SMOKE-REDUCING CIGARETTE FILTER, CIGARETTE AND MANUFACTURING METHOD THEREOF

Description

Technical Field

[0001] Provided are a smoke-component reducing cigarette filter, a cigarette, and a manufacturing method thereof.Background Art

[0002] In general, in order to manufacture a cigarette, first, various types of leaf tobaccos are mixed and processed to have a desired aroma and taste. Next, cut tobacco leaves are prepared by cutting the processed leaf tobacco, and the cut tobacco leaves are rolled with a cigarette paper to manufacture a cigarette without a filter. Next, a filter is attached to the cigarette without the filter as needed.

[0003] The cigarette paper may be made of flax, wood pulp, etc., and when burned, it is required to maintain the flammability and taste of the cigarette. The cigarette filter may include activated carbon, flavoring materials, etc., and may consist of a mono filter or multiple filters, and the cigarette filter is surrounded by a cigarette filter wrapping paper. The cut tobacco leaf portion and the cigarette filter are connected to each other by a tipping paper, and the tipping paper may include minute holes.

[0004] In general, a cigarette filter uses cellulose acetate tow that is acetylated by extracting cellulose from wood pulp. When the cigarette filter is manufactured with acetate tow, a plasticizer or a hardener is used to improve the hardness of the cigarette filter. This is because a cigarette filter and cigarette can be smoothly manufactured only when the hardness of the cigarette filter is improved. When the hardness of the cigarette filter is low, the cigarette filter is not hard, so that the cigarette filter may be caught in a drum in the manufacturing process of the cigarette filter or the cigarette. In addition, the cigarette filter should have suitable suction resistance for smoking while filtering tar, nicotine, VOC, etc. contained in the cigarette smoke. Accordingly, studies on a cigarette filter having an excellent filtering function and appropriate suction resistance while having excellent hardness and workability have been conducted with respect to various materials.

[0005] US Patent Registration No. 4,869,275 relates to "Ultra-high filtration", and discloses a cigarette filter formed in a bulky tow shape in which polymer fiber webs such as polypropylene and polyethylene terephthalate are entangled with each other by a melt-blown method. However, the bulky tow type cigarette filter using the polymer fiber webs has a high TPM filtering function of 70% or more, but is weak in a tar and nicotine filtering function, has no proper suction resistance, and is low in hardness and workability, and thus, the bulky tow type cigarette filter is not easy to be used for manufacturing the cigarette. [Prior Arts] [Patent Document] US 4,869,275 CN 205 947 106 U relates to a ventilation filter with polymer membrane support section. CN 1 057 574 A relates to adhesive-bonded fabric for use in cigarette filter and its fabrication. WO 2017 / 036909 A1 relates to a tubular element for use in the manufacture of a filter of a smoking article, the tubular element comprising a first and a second layer wound of substantially continuous strips of a cellulose-fibre-based web material. The strips have predetermined thickness and width. The web material is coated on a first surface with an activatable polymer and the first surface of the web material in the first layer faces the first surface of the web material in the second layer. An external diameter of the tubular element is substantially uniform over a given length.Disclosure / Technical Problem

[0006] An embodiment of the present invention is to have a high tar and nicotine filtering function in addition to a high TPM filtering function.

[0007] An embodiment of the present invention is to have hardness and workability easy for manufacturing a cigarette while having proper suction resistance.Technical Solution

[0008] According to one aspect of the invention, a cigarette filter comprises a first filter portion comprising an irregularly folded and packed polymer sheet, and a first cigarette filter wrapping paper surrounding the polymer sheet, wherein the polymer sheet comprises: a first polymer layer containing polyolefin or polyester, and a second polymer layer positioned on the first polymer layer and containing polyolefin, wherein a basis weight of the first polymer layer is 5 GSM to 20 GSM, a basis weight of the second polymer layer is 10 GSM to 30 GSM, and the basis weight of the second polymer layer is larger than the basis weight of the first polymer layer. The invention is defined by the appended claims.

