Gold nano-particle contained composition, gold nano-particle contained composition dispersion liquid, ink and toner

Abstract

To provide a gold nano-particle contained composition excellent in storage stability.SOLUTION: A gold nano-particle contained composition 100 comprises a gold nano-particle 10, and an amphoteric ion compound 20 having an HLB value equal to or smaller than 12 and a structure represented by any of the following general formulas (1) to (3) (in the formula, R1, R5, and R8 represent an organic group independently, R2 to R4, R6, R7, and R9 to R11 represent a hydrogen atom or an alkyl group independently, A1 to A5 represent a linking group independently, and Y- represents COO- or SO3-).SELECTED DRAWING: Figure 1

Description

[Technical field]

[0001] The present invention relates to a gold nanoparticle-containing composition, a gold nanoparticle-containing composition dispersion, an ink, and a toner. [Background technology]

[0002] Gold nanoparticles have unique structures, electrical properties, and optical properties, and are expected to be used in a variety of applications, including invisible printing, advanced electronics, and medicine. However, gold nanoparticles, especially those with anisotropic shapes such as nanorods, nanocubes, and nanoplates, are known to have low dispersion stability in media and easily aggregate. Gold nanoparticles lose their inherent properties when they aggregate, so it is necessary to improve their dispersion stability in various media.

[0003] For example, gold nanorods having a silica coating layer with improved dispersion stability in a medium have been proposed (Patent Document 1), and a toner containing gold nanorods has been proposed (Patent Document 2). [Prior art documents] [Patent documents]

[0004] [Patent Document 1] JP 2021-152223 A [Patent Document 2] JP 2022-117406 A Summary of the Invention [Problem to be solved by the invention]

[0005] The present inventors have investigated the storage stability of the dispersion of gold nanorods having a silica coating layer proposed in Patent Document 1. As a result, it was found that when this dispersion is stored at a temperature condition of 60°C, the intensity of the absorption peak decreases within 24 hours, and it was found that there is room for improvement in the storage stability. Furthermore, as in the toner described in Patent Document 2, there are cases in which gold nanorods aggregate in highly hydrophobic particles, weakening the infrared absorption properties.

[0006] Therefore, an object of the present invention is to provide a gold nanoparticle-containing composition having excellent storage stability. Another object of the present invention is to provide a gold nanoparticle-containing composition dispersion having excellent storage stability. Another object of the present invention is to provide an ink having excellent storage stability. Still another object of the present invention is to provide a toner having excellent dispersibility of gold nanoparticles. [Means for solving the problem]

[0007] That is, according to the present invention, there is provided a gold nanoparticle-containing composition, characterized in that it contains gold nanoparticles and a compound having a structure represented by any one of the following general formulas (1) to (3), whose HLB value is 12 or less.

[0008] TIFF2024108095000002.tif86170 (In the general formulas (1) to (3), R1, R5, and R8 each independently represent an organic group, and R2 to R4, R6, R7, and R9 to R 11 each independently represents a hydrogen atom or an alkyl group; A1 to A5 each independently represent a linking group; Y - is COO - or SO3 - (represents Effect of the Invention

[0009] According to the present invention, a gold nanoparticle-containing composition having excellent storage stability can be provided. According to the present invention, a gold nanoparticle-containing composition dispersion having excellent storage stability can be provided. According to the present invention, an ink having excellent storage stability can be provided. Furthermore, according to the present invention, a toner having excellent dispersibility of gold nanoparticles can be provided. [Brief description of the drawings]

[0010] [Figure 1] FIG. 1 is a schematic diagram showing one embodiment of the first gold nanoparticle-containing composition of the present invention. [Diagram 2] FIG. 2 is a schematic diagram showing another embodiment of the first gold nanoparticle-containing composition of the present invention. [Diagram 3] FIG. 2 is a schematic diagram showing one embodiment of the second gold nanoparticle-containing composition of the present invention. [Figure 4] FIG. 2 is a schematic diagram showing another embodiment of the second gold nanoparticle-containing composition of the present invention. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0011] The present invention will be described in more detail below with reference to preferred embodiments. Physical property values ​​are values ​​at room temperature (25° C.) unless otherwise specified.

[0012] <First gold nanoparticle-containing composition> The gold nanoparticle-containing composition of the present invention (first gold nanoparticle-containing composition) contains gold nanoparticles and a compound having a structure represented by any one of the following general formulas (1) to (3) and having an HLB value of 12 or less.

[0013] TIFF2024108095000003.tif86170 (In the general formulas (1) to (3), R1, R5, and R8 each independently represent an organic group, and R2 to R4, R6, R7, and R9 to R 11 each independently represents a hydrogen atom or an alkyl group; A1 to A5 each independently represent a linking group; Y - is COO - or SO3- (represents

[0014] (Gold Nanoparticles) Gold nanoparticles are nanoparticles whose main component is gold, and preferably are substantially made of gold. The shapes of gold nanoparticles include spheres (nanospheres), polyhedrons, cubes (nanocubes), bipyramids, rods (nanorods), and plates (nanoplates). Among them, gold nanoparticles are preferably gold nanorods or gold nanospheres, and may be a mixture of nanoparticles of different shapes.

[0015] The content of gold (gold element) in the metal constituting the gold nanoparticles is preferably 50% by mass or more. The arrangement of the gold element and a metal element other than the gold element may be in the form of an alloy composited at the atomic level, or in the form of a core-shell in which nanoparticles essentially made of gold are coated with a metal element other than gold. When a substance such as a dispersant is coordinated to the surface of the gold nanoparticles for dispersion stabilization, the mixture of the gold nanoparticles and the substance such as the dispersant is expressed as a gold nanoparticle-containing composition.

[0016] Gold nanoparticles are particles with a size on the order of nanometers (nm). The size of gold nanoparticles is preferably 1 nm or more and 500 nm or less, more preferably 5 nm or more and 200 nm or less, and particularly preferably 10 nm or more and 100 nm or less. The size of a particle means the maximum length of the particle. The size of gold nanoparticles can be measured, for example, by observation with a scanning electron microscope (SEM), a scanning transmission electron microscope (STEM), or a transmission electron microscope (TEM). The maximum length of gold nanoparticles may be measured using a dynamic light scattering particle size distribution analyzer (DLS). When measuring the maximum length of gold nanoparticles from SEM observation photographs, STEM observation photographs, and TEM observation photographs, the average value of 80 gold nanoparticles, excluding the top and bottom 10% of the data obtained by measuring the maximum length of any 100 gold nanoparticles, can be used.

[0017] Gold nanoparticles usually have light absorption properties derived from Localized Surface Plasmon Resonance (LSPR). The light absorption wavelength of gold nanoparticles varies depending on the size, shape, aspect ratio (the ratio of the long axis to the short axis in the case of rod-shaped particles, and the ratio of the maximum planar length to the thickness in the case of plate-shaped particles), the dielectric constant of the surroundings, etc. For example, gold nanorods exhibit two characteristic plasmon absorption bands (bands corresponding to the excitation of the surface plasmon band), one due to the long axis of the rod and the other due to the short axis of the rod. The absorption band due to the short axis is located near 530 nm, and the absorption band due to the long axis is located at 650 to 2,000 nm. The maximum absorption wavelength can be adjusted by controlling the aspect ratio (long axis / short axis). The aspect ratio of gold nanorods is usually 1.5 or more.

[0018] Gold nanospheres can be prepared according to a conventional method. For example, gold nanospheres can be obtained by adding sodium borohydride (NaBH4) to chloroauric acid (HAuCl4) in an aqueous solution and reacting for 24 hours. If necessary, a surfactant such as cetyltrimethylammonium bromide (CTAB) may be used.

[0019] Gold nanorods can be prepared, for example, according to the method proposed by B. Nikoobakft and MA El-Sayed (Chemistry of Materials, 2003, No. 15, pp. 1957-1962). For example, gold nanorods can be obtained by reducing chloroauric acid (HAuCl4) with ascorbic acid in an aqueous solution containing two types of surfactants (hexadecyltrimethylammonium bromide and benzyldimethylhexadecylammonium chloride).

[0020] There is also a method for synthesizing gold nanorod particles by reducing gold ions in an aqueous solution containing an excess of cetyltrimethylammonium bromide (CTAB), a quaternary ammonium salt. In this method, first, an aqueous solution of CTAB is added to an aqueous solution of chloroauric acid tetrahydrate, and sodium borohydride is further added to prepare a solution having seed particles. Next, a mixed solution of silver nitrate, chloroauric acid tetrahydrate, L-ascorbic acid, and CTAB is added to the prepared solution and held for a certain period of time, or this mixed solution is added little by little. This makes it easier to anisotropically grow seed particles as nuclei, and gold nanorods can be obtained.

[0021] Gold nanorods with a large aspect ratio can be obtained by adding benzyldimethylhexadecylammonium chloride when growing seed particles. Gold nanorods with a large aspect ratio can also be obtained by reducing the seed particles with sodium borohydride, a strong reducing agent, and then reducing them with triethylamine, a weak reducing agent.

