Decorative laminate, decorative film, decorative molded article, moving object, method for manufacturing decorative laminate, and method for manufacturing decorative molded article

Abstract

To provide a decorative laminate in which a design to be displayed is made close to a design by coating with a paint.SOLUTION: The decorative laminate 30 has a first surface 30A and a second surface 30A opposite to the first surface 30B. The decorative laminate 30 includes a base material layer 31, a front surface layer 33 disposed closer to the first face 30B than to the second face 30A with respect to the base material layer 31, and a design layer 40 supported by the base material layer 31. The design layer 40 includes a photoluminescent layer containing a photoluminescent material.SELECTED DRAWING: Figure 5

Description

[Technical Field]

[0001] The present disclosure relates to a decorative laminate, a decorative film having a decorative laminate, a decorated molded article having a decorative laminate, a mobile body having a decorated molded article, a method for manufacturing a decorative laminate, and a method for manufacturing a decorated molded article. [Background technology]

[0002] A paint such as that described in JP 2009-287031 A is applied to exterior members of a moving body such as an automobile. By applying the paint to the exterior members, the moving body has an excellent appearance. DISCLOSURE OF THE INVENTION

[0003] In the process of painting with paint, carbon dioxide is indirectly emitted due to volatile organic compounds contained in the paint and energy consumption in the drying process. When painting exterior components of large mobile bodies such as automobiles with paint, large amounts of volatile organic compounds and carbon dioxide are generated. In recent years, environmental concerns have been growing. In order to reduce the amount of volatile organic compounds and carbon dioxide generated, it has been considered to impart designs to exterior components of mobile bodies using decorative films having decorative laminates. In order to impart designs to exterior components of mobile bodies using decorative films instead of painting with paint, there is a demand for designs displayed by decorative laminates that are closer to designs created by painting with paint. The present disclosure aims to make designs displayed by decorative laminates closer to designs created by painting with paint.

[0004] An embodiment of the present disclosure relates to the following [1] to

[31] . [1] A decorative laminate having a first surface and a second surface opposite to the first surface, a substrate layer; a surface layer disposed closer to the first surface than the second surface with respect to the base layer; A design layer supported on the base layer, The decorative laminate includes a design layer including a photoluminescent layer containing a photoluminescent material. [2] The decorative laminate according to [1], wherein the glittering layer has a thickness of 100 μm or less. [3] The decorative laminate according to [1] or [2], wherein the glittering layer further contains a colorant. [4] The decorative laminate according to any one of [1] to [3], wherein the design layer further includes a colored layer containing a colorant. [5] The decorative laminate according to [4], wherein the design layer further includes a transparent layer disposed between the colored layer and the glittering layer. [6] The decorative laminate according to any one of [1] to [5], wherein the design layer further includes a second photoluminescent layer that is overlaid on the photoluminescent layer and contains a photoluminescent material. [7] The decorative laminate according to [6], wherein the content of the glittering material contained in the glittering layer is different from the content of the glittering material contained in the second glittering layer. [8] the glittering layer is disposed closer to the second surface than to the first surface relative to the second glittering layer, The decorative laminate according to [6] or [7], wherein the content of the photoluminescent material contained in the second photoluminescent layer is lower than the content of the photoluminescent material contained in the first photoluminescent layer. [9] the glittering layer contains a colorant, the second glittering layer contains a colorant, The decorative laminate according to any one of [6] to [8], wherein the content of the colorant contained in the glittering layer is different from the content of the colorant contained in the second glittering layer.

[10] the glittering layer is disposed closer to the second surface than to the first surface relative to the second glittering layer, The decorative laminate according to [9], wherein the content of the colorant contained in the second glittering layer is lower than the content of the colorant contained in the glittering layer.

[11] The decorative laminate according to any one of [1] to

[10] , further comprising a concealing layer disposed closer to the second surface than the first surface with respect to the design layer.

[12] The decorative laminate according to any one of [1] to

[11] , further comprising a reflective layer disposed closer to the second surface of the design layer than to the first surface.

[13] The decorative laminate according to any one of [1] to

[12] , further comprising a backer layer arranged closer to the second surface of the design layer than to the first surface.

[14] The decorative laminate according to

[13] , wherein the backer layer contains a colorant.

[15] The additive laminate according to

[14] , wherein the color of the backer layer is the same or similar color as the color of the design layer.

[16] The decorative laminate according to any one of

[13] to

[15] , further comprising an adhesive layer disposed between the backer layer and the design layer.

[17] The decorative laminate according to

[16] , wherein the adhesive layer contains a colorant.

[18] The decorative laminate according to any one of [1] to

[17] , wherein the base layer contains a colorant.

[19] The decorative laminate according to any one of [1] to

[18] , further comprising a buffer layer disposed closer to the second surface of the surface layer than to the first surface.

[20] A decorative laminate having a first surface and a second surface opposite to the first surface, a substrate layer; a design layer disposed closer to the second surface than the first surface with respect to the base layer and supported by the base layer; a backer layer disposed closer to the second surface than the first surface with respect to the design layer; The design layer includes a colored layer containing a colorant and a glittering layer containing a glittering material, the backer layer comprises a colorant; A decorative laminate, wherein the color of the backer layer is the same color as or similar to the color of the colored layer. [twenty one] [1] to

[20] , and the decorative laminate according to any one of [1] to

[20] . a bonding layer provided on the second surface of the decorative laminate. [twenty two] The decorative film according to

[21] , wherein the bonding layer is a heat seal layer. [twenty three] The decorative film according to

[21] , wherein the bonding layer is an adhesive layer. [twenty four] [1] to

[20] , and the decorative laminate according to any one of [1] to

[20] . a decorative film provided on the first surface of the decorative laminate; or The decorative film according to any one of

[21] to

[23] , further comprising a protective film provided on the first surface of the decorative laminate. [twenty five] The decorative laminate according to any one of [1] to

[20] or the decorative film according to any one of

[21] to

[24] , a molded portion disposed closer to the second surface than to the first surface.

[26]

[25] The decorated molded product according to

[25] , A moving body part comprising: the decorated molded product; and a painted part adjacent to the decorated molded product.

[27]

[25] Two decorative molded products are provided, The two decorated molded products are mobile body parts that differ in at least one of the elongation rate during molding, the molding method, and the material of the molded portion.

[28] A moving body comprising the decorated molded product according to

[25] or the moving body part according to

[26] or

[27] .

[29] A decorative laminate having a first surface and a second surface opposite to the first surface, a substrate layer; a surface layer disposed closer to the first surface than the second surface with respect to the base layer; A design layer supported on the base layer, The decorative laminate includes a design layer including a colored layer containing a colorant.

[30] forming a glittering layer containing a glittering material on a substrate layer by printing or coating; and forming a surface layer that forms a first surface.

[31]

[30] A step of vacuum forming the decorative laminate manufactured by the method according to

[30] ; and forming a molding portion near a second surface of the decorative laminate opposite to the first surface from the first surface, A method for manufacturing a decorated molded product, wherein the content of the glittering material contained in the glittering layer is determined according to the elongation rate of the decorative laminate in the step of vacuum-forming the decorative laminate.

[0005] According to the present disclosure, the design displayed by the decorative laminate can be made to resemble a design painted with paint. [Brief explanation of the drawings]

[0006] [Figure 1] FIG. 1 is a perspective view of a moving body including a decorated molded product. [Figure 2] FIG. 2 is a cross-sectional view of the decorated molded product. [Figure 2A] FIG. 2A is a cross-sectional view of a modified example of the decorated molded product. [Figure 2B] FIG. 2B is a cross-sectional view of another modified example of the decorated molded product. [Figure 3] FIG. 3 is a cross-sectional view of the decorative film. [Figure 4] FIG. 4 is a cross-sectional view of the decorative laminate of the first example. [Figure 5] FIG. 5 is a cross-sectional view of the decorative laminate of the second example. [Figure 6] FIG. 6 is a cross-sectional view of the design layer of the first example. [Figure 7] FIG. 7 is a cross-sectional view of the design layer of the second example. [Figure 8] FIG. 8 is a cross-sectional view of the design layer of the third example. [Figure 9] FIG. 9 is a cross-sectional view of the design layer of the fourth example. [Figure 10]FIG. 10 is a cross-sectional view of the design layer of the fifth example. [Figure 11] FIG. 11 is a cross-sectional view of the design layer of the sixth example. [Figure 12] FIG. 12 is a cross-sectional view of the design layer of the seventh example. [Figure 13] FIG. 13 is a cross-sectional view of the design layer of the eighth example. [Figure 14] FIG. 14 is a cross-sectional view of a decorative laminate of the third example. [Figure 15] FIG. 15 is a cross-sectional view of a decorative laminate of the fourth example. [Figure 16] FIG. 16 is a cross-sectional view of the decorative laminate of the fifth example. [Figure 17] FIG. 17 is a cross-sectional view of the decorative laminate of the sixth example. [Figure 18] FIG. 18 is a diagram illustrating an example of a method for manufacturing a decorative laminate. [Figure 19] FIG. 19 is a diagram illustrating an example of a method for manufacturing a decorative laminate. [Figure 20] FIG. 20 is a diagram for explaining an example of a method for manufacturing a decorative film. [Figure 21] FIG. 21 is a cross-sectional view showing a state in which a decorated molded product and a painted part are adjacent to each other. [Figure 22] FIG. 22 is a cross-sectional view showing two different decorated molded articles adjacent to each other. DETAILED DESCRIPTION OF THE INVENTION

[0007] An embodiment of the present disclosure will be described below with reference to the drawings. In the drawings accompanying this specification, the scale and aspect ratios may be appropriately changed and exaggerated from those of the actual objects for the sake of illustration and ease of understanding. Configurations shown in some drawings may be omitted in other drawings.

