Abstract

Material usable as dental resin, characterized in that the material comprises:- 30% to 50% polyamide,- 40% to 60% reinforcing fibers,- 10% to 30% radiopaque agent, by weight, relative to the total weight of the material.

Description

Title of the invention: Material usable as dental resin Technical field of the invention

[0001] The present invention relates to the dental field and more particularly to a material usable as dental resin. It also relates to a block or disc for CAD / CAM machining comprising the material. The invention also relates to a dental prosthetic element obtained from the block or disc, in particular an inlay-core, tenon, bridge and framework. Finally, it relates to a scan body, an abutment or a pivot comprising the dental material. Prior art

[0002] Computer-aided design and manufacturing (CAD / CAM) is a technology that is now widespread in the field of dentistry. This technique, also called CAD / CAM, allows dentists to design dental prostheses adapted to each patient, directly in their office.

[0003] Such practice improves the design of dental prostheses and generally increases the speed of treatment of patients.

[0004] Dentures are machined from a block or a disc, which are the two most common types of preforms.

[0005] The blocks generally have a substantially parallelepiped shape. They are intended to be fixed to the machining machine by means of a holding rod which may or may not be integral with the block. Documents EP3395289 and FR3058630 describe in particular blocks for CAD / CAM machining of dental prosthetic elements, such as inlay-core in particular.

[0006] The discs have a circular or oval shape.

[0007] The materials used for the design of the blocks or discs must be biocompatible, to avoid any rejection, and have sufficient mechanical resistance to withstand the stresses exerted by / on the teeth.

[0008] Ceramic materials have often been chosen for their tooth-like appearance as well as their mechanical properties.

[0009] Metals can also be used.

[0010] Composite materials comprising polymers represent a good compromise between rigidity and biocompatibility: (meth)acrylic resins, polyesters, vinylesters or epoxies are frequently used in the manufacture of such materials.

[0011] In particular, polyetheretherketone (PEEK) is a material widely used for the manufacture of prosthetics. This semi-crystalline thermoplastic is rigid and resistant effectively resists wear and abrasion. However, its price is generally high, so alternatives to PEEK are sought.

[0012] Since dental prostheses are subject to regular checks by the practitioner, in particular by means of X-rays, the materials selected must be radiopaque, in other words they must prevent the passage of X-rays.

[0013] Such materials are more easily visible on an X-ray. They appear white or light gray.

[0014] It is therefore essential to implement materials that can be used as dental resin and that present a good compromise between mechanical resistance and radiopacity.

[0015] Furthermore, it is known to use glass fiber sheets to reinforce the strength of CAD / CAM discs. These sheets comprise networks of horizontal glass fibers, parallel to each other, as described in documents EP2692312 and WO2012095878. However, such a structure of long fiber sheets is not suitable for machining in the mouth.

[0016] The problem that the invention sets out to solve is that of overcoming the constraints of the state of the art by proposing a mechanically resistant and radio-opaque material that can be used as a dental resin, which can be used for the manufacture of both discs and blocks.

[0017] The objective of the invention is also to develop a resin which can be injected to form discs of a thickness compatible with the machining of reinforcement in particular. Statement of the invention

[0018] The invention relates firstly to a material which can be used as a dental resin. This material is characterised in that it comprises: - 30% to 50% of polyamide, - 40% to 60% of reinforcing fibres, - 10% to 30% of radiopaque agent, by weight, relative to the total weight of the material.

[0019] In other words, the Applicant has developed a material which meets all of the criteria mentioned above, namely the possibility of injecting the material, mechanical resistance and radiopacity.

[0020] The Applicant has found that outside the ranges mentioned, the combination of polyamide, reinforcing fibers and radiopaque agent does not guarantee the mechanical strength, radiopacity and injectability of the material.

[0021] The material also has the advantage of being machinable in the mouth. Indeed, unlike the materials of the prior art, the material according to the invention does not have fibers at its periphery once pre-machined.

[0022] Polyamides are polymers that can be obtained by polycondensation between a carboxylic acid and an amine. They generally have a semi-crystalline structure and are particularly suitable for injection processes for their shaping.

[0023] The polyamide is, preferably, polyamide 6 and / or polyamide 6-6. Advantageously, the polyamide is polyamide 6-6. The polyamide may be polyamide 10, polyamide 11 or polyamide 12.

[0024] [Chem.l] Enh - - 13 Nylon 6: -J \Z\z “'n Em JL .1' Nylon 6,6: ' '[f

[0025] The reinforcing fibers preferably have a length of less than 5 mm, preferably between 4 and 5 mm. Fibers of this length are particularly resistant to mechanical stresses such as compression. Due to their size, these fibers are dispersed in the material and thus reinforce its mechanical resistance, making the presence of superimposed horizontal layers, the disadvantages of which have been explained previously, unnecessary.

[0026] The reinforcing fibers are advantageously chosen from the group comprising glass, Kevlar, aramid, carbon fibers, advantageously glass fibers.

