Abstract

The present invention relates to a biocidal composition for the surface treatment of a porous substrate, said composition comprising at least one hydrophilic binder, at least one biocidal compound based on a quaternary ammonium, and at least one cationic size. The present invention further relates to a method of using such a composition to impart biocidal properties, in particular antiviral properties, to a porous substrate.

Description

[Technical field]

[0001] The present invention relates to the field of porous media having biocidal properties, in particular to the field of sheet materials, more in particular to the field of fibrous materials such as paper, nonwoven materials and textiles, in particular writing and printing paper; coated paper; copy paper; packaging cardboards made from virgin and / or recycled fibers; leather; wood; security paper; security documents; and media for banknotes.

[0002] It is a particular object of the present invention to provide compositions and methods that are useful for imparting biocidal activity on surfaces and ensuring hydrophobicity in the porous substrates from which these media are derived. [Background technology]

[0003] In modern society, paper media intended for the transmission of information, in particular banknotes, but also paper media intended for packaging, such as cardboards, are increasing in number and are frequently handled every day by many people.

[0004] However, some of these people may be carriers of one or more pathogenic microorganisms, and therefore media handled by these people may become vectors of contamination and the source of epidemic and pandemic diseases of various severity. In this regard, it is also important to point out that cellulosic fiber materials, such as banknotes or cardboard, generally tend to absorb moisture, thereby apparently helping to promote the development and / or maintaining the survival of microorganisms therein.

[0005] This problem of microbial, bacterial, fungal and / or viral contamination of fibrous materials, generally cellulose, is not new, and solutions have already been developed that attempt to overcome the risk of microbial, bacterial, fungal and / or viral infection associated with their bulk handling.

[0006] The most common solution consists of treating the media, more generally their base substrate made of cellulosic materials, with at least one biocide. The incorporation of one or more biocides into the base substrate can be achieved by immersing the substrate in a solution of the biocide or by spraying, surface treating or coating the substrate with a solution containing the biocide.

[0007] Examples of biocides commonly used for these purposes include, inter alia, p-[(diiodomethyl)sulfonyl]toluene, 3-iodo-2-propynyl butylcarbamate, methyl 1H-benzimidazol-2-ylcarbamate, monolaurin, compounds based on isothiazolone derivatives or isothiazolone derivatives, chitosan, quaternary ammonium salts, in particular didecyldimethylammonium chloride, silver zinc zeolites, etc. However, these biocides often have mainly only a specific biocidal activity, i.e. bactericidal activity, fungicidal activity or virucidal activity, and therefore they must be combined to obtain a broad-spectrum biocidal effect. This is, of course, a further limitation, since the conditions under which these biocides are used are not always the same. In this respect, quaternary ammonium based compounds, in particular didecyldimethylammonium chloride (DDAC), are known to be particularly advantageous biocides due to their multiple biocidal properties, in particular antibacterial, antifungal and antiviral properties (EP 2 457 440 B).

[0008] Unfortunately, quaternary ammonium-based compounds also have the specific feature of being strongly cationic compounds and tend to strongly hydrophilize the substrates in which they are incorporated. Thus, when DDAC is used with a hydrophilic binder, such as polyvinyl alcohol or starch, and applied to a cellulose substrate, the hydrophobicity of this substrate, which can be quantified by the Cobb water absorption test, decreases, for example, to the 20-40 g / m required for writing and printing papers or for packaging papers. 2 The required standard of water quality can no longer be achieved. It should also be noted that cellulose media obtained from recycling have the special feature of being less hydrophobic than higher grade cellulose media. Moreover, they contain a lot of residual starch-based products, which favor the development or survival of microorganisms. Treatment with quaternary ammonium-based biocidal compounds, such as DDAC, therefore exacerbates this problem and is therefore sufficient to defeat the objective pursued by this compound of reducing the risk of contamination, since moisture favors the development of microorganisms. Summary of the Invention [Problem to be solved by the invention]

[0009] Therefore, there remains a need for surface treatments, especially coatings, for porous substrates, especially cellulosic substrates, that are capable of imparting biocidal properties without altering their hydrophobicity.

[0010] Similarly, there remains a need for surface treatments, particularly coatings, that can simultaneously impart biocidal properties and significant hydrophobicity to fibrous substrates resulting from recycling of high quality fibrous substrates.

[0011] It is an object of the present invention to provide economically acceptable biocidal protection, particularly for substrates intended for bulk packaging.

[0012] Another object is to provide for the use of biocides that are included in the list of biocidal products approved for contact with food.

[0013] A further objective is to ensure sustained antibacterial activity.

[0014] The ultimate aim is to provide a solution which, in addition to the desired biocidal properties, is able to provide a satisfactory hydrophobicity, in particular for substrates intended for bulk packaging or for writing paper and printing. [Means for solving the problem]

[0015] The present invention therefore proposes a novel biocidal composition for the surface treatment of substrates.

[0016] Thus, according to one of its aspects, the present invention provides a biocidal composition for the surface treatment of a porous substrate comprising: at least one hydrophilic binder, at least one biocidal compound based on quaternary ammonium, in particular a quaternary ammonium salt, in particular didecyldimethylammonium chloride (DDAC), and At least one cationic sizing agent The present invention relates to a biocidal composition comprising:

[0017] In particular, the biocidal composition comprises at least one quaternary ammonium based biocidal compound selected from polymeric or non-polymeric quaternary ammonium salts, in particular at least one quaternary ammonium based biocidal compound selected from non-polymeric quaternary ammonium salts, more in particular at least didecyldimethylammonium chloride (DDAC).

