Composition for forming surface layer, surface layer formed from said composition, surface material for writing on oil-based ink, and article including said surface material

Abstract

To provide a surface layer formation composition that makes it possible to easily erase handwritten traces of oil-based ink, and erase the handwritten traces on the surface layer.SOLUTION: The surface layer formation composition in the present invention contains at least a polyfunctional acrylate capable of forming a crosslink structure upon irradiation with ultraviolet ray, and a photopolymerization initiator. An example of the composition is a surface layer formation composition in which the polyfunctional acrylate is one or more polyfunctional acrylate selected from polyfunctional acrylate having a pentaerythritol skeleton and polyfunctional acrylate having a urethane bond, and the photopolymerization initiator is 1-hydroxycyclohexylphenyl ketone.SELECTED DRAWING: Figure 1

Description

[Technical field]

[0001] The present invention relates to a composition for forming a surface layer, etc. More specifically, the present invention relates to a composition for forming a surface layer, etc., which can provide a surface layer on which writing can be done with oil-based ink and from which the handwriting can be erased. [Background technology]

[0002] 2. Description of the Related Art Conventionally, there are surface treatment techniques aimed at forming a surface layer that is both writable and erasable with a general writing implement. For example, the following Patent Document 1 proposes a low-reflection member having a low refractive index layer containing an inorganic compound on a transparent plastic film. The surface of the low-reflection member can be written on with oil-based marker pen, and ink can be sufficiently adhered to the surface. Meanwhile, the handwriting of the oil-based marker pen can be erased by the simple task of dropping water on the surface.

[0003] In addition, the following Patent Document 2 proposes a writable and erasable writing sheet having a base film and an information recording layer provided on the base film and containing a matting agent made of silicone particles and a release agent. The surface of the writing sheet can be written on with a general writing instrument such as a colored pencil, a water-based felt-tip pen, or an oil-based ink pen, and the handwriting written with the writing instrument can be erased with tissue paper containing an erasing agent made of a mixed liquid of isopropyl alcohol and normal propyl alcohol (1:1 mass ratio). [Prior art documents] [Patent documents]

[0004] [Patent Document 1] Patent Publication No. 2019-152836 [Patent Document 2] Patent Publication No. 2005-28602 Summary of the Invention [Problem to be solved by the invention]

[0005] Therefore, the main object of the present invention is to provide a composition for forming a surface layer which can be written on with oil-based ink and which allows the handwriting of the oil-based ink to be easily erased, for example, by rubbing the handwriting with a plastic eraser. [Means for solving the problem]

[0006] In order to solve the above problems, the present invention provides a surface layer forming composition that contains at least a multifunctional acrylate capable of forming a crosslinked structure by irradiation with ultraviolet light and a photopolymerization initiator, and forms a surface layer that can be written with oil-based ink and can erase written marks. More specifically, the surface layer forming composition according to claim 1 includes one or more multifunctional acrylates selected from a multifunctional acrylate having a pentaerythritol skeleton or a multifunctional acrylate having a urethane bond. For example, the handwriting can be erased with a plastic eraser. The present invention also provides a surface layer formed by the above-mentioned surface layer forming composition, a surface material for oil-based ink writing that includes at least the surface layer, and an article that includes at least the surface material. Effect of the Invention

[0007] According to the composition for forming a surface layer of the present invention, handwriting of oil-based ink written in the present invention can be easily erased, and there is an effect that the handwriting can be erased, for example, by rubbing it with a plastic eraser. [Brief description of the drawings]

[0008] [Figure 1] FIG. 2 is a diagram for explaining the basic layer structure of a panel having a surface layer according to the present invention. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0009] The present invention provides a composition for forming a surface layer. More specifically, the present invention provides a composition for forming a surface layer that can be written on with an oil-based ink and that can easily erase the handwriting, for example, by rubbing the handwriting with a plastic eraser. The present invention will be described below with reference to the embodiments, but the present invention is not limited thereto.

[0010] Here, the type of the "oil-based ink" is not narrowly limited, and for example, oil-based inks generally used in oil-based markers and oil-based ballpoint pens can be widely applied. The "oil-based marker" that is the subject of the present invention is not narrowly limited, but for example, it is a marking pen in which an absorbent body soaked in oil-based ink is placed in a cylindrical container and a fiber or plastic pen tip is attached to the absorbent body.

