TRACK FOR AN AIRCRAFT TIRE

Description

[0001] The present invention relates to an aircraft tire, and, in particular, to the tread of an aircraft tire.

[0002] An aircraft tire is characterized by use at high pressure, load, and speed. For example, an aircraft tire of size 46x17R20, intended for use on a commercial aircraft, can be used at a pressure equal to 15.3 bars, a static load equal to 21 tons, and a maximum speed equal to 360 km / h. Generally, an aircraft tire is used at a pressure greater than 9 bars and at a deflection rate of at least 32%. The operating pressure is defined, for example, by the Tire and Rim Association (TRA) standard. The deflection rate of a tire is, by definition, its radial deformation, or its variation in radial height, when it passes from an unloaded inflated state to a statically loaded inflated state, under the pressure and load conditions recommended, for example, by the TRA standard.It is expressed in the form of a relative arrow, defined by the ratio of this variation in the radial height of the tire to half the difference between the outside diameter of the tire and the maximum diameter of the rim measured on the rim flange. The outside diameter of the tire is measured statically in an unloaded state inflated to the recommended pressure.

[0003] A tire having a geometry of revolution with respect to an axis of rotation, the geometry of the tire is generally described in a meridian plane containing the axis of rotation of the tire. For a given meridian plane, the radial, axial and circumferential directions respectively designate the directions perpendicular to the axis of rotation of the tire, parallel to the axis of rotation of the tire and perpendicular to the meridian plane. The expressions "radially", "axially" and "circumferentially" mean respectively "in the radial direction", "in the axial direction" and "in the circumferential direction".

[0004] The tread is the part of the tire intended to come into contact with the ground via a rolling surface and extending radially from a base surface to the rolling surface, axially from a first edge to a second tread edge defining the axial width of the tread, and circumferentially over the entire periphery of the tire. By convention, the axial width of the tread is defined as the width of the contact area between the tread and the ground, measured along the axial line passing through the center of the contact area, when the new tire is subjected to the load and pressure conditions recommended by the TRA standard. The tread is generally made up of raised elements separated by hollows.In the case of an aircraft tire, the raised elements are most often continuous circumferential ribs over the entire circumference of the tire and separated by circumferential hollows or grooves. The tread, which is the wearing part of the tire, comprises at least one rubber composition, most often based on natural rubber and carbon black, these two main elements giving the rubber composition the mechanical properties necessary for the conditions of use of an aircraft tire. In addition to these main elements, such a rubber composition conventionally comprises a vulcanization system and protective agents.

[0005] Radially inside the tread, a radial tire comprises a reinforcing reinforcement, consisting of a crown reinforcement and a radial carcass reinforcement radially inside the crown reinforcement. The crown reinforcement comprises at least one crown layer consisting of reinforcing elements or reinforcements coated with an elastomeric mixture and parallel to each other. The radial carcass reinforcement comprises at least one carcass layer consisting of reinforcements coated with an elastomeric mixture, parallel to each other and oriented substantially radially, that is to say forming, with the circumferential direction, an angle of between 85° and 95°.The reinforcements of the crown and carcass layers, for aircraft tires, are most often textile reinforcements, made of aliphatic polyamide, such as nylon, aromatic polyamide, such as aramid, or a hybrid material combining, for example, an aliphatic polyamide and an aromatic polyamide.

[0006] On aircraft tires, the presence of non-uniform tread wear, called irregular wear, has been observed, resulting from stresses during the different phases of the tire's life: takeoff, taxiing and landing. In particular, differential wear of the tread between a middle part and the two lateral parts of the tread, axially external to the middle part, has been highlighted, with wear of this middle part being greater. Differential wear of the middle part of the tread leads to a limitation of the tire's life, and therefore of its use and its premature retirement, although the tread generally only shows relatively little wear on the lateral parts of the tread: this is penalizing from an economic point of view.

[0007] The person skilled in the art has identified two types of wear depending on the life phase of the tire. On landing, the middle part of the tread, having an axial width at least equal to 50% and at most equal to 80% of the total axial width of the tread and coming into contact with the ground, is subject to wear called "touch wear", resulting from significant thermal heating, at the moment the tread surface comes into contact with the ground, due to the speed differential between the rotation speed of the tire and the speed of the aircraft.During the taxiing phase or "taxi phase", before takeoff or after landing, the lateral parts of the tread, positioned axially on either side of the middle part and each having an axial width at least equal to 10% and at most equal to 25% of the total axial width of the tread, are subject to wear called "taxi wear", resulting from the braking forces exerted on these lateral parts due to their rotation speed being higher than that of the middle part. Thus the tread is mainly worn at its middle part, on landing, and at its lateral parts, during the taxi phase.

[0008] To solve the problem of irregular wear specific to aircraft tires, the skilled person sought, according to a first course of action, to optimize the inflated meridian profile of the tread surface, this meridian profile being the meridian section of the tread surface of a new tire inflated to its nominal pressure and unloaded, without taking into account the circumferential grooves. Optimizing this inflated meridian profile, that is to say its geometric shape, makes it possible to optimize the geometric shape of the contact surface of the tire with the ground and, consequently, the distribution of mechanical stresses in this contact surface and therefore to act on the wear of the tread.For example, documents EP 1 163 120, EP 1 381 525, EP 1 477 333 and EP 2 310 213 describe solutions aimed at optimizing the inflated profile of the rolling surface, by acting on the extension rigidities of the crown and / or carcass layers, or on differentials in extension rigidities between the middle part and the lateral parts of the crown layers, or even on an optimized crown layer profile with a concave middle part. All these solutions are based on changes in the material and / or geometry of the crown layers.

[0009] Another way of acting on the wear of an aircraft tire is the optimization of the rubber composition(s) constituting the tread. Indeed, wear also depends on the rubber composition(s) constituting the tread and their sensitivity to abrasion, characterized in particular by their cohesion, the cohesion depending on the chemical composition. WO 2017 / 017123 A1 proposes for example a rubber composition comprising a butadiene and styrene copolymer functionalized with tin.

[0010] The inventors set themselves the objective, compared to an aircraft tire of the state of the art, of increasing the resistance to touch wear of the middle part of the tread, during landing phases, while maintaining the same level of resistance to taxi wear of the lateral parts of the tread, during taxi phases, by acting on the rubber composition(s) of the various parts of the tread.

[0011] This objective has been achieved, according to the invention, by an aircraft tire comprising a tread having an axial width L, the tread comprising: a middle part having an axial width LC at least equal to 50% and at most equal to 80% of the axial width L of the tread and consisting of a middle rubber composition, and two lateral parts, positioned axially on either side of the middle part, each having an axial width at least equal to 10% and at most equal to 25% of the axial width L of the tread and each consisting of a lateral rubber composition, wherein the middle rubber composition comprises at least one elastomeric matrix, a reinforcing filler and a crosslinking system, said elastomeric matrix comprising from 25 to 85 phr of a tin-functionalized butadiene and styrene copolymer and from 15 to 75 phr of isoprene elastomer, the total content of isoprene elastomer and tin-functionalized butadiene and styrene copolymer in the middle rubber composition being in a range of from 45 to 100 phr, and wherein at least one lateral rubber composition is different from the middle rubber composition, and wherein the at least one lateral rubber composition comprises at least one diene elastomer, a reinforcing filler and a crosslinking system, wherein the diene elastomer predominantly comprises at least one isoprene elastomer. I- DEFINITIONS

[0012] The expression "composition based on" means a composition comprising the mixture and / or the reaction product in situ of the different constituents used, some of these constituents being able to react and / or being intended to react with each other, at least partially, during the different phases of manufacturing the composition; the composition thus being able to be in a totally or partially crosslinked state or in a non-crosslinked state.

[0013] By the expression "part by weight per hundred parts by weight of elastomer" (or pce), it is meant, within the meaning of the present invention, the part, by mass per hundred parts by mass of elastomer.

[0014] In this document, unless expressly stated otherwise, all percentages (%) indicated are percentages (%) by mass.

[0015] On the other hand, any interval of values ​​designated by the expression "between a and b" represents the range of values ​​from more than a to less than b (i.e., excluding the limits a and b), while any interval of values ​​designated by the expression "from a to b" means the range of values ​​from a to b (i.e., including the strict limits a and b). In this document, when describing an interval of values ​​by the expression "from a to b", the interval represented by the expression "between a and b" is also and preferably described.

[0016] When a "majority" compound is referred to, within the meaning of the present invention, this compound is the majority among the compounds of the same type in the composition, that is to say that it is the one which represents the greatest quantity by mass among the compounds of the same type. Thus, for example, a majority elastomer is the elastomer representing the greatest mass relative to the total mass of the elastomers in the composition. In the same way, a so-called majority filler is the one representing the greatest mass among the fillers in the composition. For example, in a system comprising a single elastomer, this is the majority within the meaning of the present invention; and in a system comprising two elastomers, the majority elastomer represents more than half of the mass of the elastomers.Preferably by majority, we mean present at more than 50%, preferably more than 60%, 70%, 80%, 90%, and more preferably the “majority” compound represents 100%.

[0017] The carbon-containing compounds mentioned in the description may be of fossil or bio-sourced origin. In the latter case, they may be, partially or totally, derived from biomass or obtained from renewable raw materials derived from biomass. This includes, in particular, polymers, plasticizers, fillers, etc.

[0018] All glass transition temperature “Tg” values ​​described herein are measured in a known manner by DSC (Differential Scanning Calorimetry) according to ASTM D3418 (1999). II- DESCRIPTION OF THE INVENTION II-I Tread and tire

[0019] The aircraft tire according to the invention comprises a tread having an axial width L, the tread comprising: a middle part having an axial width LC at least equal to 50% and at most equal to 80% of the axial width L of the tread and consisting of a middle rubber composition, and two lateral parts, positioned axially on either side of the middle part, each having an axial width at least equal to 10% and at most equal to 25% of the axial width L of the tread and each consisting of a lateral rubber composition.

