Method for estimating surface tension of coal and method for producing coke

Abstract

Provided is a method for easily estimating the surface tension of coal. A method for estimating a surface tension of coal includes: subjecting a surface tension, a physical property value representing a coal rank, and a total inert content of each of different brands of coal to multiple regression analysis to determine in advance a regression equation including the surface tension of coal as an objective variable and the physical property value and the total inert content as explanatory variables; and measuring the physical property value and the total inert content of a coal of which the surface tension is to be estimated, and calculating the surface tension of the coal by using the measured physical property value and the measured total inert content, and the regression equation.

Description

DESCRIPTION Title of Invention: METHOD FOR ESTIMATING SURFACE TENSION OF COAL AND METHOD FOR PRODUCING COKE Technical Field

[0001] The present invention relates to a method for estimating the surface tension of coal and a method for producing coke. Background Art

[0002] Coke used as a blast furnace raw material for pig-iron production in blast furnaces preferably has high strength. This is because coke having low strength degrades in blast furnaces to inhibit gas permeability in blast furnaces, which hinders stable production of pig iron.

[0003] Coke is produced by carbonizing coal. Carbonization is a process for heating coal at a pyrolysis temperature or higher (about 300°C or higher) in a non-oxidizing atmosphere. Coal that softens and melts at 350°C to 600°C in a carbonization process is preferably used as a raw material of coke. When softening and melting, coal powder or particles adhere to and fuse with each other to form lump coke.

[0004] To produce coke having high strength, coal particles preferably adhere well to each other. The surface tension of heat-treated coal (semicoke) is used as a physical property value for evaluating the adhesiveness of the coal.

[0005] Examples of the method for measuring the surface tension of coal include a capillary-rise method, a maximum bubble pressure method, a drop weight method, a pendant drop method, a ring method, a Wilhelmy method, an advancing / receding contact angle method, a tilting plate method, and a film flotation method. Since coal is composed of various molecular structures and thus expected to have uneven surface tension, the film flotation method in Non- Patent Literature 1 or Patent Literature 1 expected to evaluate the surface tension distribution is said to be the most reasonable measurement method.

[00006] The film flotation method is a technique based on the idea that pulverized sample particles placed in liquid and starting to sink from floating state have the same surface tension as the liquid have. Sample particles are dropped into liquids having various surface tensions, and the mass ratio of sample particles that float in each liquid is determined. The surface tension distribution is obtained from the result. The film flotation method can measure the surface tension of any coal, regardless of the type of coal, such as hard coking coal, non- or slightly caking coal, anthracite, and heat-treated coal (semicoke) made by treating such coal with heat. Citation List Patent Literature

[0007] Patent Literature 1: Japanese Patent No. 5737473 Non Patent Literature

[0008] Non Patent Literature 1: D. W. Fuerstenau: International Journal of Mineral Processing, 20 (1987), 153 Summary of Invention Technical Problem

[0009] The film flotation method has a problem of taking a long time (about one day) to measure the surface tension of coal and is not effective in terms of time. The film flotation method also has a problem of a complicated process for measuring the surface tension, and only skilled measurers can stably measure the surface tension. The present invention solves these problems that occur in measuring the surface tension of coal and provides a method for easily estimating the surface tension of coal. Solution to Problem