[0018] More particularly, the present invention provides a biocidal composition for the surface treatment of a porous substrate comprising: at least one hydrophilic binder, The formula: (CH3)2A2N + X -at least one biocidal compound based on quaternary ammonium selected from the non-polymeric quaternary ammonium salts of A may be the same or different and is a linear C6-C 20 represents an alkyl group, and X - is an anion selected from a halide anion and a sulfonate anion, and At least one cationic sizing agent, in particular at least one cationic sizing agent selected from alkenyl ketene dimer (AnKD), alkyl ketene dimer (AKD), styrene acrylate (SAE), rosin, alkenyl succinic anhydride (ASA), and combinations thereof; The present invention relates to a biocidal composition as described above, comprising:

[0019] In particular, the quaternary ammonium based biocidal compound includes at least didecyldimethylammonium chloride (DDAC).

[0020] For the purposes of the present invention, "surface treatment" refers to the formation of a deposit of a composition on the surface of a substrate, such that the medium thus obtained has the desired surface biocidal properties and hydrophobicity. In particular, the surface treatment obtained according to the present invention results in the formation of a localized coating on the surface of the medium and / or in a surface portion of the thickness of the medium.

[0021] For purposes of the present invention, the terms "biocidal agent" or "biocidal", which are equivalent to the term "antimicrobial agent", generally refer to any agent that is effective in controlling and / or inhibiting the growth and / or reducing the density of microorganisms, such as viruses, fungi, bacteria and / or yeasts.

[0022] For the purposes of the present invention, "cationic sizing agents" refers to sizing agents formulated in the form of cationic emulsions, cationic solutions or cationic dispersions. In emulsion and dispersion formulations, the surface of the droplets or particles of the cationic sizing agent is positively charged. Cationic sizing agents can be characterized by a positive zeta potential measurement. The zeta potential can be measured using an apparatus for measuring electrophoretic mobility. Cationic sizing agents can also be characterized by titration of the cationic sizing agent, in particular with anionic electrolytes, such as anionic polyacrylamides. The titration can be measured using a Mutek PCD apparatus.

[0023] As can be seen from the examples below, the inventors have found that, contrary to all expectations, the use of a particular type of sizing agent in the surface treatment in combination with a quaternary ammonium-based biocidal compound, in particular DDAC, makes it possible to ensure significant hydrophobicity in porous substrates, in particular fibrous substrates so treated, while retaining the expected biocidal properties of the quaternary ammonium-based biocidal compound.

[0024] According to another of its aspects, the present invention relates to a porous medium, in particular a fibrous medium, which has surface biocidal properties and which has, on all or part of at least one of its outer surfaces, a surface treatment, preferably a coating, formed from a composition according to the present invention. In particular, this porous medium is selected from paper and cardboard, in particular cardboard intended to form packaging cardboard, in particular flat cardboards or corrugated cardboards, for example selected from paper and cardboard formed at least partially from recycled fibers.

[0025] According to yet another of its aspects, the present invention provides a method for producing a porous medium having surface biocidal properties in accordance with the present invention, comprising the steps of: a) providing a porous substrate, particularly a fibrous substrate, preferably a porous substrate formed at least in part from recycled fibers; b) contacting all or a portion of at least one of the exterior surfaces of said porous substrate with a composition according to the present invention under conditions conducive to forming a deposit of said composition thereon; c) drying the deposit to form a porous medium with biocidal properties. The object of the present invention is to provide a method as described above, which comprises at least the steps of:

[0026] According to yet another of its aspects, the present invention provides a method of using the compositions of the present invention to impart biocidal, especially antiviral, properties to porous substrates, especially fibrous substrates.

[0027] According to yet another of its aspects, the present invention provides a method of using a composition according to the present invention to increase the hydrophobicity of a porous substrate, particularly a fibrous substrate, especially a substrate formed at least in part from recycled fibers.

[0028] According to yet another of its aspects, the present invention provides the use of a porous medium according to the present invention for the manufacture of banknotes or security sheets, or printing, writing or copying papers.

[0029] According to yet another of its aspects, the present invention provides a method of using a porous medium according to the present invention to manufacture cardboard packaging.

[0030] According to yet another of its aspects, the invention provides methods of using porous media according to the invention to produce papers, nonwoven materials and textiles, writing and printing papers, coated papers and copy papers. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0031] Compositions according to the invention

[0032] Quaternary ammonium-based biocidal compounds

[0033] Quaternary ammonium based compounds, in particular quaternary ammonium salts, are known as antimicrobial and / or microbicidal agents, more particularly bacteriostatic (or bactericidal) and / or bactericidal and / or fungistatic (or antifungal) and / or fungicidal agents.

[0034] They are more particularly polymeric or non-polymeric quaternary ammonium salts.

[0035] Quaternary ammonium salts are generally represented by the preferred anion X - The quaternary ammonium cation has the formula:

[0036] The cation is more particularly of the formula: [ka] Wherein, R1, R2, R3, and R4 may be different species. For example, R1, R2, R3, and R4 may be selected independently from alkyl groups, aryl groups, alkylaryl groups, arylalkyl groups, cycloalkyl groups, aromatic or non-aromatic heterocyclic groups, or alkenyl groups, where the groups are substituted or unsubstituted, linear or branched, and can be optionally interrupted by one or more heteroatoms, such as one or more oxygen atoms, or one or more phosphinic acid groups.

[0037] Alternatively, two or more of the R1, R2, R3, and R4 groups, together with the nitrogen atom carrying them, may form a substituted or unsubstituted heterocyclic ring.

[0038] According to a particular embodiment, the R1, R2, R3 and R4 groups are alkyl groups, preferably linear alkyl groups, in particular C1-C 20 In particular, the R1, R2, R3 and R4 groups are saturated, preferably unsaturated, preferably linear, in particular C1-C 20 , is an alkyl group of the formula:

[0039] The R1, R2, R3 and R4 groups together contain at least 4 carbon atoms. In particular, the total number of carbon atoms in the R1, R2, R3 and R4 groups may be at least 10. Preferably, at least one of the R1, R2, R3 and R4 groups, in particular two of the R1, R2, R3 and R4 groups, contains 6 to 20 carbon atoms, in particular 8 to 18 carbon atoms.

