RTB-BASED PERMANENT MAGNETIC MATERIAL, METHOD FOR ITS MANUFACTURING AND ITS USE

Description

Technical Field

[0001] The present disclosure relates to an R-T-B permanent magnet material, a preparation method therefor, and use thereof.Background

[0002] Since the discovery of Nd 2 Fe 14 B by Soviet scientists in 1979, the researchers in the United States and Japan have been the first to study the properties of this phase, the phase composed of PrNd (with the mass ratio of Pr to Nd of 20:80 or 25:75) has been used in commercial production of sintered permanent magnet, due to its advantages of high magnetic energy product and high remanence, at present it has been widely used in motor, electroacoustic device, computer hard disk drive (HDD), military equipment, human nuclear magnetic resonance imaging (MRI), microwave communication technology, controller, instrument and so on.

[0003] With the progress of science and technology, the performance of Nd-Fe-B has been put forward higher requirements, many researchers have improved the performance of neodymium-iron-boron magnet material by adding a large amount of heavy rare earth Dy or Tb, however, excessive use of heavy rare earths will dramatically increase the cost of materials, and at the same time, the resources of heavy rare earths are relatively few.

[0004] Therefore, the technical problem to be solved urgently in this field is how to make use of the elements with abundant resources to obtain the neodymium-iron-boron material with high coercivity, high remanence and stable temperature coefficient.

[0005] CN 107 887 091 A, CN 104 979 062 A, and CN 103 366 918 A show magnet compositions that are rich in Pr, add in Al, Cu, and refractive metals, but advise a low content of Cu and refractive metal.Content of the present invention

[0006] The technical problem to be solved in the present disclosure is for overcoming the defects that the performance improvement of sintered neodymium-iron-boron magnet is excessively dependent on heavy rare earth elements in the prior art, instead, the present disclosure provides an R-T-B permanent magnet material, a preparation method therefor and a use thereof. The sintered permanent magnet product with high coercivity and stable temperature coefficient is prepared by improving the content of Pr. The PrNd used in the disclosure is associated rare earth with abundant reserves, the formulation of the disclosure can maximize the advantage of Pr and reduce the production cost effectively.

[0007] In the course of research and development, the inventors found that the phase formed by Pr easily leads to the deterioration of the temperature coefficient of the R-T-B permanent magnet material, after creative efforts, the inventors found that adding metals such as Ti, Zr or Nb while increasing the content of Pr can effectively solve the problem of the deterioration of the temperature coefficient caused by high content of Pr. The material of the invention is specified in independent claim 1. The use of the material is specified in independent claim 3. In the following description of the disclosure, a broader outlook on material compositions is given.

[0008] The present disclosure provides an R-T-B permanent magnet material, which comprises the following components by mass percentage: R': 29.5-33.0 wt.%, R' comprising R and Pr, Nd; wherein: R is a rare earth element other than Pr and Nd, the content of Pr is ≥ 8.85 wt.%, the mass ratio of Nd to R' is < 0.5; N: > 0.05 wt.%, and ≤ 4.1 wt.%, N being Ti, Zr or Nb; B: 0.90-1.2 wt.%; Fe: 62.0-68.0 wt.%.

[0009] In the present disclosure, the content of R' is preferably 30-33 wt.%, for example, 30.63-32.52 wt.%, for another example, 30.63 wt.%, 30.72 wt.%, 30.74 wt.%, 30.75 wt.%, 30.76 wt.%, 30.77 wt.%, 30.78 wt.%, 30.8 wt.%, 30.81 wt.%, 30.82 wt.%, 30.83 wt.%, 30.84 wt.%, 30.9 wt.%, 30.91 wt.%, 30.93 wt.%, 30.94 wt.%, 30.97 wt.%, 30.98 wt.%, 30.99 wt.%, 31 wt.%, 31.02 wt.%, 31.03 wt.%, 31.05 wt.%, 31.14 wt.%, 31.4 wt.%, 31.41 wt.%, 31.44 wt.%, 31.46 wt.%, 31.54 wt.%, 31.55 wt.%, 31.56 wt.%, 31.94 wt.%, 32.03 wt.% or 32.52 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0010] In the present disclosure, the content of Pr is preferably ≥ 17.00 wt.%, more preferably 17.00-20.00 wt.%, for example, 17.08 wt.%, 17.11 wt.%, 17.12 wt.%, 17.13 wt.%, 17.14 wt.%, 17.16 wt.%, 17.18 wt.%, 17.19 wt.%, 18.13 wt.%, 18.14 wt.%, 18.15 wt.%, 18.16 wt.%, 18.17 wt.%, 18.19 wt.%, 19.09 wt.%, 19.12 wt.%, 19.13 wt.%, 19.14 wt.%, 19.15 wt.%, 19.16 wt.% or 19.17 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0011] In the present disclosure, the content of Nd is preferably 11-15 wt.%, for example, 11.32-14.35 wt.%, for another example, 11.32 wt.%, 11.35 wt.%, 11.36 wt.%, 11.37 wt.%, 11.39 wt.%, 11.61 wt.%, 11.62 wt.%, 11.63 wt.%, 11.64 wt.%, 11.65 wt.%, 11.84 wt.%, 11.85 wt.%, 11.87 wt.%, 12.29 wt.%, 12.32 wt.%, 12.36 wt.%, 12.37 wt.%, 12.39 wt.%, 12.58 wt.%, 12.62 wt.%, 12.63 wt.%, 12.65 wt.%, 12.66 wt.%, 12.72 wt.%, 12.82 wt.%, 12.83 wt.%, 12.84 wt.%, 12.85 wt.%, 13.32 wt.%, 13.59 wt.%, 13.64 wt.%, 13.65 wt.%, 13.67 wt.%, 13.68 wt.%, 13.78 wt.%, 13.79 wt.%, 13.83 wt.%, 13.84 wt.%, 13.89 wt.% or 14.35 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material;

[0012] In the present disclosure, the mass ratio of Nd to R' is preferably ≥ 0.3 and < 0.5, for example, 0.36-0.45, for another example, 0.36, 0.37, 0.38, 0.39, 0.41, 0.42, 0.44 or 0.45.

[0013] In the present disclosure, R' further comprises R, R is a rare earth element other than Pr and Nd.

[0014] Wherein, the kind of R is preferably Y and / or Ce.

[0015] Wherein, the content of R is preferably 0-1 wt.%, for example, 0.25 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0016] In the present disclosure, R' further comprises a heavy rare earth element RH.

[0017] Wherein, the kind of RH can be Dy and / or Tb.

[0018] Wherein, the content of RH can be the conventional content in this field, preferably 1.0-2.5 wt.%, for example, 1.12 wt.%, 1.18 wt.%, 1.53 wt.%, 1.58 wt.%, 1.9 wt.%, 2.02 wt.% or 2.43 wt.%, the percentage refers to the mass percentage of the R-T-B permanent magnet material.

[0019] Wherein, the mass ratio of RH to R is preferably < 0.253, for example, 0.04-0.08, for another example, 0.04, 0.05, 0.06 or 0.08.

[0020] When the RH comprises Tb, the content of Tb is preferably 0.5-2wt.%, for example, 1.9 wt.%, 1.12 wt.%, 1.18 wt.% or 1.58 wt.%, the percentage refers to the mass percentage of the R-T-B permanent magnet material.

