Cementitious production from non-limestone materials.

Abstract

Methods and compositions are provided for deriving supplemental cementitious materials, such as cement and / or pozzolans, from one or more non-limestone materials, such as one or more non-limestone rocks and / or minerals, which are processed in a manner that produces a desired product, such as cement and / or supplemental cementitious material.

Description

[Technical field]

[0001] This application claims priority to U.S. Provisional Patent Application No. 63 / 173,703, filed April 12, 2021, U.S. Provisional Patent Application No. 63 / 240,319, filed September 2, 2021, and U.S. Provisional Patent Application No. 63 / 279,596, filed November 15, 2021, all of which are incorporated by reference herein. [Background technology]

[0002] Cement and cement products are necessities in modern life, essentially building the entire infrastructure of our people. The most common type of cement is ordinary Portland cement, which is used in the production of concrete, mortar, stucco, non-specialty grouts, and many other articles. Although cement is necessary for us, cement production has many drawbacks that must be addressed frequently. Portland cement is toxic and requires a large amount of energy consumption to mine, manufacture, and transport the raw materials. Furthermore, Portland cement production also releases a large amount of greenhouse gases, with Portland cement production contributing 8% of global carbon dioxide emissions. Furthermore, the International Energy Agency (IEA) estimates that cement production will increase by 12-23% by 2050.

[0003] Therefore, there is a need in the cement production field to create new, useful and more environmentally friendly methods of producing cement.

[0004] Incorporation by Reference All publications, patents, and patent applications mentioned in this specification are herein incorporated by reference to the same extent as if each individual publication, patent, or patent application was specifically and individually indicated to be incorporated by reference. [Brief description of the drawings]

[0005] [Figure 1] 1 shows a flow chart representation of the first method. [Diagram 2] 4 shows a flow chart of the second method. [Diagram 3] A method is presented to produce a calcium-rich liquid fraction and a calcium-depleted solid fraction from a non-limestone material. [Figure 4] A method for producing SCM from a calcium-depleted solid fraction is presented. [Diagram 5] Three different methods are presented for precipitating aluminum, iron, and / or magnesium from the calcium-rich liquid fraction. [Figure 6] A method for producing a calcium-containing dechlorinated solid from a calcium chloride-containing solid is disclosed. [Figure 7] A method for producing clinker from calcium-containing dechlorinated solids is presented. [Figure 8] 1 shows an apparatus for producing clinker from non-limestone starting materials comprising a first processor and a second processor. [Figure 9] 9 illustrates an embodiment of the first processor of FIG. 8. [Figure 10] 9 illustrates an embodiment of the second processor of FIG. 8. [Figure 11] A system and method for producing clinker, such as supplemental cementitious material (SCM) and clinker for OPC, from non-limestone materials, e.g., rock, using only a base precipitation unit / step is presented. [Figure 12] A system and method are presented for producing clinker, such as supplemental cementitious material (SCM) and clinker for OPC, from non-limestone materials, e.g., rock, using at least one pyrohydrolysis precipitation unit / step and a base precipitation unit / step. [Figure 13] 1 illustrates an example embodiment of a system for producing clinker, such as clinker for OPC. [Figure 14] 1 shows an optical microscope photograph of a clinker sample obtained by the procedure of Example 4. [Figure 15] The procedure of Example 5 is shown below. Summary of the Invention

[0006] The following description of embodiments of the invention is not intended to limit the invention to those embodiments, but is intended to enable any person skilled in the art to make and use the invention.

[0007] 1. Overview Methods and apparatus are presented for extracting cement precursors and minerals from non-limestone materials containing calcium and silicon elements. A method may include dissolving the non-limestone material using a leaching agent, separating a calcium-rich fraction from a calcium-poor fraction (also referred to herein as a calcium-depleted fraction), converting the calcium-poor fraction to pozzolana and / or other cement precursor compounds, extracting calcium compounds from the calcium-rich fraction, and regenerating the leaching agent. As used herein, a "calcium-rich fraction" includes a generally liquid fraction that is generated from dissolving a non-limestone material with a leaching agent, such as an acid, e.g., HCl. Obviously, this fraction may be subjected to one or more additional steps, e.g., to remove certain materials. The resulting material typically contains lesser amounts of one or more of the certain materials or is otherwise modified, but can still be referred to as a "calcium-rich fraction." Typically, the "calcium-rich fraction" continues the process until it is dehydrated to produce solids, such as solids containing calcium chloride, for example in embodiments where HCl is the leaching agent. Depending on the composition of the non-limestone material, the method may include extracting other minerals (e.g., by precipitation and / or pyrolysis or pyrohydrolysis). The method serves as a multi-purpose extraction and production process, allowing for the extraction of cement precursor materials (e.g., SCM, lime, clinker, etc.) in addition to the extraction of potentially valuable elements (e.g., aluminum, iron, magnesium, etc.). As used herein, the term "clinker" includes cement clinkers, such as Portland cement clinker, unless otherwise indicated. Additionally, the method may also be effective for the production of cement (e.g., ordinary Portland cement). In these variations, the method may further include converting the calcium compounds to cement (e.g., through a clinkering or sintering process).

[0008] The method may be particularly useful in the field of mineral excavation and concrete production. The method may be performed during or after mineral excavation to produce / extract additional resources. In this manner, both cement precursor materials and cement may be extracted and produced. In one mineral excavation embodiment, non-limestone rock may already have been excavated and processed to remove minerals from the rock. The method may then be performed to extract other minerals and produce cement products.

[0009] The method may also be particularly useful for the general purpose of cement production. The production of cement from non-limestone rocks has the potential to make cement production more environmentally friendly.

[0010] The method may provide several potential advantages. The method is not limited to always providing such advantages, but is presented merely as an exemplary representation of how the method may be used. The list of advantages is not intended to be exhaustive, and other advantages may additionally or alternatively exist.

[0011] The method may offer the advantage of enabling a more environmentally friendly method of producing cement. Currently, the most common method of producing cement is by heating limestone to produce lime and carbon dioxide. By producing cement without limestone, carbon dioxide emissions could be significantly reduced.

[0012] The method potentially provides a new resource for cement production: without the need for limestone, cement production could be expanded to many more areas of the world.

[0013] The method may further provide the advantage of simplifying concrete production. Concrete production typically requires ordinary portland cement (OPC), supplementary cementitious materials (SCM), and aggregates. Currently, concrete producers must use different sources to obtain OPC and SCM. The method may allow for extraction of SCM and production of OPC from the same source, such as the same starting material. Furthermore, the method may allow for extraction of SCM and production of OPC and aggregate from the same source. This may significantly simplify the concrete production process and may reduce the cost of concrete production. Thus, provided herein is a method of producing concrete from Portland cement and SCM, such as pozzolan, where the Portland cement and SCM, such as pozzolan, are derived from the same source, e.g., the same non-limestone material (e.g., non-limestone rocks and / or minerals). In certain embodiments, provided herein is a method of producing concrete from Portland cement, an SCM such as a pozzolan, and aggregate, where the Portland cement, the SCM such as a pozzolan, and the aggregate are derived from the same source, e.g., the same non-limestone material (such as non-limestone rocks and / or minerals). In certain embodiments, a system is provided for producing concrete, where the concrete includes Portland cement and an SCM such as a pozzolan, the Portland cement is produced from the non-limestone material, such as non-limestone rocks and / or minerals, in a cement production apparatus, such as the apparatus described herein, the SCM is produced from the non-limestone material, such as non-limestone rocks and / or minerals, in a SCM production apparatus, such as the apparatus described herein, and the cement production apparatus, the SCM production apparatus, and the non-limestone material, such as non-limestone rocks and / or minerals, are all at a single location, such as a location where the non-limestone rocks and / or minerals are mined from a source. In certain embodiments, the cement production apparatus and the SCM production apparatus are the same apparatus.The concrete may further include aggregate, and the system may further include aggregate generating equipment, such as equipment including crushers, grinders, and sieves, for generating aggregate from non-limestone materials, such as non-limestone rocks and / or minerals, the aggregate generating equipment being co-located with the cement generating equipment and the SCM generating equipment. The co-location may be, for example, such that the various equipment are all within a 10, 5, 1, or 0.5 mile radius, such as within a 1 mile radius or even within a 0.5 mile radius, and the source of the non-limestone materials, such as mined non-limestone rocks and / or minerals, may be within that radius or may be further away, but in any case within 10, 5, 4, 3, 2, or 1 mile, such as within 2 miles, of the location.

[0014] The method may also provide the potential benefit of increased utility of the materials added to make concrete, i.e., in addition to enabling concrete production, the method may also provide the benefit of mineral extraction beyond concrete production (e.g., metals such as aluminum and iron may also be extracted for use or sale).

[0015] Additionally, as an advantage of the extraction of minerals beyond their use for concrete production, the method may offer the advantage of efficient refining of minerals (e.g., refining of metals such as aluminum and iron) simultaneously with the extraction of cementitious materials.

[0016] In certain variations, the method may further provide the potential advantage of extraction of high purity SCM (e.g., micro- or nano-silica or silica fume), i.e., in variations where the extracted silica is not recycled, for example, for the production of calcium base for the extraction of metals (e.g., variations where aluminum and iron are extracted by pyrolysis), a large amount of the extracted silica may be preserved in a purer form.

[0017] The process may offer the advantage of a more energy efficient method for the extraction of cement and other minerals. In some variations, the process may incorporate the use of mechanical vapor recompression to recycle latent heat for water evaporation or other electrical heating, or to reintroduce heat from other reaction steps, to reduce energy (especially non-electrical energy) consumption.

[0018] As shown in FIG. 1 , a method for extracting cement precursors and minerals from a non-limestone starting material includes obtaining a non-limestone material S110, where the non-limestone material includes a material that includes the element calcium and optionally the element silicon; creating a calcium-rich fraction and a calcium-depleted fraction from the non-limestone material S130, where creating the calcium-rich fraction and the calcium-depleted fraction of the non-limestone material by dissolving at least calcium compounds, where dissolving the non-limestone material includes adding at least one leaching agent S132; The method includes separating a calcium-depleted fraction from the calcium-rich fraction S140 (wherein the calcium-depleted fraction may include pozzolan); separating calcium-containing compounds from the calcium-rich fraction (e.g., in the case of embodiments where HCl is the lixiviant, to produce solids comprising calcium chloride) S150; optionally decomposing the calcium compounds (e.g., dechlorinating the calcium chloride-containing solids to produce dechlorinated solids comprising calcium, and optionally clinkering the dechlorinated solids comprising calcium) S160; and optionally regenerating the lixiviant S170.

[0019] The method functions to extract pozzolans (also referred to as supplemental cementitious materials (SCM)), and / or other cement precursor materials (e.g., clinker, lime, hydrated lime, tricalcium silicate, dicalcium silicate, and calcium carbonate), magnesium compounds, and metals from non-limestone materials. Depending on the embodiment and type of non-limestone material, the method may have multiple variations in which the method may be modified with respect to desired inputs (i.e., type of non-limestone material) and / or outputs (i.e., cementitious materials and metals). Thus, depending on the embodiment, in addition to having additional / alternative steps, method steps may be omitted, repeated, or altered as required for the embodiment. The method may be particularly useful for processing calcium silicate rocks, but may be practiced with any non-limestone material containing silicon and / or calcium.

[0020] In a modified embodiment, the method may be used to produce cement. In this embodiment, as shown in FIG. 2, a method for cement production and cement precursor production includes obtaining a non-limestone material S110, where the non-limestone material includes material containing the element calcium and optionally the element silicon; creating a calcium-rich and calcium-depleted fraction from the non-limestone material S130, where creating the calcium-rich and calcium-depleted fractions of the non-limestone material by dissolving at least calcium compounds, where dissolving the non-limestone material includes adding at least one leaching agent S132; and separating the calcium-depleted fraction from the calcium-rich fraction S140, where the calcium-depleted fraction includes adding at least one leaching agent S142. the calcium-depleted fraction may include pozzolan); separating calcium-containing compounds from the calcium-rich fraction (e.g., in embodiments where HCl is the lixiviant, to produce solids comprising calcium chloride) S150; optionally decomposing the calcium compounds (e.g., dechlorinating the calcium chloride-containing solids to produce dechlorinated solids comprising calcium, and optionally clinkering the dechlorinated solids comprising calcium) S160; optionally regenerating the lixiviant S170; and, if the decomposition includes calcium compound products, producing clinker or cement from the calcium compound products S180.

[0021] The method functions to extract supplemental cementitious materials (SCM) and / or other cement precursor materials (e.g., clinker, tricalcium silicate, dicalcium silicate, lime, or hydrated lime), as well as metals, from the non-limestone material, and optionally convert the cement precursor materials to cement. Depending on the embodiment and the type of non-limestone material, the method may have multiple variations in which the method may be modified with respect to desired inputs (i.e., type of non-limestone material) and / or outputs (i.e., type of cement and metals). Thus, depending on the embodiment, in addition to having additional / alternative steps, method steps may be omitted, repeated, or altered as required for the embodiment. The method may be particularly useful for processing calcium silicate rocks, but may be practiced with any non-limestone material containing silicon and calcium. The method may be particularly useful for the production of clinker or cement, such as ordinary Portland cement (OPC), and may be implemented for the production of Portland cement types (e.g., Type 1 Portland cement, Type 2 Portland cement, Type 3 Portland cement, Type 4 Portland cement, or Type 5 Portland cement, or equivalent types), or more generally, other types of cement and cementitious materials (e.g., lime, hydrated lime, mortar, fly ash, slag, tricalcium silicate, dicalcium silicate, and silica fume). The method may additionally or alternatively allow the production of any compound that includes amorphous silica, calcium oxide (CaO), and / or magnesium oxide (MgO) as starting materials.

[0022] In some variations, the method may include additional or alternative steps. Additional steps may relate to processing materials, regenerating compounds, processing waste materials, and / or improving other reactions. Additional / alternative steps may be incorporated for desired implementations. Examples of additional / alternative steps include electrolyzing reagents / materials, pyrolyzing or pyrolyzing reagents / materials or solutions, precipitating reagents / materials, applying catalytic processes, and synthesizing reagents / materials using water electrolysis to generate both acid and base or only acid or base for initial rock dissolution and / or isolation of calcium species. In many variations, the method may include a calcium enrichment step. That is, the method may include enriching S120 non-limestone materials, thereby creating a material having a higher concentration of calcium compared to the original material. In many variations, the method may further perform a carbon capture / sequestration step. That is, the method may further include scrubbing flue gas. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0023] Starting materials Block S110, which includes obtaining non-limestone material, functions in obtaining the starting material for the process. Obtaining non-limestone material S110 may include any common process for obtaining non-limestone material, such as excavating, purchasing, finding, receiving non-limestone material, etc.

[0024] Generally, any suitable starting material can be used as long as it contains calcium in a sufficient amount to provide the desired end product, e.g., clinker or cement, e.g., final Portland cement. If a process is used that also produces a supplementary cementitious material (SCM), the starting material will also contain one or more compounds that can result in a final material containing amorphous (non-crystalline) compounds that can function as SCMs. These can include amorphous silica, in which case the starting material will also contain silicon. However, as is known in the art, other materials may result in amorphous compounds that function as SCMs, such as amorphous iron and alumina compounds, in which case the starting material will contain the necessary starting elements. In certain embodiments in which both cement, such as clinker or Portland cement, and SCM are produced, the starting material includes non-limestone rocks and / or minerals that contain calcium and silicon, e.g., calcium silicate-containing rocks and / or minerals. Any suitable rocks and / or minerals may be used, such as one or more of basalt, gabbro, pyroxenite, anorthosite, skarn, amphibolite, or combinations thereof.

[0025] In certain embodiments, non-limestone materials are used. As used herein, "non-limestone materials" includes materials containing low amounts of calcium carbonate (e.g., limestone), e.g., less than 10% calcium carbonate. Generally, a lower amount of calcium carbonate is preferred to avoid the production of carbon dioxide in various steps. However, many materials, such as non-limestone rocks and / or minerals, may contain some amount of calcium carbonate and still be suitable for use in the processes and apparatus described herein. Non-limestone materials may be rocks and / or minerals, or industrial waste, or combinations thereof. Non-limestone materials include calcium and generally silicon. Preferred non-limestone starting materials include at least 10% calcium, more preferably at least 15% calcium, and even more preferably at least 25% calcium. Preferred starting materials include less than 30, 25, 20, 15, 10, 5, 2, or 1% calcium carbonate, e.g., less than 10% or less than 5%.

[0026] In some variations, the non-limestone material includes silicate rock, but generally can include any one or more non-limestone materials that together contain calcium and possibly silicon. The non-limestone material can be discovered / selected to additionally include any set of desired compounds (and / or unknown compounds). In addition to calcium and possibly silicon, the non-limestone material may include other minerals and / or compounds. Examples include calcium compounds (e.g., calcium oxide), magnesium compounds (e.g., magnesium oxide), aluminum compounds (e.g., aluminum oxide), iron compounds (e.g., iron(II) oxide, iron(III) oxide), silicates (e.g., silicon dioxide), and carbon compounds (e.g., carbon dioxide). Examples of silicate rocks can include anorthosite, skarn, gabbro, pyroxenite, mafleite, basalt, copper skarn, tungsten skarn, fly ash, slag, old cement, concrete, mined rock, and tailings. Other examples of rocks may include mafic and ultramafic rocks. More generally, suitable non-limestone rocks and / or minerals include basalt, igneous apatite, wollastonite, anorthosite, montmorillonite, bentonite, calcium-bearing feldspar, anorthite, diopside, pyroxene, pyroxene, mafuhte, kamafuhte, clinopyroxene, coleoptile, coleoptile, augite, pigeonite, margarite, calcium serpentine, garnet, scheelite, skarn, limestone, natural gypsum, apatite, fluorapatite, or any combination thereof. Other suitable rocks and / or minerals will be apparent to those skilled in the art. Non-limestone materials may also include one or more industrial products, for example, one or more industrial waste products.

[0027] In some variations, obtaining the non-limestone material S110 may include obtaining processed or partially processed material. That is, the non-limestone material may have been initially obtained and processed for some other reason and then transferred for this processing (e.g., for salt extraction). In variations involving processed or partially processed non-limestone material, method steps may be added or omitted depending on the content of the non-limestone material. For example, in one example where some metals have already been extracted, the separation step (e.g., precipitation) and decomposition (e.g., pyrolysis) steps may be modified or omitted. In another example, a concentration step may be added (e.g., concentrating the non-limestone material S120) to use the significantly depleted non-limestone material.

[0028] In some variations, the method may include block S120, concentrating the non-limestone material. Concentrating the non-limestone material serves to increase the calcium concentration of the non-limestone material. This may be particularly useful in pre-processed rocks from which minerals or compounds have been extracted. For example, flotation, magnetic separation, and other physical and chemical separation methods may be used to remove calcium-depleted fractions of the rock.

[0029] Non-limestone materials, such as rocks and / or minerals, may be processed to provide particles within a desired size range. Any suitable process or processes may be used, such as crushing, grinding, and / or milling, sieving, and the like. Suitable size ranges include 1-500u, 5-300u, 10-200u, 20-130u, 45-90u, or combinations thereof. In a preferred embodiment, the size range is 20-130u. In a more preferred embodiment, the size range is 45-90u.

[0030] Generation of calcium-rich and calcium-depleted fractions Block S130, which includes creating a calcium-rich and a calcium-depleted fraction from the non-limestone material, functions to break down the non-limestone material to separate calcium compounds from non-calcium compounds such as SCM. Block S130 may include dissolving the non-limestone material, which includes dissolving at least the calcium compounds within the non-limestone material, thereby creating the calcium-rich and calcium-depleted fractions. In this manner, dissolving the non-limestone material S130 may partially dissolve the non-limestone material such that silica and silica compounds remain solid and other compounds (e.g., bound to calcium) are dissolved.

[0031] Dissolving the non-limestone material S130 may include adding a leaching agent S132. The leaching agent may include a single compound, multiple compounds, and / or a series of compounds. In certain embodiments, the leaching agent includes a single compound, e.g., HCl. The leaching agent may function in at least partially dissolving the non-limestone material. The leaching agent may be water, a metal salt, an acid, and / or an oxidizing agent. In general, the leaching agent may have the limitation that the leaching agent dissolves calcium compounds in the non-limestone material. In some variations, the leaching agent includes a replenishable compound(s).

[0032] In one example, the leaching agent is an acid, i.e., a first acid. In certain embodiments, only one acid is used, e.g., only HCl. The first acid functions to dissolve calcium compounds in the non-limestone material. Additionally, the first acid can dissolve non-silicate compounds (e.g., metals and salts) in the material, thereby creating a calcium-depleted solid fraction, e.g., a silicate-based solid fraction, and a minerals-based liquid fraction (a calcium-rich liquid fraction). Alternatively, the first acid may dissolve silicate materials. The first acid is preferably a strong acid, but may alternatively include a weak acid or protons generated at the anode, such as by water decomposition. In one variation, the first acid includes hydrochloric acid (HCl). In one variation, the first acid consists essentially of HCl. In another variation, the first acid includes hydroiodic acid (HI). Other examples of first acids may include hydrobromic acid, nitric acid, and hydronium ions generated by electrolysis of water. In one variation, HCl can dissolve metals in non-limestone materials to create a metal-rich liquid fraction (calcium-rich liquid fraction).

[0033] In certain embodiments, the non-limestone material, e.g., rock and / or mineral material, is contacted with a strong acid to form a pulp that includes the acid and the rock and / or minerals. Any suitable strong acid may be used, such as HCl, HBr, HI, H2SO4, or HNO3. In certain embodiments, the strong acid includes HCl, and HCl may be the only strong acid used in this procedure. Generally, in such embodiments, it will be understood that the acid used to dissolve the non-limestone material is HCl, although other acids may be used for non-essential functions, such as equipment cleaning, etc. HCl is particularly useful because it produces chlorides, such as calcium chloride, which are useful starting materials for further steps in the process. HCl also lends itself to relatively easy regeneration at one or more points in the process. For convenience, the remainder of the process will be described in terms of HCl. As will be apparent to one of skill in the art, if another acid is used in addition to or as a replacement for HCl, suitable adjustments can be made to accommodate the additional / alternative acid.

[0034] Non-limestone materials, e.g., rocks and / or minerals such as silicate rock materials, dissolve in hydrochloric acid (HCl). In certain embodiments, the percentage of the strong acid that comprises HCl is at least 20, 30, 40, 50, 60, 70, 80, 90, 95, or 99% of the strong acid. In certain embodiments, 100% of the strong acid is HCl. Any suitable concentration of HCl may be used, such as 5-40%, 10-37%, 10-30%, 15-35%, 17-23%, 20-30%, or about or exactly 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, or 30%, e.g., about or exactly 20%. In a preferred embodiment, the HCl is 10-37%. In an even more preferred embodiment, the HCl is 15-35%. The ratio of starting materials, such as solid rocks and / or minerals, to liquid, e.g., leaching agent, such as acid, in the initial pulp can be any suitable ratio. It will be appreciated that some of the solid rocks and / or minerals will immediately begin to dissolve in the acid, and these ratios will change as the solids dissolve into solution. Suitable initial ratios can be within the range of 5% solids / 95% liquid to 40% solids / 60% liquid, such as 10% solids / 90% liquid to 30% solids / 70% liquid; in a preferred embodiment, 15% solids / 85% liquid to 25% solids / 75% liquid, e.g., 20% solids / 80% liquid.

[0035] The pulp is treated to dissolve at least a sufficient amount of calcium compounds in the non-limestone materials, e.g., rocks and / or minerals, into solution to provide a good end product, e.g., to be converted into cement, such as clinker or Portland cement. In certain embodiments, at least 50, 60, 70, 80, 90, 95%, or 100%, preferably at least 70%, more preferably at least 80%, and even more preferably at least 90%, of the calcium in the starting material goes into solution. This treatment may be done in an open to air or at least unpressurized process. This treatment may include heating and / or maintaining the pulp at a temperature or temperature range for a certain period of time. Generally, a treatment period and / or temperature that results in the desired dissolution may be used. Suitable temperature ranges for maintaining the pulp include 60-115°C, 80-115°C, 90-115°C, 100-115°C, 60-112°C, 80-112°C, 90-112°C, 100-112°C, 60-110°C, 80-110°C, 90-110°C, or 100-110°C. It will be appreciated that due to the high concentration of HCL present and as material dissolves into the liquid phase, the boiling temperature of the HCl solution may exceed 100°C. Thus, in certain embodiments, the temperature is at least 95, 96, 97, 98, 99, or 100°C, in preferred embodiments, the temperature is at least 90°C, in a range of more preferred embodiments, the temperature is at least 95°C, in even more preferred embodiments, the temperature is at least 98°C, and in even more preferred embodiments, the temperature is at least 100°C. In certain embodiments, the maximum temperature is 105, 106, 107, 108, 109, 110, 111, 112, 113, 114, or 115° C., in preferred embodiments, the maximum temperature is 105° C., in more preferred embodiments, the maximum temperature is 108° C., and in even more preferred embodiments, the maximum temperature is 110° C. In certain embodiments, the temperature is brought to and / or maintained at 100-115° C. In certain embodiments, the temperature is brought to and / or maintained at 100-110° C.In certain embodiments, the temperature is brought to and / or maintained at 100-115°C. Any suitable treatment period may be used. This may depend, in part, on the calcium content of the starting material, such as non-limestone rocks and / or minerals. Materials with lower calcium content may require longer treatment to achieve the desired amount of calcium salts in solution. Thus, the treatment period may be at least 1, 2, 3, 4, 5, 6, 7, 8, or 10 hours, and / or no more than 2, 3, 4, 5, 6, 7, 8, 10, 12, 15, 20, 24, 30, 36, 40, 48, 60, or 72 hours. In certain embodiments, the period may be 2-24 hours, such as 4-18 hours, or even no more than 4-12 hours. In certain embodiments, the period may be 6-72 hours, such as 4-48 hours, or 4-36 hours, or 4-24 hours. The pulp may be agitated during processing, e.g., stirred, e.g., at 10-1000 RPM, 20-800 RPM, 50-500 RPM, 50-400 RPM, or 100-300 RPM. In a preferred embodiment, the pulp is agitated at 50-400 RPM, more preferably 100-300 RPM. Other agitation methods known in the art may be used. A calcium-depleted fraction (solids) and a calcium-enriched fraction (liquids) are produced from the pulp. A portion of the acid, such as HCl, may migrate to the gas or vapor phase during processing and may be recaptured and returned for use as a leaching agent.

[0036] In some variations, adding the first acid may include adding an organic acid or a biological acid (e.g., oxalic acid). Adding an organic first acid may selectively leach non-limestone materials, thereby allowing for selective extraction of metals. Examples of organic acids that may be incorporated include propionic acid, butyric acid, citric acid, succinic acid, malic acid, tartaric acid, and oxalic acid. In one example, the first organic acid may selectively leach all minerals from the non-limestone material (e.g., by pyrolysis). In another example, the organic first acid may selectively leach all minerals except calcium from the non-limestone material.

[0037] In some variations, a microorganism can be used to produce a first organic acid. The microorganism may be engineered to produce the organic acid by utilizing CO2 as a carbon source, so that the CO2 produced by decomposing the organic acid in a subsequent step can be recycled or mitigated by feeding this CO2 to the microorganism.

[0038] Separation of calcium-rich fraction from calcium-depleted fraction Block S140, which includes separating the calcium-depleted fraction from the calcium-rich fraction, functions to separate the solid and liquid fractions produced from the non-limestone material. In many variations, the calcium-depleted fraction includes pozzolana. In some variations where a first acid leaching agent is added (e.g., HCl first acid), this includes separating the solid fraction silicate rock (calcium-depleted fraction) from the dissolved liquid fraction (calcium-rich fraction), thus extracting the SCM from the metals in the non-limestone material. Any suitable separation method may be implemented. In some variations, block S130 may further include drying the separated solid fraction (e.g., drying the SCM). Additional or alternative acids to HCl may include HBr, HI, HNO3, or any acid that produces soluble calcium salts.