[0040] Anion of Quaternary Ammonium Salt X - In particular, the anion of the quaternary ammonium salt may be selected from halide anions, such as chloride, fluoride, bromide or iodide, and sulfonate anions. In particular, the anion of the quaternary ammonium salt may be selected from halide anions. Preferably, the anion of the quaternary ammonium salt may be chloride.

[0041] The non-polymeric quaternary ammonium salt may more particularly be of the formula: (CH3) n (A) m N + X - where A has the definitions proposed above for R1, R2, R3, and R4, and X - is an anion as defined above, n is an integer from 1 to 3, preferably 2 or 3, and m is an integer from 1 to 3, preferably 1 or 2, with the proviso that the sum of n+m is equal to 4. When m is 2 or 3, the A groups may be the same or different, in particular they are identical.

[0042] Preferably, the quaternary ammonium salt used as the antibacterial agent according to the present invention has the following formula: (CH3)n (A) m N + X - where n is 2, m is 2, and A may be the same or different and are as defined above for R1, R2, R3, and R4.

[0043] In particular, A may be the same or different, in particular may be identical, and is a linear C-C 20 , especially C8~C 18 , especially C8~C 12 , or an alkyl group thereof.

[0044] In particular, A may be the same or different, in particular may be identical, and is a linear saturated C6-C 20 , especially C8~C 18 , especially C8~C 12 , may be an alkyl group of the formula:

[0045] Examples include didecyldimethylammonium chloride (DDAC), dioctyldimethylammonium chloride, and octyldecyldimethylammonium chloride.

[0046] The quaternary ammonium based biocidal compounds may also be polymeric quaternary ammonium salts, that is, compounds having a chemical formula that includes repeating "quaternary ammonium" units.

[0047] Such "polymeric" quaternary ammonium salts may be derived from at least one compound of formula (I) in which at least one of R1, R2, R3, and R4 has a polymerizable function, in particular a function containing one or more ethylenic unsaturations, more particularly a function selected from (meth)acrylate and allyl functions.

[0048] In particular, this "polymeric" compound based on quaternary ammonium may be obtained by polymerizing at least one of the above-mentioned quaternary ammonium salts of formula (I), in which two of R1, R2, R3 and R4 are groups carrying an allyl function, in particular allyl groups, and the others are preferably alkyl groups, in particular C1-C6, in particular C1-C4, in particular methyl groups.

[0049] According to a particular embodiment, this polymeric compound based on quaternary ammonium is a homopolymer of diallyldialkylammonium chloride. In particular, it can be a polymer of diallyldimethylammonium chloride, called polyDADMAC. PolyDADMAC can be synthesized by free radical polymerization of DADMAC in the presence of peroxide as catalyst, or it can be commercially available.

[0050] According to a particular embodiment, the biocidal composition according to the invention uses at least didecyldimethylammonium chloride (DDAC).

[0051] As mentioned above, the biocidal composition of the invention comprises from 0.05% to 2.5% by dry weight, preferably from 0.25% to 1.5% by dry weight, more preferably from 0.25% to 1% by dry weight, of one or more biocidal compounds based on quaternary ammonium, in particular selected from polymeric or non-polymeric quaternary ammonium salts, in particular selected from non-polymeric quaternary ammonium salts, more in particular selected from didecyldimethylammonium chloride (DDAC), relative to the total weight of the composition.

[0052] For the purposes of the present invention, "dry weight", also referred to as "weight of active ingredient", refers to the weight content of the compound not including any volatile solvent, such as water, with which it is incorporated, unless otherwise specified.

[0053] In particular, the amount of one or more quaternary ammonium based biocidal compounds, in particular DDAC, is adjusted in the composition so that the surface treatment, preferably the coating formed from the composition, contains less than 10% by dry weight, preferably less than 5% by dry weight, of one or more quaternary ammonium based biocidal compounds, in particular DDAC, based on its total dry weight.

[0054] As can be seen from the examples herein below, the porous media obtained according to the invention advantageously have a good to excellent antiviral activity according to the criteria of standard ISO 18184:2019-06, Annex 5, after a contact time of 5 hours with the human coronavirus strains HcoV-229E and HcoV-OC43 according to standards ISO 21702:2019 or ASTM E 1093, and in particular a very strong antiviral activity against viruses of the enveloped virus family, which activity showed a 2.5- and 3-log reduction in virus titer.

[0055] Cationic Sizing Agent

[0056] As described in more detail below, the combination of such a size with a quaternary ammonium-based biocidal compound, in particular a quaternary ammonium salt such as DDAC, makes it possible to significantly neutralize the negative effect of the quaternary ammonium-based compound on the hydrophobicity of the porous substrate to be treated.

[0057] Hydrophobicity is characterized as the resistance to water penetration and is therefore measured using the Cobb test (60 s), which uses a cylindrical impregnated template to measure the amount of water absorbed in the medium over a period of 60 s in g / m2. 2 This test is routinely used in the paper industry to characterize the absorbency of paper.

[0058] In particular, the cationic size may be selected from acrylonitrile, alkenyl ketene dimer (AnKD), alkyl ketene dimer (AKD), styrene acrylate (SAE), rosin, alkenyl succinic anhydride (ASA), and combinations thereof.

[0059] In particular, the cationic size may comprise at least one compound, in particular at least one compound selected from acrylonitrile, alkenyl ketene dimer (AnKD), alkyl ketene dimer (AKD), styrene acrylate (SAE), rosin, alkenyl succinic anhydride (ASA), and combinations thereof.

[0060] More particularly, the cationic sizing agent comprises at least one alkylketene dimer (AKD) and / or one styrene acrylate (SAE), more preferably at least one alkylketene dimer (AKD).