[0010] The solutions to the above problems are as described below. (1) A method for producing coke, the method comprising: estimating the surface tensions of a plurality of coals, each of a different brand of coal by subjecting a surface tension, a physical property value representing a coal rank, and a total inert content measured according to JIS M 8816 and according to the following formula (1): Inert content in vol% = fusinite in vol% + micrinite in vol% + (2 / 3) x semifusinite in vol% + mineral matter in vol% ...(1) of each of the different brands of coal or semicoke derived from said coal to multiple regression analysis to determine in advance a regression equation including the surface tension of coal as an objective variable and the physical property value and the total inert content as explanatory variables; and measuring the physical property value and the total inert content of a coal of which the surface tension is to be estimated, and calculating the surface tension of the coal by using the measured physical property value and the measured total inert content, and the regression equation, wherein said semicoke is made by heating coal from each said brand of coal to a temperature of 350oC or higher and 8000 C or lower, wherein the physical property value representing a coal rank is the mean maximum vitrinite reflectance measured according to JIS M 8816, the volatile matter of coal, the carbon content, or the re—solidification temperature in softening and melting, and blending coals having similar surface tensions estimated by said method for estimating a surface tension of coal to from a coal blend; and carbonizing the coal blend to produce coke. (2) The method for producing coke according to (1), wherein the physical property value is a mean maximum vitrinite reflectance of the coal measured according to JIS M 8816. (3) The method for producing coke according to (1) or (2), wherein the surface tension is a surface tension of a semicoke made by heating coal to a temperature of 480°C or higher and 520°C or lower. Advantageous Effects of Invention

[0011] The surface tension of coal can easily be estimated by carrying out the method for estimating a surface tension of coal according to the present invention. When the surface tension of coal can easily be estimated in this way, the estimated value of the surface tension can be used to investigate blending of coals, which enables production of coke with high quality. Brief Description of Drawings

[0012] [Fig. 1] Fig. 1 is a graph showing plots (3 points) of the surface tension of samples having different inert contents and the regression line of the plots for each of samples having different inert contents in 6 brands (A to F) of coal. [Fig. 2] Fig. 2 is a graph showing the relationship between the measured surface tensions and the estimated surface tensions of coals G to M. [Fig. 3] Fig. 3 is a graph showing plots (3 points) of the surface tension of samples having different inert contents and the regression line of the plots for each of 3 brands (N, O, P) of coal with a heat treatment temperature [Image disponible dans le document PDF, Image available in the PDF document] [Fig. 4] Fig. 4 is a graph showing plots (3 points) of the surface tension of samples having different inert contents and the regression line of the plots for each of 3 brands (N, O, P) of coal with a heat treatment temperature [Image disponible dans le document PDF, Image available in the PDF document] Description of Embodiments

[0013] The present invention will be described below through embodiments of the present invention. The inventors of the present invention focus on coal components that soften and melt with heat (hereinafter referred as reactives) and coal components that neither soften nor melt with heat (hereinafter referred to as inerts). First, the relationship between the surface tensions of the reactives and the inerts and the surface tension of coal will be described.

[0014] Since coal inerts are harder than reactives, the inerts tend to concentrate in coarse particles of coal after pulverizing. This tendency is used to prepare samples having different inert contents from the same brand of coal by pulverizing and sifting. The total inert content (hereinafter may be referred to as TI) of each of the samples having different inert contents prepared in this way is measured, and the samples are each treated with heat at a predetermined temperature to form semicokes. The TI is the total inert content defined in JIS M 8816 and indicates the proportion (vol%) of inerts contained in coal.

[0015] In this embodiment, the coal of which the surface tension is to be estimated includes heat-treated coal, that is, semicoke. The method for estimating the surface tension of coal according to this embodiment can be applied to coal without a heat treatment as well as semicoke. Since the surface tension of semicoke is particularly useful for predicting coke strength and producing coke with high strength, the method for measuring the surface tension of semicoke, which is heat-treated coal, will be described in this embodiment. In this embodiment, the semicoke is produced in the following (a) to (c). (a) Pulverizing coal. With regard to the size of particles of pulverized coal, the coal is preferably pulverized to a particle size of 250 <semantics>μm<annotation encoding="application / x-tex">\mu m< / annotation>< / semantics> or less, more preferably pulverized to 200 µm or less, which is the size of particles in proximate analysis of coal described in JIS M8812, in order to prepare uniform samples from coal which is not uniform in macerals and properties. (b) Heating the pulverized coal to a temperature of 350°C or higher and 800°C or lower at an appropriate heating rate with no air or in an inert gas. The heating rate is preferably set according to the heating rate during production of coke in a coke oven. (c) Cooling the heated coal in an inert gas to produce semicoke.