[0039] In many variations, separating the calcium-depleted fraction from the calcium-rich fraction S140 occurs after some and / or all of block S130. In some variations, separating the calcium-depleted fraction from the calcium-rich fraction S140 may occur prior to or simultaneously with the dissolution of the non-limestone materials. This may be done by mechanically (e.g., physically grinding components to separate, separating by density, etc.) and / or electrostatically separating the calcium-rich portion from the calcium-depleted portion prior to the dissolution of the non-limestone materials.

[0040] In some variations, separating the calcium-depleted fraction from the calcium-rich fraction S140 is accomplished by filtering the non-limestone material. Filtration can be used to separate the solid and liquid portions. In one embodiment, vacuum filtration is used, where a pressure differential is used to force the fluid through a filter. In another embodiment, hot filtration is used, where the solution is heated and then forced through a filter. In another embodiment, cold filtration is used, where the solution is first cooled to crystallize additional components (e.g., SCM) and then filtered.

[0041] In some variations, a filter press is performed to separate the solid fraction. The filter press can be made by stacking multiple filter elements to allow the filter to be easily opened to remove the filtered solids. The filter press can be performed in any desired filtration process as described above.

[0042] Separating the calcium-depleted fraction from the calcium-rich fraction S140 may significantly deplete the volume of the liquid fraction. Therefore, additional solution can be added to the calcium-rich fraction to make up the volume before this occurs or after it occurs. This may be done at any separation and / or precipitation step. Additional solution may be added at any step to maintain a desired working volume.

[0043] Block S150, which includes separating calcium compounds from the calcium-rich fraction, e.g., forming solids including calcium chloride, functions to separate calcium compounds from non-limestone materials. Additionally, block S150 may include separating other metal compounds, which may or may not be part of the calcium compounds. Block S150 may be embodiment specific and may vary depending on the desired metal extraction and / or mineralogy content of the non-limestone materials. For example, in some variations, separating calcium compounds from the calcium-rich fraction S150 includes precipitating calcium compounds from a liquid or liquid-like mixture. Additionally, block S150 may depend on the preceding method steps. For example, utilizing HI as the first acid leaching agent compared to HCl may vary the specific details of block S150. Generally, separating the calcium compounds from the calcium-rich fraction S150 may include altering the thermodynamic conditions (e.g., increasing or decreasing the temperature, increasing or decreasing the pressure, increasing or decreasing the compound concentration), adding an acid or base, and / or adding an oxidizing or reducing agent. In certain embodiments, for example, when HCl is the acid, separating the calcium compounds includes dehydrating the calcium-rich liquid fraction (optionally after treating the calcium-rich liquid fraction to remove one or more non-calcium compounds) to produce a solid comprising calcium chloride.

[0044] Treatment of calcium-rich fractions The calcium-rich fraction is then further processed. In certain embodiments, the end result of the further processing is to produce cement, such as clinker or Portland cement, and generally to regenerate the acid. Furthermore, depending on the processing of the calcium-rich fraction, certain non-calcium materials may be generated, such as materials containing one or more of iron, aluminum, and / or magnesium. The further processing may depend on the potential composition of the calcium-rich fraction, which may depend at least in part on the starting material.

[0045] Generally, the calcium-rich fraction contains non-calcium salts, also referred to herein as metal compounds, in addition to calcium salts such as calcium chloride, and the following procedure may depend on the ratio, or expected ratio, of non-calcium salts (metal compounds) to calcium salts, which may be based, at least in part, on the starting material. If the ratio of one or more non-calcium salts exceeds or is expected to exceed a certain threshold in the calcium-rich fraction, the calcium-rich fraction may be treated to remove at least a portion of the one or more non-calcium salts, e.g., to bring their levels in the calcium-rich fraction below a threshold. The threshold may be determined, for example, by the desired composition of the final product, e.g., a cement such as clinker or Portland cement. For example, certain non-calcium substances, e.g., derivatives of iron, aluminum, and / or magnesium salts, may be acceptable in a cement such as a clinker or Portland cement, but only below a certain level, which often depends on the type of cement (e.g., type 1, 2, 3, 4, or 5) and / or the specifications to be met, since the specifications may vary depending on the geographic location. The threshold value may be based, at least in part, on the expected levels of non-calcium salt derived materials, such as aluminum, iron, and / or magnesium materials, in the final clinker or cement, such as Portland cement product after further processing.

[0046] In certain embodiments, the calcium-rich fraction is not processed to remove non-calcium salts. This may be the case when the starting material is particularly rich in calcium compounds, an example of such a starting material being wollastonite. In such cases, processing of the calcium-rich fraction generally involves removal of water to produce solid calcium salts, and further processing to convert the calcium salts into the desired end product, e.g., clinker or cement such as Portland cement. Such processing is further described below.

[0047] In certain embodiments, the calcium-rich fraction is treated to remove one or more non-calcium salts. Any suitable treatment or combination of treatments can be used, so long as a sufficient amount of the non-calcium salts are converted into a form that can be separated from the calcium-rich fraction, such as converted into a solid form. The treatment or combination of treatments may result in the regeneration of at least a portion of the original strong acid, e.g., HCl. It is not necessary to remove all of the non-calcium salts, so long as the percentage remaining in solution is below a threshold percentage. In certain embodiments, the calcium-rich fraction is raised to and / or maintained at one or more temperatures or temperature ranges to cause the formation of one or more insoluble non-calcium substances from the one or more non-calcium salts. Additionally or alternatively, in certain embodiments, the calcium-rich fraction is treated with one or more substances, such as one or more bases, that cause the formation of one or more insoluble non-calcium substances from the one or more non-calcium salts.

[0048] Thus, the calcium-rich fraction may contain soluble non-calcium salts, such as salts of Al, Fe, and / or Mg, sometimes referred to as metal-containing compounds. Separating the calcium-containing compounds from the calcium-rich fraction S150 includes precipitating the metal-containing compounds. In certain embodiments, this includes a one-step pyrolysis (thermohydrolysis) process. In certain embodiments, this includes a multi-step pyrolysis (thermohydrolysis) process, such as a two-step pyrolysis (thermohydrolysis) process. In certain embodiments, this includes the addition of a base. In certain embodiments, one-step pyrolysis (thermohydrolysis) and the addition of a base are used. In certain embodiments, two-step decomposition (thermohydrolysis) and the addition of a base are used. In certain embodiments, only the addition of a base is used. Generally, at least a portion of the strong acid, e.g., HCl, is also regenerated during the process(es).

[0049] In certain embodiments, raising the calcium-rich fraction to a temperature or temperature range and / or maintaining it at a temperature or temperature range (one-step pyrolysis or pyrohydrolysis) causes the formation of a set of insoluble non-calcium materials that can be removed from the calcium-rich fraction. The temperature or temperature range can be such that one or more non-calcium salts, such as at least iron and aluminum salts, form insoluble materials, such as insoluble iron and aluminum materials. Further non-calcium salts that can form insoluble materials include salts of boron, lithium, rubidium, cesium, strontium, barium, and / or radium. The temperature can be any suitable temperature or range of temperatures, for example at least 140, 145, 150, 155, 160, 165, 170, 175, or 180° C., and / or up to 145, 150, 155, 160, 165, 170, 175, 180, 185, 190, or 195° C. In certain embodiments, the calcium-enriched fraction is heated to 140-195° C., in preferred embodiments, the calcium-enriched fraction is heated to 140-185° C., in more preferred embodiments, the calcium-enriched fraction is heated to 160-185° C., or even 175-185° C. In certain embodiments, the calcium-enriched fraction is heated to at least 1600° C., for example at least 170° C., such as at least 175° C., and in certain cases at least 180° C. Any suitable method of bringing the calcium-rich fraction to and / or maintaining it at a desired temperature may be used. Methods of heating a solution at and / or maintaining it at a temperature or temperature range are well known in the art. The calcium-rich solution may be maintained at or near the desired temperature for a suitable period of time, such as at least 0, 1, 2, 5, 10, 20, 30, 40, or 50 minutes, or 1, 1.5, 2, 2.5, 3, 4, 5, 7, or 10 hours, and / or no more than 1, 2, 5, 10, 20, 30, 40, or 50 minutes, or no more than 1, 1.5, 2, 2.5, 3, 4, 5, 7, 10, or 15 hours.In certain embodiments, the calcium-rich fraction is maintained at or near the desired temperature for 10 minutes to 5 hours, such as 30 minutes to 4 hours, and in some cases 1 to 3 hours. As the calcium-rich fraction is heated and / or maintained at an elevated temperature, HCl gas is driven off. Some or all of this gas can be captured and dissolved in an aqueous medium to regenerate HCl. In certain embodiments, the HCl gas is captured and returned to the aqueous medium, such as an HCl solution that is or will be used as a leaching agent for the processing of subsequent materials containing calcium. Insoluble material generated by increasing the temperature can be separated from the remaining calcium-rich fraction by any suitable method, such as centrifugation, filtration, etc. The insoluble materials may include one or more compounds of aluminum and / or iron, such as, for example, Mg, Al, Fe, Ca, and oxides, hydroxides, oxyhydroxides, silicates, silicate hydrates, or composite phases containing any of Si, O, and H, such as Al(OH), AlO, AlO(OH), Fe(OH), Fe(OH), FeO(OH), FeO, FeO, FeO.

[0050] In certain embodiments, a two-step pyrolysis (thermohydrolysis) process is used. This is done by first incorporating a two-step pyrolysis. First, the mixture is heated to a temperature or temperature range such that aluminum salts, e.g., AlCl3, form insoluble aluminum materials, e.g., Al(OH)3, Al2O3, AlO(OH), etc., but iron salts, e.g., FeCl2 and / or FeCl3, do not form insoluble materials, e.g., Fe(OH)2, Fe(OH)3, FeO(OH), FeO, FeO2, Fe2O3, etc., or do not substantially form insoluble materials. In certain embodiments, the first temperature is less than 150°C, preferably less than 145°C, even more preferably less than 140°C. In certain embodiments, the first temperature is 130-145°C, 131-144°C, 132-141°C, 133-139°C, or 135-137°C, e.g., about or exactly 136°C, or e.g., approximately 140°C. Any suitable method of bringing the calcium-rich fraction to and / or maintaining it at the desired temperature may be used. The calcium-rich solution may be maintained at or near the desired temperature for a suitable period of time, such as at least 0, 1, 2, 5, 10, 20, 30, 40, or 50 minutes, or 1, 1.5, 2, 2.5, 3, 4, 5, 7, or 10 hours, and / or no more than 1, 2, 5, 10, 20, 30, 40, or 50 minutes, or no more than 1, 1.5, 2, 2.5, 3, 4, 5, 7, 10, or 15 hours. In certain embodiments, the calcium-rich fraction is maintained at or near the desired temperature for between 10 minutes and 5 hours, such as between 30 minutes and 4 hours, and in some cases between 1 and 3 hours. This process produces insoluble, e.g., oxidized aluminum species such as Al, Ca, and oxides, hydroxides, oxyhydroxide silicates, silicate hydrates, or composite phases containing either Si, O, and H (e.g., forming Al(OH)3, Al2O3, AlO(OH), etc.). As described for the one-step pyrolysis process, HCl is also regenerated. The insoluble, e.g., oxidized aluminum can then be separated from the calcium-rich fraction solution and these can be further processed, e.g., dried.The remaining solution is then brought to a second temperature or temperature range at which at least one non-calcium salt, such as an iron salt, forms insoluble materials such as oxides, hydroxides, oxyhydroxides, silicates, silicate hydrates, or complex phases containing Fe, Ca, and any of Si, O, and H, e.g., Fe(OH), Fe(OH), FeO(OH), FeO, FeO, FeO, or FeO. The temperature can be any suitable temperature or temperature range, e.g., at least 140, 145, 150, 155, 160, 165, 170, 175, or 180° C., and / or up to and including 145, 150, 155, 160, 165, 170, 175, 180, 185, 190, or 195° C. In certain embodiments, the remaining solution is heated to 140-195° C., in preferred embodiments, the remaining solution is heated to 145-190° C., in more preferred embodiments, the remaining solution is heated to 145-185° C., in preferred embodiments, to 165-185° C., in more preferred embodiments, to 175-185° C. In certain embodiments, the remaining solution is heated to at least 145° C., such as at least 150° C., in certain cases at least 155° C., such as to approximately 180° C. in a second heating step. Any suitable method of bringing the calcium-rich fraction to the desired temperature and / or maintaining it at the desired temperature may be used. The calcium-rich solution may be maintained at or near the desired temperature for a suitable period of time, such as at least 0, 1, 2, 5, 10, 20, 30, 40, or 50 minutes, or 1, 1.5, 2, 2.5, 3, 4, 5, 7, or 10 hours, and / or no more than 1, 2, 5, 10, 20, 30, 40, or 50 minutes, or no more than 1, 1.5, 2, 2.5, 3, 4, 5, 7, 10, or 15 hours. In certain embodiments, the calcium-rich fraction is maintained at or near the desired temperature for 10 minutes to 5 hours, such as 30 minutes to 4 hours, and in some cases 1 to 3 hours. This temperature serves to regenerate the HCl primary acid while forming insoluble, e.g., oxidized, iron species (e.g., forming Fe(OH)2, Fe(OH)3, FeO(OH), FeO, FeO2, Fe2O3, etc.), as in the first heating step.The insoluble Fe can then be separated from the calcium-rich fraction solution, which can then be further processed, e.g., dried.

[0051] In certain embodiments, the calcium-rich fraction is treated with one or more bases to cause the formation of a set of insoluble non-calcium substances that can be removed from the calcium-rich fraction. HCl can also be regenerated during the base addition. In certain embodiments, this is the only process used to cause the formation of insoluble non-calcium substances (metal compounds that precipitate). In certain embodiments, a one-step pyrolysis process and base addition is used. In certain embodiments, a two-step pyrolysis process and base addition is used. The base or bases can be any suitable base or bases, so long as the strength and amount of the base or bases is sufficient to precipitate the desired amount of metal compounds. In certain embodiments, the base or bases include calcium bases, such as one or more calcium bases that are generated as products during the process, such as CaO, Ca(OH)2, or CaSi, such as dicalcium silicate and / or tricalcium silicate. In certain embodiments, at least 10, 20, 30, 40, 50, 60, 70, 80, 90, or 95%, in preferred embodiments at least 30%, in more preferred embodiments at least 80%, and even more preferred embodiments at least 90%, of the one or more bases comprise one or more products generated during the process, such as calcium bases, such as CaO, Ca(OH)2, or CaSi, such as dicalcium silicate or tricalcium silicate. In certain embodiments, 100% of the one or more bases comprise one or more products generated during the process, such as calcium bases, such as CaO, Ca(OH)2, or CaSi, such as dicalcium silicate or tricalcium silicate. Some or all of the added base may be regenerated during further steps of the process, such as calcium salt decomposition to produce CaO, dicalcium silicate, and / or tricalcium silicate, etc. In certain embodiments, base is added to the calcium-rich fraction in a one-step process to precipitate all desired compounds, such as to precipitate Al, Fe, and Mg compounds. In certain processes, the base is added after some of the non-calcium salts (metal compounds) have been precipitated, for example by a one or two step pyrolysis process.In such cases, sufficient base is added to precipitate the remaining metal compounds or a portion thereof (eg, the remaining Fe and Mg compounds, or the remaining Mg compounds).

[0052] In certain embodiments, a base is added to precipitate the Mg compounds. The precipitate may include one or more magnesium compounds, such as Mg(OH)2, magnesium silicate hydrate, magnesium silicate alumina, and / or other magnesium compounds. The precipitate can be separated from the remaining calcium-rich fraction by any suitable method, such as those described herein. The precipitate can be further processed, for example, by drying. The magnesium precipitate can be used to react with carbon dioxide, for example, carbon dioxide in flue gases (e.g., flue gases from the combustion of natural gas or coal), such as flue gases generated as part of the process to provide energy for the entire process, and / or with other carbon dioxide sources, such as atmospheric carbon dioxide, and / or bodies of water, such as the ocean, to produce magnesium-carbon dioxide products, such as MgCO3, and in some cases Mg(HCO3)2, thus sequestering carbon dioxide. The amount of carbon dioxide sequestered in this way can reduce the total amount of carbon dioxide produced throughout the process, in some cases enough to make the entire process carbon neutral or even carbon negative. Additionally, other substances in the flue gas, such as SOx and / or NOx, that need to be removed from the flue gas, may react with the Mg precipitate, potentially lowering the levels of one or more of the substances below the levels required for the flue gas to be released into the atmosphere. Additionally or alternatively, the magnesium precipitate may sequester carbon dioxide from the atmosphere, and any suitable configuration may be used for this purpose. In certain embodiments, the magnesium precipitate, optionally processed to increase the surface area, may simply be placed in piles, spread on the ground in layers, or distributed in other suitable manner to sequester atmospheric carbon dioxide for a suitable period of time, which may be days, weeks, months, a year, or more. In certain embodiments, the magnesium precipitate may be placed in an aqueous slurry / solution, which may be contacted, for example, with the flue gas or the atmosphere.Additionally or alternatively, magnesium precipitates, of any suitable configuration, can sequester carbon dioxide from bodies of water such as seawater, producing soluble bicarbonate species that can effectively double the amount of carbon dioxide sequestered.

[0053] Decomposition of calcium compounds Block S160, which includes decomposing calcium compounds, functions to decompose calcium compounds, e.g., calcium chloride, into different calcium compounds, e.g., dechlorinated solids including calcium silicate, dicalcium silicate, and / or tricalcium silicate, preferably in a usable form. Block S160 may further include decomposing other metal compounds. Examples include magnesium compounds, aluminum compounds, and iron compounds. In some variations, the decomposing includes performing pyrolysis, e.g., pyrolysis of calcium carbonate into calcium oxide and carbon dioxide.

[0054] Additionally or alternatively, other types of decomposition may be performed (e.g., chemical decomposition, electrochemical decomposition). In some variations, block S160 includes electrochemically decomposing calcium compounds and other metal compounds by electrolysis. For example, this may be done using sodium chloride electrolysis using the chloralkali process.

[0055] In many variations, decomposing the calcium compounds S160 functions in conjunction with block S150. For example, in many variations, pyrolysis is part of isolating the calcium compounds and / or other metal compounds. In these variations, block S160 may occur immediately before, simultaneously with, or immediately after block S150.

[0056] For example, in some variations, block S160 may be incorporated to decompose and / or separate metal compounds (non-calcium compounds) from the calcium-rich fraction prior to separating calcium compounds from the calcium-rich fraction S150. In certain embodiments, one or more of the separated metals are used in the process, for example as a flux for clinkering. This may serve to improve and / or simplify the separation of calcium compounds. Furthermore, this may allow for "purer" extraction of the extracted metals for other uses. In one example, pyrolysis or pyrohydrolysis may be performed on the calcium-rich fraction to extract metals (e.g., aluminum and iron). Pyrolysis or pyrohydrolysis may be performed in any desired form (e.g., mechanical vapor recompression may be used to reintroduce heat generated from other parts of the reaction for pyrolysis or water evaporation, depending on the system implemented in some cases). In this example, the calcium-rich fraction may be heated to 160-190°C, e.g., 175-180°C, e.g., approximately 180°C, thereby hydrolyzing Al and Fe (e.g., forming Al(OH)3, Al2O3, AlO(OH), Fe(OH)2, Fe(OH)3, FeO(OH), FeO, FeO2, Fe2O3, etc.). Additionally, pyrolysis may aid in regenerating the lixiviant (e.g., regenerating HCl), as described below for block S170. Hydrolysis of the metals may effectively precipitate them out of solution. These may then be separated as a separate solid fraction from the calcium-rich fraction solution. The separated metals may also be sold as SCM, with or without the addition of silica. In certain embodiments, one or more of the separated metals are used in the process, e.g., as a flux for clinkering.

[0057] In another example embodiment, block S160 may incorporate a two-step pyrolysis prior to block S150. That is, the calcium-rich fraction may be first heated to 125-145°C, e.g., 130-140°C, e.g., 135-140°C, in some cases approximately 136°C, thereby hydrolyzing the aluminum (e.g., forming Al(OH)3, Al2O3, AlO(OH), etc.). The hydrolyzed aluminum solids may then be separated from the calcium-rich fraction. Once the aluminum has been removed from the calcium-rich fraction, a second heating of the calcium to 160-190°C, e.g., 175-185°C, e.g., approximately 180°C, may then be performed, thereby hydrolyzing the iron (e.g., forming Fe(OH)2, Fe(OH)3, FeO(OH), FeO, FeO2, Fe2O3, etc.). The hydrolyzed iron solids may then be separated from the calcium-rich fraction in the same manner. This two-step pyrolysis may allow for even "purer" separation of aluminum and iron for potential reuse. In certain embodiments, one or more of the separated metals are used in the process, for example as flux for clinkering.

[0058] In the same manner as the single-step and two-step pyrolysis, multiple-step decomposition (e.g. pyrolysis) can be incorporated depending on the composition of the calcium-rich fraction and the desired output(s). For example, multiple-step pyrolysis can be incorporated to hydrolyze other metal compounds from the calcium-rich fraction.

[0059] Generally, the calcium-rich fraction after removal of metal compounds will contain a large amount of calcium chloride (CaCl2), for example, at least 70%, at least 80%, at least 90%, in some cases at least 95%, or even at least 99% calcium chloride. The calcium-rich fraction is also typically highly concentrated, for example, from 40% CaCl2 / 60% water to 70% CaCl2 / 30% water, or from 50% / 50% to 60% / 40%, or even from 55% / 45% to 60% / 40%.

[0060] The resulting calcium compounds, including, for example, calcium chloride, remaining in the calcium-rich fraction, whether produced by an acid dissolution step, one-step pyrolysis, two-step pyrolysis, base addition, or any suitable combination thereof, can then be subjected to processing to produce one or more further products, for example, a clinker, such as a clinker for Portland cement. This may include removing water (dehydrating) from the remaining calcium-rich fraction containing calcium compounds, resulting in a calcium-rich solid comprising one or more calcium compounds, for example, one or more calcium salts, for example, CaCl2, which can be treated to convert it to, for example, dechlorinated calcium compounds, which may or may not contain lime (CaO), and / or converting it after further processing to a clinker, such as, for example, a clinker for Portland cement comprising dicalcium silicate and tricalcium silicate.

[0061] dehydration Water can be removed from the calcium-rich fraction by any suitable method, for example by heating to evaporate the water as steam. Some or all of the resulting steam can be used in further processes requiring steam, as described below. The resulting calcium compound solids include one or more calcium salts, for example CaCl2 (solids containing calcium chloride), and may further include non-calcium salts, for example iron, aluminum, and / or magnesium salts, and / or other salts, so long as they are not present in an amount that renders the final product unsuitable for its intended use, for example as a cement such as clinker or Portland cement, and / or that interferes with the process for producing a cement such as clinker or Portland cement.

[0062] The calcium compound solids, e.g., solids containing calcium chloride, can be treated, e.g., by flaking, grinding, or other suitable methods, to produce particles of a desired size for further processing. This can then be treated to decompose the calcium-containing compounds, e.g., to dechlorinate the calcium chloride-containing solids to produce calcium-containing dechlorinated solids that may or may not contain CaO, and regenerate HCl. This can be further heated (sintered) in the presence of a flux, such as a flux providing Si, Fe, and Al, to produce a clinker or cement, such as Portland cement, which can be further processed to produce a cement, such as Portland cement. It will be understood that one or more materials or processes throughout the method can be configured, adjusted, or selected to produce a desired end product. For example, the starting materials, Ca:Si ratio for dechlorination / clinkering, composition and / or amount of flux for clinkering, and / or clinkering conditions can be adjusted to produce a clinker or cement such as Portland cement that contains a desired range of amounts of dicalcium silicate, tricalcium silicate, and possibly other species that are desired to be present (or absent) in the product. Thus, one or more materials or processes can be configured, adjusted, or selected to produce a clinker that contains 40-70% w / w, in preferred embodiments 50-65%, and in more preferred embodiments 52-63% tricalcium silicate (C3S), and / or contains 10-35% w / w, in preferred embodiments 15-25%, and in some embodiments less than 15% dicalcium silicate (C2S). In certain embodiments, the MgO is below a certain threshold, for example less than 1.0%, or less than 0.6%. In certain embodiments, no more than 15, 12, 10, or 8% tricalcium aluminate (C3A) is present, such as no more than 8%. It will be appreciated that instead of or in addition to compositional properties, functional properties, such as compressive strength of the cement or mortar at one or more time points, may be desired and manipulated.

[0063] Dechlorination In certain embodiments, a calcium compound solid, such as a solid containing calcium chloride, is heated in the presence of steam, silica, and optionally a flux. Generally, no flux is required in this step, but for example, aluminum, such as Al(OH), may be used for convenience. 3、 and / or iron, e.g. Fe(OH) x A flux containing, for example, 10, 20, 30, 40, 50, 60, 70, 80, 90, 95, 98, 99%, or 100% of the silica may be added to the mixture. In certain embodiments, some or all of the silica, e.g., at least 10, 20, 30, 40, 50, 60, 70, 80, 90, 95, 98, 99%, or 100% of the silica, is silica that was generated from non-limestone rocks and / or minerals, e.g., in an earlier step of the process, e.g., in the production of SCM (pozzolana) as described herein. In certain embodiments, some or all of the flux, e.g., at least 10, 20, 30, 40, 50, 60, 70, 80, 90, 95, 98, 99%, or 100% of the flux, is iron and aluminum oxides, hydroxides, and potentially other suitable compounds, that were generated from non-limestone rocks and / or minerals, e.g., in an earlier step of the process, e.g., precipitated as insoluble salts from a calcium-rich fraction as described herein. It will be appreciated that the calcium compound solid, e.g. calcium chloride containing solid, may contain one or more substances that may act as a flux, but generally it is preferred to add an exogenous flux. Heating may be carried out in a single step at a temperature high enough to decompose the calcium containing solid, e.g. calcium chloride containing solid, and clinker / sinter the resulting compound together with the flux. In the simplest case, the calcium compound solid, e.g. calcium chloride containing solid, is heated in the presence of steam and silica to a temperature high enough to decompose the calcium compound, produce HCl, and clinker / sinter together with the flux. In a preferred embodiment, heating may be carried out at successively higher heats in two or more steps, with the flux, if used, being present only in all or part of the step (clinkering / sintering).

[0064] As mentioned above, the calcium compound solids may contain calcium chloride, and in certain embodiments, contain at least 20, 30, 40, 50, 60, 70, 80, 90, or 95%, such as at least 90%, and in some cases at least 95% calcium chloride. The decomposition process results in dechlorination of the calcium chloride in the solids, such as at least 90, 95, 97, 98, 99, 99.1, 99.5, 99.9, 99.91, 99.95, or 99.99% of the calcium chloride in the solids. Surprisingly, it has been found that at least 99%, 99.5%, 99.9%, or even 99.95% of the calcium chloride can be dechlorinated, and these levels of dechlorination result in the chloride content of the final product being low enough to meet Portland cement specifications, such as less than 1% or less than 0.1% chloride, without further processing. In a preferred embodiment, at least 99% of the calcium chloride in the solid is dechlorinated, in a more preferred embodiment, at least 99.9% of the calcium chloride in the solid is dechlorinated, and in an even more preferred embodiment, at least 99.95% of the calcium chloride in the solid is dechlorinated.