[0061] In particular, the cationic size comprises at least one styrene acrylate (SAE).

[0062] This is especially the case with surface sizes of the cationic alkylketene dimer type, e.g. Aquapel by Solenis. 商標 J 215 (AKD) or, alternatively, a surface size of the cationic styrene acrylate (SAE) type, for example a surface size of the type sold under the name Basoplast 270D by Solenis.

[0063] In particular, the cationic sizing agent is different from the quaternary ammonium based biocidal compounds used in the compositions according to the invention, in particular, the cationic sizing agent is different from a quaternary ammonium salt.

[0064] The composition according to the invention may in particular contain from 0.5% to 5% by weight, preferably from 1% to 4% by weight, more preferably from 1% to 3% by weight, relative to the total composition, of one or more commercially available cationic sizing products.

[0065] In particular, a quaternary ammonium based biocidal compound, preferably didecyldimethylammonium chloride, and one or more cationic sizes may be used in the composition according to the invention in a weight ratio of dry weight of the one or more quaternary ammonium based compounds / weight of the one or more commercially available cationic sizes products in the range of 0.1 to 0.5, preferably 0.25 to 0.375, more preferably 0.25 to 0.33.

[0066] According to a particular embodiment, the composition according to the invention may comprise from 0.08% to 1.5% by dry weight, preferably from 0.17% to 1.2% by dry weight, more preferably from 0.17% to 0.9% by dry weight, of cationic sizing agent relative to the total weight of the composition.

[0067] According to a particular embodiment, the quaternary ammonium based biocidal compound, preferably didecyldimethylammonium chloride, and the one or more cationic sizes are combined in a weight ratio of dry weight of the one or more quaternary ammonium based compounds / dry weight of the one or more cationic sizes of 0.25 to 5.9, in particular 0.3 to 3.6, preferably 0.8 to 2.5, more preferably 0.8 to 2.2.

[0068] As can be seen from the examples herein below, the porous media obtained according to the invention advantageously have a porosity of 50 g / m 2 or more, measured in 60 seconds in the Cobb test carried out according to the standard ISO 535:2014. 2 Preferably 20 to 40 g / m 2 , has a Cobb value of

[0069] Binder

[0070] In addition to a biocidal compound based on quaternary ammonium, in particular as defined above, in particular a quaternary ammonium salt, such as DDAC, and at least one cationic size, in particular as defined above, the composition according to the invention comprises at least one hydrophilic binder, which is called hydrophilic in view of its affinity for water and therefore for aqueous media.

[0071] In particular, the binder may be chosen from polyvinyl alcohol, starch, latex, in particular acrylic latex or acrylic copolymer latex, hemicellulose, carboxymethylcellulose (CMC), galactomannan, gelatin, polyurethane dispersions, and combinations thereof.

[0072] More particularly, this binder comprises at least one polyvinyl alcohol and / or one starch, more preferably at least one starch.

[0073] This may be, for example, potato starch, in particular oxidized potato starch, wheat starch or corn starch.

[0074] Thus, the composition according to the invention may contain from 1% to 50% by dry weight, preferably from 2% to 40% by dry weight, more preferably from 2% to 20% by dry weight, of one or more hydrophilic binders, relative to the total weight of the composition.

[0075] In addition to these three essential compounds, the compositions according to the invention may of course contain an aqueous solvent, in particular water, and any other compounds conventionally considered for the surface treatment of porous substrates, but also with regard to the biocidal activity desired according to the invention.

[0076] Auxiliary biocidal agent

[0077] Thus, compositions according to the invention may contain one or more bacteriostatic agents, bactericidal agents, fungistatic agents, fungicidal agents, levuricidal agents or virucidal agents other than the quaternary ammonium based biocidal compounds.

[0078] These agents are of course also selected having regard to their non-toxicity to humans under the conditions of use according to the present invention.

[0079] These one or more auxiliary biocides may in particular be chosen from p-[(diiodomethyl)sulfonyl]toluene, 3-iodo-2-propynyl butylcarbamate, methyl-1H-benzimidazol-2-ylcarbamate, monolaurin, compounds based on isothiazolone or isothiazolone derivatives, compounds based on chitosan or chitin derivatives, compounds based on zinc zeolites, compounds based on silver ions, in particular compounds based on silver chloride, compounds based on silver in supported particulate form, and compounds based on triclosan, and combinations thereof.

[0080] According to one variant, the composition according to the invention comprises at least one fungistatic and / or fungicidal agent chosen from compounds based on chitosan or chitin derivatives, compounds based on zinc zeolites, compounds based on silver ions, compounds based on silver in supported particulate form, and compounds based on triclosan, and combinations thereof.

[0081] According to one variant, the composition according to the invention comprises at least one bactericide and / or fungicide chosen from compounds based on isothiazolone or isothiazolone derivatives, compounds based on chitosan or chitin derivatives, compounds based on zinc zeolites, compounds based on silver ions, compounds based on silver in supported particle form, and compounds based on triclosan.

[0082] According to one variant, the composition according to the invention comprises at least one fungicidal and / or fungicidal agent based on p-[(diiodomethyl)sulfonyl]toluene.

[0083] According to one variant, the composition according to the invention comprises at least one fungicidal and / or fungicidal agent based on methyl-1H-benzimidazol-2-ylcarbamate.

[0084] According to one preferred variant, the composition according to the invention comprises at least 3-iodo-2-propynyl butylcarbamate (IPBC).

[0085] According to another variant, the composition according to the invention comprises at least one virucide, in particular a virucide of natural origin.

[0086] For purposes of this invention, the term "virucide" means a compound that has the ability to kill or inhibit viruses.

[0087] The virucidal agents according to the invention are more particularly intended to kill and / or inhibit viruses which are pathogenic for mammals, more particularly for humans.