[0016] With regard to the heating temperature for heating the coal, the coal is preferably heated to a temperature between 350°C at which the coal starts to soften and melt and 800°C at which coking is complete, based on the idea that the surface tension has an effect on adhesion between coal particles. However, in a range of heating temperatures of 350°C to 800°C, the temperature that particularly contributes to adhesion is 350°C to 550°C which is a temperature of softening and melting, and the adhesion structure may be set around 500°C. For this, the heating temperature is particularly preferably 480°C to 520°C, which is around 500°C, and the heating temperature is set to 500°C in this embodiment. Heating is preferably performed in an inert gas (e.g., nitrogen, argon, helium) atmosphere, which is unreactive with coal.

[0017] Cooling is preferably performed in an inert gas atmosphere, which is unreactive with coal. The heat-treated coal is preferably quenched at a cooling rate of 10 °C / sec or more. The reason for quenching is to maintain a molecular structure in the reactive state, and the cooling rate is preferably 10 °C / sec or higher at which the molecular structure may not change. Quenching may be performed by using liquid nitrogen, iced water, water, or an inert gas, such as a nitrogen gas. Quenching is preferably performed by using liquid nitrogen.

[0018] The surface tension of the coal can be measured by using the film flotation method described in Non Patent Literature 1. This method can be used for both coal and semicoke made from the coal, and the surface tension distribution can be obtained by using a finely pulverized sample. The mean of the obtained surface tension distribution is defined as a representative value of the surface tension of the sample. The measurement of the surface tension of semicoke using the film flotation method is specifically described in Patent Literature 1.

[0019] Fig. 1 is a graph showing plots (3 points) of the surface tension (mean of surface tension distribution) of samples having different inert contents and the regression line of the plots for each of 6 brands (A to F) of coal treated with heat at 500°C (semicokes). In Fig. 1, the horizontal axis represents TI (%), and the vertical axis represents the surface tension (mN / m). Each regression line is a simple regression equation of the surface tension against TI and calculated by using the least squares method so as to minimize the error between the simple regression equation and each plot. As shown in Fig. 1, an approximately linear relationship is observed between TI and surface tension for each brand of coal. A value corresponding to <semantics>TI=100<annotation encoding="application / x-tex">TI = 100< / annotation>< / semantics> on the regression line is an estimated value of the surface tension at 100% inerts (hereinafter may be referred to as <semantics>γ100<annotation encoding="application / x-tex">\gamma_{100}< / annotation>< / semantics>), and a value corresponding to <semantics>TI=0<annotation encoding="application / x-tex">TI = 0< / annotation>< / semantics> is an estimated value of the surface tension at 100% reactives (hereinafter may be referred to as γο).

[0020] Fig. 1 shows that <semantics>γ0<annotation encoding="application / x-tex">\gamma_0< / annotation>< / semantics> has a tendency of convergence to a substantially constant value, regardless of the brand of coal, and <semantics>γ100<annotation encoding="application / x-tex">\gamma_{100}< / annotation>< / semantics> does not have a tendency of convergence and greatly varies according to the brand of coal. Since a linear relationship is observed between surface tension and TI, and <semantics>γ100<annotation encoding="application / x-tex">\gamma_{100}< / annotation>< / semantics> greatly varies according to the brand of coal, the TI and <semantics>γ100<annotation encoding="application / x-tex">\gamma_{100}< / annotation>< / semantics> are considered as dominant factors that have an effect on the surface tension of coal.