[0021] When the RH comprises Dy, the content of Dy is preferably 1.5-2.5 wt.%, for example, 1.53 wt.%, 2.43 wt.% or 2.02 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0022] In the present disclosure, the content of N is preferably 0.1-4.01 wt.%, for example, 0.13 wt.%, 0.24 wt.%, 0.26 wt.%, 0.28 wt.%, 0.29 wt.%, 0.3 wt.%, 0.31 wt.%, 0.32 wt.%, 0.34 wt.%, 0.35 wt.%, 0.39 wt.%, 0.4 wt.%, 0.42 wt.%, 0.44 wt.%, 0.48 wt.%, 0.5 wt.%, 0.6 wt.%, 0.99 wt.%, 1.01 wt.%, 1.49 wt.%, 1.51 wt.%, 1.99 wt.%, 2.01 wt.%, 2.98 wt.%, 2.99 wt.% or 4.01 wt.%, further preferably 0.1-0.5 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0023] When the N is Zr, the content of Zr is preferably 0.20-4.01 wt.%, for example, 0.24 wt.%, 0.28 wt.%, 0.30 wt.%, 0.31 wt.%, 0.32 wt.%, 0.42 wt.%, 0.99 wt.%, 1.49 wt.%, 1.99 wt.%, 2.99 wt.% or 4.01 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0024] When the N is Ti, the content of Ti is preferably ≥ 0.25 wt.%, more preferably 0.25-4.01 wt.% , further preferably 0.25-0.50 wt.%, for example, 0.28 wt.%, 0.29 wt.%, 0.31 wt.%, 0.32 wt.%, 0.34 wt.%, 0.35 wt.%, 0.39 wt.%, 0.4 wt.%, 0.42 wt.%, 0.44 wt.%, 0.48 wt.%, 0.5 wt.%, 0.6 wt.%, 1.01 wt.%, 1.51 wt.%, 2.01 wt.%, 2.98 wt.% or 4.01 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0025] When the N is Nb, the content of Nb is preferably ≥ 0.1 wt.%, more preferably 0.1-0.35 wt.%, for example, 0.13 wt.%, 0.26 wt.%, 0.28 wt.%, 0.29 wt.%, 0.31 wt.% or 0.32 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0026] In the present disclosure, the content of B is preferably 0.9-1.0 wt.%, for example, 0.91 wt.%, 0.98 wt.% or 0.99 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0027] In the present disclosure, the content of Fe is preferably 62.3-68.0 wt.%, for example, 62.34 wt.%, 62.87 wt.%, 62.98 wt.%, 63.01 wt.%, 63.49 wt.%, 63.67 wt.%, 63.71 wt.%, 63.78 wt.%, 63.98 wt.%, 64.00 wt.%, 64.15 wt.%, 64.21 wt.%, 64.78 wt.%, 65.02 wt.%, 65.24 wt.%, 65.27 wt.%, 66.03 wt.%, 66.18 wt.%, 66.20 wt.%, 66.52 wt.%, 66.55 wt.%, 66.57 wt.%, 66.74 wt.%, 66.82 wt.%, 66.92 wt.%, 66.93 wt.%, 67.01 wt.%, 67.02 wt.%, 67.04 wt.%, 67.15 wt.%, 67.19 wt.%, 67.23 wt.%, 67.24 wt.%, 67.27 wt.%, 67.29 wt.%, 67.31 wt.%, 67.32 wt.%, 67.35 wt.%, 67.37 wt.%, 67.40 wt.%, 67.42 wt.%, 67.43 wt.%, 67.47 wt.%, 67.48 wt.%, 67.53 wt.%, 67.54 wt.%, 67.56 wt.%, 67.62 wt.%, 67.70 wt.%, 67.71 wt.%, 67.75 wt.%, 67.81 wt.%, 67.84 wt.%, 67.94 wt.%, 67.95 wt.% or 67.98 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0028] In the present disclosure, the R-T-B permanent magnet material further comprises one or more of Cu, Al, Ga and Co.

[0029] Wherein, the content of Cu can be the conventional content in this field, preferably ≥ 0.30 wt.%, more preferably 0.30-0.55 wt.%, for example, 0.33 wt.%, 0.34 wt.%, 0.37 wt.%, 0.38 wt.%, 0.39 wt.%, 0.4 wt.%, 0.41 wt.%, 0.42 wt.%, 0.44 wt.%, 0.45 wt.%, 0.49 wt.%, 0.51 wt.% or 0.52 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0030] Wherein, the content of Al can be the conventional content in this field, preferably 0-0.8 wt.%, but not 0, more preferably 0.041-0.70 wt.%, for example, 0.041 wt.%, 0.043 wt.%, 0.1 wt.%, 0.2 wt.%, 0.31 wt.%, 0.32 wt.%, 0.38 wt.%, 0.41 wt.%, 0.48 wt.%, 0.49 wt.%, 0.50 wt.%, 0.58 wt.%, 0.59 wt.%, 0.60 wt.%, 0.61 wt.%, 0.62 wt.%, 0.69 wt.% or 0.70 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0031] Wherein, the content of Ga can be the conventional content in this field, Ga is preferably 0.0-0.85 wt.%, but not 0, more preferably 0.21-0.81 wt.%, for example, 0.21 wt.%, 0.23 wt.%, 0.38 wt.%, 0.39 wt.%, 0.40 wt.%, 0.41 wt.%, 0.42 wt.%, 0.43 wt.%, 0.58 wt.%, 0.59 wt.% or 0.81 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0032] Wherein, the content of Co can be the conventional content in this field, the content of Co is preferably 0.0-3.0 wt.%, but not 0, more preferably 0.4-3.0 wt.%, for example, 0.49 wt.%, 0.51 wt.%, 0.95 wt.%, 1.1 wt.%, 2.35 wt.%, 2.4 wt.%, 2.42 wt.%, 2.45 wt.%, 2.51 wt.% or 2.53 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0033] In the present disclosure, the R-T-B permanent magnet material further comprises common addition element M, such as one or more of Ni, Zn, Ag, In, Sn, Bi, V, Cr, Hf, Ta, and W.

[0034] Wherein, the kind of M is preferably Cr.

[0035] Wherein, the content of M is preferably 0-0.15 wt.%, but not 0, for example, 0.05 wt.% or 0.12 wt.%.