[0020] It should be noted that the lateral portions of the tread may have different axial widths and / or have different lateral rubber compositions.

[0021] Preferably, the two lateral parts 41, 42, positioned axially on either side of the middle part 3, are different from the middle rubber composition. Advantageously, the two lateral parts 41, 42, positioned axially on either side of the middle part 3, are constituted by identical lateral rubber compositions and / or have identical axial widths (L S1 , L S2 ).

[0022] The tire according to the invention may advantageously comprise an interlayer 7 consisting of a rubber composition in contact via a radially outer face with at least the middle portion 3 of the tread 2 and via a radially inner face with the crown reinforcement 5. Contact of the radially outer face of the interlayer with at least the middle portion of the tread means that the axial width of this contact is at least equal to the axial width LC of the middle portion of the tread. Contact of the radially inner face of the interlayer with the crown reinforcement is contact with the protective reinforcement, which is the radially outermost part of the crown reinforcement intended to protect the working reinforcement, which is the radially innermost part of the crown reinforcement.This interlayer, also called a bonding layer, guarantees a better bond between the tread comprising a rubber composition according to the invention and the crown reinforcement.

[0023] The carcass reinforcement of an aircraft tire generally comprises a carcass reinforcement 6 consisting of a plurality of carcass layers extending between the two beads and distributed between a first and a second family.

[0024] The first family consists of carcass layers, wrapped, in each bead, from the inside to the outside of the tire, around a circumferential reinforcing element, called a bead wire, to form a turn-up whose end is generally radially outside the most radially outside point of the bead wire. The turn-up is the portion of carcass layer between the most radially inner point of the carcass layer and its end. The carcass layers of the first family are the carcass layers closest to the inner cavity of the tire and therefore the most axially inside, in the sidewalls.

[0025] The second family consists of carcass layers extending, in each bead, from the outside to the inside of the tire, up to a generally radially inner end at the most radially outer point of the bead wire. The carcass layers of the second family are the carcass layers closest to the outer surface of the tire and therefore the most axially outer, in the sidewalls.

[0026] Usually, the carcass layers of the second family are positioned, over their entire length, outside the carcass layers of the first family, that is to say they envelop, in particular, the turns of the carcass layers of the first family. Each carcass layer of the first and second families is made up of reinforcing elements parallel to each other, making, with the circumferential direction, an angle of between 80° and 100°.

[0027] The reinforcement elements of the carcass layers of an aircraft tire are most often cables made of textile filament yarns, preferably aliphatic polyamide or aromatic polyamide, and characterized by their mechanical properties in extension. The textile reinforcement elements are subjected to traction over an initial length of 400 mm at a nominal speed of 200 mm / min. All results are an average of 10 measurements.

[0028] The tire according to the invention may comprise a number of carcass layers ranging from 2 to 12, preferably from 5 to 10.

[0029] The tires according to the present invention can be used on any type of aircraft. They are particularly advantageous for aircraft using large tires. Indeed, the larger the size of an aircraft tire, the greater the impact of wear on landing on the overall wear of the tire. Thus, according to the invention, the tire can have a size greater than 18 inches, preferably 20 to 23 inches. II-2 Median rubber composition II-2-a Elastomeric matrix

[0030] According to the invention, the elastomeric matrix of the median rubber composition comprising from 25 to 85 parts by weight per hundred parts by weight of elastomer, pce, of a tin-functionalized butadiene and styrene copolymer and from 15 to 75 pce of isoprene elastomer, the total content of isoprene elastomer and tin-functionalized butadiene and styrene copolymer in the median rubber composition being within a range of from 45 to 100 pce.

[0031] The term "isoprene elastomer" is understood to mean, in a known manner, a homopolymer or copolymer of isoprene, in other words a diene elastomer chosen from the group consisting of natural rubber (NR), synthetic polyisoprenes (IR), various isoprene copolymers and mixtures of these elastomers. Among the isoprene copolymers, mention will be made in particular of isobutene-isoprene (butyl rubber - IIR), isoprene-styrene (SIR), isoprene-butadiene (BIR) or isoprene-butadiene-styrene (SBIR) copolymers. This isoprene elastomer is preferably natural rubber or a synthetic cis-1,4 polyisoprene, preferably natural rubber. For example, synthetic polyisoprene may be a polyisoprene having a rate (mol%) of cis-1,4 bonds greater than 90%, more preferably still greater than 98%.

[0032] The elastomers used in the context of the present invention may, for example, be block, random, sequenced, microsequenced, and may be prepared in dispersion or in solution; they may be coupled and / or star-shaped and / or functionalized with a coupling and / or star-shaped and / or functionalizing agent.

[0033] Preferably, according to the invention, the level of isoprene elastomer may be within a range from 20 to 70 phr, preferably from 20 to 65 or from 30 to 65 phr, preferably from 25 to 60 phr, preferably from 25 to 50 phr.

[0034] The isoprene elastomer may be selected from the group consisting of natural rubber, synthetic polyisoprene and their mixture. Preferably, the isoprene elastomer is natural rubber.

[0035] For the purposes of the present invention, a copolymer of butadiene units and styrene units is any copolymer obtained by copolymerization of one or more butadiene(s) with one or more styrene compounds. Suitable styrene compounds include, for example, styrene, ortho-, meta-, para-methylstyrene, the commercial mixture "vinyl-toluene", para-tert-butylstyrene, methoxystyrenes, chlorostyrenes, vinylmesitylene, divinylbenzene, vinylnaphthalene. These elastomers can have any microstructure which depends on the polymerization conditions used, in particular the presence or absence of a modifying and / or randomizing agent and the quantities of modifying and / or randomizing agent used. The elastomers can be, for example, block, random, sequenced, microsequenced, and can be prepared in dispersion or in solution.

[0036] The tin (Sn) functionalized butadiene and styrene copolymer, i.e. comprising C-Sn bonds (also called Sn functionalization), can be functionalized simply (C-Sn bonds at the end of the chain) and / or coupled (Sn atom between two chains) and / or star-shaped (Sn atom between 3 or more chains) with a functionalization and / or coupling and / or star-shaped agent. In a generic manner, all these elastomers linked to tin are referred to as tin-functionalized elastomers. These elastomers are known to those skilled in the art, for example those described in document WO 2011 / 042507.

[0037] Other types of functionalization exist for styrenic and butadiene copolymers, such as silanol or polysiloxane functional groups having a silanol end, or epoxidized styrenic and butadiene copolymers. Such functionalizations are possible within the scope of the present invention in addition to that with tin.

[0038] Those skilled in the art are well aware of the functionalizing and / or coupling and / or star-forming agents that can be used in the context of the present invention. As an example of a functionalizing agent, mention may be made of functionalizing agents derived from tin which may correspond to the general formula (X 1< 1 R 1< 2 Sn)-O-(SnR 1< 3-y X 1< y ) or (X 1< 1 R 1< 2 Sn)-O-(CH2) n -O-(SnR 1< 3-y X 1< y ), where y represents an integer of value 0 or 1, R 1< represents an alkyl, cycloalkyl, aryl, alkaryl or vinyl radical having from 1 to 12 carbon atoms, preferably a butyl, X 1< is a halogen atom, preferably chlorine, and n represents an integer from 1 to 20, preferably 4.Furthermore, as tin coupling or star-forming agents, mention may be made of tin derivatives of formula SnRxX 4 -x, x representing an integer of value 0 to 2, R representing an alkyl, cycloalkyl, aryl, alkaryl, aralkyl, vinyl radical having from 1 to 10 carbon atoms, preferably an alkyl radical having from 1 to 4 carbon atoms, and X is a halogen atom, preferably chlorine. As preferred tin derivatives, mention may be made of dibutyltin dichloride or tin tetrachloride, the latter being particularly preferred.

[0039] The tin-functionalized butadiene and styrene copolymer can be obtained in a manner known per se by reacting a tin derivative with the butadiene and styrene copolymer. The preparation of a star-shaped diene elastomer is for example described in US patent 3,393,182.

[0040] The tin-functionalized butadiene and styrene copolymer is preferably a random butadiene-styrene copolymer (SBR). This is then referred to as a tin-functionalized SBR (Sn-SBR). It may be, for example, an emulsion-prepared SBR ("ESBR") or a solution-prepared SBR ("SSBR"). Advantageously, the tin-functionalized butadiene and styrene copolymer is a solution-prepared butadiene-styrene copolymer (SSBR). The contents of (-1,2), trans-1,4 and cis-1,4 vinyl bonds in the butadiene part of the SBR may be variable. For example, the vinyl content may be between 15% and 80% (mol%), the content of trans-1,4 bonds between 15% and 80% (mol%).

[0041] Preferably, the tin-functionalized butadiene and styrenic copolymer is a low-styrene-content tin-functionalized butadiene and styrenic copolymer. The styrene content of the low-styrene-content tin-functionalized butadiene and styrenic copolymer may be in a range of 5 to 25%, preferably 5 to 20%, more preferably 10 to 19%.

[0042] Advantageously, the tin-functionalized butadiene and styrene copolymer has a glass transition temperature in the range from -70°C to -30°C.

[0043] Preferably, according to the invention, the content of tin-functionalized butadiene and styrene copolymer is within a range from 30 to 80 phr, preferably from 35 to 80 phr or from 35 to 70 phr, preferably from 40 to 75 phr, preferably from 50 to 75 phr.