[0008] In this specification, terms such as "parallel," "orthogonal," and "identical," which specify shapes and geometric conditions and their degrees, as well as values ​​of lengths and angles, are not limited to their strict meanings but are interpreted to include a range of degrees within which similar functions can be expected.

[0009] In this specification, when multiple upper limit value candidates and multiple lower limit value candidates are listed for a parameter, the parameter may be a numerical range that combines any one upper limit value candidate and any one lower limit value candidate.

[0010] FIG. 1 illustrates a mobile object 1 according to an embodiment of the present disclosure. The mobile object 1 is a movable device or equipment. In the example illustrated in FIG. 1, the mobile object 1 is an automobile. The mobile object 1 may be a motorcycle, bicycle, tricycle, train, airplane, ship, snowmobile, industrial robot, drone, etc. The automobile may be a truck, bus, taxi, ambulance, fire engine, police vehicle, construction vehicle, etc.

[0011] The moving body 1 has a decorative molded article 10. In the example shown in FIG. 1, an automobile has the decorative molded article 10 as a part of an exterior member. The part of the exterior member of the automobile is, for example, at least one of a roof, a hood, a fender, a bumper, a mirror, a door, a pillar, a sill, and a trunk lid. In the example shown, the automobile has the decorative molded article 10 as a roof 5. The moving body 1 may have a plurality of decorative molded articles 10.

[0012] The decorated molded article 10 may include a flat portion on its surface. The decorated molded article 10 may include a curved portion on its surface. Fig. 2 shows a cross-sectional view of the decorated molded article 10. In Fig. 2, the decorated molded article 10 is shown as a flat surface overall for ease of understanding.

[0013] As shown in FIG. 2, the decorated molded article 10 includes a molded portion 11 and a decorative film 20. The decorative film 20 includes a bonding layer 21 and a decorative laminate 30. The decorative laminate 30 includes a first surface 30A and a second surface 30B. The decorative laminate 30 is sheet-shaped. The first surface 30A and the second surface 30B are main surfaces of the decorative laminate 30. The second surface 30B is the surface opposite the first surface 30A. The bonding layer 21 is provided on the second surface 30B of the decorative laminate 30. In the illustrated example, the molded portion 11 is bonded to the decorative film 20 by the bonding layer 21. The bonding layer 21 may be omitted in the decorated molded article 10. The presence or absence of the bonding layer 21 can be appropriately selected depending on the molding method and the combination of the materials of the molded portion 11 and the decorative laminate 30. The molded portion 11 is disposed closer to the second surface 30B than to the first surface 30A of the decorative laminate 30. The first surface 30A of the decorative laminate 30 forms the surface of the decorative film 20 and the decorated molded article .

[0014] The molded portion 11 is the main body of the exterior member. The molded portion 11 is a member to be decorated that is decorated with the decorative film 20. The molded portion 11 has the shape of at least a part of the exterior member of the mobile object 1. For example, the molded portion 11 has the shape of the roof of an automobile. The molded portion 11 is produced by molding, for example, a thermoplastic material. The molded portion 11 can be formed into a desired shape by molding. Examples of materials for the molded portion 11 include metal, glass, and resin. Examples of resins include acrylic resin, polycarbonate resin, acrylonitrile-butadiene-styrene copolymer, polycarbonate resin, polypropylene resin, and fiber-reinforced plastic.

[0015] When the molded portion 11 is provided in the decorative film 20 by insert molding (also called film insert molding) or in-mold molding, the material of the molded portion 11 is, for example, resin. When the molded portion 11 is provided in the decorative film 20 by TOM (Three Dimension Overlay Method) molding, the material of the molded portion 11 is, for example, metal, glass, or resin. When the molded portion 11 is provided in the decorative film 20 by lamination, the material of the molded portion 11 is, for example, metal, glass, or resin.

[0016] When the molded portion 11 is made of metal, the decorated molded product 10 may further include an electrodeposition coating film 13 formed between the molded portion 11 and the decorative film 20 as an undercoat, as shown in FIG. 2A . In this case, the decorative film 20 can replace the intermediate and top coats in conventional painting. When the molded portion 11 is made of metal, the decorated molded product 10 may further include an anti-rust plating layer 15 formed on the surface of the molded portion 11 for rust prevention, as shown in FIG. 2B . The anti-rust plating layer 15 may be, for example, a zinc alloy plating film or an iron-nickel alloy plating film. When the molded portion 11 is made of metal, the molded portion 11 may be produced by applying the decorative film 20 to a molded metal plate. Alternatively, when the molded portion 11 is made of metal, the molded portion 11 may be produced by applying the decorative film 20 to a metal plate to form a laminated metal plate, and then molding the laminated metal plate.

[0017] The bonding layer 21 bonds the decorative film 20 to the molded portion 11. The bonding layer 21 is provided on the surface of the decorative film 20. The bonding layer 21 may be a heat seal layer or an adhesive layer. When the molded portion 11 is provided on the decorative film 20 by insert molding, the bonding layer 21 is preferably a heat seal layer. When the molded portion 11 is provided on the decorative film 20 by TOM molding, or when the decorative film 20 is attached to the molded portion 11, the bonding layer 21 is preferably an adhesive layer.

[0018] The heat seal layer exhibits adhesiveness when heated and is bonded to other members. The heat seal layer exhibits appropriate adhesiveness and has a thickness that prevents the decorative film 20 from becoming too thick. The thickness of the heat seal layer may be 0.2 μm or more, or 20 μm or less. The material of the heat seal layer is, for example, vinyl chloride-vinyl acetate copolymer, acrylic resin, polyester resin, or urethane resin.

[0019] The adhesive layer exhibits adhesiveness and is bonded to other components by applying pressure. The adhesive layer exhibits appropriate adhesiveness and has a thickness that prevents the decorative film 20 from becoming too thick. The thickness of the adhesive layer may be 5 μm or more or 300 μm or less. The material of the adhesive layer is, for example, an adhesive such as acrylic resin, urethane resin, silicone resin, or rubber. Before bonding the decorative film 20 to the molded portion 11, the adhesive layer may be covered with a peelable separator (not shown) to prevent the decorative film 20 from unintentionally adhering to other components.

[0020] FIG. 3 shows a cross-sectional view of an example of the decorative film 20 before being bonded to the molded portion 11. In the example shown in FIG. 3, the decorative film 20 includes a protective film 23. The protective film 23 is provided on the first surface 30A of the decorative laminate 30. The protective film 23 protects the first surface 30A of the decorative laminate 30. More specifically, the protective film 23 protects a surface layer 33 (described below) disposed on the first surface 30A of the decorative laminate 30. The protective film 23 is peelable from the decorative laminate 30. The protective film 23 is thin. The thickness of the protective film 23 may be 10 μm or more or 100 μm or less. The material of the protective film 23 is, for example, polyethylene terephthalate (PET), polyester, or polyethylene.

[0021] The decorative laminate 30 displays a design. A decorated molded product 10 including the decorative laminate 30 can display an excellent design. A mobile object 1 including the decorated molded product 10 exhibits an excellent appearance. The decorative laminate 30 may display a design such as a color or a geometric pattern. The decorative laminate 30 may display a design with a metallic or leather-like texture. The decorative laminate 30 may display a glossy or matte design. The image clarity of the design displayed by the decorative laminate 30 may be 60 or more or 95 or less. When the decorative laminate 30 displays a glossy design such as a metallic or matte design, the image clarity is measured using a Wavescan device (manufactured by BYK Japan, product name: Wavescan Dual AW-4840) to measure the measurement value "Distinctness of Image (DOI)." By displaying such an image clarity design in the decorative laminate 30, a moving body 1 such as an automobile including the decorative laminate 30 can present a painted metallic or non-metallic (also called solid painted) design.

[0022] Below, we will explain several examples of the decorative laminate 30. The same reference numerals will be used for corresponding parts in each example, and if the explanation is redundant, the explanation will be omitted.

[0023] Fig. 4 shows a cross-sectional view of a first example of a decorative laminate 30. In the example shown in Fig. 4, the decorative laminate 30 includes, in this order from the first surface 30A to the second surface 30B, a surface layer 33, a base layer 31, and a design layer 40. Fig. 5 shows a cross-sectional view of a second example of a decorative laminate 30. In the example shown in Fig. 5, the decorative laminate 30 includes, in this order from the first surface 30A to the second surface 30B, a surface layer 33, a design layer 40, and a base layer 31.

[0024] The base material layer 31 supports the other layers included in the decorative laminate 30, in particular the design layer 40. The base material layer 31 is in the form of a film. The base material layer 31 is transparent. The thickness of the base material layer 31 may be 50 μm or more, or 75 μm or more. The thickness of the base material layer 31 may be 150 μm or less, or 125 μm or less.