[0036] In a preferred embodiment of the present disclosure, the R-T-B permanent magnet material comprises the following components: R': 29.5-33.0 wt.%, Pr ≥ 17.00 wt.%, N: 0.1-4.01 wt.%, Cu: 0.30-0.55 wt.%, B: 0.9 -1.0 wt.%, Fe: 62.0-68.0 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0037] When the N is Zr, the content of N is preferably 0.25-0.35 wt.%, the content of Cu is preferably 0.30-0.41 wt.%, for example, Zr 0.32 wt.%, Cu 0.33 wt.%, Zr 0.31 wt.%, Cu 0.41 wt.%, or, Zr 0.28 wt.%, Cu 0.39 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0038] When the N is Ti, the content of N is preferably 0.30-0.60 wt.%, the content of Cu is preferably 0.34-0.51 wt.%. The content of Ti is preferably 0.31 wt.%, 0.32 wt.%, 0.34 wt.%, 0.4 wt.%, 0.42 wt.%, 0.44 wt.%, 0.5 wt.% or 0.6 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material. The content of Cu is preferably 0.34 wt.%, 0.38 wt.%, 0.4 wt.%, 0.41 wt.%, 0.44 wt.%, 0.45 wt.% or 0.51 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0039] When the N is Nb, the content of N is preferably 0.25-0.35 wt.%, the content of Cu is preferably 0.40-0.55 wt.%. The content of Nb is preferably 0.28 wt.%, 0.29 wt.%, 0.31 wt.% or 0.32 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material. The content of Cu is preferably 0.37 wt.%, 0.38 wt.%, 0.41 wt.%, 0.42 wt.%, 0.49 wt.% or 0.52 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0040] In a preferred embodiment of the present disclosure, the R-T-B permanent magnet material comprises the following components: R': 29.5-33.0 wt.%, Pr ≥ 17.00 wt.%, N: 0.2-0.6 wt.%, Al: 0-0.8 wt.%, but not 0, B: 0.9-1.0 wt.%, Fe: 62.0-68.0 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0041] When the N is Zr, the content of N is preferably 0.25-0.35 wt.%, the content of Al is preferably 0.40-0.70 wt.%, the content of Zr is preferably 0.28 wt.%, 0.31 wt.%, or 0.32 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material. The content of Al is preferably 0.49 wt.%, 0.5 wt.%, 0.59 wt.% or 0.62 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0042] When the N is Ti, the content of N is preferably 0.25-0.60 wt.%, the content of Al is preferably 0.041-0.7 wt.%. The content of Ti is preferably 0.28 wt.%, 0.31 wt.%, 0.32 wt.%, 0.34 wt.%, 0.35 wt.%, 0.39 wt.% 0.42 wt.%, 0.44 wt.%, 0.5 wt.% or 0.6 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material. The content of Al is preferably 0.041 wt.%, 0.043 wt.%, 0.1 wt.%, 0.2 wt.%, 0.31 wt.%, 0.32 wt.% 0.38 wt.%, 0.41 wt.%, 0.48 wt.%, 0.6 wt.% or 0.62 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0043] When the N is Nb, the content of N is preferably 0.25-0.35 wt.%, the content of Al is preferably 0.60-0.80 wt.%. The content of Nb is preferably 0.28 wt.%, 0.29 wt.%, 0.31 wt.%, or 0.32 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material. The content of Al is preferably 0.58 wt.%, 0.59 wt.%, 0.61 wt.%, 0.62 wt.%, 0.69 wt.%, or 0.7 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0044] In a preferred embodiment of the present disclosure, the R-T-B permanent magnet material comprises the following components: R': 29.5-33.0 wt.%, Pr ≥ 17.00 wt.%, N: 0.2-0.6 wt.%, Ga: 0-0.81 wt.%, but not 0, B: 0.9-1.0 wt.%, Fe: 62.0-68.0 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0045] When the N is Zr, the content of N is preferably 0.25-0.35 wt.%, the content of Ga is preferably 0.20-0.45 wt.%. The content of Zr is preferably 0.28 wt.%, 0.31 wt.% or 0.32 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material. The content of Ga is preferably 0.21 wt.%, 0.41 wt.% or 0.42 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0046] When the N is Ti, the content of N is preferably 0.25-0.50 wt.%, the content of Ga is preferably 0.2-0.81 wt.%. The content of Ti is preferably 0.28 wt.%, 0.29 wt.%, 0.31 wt.%, 0.34 wt.% or 0.42 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material. The content of Ga is preferably 0.23 wt.%, 0.39 wt.%, 0.41 wt.%, 0.58 wt.% or 0.81 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0047] When the N is Nb, the content of N is preferably 0.25-0.35 wt.%, the content of Ga is preferably 0.30-0.60 wt.%. The content of Nb is preferably 0.28 wt.%, 0.29 wt.%, 0.31 wt.% or 0.32 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material. The content of Ga is preferably 0.38 wt.%, 0.4 wt.%, 0.41 wt.%, 0.42 wt.%, 0.43 wt.%, 0.58 wt.% or 0.59 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0048] In a preferred embodiment of the present disclosure, the R-T-B permanent magnet material comprises the following components: R': 29.5-33.0 wt.%, Pr ≥ 17.00 wt.%, N: 0.2-0.6 wt.%, Cu: 0.30-0.55 wt.%, Al: 0-0.8 wt.%, but not 0, B: 0.9-1.0 wt.%, Fe: 62.0-68.0 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0049] Wherein, the content of N is preferably 0.28-0.6 wt.%, for example, 0.28 wt.%, 0.29 wt.%, 0.31 wt.%, 0.32 wt.%, 0.34 wt.%, 0.42 wt.%, 0.44 wt.%, 0.5 wt.% or 0.6 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0050] Wherein, the content of Cu is preferably 0.33-0.52 wt.%, for example, 0.33 wt.%, 0.34 wt.%, 0.37 wt.%, 0.38 wt.%, 0.39 wt.%, 0.4 wt.%, 0.41 wt.%, 0.42 wt.%, 0.45 wt.%, 0.51 wt.% or 0.52 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0051] Wherein, the content of Al is preferably 0.043-0.69 wt.%, for example, 0.043 wt.%, 0.1 wt.%, 0.2 wt.%, 0.32 wt.%, 0.41 wt.%, 0.48 wt.%, 0.49 wt.%, 0.58 wt.%, 0.59 wt.%, 0.61 wt.%, 0.62 wt.% or 0.69 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0052] In a preferred embodiment of the present disclosure, the R-T-B permanent magnet material comprises the following components: R': 29.5-33.0 wt.%, Pr ≥ 17.00 wt.%, N: 0.25-0.35 wt.%, Cu: 0.30-0.55 wt.%, Al: 0.45-0.7 wt.%, Ga: 0.2-0.6 wt.%, Co: 0.5-3.0 wt.%, B: 0.9-1.0 wt.%, Fe: 62.0-68.0 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0053] Wherein, the content of N is preferably 0.28-0.6 wt.%, for example, 0.28 wt.%, 0.29 wt.%, 0.31 wt.% or 0.32 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0054] Wherein, the content of Cu is preferably 0.33-0.52 wt.%, for example, 0.33 wt.%, 0.37 wt.%, 0.38 wt.%, 0.39 wt.%, 0.41 wt.%, 0.42 wt.% or 0.52 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0055] Wherein, the content of Al is preferably 0.49-0.69 wt.%, for example, 0.49 wt.%, 0.58 wt.%, 0.59 wt.%, 0.61 wt.%, 0.62 wt.% or 0.69 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0056] Wherein, the content of Ga is preferably 0.20-0.69 wt.%, for example, 0.21 wt.%, 0.38 wt.%, 0.39 wt.%, 0.4 wt.%, 0.41 wt.%, 0.42 wt.%, 0.43 wt.% or 0.59 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0057] Wherein, the content of Co is preferably 0.5-2.6 wt.%, for example, 0.51 wt.%, 1.1 wt.%, 2.35 wt.%, 2.4 wt.%, 2.42 wt.%, 2.45 wt.%, 2.51 wt.% or 2.53 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0058] In a preferred embodiment of the present disclosure, the R-T-B permanent magnet material comprises the following components: R': 29.5-33.0 wt.%, Pr ≥ 17.00 wt.%, N: 0.25-0.35 wt.%, Cr: 0-0.15 wt.%, Cu: 0.30-0.55 wt.%, Al: 0.45-0.7 wt.%, Ga: 0.2-0.6 wt.%, Co: 0.5-3.0 wt.%, B: 0.9-1.0 wt.%, Fe: 62.0-68.0 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0059] In a preferred embodiment of the present disclosure, the R-T-B permanent magnet material comprises the following components: R': 29.5-33.0 wt.%, Pr ≥ 17.00 wt.%, RH: 1.0-2.5 wt.%, N: 0.25-0.35 wt.%, Cu: 0.30-0.55 wt.%, Al: 0.45-0.7 wt.%, Ga: 0.2-0.6 wt.%, Co: 0.5-3.0 wt.%, B: 0.9-1.0 wt.%, Fe: 62.0-68.0 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0060] The present disclosure further provides a raw material composition of R-T-B permanent magnet material, which comprises the following components by mass percentage: R': 29.5-32.0 wt.%, R' comprising R and Pr, Nd; wherein: R is a rare earth element other than Pr and Nd, the content of Pr is ≥ 8.85 wt.%, the mass ratio of Nd to R' is < 0.5; N: > 0.05 wt.%, and ≤ 4.0 wt.%, N being Ti, Zr or Nb; B: 0.90-1.2 wt.%; Fe: 62.0-68.0 wt.%.

[0061] In the present disclosure, the content of R' is preferably 30.0-32.0 wt.%, further preferably 30.7-32.0 wt.%, for example, 30.7 wt.%, 30.8 wt.%, 31.0 wt.%, 31.5 wt.% or 32.0 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0062] In the present disclosure, the content of Pr is preferably ≥17.15 wt.%, more preferably 17.15-19.15 wt.%, for example, 17.15 wt.%, 18.15 wt.% or 19.15 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0063] In the present disclosure, the content of Nd is preferably 11.00-15.00 wt.%, further preferably 11.35-14.35 wt.%, for example, 11.35 wt.%, 11.65 wt.%, 11.85 wt.%, 12.35 wt.%, 12.65 wt.%, 12.85 wt.%, 13.35 wt.%, 13.65 wt.%, 13.85 wt.% or 14.35 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0064] In the present disclosure, the mass ratio of Nd to R' is preferably ≥ 0.3 and < 0.5, preferably 0.35-0.46, for example, 0.35, 0.36, 0.37, 0.38, 0.39, 0.41, 0.42, 0.43, 0.44, 0.45 or 0.46.

[0065] In the present disclosure, R' further comprises R, R is a rare earth element other than Pr and Nd.

[0066] Wherein, the kind of R is preferably Y and / or Ce.

[0067] Wherein, the content of R is preferably 0-1 wt.%, for example, 0.3 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0068] In the present disclosure, R' further comprises a heavy rare earth element RH.

[0069] Wherein, the kind of RH is preferably Dy and / or Tb.

[0070] Wherein, the content of RH can be the conventional content in this field, preferably 1.0-2.5 wt.%, for example, 1.2 wt.%, 1.5 wt.%, 2.0 wt.% or 2.5 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0071] Wherein, the mass ratio of RH to R' is preferably < 0.253, for example, 0.04-0.08, for another example, 0.04, 0.05, 0.06 or 0.08.

[0072] When the RH comprises Tb, the content of Tb is preferably 0.5-2 wt.%, for example, 1.2 wt.% or 2.0 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0073] When the RH comprises Dy, the content of Dy is preferably 1.5-2.5 wt.%, for example, 1.5 wt.% or 2.5 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0074] In the present disclosure, the content of N is preferably 0.15-4 wt.%, for example, 0.15 wt.%, 0.25 wt.%, 0.3 wt.%, 0.35 wt.%, 0.4 wt.%, 0.45 wt.%, 0.5 wt.%, 0.6 wt.%, 1.0 wt.%, 1.5 wt.%, 2.0 wt.%, 3.0 wt.% or 4.0 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0075] When the N is Zr, the content of Zr is preferably 0.25-4.0 wt.%, for example, 0.25 wt.%, 0.3 wt.%, 0.4 wt.%, 1.0wt.%, 1.5wt.%, 2.0wt.%, 3.0wt.% or 4.0wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0076] When the N is Ti, the content of Ti is preferably ≥ 0.3 wt.%, for example, 0.30 wt.%, 0.35wt.%, 0.40 wt.%, 0.45 wt.%, 0.50 wt.%, 0.60 wt.%, 1.0wt.%, 1.5wt.%, 2.0wt.%, 3.0wt.% or 4.0wt.%, more preferably 0.30-0.50 wt.%, the percentage refers to the mass percentage in the R-T-B permanent magnet material.