[0088] Such viruses can be non-enveloped and enveloped viruses.

[0089] Examples of viruses that are pathogenic for humans and that may be considered according to the invention are more particularly retroviruses, cytomegaloviruses, rotaviruses, paramyxoviruses, polioviruses, hantaviruses, coxsackie viruses, encephalomyocarditis virus, picornaviruses, such as the above picornaviruses, including rhinoviruses, DNA or RNA viruses, in particular flaviviridae, AIDS viruses, influenza viruses, in particular H1N1, coronaviruses, in particular the human coronaviruses Hcov-229E, Hcov-0C43, SARS-COV-2, smallpox virus, yellow fever virus, hepatitis C virus, and the like. C virus), Ebola viruses, herpes viruses, Epstein-Barr virus, varicella zoster virus, rubella virus, and simian virus 40, or SV40.

[0090] "Naturally derived virucide" refers to any virucide that already exists in nature or that can be synthesized from natural compounds that exist in nature.

[0091] Thus, naturally occurring virucidal agents which may be used in the context of the present invention may be obtained by extraction and purification from the natural medium which contains them, or by synthesis from natural compounds.

[0092] Examples of such virucidal agents include, in particular, monolaurin, which can be obtained by synthesis from glycerol and lauric acid.

[0093] For purposes of the present invention, the term "monolaurin" refers to both naturally occurring monolaurin and monolaurin obtained synthetically from glycerol and lauric acid.

[0094] According to one embodiment, the naturally occurring virucidal agent may in particular be chosen from monolaurin, lactoferrin and essential oils with antiviral activity, such as bay leaf essential oil.

[0095] By way of example, the compositions of the invention may contain from 0.1% to 2.0% by dry weight, for example from 0.5% to 1.5% by dry weight, of one or more naturally occurring virucides, based on the total dry weight of the composition.

[0096] In a preferred embodiment, the adjunct biocide is at least monolaurin.

[0097] According to another particular embodiment, the composition according to the invention comprises at least one filler, in particular a mineral filler.

[0098] Such ingredients are particularly advantageous for imparting enhanced surface quality, in particular improving the coefficient of friction, on surface treatments formed by the compositions according to the invention.

[0099] The filler may be selected from mineral fillers, in particular colloidal silica, sodium silicate, sodium aluminosilicate, natural or precipitated calcium carbonate, talc, natural or calcined kaolin, alumina hydrate, titanium dioxide, aluminum silicate, barium sulfate, and combinations thereof, as well as from organic fillers, in particular plastic fillers or pigments. Preferably, the composition according to the invention comprises at least one mineral filler, in particular calcium carbonate.

[0100] Thus, the composition according to the invention may contain from 0.1% to 5% by weight, and preferably from 0.1% to 1% by weight, of fillers, in particular mineral fillers, relative to the total weight of the composition.

[0101] Porous media and methods of making same according to the present invention

[0102] porous media

[0103] As can be seen from the above, the present invention also provides a porous medium having all or a portion of its outer surface treated with a composition of the present invention, particularly so as to form a coating thereon.

[0104] This porous medium may advantageously be fibrous, in particular of the paper or cardboard type, in particular cardboard intended to form packaging cardboard, said cardboard being made from virgin fibres or, preferably, at least in part or in whole from recycled fibres.

[0105] The fibrous base material suitable for producing the medium is in particular formed from natural, artificial and / or synthetic fibers, and may also contain mineral fillers.

[0106] According to one embodiment of the invention, the fibers used in the composition of the substrate include natural fibers.

[0107] Natural fibers include cellulosic fibers, such as wood fibers, such as hardwood fibers, softwood fibers, or combinations thereof, cotton fibers, bamboo fibers, straw fibers, abaca fibers, esparto fibers, hemp fibers, jute fibers, flax fibers, sisal fibers, and combinations thereof.

[0108] The paper pulp used to form paper or cardboard may be either bleached, semi-bleached, or unbleached, and may be commonly referred to as bleached fiber, semi-bleached fiber, and non-bleached fiber, respectively.

[0109] Preferably, the fibers used in the composition of the substrate comprise cellulosic fibers, especially cotton fibers.

[0110] In particular, the cellulose fibres are a mixture of cotton fibres and wood fibres.

[0111] According to an advantageous variant, this substrate is formed at least partly or to a large extent from recycled fibres, for example fibres originating from the tritiation of waste paper.

[0112] According to another embodiment of the invention, the fibers used in the composition of the substrate may comprise synthetic fibers. The presence of synthetic fibers blended with cellulose fibers in the substrate according to the invention makes it possible to improve the tear resistance properties of the substrate.

[0113] In addition to these fibres, the porous, more particularly fibrous, substrates may of course contain other components commonly used in the paper or cardboard industry, in particular humectants, such as polyol type compounds, for example glycerol (also called glycerin), propylene glycol, polyethylene glycol, butylene glycol, glyceryl triacetate or sorbitol; fillers, in particular those defined above, and anionic or cationic bulk sizes, for example those intended to develop part of the hydrophobicity of the finished substrate.

[0114] In a preferred embodiment, the porous medium obtained according to the invention is a fibrous paper or cardboard medium for banknotes or security documents, or wrapping paper, or copy paper, or card support for the manufacture of packaging cardboard, in particular cardboard intended to form packaging cardboards, in particular flat cardboards or corrugated cardboards. The porous medium may also be leather or wood surfaces treated according to the invention.

[0115] Method for manufacturing porous media

[0116] In the method according to the invention, at least one of the external surfaces of the porous substrate concerned is contacted with a composition according to the invention under conditions conducive to the formation thereon of a deposit of said composition, and the deposit thus obtained is dried to form the expected porous medium.

[0117] The drying step may in particular be carried out at a temperature of 80° C. or more, for example 90° C. or more, preferably 100° C. or more.