[0022] If necessary, the aspect ratio distribution may be adjusted by purifying the gold nanorods. Any of the commonly known methods can be used to purify the gold nanorods. For example, the gold nanorods can be purified by density gradient ultracentrifugation. Specifically, first, mixed solutions of sucrose and CTAB with different concentrations are prepared and layered in a centrifuge tube in the order of concentration gradient. A sample of gold nanorods is layered on top of the mixed solutions, and then ultracentrifugation is performed. This makes it possible to obtain gold nanorods with a small standard deviation σ and a narrower aspect ratio distribution.

[0023] When preparing gold nanoparticles, surfactants can be used as dispersants, such as cetyltrimethylammonium bromide (CTAB), benzyldimethylhexadecylammonium chloride (BDAC), dodecyltrimethylammonium chloride (DTAB), and tetradecyltrimethylammonium bromide (TTAB).

[0024] (Zwitterionic compounds) FIG. 1 is a schematic diagram showing one embodiment of the first gold nanoparticle-containing composition of the present invention. As shown in FIG. 1, a compound (zwitterionic compound 20) having a structure represented by any one of the following general formulas (1) to (3) and having an HLB value of 12 or less is strongly coordinated to the surface of a gold nanoparticle 10 via a binding portion 30 (hydrophilic portion 35). This constitutes a gold nanoparticle-containing composition 100 of this embodiment. The binding portion 30 has a positive charge (+) and a negative charge (-) that are not adjacent to each other. In addition, the zwitterionic compound 20 does not have a charge as a whole molecule. Since gold nanoparticles are usually synthesized in a solution containing a surfactant such as cetyltrimethylammonium bromide (CTAB), CTAB and the like are coordinated to the surface of the gold nanoparticles after synthesis. Recent research has revealed that a potential gradient is generated on the gold nanoparticles due to the density difference of CTAB on the gold nanoparticle surface (Kim et al., SCIENCE ADVANCES 2018, 4(2), e1700682). Since the zwitterionic compound 20 has both positive and negative charges, it is believed to strongly coordinate with the potential gradient on the surface of the gold nanoparticles 10. This is presumably why high dispersion stability is exhibited.

[0025] TIFF2024108095000004.tif86170 (In the general formulas (1) to (3), R1, R5, and R8 each independently represent an organic group, and R2 to R4, R6, R7, and R9 to R 11 each independently represents a hydrogen atom or an alkyl group; A1 to A5 each independently represent a linking group; Y - is COO - or SO3 - (represents

[0026] At least a part of the zwitterionic compound is preferably coordinated to the surface of the gold nanoparticle. As shown in FIG. 1, the zwitterionic compound 20 has a hydrophobic portion 40 and a binding portion 30 (hydrophilic portion 35). When the dispersion medium is hydrophobic, the binding portion 30 is strongly coordinated toward the surface side of the gold nanoparticle 10, and the hydrophobic portion 40 is directed toward the dispersion medium side, so that the gold nanoparticle 10 can be effectively stabilized in dispersion. On the other hand, when the dispersion medium is hydrophilic, it is presumed that the zwitterionic compound 20 forms a double layer as shown in FIG. 2, and the hydrophilic portion 35 is disposed on the outermost surface. It is considered that this constitutes a gold nanoparticle-containing composition 200 in which the gold nanoparticles 10 are stabilized in dispersion.

[0027] The first gold nanoparticle-containing composition can be prepared, for example, according to the following procedure. First, a poor solvent is added to a dispersion containing gold nanoparticles and a zwitterionic compound, if necessary, and then the mixture is centrifuged. The resulting precipitate is then dried to obtain the desired first gold nanoparticle-containing composition.

[0028] Examples of methods for coordinating at least a portion of a zwitterionic compound to the surface of gold nanoparticles include a method in which a zwitterionic compound is reacted with gold nanoparticles and exchanged with a surfactant described below, a method in which gold nanoparticles and a zwitterionic compound are allowed to coexist, etc. In the method of exchanging with a surfactant, the free and excessive surfactant can be removed by centrifugation.

[0029] In the general formulas (1) to (3), examples of the organic groups represented by R1, R5, and R8 include linear, branched, or cyclic alkyl groups which may have a substituent; linear, branched, or cyclic heteroalkyl groups which may have a substituent; aryl groups which may have a substituent; heteroaryl groups which may have a substituent; aralkyl groups which may have a substituent; and heteroaralkyl groups which may have a substituent.

[0030] In general formulas (1) to (3), R2 to R4, R6, R7, and R9 to R 11The alkyl group represented by the formula (I) is preferably an alkyl group having 1 to 18 carbon atoms. Examples of the alkyl group having 1 to 18 carbon atoms include a methyl group, an ethyl group, an n-propyl group, an isopropyl group, an n-butyl group, an n-octyl group, a 2-ethylhexyl group, a dodecyl group, and an octadecyl group. These alkyl groups may be further substituted, and may be bonded to each other to form a ring.

[0031] In the general formula (1), A1 is a linking group that connects R1 to the phosphate moiety. Examples of the linking group A1 include a carbonyl group, an alkylene group, an arylene group, and -COOR 20 -(R 20 represents an alkylene having 1 to 4 carbon atoms). A1 may be a single bond. In other words, R1 may be directly bonded to the phosphate moiety.

[0032] The alkylene group which is the linking group A1 may be either linear or branched, and is preferably an alkylene group having 1 to 4 carbon atoms. Examples of the alkylene group having 1 to 4 carbon atoms include a methylene group, an ethylene group, a propylene group, and various butylene groups.

[0033] Examples of the arylene group which is the linking group A1 include a 1,2-phenylene group, a 1,3-phenylene group, a 1,4-phenylene group, a naphthalene-1,4-diyl group, a naphthalene-1,5-diyl group, and a naphthalene-2,6-diyl group.

[0034] The linking group A1 is "-COOR 20 The carbonyl group in "-" is bonded to a site other than the phosphate ester site. 20 The alkylene having 1 to 4 carbon atoms represented by the following formula may be either linear or branched.

[0035] The linking group A1 may be further substituted with another functional group. From the viewpoint of availability of raw materials and ease of production, the linking group A1 is preferably a carbonyl group or a "-COOR" group. 20 -" is preferred.

[0036] In the general formula (1), A2 is a linking group that bonds the phosphate moiety and the quaternary ammonium moiety. Examples of the linking group A2 include an alkylene group and an arylene group. The alkylene group of the linking group A2 may be either linear or branched, and is preferably an alkylene group having 1 to 4 carbon atoms. Examples of the alkylene group having 1 to 4 carbon atoms include a methylene group, an ethylene group, a propylene group, and various butylene groups.

[0037] Examples of the arylene group which is the linking group A2 include a 1,2-phenylene group, a 1,3-phenylene group, a 1,4-phenylene group, a naphthalene-1,4-diyl group, a naphthalene-1,5-diyl group, and a naphthalene-2,6-diyl group.

[0038] The linking group A2 may be further substituted with another functional group. From the viewpoints of availability of raw materials and ease of production, the linking group A2 is preferably an alkylene group such as a methylene group or an ethylene group.

[0039] In the general formula (2), A3 is a linking group that connects R5 to the quaternary ammonium moiety. Examples of the linking group A3 include an alkylene group, an arylene group, an aralkylene group, -COOR 21 -,-CONHR 21 - and -OR 21 -(R 21 represents an alkylene group or an arylene group). A3 may be a single bond. That is, R5 may be directly bonded to the quaternary ammonium moiety.

[0040] The alkylene group which is the linking group A3 may be either linear or branched, and is preferably an alkylene group having 1 to 4 carbon atoms. Examples of the alkylene group having 1 to 4 carbon atoms include a methylene group, an ethylene group, a propylene group, and various butylene groups.

[0041] Examples of the arylene group which is the linking group A3 include a 1,2-phenylene group, a 1,3-phenylene group, a 1,4-phenylene group, a naphthalene-1,4-diyl group, a naphthalene-1,5-diyl group, and a naphthalene-2,6-diyl group.

[0042] The aralkylene group which is the linking group A3 can be an aralkylene group having 7 to 15 carbon atoms. 21 -", "-CONHR 21 -" and "-OR 21 -” Medium, R 21 The alkylene group represented by the formula (I) may be either linear or branched, and is preferably an alkylene group having 1 to 4 carbon atoms. Examples of the alkylene group having 1 to 4 carbon atoms include a methylene group, an ethylene group, a propylene group, and various butylene groups. 21 -", "-CONHR 21 -" and "-OR 21 -” Medium, R 21 Examples of the arylene group represented by the formula (I) include a 1,2-phenylene group, a 1,3-phenylene group, a 1,4-phenylene group, a naphthalene-1,4-diyl group, a naphthalene-1,5-diyl group, and a naphthalene-2,6-diyl group.

[0043] The linking group A3 may be further substituted with another functional group. From the viewpoint of availability of raw materials and ease of production, the linking group A3 is preferably -COOR 21 -or- CONHR 21 - is preferred.