[0077] When the N is Nb, the content of Nb is preferably 0.15-0.30 wt.%, for example, 0.15 wt.%, 0.25wt.% or 0.30 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0078] In the present disclosure, the content of B is preferably ≥ 0.985 wt.%, for example, 0.985 wt.% or 0.99 wt.%.

[0079] In the present disclosure, the content of Fe is 62.81-67.92 wt.%, for example, 62.81 wt.%, 62.92 wt.%, 63.31 wt.%, 63.70 wt.%, 63.77 wt.%, 63.81 wt.%, 64.02 wt.%, 64.11 wt.%, 64.22 wt.%, 64.72 wt.%, 65.02 wt.%, 65.22 wt.%, wt.%, 65.52 wt.%, 66.02 wt.%, 66.18 wt.%, 66.22 wt.%, 66.52 wt.%, 66.62 wt.%, 66.72 wt.%, 66.77 wt.%, 66.92 wt.%, 66.97 wt.%, 67.02 wt.%, 67.17 wt.%, 67.22 wt.%, 67.24 wt.%, 67.27 wt.%, 67.32 wt.%, 67.37 wt.%, 67.38 wt.%, 67.42 wt.%, 67.52 wt.%, 67.53 wt.%, 67.57 wt.%, 67.62 wt.%, 67.67 wt.%, 67.72 wt.%, 67.80 wt.%, 67.82 wt.%, 67.85 wt.%, 67.87 wt.% or 67.92 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0080] In the present disclosure, the raw material composition of R-T-B permanent magnet material further comprises one or more of Al, Cu, Ga and Co.

[0081] Wherein, the content of Cu can be the conventional content in this field, preferably ≥ 0.34 wt.%, more preferably 0.34-0.5 wt.%, for example, 0.34 wt.%, 0.38 wt.%, 0.40 wt.%, 0.45 wt.% or 0.50 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0082] Wherein, the content of Al can be the conventional content in this field, preferably 0.042-0.7 wt.%, for example, 0.042 wt.%, 0.1 wt.%, 0.2 wt.%, 0.3 wt.%, 0.4 wt.%, 0.5 wt.%, 0.6 wt.% or 0.7 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0083] Wherein, the content of Ga can be the conventional content in this field, preferably 0.0-0.8 wt.%, but not 0, more preferably 0.2-0.8 wt.%, for example, 0.2 wt.%, 0.25 wt.%, 0.4 wt.%, 0.6 wt.% or 0.8 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0084] Wherein, the content of Co can be the conventional content in this field, preferably 0.0-3.0 wt.%, but not 0, more preferably 0.5-2.5 wt.%, for example, 0.5 wt.%, 1.0 wt.% or 2.5 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0085] In the present disclosure, the raw material composition of R-T-B permanent magnet material further comprises common addition element M, such as one or more of Ni, Zn, Ag, In, Sn, Bi, V, Cr, Hf, Ta, and W.

[0086] Wherein, the kind of M is preferably Cr.

[0087] Wherein, the content of M is preferably 0-0.15 wt.%, but not 0, for example, 0.05 wt.% or 0.12 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0088] As a preferred embodiment of the present disclosure, the R-T-B permanent magnet material comprises the following components: R': 29.5-32.0 wt.%, Pr ≥ 17.15 wt.%, N: 0.3-0.6 wt.%, Cu: 0.34-0.55 wt.%, B: 0.9-1.0 wt.%, Fe: 62.0-68.0 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0089] When the N is Zr, the content of N is preferably 0.25-0.35 wt.%, the content of Cu is preferably 0.34-0.40 wt.%, for example, Zr 0.30 wt.%, Cu 0.34 wt.%, or, Zr 0.30 wt.%, Cu 0.40 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0090] When the N is Ti, the content of N is preferably 0.30-0.60 wt.%, the content of Cu is preferably 0.34-0.5 wt.%. The the content of Ti is preferably 0.3 wt.%, 0.35 wt.%, 0.4 wt.%, 0.45 wt.%, 0.5 wt.% or 0.6 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material. The content of Cu is preferably 0.34 wt.%, 0.38 wt.%, 0.4 wt.%, 0.45 wt.% or 0.5 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0091] When the N is Nb, the content of N is preferably 0.25-0.35 wt.%, the content of Cu is preferably 0.4-0.5 wt.%. The content of Nb is preferably 0.30 wt.%, the content of Cu is preferably 0.4 wt.% or 0.5 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0092] As a preferred embodiment of the present disclosure, the R-T-B permanent magnet material comprises the following components: R': 29.5-32.0 wt.%, Pr ≥ 17.15 wt.%, N: 0.2-0.6 wt.%, Al: 0-0.8 wt.%, but not 0, B: 0.9-1.0 wt.%, Fe: 62.0-68.0 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0093] When the N is Zr, the content of N is preferably 0.25-0.35 wt.%, the content of Al is preferably 0.5-0.6 wt.%. The content of Zr is preferably 0.3 wt.%, the content of Al is preferably 0.5 wt.% or 0.6 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0094] When the N is Ti, the content of N is preferably 0.30-0.60 wt.%, the content of Al is preferably 0.042-0.6 wt.%. The content of Ti is preferably 0.3 wt.%, 0.35 wt.%, 0.4 wt.%, 0.45 wt.%, 0.5 wt.% or 0.6 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material. The content of Al is preferably 0.042 wt.%, 0.1 wt.%, 0.2 wt.%, 0.3 wt.%, 0.4 wt.%, 0.5 wt.% or 0.6 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0095] When the N is Nb, the content of N is preferably 0.25-0.35 wt.%, the content of Al is preferably 0.60-0.70 wt.%. The content of Nb is preferably 0.30 wt.%, the content of Al is preferably 0.60 wt.% or 0.70 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0096] As a preferred embodiment of the present disclosure, the R-T-B permanent magnet material comprises the following components: R': 29.5-32.0 wt.%, Pr ≥ 17.15 wt.%, N: 0.3-0.4 wt.%, Ga: 0.2-0.8 wt.%, B: 0.9 -1.0 wt.%, Fe: 62.0-68.0 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0097] When the N is Zr, the content of N is preferably 0.25-0.35 wt.%, the content of Ga is preferably 0.2-0.4 wt.%. The content of Zr is preferably 0.3 wt.%, the content of Ga is preferably 0.2 wt.% or 0.4 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0098] When the N is Ti, the content of N is preferably 0.3-0.4 wt.%, the content of Ga is preferably 0.25-0.8 wt.%. The content of Ti is preferably 0.3 wt.%, 0.35 wt.% or 0.4 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material. The content of Ga is preferably 0.25 wt.%, 0.4 wt.%, 0.6 wt.% or 0.8 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0099] When the N is Nb, the content of N is preferably 0.25-0.35 wt.%, the content of Ga is preferably 0.40-0.60 wt.%, the content of Nb is preferably 0.3 wt.%, the content of Ga is preferably 0.4 wt.% or 0.60 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0100] As a preferred embodiment of the present disclosure, the R-T-B permanent magnet material comprises the following components: R': 29.5-32.0 wt.%, Pr ≥ 17.15 wt.%, N: 0.2-0.6 wt.%, Cu: 0.30-0.5 wt.%, Al: 0-0.8 wt.%, but not 0, B: 0.9 -1.0 wt.%, Fe: 62.0-68.0 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0101] Wherein, the content of N is preferably 0.25-0.3 wt.%, for example, 0.3 wt.%, 0.35 wt.%, 0.4 wt.%, 0.45 wt.%, 0.5 wt.% or 0.6 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0102] Wherein, the content of Cu is preferably 0.34-0.52 wt.%, for example, 0.34 wt.%, 0.38 wt.%, 0.4 wt.%, 0.45 wt.% or 0.5 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0103] Wherein, the content of Al is preferably 0.042-0.7 wt.%, for example, 0.042 wt.%, 0.1 wt.%, 0.2 wt.%, 0.3 wt.%, 0.4 wt.%, 0.5 wt.%, 0.6 wt.% or 0.7 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0104] As a preferred embodiment of the present disclosure, the R-T-B permanent magnet material comprises the following components: R': 29.5-32.0 wt.%, Pr ≥ 17.15 wt.%, N: 0.25-0.35 wt.%, Cu: 0.3-0.5 wt.%, Al: 0.5-0.7 wt.%, Ga: 0.2-0.6 wt.%, Co: 0.5-3.0 wt.%, B: 0.9-1.0 wt.%, Fe: 62.0-68.0 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0105] Wherein, the content of N is preferably 0.25-0.3 wt.%, for example, 0.3 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0106] Wherein, the content of Cu is preferably 0.34-0.5 wt.%, for example, 0.34 wt.%, 0.4 wt.% or 0.5 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0107] Wherein, the content of Al is preferably 0.5-0.7 wt.%, for example, 0.5 wt.%, 0.6 wt.% or 0.7 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0108] Wherein, the content of Ga is preferably 0.2-0.6 wt.%, for example, 0.2 wt.%, 0.4 wt.% or 0.6 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0109] Wherein, the content of Co is preferably 0.5-2.5 wt.%, for example, 0.5 wt.%, 1.0 wt.% or 2.5 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0110] As a preferred embodiment of the present disclosure, the R-T-B permanent magnet material comprises the following components: R': 29.5-32.0 wt.%, Pr ≥ 17.15 wt.%, N: 0.25-0.35 wt.%, Cu: 0.3-0.5 wt.%, Al: 0.5-0.7 wt.%, Ga: 0.2-0.6 wt.%, Co: 0.5-3.0 wt.%, Cr: 0-0.15 wt.%, B: 0.9-1.0 wt.%, Fe: 62.0-68.0 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0111] As a preferred embodiment of the present disclosure, the R-T-B permanent magnet material comprises the following components: R': 29.5-32.0 wt.%, Pr ≥ 17.15 wt.%, RH: 1.0-2.5 wt.%, N: 0.25-0.35 wt.%, Cu: 0.30-0.55 wt.%, Al: 0.45-0.7 wt.%, Ga: 0.2-0.6 wt.%, Co: 0.5-3.0 wt.%, B: 0.9-1.0 wt.%, Fe: 62.0-68.0 wt.%, the percentage refers to the mass percentage in the raw material composition of R-T-B permanent magnet material.