[0027] Glass fibers are particularly impact resistant and are chemically inert. They may comprise SiO2, Al2O3, and / or CaO.

[0028] Kevlar fibers have a crystalline structure and have good tensile mechanical properties but are less resistant to compression than glass fibers.

[0029] Aramid fibers are strong but can be difficult to machine.

[0030] Carbon fibers have the best compressive strength but are more expensive and have a black color that is not compatible with dental applications.

[0031] Advantageously, the radiopaque agent comprises barium and / or iodine, preferably barium.

[0032] The radiopaque agent is preferably barium sulfate.

[0033] In practice, the material comprises at least 20%, 25%, 30%, 35%, 40% or even 45% of polyamide by weight, relative to the total weight of the material.

[0034] The material may comprise less than 65%, 60%, 55%, 50% or even 49% of polyamide by weight, relative to the total weight of the material.

[0035] In practice, the material comprises at least 30%, 35%, 40%, 45%, or even 50% of reinforcing fibers by weight, relative to the total weight of the material.

[0036] The material may comprise less than 70%, 65%, 60%, or even 55%, of reinforcing fibers by weight, relative to the total weight of the material.

[0037] In practice, the material comprises at least 5%, 7%, 10%, 15%, or even 20% of radiopaque agent by weight, relative to the total weight of the material.

[0038] The material may comprise less than 40%, 35%, 30%, or even 25% of radiopaque agent by weight, relative to the total weight of the material.

[0039] In a preferred embodiment, the material comprises: - 38% to 42% polyamide 6-6, - 48% to 52% of glass fibers less than 5 mm long, -10% to 14% of barium sulfate, by weight, relative to the total weight of the material.

[0040] The material may have a translucent appearance or be tinted by the dental practitioner to match the coloration of the patient's teeth.

[0041] The present invention also relates to a block or disc for CAD / CAM machining of a dental prosthetic element comprising the material according to the invention.

[0042] In particular, the block or disc for CAD / CAM machining of a dental prosthetic element is made of the sole material according to the invention. The material comprises polyamide, reinforcing fibers, and a radiopaque agent.

[0043] The block comprises a machinable part, of substantially parallelepiped shape, as well as a holding rod intended to fix the block on a CAD / CAM machining machine.

[0044] Advantageously, the machinable part and the holding rod are made in a single piece or in two separate pieces which can be fixed to each other.

[0045] According to the invention, at least the machinable part comprises the material according to the invention.

[0046] The material according to the invention can be injected under temperature and cooling conditions which make it possible to obtain a block or disc of dimensions compatible with CAD / CAM machining.

[0047] In particular, the material must be injectable at a thickness of 14 to 18 mm to obtain a disc.

[0048] The block or disc is manufactured by injection molding, according to a particular embodiment.

[0049] The invention also relates to a dental prosthetic element obtained by CAD / CAM machining from a block or a disc comprising the material according to the invention.

[0050] Advantageously, this block or this disc is made of the material according to the invention.

[0051] The dental prosthetic element can be an inlay-core, a post, a framework, a bridge or a crown.

[0052] An inlay-core is generally made up of a rod, also called a tenon, topped with a stump of a reconstituted tooth. The role of the inlay-core is to serve as an anchor point for a dental prosthesis. Dental prosthetic elements such as crowns or bridges can be inserted into the stump of the inlay-core.

[0053] A crown is an artificial tooth that covers a damaged tooth.

[0054] The bridge allows one or more missing teeth to be replaced, by relying on the adjacent teeth. It can be made up of several crowns joined together.

[0055] The framework is a structure allowing the fixing of crowns or bridges.

[0056] The tenon corresponds to the rod holding the inlay-core.

[0057] According to one embodiment, etching may be performed on the stump before the post is placed. Etching is a technique that improves the adhesion of dental prostheses to the tooth structure. It consists of applying an acid, generally phosphoric acid or hydrofluoric acid, to the stump. The attack of the acid on the enamel and dentin helps to penetrate the resin into the collagen matrix of the tooth. The acid is rinsed off and an adhesive compound may be applied to the stump. The adhesive compound may be photopolymerized by exposure to ultraviolet radiation. The post is then placed in the stump.

[0058] The invention also relates to a scanning body, a pillar or a pivot comprising the material according to the invention.

[0059] An abutment is an implant device that is generally screwed onto an implant replacing the root of an extracted tooth, for the attachment of a crown.

[0060] A scanning body is used to indicate the position and orientation of a dental implant using a digital camera. It can be attached to the implant or to the abutment.

[0061] A pivot includes an inlay-core and a dental crown. It is a restoration technique allowing the root of a devitalized tooth to be kept and thus avoiding the installation of a dental implant. Brief description of the drawings

[0062] The manner in which the invention can be implemented and the advantages which result therefrom will emerge more clearly from the following example of implementation, given for informational and non-limiting purposes, with the support of the appended figures.