[0044] In the general formula (2), A4 is a linking group that connects the quaternary ammonium moiety and its counter anion moiety Y. Examples of the linking group A4 include an alkylene group and an arylene group.

[0045] In the general formula (3), A5 is a linking group that connects R8 to the zwitterion site. Examples of the linking group A5 include an alkylene group, an arylene group, an aralkylene group, -COOR 22-,-CONHR 22 - and -OR 22 -(R 22 represents an alkylene group or an arylene group). A5 may be a single bond. In other words, R8 may be directly bonded to the zwitterion site.

[0046] The alkylene group which is the linking group A5 may be either linear or branched, and is preferably an alkylene group having 1 to 4 carbon atoms. Examples of the alkylene group having 1 to 4 carbon atoms include a methylene group, an ethylene group, a propylene group, and various butylene groups. Examples of the arylene group that is the linking group A5 include a 1,2-phenylene group, a 1,3-phenylene group, a 1,4-phenylene group, a naphthalene-1,4-diyl group, a naphthalene-1,5-diyl group, and a naphthalene-2,6-diyl group, etc. From the viewpoints of availability of raw materials and ease of production, the linking group A5 is preferably an alkylene group such as a methylene group, an ethylene group, or a propylene group.

[0047] In the general formulas (2) and (3), Y - is the counter anion of the quaternary ammonium moiety, COO - or SO3 - The zwitterionic compound has a structure represented by formula (1), or is represented by formula (2) or formula (3) and Y - SO3 - It is preferred that the compound has a structure:

[0048] The HLB value is a physical property value that indicates the balance between the hydrophilic and hydrophobic parts of a molecule (hydrophil-lipophilic balance), and takes a value between 0 and 20. The smaller the HLB value, the higher the hydrophobicity, and the larger the HLB value, the higher the hydrophilicity. In this specification, the "HLB value" is a value calculated according to the "Griffin's formula" shown below. [Griffin's formula] HLB value = {(100 / 5) x hydrophilic part mass} / (hydrophilic part mass + hydrophobic part mass)

[0049] In general formula (1), A1 and R1 are hydrophobic moieties, and the moiety other than A1 and R1 is hydrophilic moiety. In general formula (2), A3 and R5 are hydrophobic moieties, and the moiety other than A3 and R5 is hydrophilic moiety. In general formula (3), N + R9R 10 R 11 and Y - is the hydrophilic part, and N + R9R 10 R 11 and Y - The remaining portion is the hydrophobic portion.

[0050] The HLB value is a physical property value that is usually used as an index of the balance between the hydrophilic and hydrophobic parts of a nonionic surfactant. The hydrophilicity of the hydrophilic group in an ionic surfactant is significantly higher than that of the hydrophilic group in a nonionic surfactant. For this reason, the degree of hydrophilicity per unit mass of ionic surfactants varies depending on the type of hydrophilic group. Therefore, it is generally believed that there is no method for calculating the HLB value of an ionic surfactant (for example, "New Surfactant Introduction" (by Takehiko Fujimoto, 4th edition, October 1996, published by Sanyo Chemical Industries Co., Ltd.)). However, it is presumed that the hydrophilic groups in the above-mentioned zwitterionic compounds have a relatively similar degree of hydrophilicity per unit mass. For this reason, it is considered that the degree of hydrophilicity / hydrophobicity of zwitterionic compounds can be compared by the HLB value calculated according to the above-mentioned Griffin's formula.

[0051] In the first gold nanoparticle-containing composition, the content of the zwitterionic compound relative to 100 parts by mass of gold nanoparticles is preferably 25 parts by mass or more and 5,000 parts by mass or less, more preferably 50 parts by mass or more and 2,500 parts by mass or less. In addition, it is particularly preferable that it is 75 parts by mass or more and 1,250 parts by mass or less. If the content of the zwitterionic compound relative to 100 parts by mass of gold nanoparticles is less than 25 parts by mass, the effect of improving storage stability may be somewhat insufficient. On the other hand, if the content of the zwitterionic compound relative to 100 parts by mass of gold nanoparticles is more than 5,000 parts by mass, the solubility or dispersibility of the zwitterionic compound in the dispersion medium may decrease, and the effect of improving storage stability may be somewhat insufficient.

[0052] <Second gold nanoparticle-containing composition> The gold nanoparticle-containing composition of the present invention (second gold nanoparticle-containing composition) contains gold nanoparticles and a polymer compound having a structure represented by any one of the following general formulas (4) to (6).

[0053] TIFF2024108095000005.tif85170 (In the above general formulas (4) to (6), R 12 ~R 19 each independently represents a hydrogen atom or an alkyl group; 10 each independently represents a linking group; Y - is COO - or SO3 - (where * represents the bond site to the polymer main chain)

[0054] (polymer compound) FIG. 3 is a schematic diagram showing one embodiment of the second gold nanoparticle-containing composition of the present invention. As shown in FIG. 3, a polymer compound 50 having a structure represented by any one of general formulas (4) to (6) is strongly coordinated to the surface of a gold nanoparticle 10 via a binding portion 30 (hydrophilic portion 35). This constitutes a gold nanoparticle-containing composition 300 of this embodiment. The binding portion 30 has a positive charge (+) and a negative charge (-) arranged at positions that are not adjacent to each other. In addition, the polymer compound 50 has no charge as a whole molecule. Since gold nanoparticles are usually synthesized in a solution containing a surfactant such as cetyltrimethylammonium bromide (CTAB), CTAB and the like are coordinated to the surface of the gold nanoparticles after synthesis. Recent research has revealed that a potential gradient is generated on the gold nanoparticles due to the density difference of CTAB on the gold nanoparticle surface (Kim et al., SCIENCE ADVANCES 2018, 4(2), e1700682). Since the polymer compound 50 has both positive and negative charges, it is considered to be strongly coordinated in accordance with the potential gradient on the surface of the gold nanoparticles 10. This is presumably why high dispersion stability is exhibited.

[0055] At least a portion of the polymer compound is preferably coordinated to the surface of the gold nanoparticle. As shown in FIG. 3, the polymer compound 50 has a hydrophobic polymer main chain 45 and a binding portion 30 (hydrophilic portion 35). When the dispersion medium is hydrophobic, the binding portion 30 is strongly coordinated toward the surface side of the gold nanoparticle 10, and the polymer main chain 45 is directed toward the dispersion medium side, thereby effectively stabilizing the dispersion of the gold nanoparticle 10. On the other hand, when the dispersion medium is hydrophilic, as shown in FIG. 4, it is presumed that a part of the hydrophilic portion 35 of the polymer compound 50 is coordinated to the surface of the gold nanoparticle 10, and the remaining hydrophilic portion 35 is directed toward the dispersion medium side. In other words, it is considered that the polymer compound 50 is arranged according to the degree of hydrophilicity / hydrophobicity of the dispersion medium, thereby forming a gold nanoparticle-containing composition 400 that is stabilized in dispersion in various dispersion media.

[0056] In general formula (4), R 12 ~R 19 The alkyl group represented by the formula (I) is preferably an alkyl group having 1 to 18 carbon atoms. Examples of the alkyl group having 1 to 18 carbon atoms include a methyl group, an ethyl group, an n-propyl group, an isopropyl group, an n-butyl group, an n-octyl group, a 2-ethylhexyl group, a dodecyl group, and an octadecyl group. These alkyl groups may be further substituted, and may be bonded to each other to form a ring.

[0057] In the general formula (4), A6 is a linking group that bonds the polymer main chain and the phosphate moiety. The linking group A6 includes a carbonyl group, an alkylene group, an arylene group, and -COOR 23 -(R 23 represents an alkylene having 1 to 4 carbon atoms). A6 may be a single bond. In other words, the polymer main chain may be directly bonded to the phosphate ester moiety.

[0058] The alkylene group which is the linking group A6 may be either linear or branched, and is preferably an alkylene group having 1 to 4 carbon atoms. Examples of the alkylene group having 1 to 4 carbon atoms include a methylene group, an ethylene group, a propylene group, and various butylene groups.

[0059] Examples of the arylene group which is the linking group A6 include a 1,2-phenylene group, a 1,3-phenylene group, a 1,4-phenylene group, a naphthalene-1,4-diyl group, a naphthalene-1,5-diyl group, and a naphthalene-2,6-diyl group.

[0060] Linking group A6 "-COOR 23 The carbonyl group in "-" is bonded to a site other than the phosphate ester site. 23 The alkylene having 1 to 4 carbon atoms represented by the following formula may be either linear or branched.

[0061] The linking group A6 may be further substituted with another functional group. From the viewpoint of availability of raw materials and ease of production, the linking group A6 is preferably a carbonyl group or a "-COOR" group. 23 -" is preferred.

[0062] In the general formula (4), A7 is a linking group that bonds the phosphate moiety and the quaternary ammonium moiety. Examples of the linking group A7 include an alkylene group and an arylene group. The alkylene group that is the linking group A7 may be either linear or branched, and is preferably an alkylene group having 1 to 4 carbon atoms. Examples of the alkylene group having 1 to 4 carbon atoms include a methylene group, an ethylene group, a propylene group, and various butylene groups.