[0025] The material of the base layer 31 is, for example, a thermoplastic resin. Examples of the material of the base layer 31 include (meth)acrylic resin, polyolefin (e.g., polyethylene, polypropylene, etc.), polyester (e.g., polyethylene naphthalate, polyethylene terephthalate, polybutylene terephthalate, etc.), polyamide, polycarbonate, cellulose resin, urethane resin (e.g., thermoplastic polyurethane, etc.), fluorine-based resin (e.g., polyvinylidene fluoride (PVDF), perfluoroalkoxyalkane (PFA), ethylene-tetrafluoroethylene copolymer (ETFE), perfluoroethylenepropene copolymer (FEP), polytetrafluoroethylene (PTFE), etc.), ABS resin, polycarbonate resin, and cellulose resin. From the viewpoint of transparency, the material of the base layer 31 is preferably a (meth)acrylic resin. Examples of the (meth)acrylic resin include a homopolymer or copolymer of a (meth)acrylic acid ester, and a copolymer of a (meth)acrylic acid ester and a comonomer. Examples of (meth)acrylic acid esters include methyl (meth)acrylate, ethyl (meth)acrylate, butyl (meth)acrylate, 2-ethylhexyl (meth)acrylate, hydroxyethyl (meth)acrylate, hydroxypropyl (meth)acrylate, dimethylaminoethyl (meth)acrylate, and glycidyl (meth)acrylate. Examples of comonomers include vinyl acetate, (meth)acrylonitrile, (meth)acrylamide, styrene, (meth)acrylic acid, itaconic acid, and maleic anhydride. The (meth)acrylic resin may be fluorine-modified. The material of the substrate layer 31 may be a single layer containing two or more of the above-mentioned resins, or may be composed of multiple layers. A substrate layer 31 composed of multiple layers can be produced, for example, by coextrusion.

[0026] The base layer 31 may contain a colorant. The color of the colorant contained in the base layer 31 may be chromatic or achromatic. The colorant can be used to color the base layer 31 to a desired color. The base layer 31 becomes colored and transparent. The color exhibited by the base layer 31 may be the same as the color exhibited by the backer layer 37 in the decorative laminate 30 of the third example described below. The colorant may have the same composition as the colorant contained in the glittering layer 41 and colored layer 43 of the design layer 40 described below.

[0027] In this specification, "transparent" means that the material has a transparency to the extent that it is possible to see through it from one side to the other side, and for example, has a visible light transmittance of 30% or more, more preferably 70% or more. In this specification, "colored transparent" means that the transmittance of light in a specific wavelength range is intentionally reduced, but the transmittance of visible light as a whole is high, resulting in transparency.

[0028] In this specification, visible light transmittance is specified as the average value of the total light transmittance at each wavelength when measured in 1 nm increments within a wavelength range of 380 nm to 780 nm using a spectrophotometer (Shimadzu Corporation's "UV-3600i Plus," compliant with JIS K0115). The angle of incidence when measuring visible light transmittance is set to 0° unless a specific transmission direction is specified. The angle of incidence is the angle between the normal to the incident surface and the propagation direction of the incident light, and is a value less than 90°.

[0029] The surface layer 33 protects the other layers of the decorative laminate 30. The surface layer 33 has various functions, such as abrasion resistance, weather resistance, and chemical resistance. The surface layer 33 has, for example, the abrasion resistance, weather resistance, and chemical resistance required for exterior parts of automobiles and the like, as well as the extensibility required for molding. The surface layer 33 is disposed closer to the first surface 30A of the base material layer 31 than the second surface 30B. The surface layer 33 forms the first surface 30A of the decorative laminate 30. The surface layer 33 forms the surface of the decorated molded product 10. The surface layer 33 is in the form of a thin film. The surface layer 33 is transparent. The thickness of the surface layer 33 may be 1 μm or more, or may be 2 μm or more. The thickness of the surface layer 33 may be 20 μm or less, or may be 10 μm or less. The material of the surface layer 33 is a cured product of a curable resin composition. More specifically, the material of the surface layer 33 is a cured product of an ionizing radiation curable resin composition. In each example of the decorative laminate 30, the surface layer 33 can have any configuration.

[0030] Examples of the curable component contained in the curable resin composition include a thermosetting component and an active energy ray-curable component. From the viewpoints of weather resistance, abrasion resistance, and chemical resistance, the active energy ray-curable component is preferred.

[0031] The thermosetting component is, for example, a thermosetting resin such as an epoxy resin, a melamine resin, a guanamine resin, a urea resin, an unsaturated polyester, a thermosetting urethane resin, a thermosetting (meth)acrylic resin, or an aminoalkyd resin.

[0032] The active energy ray-curable component is a component that cures when irradiated with active energy rays. Examples of active energy rays include electromagnetic waves such as ultraviolet rays (UV), X-rays, and gamma rays; and charged particle rays such as electron beams (EB), alpha rays, and ion beams.

[0033] The active energy ray curable component is, for example, a compound having at least one functional group selected from a vinyl group, an allyl group, and a (meth)acryloyl group. Examples of the active energy ray curable component include oligomers or polymers such as urethane (meth)acrylate, epoxy (meth)acrylate, polyester (meth)acrylate, and polyether (meth)acrylate; polyfunctional (meth)acrylate monomers such as trimethylolpropane tri(meth)acrylate, pentaerythritol tri(meth)acrylate, pentaerythritol tetra(meth)acrylate, dipentaerythritol tri(meth)acrylate, dipentaerythritol tetra(meth)acrylate, dipentaerythritol penta(meth)acrylate, dipentaerythritol hexa(meth)acrylate, and tris(2-(meth)acryloxyethyl)isocyanurate; and modified products thereof. The active energy ray-curable component may be a mono(meth)acrylate having one (meth)acryloyl group in the molecule.

[0034] The curable resin composition may contain a photopolymerization initiator in addition to the active energy ray-curable component.

[0035] The surface layer 33 may contain a weather resistance improver, which can improve the weather resistance of the surface layer. Examples of the weather resistance improver include an ultraviolet absorber, an antioxidant, and a hindered amine light stabilizer. The content of the weather resistance improver in the surface layer 33 may be 0.1% by mass or more. The content of the weather resistance improver in the surface layer 33 may be 10% by mass or less, or 5% by mass or less.

[0036] When the decorative film 20 includes the protective film 23, the surface layer 33 is protected by the protective film 23. In a state protected by the protective film 23, the curable resin composition that is the material of the surface layer 33 may not be cured or may be in a semi-cured state. The protective film 23 may be peeled off from the surface layer 33 before the curable resin composition is cured, or the protective film 23 may be peeled off from the surface layer 33 after the curable resin composition is cured.

[0037] The design layer 40 forms the design displayed by the decorative laminate 30. The design layer 40 is supported by the base layer 31. The design layer 40 includes at least one of a glossy layer 41 and a colored layer 43. The design layer 40 may include the glossy layer 41, a second glossy layer 42, the colored layer 43, and a transparent layer 45.

[0038] Below, we will explain several examples of the design layer 40. The same reference numerals will be used for corresponding parts in each example, and if the explanation is redundant, the explanation will be omitted.

[0039] Fig. 6 shows a cross-sectional view of the design layer 40 of the first example. In the example shown in Fig. 6, the design layer 40 includes a glittering layer 41. In the example shown, the design layer 40 consists of only the glittering layer 41.

[0040] The glittering layer 41 reflects light to give it a glossy appearance. * a * b * In the color system, the color exhibited by the glittering layer 41 is SCE L * The value of SCI L of the color exhibited by the glittering layer 41 may be 10 or more, 25 or more, 35 or more, 60 or less, 50 or less, or 48 or less. * The value may be 20 or more, 30 or more, 40 or more, 90 or less, 80 or less, or 65 or less.

[0041] The color of the glittering layer 41 is L * a * b * SCE L in color space * The value of SCI L * The color can be measured using a spectrophotometer (Konica Minolta "CM-700d") under the following conditions: a measurement diameter of 8 mm, a viewing angle of 10 degrees. *A black plate with a value of 29.9 is placed on the surface opposite to the surface on which the black plate is placed. Light from a D65 light source is irradiated on the surface opposite to the surface on which the black plate is placed. By subtracting specular reflection from the total reflection light on the material being measured, the SCE L of the material is calculated. * The value of SCI L of the material is determined from the total reflection light at the material being measured. * The value of is specified.

[0042] The glittering layer 41 includes a binder resin 41a and a glittering material 41b. The glittering material 41b is encapsulated in the binder resin 41a. The content of the glittering material 41b in the glittering layer 41 may be 3% by mass or more, or 75% by mass or less. The visible light transmittance of the glittering layer 41 may be 0.5% or more, or 1% or more. The visible light transmittance of the glittering layer 41 may be 95% or less, or 90% or less. The thickness of the glittering layer 41 may be 2 μm or more, or 3 μm or more, or 100 μm or less.

[0043] The binder resin 41a is, for example, a resin such as urethane resin, acrylic polyol resin, acrylic resin, ester resin, amide resin, butyral resin, styrene resin, urethane-acrylic copolymer, vinyl chloride-vinyl acetate copolymer resin, vinyl chloride-vinyl acetate-acrylic copolymer resin, chlorinated propylene resin, nitrocellulose resin, or cellulose acetate resin.

[0044] The glittering material 41b reflects light. Examples of the glittering material 41b include aluminum flakes, mica, and pearl pigments. The glittering material 41b is oriented in a direction along the surface on which the glittering layer 41 is formed. The average particle size of the glittering material 41b is within a range in which light is appropriately reflected by the glittering layer 41. If the average particle size of the glittering material 41b is too small, the glittering layer 41 does not sufficiently reflect light. If the average particle size of the glittering material 41b is too large, the glittering material 41b does not orient along the surface on which the glittering layer 41 is formed, causing diffuse reflection of light by the glittering layer 41, resulting in the glittering layer 41 not exhibiting a glossy appearance. The thickness of the glittering material 41b may be 20 nm or more. The thickness of the glittering material 41b may be 1 μm or less, 700 nm or less, 500 nm or less, or 300 nm or less. The average particle size of the glittering material 41b may be 5 μm or more, 10 μm or more, 25 μm or less, or 15 μm or less.

[0045] The average particle size of the photoluminescent material 41b is determined as follows: The photoluminescent layer 41 is magnified with a microscope to observe each individual photoluminescent material 41b. The particle size of each photoluminescent material 41b is measured from the observed photoluminescent material 41b. If the photoluminescent material 41b has a minor axis diameter and a major axis diameter, the average of these diameters is taken as the particle size of the photoluminescent material 41b. If the photoluminescent material 41b is aggregated, the particle size of the photoluminescent material 41b is taken as the diameter of the inscribed circle of the aggregated portion. The particle sizes of 100 photoluminescent materials 41b are measured, and the average is taken as the average particle size of the photoluminescent material 41b in the photoluminescent layer 41.