[0009] The first polymer layer may be folded to contact each other, and the second polymer layer may be folded to contact each other.

[0010] The cigarette filter may further comprise a second filter portion, wherein the second filter portion may be connected to the first filter portion and positioned at an oral region of the cigarette.

[0011] The second filter portion may include acetate tow, and may be surrounded by a second cigarette filter wrapping paper.

[0012] The polymer sheet may have a horizontal length (a) and a vertical length (b), and may be folded irregularly in a direction of the horizontal length (a).

[0013] According to a second aspect of the present invention, a cigarette comprises a cigarette filler portion; a cigarette paper surrounding the cigarette filler portion; a cigarette filter portion connected to the cigarette filler portion; and a tipping paper connecting the cigarette filler portion and the cigarette filter portion, wherein the cigarette filter portion wherein the cigarette filter portion comprises a first filter portion comprising an irregularly folded and packed polymer sheet, and a first cigarette filter wrapping paper surrounding the polymer sheet, wherein the polymer sheet comprises a first polymer layer containing polyolefin or polyester, and a second polymer layer positioned on the first polymer layer and containing polyolefin, wherein a basis weight of the first polymer layer is 5 GSM to 20 GSM, a basis weight of the second polymer layer is 10 GSM to 30 GSM, and the basis weight of the second polymer layer is larger than the basis weight of the first polymer layer.

[0014] According to a further aspect of the present invention, a manufacturing method of a cigarette filter comprises the steps of preparing a first polymer layer using polyolefin or polyester; preparing a polymer sheet by forming a second polymer layer on the first polymer layer using polyolefin; preparing a first filter portion by irregularly folding the polymer sheet; and surrounding the first filter portion with a first cigarette filter wrapping paper, wherein a basis weight of the first polymer layer is 5 GSM to 20 GSM, a basis weight of the second polymer layer is 10 GSM to 30 GSM, and the basis weight of the second polymer layer is larger than the basis weight of the first polymer layer.

[0015] The second polymer layer may be laminated on the first polymer layer by a melt-blown process.

[0016] The polymer sheet may be folded irregularly by a crimping process.Advantageous Effects

[0017] According to an embodiment of the present invention, it is possible to have a high tar and nicotine filtering function in addition to a high TPM filtering function and have hardness and workability easy for manufacturing a cigarette while having proper suction resistance.Description of Drawings

[0018] FIG.1 is a perspective view schematically illustrating a cigarette according to an embodiment of the present invention. FIG.2 is a perspective view schematically illustrating a cigarette according to an embodiment of the present invention. FIG.3 is a cross-sectional view taken along the line II-II of a cigarette of FIG.2. FIG.4 is a perspective view illustrating a sheet constituting a cigarette filter according to an embodiment of the present invention. FIG.5 is a perspective view schematically illustrating a cigarette according to an embodiment of the present invention. Best Mode

[0019] Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings so as to be easily implemented by those with ordinary skill in the art to which the present invention pertains. Parts not associated with description are omitted for clearly describing the present invention and like reference numerals designate like or similar components throughout the specification. In the case of well-known technology, detailed description thereof will be omitted.

[0020] In the drawings, the thicknesses of various layers and regions are exaggerated for clarity. When a part such as a layer, a film, a region, a substrate, etc., is located "on" the other part, there are cases where the part may be located "directly on" the other part and another part may be interposed therebetween. In contrast, when a certain part is located "directly on" the other part, there are no intervening parts present. On the contrary, when a part such as a layer, a film, a region, a substrate, etc., is located "below" the other part, there are cases where the part may be located "directly below" the other part and another part may be interposed therebetween. In contrast, when a certain part is located "directly below" the other part, there are no intervening parts present.

[0021] Throughout the specification, when a certain part "comprises" a certain component, unless otherwise described to the contrary, it is meant that another component may be further included without excluding another component.

[0022] Then, a smoke-component reducing cigarette filter and a cigarette according to an embodiment of the present invention will be described.