[0063] Examples of the arylene group which is the linking group A7 include a 1,2-phenylene group, a 1,3-phenylene group, a 1,4-phenylene group, a naphthalene-1,4-diyl group, a naphthalene-1,5-diyl group, and a naphthalene-2,6-diyl group.

[0064] The linking group A7 may be further substituted with another functional group. From the viewpoints of availability of raw materials and ease of production, the linking group A7 is preferably an alkylene group such as a methylene group or an ethylene group.

[0065] In the general formula (5), A8 is a linking group that connects the polymer main chain to the quaternary ammonium moiety. Examples of the linking group A8 include an alkylene group, an arylene group, an aralkylene group, -COOR 24 -,-CONHR 24 - and -OR 24 -(R 24 represents an alkylene group or an arylene group). A8 may be a single bond. In other words, the polymer main chain may be directly bonded to the quaternary ammonium moiety.

[0066] The alkylene group which is the linking group A8 may be either linear or branched, and is preferably an alkylene group having 1 to 4 carbon atoms. Examples of the alkylene group having 1 to 4 carbon atoms include a methylene group, an ethylene group, a propylene group, and various butylene groups.

[0067] Examples of the arylene group which is the linking group A8 include a 1,2-phenylene group, a 1,3-phenylene group, a 1,4-phenylene group, a naphthalene-1,4-diyl group, a naphthalene-1,5-diyl group, and a naphthalene-2,6-diyl group.

[0068] The aralkylene group of the linking group A8 can be an aralkylene group having 7 to 15 carbon atoms. 24 -", "-CONHR 24 -" and "-OR 24 -” Medium, R 24 The alkylene group represented by the formula (I) may be either linear or branched, and is preferably an alkylene group having 1 to 4 carbon atoms. Examples of the alkylene group having 1 to 4 carbon atoms include a methylene group, an ethylene group, a propylene group, and various butylene groups. 24 -", "-CONHR 24-" and "-OR 24 -” Medium, R 24 Examples of the arylene group represented by the formula (I) include a 1,2-phenylene group, a 1,3-phenylene group, a 1,4-phenylene group, a naphthalene-1,4-diyl group, a naphthalene-1,5-diyl group, and a naphthalene-2,6-diyl group.

[0069] The linking group A8 may be further substituted with another functional group. From the viewpoint of availability of raw materials and ease of production, the linking group A8 is preferably -COOR 24 -or- CONHR 24 - is preferred.

[0070] In the general formula (5), A9 represents a quaternary ammonium moiety and its counter anion moiety, Y - Examples of the linking group A9 include an alkylene group and an arylene group.

[0071] In general formula (6), A 10 is a linking group that connects the polymer main chain to the zwitterionic moiety. 10 Examples of the alkylene group include an alkylene group, an arylene group, an aralkylene group, -COOR 25 -,-CONHR 25 - and -OR 25 -(R 25 represents an alkylene group or an arylene group). 10 may be a single bond, that is, the polymer main chain may be directly bonded to the zwitterionic site.

[0072] Linking group A 10 The alkylene group represented by the formula (I) may be either linear or branched, and is preferably an alkylene group having 1 to 4 carbon atoms. Examples of the alkylene group having 1 to 4 carbon atoms include a methylene group, an ethylene group, a propylene group, and various butylene groups. 10Examples of the arylene group include a 1,2-phenylene group, a 1,3-phenylene group, a 1,4-phenylene group, a naphthalene-1,4-diyl group, a naphthalene-1,5-diyl group, and a naphthalene-2,6-diyl group. 10 From the viewpoints of availability of raw materials and ease of production, it is preferable that is an alkylene group such as a methylene group, an ethylene group, or a propylene group.

[0073] In the general formulas (5) and (6), Y - is the counter anion of the quaternary ammonium moiety, COO - or SO3 - The polymer compound has a structure represented by formula (1), or is represented by formula (2) or formula (3) and Y - SO3 - It is preferred that the compound has a structure:

[0074] The polymer compound preferably has a polymer main chain containing a unit represented by the following general formula (7).

[0075] TIFF2024108095000006.tif29170 (In the above general formula (7), R 25 represents a hydrogen atom or an alkyl group, R 26 represents an alkyl group, a carboxylic acid ester group, a carboxylic acid amide group, an alkoxy group, or an aryl group.

[0076] In general formula (7), R 25 Examples of the alkyl group represented by the formula (I) include alkyl groups having 1 to 4 carbon atoms. Examples of the alkyl group having 1 to 4 carbon atoms include a methyl group, an ethyl group, an n-propyl group, an isopropyl group, and an n-butyl group. 25 From the viewpoint of polymerizability, it is preferable that R is a hydrogen atom or a methyl group.

[0077] In general formula (7), R 26Examples of the alkyl group represented by the formula (1) include alkyl groups having 1 to 30 carbon atoms. Examples of the alkyl group having 1 to 30 carbon atoms include a methyl group, an ethyl group, an n-propyl group, an n-butyl group, an n-hexyl group, an n-decyl group, an n-hexadecyl group, an octadecyl group, a docosyl group, and a triacontyl group.

[0078] In general formula (7), R 26 The carboxylic acid ester group represented by the formula: 27 (R 27 Examples of the carboxylate group include a methyl ester group, an ethyl ester group, an n-propyl ester group, an isopropyl ester group, an n-butyl ester group, a tert-butyl ester group, an octyl ester group, a 2-ethylhexyl ester group, a dodecyl ester group, an octadecyl ester group, a docosyl ester group, a triacontyl ester group, a phenyl ester group, and a 2-hydroxyethyl ester group.

[0079] In general formula (7), R 26 The carboxylic acid amide group represented by the formula: -CO-NR 28 R 29 (R 28 and R 29 are each independently a hydrogen atom, an alkyl group having 1 to 30 carbon atoms, or a phenyl group. Examples of the carboxylic acid amide group include an N-methylamide group, an N,N-dimethylamide group, an N,N-diethylamide group, an N-isopropylamide group, an N-tert-butylamide group, an Nn-decylamide group, an Nn-hexadecylamide group, an N-octadecylamide group, an N-docosylamide group, an N-triacontylamide group, and an N-phenylamide group.

[0080] In general formula (7), R 26Examples of the alkoxy group represented by the formula (I) include an alkoxy group having 1 to 30 carbon atoms and a hydroxyalkoxy group having 1 to 30 carbon atoms. Examples of the alkoxy group include a methoxy group, an ethoxy group, an n-propoxy group, an isopropoxy group, an n-butoxy group, an n-hexyloxy group, a cyclohexyloxy group, an n-octyloxy group, a 2-ethylhexyloxy group, a dodecyloxy group, an octadecyloxy group, a docosyloxy group, a triacontyloxy group, and a 2-hydroxyethoxy group.

[0081] In general formula (7), R 26 Examples of the aryl group represented by the formula (I) include a phenyl group, a 1-naphthyl group, and a 2-naphthyl group.

[0082] R in general formula (7) 26 may be further substituted. Examples of the substituent include alkoxy groups such as methoxy and ethoxy groups, amino groups such as N-methylamino and N,N-dimethylamino groups, acyl groups such as acetyl groups, halogen atoms such as fluorine and chlorine atoms, and the like.

[0083] R in general formula (7) 25 and R 26 can be appropriately selected from the various substituents described above depending on the application. For example, when a highly hydrophobic dispersion medium is used, it is preferable to select a substituent having a long alkyl chain in order to improve dispersibility and stability.

[0084] The content (mol%) of the unit represented by general formula (7) in the polymer compound is preferably 30 mol% to 98 mol%, more preferably 40 mol% to 97 mol%, based on the total units. Also, it is particularly preferably 50 mol% to 90 mol%. By setting the content of the unit represented by general formula (7) in the polymer compound within the above range, the coordination of the polymer compound to the gold nanoparticle surface is stabilized, and the dispersibility of the gold nanoparticles can be further improved.

[0085] In the second gold nanoparticle-containing composition, the content of the polymer compound per 100 parts by mass of gold nanoparticles is preferably 25 parts by mass or more and 5,000 parts by mass or less, more preferably 50 parts by mass or more and 2,500 parts by mass or less. In addition, it is particularly preferable that the content is 75 parts by mass or more and 1,250 parts by mass or less. If the content of the polymer compound per 100 parts by mass of gold nanoparticles is less than 25 parts by mass, the effect of improving storage stability may be somewhat insufficient. On the other hand, if the content of the polymer compound per 100 parts by mass of gold nanoparticles is more than 5,000 parts by mass, the solubility or dispersibility of the polymer compound in the dispersion medium may decrease, and the effect of improving storage stability may be somewhat insufficient.

[0086] The weight-average molecular weight of the polymer compound is preferably from 1,000 to 100,000, and more preferably from 2,000 to 50,000. When the same amounts of a zwitterionic compound and a polymer compound are used relative to gold nanoparticles, the use of the polymer compound is more effective in increasing the storage stability of the resulting gold nanoparticle-containing composition or gold nanoparticle-containing composition dispersion.