[0044] The total content of isoprene elastomer and tin-functionalized butadiene and styrene copolymer may be 100 pce. In other words, according to this embodiment, the elastomeric matrix of the composition of the tread of the aircraft tire according to the invention comprises exclusively isoprene elastomer and tin-functionalized butadiene and styrene copolymer.

[0045] Alternatively, the total content of isoprene elastomer and tin-functionalized butadiene and styrene copolymer may also be within the range of 45 to less than 100 phr. In other words, according to this embodiment, the elastomeric matrix of the composition of the tread of the aircraft tire according to the invention comprises from more than 0 to 55 phr of another diene elastomer in addition to the isoprene elastomer and the tin-functionalized butadiene and styrene copolymer. The total content of isoprene elastomer and tin-functionalized butadiene and styrene copolymer may be, for example, within the range of 50 to less than 100 phr, preferably from 45 to 90 phr, preferably from 70 to 80 phr.

[0046] "Other diene elastomer" means a diene elastomer other than isoprene elastomer and tin-functionalized butadiene and styrenic copolymer.

[0047] By "diene" elastomer, one (meaning one or more) elastomers derived at least in part (i.e., a homopolymer or a copolymer) from diene monomers (monomers carrying two carbon-carbon double bonds, conjugated or not) must be understood in a known manner.

[0048] These diene elastomers are well known to those skilled in the art and the term diene elastomer capable of being used in the compositions is understood more particularly to mean: any homopolymer obtained by polymerization of a conjugated diene monomer having from 4 to 12 carbon atoms; any copolymer obtained by copolymerization of one or more conjugated dienes with each other or with one or more aromatic vinyl compounds having from 8 to 20 carbon atoms.

[0049] Suitable conjugated dienes include, in particular, 1,3-butadiene, 2-methyl-1,3-butadiene, 2,3-di(C 1 -C 5 alkyl)-1,3-butadienes such as, for example, 2,3-dimethyl-1,3-butadiene, 2,3-diethyl-1,3-butadiene, 2-methyl-3-ethyl-1,3-butadiene, 2-methyl-3-isopropyl-1,3-butadiene, aryl-1,3-butadiene, 1,3-pentadiene, 2,4-hexadiene. Suitable vinyl aromatic compounds are, for example, styrene, ortho-, meta-, para-methylstyrene, the commercial mixture "vinyl-toluene", para-tert-butylstyrene, methoxystyrenes, vinylmesitylene, divinylbenzene, vinylnaphthalene.

[0050] Preferably, according to this embodiment of the invention, the other diene elastomer may be chosen from the group comprising or consisting of non-tin-functionalized butadiene and styrene copolymers, polybutadienes and their mixtures.

[0051] The non-tin-functionalized butadiene-styrene copolymer may be, for example, butadiene-styrene copolymer (SBR). It may be, for example, an emulsion-prepared SBR ("ESBR") or a solution-prepared SBR ("SSBR"). The contents of (-1,2), trans-1,4 and cis-1,4 vinyl bonds in the butadiene part of the SBR may be variable. For example, the vinyl content may be between 15% and 80% (mol%), the content of trans-1,4 bonds between 15% and 80% (mol%).

[0052] Preferably, according to this embodiment of the invention, the other diene elastomer mainly comprises a polybutadiene.

[0053] Preferably, the polybutadiene may be, for example, a polybutadiene comprising predominantly cis-1,4 bonds. It may be, for example, a composite polybutadiene comprising 5 to 25% of syndiotactic 1,2-polybutadiene in a cis-1,4-polybutadiene matrix, for example “VCR412 UBEPOL” from the company UBE, comprising 12% of syndiotactic 1,2-polybutadiene in a cis-1,4-polybutadiene matrix.

[0054] The rate of the other diene elastomer may depend on the nature of this other diene elastomer. This rate may be within a range from more than 0 to 50 pce, preferably from 10 to 55 pce, preferably from 20 to 30 pce.

[0055] In particular, when the other diene elastomer mainly comprises a polybutadiene mainly comprising cis-1,4 bonds, the level of diene elastomer can be in a range from 10 to 30 pce, preferably from 15 to 25 pce.

[0056] When the other diene elastomer mainly comprises composite polybutadiene comprising 5 to 25% of syndiotactic 1,2-polybutadiene in a cis-1,4-polybutadiene matrix, the level of the other diene elastomer is in a range from 10 to 55 phr, preferably from 30 to 55 phr, preferably from 40 to 55 phr, preferably from 45 to 50 phr. II-2-b Reinforcing charge

[0057] The middle rubber composition of the tread of the tire according to the invention further comprises a reinforcing filler, known for its ability to reinforce a rubber composition usable for the manufacture of tires.

[0058] The reinforcing filler may comprise carbon black and / or a reinforcing inorganic filler (preferably silica). Advantageously, the reinforcing filler comprises mainly, preferably exclusively, carbon black.

[0059] The blacks that can be used in the context of the present invention can be any black conventionally used in tires or their treads (so-called tire-grade blacks). Among the latter, mention will be made more particularly of reinforcing carbon blacks of the 100, 200, 300 series, or blacks of the 500, 600 or 700 series (ASTM grades), such as for example blacks N115, N134, N234, N326, N330, N339, N347, N375, N550, N683, N772). These carbon blacks can be used in the isolated state, as commercially available, or in any other form, for example as a support for certain of the rubber additives used. Carbon blacks could, for example, already be incorporated into the diene elastomer, in particular isoprene, in the form of a masterbatch (see, for example, applications WO 97 / 36724 or WO 99 / 16600).

[0060] Examples of organic fillers other than carbon blacks include functionalized polyvinyl organic fillers as described in applications WO 2006 / 069792, WO 2006 / 069793, WO 2008 / 003434 and WO 2008 / 003435.

[0061] Advantageously, the carbon black comprises predominantly, preferably exclusively, a carbon black having a BET specific surface area of ​​less than or greater than 80 m 2 < / g, preferably within a range of between 80 and 170 m 2 < / g, more preferably between 120 and 145 m 2 < / g.

[0062] The BET specific surface area of ​​carbon blacks is measured according to standard D6556-10 [multi-point method (minimum 5 points) - gas: nitrogen - relative pressure range P / P0: 0.1 to 0.3].

[0063] By "reinforcing inorganic filler" is meant here any inorganic or mineral filler, whatever its color and origin (natural or synthetic), also called "white" filler, "light" filler or even "non-black" filler as opposed to carbon black, capable of reinforcing on its own, without any other means than an intermediate coupling agent, a rubber composition intended for the manufacture of pneumatic tires, in other words capable of replacing, in its reinforcing function, a conventional tire-grade carbon black; such a filler is generally characterized, in a known manner, by the presence of hydroxyl groups (-OH) on its surface.

[0064] The physical state in which the reinforcing inorganic filler is present is indifferent, whether in the form of powder, microbeads, granules, beads or any other suitable densified form. Of course, the term reinforcing inorganic filler also means mixtures of different reinforcing inorganic fillers, in particular highly dispersible siliceous and / or aluminous fillers as described below.

[0065] Suitable reinforcing inorganic fillers are, in particular, mineral fillers of the siliceous type, preferably silica (SiO 2 ). The silica used may be any reinforcing silica known to those skilled in the art, in particular any precipitated or pyrogenic silica having a BET surface area and a CTAB specific surface area both less than 450 m2 / g, preferably from 30 to 400 m2 / g, in particular between 60 and 300 m2 / g.

[0066] The silicas or other reinforcing inorganic fillers that can be used in the context of the present invention may be any silica known to those skilled in the art, in particular any precipitated or pyrogenic silica having a BET surface area and a CTAB specific surface area both less than 450 m2 / g, preferably from 30 to 400 m2 / g.

[0067] The BET specific surface area of ​​silica or reinforcing inorganic fillers is determined in a known manner by gas adsorption using the Brunauer-Emmett-Teller method described in "The Journal of the American Chemical Society" Vol. 60, page 309, February 1938, more precisely according to the French standard NF ISO 9277 of December 1996 (multipoint volumetric method (5 points) - gas: nitrogen - degassing: 1 hour at 160°C - relative pressure range p / po: 0.05 to 0.17). The CTAB specific surface area of ​​silica is determined according to the French standard NF T 45-007 of November 1987 (method B).

[0068] Preferably, the reinforcing inorganic filler, preferably silica, has a BET specific surface area of ​​less than 200 m 2 < / g and / or a CTAB specific surface area of ​​less than 220 m 2 < / g, preferably a BET specific surface area in a range from 125 to 200 m 2 < / g and / or a CTAB specific surface area in a range from 140 to 170 m 2 < / g.

[0069] Examples of reinforcing inorganic fillers that can be used in the context of the present invention include the highly dispersible precipitated silicas (known as "HDS") "Ultrasil 7000" and "Ultrasil 7005" from the company Evonik, the silicas "Zeosil 1165MP, 1135MP and 1115MP" from the company Rhodia, the silica "Hi-Sil EZ150G" from the company PPG, the silicas "Zeopol 8715, 8745 and 8755" from the company Huber, the silicas with a high specific surface area as described in application WO 03 / 16837.

[0070] To couple the reinforcing silica to the diene elastomer, an at least bifunctional coupling agent (or bonding agent) is used in a well-known manner, intended to ensure a sufficient connection, of a chemical and / or physical nature, between the silica (surface of its particles) and the diene elastomer. In particular, at least bifunctional organosilanes or polyorganosiloxanes are used.

[0071] The skilled person can find examples of coupling agent in the following documents: WO 02 / 083782, WO 02 / 30939, WO 02 / 31041, WO 2007 / 061550, WO 2006 / 125532, WO 2006 / 125533, WO 2006 / 125534, US 6,849,754, WO 99 / 09036, WO 2006 / 023815, WO 2007 / 098080, WO 2010 / 072685 and WO 2008 / 055986.

