Isocyanate-functionalized organosilanes as adhesion promoters in sealant and primer compositions.

Abstract

The present invention relates to a method for sealing a substrate, which comprises optionally a step (1) of applying a primer composition and necessarily a step (2) of applying a sealant composition, the sealant composition being obtainable by mixing together components (A) and (B) of a 2K sealing system, comprising in (A) a thiol group containing polymer component (a1) and in (B) a component (b) suitable for curing the sealant composition by at least partially inducing a chemical transformation of the thiol group of component (a1), comprising at least one hydrolyzable group X, at least one NCO group and at least one carboxyl group X, ... The present invention relates to a process in which a spacer unit comprising a moiety MS containing at least one sulfur atom and arranged between the X and NCO groups is at least present as component (a2) in the sealant composition applied in step (2) if no step is performed, or at least present as a component in the primer composition applied in step (1) if step (1) is performed, to sealed substrates obtainable by this process, to a process for the use of said organosilane component to improve adhesion, to sealant compositions used in step (2), to such 2K sealing systems, and to the organosilane component itself.

Description

[Technical field]

[0001] The present invention relates to a method for sealing a substrate, which comprises optionally a step (1) of applying a primer composition and necessarily a step (2) of applying a sealant composition, the sealant composition being obtainable by mixing together components (A) and (B) of a 2K sealing system, comprising in (A) a thiol group containing polymer component (a1) and in (B) a component (b) suitable for curing the sealant composition by at least partially inducing a chemical transformation of the thiol group of component (a1), comprising at least one hydrolyzable group X, at least one NCO group and at least one carboxyl group X, ... The present invention relates to a process in which a spacer unit comprising a moiety MS containing at least one sulfur atom and arranged between the X and NCO groups is at least present as component (a2) in the sealant composition applied in step (2) if no step is performed, or at least present as a component in the primer composition applied in step (1) if step (1) is performed, to sealed substrates obtainable by this process, to a process for the use of said organosilane component to improve adhesion, to sealant compositions used in step (2), to such 2K sealing systems, and to the organosilane component itself. [Background technology]

[0002] Sealants are used in a wide range of applications, for example in the aerospace sector, but also widely in the automotive sector. They are furthermore used for sealing construction elements, for connecting metal sheets to existing structures, for example aircraft segments, and / or for corrosion protection where the corrosion protection layer of metal elements has been damaged or removed, for example in the region of holes. They may also perform a temporary transport function, for example during the transportation of structures to be mounted and which must then be provided with permanent supporting connection elements.

[0003] Silanes, particularly organosilanes, are known to act as adhesion promoters for a variety of substrates, especially polar surfaces such as metals and glass, but also ceramics and polymers. Silanes are compatible with many chemical systems, allowing them to be used in a variety of different materials, including sealant materials. Silanes, compared to other chemically different adhesion promoters such as phenolic resins or polyolefins, usually do not significantly affect the pH environment within the material in which they are utilized. This is particularly important in applications where ambient conditions, such as a constant pH environment, are important for the curing properties of the material, as is the case for sealants based on polysulfides and / or polythioethers. The use of silanes as adhesion promoters in such materials has the added advantage that they can be used with other adhesion promoters, for example polyolefins and / or organometallic compounds such as titanates. Typically, silanes used for this purpose have aliphatic and / or aromatic spacers (linkers) attached to functional groups such as amino, thiol, hydroxy, or epoxide groups, depending on the system in which the silane is used.

[0004] EP3023429A1 discloses certain cycloaliphatic OH-functional silanes for use as adhesion promoters and crosslinkers. CN104937054A discloses adhesion improvers that are reaction products of isocyanate-functional silanes with additional silanes that have functional groups reactive to isocyanate groups. WO2006 / 050915A1 discloses a method for coating metal surfaces utilizing an aqueous composition that contains at least one Si-containing component, such as an organosilane. US2019 / 0119539A1 discloses compositions that include combinations of different silanes, such as aminohydrocarbylalkoxysilanes, alkenylalkoxysilanes, and mercaptohydrocarbylalkoxysilanes. The compositions are useful as water-based primers.

[0005] WO 03 / 054049 A1 relates to isocyanate-functional silanes, prepared for example from the reaction of amino-functional organosilanes with low volatility polyisocyanates, for use as adhesion promoters in polyurethane compositions. WO 02 / 051954 A2 relates to 2K coating compositions containing compounds containing alkoxysilane groups and succinyl urea groups.

[0006] However, the sealant systems known in the prior art do not always provide sufficient adhesive properties, and the silanes known in the prior art do not always provide sufficient adhesion-promoting properties, especially for a variety of different substrates, in the field of sealants for the aviation industry, and in sealant compositions containing polymers with thiol groups, such as sealant compositions based on polysulfides and / or polythioethers. Moreover, the silanes known from the prior art, when incorporated into sealant compositions containing the aforementioned polymers with thiol groups, often lead to relatively poor processing properties, especially as far as undesirable viscosity changes, for example undesirable decreases in viscosity over storage time, are concerned. These disadvantageous properties are often observed in particular when amino-containing silanes are used as such or derived from amino-containing precursor silanes, such as the silanes disclosed in WO03 / 054049A1 and WO02 / 051954A2.

[0007] The functionalization of polymers with silanes is further known, for example, from US 2016 / 0319068 A1, EP 3293217 A1 and DE 19821356 A1, and US 2018 / 112026 A1. US 2016 / 0319068 A1 discloses polyester polyols containing esterified units, which are modified with amino-functional silanes. These polymers can be used as adhesion promoters for urethane systems. EP 3293217 A1 discloses silane-modified copolymers as adhesion improvers. US 2018 / 112026 A1 discloses modified polyisocyanates that can be obtained by reacting polyisocyanates based on 1,5-diisocyanatopentane with organosilanes, such as amino-functional organosilanes. DE 19821356 A1 discloses the preparation and use of silane-modified butyl rubber, for which purpose mercapto-functional silanes are used. However, the use of such modified polymers disclosed in these documents necessarily requires a step of pre-modifying the polymer before use in materials such as sealants, which is undesirable, at least from an economic point of view. Furthermore, pre-modifying the polymer limits the flexibility of the end user in terms of the freedom in formulating the material composition. As far as DE 19821356 A1 is concerned, the rubbers / polymers disclosed therein are not suitable for use as sealants, especially aircraft sealants, since they show at least poor resistance to non-polar solvents such as mineral oil-based fuels. This is particularly disadvantageous for sealants used for sealing the inside of aircraft fuel tanks.

[0008] Therefore, there is a need for sealing systems, compositions, and methods for sealing substrates that do not exhibit the above-mentioned drawbacks, especially when the substrate is a substrate used in the aircraft industry, such as a fuel tank.In particular, there is a need for sealing systems and compositions containing thiol-containing polymers that provide excellent adhesion properties to a variety of different substrates and surfaces, and for widely available adhesion promoters suitable for such systems and compositions that are easy and economically advantageous to incorporate into these systems and compositions without imparting processing properties. [Prior art documents] [Patent documents]

[0009] [Patent Document 1] EP3023429A1 [Patent Document 2] CN104937054A [Patent Document 3] WO2006 / 050915A1 [Patent Document 4] US2019 / 0119539A1 [Patent Document 5] WO03 / 054049A1 [Patent Document 6] WO02 / 051954A2 [Patent Document 7] US2016 / 0319068A1 [Patent Document 8] EP3293217A1 [Patent Document 9] DE19821356A1 [Patent Document 10] US2018 / 112026A1 Summary of the Invention [Problem to be solved by the invention]

[0010] Therefore, the object of the present invention is to provide a sealing system and a sealing composition containing a thiol group-containing polymer, and a method for sealing a substrate using these systems and compositions, which not only provide excellent adhesion properties to a variety of different substrates and surfaces, especially when the substrate is a substrate used in the aircraft industry, such as a fuel tank, but also allow the use of widely available adhesion promoters suitable for such systems and compositions, which make the incorporation of these adhesion promoters easy and economically advantageous, and do not show any drawbacks as far as the processability of these systems and compositions is concerned.At the same time, the sealed substrate, such as the sealed interior of a fuel tank, should show excellent resistance to liquid media, especially fuel. [Means for solving the problem]

[0011] This object has been solved by the subject matter of the present claims and the preferred embodiments thereof disclosed herein, ie the subject matter described herein.