[0087] <Gold nanoparticle-containing composition dispersion> The gold nanoparticle-containing composition dispersion of the present invention (first gold nanoparticle-containing composition dispersion) contains a dispersion medium and a gold nanoparticle-containing composition dispersed in the dispersion medium. This gold nanoparticle-containing composition is the first gold nanoparticle-containing composition described above, which contains gold nanoparticles and a compound having a structure represented by any one of general formulas (1) to (3) and whose HLB value is 12 or less. That is, the first gold nanoparticle-containing composition dispersion can be obtained by dispersing the first gold nanoparticle-containing composition described above in a dispersion medium according to a conventional method. Note that it is also possible to return the first gold nanoparticle-containing composition to the first gold nanoparticle-containing composition by removing the dispersion medium by drying the first gold nanoparticle-containing composition dispersion, for example.

[0088] The gold nanoparticle-containing composition dispersion of the present invention (second gold nanoparticle-containing composition dispersion) contains a dispersion medium and a gold nanoparticle-containing composition dispersed in the dispersion medium. This gold nanoparticle-containing composition is the second gold nanoparticle-containing composition described above, which contains gold nanoparticles and a polymer compound having a structure represented by any one of general formulas (4) to (6). That is, the second gold nanoparticle-containing composition dispersion can be obtained by dispersing the second gold nanoparticle-containing composition described above in a dispersion medium according to a conventional method. Note that the second gold nanoparticle-containing composition dispersion can be returned to the second gold nanoparticle-containing composition by removing the dispersion medium by drying the second gold nanoparticle-containing composition dispersion, for example.

[0089] The content (mass%) of gold nanoparticles in the gold nanoparticle-containing composition dispersion is preferably 0.001% by mass or more and 10% by mass or less, more preferably 0.005% by mass or more and 5% by mass or less, based on the total mass of the dispersion. If the content of gold nanoparticles is less than 0.001% by mass, properties such as infrared absorption may be difficult to exhibit. On the other hand, if the content of gold nanoparticles is more than 10% by mass, the effect of improving storage stability may be slightly reduced. The content of gold nanoparticles in the gold nanoparticle-containing composition dispersion can be measured by thermogravimetric differential thermal analysis (TG-DTA).

[0090] (dispersion medium) Examples of the dispersion medium include water, alcohols such as methanol, ethanol, propanol, hexanol, and ethylene glycol, aromatic hydrocarbons such as xylene and toluene, hydrocarbons such as hexane, alicyclic hydrocarbons such as cyclohexane, ketones such as acetone and methyl ethyl ketone, esters such as ethyl acetate and butyl acetate, ethers such as ethylene glycol monobutyl ether, dimethyl sulfoxide, dimethylformamide, etc. If necessary, these dispersion media can be used in combination.

[0091] (Additives) The gold nanoparticle-containing composition dispersion liquid may contain various additives as necessary, such as surfactants, pH adjusters, surface slip agents, rust inhibitors, preservatives, fungicides, antioxidants, reduction inhibitors, evaporation promoters, and chelating agents.

[0092] <Ink> The ink of the present invention contains a gold nanoparticle-containing composition dispersion (a first gold nanoparticle-containing composition dispersion or a second gold nanoparticle-containing composition dispersion). The ink is preferably an ink for inkjet recording.

[0093] The content (mass%) of gold nanoparticles in the ink is preferably 0.001% by mass or more and 10% by mass or less, and more preferably 0.005% by mass or more and 5% by mass or less, based on the total mass of the ink. If the content of gold nanoparticles is less than 0.001% by mass, properties such as infrared absorption may be difficult to exhibit. On the other hand, if the content of gold nanoparticles is more than 10% by mass, the effect of improving storage stability may be somewhat reduced. The content of gold nanoparticles in the ink can be measured by thermogravimetric differential thermal analysis (TG-DTA).

[0094] The dispersion medium contained in the ink may be the same as that contained in the gold nanoparticle-containing composition dispersion liquid. The ink may contain various additives as necessary. Examples of additives include surfactants, pH adjusters, surface slip agents, rust inhibitors, preservatives, fungicides, antioxidants, reduction inhibitors, evaporation promoters, and chelating agents.

[0095] <Toner> The toner of the present invention contains a binder resin and a gold nanoparticle-containing composition. Since the dispersibility of the gold nanoparticles in the toner can be increased, the toner can be produced while maintaining the properties of the gold nanoparticles.

[0096] The toner of the present invention (first gold nanoparticle-containing toner) contains a binder resin and a gold nanoparticle-containing composition. This gold nanoparticle-containing composition is the first gold nanoparticle-containing composition described above, which contains gold nanoparticles and a compound having a structure represented by any one of general formulas (1) to (3) and whose HLB value is 12 or less. In other words, the first gold nanoparticle-containing toner can be obtained by mixing the first gold nanoparticle-containing composition described above with a binder resin according to a conventional method.

[0097] The toner of the present invention (second gold nanoparticle-containing toner) contains a binder resin and a gold nanoparticle-containing composition. This gold nanoparticle-containing composition is the above-mentioned second gold nanoparticle-containing composition, which contains gold nanoparticles and a compound having a structure represented by any one of general formulas (4) to (6). That is, the second gold nanoparticle-containing toner can be obtained by mixing the above-mentioned second gold nanoparticle-containing composition with a binder resin according to a conventional method.

[0098] Examples of the binder resin include styrene-acrylic resin, polyester resin, and epoxy resin. Two or more types of binder resins may be used. The binder resin may be any of a resin having a linear molecular structure, a resin having a branched molecular structure, and a crosslinked resin.

[0099] The toner may contain various additives, such as wax, charge control agent, and external additives, if necessary.

[0100] <Various measurement methods, etc.> (Confirmation of the coordinates) Whether or not the zwitterionic compound or polymeric compound is coordinated to the surface of the gold nanoparticles can be confirmed by infrared absorption spectroscopy (IR). For the gold nanoparticle-containing composition, the gold nanoparticle-containing composition itself can be used as a sample. In addition, for the gold nanoparticle-containing composition dispersion, a poor solvent is added as necessary, centrifuged, and the resulting precipitate is dried and used as a sample. If a characteristic peak is observed at the bond by measuring the IR spectrum, it can be determined that the zwitterionic compound or polymeric compound is coordinated to the surface of the gold nanoparticles.

[0101] (Method of determining gold content) The gold content in the gold nanoparticle-containing composition and the gold nanoparticle-containing composition dispersion can be quantified by ICP emission spectrometry in accordance with JIS K 0116:2014. The gold nanoparticle-containing composition itself can be used as a sample, and the gold content can be quantified by ICP emission spectrometry. In the case of the gold nanoparticle-containing composition dispersion, a hot plate or the like is used to heat the composition to obtain a dried product. Next, aqua regia is added to the dried product, and then a microwave sample pretreatment device (trade name "ETHOS PRO", manufactured by Milestone General) or the like is used to perform microwave acid decomposition to obtain a liquid. The gold content can then be quantified by ICP emission spectrometry using an ICP emission spectrometry device (trade name "CIROS CCD" (manufactured by SPECTRO), etc.).

[0102] (Measurement of weight average molecular weight of polymer compounds) The weight average molecular weight of the polymer compound can be calculated in terms of monodisperse polymethyl methacrylate by gel permeation chromatography (GPC). Measurement of the weight average molecular weight by GPC can be carried out, for example, as follows.

[0103] The sample is added to the eluent below to adjust the concentration to 1% by mass, and left to stand at room temperature (25°C) for 24 hours to obtain a solution. The solution obtained is filtered through a solvent-resistant membrane filter with a pore size of 0.45 μm, and the sample is analyzed according to the conditions shown below. In addition, a molecular weight calibration curve made with standard polymethyl methacrylate resin (product name "EasiVial PM Polymer Standard Kit", manufactured by Agilent Technologies) is used to calculate the molecular weight distribution. Equipment: Agilent 1260 infinity system (Agilent Technologies) Column: PFG analytical linear M columns (PSS) Eluent: 2,2,2-trifluoroethanol ·Flow rate: 0.2mL / min Oven temperature: 40℃ Sample injection volume: 20μL EXAMPLES

[0104] The present invention will be described in more detail below with reference to examples and comparative examples, but the present invention is not limited to the following examples without departing from the gist of the invention. "Parts" and "%" used to describe the amounts of components are based on mass unless otherwise specified.

[0105] [Examples 1 to 18, Comparative Examples 1 and 2] <Preparation of gold nanoparticle dispersion> (Gold nanoparticle dispersion A) 500 mL of 0.0005 mol / L chloroauric acid tetrahydrate (Kishida Chemical) aqueous solution and 500 mL of 0.2 mol / L cetyltrimethylammonium bromide (Kishida Chemical) aqueous solution were mixed, followed by adding 60 mL of 0.01 mol / L sodium borohydride (Tokyo Chemical Industry Co., Ltd.) to obtain solution A, which is a seed particle solution.