[0112] The present disclosure further provides a preparation method for the R-T-B permanent magnet material, which comprises the following steps: the molten liquid of the raw material composition of the R-T-B permanent magnet material is subjected to casting, hydrogen decrepitation, forming, sintering and aging.

[0113] Wherein, the molten liquid of the raw material composition of R-T-B permanent magnet material is prepared by the conventional preparation method in this field, for example, melting in a high frequency vacuum induction melting furnace. The vacuum degree of the melting furnace can be 5×10 -2< Pa. The melting temperature can be 1500°C or less.

[0114] Wherein, the casting process is conventional casting process in this field, for example, cooling at a rate of 10 2< °C / s -10 4< °C / s in an Ar atmosphere (for example, an Ar atmosphere of 5.5 ×10 4< MPa).

[0115] Wherein, the hydrogen decrepitation process is conventional hydrogen decrepitation process in this field, for example, comprises hydrogen absorption, dehydrogenation and cooling treatment.

[0116] The hydrogen absorption can be carried out under the hydrogen pressure of 0.15 MPa.

[0117] The dehydrogenation can be carried out under the condition that the temperature rises while evacuation.

[0118] Wherein, after the hydrogen decrepitation process, it can also be pulverized by conventional means in this field. The pulverizing process can be a conventional pulverizing process in the field, for example, jet mill pulverization.

[0119] The jet mill pulverization can be performed in a nitrogen atmosphere with an oxidizing gas content of 150 ppm or less. The oxidizing gas refers to the oxygen or moisture content.

[0120] The pressure of the crushing chamber of the jet mill pulverization can be 0.38 MPa.

[0121] The Time of the jet mill pulverization can be 3 h.

[0122] After the pulverization, a lubricant can be added to the powder by conventional means in this field, for example, zinc stearate. The added amount of the lubricant can be 0.10-0.15%, for example, 0.12%, by weight of the mixed powder.

[0123] Wherein, the forming process can be conventional forming process in the field, for example, magnetic field forming method or a hot pressing and thermal deformation method.

[0124] Wherein, the sintering process can be conventional sintering process in this field, for example, under vacuum conditions (for example, under the vacuum of 5×10 -3< Pa), preheating, sintering and cooling.

[0125] The temperature of the preheating can be 300-600 °C. The time of the preheating can be 1-2 h. Preferably, the preheating is preheating at 300 °C and 600°C for 1h respectively.

[0126] The temperature of the sintering can be conventional sintering temperature in this field, for example, 1040-1090 °C, for another example, 1050 °C.

[0127] The time of the sintering can be conventional sintering time in this field, for example, 2h.

[0128] Ar gas can be introduced to make the air pressure reach 0.1MPa before the cooling.

[0129] Wherein, preferably, the grain boundary diffusion treatment is further carried out after sintering and before the aging treatment.

[0130] The grain boundary diffusion treatment can be conventional process in this field, for example, attaching substance containing Tb and / or substance containing Dy to the surface of the R-T-B permanent magnet material by evaporating, coating or sputtering, then carrying out diffusion heat treatment.

[0131] The substance containing Tb may be Tb metal, a Tb-containing compound (for example, a Tb-containing fluoride) or alloy.

[0132] The substance containing Dy may be Dy metal, a Dy-containing compound (for example, a Dy-containing fluoride) or alloy.

[0133] The temperature of the diffusion heat treatment is preferably 800-900 °C, for example, 850 °C.

[0134] The time of the diffusion heat treatment is preferably 12-48 h, for example, 24 h.

[0135] Wherein, in the aging treatment, the temperature of the secondary aging is 500-650 °C, for example, 600-650 °C, for another example, 630 °C.

[0136] In the secondary aging, the temperature is increased to 500-650 °C with a heating rate of 3-5 °C / min. The starting point for the heating can be room temperature.

[0137] The treatment time of the secondary aging can be 3h.

[0138] The present disclosure also provides an R-T-B permanent magnet material prepared by the preparation method.

[0139] The present disclosure also provides an R-T-B permanent magnet material, wherein, the main phase crystalline particle is R" 2 Fe 14 B, the R" comprises Pr and Nd, the mass fraction of Pr in the R" is ≥ 60%.

[0140] Wherein, preferably, the components of the R-T-B permanent magnet material are as described above.

[0141] The present disclosure also provides a use of the R-T-B permanent magnet material as electronic components.

[0142] Wherein, the use can be in the automobile drive field, wind power field, servo motor and household electrical appliance field (e.g. air conditioner).

[0143] In the present disclosure, the room temperature refers to 25 °C±5 °C.

[0144] On the basis of conforming to the common knowledge in this field, the above optimal conditions can be combined at will, so as to obtain better examples of the present disclosure.

[0145] The reagents and raw materials used in the present disclosure are commercially available.

[0146] The positive progressive effects of the present disclosure are as follows: (1) The rare earth permanent magnet of the present disclosure has high coercivity, high remanence and stable temperature coefficient and can effectively solve the problem of deterioration of temperature coefficient of the permanent magnet caused by high Pr (Pr ≥ 8.85 wt.%). (2) The rare earth permanent magnet of the present disclosure can utilize the strong anisotropy of Pr 2 Fe 14 B under the condition of no heavy rare earth to realize high coercivity, which is nearly 2kOe higher than the coercivity of conventional process, realizing significant improvement of the performance of products with no heavy rare earth, especially for products with no heavy rare earth in the fields such as automobile drive field and wind power field. At the same time, the utilization amount of the heavy rare earths is effectively saved in the products containing heavy rare earths (for example, servo, air conditioner, etc.) and the production cost is reduced. Brief description of the drawings

[0147] Figure 1 is the distribution diagram of Fe, Ga, Pr, Nd and Co formed by the FE-EPMA surface scanning of the sintered magnet prepared in Embodiment 50. Figure 2 is the distribution diagram of Al, Cu, Zr and B formed by the FE-EPMA surface scanning of the sintered magnet prepared in Embodiment 50. Detailed description of the preferred embodiment

[0148] The following examples further illustrate the present disclosure, but the present disclosure is not limited thereto. Below presents preferred embodiments of the present disclosure based on the drawings in order to illustrate the technical schemes of the present disclosure in detail. In the following table, wt.% refers to the percentage by mass of the component in the raw material composition of the R-T-B permanent magnet material, and " / " means that the element is not added. "Br" refers to remanence, and "Hcj" refers to intrinsic coercivity. Only Embodiments 44-61 are part of the claimed invention.

