemented carbide.

[0085] [Table 2]

[0086] [Cutting tool manufacturing] The obtained round bar made of cemented carbide was machined to produce a drill for machining printed circuit boards (PCB (Printed Circuit Board) drill) with a cutting edge diameter of φ0.3 mm.

[0087] [Evaluation of cemented carbide] <Content (volume %) of tungsten carbide particles and binder phase (volume %) of cemented carbide> The content (volume %) of tungsten carbide particles and the content (volume %) of the binder phase of the cemented carbide of each sample were measured. The specific measurement method is as described in the first embodiment. The results are shown in the "WC particle content" and "binder phase content" columns of "Cemented carbide" in Table 3. Furthermore, the total content of tungsten carbide particles and the binder phase of the cemented carbide are shown in the "WC particle + binder phase content" column of "Cemented carbide" in Table 3. In Table 3, it was confirmed that the cemented carbide having a "WC particle + binder phase content" column of less than 100% by volume further contains at least one selected from the group consisting of carbides, nitrides, and carbonitrides containing the first element.

[0088] <Cobalt content in binder phase> The cobalt content in the binder phase of each cemented carbide sample was measured. The specific measurement method is as described in embodiment 1. The results are shown in the "Co content in binder phase" column of "Cemented carbide" in Table 3. It was also confirmed that in all samples, the binder phase contained, in addition to cobalt, the same first element as the first element listed in the "Type of first element" column of "Cemented carbide" in Table 3.

[0089] <Content of the first element in cemented carbide> For each sample of cemented carbide, the type of the first element contained in the cemented carbide and the total content (atomic %) of the first element in the cemented carbide were measured. The specific measurement method is as described in embodiment 1. The results are shown in the "Type of first element" and "Content of first element" columns of "Cemented carbide" in Table 3. When there is one type of first element, the "Content of first element" means the content of one type of first element. When there are two types of first elements, the "Content of first element" means the total content of two types of first elements.

[0090] <Presence or absence of segregation of the first element in the first interface region> In each sample of cemented carbide, the presence or absence of segregation of the first element in the first interface region between adjacent tungsten carbide particles was confirmed. The specific confirmation method is as described in embodiment 1. The results are shown in the "Segregation of the first element" column of "Cemented carbide" in Table 3.

[0091] <Rockwell hardness> The Rockwell hardness (HRC) of each sample of cemented carbide was measured in accordance with "JIS Z 2245:2016 Rockwell hardness test - Test method". The measurement conditions were room temperature (23℃±5℃), test force of 60N, and holding time of 4 seconds. The results are shown in the "Rockwell hardness" column in Table 3.

[0092] [Cutting tool evaluation] <Cutting test> Using each sample PCB drill, a commercially available printed circuit board for automotive use was drilled, and the hole position accuracy was evaluated. The conditions for the drilling were a rotation speed of 120 krpm, a feed rate of 2 m / min, and a drawing rate of 25 m / min. The number of holes drilled (the number of hits) was measured when the hole position accuracy (ave+3σ(μm)) exceeded 70 μm. The results are shown in the "Cutting test" column of Table 3. The values ​​in Table 3 are the actual number of holes drilled rounded down to the nearest ten. For example, if the actual number of holes drilled was 6250, it would be listed as 6200 in the "Cutting test" column. The higher the number of holes drilled, the better the hole position accuracy of the cutting tool and the longer the tool life.

[0093] [Table 3]

[0094] <Consideration> The cemented carbide and cutting tools of Samples 1 to 13 correspond to Examples. The cemented carbide and cutting tools of Samples 1-1 to 1-8 correspond to Comparative Examples. It was confirmed that the cutting tools of Samples 1 to 13 (Examples) had better hole position accuracy and longer tool life than the cutting tools of Samples 1-1 to 1-8 (Comparative Examples). This is presumably because the cemented carbide of Samples 1 to 13 has excellent wear resistance and breakage resistance.

[0095] Although the embodiments and examples of the present disclosure have been described above, it is intended from the outset that the configurations of the above-described embodiments and examples may be appropriately combined or modified in various ways. The embodiments and examples disclosed herein are illustrative in all respects and should not be considered as limiting. The scope of the present invention is indicated by the claims, not by the embodiments and examples described above, and is intended to include the meaning equivalent to the claims and all modifications within the scope. [Explanation of symbols]

[0096] 1 tungsten carbide particle, 2 binder phase, 3 cemented carbide, 10 cutting tool, 11 cutting edge.

Claims

1. A cemented carbide comprising a plurality of tungsten carbide particles and a binder phase, The cemented carbide contains 80 volume % or more of the tungsten carbide particles and the binder phase in total, The cemented carbide contains the binder phase in an amount of 0.1% by volume or more and 20% by volume or less, The cemented carbide comprises at least one first element selected from the group consisting of titanium, tantalum, niobium, zirconium, hafnium and molybdenum; The cemented carbide contains the first element in a total amount of 0.01 atomic % or more and 10.0 atomic % or less, The binder phase contains 50% by mass or more of cobalt, the first element is not segregated in a first interface region between adjacent tungsten carbide particles, When the tungsten carbide particles adjacent to each other are a first tungsten carbide particle and a second tungsten carbide particle, the first tungsten carbide particle and the second tungsten carbide particle form a first interface, The first interface region includes a first A region having a distance of 1.2 nm or less from the first interface to the first tungsten carbide particle side, and a first B region having a distance of 1.2 nm or less from the first interface to the second tungsten carbide particle side. A cemented carbide alloy.

2. 2. The cemented carbide of claim 1, wherein the total content of the first elements in the cemented carbide is 0.1 atomic % or more and 5 atomic % or less.

3. 3. The cemented carbide of claim 1 or claim 2, wherein the cemented carbide comprises up to 18% by volume of the binder phase.

4. A cutting tool having a cutting edge made of the cemented carbide according to claim 1 or 2.

Images