[0106] 10 g of cetyltrimethylammonium bromide was dissolved in 500 mL of 0.15 mol / L benzyldimethylhexadecylammonium chloride (Tokyo Chemical Industry Co., Ltd.) aqueous solution. 20 mL of 0.004 mol / L silver nitrate aqueous solution was added, and then 500 mL of 0.001 mol / L chloroauric acid tetrahydrate aqueous solution was further added. Next, 7 mL of 0.078 mol / L L-ascorbic acid aqueous solution (Kishida Chemical Co., Ltd.) was added to obtain solution B.

[0107] 10 g of cetyltrimethylammonium bromide was dissolved in 500 mL of 0.15 mol / L benzyldimethylhexadecylammonium chloride (Tokyo Chemical Industry Co., Ltd.) aqueous solution. 20 mL of 0.004 mol / L silver nitrate aqueous solution was added, and then 500 mL of 0.0005 mol / L chloroauric acid tetrahydrate aqueous solution was further added. Next, 3.6 mL of 0.078 mol / L L-ascorbic acid aqueous solution (Kishida Chemical Co., Ltd.) was added to obtain solution C.

[0108] After dropping 1.2 mL of solution A into solution B, 2.0 mL of solution C was added at a rate of 1.0 mL / 20 min to anisotropically grow seed particles that serve as nuclei. After centrifugation at 10,000×g for 5 min, the solution was redispersed in water so that the gold nanoparticle content was 0.04%, to obtain gold nanoparticle dispersion A. The gold nanoparticles in the obtained gold nanoparticle dispersion A were gold nanorods with an aspect ratio (average value) of 6.

[0109] (Gold nanoparticle dispersion B) Except for changing the amount of solution C to 25.0 mL, gold nanoparticle dispersion B was obtained in the same manner as for the above-mentioned gold nanoparticle dispersion A. The gold nanoparticles in the obtained gold nanoparticle dispersion B were gold nanorods with an aspect ratio (average value) of 13.

[0110] (Gold nanoparticle dispersion C) 10 mL of 0.029 mol / L sodium borohydride was added to 300 mL of 0.00026 mol / L chloroauric acid tetrahydrate (Kishida Chemical) aqueous solution while stirring. The mixture was allowed to react for 24 hours to obtain gold nanoparticle dispersion C. The gold nanoparticles in the obtained gold nanoparticle dispersion C were gold nanospheres, and the average particle size was 14 nm.

[0111] <Production and preparation of zwitterionic compounds> (compound a) 100 parts of 2-hexadecanol, 73 parts of triethylamine, and 3,000 parts of toluene were mixed and cooled to 0°C. 79 parts of 2-chloro-1,3,2-dioxaphospholane-2-oxide were added dropwise while stirring. After keeping at 0°C for 15 minutes, the temperature was raised to room temperature and stirred for 4 hours. The resulting precipitate was filtered, and the solvent was distilled off under reduced pressure to obtain a product. The obtained product was dissolved in 2,700 parts of acetonitrile, and then 491 parts of triethylamine was added while cooling in a dry ice-acetone bath. After stirring at 70°C for 48 hours, the mixture was diluted with methanol. The mixture was purified by column chromatography to obtain a compound a having a structure represented by general formula (1).

[0112] (compound b) Compound b having a structure represented by general formula (1) was obtained in the same manner as in the case of compound a, except that 59 parts of 2-nonanol was used instead of 100 parts of 2-hexadecanol.

[0113] (compound c) 63 parts of 2-(benzyloxy)ethanol and 73 parts of triethylamine were mixed in 3000 parts of toluene and cooled to 0°C. 79 parts of 2-chloro-1,3,2-dioxaphospholane-2-oxide were added dropwise while stirring. The mixture was kept at 0°C for 15 minutes, warmed to room temperature, and stirred for 4 hours. The precipitate was filtered and the solvent was distilled off under reduced pressure. The resulting residue was dissolved in 2700 parts of acetonitrile, and 491 parts of triethylamine was added while cooling in a dry ice-acetone bath. After stirring at 70°C for 48 hours, the mixture was diluted with methanol. After purification by column chromatography, the product was dissolved in 2700 parts of methanol and 10 parts of palladium / carbon (10%) were added. The mixture was stirred for 4 hours under a hydrogen atmosphere. The mixture was filtered and the solvent was distilled off under reduced pressure. 3000 parts of anhydrous dimethylformamide and 250 parts of nonanoic acid were mixed, and 326 parts of N,N'-dicyclohexylcarbodiimide and 193 parts of 4-dimethylaminopyridine were added at 0°C. The mixture was heated to room temperature and stirred for 12 hours. The mixture was diluted with methanol and purified by column chromatography to obtain compound c having a structure represented by general formula (1).

[0114] (compound d) As compound d, 2-(methacryloyloxy)ethyl 2-(trimethylammonio)ethyl phosphate (manufactured by Tokyo Chemical Industry Co., Ltd.) having a structure represented by general formula (1) was prepared.

[0115] The structures and properties of compounds a to d are shown in Table 1. In Table 1, X represents the bonding site between A1 and R1, X' represents the bonding site between A1 and the phosphate ester site, Y represents the bonding site between A2 and the phosphate ester site, Y' represents the bonding site between A2 and the quaternary ammonium cation site, and Z represents the bonding site between R1 and A1.

[0116] TIFF2024108095000007.tif102170

[0117] (compound e) As compound e, octadecyldimethyl(3-sulfopropyl)ammonium hydroxide inner salt (manufactured by Tokyo Chemical Industry Co., Ltd.) having a structure represented by general formula (2) was prepared. The structure and properties of compound e are shown in Table 2. In Table 2, X indicates the bonding site between R5 and A3, Y indicates the bonding site between A4 and the quaternary ammonium cation site, and Y' indicates the bonding site between A4 and SO3 - The binding site is shown.

[0118] TIFF2024108095000008.tif38170

[0119] <Production of polymer compounds> (polymer compound a) A reaction vessel equipped with a cooling tube, a stirrer, a thermometer, and a nitrogen inlet tube was prepared. 17.9 parts of 2-(methacryloyloxy)ethyl 2-(trimethylammonio)ethyl phosphate, 82.1 parts of octadecyl methacrylate, 4.1 parts of azobisisobutyronitrile, and 900 parts of n-butanol were placed in this reaction vessel. After bubbling with nitrogen gas for 30 minutes, the polymerization reaction was completed by heating at 65°C for 8 hours. After cooling to room temperature, the solvent was distilled off under reduced pressure. The resulting residue was dissolved in methanol and purified by dialysis using a dialysis membrane (trade name "Spectra / Por7 MWCO 1kDa", manufactured by Spectrum Laboratories). After distilling off the solvent under reduced pressure, the mixture was dried under reduced pressure at 50°C and 0.1 kPa or less to obtain a polymer compound a having a structure represented by general formula (4). It was confirmed that the content of the unit represented by general formula (7) in the obtained polymer compound a was 79 mol% based on the total units.

[0120] (polymer compound b) Polymer compound b having a structure represented by general formula (4) was obtained in the same manner as in the case of polymer compound a, except that 27.7 parts of ethyl methacrylate was used instead of 82.1 parts of octadecyl methacrylate.

[0121] (polymer compound c) The amount of 2-(methacryloyloxy)ethyl 2-(trimethylammonio)ethyl phosphate was 89.5 parts, and 8.6 parts of butyl methacrylate was used instead of 82.1 parts of octadecyl methacrylate. Furthermore, 900 parts of 2,2,2-trifluoroethanol was used instead of 900 parts of n-butanol. Except for these, the polymer compound c having a structure represented by general formula (4) was obtained in the same manner as in the case of the polymer compound a described above.

[0122] (polymer compound d) Instead of 17.9 parts of 2-(methacryloyloxy)ethyl 2-(trimethylammonio)ethyl phosphate and 82.1 parts of octadecyl methacrylate, 89.5 parts of 2-(methacryloyloxy)ethyl 2-(trimethylammonio)ethyl phosphate were used. Furthermore, instead of 900 parts of n-butanol, 900 parts of 2,2,2-trifluoroethanol were used. Except for these, the polymer compound d having a structure represented by general formula (4) was obtained in the same manner as in the case of the polymer compound a described above.

[0123] The structures and properties of polymer compounds a to d are shown in Table 3. In Table 3, X indicates the bonding site between A6 and the polymer main chain, X' indicates the bonding site between A6 and the phosphate ester site, Y indicates the bonding site between A9 and the phosphate ester site, Y' indicates the bonding site between A9 and the quaternary ammonium cation site, and Z indicates R 26 The bonding sites between the polymer backbone and the carboxyl group are shown.

