Thermosetting inkjet ink and printing method

Abstract

The present invention addresses the problem of providing a thermosetting inkjet ink which is capable of forming a coating film that exhibits excellent adhesion to a substrate, while having high surface hardness and good surface tackiness. The present invention also addresses the problem of providing a printing method which is capable of forming a coating film that exhibits excellent adhesion to a substrate, while having high surface hardness and good surface tackiness.　A thermosetting inkjet ink according to the present invention contains a thermosetting compound, and is characterized by containing a photopolymerizable compound, a thermosetting compound, a photopolymerization initiator and a gelling agent, while being also characterized in that: the photopolymerization initiator is an acylphosphine-based initiator or an aminoacetophenone-based initiator; the content of the photopolymerization initiator is within the range of from 1 mmol / kg to 100 mmol / kg; and the photopolymerization initiator undergoes a sol-gel phase transition induced by temperature.

Description

[Technical field]

[0001] The present invention relates to a thermosetting inkjet ink and a printing method, more particularly to a thermosetting inkjet ink capable of forming a coating film having excellent substrate adhesion, high surface hardness, and good surface tackiness, and also to a printing method capable of forming a coating film having excellent substrate adhesion, high surface hardness, and good surface tackiness. [Background technology]

[0002] Conventionally, photolithography and screen printing have been used to form etching resists, solder resists and markings on printed circuit boards. As a method for manufacturing a printed circuit board using an inkjet printer, an etching resist is formed by drawing a conductor circuit pattern on a copper-clad laminate for printed wiring boards using an inkjet printer, and then an etching process is performed (see, for example, Patent Document 1). This method can significantly reduce the number of steps and labor compared to the photolithography development method that requires a photomask, or the screen printing method using resist ink or marking ink that requires a screen plate, and at the same time, it can reduce consumables such as developing solution, various inks, and cleaning solvents, and can also reduce wastewater, which is expected to lead to a cleaner environment.

[0003] Also for solder resist, it has already been proposed to form a cured film by performing provisional curing with light using an inkjet method and then performing main curing with heat (see, for example, Patent Documents 2 and 3).

[0004] However, in the case of printed circuit boards, the adhesion at the film interface between the solder resist formed with the inks using these ink-jet methods and the metal substrate, for example, a copper substrate, is insufficient, which has been a problem. [Prior art documents] [Patent documents]

[0005] [Patent Document 1] Patent No. 5731746 [Patent Document 2] Patent No. 4936725 [Patent Document 3] Patent No. 5969208 Summary of the Invention [Problem to be solved by the invention]

[0006] The present invention has been made in consideration of the above problems and circumstances, and an object of the present invention is to provide a thermosetting ink-jet ink capable of forming a coating film having excellent substrate adhesion, high surface hardness, and good surface tackiness, and also to provide a printing method capable of forming a coating film having excellent substrate adhesion, high surface hardness, and good surface tackiness. [Means for solving the problem]

[0007] In order to solve the above problems, the present inventors have studied the causes of the above problems and found that by suppressing the temporary curing caused by light, specifically by limiting the amount of photopolymerization initiator used within a specific range and using a gelling agent, in order to increase the reactivity of the thermosetting compound, the main effect caused by heat can be improved and a coating film with good metal adhesion can be obtained. Furthermore, they found that the decrease in surface tackiness caused by reducing the amount of photopolymerization initiator used can be prevented by using a gelling agent, which led to the present invention. That is, the above-mentioned problems of the present invention are solved by the following means.

[0008] 1. A thermosetting inkjet ink containing a thermosetting compound, The composition contains a photopolymerizable compound, a thermosetting compound, a photopolymerization initiator, and a gelling agent, The photopolymerization initiator is an acylphosphine-based initiator or an aminoacetophenone-based initiator, and the content thereof is within the range of 1 to 100 mmol / kg; and A thermosetting inkjet ink that undergoes a sol-gel phase transition due to temperature.

[0009] 2. The thermosetting inkjet ink described in item 1, wherein the thermosetting compound is a blocked isocyanate in which a polyisocyanate is blocked with a blocking agent.

[0010] 3. The thermosetting ink-jet ink described in 2 above, wherein the polyisocyanate is an aliphatic polyisocyanate.

[0011] 4. The thermosetting inkjet ink described in any one of items 1 to 3, wherein the content of the photopolymerization initiator is within the range of 1 to 70 mmol / kg.

[0012] 5. The thermosetting ink-jet ink according to any one of items 1 to 4, further comprising a thioxanthone-based initiator in an amount within the range of 40 to 400 mmol / kg as a photopolymerization initiator.

[0013] 6. The thermosetting ink-jet ink according to any one of items 1 to 4, further comprising a thioxanthone-based initiator in an amount within the range of 100 to 400 mmol / kg as a photopolymerization initiator.

[0014] 7. A printing method using a thermosetting inkjet ink, comprising: the thermosetting inkjet ink contains a photopolymerizable compound, a thermosetting compound, and a photopolymerization initiator; The photopolymerization initiator is an acylphosphine-based initiator or an aminoacetophenone-based initiator, and the content thereof is within the range of 1 to 100 mmol / kg; and A printing method comprising the following steps (1) to (3): (1) A process in which a thermosetting inkjet ink is ejected from a nozzle and landed on a recording medium. (2) A step of pre-curing the deposited thermosetting inkjet ink by irradiating it with actinic rays in an atmosphere with an oxygen concentration in the range of 0.1 to 10.0% by volume. (3) Then, the partially cured thermosetting inkjet ink is heated to completely cure it.

[0015] 8. The printing method described in item 7, wherein the thermosetting compound is a blocked isocyanate in which a polyisocyanate is blocked with a blocking agent.

[0016] 9. The printing method according to item 8, wherein the polyisocyanate is an aliphatic polyisocyanate.

[0017] 10. The printing method described in any one of items 7 to 9, wherein the content of the photopolymerization initiator is within the range of 1 to 70 mmol / kg.

[0018] 11. The printing method described in any one of items 7 to 10, wherein the photopolymerization initiator further contains a thioxanthone-based initiator in the range of 40 to 400 mmol / kg.

[0019] 12. The printing method described in any one of items 7 to 10, wherein the photopolymerization initiator further contains a thioxanthone-based initiator in the range of 100 to 400 mmol / kg.

[0020] 13. The printing method according to any one of items 7 to 12, wherein the thermosetting ink-jet ink contains a gelling agent. Effect of the Invention

[0021] According to the above-mentioned means of the present invention, it is possible to provide a thermosetting ink-jet ink capable of forming a coating film having excellent substrate adhesion, high surface hardness, and good surface tackiness, and also to provide a printing method capable of forming a coating film having excellent substrate adhesion, high surface hardness, and good surface tackiness.