[0118] This contacting step may be carried out according to various variations.

[0119] The formation of the deposit may be carried out according to different application methods of the composition.

[0120] According to one embodiment, the fibrous base material is immersed in a solution comprising at least the composition according to the invention.

[0121] According to another embodiment, a solution comprising at least the composition according to the invention is sprayed onto at least one lateral surface of said substrate.

[0122] According to another embodiment, at least one of the outer surfaces of the substrate is coated with a coating solution containing at least the composition according to the invention. The coating may be carried out by an air knife system, a curtain coater, by a pencil, a knife or a doctor blade system, by a roller, in particular a predosed roller, an engraved roller or a transfer roller, by a size press, by an impregnator or by a film press.

[0123] According to another embodiment, at least one of the outer surfaces of the substrate is surface treated with a surface treatment bath comprising at least the composition according to the invention.

[0124] According to another embodiment, the porous substrate, after having undergone a prior coating and / or surface treatment, is printed over part or all of its surface with an ink comprising at least a composition according to the invention.

[0125] According to another embodiment, an overprint varnish comprising at least one composition according to the invention is applied to at least one of the outer surfaces of the porous substrate, preferably after it has undergone a prior coating and / or surface treatment and printing. It can be applied by flexography, gravure printing or spraying.

[0126] These embodiments are particularly advantageous insofar as their implementation is compatible with conventional methods for producing porous media, especially fibrous media, especially paper-type porous media, i.e., simultaneously with conventional manufacturing processes.

[0127] Therefore, advantageously, no additional steps are required beyond those required for the manufacture of the medium.

[0128] These different methods of contacting the composition with one or more exterior surfaces of the substrate to be treated can of course be combined where appropriate, provided such combinations are compatible with the substrate exhibiting the desired biocidal activity and hydrophobicity properties.

[0129] application

[0130] The present invention relates to a method of using a porous medium, in particular a fibrous medium according to the invention, for producing paper for coverings (kraftliner or testliner) and / or corrugated materials used in the construction of packaging board.

[0131] The invention also relates to the use of a porous medium according to the invention for producing banknotes or security documents.

[0132] A banknote, security document or cardboard packaging according to the invention has the same properties as a porous medium according to the invention, measured according to the characterization methods defined for this fibrous medium.

[0133] The invention also relates to the use of the porous media according to the invention for producing paper, nonwoven materials and textiles, writing and printing papers, coated papers and copy papers.

[0134] According to one embodiment, the porous medium according to the invention is intended to form a security sheet incorporating at least one security element that allows the authentication of said sheet. In particular, said security element is selected from visual devices, in particular optical variable devices (also called OVD), holograms, lenticular devices, elements with interference effect, in particular iridescent elements, liquid crystals, pigments with magnetically orientable effects, and multi-layer interference structures. These optically variable devices may be present on a security thread incorporated in the fibrous substrate, or on a strip or patch applied or printed on the fibrous substrate. Other visual security elements include watermarks created during the process for manufacturing the fibrous substrate. In particular, the security elements are selected from what are known as luminescent elements; these luminescent elements can be revealed under UV or IR and can be in the form of security particles, security fibrets, security planchets or security threads incorporated in at least a part of the fibrous substrate, or strips or patches applied or printed on the fibrous substrate. In particular, the security elements are selected from elements that can be detected in an automated manner, in particular optically or magnetically, where these detectable elements are generally called markers or taggants and are incorporated in the fibrous medium or in the visual or luminescent security elements. The security sheet may also include a radio frequency identification device (also called RFID), which also provides the security sheet with the functions of identification and traceability.

[0135] According to one embodiment, the security sheet considered according to the invention is or forms part of a security document. Preferably, the security document considered according to the invention is an official document, in particular an ID document, a passport, a residence permit or a visa.

[0136] According to another embodiment, the porous medium according to the invention may be for forming a driver's license, an access card, a loyalty card, a photocopy card, a canteen card, a playing card, a collector's card, a payment instrument, in particular a payment card, a banknote, a voucher or a receipt, a ticket for a cultural or sporting event, a certificate of authenticity, a book or a magazine.

[0137] The following non-limiting examples will enable a better understanding of how the invention can be put into practice and its advantages.

[0138] Working Example

[0139] Materials and Methods

[0140] The following raw materials were used: a bath of carboxylated potato starch with an AI content of 8% or 10%, sold under the name Perfectamyl P 255SH by Avebe; Wheat starch; corn starch; a bulk sizing agent of the cationic styrene acrylate type with an active ingredient content of 26.5% sold under the name Fennosize KD 860D by Kemira; a surface sizing agent of the cationic styrene acrylate (SAE) type with an active ingredient content of 30%, sold under the name Basoplast 270D by Solenis; Aquapel by Solenis 商標 a cationic alkylketene dimer type surface size having a 15% content of the active ingredient AKD, sold under the name J 215 (AKD); Didecyldimethylammonium chloride (DDAC), sold by Thor, Stepan Europe and Lonza as a solution with a 50% content of the active ingredient DDAC; a solution of 3-iodo-2-propynyl butylcarbamate (IPBC) with a 20% content of the active ingredient IPBC, sold by Thor; Calcium carbonate sold by Omya under the name Hydrocarb 90 OG.

[0141] In the following examples, weight percentages are expressed as percentages by weight of the commercial source of the compounds according to the invention, unless otherwise specified.

[0142] 1. Test to evaluate hydrophobicity

[0143] The Cobb test, carried out according to ISO 535:2014, lasts for 60 seconds and makes it possible to characterize the absorption of water by the sample.

[0144] 2. Tests to evaluate wet recovery

[0145] The purpose of this test is to measure the weight of bath taken up during coating / surfacing by weighing the paper before and after coating / surfacing, without drying. 2 ) or weight percent of applied wet coating.