[0012] The first subject of the present invention is a process for producing a medicament comprising at least step (2) and optionally step (1), i.e. (1) applying a primer composition at least partially to a surface of an optionally precoated substrate to at least partially form a primer film on said surface; (2) applying a sealant composition at least partially to the surface of the optionally precoated substrate if optional step (1) is not performed, or to the primer film if optional step (1) is performed; A method for sealing an optionally precoated substrate comprising: wherein the sealant composition is different from the primer composition optionally applied in step (1) and is obtainable by mixing together the components of a sealing system, said sealing system being a two-component (2K) sealing system comprising two components (A) and (B) which are separate from each other, component (A) of the sealing system comprises at least one polymer component (a1) containing two or more thiol groups selected from polyether, polythioether, polysulfide, polythioether-sulfide components and mixtures thereof; and component (B) of the sealing system comprises at least one component (b) suitable for curing the sealant composition by at least partially inducing chemical transformation of two or more thiol groups of component (a1); The following ingredients: (i) at least one hydrolyzable group X; (ii) at least one isocyanate group, and (iii) a spacer unit disposed between the at least one hydrolyzable group X and the at least one isocyanate group, the spacer unit comprising at least one moiety MS that comprises at least one sulfur atom; At least one organosilane component containing Characterized in that it is at least present as component (a2) in component (A) of the sealing system used to prepare the sealant composition applied in step (2) when optional step (1) is not performed, or at least present as a component in the primer composition applied in step (1) when step (1) is performed.

[0013] A further subject of the invention are encapsulated substrates obtainable by the process according to the invention.

[0014] A further subject of the present invention is the use of an organosilane component as defined above and / or below, which when incorporated in a primer composition as defined above and / or below, such as a primer composition used in step (1) of the process of the invention, or a sealant composition as defined above and / or below, such as a sealant composition used in step (2) of the process of the invention, in particular as component (A) of the sealing system used to prepare said sealant composition, improves the adhesion of the primer composition or sealant composition to said substrate when applied to at least a portion of the surface of an optionally precoated substrate.

[0015] A further subject of the present invention is a sealant composition as defined above and / or below, obtainable by mixing with one another components (A) and (B) of a sealing system as defined above and / or below, said component (A) of the sealing system comprising at least one organosilane component as defined above and / or below.

[0016] A further subject of the present invention is a two-component (2K) sealing system comprising components (A) and (B) as defined above and / or below, which are distinct from one another, component (A) of said sealing system comprising at least one organosilane component as defined above and / or below.

[0017] A further subject of the present invention is an organosilane component as defined above and / or below, optionally incorporated in a primer composition as defined above and / or below.A further subject of the present invention is thus a primer composition as defined above and / or below, comprising at least an organosilane component as defined above and / or below.

[0018] Particularly surprisingly, it has been found that the aforementioned organosilane components, when incorporated into sealant and / or primer compositions, represent widely applicable adhesion promoters, especially when used in the method of the present invention. It has been found that said adhesion promoters can be easily incorporated into various sealant compositions, and also into suitable primer compositions that are applied prior to application of the actual sealant composition to the substrate surface. It has been found that excellent adhesion to various substrates, including metal substrates and precoated substrates, such as metal substrates having at least one organic coating layer, can be achieved, and that the adhesion promoters are effectively chemically incorporated into the polymer matrix and network formed after application. Even more surprisingly, it has been found that the organosilane components function as linkers between the substrate surface and the applied primer / sealant.

[0019] Furthermore, it has been found, particularly surprisingly, that one or more hydrolyzable groups X of the organosilane component, such as alkoxy groups / silyl ether groups, mediate adhesion to the surface to which the organosilane component is applied, in particular by reacting with OH groups in a condensation reaction, while at the same time at least one NCO group of the organosilane component can react with a thiol group of component (a1) of the sealant composition. In particular, it has been found that a significant improvement in adhesion in the sealant and / or primer materials used is the result of at least one moiety MS present in the spacer unit of the organosilane component. It is hypothesized that the presence of at least one moiety MS has an additional adhesion-promoting effect based on the formation of hydrogen bonds. It has been found that the use of conventional organosilanes, such as (3-glycidyloxypropyl)trimethoxysilane and (3-mercaptopropyl)-trimethoxysilane, and organosilanes that do not contain the moiety MS containing at least one sulfur atom, such as organosilanes prepared from diisocyanates and amino-functional silane precursors, such as bis[3-(trimethoxysilyl)propyl]amine, do not have the desired effect of significantly improving adhesion.

[0020] Moreover, it has surprisingly been discovered that the aforementioned organosilane components provide great flexibility and latitude in formulating sealant and primer compositions.

[0021] In particular, no pre-modification step is required to modify any of the polymeric components of the sealant composition to improve adhesion; instead, the aforementioned organosilane components can simply be incorporated into the various sealant compositions themselves.

[0022] Furthermore, it has surprisingly been found that sealant and primer compositions comprising the aforementioned organosilane components are particularly applicable in the aircraft and aerospace fields, for example as aircraft sealants, particularly for sealing the interior of aircraft fuel tanks, and that the corresponding sealed substrates exhibit excellent resistance to liquid media, such as organic solvents and fuels, particularly non-polar solvents such as mineral oil-based fuels.

[0023] Moreover, it has surprisingly been discovered that sealant and primer compositions including the aforementioned organosilane components can provide sealed substrates that exhibit excellent physical and mechanical properties, such as tensile strength.

[0024] Finally, it has been surprisingly found that sealant and primer compositions containing the aforementioned organosilane components exhibit excellent processing properties, and in particular excellent viscosity characteristics, since no undesirable viscosity changes, such as an undesirable decrease in viscosity, are observed over storage time. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0025] The term "comprising" in the sense of the present invention, for example in relation to a sealant composition, preferably has the meaning "consisting of". For example, in relation to a sealant composition, in addition to any essential components present therein, it is also possible for one or more of the further optional components specified below to be included therein. All components may in each case be present in their preferred embodiments as specified below.

[0026] The proportions and amounts in wt% (mass%) of any constituents given below present in the respective components of the sealing system add up to 100% by weight in each case relative to the total weight of the respective component.Similarly, the proportions and amounts in wt% (mass%) of any constituents given below present in the sealant or primer composition add up to 100% by weight in each case relative to the total weight of the respective composition.

[0027] Method for sealing optionally pre-coated substrates A first subject of the invention is a method for encapsulating an optionally precoated substrate, comprising at least step (2) and optionally also step (1).

[0028] The at least one organosilane component is at least present as component (a2) in component (A) of the sealing system used to prepare the sealant composition applied in step (2) if optional step (1) is not performed, or is at least present as a component in the primer composition applied in step (1) if step (1) is performed.

[0029] Preferably, the organosilane component is present in component (A) used to prepare the sealant composition applied in step (2) and is not present in the primer composition optionally applied in step (1). Alternatively, but also preferably, the organosilane component is not present in component (A) used to prepare the sealant composition applied in step (2), but is present in the primer composition applied in step (1). In this case, step (1) is necessarily performed. Further alternatively, but also preferably, the organosilane component is present in component (A) used to prepare the sealant composition applied in step (2) and is also present in the primer composition optionally applied in step (1).

[0030] Preferably, the organosilane component is at least present in component (A) used to prepare the sealant composition applied in step (2). In particular, the organosilane component is present in component (A) used to prepare the sealant composition applied in step (2) and is not present in the primer composition optionally applied in step (1).

[0031] Optional step (1) and primer composition According to optional step (1), the primer composition is at least partially applied to a surface of the optionally precoated substrate to at least partially form a primer film on said surface. Any type of contact may be used to carry out step (1), such as dipping, brushing and / or spraying.

[0032] Optional step (1) is preferably carried out using a 1K-compressed air bearing cartridge device equipped with a 1K-low pressure or 1K-high pressure supply system, or it may be carried out manually.

[0033] Step (1) is preferably carried out at a temperature in the range of 0 to 60° C., more preferably 5 to 45° C. In particular, heating is not carried out.

[0034] Base material Suitable substrates are metal substrates, but plastic substrates, such as polymeric substrates and / or fiber-based composites, can also be used. Preferred substrates are those available in the aerospace industry, such as fuel tanks. Preferably, the sealed surface in this case is the inner surface of a fuel tank.

[0035] Suitable metal substrates for use according to the present invention are any substrates commonly used and known to those skilled in the art. The substrates for use according to the present invention are preferably metal substrates, including steel substrates. However, most preferred are aluminum and / or aluminum alloy substrates.

[0036] Preferably, when the substrate is a plastic substrate, thermoplastic polymers are used.Suitable polymers are polyesters, including polymethyl (meth)acrylate, polybutyl (meth)acrylate, polyethylene terephthalate, polybutylene terephthalate, polyvinylidene fluoride, polyvinyl chloride, polycarbonate and polyvinyl acetate, polyamides, polyolefins, such as polyethylene, polypropylene, polystyrene, and also polybutadiene, polyacrylonitrile, polyacetal, polyacrylonitrile-ethylene-propylene-diene-styrene copolymer (A-EPDM), ASA (acrylonitrile-styrene-acrylic acid ester copolymer) and ABS (acrylonitrile-butadiene-styrene copolymer), polyetherimide, phenolic resin, urea resin, melamine resin, alkyd resin, epoxy resin, polyurethanes, including TPU, polyetherketone, polyphenylene sulfide, polyether, polyvinyl alcohol, and mixtures thereof.Particularly preferred are polycarbonates and poly(meth)acrylates.