[0065] In certain embodiments, calcium compound solids, e.g., solids containing calcium chloride, are heated in the presence of steam and silica to one or more temperatures or temperature ranges sufficient to drive chlorine gas from the solids. The chlorine gas combines with protons from the steam to regenerate HCl, which can be recycled as described above. At the same time, calcium chloride is converted to dechlorinated calcium compounds, which may or may not contain calcium oxide. Generally, the dechlorinated compounds include one or more silicates, such as dicalcium silicate. The temperature should not be so high as to produce tricalcium silicate, or only in trace amounts.

[0066] One overall reaction may be as follows: CaCl2+H2O→CaO+2HCl

[0067] More generally, however, the reaction can be expressed as: CaCl2 + SiO2 + H2O → Ca silicates and other species + 2HCl

[0068] While it is possible for the decomposition and clinkering / sintering to occur at one temperature, it is preferred to perform the decomposition and clinkering (e.g., sintering) in a multi-step process at successively higher temperatures, where the material may be held at a given temperature for a specific period of time, e.g., 0.5-5 hours, or 0.75-4 hours, or 1-3 hours, e.g., 1, 2, or 3 hours, and / or the temperature may be increased successively at one or more suitable rates. This improves the efficiency and yield of dechlorination, and as described elsewhere, surprisingly high levels of dechlorination are achieved by this process. In particular, in certain embodiments, silica is present during heating, e.g., in a Ca:Si molar ratio of 2.5 to 3.25. Also, heating can be kept at a controlled rate, e.g., 80, 70, 60, 50, 40, 30, 25, 20, 15, 10, 5, 2, or 1 °C / min or less, e.g., 20 °C / min or less, or 10 °C / min or less, after reaching a threshold temperature, e.g., 700-750 °C, e.g., a threshold of 700, 710, 720, 730, 740, or 750 °C, until a second threshold temperature, e.g., 800-1000 °C, e.g., 800, 810, 820, 830, 840, 850, 860, 870, 880, 890, 900, 910, 920, 930, 940, 950, 960, 970, 980, 990, or 1000 °C, is reached. In some cases, the material can be kept at one or more temperatures or temperature ranges for one or more periods of time before proceeding. The exact rate and threshold may depend on the material and other conditions. Additionally or alternatively, the temperature may be increased gradually from one temperature to the next. Heating may be performed in any suitable system, such as a fluidized bed or a kiln, and in a preferred embodiment, heating is performed in a kiln, such as a rotary kiln.

[0069] Accordingly, provided herein is a method of dechlorinating calcium chloride, comprising heating calcium chloride to a first temperature in the presence of steam, silica, and optionally a flux comprising an iron and / or aluminum compound, such as one or more of the iron and / or aluminum compounds disclosed herein, and then 1) holding the calcium chloride and other components at the first temperature for a first period of time to produce a first set of one or more products comprising at least HCl, and optionally removing HCl; heating the remainder of the first set of one or more products to a second temperature, in the presence of steam, to a second, higher temperature, and holding the one or more products and the steam at the second temperature to produce a second set of one or more products comprising HCl, and optionally removing HCl; and optionally 2) heating the remainder of the first set of products to a second temperature, in the presence of steam, to a second, higher temperature, and holding the one or more products and the steam at the second temperature to produce a second set of one or more products comprising HCl, and optionally removing HCl; and then, in certain embodiments, an additional step of further heating to a fourth temperature and holding at each temperature for a specific period of time to produce a set of products (one of which is HCl) (temperature, aluminum and / or iron compounds (if used; as noted, generally unnecessary at this stage), silica, and period of time can be as described); or 2) gradually heating the calcium chloride and other components from the first temperature to a second, higher temperature, where the heating rate is slow enough to allow a desired level, e.g., maximum, of HCl production and dechlorination, whereby calcium chloride is at least 95% dechlorinated, and in preferred embodiments at least 99.9% dechlorinated, and in more preferred embodiments at least 99.95% dechlorinated.

[0070] In certain embodiments, a method of dechlorinating a solid comprising calcium chloride is provided, the method comprising: (i) combining a solid comprising calcium chloride with a solid comprising silica; and (ii) heating the combined calcium chloride and silica in the presence of steam to a temperature of 750-1250° C. to produce HCl gas and a dechlorinated calcium product. In certain embodiments, the temperature is 900-1250° C. In certain embodiments, the temperature is 1000-1250° C. In certain embodiments, the temperature is 1100-1250° C. In certain embodiments, when the temperature reaches 700-750° C., e.g., 700° C., optionally 720° C., optionally 750° C., heating proceeds at a rate of no more than 60, 50, 40, 30, 10, or 5° C. per minute until a temperature of 800-850° C. is reached. Without being bound by theory, it is believed that the threshold temperature and rate at or below a particular level are based on avoiding or reducing melting of calcium chloride and ensuring that dechlorination and / or reaction with silica can occur. In certain embodiments, the calcium chloride-containing solid and the silica-containing solid are combined to achieve a Ca-Si molar ratio of 1-4, preferably 2.5-3.5, more preferably 2.5-3.25. In certain embodiments, the calcium chloride-containing solid is present at 50-90 wt. % and the silica is present at 10-40 wt. %. In certain embodiments, the calcium chloride-containing solid comprises at least 80, 90, 92, 93, 94, 95, 96, 97, 98, or 99% calcium chloride. In certain embodiments, the silica-containing solid comprises at least 50, 60, 65, 70, 75, 80, 85, 90, or 95%, such as at least 60%, preferably at least 75%, more preferably at least 80% silica. In certain embodiments, the calcium chloride-containing solids comprise at least 90% calcium chloride and the silica-containing solids comprise at least 80% silica. In certain embodiments, the steam is present at 5-100% by volume. In certain embodiments, the chloride content is reduced by at least 80, 90, 95, 96, 97, 98, or 99%.This may be accomplished by using incremental heating, holding the material at one or more temperatures for one or more periods of time, and / or other operations, as described herein. In certain embodiments, the dechlorinated calcium product comprises at least 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, or 80% by weight dicalcium silicate, in some cases at least 30%, such as at least 50%, and less than 30, 20, 15, 12, 10, 9, 8, 7, 6, 5, 4, 3, 2, or 1% by weight CaO, in some cases less than 10%, such as less than 5% CaO. In certain embodiments, the dechlorinated calcium product comprises at least 30% dicalcium silicate and less than 10% CaO. The dechlorinated calcium product may contain less than 5% Cl, in some cases less than 1% Cl.

[0071] In a particular embodiment, a solid composition is provided that includes: 1) a solid comprising at least 50, 60, 70, 80, 90, or 95% calcium chloride, e.g., at least 90%, in a preferred embodiment at least 95% calcium chloride; 2) silica; and, optionally, 3) a flux comprising one or more iron compounds, e.g., one or more of Fe(OH)2, Fe(OH)3, FeO(OH), FeO, FeO2, Fe2O3, and / or one or more aluminum compounds, e.g., one or more of Al(OH)3, Al2O3, AlO(OH). The composition may have constituents in the following proportions (by weight): calcium chloride solids 50-90%, silica 10-40%, iron compounds acting as fluxes 0-4%, aluminum compounds acting as fluxes 0-4%. In a preferred embodiment, the proportions are: calcium chloride solids 60-85%, silica 15-30%, iron compounds acting as fluxes 1-3%, aluminum compounds acting as fluxes 1-3%. In a more preferred embodiment, the proportions are 70-80% calcium chloride solids, 15-25% silica, 1-2% iron compounds acting as fluxes, and 1-2% aluminum compounds acting as fluxes. In certain embodiments, all components are derived from a single source, for example a single source that includes non-limestone rocks and / or minerals.

[0072] The calcium compound solids are preferably heated and held in the presence of steam, and generally silica, and optionally a flux, to a first temperature, such as a first temperature at which HCl can be handled according to methods known in the art. In certain embodiments, the solids are heated to 1250° C. or less, e.g., 800-1250° C., and in certain cases 850-1000° C., in the presence of steam, silica, and optionally aluminum and iron containing compounds, to produce HCl and a product containing dechlorinated calcium compounds (e.g., optionally including CaO). The solids may be heated in any suitable manner and system, e.g., a fluidized bed or kiln. In this and other steps, silica may be present in any suitable ratio relative to the calcium compound, e.g., CaCl2. For example, a 100-105 g sample may contain about 80 gm CaCl2, about 20 gm silica, and optionally about 1-3 gm each of aluminum and iron compounds. It will be appreciated that this is merely an example and that the proportions of the various components may vary according to the specifications of the type of cement, such as clinker or Portland cement, being produced, as will be apparent to those skilled in the art.

[0073] The product containing the dechlorinated calcium compounds (e.g., optionally including CaO) can then be heated to a second temperature, optionally to a third temperature, and optionally even to a fourth temperature, generally also in the presence of steam, silica (at this point some or all of the silica may have formed silicates), and a flux such as an aluminum and / or iron compound acting as a flux, with steam not being present at one or more of the highest temperatures. Thus, the product containing the dechlorinated calcium compounds (e.g., optionally including CaO) is clinkered in a process that may include sintering in the presence of a flux, such as an aluminum and / or iron containing flux, to produce a clinker, such as a Portland cement clinker. "Clinkering", as the term is used herein, includes the process of treating solid materials at high temperatures to produce a cement clinker. "Clinkering" and "sintering" are generally used interchangeably herein. The processes described herein may include varying amounts of sintering, or may not include sintering, so long as the desired product is produced. The flux may include materials produced in earlier steps of the process, such as aluminum and / or iron compounds removed from the calcium-rich fraction, as described above. In certain embodiments, at least 10, 20, 30, 40, 50, 60, 70, 80, 90, or 95%, such as at least 50%, in some cases at least 70%, and in certain embodiments at least 90%, of the exogenous flux containing aluminum and / or iron comprises one or more compounds removed from the calcium-rich fraction. In certain embodiments, 100% of the exogenous flux containing aluminum and / or iron comprises one or more compounds removed from the calcium-rich fraction. In certain embodiments, exogenous fluxes that are not produced in earlier stages of the process, such as clay, are used, as known in the art. Whether and, if any, the amount of exogenous flux is present may be determined, at least in part, by the desired final composition, such as the type of Portland cement produced.In certain embodiments, a flux is used that includes both iron-containing and aluminum-containing compounds.

[0074] When only the second temperature is used, the process includes heating the product containing dechlorinated calcium compounds (e.g., optionally including CaO) in the presence of a flux to 1200-1550°C, preferably below 1450°C, to form a clinker, such as Portland cement clinker, containing dicalcium silicate and tricalcium silicate, and optionally the clinker or intermediate also containing tricalcium aluminate and / or tetracalcium aluminoferrate. When an intermediate temperature is used, the temperature may be, for example, 900-1100°C, e.g., 950-1050°C, the temperature may be, for example, 1100-1300°C, e.g., 1150-1250°C, and the temperature may be, for example, 1400-1600°C, e.g., 1450-1550°C. In an exemplary embodiment, the temperature is held successively at 850, 1000, 1200, and 1500°C for one hour each. These are merely examples and one of ordinary skill in the art can determine the optimum or desired temperatures.

[0075] During the heating process, base that may have been used in the base precipitation step, e.g., one or more calcium bases, can be regenerated, for example, at least 10, 20, 30, 40, 50, 60, 70, 80, 85, 90, 95, 98, or 99% of the amount of base used in the base precipitation step can be regenerated.

[0076] At the end of the process clinker may remain, which may have a diameter in millimeters, for example 0.5-50 mm, or 1-40 mm, or 1-30 mm, although other sizes are also acceptable for further processing.

[0077] Thus, provided herein is a clinker, such as a Portland cement clinker, comprising dicalcium silicate and tricalcium silicate, where the dicalcium silicate and tricalcium silicate are derived from non-limestone materials, such as non-limestone rocks and minerals, for example, in the processes described herein. In certain embodiments, the calcium and silicate are derived from the same starting material, for example, non-limestone materials, such as the same non-limestone rocks and / or minerals. As used herein, "dicalcium silicate" (also referred to herein as belite, C2S) and "tricalcium silicate" (also referred to herein as alite, C3S) include the meanings known in the art of cement and concrete production, for example, tricalcium silicate may include small amounts of other constituents, for example, 3-4% of substituted oxides, and dicalcium silicate may include small amounts of other oxides in addition to CaO and SiO2.

[0078] Also provided herein is a concrete comprising a cement, such as a Portland cement, such as OPC, produced by one or more of the processes described herein, i.e., a process that does not require calcination of limestone. In certain embodiments, the concrete can also comprise a cement, such as a Portland cement, such as OPC, produced by a conventional process, i.e., a process that requires calcination of limestone.

[0079] Also provided is a method for producing clinker from calcium compound solids containing calcium chloride (CaCl2), comprising: (a) dechlorinating calcium compound solids containing CaCl2 to produce a dechlorinating composition containing Ca and having a Cl content of less than 10% w / w; and (b) heating the dechlorinating composition in the presence of a flux to produce a clinker. Clinkers, for example Portland cement clinkers such as OPC clinkers, can contain dicalcium silicate and tricalcium silicate. The composition containing CaCl2 can also contain silica, for example, the molar ratio of Ca:Si can be 1.0 to 5.0, preferably 2.0 to 4.0, more preferably 2.5 to 3.25.

[0080] Leaching agent regeneration Block S170, which includes regenerating the leaching agent, functions to replenish the leaching agent used in the decomposition of the non-limestone materials. In some variations, regenerating the leaching agent S170 may simply include adding new leaching agent to replace previously consumed leaching agent. Additionally or alternatively, a process (e.g., thermal, chemical, or electrical stimulation) may be performed in regenerating the leaching agent S170.

[0081] In embodiments where the leaching agent comprises a strong acid such as HCl, at least 10, 20, 30, 40, 50, 60, 70, 80, 85, 90, 95, 98, or 99% of the initial acid such as the initial HCl may be regenerated at the end of all acid regeneration steps such as HCl regeneration. In a preferred embodiment, at least 80% of the initial HCl is regenerated. In another preferred embodiment, at least 90% of the initial HCl is regenerated. An amount of strong acid such as HCl that is not regenerated can be added back, i.e., replenished, to provide sufficient acid, e.g., sufficient HCl, for subsequent processing of the non-limestone material.

[0082] In many variations, regenerating the leaching agent S170 may occur in conjunction with block S160 as part of the decomposition process. For example, in one example, a separate pyrolysis may occur. For example, in one embodiment, calcium sulfite is pyrolyzed to produce calcium oxide and calcium silicate while simultaneously regenerating sulfur dioxide.

[0083] Additionally or alternatively, regenerating the lixiviant may be a separate process, for example, calcium sulfate may be pyrolyzed to produce calcium oxide or calcium silicate and sulfur dioxide, which then needs to be converted to sulfuric acid to regenerate the lixiviant.

[0084] Clinker or cement production In some variations, the method may include a cement production step. That is, in variations where decomposition includes calcium compound products (e.g., calcium oxide, dicalcium silicate, and / or tricalcium silicate), the method may include a block S180 that includes producing cement from the calcium compound products. As previously discussed, the type of cement produced may be embodiment specific (e.g., ordinary Portland cement). In many variations, producing cement may include clinkering / sintering the calcium compound products, which serves to produce the cement. In other variations, producing cement from the calcium compound products S180 may include directly producing calcium silicate via pyrolysis or electrochemical intercalation of silica into the calcium-containing compound products. Alternatively, other processes may be performed to produce the cement, which may depend on the type of calcium compound products and the desired cement output.

[0085] In one embodiment, a method is provided that includes contacting a non-limestone material with a leaching agent to create a pulp, and deriving a calcium-rich liquid fraction and a calcium-depleted solid fraction from the pulp. See, for example, FIG. 3. In a preferred embodiment, the non-limestone material includes calcium and the acid is hydrochloric acid to produce a calcium-rich liquid fraction that includes calcium chloride. In certain embodiments, the non-limestone material includes rocks and / or minerals, such as one or more of the rocks and minerals described herein. In certain embodiments, the method includes treating the calcium-rich liquid fraction that includes calcium chloride to produce solids that include calcium chloride, and dechlorinating the calcium chloride-containing solids to produce dechlorinated solids that include calcium compounds. In certain embodiments, the dechlorinated solids that include calcium compounds are treated to produce clinker, which may be further processed to produce a cement, such as ordinary Portland cement. As described elsewhere herein, various parameters and / or conditions of the material can be set, adjusted, and / or selected to produce a clinker that is processed into a cement having desired properties, such as compositional properties such as dicalcium silicate and / or tricalcium silicate and / or other components within a desired concentration range. The calcium-depleted solid fraction can be separated from the calcium-rich liquid fraction. In certain embodiments, the non-limestone starting material contains both calcium and silicon, and the calcium-depleted solid fraction contains silica, such as amorphous silica, and the calcium-depleted solid fraction can be further processed for use as a supplemental cementitious material (SCM), such as by operations such as rinsing, drying, and storing for further use. See, for example, FIG. 4. The solids can also be subjected to processes such as producing particles of a desired size or one or more size ranges. In certain embodiments, the calcium-rich liquid fraction containing calcium chloride contains non-calcium salts, such as aluminum, iron, and / or magnesium salts, and processing the calcium-rich fraction includes treating the liquid to precipitate one or more insoluble aluminum, iron, or magnesium compounds. For example, see FIG.The precipitation process generally comprises at least contacting the calcium-rich liquid fraction with a base, such as a calcium base, such as a calcium base containing calcium silicates, such as dicalcium silicate and / or tricalcium silicate, and in certain embodiments, at least a portion of the calcium base is provided from a subsequent operation, such as dechlorination and / or clinkering. In certain embodiments, the only precipitation step is a base precipitation step. Alternatively, the precipitation can also comprise one or more pyrohydrolysis steps, usually preceding the base precipitation, to precipitate aluminum and / or iron compounds. A one-step pyrohydrolysis step may be used, which can precipitate both aluminum and iron compounds, or a two-step pyrohydrolysis process may be used, where the aluminum compounds are precipitated in a first step and the iron compounds are precipitated in a second step. When pyrohydrolysis is used, the base precipitation generally produces mainly magnesium species. One-step and two-step pyrohydrolysis can be carried out as described elsewhere. Depending on whether pyrohydrolysis is used and the magnesium content in the starting material, e.g., the Ca / Mg ratio, more or less base can be used, so that if material from the final process is used as the base source, the amount can be, for example, 1 / 20 of the clinker (if the starting material is Ca:Mg 20:1) or even 1 / 2 of the clinker (e.g., if the starting material is 1:1), provided that material consumed early in the process is replaced later in the process. Part of the HCl can be regenerated during the precipitation step. After one or more precipitation steps, insoluble solids can be separated from the calcium-rich liquid containing calcium chloride, and the calcium-rich liquid fraction is dehydrated to produce solids containing calcium chloride. The calcium chloride containing solid can then be dechlorinated, such as by combining with silica in a ratio that results in a Ca:Si molar ratio of 1 to 4, such as 2 to 4, in a preferred embodiment 2.45 to 3.25, and in a more preferred embodiment 2.5 to 3.25, and heating in the presence of steam, such as 5 to 100% by volume of steam (see, e.g., FIG. 6).Some or all of the silica, for example at least 10, 20, 30, 40, 50, 60, 70, 80, 90, 95, or 99%, or 100%, can be provided from the calcium-depleted solid fraction. Some or all of the steam, for example at least 10, 20, 30, 40, 50, 60, 70, 80, 90, 95, or 99%, or 100%, can be provided from the dehydration step. The dechlorination can proceed under conditions described herein to produce dechlorinated solids that include calcium compounds, and the dechlorinated solids can contain less than 10, 8, 7, 6, 5, 4, 3, 2, 1, or 0.1%, preferably less than 5%, and in some cases more preferably less than 1% w / w Cl. The dechlorination also produces HCl, which can be returned to the step of contacting the non-limestone material with acid. The dechlorinated solids may include one or more calcium silicates, such as dicalcium silicate and others, where the dicalcium silicate may be present, for example, at least 1, 5, 10, 20, 30, or 40%, such as at least 5% w / w. There may be little or no CaO present in the dechlorinated solids, such as less than 10, 5, 3, 2, or 1% w / w. The dechlorinated solids containing calcium may be processed to produce clinker (see, for example, FIG. 7), for example, by heating in the presence of a flux, such as a flux containing aluminum and iron compounds, such as oxides (including hydroxides as used herein) of aluminum and iron. The conditions for producing the clinker may be as described herein. In certain embodiments, some or all of the flux, for example at least 10, 20, 30, 40, 50, 60, 70, 80, 90, 95, or 99%, or 100%, is provided from one or more precipitates. In certain embodiments, some or all of the flux, for example at least 10, 20, 30, 40, 50, 60, 70, 80, 90, 95, or 99%, or 100%, is provided by one or more exogenous materials, such as clay, etc. The clinker thus produced contains at least hydraulic calcium silicates, such as dicalcium silicate and tricalcium silicate.The conditions of the various steps (e.g. Ca:Si ratio for dechlorination and production of clinker, composition of flux for production of clinker, etc.) can be adjusted to produce a clinker containing dicalcium silicate and tricalcium silicate in the desired proportions, such as 40-70% tricalcium silicate (C3S), preferably 50-65%, e.g. 52-63%, and 10-35% dicalcium silicate (C2S), e.g. 15-25%. The clinker can also contain e.g. 5-12% tricalcium aluminate, and / or e.g. 6-12% tetracalcium aluminate ferroaluminate (C4AF). The process can further include processing the clinker to produce a cement, such as a Portland cement, such as OPC. The cement thus produced can be used in the production of concrete, for example by mixing with aggregate and water, and possibly with SCM. The aggregate and / or SCM can also be produced from non-limestone materials. Setting and hardening is generally similar or identical to that seen with conventionally produced cements of the same composition, such as those produced by calcining limestone and then sintering the product. Processing can include sizing and screening, such as by crushing, grinding, or milling, and can also include the addition of one or more additional materials, such as gypsum.

[0086] An exemplary process utilizing a single precipitation step (calcium base precipitation where some or all of the calcium base is generated during the process) is shown in Figure 11. An exemplary process utilizing one or more pyrohydrolysis precipitations followed by base precipitation is shown in Figure 12.

[0087] In certain embodiments, the insoluble magnesium species, e.g., magnesium silicate, magnesium hydroxide, etc., produced during the precipitation step of the above process or other processes described herein, can be used to sequester carbon dioxide (and potentially other components, e.g., SOx, NOx, and / or other components), such as atmospheric carbon dioxide and / or carbon dioxide that is a component of flue gas produced in one or more combustion steps to generate energy for the process. Carbon dioxide reacts with the magnesium species to produce magnesium carbonate. In certain embodiments, the magnesium species can be placed in a body of water, such as the ocean, where they form magnesium bicarbonate, thus sequestering twice as much carbon dioxide as magnesium carbonate produced. These may also produce a buffering effect.

[0088] It will be appreciated that the processes provided herein may produce less carbon dioxide than traditional methods of producing cement, which typically require calcination and sintering of limestone. Calcination produces carbon dioxide from limestone, and both calcination and sintering produce carbon dioxide from the combustion of fuel to heat the material. The processes as provided herein do not utilize starting materials that contain large amounts of calcium carbonate, and in fact, calcium carbonate is not required, although some may be present in non-limestone materials. Depending on the starting material (e.g., materials with high magnesium content can produce more magnesium species for sequestering carbon dioxide), and depending on other factors, such as the fuel used to provide energy for the various steps (e.g., heating), and transportation, among others, the carbon dioxide produced may be less than 80, 70, 60, 50, 40, or 30% of the amount produced in traditional processes to produce the same amount of comparable cement from limestone. In certain embodiments, the processes as provided herein may produce less than 500 kg of carbon dioxide per 1000 kg of cement produced, for example when coal is used as fuel. In certain embodiments, the process as provided herein may produce less than 300 kg of carbon dioxide per 1000 kg of cement produced, for example when natural gas is used as fuel. When one or more magnesium species produced during the process are used to sequester carbon dioxide, for example from flue gas or atmospheric carbon dioxide, and / or when placed in a body of water, such as the ocean, the carbon dioxide produced may be less than 250, 200, 150, 100, or 50 kg of carbon dioxide per 1000 kg of cement produced. In certain embodiments, the process is carbon neutral or even carbon negative, for example, at least 50, 75, 100, 125, 150, 200, 250, 300, 400, or 500 kg of carbon dioxide is sequestered per 1000 kg of cement produced. In general, when magnesium species are placed in a body of water, such as the ocean, a smaller carbon positive value or a larger carbon negative value is produced, since bicarbonate may be produced, which may sequester 2 CO2 per Mg.It will be appreciated that the reduction in the amount of carbon dioxide compared to conventional processes, or even negative carbon dioxide, can be converted into carbon credits. Such credits can be based on avoided carbon dioxide (e.g., compared to conventional processes to produce the same amount of equivalent cement), and in some cases, sequestered carbon dioxide (e.g., by magnesium species produced during the process). Appropriate monitoring / calculation of produced carbon dioxide versus avoided and / or sequestered carbon dioxide can be performed, along with measures to ensure compliance with existing standards and regulations.

[0089] Exemplary embodiments of the above-mentioned method are provided herein. These examples are intended to illustrate various possible implementations of the method without imposing additional limitations on the method. Although not explicitly included in all examples, any of the examples may include additional concentration steps (e.g., block S120) if desired or necessary, depending on the non-limestone material obtained.

[0090] In a first example, obtaining the non-limestone material S110 includes obtaining a silicate rock material. Dissolving the non-limestone material S130 includes adding hydrogen iodide (HI) primary acid as a leaching agent. Thus, the silicate rock material dissolves in the HI. Separating the calcium-depleted fraction from the calcium-rich fraction S140 includes separating the solid fraction, primarily SiO2, from the liquid fraction, and then drying the SiO2 and packaging it as SCM. The SCM can then be stored and packaged, sold, or utilized in any desired manner. Separating the calcium-containing compounds from the calcium-rich fraction S140 includes precipitating the metal-containing compounds. This includes slowly adding CaSiO3, followed by Ca(OH), Ca2SiO4, Ca3SiO5, electrochemically generated hydroxide or NaOH, or similarly strong enough base, thereby neutralizing the HI primary acid; Al(OH)3, Fe(OH) xand Mg(OH)2; forming CaI2; and lowering the temperature to precipitate CaI2 and H2O. Decomposing the calcium compounds S160 and regenerating the leaching agent S170 are simultaneously performed by pyrolyzing the calcium-containing compounds. Thus, pyrolyzing CaI2 can form CaO, CaSiO3, Ca2SiO4, or Ca3SiO5 and regenerate HI first acid. In one embodiment of cement production, a first example is decomposing CaO into SiO2, Al(OH)3, and Fe(OH) in a kiln. x The method may further include sintering the calcium oxide, including sintering the flue gas with Mg(OH)2 to form ordinary Portland cement. Further, this example may include scrubbing the flue gas with Mg(OH)2 to produce MgCO3. Additionally or alternatively, the Mg(OH)2 can be placed in a waste pile where it can be exposed to air and slowly converted to MgCO3.