[0023] FIG.1 is a perspective view schematically illustrating a cigarette according to an embodiment of the present invention, FIG.2 is a perspective view schematically illustrating a cigarette according to an embodiment of the present invention, FIG.3 is a cross-sectional view taken along the line II-II of a cigarette of FIG.2, FIG.4 is a perspective view illustrating a sheet constituting a cigarette filter according to an embodiment of the present invention, and FIG.5 is a perspective view illustrating a sheet constituting a cigarette filter according to an embodiment of the present invention.

[0024] Referring to Figs 1 to 5, a cigarette 1 includes a cigarette filler portion 10 burned by fire and a cigarette filter portion 20 filtering the cigarette smoke. The cigarette filler portion 10 may be surrounded by a cigarette paper 19, and the cigarette filter portion 20 may be surrounded by cigarette filter wrapping papers 27, 28 and 29. The cigarette filler portion 10 and the cigarette filter portion 20 may be connected to each other by a tipping paper 31. A circumference of the cigarette may be about 10 mm to about 30 mm.

[0025] The cigarette paper 19 may include a filler, thereby increasing the opacity of the cigarette paper, imparting the porosity to the cigarette paper, improving the smoothness and ash integrity of the cigarette paper, and increasing the whiteness of the cigarette paper. For example, the filler includes materials such as calcium carbonate, titanium dioxide, and magnesium oxide.

[0026] The cigarette filter portion 20 may be a multiple filter including two or more filter members. For example, referring to FIG.2, the cigarette filter portion 20 may include a first filter portion 21 and a second filter portion 22. Referring to FIG.5, the cigarette filter portion may include a first filter portion 21, a second filter portion 22, and a third filter portion 23.

[0027] In addition, the cigarette filter portion 20 may include an adsorbent, a flavoring agent, and the like. For example, the adsorbent may be activated carbon or the like, and the flavoring agent may be a herbal flavoring material or the like. In the multiple filter, one or more filter members may include at least one of an adsorbent and a flavoring agent.

[0028] Referring to FIGS. 3 and 4, the first filter portion 21 is surrounded by a first cigarette filter wrapping paper 28 and may include an adsorbent, a flavoring agent, and the like. A polymer sheet 210 is irregularly folded in the first filter portion 21. The polymer sheet 210 includes a first polymer layer 211 and a second polymer layer 212 positioned on the first polymer layer 211.

[0029] The first polymer layer 211 includes one or more polyolefins such as polypropylene, polyesters such as polyethylene terephthalate, and the like. For example, a basis weight of the first polymer layer 21 is 5 GSM to 20 GSM, and in this range, the adhesion between the second polymer layer 212 and the first polymer layer 211 may be improved.

[0030] The second polymer layer 212 includes polyolefin such as polypropylene. The second polymer layer 212 may be formed on the first polymer layer 211. For example, the second polymer layer 212 may be formed by a melt-blown method. The second polymer layer 212 may be sprayed toward the first polymer layer 211 by a spinning nozzle in a molten state, and may be laminated on the first polymer layer 211. A basis weight of the second polymer layer 212 is 10 GSM to 30 GSM, and in this range, the adhesion between the second polymer layer 212 and the first polymer layer 211 may be improved. The basis weight of the second polymer layer 212 is larger than the basis weight of the first polymer layer 211.

[0031] The polymer sheet 210 is irregularly folded without a plasticizer. For example, as illustrated in FIG.3, the first polymer layer 211 may be folded to contact each other, and the second polymer layer 212 may be folded to contact each other. Since the plasticizer is not included, the thermal stability of the cigarette filter may be increased, the process may be simplified, and the cost may be reduced. The size of the polymer sheet 210 may have a horizontal length a of about 150 to 300 mm and a vertical length b of about 5 to 30 mm. The polymer sheet 210 may be irregularly folded in a direction of the horizontal length a.