[0037] However, fiber-based composites, such as carbon fiber composites, may also be used as substrates.

[0038] The substrate used may be subjected to a pretreatment leading to a pre-coating. For example, an epoxy-based coating may be applied before the optional steps (1) and (2) are carried out. Preferably, the substrate used has at least one preferably cured coating layer, for example an epoxy-based coating layer, before the optional steps (1) and (2) are carried out.

[0039] Primer Composition The at least one organosilane component is at least present as a component in the primer composition applied in step (1), if step (1) is performed.

[0040] The organosilane component contains (i) at least one hydrolyzable group X, (ii) at least one isocyanate group, and (iii) a spacer unit disposed between the at least one hydrolyzable group X and the at least one isocyanate group, said spacer unit comprising at least one moiety MS as described above.

[0041] The organosilane component that may be present in the primer composition applied in step (1) is described in further detail below with respect to its optional presence as component (a2) in the sealant composition applied in step (2). The relevant disclosure regarding component (a2) applies equally when the organosilane component is present in the primer composition.

[0042] Preferably, the organosilane component, at least when present as a component in the primer composition applied in step (1), is present therein in an amount in the range of 0.10 to 15.0 mass %, preferably 0.20 to 12.5 mass %, more preferably 0.30 to 10.0 mass %, even more preferably 0.40 to 7.5 mass %, and still more preferably 0.50 to 6.0 mass %, in each case relative to the total mass of the primer composition.

[0043] The primer composition is different from the sealant composition applied in step (2). The primer composition may preferably contain each of the components (a3)-(a6) identified and discussed below in connection with the sealant composition. Preferably, the primer composition does not contain any component (a1), i.e., does not contain any polymeric component containing two or more thiol groups selected from polyether, polythioether, polysulfide, polythioether-sulfide components and mixtures thereof. Preferably, the primer composition does not contain any component (b), and in particular does not contain any components (b1)-(b4).

[0044] Preferably, the primer composition is an organic solvent(s)-based (solvent-based, non-aqueous) composition. The term "solvent-based" or "non-aqueous" is preferably understood in this respect for the purposes of the present invention to mean that the organic solvent(s) are present as the solvent(s) and / or as the diluent(s) and as the main component of any solvent and / or diluent present in the primer composition. Preferably, the organic solvent(s) are present in an amount of at least 35% by weight, relative to the total weight of the primer composition. A solvent-based primer composition preferably comprises a fraction of organic solvent(s) of at least 40 or 45% by weight, more preferably at least 50 or 55% by weight, very preferably at least 60 or 65% by weight, in each case relative to the total weight of the composition. As organic solvent, any conventional organic solvent known to the skilled person can be used. The term "organic solvent" is known to the skilled person, in particular from Council Directive 1999 / 13 / EC of 11 March 1999. Examples of such organic solvents include heterocyclic, aliphatic, or aromatic hydrocarbons, monohydric or polyhydric alcohols, especially ethanol and / or propanol, ethers, esters, ketones, xylene, butanol, ethyl glycol and butyl glycol and their acetates, butyl diglycol, diethylene glycol dimethyl ether, cyclohexanone, methyl ethyl ketone, methyl isobutyl ketone, acetone, isophorone, or mixtures thereof. The solvent-based composition is preferably free or essentially free of water. The term "essentially" in this context preferably means that water is not intentionally added when preparing the composition.

[0045] Preferably, the primer composition comprises at least 40 or 45% by weight, more preferably at least 50 or 55% by weight, very preferably at least 60% by weight of the non-alcoholic organic solvent(s) fraction, in each case relative to the total weight of the composition. Most preferred are aromatic hydrocarbons such as xylene and / or aliphatic hydrocarbons such as gasoline ethers.

[0046] Preferably, the primer composition comprises an alcohol organic solvent(s) fraction of 0 to 30% by weight, more preferably 0 to 25% by weight and very preferably 0 to 20% by weight, in each case relative to the total weight of the composition. Most preferred are isopropyl alcohol, butanol and / or methoxypropanol.

[0047] In addition to at least one organosilane component, the primer composition may contain, and preferably contains, at least one further adhesion promoter, such as at least one further organosilane different from the aforementioned organosilane components. Examples include, for example, (3-aminopropyl)trimethoxysilane, (3-aminopropyl)triethoxysilane, N-2-aminoethyl-3-aminopropyltrimethoxysilane, (3-mercaptopropyl)trimethoxysilane, (3-mercaptopropyl)triethoxysilane, (3-glycidyloxypropyl)trimethoxysilane and / or (3-glycidyloxypropyl)triethoxysilane, vinyltrimethoxysilane. Additionally or alternatively, other adhesion promoters, such as titanates, such as titanium acetylacetonate (TAA) and / or Ti-n-butanolate (TnBt) and / or isopropyl titanate, and for example zirconates, may be used. When present, the additional adhesion promoter is preferably present in the primer composition in an amount of 0 to 7.5 wt.%, more preferably 0 to 6.5 wt.%, especially 0 to 5.0 wt.%, based on the total weight of the composition. Most preferably, at least one additional titanate and / or zirconate is present in one of the aforementioned amounts.

[0048] Step (2): Sealant composition and sealing system According to step (2), the sealant composition is applied at least partially to the surface of the optionally precoated substrate if optional step (1) is not performed, or to the primer film if optional step (1) is performed.

[0049] To carry out step (2), any type of contact may be used, such as extrusion brushing and / or spraying. Step (2) is preferably carried out at a temperature in the range of 0 to 60° C., more preferably 5 to 45° C. In particular, no heating is carried out.

[0050] Preferably, step (2) is carried out using a 2K-compressed air bearing cartridge device equipped with a 2K-low pressure or 2K-high pressure supply system, or it may be carried out manually.

[0051] Sealant compositions and sealing systems The sealant composition, different from the primer composition optionally applied in step (1), can be obtained by mixing together the components of the sealing system, said sealing system being a two-component (2K) sealing system comprising, preferably consisting of, two components (A) and (B) that are separate from each other. For example, the components (A) and (B) of the sealing system can be stored separately until they are mixed together to prepare the sealant composition.

[0052] Each of the two components (A) and (B) of the sealing system may contain water and / or at least one organic solvent, however it is also possible, and even preferred, that no organic solvent and / or water is present therein.

[0053] The amount of water present in component (A) is preferably less than 3.0% by weight, more preferably less than 2.0% by weight, even more preferably less than 1.0% by weight, and still more preferably less than 0.5% by weight, in each case relative to the total weight of component (A).

[0054] When at least one component (b1) and / or at least one component (b3) and / or at least one component (b4) are present in each case as component (b) in (B), the amount of water present in component (B) is preferably less than 3.0% by weight, more preferably less than 2.0% by weight, even more preferably less than 1.0% by weight, and even more preferably less than 0.5% by weight, in each case relative to the total weight of component (B). Components (b1), (b3) and (b4) are defined below.

[0055] When at least one component (b2), such as manganese dioxide, is present as component (b) in component (B), the amount of water present in component (B) is preferably less than 8.5% by weight, more preferably less than 7.5% by weight, even more preferably less than 7.0% by weight, and even more preferably less than 6.0% by weight, in each case relative to the total weight of component (B). Component (b2) is defined below.

[0056] If at least one organic solvent is present, in particular if the sealant composition is a sprayable composition, the organic solvent(s) are preferably present in an amount of up to 70% by weight or up to 65% by weight, relative to the total weight of the sealant composition. In this case, the sealant composition preferably comprises an organic solvent(s) fraction of up to 60% by weight, in each case relative to the total weight of the composition. Alternatively, if at least one organic solvent is present, in particular if the sealant composition is not a sprayable composition, the organic solvent(s) are preferably present in an amount of up to 10% by weight, relative to the total weight of the sealant composition. The sealant composition in this case preferably comprises an organic solvent(s) fraction of up to 7.5% by weight, more preferably up to 5% by weight, in each case relative to the total weight of the composition. Any conventional organic solvent known to those skilled in the art can be used as organic solvent. The term "organic solvent" is known to those skilled in the art, in particular from Council Directive 1999 / 13 / EC of 11 March 1999. Examples of such organic solvents include heterocyclic, aliphatic or aromatic hydrocarbons, mono- or polyhydric alcohols, in particular ethanol and / or propanol, ethers, esters, ketones, xylene, butanol, ethyl glycol and butyl glycol and their acetates, butyl diglycol, diethylene glycol dimethyl ether, cyclohexanone, methyl ethyl ketone, methyl isobutyl ketone, acetone, isophorone, or mixtures thereof. The solvents present may be identical or different from one another.