[0072] Mention may be made in particular of alkoxysilane-polysulfide compounds, in particular bis-(trialkoxylsilylpropyl) polysulfides, especially bis 3-triethoxysilylpropyl disulfide (abbreviated as "TESPD") and bis 3-triethoxysilylpropyl tetrasulfide (abbreviated as "TESPT"). It should be remembered that TESPD, of formula [(C 2 H 5 O) 3 Si(CH 2 ) 3 S] 2 , is notably marketed by the company Degussa under the names Si266 or Si75 (in the second case, in the form of a mixture of disulfide (75% by weight) and polysulfides). TESPT, of formula [(C 2 H 5 O) 3 Si(CH 2 ) 5 S 2 ] 2 is marketed in particular by the company Degussa under the name Si69 (or X50S when it is supported at 50% by weight on carbon black), in the form of a commercial mixture of polysulfides Sx with an average value for x which is close to 4.

[0073] The level of reinforcing filler, preferably carbon black, in the composition is preferably within a range from 20 to 100 phr, preferably from 25 to 75 phr, more preferably from 30 to 70 phr.

[0074] Furthermore, the level of reinforcing inorganic filler, preferably silica, in the composition is within a range from 0 to 20 pce, preferably from 1 to 15 pce. II-2-c Crosslinking system

[0075] The crosslinking system of the middle rubber composition of the tire tread according to the invention may be based on molecular sulfur and / or sulfur and / or peroxide donors, well known to those skilled in the art.

[0076] The crosslinking system is preferably a sulfur-based vulcanization system (molecular sulfur and / or sulfur donor agent).

[0077] Sulphur is used at a preferential rate of between 0.5 and 10 pce. Advantageously, the sulphur rate is between 0.5 and 2 pce, preferably between 0.5 and 1.5 pce, more preferably between 0.5 and 1.4 pce.

[0078] The composition of the outer sidewall of the tire according to the invention advantageously comprises a vulcanization accelerator, which is preferably chosen from the group consisting of thiazole type accelerators and their derivatives, sulfenamide type accelerators, thiourea type accelerators and their mixtures. Advantageously, the vulcanization accelerator is chosen from the group consisting of 2-mercaptobenzothiazyl disulfide (MBTS), N-cyclohexyl-2-benzothiazyl sulfenamide (CBS), N,N-dicyclohexyl-2-benzothiazyl sulfenamide (DCBS), N-tert-butyl-2-benzothiazyl sulfenamide (TBBS), N-tert-butyl-2-benzothiazyl sulfenimide (TBSI), morpholine disulfide, N-morpholino-2-benzothiazyl sulfenamide (MBS), dibutylthiourea (DBTU), and their mixtures. Particularly preferably, the primary vulcanization accelerator is N-cyclohexyl-2-benzothiazyl sulfenamide (CBS).

[0079] The vulcanization accelerator content is preferably within a range of 0.2 to 10 pce, preferably 0.5 to 2 pce, preferably between 0.5 and 1.5 pce, more preferably between 0.5 and 1.4 pce. II-2-d Plasticizers

[0080] Advantageously, the middle rubber composition of the tread of the tire according to the invention may comprise from 1 to 30 pce of a plasticizing resin mainly composed of units derived from aromatic and cycloaliphatic monomers. This resin is also called aromatic / cycloaliphatic resin in the following.

[0081] Plasticizing resins in general are known to those skilled in the art. They are also sometimes called hydrocarbon resins or high glass transition temperature resins.

[0082] In a manner known to those skilled in the art, the term "plasticizing resin" is reserved in the present application, by definition, for a compound which is on the one hand solid at room temperature (23°C) (as opposed to a liquid plasticizing compound such as an oil).

[0083] Hydrocarbon resins are polymers well known to those skilled in the art, miscible by nature in diene elastomer compositions when they are also described as "plasticizers". They have been described for example in the work entitled " Hydrocarbon Resins" by R. Mildenberg, M. Zander and G. Collin (New York, VCH, 1997, ISBN 3-527-28617-9) of which chapter 5 is devoted to their applications, notably in pneumatic rubber (5.5. "Rubber Tires and Mechanical Goods"). They can be aliphatic, aromatic or aliphatic / aromatic, i.e. based on aliphatic and / or aromatic monomers. They can be natural or synthetic, petroleum-based or not (if this is the case, also known as petroleum resins). They are preferably exclusively hydrocarbon-based, i.e. they only contain carbon and hydrogen atoms.

[0084] The specific resin for the invention is mainly composed of units derived from aromatic and cycloaliphatic monomers.

[0085] By cycloaliphatic monomers, according to the present invention and conventionally for those skilled in the art, are meant saturated cyclic monomers and the monomers will preferably be chosen from the group consisting of cyclopentadiene (abbreviated CPD), dicyclopentadiene (abbreviated DCPD) and their mixtures.

[0086] As aromatic monomers, monomers from the group consisting of styrene, alpha-methyl styrene, vinyl toluene, indene and their mixtures will preferably be chosen.

[0087] Thus, preferably, the hydrocarbon resin composed mainly of units derived from aromatic and cycloaliphatic monomers is such that the cycloaliphatic monomers are chosen from the group consisting of cyclopentadiene, dicyclopentadiene and their mixtures, and the aromatic monomers are chosen from the group consisting of styrene, alpha-methyl styrene, vinyl toluene, indene and their mixtures. More preferably, the aromatic monomer is styrene.

[0088] The resin useful for the purposes of the invention, mainly composed of units derived from aromatic and cycloaliphatic monomers, may comprise, in addition to these units, and to a minor extent, aliphatic units, that is to say based on aliphatic monomers, other than cycloaliphatic monomers. As such, the resin may comprise, to a minor extent, units derived from olefinic monomers.

[0089] The aromatic / cycloaliphatic resin preferably has an aromatic proton content in the range of 3 to 40%, preferably 5 to 30%. It also preferably has an ethylenic proton content in the range of 2 to 15%, preferably 3 to 10%.

[0090] Also preferably, the aromatic / cycloaliphatic resin has an ethylenic proton content in a range from 2 to 15%, preferably from 3 to 10%.

[0091] According to a preferred embodiment, the hydrocarbon resin useful for the purposes of the invention has a glass transition temperature (Tg) within a range from 30°C to 150°C, preferably from 30 to 120°C.

[0092] The hydrocarbon resin useful for the purposes of the invention has an average molecular mass Mn within a range from 300 g / mol to 3000 g / mol and preferably from 400 to 1500 g / mol.

[0093] Preferably, the hydrocarbon resin useful for the purposes of the invention has a polymolecularity index (PMI) in a range from 1 to 4, and preferably from 1.5 to 3.5.

[0094] There are many hydrocarbon resins available commercially. These resins can have characteristics, including chemical composition, Tg, Mn, aromatic proton content, ethylenic proton content, or Ip, which vary depending on the supplier. Examples of aromatic / cycloaliphatic plasticizing resins include commercial resins such as “Novares TC160” (Mn=710g / mol; Mw=2000g / mol; Ip=2.8, Tg=106°C), “Novares TC100” (Mn=460g / mol; Mw=840g / mol; Ip=1.8, Tg=42°C) marketed by Rütgers, “QUINTONE 2940” resins (Mn=560g / mol, Mw=1400g / mol, Ip=2.5, Tg=77°C), marketed by Nippon Zeon, and “LX1200-130” resin marketed by Neville (Mn=660g / mol, Mw=1900g / mol, Ip=2.8, Tg=60°C)

[0095] The macrostructure (Mw, Mn, Ip and Mz) of the hydrocarbon resin is determined by size exclusion chromatography (SEC) based on ISO 16014 (Determination of average molecular mass and molecular mass distribution of polymers using size exclusion chromatography), ASTM D5296 (Molecular Weight Averages and molecular weight distribution of polystyrene by High performance size exclusion chromatography), and DIN 55672 (size exclusion chromatography).

[0096] For these measurements, the resin sample is solubilized in non-antioxidized tetrahydrofuran to a concentration of 1.5 g / l. The solution is filtered with a 0.45 µm porosity Teflon filter, using for example a disposable syringe fitted with a filter. A volume of 100 µl is injected through a set of size exclusion chromatography columns. The mobile phase is eluted with a flow rate of 1 ml / min. The columns are thermostated in an oven at 35°C. Detection is ensured by a refractometer thermostated at 35°C. The stationary phase of the columns is based on a polystyrene divinylbenzene gel with controlled porosity. Polymer chains are separated according to the size they occupy when solubilized in the solvent: the larger the volume they occupy, the less accessible the pores of the columns are to them and the shorter their elution time.

[0097] A Moore calibration curve linking the logarithm of the molar mass (logM) to the elution time (te) is previously produced with polystyrene standards, and modeled by a polynomial of order 3: Log (molar mass of polystyrene) = a + b te + c te2 + d te3.

[0098] For the calibration curve, polystyrene standards with narrow molecular distributions (polydispersity index, Ip, less than or equal to 1.1) are used. The molar mass range of these standards extends from 160 to approximately 70,000 g / mol. These standards can be grouped into "families" of 4 or 5 standards with an increment of approximately 0.55 in log of M between each.

[0099] Certified standard kits (ISO 13885 and DIN 55672) can be used, such as the vial kits from PSS (polymer standard service, reference PSS-pskitr1l-3), as well as an additional PS standard of Mp = 162 g / mol (Interchim, reference 178952). These kits come in the form of 3 vials, each containing a family of standard polystyrene in suitable quantities: Black vial: Mp = 1,220, 4,850, 15,500 and 67,500 g / mol. Blue vial: Mp = 376, 3,470, 10,400, 46,000 g / mol. Yellow vial: Mp = 266, 1,920, 7,200, 28,000 g / mol. PS162: Mp = 162 g / mol

[0100] The number-average molar masses (Mn), mass-average molar masses (Mw), Mz, and polydispersity of the analyzed resin are calculated from this calibration curve. This is why we speak of molar masses relative to a polystyrene calibration.