[0022] Although the mechanism by which the effects of the present invention are expressed or the mechanism of action has not been clarified, it is speculated as follows.

[0023] The conventional double cure method, in which a hardened solder resist film is formed using light and heat by an inkjet method, did not provide sufficient adhesion to the metal substrate. Since adhesion to the substrate is believed to be achieved by the thermosetting reaction, it is important to increase the reactivity of the thermosetting compound. Although adhesion can be increased by increasing the thermosetting temperature, this increases the process load and is not realistic.

[0024] In the present invention, the provisional curing by light is suppressed, and the thermosetting property is improved by using a gelling agent, and high metal adhesion is obtained. Specifically, it is presumed that by reducing the amount of photopolymerization initiator used within a specific range, not only the compound having a photopolymerizable group consumed in the photocuring (provisional curing) but also the thermosetting compound is reduced, so that when the subsequent thermal curing is performed, a relatively large amount of the thermosetting compound can be left in the vicinity of the metal substrate. Furthermore, since the gelling agent is not incorporated in the polymerization reaction when irradiated with active light rays, for example, ultraviolet light (UV light), and has a melting property when heated, it functions as a dissolving agent for the thermosetting agent during thermal polymerization and promotes the thermal curing reaction.

[0025] On the other hand, as the photocuring property is reduced, the surface tackiness tends to deteriorate, the surface becomes sticky, and handling during processing becomes difficult (for example, due to double-sided printing or dust contamination). However, it was found that the gelling agent also functions to improve the surface curing property during photocuring, and handling during processing is no longer a problem.

[0026] Furthermore, the printing method using the thermosetting inkjet ink of the present invention includes a step of provisionally curing the ink by irradiating the ink with active light rays in an atmosphere having an oxygen concentration of 0.1 to 10.0% by volume without using a gelling agent, as a measure to deal with the poor surface tackiness that accompanies the deterioration of the photocurability. By using such a printing method, the surface tackiness can be improved without using a gelling agent.

[0027] This is believed to be because no oxygen radicals are generated, and the radical monomers remaining in the film cured by actinic rays accelerate the thermosetting reaction. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0028] The thermosetting inkjet ink of the present invention is a thermosetting inkjet ink containing a thermosetting compound, and is characterized in that it contains a photopolymerizable compound, a thermosetting compound, a photopolymerization initiator, and a gelling agent, the photopolymerization initiator is an acylphosphine initiator or an aminoacetophenone initiator, the content of which is within the range of 1 to 100 mmol / kg, and the ink undergoes a sol-gel phase transition depending on temperature. This characteristic is a technical characteristic common to or corresponding to each of the following embodiments (configurations). As an embodiment of the present invention, from the viewpoint of exerting the effects of the present invention, it is preferable that the thermosetting compound is a blocked isocyanate in which a polyisocyanate is blocked with a blocking agent. In addition, it is preferable that the polyisocyanate is an aliphatic polyisocyanate, since this can provide high adhesion to the substrate and also improve the pencil hardness. Furthermore, in the present invention, the content of the photopolymerization initiator is preferably within the range of 1 to 70 mmol / kg. As an embodiment of the present invention, from the viewpoint of exerting the effects of the present invention, it is preferable that a thioxanthone-based initiator is further contained in the range of 40 to 400 mmol / kg as a photopolymerization initiator, and it is preferable that a thioxanthone-based initiator is further contained in the range of 100 to 400 mmol / kg from the viewpoint of surface tackiness and substrate adhesion. The printing method of the present invention is a printing method using a thermosetting ink-jet ink, characterized in that the thermosetting ink-jet ink contains a photopolymerizable compound, a thermosetting compound, and a photopolymerization initiator, the photopolymerization initiator is an acylphosphine-based initiator or an aminoacetophenone-based initiator, the content of which is within the range of 1 to 100 mmol / kg, and the printing method includes the steps (1) to (3). As an embodiment of the printing method of the present invention, from the viewpoint of manifesting the effects of the present invention, it is preferable that the thermosetting compound is a blocked isocyanate in which a polyisocyanate is blocked with a blocking agent. In addition, it is preferable that the polyisocyanate is an aliphatic polyisocyanate, since this can provide high adhesion to the substrate and also improve the pencil hardness. Furthermore, in the present invention, the content of the photopolymerization initiator is preferably within the range of 1 to 70 mmol / kg. Furthermore, from the viewpoint of exerting the effects of the present invention, it is preferable that a thioxanthone-based initiator is further contained as a photopolymerization initiator in a range of 40 to 400 mmol / kg, and it is preferable that a thioxanthone-based initiator is further contained in a range of 100 to 400 mmol / kg from the viewpoint of surface tackiness and substrate adhesion. Furthermore, in the printing method, it is preferable that the thermosetting ink-jet ink contains a gelling agent.

[0029] The present invention, its components, and embodiments for carrying out the present invention will be described in detail below. In this application, the symbol "to" is used to mean that the numerical values ​​before and after the symbol "to" are included as the lower limit and upper limit.

[0030] In the present invention, "(meth)acrylate" means acrylate or methacrylate, "(meth)acryloyl group" means acryloyl group or methacryloyl group, and "(meth)acrylic" means acrylic or methacrylic.

[0031] Overview of the Thermosetting Inkjet Ink of the Present Invention The thermosetting inkjet ink of the present invention contains a photopolymerizable compound, a thermosetting compound, a photopolymerization initiator, and a gelling agent, The photopolymerization initiator is an acylphosphine-based initiator or an aminoacetophenone-based initiator, and the content thereof is within the range of 1 to 100 mmol / kg; and It is characterized by a sol-gel phase transition due to temperature.

[0032] As described above, in the present invention, the thermosetting property is improved by suppressing the temporary curing by light, and the adhesion to the substrate is improved. In addition, by using a gelling agent that is not incorporated in the photopolymerization reaction, the thermally polymerizable compound is melted and the thermosetting property is further promoted. The amount of photopolymerization initiator is reduced to suppress the degree of polymerization during photocuring, but on the other hand, the photocuring property is reduced, which leads to poor surface tackiness and makes handling during the process difficult (e.g. double-sided printing or dust contamination). Therefore, by using a thermosetting inkjet ink containing an added gelling agent, the surface hardening properties are increased while the degree of polymerization inside is suppressed, making it possible to achieve both substrate adhesion and surface tackiness while maintaining high surface hardness.

[0033] If the content of the photopolymerization initiator is less than 1 mol / kg, the surface hardness will be insufficient due to insufficient surface curing, and if the content exceeds 100 mmol / kg, the adhesion to the substrate will not be strong enough, which is undesirable.