[0057] Component (A) Component (a1) Component (A) of the sealing system comprises at least one polymer component (a1) containing two or more thiol groups (mercapto groups) selected from polyether, polythioether, polysulfide, polythioether-sulfide components and mixtures thereof, preferably selected from polythioether, polysulfide, polythioether-sulfide components and mixtures thereof, more preferably selected from polythioether, polysulfide components and mixtures thereof, in particular selected from polysulfide components.

[0058] The terms "polymer" and "polymeric" are known to those skilled in the art and, for the purposes of the present invention, include polyadducts, polymerization products and polycondensates. The term "polymer" includes both homopolymers and copolymers.

[0059] Due to the presence of the thiol group, (a1) is necessarily a sulfur atom-containing component. The thiol group of (a1) can be chemically reacted with component (b) or a part thereof, for example with a suitable functional group thereof. For example, when component (b1) is present as component (b), its epoxide group can be reacted to form at least one of a hydroxythioether, a hydroxythioether sulfide and / or a hydroxysulfide moiety. For example, when component (b2) is present as component (b), for example as containing manganese oxide, a S-S bond is formed.

[0060] Preferably, the polymer component (a1) contains a terminal thiol group. Component (a1) may be branched or linear. Preferably, the polymer component (a1) is liquid at ambient conditions (18-23° C., 50% relative humidity).

[0061] Suitable polymer components for use as (a1) are disclosed, for example, in US 2004 / 097643 A1 and WO 2016 / 128548 A1 and WO 2015 / 014876 A2.

[0062] At least one polythioether, when used as (a1), is preferably a liquid (at ambient conditions) polythioether. The polythioether may contain up to about 50 mol% of disulfide groups in the molecule. The respective polymers may then be named polythioether sulfides. Preferred compounds of this type are described in WO2015 / 014876A2.

[0063] Preferably, the polymer component (a1) has a number average molecular weight in the range of 500 to 10000 g / mol, more preferably 900 to 5000 g / mol. Most preferred, especially when (a1) is at least one polysulfide, is a number average molecular weight in the range of 2500 to 6000 g / mol, more preferably 3300 to 5000 g / mol. Examples of such polymers include the polysulfides commercially available, for example, as Thioplast® G131, Thioplast® G10, Thioplast® G12, Thiokol® LP32 and / or Thiokol® LP12. Also preferred are polymer components (a1) having a number average molecular weight in the range of 500 to 2500 g / mol, more preferably 700 to 2000 g / mol or 800 to 1200 g / mol. In this case, examples of such polymers include the polysulfides commercially available, for example, as Thiokol® LP3, Thioplast® G4 or Thioplast® G44.

[0064] Optionally, if at least two components (a1) with different number average molecular weights are present in component (A): long chain polymers, in particular with a number average molecular weight in the range of 2500 to 6000 g / mol, particularly preferably in the range of 3300 to 5000 g / mol, may be present in addition to short chain polymers, in particular with a number average molecular weight in the range of 500 to 2500 g / mol, particularly preferably in the range of 800 to 1500 g / mol. Optionally, at least one of the aforementioned short chain polymers used in combination with at least one of the aforementioned long chain polymers may be replaced by at least one polymeric, oligomeric or monomeric mercaptan, preferably solid or liquid, having three thiol groups and having a number average molecular weight in the range of 160 to 1200 g / mol. Alternatively, said mercaptan may be further added to the combination of at least one short chain polymer with at least one long chain polymer. Examples of such suitable mercaptans are thiocyanuric acid (1,3,5-triazine-2,4,6-trithiol) and benzene-1,3,5-trithiol (1,3,5-trimercaptobenzene). If the mercaptan used is non-polymeric, it formally represents constituent (a6) of component (A). Preferably, the at least one mercaptan, if present, is present in an amount ranging from 0.05 to 3.0% by weight, relative to the total weight of component (A).

[0065] The sulfur-containing polymer component (a1) preferably has a mercaptan content, referring to reactive SH-groups, in the range of 0.5-10.0% by weight, more preferably 0.8-8.0% by weight, in particular 1.2-7.0% by weight, based on the total weight of (a1). The mercaptan content can be determined by direct titration of the SH-terminated polymer with iodine solution. The polymer is dissolved in a solvent mixture consisting of 40% by volume of pyridine and 60% by volume of benzene and titrated with benzene-iodine solution while stirring until a weak yellow color remains.

[0066] Preferably, component (a1) has a total sulfur content in the range of from 1 to 50% by weight, more preferably from 5 to 45% by weight, especially from 12 to 36% by weight.

[0067] Preferably, component (a1) has an average functionality of reactive end groups of mercapto groups per molecule in the range of 1.5 to 2.5 or 1.9 to 2.2. Functionality refers to the average number of mercapto groups per molecule. It is calculated as the ratio of molecular weight to equivalent weight and is determined by NMR.

[0068] Preferably, component (a1) has an average glass transition temperature T in the range of -80 to -30 ° C. or -60 to -40 ° C., measured according to the AITM1-0003 Airbus Industrie test method of June 1995. g has.

[0069] Preferably, component (A) and the sealant composition itself does not include any components that contain (meth)acrylate groups (methacrylate groups and / or acrylate groups).

[0070] Preferably, component (a1) is present in the sealant composition obtained after mixing together components (A) and (B) of the sealing system in an amount in the range of 50 to 95% by weight, based on the total weight of the sealant composition.

[0071] Constituent (a2) The at least one organosilane component is at least present as component (a2) in component (A) of the sealing system used to prepare the sealant composition applied in step (2) if optional step (1) is not performed.

[0072] Preferably, the organosilane component, at least when present as component (a2) in component (A) of the sealing system used to prepare the sealant composition applied in step (2), is present in (A) in an amount in the range of 0.05 to 10.0 mass %, more preferably 0.10 to 7.5 mass %, still more preferably 0.15 to 7.5 mass %, even more preferably 0.20 to 5.0 mass %, still more preferably 0.25 to 4.5 mass %, in each case relative to the total mass of component (A).

[0073] Preferably, the organosilane component, when at least present as component (a2) in component (A) of the sealing system used to prepare the sealant composition applied in step (2), is present in (A) in an amount in the range of 0.02 to 7.5% by weight, preferably 0.10 to 7.0% by weight, more preferably 0.20 to 6.5% by weight, even more preferably 0.40 to 6.0% by weight, still more preferably 0.50 to 5.5% by weight, in each case relative to the total weight of the sealing composition obtainable by mixing together at least components (A) and (B) of the sealing system.

[0074] The organosilane component contains (i) at least one hydrolyzable group X, (ii) at least one isocyanate group, and (iii) a spacer unit disposed between the at least one hydrolyzable group X and the at least one isocyanate group, said spacer unit comprising at least one moiety MS, at least one moiety MS comprising at least one sulfur atom and preferably selected from the group consisting of thiocarbamate, thiourea, thioester, thioketo, thiourethane and thioamide moieties. Each of the moieties MS is preferably a divalent moiety present within the spacer unit. The term thiocarbamate preferably includes O-thiocarbamate (-OC(=S)-N-) and S-thiocarbamate (-S-(C=O)-N-). Preferably, the thiocarbamate moiety is an S-thiocarbamate moiety. Thus, preferably, the moiety MS contains at least one divalent -C(=X)- group, where X is a chalcogen atom selected from oxygen and sulfur. Preferably, the organosilane component contains exactly one moiety MS.

[0075] Preferably, the organosilane component comprises at least two, preferably at least three, hydrolyzable groups X, preferably an alkoxy group. The hydrolyzable groups X may be identical to each other or at least two of these groups may be different from each other. Preferably, the hydrolyzable groups X are alkoxy groups, in particular C1-C4 alkoxy groups. Particularly preferred are methoxy, ethoxy, n-propoxy, iso-propoxy, n-butoxy, sec-butoxy and tert-butoxy groups. Most preferred are ethoxy and methoxy groups.

[0076] The organosilane component can be monomeric, oligomeric or polymeric, preferably non-polymeric, and more preferably monomeric.

[0077] Preferably, at least one organosilane component has a number average molecular weight in the range of 200 to 2000 g / mol, more preferably 250 to 1800 g / mol, even more preferably 300 to 1500 g / mol, and still more preferably 350 to 650 g / mol.

[0078] Preferably, the spacer unit located between at least one hydrolyzable group X and at least one isocyanate group and containing at least one moiety MS is a trivalent or divalent, more preferably a divalent, non-hydrolyzable organic residue, preferably aliphatic, including alicyclic, heteroaliphatic, including heteroalicyclic, and / or aromatic, including heteroaromatic. The residue is preferably C1-C 20 Aliphatic group, C1~C 20 Heteroaliphatic groups, C3-C 20 Alicyclic groups, 3- to 20-membered heteroalicyclic groups, 5- to 20-membered aryl or heteroaryl groups, C 1~10 C3-C bonded via aliphatic groups 20 Alicyclic group, C 1~10 A 3- to 20-membered heteroalicyclic group bonded via an aliphatic group, C 1~10The moiety MS is further disposed within each of these residues. Preferably, the spacer unit has a chain length separating at least one hydrolyzable group X and at least one isocyanate group of at least 6 carbon and / or heteroatoms, and preferably includes at least one atom of the moiety MS within the chain.

