LARGE GLASS CERAMIC WORKTOP

Description

[0001] The present invention relates to a work surface, or work table or counter or piece of furniture, formed from at least one large plate positioned or intended to be positioned horizontally on one or more support elements (case of a piece of furniture, support leg(s)) in order to provide a stable surface intended for different uses. In particular, the present invention relates to a table or piece of furniture having a surface or top capable of simultaneously or successively allowing different activities and / or supporting objects, in particular capable of allowing the cooking or reheating of food in suitable containers and offering other uses.

[0002] Materials commonly used to make worktops include, for example, wood, quartz, Corian ®, etc. For cooking food, there are also large cooking surfaces in kitchens, particularly for professional use, these plates being generally metallic and / or composite. In particular, there are multi-layer panels, based on ceramic layers or materials such as stoneware, metallic layers or materials such as aluminum and insulating plastic layers or materials such as Bakelite, these panels generally having a significant thickness (of the order of 12 mm for example) and being complex to produce.

[0003] At the same time, cooking surfaces made of glass-ceramic or reinforced glass materials, of more limited dimensions (in particular with a surface area generally less than 0.4 m 2 < , plates with a larger surface area which may be more difficult to obtain using the processes usually used, and which may pose problems in terms of flatness, handling, etc.), exist, particularly for domestic uses, the use of glass-ceramic material having become widespread in recent years for cooking plates, in particular due to the performance of this material for this use and the attractive appearance of the plates produced.

[0004] There are currently different types of glass-ceramic hobs, each variant being the result of significant studies and numerous tests, given that it is very delicate to make modifications to these hobs and / or to their production process without risking an adverse effect on the desired properties: to be able to be used as a cooking hob, a glass-ceramic hob must generally have a transmission in the wavelengths of the visible range that is both low enough to mask at least part of the underlying heating elements when at rest and high enough so that, depending on the case (radiant heating, induction heating, etc.), the user can visually detect the heating elements in working order for safety purposes; it must also have a high transmission in the wavelengths of the infrared range, particularly in the case of radiant hobs.The plates thus designed are intended exclusively for use as cooking plates and are not traditionally intended to receive objects other than heat-resistant utensils used for cooking food, nor intended for the performance of activities other than cooking food.

[0005] The state-of-the-art documents EP2217036A1, FR2955574A1 and US2012263957A1 are relevant to the invention defined below.

[0006] The present invention sought to expand the range of existing household equipment products, for domestic or professional use, by developing a new type of interactive product allowing more varied uses.

[0007] This aim has been achieved by the new equipment or article or installation according to the invention, advantageously interactive, this furniture / household equipment comprising: at least one work surface (or counter or table) formed from at least one substrate (in particular plate or surface or tray) made of (or (based on) a or essentially consisting of a) monolithic (or monobloc or single-piece) glass material, advantageously essentially flat, with a surface area (length by width of its face of largest dimensions) greater than 0.7 m 2< , said substrate having a brightness L* of less than 10, a blur of less than 30%, and a light transmission TL of less than 10%, at least one heating element (in particular under the substrate and hidden by it when this heating element is not in operation / is at rest), at least one light source, intended to materialize (make visible) one or more zones (such as the heating zones) or one or more elements or displays (for example an operating status indicator or a power indicator) of the substrate, in particular by light transmission through the substrate, this source being located under the substrate and being hidden by it when this source is not in operation / is at rest, at least one communication interface with at least one element of the plane (for example with the light source(s) and / or the heating element(s).

[0008] The product developed according to the invention meets the desired aim, the present invention thus proposing a new interactive equipment (allowing in particular the activation of functions such as cooking food, and the display of zones or data) which can be used just as well in the kitchen as in another living room, the work surface being able to be part of a solid or non-solid piece of furniture, a table, a counter, etc., this work surface being mounted or able to be mounted horizontally on (in particular at the top of) one or more support elements (case of a piece of furniture, support leg(s)) in order to offer a stable surface intended for different uses, the work surface or the equipment according to the invention having a continuous upper surface able to allow simultaneous or successive activities (such as work, games, reading, etc.), the support of objects (such as papers, computers, vases, dishes, etc.), and the preparation or cooking or reheating of food in suitable containers.

[0009] As previously indicated, the worktop is formed from a substrate or plate of monolithic glass material (the glass material having been formed from a single block / in a single piece, even if the substrate may, if necessary, have recesses, generally made in the already formed piece, for aesthetic or functional purposes) of large dimensions, the advantage of such a monolithic plate of large dimensions being in particular to offer a surface that is mainly continuous / uniform / without joints, aesthetic and easy to maintain, as well as greater comfort of use and greater safety (in terms of sealing in the event of liquid spillage, etc.), etc.The substrate consists essentially, or even solely, of the glass material, this substrate / glass material possibly being provided with decorative or functional coatings of low thickness (in particular of the order of a few tens of nanometers to a few hundred microns, or even more), for example enamel, paint, thin layers, etc., as specified later.

[0010] Unlike the use in glass-ceramics in particular, this (substrate in) glass material is of large dimensions, its surface (corresponding to the product of its length by its width for its face of larger dimensions - generally its upper face, intended to be visible and to serve as a support for articles (household or work or cooking) being of dimensions greater than 0.7 m 2< , preferably greater than 0.9 m 2< , in particular greater than 1 m 2< , in particular greater than or equal to 2 m 2< . However, the manufacture of large plates, in the case of glass-ceramics in particular, poses numerous problems in terms of flatness and handling.A large plate, yet with good flatness, can nevertheless be advantageously obtained by reducing the passage speed (or lengthening the ceramization arch or increasing the residence time in the arch) compared to the speed (or the length of the arch or the standard time) usually used to obtain vitroceramic plates of usual dimensions less than 0.4 m 2 < , as explained later in the process described.