[0046] For example, when the decorative laminate 30 stretches during molding, the planar arrangement of the photoluminescent material 41b in the photoluminescent layer 41 may change before and after the stretching. Taking this into consideration, the photoluminescent materials 41b in the photoluminescent layer 41 may be arranged so as to overlap in the stacking direction in a cross-sectional view. Specifically, a photoluminescent material 41b in the photoluminescent layer 41 may be arranged so as to at least partially overlap with another photoluminescent material 41b located above or below it in the stacking direction. A photoluminescent material 41b in the photoluminescent layer 41 may overlap with one or more other photoluminescent materials 41b in the stacking direction, or may overlap with two or more other photoluminescent materials 41b in the stacking direction, or may overlap with three or more other photoluminescent materials 41b in the stacking direction.

[0047] FIG. 7 shows a cross-sectional view of the design layer 40 of the second example. In the example shown in FIG. 7, the design layer 40 includes a glittering layer 41. In the example shown, the design layer 40 consists only of the glittering layer 41. The glittering layer 41 reflects light to give it a glossy appearance and displays color. The glittering layer 41 includes a binder resin 41a, a glittering material 41b, and a colorant 41c. The glittering material 41b and the colorant 41c are encapsulated in the binder resin 41a.

[0048] The colorant 41c colors the glittering layer 41 in a desired color. The color of the colorant 41c may be chromatic or achromatic. The colorant 41c is a dye or a pigment. The colorant 41c may be a combination of a dye and a pigment. The colorant 41c is a material different from the glittering material 41b. For example, aluminum flakes, mica, and pearl pigments are not used as the colorant 41c. Considering weather resistance, the colorant 41c is preferably a pigment. The pigment may be a colored pigment or a fluorescent pigment. The coloring pigment may be an organic pigment, such as a quinacridone pigment (e.g., quinacridone red), an azo pigment (e.g., pigment red), a phthalocyanine pigment (e.g., phthalocyanine blue, phthalocyanine green), or a perylene pigment (e.g., perylene red), or an inorganic pigment (e.g., titanium oxide, carbon black). If the average particle size of the colorant 41c is too large, the colorant 41c may inhibit light reflection from the glittering material 41b. If the average particle size of colorant 41c is too small, colorant 41c will aggregate too much. The average particle size of colorant 41c may be 5 nm or more, or 1500 nm or less. The average particle size of colorant 41c can be determined in the same manner as the average particle size of glittering material 41b.

[0049] Fig. 8 shows a cross-sectional view of the design layer 40 of the third example. In the example shown in Fig. 8, the design layer 40 includes a glittering layer 41 and a colored layer 43. In the design layer 40, the glittering layer 41 may be disposed closer to the first surface 30A of the decorative laminate 30 than the colored layer 43, or the colored layer 43 may be disposed closer to the first surface 30A of the decorative laminate 30 than the glittering layer 41. Similar to the glittering layer 41 in the design layer 40 of the first example, the glittering layer 41 reflects light to impart a glossy appearance. The glittering layer 41 includes a binder resin 41a and a glittering material 41b.

[0050] The colored layer 43 displays a color. The colored layer 43 includes a binder resin 43a and a colorant 43c. The colorant 43c is encapsulated in the binder resin 43a. The binder resin 43a of the colored layer 43 may have a similar structure to the binder resin 41a of the glittering layer 41 in the design layer 40 of the first example. The color of the colorant 43c may be a chromatic color or an achromatic color. The colorant 43c of the colored layer 43 may have a similar structure to the colorant 41c of the glittering layer 41 in the design layer 40 of the second example. The visible light transmittance of the colored layer 43 may be 5% or more or 90% or less. The thickness of the colored layer 43 may be 2 μm or more or 50 μm or less.

[0051] FIG. 9 shows a cross-sectional view of the design layer 40 of the fourth example. In the example shown in FIG. 9, the design layer 40 includes a glittering layer 41 and a colored layer 43. In the design layer 40, the glittering layer 41 may be disposed closer to the first surface 30A of the decorative laminate 30 than the colored layer 43, or the colored layer 43 may be disposed closer to the first surface 30A of the decorative laminate 30 than the glittering layer 41. Similar to the glittering layer 41 in the design layer 40 of the second example, the glittering layer 41 reflects light to impart a gloss and displays color. The glittering layer 41 includes a binder resin 41a, a glittering material 41b, and a colorant 41c. The colored layer 43 displays color similar to the colored layer 43 in the design layer 40 of the third example. The colored layer 43 includes a binder resin 43a and a colorant 43c.

[0052] FIG. 10 shows a cross-sectional view of a fifth example of the design layer 40. In the example shown in FIG. 10, the design layer 40 includes a glossy layer 41, a second glossy layer 42, and a colored layer 43. The second glossy layer 42 is overlaid on the glossy layer 41. In the design layer 40, the second glossy layer 42 is disposed closer to the first surface 30A of the decorative laminate 30 than the second surface 30B of the decorative laminate 30, relative to the glossy layer 41. In the design layer 40, the colored layer 43, the second glossy layer 42, and the glossy layer 41 are disposed in this order from the first surface 30A toward the second surface 30B. The order of the colored layer 43, the second glossy layer 42, and the glossy layer 41 in the design layer 40 is not limited to the example shown. In the design layer 40, the second glossy layer 42, the colored layer 43, and the glossy layer 41 may be arranged in this order from the first surface 30A to the second surface 30B. The glossy layer 41 reflects light to impart a gloss, similar to the glossy layer 41 in the design layer 40 of the first example. The glossy layer 41 contains a binder resin 41a and a glossy material 41b. The colored layer 43 displays a color, similar to the colored layer 43 in the design layer 40 of the third example. The colored layer 43 contains a binder resin 43a and a colorant 43c.

[0053] The second glossy layer 42 may have a similar configuration to the glossy layer 41. The second glossy layer 42 reflects light to give it a glossy appearance. The second glossy layer 42 includes a binder resin 42a and a glossy material 42b. The glossy material 42b is encapsulated in the binder resin 42a. The binder resin 42a of the second glossy layer 42 may have a similar configuration to the binder resin 41a of the glossy layer 41 in the design layer 40 of the first example. The glossy material 42b of the second glossy layer 42 may have a similar configuration to the glossy material 41b of the glossy layer 41 in the design layer 40 of the first example. The content of the glossy material 41b contained in the glossy layer 41 is different from the content of the glossy material 42b contained in the second glossy layer 42. In this example, the content of the glittering material 41b in the glittering layer 41 is higher than the content of the glittering material 42b in the second glittering layer 42. The content of the glittering material refers to the ratio of the area occupied by the glittering material per unit area in the cross section of the layer containing the glittering material. The second glittering layer 42 may display a color. The second glittering layer 42 may contain a colorant. The colorant contained in the second glittering layer 42 may have a similar composition to the colorant 41c of the glittering layer 41 in the design layer 40 of the second example. The content of the colorant in the second glittering layer 42 may be the same as or different from the content of the colorant 41c in the glittering layer 41. The content of the colorant in the second glittering layer 42 may be lower or higher than the content of the colorant 41c in the glittering layer 41.

[0054] When layers containing a photoluminescent material are stacked, such as the photoluminescent layer 41 and the second photoluminescent layer 42, the photoluminescent material content of the lower layer may be lower, the same as, or higher than that of the upper layer. The photoluminescent material content of the upper layer may be 5% or more, or 1000% or less, of the photoluminescent material content of the lower layer. The ratio of the photoluminescent material content of the upper layer to the photoluminescent material content of the lower layer is set so as to minimize changes in the light reflectance of the stacked layers containing the photoluminescent material when the decorative laminate 30 is molded and stretched. When each layer containing a photoluminescent material contains a colorant, the colorant content of the lower layer may be lower, the same as, or higher than that of the upper layer. The upper layer refers to the layer closest to the first surface 30A of the decorative laminate 30. The lower layer refers to the layer closest to the second surface 30B of the decorative laminate 30. The content of the luster material in the layer containing the luster material is compared in terms of the ratio of the area occupied by the luster material per unit area in the cross section of the layer.

[0055] In each example of the glittering layer 41, the content of the glittering material on the side closer to the second surface 30B may be lower, the same as, or higher than the content of the glittering material on the side closer to the first surface 30A. When each example of the glittering layer 41 contains a colorant, the content of the colorant on the side closer to the second surface 30B may be lower, the same as, or higher than the content of the colorant on the side closer to the first surface 30A.

[0056] The glittering layer 41 and the second glittering layer 42 may be superimposed so as to be in direct contact with each other. In this case, the glittering layer 41 and the second glittering layer 42 are easily adhered to each other by the binder resins of each layer.

[0057] FIG. 11 shows a cross-sectional view of the design layer 40 of the sixth example. In the example shown in FIG. 11, the design layer 40 includes a glossy layer 41, a colored layer 43, and a transparent layer 45. The transparent layer 45 is disposed between the glossy layer 41 and the colored layer 43. The glossy layer 41 reflects light to impart a gloss, similar to the glossy layer 41 in the design layer 40 of the first example. The glossy layer 41 includes a binder resin 41a and a glossy material 41b. The colored layer 43 displays a color, similar to the colored layer 43 in the design layer 40 of the third example. The colored layer 43 includes a binder resin 43a and a colorant 43c.