[0079] Preferably, at least one moiety MS of the spacer unit of the organosilane component represents a thiocarbamate and / or thiourea moiety. Preferably, the thiocarbamate moiety is an S-thiocarbamate moiety.

[0080] Preferably, at least one organosilane component contains exactly one isocyanate group.

[0081] Preferably, the at least one organosilane component is preferably obtainable from the reaction of at least one diisocyanate and / or polyisocyanate with at least one organosilane precursor comprising at least one functional group reactive towards isocyanate groups, said at least one functional group reactive towards isocyanate groups being preferably a thiol group. Diisocyanates have exactly two NCO-groups, whereas polyisocyanates have more than two NCO-groups. Suitable polyisocyanates are, for example, isocyanurates, such as isophorone diisocyanate (IPDI) and HMDI (hexamethylene diisocyanate) trimer. Suitable diisocyanates are aliphatic and cycloaliphatic diisocyanates, such as isophorone diisocyanate (IPDI) and HMDI (hexamethylene diisocyanate), HMDI and / or IPDI uredione and / or allophanate, and hydrogenated MDI (methylene diphenyl isocyanate). Aromatic diisocyanates such as TDI and XDI are also suitable. However, the use of aliphatic and cycloaliphatic diisocyanates is preferred.

[0082] Preferably, the at least one organosilane component can be obtained by reacting at least one diisocyanate with at least one organosilane precursor containing at least one functional group reactive to isocyanate groups, said at least one functional group reactive to isocyanate groups being preferably a thiol group, especially when at least one diisocyanate and at least one organosilane precursor are used in approximately equimolar amounts, respectively.Suitable diisocyanates are aliphatic and cycloaliphatic diisocyanates, such as isophorone diisocyanate (IPDI) and HMDI (hexamethylene diisocyanate).Aromatic diisocyanates such as TDI and XDI are also suitable.However, the use of aliphatic and cycloaliphatic diisocyanates is preferred.

[0083] Preferably, the at least one organosilane component is obtainable from the reaction of at least one, preferably aliphatic and / or cycloaliphatic diisocyanate with at least one organosilane precursor comprising at least one thiol group as a functional group reactive towards isocyanate groups.

[0084] The at least one organosilane precursor is preferably a monosilane, preferably having at least two, particularly preferably three, hydrolyzable groups X, and / or at least one bis(silane), preferably having at least four, particularly preferably six, hydrolyzable groups X.

[0085] Preferably, at least one organosilane precursor represented by the general formula (I) and / or (II) is used for reaction with at least one diisocyanate, Si(X) 4-y (R) y , (I), Si(X) 3-z (T) z -(RA)-Si(X) 3-z (T) z (II), In the case of the general formula (I), Each X is independently a hydrolyzable group, and preferably each X is independently O-C 1~4 alkyl, The parameter y is an integer ranging from 1 to 3, but is at least 1, and preferably exactly 1; and R is a non-hydrolyzable organic group, at least one of the groups R contains at least one functional group that is reactive towards isocyanate groups, in particular at least one thiol group, And in the case of the general formula (II), X is, in each occurrence independently of one another, a hydrolyzable group and preferably, in each occurrence independently of one another, O-C 1~4 -alkyl, R A represents a divalent non-hydrolyzable organic group containing at least one functional group reactive towards isocyanate groups, in particular at least one thiol group, the parameter z is in each case an integer ranging from 0 to 3, preferably 0 in each case, and T is a non-hydrolyzable organic group different from the group (RA) and preferably does not have a functional group that is reactive towards an isocyanate group.

[0086] Optional components (a3) ​​and (a4) Component (A) may additionally contain at least one filler (a3) ​​and / or at least one pigment (a4).

[0087] The term "filler" is known to the skilled artisan, for example from DIN 55943 (date: October 2001). "Fillers" for the purposes of the present invention are preferably constituents that are substantially, preferably completely insoluble in the medium that surrounds them, such as each of the components (A) and (B) and the sealant composition, and are used in particular to adjust the viscosity and thixotropy of the components and the sealant composition, to adjust the specific density of the cured sealant, and / or to increase the mechanical properties of the cured sealant. "Fillers" in the sense of the present invention have a refractive index that differs from "pigments", the refractive index of fillers being less than 1.7, while the refractive index of pigments is 1.7 or higher. Preferably, "fillers" for the purposes of the present invention are inorganic and / or organic fillers. Examples of inorganic fillers are chalk and talcum. Examples of organic fillers are powders prepared from heat-resistant polymers, such as polyamides, polysulfones, polyphenylene sulfides, polyether ketones and polymer hollow spheres.

[0088] Preferably, the amount of filler present in component (A) of the sealing system is in the range from 0 to 55.0% by weight, more preferably in the range from 0 to 50.0% by weight, even more preferably in the range from 0 to 45.0% by weight, still more preferably in the range from 0 to 40.0% by weight, also more preferably in the range from 0 to 35.0% by weight or 0 to 30.0% by weight and in particular in the range from 0 to 25.0% by weight, in each case relative to the total weight of component (A).

[0089] Preferably, the amount of any pigment present in component (A) of the sealing system is in the range of 0 to 35.0% by weight, more preferably in the range of 0 to 30.0% by weight, even more preferably in the range of 0 to 25.0% by weight, still more preferably in the range of 0 to 20.0% by weight and more preferably in the range of 0 to 15.0% by weight, in each case relative to the total weight of component (A).

[0090] The term "pigment" is known to the skilled person, for example from DIN 55943 (date: October 2001). "Pigment" in the sense of the present invention preferably refers to a component in powder or flake form that is substantially, preferably completely insoluble in the medium surrounding it, such as each of components (A) and (B) and the sealant composition, and is a substance that can be used as a colorant and / or pigment due to its magnetic, electric and / or electromagnetic properties. Preferably, "pigments" for the purposes of the present invention are inorganic and / or organic pigments. An example of an inorganic pigment is titanium dioxide.

[0091] Optional component (a5) Component (A) may additionally contain, and preferably contains, at least one curing catalyst (a5) when component (B) of the sealing system contains at least one component (b1) containing two or more epoxide groups as component (b). Suitable curing catalysts are amines, especially tertiary amines, amidines and / or guanidines. Examples include 1,4-diazabicyclo(2.2.2)octane, 1,5-diazabicyclo(4.3.0)non-5-ene (DBN) and 1,8-diazabicyclo(5.4.0)undec-7-ene (DBU).

[0092] Further optional components (a6) Component (A) of the sealing system may contain one or more optional components (a6).

[0093] Component (a6) may be a flame retardant such as a phosphorus-containing flame retardant, in particular at least one phosphoric acid ester. The flame retardant, if used, is preferably liquid (at 1 bar and 23° C.). If present in component (A), the flame retardant is preferably present in (A) in an amount of 0.1 to 30.0% by weight, more preferably 1.0 to 25.0% by weight, in particular 5.0 to 20.0% by weight, based on the total weight of component (A).

[0094] Component (a6) may be a light stabilizer, in particular a UV stabilizer. Examples include, for example, sterically hindered amines (HALS: hindered amine light stabilizers). In principle, any light stabilizer commercially available from the Tinuvin® series or other manufacturers can be used. Liquid light stabilizers are preferred. If the light stabilizer is present in component (A), it is preferably present in (A) in an amount of 0.05 to 5.0% by weight, more preferably 0.1 to 3.5% by weight, in particular 0.1 to 2.0% by weight, based on the total weight of component (A).

[0095] Component (a6) may be an additional adhesion promoter other than the aforementioned organosilane components. In particular, an organosilane different from component (a2) may be used. Examples include, for example, (3-aminopropyl)trimethoxysilane, (3-aminopropyl)triethoxysilane, N-2-aminoethyl-3-aminopropyltrimethoxysilane, (3-mercaptopropyl)trimethoxysilane, (3-mercaptopropyl)triethoxysilane, (3-glycidyloxypropyl)trimethoxysilane and / or (3-glycidyloxypropyl)triethoxysilane, vinyltrimethoxysilane. Additionally or alternatively, other adhesion promoters may be used, for example titanates and / or zirconates, such as titanium acetylacetonate (TAA) and / or Ti-n-butanolate (TnBt) and / or isopropyl titanate. The additional adhesion promoter, if present in component (A), is preferably present in component (A) in an amount of 0.05 to 5.0 mass %, more preferably 0.1 to 3.5 mass %, especially 0.1 to 2.0 mass %, based on the total mass of component (A).