[0091] In a second example, obtaining the non-limestone material S110 includes obtaining a silicate rock material. Dissolving the non-limestone material S130 includes adding hydrochloric acid (HCl) first acid. Thus, the silicate rock material dissolves in the hydrochloric acid (HCl). Separating the calcium-depleted fraction S140 from the calcium-rich fraction includes separating the solid fraction, primarily SiO2, from the liquid fraction, and then drying the SiO2 and packaging it as SCM, which can be used as desired (e.g., for cement production, for storage, for sale). Separating calcium-containing compounds from the calcium-rich fraction S140 includes precipitating metal-containing compounds. This includes slowly adding CaSiO3; adding Ca(OH)Ca2SiO4, Ca3SiO5, or a similarly strong base, thereby neutralizing the HCl first acid; and separating Al(OH)3, Fe(OH) x, and Mg(OH)2 to form CaCl2. Then, SO2, a lixiviant, is added to precipitate CaSO3 and regenerate HCl. Decomposing calcium compounds S160 and regenerating the lixiviant S170 are simultaneously performed by pyrolyzing calcium-containing compounds. Thus, pyrolysis of CaSO3 can form CaO, CaSiO3, Ca2SiO4 or Ca3SiO5 and regenerate SO2. In one embodiment of cement production, a second example is decomposing CaO to SiO2, Al(OH)2 in a kiln. 3 and Fe(OH) x The method may further include sintering the calcium oxide, including sintering the flue gas with Mg(OH)2 to form ordinary Portland cement. This example may further include scrubbing the flue gas with Mg(OH)2 to produce MgCO3. Additionally, or alternatively, the Mg(OH)2 may be placed in a waste pile where it may be exposed to air and slowly converted to MgCO3. Example 2 may be particularly applicable in embodiments having a high concentration of Ca(OH)2.

[0092] In a third example, obtaining non-limestone material S110 includes obtaining a silicate rock material. Dissolving the non-limestone material S130 includes adding hydrochloric (HCl) primary acid. Thus, the silicate rock material dissolves in the hydrochloric (HCl) primary acid. Separating the calcium-depleted fraction from the calcium-rich fraction S140 includes separating the solid fraction, primarily SiO2, from the liquid fraction and then drying and packaging the SiO2 as SCM. Separating calcium-containing compounds from the calcium-rich fraction S150 includes precipitating metal-containing compounds. This includes slowly adding H2SO4 to form CaSO4 and HCl; and adding additional HCl to precipitate metal chlorides (e.g., AlCl3, FeCl4, FeCl5, FeCl6, FeCl7, FeCl8, FeCl9, FeCl10, FeCl20, FeCl30, FeCl40, FeCl50, FeCl60, FeCl70, FeCl80, FeCl90, FeCl20, FeCl20, FeCl20, FeCl30, FeCl40, FeCl40, FeCl5 ... xDecomposing the calcium compounds S160 may be performed by pyrolyzing the calcium compounds, i.e., CaO, CaSO4 are pyrolyzed and SO2 is regenerated. Regenerating the leaching agent S170 is performed by pyrolyzing the metal-containing compounds in the presence of water, i.e., AlCl3, FeCl x , MgCl2, and HCl primary acid are regenerated. In a cement production variant, the third example may further include pyrolyzing CaSO4 with Al2O3, Fe2O3, and SiO2 to produce ordinary Portland cement and SO2. This example may further include scrubbing the flue gas with Mg(OH)2 to produce MgCO3. Additionally or alternatively, the Mg(OH)2 may be placed in a waste pile where it may be exposed to air and slowly converted to MgCO3.

[0093] In a fourth example, obtaining the non-limestone material S110 includes obtaining a silicate rock material. Dissolving the non-limestone material S130 includes adding hydrochloric (HCl) first acid. Thus, the silicate rock material dissolves in the hydrochloric (HCl) first acid. Separating the calcium-depleted fraction from the calcium-rich fraction S140 includes separating the solid fraction, primarily SiO2, from the liquid fraction and then drying and packaging the SiO2 as SCM. Separating the calcium-containing compounds from the calcium-rich fraction S140 includes precipitating the metal-containing compounds. This is done by neutralizing the first acid by slowly adding NaOH to separate Al(OH)3, Fe(OH), xand Mg(OH)2 to form NaCl; electrolyzing NaCl to regenerate NaOH to form H2 and Cl2; and using a synthesis unit to generate HCl from H2 and Cl2. This synthesis unit includes a typical synthesis unit for a chlor-alkali process. For example, the synthesis unit may include burning chlorine with H2 for an HCl synthesis unit. In a variant of cement production, a fourth example is the synthesis of CaOH2 to SiO2, Al(OH)3, and Fe(OH)2 in a kiln. x The method may further include sintering the calcium product, including sintering the flue gas with Mg(OH)2 to form ordinary Portland cement. Further examples of this may include scrubbing the flue gas with Mg(OH)2 to produce MgCO3. Additionally or alternatively, the Mg(OH)2 in the waste pile can now be slowly converted to MgCO3 upon contact with air.

[0094] In a fifth example, organic or biological acids are utilized as leaching agents. In this example, obtaining the non-limestone material S110 includes obtaining a silicate rock material. Dissolving the non-limestone material S130 includes adding a leaching agent that is an organic acid first acid (e.g., oxalic acid). Any organic acid (e.g., oxalic acid) can selectively leach other metals (e.g., Al, Fe, and Mg) leaving most of the calcium compounds or (unlike oxalic acid) selectively leach calcium leaving other metals. Separation of the leached metal-organic acid complexes (e.g., metal oxalates) can be separated from the spent non-limestone feedstock using flotation. The organic acid-metal complexes can then be oxidized (e.g., burned) to produce carbon dioxide and metal oxides. Alternatively, if calcium is leached, the calcium oxide can be oxidized and sintered to make cement. Regenerating the organic acid leachant can include using engineered microorganisms, carbon dioxide, and sunlight. In embodiments where the calcium is left in the spent rock, the method steps can be repeated to better leach and precipitate the calcium.

[0095] In a sixth example, obtaining the non-limestone material S110 includes obtaining a silicate rock material. Dissolving the non-limestone material S130 includes using an electrolytic cell to decompose water or salt to generate an acid at the anode and a base at the cathode, and reacting the acid with the non-limestone material. Thus, the silicate rock material dissolves in the electrolytically generated first acid, which may be hydronium ions, HCl, HBr, and any sufficiently strong acid. Separating the calcium-depleted fraction from the calcium-rich fraction S140 includes separating the solid fraction, primarily SiO2, from the liquid fraction, and then drying and packaging the SiO2 as SCM. Separating the calcium-containing compounds from the calcium-rich fraction S140 includes precipitating the metal-containing compounds. This is done by slowly adding a base, which can be hydroxide ions, NaOH, Ca(OH)2, or any other sufficiently strong base, generated at the cathode by the decomposition of water or salt, thereby neutralizing the first acid and forming Al(OH)3, Fe(OH) x , Mg(OH)2, and finally Ca(OH)2. In a variant of cement production, the sixth example is the kiln-assisted precipitation of CaOH2 with SiO2, Al(OH)3, and Fe(OH) x The method may further include sintering the calcium product, including sintering the flue gas with Mg(OH)2 and / or other magnesium compounds to form ordinary Portland cement. Further examples of this may include scrubbing the flue gas with Mg(OH)2 and / or other magnesium compounds to produce MgCO3. Additionally or alternatively, the Mg(OH)2 and / or other magnesium compounds may be placed in a waste pile where it is exposed to air and slowly converted to MgCO3.

[0096] In a seventh example, obtaining non-limestone material S110 includes, for example, obtaining non-limestone rock and / or minerals, e.g., silicate rock material. Any suitable starting material may be used, so long as it contains calcium in a sufficient amount to result in the desired end product, e.g., final clinker or cement, such as Portland cement. If a process is used that also produces a supplemental cementitious material (SCM), the starting material will also contain one or more compounds that may result in a final material that contains amorphous (non-crystalline) compounds that may function as SCMs. These may include amorphous silica, in which case the starting material will also include silicon. However, as is known in the art, other materials may result in amorphous compounds that function as SCMs, such as amorphous iron and alumina compounds, in which case the starting material will include the necessary starting elements. In certain embodiments in which both cement, such as clinker or Portland cement, and SCM are produced, the starting material includes non-limestone materials, such as non-limestone rocks and / or minerals that contain calcium and silicon, e.g., calcium silicate-containing rocks and / or minerals. When rocks and / or minerals are used, any suitable rocks and / or minerals may be used, such as one or more of basalt, gabbro, pyroxenite, anorthosite, skarn, amphibolite, or combinations thereof. Other suitable rocks and / or minerals are described herein or will be apparent to one of skill in the art.

[0097] Generally, non-limestone materials, e.g., rocks and / or minerals, are processed to provide a calcium-rich fraction comprising one or more calcium salts and a calcium-depleted fraction, generally solid. The calcium-depleted fraction, e.g., solids, may be removed. In certain embodiments, the solids may comprise amorphous compounds, such as amorphous silica, and may be used as SCM. The calcium-rich fraction may be a solution comprising calcium salts, and may also comprise non-calcium salts, such as Fe, Al, Mg (e.g., their chlorides), and / or other salts. In certain cases, the nature and concentration of the non-calcium salts are such that the calcium-rich fraction does not need to be further processed, since the contents may be converted into an acceptable end product, e.g., a cement, such as clinker or Portland cement. This may be the case, for example, when the starting material comprises or consists of wollastonite. In other cases, the nature and concentration of the non-calcium salts necessitates the removal of one or more of them from the solution. In this case, the calcium-rich fraction is treated to reduce the concentration of non-calcium salts to a level acceptable for the production of an end product, such as a cement, such as a final clinker or Portland cement product. The solution can then be treated to produce further products, such as by treating one or more calcium salts to solid form, and treating one or more calcium salts to decompose to provide at least dicalcium silicate and tricalcium silicate in a suitable ratio for a cement, such as a clinker or Portland cement. One or more of the above treatments can serve to regenerate one or more of the starting materials. For example, if the starting material includes an acid, such as a strong acid, at least a portion of the acid can be regenerated. The material can be further processed, such as to a suitable size or size range, for use, for example, as Portland cement. The process can be any suitable type of process, such as a batch process, a continuous process (including, for example, one or more countercurrent processes), a semi-continuous process, etc., as known in the art.

[0098] Non-limestone materials, e.g., rocks and / or minerals, may be processed to provide particles within a desired size range. Any suitable process or processes may be used, such as crushing, grinding, and / or milling, sieving, and the like. Suitable size ranges include 1-500u, 5-300u, 10-200u, 20-130u, 45-90u, or combinations thereof. In a preferred embodiment, the size range is 20-130u. In a more preferred embodiment, the size range is 45-90u.

[0099] The non-limestone material, e.g., rock and / or mineral material, is contacted with a strong acid to form a pulp that includes the acid and the non-limestone material, e.g., rock and / or minerals. Any suitable strong acid may be used, such as HCl, HBr, HI, H2SO4, or HNO3. In certain embodiments, the strong acid includes HCl. For convenience, the remainder of the process will be described in terms of HCl. As will be apparent to one of skill in the art, if another acid is used in addition to or as a replacement for HCl, suitable adjustments can be made to accommodate the additional / alternative acid.

[0100] Dissolving the non-limestone material S130 includes adding hydrochloric acid (HCl). Thus, the non-limestone material, e.g., rocks and / or minerals, such as silicate rock material, dissolves in hydrochloric acid (HCl). In certain embodiments, the percentage of the strong acid that comprises HCl is at least 20, 30, 40, 50, 60, 70, 80, 90, 95, or 99% of the strong acid. In a preferred embodiment, at least 90% of the strong acid is HCl. In a more preferred embodiment, at least 95% of the strong acid is HCl. In an even more preferred embodiment, at least 98% of the strong acid is HCl. In an even more preferred embodiment, 99-100% of the strong acid is HCl, e.g., 100% of the strong acid is HCl. Any suitable concentration of strong acid, e.g., HCl, may be used, such as 5-40%, 10-37%, 10-30%, 15-35%, 17-23%, 20-30% wt / wt, or about or exactly 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, or 30%, e.g., about or exactly 20%. In a preferred embodiment, the HCl is 10-37%. In an even more preferred embodiment, the HCl is 15-35%. The ratio of solid non-limestone material, e.g., rocks and / or minerals, to liquid (acid) in the initial pulp may be any suitable ratio. It will be appreciated that some of the solid rocks and / or minerals will immediately begin to dissolve in the acid, and that these ratios will change as the solids dissolve into solution. Suitable initial ratios may be within the range of 5% solids / 95% liquid to 40% solids / 60% liquid, for example 10% solids / 90% liquid to 30% solids / 70% liquid; in a preferred embodiment 15% solids / 85% liquid to 25% solids / 75% liquid, for example 20% solids / 80% liquid.

[0101] The pulp is treated to dissolve at least a sufficient amount of calcium compounds in the non-limestone materials, e.g., rocks and / or minerals, into solution to provide a good end product, e.g., to be converted into cement, such as clinker or Portland cement. In certain embodiments, at least 50, 60, 70, 80, 90, or 95%, preferably at least 70%, more preferably at least 80%, and even more preferably at least 90%, of the calcium in the starting material goes into solution. This treatment may be done in an open to air or at least unpressurized process. This treatment may include heating and / or maintaining the pulp at a temperature or temperature range for a certain period of time. Generally, a treatment period and / or temperature that results in the desired dissolution may be used. Suitable temperature ranges for maintaining the pulp include 60-115°C, 70-115°C, 80-115°C, 90-115°C, 100-115°C, 60-112°C, 70-112°C, 80-112°C, 90-112°C, 100-112°C, 60-110°C, 80-110°C, 90-110°C, or 100-110°C. It will be appreciated that due to the high concentration of HCl present and as material dissolves into the liquid phase, the boiling temperature of the HCl solution may exceed 100°C. Thus, in certain embodiments, the temperature is at least 95, 96, 97, 98, 99, or 100°C, in preferred embodiments, the temperature is at least 90°C, in a range of more preferred embodiments, the temperature is at least 95°C, in even more preferred embodiments, the temperature is at least 98°C, and in even more preferred embodiments, the temperature is at least 100°C. In certain embodiments, the maximum temperature is 105, 106, 107, 108, 109, 110, 111, 112, 113, 114, or 115° C., in preferred embodiments, the maximum temperature is 105° C., in more preferred embodiments, the maximum temperature is 108° C., and in even more preferred embodiments, the maximum temperature is 110° C. In certain embodiments, the temperature is brought to and / or maintained at 100-115%. In certain embodiments, the temperature is brought to and / or maintained at 100-110° C. Any suitable treatment period may be used.This may depend, to some extent, on the calcium content of the starting material, such as non-limestone rocks and / or minerals. Materials with lower calcium content may require longer treatment to achieve the desired amount of calcium salts in solution. Thus, the treatment period may be at least 1, 2, 3, 4, 5, 6, 7, 8, or 10 hours, and / or not more than 2, 3, 4, 5, 6, 7, 8, 10, 12, 15, 20, 24, 30, 36, 40, 48, 60, or 72 hours. In certain embodiments, the period may be 2 to 24 hours, such as 4 to 18 hours, or even not more than 4 to 12 hours. In certain embodiments, the period may be 6 to 72 hours, such as 4 to 48 hours, or 4 to 36 hours, or 4 to 24 hours. The pulp may be agitated during processing, for example, at 10-1000 RPM, 20-800 RPM, 50-500 RPM, 50-400 RPM, or 100-300 RPM. In a preferred embodiment, the pulp is agitated at 50-400 RPM, more preferably 100-300 RPM. Other agitation methods known in the art may be used.

[0102] A calcium-depleted fraction (solid) and a calcium-rich fraction (liquid) are produced from the pulp. See, for example, FIG.

[0103] Separating the calcium-depleted fraction from the calcium-rich fraction S140 involves separating the solid fraction, which may be primarily SiO2, e.g., amorphous silica, and / or other amorphous materials suitable for use as an SCM, such as a pozzolan, from the liquid fraction, optionally followed by rinsing the solid fraction, such as SiO2, and then drying and, in certain cases, packaging as an SCM. Further details of processes directed to the production of SCMs, such as pozzolans, are provided below. If the solid fraction contains silica, a portion of the solid fraction may be subjected to a dechlorination and / or clinkering process, as described below.

[0104] The calcium-rich fraction is further processed. In certain embodiments, the end result of the further processing is to produce a clinker or cement, such as a hydraulic cement, such as Portland cement, e.g., Ordinary Portland Cement (OPC), and generally to regenerate the acid. Furthermore, depending on the processing of the calcium-rich fraction, certain non-calcium materials may be generated, such as materials containing one or more of iron, aluminum, and / or magnesium. The further processing may depend on the potential composition of the calcium-rich fraction, which may depend at least in part on the starting material.

[0105] Generally, the calcium-rich fraction contains, in addition to calcium salts, non-calcium salts, also referred to herein as metal compounds, and the following procedure may depend on the ratio, or expected ratio, of non-calcium salts (metal compounds) to calcium salts, which may be based, at least in part, on the starting material. If the ratio of one or more non-calcium salts exceeds or is expected to exceed a certain threshold in the calcium-rich fraction, the calcium-rich fraction may be treated to remove at least a portion of the one or more non-calcium salts, e.g., to bring their level in the calcium-rich fraction below a threshold. The threshold may be determined, for example, by the desired composition of the final product, e.g., a cement, such as a hydraulic cement, e.g., Portland cement, e.g., OPC. For example, certain non-calcium materials, e.g., derivatives of iron, aluminum, and / or magnesium salts, may be acceptable in hydraulic cements such as Portland cements, such as OPC, but only below a certain level, which often depends on the type of cement (e.g., ASTM Type 1, 2, 3, 4, or 5, or similar standards) and / or the standards to be met, as standards may vary depending on geographic location. The threshold value may be based, at least in part, on the expected levels of non-calcium salt derived materials, such as aluminum, iron, and / or magnesium materials, in the final clinker or product of the cement, such as Portland cement, such as OPC, after further processing.

[0106] In certain embodiments, the calcium-rich fraction is not processed to remove non-calcium salts. This may be the case when the starting material is particularly rich in calcium compounds, an example of such a starting material being wollastonite. In such cases, processing of the calcium-rich fraction generally involves removal of water to produce solid calcium salts, and further processing to convert the calcium salts into the desired end product, e.g., clinker or cement such as Portland cement. Such processing is further described below.

[0107] In certain embodiments, the calcium-rich fraction is treated to remove one or more non-calcium salts. Any suitable treatment or combination of treatments can be used, so long as a sufficient amount of the non-calcium salts are converted into a form that can be separated from the calcium-rich fraction, such as converted into a solid form. The treatment or combination of treatments may result in the regeneration of at least a portion of the original strong acid, e.g., HCl. It is not necessary to remove all of the non-calcium salts, so long as the percentage remaining in solution is below a threshold percentage. In certain embodiments, the calcium-rich fraction is raised to and / or maintained at one or more temperatures or temperature ranges to cause the formation of one or more insoluble non-calcium substances from the one or more non-calcium salts. Additionally or alternatively, in certain embodiments, the calcium-rich fraction is treated with one or more substances, such as one or more bases, that cause the formation of one or more insoluble non-calcium substances from the one or more non-calcium salts.

[0108] Thus, the calcium-rich fraction may contain soluble non-calcium salts, such as salts of Al, Fe, and / or Mg, sometimes referred to as metal-containing compounds. Separating calcium-containing compounds from the calcium-rich fraction S150 includes precipitating the soluble non-calcium salts (metal-containing compounds). In certain embodiments, this includes a one-step pyrolysis (thermohydrolysis) process. In certain embodiments, this includes a multi-step pyrolysis (thermohydrolysis) process, such as a two-step pyrolysis process. In certain embodiments, this includes the addition of a base. In certain embodiments, one-step pyrolysis (thermohydrolysis) and the addition of a base are used. In certain embodiments, two-step decomposition (thermohydrolysis) and the addition of a base are used. In certain embodiments, only the addition of a base is used. Generally, during the process(es), at least a portion of the strong acid, e.g., HCl, is also regenerated.

[0109] In certain embodiments, raising the calcium-rich fraction to a temperature or temperature range and / or maintaining it at a temperature or temperature range (one-step pyrolysis or pyrohydrolysis) causes the formation of a set of insoluble non-calcium materials that can be removed from the calcium-rich fraction. The temperature or temperature range can be such that one or more non-calcium salts, such as at least iron and aluminum salts, form insoluble materials, such as insoluble iron and aluminum materials. Further non-calcium salts that can form insoluble materials include salts of boron, lithium, rubidium, cesium, strontium, barium, and / or radium. The temperature may be any suitable temperature or range of temperatures, for example at least 140, 145, 150, 155, 160, 165, 170, 175, or 180° C., and / or up to 145, 150, 155, 160, 165, 170, 175, 180, 185, 190, or 195° C. In certain embodiments, the calcium-enriched fraction is heated to between 140 and 195° C., in preferred embodiments, the calcium-enriched fraction is heated to between 140 and 185° C., in more preferred embodiments, the calcium-enriched fraction is heated to between 150 and 185° C., or even to between 175 and 185° C. In certain embodiments, the calcium-enriched fraction is heated to at least 140° C., such as at least 150° C., for example at least 160° C., and in certain cases at least 170° C. Any suitable method of bringing the calcium-rich fraction to and / or maintaining it at a desired temperature may be used. Methods of heating a solution at and / or maintaining it at a temperature or temperature range are well known in the art. The calcium-rich solution may be maintained at or near the desired temperature for a suitable period of time, such as at least 0, 1, 2, 5, 10, 20, 30, 40, or 50 minutes, or 1, 1.5, 2, 2.5, 3, 4, 5, 7, or 10 hours, and / or no more than 1, 2, 5, 10, 20, 30, 40, or 50 minutes, or no more than 1, 1.5, 2, 2.5, 3, 4, 5, 7, 10, or 15 hours.In certain embodiments, the calcium-rich fraction is maintained at or near the desired temperature for 10 minutes to 5 hours, such as 30 minutes to 4 hours, and in some cases 1 to 3 hours. As the calcium-rich fraction is heated and / or maintained at an elevated temperature, HCl gas is driven off. Some or all of this gas can be captured and dissolved in an aqueous medium to regenerate HCl. In certain embodiments, the HCl gas is captured and returned to the aqueous medium, such as an HCl solution that is or will be used as a leachant for the processing of subsequent materials containing calcium. Insoluble material generated by increasing the temperature can be separated from the remaining calcium-rich fraction by any suitable method, such as centrifugation, filtration, and the like. The insoluble material can include one or more compounds of aluminum and / or iron, such as Al(OH)3, Al2O3, AlO(OH), Fe(OH)2, Fe(OH)3, FeO(OH), FeO, FeO2, Fe2O3, and the like.

[0110] In certain embodiments, a two-step pyrolysis process is used. This is done by first incorporating a two-step pyrolysis (two-step pyrohydrolysis). First, the mixture is heated to a temperature or temperature range such that aluminum salts, such as AlCl3, form insoluble aluminum substances, such as Al(OH)3, Al2O3, AlO(OH), etc., but iron salts, such as FeCl2 and / or FeCl3, do not form or do not substantially form insoluble substances, such as Fe(OH)2, Fe(OH)3, FeO(OH), FeO, FeO2, Fe2O3, etc. In certain embodiments, the first temperature is less than 150°C, or less than 145°C, or less than 140°C. In certain embodiments, the first temperature is 130-145°C, 131-144°C, 132-141°C, 133-139°C, or 135-137°C, such as about or exactly 136°C, or such as approximately 140°C. Any suitable method of bringing the calcium-rich fraction to the desired temperature and / or maintaining it at the desired temperature may be used. The calcium-rich solution may be maintained at or near the desired temperature for a suitable period of time, such as at least 0, 1, 2, 5, 10, 20, 30, 40, or 50 minutes, or 1, 1.5, 2, 2.5, 3, 4, 5, 7, or 10 hours, and / or no more than 1, 2, 5, 10, 20, 30, 40, or 50 minutes, or no more than 1, 1.5, 2, 2.5, 3, 4, 5, 7, 10, or 15 hours. In certain embodiments, the calcium-rich fraction is maintained at or near the desired temperature for 10 minutes to 5 hours, such as 30 minutes to 4 hours, and in some cases 1 to 3 hours. This process causes aluminum to form insoluble compounds, e.g., oxidize aluminum (e.g., form Al(OH)3, Al2O3, AlO(OH), etc.). HCl is also regenerated, as described for the one-step pyrolysis process. The insoluble, e.g., oxidized, aluminum compounds can then be separated from the calcium-rich fraction solution and these can be further processed, e.g., dried.The remaining solution is then brought to a second temperature or temperature range at which at least one or more non-calcium salts, such as iron salts, form insoluble materials, e.g., Fe(OH)2, Fe(OH)3, FeO(OH), FeO, FeO2, Fe2O3, etc. The temperature can be any suitable temperature or temperature range, e.g., at least 140, 145, 150, 155, 160, 165, 170, 175, or 180°C, and / or up to 145, 150, 155, 160, 165, 170, 175, 180, 185, 190, or 195°C. In certain embodiments, the remaining solution is heated to between 140 and 195°C, in preferred embodiments, the remaining solution is heated to between 150 and 190°C, and in more preferred embodiments, the remaining solution is heated to between 175 and 185°C. In certain embodiments, the remaining solution is heated to at least 145°C, such as at least 170°C, in certain cases at least 175°C, such as approximately 180°C in a second heating step. Any suitable method of bringing the calcium-rich fraction to the desired temperature and / or maintaining it at the desired temperature may be used. The calcium-rich solution may be maintained at or near the desired temperature for a suitable period of time, such as at least 0, 1, 2, 5, 10, 20, 30, 40, or 50 minutes, or 1, 1.5, 2, 2.5, 3, 4, 5, 7, or 10 hours, and / or no more than 1, 2, 5, 10, 20, 30, 40, or 50 minutes, or no more than 1, 1.5, 2, 2.5, 3, 4, 5, 7, 10, or 15 hours. In certain embodiments, the calcium-rich fraction is maintained at or near the desired temperature for between 10 minutes and 5 hours, such as between 30 minutes and 4 hours, in some cases between 1 and 3 hours. This temperature, like the first heating step, serves to cause the formation of insoluble iron compounds, e.g., oxidize the iron (e.g., form Fe(OH)2, Fe(OH)3, FeO(OH), FeO, FeO2, Fe2O3, etc.), while simultaneously regenerating the HCl first acid. The insoluble, e.g., oxidized Fe, can then be separated from the calcium-rich fraction solution, which can then be further processed, e.g., dried.