[0063] [Fig-1] is an X-ray of an inlay-core obtained from a block 1 whose manufacture is detailed below.

[0064] [Fig.2] is an X-ray of an inlay-core obtained from a block 2 whose manufacture is detailed below.

[0065] [Fig.3] is an X-ray of an inlay-core obtained from a block 3 whose manufacture is detailed below. Examples of embodiments of the invention

[0066] Example 1: Manufacture of blocks for CAD / CAM machining

[0067] Three blocks for CAD / CAM machining are manufactured comprising the material according to the invention, according to the following protocol.

[0068] A material consisting of 39% polyamide 6-6, 48% glass fibers less than 5 mm long and 13% barium sulfate by weight is injected. Block 1 is formed by injection and then molded under the following conditions.

[0069] Injection molding is carried out using a SELECT® 200T press. The mixture is heated and melted at 250°C, then injected at 90°C into a mold having a temperature of 70°C. The mold is cooled and the block is recovered.

[0070] This same process is implemented for the manufacture of blocks 2 and 3.

[0071] Block 2 is obtained by injection and molding of a material consisting of 40% of polyamide 6-6, 50% glass fibers less than 5 mm long and 10% barium sulfate, by weight.

[0072] Block 3 is obtained by injection and molding of a material consisting of 38% polyamide 6-6, 52% glass fibers less than 5 mm long and 10% barium sulfate.

[0073] The compositions of the blocks are detailed in Table 1, in mass percentage relative to the total weight of the material.

[0074] [Tab.l] Polyamide 6-6 (%) Block 1 39 Block 2 40 Block 3 38 | Glass fibers (%) 48 50 52 | Barium sulfate CO 13 10 10

[0075] Example 2: Manufacture of discs for CAD / CAM machining

[0076] Three discs for CAD / CAM machining are manufactured comprising the material according to the invention, according to the following protocol.

[0077] Thus, the disc 1 is shaped by injection molding a material consisting of 39% polyamide 6-6, 48% glass fibers less than 5 mm long and 13% barium sulfate by weight.

[0078] Injection molding is carried out using a SELECT 200T press. The mixture is heated and melted at 250°C, then injected at 90°C into a mold having a temperature of 70°C. The mold is cooled for a few minutes and the disc is recovered.

[0079] This same process is implemented for the manufacture of discs 2 and 3.

[0080] The disc 2 is obtained from a material consisting of 40% polyamide 6-6, 50 % of glass fibers less than 5 mm in length and 10% of barium sulfate, by weight.

[0081] The disc 3 is obtained from a material consisting of 38% polyamide 6-6, 52% glass fibers less than 5 mm long and 10% barium sulfate.

[0082] The three discs have a diameter of 98 mm and a thickness of 14 mm.

[0083] The compositions of the discs are detailed in Table 2, in percentage mass relative to the total weight of the material.

[0084] [Tab.2] Polyamide 6-6 (%) Disc 1 39 | Disc 2 40 Disc 3 38 Glass fibers (%) 48 50 52 Barium sulfate (%) 13 | 10 10

[0085] Example 3: Radio-opacity

[0086] [Fig.l], [Fig.2] and [Fig.3] show that for each of the materials used, the implanted dental prosthetic element has satisfactory radiopacity.

Claims

Claims

1. Material usable as dental resin, characterized in that the material comprises: - 30% to 50% polyamide, - 40% to 60% reinforcing fibers, - 10% to 30% radiopaque agent, by weight, relative to the total weight of the material.

2. Material according to claim 1, characterized in that the polyamide is polyamide 6 and / or polyamide 6-6, advantageously polyamide 6-6.

3. Material according to one of claims 1 or 2, characterized in that the reinforcing fibers have a length of less than 5 mm, preferably between 4 and 5 mm.

4. Material according to one of claims 1 to 3, characterized in that the reinforcing fibers are chosen from the group comprising glass, Kevlar, aramid, carbon fibers, advantageously glass fibers.

5. Material according to one of claims 1 to 4, characterized in that the radiopaque agent is barium sulfate.

6. Material according to one of claims 1 to 5, characterized in that it comprises: - 38% to 42% of polyamide 6-6, - 48% to 52% of glass fibers of length less than 5 mm, - 10% to 14% of barium sulfate, by weight, relative to the total weight of the material.

7. Block or disc for CAD / CAM machining of a dental prosthetic element, characterized in that it comprises the material according to one of claims 1 to 6.

8. Block or disc for CAD / CAM machining of a dental prosthetic element, characterized in that it is made of the material according to one of claims 1 to 6.

9. Dental prosthetic element obtained by CAD / CAM machining of a block or disc according to one of claims 7 or 8, characterized in that said dental prosthetic element is an inlay-core, a tenon, a framework, a bridge or a crown.

10. A scanning body, pillar or pivot comprising the material of one of claims 1 to 6.

Images