[0058] The transparent layer 45 separates the glossy layer 41 and the colored layer 43. The transparent layer 45 contains a binder resin 45a. The binder resin 45a of the transparent layer 45 may have a configuration similar to that of the binder resin 41a of the glossy layer 41 in the design layer 40 of the first example. The transparent layer 45 has a thickness corresponding to the distance between the glossy layer 41 and the colored layer 43. The thickness of the transparent layer 45 may be 10 μm or more, or may be 25 μm or more. The thickness of the transparent layer 45 may be 300 μm or less, or may be 200 μm or less.

[0059] FIG. 12 shows a cross-sectional view of the design layer 40 of a seventh example. In the example shown in FIG. 12, the design layer 40 includes a glossy layer 41, a second glossy layer 42, a colored layer 43, and a transparent layer 45. The second glossy layer 42 is overlaid on the glossy layer 41. In the design layer 40, the second glossy layer 42 is disposed closer to the first surface 30A of the decorative laminate 30 than the second surface 30B of the decorative laminate 30 with respect to the glossy layer 41. In the design layer 40, the colored layer 43, the transparent layer 45, the second glossy layer 42, and the glossy layer 41 are disposed in this order from the first surface 30A toward the second surface 30B. The order of the colored layer 43, the transparent layer 45, the second glossy layer 42, and the glossy layer 41 in the design layer 40 is not limited to the example shown. In the design layer 40, the second glossy layer 42, the transparent layer 45, the colored layer 43, and the glossy layer 41 may be arranged in this order from the first surface 30A to the second surface 30B. The glossy layer 41 reflects light to impart gloss, similar to the glossy layer 41 in the design layer 40 of the first example. The glossy layer 41 includes a binder resin 41a and a glossy material 41b. The second glossy layer 42 reflects light to impart gloss, similar to the second glossy layer 42 in the design layer 40 of the fifth example. The second glossy layer 42 includes a binder resin 42a and a glossy material 42b. The colored layer 43 displays color, similar to the colored layer 43 in the design layer 40 of the third example. The colored layer 43 includes a binder resin 43a and a colorant 43c. The transparent layer 45, like the transparent layer 45 in the design layer 40 of the sixth example, separates the glittering layer 41 from the colored layer 43. The transparent layer 45 contains a binder resin 45a.

[0060] FIG. 13 shows a cross-sectional view of the design layer 40 of the eighth example. In the example shown in FIG. 13, the design layer 40 includes a colored layer 43. In the example shown, the design layer 40 consists only of the colored layer 43. The colored layer 43 displays color, similar to the colored layer 43 in the design layer 40 of the third example. The colored layer 43 includes a binder resin 43a and a colorant 43c. The design layer 40 in the eighth example forms a design in, for example, piano black color.

[0061] The design layer 40 is not limited to the examples described above. The design layer 40 may be, for example, a combination of the design layers 40 described above. The design layer 40 may include other layers to form the design. For example, the design layer 40 may further include a third glossy layer containing a glossy material encapsulated in a binder resin.

[0062] Fig. 14 shows a cross-sectional view of a third example of the decorative laminate 30. In the example shown in Fig. 14, the decorative laminate 30 includes, in this order from the first surface 30A to the second surface 30B, a surface layer 33, a base layer 31, a design layer 40, an adhesive layer 38, and a backer layer 37. Not limited to the example shown, the backer layer 37 and / or the adhesive layer 38 may be omitted.

[0063] The backer layer 37 maintains the shape of the decorative laminate 30 when the decorative film 20 having the decorative laminate 30 is molded. The backer layer 37 is disposed closer to the second surface 30B of the design layer 40 than the first surface 30A. In the illustrated example, the backer layer 37 forms the second surface 30B of the decorative laminate 30. Similar to the buffer layer 39 described below, the backer layer 37 may cushion the impact on the other layers of the decorative laminate 30 and the molded portion 11 when the decorative laminate 30 is impacted by an external force such as a flying stone. The backer layer 37 is sheet-shaped. The thickness of the backer layer 37 may be 50 μm or more or 500 μm or less. The backer layer 37 is made of, for example, a thermoplastic resin. Specifically, the backer layer 37 may be made of, for example, an acrylonitrile-butadiene-styrene copolymer, polypropylene, polycarbonate, polymethyl methacrylate, or polyvinyl chloride.

[0064] The backer layer 37 may be colored. The backer layer 37 may contain a colorant. The color of the colorant contained in the backer layer 37 may be chromatic or achromatic. The colorant can be used to color the backer layer 37 to a desired color. The color of the backer layer 37 is preferably set to match the color of the design layer 40. The colorant contained in the backer layer 37 may have the same composition as the colorant contained in the glittering layer 41 and colored layer 43 of the design layer 40 described above.

[0065] The color of the backer layer 37 may be a similar color to the color of the design layer 40. The color of the backer layer 37 may be a similar color to the color of the design layer 40. Similar colors refer to colors with the same hue, including colors with different lightness and saturation. Similar colors refer to colors within a 30-degree angle from the center of the color wheel on a continuous color wheel, including colors with different lightness and saturation. For example, if the color of the design layer 40 is red, a brown backer layer 37 can be used.

[0066] L * a * b * In the color system, the L of the color exhibited by the backer layer 37 * The value of L * 1 and the color L of the design layer 40 * The value of L * The difference from 2 may be 10 or less, 8 or less, 6 or less, or 4 or less. * a * b * In the color system, the color of the backer layer 37 is a * The value of a * 1 and b * The value of b * 1 and the color a presented by the design layer 40 * The value of a * 2 and b * The value of b * 2 and ((a * 1-a * 2) 2 +(b * 1-b * 2) 2 ) 1 / 2The value of L of the color exhibited by the backer layer 37 and the color exhibited by the design layer 40 may be 20 or less, 17 or less, 15 or less, 13 or less, or 11 or less. * a * b * L in color space * The value of a * The value of b * The value of can be measured as follows using a spectrophotometer (Konica Minolta "CM-700d") with a measurement diameter of 8 mm and a viewing angle of 10 degrees. * A black plate with a value of 29.9 is placed on the opposite side of the surface where the black plate is placed. Light from a D65 light source is irradiated on the surface opposite to the surface where the black plate is placed. The L value of the material is calculated from the total reflection light at the material to be measured. * The value of a * The value of b * The value of is specified.

[0067] The adhesive layer 38 bonds the backer layer 37 to the other layers of the decorative laminate 30. In the illustrated example, the adhesive layer 38 bonds the backer layer 37 to the design layer 40. The adhesive layer 38 is disposed between the backer layer 37 and the design layer 40. Similar to the buffer layer 39 described below, the adhesive layer 38 may cushion the impact on the other layers of the decorative laminate 30 and the molded portion 11 when the decorative laminate 30 is subjected to an external impact such as a flying stone. The adhesive layer 38 is thin. The thickness of the adhesive layer 38 may be 1 μm or more or 20 μm or less. The visible light transmittance of the adhesive layer 38 may be 0% or more, 50% or more, 100% or less, or 20% or less. Examples of materials for the adhesive layer 38 include thermoplastic resins such as acrylic resins, vinyl chloride-vinyl acetate copolymers, chlorinated polyolefin resins, and acid-modified polyolefin resins; two-component curing urethane resins; and curable resins such as epoxy resins.

[0068] The adhesive layer 38 may be colored. The adhesive layer 38 may contain a colorant. The color of the colorant contained in the adhesive layer 38 may be chromatic or achromatic. The colorant can be used to color the adhesive layer 38 a desired color. The color of the adhesive layer 38 is preferably set to match the color of the design layer 40. The color may be set in the same way as the color of the backer layer 37 in the decorative laminate 30 of the third example described above. The colorant contained in the adhesive layer 38 may have the same configuration as the colorant contained in the glittering layer 41 and colored layer 43 of the design layer 40 described above.

[0069] Fig. 15 shows a cross-sectional view of a fourth example of the decorative laminate 30. In the example shown in Fig. 15, the decorative laminate 30 includes, in this order from the first surface 30A to the second surface 30B, a surface layer 33, a base layer 31, a design layer 40, an adhesive layer 38, a hiding layer 35, and a backer layer 37. The backer layer 37 and / or the adhesive layer 38 may be omitted.

[0070] The concealing layer 35 conceals other components provided on the second surface 30B of the decorative laminate 30, such as the molded portion 11, so that they are less easily observed from the first surface 30A of the decorative laminate 30. The concealing layer 35 is disposed closer to the second surface 30B of the design layer 40 than to the first surface 30A. In the illustrated example, the concealing layer 35 is disposed between the adhesive layer 38 and the backer layer 37. The illustrated example is not limiting, and the concealing layer 35 may also be disposed between the design layer 40 and the adhesive layer 38. The concealing layer 35 is thin-film shaped. The thickness of the concealing layer 35 may be 2 μm or more, 10 μm or more, 100 μm or less, or 20 μm or less. The visible light transmittance of the concealing layer 35 is sufficiently low. Specifically, the visible light transmittance of the concealing layer 35 may be 20% or less.

[0071] The concealing layer 35 contains a colorant. The color of the colorant contained in the concealing layer 35 may be chromatic or achromatic. The colorant allows the concealing layer 35 to be colored a desired color. The color of the concealing layer 35 is preferably set to match the color of the design layer 40. The color may be set in the same manner as the color of the backer layer 37 in the decorative laminate 30 of the third example described above. The colorant contained in the concealing layer 35 may have the same configuration as the colorant contained in the glittering layer 41 and colored layer 43 of the design layer 40 described above.

[0072] Fig. 16 shows a cross-sectional view of a fifth example of a decorative laminate 30. In the example shown in Fig. 16, the decorative laminate 30 includes, in this order from the first surface 30A to the second surface 30B, a surface layer 33, a base layer 31, a design layer 40, a reflective layer 36, an adhesive layer 38, and a backer layer 37. The backer layer 37 and / or the adhesive layer 38 may be omitted.