[0011] The substrate / glass material according to the invention is advantageously flat (or predominantly or almost flat), and in particular has a flatness (height between the highest point and the lowest point of the substrate relative to the mean plane of the substrate, with the exception of any voluntary deformations made to the substrate for aesthetic or functional purposes) of less than 0.1% of the diagonal of the substrate, and preferably less than 3 mm, in particular less than 2 mm, in particular less than 1 mm, or even of the order of zero, depending on the size / surface / diagonal of the substrate, the flatness being measured using a SurFlat reference undulometer marketed by the company Visuol. The substrate is generally of geometric shape, in particular rectangular, or even square, or even circular or oval, etc., and generally has an "upper" face (visible face) in the position of use, another "lower" face (generally hidden, in the frame or box of the furniture incorporating the worktop) in the position of use, and a slice (or edge or thickness). The upper face is generally flat and smooth but may also have at least one raised area and / or at least one hollow area and / or at least one opening and / or beveled edges (these shapes having been added during the manufacture of the substrate, for example by rolling or collapsing or pressing, etc., or having been added in rework), etc., these variations in shape advantageously constituting continuous variations of the plate (without change of materials or connections). The lower face may in particular be smooth or provided with studs increasing its mechanical resistance and obtained for example by rolling.

[0012] The thickness of the substrate made of monolithic glass material is generally at least 2 mm, in particular at least 2.5 mm, in particular is of the order of 3 to 30 mm, and advantageously is less than 15 mm, in particular is of the order of 3 to 15 mm, in particular 3 to 10 mm.

[0013] The glass material of the substrate used is advantageously resistant to high temperature and / or has a zero or almost zero expansion coefficient (for example less than 15.10 -7< K -1< ), in particular is advantageously glass-ceramic or reinforced glass (in particular chemically or thermally toughened). Preferably, the substrate is a glass-ceramic substrate. As defined according to the invention, the substrate / glass material is advantageously low transmissivity, low diffusivity and dark in color (defined by the brightness L*), in particular black or dark brown in color, this material allowing in particular a display by light transmission through the substrate, as specified below.

[0014] The glass ceramic used may in particular be of composition as described in the patent applications published under the following numbers: WO2012156444, WO2012001300, DE202012011811, this glass ceramic being in particular a lithium aluminosilicate glass ceramic.

[0015] For example, a glass-ceramic comprising the following constituents and / or obtained by ceramization from a glass of the following composition, within the limits below expressed in weight percentages, is advantageously used: SiO 2 : 52 - 75%; Al 2 O 3 : 18 - 27%; Li 2 O: 2.5 - 5.5%; K 2 O: 0 - 3%; Na 2 O: 0 - 3%; ZnO: 0 - 3.5%; MgO: 0 - 3%; CaO: 0 - 2.5%; BaO: 0 - 3.5%; SrO: 0 - 2%; TiO 2 : 1.2 - 5.5%; ZrO 2 : 0 - 3%; P 2 O 5 : 0 - 8 %, and preferably within the following limits expressed in weight percentages: SiO 2 : 64 - 70 %; Al 2 O 3 : 18 - 21 %; Li 2 O : 2.5 - 3.9 %; K 2 O : 0 - 1.0 %; Na 2 O : 0 - 1.0 %; ZnO : 1.2 - 2.8 %; MgO : 0.20 - 1.5 %; CaO : 0 - 1 %; BaO: 0 - 3 %; SrO: 0 - 1.4 %; TiO 2 : 1.8 - 3.2 %; ZrO 2 : 1.0 - 2.5 %.

[0016] The glass ceramic may be arsenic-refined (i.e. (mother glass of) composition comprising in the order of 0.5% to 1.5% by weight of arsenic oxide (expressed as As 2 O 3 ), or may be non-arsenic-refined (in particular having an arsenic oxide content of less than 0.2%, in particular less than 0.1%, or even zero) / tin-refined.

[0017] The glass material may also be a non-ceramic tempered glass, for example a tempered lithium aluminosilicate as described in the patent applications published under the following numbers: FR1060677, WO2012080672, or in the application filed in France under number 1363157, or a tempered glass of another type (soda-lime, borosilicate, etc.), for example as described in the application published under number WO2012146860.

[0018] The glass-ceramic or tempered glass is obtained by the respective processes described in the aforementioned documents using the processing cycles and temperatures making it possible to obtain the glass material having the selected characteristics given in the definition of the invention. In the case of glass-ceramics, these processes are preferably modified by reducing the passage speed by at least 25%, preferably by at least 50%, or by increasing the length of the ceramization arch or the residence time in said arch by at least 25%, preferably by at least 50%, compared respectively to the speeds, lengths and times normally used, in order to obtain a large-sized flat substrate as required according to the invention, as explained later.

[0019] As defined according to the invention, the substrate forming the work surface is selected so as to have a brightness L* of less than 10, preferably less than 5, in particular less than 4, or even less than 2, a blur of less than 30%, in particular less than 28%, and a light transmission TL of less than 10%, in particular less than or equal to 5%, in particular from 0.8% to 5%, this light transmission preferably being non-zero (greater than 0%). The substrate has these characteristics over most (in particular over at least 80%, or even over 100%) of its surface, with the exception of any localized decorations (for example enamel) or localized components applied to its surface.These properties are generally those of the glass material forming the substrate itself, without the presence of any coating, but where appropriate may result from the combination of the glass material and a coating applied to the majority of one and / or the other of its main faces. Advantageously, these are the intrinsic characteristics of the glass material substrate, that is to say that said glass material substrate has these characteristics in itself without the presence of any coating.

