Milk fiber semi-worsted blended yarn

Abstract

The invention belongs to the technical field of spinning tools, and particularly relates to milk fiber semi-worsted blended yarn.. The milk fiber semi-worsted blended yarn is composed of, by weight percentage, 30-50% of milk fiber, 10-30% of cashmere and 30-50% of modal fiber. Due to the fact that a semi-worsted technology is organically combined by two kinds of spinning machinery of wool spinning and cotton spinning, the technology has the advantages of being high in yield, short in procedure, saving in used labor, low in cost and the like. The yarn manufactured through the semi-worsted technology is as soft as cotton, as glossy as silk and as smooth as flax, and meanwhile, the yarn is better than the cashmere in wear-resistance, anti-pilling performance and strength.

Description

technical field

[0001] The invention belongs to the technical field of spinning equipment, in particular to a milk fiber semi-worsted blended yarn. Background technique

[0002] Cashmere is a high-grade wool textile raw material, and its thermal performance is unmatched by other fibers. However, the whole cashmere mainly woven from cashmere yarn (the quality of cashmere usually accounts for more than 90% of the quality of the whole cashmere fabric), due to its smoothness, moisture absorption and other characteristics are not That's fine, it's not normally used as a close-fitting garment. In addition, the output of cashmere is limited, and the fabrics made of all cashmere are expensive, which cannot meet the living needs of the broad masses of the people. Contents of the invention

[0003] The purpose of the present invention is to solve the technical problems described above, a kind of milk fiber semi-worsted blended yarn is provided, and its technical scheme is as follo...

Examples

Embodiment 1

[0015] Take 45 kg of milk fiber, 43 kg of modal fiber, and 12 kg of cashmere, wherein the milk fiber, when the relative humidity changes from 40% to 90% at an ambient temperature of 20°C, has a moisture absorption of ≥ 18 J / gram. The semi-worsted process is used to make the yarn. The specific process is as follows: Wool-carding-drawing-roving-fine sand-winding-doubling-two-for-one twisting-winding. The yarn count used is 32NM.

Embodiment 2

[0017] Take 40 kg of milk fiber, 50 kg of modal fiber, and 10 kg of cashmere, wherein the milk fiber, when the relative humidity changes from 40% to 90% at an ambient temperature of 24 ° C, has a moisture absorption of ≥ 18 J / gram. The semi-worsted process is used to make the yarn. The specific process is as follows: Wool-carding-drawing-roving-fine sand-winding-doubling-two-for-one twisting-winding. The yarn count used is 60NM.

Embodiment 3

[0019] Take 50 kg of milk fiber, 40 kg of modal fiber, and 10 kg of cashmere, wherein the milk fiber, when the relative humidity changes from 40% to 90% at an ambient temperature of 26 ° C, has a moisture absorption of ≥ 18 J / gram. The semi-worsted process is used to make the yarn. The specific process is as follows: Wool-carding-drawing-roving-fine sand-winding-doubling-two-for-one twisting-winding, and the yarn count used is 100NM.

technical field

[0001] The invention belongs to the technical field of spinning equipment, in particular to a milk fiber semi-worsted blended yarn. Background technique

[0002] Cashmere is a high-grade wool textile raw material, and its thermal performance is unmatched by other fibers. However, the whole cashmere mainly woven from cashmere yarn (the quality of cashmere usually accounts for more than 90% of the quality of the whole cashmere fabric), due to its smoothness, moisture absorption and other characteristics are not That's fine, it's not normally used as a close-fitting garment. In addition, the output of cashmere is limited, and the fabrics made of all cashmere are expensive, which cannot meet the living needs of the broad masses of the people. Contents of the invention

[0003] The purpose of the present invention is to solve the technical problems described above, a kind of milk fiber semi-worsted blended yarn is provided, and its technical scheme is as follo...

Examples

Embodiment 1

[0015] Take 45 kg of milk fiber, 43 kg of modal fiber, and 12 kg of cashmere, wherein the milk fiber, when the relative humidity changes from 40% to 90% at an ambient temperature of 20°C, has a moisture absorption of ≥ 18 J / gram. The semi-worsted process is used to make the yarn. The specific process is as follows: Wool-carding-drawing-roving-fine sand-winding-doubling-two-for-one twisting-winding. The yarn count used is 32NM.

Embodiment 2

[0017] Take 40 kg of milk fiber, 50 kg of modal fiber, and 10 kg of cashmere, wherein the milk fiber, when the relative humidity changes from 40% to 90% at an ambient temperature of 24 ° C, has a moisture absorption of ≥ 18 J / gram. The semi-worsted process is used to make the yarn. The specific process is as follows: Wool-carding-drawing-roving-fine sand-winding-doubling-two-for-one twisting-winding. The yarn count used is 60NM.

Embodiment 3

[0019] Take 50 kg of milk fiber, 40 kg of modal fiber, and 10 kg of cashmere, wherein the milk fiber, when the relative humidity changes from 40% to 90% at an ambient temperature of 26 ° C, has a moisture absorption of ≥ 18 J / gram. The semi-worsted process is used to make the yarn. The specific process is as follows: Wool-carding-drawing-roving-fine sand-winding-doubling-two-for-one twisting-winding, and the yarn count used is 100NM.