[0073] The reflective layer 36 reflects light so that other components provided on the second surface 30B of the decorative laminate 30, such as the molded portion 11, cannot be observed from the first surface 30A of the decorative laminate 30, and so that the design formed by the design layer 40 can be more clearly observed. The reflective layer 36 reflects light that is transmitted without being reflected by the glittering layer 41 of the design layer 40. The reflective layer 36 is disposed closer to the second surface 30B of the design layer 40 than to the first surface 30A. In the illustrated example, the reflective layer 36 is disposed between the design layer 40 and the adhesive layer 38. The illustrated example is not limiting, and the reflective layer 36 may also be disposed between the adhesive layer 38 and the backer layer 37. The reflective layer 36 is thin-film shaped. The thickness of the reflective layer 36 may be 30 nm or more, 2 μm or more, 20 μm or less, or 100 nm or less. The visible light transmittance of the reflective layer 36 may be 0% or more or 20% or less. The material of the reflective layer 36 is, for example, a vapor-deposited film of aluminum, indium or tin, or achromatic or silver ink.

[0074] Fig. 17 shows a cross-sectional view of a sixth example of a decorative laminate 30. In the example shown in Fig. 17, the decorative laminate 30 includes, in this order from the first surface 30A to the second surface 30B, a surface layer 33, a buffer layer 39, a base material layer 31, a design layer 40, an adhesive layer 38, and a backer layer 37. The backer layer 37 and / or the adhesive layer 38 may be omitted.

[0075] The buffer layer 39 cushions the impact on the other layers of the decorative laminate 30 and the molded portion 11 when the decorative laminate 30 is impacted by a flying stone or the like. The buffer layer 39 is a chip-resistant layer that contains, for example, a plasticizer. Examples of plasticizers include phthalate-based plasticizers, fatty acid-based plasticizers, phosphoric acid-based plasticizers, polyester-based plasticizers, polyethylene-based plasticizers, and epoxy-based plasticizers. Examples of phthalate-based plasticizers include phthalate diesters such as dioctyl phthalate, di-2-ethylhexyl phthalate, dihexyl phthalate, dibutyl phthalate, diheptyl phthalate, diisodecyl phthalate, and diisononyl phthalate. Examples of fatty acid plasticizers include aliphatic polybasic acid diesters such as dioctyl adipate, dioctyl azelate, and dioctyl cebarate; and citric acid triesters such as tributyl acetyl citrate, trioctyl acetyl citrate, and tributyl citrate. The buffer layer 39 is a chip-resistant layer containing, for example, an elastomer. Examples of elastomers include styrene-based elastomers, polyester-based elastomers, urethane-based elastomers, olefin-based elastomers, and polyamide-based elastomers.

[0076] The buffer layer 39 is disposed closer to the second surface 30B of the surface layer 33 than to the first surface 30A. In the illustrated example, the buffer layer 39 is disposed between the surface layer 33 and the base layer 31. The buffer layer 39 may be disposed between the base layer 31 and the design layer 40, between the design layer 40 and the adhesive layer 38, or between the adhesive layer 38 and the backer layer 37. The backer layer 37 may also function as the buffer layer 39. In other words, the backer layer 37 and the buffer layer 39 may be the same layer. The buffer layer 39 is thin. The thickness of the buffer layer 39 may be 10 μm or more or 500 μm or less. The buffer layer 39 may include multiple layers. The material of the buffer layer 39 is, for example, a resin containing a polyester plasticizer such as adipic acid polyester or phthalic acid polyester, a vinyl chloride-vinyl acetate copolymer, a polyurethane resin, a polyester resin, an epoxy resin, an acrylic resin, or a polyolefin resin. The amount of plasticizer contained in the buffer layer 39 may be 1 part by mass or more, or may be less than 40 parts by mass.

[0077] The decorative laminate 30 including the buffer layer 39 is less likely to damage the displayed design. Even when a stone chip test is performed on the decorative laminate 30 including the buffer layer 39, it can be visually confirmed that the displayed design is hardly damaged. Even when a stone chip test is performed on the decorative laminate 30 including the buffer layer 39, the buffer layer 39 cushions the impact, thereby preventing peeling and cracking of the layers that make up the decorative film 20. Even when a stone chip test is performed on the decorative laminate 30 including the buffer layer 39, the buffer layer 39 cushions the impact, thereby preventing peeling of the decorative film 20 including the decorative laminate 30 from the molded portion 11. The stone chip test is performed using a Gravelo Tester JA400 (manufactured by Suga Testing Machines) under the following conditions. <Test conditions> Shot material: No. 7 crushed stone as specified in JIS A5001 (crushed stone for roads) Amount of shot: 50g Distance: 35cm Shot pressure: 0.39MPa Shot angle: 90° Test temperature: -20℃

[0078] When the buffer layer 39 is disposed closer to the second surface 30B of the decorative laminate 30 than the design layer 40, the buffer layer 39 may contain a colorant. The color of the buffer layer 39 may be the same color as or similar to the color of the design layer 40.

[0079] The decorative laminate 30 is not limited to the above-described examples. The decorative laminate 30 may be, for example, a combination of the decorative laminates 30 of the above-described examples. For example, the decorative laminate 30 may include, in this order from the first surface 30A to the second surface 30B, a surface layer 33, a design layer 40, a substrate layer 31, a buffer layer 39, a concealing layer 35, a reflective layer 36, a colored adhesive layer 38, and a colored backer layer 37. When the decorative laminate 30 includes the concealing layer 35 and the reflective layer 36, the reflective layer 36 is disposed closer to the second surface 30B than the first surface 30A with respect to the concealing layer 35. The decorative laminate 30 may also include other layers that exhibit desired functions. For example, the decorative laminate 30 may include, in this order from the first surface 30A to the second surface 30B, a surface layer 33, a design layer 40, a base material layer 31, a buffer layer 39, a reflective layer 36, a concealing layer 35, a colored adhesive layer 38, and a colored backer layer 37.

[0080] In the decorative laminate 30, the layers capable of cushioning the impact on the other layers of the decorative laminate 30 and the molded portion 11 when an external impact is received, such as by a flying stone, are sufficiently thick to adequately cushion the external impact. In the decorative laminate 30, the ratio of the total thickness of the adhesive layer 38, backer layer 37, and buffer layer 39 to the total thickness of the surface layer 33, base layer 31, and design layer 40 may be 0.14 or more or 19 or less. When the buffer layer 39 is omitted from the decorative laminate 30, the ratio of the total thickness of the adhesive layer 38 and backer layer 37 to the total thickness of the surface layer 33, base layer 31, and design layer 40 may be 0.12 or more or 9.6 or less. When the backer layer 37 is omitted in the decorative laminate 30, the ratio of the total thickness of the adhesive layer 38 and the buffer layer 39 to the total thickness of the surface layer 33, the base layer 31, and the design layer 40 may be 0.020 or more or 9.6 or less.

[0081] The thickness of the decorative laminate 30 may be 60 μm or more, 100 μm or more, 1 mm or less, or 500 μm or less. When the decorative laminate 30 is sufficiently thin, the decorative laminate 30 can be wound into a roll. The decorative laminate 30 can be easily handled. When the decorative laminate 30 is sufficiently thin, the time required to heat the decorative laminate 30 to a temperature at which it can be molded is shortened when molding the decorative laminate 30. This makes it easier to manufacture the decorated molded product 10. When the decorative laminate 30 is sufficiently thin, the cost of the decorative laminate 30 itself can be reduced. When the decorative laminate 30 is sufficiently thick, the decorative laminate 30 can maintain an appropriate shape even when molded. The decorative laminate 30 is sufficiently thick, so that the decorative laminate 30 is less likely to be damaged by heat when it is molded, even if the temperature of the decorative laminate 30 is raised to a temperature at which the decorative laminate 30 can be molded.

[0082] An example of a manufacturing method for the decorative laminate 30, the decorative film 20, and the decorated molded article 10 will be described. The manufacturing method for the decorative laminate 30 includes a step of printing or applying a design layer 40 to a base layer 31, and a step of forming a surface layer 33. The manufacturing method for the decorative film 20 includes a step of providing a bonding layer 21 on the decorative laminate 30. The manufacturing method for the decorated molded article 10 includes a step of vacuum-forming the decorative film 20 or the decorative laminate 30, and a step of forming a molded portion 11 on the decorative film 20 or the decorative laminate 30.

[0083] As shown in FIG. 18 , a design layer 40 is provided on a base layer 31. Each layer included in the design layer 40 is printed or coated on the base layer 31 in order. As an example, a process for providing the design layer 40 of the example shown in FIG. 8 on the base layer 31 by printing will be described. A colored layer 43 containing a binder resin 43a and a colorant 43c is printed on the base layer 31. A photoluminescent layer 41 containing a binder resin 41a and a photoluminescent material 41b is printed on the colored layer 43. The colored layer 43 and the photoluminescent layer 41 are provided by any printing method, such as offset printing, inkjet printing, gravure printing, or screen printing. The printing method may be selected appropriately depending on the colorant and photoluminescent material contained in the colored layer 43 and the photoluminescent layer 41. Because the thickness of the provided glittering layer 41 is sufficiently thin and the average particle size of the glittering material 41b is sufficiently small, the glittering material 41b contained in the glittering layer 41 is oriented along the surface on which the glittering layer 41 is formed. Forming the glittering layer 41 by printing makes it easier to orient the glittering material 41b in a direction along the main surface compared to painting.