[0111] In certain embodiments, the calcium-rich fraction is treated with one or more bases to cause the formation of a set of insoluble non-calcium substances that can be removed from the calcium-rich fraction. HCl can also be regenerated during the base addition. In certain embodiments, this is the only process used to cause the formation of insoluble non-calcium substances (metal compounds that precipitate). In certain embodiments, a one-step pyrolysis process and base addition is used. In certain embodiments, a two-step pyrolysis process and base addition is used. The base or bases can be any suitable base or bases, so long as the strength and amount of the base or bases is sufficient to precipitate the desired amount of metal compounds. In certain embodiments, the base or bases include a calcium base. In certain embodiments, the base or bases include a substance or substances that are generated as products during the process, such as a calcium base, such as CaO, Ca(OH)2, or CaSi, such as dicalcium silicate or tricalcium silicate. In certain embodiments, at least 10, 20, 30, 40, 50, 60, 70, 80, 90, or 95% of the one or more bases comprise one or more products produced during the process, such as calcium bases, e.g., CaO, Ca(OH)2, or CaSi, e.g., dicalcium silicate or tricalcium silicate. In certain embodiments, 100% of the one or more bases comprise one or more products produced during the process, such as calcium bases, e.g., CaO, Ca(OH)2, or CaSi, e.g., dicalcium silicate or tricalcium silicate. Some or all of the added base may be regenerated during further steps of the process, e.g., calcium salt decomposition to produce CaO, dicalcium silicate, and / or tricalcium silicate, etc. In certain embodiments, base is added to the calcium-rich fraction in a one-step process to precipitate all desired compounds, e.g., to precipitate Al, Fe, and Mg compounds. In certain processes, the base is added after some of the non-calcium salts (metal compounds) have been precipitated, for example by a one or two step pyrolysis process.In such cases, sufficient base is added to precipitate the remaining metal compounds or a portion thereof (e.g., the remaining Fe and Mg compounds, or the remaining Mg compounds, or a portion thereof). In certain embodiments, a base is added to precipitate the Mg compounds. The precipitate may include one or more magnesium compounds, such as Mg(OH)2, magnesium silicate hydrate, magnesium silicate alumina, and / or other magnesium compounds. The precipitate can be separated from the remaining calcium-rich fraction by any suitable method, such as those described herein. The precipitate can be further processed, for example, by drying. The magnesium precipitate can be used to react with carbon dioxide, for example, in flue gases, such as flue gases (e.g., flue gases from the combustion of natural gas or coal) generated as part of the process to provide energy for the overall process, and / or with other carbon dioxide sources, such as atmospheric carbon dioxide, and / or carbon dioxide in a body of water, such as the ocean, to produce a magnesium-carbon dioxide product, for example, MgCO3 (and / or bicarbonate, in the case of a body of water), thus sequestering carbon dioxide. The amount of carbon dioxide sequestered in this manner can reduce the total amount of carbon dioxide produced throughout the process, potentially enough to make the entire process carbon neutral or even carbon negative. Additionally, other substances in the flue gas that need to be removed from the flue gas, such as SOx and / or NOx, can be reacted with the Mg precipitate, potentially reducing the level of one or more of the substances below the level required for the flue gas to be released into the atmosphere. Additionally or alternatively, the magnesium precipitate can sequester carbon dioxide from the atmosphere, and any suitable configuration can be used for this purpose. In certain embodiments, the magnesium precipitate, optionally processed to increase the surface area, can simply be placed in piles, spread on the ground in layers, or distributed in other suitable manner to sequester atmospheric carbon dioxide for any suitable period, which can be days, weeks, months, a year, or more.

[0112] Reduced carbon dioxide production Thus, the processes for producing cements such as clinker or Portland cement and / or SCMs described herein do not produce as much carbon dioxide as standard processes. In fact, in certain embodiments, the processes described herein may be carbon negative. The cements such as clinker or Portland cement and / or SCMs produced by the processes disclosed herein may be used, for example, in concrete, mortar, stucco, grout, etc., as cements such as clinker or Portland cement and / or SCMs are typically used. Because the processes described herein produce less carbon dioxide than conventional processes for producing Portland cement and may even be carbon negative in some cases, replacing some or all of the standard cements such as clinker or Portland cement with the cements such as clinker or Portland cement produced by the processes described herein may reduce the carbon footprint of concrete or other products, and in fact, in certain cases, the concrete may even be carbon negative. The same may be true for SCMs. In embodiments where the cement, such as clinker or Portland cement, SCM, and possibly aggregates are produced in one location and blended into the concrete at that location, further carbon reductions are realized due to reduced (or eliminated) transportation of the various components. The amount of carbon dioxide avoided and / or sequestered by using the cement, such as clinker or Portland cement, and / or SCM produced in the processes described herein instead of standard clinker or Portland cement and / or SCM can be calculated based on inputs and outputs, etc., as known in the art, such that carbon credits can be obtained based on the carbon dioxide avoided / sequestered.Accordingly, provided herein is a method of obtaining carbon credits, the method comprising carrying out one or more of the processes described herein to produce a cement, such as clinker or Portland cement, and optionally SCM, using the cement, such as clinker or Portland cement, and optionally SCM, as a substitute for a cement, such as clinker or Portland cement, and optionally SCM, produced by a standard method, evaluating the carbon dioxide produced and consumed in the process(es) described herein, determining the amount of carbon dioxide avoided and / or sequestered compared to concrete produced with the cement, such as clinker or Portland cement, and optionally SCM, by a standard method, and obtaining carbon credits based on the amount.

[0113] In certain embodiments where a one- or two-step pyrolysis process is used, precipitating the metal compounds may include adding a base such as a calcium base (e.g., CaO, Ca(OH)2, or CaSi), e.g., as described above, thereby precipitating magnesium from the calcium-rich fraction, effectively leaving only calcium compounds, or calcium compounds with sufficiently low levels of metal compounds to be acceptable in one or more end products of the process. Additionally, HCl may be regenerated during the base precipitation step.

[0114] Generally, the calcium-rich fraction after removal of metal compounds will contain a large amount of calcium chloride, for example at least 90%, in some cases at least 95%, or even at least 99% calcium chloride. The calcium-rich fraction is also typically highly concentrated, for example, from 40% CaCl2 / 60% water to 70% CaCl2 / 30% water, or from 50% / 50% to 60% / 40%, or even from 55% / 45% to 60% / 40%.

[0115] The resulting calcium compounds remaining in the calcium-rich fraction, whether produced by an acid dissolution step, one-step pyrolysis, two-step pyrolysis, base addition, or any suitable combination thereof, can then be subjected to processing to produce one or more further products, e.g., cement such as clinker or Portland cement. This may include removing water from the remaining calcium-rich fraction containing calcium compounds, resulting in calcium-rich solids comprising one or more calcium compounds, e.g., one or more calcium salts, e.g., CaCl2, which can be treated, e.g., to convert to a dechlorinated calcium product and thence to a clinker, e.g., clinker for the production of Portland cement comprising dicalcium silicate and tricalcium silicate.

[0116] Water can be removed from the calcium-rich fraction by any suitable method, for example, by heating to evaporate the water as steam. Some or all of the resulting steam can be used in further processes requiring steam, as described below. The resulting calcium compound solids include one or more calcium salts, e.g., CaCl2, also referred to herein as "calcium chloride-containing solids", and may further include non-calcium salts, e.g., iron, aluminum, and / or magnesium salts, and / or other salts, so long as they are not present in an amount that renders the final product unsuitable for its intended use, e.g., as a cement, such as clinker or Portland cement, and / or that interferes with the process for producing a cement, such as clinker or Portland cement.

[0117] The calcium compound solids (solids containing calcium chloride) can be treated, for example, by flaking, grinding, or other suitable methods, to produce particles of a desired size for further processing. It can then be treated to decompose the calcium-containing compounds, for example, into CaO and / or other calcium-containing dechlorinated products and regenerate HCl. It can be further heated (sintered) in the presence of a flux, such as a flux providing Si, Fe, and Al, to produce a clinker, such as a clinker for Portland cement, to produce a clinker, which can be further processed to produce a cement, such as Portland cement.

[0118] In certain embodiments, the calcium compound solid (a solid comprising calcium chloride) is prepared by mixing the solid with steam, silica, and optionally aluminum, e.g., Al(OH). 3、 and / or iron, e.g. Fe(OH) xThe silica is heated in the presence of an exogenous flux, such as an exogenous flux containing. Generally, a flux is not required at this step, but may be added for convenience. In certain embodiments, some or all of the silica, e.g., at least 10, 20, 30, 40, 50, 60, 70, 80, 90, 95, 98, 99%, or 100% of the silica, is silica that was produced from non-limestone materials, such as non-limestone rocks and / or minerals, e.g., in an earlier step of the process, e.g., in the production of SCM (pozzolana) as described herein. In certain embodiments, some or all of the exogenous flux, e.g., at least 10, 20, 30, 40, 50, 60, 70, 80, 90, 95, 98, 99% of the flux, or 100% of the flux, are iron and aluminum oxides, hydroxides, and potentially other suitable compounds, e.g., generated from non-limestone rocks and / or minerals in earlier steps of the process, e.g., precipitated as insoluble salts from a calcium-rich fraction as described herein. It will be understood that the calcium compound solids (solids including calcium chloride) can include one or more substances that can act as fluxes, but generally it is preferred to add exogenous fluxes. Heating can be done in a single step at a temperature high enough to decompose the calcium-containing solids and clinker, e.g., sinter, the resulting compounds together with the flux. In the simplest case, calcium compound solids are heated with an intrinsic flux in the presence of steam to a temperature high enough to decompose the calcium compound, produce HCl, and produce clinker, e.g., to a temperature high enough to sinter. In preferred embodiments, heating may be carried out at successively higher heats in two or more steps, and an exogenous flux, if used, is present only in all or part of the steps (e.g., heating, clinkering, e.g., sintering).

[0119] As mentioned above, the calcium compound solid (solid containing calcium chloride) comprises calcium chloride, and in certain embodiments comprises at least 20, 30, 40, 50, 60, 70, 80, 90, 92, 95, 96, 97, 98, or 99%, such as at least 90%, and in some cases at least 95% calcium chloride. The decomposition process results in the dechlorination of calcium chloride in the solid, such as at least 80, 90, 95, 96, 97, 98, 99, 99.1, 99.5, 99.9, 99.91, 99.95, or 99.99% of calcium chloride in the solid, i.e., the amount of chloride in the starting material is driven off, preferably at least 90%, more preferably at least 95%, and even more preferably at least 99%. Surprisingly, it has been found that at least 99%, 99.5%, 99.9%, or even 99.95% of the calcium chloride can be dechlorinated, and these levels of dechlorination result in a final product with a chloride content low enough to meet Portland cement specifications, such as less than 1% or even less than 0.1% chloride, without further processing. In a preferred embodiment, at least 99% of the calcium chloride in the solids is dechlorinated, in a more preferred embodiment, at least 99.9% of the calcium chloride in the solids is dechlorinated, and in an even more preferred embodiment, at least 99.95% of the calcium chloride in the solids is dechlorinated.

[0120] In certain embodiments, calcium compound solids (solids containing calcium chloride) are heated in the presence of steam to one or more temperatures or temperature ranges sufficient to drive chlorine gas from the solids. The chlorine gas combines with protons from the steam to regenerate HCl, which can be recycled as described above. At the same time, calcium chloride is converted to dechlorinated calcium compounds, which may or may not contain calcium oxide. One overall reaction may be as follows: CaCl2+H2O→CaO+2HCl

[0121] More generally, the reaction can be expressed as follows: CaCl2 + SiO2 + H2O → Ca silicates and other species + 2HCl

[0122] Intermediate compounds such as calcium silicate chloride, calcium silicate aluminum chloride compounds, etc. may form, and as the process reaches higher temperatures, monocalcium silicate and dicalcium silicate may form. CaO may be present, but is not necessarily present. Thus, in certain embodiments, the process produces a product that contains dicalcium silicate in an amount of at least 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, or 80% by weight, in some cases at least 30%, such as at least 50%, and less than 30, 20, 15, 12, 10, 9, 8, 7, 6, 5, 4, 3, 2, or 1% by weight, in some cases less than 10%, such as less than 5% CaO. In general, the product of dechlorination contains little or no tricalcium silicate, such as less than 20, 15, 10, 5, 3, 2, 1, 0.5, or 0.1%, such as less than 5%. In certain embodiments, a product is formed that contains at least 30% dicalcium silicate and less than 10% CaO, and in some cases less than 0.5% tricalcium silicate, which can then be further processed to produce a clinker.

[0123] Thus, in certain embodiments, there is provided a process for producing a clinker, such as a clinker that can be converted into a cement, such as Portland cement, comprising 1) providing a composition comprising dicalcium silicate, for example in an amount of at least 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, or 80% by weight, in some cases at least 30%, such as at least 50%, and less than 30, 20, 15, 12, 10, 9, 8, 7, 6, 5, 4, 3, 2, or 1% by weight, in some cases less than 10%, such as less than 5%, CaO, for example a composition comprising at least 30% dicalcium silicate and less than 10% CaO, in preferred embodiments a composition that contains little or no tricalcium silicate, such as less than 5% or less than 1%, or even less than 0.5%, and 2) treating the composition under conditions to produce a clinker, such as a clinker that can be processed into a Portland cement, such as OPC (clinkering). In certain embodiments, the process of step 2) comprises heating the composition in the presence of a flux comprising aluminum and / or iron compounds, such as aluminum oxide and / or iron oxide, as described in more detail below, to a temperature of, for example, 1200-1600° C. Some or all of the flux may be produced in the process producing the composition of step 1). The resulting clinker comprises tricalcium silicate, for example at least 10, 20, 25, 30, 35, 40, 45, 50, 55, or 60% w / w, in preferred embodiments at least 50%.

[0124] While it is possible for the decomposition and clinkering to take place at one temperature, it is preferred to carry out the decomposition and clinkering in a multi-step process at successively higher temperatures, where the material may be held at a given temperature for a specific period of time, e.g., 0.5-5 hours, or 0.75-4 hours, or 1-3 hours, e.g., 1, 2, or 3 hours. This improves the efficiency and yield of the dechlorination, and as described elsewhere, surprisingly high levels of dechlorination are achieved by this process. Additionally or alternatively, the temperature may be gradually increased from one temperature to the next. Heating may take place in any suitable system, such as a fluidized bed or a kiln, and in a preferred embodiment, the heating takes place in a kiln, such as a rotary kiln.

[0125] Accordingly, provided herein is a method of dechlorinating calcium chloride, comprising heating calcium chloride to a first temperature in the presence of steam, silica, and optionally a flux comprising an iron and / or aluminum compound, such as one or more of the iron and / or aluminum compounds disclosed herein, and then 1) holding the calcium chloride and other components at the first temperature for a first period of time to produce a first set of one or more products comprising at least HCl and removing HCl; heating the remainder of the first set of one or more products to a second temperature in the presence of steam, to a second, higher temperature, and holding the one or more products and the steam at the second temperature to produce a second set of one or more products comprising HCl and removing HCl; and optionally, e.g., a third, temperature and then in certain embodiments, an additional step of further heating to a fourth temperature and holding at each temperature for a specific period of time to produce a set of products, one of which is HCl (where the temperature, aluminum and / or iron compounds, silica, and period of time can be as described); or 2) gradually heating the calcium chloride and other components from the first temperature to a second, higher temperature, where the heating rate is slow enough to allow a desired degree, e.g., maximum, of HCl production, whereby the calcium chloride is at least 95% dechlorinated, and in preferred embodiments at least 99.9% dechlorinated, and in more preferred embodiments at least 99.95% dechlorinated to produce a dechlorinated calcium product.

[0126] In certain embodiments, a solid composition is provided that includes: 1) a solid comprising calcium chloride, e.g., at least 50, 60, 70, 80, 90, or 95% calcium chloride, e.g., at least 90%, in a preferred embodiment at least 95% calcium chloride; 2) a solid comprising silica, e.g., at least 50, 60, 65, 70, 75, 80, 85, 90, or 95%, e.g., at least 60%, preferably at least 75%, more preferably at least 80% silica; and, optionally, 3) a flux comprising one or more iron compounds, e.g., one or more of Fe(OH)2, Fe(OH)3, FeO(OH), FeO, FeO2, Fe2O3, and / or one or more aluminum compounds, e.g., one or more of Al(OH)3, Al2O3, AlO(OH). In certain embodiments, the solid comprising calcium chloride comprises at least 80% calcium chloride, and the solid comprising silica comprises at least 60% silica. In a particular embodiment, the solids containing calcium chloride comprise at least 90% calcium chloride and the solids containing silica comprise at least 80% silica. In general, the solids are combined such that the Ca-Si molar ratio is between 2.5 and 3.25. The composition may have components in the following proportions (by weight): 50-90% calcium chloride solids, 10-40% silica solids, 0-4% iron compounds, which function as a flux, if used, and 0-4% aluminum compounds, which function as a flux, if used. In a preferred embodiment, the proportions are 60-85% calcium chloride solids, 15-30% silica solids, 1-3% iron compounds, which function as a flux, if used, and 1-3% aluminum compounds, which function as a flux, if used. In a more preferred embodiment, the proportions are 70-80% calcium chloride solids, 15-25% silica solids, 1-2% iron compounds, which function as a flux, if used, and 1-2% aluminum compounds, which function as a flux, if used. In certain embodiments, all of the components are derived from a single source, for example a single source that includes non-limestone rocks and / or minerals.In certain embodiments, a composition comprising calcium chloride-containing solids and silica-containing solids is produced by a process described herein, e.g., treating a non-limestone starting material by acid dissolution and further processing to produce calcium chloride-containing solids, and adding silica-containing solids to the calcium chloride-containing solids in a desired ratio, such as a Ca-Si molar ratio of 2.5 to 3.25. The silica-containing solids can be any suitable solid. In certain embodiments, some or all of the solids are produced in the process to produce calcium chloride-containing solids, e.g., as calcium-depleted solids from the acid dissolution step.

[0127] It is preferred to heat the calcium compound solids in the presence of steam and generally silica, and optionally a flux, to a first temperature, such as a first temperature at which HCl can be handled according to methods known in the art, and hold, or heat in an incremental manner. In certain embodiments, the solids are heated to 1250°C or less, for example, 750-1250°C, 800-1250°C, in certain cases 850-1000°C, in some cases 900-1250°C, preferably 1000-1250°C, and even more preferably 1100-1250°C, in the presence of steam, silica, and optionally an aluminum and iron containing compound, to produce HCl and dechlorinated calcium products. The solid mixture may be heated rapidly to 700-750°C. When the temperature reaches 700, 705, 710, 715, 720, 730, 740, or 750° C., preferably 700° C. or 720° C., the heating should generally proceed at a rate of no more than 2, 5, 10, 15, 20, 25, 30, 40, 50, 60, 70, or 100° C. per minute, preferably no more than 30° C., even more preferably no more than 20° C., and even more preferably no more than 10° C. / minute, until the temperature reaches 800, 850, 900, 950, or 1000° C., preferably 1000° C. Without being bound by theory, it is believed that within the range of about 700 to about 1000° C., calcium chloride may melt undesirably and the amount of chlorine driven off may be reduced, but keeping the heating at a controlled rate may instead favor the reaction between calcium and silica and the production of HCl to produce products that allow more chlorine to be driven off. The process may be held at one or more temperatures ("soaking") for a period of 1-180 minutes, e.g., 5-120 minutes, e.g., 10-120 minutes. Example 4 shows exemplary soaking temperatures and times, but these are merely illustrative. Additionally or alternatively, the temperature may be continuously ramped up at a constant or variable rate. Such refinements may be determined through routine experimentation. Steam may be present in any suitable concentration, such as 5-100% by volume. Steam flow may be initiated when T>300°C.

[0128] The solids may be heated in any suitable manner and system, such as a fluidized bed or kiln. In this and other steps, the silica may be present in any suitable ratio to the calcium compound, such as CaCl2. For example, a 100-105 g sample may contain about 80 gm CaCl2, about 20 gm silica, and optionally about 1-3 gm each of aluminum and iron compounds. This is merely illustrative, and one skilled in the art will appreciate that the ratios of the various components may vary according to the specifications for the type of Portland cement being produced. For example, a higher ratio of calcium to silica may produce a final product with a higher ratio of C3S compared to C2S.

[0129] The dechlorinated calcium product (possibly a CaO-containing product, but possibly containing little or no CaO) can then be heated to a second temperature, optionally to a third temperature, and optionally even to a fourth temperature, generally also in the presence of one or more of lower temperature steam, silica or compounds formed from silica and calcium, and optionally aluminum and / or iron compounds acting as fluxes, and at one or more temperatures, e.g. the higher temperature, steam may not be present. Thus, the dechlorinated calcium product (e.g. CaO-containing product or non-CaO-containing product) is clinkered, i.e. clinkerized (optionally sintered), e.g. in the presence of silica and optionally a flux, e.g. an aluminum and / or iron containing flux, to produce a clinker, such as Portland cement clinker. The flux may include materials produced in earlier steps of the process, e.g. aluminum and / or iron compounds removed from the calcium-rich fraction, as described above. In certain embodiments, at least 10, 20, 30, 40, 50, 60, 70, 80, 90, or 95%, such as at least 50%, in some cases at least 70%, and in certain embodiments at least 90%, of the exogenous flux containing aluminum and / or iron comprises one or more compounds to be removed from the calcium-rich fraction. In certain embodiments, in certain embodiments, 100% of the exogenous flux containing aluminum and / or iron comprises one or more compounds to be removed from the calcium-rich fraction. Whether or not exogenous flux is present, and if so, the amount, may be determined, at least in part, by the desired final composition, for example, the type of cement, such as clinker or Portland cement, to be produced. In certain embodiments, a flux containing both iron-containing and aluminum-containing compounds is used.

[0130] When only the second temperature is used, the process includes heating the dechlorinated calcium product (which may be a CaO-containing product, but which may contain little or no CaO) in the presence of silica and optionally a flux to 1200-1550°C, preferably up to 1450°C, to form a Portland cement clinker containing dicalcium silicate and tricalcium silicate, and optionally the clinker also containing tricalcium aluminate and / or tetracalcium aluminoferrate. When an intermediate temperature is used, the temperature may be, for example, 900-1100°C, e.g., 950-1050°C, the temperature may be, for example, 1100-1300°C, e.g., 1150-1250°C, and the temperature may be, for example, 1400-1600°C, e.g., 1450-1550°C. In an exemplary embodiment, the temperature is held successively at 850, 1000, 1200, and 1500°C for one hour each. These are merely examples, and one of ordinary skill in the art can select optimal temperatures and durations through routine experimentation.

[0131] During the heating process, base that may have been used in the base precipitation step, e.g., one or more calcium bases, can be regenerated, for example, at least 10, 20, 30, 40, 50, 60, 70, 80, 85, 90, 95, 98, or 99% of the amount of base used in the base precipitation step can be regenerated.

[0132] At the end of the process clinker may remain, which may have a diameter in millimeters, for example 0.5-50 mm, or 1-40 mm, or 1-30 mm, although other sizes are also acceptable for further processing.

[0133] In certain embodiments, a method of producing a clinker from solids comprising calcium chloride is provided, the method comprising dechlorinating solids comprising CaCl to produce a dechlorinated composition comprising Ca and having less than 10% Cl w / w, and heating the dechlorinated composition in the presence of a flux to produce a clinker for producing Portland cement, such as a clinker comprising dicalcium silicate and tricalcium silicate.

[0134] In certain embodiments, provided herein is a method of producing a clinker comprising heating a composition comprising dicalcium silicate and no more than 20, 15, 10, 5, 2, or 1% CaO, e.g., no more than 10% CaO, in the presence of a flux to produce a clinker. The composition may contain less than 5, 4, 3, 2, 1, 0.5, or 0.1% tricalcium silicate, and the clinker comprises at least 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, or 60% tricalcium silicate. The flux may comprise aluminum oxide and / or iron oxide.

[0135] 1. A method for producing both clinker and supplementary cementitious material (SCM) from a starting material comprising non-limestone material comprising calcium and silicon, the method comprising: (i) dissolving the non-limestone material in HCl to produce a calcium-rich liquid fraction comprising calcium chloride and a calcium-depleted solid fraction comprising silica; (ii) producing the SCM from the calcium-depleted solid fraction comprising silica; and (iii) producing a clinker from the calcium-rich liquid fraction comprising calcium chloride.

[0136] Clinker, such as Portland cement clinker, may be further processed, e.g., treated, such as in combination with calcium sulfate, to create particles in a desired size range.

[0137] At the end of all acid regeneration steps, such as HCl regeneration, at least 10, 20, 30, 40, 50, 60, 70, 80, 85, 90, 95, 98, or 99% of the initial acid, such as the initial HCl, may be regenerated. In a preferred embodiment, at least 80% of the initial HCl is regenerated. In another preferred embodiment, at least 90% of the initial HCl is regenerated. An amount of strong acid, such as unregenerated HCl, can be added back, i.e., replenished, to provide sufficient acid, e.g., sufficient HCl, for subsequent processing of the non-limestone material.

[0138] In a seventh example, as previously described, decomposing calcium compounds S160 and regenerating the leaching agent S170 can be performed simultaneously with pyrolysis to precipitate iron and aluminum. In a cement production variant, the seventh example involves dechlorinating calcium compounds (e.g., CaO, CaOH, etc.) to SiO, Al(OH), and Fe(OH) in a kiln. x and clinkering, e.g., sintering the calcium product, to form a clinker, such as a clinker for ordinary Portland cement. This example may further include scrubbing the flue gas with insoluble Mg compounds, e.g., Mg(OH)2, produced during the process to produce MgCO3. Additionally or alternatively, the insoluble Mg compounds, e.g., Mg(OH)2, produced during the process may be placed in a waste pile where it may be exposed to air and slowly converted to MgCO3. Additionally or alternatively, the insoluble Mg compounds produced during the process may be placed in a body of water, such as the ocean. Bicarbonate may also be formed during this process.

[0139] Method for producing supplemental cementitious materials (SCM) In certain embodiments, methods are provided for producing SCMs, such as pozzolans, from non-limestone materials, e.g., rocks and / or minerals. Generally, the methods include exposing non-limestone materials, such as non-limestone rocks and / or minerals, to a leaching agent, e.g., a strong acid that dissolves certain components of the non-limestone material to produce a liquid leachate while leaving behind a solid leachate residue that includes one or more amorphous substances that may function as SCMs, such as pozzolans, and separating the solid leachate residue from the liquid leachate. Optional further steps may include treating the SCM to remove the liquid leachate, e.g., by rinsing, treating the SCM to dry it, and / or treating the SCM to produce SCMs in a desired size range.

[0140] The non-limestone materials can be any suitable material so long as they contain one or more compounds that can result in a final material that includes amorphous (non-crystalline) materials that can function as SCMs. These can include amorphous silica, in which case the starting materials will also include silicon-based materials such as silica, silicates, silica compounds, and / or silicate compounds. However, as is known in the art, other materials can result in amorphous compounds that function as SCMs, such as amorphous iron and aluminum materials, in which case the starting materials will include the necessary starting elements. In general, "amorphous materials," as the term is used herein, include materials that can exist as one or more crystalline or amorphous polymorphs, which may be referred to as amorphous polymorphs, or amorphous materials, or amorphous materials. In certain embodiments, the non-limestone materials include silicon. In certain embodiments, the non-limestone materials include rocks and / or minerals that include silicon. In certain embodiments, the non-limestone material includes rocks and / or minerals containing non-silicic materials that serve as materials for producing amorphous materials, such as iron and / or aluminum-containing materials, which may be present in addition to silicon, or may in some cases serve as the primary or only source of amorphous materials in the final SCM. In certain embodiments, the non-limestone material, e.g., rocks and / or minerals, includes calcium silicate. Exemplary suitable non-limestone rocks and / or minerals include basalt, gabbro, pyroxenite, anorthosite, skarn, amphibolite, or combinations thereof. Other suitable non-limestone materials may be as described elsewhere herein.

[0141] Non-limestone materials, e.g., rocks and / or minerals, may be processed to provide particles within a desired size range. Any suitable process or processes, such as crushing and sieving, may be used. Suitable size ranges include 1-500u, 5-300u, 10-200u, 20-130u, 45-90u, or combinations thereof. In a preferred embodiment, the size range is 20-130u. In a more preferred embodiment, the size range is 45-90u.

[0142] The non-limestone material, e.g., rock and / or minerals, is contacted with a leaching agent, which may be any suitable leaching agent, such as those described herein. In certain embodiments, the leaching agent comprises a strong acid, and the contacting process produces a pulp that includes the acid and the rock and / or minerals. Any suitable leaching agent, e.g., a strong acid, such as HCl, HBr, HI, H2SO4, or HNO3, may be used. In certain embodiments, the strong acid comprises HCl. In certain embodiments, the only acid used is HCl. For convenience, the remainder of the process will be described in terms of HCl. As will be apparent to one of skill in the art, if another acid is used in addition to or as a replacement for HCl, suitable adjustments can be made to accommodate the additional / alternative acid.