[0034] When the heat curing agent is a blocked isocyanate, especially when it is an aliphatic polyisocyanate type, the solubility with the gelling agent during heat curing increases, resulting in higher adhesion to the substrate. Furthermore, the pencil hardness can be improved by the polymerization proceeding uniformly throughout the coating film.

[0035] Furthermore, increasing the amount of thioxanthone initiator, which is an initiator that is effective in improving surface tackiness, also improves substrate adhesion. This is thought to be because while the light absorption at the surface during photopolymerization improves, the number of photons in the depth direction decreases, resulting in a decrease in the degree of polymerization at the substrate interface and a greater promotion of the thermal curing reaction.

[0036] <<Details of the Thermosetting Inkjet Ink of the Present Invention>> The composition of the thermosetting inkjet ink of the present invention will be described in detail below.

[0037] [Thermosetting compound] The thermosetting compound used in the present invention is preferably at least one selected from a cyclic ether group-containing thermosetting compound, an isocyanate group-containing thermosetting compound, and a compound containing a maleimide group.

[0038] (Cyclic ether group-containing thermosetting compound) The cyclic ether group-containing thermosetting compound may have a plurality of cyclic ether groups in the molecule, and is preferably a compound having an epoxy group or an oxetanyl group.

[0039] Examples of the compound having an epoxy group include various chain epoxy group-containing monomers (e.g., glycidyl (meth)acrylate, β-methylglycidyl (meth)acrylate, glycidyl vinyl ether, allyl glycidyl ether, etc.), various (2-oxo-1,3-oxolane) group-containing vinyl monomers (e.g., (2-oxo-1,3-oxolane)methyl (meth)acrylate, etc.), various alicyclic epoxy group-containing vinyl monomers (e.g., 3,4-epoxycyclohexyl (Meth)acrylate, 3,4-epoxycyclohexylmethyl (meth)acrylate, 3,4-epoxycyclohexylethyl (meth)acrylate, etc.), bisphenol A diglycidyl ether, bisphenol F diglycidyl ether, bisphenol S diglycidyl ether, brominated bisphenol A diglycidyl ether, brominated bisphenol F diglycidyl ether, brominated bisphenol S diglycidyl ether, hydrogenated bisphenol A diglycidyl ether, hydrogenated bisphenol F diglycidyl ether, hydrogenated bisphenol S diglycidyl ether, 1,4-butanediol diglycidyl ether, 1,6-hexanediol diglycidyl ether, glycerin triglycidyl ether, trimethylolpropane triglycidyl ether, polyethylene glycol diglycidyl ether, polypropylene glycol diglycidyl ethers; polyglycidyl ethers of polyether polyols obtained by adding one or more alkylene oxides to aliphatic polyhydric alcohols such as ethylene glycol, propylene glycol, and glycerin; diglycidyl esters of aliphatic long-chain dibasic acids; monoglycidyl ethers of aliphatic higher alcohols; monoglycidyl ethers of polyether alcohols obtained by adding phenol, cresol, butylphenol, or these with alkylene oxides; and glycidyl esters of higher fatty acids.

[0040] Further, examples of the compound having an epoxy group include a compound having a (meth)acryloyl group and an epoxy group, a partial (meth)acrylic compound of an epoxy compound, etc. Examples of the compound having a (meth)acryloyl group and an epoxy group include glycidyl (meth)acrylate, 4-hydroxybutyl (meth)acrylate glycidyl ether, etc.

[0041] Examples of compounds having an oxetanyl group include bis[(3-methyl-3-oxetanylmethoxy)methyl]ether, bis[(3-ethyl-3-oxetanylmethoxy)methyl]ether, 1,4-bis[(3-methyl-3-oxetanylmethoxy)methyl]benzene, 1,4-bis[(3-ethyl-3-oxetanylmethoxy)methyl]benzene, (3-methyl-3-oxetanyl)methyl acrylate, (3-ethyl-3-oxetanyl)methyl Examples of the oxetanes include polyfunctional oxetanes such as aryl acrylate, (3-methyl-3-oxetanyl)methyl methacrylate, (3-ethyl-3-oxetanyl)methyl methacrylate, and oligomers or copolymers thereof, as well as ethers of oxetane alcohols with novolac resins, poly(p-hydroxystyrene), cardo-type bisphenols, calixarenes, calixresorcinarenes, silsesquioxane, and other resins having a hydroxyl group. Other examples include copolymers of unsaturated monomers having an oxetane ring and alkyl (meth)acrylates.

[0042] (Isocyanate group-containing thermosetting compound) The isocyanate group-containing thermosetting compound is not particularly limited as long as it is a compound having two or more isocyanate groups in the molecule, and specific examples thereof include aromatic compounds such as 2,4-tolylene diisocyanate (2,4-TDI), 2,6-tolylene diisocyanate (2,6-TDI), 4,4'-diphenylmethane diisocyanate (4,4'-MDI), 2,4'-diphenylmethane diisocyanate (2,4'-MDI), 1,4-phenylene diisocyanate, xylylene diisocyanate (XDI), tetramethylxylylene diisocyanate (TMXDI), tolidine diisocyanate (TODI), and 1,5-naphthalene diisocyanate (NDI). Examples of the polyisocyanate include aromatic polyisocyanates; aliphatic polyisocyanates such as hexamethylene diisocyanate (HDI), trimethylhexamethylene diisocyanate (TMHDI), lysine diisocyanate, and norbornane diisocyanate methyl (NBDI); alicyclic polyisocyanates such as transcyclohexane-1,4-diisocyanate, isophorone diisocyanate (IPDI), H6XDI (hydrogenated XDI), H12MDI (hydrogenated MDI), and H6TDI (hydrogenated TDI); polyisocyanates such as polymethylene polyphenylene polyisocyanate; and biuret derivatives, isocyanurate derivatives, and carbodiimide-modified derivatives of these.

[0043] Among these, blocked isocyanates, which are polyfunctional isocyanates having an isocyanate group protected with a thermally dissociable blocking agent, are particularly preferred from the viewpoints of substrate adhesion and surface hardness of the coating film. In other words, it is preferable that the polyisocyanate is a blocked isocyanate blocked with a blocking agent. The heat curing reaction proceeds by thermal dissociation of the isocyanate group protected by the blocking agent, but in the case of the double cure method, it is difficult to promote the heat curing reaction after UV polymerization, but in the case of the present invention, since the gelling agent is not incorporated into the monomer polymerization during UV irradiation and has a warm melting property, it functions as a dissolving aid for the heat curing agent during thermal polymerization and promotes the heat curing reaction. The effect is remarkable because of the high compatibility between isocyanate and gelling agent. In particular, the solubility is further increased in the case of aliphatic polyisocyanate type, resulting in higher adhesion to the substrate. The heat curing agent becomes uniform in the coating film during thermal polymerization, and the surface hardness is also improved.