[0084] As another example of providing a design layer 40 on the base layer 31 shown in FIG. 18 , a process for providing the design layer 40 of the example shown in FIG. 8 on the base layer 31 by coating will be described. A colored layer 43 containing a binder resin 43a and a colorant 43c is coated on the base layer 31. A glittering layer 41 containing a binder resin 41a and a glittering material 41b is coated on the colored layer 43. The colored layer 43 and the glittering layer 41 are provided by any coating method, such as air spray coating, ultrasonic spray coating, or electrostatic spray coating. The coating method may be appropriately selected depending on the colorant and glittering material contained in the colored layer 43 and the glittering layer 41. Because the thickness of the provided glittering layer 41 is sufficiently thin and the average particle size of the glittering material 41b is sufficiently small, the glittering material 41b contained in the glittering layer 41 is oriented along the surface on which the glittering layer 41 is formed. By forming the glittering layer 41 by coating, the glittering material 41b can be oriented on the main surface in the same manner as when it is painted.

[0085] The content of the photoluminescent material 41b contained in the photoluminescent layer 41 is determined according to the elongation rate of the decorative laminate 30 in the process of vacuum-forming the decorative film 20 or the decorative laminate 30. For example, if the decorative laminate 30 elongates by 100% in the process of vacuum-forming the decorative film 20 or the decorative laminate 30, the content of the photoluminescent material 41b contained in the photoluminescent layer 41 of the design layer 40 in the decorative laminate 30 before vacuum-forming may be at least twice the content of the photoluminescent material 41b that should be contained in the photoluminescent layer 41 in the decorated molded product 10. As a result, in a cross-sectional view, the photoluminescent material 41b in the photoluminescent layer 41 is arranged so as to overlap in the stacking direction.

[0086] When manufacturing the decorative laminate 30 including the concealing layer 35, the concealing layer 35 is printed on top of the design layer 40. The concealing layer 35 is provided by any printing method such as offset printing, inkjet printing, gravure printing, or screen printing.

[0087] When manufacturing the decorative laminate 30 including the reflective layer 36, the reflective layer 36 is provided by overlapping the design layer 40. The reflective layer 36 is provided by vapor deposition of metal or by printing achromatic or silver ink.

[0088] When manufacturing the decorative laminate 30 including the buffer layer 39, the buffer layer 39 is provided at a desired position on the decorative laminate 30. The buffer layer 39 is provided by any printing method such as offset printing, inkjet printing, gravure printing, or screen printing, by thermal lamination, or by bonding using an adhesive.

[0089] When manufacturing the decorative laminate 30 including the backer layer 37 and the adhesive layer 38, the backer layer 37 provided with the adhesive layer 38 is laminated to the design layer 40, as shown in Fig. 19. The backer layer 37 is bonded to the design layer 40 by the adhesive layer 38.

[0090] The surface layer 33 is formed. The surface layer 33 is provided to form the first surface 30A of the decorative laminate 30. The surface layer 33 is provided by any printing method, such as offset printing, inkjet printing, gravure printing, or screen printing. Alternatively, the surface layer 33 may be formed, for example, by applying an ionizing radiation-curable resin composition to the surface of the base layer 31 opposite to the surface on which the design layer 40 is provided, and then curing the composition by irradiating the composition with ultraviolet rays or electron beams. Alternatively, the surface layer 33 may be formed, for example, by applying a thermosetting resin composition to the surface of the base layer 31 opposite to the surface on which the design layer 40 is provided, and then heating the composition to cure the composition. The surface layer 33 may be provided on the base layer 31 before the design layer 40 is printed or applied to the base layer 31. When the decorative film 20 includes a protective film 23, the step of curing the composition by irradiating the composition with ultraviolet light or electron beams or by heating the composition may be carried out after removing the protective film 23.

[0091] The surface layer 33 does not have to be completely cured. The surface layer 33 is bonded to the base layer 31 and the design layer 40, but may be in a stretchable state. The curing of the surface layer 33 can be controlled by adjusting the intensity of the ultraviolet or electron beam irradiated onto the composition that will become the surface layer 33, or the temperature at which the composition that will become the surface layer 33 is heated. By not completely curing the surface layer 33, it is possible to prevent the surface layer 33 from being damaged before the decorative film 20 or decorated molded article 10 that includes the decorative laminate 30 is manufactured.

[0092] Through the above steps, the decorative laminate 30 is manufactured.

[0093] 20 , when the decorative film 20 includes the protective film 23, the protective film 23 is provided on the surface layer 33. The protective film 23 is provided by being attached to the surface layer 33. The protective film 23 may be provided on the surface layer 33 before the design layer 40 is printed or applied to the base layer 31.

[0094] A bonding layer 21 is provided on the decorative laminate 30. When the bonding layer 21 is a heat seal layer, the bonding layer 21 is provided by coating the second surface 30B of the decorative laminate 30. When the bonding layer 21 is an adhesive layer, the bonding layer 21 is provided by applying an adhesive to the second surface 30B of the decorative laminate 30. Whether the bonding layer 21 is a heat seal layer or an adhesive layer, the bonding layer 21 may be provided on the second surface 30B of the decorative laminate 30 by any printing method, such as offset printing, inkjet printing, gravure printing, or screen printing.

[0095] Through the above steps, the decorative film 20 is manufactured.

[0096] The decorative film 20 and the decorative laminate 30 are vacuum-formed. The decorative laminate 30 stretches to conform to the surface of the decorated molded article 10 to be manufactured. The vacuum-formed decorative laminate 30 displays the desired design on the decorated molded article 10. The decorative laminate 30 is formed to be larger than the decorated molded article 10. The vacuum-formed decorative laminate 30 is trimmed to match the surface shape of the decorated molded article 10.

[0097] The molded portion 11 is formed closer to the second surface 30B than to the first surface 30A of the decorative laminate 30. The molded portion 11 may be provided directly on the decorative laminate 30 by injection molding such as insert molding, or by TOM molding, or may be provided by molding using another method. When the bonding layer 21 is a heat seal layer, the bonding layer 21 bonds the decorative film 20 to the molded portion 11 when heated. When the bonding layer 21 is an adhesive layer, the bonding layer 21 bonds the decorative film 20 to the molded portion 11 when pressure is applied.

[0098] If the surface layer 33 is not completely hardened, after forming the molded portion 11 on the decorative laminate 30, the surface layer 33 may be hardened by irradiating it with ultraviolet light or electron beams, or by heating it.

[0099] When the decorative film 20 includes the protective film 23, the protective film 23 is removed from the surface layer 33. The protective film 23 is preferably removed after the decorative laminate 30 has been trimmed, in order to prevent shavings generated when the decorative laminate 30 is trimmed from adhering to the surface layer 33. For example, the protective film 23 may be removed after the decorative laminate 30 has been trimmed and before the molded portion 11 is formed on the decorative laminate 30, or may be removed after the molded portion 11 is formed on the decorative laminate 30. After the protective film 23 has been removed, the composition that forms the surface layer 33 may be cured.

[0100] Through the above steps, the decorated molded product 10 is manufactured.

[0101] Instead of painting with paint, it is being considered to impart designs to molded parts such as exterior components of mobile bodies using decorative films. There is a demand for designs displayed by the decorative laminate of the decorative film to be closer to designs created by painting with paint.

[0102] In the decorative laminate 30 of this embodiment, the design layer 40 includes a photoluminescent layer 41 containing a photoluminescent material 41b. The design layer 40 can form a design similar to that achieved by painting with paint by reflecting light with the photoluminescent layer 41. The design displayed by the decorative laminate 30 can be made to resemble a design achieved by painting with paint. The decorative laminate 30 can display an excellent design. By using the decorative laminate 30, it is possible to reduce emissions of volatile organic compounds and carbon dioxide during the production of the decorated molded product 10.

[0103] The decorative laminate 30 includes a surface layer 33. The surface layer 33 protects the design layer 40. The surface layer 33 enables the decorated molded article 10 including the decorative laminate 30 to exhibit the durability required when the decorated molded article 10 is used as a part of an exterior member of a mobile object 1.

[0104] The thickness of the glittering layer 41 is 100 μm or less. Because the thickness of the glittering layer 41 is sufficiently small, the glittering material 41b can be oriented along the surface on which the glittering layer 41 is formed. The design layer 40 can form a glossy design due to the glittering layer 41. The decorative laminate 30 can display a more excellent design.

[0105] The glittering layer 41 contains a colorant 41c. By coloring the glittering layer 41 with the colorant 41c, the glittering layer 41 reflects light and exhibits color. The design layer 40 can form a design that exhibits gloss and color thanks to the glittering layer 41. The decorative laminate 30 can display a more excellent design.

[0106] The design layer 40 includes a colored layer 43 containing a colorant 43c. In the design layer 40, the glossy layer 41 and the colored layer 43 are different layers. The design layer 40 can form a design with depth. The decorative laminate 30 can display a more excellent design.

[0107] The design layer 40 includes a transparent layer 45. The transparent layer 45 is disposed between the colored layer 43 and the glittering layer 41. The transparent layer 45 separates the glittering layer 41, which provides luster, from the colored layer 43, which provides color. The design layer 40 can form a design with greater depth. The decorative laminate 30 can display a more excellent design.

[0108] The design layer 40 includes a second glossy layer 42. The second glossy layer 42 can reflect light that was not reflected by the glossy layer 41. The second glossy layer 42 adjusts the amount of light reflected by the decorative laminate 30, making it possible to appropriately display the design of the decorative laminate 30. The second glossy layer 42 allows the design layer 40 to form a design with greater depth. The decorative laminate 30 can display a more excellent design.

[0109] The content of the glittering material 41b in the glittering layer 41 is different from the content of the glittering material 42b in the second glittering layer 42. The design layer 40 can form a more complex design. The decorative laminate 30 can display a more excellent design.