[0096] Component (a6) may be an additive selected from the group consisting of antifoaming agents, rheological additives, plasticizers such as phthalates, and viscosity reducers, especially non-reactive viscosity reducers, such as hydrocarbon mixtures based on naphthalene derivatives and / or indene-coumarone resins, tall oil and rapeseed methyl ester (biodiesel), diluents based on rapeseed oil and / or other esters, and mixtures of such additives. The at least one additive, if present in component (A), is preferably present in an amount of 0.05 to 40.0% by weight, more preferably 0.1 to 30.0% by weight, in particular 0.1 to 20.0% by weight, relative to the total weight of component (A). In particular, the amount of at least one antifoaming agent, if present, is preferably in the range of 0.1 to 2.5% by weight, relative to the total weight of component (A). In particular, the amount of at least one reactive diluent, if present, is preferably in the range of 0.1 to 20.0% by weight, relative to the total weight of component (A). Specifically, when at least one rheological additive is present, its amount is preferably in the range of 0.1 to 5.0% by weight, based on the total weight of component (A). Specifically, when at least one plasticizer is present, its amount is preferably in the range of 0.1 to 2.5% by weight, based on the total weight of component (A). Specifically, when at least one viscosity reducer is present, its amount is preferably in the range of 0.1 to 20.0% by weight, based on the total weight of component (A).

[0097] As outlined above in relation to component (a1), component (a6) may further comprise at least one non-polymeric mercaptan having three thiol groups and a number average molecular weight in the range of 160 to 800 g / mol. Preferably, said at least one non-polymeric mercaptan, if present, is present as component (a6) in an amount in the range of 0.05 to 3.0% by weight, more preferably 0.05 to 1.5% by weight, in each case relative to the total weight of component (A).

[0098] Component (B) and Component (b) Component (B) of the sealing system comprises at least one component (b), which is suitable for curing the sealant composition by at least partially inducing a chemical transformation of two or more thiol groups of component (a1). In other words, component (b) or a part thereof is capable of chemically reacting with the thiol groups of component (a1). Component (b) thus represents a curing agent. The resulting chemical transformation may be applied to all thiol groups of component (a1) or may be applied only to a part of the thiol groups of component (a1). However, preferably, the chemical transformation is induced not only partially but also substantially to all thiol groups of component (a1).

[0099] Preferably, the at least one component (b) is selected from the group consisting of components comprising two or more epoxide groups (component (b1)), components which are metal oxides and / or metal peroxides, in particular manganese dioxide (component (b2)), components which are organic peroxides (component (b3)), components which comprise two or more vinyl groups (component (b4)), and mixtures thereof, more preferably from the group consisting of components comprising two or more epoxide groups (component (b1)), components which are metal oxides and / or metal peroxides, in particular manganese dioxide (component (b2)), and mixtures thereof, in particular representing as component (b1) at least one component which comprises two or more epoxide groups or as component (b2) at least one metal oxide and / or metal peroxide, in particular manganese dioxide.

[0100] Preferably, component (b) is present in component (B) of the sealing system used to prepare the sealant composition applied in step (2) in an amount in the range of 30 to 100% by weight, based on the total weight of component (B).

[0101] Component (b1) Component (b1) contains two or more epoxide groups. Preferably, the epoxide groups are present in (b1) as terminal groups. Component (b1) can be monomeric, oligomeric or polymeric. Preferably, component (b1) is aliphatic and / or aromatic.

[0102] Preferably, component (b1) is present in component (B) of the sealing system used to prepare the sealant composition applied in step (2) in an amount in the range of 50 to 100% by weight, based on the total weight of component (B).

[0103] Preferably, (b1) has an epoxide functionality of from 2.0 to 5.0, more preferably from 2.0 to 3.0, especially from 2.2 to 2.8.

[0104] Component (b1) is in particular selected from diglycidyl ethers of bisphenol A, diglycidyl ethers of bisphenol F, and aliphatic polyglycols and / or hydantoin epoxy derivatives. Epoxy-terminated polythioethers or polythioether sulfides and / or epoxidized polysulfides may also be used. Particularly preferred is at least one epoxy novolac resin (epoxidized phenol formaldehyde resin), preferably a crosslinked epoxy novolac resin. It is also possible to use more than component (b1), for example bisphenol A / F epoxy resins or bisphenol F novolac resins, based on some of the above classes. Component (B) may additionally contain a diluent, for example to adjust the viscosity and flexibility. Examples of diluents include 1,4-butanediol diglycidyl ether, 2-ethylhexyl-glycidyl ether and 1,6-hexanediol diglycidyl ether.

[0105] Preferably, (b1) is at least one epoxide-terminated polysulfide polymer and / or polythioether polymer and / or polythioether sulfide polymer having no terminal mercapto groups and functioning as a curing agent by virtue of its two terminal epoxide groups, said polymer being preferably present as a liquid or highly viscous polymer, in particular having an epoxy equivalent in the range of 200 to 800 g / eq.

[0106] Preferably, the epoxy (epoxide) equivalent of (b1) is in the range of 120 to 800 g / eq, particularly preferably in the range of 140 to 700 g / eq, and most preferably in the range of 170 to 400 g / eq.

[0107] Most particularly preferred are components (b1) based on bisphenol A epoxy resins having an epoxy equivalent in the range from 170 to 200 g / eq, based on bisphenol F resins having an epoxy equivalent in the range from 150 to 180 g / eq and based on epoxy novolac resins having an epoxy equivalent in the range from 160 to 220 g / eq.

[0108] Suitable commercially available examples include, for example, bisphenol F epoxy resins such as DEN354 (Olin Epoxy), bisphenol A resins such as DER336, DER331 (Olin Epoxy), bisphenol A / F epoxy resins such as DER351, DER324, DER335 (Olin Epoxy), epoxy novolac resins such as DEN431, DEN438, DEN439 (Olin Epoxy), epoxy-terminated prepolymers based on polysulfides and / or polythioethers such as Thioplast EPS25 (Akzo Nobel), epoxy-terminated reactive diluents based on alcohols / glycols such as 1,4-butanediol diglycidyl ether (DER731; Olin Epoxy), and 1,6-hexanediol diglycidyl ether (DER734; Olin Epoxy).

[0109] Preferably, the molar ratio of every component (b1) to every component (a1) ranges from 0.90:1 to 2:1.

[0110] Constituent (b2) Component (b2) is at least one metal oxide and / or metal peroxide, in particular manganese dioxide. Manganese dioxide means manganese(IV) oxide. Another suitable component (b2) is calcium peroxide.

[0111] Preferably, component (b2) is present in component (B) of the sealing system used to prepare the sealant composition applied in step (2) in an amount in the range of 30 to 90% by weight, based on the total weight of component (B).

[0112] Component (b3) Component (b3) is at least one organic peroxide. Examples of suitable organic peroxides are organic hydroperoxides, such as cumenyl hydroperoxide.

[0113] Preferably, component (b3) is present in component (B) of the sealing system used to prepare the sealant composition applied in step (2) in an amount in the range of 30 to 100% by weight, based on the total weight of component (B).

[0114] Constituent (b4) Component (b4) contains two or more vinyl groups. Preferably, the vinyl groups are present in (b4) as end groups. Component (b4) can be monomeric, oligomeric or polymeric, and is preferably monomeric. Preferably, (b4) is aliphatic and / or aromatic. Examples of component (b4) are divinyl ethers, such as diethylene glycol divinyl ether, triethylene glycol divinyl ether and butanediol divinyl ether.

[0115] Preferably, component (b4) is present in component (B) of the sealing system used to prepare the sealant composition applied in step (2) in an amount in the range of 30 to 100% by weight, based on the total weight of component (B).

[0116] Component (b4), when used as component (b) of component (B), is preferably present in combination with at least one radical generator. Examples of suitable radical generators are 1-hydroxycyclohexyl phenyl ketone and 2-hydroxy-2-methyl-1-phenylpropan-1-one.

[0117] Optional components (b5) Component (B) of the sealing system may contain one or more optional components (b5). Component (b5) may be an additive selected from the group consisting of reactive diluents, such as bis-oxazolidines and / or aldimines, and plasticizers, such as phthalates. In particular, at least one plasticizer component (b5) is present in component (B) of the sealing system when component (B) contains at least one component (b2), in particular manganese dioxide.

[0118] Specifically, when at least one reactive diluent is present, its amount is preferably in the range of 0.1 to 20.0% by weight, based on the total weight of component (B). Specifically, when at least one plasticizer is present, its amount is preferably in the range of 10.0 to 70.0% by weight, based on the total weight of component (B).

[0119] Optional constituent (b6) Component (B) may additionally contain, and preferably does contain, at least one curing catalyst (b6).