[0143] Any suitable concentration of HCl may be used, such as 5-40%, 10-37%, 10-30%, 15-35%, 17-23%, 20-30%, or about or exactly 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, or 30%, for example about or exactly 20%. In a preferred embodiment, the HCl is 10-37%. In an even more preferred embodiment, the HCl is 15-35%.

[0144] The ratio of solid non-limestone materials, e.g., solid rocks and / or minerals, to liquid (acid) in the initial pulp can be any suitable ratio. It will be understood that some of the solid rocks and / or minerals will immediately begin to dissolve in the acid, and these ratios will change as the solids go into solution. Suitable initial ratios can be within the range of 5% solids / 95% liquid to 40% solids / 60% liquid, e.g., 10% solids / 90% liquid to 30% solids / 70% liquid; in a preferred embodiment, 15% solids / 85% liquid to 25% solids / 75%, e.g., 20% solids / 80% liquid. In certain embodiments, provided herein is a pulp composition comprising solid non-limestone rocks and / or minerals and a liquid leaching agent, such as a strong acid, such as HCl, wherein the pulp comprises solids and liquids in a ratio of 5% solids / 95% liquid to 40% solids / 60% liquid, such as 10% solids / 90% liquid to 30% solids / 70% liquid, in preferred embodiments 15% solids / 85% liquid to 25% solids / 75% liquid, such as 20% solids / 80% liquid. In certain embodiments, the solid non-limestone rocks and / or minerals comprise at least 60, 70, 80, 90, or 95% of the particles in the size range of 1-500u, 5-300u, 10-200u, 20-130u, 45-90u, or combinations thereof. In a preferred embodiment, the size range is 20-130u. In a more preferred embodiment, the size range is 45-90u. In certain embodiments, the leaching agent is a strong acid, such as HCl, and is present in a concentration of 10-40%, such as 10-35%, in some cases 15-35%, or even 20-30%.

[0145] The pulp is treated to dissolve at least a portion, preferably a majority, of the non-amorphous materials, such as non-silica materials, into the solution, leaving a solid rich in amorphous substances, such as amorphous silica. The treatment may be carried out in an open to air or at least unpressurized process. Generally, treatment duration and / or temperature can be used and adjusted, for example, according to the starting material. Suitable temperature ranges for maintaining the pulp include 60-115°C, 80-115°C, 90-115°C, 100-115°C, 60-112°C, 80-112°C, 90-112°C, 100-112°C, 60-110°C, 80-110°C, 90-110°C, or 100-110°C. It will be appreciated that the boiling temperature of the HCl solution increases as more material dissolves into the liquid phase. Thus, in certain embodiments, the temperature is at least 95, 96, 97, 98, 99, or 100°C, in preferred embodiments, the temperature is at least 90°C, in more preferred embodiments, the temperature is at least 95°C, in even more preferred embodiments, the temperature is at least 98°C, and in even more preferred embodiments, the temperature is at least 100°C. In certain embodiments, the maximum temperature is 105, 106, 107, 108, 109, 110, 111, 112, 113, 114, or 115°C, in preferred embodiments, the maximum temperature is 105°C, in more preferred embodiments, the maximum temperature is 108°C, and in even more preferred embodiments, the maximum temperature is 110°C. Thus, in certain embodiments, the temperature is maintained between 100 and 110°C.

[0146] Any suitable treatment period may be used, which may depend, in part, on the starting material, such as non-limestone rocks and / or minerals. Thus, the treatment period may be at least 1, 2, 3, 4, 5, 6, 7, 8, or 10 hours, and / or no more than 2, 3, 4, 5, 6, 7, 8, 10, 12, 15, 20, 24, 30, 36, 40, 48, 60, or 72 hours. In certain embodiments, the period may be 2 to 24 hours, such as 4 to 18 hours, or even no more than 4 to 12 hours. In certain embodiments, the period may be 6 to 72 hours, such as 4 to 48 hours, or 4 to 36 hours, or 4 to 24 hours.

[0147] The pulp may be agitated during processing, for example, at 10-1000 RPM, 20-800 RPM, 50-500 RPM, 50-400 RPM, or 100-300 RPM. In preferred embodiments, the pulp is agitated at 50-400 RPM, more preferably 100-300 RPM. Other suitable forms of agitation may be used.

[0148] After a suitable treatment period has been reached, a solution containing salts of dissolved materials from the non-limestone materials (also referred to herein as leachate, or pregnant leach solution or PLS) and the undissolved portion of the solids (also referred to herein as leach residue) have been produced. The leach residue is separated from the leachate. Any suitable method may be used, such as simply draining the PLS, centrifugation, filtration, and methods described herein.

[0149] The leach residue generally contains one or more amorphous materials, e.g., one or more amorphous materials that can function as SCMs, such as pozzolans. In certain embodiments where the starting material contains silicon, the leach residue contains amorphous silica. Additionally or alternatively, the leach residue may contain other amorphous compounds, such as amorphous Fe and / or Al, e.g., amorphous alumina, amorphous iron oxide, etc., that can also function as SCMs, such as pozzolans. In certain embodiments, the leach residue comprises at least 10, 20, 30, 40, 50, 60, 70, or 80% by weight of amorphous silica. The leach residue may be treated to remove some or all of the leachate, such as by rinsing with water. It may then be dried. The dried leach residue may be an SCM and may be used as is, or after further processing, such as by crushing and sieving to reduce the size of the particles to a desired range.

[0150] In certain embodiments in which the starting material comprises silicon, the leach residue contains amorphous silica. Additionally or alternatively, the leach residue may contain other amorphous compounds, such as amorphous Fe, Al, and / or Mg compounds, e.g., amorphous alumina, amorphous iron oxide, amorphous magnesium oxide, etc., which may also function as SCMs, such as pozzolans.

[0151] Device In one aspect, provided herein is an apparatus, such as an apparatus suitable for performing one or more of the processes described herein. In a particular embodiment, an apparatus is provided for producing SCM (pozzolana) from non-limestone materials, such as non-limestone rocks and / or minerals, comprising one or more leaching vessels, a separation system for separating solids produced in the leaching vessel from liquids, and a processing system for processing the separated solids to produce SCM. Further components may include one or more energy sources for the process performed by the apparatus, one or more systems for processing the non-limestone materials, such as non-limestone rocks and / or minerals, to make them suitable for leaching (which may be the same as, but are typically different from, the processing system for processing the separated solids). The exact configuration of components may depend, in some cases, on the type of process being performed. For example, in a batch process, the leaching vessel may be a container, such as a tank, that includes a material that can withstand the temperature and acidity of the leaching process and is sufficiently waterproof, e.g., completely waterproof, to contain the acid during leaching. In a continuous process, such as a countercurrent leaching process, the leaching vessel may include a first conveyor for conveying non-limestone materials, such as non-limestone rocks and / or minerals, in a first direction and a second conveyor for conveying a leaching agent, such as a strong acid, such as HCl, in the opposite direction so that the two contact each other in a countercurrent fashion, with the components in contact with the leaching agent including materials that can withstand the leaching agent and temperature used. Other configurations for other types of leaching processes will be readily apparent to those skilled in the art. The separation system may include, for example, one or more centrifuges, filters, filter presses, and the like, as described elsewhere herein. The processing system may include a dryer, which may be any suitable dryer, and possibly even a dryer that simply exposes the SCM to the atmosphere to dry, or any other suitable dryer, such as one that provides heat to the SCM to accelerate drying. Such equipment is well known in the art. The processing system may include an optional rinser to rinse the leaching agent and leachate from the SCM prior to drying.The processing system may also include one or more components for processing the SCM to produce particles within a desired size range or set of size ranges, such as crushers, ball mills, sieves, and / or other components known in the art. The one or more energy sources may be one or more suitable configurations of connections to an energy grid, such as an electrical grid, a renewable energy source (e.g., solar, wind, geothermal, etc.), an energy storage device, such as a battery, a fossil fueled generator, such as a natural gas or coal-fired generator, other suitable generators, or any suitable combination thereof. In embodiments in which a fossil fueled generator is used, the energy source may further include a system for scrubbing the flue gas produced by the fossil fueled generator to reduce SOx, NOx, and / or other regulated pollutants to acceptable levels and / or reduce the carbon dioxide content of the flue gas. In certain embodiments, such a system includes an apparatus for contacting the flue gas with magnesium compounds produced by further processing the calcium-rich fraction (as described in more detail below), and the system removes carbon dioxide, and optionally SOx and / or NOx, from the flue gas.

[0152] In a particular embodiment, an apparatus is provided for producing clinker or cement such as Portland cement from non-limestone materials such as non-limestone rocks and / or minerals, the apparatus comprising one or more leaching vessels, a separation system for separating a calcium-depleted solid fraction produced in the leaching vessel from a calcium-rich liquid fraction, a processing system for removing non-calcium compounds and materials from the calcium-rich fraction, a system for precipitating solid calcium compounds from the calcium-rich fraction, a system for decomposing the solid calcium compounds into products containing dechlorinated products and processing to produce Portland cement clinker, and a system for processing the Portland cement clinker into Portland cement. Further components may include one or more energy sources for the process performed by the apparatus, one or more systems for processing the non-limestone materials such as non-limestone rocks and / or minerals to make them suitable for leaching (which may be the same as, but are typically different from, the processing system for processing the separated solids). If SCM is also produced, additional components are included as described above. The leaching vessel, separation system, energy source, system for processing non-limestone materials such as non-limestone rocks and / or minerals are as described above. The processing system for removing non-calcium compounds and materials from the calcium-rich fraction may include one or more systems for heating and maintaining the calcium-rich fraction at a desired temperature or temperature range and / or a system for adding a base to the calcium-rich fraction, and a separation system for removing insoluble non-calcium compounds and materials from the calcium-rich fraction. Systems for heating and maintaining a solution at a temperature are known in the art and may include any suitable configuration, such as a heat source applied to the outside or inside of the leaching vessel, one or more temperature sensors, a control system, etc. The system for adding a base may include a transport mechanism for transporting the base (e.g., bases generated later in the process such as CaO, dicalcium silicate, and / or tricalcium silicate) to the calcium-rich fraction, metering the amount of base, introducing the base, timing the reaction, etc.All components of these systems may be well known in the art. In certain embodiments, both the system for heating the calcium-rich fraction and the system for adding a base to the calcium-rich fraction are incorporated in the apparatus. The system for separating the insoluble compounds and / or materials is as described. If a strong acid such as HCl is used as the leaching agent and the strong acid such as HCl is regenerated, the apparatus may further include one or more components for capturing HCl gas and contacting it with an aqueous liquid to produce liquid HCl, for example, as systems well known in the art. The system for precipitating calcium-containing solids from the calcium-rich fraction may be as simple as a heat source for heating the calcium-rich solution to produce steam. Optionally, a transport system, such as one or more conduits, may be included to transport steam to the system for decomposing the calcium-containing solids into Portland cement clinker. The system for decomposing calcium-containing solids into dechlorinated products and sintering into Portland cement clinker may include one or more heat sources, one or more devices for introducing steam, silica, and generally one or more aluminum and / or iron containing fluxes to the calcium-containing solids, and a device for containing the sintered calcium-containing solids, such as a fluidized bed or a kiln, preferably a rotary kiln. Optional systems for processing Portland cement clinker into Portland cement are well known in the art and may include crushers, ball mills, sieves, etc. The system for decomposing solid calcium compounds may further include a device for capturing and transporting the regenerated acid, e.g., regenerated HCl, back to the HCl source.

[0153] In certain embodiments, an apparatus is provided for producing a clinker, such as a clinker suitable for producing a cement, such as Portland cement, from non-limestone materials, such as rocks and / or minerals, and / or other suitable starting materials as described herein. Generally, such an apparatus comprises at least a first processor configured to process the non-limestone starting material to produce a solid comprising one or more calcium compounds, such as CaCl2, operably connected to a second processor configured to form a clinker, such as an OPC clinker, from a solid composition comprising one or more calcium compounds, such as calcium chloride, and optionally produce a cement, such as OPC, from the clinker. See, e.g., FIG. 8.

[0154] The first processor may include a leacher, operably connected to one or more precipitators, which are operably connected to a dehydrator. See, for example, Figure 9. In certain embodiments where a starting material is used that can be used without precipitating non-calcium salts, the first system may include a leacher and a dehydrator without including one or more precipitators.

[0155] The leacher may be configured to contact the non-limestone material with an acid to produce a first calcium-rich liquid fraction and a calcium-depleted solid fraction. It may be operatively connected to a material processing system including a material processor, such as a crusher and / or mill, configured to process the non-limestone starting material, for example, to reduce the size of the non-limestone material and / or classify the material into one or more size ranges, and one or more sizing screens, or other suitable configurations. The leacher generally includes a leaching vessel for holding and processing the pulp created from the acid and the non-limestone material. Any suitable material may be used as long as it can withstand the leaching conditions. The leacher may include a heating element and / or an agitator. It may be operatively connected to an acid reservoir. It may be operatively connected to a first separator, which may also be operatively connected to a precipitator, which may be configured to separate a calcium-rich liquid fraction from a calcium-depleted solid fraction and direct the calcium-rich liquid fraction to the precipitator. The first separator may be operatively connected to a solids processing system, including, for example, rinsers and dryers, for processing calcium-depleted solids, such as silica (for convenience, the solids are described as silica, but it will be understood that other materials may be included in certain cases). A portion of the silica may be used for dechlorination and / or clinkering (see below), in which case the solids processing system is operatively connected to the dechlorinator and / or clinker to provide silica. A portion of the silica may be used as SCM, and the apparatus may further include one or more additional processors for further processing as necessary or desired to provide one or more desired characteristics, such as particle size, storage, etc.

[0156] The precipitator may be configured to remove one or more non-calcium salts from the calcium-rich fraction by converting the one or more non-calcium salts removed from the calcium-rich fraction to a solid form. Typically, the precipitator is operatively connected to the separation system of the leaching vessel such that the calcium-rich liquid fraction passes from the separation system to the precipitator, or to a first precipitation unit in the series if multiple precipitation units are used. The precipitator, or each precipitation unit if multiple precipitation units are used, is operatively connected to a second (and possibly a third and / or fourth) separator for separating solids produced in the precipitator or precipitation units from the calcium-rich liquid fraction.

[0157] The precipitator includes a first precipitation unit, which is a base precipitation unit configured to precipitate a first set of non-calcium compounds. The base precipitation unit may be operably connected to one or more base sources. The base source may include a calcium base source. The base precipitation is as described in more detail elsewhere herein. In certain embodiments, at least a portion of the calcium base source includes a source operably connected to the dechlorinator and / or the cleanser to receive one or more products therefrom. In certain embodiments, the precipitator includes only a base precipitation unit. In these cases, the base precipitation generally results in the precipitation of aluminum, iron, and magnesium species, which are also described in more detail elsewhere herein.

[0158] In certain embodiments, the precipitator further comprises a second precipitation unit, which is a pyrohydrolysis precipitation unit configured to precipitate a second set of non-calcium compounds from the calcium-rich liquid fraction. As described above, this may be operatively connected to a third separator for separating the second set of precipitated non-calcium compounds from the calcium-rich liquid fraction. In certain embodiments, the precipitator comprises a third precipitation unit, which is a pyrohydrolysis unit for precipitating a third set of non-calcium compounds from the calcium-rich liquid fraction, which may be operatively connected to a fourth separator for separating the third set of precipitated non-calcium compounds from the calcium-rich liquid fraction. In certain embodiments, the second and third precipitation units are the same and the second and third sets of precipitated non-calcium compounds are the same. For example, the second / third precipitation units may be configured to perform a one-step pyrohydrolysis, as described in more detail elsewhere herein, and the second / third set of precipitated non-calcium products may comprise Al- and Fe-species, also as described in more detail elsewhere herein. In certain embodiments, the second and third precipitation units are different, the second precipitation unit being configured to precipitate aluminum compounds by heating the calcium-rich liquid to a first temperature or temperature range, e.g., as described in more detail elsewhere herein, and the third precipitation unit being configured to precipitate iron compounds by heating the calcium-rich liquid to a second temperature or temperature range higher than the first temperature or temperature range, e.g., as described in more detail elsewhere herein. The apparatus may further include one or more units for transporting one or more of the non-calcium precipitated products to the cleansers and / or dechlorinators. These generally include aluminum and iron compounds that may function as fluxes in the cleansers.

[0159] The precipitator is operatively connected to the dehydrator for delivering the calcium rich liquid, from which the non-calcium compounds have been removed, to the dehydrator.

[0160] The dehydrator is configured to remove water from the calcium-rich liquid fraction from the precipitator to produce solids containing one or more calcium compounds, such as calcium chloride, for example, by heating the calcium-rich liquid to evaporate the water until a desired level of dryness is achieved. The dehydrator may include a heating element. In certain embodiments, the dehydrator may include an apparatus, such as an apparatus including a conduit, configured to transport the steam generated in the dehydrator to the dechlorinator and optionally to the clincolor. The solid product produced by the dehydrator is a solid containing one or more calcium compounds, such as calcium chloride, which may exist in one or more hydration states, for example, anhydrous, monohydrate, etc. Depending on the starting material and process, the solid may be 80, 90, 95, or greater than 98% CaCl2. It is desirable to configure the dehydrator to produce calcium chloride in a lower hydration state, for example, anhydrous, because less energy is required to drive off the remaining water in further steps. Further processing equipment may be connected to the dehydrator to reduce the size of the solids, for example, by producing particles, flakes, etc. from the solids.

[0161] The second processor includes a dechlorinator and a cleanser (cement kiln). See, for example, FIG. 10. The dechlorinator, operably connected to the dehydrator and receiving solids containing calcium chloride (which may be further processed on the way to the dechlorinator), is configured to dechlorinate the solids containing CaCl2 to produce dechlorinated solids containing calcium compounds. The dechlorinator is operably connected to a cleanser configured to heat the dechlorinated solids in the presence of a flux to produce clinker. The dechlorinator and cleanser can be a single unit. In a preferred embodiment, the dechlorinator and cleanser are separate units. In a preferred embodiment, one or both of the dechlorinator and / or cleanser include a rotary kiln. In a more preferred embodiment, both the dechlorinator and cleanser include a rotary kiln.

[0162] The dechlorinator may be configured to produce dechlorinated solids containing calcium compounds and less than 20, 15, 10, 8, 7, 6, 5, 4, 3, 2, or 1 wt. % Cl. Methods and systems for dechlorinating solids containing calcium chloride to low levels of chloride may be as described herein. For example, the dechlorinator may be configured to continue heating at a rate low enough to keep the material below 1, 2, 3, 5, 7, 10, 15, 20, 30, 40, 50, 60, or 80° C. when the material reaches a threshold temperature, e.g., another temperature, such as 700-750° C., up to 800-1000° C. Additionally or alternatively, the dechlorinator may be configured to hold the material at one or more temperatures for one or more time periods and / or adjust and / or maintain the heating at one or more desired incremental rates. The dechlorinator is operably connected to one or more steam sources and one or more silica sources. One of the steam sources may be a dehydrator. The one or more silica sources may include calcium-depleted solids separated from the calcium-rich fraction in the first processor or a portion thereof, such as the first separator, which may be further processed, for example, by rinsing and drying, and then transported to the dechlorinator. The silica is mixed with the calcium chloride-containing solids from the dehydrator. This may be done prior to the dechlorinator. The silica may be mixed in a desired ratio, for example, a molar ratio of Ca:Si 1-4, preferably 2-4, more preferably 2.5-3.5, and even more preferably 2.5-3.25. HCl is produced by the dechlorinator, which may be operatively connected to the leacher to replenish the HCl to the leacher, the acid reservoir, or both.

[0163] The cleanar is configured to receive the dechlorinated solids containing calcium compounds from the dechlorinator and further process the solids (at least in the initial stage) in the presence of the flux and, optionally, steam to produce clinker. The cleanar heats the dechlorinated solids containing calcium compounds mixed with the flux to one or more temperatures and / or for one or more time periods, e.g., as described herein. One or more flux sources are operably connected to the cleanar. Any suitable flux may be used. In certain embodiments, some or all of the flux comprises one or more species produced in the first processor, e.g., in one or more precipitation units of a precipitator, and the cleanar is operably connected to the first processor, e.g., one or more precipitation units, e.g., one or more precipitation units producing aluminum and / or iron species, including aluminum oxide and / or iron oxide, which may include Al2O3 and / or Fe2O3, etc. In certain embodiments, the flux includes materials not produced in the process, such as clays and other materials as known in the art, and the one or more flux sources include one or more other materials. In certain embodiments, the Clincolor also functions as a calcium base source, and one or more products of the Clincolor, including, for example, dicalcium silicate and / or tricalcium silicate, are used as calcium bases in the precipitator, and the Clincolor is operably connected to the precipitator, for example, to a base precipitation unit.

[0164] In certain embodiments, the system further includes a clinker processor configured to receive the clinker from the clinker and further process it to produce a cement, e.g., a Portland cement, such as OPC. The clinker processor may be configured to adjust the size / size distribution of the clinker, e.g., through grinding, crushing, screening, etc., and / or introduce additional materials, such as gypsum. The clinker processor may also be configured to prepare the processed material, e.g., a cement, such as OPC, for transport and / or sale.

[0165] In certain embodiments, the clinker is operably connected to a concrete production facility, generally near a source of starting materials such as non-limestone materials, and the concrete production facility produces concrete using cement from the clinker, and in certain embodiments, also using aggregates produced from the same non-limestone materials used to produce the cement and / or SCM.

[0166] FIG. 13 illustrates one embodiment of a system and method for producing clinker from non-limestone materials. Starting material, such as non-limestone materials described herein, e.g., non-limestone rocks and / or minerals, is provided via a feed (1301) to a material processor (1302) that includes a crusher (1303) that processes the starting material into crushed particles comprising a plurality of sizes. The crushed particles are then passed through one or more screens (1304) that separate crushed particles in a desired size range from crushed particles in a larger size range. The larger than desired crushed particles are returned to the crusher (1303) and optionally mixed with fresh starting material for further processing. The crushed particles in the desired size range are then fed to a mill (1305) where the crushed particles are broken down into finer sizes. The ground particles are combined with the air stream (1306) and fed into a baghouse (1307) where the ground particles are separated from the air and fed into a hopper (1309) and the clean air is exhausted (1308).

[0167] The ground particles are then transferred from the hopper to a leaching vessel (1310) where the ground particles are contacted with a leaching agent, e.g., an acid such as HCl, in a leaching tank (1311) to form a pulp. The leaching agent is provided from an acid storage tank (1312). Additional leaching agent can be added or removed (1313) from the acid storage tank (1312) as needed. The leaching tank (1311) may include an agitator / agitation element. The leaching tank may include one or more heating elements (not shown) for heating the pulp. The leaching system may include an acid recovery element (1314) that recovers the evaporated acid and returns it to the leaching tank (1311) and / or vents it (1315). Water may be added to the acid storage tank from any suitable source, e.g., a boiler / vapor recompression system (1316), to prepare the desired concentration of acid. After suitable processing, the treated pulp, which generally includes a calcium-rich liquid fraction and a calcium-depleted solid fraction, may be transported through a first separator, which in this example includes a leaching filter (1317), to separate the calcium-depleted solid fraction from the calcium-rich liquid fraction. Water (1318), and / or any other suitable fluid, may be added to the leaching filter at any time, for example to rinse the calcium-depleted solid fraction. The calcium-depleted solid fraction may be transported to a kiln (1319) for drying. Generally, the solid calcium-depleted fraction includes silica, and some or all of the solid fraction may be used as a silica source at a later stage of the process, for example during dechlorination. Additionally or alternatively, some or all of the solid fraction may be further processed, for example to obtain a desired size range, to provide a supplemental cementitious material (SCM), which may be sold and / or used in combination with the cement produced during the process to make concrete, etc.

[0168] The calcium-rich liquid fraction from the first separator, e.g., leach filter (1317), is then sent to a precipitation unit, which is a thermal hydrolysis precipitation unit, in this embodiment a molten salt hydrolysis chamber (1320), for heating with or without pretreatment to remove water, NaCl, and / or KCl from the leachate (1321). The molten salt hydrolysis chamber, e.g., thermal hydrolysis chamber (1320), processes the calcium-rich liquid fraction at one or more temperatures for a predefined period at each temperature to promote certain chemical reactions, including the conversion of soluble species of iron and / or aluminum, e.g., iron chloride and / or aluminum chloride, to insoluble species, which may include oxides such as iron oxide and / or aluminum oxide. The treated calcium-rich liquid fraction is then cooled in a quencher (1322) and mixed with water in a mixer (1323). Depending on the treatment protocol, insoluble aluminum and iron species, e.g., oxides, may be recovered after treatment (1324), e.g., in a separator during the addition of water in the mixer (1323). The treated calcium-rich liquid fraction is then transferred to a precipitation unit, which is a base precipitation unit comprising a precipitation vessel (1325), where the treated calcium-rich liquid fraction is contacted with one or more basic chemicals, such that soluble magnesium species, e.g., magnesium chloride, are converted and precipitated into insoluble magnesium species, e.g., magnesium oxide. Prior to contacting with the treated leachate, the base may be treated in a slaker (1326). The insoluble precipitated magnesium species, e.g., magnesium oxide species, are then separated from the treated calcium-rich liquid fraction, e.g., through a separator comprising a series of settling units (1327) and / or filters (1328), and optionally rinsed with water, or any other suitable liquid (1329). In certain embodiments (not shown), the system does not include a pyrohydrolysis chamber, and a precipitation unit that is a base precipitation unit serves to precipitate aluminum, iron, and / or magnesium species.

[0169] The treated calcium-rich liquid fraction can be transferred to an acid storage tank, e.g., an acid reservoir (1312) and / or a dehydrator (1330), where the calcium-rich liquid fraction is dehydrated, leaving calcium chloride-containing solids, generally containing high concentrations of calcium chloride, in one or more hydration states. The calcium chloride-containing solids (which may be in one or more hydration states) are then sent to a dechlorinator (1331), where they are mixed with one or more suitable silicate species (such as silica from the calcium-depleted solid fraction) and heated in the presence of steam to convert the calcium chloride-containing solids to dechlorinated solids containing calcium compounds as described elsewhere herein, while simultaneously regenerating a leachant, such as HCl, which can be returned to the leach tank or acid reservoir. The dechlorinated solids containing calcium compounds can be stored for later use (1332) and / or transferred to a clinker (cement kiln) (1333) in combination with a suitable flux for conversion to clinker. Some or all of the flux may contain insoluble metal species, including metal oxides such as iron oxide and / or aluminum oxide, that were separated from the treated leachate (1324). After heat treatment in the clinker (cement kiln) (1333), the clinker may then be transferred to a cooling unit (1334) and the cooled clinker may then be transferred to a mill (1335) for processing into cement. A portion of the dechlorinated solids, clinker and / or cement, including calcium compounds, may be used as part or all of the base for precipitation of magnesium in the precipitation tank (1325). Some or all of the cement may be sold. Some or all of the cement may be used to produce concrete, possibly in combination with a portion of the calcium-depleted solid fraction (acting as SCM) and / or aggregates formed from the starting materials, for example in the crushing and / or grinding process.

[0170] In certain embodiments, provided herein is a concrete production facility that includes a cement source and an aggregate source, both of which are derived from the same material, e.g., a non-limestone material as described herein. The facility can further include a source of SCM, both of which are derived from the same material. The facility can further include a mixer for mixing the cement, aggregate, and optionally the SCM to produce concrete. In certain embodiments, the system also includes a cement source that is produced by conventional methods (calcining and sintering), and in certain embodiments, this conventional cement is also provided to the mixer.