[0044] The thermally dissociable blocking agent is preferably at least one compound selected from the group consisting of oxime compounds, pyrazole compounds, and active ethylene compounds, from the viewpoints of ink storage stability and thermal dissociability.

[0045] Examples of the oxime compounds include formamide oxime, acetaldoxime, acetoxime, methyl ethyl ketone oxime, and cyclohexanone oxime.

[0046] Examples of the pyrazole-based compounds include pyrazole, 3-methylpyrazole, and 3,5-dimethylpyrazole.

[0047] Examples of active ethylenic compounds include dimethyl malonate, diethyl malonate, methyl acetoacetate, ethyl acetoacetate, and acetylacetone.

[0048] Examples of the polyfunctional isocyanate having an isocyanate group protected with a blocking agent include 2-[(3,5-dimethylpyrazolyl)carbonylamino]ethyl methacrylate, 2-[(3-butylidene)aminooxycarbonylamino]ethyl methacrylate, 2-[(3,5-dimethylpyrazolyl)carbonylamino]ethyl acrylate, and 2-[(3-butylidene)aminooxycarbonylamino]ethyl acrylate.

[0049] (Compounds containing maleimide groups) Examples of compounds containing a maleimide group include N-methylmaleimide, N-ethylmaleimide, N-hexylmaleimide, N-propylmaleimide, N-butylmaleimide, N-octylmaleimide, N-dodecylmaleimide, N-cyclohexylmaleimide, N-phenylmaleimide, Np-carboxyphenylmaleimide, Np-hydroxyphenylmaleimide, Np-chlorophenylmaleimide, Np-tolylmaleimide, Np-xylylmaleimide, No-chlorophenylmaleimide, No-tolylmaleimide, N-benzylmaleimide, N-2,5-diethylphenylmaleimide, N-2,5-dimethylphenylmaleimide, Nm-tolylmaleimide, N-α-naphthylmaleimide, No-xylylmaleimide, Nm-xylylmaleimide, amide, bismaleimide methane, 1,2-bismaleimide ethane, 1,6-bismaleimide hexane, bismaleimide dodecane, N,N'-m-phenylene dimaleimide, N,N'-p-phenylene dimaleimide, 4,4' bismaleimide diphenyl ether, 4,4'-bismaleimide diphenyl methane, 4,4'-bismaleimide-di(3-methylphenyl) methane, 4,4'-bismaleimide-di(3-ethylphenyl) methane, 4,4'-bismaleimide-di(3-methyl-5-ethyl-phenyl) methane, N,N'-(2,2-bis-(4-phenoxyphenyl) propane) dimaleimide, N,N'-2,4-tolylene dimaleimide, N,N'-2,6-tolylene dimaleimide, N,N'-m-xylylene dimaleimide, bisphenol A diphenyl ether bismaleimide, and the like. Of these, bismaleimide is preferred.

[0050] [Photopolymerizable compound] Examples of the photopolymerizable compound include a radically polymerizable compound and a cationic polymerizable compound.

[0051] The photopolymerizable compound may be any compound that undergoes a polymerization or crosslinking reaction by irradiation with actinic rays, polymerizing or crosslinking, and curing the ink. Examples of the photopolymerizable compound include radically polymerizable compounds and cationic polymerizable compounds. The photopolymerizable compound may be any of a monomer, a polymerizable oligomer, a prepolymer, and a mixture thereof. The photopolymerizable compound may be contained in the inkjet ink in one type or in two or more types.

[0052] The content of the photopolymerizable compound can be, for example, from 1% by mass to 97% by mass relative to the total mass of the ink-jet ink. The radical polymerizable compound is preferably an unsaturated carboxylic acid ester, and more preferably a (meth)acrylate. In the present invention, "(meth)acrylate" means acrylate or methacrylate, "(meth)acryloyl group" means acryloyl group or methacryloyl group, and "(meth)acrylic" means acrylic or methacrylic.

[0053] Examples of (meth)acrylates include isoamyl (meth)acrylate, stearyl (meth)acrylate, lauryl (meth)acrylate, octyl (meth)acrylate, decyl (meth)acrylate, isomylstyryl (meth)acrylate, isostearyl (meth)acrylate, 2-ethylhexyl-diglycol (meth)acrylate, 2-hydroxybutyl (meth)acrylate, 2-(meth)acryloyloxyethylhexahydrophthalate, butoxyethyl (meth)acrylate, ethoxydiethylene glycol (meth)acrylate, methoxydiethylene glycol (meth)acrylate, methoxypolyethylene glycol (meth)acrylate, methoxypropylene glycol (meth)acrylate, phenoxyethyl (meth)acrylate, tetrahydrofurfuryl (meth)acrylate, isobornyl (meth)acrylate, monofunctional acrylates including t-butylcyclohexyl (meth)acrylate, 2-hydroxyethyl (meth)acrylate, 2-hydroxypropyl (meth)acrylate, 2-hydroxy-3-phenoxypropyl (meth)acrylate, 2-(meth)acryloyloxyethyl succinate, 2-(meth)acryloyloxyethyl phthalate, 2-(meth)acryloyloxyethyl-2-hydroxyethyl phthalate, and t-butylcyclohexyl (meth)acrylate, as well as triethylene glycol di(meth)acrylate, tetraethylene glycol di(meth)acrylate, polyethylene glycol di(meth)acrylate, tripropylene glycol di(meth)acrylate, polypropylene glycol di(meth)acrylate, 1,4-butanediol di(meth)acrylate, 1,6-hexanediol di(meth)acrylate, 1,Examples of the acrylates include bifunctional acrylates such as 9-nonanediol di(meth)acrylate, neopentyl glycol di(meth)acrylate, dimethylol-tricyclodecane di(meth)acrylate, PO adduct di(meth)acrylate of bisphenol A, hydroxypivalic acid neopentyl glycol di(meth)acrylate, polytetramethylene glycol di(meth)acrylate, polyethylene glycol diacrylate, tripropylene glycol diacrylate, and tricyclodecane dimethanol diacrylate, as well as multifunctional acrylates such as trimethylolpropane tri(meth)acrylate, pentaerythritol tri(meth)acrylate, pentaerythritol tetra(meth)acrylate, dipentaerythritol hexa(meth)acrylate, ditrimethylolpropane tetra(meth)acrylate, glycerin propoxy tri(meth)acrylate, and pentaerythritol ethoxy tetra(meth)acrylate.