[0149] The formulas of R-T-B permanent magnet materials of the embodiments and comparative embodiments are shown in Table 1. Table 1No.R kindR contentNd wt.%Pr wt.%RH kindRH wt.%Cu wt.%Al wt.%Ga wt.%Co wt.%N kindN wt.%M kindM wt.%B wt.%Fe wt.%Embodiment 1 / / 13.8517.15 / / / / / / Zr0.25 / / 0.9balanceEmbodiment 2 / / 13.8517.15 / / / / / / Zr0.3 / / 0.9balanceEmbodiment 3 / / 12.8518.15 / / / / / / Zr0.3 / / 0.9balanceEmbodiment 4 / / 11.8519.15 / / / / / / Zr0.3 / / 0.985balanceEmbodiment 5 / / 13.8517.15 / / / / Zr0.4 / / 0.985balanceEmbodiment 6 / / 11.8519.15 / / / / / / Zr1.0 / / 0.985balanceEmbodiment 7 / / 11.8519.15 / / / / / / Zr1.5 / / 0.985balanceEmbodiment 8 / / 11.8519.15 / / / / / / Zr2.0 / / 0.985balanceEmbodiment 9 / / 12.8518.15 / / / / / / Zr3.0 / / 0.985balanceEmbodiment 10 / / 11.8519.15 / / / / / / Zr4.0 / / 0.985balanceEmbodiment 11 / / 13.6517.15 / / / / / / Ti0.3 / / 0.985balanceEmbodiment 12 / / 12.6518.15 / / / / / / Ti0.4 / / 0.985balanceEmbodiment 13 / / 11.6519.15 / / / / / / Ti0.5 / / 0.985balanceEmbodiment 14 / / 11.6519.15 / / / / / / Ti1 / / 0.985balanceEmbodiment 15 / / 11.6519.15 / / / / / / Ti1.5 / / 0.985balanceEmbodiment 16 / / 11.6519.15 / / / / / / Ti2.0 / / 0.985balanceEmbodiment 17 / / 11.6519.15 / / / / / / Ti3.0 / / 0.985balanceEmbodiment 18 / / 11.6519.15 / / / / / / Ti4.0 / / 0.985balanceEmbodiment 19 / / 14.3517.15 / / / / / / Nb0.3 / / 0.985balanceEmbodiment 20 / / 13.3518.15 / / / / / / Nb0.15 / / 0.985balanceEmbodiment 21 / / 12.3519.15 / / / / / / Nb0.25 / / 0.985balanceEmbodiment 22 / / 13.8517.15 / / 0.34 / / / Zr0.3 / / 0.985balanceEmbodiment 23 / / 12.6518.15 / / 0.4 / / / Ti0.3 / / 0.985balanceEmbodiment 24 / / 13.6517.15 / / 0.45 / / / Ti0.4 / / 0.985balanceEmbodiment 25 / / 11.6519.15 / / 0.5 / / / Ti0.5 / / 0.985balanceEmbodiment 26 / / 12.3519.15 / / 0.5 / / / Nb0.3 / / 0.985balanceEmbodiment 27 / / 11.6519.15 / / / 0.042 / / Ti0.3 / / 0.985balanceEmbodiment 28 / / 11.6519.15 / / / 0.1 / / Ti0.5 / / 0.985balanceEmbodiment 29 / / 11.6519.15 / / / 0.2 / / Ti0.6 / / 0.985balanceEmbodiment 30 / / 12.6518.15 / / / 0.3 / / Ti0.35 / / 0.985balanceEmbodiment 31 / / 13.6517.15 / / / 0.4 / / Ti0.40 / / 0.985balanceEmbodiment 32 / / 13.8517.15 / / / 0.5 / / Zr0.3 / / 0.985balanceEmbodiment 33 / / 12.6518.15 / / / 0.6 / / Ti0.3 / / 0.985balanceEmbodiment 34 / / 12.3519.15 / / / 0.7 / / Nb0.3 / / 0.985balanceEmbodiment 35 / / 13.8517.15 / / / / 0.2 / Zr0.3 / / 0.985balanceEmbodiment 36 / / 13.6517.15 / / / / 0.25 / Ti0.3 / / 0.985balanceEmbodiment 37 / / 12.6518.15 / / / / 0.4 / Ti0.3 / / 0.985balanceEmbodiment 38 / / 11.6519.15 / / / / 0.6 / Ti0.35 / / 0.985balanceEmbodiment 39 / / 11.6519.15 / / / / 0.8 / Ti0.40 / / 0.985balanceEmbodiment 40 / / 12.3519.15 / / / / 0.6 / Nb0.3 / / 0.985balanceEmbodiment 41 / / 13.8517.15 / / / / / 0.5Zr0.3 / / 0.985balanceEmbodiment 42 / / 12.6518.15 / / / / / 1Ti0.3 / / 0.985balanceEmbodiment 43 / / 12.3519.15 / / / / / 2.5Nb0.3 / / 0.985balanceEmbodiment 44 / / 13.6517.15 / / 0.340.042 / / Ti0.3 / / 0.985balanceEmbodiment 45 / / 13.6517.15 / / 0.380.1 / / Ti0.5 / / 0.985balanceEmbodiment 46 / / 13.6517.15 / / 0.400.2 / / Ti0.6 / / 0.985balanceEmbodiment 47 / / 12.6518.15 / / 0.40.3 / / Ti0.35 / / 0.985balanceEmbodiment 48 / / 13.6517.15 / / 0.450.4 / / Ti0.4 / / 0.985balanceEmbodiment 49 / / 11.6519.15 / / 0.50.5 / / Ti0.45 / / 0.985balanceEmbodiment 50 / / 13.8517.15 / / 0.340.50.20.5Zr0.3 / / 0.985balanceEmbodiment 51 / / 12.6518.15 / / 0.40.60.41Ti0.3 / / 0.985balanceEmbodiment 52 / / 12.3519.15 / / 0.50.70.62.5Nb0.3 / / 0.985balanceEmbodiment 53 / / 12.8518.15 / / 0.40.60.42.5Zr0.3Cr0.050.985balanceEmbodiment 54 / / 12.8518.15 / / 0.40.60.42.5Zr0.3Cr0.120.985balanceEmbodiment 55 / / 12.3518.15Dy1.50.40.60.42.5Nb0.3 / / 0.99balanceEmbodiment 56 / / 11.3518.15Dy2.50.40.60.42.5Nb0.3 / / 0.99balanceEmbodiment 57 / / 11.3518.15Tb20.40.60.42.5Nb0.3 / / 0.99balanceEmbodiment 58 / / 11.3518.15Tb1.20.40.60.42.5Nb0.3 / / 0.99balanceEmbodiment 59Ce0.311.3518.15Tb1.20.40.60.42.5Nb0.3 / / 0.99balanceComparative Embodiment 1 / / 13.8517.15 / / / / / / Mo2.16 / / 0.985balanceComparative Embodiment 2 / / 13.8517.15 / / / / / / Zr0.02 / / 0.985balance Embodiment 1

[0150] The preparation method for the RTB-based permanent magnet material is as follows: (1) Melting process: according to the formula shown in Table 1, the pre-prepared raw materials were put into the crucible made of aluminum oxide, and was vacuum melted in the high frequency vacuum induction melting furnace and in a vacuum of 5×10 -2< Pa at a temperature of 1500°C or less. (2) Casting process: Ar gas was introduced into the melting furnace after vacuum melting to make the air pressure reach 55,000 Pa, and then casting was carried out, and quenching alloy was obtained at the cooling rate of 10 2< °C / s to 10 4< °C / s. (3) Hydrogen decrepitation process: the hydrogen decrepitation furnace with quench alloy placed therein was vacuumed at room temperature, and then hydrogen with a purity of 99.9% was introduced into the hydrogen decrepitation furnace to maintain the hydrogen pressure at 0.15MPa; after full hydrogen absorption, the temperature was raised while vacuuming for full dehydrogenation; then cooled, and took out the powder obtained from hydrogen decrepitation. (4) Micro-pulverization process: in nitrogen atmosphere with an oxidizing gas content of 150 ppm or less and under the condition of a pressure of 0.38MPa in the pulverization chamber, the powder obtained from hydrogen decrepitation was pulverized by jet mill pulverization for 3 hours to obtain fine powder. Oxidizing gas refers to oxygen or moisture. (5) Zinc stearate was added to the powder pulverized by jet mill, and the addition amount of zinc stearate was 0.12% by weight of the mixed powder, and then a V-type mixer was used to fully mix. (6) Magnetic field forming process: using a rectangular oriented magnetic field forming machine, in an orientation magnetic field of 1.6T, under a molding pressure of 0.35ton / cm 2< , the above-mentioned powder added with zinc stearate was formed into a cube with a side length of 25mm through primary forming, and it was demagnetized in a magnetic field of 0.2T after the primary forming. In order to keep the formed body obtained after primary forming from contacting the air, it was sealed, and then secondary forming was performed under a pressure of 1.3 ton / cm 2< using a secondary molding machine (isostatic pressing machine). (7) Sintering process: each formed body was moved to the sintering furnace for sintering, sintered in the vacuum of 5×10 -3< Pa and at 300 °C and 600 °C for 1 h respectively; then, it was sintered at the temperature of 1050°C for 2 hours; Ar was then introduced to make the air pressure reach 0.1MPa and then cooled to room temperature. (8) Aging treatment process: the sintered body was heated from 20°C to 630°C at a heating rate of 3-5 °C / min in the Ar of high purity; after 3 hours of heat treatment at 630°C, it was cooled to room temperature and taken out. Embodiment 2- Embodiment 59