[0146] 3. Testing for antifungal properties

[0147] These are characterized by the textile standard AATCC-30 test 3 using Aspergillus niger van Thiegem (DSM 1957) and a fungistatic control according to AFNOR standard NFX41517 using a mixture of 10 strains with a contact time of 14 days.

[0148] 4. Testing for antiviral properties

[0149] All tests performed with the coronavirus strain HcoV-229E are carried out according to the standard ISO 21702:2019, but with a contact time of 5 hours.

[0150] All tests carried out with the coronavirus strain OC43 (ATCC VR-1558) are carried out according to the standard ASTM E1053, but with a contact time of 5 hours.

[0151] All tests carried out with bacteriophage MS2 are carried out according to the standard ISO18184:2019-06, but with a contact time of 18 h.

[0152] The results are expressed as logarithmic values ​​and correspond to the reduction in viral load for each contact time relative to a control without antimicrobial treatment.

[0153] 5. Measurement of the coefficient of friction

[0154] The coefficient of friction is determined in accordance with NF Q03-082, March 1984.

[0155] Example 1: Preparation of inventive and non-inventive biocidal compositions

[0156] A starch bath was prepared by cooking an aqueous starch composition of the carboxylated potato starch type (Perfectamyl P 255SH) at 90° C. for 20 minutes.

[0157] Compositions 1 and 2 of the present invention were prepared from this starch by mixing the respective surface sizes in the starch bath. Once a homogenous mixture was obtained, DDAC, and optionally IBPC, were added to the bath.

[0158] Control compositions 3-5 were prepared similarly.

[0159] The ratios used are shown in Table 1 below.

[0160] [Table 1]

[0161] Example 2: Preparation of inventive and non-inventive porous media by treatment of recycled pulp-based substrates

[0162] The porous substrates were manufactured according to conventional paper manufacturing methods from recycled pulp consisting of 100% recycled cardboard fibers, with or without the cationic styrene acrylate type bulk size Fennosize KD 860D, the content of which is given in Table 2 below as the weight % of the commercial product relative to the dry matter weight of the recycled pulp. 2 It has a weighing of .

[0163] The resulting substrates were surface treated in a size press with various compositions as detailed in Example 1.

[0164] [Table 2]

[0165] As can be seen from these results, detailed below, the compositions of the present invention, such as those in Tests A and B, make it possible to obtain an advantageous trade-off between the hydrophobic properties of the paper and the biocidal activity.

[0166] Thus, comparing Control C with Control D, when DDAC is present in the composition used to surface treat the fibrous substrate, the Cobb value is 30 g / m 2 ~186g / m 2 It was found that the hydrophilicity of the fibrous substrate increased sharply at 100° C., thus indicating hydrophilization of the fibrous substrate by DDAC.

[0167] However, a comparison of Test A with Control Test D shows that the use of the inventive composition 1 significantly reduces the Cobb value and therefore improves the hydrophobicity of the recycled paper. This same advantageous result was verified in Test B.

[0168] Moreover, the two culture media obtained according to Test A and Test B were found to contain the coronavirus HcoV-229, a representative of enveloped viruses. E It showed very strong antiviral activity against the virus, with a value of 2.5 log.

[0169] Finally, a comparison of the media obtained according to Test A and Test B demonstrated an improvement in antifungal activity when IPBC was added to Composition A.

[0170] Example 3: Production of inventive and non-inventive porous media from a substrate based on recycled pulp

[0171] A fibrous substrate was produced from a high-grade pulp consisting of 80% bleached softwood fibers and 20% eucalyptus kraft pulp, with or without the cationic styrene acrylate type bulk size Fennosize KD 860D, the content of which is given in Table 3 as a commercial weight percentage relative to the dry weight of the recycled pulp, The substrate thus obtained was surface treated according to the process described in Example 2, using one of the compositions detailed in Table 3 below.

[0172] [Table 3]

[0173] Comparison of Tests F and G according to the invention with Control Test H shows that the substrates treated with Compositions 1 and 2 of the invention have Cobb values ​​identical to the Cobb values ​​of the untreated substrate, despite the presence of DDAC. Thus, the combination of a surface sizing agent, such as cationic styrene acrylate, with DDAC makes it possible to restore the hydrophobicity of fibrous substrates that do not contain DDAC.

[0174] Comparison of the tests according to the invention with the control tests also demonstrates the improvement in antifungal activity obtained by surface treating fibrous substrates with the compositions according to the invention, according to both the AATCC 30 and NFX 41517 standards. It is also noted that the antifungal activity is further improved by the presence of IPBC in the compositions according to the invention, as demonstrated by test G.

[0175] Example 4: Preparation of inventive and non-inventive biocidal compositions

[0176] The following compositions 6 to 10 were prepared using cooked wheat starch according to the protocol already defined in Example 1, and Table 4 shows the proportions of their various components.

[0177] In the case of composition 10 of the present invention, the CaCO3 was first incorporated into the starch bath and stirred for an extended period until dispersed, prior to adding the other compounds.

[0178] Each of the compositions is based on non-recycled pulp and has a weight of 160 g / m 2The coatings are applied to one side of a fibrous paper substrate having a basis weight of 100 g / m2 and having a bulk sizing. Such substrates are conventionally used for packaging board. The surface treatment is carried out according to the pencil application process. Each of the coatings is analyzed for its hydrophobic properties as described above and the measured values ​​are shown in Table 4 below.

[0179] [Table 4]

[0180] These results confirm the effect of the presence of DDAC on hydrophobicity (Control J vs. Control I) and the effectiveness of the cationic sizing agent in restoring this hydrophobicity (Tests K-M vs. Control Test).