[0054] From the viewpoint of photosensitivity and the like, the (meth)acrylate is preferably stearyl (meth)acrylate, lauryl (meth)acrylate, isostearyl (meth)acrylate, ethoxydiethylene glycol (meth)acrylate, isobornyl (meth)acrylate, tetraethylene glycol di(meth)acrylate, glycerin propoxy tri(meth)acrylate, or the like.

[0055] The (meth)acrylate may be a modified product. Examples of modified (meth)acrylates include ethylene oxide-modified trimethylolpropane tri(meth)acrylate, ethylene oxide-modified (meth)acrylate including ethylene oxide-modified pentaerythritol tetraacrylate, caprolactone-modified (meth)acrylate including caprolactone-modified trimethylolpropane tri(meth)acrylate, and caprolactam-modified (meth)acrylate including caprolactam-modified dipentaerythritol hexa(meth)acrylate.

[0056] The (meth)acrylate may be a polymerizable oligomer. Examples of the (meth)acrylate that is a polymerizable oligomer include an epoxy (meth)acrylate oligomer, an aliphatic urethane (meth)acrylate oligomer, an aromatic urethane (meth)acrylate oligomer, a polyester (meth)acrylate oligomer, and a linear (meth)acrylic oligomer.

[0057] The cationically polymerizable compound may be an epoxy compound, a vinyl ether compound, an oxetane compound, etc. The inkjet ink may contain only one type of cationically polymerizable compound, or may contain two or more types of cationically polymerizable compounds.

[0058] [Gelling agent] It is preferred that the gelling agent according to the present invention exists in the cured film after curing with actinic rays without being incorporated into the polymerization, and that it becomes in a molten state in the coating film during thermal polymerization, thereby making the heat curing agent uniform.

[0059] Such a gelling agent is preferably at least one of the compounds represented by the following general formula (G1) or (G2), in that it is dispersed in the cured film without inhibiting the curing of the ink, and is also preferable in that it has good pinning properties in inkjet printing, can be drawn with both fine lines and a thick film, and has excellent fine line reproducibility.

[0060] General formula (G1): R1-CO-R2 General formula (G2): R3-COO-R4 (In the formula, R1 to R4 each independently represent an alkyl chain having a linear portion having 12 or more carbon atoms and which may be branched.) The ketone wax represented by the general formula (G1) or the ester wax represented by the general formula (G2) has a linear or branched hydrocarbon group (alkyl chain) with 12 or more carbon atoms, which enhances the crystallinity of the gelling agent, improves water resistance, and creates more sufficient spaces in the house-of-cards structure described below. This makes it easier for ink media such as solvents and photopolymerizable compounds to be fully enclosed in the spaces, improving the pinning ability of the ink.

[0061] In addition, the number of carbon atoms in the linear or branched hydrocarbon group (alkyl chain) is preferably 26 or less. If the carbon number is 26 or less, the melting point of the gelling agent will not be excessively high, and therefore it is not necessary to excessively heat the ink when ejecting it.

[0062] From the above viewpoint, it is particularly preferable that R1 and R2, or R3 and R4, are linear hydrocarbon groups having 12 to 23 carbon atoms.

[0063] In addition, from the viewpoint of increasing the gelation temperature of the ink and gelling the ink more rapidly after it has landed, it is preferable that either R1 or R2, or either R3 or R4, is a saturated hydrocarbon group having 12 to 23 carbon atoms. From the above viewpoint, it is more preferable that both R1 and R2, or both R3 and R4, are saturated hydrocarbon groups having 11 or more and less than 23 carbon atoms.

[0064] Examples of the ketone wax represented by the general formula (G1) include dilignoceryl ketone (C24-C24), dibehenyl ketone (C22-C22), distearyl ketone (C18-C18), dieicosyl ketone (C20-C20), dipalmityl ketone (C16-C16), dimyristyl ketone (C14-C14), dilauryl ketone (C12-C12), lauryl myristyl ketone ( These include: lauryl palmityl ketone (C12-C14), myristyl palmityl ketone (C14-C16), myristyl stearyl ketone (C14-C18), myristyl behenyl ketone (C14-C22), palmityl stearyl ketone (C16-C18), palmityl behenyl ketone (C16-C22), and stearyl behenyl ketone (C18-C22). The number of carbons in the parentheses above indicates the number of carbons in each of the two hydrocarbon groups separated by the carbonyl group.

[0065] Commercially available examples of the ketone wax represented by general formula (G1) include Stearonne (manufactured by Alfa Aeser; Stearon), 18-Pentatriacontanone (manufactured by Alfa Aeser), Hentriacontan-16-one (manufactured by Alfa Aeser), and Kaowax T-1 (manufactured by Kao Corporation).

[0066] Examples of fatty acids or ester waxes represented by general formula (G2) include behenyl behenate (C21-C22), icosanoic acid icosyl (C19-C20), stearyl stearate (C17-C18), palmityl stearate (C17-C16), lauryl stearate (C17-C12), cetyl palmitate (C15-C16), stearyl palmitate (C15-C18), and the like. ), myristyl myristate (C13-C14), cetyl myristate (C13-C16), octyldodecyl myristate (C13-C20), stearyl oleate (C17-C18), stearyl erucate (C21-C18), stearyl linoleate (C17-C18), behenyl oleate (C18-C22), and arachidyl linoleate (C17-C20). The number of carbon atoms in the parentheses above indicates the number of carbon atoms in each of the two hydrocarbon groups separated by the ester group.

[0067] Commercially available examples of the ester wax represented by general formula (G2) include Unistar M-2222SL and Sperm Acetate, manufactured by NOF Corporation ("Unistar" is a registered trademark of the company), Exepar SS and Exepar MY-M, manufactured by Kao Corporation ("Exepar" is a registered trademark of the company), EMALEX CC-18 and EMALEX CC-10, manufactured by Nippon Emulsion Co., Ltd. ("EMALEX" is a registered trademark of the company), and Amureps PC, manufactured by Kokyu Alcohol Kogyo Co., Ltd. ("Amureps" is a registered trademark of the company).

[0068] These commercially available products are often mixtures of two or more kinds, and therefore may be separated and purified as necessary before being added to the ink. Among these gelling agents, ketone wax, ester wax, higher fatty acid, higher alcohol, and fatty acid amide are preferred from the viewpoint of solubility.

[0069] The content of the gelling agent according to the present invention is preferably within the range of 0.5 to 5.0% by mass relative to the total mass of the ink. By setting the content of the gelling agent within the above range, the solubility of the gelling agent in the solvent component is improved. From the above viewpoint, the content of the gelling agent in the inkjet ink is more preferably within the range of 0.5 to 2.5% by mass.