[0171] Embodiment In embodiment 1, a method of producing clinker is provided, comprising: (a) contacting a non-limestone material containing calcium with hydrochloric acid to produce a calcium-depleted solid fraction and a calcium-rich liquid fraction containing calcium chloride; (b) treating the calcium-rich liquid fraction to produce a solid containing calcium chloride; (c) dechlorinating the solid containing calcium chloride to produce a dechlorinated solid containing calcium compounds; and (d) treating the dechlorinated solid containing calcium to produce a clinker. In embodiment 2, a method is provided as in embodiment 1, further comprising separating the calcium-depleted solid fraction from the calcium-rich liquid fraction. In embodiment 3, a method is provided as in embodiment 1 or embodiment 2, wherein the calcium-rich liquid fraction comprises one or more non-calcium salts of magnesium, iron, and / or aluminum, and treating the calcium-rich liquid fraction comprises treating the liquid to precipitate one or more insoluble magnesium, iron, and / or aluminum compounds. In embodiment 4, a method is provided as in embodiment 3, wherein treating the calcium-rich liquid fraction comprises contacting the fraction with a base. In embodiment 5, the method of embodiment 4 is provided, wherein the treatment of the calcium-rich liquid fraction comprises subjecting the fraction to pyrohydrolysis to precipitate insoluble compounds containing aluminum and / or iron, removing the insoluble compounds containing aluminum and / or iron, and then contacting the remaining calcium-rich liquid fraction with a base. In embodiment 6, the method of any of the preceding embodiments is provided, further comprising dehydrating the calcium-rich liquid fraction to produce solids comprising calcium chloride. In embodiment 7, the method of embodiment 7 is provided, wherein the dechlorination of the solids comprising calcium chloride comprises heating the solids in the presence of steam and silica to produce dechlorinated solids comprising calcium. In embodiment 8, the method of embodiment 7 is provided, wherein the calcium and silica are present in a molar ratio of Ca:Si between 2.45 and 3.25. In embodiment 9, the method of embodiment 7 is provided, wherein the treatment of the dechlorinated solids comprising calcium to produce clinker comprises heating the solids with a flux.In embodiment 10, the method of embodiment 9 is provided, wherein the flux comprises aluminum oxide and iron oxide. In embodiment 11, the method of any of the preceding embodiments is provided, further comprising processing the clinker to produce cement.

[0172] In embodiment 12, there is provided a method for preparing a solid material comprising one or more magnesium compounds capable of reacting with carbon dioxide to sequester carbon dioxide, comprising: (a) contacting a non-limestone starting material with an acid to produce a calcium-rich liquid fraction containing magnesium and a calcium-depleted solid fraction; (b) treating the calcium-rich liquid fraction to precipitate one or more magnesium compounds capable of reacting with carbon dioxide to sequester carbon dioxide; (c) separating the magnesium-rich precipitate from the calcium-rich liquid fraction; and (d) rinsing and drying the magnesium-rich precipitate. In embodiment 13, there is provided a method according to embodiment 12, further comprising separating the one or more magnesium compounds capable of reacting with carbon dioxide to sequester carbon dioxide from the liquid. In embodiment 14, there is provided a method according to embodiment 13, further comprising rinsing and drying the one or more magnesium compounds capable of reacting with carbon dioxide to sequester carbon dioxide. In embodiment 15, there is provided a method according to any one of embodiments 12-14, wherein the one or more magnesium compounds capable of reacting with carbon dioxide to sequester carbon dioxide include magnesium oxide, magnesium hydroxide, magnesium oxyhydroxide, magnesium silicate, magnesium silicate hydrate, complexes or combinations thereof. In embodiment 16, there is provided a method according to any one of embodiments 12-15, further comprising contacting the one or more magnesium compounds capable of reacting with carbon dioxide to sequester carbon dioxide with carbon dioxide to sequester the carbon dioxide as magnesium carbonate or magnesium bicarbonate. In embodiment 17, there is provided a method according to embodiment 16, wherein the contacting comprises exposing the one or more magnesium compounds capable of reacting with carbon dioxide to sequester carbon dioxide to flue gas comprising carbon dioxide, e.g., flue gas produced during a process for producing one or more magnesium compounds capable of reacting with carbon dioxide to sequester carbon dioxide, to produce magnesium carbonate.In embodiment 18, there is provided a method as described in embodiment 16, wherein the contacting comprises exposing one or more magnesium compounds capable of reacting with and sequestering carbon dioxide to air containing carbon dioxide to produce magnesium carbonate. In embodiment 19, there is provided a method as described in embodiment 16, wherein the contacting comprises placing one or more magnesium compounds capable of reacting with and sequestering carbon dioxide in a body of water, such as an ocean, to react with carbon dioxide in the body of water to produce magnesium bicarbonate.

[0173] In embodiment 20, a method of obtaining carbon credits is provided, comprising: (a) performing the method of any one of embodiments 1-18, 27-72, or 139-161 to calculate a value of a net carbon dioxide (CO2) avoided and / or a value of a net CO2 sequestered; (ii) tracking one or more amounts of sequestered CO2, one or more amounts of avoided CO2, and one or more amounts of CO2 emissions; (iii) determining the amount of CO2 avoided and / or the amount of CO2 sequestered from the one or more amounts of sequestered CO2, the one or more amounts of avoided CO2, and the CO2 emissions; and (b) obtaining carbon credits based on the value of avoided and / or sequestered CO2 obtained in (iii) of (a). In embodiment 21, there is provided a method according to embodiment 20, wherein the value of avoided CO2 is determined by producing an equivalent amount of cement by a process comprising calcining limestone and comparing it to the amount of CO2 produced by a process according to any one of embodiments 1-18, 27-72, or 139-161. In embodiment 22, there is provided a method according to embodiment 20 or 21, wherein the value of sequestered CO2 is determined by sequestering CO2 with Mg compounds and quantifying the amount of CO2 sequestered by a given amount of Mg compounds. In embodiment 23, there is provided a method according to embodiment 22, wherein at least a portion of the sequestered CO2 is atmospheric CO2.

[0174] In embodiment 24, there is provided a composition comprising at least 50, 60, 70, 80, 90 or 95%w / w calcium chloride, for example at least 90%, in preferred embodiments at least 95%, and at least 50, 60, 65, 70, 75, 80, 85, 90 or 95%, for example at least 60%, preferably at least 75%, more preferably at least 80%w / w silica.In embodiment 25, there is provided a composition according to embodiment 24, comprising less than 10, 8, 7, 6, 5, 4, 3, 2, 1, 0.5 or 0.1%w / w Cl, in preferred embodiments less than 5%, and in more preferred embodiments less than 1% Cl. In embodiment 26, there is provided a composition according to embodiment 24 or 25, comprising less than 20, 15, 10, 8, 7, 6, 5, 4, 3, 2, 1, 0.5, or 0.1% w / w CaO, in preferred embodiments less than 5%, and in more preferred embodiments less than 0.5%.

[0175] In embodiment 27, a method of dechlorinating a solid comprising calcium chloride is provided, the method comprising: (i) combining a solid comprising calcium chloride with a solid comprising silica; and (ii) heating the combined calcium chloride and silica in the presence of steam to a temperature of 750-1250°C to produce HCl gas and a dechlorinated calcium product. In embodiment 28, the method of embodiment 27 is provided, wherein the temperature is 900-1250°C. In embodiment 29, the method of embodiment 27 is provided, wherein the temperature is 1000-1250°C. In embodiment 30, the method of embodiment 27 is provided, wherein the temperature is 1100-1250°C. In embodiment 31, the method of any of embodiments 27-30 is provided, wherein once a temperature of 700-750°C is reached, heating proceeds at a rate of no more than 60, 50, 40, 30, 10, or 5°C per minute until a temperature of 800-850°C is reached. In embodiment 32, the method according to any one of embodiments 27 to 31 is provided, in which the solid comprising calcium chloride and the solid comprising silica are combined such that the Ca-Si molar ratio is between 2.5 and 3.5. In embodiment 33, the method according to any one of embodiments 27 to 31 is provided, in which the solid comprising calcium chloride is present at 50 to 90% by weight and the silica is present at 10 to 40% by weight. In embodiment 34, the method according to any one of embodiments 27 to 33 is provided, in which the solid comprising calcium chloride comprises at least 80, 90, 92, 93, 94, 95, 96, 97, 98, or 99%, preferably at least 90%, more preferably at least 95%, of calcium chloride. In embodiment 35, the method according to any one of embodiments 27 to 34 is provided, in which the solid comprising silica comprises at least 50, 60, 65, 70, 75, 80, 85, 90, or 95%, preferably at least 60%, more preferably at least 75%, even more preferably at least 80% of silica. In embodiment 36, there is provided a method according to embodiment 35, wherein the calcium chloride-containing solid comprises at least 90% calcium chloride and the silica-containing solid comprises at least 80% silica. In embodiment 37, there is provided a method according to any of embodiments 27-36, wherein the steam is present at 5-100% by volume.In embodiment 38, there is provided a method according to any one of embodiments 27-37, wherein the chloride content is reduced by at least 60, 70, 80, 90, 95, 96, 97, 98, or 99%, preferably by at least 90%, more preferably by at least 95%, and even more preferably by at least 99%. In embodiment 39, there is provided a method according to any one of embodiments 27-38, wherein the dechlorinated calcium product comprises at least 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, or 80% by weight of dicalcium silicate, preferably at least 15%, more preferably at least 25% dicalcium silicate, and the amount of CaO is less than 30, 20, 15, 12, 10, 9, 8, 7, 6, 5, 4, 3, 2, or 1% by weight, preferably less than 10%, more preferably less than 5%. In embodiment 40, there is provided a method according to embodiment 40, wherein the calcium dechlorination product comprises at least 15% dicalcium silicate and less than 10% CaO.

[0176] In embodiment 41, a method for producing clinker from a solid containing calcium chloride is provided, comprising: (a) dechlorinating the solid containing calcium chloride to produce a dechlorinated composition containing Ca and having an amount of Cl less than 10% w / w; and (b) heating the dechlorinated composition in the presence of a flux to produce a clinker. In embodiment 42, the method according to embodiment 41 is provided, wherein the clinker comprises dicalcium silicate and tricalcium silicate. In embodiment 43, the method according to embodiment 41 or 42 is provided, wherein the clinker comprises Portland cement clinker. In embodiment 44, the method according to any one of embodiments 41 to 43 is provided, wherein the composition comprising calcium chloride further comprises silica. In embodiment 45, the method according to embodiment 44 is provided, wherein the molar ratio of Ca:Si in the composition comprising calcium chloride and silica is 1.0 to 5.0, preferably 2.0 to 4.0, more preferably 2.5 to 3.25. In embodiment 46, the method according to any one of embodiments 41-45 is provided, wherein the composition comprising calcium chloride comprises at least 80, 90, 92, 95, 96, 97, 98, or 99%, preferably at least 80%, more preferably at least 90%, and even more preferably at least 95% calcium chloride. In embodiment 47, the method according to any one of embodiments 41-46 is provided, wherein the dechlorination composition comprises less than 30, 20, 10, 8, 5, 4, 3, 2, or 1%, preferably less than 10%, and more preferably less than 5% CaO. In embodiment 48, the composition according to any one of embodiments 41-47 is provided, wherein the dechlorination composition comprises less than 10, 8, 6, 5, 4, 3, 2, or 1%, preferably less than 10%, more preferably less than 5%, and even more preferably less than 1% Cl by weight. In embodiment 49, there is provided a method according to any one of embodiments 41-48, wherein the dechlorinating composition comprises at least 2, 5, 10, 15, 20, 25, 30, 35, or 40%, preferably at least 15%, more preferably at least 25%, dicalcium silicate. In embodiment 50, there is provided a method according to any one of embodiments 41-49, wherein dechlorinating the composition comprising calcium chloride comprises heating the composition.In embodiment 51, the method of embodiment 50 further comprises introducing steam when the composition comprising calcium chloride reaches a temperature of 300° C. or more. In embodiment 52, the method of embodiment 51 is provided, wherein heating the composition comprising calcium chloride in the presence of steam comprises heating to a temperature of at least 750° C. and / or 1250° C. or less. In embodiment 53, the method of embodiment 52 is provided, wherein heating between 700-750° C. and 800-1000° is performed at a rate of 100, 80, 50, 40, 30, 25, 20, 15, 10, 5, or 1° / min or less or slower. In embodiment 54, the method of any one of embodiments 41-53 is provided, wherein HCl is produced during dechlorination. In embodiment 55, the method of any one of embodiments 41-54 is provided, wherein the flux comprises an iron compound and / or an aluminum compound. In embodiment 56, the method of embodiment 55 is provided, in which the aluminum compound comprises Al2O3 and / or the iron compound comprises Fe2O3. In embodiment 57, the method of embodiment 55 or embodiment 56 is provided, in which the composition comprising the iron compound and / or the aluminum compound and calcium chloride is produced from the same starting material. In embodiment 58, the method of embodiment 57 is provided, in which the starting material comprises calcium-containing rocks and / or minerals. In embodiment 59, the method of any one of embodiments 44-58 is provided, in which the silica is produced from the same starting material as the starting material of the composition comprising calcium chloride. In embodiment 60, the method of any one of embodiments 41-59 is provided, in which heating the dechlorination composition in the presence of the flux comprises heating the composition to 1200-1600, preferably 1400-1600 °C. In embodiment 61, the method of embodiment 60 is provided, in which the composition comprises heating to 1500-1600 °C. In embodiment 62, the method of embodiment 60 is provided, comprising heating the composition to 1450-1500° C. In embodiment 63, the method of any one of embodiments 41-62 is provided, wherein the dechlorination and / or heating of the dechlorination composition is performed in a kiln.In embodiment 64, the method of embodiment 63 is provided, wherein the kiln comprises a rotary kiln.

[0177] In embodiment 65, there is provided a method for producing a clinker, comprising heating a composition comprising dicalcium silicate and not more than 20, 15, 10, 5, 2, or 1% CaO, such as not more than 10% CaO, in the presence of a flux to produce a clinker. In embodiment 66, there is provided a method according to embodiment 65, in which the composition has an amount of tricalcium silicate less than 5, 4, 3, 2, 1, 0.5, or 0.1%, preferably less than 1%, more preferably less than 0.1%, and the clinker comprises at least 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, or 60%, preferably at least 20%, more preferably at least 50%, of tricalcium silicate. In embodiment 67, there is provided a method according to embodiment 65 or 66, in which the flux comprises aluminum oxide and / or iron oxide.

[0178] In embodiment 68, a method for producing both clinker and auxiliary cementitious material (SCM) from a starting material including non-limestone material containing calcium and silicon is provided, comprising: (i) dissolving the non-limestone material in HCl to produce a calcium-rich liquid fraction including calcium chloride and a calcium-depleted solid fraction including silica; (ii) producing SCM from the calcium-depleted solid fraction including silica; and (iii) producing clinker from the calcium-rich liquid fraction including calcium chloride. In embodiment 69, a method according to embodiment 68 is provided, further comprising producing aggregate from the non-limestone material. In embodiment 70, a method according to embodiment 68 or embodiment 69 is provided, further comprising producing cement from the clinker. In embodiment 71, a method according to embodiment 70 is provided, further comprising combining cement, aggregate, and water to produce concrete. In embodiment 72, a method according to embodiment 71 is provided, further comprising combining SCM with cement, aggregate, and water to produce concrete.

[0179] In embodiment 73, there is provided an apparatus for producing clinker from non-limestone materials, comprising: (i) a first processor configured to process the non-limestone starting material to produce a solid composition comprising calcium chloride; and (ii) a second processor configured to form a clinker from the solid composition comprising calcium chloride, the first processor being operably connected to the second processor. In embodiment 74, there is provided an apparatus according to embodiment 73, wherein the first processor comprises: (a) a leacher configured to contact the non-limestone material with an acid to produce a first calcium-rich liquid fraction and a calcium-depleted solid fraction; (b) a precipitator configured to remove one or more non-calcium salts from the calcium-rich fraction by converting the one or more non-calcium salts removed from the calcium-rich fraction to a solid form; and (c) a dehydrator configured to remove water from the calcium-rich liquid fraction from the precipitator to produce solids comprising calcium chloride, the leacher being operably connected to the precipitator. In embodiment 75, there is provided an apparatus according to embodiment 73 or embodiment 74, wherein the first processor further comprises a material processor operably connected to the leaching vessel and configured to process the non-limestone starting material. In embodiment 76, there is provided an apparatus according to embodiment 75, wherein the material processor is configured to reduce the size of the non-limestone material and / or classify the material into one or more size ranges. In embodiment 77, there is provided an apparatus according to any one of embodiments 74-76, wherein the first processor further comprises an acid storage tank operably connected to the leaching vessel. In embodiment 78, there is provided an apparatus according to any one of embodiments 74-77, wherein the leaching vessel comprises a heating element. In embodiment 79, there is provided an apparatus according to any one of embodiments 74-78, wherein the leaching vessel comprises an agitator. In embodiment 80, there is provided an apparatus according to any one of embodiments 74 to 79, wherein the infuser further comprises a first separator operably connected to the infuser and the precipitator and configured to separate the calcium-rich liquid fraction and the calcium-depleted solid fraction and direct the calcium-rich liquid fraction to the precipitator.In embodiment 81, there is provided an apparatus according to any one of embodiments 74 to 80, wherein the precipitator is operably connected to a second separator for separating solids from the calcium-rich liquid fraction. In embodiment 82, there is provided an apparatus according to any one of embodiments 74 to 81, wherein the precipitator comprises a first precipitation unit, the first precipitation unit being a base precipitation unit configured to precipitate a first set of non-calcium compounds. In embodiment 83, there is provided an apparatus according to embodiment 82, further comprising one or more base sources operably connected to the first precipitation unit. In embodiment 84, there is provided an apparatus according to embodiment 83, wherein the one or more base sources comprise a calcium base source. In embodiment 85, there is provided an apparatus according to any one of embodiments 82 to 85, wherein the precipitator comprises a second precipitation unit, the second precipitation unit being a pyrohydrolysis precipitation unit configured to precipitate a second set of non-calcium compounds from the calcium-rich liquid fraction. In embodiment 86, there is provided an apparatus according to embodiment 85, wherein the second precipitation unit is operatively connected to a third separator for separating the second set of precipitated non-calcium compounds from the calcium-rich liquid fraction. In embodiment 87, there is provided an apparatus according to embodiment 85 or embodiment 86, wherein the precipitator comprises a third precipitation unit, the third precipitation unit being a pyrohydrolysis unit for precipitating the third set of non-calcium compounds from the calcium-rich liquid fraction. In embodiment 88, there is provided an apparatus according to embodiment 87, wherein the third precipitation unit is operatively connected to a fourth separator for separating the third set of precipitated non-calcium compounds from the calcium-rich liquid fraction. In embodiment 89, there is provided an apparatus according to embodiment 87 or embodiment 88, wherein the second and third precipitation units are the same and the second and third sets of precipitated non-calcium compounds are the same.In embodiment 90, there is provided the apparatus according to embodiment 87 or embodiment 88, wherein the second and third precipitation units are different, the second precipitation unit being configured to precipitate aluminum compounds by heating the calcium-rich liquid to a first temperature or temperature range, and the third precipitation unit being configured to precipitate iron compounds by heating the calcium-rich liquid to a second temperature or temperature range higher than the first temperature or temperature range. In embodiment 91, there is provided the apparatus according to any one of embodiments 74 to 90, wherein the dehydrator comprises a heating element. In embodiment 92, there is provided the apparatus according to any one of embodiments 73 to 91, wherein the second processor comprises (a) a dechlorinator configured to dechlorinate solids comprising CaCl2 to produce dechlorinated solids comprising calcium compounds, and (b) a cleanser configured to heat the dechlorinated solids in the presence of a flux to produce clinker, the dechlorinator being operably connected to the cleanser. In embodiment 93, the apparatus of embodiment 92 is provided, wherein the dechlorinator is configured to produce dechlorinated solids comprising calcium compounds and having Cl content less than 20, 15, 10, 8, 7, 6, 5, 4, 3, 2, or 1 wt.%. In embodiment 94, the apparatus of embodiment 92 or embodiment 93 is provided, wherein the base source comprises dechlorinated solids from the dechlorinator and / or cement clinker from a cement kiln. In embodiment 95, the apparatus of any one of embodiments 92-94 is provided, wherein the dechlorinator is operably connected to (1) one or more steam sources, and (2) one or more silica sources. In embodiment 96, the apparatus of embodiment 95 is provided, wherein the one or more steam sources comprise a dehydrator of the first processor. In embodiment 97, the apparatus of embodiment 95 or embodiment 96 is provided, wherein the one or more silica sources comprise the first processor or a portion thereof. In embodiment 98, there is provided the apparatus of embodiment 97, wherein the first processor or a portion thereof comprises a first separator. In embodiment 99, there is provided the apparatus of any one of embodiments 92-98, wherein the clean colorer is operably connected to one or more flux sources.In embodiment 100, there is provided an apparatus according to embodiment 99, wherein the one or more flux sources comprise a first processor or a portion thereof. In embodiment 101, there is provided an apparatus according to embodiment 100, wherein the first processor or a portion thereof comprises a precipitator. In embodiment 102, there is provided an apparatus according to any one of embodiments 92-101, wherein the dechlorinator and / or the clinker comprises a rotary kiln. In embodiment 103, there is provided an apparatus according to any one of embodiments 92-102, further comprising a clinker processor for processing clinker from the clinker. In embodiment 104, there is provided an apparatus according to any one of embodiments 73-102, further comprising a control system, the control system including: (i) one or more input sources from the first processor and / or the second processor; (ii) a processor for processing the inputs from the one or more input sources and providing an output; and (iii) one or more actuators for receiving the output and adjusting the operation of one or more of the first processor and / or the second processor. In embodiment 105, there is provided an apparatus according to embodiment 104, wherein the one or more input sources include one or more sensors, such as one or more temperature sensors for detecting the temperature of the infuser, the dehydrator, the dechlorinator, and / or the cleanolor, or a portion thereof. In embodiment 106, there is provided an apparatus according to embodiment 104 or embodiment 105, wherein the actuators include one or more actuators for adjusting the operation of the heating elements of the infuser, the dehydrator, the dechlorinator, and / or the cleanolor.

[0180] In embodiment 107, a network is provided that includes a plurality of devices described in any one of embodiments 73 to 106, wherein the devices are spatially separated and each of the devices transmits information to a common controller and / or to a plurality of controllers.

[0181] In embodiment 108, there is provided an apparatus for producing solids comprising calcium chloride from non-limestone materials comprising calcium, the apparatus comprising a processor configured to process the non-limestone starting material to produce solids comprising calcium chloride. In embodiment 109, there is provided an apparatus according to embodiment 108, wherein the processor comprises: (a) a leacher configured to contact the non-limestone material with an acid to produce a first calcium-rich liquid fraction and a calcium-depleted solid fraction; (b) a precipitator configured to remove one or more non-calcium salts from the calcium-rich fraction by converting the one or more non-calcium salts removed from the calcium-rich fraction to a solid form; and (c) a dehydrator configured to remove water from the calcium-rich liquid fraction from the precipitator to produce solids comprising calcium chloride, the leacher operably connected to the precipitator. In embodiment 110, there is provided an apparatus according to embodiment 108 or embodiment 109, wherein the processor further comprises a material processor operably connected to the leacher, configured to process the non-limestone starting material. In embodiment 111, there is provided an apparatus according to embodiment 110, wherein the material processor is configured to reduce the size of the non-limestone material and / or classify the material into one or more size ranges. In embodiment 112, there is provided an apparatus according to any one of embodiments 109-111, wherein the processor further comprises an acid storage tank operably connected to the leaching device. In embodiment 113, there is provided an apparatus according to any one of embodiments 109-112, wherein the leaching device comprises a heating element. In embodiment 114, there is provided an apparatus according to any one of embodiments 109-113, wherein the leaching device comprises an agitator. In embodiment 115, there is provided an apparatus according to any one of embodiments 109-114, wherein the leaching device further comprises a first separator operably connected to the leaching device and the settling device, configured to separate the calcium-rich liquid fraction and the calcium-depleted solid fraction and direct the calcium-rich liquid fraction to the settling device. In embodiment 116, there is provided an apparatus according to any one of embodiments 109 to 115, wherein the precipitator is operatively connected to a second separator for separating solids from the calcium-rich liquid fraction.In embodiment 117, there is provided an apparatus according to any one of embodiments 109 to 116, wherein the precipitator comprises a first precipitation unit that is a base precipitation unit configured to precipitate a first set of non-calcium compounds. In embodiment 118, there is provided an apparatus according to embodiment 117, further comprising one or more base sources operatively connected to the first precipitation unit. In embodiment 119, there is provided an apparatus according to embodiment 118, wherein the one or more base sources comprise a calcium base source. In embodiment 120, there is provided an apparatus according to any one of embodiments 109 to 120, wherein the precipitator comprises a second precipitation unit that is a pyrohydrolysis precipitation unit configured to precipitate a second set of non-calcium compounds from the calcium-rich liquid fraction. In embodiment 121, there is provided an apparatus according to embodiment 121, wherein the second precipitation unit is operatively connected to a third separator for separating the second set of precipitated non-calcium compounds from the calcium-rich liquid fraction. In embodiment 122, there is provided an apparatus according to embodiment 120 or embodiment 121, wherein the precipitator comprises a third precipitation unit which is a pyrohydrolysis unit for precipitating a third set of non-calcium compounds from the calcium-rich liquid fraction. In embodiment 123, there is provided an apparatus according to embodiment 122, wherein the third precipitation unit is operatively connected to a fourth separator for separating the third set of precipitated non-calcium compounds from the calcium-rich liquid fraction. In embodiment 124, there is provided an apparatus according to embodiment 122 or embodiment 123, wherein the second and third precipitation units are the same and the second and third sets of precipitated non-calcium compounds are the same. In embodiment 125, there is provided an apparatus as described in embodiment 122 or embodiment 123, wherein the second and third precipitation units are different, the second precipitation unit being configured to precipitate aluminum compounds by heating the calcium-rich liquid to a first temperature or temperature range, and the third precipitation unit being configured to precipitate iron compounds by heating the calcium-rich liquid to a second temperature or temperature range that is higher than the first temperature or temperature range.In embodiment 126, there is provided an apparatus according to any one of embodiments 109 to 125, wherein the dehydrator comprises a heating element.

[0182] In embodiment 127, an apparatus for producing clinker from solids comprising calcium chloride is provided, the apparatus comprising: (a) a dechlorinator configured to dechlorinate solids comprising calcium chloride to produce dechlorinated solids comprising calcium compounds; and (b) a cleanser configured to heat the dechlorinated solids in the presence of a flux to produce clinker, the dechlorinator being operably connected to the cleanser. In embodiment 128, the apparatus of embodiment 127 is provided, the dechlorinator is configured to produce dechlorinated solids comprising calcium compounds and less than 20, 15, 10, 8, 7, 6, 5, 4, 3, 2, or 1 wt. % Cl. In embodiment 129, the apparatus of embodiment 127 or embodiment 128 is provided, the dechlorinator is operably connected to (1) one or more steam sources, and (2) one or more silica sources. In embodiment 130, the apparatus of any one of embodiments 127-129 is provided, the cleanser is operably connected to one or more flux sources. In embodiment 131, there is provided an apparatus according to any one of embodiments 127-130, wherein the dechlorinator and / or the cleanar comprises a rotary kiln. In embodiment 132, there is provided an apparatus according to any one of embodiments 127-131, further comprising a clinker processor for processing clinker from a cement kiln. In embodiment 133, there is provided an apparatus according to any one of embodiments 127-132, further comprising a control system, the control system comprising (i) one or more input sources from the dechlorinator and / or the cleanar, (ii) a processor for processing inputs from the one or more input sources and providing outputs, and (iii) one or more actuators for receiving the outputs and adjusting one or more operations of the dechlorinator and / or the cleanar. In embodiment 134, there is provided an apparatus according to embodiment 133, wherein the one or more input sources comprise the dechlorinator and / or the cleanar, or one or more sensors, for example one or more temperature sensors for detecting the temperature of a portion thereof.In embodiment 135, there is provided the apparatus of embodiment 133 or embodiment 134, wherein the actuator comprises one or more actuators for adjusting the operation of the heating elements of the dechlorinator and / or the cleanar.