[0020] The brightness L* is a component defined in the CIE colorimetric system and is evaluated in a known manner, in particular using a Byk-Gardner Color Guide 45 / 0 colorimeter (reflection colorimetry) on the upper face of the substrate placed on an opaque white background.

[0021] The haze measures the level of light scattering and is defined, within the framework of the invention, as being the ratio of the diffuse transmission to the total transmission at a wavelength equal to 550 nm, this haze being evaluated for example using the spectrophotometer equipped with an integrating sphere used for light transmission measurements.

[0022] The luminous transmission TL is measured according to ISO 9050:2003 using illuminant D65, and is the total transmission (integrated in the visible range), taking into account both direct transmission and any diffuse transmission, the measurement being made for example using a spectrophotometer equipped with an integrating sphere, the measurement at a given thickness then being converted where appropriate to the reference thickness of 4 mm according to ISO 9050:2003.

[0023] The substrate according to the invention as defined above is in particular of dark appearance, and is formed from a low transmissive and low diffusing material, in particular is of black or brown appearance, making it possible in particular, in combination with light sources placed underneath, to display light zones making it possible to signal the cooking zones when they are in working order, while masking the underlying elements, in particular when at rest. The glass material used also has an opacity indicator (or factor or coefficient) Ω of less than 100, and advantageously greater than 93, in order in particular to allow said display by underlying sources in an embodiment of the invention or a projection display as indicated later,this opacity indicator in the present invention being determined by the formula Ω = 100 - ΔE* and being evaluated by measuring (reflection colorimetry carried out using a Byk-Gardner Color Guide 45 / 0 colorimeter) the color variation ΔE*, corresponding to the difference between the color, measured in reflection on the upper face of the substrate, for the substrate placed on an opaque black background and that for the substrate placed on an opaque white background (ΔE* = ((LN *-LB *) 2< + (a N *-a B *) 2< + (b N *-b B *) 2< ) ½< , LB *,a B *,b B * being the colorimetric coordinates of the first measurement on a white background and LN *,a N *,b N * being those of the second measurement on a black background in the colorimetric system established in 1976 by the CIE).,

[0024] The substrate is preferably based on a black glass-ceramic generally comprising crystals of β-quartz structure within a residual glassy phase, the absolute value of its coefficient of expansion being advantageously less than or equal to 15.10 -7 < / °C, or even 5.10 -7 < / °C, and having the characteristics previously mentioned, such as the glass-ceramic of the plates marketed under the name Kerablack+ by the company Eurokera. In particular, it may be an arsenic-refined glass-ceramic of composition as described in patent application EP0437228 or US5070045 or FR2657079, or a tin-refined glass-ceramic, having an arsenic oxide content of less than 0.2% (or even less than 0.1%, or even less than or equal to 500 ppm, or even zero), for example of composition as described in patent application WO 2012 / 156444.

[0025] Where appropriate, the substrate may also comprise colorants, for example giving certain shades or tints, at levels preferably less than 10% by weight, for example vanadium oxide, iron oxide, cobalt oxide, cerium oxide, selenium oxide, chromium oxide, or even nickel oxide, copper oxide and / or manganese oxide, etc.

[0026] As defined above, the article according to the invention also comprises at least one heating element (or heating element), for example one or more radiant or halogen burners or one or more gas burners and / or one or more induction heating means, these heating means generally being located under the work surface and hidden by the latter when at rest. The work surface of the article according to the invention may comprise one or more heating elements, as well as one or more burners. The term "fire" means a cooking location. The article according to the invention may comprise several types of heating elements or burners (gas burners, radiant, halogen or induction burners). Preferably, the article according to the invention comprises as heating element(s) one or more induction heating means.

[0027] The heating means may be located in a defined area (for example on one end of the substrate) or several areas of the substrate, or may be uniformly distributed under the substrate, occupying for example at least 25% of the surface area of ​​the substrate, or may even occupy a surface area almost equivalent to that of the substrate (for example more than 50%, in particular more than 75%, or even more than 85%, or even 100% of the main surface area of ​​the substrate), a plurality of small-sized inductors lining for example the substrate under its lower face, to allow heating as needed in any area.

[0028] The cooking areas on the worktop, directly above the heating means, may be indicated (or not, for example in the case of a worktop equipped with heating means covering its entire surface area), upon activation and / or permanently, in particular by means of one or more light sources and / or by means of a fixed decoration, for example in enamel. The dimensions of the motifs used to indicate the cooking areas (as well as those of motifs which may indicate other areas or functions) may be more or less important, for example they may be circles delimiting each of the heating elements, or small motifs (triangles, crosses, etc.) in their center or at their base, etc.

[0029] Preferably, the cooking locations (and / or where appropriate other zones and / or elements and / or functions and / or decorations) are indicated by at least one light source as mentioned in the definition of the invention, this source, once activated, indicating, for example, the location using a light pattern (in particular of the disc, circle, cross, triangle, etc. type) of fixed or variable color and / or dimensions. Alternatively, they may be indicated permanently, by a fixed pattern (in particular of the round, circle, cross, triangle, etc. type), obtained in particular by depositing layer(s) (in particular such as that(s) used for the decoration of glass-ceramics), for example enamel, on the surface of the plate (in particular on the upper face).

[0030] According to the invention, the cooking location(s) (and / or where appropriate other areas and / or elements and / or functions and / or decorations) are indicated by, and / or highlighted using or by means of, at least one light source as mentioned in the definition of the invention, upon activation of said source, said source being placed under the substrate (in the use position) and being hidden by the latter when at rest, said source allowing a light display by transmission through the substrate / work surface.

