Method for making brick powder concrete from waste sintered shale brick powder

A technology of concrete and shale bricks, applied in the field of concrete, can solve problems such as increasing jobs, and achieve the effects of saving resources, improving performance, and reducing environmental pollution

CN110156406AActive Publication Date: 2019-08-23GUANGXI UNIVERSITY OF TECHNOLOGY +1
4 Cites 1 Cited by

Patent Information

Authority / Receiving Office
CN · China
Current Assignee / Owner
Publication Date
2019-08-23

Smart Images

  • Figure 1
    Figure 1
  • Figure 2
    Figure 2
  • Figure 3
    Figure 3
Patent Text Reader

Abstract

A method for making brick powder concrete from waste sintered shale brick powder comprises the following steps: (1) impurity removal; (2) crushing and drying treatment; (3) grinding, sieving and drying treatment for obtaining the waste sintered shale brick powder; (4) weighing of the following raw materials: cement, medium sands, cobblestones, water, the waste sintered shale brick powder, magnesium borate, zirconia, hydroxypropyl methylcellulose, bentonite and mica according to corresponding parts by weight; (5) oscillation stirring of the raw materials with 100-200 Hz ultrasonic waves to obtain a mixed slurry; and (6) molding of the mixed slurry. Sintered shale bricks which are wastes are processed to form the powder, and the powder is used for partially replacing the cement to produce the brick powder concrete, and the integral performances of the brick powder concrete are effectively better than those of ordinary concrete.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention relates to the technical field of concrete, in particular to a method for making brick powder concrete by using waste sintered shale brick powder. Background technique

[0002] Concrete is one of the fundamental materials widely used in the civil engineering industry. According to the statistics of the National Bureau of Statistics, my country's commercial concrete output in 2016 reached 1,792 million cubic meters, an increase of 7.4%, and an increase of 5.4 percentage points year-on-year. With the rapid economic development, the application of concrete is more and more extensive. Every day in our country, old buildings are demolished and new ones rise. As a result, a large amount of construction waste will be generated every day. Abandoned sintered shale bricks account for a large part of construction waste. At the same time, shale brick manufacturers also produce a large number of discarded bricks. These bricks have no reasonable tre...

Examples

Embodiment 1

[0044] The method for making brick powder concrete by using waste sintered shale brick powder comprises the following steps:

[0045] (1) Recycling waste sintered shale bricks, using manual hammering, preliminary crushing, and sorting to remove impurities from waste sintered shale bricks;

[0046] (2) Use a jaw crusher to crush the waste sintered shale bricks after removal of impurities, and dry them after crushing;

[0047] (3) Finely grind the broken waste sintered shale bricks, sieve with a vibrating sieve machine, and dry them in an oven to obtain waste sintered shale brick powder. The fineness of the waste sintered shale brick powder is 0.08 mm;

[0048] (4) In parts by weight, the raw materials used are as follows: 359 parts by weight of cement, 600 parts by weight of medium sand, 1100 parts by weight of stones with a particle size of 18 mm, 190 parts by weight of water, 246 parts by weight of waste sintered shale brick powder 3 parts by weight, 3 parts by weight of ma...

Embodiment 2

[0053] The method for making brick powder concrete by using waste sintered shale brick powder comprises the following steps:

[0054] (1) Recycling waste sintered shale bricks, using manual hammering, preliminary crushing, and sorting to remove impurities from waste sintered shale bricks;

[0055] (2) Use a jaw crusher to crush the waste sintered shale bricks after removal of impurities, and dry them after crushing;

[0056] (3) Finely grind the broken waste sintered shale bricks, sieve with a vibrating sieve machine, and dry them in an oven to obtain waste sintered shale brick powder. The fineness of the waste sintered shale brick powder is 0.10 mm;

[0057] (4) In terms of parts by weight, the raw materials used are as follows: 400 parts by weight of cement, 610 parts by weight of medium sand, 1135 parts by weight of stones with a particle size of 20mm, 200 parts by weight of water, 48 parts by weight of waste sintered shale brick powder Part, 4 parts by weight of magnesiu...

Embodiment 3

[0062] The method for making brick powder concrete by using waste sintered shale brick powder is characterized in that it comprises the following steps:

[0063] (1) Recycling waste sintered shale bricks, using manual hammering, preliminary crushing, and sorting to remove impurities from waste sintered shale bricks;

[0064] (2) Use a jaw crusher to crush the waste sintered shale bricks after removal of impurities, and dry them after crushing;

[0065] (3) Finely grind the broken waste sintered shale bricks, sieve with a vibrating sieve machine, and dry them in an oven to obtain waste sintered shale brick powder. The fineness of the waste sintered shale brick powder is 0.15 mm;

[0066] (4) In parts by weight, the raw materials used are as follows: 445 parts by weight of cement, 620 parts by weight of medium sand, 1185 parts by weight of stones with a particle size of 22mm, 210 parts by weight of water, 96 parts by weight of waste sintered shale brick powder Part, 5 parts by...