[0183] In embodiment 136, a system is provided comprising: (a) a first processor configured to produce cement from the non-limestone material; and (b) a second processor configured to produce SCM from the non-limestone material. In embodiment 137, the system of embodiment 136 is provided, further comprising (c) a third processor for producing aggregate from the non-limestone material. In embodiment 138, the system of embodiment 136 and embodiment 137 is provided, wherein the first and second processors are the same.

[0184] In embodiment 139, there is provided a method of dissolving calcium-containing non-limestone material in an acid to produce a clinker, the method comprising: (a) producing a calcium-rich liquid fraction and a calcium-depleted solid fraction comprising calcium chloride; (b) separating the calcium-depleted solid fraction from the calcium-rich liquid fraction; (c) producing solids comprising calcium chloride from the calcium-rich liquid; and (d) treating the calcium chloride-containing solids to form a clinker. In embodiment 140, there is provided a method according to embodiment 139, wherein the non-limestone material further comprises silicon. In embodiment 141, there is provided a method according to embodiment 139 or embodiment 140, wherein the non-limestone material comprises rocks and / or minerals. In embodiment 142, there is provided a method according to embodiment 141, wherein the non-limestone material containing rocks and / or minerals comprises anorthosite, skarn, gabbro, pyroxenite, mafic rock, ultramafic rock, or a combination thereof. In embodiment 143, there is provided a method according to any one of embodiments 139-142, wherein no more than 40, 30, 20, 15, 10, 5, 4, 3, 2, or 1%, preferably no more than 10%, more preferably no more than 5% of the calcium in the starting material is present as calcium carbonate. In embodiment 144, there is provided a method according to any one of embodiments 139-143, wherein the starting material further comprises aluminum, iron, and / or magnesium. In embodiment 145, there is provided a method according to any one of embodiments 139 to 144, wherein less than 90, 80, 70, 60, 50, 40, 30, 20, 10, or 5% of the CO2 emissions are produced from the limestone compared to producing the same amount of hydraulic cement by a process including calcining the limestone. In embodiment 146, there is provided a method according to embodiment 145, wherein less than 80% of the CO2 emissions are produced. In embodiment 147, there is provided a method according to embodiment 145, wherein less than 60% of the CO2 emissions are produced. In embodiment 148, there is provided a method according to embodiment 145, wherein less than 40% of the CO2 emissions are produced.In embodiment 149, there is provided a method according to any one of embodiments 139-148, further producing a supplemental cementitious material (SCM), Mg derivatives, and / or aggregates. In embodiment 150, there is provided a method according to embodiment 149, wherein the SCM, Mg derivatives, and / or aggregates are produced from the same starting materials used to produce the cement. In embodiment 151, there is provided a method according to any one of embodiments 139-151, wherein the acid comprises HCl, HBr, HI, HNO3, or a combination thereof. In embodiment 152, there is provided a method according to embodiment 151, wherein the acid comprises at least 80, 90, 95, 99, or 100% HCl. In embodiment 153, there is provided a method according to any one of embodiments 139-152, wherein the acid is at a concentration of 10-37%. In embodiment 154, there is provided a method according to embodiment 153, wherein the acid is at a concentration of 15-25%. In embodiment 155, there is provided a method according to embodiment 153, wherein the concentration of the acid is 20%. In embodiment 156, there is provided a method according to any one of embodiments 139-155, wherein producing a solid comprising calcium compounds comprising calcium chloride from a calcium-rich liquid comprises precipitating one or more compounds comprising aluminum, iron, and / or magnesium from the calcium-rich liquid. In embodiment 157, there is provided a method according to any one of embodiments 139-156, wherein producing a solid comprising calcium compounds comprising calcium chloride from a calcium-rich liquid comprises dehydrating the liquid to produce a solid comprising calcium chloride. In embodiment 158, there is provided a method according to any one of embodiments 139-157, wherein treating the solid comprising calcium chloride to form a clinker comprises dechlorinating the solid comprising calcium chloride to produce a dechlorinated solid comprising calcium compounds. In embodiment 159, there is provided a method according to embodiment 158, wherein the dechlorinating comprises heating the solid comprising calcium chloride in the presence of steam and silica. In embodiment 160, there is provided the method of embodiment 158 ​​or embodiment 159, further comprising treating the dechlorinated solids comprising calcium compounds to produce a clinker.In embodiment 161, there is provided a method according to embodiment 160, wherein the treating comprises heating the dechlorinated solids comprising the calcium compound in the presence of a flux.

[0185] Throughout this specification, when compositions are described as having, including, or comprising certain components, or when processes and methods are described as having, including, or comprising certain steps, it is additionally contemplated that there are compositions of the invention that consist essentially of or consist of the recited components, and that there are processes and methods of the invention that consist essentially of or consist of the recited process steps.

[0186] In this application, when an element or component is said to be included in and / or selected from a list of enumerated elements or components, it is understood that the element or component may be any one of the listed elements or components, or the element or component may be selected from the group consisting of two or more of the listed elements or components.

[0187] Furthermore, it should be understood that elements and / or features of the compositions or methods described herein may be combined in various ways without departing from the spirit and scope of the invention, whether expressly or implicitly stated herein. For example, where reference is made to a particular compound, that compound may be used in various embodiments of the compositions of the invention and / or methods of the invention, unless otherwise understood by the context. In other words, although embodiments are described and illustrated herein so that a clear and concise application may be described and depicted, it is intended and will be understood that the embodiments may be combined or separated in various ways without departing from the teachings and invention(s) of the present application. For example, it will be understood that all features described and illustrated herein may be applicable to all aspects of the invention(s) described and illustrated herein.

[0188] The terms "a" and "an" and "the" and similar references in the context of describing the present invention (particularly in the context of the claims below) should be construed to include both the singular and the plural, unless otherwise indicated in the specification or clearly contradicted by the context. For example, the term "a cell" includes a plurality of cells, including mixtures thereof. When the plural is used for compounds, salts, etc., this is construed to mean a single compound, salt, etc.

[0189] The phrase "at least one of" should be understood to include each of the listed items following the phrase individually, and various combinations of two or more of the listed items, unless otherwise understood from context and usage. The phrase "and / or" in the context of more than two listed items should be understood to have the same meaning, unless otherwise understood by context.

[0190] Use of the terms "include," "includes," "including," "have," "has," "having," "contain," "contains," or "containing," including grammatical equivalents thereof, should be understood to be generally open-ended and non-limiting, e.g., not excluding additional, unrecited elements or steps, unless otherwise specifically stated or otherwise understood by context.

[0191] When a term such as "about" or "approximately" is used before a quantitative value, the present invention also includes the specific quantitative value itself unless otherwise specified. As used herein, the term "about" refers to a ±10% variation from the nominal value, unless otherwise indicated or estimated.

[0192] It should be understood that the order of steps or order for performing certain actions is immaterial so long as the invention remains operable. Moreover, two or more steps or actions may be performed simultaneously.

[0193] The use of any and all examples or exemplary language herein, e.g., "such as" or "including," is intended merely to better illustrate the invention and does not impose limitations on the scope of the invention unless otherwise claimed. No language in the specification should be construed as indicating any non-claimed element as essential to the practice of the invention. EXAMPLES

[0194] Example 1 In this example, highly efficient leaching of calcium from non-limestone rocks was demonstrated.

[0195] The following leaching parameters were used for the Ca-bearing rocks, resulting in greater than 90% Ca extraction as measured by inductively coupled plasma optical emission spectroscopy (ICP-OES): Calcium mass balance was completed by X-ray fluorescence (XRF) measurements of the initial rock and leach residues.

[0196] [Table 1]

[0197] In all cases, calcium yields from the rocks were greater than 90%, with skarn and anorthosite exceeding 95% and 99%, respectively. Thus, the HCl process can be used to extract a high percentage of calcium from a variety of non-limestone rocks.

[0198] Example 2 In this example, the preferential precipitation of non-calcium components from a calcium-containing solution was demonstrated.

[0199] Test solutions of the following compositions were prepared by adding CaCl2 to the leachate produced in the same manner as in Example 1. The compositions were as follows:

[0200] [Table 2]

[0201] Heating the above solution (trace elements not listed) to 150°C for 2 hours precipitated a solid highly depleted in Ca and enriched in Fe and Al. These data indicate that the non-Mg, non-Ca components can be substantially removed by hydrolysis. The composition of the precipitant as determined by XRF was as follows:

[0202] [Table 3]

[0203] The composition of the precipitant was found to be highly concentrated in iron and aluminum components, with very small amounts of calcium and magnesium components, thus indicating that iron and aluminum can be selectively removed by heating the solution.

[0204] Example 3 In this example, the production of dicalcium silicate and tricalcium silicate from a non-limestone rock derived composition and extremely high chloride depletion were demonstrated.

[0205] CaCl2 was mixed with SiO2 (produced from leaching of anorthosite rock) in a CaCl2:SiO2 molar ratio of 3:1. The material was placed in a crucible and heated for 1 hour at 850°C, 1000°C, 1200°C, and 1500°C in sequence, using a steam atmosphere at all temperatures except 1500°C. Both dicalcium silicate and tricalcium silicate were produced in large quantities, as determined by X-ray diffraction (XRD) (below).

[0206] [Table 4]

[0207] It was also surprisingly shown that CaCl2 could be dechlorinated to greater than 99.5% as shown by XRF.

[0208] [Table 5]

[0209] Thus, this example demonstrates the production of a solid material containing dicalcium silicate and tricalcium silicate, as well as the depletion of chloride to levels well below Portland cement standards.

[0210] Example 4 Laboratory production of portland cement clinker by alternative routes.

[0211] The starting feedstock was a mixture of CaCl2, SiO2, Fe2O3, and Al2O3 with Ca-Si molar ratios ranging from 2.5 to 3.25, with the amount of Al2O3-Fe2O3 adjusted to meet the specific Portland cement / clinker requirements desired as the final product. The feedstock was subjected to a two-step high-temperature process to produce clinkered materials that met the various Portland cement chemical composition requirements depending on the starting ratios. The first step process was dechlorination. In dechlorination, the mixture was subjected to reaction with superheated steam (5% to 100% by volume) at temperatures ranging from 750°C to 1250°C. Additional dechlorination may be performed at higher temperatures, for example in the clinkering process. It should be noted that Al2O3 and Fe2O3 are not essential components for dechlorination and may be added later. The objective of dechlorination is to reduce the Cl content to less than 5% by weight, preferably less than 1% by weight. The dechlorinated product was then subjected to clinkering at temperatures ranging from 1400°C to 1600°C to produce a clinker that met the chemical, compositional, and performance requirements of the OPC standard. Clinkering of the dechlorinated product can also be carried out in the presence of water vapor similar to or greater than the moisture content in the combustion flue gas, potentially resulting in a clinker containing less than 0.01 wt% residual Cl.

[0212] General Laboratory Procedure for Dechlorination i. Samples of known purity CaCl2, SiO2, Al2O3 and Fe2O3 were dried in a muffle / box furnace at 300°C for 2 hours to ensure the starting materials were dry.

[0213] ii. The dried samples were weighed and mixed in the desired composition with Ca-Si molar ratios ranging from 2.5 to 3.25. The amounts of Al2O3 and Fe2O3 were calculated considering the theoretical mass losses during dechlorination.

[0214] iii. The samples were ball milled overnight to ensure homogeneity of chemical composition. The ball milled mixture was then used as the feed sample for dechlorination.

[0215] iv. The platinum crucible was weighed and the weighed feed sample in the crucible was dried at 300° C. for 2 hours to ensure dryness. The tube furnace was preheated to 300° C.

[0216] v. After 2 hours the sample + crucible was weighed and placed in a tube furnace.

[0217] vi. The tube furnace was then programmed to reach 850 °C at an incremental rate of about 10 °C / min. This first "soak" temperature could be in the range of 750-1250 °C depending on the experimental goals. Steam flow was initiated at about 750 °C-800 °C. Steam flow can be initiated earlier without adverse effects as long as T is above 300 °C.

[0218] The ramp rate can vary from 5 to 20 °C, but is often limited by the laboratory furnace and not necessarily by process requirements. Samples can be heated rapidly to about 700 °C to about 700 °C without adverse effects. Heating from about 700 °C to about 1000 °C can generally be done more slowly to allow time for the CaCl2 / SiO2 mixture to form a solid solution and react with H2O to dechlorinate and produce HCl(g). Heating at a ramp rate of 10 °C / min satisfies the slow melting requirement without prematurely melting the CaCl2 fraction before it can react with H2O(g) and SiO2(s).

[0219] vii. A peristaltic pump was used to maintain the flow rate of water to the steam generator so that the amount of water added during the course of the experiment was in stoichiometric excess.

[0220] viii. The heat treatment program typically consisted of soaks at 850°C for 60 minutes, 1000°C for 60 minutes, and 1100°C for 120 minutes. However, heat treatment cycle conditions are often varied. For example, the dechlorination reaction conditions were varied between 750 and 1250°C with various intermediate ramp and soak temperatures.

[0221] ix. After the reaction time at peak temperature, the water flow was stopped and the crucible was ramped down in the furnace at 10° C. / min. The crucible was removed at about 600° C. This step was done for safety and laboratory convenience. The sample itself can be removed from the furnace at the end of the peak temperature without ill effects.

[0222] x. Weigh the crucible containing the sample and then transfer the sample to an airtight scintillation vial.

[0223] General laboratory procedure for clinkering i. Weigh a platinum crucible and dry the weighed dechlorinated sample in the crucible at 300° C. for 2 hours to ensure that the sample was dry. Preheat a tube furnace to 300° C.

[0224] ii. After 2 hours, the sample + crucible was weighed and placed in a tube furnace.

[0225] iii. The tube furnace was then programmed to reach 1500°C-1600°C at a ramp rate of about 10°C / min. The clinkering temperature range can be 1400-1600°C. For grey OPC, 1450-1500°C is typical. For white OPC, 1500-1600°C is typical. The ramp rate is based on laboratory equipment limitations. Clinkering can be achieved by placing the sample directly into a furnace preheated at the clinkering temperature and / or the ramp rate may be higher or the initial furnace temperature may be higher.

[0226] iv. The steam / O2 flow was started at about 350°C. The steam concentration in the feed gas can vary from 0.5% to 10%. Also, instead of the steam / O2 mixture, combustion flue gas can be used as the source of steam and O2.

[0227] v. The heat treatment cycle typically consisted of a 5 hour soak at 1500°C. The clinkering time can vary, in some cases up to 15 minutes, depending on conditions.

[0228] vi. After the reaction time, the crucible was pulled out of the tube furnace and placed on a refractory brick and the temperature was quenched in air.

[0229] vii. The crucible containing the clinker sample was weighed and then transferred to an airtight scintillation vial.

[0230] The materials were tested by XRF and Bogue calculations were performed. Table 1 presents the results for various starting materials and final products.

[0231] [Table 6]

[0232] FIG. 14 shows exemplary optical micrographs of clinker samples taken in Test 1. Alite (C3S) is shown as the dark areas in both micrographs. The arrows in the right micrograph point to ferrite and aluminate phases. The arrow in the left micrograph points to one of many small brown belite (C2S) inclusions.

[0233] This example demonstrates that clinkers having various percentages of C3S, C2S, C3A, and C4AF, for example meeting ASTM standards for various types of cement, can be produced from calcium chloride, silica, aluminum oxide, and iron oxide starting materials.

[0234] Example 5 In this example, a supplemental cementitious material (SCM) was produced from rock. In one experiment, an SCM was produced that met the ASTM requirements for fly ash, and in another experiment, an SCM was produced that met the ASTM requirements for silica fume.

[0235] Figure 15 shows a simplified process flow diagram for leaching of Ca-bearing material. The process included receiving the material, crushing and grinding, leaching, liquid / solids separation, drying, and processing of the solids to meet ASTM standards. Each step is described in a subsection.

[0236] Preparation of Feed Materials The feed material (77.6% anorthite (CaAl2Si2O8), 3.4% quartz (SiO2), 1.2% muscovite or related mica KAl2 (AlSiO3)) ranges in size from 5 inches to several hundred microns. 10 Anorthosite from Greenland, Canada was received containing 0.01% kaolinite Al2Si2O5(OH)2, 0.4% kaolinite Al2Si2O5(OH)4, and 17.4% amorphous material. The as-received material was inspected for visible moisture content. If damp or wet, it was dried in a drying oven at 110°C. Material larger than 1000 microns was crushed to P80 in the 1200-1000 micron range. The raw rock was then ground to P80 in the 45-90 micron range. The initial composition of the prepared rock was then analyzed by X-ray fluorescence (XRF).

[0237] leaching Reagent grade hydrochloric acid (HCl) was used as the leaching reagent. Due to its corrosive nature, all reactor vessel construction materials consisted of borosilicate glass and Teflon. The reflux condenser was connected to a recirculating water cooler set at 15-20 °C for water and acid recovery. The heating mantle was connected to a temperature controller and a J-type thermocouple was used to measure the temperature inside the reactor. Leaching of the Ca-bearing raw rock was carried out as follows: 1. The target leaching conditions were 15-30% wt / wt HCl, 10-30% wt / v pulp density (weight of solids relative to the volume of leach solution), 6-24 hours, and 50-70% volumetric loading of the reactor vessel. The leaching conditions used to produce fly ash and silica fume were 20% wt / wt HCl, 27% pulp density (27 gm of raw rock for every 100 mL of leach solution). 2. Once the leaching parameters were defined, the required amount of raw rock was calculated and measured accurately to within 0.1-1 mg. The required amounts of raw acid and water were also determined. 3. The leaching reagent was added to the reactor vessel with slow stirring at 100-150 rpm. While stirring, the raw rock was slowly added to the reactor through the solids feed port. 4. The vessel was closed and the agitation was increased to 200-300 rpm for the reaction. Heating was started to the temperature target range of 100-120°C. Once the reaction mixture reached the target temperature, the reaction was allowed to continue for a predefined period of time. In case of fly ash, the period was 24 hours, after which the materials were separated. In case of silica fume, leaching was carried out for 24 hours in the first step, after which the residue was obtained, which was then leached again for another 4 hours at the same acid concentration and pulp density. At the end of the reaction, heating was stopped and the reaction mixture, i.e. the pulp consisting of pregnant leach liquor (PLS) and solids (residue), was allowed to cool to 60-70°C.

[0238] Solid / Liquid Separation The solid / liquid separation of the products is shown in FIG. 15 and proceeds as follows: 1. One end of the corrosion resistant tubing connected to the adapter was placed into the reaction vessel outlet port and into a corrosion resistant collection vessel. The reaction mixture was allowed to flow into the collection bottle, which was then filtered or centrifuged. 2. Centrifugation: a. The PLS pulp was evenly distributed into centrifuge bottles and inserted into the centrifuge rotor. b. The centrifuge was run for 5 to 10 minutes. c. The supernatant was collected and processed for physical property data collection (density, pH, volume, RmV) after which an aliquot was sent for chemical analysis. 3. Filtration a. The filtration assembly consisted of a filtration flask, a Buchner funnel, filter papers of various grades (3, 4, 5, 50), and a vacuum pump. b. The filter paper was placed in a Buchner funnel, wetted, and the pump was turned on to ensure a good seal. c. The pulp was added to the funnel and separation was carried out. The filtered pregnant leachate was collected and processed for physical property data collection (density, pH, volume, RmV) after which an aliquot was sent for chemical analysis. 4. The filter cake / centrifugation pellet was re-pulped by adding water to approximately 25-50% solids by volume and then another filtration or centrifugation step was performed. The pH of the filter cake was monitored so that the end of the filtration / centrifugation was indicated by a cake pH of about 6-7. 5. Collect the filter cake / solid pellet in a drying dish and record the wet weight.

[0239] Drying Prior to the drying solids process, the residual material collected from the S / L separation step was placed in a drying oven at 110 °C for 24-48 h. At the end of the drying process, the dry weight of the cake was recorded and the moisture content retained was calculated. The solids were deagglomerated using a mortar and pestle.

[0240] Analysis method Sample preparation Liquid Fraction Three streams were collected from the leaching: PLS, wash, and retentate, as shown in Figure 15. Aliquots of the PLS and wash fractions were analyzed by inductively coupled plasma optical emission spectroscopy (ICP-OES).

[0241] Solid fraction After collection, the residue was subjected to loss on ignition (LOI) analysis according to ASTM D7348. A fraction of the oxidized residue sample was subjected to lithium borate fusion, thereby producing glass beads, which were analyzed using X-ray fluorescence (XRF).

[0242] Generate SCM The specifications for silica fume and fly ash were provided by ASTM C1240 and C618, Tables 1 and 2, respectively. To meet the SCM specifications, the following procedures were carried out:

[0243] 1. 325 mesh ASTM sieves were calibrated according to ASTM C430 using NIST 46h OPC fineness standards. 2. Fineness tests were performed in triplicate on the residue samples. 3. Based on the fineness results, the grinding media and duration required to reach the required particle size were determined. 4. Take a grinding jar and add grinding media until it is 40-50% full. Add solids to approximately 1 / 2 inch above the surface of the media. 5. The jar containing the solids + media was placed on a ball mill and ground. 6. Repeat step 2 and inspection for size testing. 7. If necessary, steps 2-6 were repeated as necessary.

[0244] Testing of Supplementary Cementitious Materials (SCM) in accordance with ASTM C618 "Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete." The "fly ash" samples were evaluated for compliance with the standard physical and compositional requirements of ASTM C618.

[0245] Mixing ratio and results The analytical results of the chemical composition of the samples are shown in Table 2 (ASTM / C618). The proportions and flow rates of the test mortar samples are shown in Table 3. The SCM content was 20% by weight of its mixture with Portland cement (Reference: ASTM C618 and ASTM C311). The test results of the standard physical requirements of "fly ash" are shown in Table 4 (ASTM C618).

[0246] [Table 7]

[0247] [Table 8]

[0248] [Table 9]

[0249] Flow Rate (%), ASTM C1437 102 105 SCM samples of "Fly Ash" conform to the standard physical and compositional requirements for "Class F" fly ash as specified by ASTM C618.

[0250] Testing of Silica Fume in Accordance with ASTM C1240 "Standard Specification for Silica Fume Used in Cementitious Mixtures" Samples of "Silica Fume" were evaluated for compliance with the standard physical and compositional requirements of ASTM C1240.

[0251] Analytical results of the chemical composition of the samples are shown in Table 5 (ASTM C1240). The proportions and flow rates of the test mortar samples are shown in Table 6 (ASTM C1240 and ASTM C311). Test results of the standard physical requirements for "Silica Fume" are shown in Table 7 (ASTM C1240).

[0252] [Table 10]

[0253] [Table 11]

[0254] [Table 12]

[0255] Silica fume sample "Silica fume" conforms to the standard physical and chemical requirements specified by ASTM C1240.

[0256] This example demonstrates that various types of SCMs that meet industry standards can be produced from non-limestone starting materials, in this case rocks and / or minerals, and that the SCMs meet industry standards for composition and functionality.

[0257] As can be seen from the foregoing detailed description and the drawings and claims, those skilled in the art can make modifications and variations to the embodiments of the present invention without departing from the scope of the invention, which is defined in the following claims.

Claims

1. (i) processing a non-limestone material containing calcium and iron to provide particles within a desired size range; (ii) subjecting the particles to magnetic separation to remove iron-containing materials to produce particles depleted in iron-containing materials; (iii) contacting the depleted particles with a first acid to produce a calcium-depleted solid fraction and a first liquid fraction containing calcium; (iv) Producing a cement material from the liquid fraction. The method includes:

2. The method of claim 1, wherein the desired size range is 1 to 500 μm.

3. The method of claim 1, wherein the desired size range is 10 to 200 μm.

4. The method of claim 1, wherein the desired size range is 20 to 130 μm.

5. The method of claim 1, wherein the non-limestone material further comprises silicon and the calcium-depleted solid comprises silica.

6. The method of claim 1, wherein the non-limestone material comprises rocks and / or minerals.

7. The method of claim 6, wherein the rocks and / or minerals include basalt, igneous apatite, wollastonite, anorthosite, montmorillonite, bentonite, calcium-bearing feldspar, anorthite, diopside, pyroxene, pyroxene, mafleite, kamafleite, clinopyroxene, coulombite, coulombite, augite, pigeonite, margarite, calcium serpentine, garnet, scheelite, skarn, limestone, natural gypsum, apatite, fluorapatite, or any combination thereof.

8. The method of claim 1, wherein the first acid comprises hydrochloric acid (HCl).

9. The method of claim 8, wherein the first liquid fraction is contacted with a second acid comprising H2SO4 to produce CaSO4 solids.

10. The method of claim 9, wherein the non-limestone material comprises aluminum, and contacting the first liquid fraction with a second acid comprising H2SO4 produces a second liquid fraction comprising aluminum.

11. The method of claim 10, wherein the aluminum-containing second liquid fraction is contacted with HCl to precipitate AlCl 3 .

12. The method of claim 9, further comprising processing the CaSO 4 solids to produce a cement material, the processing comprising decomposing CaSO 4 to produce SO 2 .

13. The method of claim 12, wherein decomposing the CaSO 4 comprises pyrolyzing CaSO 4 with Al 2 O 3 , Fe 2 O 3 and SiO 2 to form ordinary Portland cement and SO 2 .

14. The method of claim 8, wherein the first liquid fraction comprises CaCl2, and the method further comprises dehydrating the first liquid fraction to produce solid CaCl2 from the first liquid fraction, and processing the solid CaCl2 to produce a cement material.

15. The method of claim 1, wherein the first liquid fraction is treated with a base to precipitate Ca(OH) 2 .

16. The method of claim 15, wherein the Ca(OH) 2 is processed to produce a cement material.

17. An apparatus for processing non-limestone materials containing calcium and iron, comprising: (i) a first processor configured to process the non-limestone material to produce particles within a desired size range; (ii) a second processor configured to subject the particles to magnetic separation to remove ferrous material and produce particles depleted in ferrous material; (iii) a third processor configured to form a cement material from the depleted particles; and wherein the first processor is operably connected to the second processor, and the second processor is operably connected to the third processor.

18. The apparatus described in claim 17, wherein the first processing device and the second processing device are identical.

19. The apparatus described in claim 17, wherein the third processor includes an extractor configured to contact the depleted particles with an acid to produce a first calcium-rich liquid fraction and a calcium-depleted solid fraction.

20. The apparatus of claim 19, wherein the leaching device is operably connected to a first precipitator configured to precipitate one or more solids from the first calcium-rich liquid fraction.

21. The first precipitator precipitates one or more solids from the first calcium-rich liquid fraction.

21. An apparatus as claimed in claim 20, configured to precipitate calcium-containing solids from the first calcium-rich liquid fraction to produce a calcium-depleted liquid fraction.

22. The apparatus of claim 20, wherein the first precipitator is operably connected to a source of strong acid for precipitating calcium-containing solids.

23. The apparatus of claim 20, wherein the first precipitator is operably connected to a base source for precipitating calcium-containing solids.

24. The apparatus of claim 20, wherein the first precipitator is configured to dehydrate a calcium-rich liquid fraction to produce a calcium-containing solid.

25. The apparatus of claim 21, further comprising a second precipitator operably connected to the first precipitator for precipitating one or more metal-containing solids from the calcium-depleted liquid fraction.