[0032] In the polymer sheet 210, a ratio of the horizontal length a to a diameter of the first filter portion 21 may be about 20 to about 45. When the ratio of the horizontal length a to the diameter of the first filter portion 21 is about 20 or more, the workability for manufacturing the cigarette may be easy, and a function of filtering TPM, tar, nicotine, etc. of the first filter portion 21 may be maintained. When the ratio of the horizontal length a to the diameter of the first filter portion 21 is about 45 or less, the polymer sheet 210 may be folded smoothly in a crimping process, and the first filter portion 21 may have proper suction resistance. For example, when the diameter of the first filter portion 21 is about 8 mm, the horizontal length a of the polymer sheet 210 may be about 160 mm to 360 mm. The horizontal length a may be preset according to the diameter of the first filter portion 21

[0033] The vertical length b of the polymer sheet 210 may be an integer multiple of the length of the first filter portion 21. After the polymer sheet 210 is folded, the polymer sheet 210 may be cut by the length of the first filter portion 21.

[0034] Referring to FIG.3, the first filter portion 21 includes a plurality of pores 229. The pore 229 is a space in which the polymer sheet 21 is not folded in the first filter portion 21. Through the pores 229 and the pores of the polymer sheet 210, a user may inhale cigarette smoke.

[0035] For example, the first filter portion 21 may be densely packed with the polymer sheet 210 folded irregularly by a crimping method.

[0036] Depending on the packed degree of the polymer sheet 210, the horizontal length a may be preset, and an area of the plurality of pores 229 may be changed.

[0037] Since the polymer sheet 210 including the first polymer layer 211 and the second polymer layer 212 is irregularly folded and packed, the cigarette filter portion 20 including the first filter portion 21 may have a high tar and nicotine filtering function in addition to a high TPM filtering function. In addition, due to the dense packing and pores of the polymer sheet 210, and the pores 229 of the first filter portion 21, the cigarette filter portion 20 may have the hardness and workability easy to manufacture the cigarette while having appropriate suction resistance.

[0038] The second filter portion 22 is surrounded by the second cigarette filter wrapping paper 29 and may include an adsorbent, a flavoring agent, and the like. The second filter portion 22 may include acetate tow. Referring to FIGS. 2 and 5, the second filter portion 22 is positioned at an oral region of the cigarette.

[0039] The third filter portion 23 is surrounded by the third cigarette filter wrapping paper 27 and may include an adsorbent, a flavoring agent, and the like. The third filter portion 23 may include acetate tow. Referring to FIG.5, the third filter portion 23 is positioned between the cigarette filler portion 10 and the first filter portion 21.

[0040] Then, a manufacturing method of a cigarette filter will be described in detail.

[0041] The manufacturing method of the cigarette filter comprises the steps of preparing a first polymer layer using at least one of polyolefin, polyester, etc., preparing a polymer sheet by forming a second polymer layer on the first polymer layer using polyolefin, preparing a first filter portion by irregularly folding the polymer sheet, and surrounding the first filter portion with a first cigarette filter wrapping paper, wherein a basis weight of the first polymer layer is 5 GSM to 20 GSM, a basis weight of the second polymer layer is 10 GSM to 30 GSM, and the basis weight of the second polymer layer is larger than the basis weight of the first polymer layer.

[0042] The second polymer layer may be laminated on the polymer layer by a melt-blown process.

[0043] The polymer sheet may be folded irregularly by a crimping process.Modes of the Invention

[0044] Hereinafter, the present invention will be described in more detail with reference to the Examples.Preparation of polymer sheet / Example 1

[0045] A first polymer layer having a basis weight of about 14 GSM was prepared using polypropylene. A polymer sheet was prepared by laminating a second polymer layer having a basis weight of about 18 GSM on the first polymer layer using polypropylene by a melt-blown process. The thickness of the prepared polymer sheet was about 127 micrometers.Preparation of cigarette filter portion / Example 2