[0011] The "oil-based ink" of the oil-based marker is not narrowly limited, but is an ink having a composition containing at least an organic solvent, a resin, and a dye. A more detailed representative composition example of the oil-based ink for oil-based marker is an oil-based ink composed of a solvent containing 65 to 91 mass% in total of propylene glycol monomethyl ether, ethyl alcohol, isopropyl alcohol, benzyl alcohol, methyl ethyl ketone, etc., 1 to 10 mass% of resin, and 1 to 20 mass% of dye.

[0012] The "plastic (synthetic resin) eraser" (hereinafter "eraser") applicable to the present invention is a commercially available synthetic resin eraser (so-called rubber eraser) that is generally used to erase drawings made mainly with a pencil or mechanical pencil. One example is a plastic eraser whose main component is polyvinyl chloride.

[0013] The surface layer forming composition according to the present invention is used to form a surface layer of various surface materials that require writing with oil-based ink. For example, it can be widely used in writing boards such as blackboards and whiteboards, memo pads, drawing boards, cards, cases for home appliances, and even wall materials for buildings.

[0014] In addition, the surface layer formed by the composition for forming a surface layer according to the present invention is not limited to a planar shape, and can be used on the surface of various types of articles. For example, it can be widely used in office supplies including stationery, files, storage items, etc., furniture such as desks and storage cabinets, and office equipment including various electronic devices. Suitable examples of the article according to the present invention include wristbands and smartphone cases. The wristbands and smartphone cases are useful when you want to temporarily record information in a situation where you do not have the space to carry a notebook or memo paper. Another suitable example of the article according to the present invention is a tag and a nameplate. The tags and nameplates can be used as markers when sorting and storing items, and can be rewritten with oil-based ink, allowing for repeated use.

[0015] The method of forming the surface layer on the substrate using the composition for forming a surface layer is not particularly limited, but for example, the composition for forming a surface layer can be directly applied to the substrate or sprayed. Alternatively, a method of preparing a sheet using the composition for forming a surface layer in advance and attaching the sheet to the substrate using an adhesive or the like may be adopted.

[0016] Here, the surface layer-forming composition refers to a composition capable of forming a UV-curable resin (A) by irradiation with ultraviolet light, and contains a multifunctional acrylate (B) and a photopolymerization initiator (C), and, if necessary, contains an additive (D) for adjusting the physical properties of the composition, such as the surface tension.

[0017] (A) About UV-curable resin. A UV-curable resin is a resin in which a crosslinked structure is formed by a reaction between polymerizable monomers or oligomers such as vinyl groups, acryloyl groups, or epoxy groups, using radicals or cations generated by irradiation with light (ultraviolet rays) as the initiating species. From the viewpoints of the abundance of types of monomers and oligomers that can be used and cost, the present invention relates to a UV-curable resin containing a multifunctional acrylate that uses radicals as the initiating species.

[0018] (B) Regarding multifunctional acrylates. The (B) multifunctional acrylate used in the present invention is a main component of the composition for forming a surface layer, and examples thereof include various (b1) multifunctional acrylate monomers and (b2) multifunctional acrylate oligomers, but are not limited thereto.

[0019] (b1) Regarding polyfunctional acrylate monomers. The polyfunctional acrylate monomer is a general term for a compound having two or more acryloyl groups in the molecule, and can be selected from various known polyfunctional acrylate monomers.

[0020] Suitable polyfunctional acrylate monomers that can be employed in the present invention include, for example, pentaerythritol triacrylate, pentaerythritol tetraacrylate, dipentaerythritol tetraacrylate, dipentaerythritol pentaacrylate, dipentaerythritol hexaacrylate, tripentaerythritol acrylate, diglycerol EO modified acrylate (wherein EO means ethylene oxide), trimethylolpropane triacrylate, trimethylolpropane PO modified triacrylate (wherein PO means propylene oxide), trimethylolpropane EO modified triacrylate, alkoxylated pentaerythritol tetraacrylate, isocyanuric acid EO modified diacrylate, isocyanuric acid EO modified triacrylate, phenol EO modified acrylate, 2-ethylhexyl EO modified acrylate, N-acryloyloxyethyl hexahydrophthalimide, bisphenol F EO modified diacrylate, bisphenol A Examples of the monomer include, but are not limited to, EO-modified diacrylate, tripropylene glycol diacrylate, polyethylene glycol diacrylate, tris[2-hydroxyethyl]isocyanurate triacrylate, ethoxylated trimethylolpropane triacrylate, propoxylated trimethylolpropane triacrylate, propoxylated glyceryl triacrylate, and ditrimethylolpropane tetraacrylate.