[0031] In another advantageous embodiment, the face, in particular the upper face (in the position of use) or the visible face, of the plate is coated with an opacifying coating, in particular an enamel or thin layers, the coverage rate of said opacifying coating in the coated area being at least 5%, preferably at least 20%, in particular at least 45%, or even 100%, the enamel having, where appropriate (in particular when the coverage rate is less than 100%), a pigment content greater than 2% (relative to the rate of frit + pigment(s) in the enamel), in particular greater than 5%, preferably greater than 10%, in particular between 5 and 30%, and / or having a refractive index different from that of the substrate.

[0032] One or more light sources may also enable the display of other elements or functions, for example the display of control means or zones (in the form of keys, logos, or even keyboards, etc.) or indicators (of intensity / power, time, etc.), which can be activated, for example, by contact on the surface of the hob (using, for example, sensors located under the surface) or remotely (in particular by wireless communication), or even by simple movement of the hand (by sensors located, where appropriate, outside and recording the movement, for example by triangulation, to convert it, using, in particular, a suitable algorithm and interface, into the activation of a function, for example), or where appropriate by placing a specific object (saucepan, etc.) in a specific location (such as a cooking zone) of the hob.The light source(s) may also allow the display of decorations, or various data (display for example of computer pages, cooking recipes, etc.) downloaded for example by wireless communication using an appropriate interface and transmitted from the light sources to the surface of the plate.

[0033] Where appropriate, the article according to the invention may comprise several light sources, for lighting several areas or for displaying complex texts or decorations, or for homogenizing the lighting, these sources being able to be arranged along different axes and lighting angles to obtain the desired effect, without unwanted reflections or shadows. According to an embodiment not forming part of the invention, in the case of lighting by projection onto the screen-forming plane, several sources are for example arranged so that the angle between each source (or between each element, for example mirror, sending the light towards the work plane) and the normal to the work plane is between 5 and 60°, preferably between 30 and 45° to minimize the effects of shadows projected by a person operating on the work plane.

[0034] The light source(s) may advantageously be formed by light-emitting diodes for reasons including size, efficiency, durability and resistance to surrounding conditions (heat, etc.).

[0035] These diodes are advantageously of the semiconductor chip(s) type, made of mineral materials (LEDs), emitting in particular in one direction, and can be encapsulated, that is to say comprise a semiconductor component and an envelope (for example made of epoxy or nylon type resin), encapsulating the semiconductor component. These diodes can also be semiconductor chips without collimating lenses, for example of a size of the order of a hundred µm or mm, possibly with minimal encapsulation (for example protective).

[0036] The diodes may, if necessary, be carried by a support or strip or base, this base being able to have a surface (flat or inclined) treated and / or made reflective for better luminous efficiency, for example coated with a lacquer or paint and / or mirror layer, and / or coupled with a white or metallic reflector to better direct the emitted radiation.

[0037] Where appropriate, organic light-emitting diodes (OLEDs) may also be used, consisting in particular of a superposition of organic semiconductor layers between electrodes, and producing different colors at pixel level depending on the path of electricity through the organic layers. Other types of light sources may also be used, in conjunction with or alternatively to the aforementioned diodes, for example halogen or incandescent lamps, lasers or liquid crystal displays, the sources possibly being used in combination with lenses or mirrors, etc.

[0038] The assembly of each source or sources (to the plate or to another part of the equipment or to an external part (associated with said equipment) can be done by welding, clipping, gluing, etc., if necessary by means of another element; for example, diodes can be mounted, welded to a support itself housed at the bottom of a metal profile, by clipping or gluing the profile. The positioning of the source(s) (in relation to the plate in particular) is adapted to allow a display through the substrate .

[0039] The sources, as well as their power supply and actuation, can be separated or not so as to allow simultaneous or individual lighting of the desired lighting zones, according to requirements. Each source can be monochromatic (pure color) or polychromatic (synthetic color).

[0040] By "monochromatic light source" is meant a light source having a single emission peak in the visible wavelength range and such that the width of the peak varies from 1 to 100 nm, preferably from 5 to 50 nm.

[0041] A "polychromatic light source" means a light source that has at least two emission peaks at different wavelengths in the visible wavelength range. The color perceived (by the retina) then results from a mixture of the different wavelengths. This may be an LED, and / or an LED display, with an emission spectrum having a main emission peak and another emission peak, for example fluorescence, broader than the main peak, and generally of lower intensity. The polychromatic LED emits in particular with a first emission (of high or low intensity) between 400 and 500 nm and with a second emission (of high or low intensity) in the visible range beyond 500 nm (for example, the case of LEDs formed from at least one electroluminescent crystal and photoluminescent phosphor(s)).In particular, white LEDs made, for example, from a semiconductor crystal chip such as indium gallium nitride (InGaN) emitting in the blue, covered with a transparent resin (such as silicone or epoxy) containing mineral phosphors (for example YAG:Ce), absorbing the blue and emitting in the yellow, can be used as sources. Polychromatic emission LEDs can also be used, for example formed from three monochromatic sources of independently regulated intensities of the "RGB" type (with three sources: red, green and blue), etc.

[0042] One or more sources may also be integrated into or coupled to or combined with one or more display-type structures (for example, light-emitting diodes known as “7-segment” or liquid crystals), electronic control strip or screen with sensitive keys and digital display (where appropriate by wireless communication using an interface), etc.