[0101] To calculate the average masses and the Ip, the integration limits of the product elution are defined on the chromatogram corresponding to the injection of the sample. The refractometric signal defined between the 2 integration limits is "cut" every second. For each of the "elementary cuts", the elution time ti and the area of ​​the detector signal Ai are recorded.

[0102] We recall here that: Ip = Mw / Mn with Mw average molecular mass in weight, and Mn molecular mass in number. We also recall that the masses Mw, Mn and Mz are average masses calculated according to the formulas below: Mz = ∑ Ai ∗ Mi 2 ∑ Ai ∗ Mi Mn = ∑ Ai ∑ Ai Mi Mw = ∑ Ai ∗ Mi ∑ Ai in which Ai is the amplitude of the refractometric detector signal corresponding to the mass Mi and the elution time ti.

[0103] The equipment used for SEC measurement is a liquid chromatography chain, for example the WATERS Alliance 2690 chain comprising a pump, a degasser and an injector; a differential refractometer (for example the WATERS 2410 refractometer), data acquisition and processing software, for example the WATERS EMPOWER software, a column oven, for example the WATERS “columns Heater Module” and 4 columns connected in series in the following order: Table 1 Number Brand Molar mass range (g / mol) Length (mm) Internal diameter (mm) Particle size s (µm) Trade name References (for information purposes only) Columns 1 and 2 Polymer Laboratories 200 - 400000 300 7,5 5 MIXED-D PL1110-6504 Columns 3 and 4 Polymer Laboratories 200 - 30000 300 7,5 3 MIXED-E PL1110-6300

[0104] The aromatic proton rate (%HA) and the ethylenic proton rate (%HE) are measured by 1H NMR. This determination is carried out relative to all the detected signals. Thus, the results obtained are expressed in % of peak area.

[0105] Samples are solubilized in deuterated chloroform (CDCl3) at a rate of approximately 10 mg of resin in approximately 1 mL of solvent. Spectra are acquired on a Bruker Avance 500 MHz spectrometer equipped with a Bruker BBO z-grad 5 mm broadband probe. The 1H NMR experiment uses a single 30° pulse sequence and a 5-second repetition delay between each acquisition. 64 accumulations are performed at room temperature. Chemical shifts are calibrated relative to the protonated impurity of deuterated chloroform; δppm 1H at 7.20 ppm. The 1H NMR signals of aromatic protons are located between 8.5 ppm and 6.2 ppm. Ethylene protons generate signals between 6.2 ppm and 4.5 ppm. Finally, the signals corresponding to aliphatic protons are located between 4.5 ppm and 0 ppm. The areas of each category of protons are reported to the sum of these areas to give a distribution in % of area of ​​each category of protons.

[0106] The rate of aromatic / cycloaliphatic resin is preferably within a range of 2 to 30 pce, more preferably 2 to 15 pce.

[0107] Preferably for the invention, the composition of the tread of the aircraft tire of the invention does not comprise any resin other than the C5 resin described above.

[0108] Examples of aromatic / cycloaliphatic plasticizing resins include commercial resins such as “Novares TC160” (Mn=710g / mol; Mw=2000g / mol; Ip=2.8, Tg=106°C), “Novares TC100” (Mn=460g / mol; Mw=840g / mol; Ip=1.8, Tg=42°C) marketed by the company Rütgers.

[0109] According to a particular embodiment, the plasticizing resin mainly composed of units derived from aromatic and cycloaliphatic monomers has an aromatic proton content of between 0 and 12%, an ethylenic proton content greater than 3%, a number average molecular mass greater than 500 g / mol and a polymolecularity index greater than 2.

[0110] According to this embodiment, the aromatic / cycloaliphatic resin has an aromatic proton content of between 0 and 12%, preferably an aromatic proton content in a range from 1 to 10%, preferably from 2 to 7%.

[0111] Furthermore, according to this embodiment, the aromatic / cycloaliphatic resin has an ethylenic proton level greater than 3%, preferably an ethylenic proton level within a range of 3 to 7%.

[0112] According to this embodiment, the hydrocarbon resin useful for the purposes of the invention can advantageously have a glass transition temperature (Tg) within a range from 30°C to 150°C, preferably from 30 to 120°C.

[0113] Still according to this embodiment, the hydrocarbon resin useful for the needs of the invention can advantageously have a number-average molecular mass (Mn) greater than 500 g / mol, preferably within a range from 500 g / mol to 1500 g / mol and preferably from 500 to 1000 g / mol.

[0114] According to this embodiment, the hydrocarbon resin useful for the purposes of the invention can advantageously have a polymolecularity index (PMI) greater than 2, preferably within a range from 2 to 5, and preferably from 3 to 4.5.

[0115] According to this embodiment, the hydrocarbon resin composed mainly of units derived from aromatic and cycloaliphatic monomers, advantageously also comprises units derived from pine derivatives, preferentially chosen from the group consisting of alphapinene, betapinene, rosin, turpentine, tall oil and mixtures thereof. According to this preferred embodiment, the resin is also preferentially modified with maleic anhydride.

[0116] As an example of aromatic / cycloaliphatic plasticizing resins meeting this embodiment, we can cite in particular the DCPD / Aromatic hydrocarbon resin “Nevroz 1420” from the Neville company.

[0117] Advantageously, whatever the embodiment of the present invention, the median rubber composition comprises 0 to 20 pce of a liquid plasticizer.

[0118] A plasticizer is considered liquid when, at 23°C, it has the capacity to eventually take the shape of its container, this definition being given in contrast to plasticizing resins which are by nature solid at room temperature. Examples of liquid plasticizers include vegetable oils, mineral oils, ether, ester, phosphate, sulfonate plasticizers and their mixtures.

[0119] Preferably, the liquid plasticizer level of the median rubber composition is equal to 0. II-2-e Various additives

[0120] The rubber compositions of the tire tread according to the invention may optionally also comprise all or part of the usual additives usually used in elastomer compositions for tires, such as for example plasticizers (such as plasticizing oils and / or plasticizing resins), pigments, protective agents such as anti-ozone waxes, chemical anti-ozonants, antioxidants, anti-fatigue agents, reinforcing resins (as described for example in application WO 02 / 10269). II-3 Lateral rubber composition

[0121] According to the invention, at least one lateral rubber composition is different from the middle rubber composition. The difference is advantageously linked to the absence of tin-functionalized butadiene and styrene copolymer, or by its presence at a rate of less than 25 pce.

[0122] Thus, advantageously, the lateral rubber composition does not comprise tin-functionalized butadiene and styrene copolymer, or comprises less than 25 phr, preferably less than 15 phr, more preferably less than 10 phr. In a particularly advantageous manner, the lateral rubber composition does not comprise tin-functionalized butadiene and styrene copolymer.

[0123] The at least one lateral rubber composition comprises at least one diene elastomer, a reinforcing filler and a crosslinking system, wherein the diene elastomer predominantly comprises at least one isoprene elastomer.

[0124] Particularly advantageously, the lateral rubber composition comprises more than 85 phr, preferably at least 90 phr of at least one isoprene elastomer. More preferably, it comprises 100 phr of at least one isoprene elastomer.

[0125] The isoprene elastomer of the lateral rubber composition may be selected from the group consisting of natural rubber, synthetic polyisoprenes and mixtures thereof. Preferably the at least one isoprene elastomer of the lateral rubber composition is a natural rubber.

[0126] The lateral rubber composition also advantageously comprises one or more reinforcing fillers, preferably chosen from carbon blacks, silicas and their mixtures, preferably at a rate in a range from 20 to 200 phr, preferably from 20 to 70 phr, more preferably from 40 to 55 phr. Advantageously, the reinforcing filler comprises mainly, preferably exclusively, carbon black. The carbon black of the lateral rubber composition advantageously has a BET specific surface area of ​​less than or greater than 80 m 2 / g, preferably in a range between 80 and 170 m 2 / g, more preferably between 120 and 145 m 2 / g.

[0127] The lateral rubber composition advantageously comprises a crosslinking system based on molecular sulfur and / or sulfur donors and / or peroxide, preferably based on molecular sulfur and / or sulfur donors, preferably at a rate of between 0.5 and 12 pce, preferably between 1 and 10 pce.

[0128] Finally, the lateral rubber composition may comprise all or part of the usual additives usually used in elastomer compositions for tires such as those previously mentioned. II-4 Rubber composition of the interlayer

[0129] The tire comprising a crown reinforcement radially inside the tread, the tire advantageously comprises an interlayer consisting of a rubber composition in contact by a radially outer face with at least the middle portion of the tread and by a radially inner face with the crown reinforcement. Contact of the radially outer face of the interlayer with at least the middle portion of the tread means that the axial width of this contact is at least equal to the axial width LC of the middle portion of the tread. Contact of the radially inner face of the interlayer with the crown reinforcement is contact with the protective reinforcement, which is the radially outermost part of the crown reinforcement intended to protect the working reinforcement, which is the radially innermost part of the crown reinforcement.This interlayer, also called a bonding layer, guarantees a better bond between the tread comprising a rubber composition according to the invention and the crown reinforcement.

[0130] The interlayer advantageously comprises at least one diene elastomer, a reinforcing filler and a crosslinking system, wherein the diene elastomer predominantly comprises at least one isoprene elastomer.

[0131] Particularly advantageously, the interlayer is as defined, preferably identical to, the lateral rubber composition of the tread of the tire according to the invention.