[0151] The raw materials were prepared according to the formulas shown in Table 1, and other process conditions were the same as those in Embodiment 1, and R-T-B series sintered magnets were obtained.Embodiment 60

[0152] Based on the sintered body obtained in Embodiment 55, the grain boundary diffusion treatment was carried out first, and then the aging treatment was carried out. Wherein, the aging treatment process is the same as in Embodiment 1, and the grain boundary diffusion treatment process is as follows:

[0153] The sintered body was processed into the magnet with diameter of 20 mm, and the thickness of the sheet material was less than 3 mm, the direction of the thickness was the direction of magnetic field orientation, after the surface was cleaned, the raw material prepared with Dy fluoride was coated on the magnet through fully spraying respectively, after drying the coated magnet, the metal attached with Tb was sputtered on the surface of the magnet in the high purity Ar atmosphere, and diffusing heat treatment was carried out at 850°C for 24 hours. Cooled to room temperature.Embodiment 61

[0154] Based on the sintered body obtained in Embodiment 58, and the grain boundary diffusion treatment was carried out first, and then the aging treatment was carried out. Wherein, the aging treatment process is the same as in Embodiment 1, and the grain boundary diffusion treatment process is as follows:

[0155] The sintered body was processed into the magnet with diameter of 20 mm, and the thickness of the sheet material was less than 3 mm, the direction of the thickness was the direction of magnetic field orientation, after the surface was cleaned, the raw material prepared with Tb fluoride was coated on the magnet through fully spraying respectively, after drying the coated magnet, the metal attached with Tb was sputtered on the surface of the magnet in the high purity Ar atmosphere, and diffusing heat treatment was carried out at 850°C for 24 hours. Cooled to room temperature.Effect embodiment

[0156] The magnetic properties and compositions of R-T-B permanent magnet materials prepared in Embodiments 1-61 and Comparative embodiments 1-3 were determined, and the crystal phase structure of the magnets was observed by Fe-EPMA. (1) Evaluation of magnetic properties: The NIM-10000H BH bulk rare earth permanent magnetic nondestructive measurement system in National Institute of Metrology, China was used for magnetic properties detection of permanent magnetic materials. The test results of magnetic properties are shown in Table 2 below. Therein, 1kGs=0.1T and 1kOe =1000 / (4π)kA / m. Table 2No.Br (kGs)Hcj (kOe)Absolute value of Hcj temperature coefficient at 80 °CAbsolute value of Hcj temperature coefficient at 150 °CAbsolute value of Hcj temperature coefficient at 180 °CEmbodiment 114.0317.620.685 / / Embodiment 214.0517.650.678 / / Embodiment 314.0117.880.675 / / Embodiment 413.9618.130.669 / / Embodiment 513.8617.720.681 / / Embodiment 613.7818.650.663 / / Embodiment 713.6418.990.660 / / Embodiment 813.4919.330.655 / / Embodiment 913.2319.750.651 / / Embodiment 1012.9320.690.642 / / Embodiment 1114.0817.670.683 / / Embodiment 1214.0317.950.673 / / Embodiment 1313.9518.210.667 / / Embodiment 1413.8318.820.663Embodiment 1513.6519.20.653Embodiment 1613.5519.540.648Embodiment 1713.2620.220.645Embodiment 1812.9820.90.628Embodiment 1913.8917.880.672 / / Embodiment 2013.9118.030.671 / / Embodiment 2113.8918.350.658 / / Embodiment 2214.0318.470.656 / / Embodiment 2314.0118.780.653 / / Embodiment 2414.0318.560.654Embodiment 2513.9819.100.646Embodiment 2613.8419.580.640 / / Embodiment 2714.0518.20.667 / / Embodiment 2813.8819.010.649 / / Embodiment 2913.7519.570.640 / / Embodiment 3013.7519.230.635 / / Embodiment 3113.6519.460.632 / / Embodiment 3213.5120.130.619 / / Embodiment 3313.4420.790.614 / / Embodiment 3413.1521.850.608 / / Embodiment 3514.0119.010.649 / / Embodiment 3613.9919.410.632 / / Embodiment 3713.9820.530.618 / / Embodiment 3813.9822.290.583 / / Embodiment 3913.8523.580.568 / / Embodiment 4013.7422.450.581 / / Embodiment 4114.0017.650.674 / / Embodiment 4213.9817.820.673 / / Embodiment 4313.7818.890.651 / / Embodiment 4413.9219.20.638 / / Embodiment 4513.8919.810.648 / / Embodiment 4613.7520.420.621 / / Embodiment 4713.9820.010.623 / / Embodiment 4813.5921.120.595 / / Embodiment 4913.3122.20.582 / / Embodiment 5013.5122.290.583 / / Embodiment 5113.124.45 / 0.489 / Embodiment 5212.9527.09 / 0.461 / Embodiment 5313.2924.73 / 0.493 / Embodiment 5413.0527.93 / 0.456 / Embodiment 5512.5328.83 / 0.451 / Embodiment 5612.3330.5 / / 0.431Embodiment 5712.4531.8 / / 0.425Embodiment 5812.7229.2 / 0.442 / Embodiment 5912.3126.9 / 0.512Embodiment 6012..4034.85 / / 0.401Embodiment 6112.2140.52 / / 0.372Comparative Embodiment 113.6019.650.638 / / Comparative Embodiment 214.1116.460.701 / / Comparative Embodiment 314.214.80.771 / / (2) Composition determination: The components were determined by high frequency inductively coupled plasma emission spectrometer (ICP-OES). The composition test results are shown in Table 3 below. Table 3 No.Ce wt.%Nd wt.%Pr wt.%RH kindRH wt.%Cu wt.%Al wt.%Ga wt.%Co wt.%N kindN wt.%M kindM wt.%B wt.%Fe wt.%Embodiment 1 / 13.7817.12 / / / / / / Zr0.24 / / 0.913balanceEmbodiment 2 / 13.8317.11 / / / / / / Zr0.31 / / 0.912balanceEmbodiment 3 / 12.8418.14 / / / / / / Zr0.30 / / 0.9120balanceEmbodiment 4 / 11.8719.13 / / / / / / Zr0.32 / / 0.983balanceEmbodiment 5 / 13.8417.19 / / / / / / Zr0.42 / / 0.987balanceEmbodiment 6 / 11.8419.148 / / / / / / Zr0.99 / / 0.985balanceEmbodiment 7 / 11.85119.148 / / / / / / Zr1.49 / / 0.988balanceEmbodiment 8 / 11.85219.147 / / / / / / Zr1.99 / / 0.985balanceEmbodiment 9 / 12.85218.151 / / / / / / Zr2.99 / / 0.985balanceEmbodiment 10 / 11.85419.152 / / / / / / Zr4.01 / / 0.988balanceEmbodiment 11 / 13.5917.13 / / / / / / Ti0.31 / / 0.989balanceEmbodiment 12 / 12.6218.13 / / / / / / Ti0.42 / / 0.988balanceEmbodiment 13 / 11.6519.13 / / / / / / Ti0.48 / / 0.987balanceEmbodiment 14 / 11.6419.14 / / / / / / Ti1.01 / / 0.985balanceEmbodiment 15 / 11.6319.13 / / / / / / Ti1.51 / / 0.988balanceEmbodiment 16 / 11.65219.151 / / / / / / Ti2.01 / / 0.985balanceEmbodiment 17 / 11.65119.149 / / / / / / Ti2.98 / / 0.985balanceEmbodiment 18 / 11.64819.148 / / / / / / Ti4.01 / / 0.988balanceEmbodiment 19 / 14.3517.19 / / / / / / Nb0.29 / / 0.984balanceEmbodiment 20 / 13.3218.14 / / / / / / Nb0.13 / / 0.985balanceEmbodiment 21 / 12.3219.12 / / / / / / Nb0.26 / / 0.989balanceEmbodiment 22 / 13.8317.19 / / 0.33 / / / Zr0.32 / / 0.985balanceEmbodiment 23 / 12.6318.19 / / 0.41 / / / Ti0.31 / / 0.988balanceEmbodiment 24 / 13.6517.13 / / 0.44 / / / Ti0.4 / / 0.985balanceEmbodiment 25 / 11.6219.12 / / 0.51 / / / Ti0.5 / / 0.985balanceEmbodiment 26 / 12.3219.09 / / 0.49 / / / Nb0.29 / / 0.988balanceEmbodiment 27 / 11.6119.14 / / / 0.041 / / Ti0.28 / / 0.989balanceEmbodiment 28 / 11.64819.148 / / / 0.1 / / Ti0.5 / / 0.985balanceEmbodiment 29 / 11.64719.148 / / / 0.2 / / Ti0.6 / / 0.985balanceEmbodiment 30 / 12.6618.14 / / / 0.31 / / Ti0.35 / / 0.985balanceEmbodiment 31 / 13.6817.16 / / / 0.38 / / Ti0.39 / / 0.988balanceEmbodiment 32 / 13.8317.08 / / / 0.5 / / Zr0.31 / / 0.989balanceEmbodiment 33 / 12.5818.19 / / / 0.6 / / Ti0.28 / / 0.985balanceEmbodiment 34 / 12.2919.15 / / / 0.7 / / Nb0.32 / / 0.989balanceEmbodiment 35 / 13.7917.18 / / / / 0.21 / Zr0.31 / / 0.985balanceEmbodiment 36 / 13.6417.16 / / / / 0.23 / Ti0.28 / / 0.985balanceEmbodiment 37 / 12.6618.17 / / / / 0.41 / Ti0.29 / / 0.988balanceEmbodiment 38 / 11.6419.14 / / / / 0.58 / Ti0.34 / / 0.985balanceEmbodiment 39 / 11.6419.14 / / / / 0.81 / Ti0.42 / / 0.985balanceEmbodiment 40 / 12.3919.17 / / / / 0.58 / Nb0.31 / / 0.985balanceEmbodiment 41 / 13.8917.16 / / / / / 0.49Zr0.28 / / 0.989balanceEmbodiment 42 / 12.6618.16 / / / / / 0.95Ti0.31 / / 0.989balanceEmbodiment 43 / 12.3919.16 / / / / / 2.4Nb0.28 / / 0.988balanceEmbodiment 44 / 13.6417.13 / / 0.340.043 / 0Ti0.32 / / 0.985balanceEmbodiment 45 / 13.64817.147 / / 0.380.1 / 0Ti0.50.988balanceEmbodiment 46 / 13.65117.148 / / 0.400.2 / 0Ti0.60.985balanceEmbodiment 47 / 12.6518.15 / / 0.40.32 / 0Ti0.34 / / 0.988balanceEmbodiment 48 / 13.6717.14 / / 0.450.41 / 0Ti0.42 / / 0.989balanceEmbodiment 49 / 11.6319.14 / / 0.510.48 / 0Ti0.44 / / 0.984balanceEmbodiment 50 / 13.8417.14 / / 0.330.490.210.51Zr0.32 / / 0.985balanceEmbodiment 51 / 12.7218.19 / / 0.410.620.391.1Ti0.31 / / 0.989balanceEmbodiment 52 / 12.3919.16 / / 0.520.690.592.4Nb0.29 / / 0.985balanceEmbodiment 53 / 12.8218.15 / / 0.410.620.412.53Zr0.31Cr0.050.988balanceEmbodiment 54 / 12.8318.16 / / 0.390.590.422.45Zr0.28Cr0.120.985balanceEmbodiment 55 / 12.3618.14Dy1.530.370.610.412.4Nb0.32 / / 0.989balanceEmbodiment 56 / 11.3618.15Dy2.430.420.590.402.35Nb0.31 / / 0.985balanceEmbodiment 57 / 11.3718.13Tb1.90.410.590.432.4Nb0.29 / / 0.988balanceEmbodiment 58 / 11.3218.19Tb1.120.410.590.412.53Nb0.29 / / 0.987balanceEmbodiment 590.2511.3518.15Tb1.180.420.620.382.4Nb0.28 / / 0.99balanceEmbodiment 60 / 12.3718.13Dy2.020.380.620.422.42Nb0.31 / / 0.988balanceEmbodiment 61 / 11.3918.17Tb1.580.410.580.422.51Nb0.28 / / 0.988balanceComparative Embodiment 1 / 13.7917.13 / / / / / / Mo2.13 / / 0.989balanceComparative Embodiment 2 / 13.8317.11 / / / / / / Zr0.01 / / 0.989balanceComparative Embodiment 3 / 25.36.1 / / / / / / Zr0.29 / / 0.987balance (3) FE-EPMA inspection: the perpendicularly oriented surface of the permanent magnet material in Embodiment 50 was polished and inspected using a field emission electron probe micro-analyzer (FE-EPMA) (Japan Electronics Corporation (JEOL), 8530F). The distribution of Pr, Cu, Al, B, Fe, Co and other elements in the permanent magnet material was first determined by FE-EPMA surface scanning, and then the content of Pr, Cu,Al and other elements in the key phase was determined by FE-EPMA single-point quantitative analysis with the test conditions of acceleration voltage 15 kv and probe beam current 50 nA.

