A kind of high flow reinforced flame retardant PBT material and preparation method thereof

A high-flow, PBT resin technology, applied in the field of polymer materials, can solve problems such as odor problems, floating fibers, and poor fluidity, and achieve the effects of improved fluidity, good dispersion, and good appearance

CN107266880BActive Publication Date: 2019-04-30武汉顺威赛特工程塑料有限公司
8 Cites 0 Cited by

Patent Information

Authority / Receiving Office
CN · China
Patent Type
Patents(China)
Current Assignee / Owner
Publication Date
2019-04-30

Smart Images

  • Figure 1
    Figure 1
  • Figure 2
    Figure 2
Patent Text Reader

Abstract

The invention relates to a high-fluidity and reinforced-flame-retardant PBT material. The PBT material is composed of the following raw materials, in percent by weight: 49-68% of PBT resin, 11.5-13.5% of a flame retardant, 0-3% of a toughening agent, 20-33% of glass fibers, 0.2-0.5% of hyperbranched resin and 0.3-1% of other auxiliary agents. A preparation method of the high-fluidity and reinforced-flame-retardant PBT material is simple, firstly, the PBT resin is dried, and the dried PBT resin and the flame retardant are mixed and stirred, secondly, the toughening agent, the hyperbranched resin and the other auxiliary agents are added, and uniform stirring is performed, and finally, the uniformly mixed raw materials and the glass fibers are added to a melt extruder for extrusion, so that the high-fluidity and reinforced-flame-retardant PBT material is obtained. Compared with the prior art, the high-fluidity and reinforced-flame-retardant PBT material has the beneficial effects that the high-fluidity and reinforced-flame-retardant PBT material has good thermal stability, no white stripes precipitate during injection molding at 300 DEG C, besides, pungent smells cannot be emitted under high-temperature heating, the surface of a product is smooth, and the high-fluidity and reinforced-flame-retardant PBT material can be used for electronic appliance appearance parts such as blade handles, air discharging grilles and hot-runner one-module-multiple-output products which need high fluidity.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention belongs to the field of macromolecular materials, and in particular relates to a high-fluidity reinforced flame-retardant PBT material and a preparation method thereof. Background technique

[0002] PBT resin is cost-effective, has excellent comprehensive mechanical properties, high temperature resistance, and is easy to flame retardant. It especially solves the shortcomings of nylon’s unstable water absorption size on the one hand and poor electrical performance of nylon water absorption on the other hand. After modification and processing, it includes the current low temperature resistance. 40℃ super-tough PBT is widely used in heat-resistant parts of home appliances and electronic appliances, and has the potential to replace nylon.

[0003] Hyperbranched resins are different from the previous branched resins. For example, the branched high-flow nylon resin of Zhuzhou Times New Material Technology Co., Ltd. can actually be considered as...

Examples

Embodiment Construction

[0020] The technical solution of the present invention will be further described in detail below in conjunction with specific examples, and the given examples are only used to explain the present invention, and are not intended to limit the scope of the present invention.

[0021] The methods adopted in the present invention are conventional methods without special instructions, and the raw materials used in the present invention are commercially available products without special instructions. Specifically, the PBT resin is starester@HQ-Ⅱ produced by Nantong Xingchen Company by PTA method; the main flame retardant is brominated polystyrene B-701 produced in Oseki, Japan; the synergistic flame retardant is Hunan Chenzhou ordinary grade Antimony trioxide, purity 99.8%; toughening agent is DuPont PTW, hyperbranched resin is Hyper C100 from Wuhan Hyperbranched Resin Technology Co., Ltd.; processing aids including silicone masterbatch are Dow Corning MB50-002.

[0022] The inventi...