[0181] Antiviral activity was measured for Test M using the coronavirus strain OC43 according to the method described in the Materials and Methods section above. The resulting reduction in viral load was 3.1-log versus a reference fibrous substrate without antimicrobial treatment. Thus, the composition according to the invention was found to provide effective antiviral protection to fibrous substrates.

[0182] Test M also revealed that media treated with composition 10, which also contained calcium carbonate, had an advantageously improved coefficient of friction compared to the coefficient of friction observed in Test K.

[0183] Example 5: Preparation of a biocidal composition according to the invention

[0184] An aqueous starch bath was first prepared from 11.4% by weight cooked corn starch, and the whole was heated to 65° C. until a homogenous mixture was obtained.

[0185] Composition 11, comprising 96.5% by weight of cooked corn starch of this bath, 3.9% by weight of surface size Aquapel J 215 having an AI content of 15% by weight, and 0.5% by weight of DDAC solution having a DDAC content of 50% by weight, was prepared according to a protocol similar to that described in Example 1.

[0186] This composition 11 has a density of 190 g / m 2 The dry deposition weight was 9.5 g / m2 on a recycled pulp paper by surface treatment in a size press. 2 It was.

[0187] The Cobb value obtained according to the method detailed in the Materials and Methods section above was 49.2 g / m 2 The reduction in viral load caused by the coronavirus HCoV-229E strain was 1.6-log compared to the reference fibrous substrate without antimicrobial treatment.

[0188] The expected antiviral and hydrophobic properties were indeed observed.

[0189] Example 6: Preparation of a biocidal composition according to the invention

[0190] A composition 12 is prepared comprising 96% by weight of the commercial product Mowiol 10-98 having a polyvinyl alcohol content of 7.8% by weight, 2% by weight of a DDAC solution having a DDAC content of 80% by weight, 1.5% by weight of Basoplast 270D surface size having an AI content of 30% by weight, and 0.5% by weight of the commercial product Fennostrength XO (PAE resin).

[0191] The composition 12 thus formed was then mixed with 115 g / m 2 The dry deposition was 1.8 g / m2 on a paper of 100 mm diameter and 100 mm thickness by surface treatment in a size press. 2 It was.

[0192] The Cobb value was 42 g / m2, measured according to the method detailed in the Materials and Methods section above. 2 The viral load, assessed for the coronavirus OC43 strain according to the method described above, was greater than 3-log relative to the reference filamentous substrate without antimicrobial treatment.

[0193] The expected antiviral protection and hydrophobicity were indeed observed.

Claims

1. 1. A biocidal composition for the surface treatment of a porous substrate, comprising: at least one hydrophilic binder, The formula: (CH 3 ) 2 A 2 N + X - at least one biocidal compound based on quaternary ammonium selected from the non-polymeric quaternary ammonium salts of A may be the same or different and is a linear C 6 ~C 20 represents an alkyl group, and X - is an anion selected from a halide anion and a sulfonate anion, and At least one cationic sizing agent The biocidal composition comprising:

2. The biocidal composition of claim 1, wherein the cationic sizing agent is selected from alkenyl ketene dimer (AnKD), alkyl ketene dimer (AKD), styrene acrylate (SAE), rosin, alkenyl succinic anhydride (ASA), and combinations thereof.

3. 2. The composition of claim 1, comprising at least didecyl dimethyl ammonium chloride (DDAC), dioctyl dimethyl ammonium chloride, or octyl decyl dimethyl ammonium chloride.

4. The composition of claim 1, wherein the at least one cationic sizing agent comprises an alkyl ketene dimer (AKD) and / or a styrene acrylate (SAE).

5. The composition described in claim 1, wherein the hydrophilic binder is selected from polyvinyl alcohol, starch, latex, hemicellulose, carboxymethyl cellulose (CMC), galactomannan, gelatin, polyurethane dispersions, and combinations thereof.

6. The composition of claim 1, comprising from 1% to 50% by dry weight of one or more hydrophilic binders, based on the total weight of the composition.

7. 10. The composition of claim 1, comprising from 0.05% to 2.5% by dry weight of one or more quaternary ammonium based biocidal compounds, based on the total weight of the composition.

8. 2. The composition of claim 1, comprising from 0.08% to 1.5% by dry weight of one or more cationic sizing agents, based on the total weight of the composition.

9. The composition of claim 1 , wherein the composition further comprises at least one mineral filler.

10. The composition of claim 1, comprising from 0.1% to 5% by weight of one or more fillers, based on the total weight of the composition.

11. 10. The composition of claim 1, further comprising one or more bacteriostatic agents, one or more bactericidal agents, one or more fungistatic agents, one or more fungicidal agents, one or more yeasticides, or one or more virucide agents other than the quaternary ammonium based biocidal compound.

12. The composition of claim 1 comprising water.

13. 13. A porous medium having surface biocidal properties and having on all or part of at least one of its outer surfaces a coating formed from a composition according to any one of claims 1 to 12.

14. 50g / m2, measured for 60 seconds using the Cobb test performed according to standard ISO 535:2014 2 14. The porous medium of claim 13 having a Cobb value of:

15. The porous medium of claim 13, wherein the porous medium is fibrous.

16. 14. A method for producing a porous medium having surface biocidal properties according to claim 13, comprising the steps of: a) providing a porous substrate; b) contacting all or a portion of at least one of the exterior surfaces of the porous substrate with a composition according to any one of claims 1 to 12 under conditions conducive to forming a deposit of the composition thereon; and c) drying the deposit to form a porous medium with biocidal properties. The method comprises at least the steps of:

17. Use of a composition according to any one of claims 1 to 12 to impart biocidal properties to a porous substrate or to increase the hydrophobicity of a porous substrate.

18. 14. Use of the porous medium according to claim 13 for producing banknotes or security sheets, or printing, writing or copying paper, or for producing packaging cardboard, or for producing paper, nonwoven material or textile fabric, writing or printing paper, coated paper or copy paper.