[0043] In addition to the source(s), the article according to the invention may also comprise at least one waveguide intended to propagate light from one part of the article to another (in particular by total internal reflection or by metallic reflection), in particular when the sources are placed under the work surface, each light source then being attached to the guide concerned and cooperating with it by emitting its light radiation within it so that the guide transmits it, the light source(s) emitting / being coupled for example by the edge or side of the guide. This guide is advantageously clear or transparent, and may in particular be attached (assembled after having been designed separately) under the lower face of the plate. It may be organic and / or plastic (for example polycarbonate or polymethyl methacrylate PMMA), or mineral, and is preferably mineral; in particular, it is a glass.The article according to the invention may comprise several guides each dedicated to one or more lighting zones, or a unitary guide, provided where appropriate with openings. The guide may be secured to the substrate by gluing and / or clipping, or by encapsulation, etc. The assembly of the guide may be done directly on the substrate or on another part of the equipment or a support on which the worktop is mounted, for example it may be secured to the box on which the worktop rests. The guide makes it possible, among other things, to better conduct the light to the desired lighting zones and is particularly suitable with the substrate used according to the present invention.

[0044] One of the sources being placed under the work surface, where appropriate associated with at least one waveguide, the equipment may also comprise in the lighting zone, at least one means for extracting the radiation emitted by the source(s), for example one or more diffusing elements or treatments, in particular a layer applied to the surface and / or any differential treatment or texturing of the surface (local or over the entire surface) of the waveguide or of the extraction surface, such as laser engraving, enamel printing, chemical (acid, etc.) or mechanical (sandblasting, etc.) etching, etc. An extraction surface may, where appropriate, be provided in the thickness of the guide, for example using internal laser engraving technology. The geometry and roughness of the edge of a waveguide may also be worked to allow local and controlled extraction of the light.The extraction means allow the radiation to be extracted from the guide to the desired lighting area. They can be combined, if necessary, with another treatment to target the lighting areas, for example with an occulting screen print (masking certain areas and preventing the passage of light) deposited on part of one side of the substrate.

[0045] The equipment may also comprise at least one filter (coupled (in operation) to at least one source (as well as to the plate, the colored area obtained resulting in particular from (the action / effect of) these three components)), so as to form a colored luminous area of ​​chosen color (the color of a source perceived through a dark-colored vitroceramic substrate being modified compared to the original color of the source by the passage through the plate), generally positioned between the source and the plate, this filter being able in particular to be combined (or secured) to the source and / or to the plate and / or possibly to another intermediate element.

[0046] By "filter" is meant an optical filter (acting on the transmission of light), in particular colored (the action on the transmission of the wavelength being done as a function of the wavelengths), this filter being in particular an element or material, generally flat, in particular in the form of a film or layer or composite, based on at least one organic or mineral material, (semi-)transparent (in the sense in particular that it is transparent to certain wavelength(s) of the visible and not transparent to / by blocking / affecting other(s), this filter also generally having a light transmission of at least 5% and in particular of at least 30%), in particular making it possible to absorb and / or reflect and / or re-emit certain wavelengths of the visible spectrum.This filter can advantageously be an absorption filter (the action on the transmission of light being done by absorption at certain wavelengths, the absorbed light being able in particular to be converted into heat and / or emitted at other wavelengths), or can also be a reflection filter (the action on the transmission of light being done by reflection at certain wavelengths). The filter can be added (manufactured separately) and combined with at least one light source and / or the working surface, or it can be integrated or produced directly on said surface and / or said source, for example in the form of a printed layer, for example by inkjet. The radiation emitted by the source passes through the corrective filter in order to produce the desired display through the substrate with which this assembly is combined.The filter can be used to form different colors, for example at least one colored area of ​​white color or of a synthetic color obtained by mixing at several wavelengths.

[0047] Filters can be colored transparent polymers, colored glasses, the coloring being done by deposition or in the mass, or can be layers deposited on the sources or the substrate or another support, etc.Preferably, one or more absorption filters are used, advantageously making it possible to obtain the chosen effect or color regardless of the angle of incidence of the observation, formed for example by depositing (by screen printing, by inkjet or laser printing, by spray, by dipping, by roller application, etc.) one or more mineral or organic dyes or pigments (possibly dissolved or dispersed in a medium, in particular a silicone, epoxy or acrylic resin, or polyurethane, a UV-curing ink, or a sol-gel type mineral matrix) on the surface of the chosen substrate (glass or plastic / polymer type polyethylene terephthalate, polycarbonate, acrylate, polyetheretherketone (PEEK), etc.), the selected dyes or pigments advantageously being heat-resistant.

[0048] It is also possible to use one or more filters acting by light reflection (this reflection being in particular controlled by interference occurring within a stack of thin layers made up of different materials, a thin layer being a layer whose thickness is less than the wavelength of the light), in particular dichroic type filters, based on semi-reflective interference stacks (of layers), etc., produced for example by deposition (under vacuum) in physical vapor phase (PVD) or chemical vapor phase (CVD) of layers of alternating high and low refractive indices, the substrate on which the deposition is carried out being able to be a glass material or a polymer.

[0049] The filter(s) are chosen depending, where appropriate, on the plate used, the desired color, the source, and the desired effect (for example, preservation of the color of the source for a given source or whatever this source may be, or obtaining a target color different from the initial color of the source after transmission through the plate / filter assembly), by combining existing filters where appropriate or by creating an appropriate filter to achieve the desired transmission spectrum by acting on different variables (pigment concentration, type of pigments, thickness of the filter, etc. in the case of an absorption filter, or number of layers, index of each material, thickness of the filter, in the case of a dichroic filter, etc.).