[0110] The content of the glittering material 41b in the glittering layer 41 closer to the second surface 30B is higher than the content of the glittering material 42b in the second glittering layer 42 closer to the first surface 30A. Even if the decorative laminate 30 is stretched by vacuum forming during the manufacturing process of the decorated molded product 10, making it difficult for the second glittering layer 42 to reflect light, the glittering layer 41 can easily reflect light. The glittering layer 41 is more likely to reflect light that was not reflected by the second glittering layer 42. The glittering layer 41 and the second glittering layer 42 make it easier for the design layer 40 to form a design with greater depth. The decorative laminate 30 can display a more excellent design.

[0111] The glittering layer 41 and the second glittering layer 42 contain a colorant, and the content of the colorant in the glittering layer 41 is different from the content of the colorant in the second glittering layer 42. The design layer 40 can form a design with greater depth. The decorative laminate 30 can display a more excellent design.

[0112] The content of colorant in the glittering layer 41 closer to the second surface 30B is higher than the content of colorant in the second glittering layer 42 closer to the first surface 30A. The design layer 40 can form a design with greater depth. The decorative laminate 30 can display a more excellent design.

[0113] The decorative laminate 30 includes a concealing layer 35. The concealing layer 35 makes it difficult to observe other components provided on the second surface 30B of the decorative laminate 30. The concealing layer 35 allows the decorative laminate 30 to more clearly display the design formed by the design layer 40. The decorative laminate 30 can display a more excellent design.

[0114] The decorative laminate 30 includes a reflective layer 36. The reflective layer 36 can reflect light that is not reflected by the glittering layer 41. The reflective layer 36 adjusts the amount of light reflected by the decorative laminate 30, making it possible to tailor the design displayed by the decorative laminate 30 to suit the application. The reflective layer 36 allows the design layer 40 to form a design with greater depth. The decorative laminate 30 can display a more superior design.

[0115] The decorative laminate 30 includes a backer layer 37. The backer layer 37 allows the shape of the decorative laminate 30 to be maintained so that the design displayed by the decorative laminate 30 is not impaired, even when the decorative film 20 having the decorative laminate 30 is vacuum formed. Even when a decorated molded product 10 is manufactured using the decorative film 20 having the decorative laminate 30, the design displayed by the decorative laminate 30 can be maintained as an excellent design.

[0116] When the decorative film 20 having the decorative laminate 30 is vacuum-formed, the decorative laminate 30 stretches. For example, the area of ​​the decorative laminate 30 can stretch from 1.01 to 5 times its original size. When the design layer 40 stretches, color unevenness can occur in the color exhibited by the design layer 40. For example, when the decorative film 20 stretches, the transmittance of the design layer 40 increases, making it easier for the color of the layer below the design layer 40 to be reflected. The design displayed by the decorative laminate 30 can deteriorate. At least one of the backer layer 37, adhesive layer 38, and base layer 31 contains a colorant. By coloring at least one of the backer layer 37, adhesive layer 38, and base layer 31, color unevenness in the color exhibited by the design layer 40 can be reduced. Deterioration of the design displayed by the decorative laminate 30 can be suppressed. Specifically, in the design displayed by the decorative laminate 30, the color difference ΔE * The value of ab can be set to 3.0 or less.

[0117] ΔE * The value of ab is L * a * b * In the color system, the L between two points of the target material * The difference in the value of ΔL * , a * The difference in the value of Δa * and b * The difference in the value of Δb * Regarding ΔE * ab=[(ΔL * ) 2 +(Δa * ) 2 +(Δb * ) 2 ] 1 / 2 is the value calculated by

[0118] FIG. 21 shows a mobile body part 1A that a mobile body 1 has as a part of an exterior member, etc. The mobile body part 1A shown in FIG. 21 has a decorated molded product 10 and a painted part 50. In the example shown in FIG. 21, the decorated molded product 10 and the painted part 50 are adjacent to each other in the mobile body part 1A. As shown in FIG. 21, the decorated molded product 10 includes a decorative film 20 and a molded part 11 bonded to the decorative film 20. The painted part 50 includes a molded part 11 that is different from the molded part 11 included in the decorated molded product 10 and a coating agent 51 applied to the molded part 11. The coating agent 51 allows the painted part 50 to display a design. In the decorated molded product 10, at least one of the backer layer 37, adhesive layer 38, and base material layer 31 included in the decorative laminate 30 is colored, thereby reducing color unevenness in the color of the design layer 40. This makes it possible to make the difference in color between the decorative laminate 30 and the painted part 50 less noticeable. Specifically, the color difference ΔE between the design displayed by the decorative laminate 30 and the design displayed by the painted part * The value of ab can be set to 3.0 or less.

[0119] FIG. 22 shows a mobile body part 1B that a mobile body 1 has as a part of an exterior member, etc. The mobile body part 1B shown in FIG. 22 has two different decorative molded articles 10. In the example shown in FIG. 22, the two decorative molded articles 10 are adjacent to each other in the mobile body part 1B. Each of the two illustrated decorative molded articles 10 includes a decorative film 20 and a molded portion 11 joined to the decorative film 20. In the illustrated mobile body part 1B, the decorative film 20 included in one of the two decorative molded articles 10 is different from the decorative film 20 included in the other of the two decorative molded articles 10. Furthermore, the molded portion 11 included in one of the two decorative molded articles 10 is different from the molded portion 11 included in the other of the two decorative molded articles 10. The two decorative molded articles 10 may have different elongation rates during molding, may be formed using different molding methods, or may have different materials for the molded portions 11. At least one of the backer layer 37, adhesive layer 38, and base material layer 31 of the decorative laminate 30 included in each of the decorated molded products 10 is colored, thereby reducing color unevenness exhibited by the design layer 40. This makes it possible to make the color difference between the decorative laminates 30a and 30b less noticeable. Specifically, the color difference ΔE between the designs displayed by the decorative laminates 30 included in each of the decorated molded products 10 * The value of ab can be set to 3.0 or less.

[0120] The decorative laminate 30 includes a buffer layer 39. The buffer layer 39 can cushion external impacts on the other layers of the decorative laminate 30. It can prevent the decorative film 20 having the decorative laminate 30 from peeling off from the molded portion 11 due to an external impact. It can prevent the design layer 40 from being damaged by an external impact, thereby preventing deterioration of the design displayed by the decorative laminate 30.

[0121] When the bonding layer 21 included in the decorative film 20 is a heat seal layer, the molding portion 11 and the bonding layer 21 are easily bonded firmly when the molding portion 11 is molded on the decorative film 20. When the molding portion 11 is provided on the decorative film 20 by insert molding, the heat seal layer can be deformed to fit the shape of the molding portion 11. The molding portion 11 and the bonding layer 21 are easily bonded more firmly.

[0122] When the bonding layer 21 contained in the decorative film 20 is an adhesive layer, the decorative film 20 and the molded portion 11 can be bonded in various ways, for example, when the molded portion 11 is provided on the decorative film 20 by TOM molding, or when the decorative film 20 is attached to the molded portion 11.

[0123] The decorative film 20 includes a protective film 23. The protective film 23 can protect the surface layer 33 before the composition is cured. It can prevent the surface layer 33 from being scratched or from being contaminated with foreign matter. It can prevent deterioration of the design displayed by the decorative laminate 30 due to scratches on the surface layer 33 or foreign matter.

[0124] In the manufacturing method of the decorated molded product 10, the content of the glittering material 41b contained in the glittering layer 41 is determined according to the elongation rate of the decorative laminate 30 during the vacuum forming process of the decorative laminate 30. Even if the decorative laminate 30 is elongated by vacuum forming, the glittering layer 41 appropriately reflects light and exhibits a glossy appearance. In the decorated molded product 10, the decorative laminate 30 can appropriately display the design.

[0125] The decorative laminate 30 of this embodiment has a first surface 30A and a second surface 30B opposite the first surface 30A. The decorative laminate 30 includes a base layer 31, a surface layer 33 disposed on the base layer 31 closer to the first surface 30A than the second surface 30B, and a design layer 40 supported on the base layer 31. The design layer 40 includes a photoluminescent layer 41 containing a photoluminescent material 41b. According to the decorative laminate 30 of this embodiment, the design layer 40 can form a design similar to that achieved by painting with paint by reflecting light with the photoluminescent layer 41. The design displayed by the decorative laminate 30 can be made to resemble a design achieved by painting with paint. The decorative laminate 30 can display an excellent design. The production of the decorated molded article 10 can reduce emissions of volatile organic compounds and carbon dioxide.

[0126] Although each embodiment has been described with reference to specific examples, the above-mentioned specific examples do not limit each embodiment. Each of the above-mentioned embodiments can be implemented with various other specific examples, and various omissions, substitutions, changes, additions, etc. can be made within the scope of the gist thereof. [Explanation of symbols]

[0127] 1. Mobile 10 Decorative moldings 11 Molding section 20 Decorative film 21 Bonding layer 23 Protective film 30 Decorative laminate 30A 1st side 30B 2nd side 31 Base material layer 33 Surface layer 35 Hidden Layer 36 Reflective layer 37 Backer Tier 38 Adhesive layer 39 Buffer layer 40 Design Layer 41 Photoluminescent layer 41b Photoluminescent material 41c Colorant 42 2nd photoluminescent layer 42b Photoluminescent material 43 Colored layer 43c Colorant 45 Transparent layer

Claims

[Claim 1] A decorative laminate having a first surface and a second surface opposite to the first surface, a substrate layer; a surface layer disposed closer to the first surface than the second surface with respect to the base layer; A design layer supported on the base layer, The decorative laminate, wherein the design layer includes a glittering layer containing a glittering material.