[0021] The inventors of the present invention have studied the relationship between <semantics>γ100<annotation encoding="application / x-tex">\gamma_{100}< / annotation>< / semantics> and coal properties and have found that <semantics>γ100<annotation encoding="application / x-tex">\gamma_{100}< / annotation>< / semantics> shows a strong correlation with the mean maximum vitrinite reflectance (hereinafter may be referred to as Ro) of coal. With TI and Ro as main dominant factors that have an effect on the surface tension of coal, it is determined whether the surface tension of coal can be estimated from the measured values of TI and <semantics>R0<annotation encoding="application / x-tex">R_0< / annotation>< / semantics>. Table 1 shows the properties of the coals G to M, which are used in the determination. Ro is an example physical property value representing a coal rank. Examples of physical property values representing coal ranks other than Ro include the volatile matter of coal, the carbon content, and the re- solidification temperature in softening and melting. These physical property values all show a good correlation with Ro. Thus, the volatile matter of coal, the carbon content, or the re-solidification temperature in softening and melting can thus be used as a dominant factor that has an effect on the surface tension, instead of <semantics>R0<annotation encoding="application / x-tex">R_0< / annotation>< / semantics>. These physical property values can be used as an explanatory variable in multiple regression analysis described below.

[0022] [Table 1] [Image disponible dans le document PDF, Image available in the PDF document]

[0023] In Table 1, "logMF (log / ddpm)" is a common logarithmic value of the maximum fluidity (MF / ddpm) of coals measured by the Gieseler plastometer method described in JIS M8801. "Ro (%)" is a mean maximum vitrinite reflectance of coals G to M in JIS M 8816. "TI (%)" is a total inert content (vol%) and calculated in accordance with Methods of microscopical measurement for the macerals for coal and coal blend in JIS M 8816 and the following formula (1) based on the Parr formula described in explanation of the Methods.

[0024] [Image disponible dans le document PDF, Image available in the PDF document] <semantics>(vol%)+(2 / 3)×semifusinite(vol%)+mineralmatter(vol%)<annotation encoding="application / x-tex">(vol\%) + (2 / 3) \times semifusinite (vol\%) + mineral matter (vol\%)< / annotation>< / semantics> <semantics>⋯<annotation encoding="application / x-tex">\cdots< / annotation>< / semantics> (1) The "measured surface tension (mN / m)" is a surface tension (representative value) obtained by measuring semicokes made by treating coals G to M with heat at 500°C in accordance with the film flotation method. The "estimated surface tension (mN / m)" is an estimated surface tension calculated by using the measured values of <semantics>R0<annotation encoding="application / x-tex">R_0< / annotation>< / semantics> and <semantics>TI<annotation encoding="application / x-tex">TI< / annotation>< / semantics> and the regression equation including the surface tension <semantics>(Y)<annotation encoding="application / x-tex">(Y)< / annotation>< / semantics> as an objective variable and <semantics>R0<annotation encoding="application / x-tex">R_0< / annotation>< / semantics> and <semantics>TI<annotation encoding="application / x-tex">TI< / annotation>< / semantics> as explanatory variables <semantics>(X1,X2)<annotation encoding="application / x-tex">(X_1, X_2)< / annotation>< / semantics>.

[0025] The coals in Table 1 are examples of coal commonly used as a coke raw material. Coal used as a coke raw material has an MF of 0 to <semantics>60000<annotation encoding="application / x-tex">60000< / annotation>< / semantics> ddpm (log MF: 4.8 or less), a <semantics>R0<annotation encoding="application / x-tex">R_0< / annotation>< / semantics> of 0.6% to 1.8%, and a TI of 3 to 50 vol%. The method for estimating the surface tension of coal according to this embodiment can be suitably used for coals in such ranges.

[0026] The regression equation including the surface tension as an objective variable and Ro and TI as explanatory variables can be represented by the following formula (2).