[0120] As outlined above, when the sealing system component (B) contains at least one component (b1) containing two or more epoxide groups as component (b), at least one curing catalyst, if present, is preferably present in component (A) as component (a5) and not present in component (B). Suitable curing catalysts in this case are amines, especially tertiary amines, amidines and / or guanidines. For example, 1,4-diazabicyclo(2.2.2)octane, 1,5-diazabicyclo(4.3.0)non-5-ene (DBN) and 1,8-diazabicyclo(5.4.0)undec-7-ene (DBU).

[0121] If component (B) of the sealing system comprises at least one component (b2) as component (b), then at least one curing catalyst (b6) is preferably present in component (B). Suitable curing catalysts in this case are, for example, tetrabenzyl thiuram disulfide, diphenyl guanidine and / or zinc bis(diethyldithiocarbamate).

[0122] If component (B) of the sealing system comprises at least one component (b3) as component (b), then at least one curing catalyst (b6) is preferably present in component (B). A suitable curing catalyst in this case is, for example, zinc diethylcarbamate.

[0123] If component (B) of the sealing system comprises at least one component (b4) as component (b), at least one curing catalyst (b6) is preferably present in component (B). Suitable curing catalysts in this case are in particular suitable photoinitiators, such as acetophenone, benzoin ether and / or benzoyl oxime. Curing is preferably carried out via UV light.

[0124] Optional components (b7) Component (B) may additionally contain at least one flame retardant (b7). Component (b7) may be a phosphorus-containing flame retardant, in particular at least one phosphoric acid ester. The flame retardant, if used, is preferably liquid (at 1 bar and 23° C.). If present in component (A), the flame retardant is preferably present in component (A) in an amount of 5.0 to 65.0% by weight, more preferably 25.0 to 65.0% by weight, in particular 40.0 to 65.0% by weight, in each case based on the total weight of component (B).

[0125] Optional step (3) Preferably, the method of the present invention further comprises a curing step (3), i.e. (3) curing at least the sealant composition applied in step (2) at ambient temperature (18-23°C) or at an elevated temperature, such as 80°C, for 0.5 hours to 14 days. Further includes:

[0126] Preferably, curing according to step (3) refers to chemical curing, e.g. chemical crosslinking, at ambient or elevated temperature. If at least one component (b1) or (b4) is used as component (b), curing may additionally or alternatively be induced via UV light.

[0127] Preferably, the sealant composition is applied in a dry layer thickness in the range of from 15 μm to 20 mm, more preferably from 50 μm to 15 mm, especially from 0.5 to 10 mm.

[0128] Encapsulated Substrate A further subject of the invention are encapsulated substrates obtainable by the process according to the invention.

[0129] All preferred embodiments described herein above in relation to the method of the present invention and its preferred embodiments are also preferred embodiments of the encapsulated substrate of the present invention.

[0130] Use of organosilane components to improve adhesion A further subject of the present invention is the use of an organosilane component as defined above, which when incorporated in a primer composition as defined above, such as the primer composition used in step (1) of the process of the present invention, or in a sealant composition as defined above, such as the sealant composition used in step (2) of the process of the present invention, in particular in component (A) of the sealing system used to prepare said sealant composition, improves the adhesion of the primer composition or sealant composition to the substrate, when applied to at least a portion of the surface of an optionally precoated substrate.

[0131] All preferred embodiments described herein above in relation to the inventive method and the inventive sealed substrate and preferred embodiments thereof are also preferred embodiments of the inventive method of use.

[0132] Sealant compositions and sealing systems A further subject of the invention is a sealant composition as defined above, which can be obtained by mixing together components (A) and (B) of a sealing system as defined above, said component (A) of the sealing system comprising at least one organosilane component as defined above.

[0133] The resulting sealing composition may be, but need not be, sprayable.

[0134] Preferably, the sealing composition is obtainable by mixing components (A) and (B) in a mass ratio (component (A) / component (B)) in the range of 100:1 to 1:1. More preferably, the mixing is carried out in a mass ratio in the range of 100:1 to 1.1:1, even more preferably in a mass ratio in the range of 100:1 to 2:1, in particular in a mass ratio in the range of 100:1 to 3:1, and most preferably in a mass ratio in the range of 20:1 to 4:1.

[0135] A further subject of the present invention is a two-component (2K) sealing system comprising components (A) and (B) as defined above that are distinct from one another, component (A) of said sealing system comprising at least one organosilane component as defined above.

[0136] All preferred embodiments described herein above in relation to the inventive method, the inventive sealed substrate and the inventive method of use and their preferred embodiments are also preferred embodiments of the inventive sealant composition and the inventive sealing system.

[0137] Preferably, the sealing system consists of components (A) and (B).

[0138] Organosilane components A further subject of the present invention is an organosilane component as defined above, optionally incorporated in a primer composition as defined above.

[0139] All preferred embodiments described herein above in connection with the inventive method, the inventive sealed substrate, the inventive method of use, the inventive sealant composition and the inventive sealing system, and preferred embodiments thereof, are also preferred embodiments of the inventive organosilane component.

[0140] Primer Composition A further subject of the invention is a primer composition as defined above, comprising at least one organosilane component as defined above.

[0141] All preferred embodiments described herein above in connection with the inventive method, the inventive sealed substrate, the inventive method of use, the inventive sealant composition and the inventive sealing system, and the inventive organosilane component, and preferred embodiments thereof, are also preferred embodiments of the inventive primer composition.

[0142] method 1. Peel test Peel testing was performed in accordance with AMS-C-27725.

[0143] 2. Immersion test The immersion test was performed in accordance with AMS2629 (Type 1, 7 days).

[0144] 3. Number average molecular weight The number average molecular weights of components (a1) and (b1) were determined by GPC (gel permeation chromatography) against polystyrene standards. THF (tetrahydrofuran) was used as the mobile phase. The number average molecular weights of the organosilane component (a2) were determined by NMR spectroscopy for the monomeric and oligomeric components and by GPC for the polymeric component. EXAMPLES

[0145] The following examples further illustrate the present invention but are not to be construed as limiting its scope. "pbw" means parts by weight. Unless otherwise defined, "parts" means "parts by weight".

[0146] 1. Synthesis of NCO-functionalized organosilanes OS1–OS4 1.1 Synthesis of OS1 containing a urea moiety (comparative example) OS1 was prepared by slowly adding IPDI (isophorone diisocyanate) dropwise to bis[3-(trimethoxysilyl)propyl]amine with stirring. IPDI and bis[3-(trimethoxysilyl)propyl]amine were used in equimolar amounts. The resulting product was used as OS1 without purification.

[0147] 1.2 Synthesis of OS2 containing an S-thiocarbamate moiety (example of the invention) OS2 was prepared by heating an equimolar mixture of IPDI and (3-mercaptopropyl)methyldimethoxysilane, additionally containing 0.0005 moles of 1,4-dimethylpiperazine, to 75° C. under an inert gas atmosphere with stirring for 4 hours. The resulting product was used as OS2 without purification. The NCO content of OS2 was 10.2% by weight.

[0148] 1.3 Synthesis of OS3 containing an S-thiocarbamate moiety (inventive example) OS3 was prepared by heating an equimolar mixture of HMDI (hexamethylene diisocyanate) and (3-mercaptopropyl)trimethoxysilane, additionally containing 0.0005 moles of 1,4-dimethylpiperazine, to 75° C. under an inert gas atmosphere for 4 hours with stirring. The resulting product was used as OS3 without purification. The NCO content of OS3 was 11.6% by weight.

[0149] 1.4 Synthesis of OS4 containing an S-thiocarbamate moiety (inventive example) OS4 was prepared by heating an equimolar mixture of IPDI and (3-mercaptopropyl)trimethoxysilane, additionally containing 0.0005 moles of 1,4-dimethylpiperazine, to 75° C. under an inert gas atmosphere with stirring for 4 hours. The resulting product was used as OS4 without purification. The NCO content of OS4 was 9.9% by weight.

[0150] 2. Preparation of Sealant Compositions and Sealed Substrates 2.1 A number of exemplary sealant compositions were prepared. Each sealant composition was prepared by mixing together two components (A) and (B) of a two-component sealing system. The composition of component (A) of each sealing system is shown in Table 1. Component (A) was prepared by mixing together the components shown in Table 1 in the order shown in Table 1.

[0151] [Table 1]

[0152] Thioplast® LP12 and Thioplast® LP33 are commercially available SH-group containing polysulfides. Filler 1 and Filler 2 are commercially available fillers. Pigment 1 is a commercially available pigment. Rheological Additive 1 is a commercially available hydrophobic fumed silica. OS is one of the NCO-functionalized organosilanes OS1 to OS4 or one of the commercially available organosilanes (3-glycidyloxypropyl)trimethoxysilane (COS1) and (3-mercaptopropyl)trimethoxysilane (COS2).

[0153] Depending on which organosilanes OS1 to OS4, COS1 and COS2 were used, different components "A" of the sealing system were thus obtained, namely SC-A-OS1, SC-A-OS2, SC-A-OS3, SC-A-OS4, SC-A-COS1 and SC-A-COS2.