[0050] The filter can be added / deposited if necessary on the plate (on its lower face), in particular by gluing, deposition (of a layer acting as a filter) by laser or inkjet printing, by screen printing, by spray, etc., or can be fixed between the source and the plate, or be mounted on the source (by deposition, gluing, encapsulation, capping, etc.). If necessary, the filter can be inserted between the light source and the light injection surface of a waveguide.

[0051] The source / plate combination and, where appropriate, filter makes it possible to obtain a colored or white display through the dark substrate and / or on said substrate, with particularly sought-after lighting effects in terms of design. The article may have one or more light / display zones for functional and / or decorative use, said zone(s) being able to be in any zone of the plate (including heating zones), and it is possible to have several differentiated light / display zones (color, luminance level), and / or each zone may itself have different colors.

[0052] As indicated previously, the equipment according to the invention also comprises at least one communication interface with at least one element of the plan (such as the light source(s) and / or the heating element(s).

[0053] This communication interface (man-machine or machine-machine in particular) may be a device making it possible in particular to control or transmit commands to the heating elements and / or to the light sources, from or via control buttons or keys integrated into the work surface or located on an external element which is advantageously removable or mobile, in the case in particular of control by wireless communication.

[0054] Preferably, the interface allows wireless communication with a unit external to the work surface (this unit may be part of the equipment according to the invention and may itself constitute an interface), allowing for example the remote activation of the heating zones and / or the light sources and / or the control of different functions (increase or decrease in power or heating time, display of data on the work surface, etc.), the commands given by the external unit being transmitted by the interface to the relevant components of the equipment. The interface may also be a control interface located at the level of the surface (control panel) transmitting the commands by wires or possibly wirelessly to other components of the surface or outside the surface (for example to the sources remote from the surface in the case of projection lighting).

[0055] The external unit in the case of remote control can be, for example, in the form of a keyboard, a tablet or a touch screen, a mobile phone, this unit being able to be fixed (for example fixed on a wall) or mobile. This embodiment has the particular advantage of avoiding fingerprints (unsightly and visible on glass materials) on the worktop or cooking zones. Activating the remote controls also makes it possible to reduce the risk of burns by avoiding handling the controls near the cooking zones. For safety reasons in particular, wireless communication can advantageously be designed to be of limited range (for example limited to the volume of the room in which the equipment is located) and / or equipped with safety features to prevent accidental activation by a person who is not present.Wireless communication is carried out in particular by electromagnetic or radio waves, where appropriate using systems such as Bluetooth, WLAN, Wi-Fi, etc.

[0056] The interface can allow the transmission of different signals initiated by contact or even by movement to activate different components as already mentioned (for example it can convert a movement, detected by sensors by triangulation, these sensors being connected to this interface (and forming part of it where appropriate), into the activation of a function (for example the increase in heating power, lighting of the heating zones, etc.). It can also allow the downloading and / or transmission of various data (such as internet pages, wallpapers, cooking recipes, etc.), this data being for example transmitted to light sources allowing in particular their display on the surface of the work surface.

[0057] At least one interface is generally located on or under the work surface or nearby. The equipment according to the invention may also comprise several interfaces, of the same type or different, allowing for example the activation of different elements, or the equipment may comprise several interfaces, possibly operating differently (of different constitution, operating at different frequencies, etc.) to control the same element (for example a heating zone) with a reinforced level of security. Where appropriate, an interface may be provided in particular for coordinating the activation of the heating zones with the activation of the light sources. The interface may be formed of sensor(s), connector(s), control element(s), any other electrical or electronic or electromagnetic component, etc.

[0058] In addition to the interface, the equipment or work surface may be equipped with various cables, connectors or other elements, particularly electrical ones, contributing to the transmission of commands from one part of the equipment to another.

[0059] The equipment, in particular the worktop, according to the invention may also include various functional and / or decorative coatings, in particular among those generally used with the glass materials concerned, for example based on enamel, paint, thin layer(s) (for example metallic, dielectric, etc.), etc. For example, one of the faces of the substrate may include one or more layers or one or more enamel patterns, for decorative purposes and / or in order to indicate one or more elements (displays, cooking zones, etc.), and / or serving as masking (to avoid, for example, direct vision of the sources, this masking however not being necessary with the substrates selected according to the invention), and / or for other functions (as a light extractor or to homogenize the lighting, etc.).In particular, the worktop may be provided with a functional layer giving it one or more additional properties such as anti-scratch, mechanical reinforcement, etc. The coating may be carried out, for example, by processes such as screen printing, sputtering, inkjet or enamel, etc., the coating being able to be applied in particular to the visible face or to the opposite face, depending on the type of coating and the desired function. For example, in the case of an enamel decoration, this is preferably deposited on the upper face for reasons of visibility in particular, while an opacifying layer of paint is preferably deposited on the opposite, non-visible face for better protection against abrasion in particular, etc.

[0060] As indicated previously, the decorations (or at least part of them) or displays of the work surface can also be obtained with advantages by light display (rather than by depositing a coating), or even by light projection onto the screen-forming surface when the latter is coated with at least one opacifying layer (in particular enamel), as already mentioned previously.

[0061] The following describes a method for manufacturing equipment according to the invention, in particular the worktop of said equipment, the worktop being formed from at least one glass-ceramic substrate with a surface area greater than 0.7 m 2 < , in which at least one cycle of ceramization of a glass plate with a surface area greater than 0.7 m 2 < is carried out to obtain said substrate, and according to which the passage speed is reduced by at least 25%, preferably by at least 50%, or the length of the ceramization arch or the residence time in said arch is increased by at least 25%, preferably by at least 50%, relative respectively to the optimal or usual speed, length or residence time for obtaining a glass-ceramic substrate with a surface area less than 0.4 m 2 < .