[0070] Moreover, it is preferable that the gelling agent crystallizes in the ink at a temperature equal to or lower than the gelling temperature of the ink. The gelling temperature refers to the temperature at which the gelling agent undergoes a phase transition from sol to gel and the viscosity of the ink suddenly changes when the ink that has been solated or liquefied by heating is cooled. Specifically, the solated or liquefied ink is cooled while the viscosity is measured using a viscoelasticity measuring device (e.g., MCR300, manufactured by Physica), and the temperature at which the viscosity suddenly increases can be determined as the gelling temperature of the ink.

[0071] [Photopolymerization initiator] The photopolymerization initiator according to the present invention is preferably an acylphosphine-based initiator or an aminoacetophenone-based initiator. The acylphosphine-based initiator is preferably an acylphosphine oxide. The acylphosphine oxide is a photopolymerization initiator that has absorption at long wavelengths and is effective in increasing internal sensitivity. Specific examples include monoacylphosphine oxide and bisacylphosphine oxide. In addition, the aminoacetophenone-based initiator is a photopolymerization initiator having a structure in which a strong electron donating group such as an alkylthio group or a dialkylamino group is substituted at the para position of the benzoyl group. Due to this substituent, the absorption tail extends to long wavelengths. This is advantageous for increasing internal sensitivity. Specific examples include 2-methyl-1-[4-(methylthio)phenyl]-2-morpholinopropan-1-one and 2-benzyl-2-dimethylamino-I-(4-morpholinophenyl)-butanone-1.

[0072] The smaller the amount added, the better, since it suppresses the temporary curing by light and promotes the heat curing reaction. However, since the surface tackiness is deteriorated by reducing the temporary curing by light, the amount is preferably within the range of 1 to 100 mmol / kg. By keeping it within the range of 1 to 70 mmol / kg, the adhesion to the substrate can be further improved.

[0073] In the present invention, it is preferable to further add a thioxanthone initiator. Increasing the amount of thioxanthone initiator, which is an initiator effective in improving surface curing properties, improves adhesion to the substrate in particular. It is believed that while light absorption at the surface improves, the number of photons in the depth direction decreases, resulting in a decrease in the degree of polymerization at the substrate interface and further accelerating the thermosetting reaction.

[0074] Specific examples of thioxanthone initiators include 2-isopropylthioxanthone, 2-4-dimethylthioxanthone, 2,4-diethylthioxanthone, and 2,4-dichlorothioxanthone. From the above viewpoints, the amount added is preferably within the range of 40 to 400 mmol / kg, more preferably within the range of 100 to 400 mmol / kg.

[0075] [Coloring agent] The ink of the present invention may further contain a colorant, if necessary. The colorant may be a dye or a pigment, but a pigment is preferred because it has good dispersibility in the components of the ink and has excellent weather resistance. The pigment is not particularly limited, but examples thereof include the organic pigments or inorganic pigments listed in the Color Index as follows:

[0076] Examples of red or magenta pigments include Pigment Red 3, 5, 19, 22, 31, 38, 43, 48:1, 48:2, 48:3, 48:4, 48:5, 49:1, 53:1, 57:1, 57:2, 58:4, 63:1, 81, 81:1, 81:2, 81:3, 81:4, 88, 104, 108, 112, 122, 123, 144, 146, 149, 166, 168, 169, 170, 177, 178, 179, 184, 185, 208, 216, 226, 257, Pigment Violet 3, 19, 23, 29, 30, 37, 50, 88, Pigment Orange 13, 16, 20, 36 or a mixture thereof.

[0077] Examples of blue or cyan pigments include pigments selected from Pigment Blue 1, 15, 15:1, 15:2, 15:3, 15:4, 15:6, 16, 17-1, 22, 27, 28, 29, 36, 60, or mixtures thereof.

[0078] Examples of green pigments include pigments selected from Pigment Green 7, 26, 36, 50, or mixtures thereof.

[0079] Examples of yellow pigments include pigments selected from Pigment Yellow 1, 3, 12, 13, 14, 17, 34, 35, 37, 55, 74, 81, 83, 93, 94, 95, 97, 108, 109, 110, 137, 138, 139, 153, 154, 155, 157, 166, 167, 168, 180, 185, and 193, or mixtures thereof.

[0080] Examples of the black pigment include pigments selected from Pigment Black 7, 28, and 26, or mixtures thereof.

[0081] Examples of commercially available pigments include Black Pigment (manufactured by Mikuni), Chromofine Yellow 2080, 5900, 5930, AF-1300, 2700L, Chromofine Orange 3700L, 6730, Chromofine Scarlet 6750, Chromofine Magenta 6880, 6886, 6891N, 6790, 6887, Chromofine Violet RE, Chromofine Red 6820, 6830, Chromofine Blue HS-3, 5187, 5108, 5197, 5085N, SR-5020, 5026, 5050, 4920, 4927, 4937, 4824, 4933GN-EP, 4940, 4973, 5205, 5208, 5214, 5221, 5000P, CHROMO FINE GREEN 2GN, 2GO, 2G-550D, 5310, 5370, 6830, CHROMO FINE BLACK A-1103, SEIKA FAST YELLOW 10GH, A-3, 2035, 2054, 2200, 2270, 2300, 2400(B), 2500, 2600, ZAY-260, 2700(B), 2770, Seika Fast Red 8040, C405(F), CA120, LR-116, 1531B, 8060R, 1547, ZAW-262, 1537B, GY, 4R-4016, 3820, 3891, ZA-215, Seika Fast Carmine 6B1476T-7, 1483LT, 3840, 3870, Seika Fast Bordeaux 10B-430, Seika Light Rose R40, Seika Light Violet B800, 7805, Seika Fast Maroon 460N, Seika Fast Orange 900, 2900, Seika Light Blue C718, A612, Cyanine Blue 4933M, 4933GN-EP, 4940, 4973 (all manufactured by Dainichi Seika Chemicals); KET Yellow 401, 402, 403, 404, 405, 406, 416, 424, KET Orange 501, KET Red 301, 302, 303, 304, 305, 306, 307, 308, 309, 310, 336, 337, 338, 346, KET Blue 101, 102, 103, 104, 105, 106, 111, 118, 124, KET Green 201 (manufactured by DIC);Colortex Yellow 301, 314, 315, 316, P-624, 314, U10GN, U3GN, UNN, UA-414, U263, Finecol Yellow T-13, T-05, Pigment Yellow1705, Colortex Orange 202, Colortex Red101, 103, 115, 116, D3B, P-625, 102, H-1024, 105C, UFN, UCN, UBN, U3BN, URN, UGN, UG276, U456, U457, 105C, USN, Colortex Maroon601, Colortex BrownB610N, Colortex Violet600, Pigment Red 122, Colortex Blue516, 517, 518, 519, A818, P-908, 510, Colortex Green 402, 403, Colortex Black 702, U905 (all manufactured by Sanyo Dye Co., Ltd.); Lionol Yellow 1405G, Lionol Blue FG7330, FG7350, FG7400G, FG7405G, ES, ESP-S (all manufactured by Toyo Ink Co., Ltd.); Toner Magenta E02, Permanent Rubin F6B, Toner Yellow HG, Permanent Yellow GG-02, Hostapearm Blue B2G (all manufactured by Hoechst Industries AG); Novoperm P-HG, Hostaperm Pink E, Hostaperm Blue B2G (all manufactured by Clariant); carbon black #2600, #2400, #2350, #2200, #1000, #990, #980, #970, #960, #950, #850, MCF88, #750, #650, MA600, MA7, MA8, MA11, MA100, MA100R, MA77, #52, #50, #47, #45, #45L, #40, #33, #32, #30, #25, #20, #10, #5, #44, CF9 (all manufactured by Mitsubishi Chemical), etc.;