[0021] In addition to the above-mentioned polyfunctional acrylate monomers, commercially available polyfunctional polyester acrylates include "M-7100", "M-7300", "M-8030", "M-8060", "M-8100", "M-8530", "M-8560", and "M-9050" sold by Toagosei Co., Ltd. Commercially available dendrimer-type hyperbranched acrylates include "Viscoat #1000LT" and "SIRIUS-501" sold by Osaka Organic Chemical Industry Co., Ltd.

[0022] Among the above-mentioned polyfunctional acrylate monomers, polyfunctional acrylate monomers having a pentaerythritol skeleton are particularly suitable as the polyfunctional acrylate used in the present invention. The polyfunctional acrylate having a pentaerythritol skeleton is excellent in scratch resistance due to increased curing speed and improved crosslinking density, and mechanical strength such as hard coat. Therefore, the surface layer formed of the composition having a UV-curable resin structure having a pentaerythritol skeleton realizes scratch resistance and mechanical strength that can withstand impacts caused by repeated writing and erasing.

[0023] (b2) Regarding multifunctional acrylate oligomers. The polyfunctional acrylate oligomer is a general term for compounds that have a higher molecular weight than the polyfunctional acrylate monomer and have two or more acrylic groups in multiple repeating units, and can be selected from various known polyfunctional acrylate oligomers. The polyfunctional acrylate oligomers are broadly classified into epoxy acrylates, urethane acrylates, and polyester acrylates according to the type of repeating unit. Among the polyfunctional acrylate oligomers, urethane acrylates are particularly suitable as the polyfunctional acrylates used in the present invention. Urethane acrylates are synthesized from polyols, diisocyanates, and acrylates having hydroxyl groups, and can be easily molecular designed by combining various known polyols. The urethane acrylates are excellent in toughness, hardness, chemical resistance, and adhesion. For this reason, the surface layer formed of the composition having the UV-curable resin structure containing the urethane bond has properties such as being moderately difficult for the solvents and dyes of oil-based ink to penetrate, thereby achieving a function of easily fixing the oil-based ink to the surface without being repelled when writing, and a function of easily erasing with an eraser. Furthermore, it has hardness and toughness that can withstand repeated writing and erasing, and appropriate adhesion to the substrate as a surface layer forming composition.

[0024] The urethane acrylate that can be adopted in the present invention is not particularly limited, but commercially available ones can be used appropriately. For example, "M-1100" (2-functional) and "M-1200" (2-functional) sold by Toagosei Co., Ltd., and "UN-3320HA" (6-functional), "UN-3320HC" (6-functional), "UN-906S" (6-functional), "UN-901T" (9-functional), "UN-952" (10-functional), "UN-904" (10-functional), "UN-905" (15-functional), and "UN-3320HS" (15-functional) sold by Negami Chemical Industry Co., Ltd. ), and "UV-1700B" (10 functional), "UV-6300B" (7 functional), "UV-7550B" (3 functional), "UV-7600B" (6 functional), "UV-7605B" (6 functional), "UV-7610B" (9 functional), "UV-7620EA" (9 functional), "UV-7630B" (6 functional), "UV-7640B" (6 to 7 functional), and "UV-7650" (4 to 5 functional) sold by Mitsubishi Chemical Corporation.

[0025] (C) Photopolymerization initiator. The photopolymerization initiator absorbs light energy mainly in the ultraviolet region of wavelength 250 to 400 nm to generate radicals, which attack the double bonds of the (B) polyfunctional acrylate to initiate polymerization. Regarding the type and amount of the photopolymerization initiator, any of those commonly used in the photopolymerization of photopolymerizable acrylic polymers can be widely used.