[0046] The polymer sheet prepared in Example 1 was irregularly folded by a crimping process to prepare a cylindrical first filter portion without using a plasticizer. The prepared first filter portion was about 12 mm in the length, about 57 mmH 2 O in the suction resistance, and about 88% in the hardness. The workability of preparing the first filter portion was good. The second filter portion was prepared using TEC as a plasticizer for acetate tow. The prepared second filter portion was about 15 mm in the length, about 60 mmH 2 O in the suction resistance, and about 91% in the hardness. A double cigarette filter was prepared by combining the prepared first filter portion and second filter portion. The prepared double cigarette filter had the suction resistance of about 476 mmH 2 O and the hardness of about 93%Comparative Example 1

[0047] The first filter portion was prepared using TEC as a plasticizer for acetate tow. The prepared first filter portion was about 12 mm in the length, about 57 mmH 2 O in the suction resistance, and about 91% in the hardness. The second filter portion was prepared using TEC as a plasticizer for acetate tow. The prepared second filter portion was about 15 mm in the length, about 60 mmH 2 O in the suction resistance, and about 91% in the hardness. A double cigarette filter was prepared by combining the prepared first filter portion and second filter portion. The prepared double cigarette filter had the suction resistance of about 465 mmH 2 O and the hardness of about 92%.Physical properties of cigarette filter

[0048] When comparing the hardness of the double cigarette filter prepared in Example 2 with the hardness of the double cigarette filter prepared in Comparative Example 1, the double cigarette filter of Example 2 had a slightly higher value than the double cigarette filter of Comparative Example 1, and thus the workability to manufacture the filter was better.Preparation of cigarette / Example 3

[0049] A cigarette filler portion was prepared using 580 mg of cut tobacco leaves of THE ONE blue, and a cigarette was prepared by combining the double cigarette filter of Example 2 with the cigarette filler portion. The workability of using the double cigarette filter of Example 2 for manufacturing the cigarette was good.Comparative Example 2

[0050] A cigarette filler portion was prepared using 580 mg of cut tobacco leaves of THE ONE blue, and a cigarette was prepared by combining the double cigarette filter of Comparative Example 1 with the cigarette filler portion.Physical properties of cigarette

[0051] The cigarette of Example 3 was about 860 mg in total weight, about 25 mm in circumference, about 160 mmWG in encapsulated pressure drop (EPD), and about 76% in ventilation rate (VR).

[0052] The cigarette of Comparative Example 2 was about 860 mg in total weight, about 25 mm in circumference, about 160 mmWG in encapsulated pressure drop (EPD), and about 76% in ventilation rate (VR).Smoke components and filtering of cigarette

[0053] General smoke components of the cigarette of Example 3 and the cigarette of Comparative Example 2 were shown in Table 1. [Table 1]TPM(mg / cig)Tar(mg / cig)Nicotine (mg / cig.)CO(mg / cig. )Puff o.(times)Moisture (mg / cig.)Example 31.521.300.112.48.50.12Comparative Exmple 22.362.010.162.58.40.19Reduction rate (%)35.435.730.8--35.9

[0054] Referring to Table 1, TPM, tar, nicotine, and moisture as smoke components of the cigarette of Example 3 were reduced by about 30% to about 36% depending on a type compared with the smoke components of Comparative Example 2.

[0055] Filter removal abilities of the cigarette of Example 3 and the cigarette of Comparative Example 2 were shown in Table 2. Table 2]SRE (%)TRE (%)NRE (%)WRE (%)Puff No. (Times)Example 377.076.263.430.76.8Comparative Example 267.762.252.339.56.5

[0056] SRE was a TPM removal ability of the cigarette, TRE was a tar removal ability of the cigarette, NRE was a nicotine removal ability of the cigarette, and WRE was a moisture removal ability of the cigarette. Referring to Table 2, the TPM removal ability, the tar removal ability, and the nicotine removal ability of the cigarette of Example 3 were about 10% higher than those of the cigarette of Comparative Example 2.