[0062] As a reminder, the manufacture of glass-ceramic plates generally takes place as follows: in a melting furnace, the glass of the composition chosen to form the glass-ceramic is melted, then the molten glass is rolled into a standard ribbon or sheet by passing the molten glass between rolling rollers and the glass ribbon is cut to the desired dimensions. The plates thus cut are then ceramized in a manner known per se, ceramization consisting of firing the plates according to the chosen thermal profile to transform the glass into the polycrystalline material called "glass-ceramic" whose coefficient of expansion is zero or almost zero and which resists thermal shock of up to 700°C.Ceramization generally comprises a step of progressively raising the temperature to the nucleation range, generally located in the vicinity of the glass transformation range, a step of crossing the nucleation interval over several minutes, a further progressive rise in temperature to the temperature of the ceramization plateau, maintaining the temperature of the ceramization plateau for several minutes and then rapid cooling to room temperature. Where appropriate, the process also comprises a cutting operation (generally before ceramization), for example by water jet, mechanical tracing with a wheel, etc. followed by a shaping operation (grinding, beveling, etc.). The process may also comprise a rolling or collapsing step to form particular reliefs.

[0063] In this process, the glass ceramic follows a ceramization cycle giving it the desired properties, in particular a dark / black / brown appearance, with low transmissivity and low diffusion.

[0064] Other details and advantageous characteristics will emerge below from the description of a non-limiting embodiment of the invention with reference to the appended drawings in which: There figure 1 represents a schematic perspective view of equipment according to the invention; The figure 2 represents a schematic top view of similar equipment (surface utensils or underlying furniture elements not being shown); figure 3 represents a schematic side view in which a section of the furniture (23) has been removed to reveal certain components of the equipment.

[0065] In this example, the equipment (1) according to the invention comprises a piece of furniture (2) formed of a box (4) surmounted by a work surface (5) formed of at least one monolithic substrate (6) in vitroceramic with a surface area of ​​2.2 m 2 <. This substrate is for example a plate of the type marketed under the reference KeraBlack + by the company Eurokera, this plate having a smooth upper face and a lower face provided with studs, and a thickness of 4 mm, and having a brightness L * of 0.23, a haze of 0.75%, a light transmission TL of 1.34%, and an opacity indicator of 99.27. This substrate is for example obtained by proceeding as in patent application WO2012156444 but by reducing the speed of passage in the ceramization arch by 50%.

[0066] Alternatively, this substrate may also be, for example, a 1.1 m 2 < glass-ceramic plate of the type marketed under the reference KeraVision by the company Eurokera, this plate having a smooth upper face and a smooth lower face, and a thickness of 6 mm, and having a brightness L* of 1.08, a haze of 2.17%, a light transmission TL of 3.69%, and an opacity indicator of 95.69. This substrate is for example obtained by proceeding as in patent application WO2012001300 but by reducing the speed of passage in the ceramization arch by 50%.

[0067] The substrate used has a black color (in both cases mentioned above). In both cases, the glass-ceramic substrate obtained has a flatness of less than 2 mm (the flatness obtained being between 2 and 3 mm for a speed reduced by only 25%, and being more than 15 mm for a speed unchanged compared to that used in the aforementioned application to obtain a plate of standard dimensions less than 0.4 m 2 < ), the flatness sought for good optical properties and good thermal coupling and efficiency properties in particular, being less than 3 mm, preferably less than 2 mm.

[0068] The equipment further comprises in the present example three heating elements (7), for example inductors, arranged under the plate (6). These inductors are in the present case distributed in the middle of the work surface, but could just as easily be located at one end of the plane.

[0069] The equipment also comprises three light sources (8), intended to indicate the cooking locations, and placed under the substrate, these sources being hidden by the substrate when they are at rest. These sources make it possible to indicate the cooking locations, using for example a colored light circle (9) delimiting each location (the colors may be identical or different depending on the locations) and surrounding the inductors, when these sources are activated, or even when the heating elements are activated if the sources are connected to said elements by an appropriate interface. In the present case, the sources are offset laterally relative to the cooking zones (as indicated in figure 2 ), and the light is transmitted to the heating zones via a waveguide (10). This optical guide (10) is for example in the form of a 3 mm thick clear borosilicate glass plate and the sources (8) are formed for example of a plurality of LEDs carried by a base housed in a profile, the sources being located on a part of the edge of the guide outside the lighting zones and the heating zones, the article further comprising means for extracting the radiation emitted by the sources, these means being in the form of enamelled or sandblasted zones 11 each located under each of the desired lighting zones.

[0070] The equipment further comprises at least one communication interface (12) (hidden by the substrate) with the heating elements, and where appropriate with the light sources, this interface also communicating wirelessly with an external unit in the form, for example, of a touch pad (13) for activating different zones and functions of the hob or equipment. The external unit can advantageously be mobile and rest on the work surface ( figure 1 ) or serve for remote activation ( figure 3 ) of different areas or functions. Alternatively or cumulatively, the interface could also comprise or be connected to a fixed control strip located on the surface of the substrate (2) for the activation of different areas and functions, in particular of the substrate.

[0071] Where appropriate, the equipment may be associated with or also include an extractor hood (14) overhanging the work surface, this hood also being able to integrate at least one light source (8') for lighting the work surface or signaling the cooking zones (in particular in the latter case when the upper face of the substrate (6) is coated with an opaque enamel).