[0124] TIFF2024108095000009.tif92170

[0125] (polymer compound e) Instead of 17.9 parts of 2-(methacryloyloxy)ethyl 2-(trimethylammonio)ethyl phosphate, 42.3 parts of 3-[[2-(methacryloyloxy)ethyl]dimethylammonio]propane-1-sulfonic acid were used. Also, instead of 82.1 parts of octadecyl methacrylate, 25.8 parts of hexyl methacrylate were used. Furthermore, instead of 900 parts of n-butanol, 900 parts of 2,2,2-trifluoroethanol were used. Except for these, the polymer compound e having a structure represented by the general formula (5) was obtained in the same manner as in the case of the polymer compound a described above.

[0126] (polymer compound f) Instead of 17.9 parts of 2-(methacryloyloxy)ethyl 2-(trimethylammonio)ethyl phosphate, 32.6 parts of 2-[[2-(methacryloyloxy)ethyl]dimethylammonio]acetic acid were used. Also, instead of 82.1 parts of octadecyl methacrylate, 25.8 parts of hexyl methacrylate were used. Furthermore, instead of 900 parts of n-butanol, 900 parts of 2,2,2-trifluoroethanol were used. Except for these, a polymer compound f having a structure represented by general formula (5) was obtained in the same manner as in the case of the polymer compound a described above.

[0127] The structures and properties of polymer compounds e and f are shown in Table 4. In Table 4, X indicates the bonding site between A8 and the polymer main chain, X' indicates the bonding site between A8 and the quaternary ammonium cation site, Y indicates the bonding site between A9 and the quaternary ammonium cation site, and Y' indicates the bonding site between A9 and SO3 - Or CO2 - Z indicates the binding site with R 26 The bonding sites between the polymer backbone and the carboxyl group are shown.

[0128] TIFF2024108095000010.tif58170

[0129] <Production of gold nanoparticle-containing composition dispersion> (Preparation of aqueous solutions of zwitterionic compounds) 5 parts of each zwitterionic compound and 95 parts of ion-exchanged water were placed in a vessel equipped with a stirrer and a thermometer, heated to 80° C., and heated for 5 minutes. After confirming that the zwitterionic compound was completely dissolved, the mixture was cooled to room temperature to obtain aqueous solutions of the zwitterionic compounds a to e, respectively.

[0130] (Preparation of aqueous solutions of polymer compounds) 5 parts of each polymer compound and 95 parts of ion-exchanged water were placed in a container equipped with a stirrer and a thermometer, heated to 80° C., and heated for 5 minutes. After confirming that the polymer compounds were completely dissolved, the mixture was cooled to room temperature to obtain aqueous solutions of polymer compounds a to f, respectively.

[0131] (Gold nanoparticle-containing composition dispersion 1) 100 parts of gold nanoparticle dispersion A and 4.2 parts of the aqueous solution of zwitterionic compound a were mixed and then stirred for 3 hours to obtain gold nanoparticle-containing composition dispersion 1.

[0132] (Gold nanoparticle-containing composition dispersions 2 to 20) Gold nanoparticle-containing composition dispersions 2 to 20 were obtained in the same manner as for the above-mentioned gold nanoparticle-containing composition dispersion 1, except that the formulations shown in Tables 5-1 and 5-2 were used.

[0133] TIFF2024108095000011.tif190170

[0134] TIFF2024108095000012.tif189170

[0135] <Evaluation> The gold nanoparticle-containing composition dispersions 1 to 20 produced in Examples 1 to 18 and Comparative Examples 1 and 2 were evaluated for storage stability as shown below.

[0136] (Storage stability) 100 g of the gold nanoparticle-containing composition dispersion was placed in a 180 mL sealed glass container, sealed, and stored in an oven at 80° C. for 4 days. The absorption spectra of each of the gold nanoparticle-containing composition dispersions 1 to 20 before and after storage were measured according to the measurement conditions shown below, and the absorption intensity maintenance rate was calculated from the following formula (X). The storage stability was then evaluated according to the evaluation criteria shown below. The results are shown in Table 6. Absorption strength maintenance rate (%) = (A2 / A1) × 100 (X) A1: Absorption intensity at the maximum absorption wavelength of the gold nanoparticle-containing composition dispersion before storage A2: Absorption intensity at the maximum absorption wavelength of the gold nanoparticle-containing composition dispersion after storage

[0137] [Absorption spectrum measurement conditions] Measuring device: UV-visible near-infrared spectrophotometer (product name "V-670", manufactured by JASCO Corporation) Wavelength range: 400~1,800nm

[0138] [Evaluation Criteria] A: Absorption strength maintenance rate was 70% or more. B: The absorption strength maintenance rate was 50% or more and less than 70%. C: The absorption strength maintenance rate was 10% or more and less than 50%. D: The absorption strength maintenance rate was less than 10%.

[0139] TIFF2024108095000013.tif157170

[0140] [Example 19] <Toner manufacturing> (Saturated polyester 1 dispersion) The materials shown below were thoroughly mixed to obtain a saturated polyester 1 dispersion. Saturated polyester 1 (polycondensate of ethylene oxide-modified bisphenol A and terephthalic acid, glass transition temperature: 60°C, weight average molecular weight: 29,000, number average molecular weight: 6,000): 20 parts Toluene: 80 parts

[0141] (Toner 1) 104 parts of gold nanoparticle-containing composition dispersion 1 were distilled under reduced pressure, and 416 parts of saturated polyester 1 dispersion were added. The mixture was thoroughly stirred using a magnetic stirrer, and then dropped into heptane (Kishida Chemical) to cause reprecipitation. The resulting precipitate was collected by suction filtration to obtain a mixture of gold nanoparticles and saturated polyester in a powder state. 5 parts of ester wax (peak temperature of maximum endothermic peak in DSC measurement = 70 ° C, Mn = 704) were added to 100 parts of the resulting mixture, and thoroughly mixed using a mixer (product name "FM Mixer", manufactured by Nippon Coke & Co., Ltd.). Then, the mixture was melt-kneaded using a twin-screw kneader (product name "PCM-30 type", manufactured by Ikegai Co., Ltd.) set at a temperature of 150 ° C, to obtain a kneaded product. The kneaded product obtained was spread in a sheet shape on a water-cooled metal belt, cooled, and then coarsely crushed to 1 mm or less using a hammer mill to obtain a coarsely crushed product. The obtained coarsely crushed material was finely pulverized using a mechanical grinder (trade name "T-250", manufactured by Freund Turbo) and then classified using a rotary classifier (trade name "200TSP", manufactured by Hosokawa Micron) to obtain toner particles 1.

[0142] 100 parts of the obtained toner particles 1 and 1 part of hydrophobic silica fine powder (number average particle size of primary particles: 7 nm) surface-treated with hexamethyldisilazane were mixed using a mixer (product name "FM Mixer", manufactured by Nippon Coke & Co., Ltd.) to obtain toner 1.

[0143] [Example 20] (Toner 2) Toner 2 was obtained in the same manner as for Toner 1 described above, except that Gold Nanoparticle-Containing Composition Dispersion 8 was used instead of Gold Nanoparticle-Containing Composition Dispersion 1.

[0144] [Comparative Example 3] (Toner 3) Toner 3 was obtained in the same manner as for Toner 1 described above, except that Gold Nanoparticle-Containing Composition Dispersion 19 was used instead of Gold Nanoparticle-Containing Composition Dispersion 1.

[0145] <Evaluation> The light absorbency of the toners 1 to 3 produced in Examples 19 and 20 and Comparative Example 3 was evaluated as follows.

[0146] (Preparation of thermal fixing film) Three SUS plates with a thickness of 1 cm and a diameter of 5 cm were heated to 100°C on a hot plate. A press machine equipped with a heating mechanism was prepared, and one of the heated SUS plates was placed on the hot plate of the press machine heated to 100°C. A 5cm x 5cm white PET film (manufactured by Toray) was placed on the SUS plate, and 2mg of toners 1 to 3 were placed in the center of the PET film. The remaining second SUS plate was further placed and pressed at 30MPa for 30 seconds. The second SUS plate and the PET film were peeled off, and the temperature of the press machine and hot plate was lowered to 80°C. The PET film with the toner heat-fixed was placed again on the first SUS plate, and a third SUS plate coated with a release agent (manufactured by Daikin) was placed on top of it. The surface was smoothed by pressing at 30MPa for 30 seconds, and five sheets of each of thermally fixed films 1 to 3 were produced.

[0147] (Light absorption in the near infrared region) The dispersibility of gold nanoparticles in the toner was evaluated by the light absorption in the near infrared region. The prepared thermal fixing films 1 to 3 were subjected to spectroscopic analysis measurement in the wavelength range of 900 nm to 1800 nm using an ultraviolet-visible-near infrared spectrophotometer (product name "MV-3300", manufactured by JASCO). The maximum reflectance (%) of the thermal fixing film was calculated using the spectroscopic analysis measurement value of a white PET film alone as a blank. The light absorption (%) was calculated by subtracting the maximum reflectance from 100. The average value of the five sheets was adopted as the light absorption, and the light absorption was evaluated according to the evaluation criteria shown below. The results are shown in Table 7. [Evaluation Criteria] A: The light absorptance was 15% or more. B: The light absorptance was 10% or more and less than 15%. C: The light absorptance was less than 10%.