[0026] Examples of photopolymerization initiators that can be used in the present invention include alkylphenone photopolymerization initiators such as 2-hydroxy-2-methyl-1-phenylpropanone, 1-hydroxycyclohexyl-phenyl ketone, 2-hydroxy-1-(4-(4-(2-hydroxy-2-methylpropionyl)benzyl)phenyl)-2-methylpropan-1-one, 1-[4-(2-hydroxyethoxyl)-phenyl]-2-hydroxy-methylpropanone, 2-benzyl-2-(dimethylamino)-4'-morpholinobutyrophenone, 2-dimethylamino-2-(4-methyl-benzyl)-1-(4-morpholin-4-yl-phenyl)-butan-1-one, and 2-methyl-1-[4-(methylthio)phenyl]-2-morpholinopropan-1-one, and acetophenones such as 2,2-dimethoxy-2-phenylacetophenone. Photopolymerization initiators that can be used include acylphosphine oxide-based photopolymerization initiators such as bis(2,6-dimethoxybenzoyl)-2,4,4-trimethylpentylphosphine oxide, 2,4,6-trimethylbenzoyl-diphenylphosphine oxide, ethyl(2,4,6-trimethylbenzoyl)-phenylphosphineate, and bis(2,4,6-trimethylbenzoyl)phenylphosphine oxide, and benzophenone-based photopolymerization initiators such as benzophenone, 4-methylbenzophenone, 4-phenylbenzophenone, o-methylbenzoyl benzoate, 4-(4-methylphenylthio)benzophenone, 2-4-6 trimethylbenzophenone, 2,4-dimethylthioxanthone, 2-isopropylthioxanthone, and methylbenzoyl formate 4,4 bis(diethylamino)benzophenone.

[0027] (D) Additives for adjusting the physical properties of the composition, such as the surface tension. In the present invention, in addition to the material forming the curable acrylic resin, an additive for adjusting the physical properties such as the surface tension of the composition may be included as necessary. The additives that can be used in the present invention are not particularly limited, but commercially available ones can be used as appropriate. For example, the "BYK-UV" series sold by BYK Japan Co., Ltd. can be mentioned. Among them, "BYK-UV3500" (polyether-modified polydimethylsiloxane having an acrylic group) is particularly suitable as an additive used in the present invention. By adding the BYK-UV3500, it is expected that the surface tension will be reduced and a uniform and smooth surface layer will be obtained.

[0028] Regarding mixing of (b1) a multifunctional acrylate monomer and (b2) a multifunctional acrylate oligomer. As described above, the (b1) polyfunctional acrylate monomer plays a role in increasing the mechanical strength of the coating film, such as the solvent resistance and scratch resistance, and also functions as a reactive diluent. On the other hand, if the amount of the polyfunctional acrylate monomer added is too large, the polymerization shrinkage rate increases, which may cause a deterioration in flexibility and adhesion to the substrate. In contrast, (b2) polyfunctional acrylate oligomers, particularly urethane acrylates preferably used in the present invention, have impact resistance and flexibility specific to polyurethanes, but have high viscosity and therefore require a reactive diluent. Considering the characteristics of (b1) the multifunctional acrylate monomer and (b2) the multifunctional acrylate oligomer, by mixing them, it is possible to complement each other's improvements, and to maintain the stability of the coating film on the substrate for a long period of time while having mechanical strength that can withstand repeated writing and erasing.

[0029] Here, the basic layer structure of the panel having a surface layer according to the present invention will be described with reference to the accompanying drawings, in which: Fig. 1 is a cross-sectional view showing an example of the layer structure.

[0030] First, the facing material denoted by reference numeral 1 at least comprises a base layer 11 and a surface layer 12 laminated on the base layer 11. In a configuration in which the surface layer 12 is formed into a sheet and then laminated on the base layer 11, an adhesive layer (not shown) is interposed between the base layer 11 and the surface layer 12. The surface layer 12 may be formed directly on the base layer 11 by a coating or spraying method. The total number of layers in the layer structure is not particularly limited. In other words, a necessary layer may be interposed between the base layer 11 and the surface layer 12 according to the purpose.