[0157] The magnetic steel prepared by the formula of Embodiment 50 was mainly analyzed for Fe, Ga, Pr, Nd, Co, Al, Cu, Zr and B elements by using a field emission electron probe microanalyzer (FE-EPMA). 1) It can be seen from Fig. 1 that Pr is mainly distributed in the main phase, and the Pr content in the main phase of R 2 Fe 14 B is more than 60% of the total rare earth content, the grain boundary phase contains some Pr which exists in the form of α-Pr and / or Pr 2 O 3 , and the grain boundary phase also contains α-Nd and / or Nd 2 O 3 . It can be seen that the (PrNd) 2 Fe 14 B formed by the addition of Pr in the main phase will slightly decrease the remanence of the magnet, which is due to the slightly lower saturation magnetization intensity of Pr 2 Fe 14 B; the Hcj of the magnet is improved, which is due to the higher anisotropy field of Pr 2 Fe 14 B than that of Nd 2 Fe 14 B. In addition, due to the characteristics of easy oxidation of rare earth, some Pr 2 O 3 and Nd 2 O 3 will appear at the grain boundary, and the rest are α series of rare earths, all the phases at the grain boundary are nonmagnetic, so the demagnetization coupling between the main phase and the main phase is effectively isolated, which helps to improve the Hcj of the magnet. 2) As can be seen from Figure 1 and Figure 2, Al (80%-95%) is distributed in the main phase, which tends to decrease the remanence while increasing the coercivity, in addition, Al is distributed at the grain boundary. Cu ( 55 %-68 % ) is distributed in the main phase, according to the analysis of EPMA results, there is obvious Cu element in the grain boundary and in the intergranular triangle. The interaction of Cu element and Al element at grain boundary increases the wettability of grain boundary and main phase, makes grain boundary smoother, repairs grain boundary defects and effectively improves coercivity. Wherein, the grain boundary refers to the boundary between two grains, and the intergranular triangle refers to the void formed by three or more grains. 3) As can be seen from Figure 1 and Figure 2, Zr is dispersed in the main phase and grain boundary phase. The melting point of Pr 2 Fe 14 B is slightly lower than that of normal Nd 2 Fe 14 B, meanwhile, the temperature of the ternary eutectic point also changes and its temperature coefficient deteriorates. However, when high Pr is combined with Zr element, Zr element is dispersed everywhere, which improves the temperature resistance of magnetic steel, facilitates the densification of sintering process, and makes up for the defect of deterioration of temperature coefficient caused by Pr, it can be seen that Zr element and high Pr have synergistic effect. At the same time, the high melting point metal Zr is distributed at the grain boundary, which is beneficial to the pinning of magnetic domains in magnet steel, it is not easy to demagnetize at high temperature, which effectively improves the high temperature performance of magnet.

[0158] According to the properties of magnets with Ti and Nb in the high Pr system, the distribution of Ti and Nb in the high Pr magnets is the same / similar to that of Zr elements, which provides sintered permanent magnets with high coercivity and stable temperature coefficient by synergism with high Pr.

Claims

1. An R-T-B permanent magnet material, which comprises the following components by mass percentage: R': 29.5-33.0 wt.%, Pr 17.00-20.00 wt.%, N: 0.24-0.6 wt.%, Cu: 0.30-0.55 wt.%, Al: 0-0.8 wt.%, but not 0, B: 0.9-1.0 wt.%, Fe: 62.0-68.0 wt.%; wherein R' comprises R and Pr, Nd; wherein the mass ratio of Nd to R' is < 0.5 wherein R is a rare earth element other than Pr and Nd; and wherein N is Ti, Zr, or Nb.

2. The R-T-B permanent magnet material according to claim 1, wherein the content of N is preferably 0.28-0.6 wt.%, the content of Cu is preferably 0.33-0.52 wt.%, and the content of Al is preferably 0.043-0.69 wt.%.

3. A use of the R-T-B permanent magnet material according to claim 1 or claim 2 as electronic components.