[0148] TIFF2024108095000014.tif43170

[0149] The disclosure of this embodiment includes the following configuration. (Configuration 1) A gold nanoparticle-containing composition, comprising gold nanoparticles and a compound having a structure represented by any one of the following general formulas (1) to (3), the compound having an HLB value of 12 or less: TIFF2024108095000015.tif86170 (In the general formulas (1) to (3), R1, R5, and R8 each independently represent an organic group, and R2 to R4, R6, R7, and R9 to R 11 each independently represents a hydrogen atom or an alkyl group; A1 to A5 each independently represent a linking group; Y - is COO - or SO3 - (represents (Configuration 2) The gold nanoparticle-containing composition according to configuration 1, wherein at least a portion of the compound is coordinated to the surface of the gold nanoparticle. (Configuration 3) The gold nanoparticle-containing composition according to configuration 1 or 2, wherein the gold nanoparticles are gold nanorods. (Configuration 4) A gold nanoparticle-containing composition, comprising gold nanoparticles and a polymer compound having a structure represented by any one of the following general formulas (4) to (6): TIFF2024108095000016.tif85170 (In the above general formulas (4) to (6), R 12 ~R 19 each independently represents a hydrogen atom or an alkyl group; 10 each independently represents a linking group; Y - is COO - or SO3 - (where * indicates the site of attachment to the polymer main chain) (Configuration 5) The gold nanoparticle-containing composition according to Configuration 4, wherein at least a portion of the polymer compound is coordinated to the surface of the gold nanoparticle. (Configuration 6) The gold nanoparticle-containing composition according to Configuration 4 or 5, wherein the polymer compound has a polymer main chain containing a unit represented by the following general formula (7): TIFF2024108095000017.tif29170 (In the above general formula (7), R 25 represents a hydrogen atom or an alkyl group, R26 represents an alkyl group, a carboxylic acid ester group, a carboxylic acid amide group, an alkoxy group, or an aryl group. (Configuration 7) 7. The gold nanoparticle-containing composition according to any one of claims 4 to 6, wherein the gold nanoparticles are gold nanorods. (Configuration 8) A gold nanoparticle-containing composition dispersion liquid containing a dispersion medium and a gold nanoparticle-containing composition dispersed in the dispersion medium, The gold nanoparticle-containing composition dispersion liquid contains gold nanoparticles and a compound having a structure represented by any one of the following general formulas (1) to (3), and whose HLB value is 12 or less. TIFF2024108095000018.tif86170 (In the general formulas (1) to (3), R1, R5, and R8 each independently represent an organic group, and R2 to R4, R6, R7, and R9 to R 11 each independently represents a hydrogen atom or an alkyl group; A1 to A5 each independently represent a linking group; Y - is COO - or SO3 - (represents (Configuration 9) A gold nanoparticle-containing composition dispersion liquid containing a dispersion medium and a gold nanoparticle-containing composition dispersed in the dispersion medium, The gold nanoparticle-containing composition dispersion liquid contains gold nanoparticles and a polymer compound having a structure represented by any one of the following general formulas (4) to (6). TIFF2024108095000019.tif85170 (In the above general formulas (4) to (6), R 12 ~R 19 each independently represents a hydrogen atom or an alkyl group; 10 each independently represents a linking group; Y - is COO - or SO3 - (where * indicates the site of attachment to the polymer main chain) (Configuration 10) An ink comprising the gold nanoparticle-containing composition dispersion liquid according to Configuration 8 or 9. (Configuration 11) A toner comprising a binder resin and a gold nanoparticle-containing composition, The toner, characterized in that the gold nanoparticle-containing composition contains gold nanoparticles and a compound having a structure represented by any one of the following general formulas (1) to (3), whose HLB value is 12 or less. TIFF2024108095000020.tif85170 (In the general formulas (1) to (3), R1, R5, and R8 each independently represent an organic group, and R2 to R4, R6, R7, and R9 to R 11 each independently represents a hydrogen atom or an alkyl group; A1 to A5 each independently represent a linking group; Y - is COO - or SO3 - (represents (Configuration 12) A toner comprising a binder resin and a gold nanoparticle-containing composition, The toner, wherein the gold nanoparticle-containing composition contains gold nanoparticles and a polymer compound having a structure represented by any one of the following general formulas (4) to (6): TIFF2024108095000021.tif85170 (In the above general formulas (4) to (6), R 12 ~R 19 each independently represents a hydrogen atom or an alkyl group; 10 each independently represents a linking group; Y - is COO - or SO3 - (where * indicates the site of attachment to the polymer main chain) [Explanation of symbols]

[0150] 10: Gold nanoparticles 20: Zwitterionic compounds 30:Joining part 35:Hydrophilic part 40: Hydrophobic section 45: Polymer main chain 50: Polymer compound 100, 200, 300, 400: Gold nanoparticle-containing composition

Claims

1. A gold nanoparticle-containing composition comprising gold nanoparticles and a compound having a structure represented by any one of the following general formulas (1) to (3), the compound having an HLB value of 12 or less: (In the above general formulas (1) to (3), R １ , R ５ , and R ８ each independently represents an organic group; R ２ ~R ４ , R ６ , R ７ , and R ９ ~R １１ each independently represents a hydrogen atom or an alkyl group; A １ ~A ５ each independently represents a linking group; Y － is COO － Or SO ３ － (represents

2. The gold nanoparticle-containing composition of claim 1 , wherein at least a portion of the compound is coordinated to the surface of the gold nanoparticle.

3. The gold nanoparticle-containing composition according to claim 1 or 2, wherein the gold nanoparticles are gold nanorods.

4. A gold nanoparticle-containing composition comprising gold nanoparticles and a polymer compound having a structure represented by any one of the following general formulas (4) to (6): (In the above general formulas (4) to (6), R １２ ~R １９ each independently represents a hydrogen atom or an alkyl group; A ６ ~A １０ each independently represents a linking group; Y － is COO － Or SO ３ － (where * represents the bond site to the polymer main chain)

5. The gold nanoparticle-containing composition according to claim 4 , wherein at least a portion of the polymer compound is coordinated to the surface of the gold nanoparticle.

6. The gold nanoparticle-containing composition according to claim 4 , wherein the polymer compound has a polymer main chain containing a unit represented by the following general formula (7): (In the general formula (7), R ２５ represents a hydrogen atom or an alkyl group; R ２６ represents an alkyl group, a carboxylic acid ester group, a carboxylic acid amide group, an alkoxy group, or an aryl group.

7. The gold nanoparticle-containing composition according to claim 4 , wherein the gold nanoparticles are gold nanorods.

8. A gold nanoparticle-containing composition dispersion liquid containing a dispersion medium and a gold nanoparticle-containing composition dispersed in the dispersion medium, The gold nanoparticle-containing composition dispersion liquid contains gold nanoparticles and a compound having a structure represented by any one of the following general formulas (1) to (3), the compound having an HLB value of 12 or less: (In the above general formulas (1) to (3), R １ , R ５ , and R ８ each independently represents an organic group; R ２ ~R ４ , R ６ , R ７ , and R ９ ~R １１ each independently represents a hydrogen atom or an alkyl group; A １ ~A ５ each independently represents a linking group; Y － is COO － Or SO ３ － (represents

9. A gold nanoparticle-containing composition dispersion liquid containing a dispersion medium and a gold nanoparticle-containing composition dispersed in the dispersion medium, The gold nanoparticle-containing composition dispersion liquid contains gold nanoparticles and a polymer compound having a structure represented by any one of the following general formulas (4) to (6). (In the above general formulas (4) to (6), R １２ ~R １９ each independently represents a hydrogen atom or an alkyl group; A ６ ~A １０ each independently represents a linking group; Y － is COO － Or S.O. ３ － (where * represents the bond site to the polymer main chain)

10. An ink comprising the gold nanoparticle-containing composition dispersion liquid according to claim 8 or 9.

11. A toner comprising a binder resin and a gold nanoparticle-containing composition, The toner is characterized in that the gold nanoparticle-containing composition contains gold nanoparticles and a compound having a structure represented by any one of the following general formulas (1) to (3), the compound having an HLB value of 12 or less: (In the above general formulas (1) to (3), R １ , R ５ , and R ８ each independently represents an organic group; R ２ ~R ４ , R ６ , R ７ , and R ９ ~R １１ each independently represents a hydrogen atom or an alkyl group; A １ ~A ５ each independently represents a linking group; Y － is COO － Or S.O. ３ － (represents

12. A toner comprising a binder resin and a gold nanoparticle-containing composition, The toner, characterized in that the gold nanoparticle-containing composition contains gold nanoparticles and a polymer compound having a structure represented by any one of the following general formulas (4) to (6): (In the above general formulas (4) to (6), R １２ ~R １９ each independently represents a hydrogen atom or an alkyl group; A ６ ~A １０ each independently represents a linking group; Y － is COO － Or SO ３ － (where * represents the bond site to the polymer main chain)