[0031] The present invention will be described below based on experimental examples, but the present invention is not limited to these experimental examples. Each experimental example of the surface layer forming composition having the composition shown in Table 1 below was prepared by the following method.

[0032] (Experimental Example 1) A solvent, methyl ethyl ketone (manufactured by Sanyo Chemical Industries, Ltd.), was added to a polyfunctional acrylate component, pentaerythritol (tri / tetra)acrylate (PETRA, manufactured by Daicel Allnex Co., Ltd.), so that the solid content was 40% by mass, to obtain a blended liquid. A photopolymerization initiator (IRGACURE 184, manufactured by IGM Co., Ltd.) was added to the blended liquid in an amount of 5 parts by mass relative to 100 parts by mass of the pentaerythritol (tri / tetra)acrylate, to obtain a surface layer forming composition. The surface layer forming composition was then applied to a PET film (Lumirror S10, manufactured by Toray Industries, Inc., thickness 100 μm) using a No. 12 bar coder, and the oven was set to 90 ° C. and pre-dried for 90 seconds. The surface layer to be used for evaluation was obtained by ultraviolet curing using a metal halide lamp (manufactured by Eye Graphics Co., Ltd.) with an integrated irradiation dose of 500 mJ / cm2.

[0033] (Experimental Example 2) A composition for forming a surface layer and a surface layer were obtained in the same manner as in Experimental Example 1, except that dipentaerythritol hexaacrylate (DPHA, manufactured by Daicel Allnex) was used as the multifunctional acrylate component and the photopolymerization initiator (IRGACURE 184, manufactured by IGM) was added in an amount of 3 parts by mass per 100 parts by mass of the dipentaerythritol acrylate.

[0034] (Experimental Example 3) A composition for forming a surface layer and a surface layer were obtained in the same manner as in Experimental Example 1, except that a 10-functional urethane acrylate (UV-1700B, manufactured by Mitsubishi Chemical Corporation) was used as the multifunctional acrylate component and the photopolymerization initiator (IRGACURE 184, manufactured by IGM) was added in an amount of 3 parts by mass per 100 parts by mass of the 10-functional urethane acrylate.

[0035] (Experimental Example 4) A composition for forming a surface layer and a surface layer were obtained in the same manner as in Experimental Example 1, except that a hexafunctional urethane acrylate 1 (UV-7600B, manufactured by Mitsubishi Chemical Corporation) was used as the multifunctional acrylate component, and the photopolymerization initiator (IRGACURE, manufactured by IGM Corporation) was added in an amount of 3 parts by mass per 100 parts by mass of the hexafunctional urethane acrylate.

[0036] (Experimental Example 5) A surface layer-forming composition and a surface layer were obtained in the same manner as in Experimental Example 1, except that a hexafunctional urethane acrylate 1 (UV-7600B, manufactured by Mitsubishi Chemical Corporation) was used as the multifunctional acrylate component, the photopolymerization initiator (IRGACURE 184, manufactured by IGM) was added in an amount of 3 parts by mass per 100 parts by mass of the hexafunctional urethane acrylate, and further, a polyether-modified polydimethylsiloxane having an acrylic group (BYK-UV3500, manufactured by BYK Japan) was added as an additive in an amount of 1 part by mass per 100 parts by mass of the hexafunctional urethane acrylate.

[0037] (Experimental Example 6) A composition for forming a surface layer and a surface layer were obtained in the same manner as in Experimental Example 1, except that a hexafunctional urethane acrylate 2 (UN-3320HA, manufactured by Negami Chemical Industries, Ltd.) was used as the multifunctional acrylate component, and the photopolymerization initiator (IRGACURE 184, manufactured by IGM Co., Ltd.) was added in an amount of 3 parts by mass per 100 parts by mass of the hexafunctional urethane acrylate.

[0038] (Experimental Example 7) A surface layer forming composition and a surface layer were obtained in the same manner as in Experimental Example 1, except that hexafunctional urethane acrylate 2 (UN-3320HA, manufactured by Negami Chemical Industries, Ltd.) and silicon-containing hexafunctional urethane acrylate (UN-906S, manufactured by Negami Chemical Industries, Ltd.) were mixed as the multifunctional acrylate component, and the photopolymerization initiator (IRGACURE 184, manufactured by IGM Co., Ltd.) was added in an amount of 3 parts by mass relative to 100 parts by mass of the mixture of the hexafunctional urethane acrylate and the silicon-containing hexafunctional urethane acrylate. Note that 99 parts by mass of the mixture of the hexafunctional urethane acrylate and the silicon-containing hexafunctional urethane acrylate and the silicon-containing hexafunctional urethane acrylate account for 1 part by mass of the mixture.