[0027] Surface tension = <semantics>a+b1×R0+b2×TI⋯<annotation encoding="application / x-tex">a + b_1 \times R_0 + b_2 \times TI \cdots< / annotation>< / semantics> (2) In the formula <semantics>(2)<annotation encoding="application / x-tex">(2)< / annotation>< / semantics>, a, <semantics>b1<annotation encoding="application / x-tex">b_1< / annotation>< / semantics>, and <semantics>b2<annotation encoding="application / x-tex">b_2< / annotation>< / semantics> are parameters of the regression equation.

[0028] In this embodiment, the measured surface tensions and the measured values of Ro and TI of different brands of coals G to L are subjected to multiple regression analysis to calculate the parameters of the formula (2) and thus to obtain the following regression equation (3).

[0029] Estimated surface tension = <semantics>42.805−3.123R0+0.0614TI<annotation encoding="application / x-tex">42.805 - 3.123R_0 + 0.0614TI< / annotation>< / semantics> <semantics>⋯<annotation encoding="application / x-tex">\cdots< / annotation>< / semantics> (3) In Table 1, the "estimated surface tension (mN / m)" is an estimated surface tension calculated by using the regression equation (3). Coal M is not used to calculate the parameters of the regression equation (3), but the estimated surface tension of coal M calculated by using the regression equation (3) is substantially the same as the measured surface tension of coal M.

[0030] Fig. 2 is a graph showing the relationship between the measured surface tensions and the estimated surface tensions of coals G to M. In Fig. 2, the horizontal axis represents the measured surface tension <semantics>(mN / m)<annotation encoding="application / x-tex">(mN / m)< / annotation>< / semantics>, and the vertical axis represents the estimated surface tension <semantics>(mN / m)<annotation encoding="application / x-tex">(mN / m)< / annotation>< / semantics>. In Fig. 2, the solid circle plots represent coals G to L in Table 1, and the solid square plots represent coal M in Table 1. Fig. 2 indicates a very strong correlation between the measured surface tensions and the estimated surface tensions. This result demonstrates that the surface tension of coal can be accurately estimated by using the method for estimating the surface tension of coal according to this embodiment.

[0031] Fig. 2 shows an example of estimating the surface tension of coals treated with heat at 500°C, but the heat treatment temperature of coals in this embodiment is not limited to 500°C. To confirm that the method for estimating the surface tension of coal according to this embodiment is not limited to the case of heat treatment at 500°C, it is determined whether the relationship between TI and surface tension shown in Fig. 1 is also established at other heat treatment temperatures.

[0032] Samples having different TI contents are prepared by the above method using 3 brands (N, O, P) of coal. The samples are converted into semicokes according to the method including (a) to (c) described above under the same conditions except that only the heat treatment temperature is changed to 400°C and 600°C. The surface tension of each semicoke is measured, and the relationship between TI and surface tension is determined in the same manner as in Fig. 1.

[0033] Fig. 3 is a graph showing plots (3 points) of the surface tension of samples having different inert contents and the regression line of the plots for each of 3 brands (N, O, P) of coal with a heat treatment temperature of 400°C. Fig. 4 is a graph showing plots (3 points) of the surface tension of samples having different inert contents and the regression line of the plots for each of 3 brands (N, O, P) of coal with a heat treatment temperature of 600°C. In Fig. 3 and Fig. 4, the horizontal axis represents TI (%), and the vertical axis represents the surface tension <semantics>(mN / m)<annotation encoding="application / x-tex">(mN / m)< / annotation>< / semantics>.

[0034] As shown in Fig. 3 and Fig. 4, a relationship similar to that in Fig. 1 is established between the TI and the surface tension of semicokes prepared at different heat treatment temperatures, and this tendency does not change for the same coal. Since a relationship similar to that in Fig. 1 is established between the TI and the surface tension even when the heat treatment temperature is changed, the method for estimating the surface tension of coal according to this embodiment can be used for semicokes prepared at different temperatures.