[0082] The pigment can be dispersed by using, for example, a ball mill, a sand mill, an attritor, a roll mill, an agitator, a Henschel mixer, a colloid mill, an ultrasonic homogenizer, a pearl mill, a wet jet mill, a paint shaker, or the like.

[0083] The pigment is preferably dispersed so that the volume average particle size of the pigment particles is preferably within a range of 0.08 to 0.5 μm, and the maximum particle size is preferably within a range of 0.3 to 10 μm, more preferably within a range of 0.3 to 3 μm. The dispersion of the pigment is adjusted by selecting the pigment, dispersant, and dispersion medium, and by adjusting the dispersion conditions and filtration conditions.

[0084] The ink of the present invention may further contain a dispersant to enhance the dispersibility of the pigment. Examples of dispersants include carboxylates having a hydroxyl group, salts of long-chain polyaminoamides and high molecular weight acid esters, salts of high molecular weight polycarboxylic acids, salts of long-chain polyaminoamides and polar acid esters, high molecular weight unsaturated acid esters, polymer copolymers, modified polyurethanes, modified polyacrylates, polyether ester-type anionic surfactants, naphthalenesulfonic acid-formaldehyde condensate salts, aromatic sulfonic acid-formaldehyde condensate salts, polyoxyethylene alkyl phosphate esters, polyoxyethylene nonylphenyl ether, and stearylamine acetate, etc. Examples of commercially available dispersants include the Solsperse series from Avecia and the PB series from Ajinomoto Fine-Techno Co., Ltd.

[0085] The ink of the present invention may further contain a dispersing aid, if necessary. The dispersing aid may be selected depending on the pigment. The total amount of the dispersant and the dispersion aid is preferably within the range of 1 to 50% by mass relative to the pigment.

[0086] The ink of the present invention may further contain a dispersion medium for dispersing the pigment as necessary. Although a solvent may be contained in the ink as the dispersion medium, in order to suppress the solvent from remaining in the formed image, it is preferable to use the above-mentioned photopolymerizable compound (particularly a monomer having a low viscosity) as the dispersion medium.

[0087] The dye may be an oil-soluble dye. Examples of oil-soluble dyes include the following dyes: Examples of magenta dyes include MS Magenta VP, MS Magenta HM-1450, MS Magenta HSo-147 (all manufactured by Mitsui Chemicals), AIZENSOT Red-1, AIZEN SOT Red-2, AIZEN SOTRed-3, AIZEN SOT Pink-1, SPIRON Red GEH SPECIAL (all manufactured by Hodogaya Chemical), RESOLIN Red FB 200%, MACROLEX Red Violet R, MACROLEX ROT5B (all manufactured by Bayer Japan), KAYASET Red B, KAYASET Red 130, KAYASET Red 802 (all manufactured by Nippon Kayaku), PHLOXIN, ROSE BENGAL, ACID Red (all manufactured by Daiwa Kasei), HSR-31, DIARESIN Red K (all manufactured by Mitsubishi Kasei), and Oil Red (manufactured by BASF Japan).

[0088] Examples of cyan dyes include MS Cyan HM-1238, MS Cyan HSo-16, Cyan HSo-144, and MS Cyan VPG (all manufactured by Mitsui Chemicals), AIZEN SOT Blue-4 (manufactured by Hodogaya Chemical), RESOLIN BR.Blue BGLN 200%, MACROLEX Blue RR, CERES Blue GN, SIRIUS SUPRATURQ.Blue Z-BGL, and SIRIUS SUPRA TURQ.Blue FB-LL 330% (manufactured by Bayer Japan), KAYASET Blue FR, KAYASET Blue N, KAYASET Blue 814, Turq.Blue GL-5 200, and Light Blue BGL-5200 (manufactured by Nippon Kayaku), DAIWA Blue 7000, and OleosolFast Blue GL (manufactured by Daiwa Kasei), DIARESIN Blue P (manufactured by Mitsubishi Kasei), and SUDAN Blue. 670, NEOPEN Blue 808, ZAPON Blue 806 (all manufactured by BASF Japan Ltd.), etc.

[0089] Examples of yellow dyes include MS Yellow HSm-41, Yellow KX-7, Yellow EX-27 (manufactured by Mitsui Chemicals), AIZEN SOT Yellow-1, AIZEN SOT Yellow W-3, AIZEN SOT Yellow-6 (all manufactured by Hodogaya Chemical Co., Ltd.), MACROLEX Yellow 6G, MACROLEX FLUOR.Yellow 10GN (all manufactured by Bayer Japan Ltd.), KAYASET Yellow SF-G, KAYASET Yellow 2G, KAYASET Yellow AG, KAYASET Yellow EG (all manufactured by Nippon Kayaku Co., Ltd.), DAIWA Yellow 330HB (manufactured by Daiwa Kasei Co., Ltd.), HSY-68 (manufactured by Mitsubishi Kasei Corporation), SUDAN Yellow 146, NEOPEN Yellow 075 (all manufactured by BASF Japan Ltd.), and the like.

[0090] Examples of black dyes include MS Black VPC (manufactured by Mitsui Chemicals), AIZEN SOT Black-1, AIZEN SOT Black-5 (all manufactured by Hodogaya Chemical Co., Ltd.), RESORIN Black GSN 200%, RESOLIN Black BS (all manufactured by Bayer Japan KK), KAYASET Black AN (manufactured by Nippon Kayaku Co., Ltd.), DAIWA Black MSC (manufactured by Daiwa Kasei Co., Ltd.), HSB-202 (manufactured by Mitsubishi Kasei Corporation), NEPTUNE Black X60, NEOPEN Black X58 (all manufactured by BASF Japan KK), and the like.