[0039] (Experimental Example 8) A surface layer-forming composition and a surface layer were obtained in the same manner as in Experimental Example 1, except that pentaerythritol (tri / tetra)acrylate 1 (PETRA, manufactured by Daicel Allnex Co., Ltd.) similar to that in Experimental Example 1 and hexafunctional urethane acrylate 2 similar to that in Experimental Example 6 were mixed as polyfunctional acrylate components, and the photopolymerization initiator (IRGACURE 184, manufactured by IGM Co., Ltd.) was added in an amount of 3 parts by mass relative to 100 parts by mass of the mixture of the pentaerythritol (tri / tetra)acrylate and the hexafunctional urethane acrylate. Note that 25 parts by mass of the mixture of the pentaerythritol (tri / tetra)acrylate and the hexafunctional urethane acrylate accounts for the pentaerythritol (tri / tetra)acrylate, and 75 parts by mass of the mixture of the pentaerythritol (tri / tetra)acrylate and the hexafunctional urethane acrylate accounts for 100 parts by mass.

[0040] (Experimental Example 9) A composition for forming a surface layer and a surface layer were obtained in the same manner as in Experimental Example 8, except that out of 100 parts by mass of the mixture of the pentaerythritol (tri / tetra)acrylate 1 and the hexafunctional urethane acrylate 2, the pentaerythritol (tri / tetra)acrylate 2 and the hexafunctional urethane acrylate 2 each accounted for 50 parts by mass.

[0041] (Experimental Example 10) A composition for forming a surface layer and a surface layer were obtained in the same manner as in Experimental Example 8, except that 75 parts by mass of the 100 parts by mass of the mixture of the pentaerythritol (tri / tetra)acrylate 1 and the hexafunctional urethane acrylate 2 was accounted for by the pentaerythritol (tri / tetra)acrylate 1, and 25 parts by mass of the 100 parts by mass of the mixture was accounted for by the hexafunctional urethane acrylate 2.

[0042] (Experimental Example 11) A composition for forming a surface layer and a surface layer were obtained in the same manner as in Experimental Example 1, except that trimethylolpropane triacrylate (TMPTA, manufactured by Daicel Allnex Corporation) was used as the multifunctional acrylate component and the photopolymerization initiator (IRGACURE 184, manufactured by IGM Corporation) was added in an amount of 3 parts by mass per 100 parts by mass of the trimethylolpropane triacrylate.

[0043] (Experimental Example 12) A surface layer-forming composition and a surface layer were obtained in the same manner as in Experimental Example 1, except that a monofunctional acrylate, dicyclopentenyloxyethyl acrylate (FA-512AS, manufactured by Showa Denko Materials Co., Ltd.), was used, and the photopolymerization initiator (IRGACURE 184, manufactured by IGM Co., Ltd.) was added in an amount of 3 parts by mass per 100 parts by mass of the dicyclopentenyloxyethyl acrylate.

[0044] Regarding evaluation. The surface layer obtained from the surface layer-forming composition prepared by the above method was evaluated for (1) the writability of oil-based marker, (2) the erasability of the oil-based marker writing, and (3) the scratch resistance of each blended composition by the following methods. The results of each evaluation are shown in Table 1 below together with the respective compositions.

[0045] (1) Writability with oil-based markers The composition of each experimental example was applied to a PET film (Toray Mirror S10, 100 μm thick) using a No. 10 bar coder, and then heated in an oven at 150° C. for 10 minutes. After 24 hours, the film was written on with a permanent marker and the handwriting was visually evaluated. The permanent marker used in this experiment was Zebra's Mackie (registered trademark).

[0046] The writability was evaluated on a three-level scale according to the following criteria: ◎ (Good); I was able to write with oil-based ink without it repelling. ○ (passed): Less than 5% of the oil-based ink was repelled. × (Failed): More than 5% of the oil-based ink was repelled, or writing was not possible.