[0035] Patent Literature 1 also discloses that the surface tensions of semicokes prepared at heat treatment temperatures of 350°C or higher and 800°C or lower show the same tendency regardless of the type of coal. This indicates that the method for estimating the surface tension of coal according to this embodiment can be used for semicokes prepared at a temperature of 350°C or higher and 800°C or lower as well as semicokes made by a heat treatment at 500°C. In other words, estimation of the surface tension of a coal treated with heat at a predetermined temperature of 350°C or higher and 800°C or lower can be done by using the regression equation obtained by multiple regression analysis using the data of surface tensions obtained by treating coals at the predetermined temperature.

[0036] In general, coal maceral analysis regarding TI, physical property values representing coal ranks, such as Ro, and other parameters are widely used in business transactions for the purpose of expressing the characteristics of coal, and these parameters are analyzed and available. Therefore, as long as the surface tension of a coal can be estimated from the coal rank and the TI of the coal, the surface tension of the coal can be estimated without relying on skilled measurers, and the time for measuring the surface tension can be saved.

[0037] When the regression equation (3) is determined in advance, the measurement of Ro and TI of a coal of which the surface tension is to be estimated allows estimation of the surface tension of the coal. The surface tension of the coal can thus be estimated accurately, easily, and readily by carrying out the method for estimating the surface tension of coal according to this embodiment. The strength of a coke made from a coal blend containing a mixture of coals with different surface tensions is lower than that of a coke made from a coal blend containing a mixture of coals with similar surface tensions. If the surface tension of coal can be estimated in this way, the estimated value of the surface tension can be used to investigate blending of coals. The use of a coal blend having the blending ratio set by the blending investigation to produce coke thus enables production of coke with high quality.

Claims

<pat:Claims com:id="claims"> <pat:Claim com:id="CLM-00001"> <pat:ClaimNumber>1< / pat:ClaimNumber> <pat:ClaimText>1. A method for producing coke, the method comprising: estimating the surface tensions of a plurality of coals, each of a different brand of coal by subjecting a surface tension, a physical property value representing a coal rank, and a total inert content measured according to JIS M 8816 and according to the following formula (1): Inert content in vol% = fusinite in vol% + micrinite in vol% + <semantics>(2 / 3)<annotation encoding="application / x-tex">(2 / 3)< / annotation>< / semantics> x semifusinite in vol% + mineral matter in vol% ...( 1) of each of the different brands of coal or semicoke derived from said coal to multiple regression analysis to determine in advance a regression equation including the surface tension of coal as an objective variable and the physical property value and the total inert content as explanatory variables; and measuring the physical property value and the total inert content of a coal of which the surface tension is to be estimated, and calculating the surface tension of the coal by using the measured physical property value and the measured total inert content, and the regression equation, wherein said semicoke is made by heating coal from each said brand of coal to a temperature of 350°C or higher and <semantics>800∘<annotation encoding="application / x-tex">800^{\circ}< / annotation>< / semantics> C or lower, wherein the physical property value representing a coal rank is the mean maximum vitrinite reflectance measured according to JIS M 8816, the volatile matter of coal, the carbon content, or the re-solidification temperature in softening and melting, and blending coals having similar surface tensions estimated by said method for estimating a surface tension of coal to from a coal blend; and carbonizing the coal blend to produce coke. < / pat:ClaimText> < / pat:Claim> <pat:Claim com:id="CLM-00002"> <pat:ClaimNumber>2< / pat:ClaimNumber> <pat:ClaimText>2. The method for producing coke according to Claim 1, wherein the physical property value is a mean maximum vitrinite reflectance of the coal measured according to JIS M 8816. < / pat:ClaimText> < / pat:Claim> <pat:Claim com:id="CLM-00003"> <pat:ClaimNumber>3< / pat:ClaimNumber> <pat:ClaimText>3. The method for producing coke according to Claim 1 or 2, wherein the surface tension is a surface tension of a semicoke made by heating coal to a temperature of 480°C or higher and 520°C or lower. < / pat:ClaimText> < / pat:Claim> < / pat:Claims>