[0132] The interlayer may thus comprise more than 85 pce, preferably at least 90 pce of at least one isoprene elastomer. More preferably, it comprises 100 pce of at least one isoprene elastomer.

[0133] The isoprene elastomer of the interlayer may be selected from the group consisting of natural rubber, synthetic polyisoprenes and their mixtures. Preferably, the at least one isoprene elastomer of the interlayer is a natural rubber.

[0134] The interlayer also advantageously comprises one or more reinforcing fillers, preferably chosen from carbon blacks, silicas and their mixtures, preferably at a rate within a range from 20 to 200 phr, preferably from 20 to 70 phr, more preferably from 40 to 55 phr. Advantageously, the reinforcing filler comprises mainly, preferably exclusively, carbon black.

[0135] The interlayer advantageously comprises a crosslinking system based on molecular sulfur and / or sulfur donors and / or peroxide, preferably based on molecular sulfur and / or sulfur donors, preferably at a rate of between 0.5 and 12 pce, preferably between 1 and 10 pce.

[0136] Finally, the interlayer may comprise all or part of the usual additives usually used in elastomer compositions for tires such as those previously mentioned. II-5 Preparation of rubber compositions

[0137] The medial and lateral rubber compositions of the tread and the composition of the interlayer of the tire according to the invention can be manufactured in suitable mixers, using two successive preparation phases well known to those skilled in the art: a first phase of working or thermomechanical mixing (so-called "non-productive" phase), which can be carried out in a single thermomechanical step during which all the necessary constituents are introduced into a suitable mixer such as a conventional internal mixer (for example of the 'Banbury' type), in particular the elastomeric matrix, the reinforcing filler, any other various additives, with the exception of the crosslinking system. The incorporation of the possible filler into the elastomer can be carried out in one or more stages by thermomechanical mixing.In the case where the filler is already incorporated in whole or in part into the elastomer in the form of a masterbatch as described for example in applications WO 97 / 36724 or WO 99 / 16600, it is the masterbatch which is directly mixed and where appropriate the other elastomers or fillers present in the composition which are not in the form of a masterbatch are incorporated, as well as any other various additives other than the crosslinking system. The non-productive phase can be carried out at high temperature, up to a maximum temperature of between 110°C and 200°C, preferably between 130°C and 185°C, for a duration generally of between 2 and 10 minutes.a second phase of mechanical work (so-called "productive" phase), which is carried out in an external mixer such as a cylinder mixer, after cooling the mixture obtained during the first non-productive phase to a lower temperature, typically below 120°C, for example between 40°C and 100°C. The crosslinking system is then incorporated, and everything is then mixed for a few minutes, for example between 5 and 15 min.

[0138] Such phases have been described for example in applications EP-A-0501227, EP-A-0735088, EP-A-0810258, WO00 / 05300 or WO00 / 05301.

[0139] The final composition thus obtained is then calendered, for example, in the form of a sheet or plate, in particular for characterization in the laboratory, or extruded (or co-extruded with another rubber composition) in the form of a semi-finished (or profiled) rubber product usable, for example, as a tire tread. These products can then be used for the manufacture of tires, according to techniques known to those skilled in the art.

[0140] The composition can be either in the raw state (before crosslinking or vulcanization), or in the cooked state (after crosslinking or vulcanization), can be a semi-finished product which can be used in a tire.

[0141] The crosslinking of the composition can be carried out in a manner known to those skilled in the art, for example at a temperature between 130°C and 200°C, under pressure. III- BRIEF DESCRIPTION OF THE FIGURES

[0142] There figure 1, not shown to scale to facilitate understanding, presents a sectional view in a meridian plane of the crown of an aircraft tire according to the invention, comprising radially from the outside to the inside a tread 2, a crown reinforcement 5 and a carcass reinforcement 6. The tread 2 having an axial width L comprises a middle portion 3, having an axial width LC at least equal to 50% and at most equal to 80% of the axial width L of the tread and consisting of a middle rubber composition, and two lateral portions 41, 42, positioned axially on either side of the middle portion 3, each having an axial width (L S1 , L S2 ) at least equal to 10% and at most equal to 25% of the axial width L of the tread and each consisting of a lateral rubber composition. figure 2shows a sectional view in a meridian plane of the crown of an aircraft tire according to a particular embodiment of the invention, in which the tire 1 also comprises an intermediate layer 7 consisting of a rubber composition in contact via a radially outer face with the tread 2 and via a radially inner face with the crown reinforcement 5. V- EXAMPLES V-1 Measures and tests used Tensile tests (Examples 1 and 2)

[0143] These tensile tests allow the determination of the elastic moduli and the properties at break and are based on the NF ISO 37 standard of December 2005 on a type 2 dumbbell test piece. The elongation at break thus measured at 60°C is expressed as a % elongation. Tensile tests (Examples 3 and 4)

[0144] These tests allow the determination of elastic stresses and breaking properties; those carried out on cooked mixtures are carried out in accordance with the AFNOR-NF-T46-002 standard of September 1988.

[0145] The elongations at break (in %) are measured at two temperatures: at 23°C and at 100°C, under normal hygrometry conditions (50% relative humidity), according to the French standard NF T 40-101 (December 1979), the stresses at break (in MPa) and the energy at break can also be measured, the energy at break (Energie Rupture) being the product of the stress at break and the elongation at break. The results are given on a base of 100, i.e. the values ​​are expressed relative to a control, whose elongation at break is considered as the reference at 100. Weight loss

[0146] This test determines the mass loss of a sample of aircraft tire tread compound when subjected to an abrasion test on a high-speed abraser.

[0147] The high-speed abrasion test is performed according to the principle described in the article by SK Clark "Touchdown dynamics", Precision Measurement Company, Ann Arbor, MI, NASA, 35 Langley Research Center, Computational Modeling of Tires pages 9-19 published in August 1995. The tread material rubs on a surface such as a Norton Vulcan A30S-BF42 disc. The linear velocity at contact is 70 m / s with an average contact pressure of 15 to 20 bar. An energy of 10 to 20 MJ / m2 of contact surface is involved during the experiment.

[0148] The elements of the constant energy tribometry device according to the above-mentioned article by SK Clark are a motor, a clutch, a rotating plate and a sample holder.

[0149] Elements of the constant energy tribometry device according to the article by SK Clark mentioned above: roulette (O-ring of test material mounted on a grooved pulley) rotating plate, for example consisting of a Norton disc secured to the axle of an electric motor and a flywheel

[0150] Performance is evaluated based on mass loss according to the following formula: [Mass loss performance = control mass loss / sample mass loss]

[0151] Results are expressed in base 100. A performance for the sample greater than 100 is considered better than the control. Dynamic properties (after cooking)

[0152] The dynamic properties G* and tan(δ)max are measured on a viscoanalyzer (Metravib V A4000), according to the ASTM D 5992 - 96 standard. The response of a sample of vulcanized composition (cylindrical specimen 4 mm thick and 400 mm2 in cross-section) is recorded, subjected to sinusoidal stress in alternating simple shear, at a frequency of 10 Hz, at 60 ° C according to the ASTM D 1349 - 99 standard. A peak-to-peak strain amplitude sweep is carried out from 0.1 to 50% (forward cycle), then from 50% to 1% (return cycle). The results used are the complex dynamic shear modulus (G*) and the loss factor tan(δ). For the return cycle, the maximum value of tan(δ) observed (tan(δ)max) is indicated, as well as the difference in complex modulus (G*) between the values ​​at 0.1% and 50% deformation (Payne effect). For the values ​​of tan(δ)max at 60°C, the lower the value, the lower the hysteresis and therefore the lower the heating of the composition. Tearability

[0153] The tearability indices are measured at two temperatures: 23°C and 100°C. In particular, the force required to achieve rupture (FRD, in N / mm) is determined and the strain at rupture (DRD, in %) is measured on a specimen measuring 10 x 85 x 2.5 mm, notched in the center of its length by 3 notches to a depth of 5 mm, to cause the specimen to rupture. Thus, the energy required to cause rupture (Energy) of the specimen, which is the product of the FRD and DRD, can be determined. The results are given on a base of 100, i.e. the values ​​are expressed relative to a control, whose strain at rupture (DRD) is considered as the reference at 100. Roasting time (or fixing time)

[0154] The measurements are carried out at 130°C, in accordance with the French standard NF T 43-005. The evolution of the consistometric index as a function of time makes it possible to determine the fixing time of the rubber compositions, assessed in accordance with the aforementioned standard by the parameter T5 (case of a large rotor), expressed in minutes, and defined as the time necessary to obtain an increase in the consistometric index (expressed in MU) of 5 units above the minimum value measured for this index. Microstructure of elastomers