[0047] (2) Ability to erase oil-based marker marks The composition obtained in each experimental example was applied to a PET film (Toray Mirror S10, 100 μm thick) using a No. 10 bar coder, and then heated in an oven at 150°C for 10 minutes. After 24 hours, the film was written on with an oil-based marker, and after another 24 hours, the film was rubbed with a plastic eraser under specified conditions, and the handwriting was visually evaluated. The rub conditions were distance: 10 cm, speed: 10 round trips / 6 seconds, and load: 800 g.

[0048] The erasability was evaluated on a three-level scale according to the following criteria: ◎ (Good): Erased with less pressure and fewer reciprocations than the test conditions. 〇(Pass); Erased successfully. × (failed); Handwriting that cannot be erased remains.

[0049] (3) Scratch resistance The composition obtained in each experimental example was applied to a PET film (Toray Mirror S10, thickness 100 μm) using a No. 10 barcoder, and then heated in an oven at 150°C for 10 minutes. After 24 hours, steel wool #0000 (Bonstar, manufactured by Nippon Steel Wool Co., Ltd.) was placed on the surface layer and scratched under specified conditions to confirm surface scratches. Scratching conditions were distance: 5 cm, speed: 10 round trips / 7 seconds, and load: 1 kg.

[0050] The scratch resistance was evaluated on a two-level scale according to the following criteria: ○(pass); no scratches × (failed); damaged

[0051] Table 1 shows the composition ratios of the experimental examples of the present invention and the evaluation results of each experimental example.

[0052] [Table 1]

[0053] (Discussion of the experimental example) As shown in Table 1 above, all of the compositions for forming a surface layer in Experimental Examples 1 to 11 were judged to pass or above (◯ or ◎ symbol) in the evaluation items of (1) writability with oil-based marker and (2) erasability of handwriting with oil-based marker. That is, all of the compositions for forming a surface layer in Experimental Examples 1 to 11 were excellent in both writability with oil-based marker and erasability with an eraser. Furthermore, Experimental Examples 1 to 10 were also excellent in (3) scratch resistance with steel wool.

[0054] On the other hand, the surface layer-forming composition of Experimental Example 12 failed both (2) the erasability of oil-based marker writing and (3) the scratch resistance. That is, the surface layer-forming compositions of Experimental Examples 1 to 11 were all superior to the surface layer-forming composition of Experimental Example 12 in terms of both the writability and erasability of oil-based ink.

[0055] From the results of Experimental Examples 1 and 2 (using a multifunctional acrylate monomer) and Experimental Examples 3, 4, and 6 (using urethane acrylate as the multifunctional acrylate oligomer), it was found that the multifunctional acrylate, whether a multifunctional acrylate monomer or a multifunctional acrylate oligomer, is superior in terms of writability with oil-based ink and erasability with an eraser.

[0056] Experimental Examples 1 and 2 are experimental examples in which a polyfunctional acrylate monomer having a pentaerythritol skeleton is used as the polyfunctional acrylate. The polyfunctional acrylate monomer "PETRA" used in Experimental Example 1 is a polyfunctional acrylate monomer containing pentaerythritol triacrylate having three acryloyl groups and one hydroxyl group, and pentaerythritol tetraacrylate having four acryloyl groups. On the other hand, the polyfunctional acrylate monomer "DPHA" used in Experimental Example 2 is dipentaerythritol hexaacrylate having six acryloyl groups. Both have high hardness and excellent curability and scratch resistance, but "PETRA" differs in that it contains pentaerythritol triacrylate having a hydroxyl group. In contrast, in the results shown in Table 1, both Experimental Examples 1 and 2 were acceptable or better, but Experimental Example 2 was superior in (2) the ability to erase oil-based marker writing. Therefore, it has been found that polyfunctional monomers containing pentaerythritol are useful as the polyfunctional acrylate used in the present invention, and those having a lower acid value are particularly useful.