[0072] The equipment also comprises other elements, in particular electric cables (15) for activating the heating elements and for activating the sources, and comprises drawers (16) or cupboards (17) arranged in the box supporting the worktop, for the storage of various articles, etc. The equipment may also comprise other elements, for example the worktop may comprise a frame, the substrate may be coated with a permanent decoration, localized or not, for example enamel, the box may be solid or comprise different recesses (such as the recess (18), or integrate other elements (for example a built-in oven, etc.). The worktop (5) may serve different purposes, such as writing (as symbolized by the paper and pen (19)), supporting objects (as symbolized by the dishes (20)) while allowing the cooking of food (as symbolized by the cooking containers (21)), etc.If necessary, the box can also be replaced by support legs (for example only walls 22 and 23, or four legs at the four corners, the equipment under the worktop in this case being preferably hidden by localized formwork a few centimeters thick under the substrate) like a table.

[0073] The equipment according to the invention can in particular be used with advantages to create a new range of multi-use and interactive furniture integrating in particular cooking zones or a cooking function.

Claims

1. Item of furniture and / or appliance (1) comprising: - at least one worktop (5) formed from at least one substrate (6) made of a monolithic glazing material and of area larger than 0.7 m2, the glazing material having an opacity indicator higher than 93 and lower than 100, said substrate having a lightness L* lower than 10, a haze lower than 30% and a light transmission TL lower than 10%; - at least one heating element (7); - at least one light source (8), intended to light up one or more zones or one or more elements or displays of the substrate, this source being located under the substrate and being hidden thereby when this source is turned off; and - at least one interface for communicating (12) between a human and at least a machine selected from a light source and a heating element.

2. Item (1) according to claim 1, characterized in that the area of the substrate (6) made of a glazing material is larger than 0.9 m2, especially larger than 1 m2 and in particular at least 2 m2, the thickness of said substrate being at least 2 mm, especially at least 2.5 mm, and in particular about 3 to 30 mm, said thickness advantageously being smaller than 15 mm, in particular about 3 to 15 mm and especially from 3 to 10 mm.

3. Item (1) according to claim 1 or 2, characterized in that the substrate (6) has a geometrical shape selected from un square or a rectangle, the substrate having a flatness lower than 0.1% of a diagonal of the square substrate or of the rectangle substrate, and the flatness being preferably lower than 3 mm, especially lower than 2 mm and in particular lower than 1 mm or even of about zero.

4. Item (1) according to anyone of claims 1 to 3, characterized in that the substrate (6) is made of tempered glass or glass-ceramic and preferably is made of glass-ceramic.

5. Item (1) according to anyone of claims 1 to 4, characterized in that the substrate (6)is dark in appearance, and has a lightness L* lower than 5, a haze lower than 28%, and a light transmission TL lower than or equal to 5%6. Item (1) according to anyone of claims 1 to 5, characterized in that the item (1) comprises by way of heating element(s) (7) one or more inductive heating means, the one or more heating elements possibly being located in one or more zones of the substrate or being uniformly distributed under the substrate (6), for example occupying at least 25% of the area of the substrate, or occupying more than 50%, especially more than 75%, or even more than 85% of the area of the substrate.

7. Item (1) according to anyone of claims 1 to 6, characterized in that one or more cooking locations are signaled and / or revealed by means of the at least one light source (8), on activation of said source allowing a luminous display to be formed via the transmission of light through the worktop (5).

8. Item (1) according to anyone of claims 1 to 6, characterized in that the visible face of the substrate (6) is coated with an opacifying coating, in particular an enamel or thin films, the degree of coverage of said opacifying coating in the coated zone being at least 5%, preferably at least 20%, in particular at least 45% or even 100%, and the one or more cooking locations are signaled and / or revealed by means of at least one other light source (8), on activation of the one or more other source, said other source being located on the same side as the visible face of the substrate (6), or on the side on which the display is to be formed or from which it is intended to be viewed, and allowing a luminous display to be formed via projection onto this face, which forms a screen.

9. Item (1) according to claim 8, characterized in that the visible face of the substrate is coated with an enamel having a pigment content higher than 2%, in particular higher than 5%, preferably higher than 10%, especially comprised between 5 and 30%, and / or having a refractive index different from that of the substrate.

10. Item (1) according to anyone of claims 1 to 9, characterized in that the one or more light sources (8) are activatable via contact with the surface of the worktop and / or with the interface (12) and / or with an external system, or via a movement of the hand.

11. Item (1) according to anyone of claims 1 to 10, characterized in that the item furthermore comprises at least one waveguide, the light source (8) being attached to the waveguide.

12. Item (1) according to anyone of claims 1 to 11, characterized in that the item comprises at least one optical filter so as to form a colored luminous zone of a chosen color, this filter generally being placed between the source and the substrate and possibly being securely fastened to the source (8) and / or to the substrate (6) and / or optionally to another intermediate element.

13. Item (1) according to anyone of claims 1 to 12, characterized in that the interface (12) enables wireless communication, in particular with a system external to the worktop, for example allowing heating elements (7) and / or light sources (8) to be activated to be controlled remotely, the external system for example taking the form of a keyboard, a tablet or a touch screen (13) or a cellphone, this system possibly being fixedly mounted or movable, the wireless communication for example being of limited range, for example of range limited to the volume of the room in which the item is located.

14. Item (1) according to anyone of claims 1 to 13, characterized in that the item comprises one or more interfaces (12), of the same or different types, or allowing the activation of the heating zones to be coordinated with the activation of the light sources (8).

15. Item (1) according to anyone of claims 1 to 14, characterized in that the worktop (5) is mounted, in particular horizontally, on at least one or more than one supporting element, such as a carcass (4) of a unit (2) or one or more supporting legs, thus forming, with said supporting elements, a table, an optionally unapertured unit, or a counter.