[0057] Specific smoke components of the cigarette of Example 3 and the cigarette of Comparative Example 2 were shown in Table 3. [Table 3]VOCs (µg / cig.)Phenolic (µg / cig.)Ammonia (mg / cig.)Example 3111.0433.581.29Comparative Example 2130.0851.241.86Reduction rate (%)14.634.530.6

[0058] Referring to Table 3, VOCs, phenolic, and ammonia as specific smoke components of the cigarette of Example 3 were reduced by about 15% to about 35% depending on a type as compared with the smoke components of Comparative Example 2. The phenolic was associated with the particulate components of the cigarette smoke.Explanation of Reference Numerals and Symbols

[0059] a.1:Cigarette10:Cigarette filler portionb.20:Cigarette filter portion21:First filter portionc.22:Second filter portion23:Third filter portiond.210:Polymer sheet211:First polymer layere.212:Second polymer layer229:Pores

Claims

1. A cigarette filter comprising a first filter portion (21) comprising an irregularly folded and packed polymer sheet (210), and a first cigarette filter wrapping paper (28) surrounding the polymer sheet (210), wherein the polymer sheet (210) comprises: a first polymer layer (211) containing polyolefin or polyester, and a second polymer layer (212) positioned on the first polymer layer (211) and containing polyolefin, wherein a basis weight of the first polymer layer (211) is 5 GSM to 20 GSM, a basis weight of the second polymer layer (212) is 10 GSM to 30 GSM, and the basis weight of the second polymer layer (212) is larger than the basis weight of the first polymer layer (211).

2. The cigarette filter of claim 1, wherein the first polymer layer (211) is folded to contact each other, and the second polymer layer (212) is folded to contact each other.

3. The cigarette filter of claim 2, further comprising a second filter portion (22), wherein the second filter portion (22) is connected to the first filter portion (21) and positioned at an oral region of a cigarette (1).

4. The cigarette filter of claim 3, wherein the second filter portion (22) includes acetate tow, and is surrounded by a second cigarette filter wrapping paper (29).

5. The cigarette filter of claim 1, wherein the polymer sheet (210) has a horizontal length (a) and a vertical length (b), and is folded irregularly in a direction of the horizontal length (a).

6. A cigarette (1) comprising: a cigarette filler portion (10); a cigarette paper (19) surrounding the cigarette filler portion (10); a cigarette filter portion (20) connected to the cigarette filler portion (10); and a tipping paper (31) connecting the cigarette filler portion (10) and the cigarette filter portion (20), wherein the cigarette filter portion (20) comprises a first filter portion (21) comprising an irregularly folded and packed polymer sheet (210), and a first cigarette filter wrapping paper (28) surrounding the polymer sheet (210), wherein the polymer sheet (210) comprises a first polymer layer (211) containing polyolefin or polyester, and a second polymer layer (212) positioned on the first polymer layer (211) and containing polyolefin, wherein a basis weight of the first polymer layer (211) is 5 GSM to 20 GSM, a basis weight of the second polymer layer (212) is 10 GSM to 30 GSM, and the basis weight of the second polymer layer (212) is larger than the basis weight of the first polymer layer (211).

7. A manufacturing method of a cigarette filter comprising the steps of: preparing a first polymer layer (211) using polyolefin or polyester; preparing a polymer sheet (210) by forming a second polymer layer (212) on the first polymer layer (211) using polyolefin; preparing a first filter portion (21) by irregularly folding the polymer sheet (210); and surrounding the first filter portion (21) with a first cigarette filter wrapping paper (28), wherein a basis weight of the first polymer layer (211) is 5 GSM to 20 GSM, a basis weight of the second polymer layer (212) is 10 GSM to 30 GSM, and the basis weight of the second polymer layer (212) is larger than the basis weight of the first polymer layer (211).

8. The manufacturing method of the cigarette filter of claim 7, wherein the second polymer layer (212) is laminated on the first polymer layer (211) by a melt-blown process.

9. The manufacturing method of the cigarette filter of claim 8, wherein the polymer sheet (210) is irregularly folded by a crimping process.