[0057] Experimental Examples 3, 4, and 6 are experimental examples in which urethane acrylate, which is a multifunctional acrylate oligomer, was used as the multifunctional acrylate. Experimental Examples 3 and 4 are 10-functional and 6-functional urethane acrylates, respectively. Both have high hardness, but Experimental Example 3 has a higher hardness, while Experimental Example 4 is characterized by excellent adhesion to various plastics. Furthermore, since Experimental Example 6 was also a hexafunctional urethane acrylate, it was demonstrated by experiment that urethane acrylates are useful as polyfunctional acrylates for use in the present invention, and further that urethane acrylates having a functionality of at least 6 and no more than 10 are useful.

[0058] Experimental Example 5 is an experimental example in which a hexafunctional urethane acrylate is used as the multifunctional acrylate, and polyether-modified polydimethylsiloxane having an acrylic group is further added as an additive. From the results in Table 1, it is considered that the surface layer forming composition of the present invention can use, in addition to the multifunctional monomer and photoinitiator that form the resin composition, an additive that adjusts the physical properties of the composition, such as polyether-modified polydimethylsiloxane having an acrylic group, if necessary.

[0059] In addition, the results of Experimental Examples 1 and 8 to 10 show that it is possible to mix a polyfunctional acrylate monomer containing a pentaerythritol skeleton with a polyfunctional acrylate oligomer having a urethane acrylate structure as needed. In particular, in Experimental Example 1, the evaluation of (2) the erasability of oil-based marker writing was improved by mixing it with a hexafunctional urethane acrylate rather than using only pentaerythritol (tri / tetra)acrylate as the polyfunctional acrylate, and therefore it is considered useful to mix multiple types of polyfunctional acrylates as needed.

[0060] In Experimental Example 11 (using a trifunctional acrylate monomer), the writability and erasability of the oil-based marker, which are the object of the present invention, were both passed or better (◯ or ◎ symbol). This shows that a multifunctional acrylate monomer having three or more functionalities is useful as the acrylate monomer.

[0061] In Experimental Example 12 (using a monofunctional acrylate monomer), both the erasability of oil-based marker writing and the scratch resistance were unsatisfactory, which indicates that the acrylate monomer that can be used in the present invention must be a polyfunctional acrylate monomer.

[0062] The results of Experimental Examples 1, 2, 11, and 12 suggest that when a polyfunctional acrylate monomer having a pentaerythritol skeleton is selected as the polyfunctional acrylate component, it is favorable when the number of functional groups is at least 3 to 6.

[0063] As described above, the results of Experimental Examples 3, 4, and 6 suggest that when a urethane acrylate is selected as the multifunctional acrylate component, it is preferable if the number of functional groups is at least 6 to 10, but this is merely suggested by the experimental results, and the number of functional groups is not limited to this range. Although not particularly shown in the experimental examples, it has been found that the object of the present invention can be achieved even with a urethane acrylate oligomer having 15 functional groups.

[0064] Moreover, the evaluation of (3) scratch resistance was passed for all of Experimental Examples 1 to 11. This result suggests that when a polyfunctional acrylate having at least 6 or more functional groups is used in the present invention, not only the writability and erasability of oil-based marker, which is the main object of the present invention, but also the mechanical strength sufficient to withstand repeated writing and erasing is provided. [Explanation of symbols]

[0065] 1. Surface material 11 Base material layer 12 Surface layer

Claims

1. A multifunctional acrylate capable of forming a crosslinked structure upon irradiation with ultraviolet light; At least a photopolymerization initiator is included, The polyfunctional acrylate is Pentaerythritol triacrylate, pentaerythritol tetraacrylate and It is a hexafunctional urethane acrylate, A composition for forming a surface layer, which is written with an oil-based ink having a composition containing at least an organic solvent, a resin and a dye, and the written trace is erased with a plastic eraser, and this writing and erasing process is repeated.

2. A surface layer formed by the composition for forming a surface layer described in claim 1, which is written with an oil-based ink having a composition containing at least an organic solvent, a resin and a dye, and the written handwriting is erased with a plastic eraser, and this writing and erasing process is repeated.

3. 3. A surface material for oil-based ink writing, comprising at least the surface layer described in claim 2, which is written on with oil-based ink having a composition containing at least an organic solvent, a resin and a dye, and the written traces are erased with a plastic eraser, and this writing and erasing process is repeated.

4. An article comprising at least the oil-based ink writing surface material according to claim 3 .