[0154] 2.2 100 parts by weight of each of the components "A" SC-A-OS1, SC-A-OS2, SC-A-OS3, SC-A-OS4, SC-A-COS1 and SC-A-COS2 were mixed with 10 parts by weight of the hardener component "B". Component "B" contains a manganese dioxide hardener. In each case a commercial product was used as component (B) (Naftoseal® MC780B-2 hardener from Chemetall GmbH).

[0155] 2.3 Each of the components "A", namely SC-A-OS1, SC-A-OS2, SC-A-OS3, SC-A-OS4, SC-A-COS1 and SC-A-COS2, was mixed with component "B" and then the sealant compositions obtained after mixing, namely SC-OS1, SC-OS2, SC-OS3, SC-OS4, SC-COS1 and SC-COS2, were applied in each case to the substrates by applying air pressure to the cartridge. The following substrates S1 to S3 were used:

[0156] Substrate S1: Aluminum substrate (AL2024), Substrate S2: Aluminum substrate (AL2024) coated with a commercial base coat (Mankiewicz Seevenax313-81); Substrate S3: Aluminum substrate (AL2024) coated with a commercially available integral fuel tank coating (DeSoto 823-707).

[0157] After application to one of the substrates, the applied sealant composition was allowed to cure for 14 days at room temperature (23° C.) and 50% relative humidity. The sealed substrates were then subjected to a number of tests as outlined below.

[0158] 3. Investigating the properties of the encapsulated substrate 3.1 Sealant applied to the surface of substrate S1 Several properties of the encapsulated and cured substrates were investigated. Measurements were performed as disclosed in the Methods section. The results are shown in Table 3.1.

[0159] [Table 2]

[0160] 3.2 Sealant applied to the surface of substrate S2 Several properties of the encapsulated and cured substrates were investigated. Measurements were performed as disclosed in the Methods section. The results are shown in Table 3.2.

[0161] [Table 3]

[0162] 3.3 Sealant applied to the surface of substrate S3 Several properties of the encapsulated and cured substrates were investigated. Measurements were performed as disclosed in the Methods section. The results are shown in Table 3.3.

[0163] [Table 4]

Claims

1. At least step (2) and optionally step (1), i.e. (1) applying a primer composition at least partially to a surface of an optionally precoated substrate to at least partially form a primer film on said surface; (2) applying a sealant composition at least partially to the surface of the optionally precoated substrate if optional step (1) is not performed, or to the primer film if optional step (1) is performed; A method for sealing an optionally precoated substrate comprising: the sealant composition is different from the primer composition optionally applied in step (1) and can be obtained by mixing together the components of a sealing system, the sealing system being a two-component (2K) sealing system comprising two components (A) and (B) which are separate from each other, component (A) of the sealing system comprises at least one polymer component (a1) containing two or more thiol groups selected from polyether, polythioether, polysulfide, polythioether-sulfide components and mixtures thereof; and component (B) of the sealing system comprises at least one component (b) suitable for curing the sealant composition by at least partially inducing chemical transformation of two or more thiol groups of component (a1); The following ingredients: (i) at least one hydrolyzable group, X; (ii) at least one isocyanate group, and (iii) a spacer unit disposed between the at least one hydrolyzable group X and the at least one isocyanate group, the spacer unit comprising at least one moiety MS that comprises at least one sulfur atom; At least one organosilane component containing A method characterized in that it is at least present as component (a2) in component (A) of the sealing system used to prepare the sealant composition applied in step (2) when optional step (1) is not performed, or is at least present as a component in the primer composition applied in step (1) when step (1) is performed.

2. 10. The method of claim 1, wherein the at least one organosilane component is at least present in component (A) used to prepare the sealant composition applied in step (2).

3. 2. The method according to claim 1, characterized in that the at least one organosilane component, when at least present as component (a2) in component (A) of the sealing system used to prepare the sealant composition applied in step (2), is present in (A) in an amount in the range of 0.05 to 10.0% by weight, preferably 0.10 to 7.5% by weight, more preferably 0.15 to 7.5% by weight, even more preferably 0.20 to 5.0% by weight, still more preferably 0.25 to 4.5% by weight, in each case relative to the total weight of component (A) of the sealing system, or when at least present as a component in the primer composition applied in step (1), is present in the primer composition in an amount in the range of 0.10 to 15.0% by weight, preferably 0.20 to 12.5% ​​by weight, more preferably 0.30 to 10.0% by weight, even more preferably 0.40 to 7.5% by weight, still more preferably 0.50 to 6.0% by weight, in each case relative to the total weight of the primer composition.

4. 2. The method according to claim 1, characterized in that the at least one moiety MS of the spacer unit of the organosilane component, which comprises at least one sulfur atom, is selected from the group consisting of thiocarbamate, thiourea, thioester, thioketo, thiourethane and thioamide moieties, preferably representing a thiocarbamate, thiourethane and / or thiourea moiety.

5. The method of claim 1 , wherein the at least one organosilane component contains exactly one isocyanate group.

6. 2. The method according to claim 1, characterized in that the at least one organosilane component is obtainable from the reaction of at least one, preferably aliphatic and / or cycloaliphatic diisocyanate with at least one organosilane precursor comprising at least one thiol group as a functional group reactive towards isocyanate groups, in particular when the at least one diisocyanate and the at least one organosilane precursor are used in approximately equimolar amounts, respectively.

7. 2. The method of claim 1, wherein the at least one organosilane component is monomeric, preferably the spacer unit having a chain length separating the at least one hydrolyzable group X and the at least one isocyanate group of at least 6 carbon and / or heteroatoms, preferably including atoms of at least one moiety MS within the chain.

8. 2. The method of claim 1, wherein the organosilane component comprises at least two, preferably at least three, hydrolyzable groups X, where X is preferably an alkoxy group having 1 to 4 carbon atoms.

9. The at least one organosilane component is preferably a mixture of at least one aliphatic and / or cycloaliphatic diisocyanate and a diisocyanate having the general formula (I) and / or (II), i.e. Si(X) ４－ｙ (R) ｙ , (I), Si(X) ３－ｚ (T) ｚ -(1A)-Si(X) ３－ｚ (T) ｚ (II), (In the case of general formula (I), Each X is independently a hydrolyzable group, and preferably each X is independently O—C １～４ alkyl, The parameter y is an integer ranging from 1 to 3, but is at least 1, and preferably exactly 1; and R is a non-hydrolyzable organic group, at least one of the groups R containing at least one functional group that is reactive towards an isocyanate group; And in the case of the general formula (II), X is, in each occurrence independently of one another, a hydrolyzable group, preferably, in each occurrence independently of one another, O—C １～４ - alkyl, RA represents a divalent non-hydrolyzable organic group containing at least one functional group that is reactive towards isocyanate groups; the parameter z in each occurrence is an integer ranging from 0 to 3, preferably 0 in each occurrence; and T is a non-hydrolyzable organic group different from the group (RA), and preferably does not have a functional group reactive with an isocyanate group.

2. The process according to claim 1, characterized in that it is obtained from the reaction of at least one organosilane precursor represented by

10. 2. The method according to claim 1, characterized in that the at least one component (b) present in component (B) and suitable for curing the sealant composition is selected from the group consisting of components comprising two or more epoxide groups (component (b1)), components which are metal oxides and / or metal peroxides, in particular manganese dioxide (component (b2)), components which are organic peroxides (component (b3)), components which comprise two or more vinyl groups (component (b4)), and mixtures thereof, preferably selected from the group consisting of components comprising two or more epoxide groups (component (b1)), components which are metal oxides and / or metal peroxides, in particular manganese dioxide (component (b2)), and mixtures thereof, in particular representing as component (b1) at least one component which comprises two or more epoxide groups or as component (b2) at least one metal oxide and / or metal peroxide, in particular manganese dioxide.

11. An encapsulated substrate obtainable by the method according to any one of claims 1 to 10.

12. 11. A method of using an organosilane component as defined in any one of claims 1 to 10, when incorporated into a primer composition as defined in any one of claims 1 to 10, or a sealant composition as defined in any one of claims 1 to 10, applied to at least a portion of a surface of an optionally precoated substrate, to improve adhesion of said primer composition or said sealant composition to said substrate.

13. 15. A sealant composition as defined in any one of claims 1 to 10 obtainable by mixing together components (A) and (B) of a sealing system as defined in any one of claims 1 to 10 or as defined in claim 14, said sealing system component (A) comprising at least one organosilane component as defined in any one of claims 1 to 10.

14. 11. A two-component (2K) sealing system comprising components (A) and (B) as defined in any one of claims 1 to 10 which are separate from one another, wherein component (A) of the sealing system comprises at least one organosilane component as defined in any one of claims 1 to 10.

15. 11. An organosilane component as defined in any one of claims 1 to 10, optionally incorporated in a primer composition as defined in any one of claims 1 to 10.