[0155] Generally, regarding the composition of elastomers, the microstructure is determined by 1H NMR analysis, supplemented by 13C NMR analysis when the resolution of 1H NMR spectra does not allow the attribution and quantification of all species. Measurements are carried out using a BRUKER 500 MHz NMR spectrometer at frequencies of 500.43 MHz for proton observation and 125.83 MHz for carbon observation. For measurements on mixtures or non-soluble elastomers but having the capacity to swell in a solvent, a 4 mm z-grad HRMAS probe is used to observe the proton and carbon in proton-decoupled mode. The spectra are acquired at rotation speeds of 4000 Hz to 5000 Hz. For measurements on soluble elastomers, a liquid NMR probe is used to observe the proton and carbon in proton-decoupled mode.The preparation of insoluble samples is carried out in rotors filled with the analyzed material and a deuterated solvent allowing swelling, generally deuterated chloroform (CDCl3). The solvent used must always be deuterated and its chemical nature can be adapted by the skilled person. The quantities of material used are adjusted in order to obtain spectra with sufficient sensitivity and resolution. Soluble samples are dissolved in a deuterated solvent (approximately 25 mg of elastomer in 1 mL), generally deuterated chloroform (CDCl3). The solvent or solvent blend used must always be deuterated and its chemical nature can be adapted by the skilled person. The sequences used for proton NMR and carbon NMR are identical for a soluble sample and a swollen sample. For proton NMR, a single pulse sequence of 30° is used.The spectral window is set to observe all the resonance lines belonging to the analyzed molecules. The accumulation number is set to obtain a sufficient signal-to-noise ratio for the quantification of each pattern. The recycling time between each pulse is adapted to obtain a quantitative measurement. For carbon NMR, a single 30° pulse sequence is used with proton decoupling only during acquisition to avoid “Nuclear Overhauser” (NOE) effects and remain quantitative. The spectral window is set to observe all the resonance lines belonging to the analyzed molecules. The accumulation number is set to obtain a sufficient signal-to-noise ratio for the quantification of each pattern. The recycling time between each pulse is adapted to obtain a quantitative measurement. NMR measurements are carried out at 25°C. V-2 Preparation of compositions

[0156] In the following examples, the rubber compositions were produced as described in point II-5 above. In particular, the diene elastomers, the reinforcing fillers, and the various other ingredients, with the exception of the vulcanization system, are successively introduced into an internal mixer (final filling rate: approximately 70% by volume), the initial tank temperature of which is approximately 80°C. Thermomechanical work (non-productive phase) is then carried out in one step, which lasts a total of approximately 3 to 4 minutes, until a maximum "fall" temperature of 165°C is reached. The mixture thus obtained is recovered, cooled, and then sulfur and a sulfamide-type accelerator are incorporated into a mixer (homo-finisher) at 70°C, mixing everything (productive phase) for an appropriate time (for example, approximately ten minutes). V-3 Rubber composition tests Example 1:

[0157] This example aims to show the influence of the incorporation rate of tin-functionalized SBR in compositions of the middle part of aircraft tire treads on the performance compromise between wear resistance and the conservation of mechanical and thermal properties.

[0158] T1, T2 and T3 are control compositions. T1 corresponds to the composition of an aircraft tread conventionally used by those skilled in the art; it is based on natural rubber as the sole elastomer. T2 corresponds to a tread composition in which the natural rubber has been replaced by a tin-functional SBR. T3 corresponds to a tread composition in which half of the natural rubber has been replaced by a polybutadiene.

[0159] Tests C1 to C3 are in accordance with the invention. Compositions C1 to C3 differ in the respective levels of natural rubber and tin SBR.

[0160] The mass loss and elongation at break performance results at 60°C are expressed as a percentage base 100 relative to the control composition T1, corresponding to the usual tread compositions.

[0161] Table 2 shows the compositions tested (in pce), as well as the results obtained. Table 2 T1 C1 C2 C3 T2 T3 NR (1) 100 70 50 25 - 50 SBR (2) - 30 50 75 100 - BR (3) - - - - - 50 Carbon black (4) 49 49 49 49 49 49 Antioxidant (5) 1.5 1.5 1.5 1.5 1.5 1.5 Anti-ozone wax 1 1 1 1 1 1 Stearic acid 2.5 2.5 2.5 2.5 2.5 2.5 Zinc oxide (6) 3 3 3 3 3 3 Accelerator (7) 0.85 0.85 0.85 0.85 0.85 0.85 Sulfur 1.6 1.6 1.6 1.6 1.6 1.6 Performance Mass loss in % base 100 compared to T1 100 105 114 126 157 102 Elongation at break at 60°C in % base 100 compared to T1 100 91 82 80 59 85 Tan delta max at 60°C 0.19 0.18 0.18 0.17 0.17 0.17 (1) Natural rubber (2) Tin-functionalized solution SBR with 24% 1.2-dimethyl-1,4-cis polybutadiene units - 15.5% styrene units - Tg = -65°C (3) 98% 1.4-cis neodymium polybutadiene - Tg = -108°C (4) Carbon black grade N234 according to ASTM D-1765 (5) N-1,3-dimethylbutyl-N-phenylparaphenylenediamine "Santoflex 6-PPD" from Flexsys (6) Industrial grade zinc oxide from Umicore (7) N-cyclohexyl-2-benzothiazyl sulfenamide "Santocure CBS" from Flexsys

[0162] The results presented in Table 2 above show that the mass loss performance, representative of better wear resistance during the landing phase, of compositions C1 to C3 is always significantly improved compared to the control.

[0163] Furthermore, these compositions C1 to C3 have an elongation at break at 60°C which is 20% lower than the control T1 (composition of an aircraft tread conventionally used by those skilled in the art to manufacture an aircraft tire tread) which remains an acceptable level of mechanical properties. Beyond a 20% decrease compared to T1, it can be considered that the mechanical properties could no longer be considered sufficient for the tread composition to be used on aircraft tires.

[0164] The above results also show that the thermal stability of the composition, represented by the values ​​of Tan delta max at 60°C, is maintained, or even improved, compared to the control T1.

[0165] As the results of the T2 compound show, the absence of natural rubber in the compound causes a significant decrease in mechanical properties. In addition, the T3 compound, corresponding to a tread compound in which half of the natural rubber has been replaced by polybutadiene, does not significantly improve wear resistance.

[0166] Thus, only the median compositions in accordance with the invention have the advantage of allowing better wear resistance of the median part of the tread during the landing phase of the aircraft, while maintaining or even improving the thermal properties of the composition and keeping the mechanical properties at an acceptable level. It is observed that the use of 45 to 75 pce of tin SBR in the composition leads to a better performance compromise between wear resistance and the maintenance of thermal and mechanical properties. Example 2:

[0167] This example aims to show the influence of the incorporation of other diene elastomers in addition to the tin-functionalized SBR on the performance compromise between wear resistance and the conservation of the mechanical and thermal properties of the middle part of the tread.

[0168] C2 corresponds to composition C2 of Example 1. It corresponds to an embodiment of the invention in which only the tin-functionalized SBR is present in addition to the diene elastomer.

[0169] Tests C4 and C5 are also consistent with the median rubber composition according to the invention. Compositions C4 and C5 comprise complementary synthetic elastomers of different nature as indicated in Table 3 below.

[0170] The mass loss and elongation at break performance results at 60°C are expressed as a percentage base 100 relative to the control composition T1 of Example 1.

[0171] Table 3 shows the compositions tested (in pce), as well as the results obtained. Table 3 C2 C4 C5 NR (1) 50 35 30 SBR (2) 50 45 - SBR (8) - - 20 BR (3) - 20 - VCR412 (9) - - 50 Carbon black (4) 49 49 49 Antioxidant (5) 1.5 1.5 1.5 Anti-ozone wax 1 1 1 Stearic acid 2.5 2.5 2.5 Zinc oxide (6) 3 3 3 Accelerator (7) 0.85 0.85 0.85 Sulfur 1.6 1.6 1.6 Performance Mass loss in % base 100 compared to T1 114 118 138 Elongation at break at 60°C in % base 100 compared to T1 82 108 95 Tan delta at 60°C 0.18 0.18 0.20 (1) to (7): see Table 2 (8) SBR solution functionalized with tin with 24% of 1,2-polybutadiene units - 26.5% of styrene units - Tg = -48°C (9) “VCR412 UBEPOL” from the company UBE - composite polybutadiene: 12% of syndiotactic 1,2-polybutadiene in a 1,4-cis polybutadiene matrix.

[0172] The results presented in Table 3 above show that the mass loss performance, representative of better wear resistance during the landing phase, of compositions C4 and C5 is always significantly improved compared to control T1, and are comparable, or even superior to composition C2 in accordance with the present invention.

[0173] Furthermore, these compositions exhibit an elongation at break at 60°C well below 20%, or even higher, compared to the control T1, and the thermal stability of the composition is also maintained compared to the control T1. These results are comparable, or even higher, to the composition C2 in accordance with the present invention.

[0174] Thus, the median rubber compositions in accordance with the invention, whether or not they comprise another diene elastomer in addition to the isoprene elastomer and the tin-functionalized SBR, have the advantage of providing better wear resistance during the landing phase of the aircraft, while maintaining or even improving the thermal properties of the composition and retaining good mechanical properties. Example 3:

[0175] These examples aim to show the influence of the incorporation of a hydrocarbon resin composed mainly of dicyclopentadiene and aromatic units in aircraft tire tread compositions on the performance compromise between cut resistance and fixing time. Three types of elastomer matrices were tested.

[0176] Tables 4 and 5 present all the compositions tested (in pce), as well as the results obtained.

[0177] T4 and T5 are control compositions. Compositions C6 to C12 are in accordance with the invention.

[0178] The elongation at break performance results at 23°C and 100°C are expressed as a percentage base 100 compared to the control composition, as are the tear resistance performance results at 23°C and 100°C. The increase in fixing time is expressed in minutes compared to the control. Table 4 T4 C6 C7 C8 C9 NR (1) 50 50 50 50 50 SBR (2) 50 50 50 50 50 Carbon black (10) 49 49 49 49 49 Silica (12) 5 5 5 5 5 Coupling agent (13) 1 1 1 1 1 Hydrocarbon resin (11) 0 2,5 5 7,5 10 Antioxidant (5) 1,5 1,5 1,5 1,5 1,5 Anti-ozone wax 1 1 1 1 1 Stearic acid 2,5 2,5 2,5 2,5 2,5 ZnO (6) 3 3 3 3 3 Accelerator (7) 0,8 0,8 0,8 0,8 0,8 Sulfur 1,5 1,5 1,5 1,5 1,5 Elongation at break at 23°C (base 100) 100 104 116 121 123 Elongation at break at 100°C (base 100) 100 115 130 142 157 DRD at 23°C (base 100) 100 113 143 177 189 DRD at 100°C (base 100) 100 113 144 179 108 Increase grilling time (minutes) 0 15 17 20 22 (1), (2), (5) to (7): see Table 2 (10) Carbon black grade N115 according to ASTM D-1765 (11) DCPD / Aromatic hydrocarbon resin “Novares TC160” from Rütgers Mn=710g / mol; Mw=2000g / mol; Ip=2.8, Tg=106°C. Aromatic protons: 13%, Ethylenic protons: 5.6%, Aliphatic protons: 81.4% (12) Silica “Zeosil 1165 MP” from Solvay-Rhodia type “HDS” (13) Silane Table 5 T5 C10 C11 C12 NR (1) 35 35 35 35 SBR (2) 65 65 65 65 Carbon black (10) 49 49 49 49 Silica (12) 5 5 5 5 Coupling agent (13) 1 1 1 1 Hydrocarbon resin (11) 0 5 7,5 10 Antioxidant (5) 1,5 1,5 1,5 1,5 Anti-ozone wax 1 1 1 1 Stearic acid 2,5 2,5 2,5 2,5 ZnO (6) 3 3 3 3 Accelerator (7) 0,8 0,8 0,8 0,8 Sulfur 1,5 1,5 1,5 1,5 Elongation at break at 23°C (base 100) 100 116 128 132 Elongation at break at 100°C (base 100) 100 101 102 99 DRD at 23°C (base 100) 100 146 147 216 DRD at 100°C (base 100) 100 131 149 162 Increased fixation time (minutes) 0 18 20 22 (1), (2), (5) to (7): see Table 2 (10) to (13): see Table 4

[0179] These results show that the cutting resistance performance as represented by the elongation at break and tearability measurements, both at 23°C and 100°C, is greatly improved by the invention. Similarly, the scorching time is significantly extended, allowing for an increase in industrial productivity during the manufacture of aircraft tires. Example 4:

[0180] These examples aim to show the influence of the incorporation of a specific hydrocarbon resin in mid-rubber compositions of aircraft tire treads on the performance trade-off between cut resistance and processability. Two types of elastomer matrices were tested.

[0181] Table 6 presents all the compositions tested (in pce) as well as the results obtained.

[0182] T6 is a control composition. Compositions C13 to C15 are in accordance with the invention.

[0183] The elongation at break performance results at 23°C and 100°C are expressed as a percentage base 100 relative to the control composition, as are the tear strength performance results at 23°C and 100°C. Processability is represented by Mooney viscosity values ​​in Mooney units. Table 6 T6 C13 C14 C15 NR (1) 50 50 50 50 SBR (2) 50 50 50 50 Carbon black (10) 49 49 49 49 Silica (12) 5 5 5 5 Coupling agent (13) 1 1 1 1 Hydrocarbon resin (14) 0 5 7,5 10 Antioxidant (5) 1,5 1,5 1,5 1,5 Anti-ozone wax 1 1 1 1 Stearic acid 2,5 2,5 2,5 2,5 ZnO (6) 3 3 3 3 Accelerator (7) 0,8 0,8 0,8 0,8 Sulfur 1,5 1,5 1,5 1,5 Elongation at break at 23°C (base 100) 100 112 121 122 Elongation at break at 100°C (base 100) 100 130 143 159 DRD at 23°C (base 100) 100 152 185 190 DRD at 100°C (base 100) 100 162 198 230 Mooney Viscosity (UM) 94 89 87 87 (1), (2), (5) to (7): see Table 2 (10), (12) and (13): see Table 4 (14) DCPD / Aromatic hydrocarbon resin “Nevroz 1420” from the company Neville Mn=913g / mol; Mw=3540g / mol; Ip=3.9, Tg=90°C. Aromatic protons: 3%, Ethylenic protons: 5%, Aliphatic protons: 92%, also including units from pine derivatives

[0184] All the results show that the cutting resistance performance as represented by the elongation at break and tearability measurements, both at 23°C and 100°C, is greatly improved by the embodiment of the invention according to which the middle rubber composition of the tread comprises at least one hydrocarbon resin mainly composed of units derived from aromatic and cycloaliphatic monomers. At the same time, the Mooney viscosity is reduced in the compositions useful in the invention, making it possible to increase industrial productivity during the manufacture of aircraft tires.

[0185] In summary, the median rubber compositions in accordance with the invention, based on at least in particular 25 to 85 pce of a tin-functionalized butadiene and styrene copolymer and 15 to 75 pce of isoprene elastomer, constituting the median part of the tread of an aircraft tire, give the tire significantly improved resistance to wear and tear during landing.

[0186] Based on these results, it is estimated that a tire according to the invention, compared to the reference tire, allows an overall gain in wear life over the entire tire usage cycle including the landing, rolling and braking phases.

[0187] This gain in lifespan on tire wear according to the invention, obtained thanks to more regular wear of the tread, also presents an advantage in terms of retreading the tire, that is to say the replacement of the worn tread of the tire at the end of its life.

[0188] For a state-of-the-art tire at the end of its life, for which the tread shows differential wear between the middle part and the lateral parts, the retreading operation most often requires, in addition to the removal of the worn tread, the removal of the radially outermost crown layer, generally consisting of metal reinforcements and called the protective layer, said protective layer often being damaged at the end of the tire's life due to its proximity to the tread.

[0189] For a tire according to the invention, due to more regular wear across the axial width of the tread, removal of the protective layer is no longer necessary, due to its integrity at the end of the tire's life, resulting in an economic gain on the retreading operation.

Claims

1. Aircraft tyre (1), comprising a tread (2) having an axial width L, the tread (2) comprising: - a middle portion (3) having an axial width LC at least equal to 50% and at most equal to 80% of the axial width L of the tread and consisting of a middle rubber composition, - and two lateral portions (41, 42) positioned axially on either side of the middle portion (3), each having an axial width (LS1, LS2) at least equal to 10% and at most equal to 25% of the axial width L of the tread and each consisting of a lateral rubber composition, characterized in that the middle rubber composition comprises at least one elastomeric matrix, a reinforcing filler and a crosslinking system, said elastomeric matrix comprising from 25 to 85 parts by weight per hundred parts by weight of elastomer, phr, of a tin-functionalized butadiene and styrene copolymer and from 15 to 75 phr of isoprene elastomer, the total content of isoprene elastomer and of butadiene and of tin-functionalized butadiene and styrene copolymer in the middle rubber composition being within a range extending from 45 to 100 phr, in that at least one lateral rubber composition is different from the middle rubber composition, and in that the at least one lateral rubber composition comprises at least one diene elastomer, a reinforcing filler and a crosslinking system, which the diene elastomer predominantly comprises at least one isoprene elastomer.

2. Tyre (1) according to Claim 1, wherein the content of the isoprene elastomer in the middle rubber composition is within a range extending from 20 to 65 phr, preferably from 25 to 60 phr.

3. Tyre (1) according to either one of the preceding claims, wherein the content of tin-functionalized butadiene and styrene polymer in the middle rubber composition is within a range extending from 35 to 80, preferably from 40 to 75 phr.

4. Tyre (1) according to any one of the preceding claims, wherein the elastomeric matrix of the middle rubber composition comprises more than 0 to 55 phr, preferably more than 0 to 50 phr of another diene elastomer.

5. Tyre (1) according to Claim 4, wherein the other diene elastomer of the middle rubber composition is selected from the group consisting of non-tin-functionalized butadiene and styrene copolymers, polybutadienes, and mixtures thereof.

6. Tyre (1) according to any one of the preceding claims, wherein the reinforcing filler of the middle rubber composition comprises carbon black and / or a reinforcing inorganic filler, preferably the reinforcing filler of the middle rubber composition comprises predominantly, preferably exclusively, carbon black.

7. Tyre (1) according to any one of the preceding claims, wherein the content of reinforcing filler, preferably of carbon black, in the middle rubber composition is within a range extending from 20 to 100 phr, preferably from 25 to 75 phr, more preferably from 30 to 70 phr.

8. Tyre (1) according to any one of the preceding claims, wherein the middle rubber composition also comprises from 1 to 30 phr of at least one hydrocarbon-based resin predominantly composed of units derived from aromatic and cycloaliphatic monomers.

9. Tyre (1) according to Claim 8, wherein the hydrocarbon-based resin predominantly composed of units derived from aromatic and cycloaliphatic monomers is such that the cycloaliphatic monomers are selected from the group consisting of cyclopentadiene, dicyclopentadiene and mixtures thereof, and the aromatic monomers are selected from the group consisting of styrene, alpha-methylstyrene, vinyltoluene, indene and mixtures thereof.

10. Tyre (1) according to either one of Claims 8 and 9, wherein the hydrocarbon-based resin predominantly composed of units derived from aromatic and cycloaliphatic monomers has an aromatic proton content of between 0 and 12%, an ethylenic proton content greater than 3%, a number-average molecular weight greater than 500 g / mol and a polydispersity index greater than 2.

11. Tyre (1) according to any one of the preceding claims, wherein the lateral rubber composition comprises more than 85 phr, preferably at least 90 phr of at least one isoprene elastomer.

12. Tyre (1) according to any one of the preceding claims, wherein the two lateral portions (41, 42), positioned axially on either side of the middle portion (3), are different from the middle rubber composition.

13. Tyre (1) according to any one of the preceding claims, wherein the two lateral portions (41, 42), positioned axially on either side of the middle portion (3), are formed by identical lateral rubber compositions.

14. Tyre (1) according to any one of the preceding claims, wherein the two lateral portions (41, 42), positioned axially on either side of the middle portion (3), have identical axial widths (LS1, LS2).