[0091] The ink of the present invention may contain one or more types of colorants and may be toned to a desired color. The content of the colorant is preferably within a range of 0.1 to 20% by mass, and more preferably within a range of 0.4 to 10% by mass, based on the total amount of the ink.

[0092] [Other ingredients] The ink of the present invention may further contain other components including a polymerization inhibitor and a surfactant, as long as the effects of the present invention are obtained. Only one type of these components may be contained in the ink of the present invention, or two or more types may be contained.

[0093] (Polymerization inhibitor) Examples of polymerization inhibitors include (alkyl)phenols, hydroquinone, catechol, resorcinol, p-methoxyphenol, t-butylcatechol, t-butylhydroquinone, pyrogallol, 1,1-picrylhydrazyl, phenothiazine, p-benzoquinone, nitrosobenzene, 2,5-di-t-butyl-p-benzoquinone, dithiobenzoyl disulfide, picric acid, cupferron, aluminum N-nitrosophenylhydroxyamine, tri-p-nitrophenylmethyl, N-(3-oxyanilino-1,3-dimethylbutylidene)aniline oxide, dibutylcresol, cyclohexanone oxime cresol, guaiacol, o-isopropylphenol, butyraldoxime, methyl ethyl ketoxime, and cyclohexanone oxime.

[0094] Examples of commercially available polymerization inhibitors include Irgastab UV10 (manufactured by BASF) and Genorad 18 (manufactured by Rahn AG). The amount of the polymerization inhibitor can be set arbitrarily within the range in which the effects of the present invention can be obtained.

[0095] The amount of the polymerization inhibitor can be, for example, not less than 0.001% by mass and less than 1.0% by mass with respect to the total mass of the ink.

[0096] (Surfactant) Examples of the surfactant include anionic surfactants such as dialkyl sulfosuccinates, alkyl naphthalene sulfonates, and fatty acid salts; nonionic surfactants such as polyoxyethylene alkyl ethers, polyoxyethylene alkyl allyl ethers, acetylene glycols, and polyoxyethylene-polyoxypropylene block copolymers; cationic surfactants such as alkylamine salts and quaternary ammonium salts; and silicone-based and fluorine-based surfactants.

[0097] Examples of silicone surfactants include polyether-modified polysiloxane compounds, specifically Tego rad 2250 manufactured by Evonik, KF-351A, KF-352A, KF-642 and X-22-4272 manufactured by Shin-Etsu Chemical Co., Ltd., BYK307, BYK345, BYK347 and BYK348 manufactured by BYK-Chemie ("BYK" is a registered trademark of the company), and TSF4452 manufactured by Momentive Performance Materials.

[0098] The fluorosurfactant refers to a surfactant in which some or all of the hydrogen atoms bonded to the carbon atoms of the hydrophobic group of a normal surfactant are substituted with fluorine. Examples of fluorine-based surfactants include Megafac F, manufactured by DIC Corporation ("Megafac" is a registered trademark of the company), Surflon, manufactured by AGC Sei Chemical Co., Ltd. ("Surflon" is a registered trademark of the company), Fluorad FC, manufactured by 3M Corporation ("Fluorad" is a registered trademark of the company), Monflor, manufactured by Imperial Chemical Industries, Zonyls, manufactured by E.I. duPont Nemelas and Company, Licowet VPF, manufactured by Lubenberge-Hoechst, and FTERGENT, manufactured by Neos Corporation ("FTERGENT" is a registered trademark of the company).

[0099] The amount of the surfactant can be set arbitrarily as long as the effects of the present invention can be obtained. The amount of the surfactant can be, for example, 0.001% by mass or more and less than 1.0% by mass with respect to the total mass of the ink.

[0100] (Cure accelerator) In the present invention, a curing accelerator may be included as necessary. The curing accelerator is not particularly limited as long as it accelerates the thermal curing of the resin component. Examples of the curing accelerator include imidazoles, dicyandiamide derivatives, dicarboxylic acid dihydrazide, triphenylphosphine, tetraphenylphosphonium tetraphenylborate, 2-ethyl-4-methylimidazole-tetraphenylborate, and 1,8-diazabicyclo[5.4.0]undecene-7-tetraphenylborate.

[0101] (Coupling Agent) In the present invention, various coupling agents may be included as necessary. By including a coupling agent, the adhesion to the substrate can be improved. Examples of the various coupling agents include silane-based, titanium-based, and aluminum-based coupling agents.

[0102] (Ion scavenger) In the present invention, an ion scavenger may be included as necessary. The inclusion of an ion scavenger has the advantage that ionic impurities are adsorbed, improving the insulating properties of the cured film under hygroscopic conditions.

[0103] Examples of the ion trapping agent include inorganic ion adsorbents such as triazine thiol compounds, bisphenol-based reducing agents, zirconium compounds, and antimony bismuth-based magnesium aluminum compounds.

[0104] (solvent) In the ink of the present invention, essentially no solvent is preferred from the viewpoint of curability, but a solvent may be added to adjust the ink viscosity.

[0105] [Physical Properties] The viscosity of the ink of the present invention at 25° C. is 1 to 1×10 4 A viscosity within the Pa·s range is preferable in that the ink is sufficiently gelled when it lands and is cooled to room temperature, resulting in good pinning properties.

[0106] From the viewpoint of improving the ejection properties from an inkjet head, the viscosity of the ink of the present invention at 80° C. is preferably within the range of 3 to 20 mPa·s, and more preferably within the range of 7 to 9 mPa·s.

[0107] The ink of the present invention preferably has a phase transition point in the range of 40° C. or higher and lower than 100° C. When the phase transition point is 40° C. or higher, the ink quickly gels after landing on a recording medium, resulting in higher pinning properties. When the phase transition point is lower than 100° C., the ink is easy to handle and has high ejection stability. From the viewpoint of enabling the ink to be discharged at a lower temperature and reducing the load on the image forming apparatus, the phase transition point of the ink of the present invention is more preferably within the range of 40 to 60°C.

[0108] The viscosity at 80° C., the viscosity at 25° C. and the phase transition point of the ink of the present invention can be determined by measuring the temperature change of the dynamic viscoelasticity of the ink using a rheometer.

[0109] In the present invention, the viscosity and phase transition point are values ​​obtained by the following method. The ink of the present invention is heated to 100°C, and the viscosity is measured using a stress-controlled rheometer Physica MCR301 (cone plate diameter: 75 mm, cone angle: 1.0°) manufactured by Anton Paar. The ink is then cooled to 20°C under conditions of a shear rate of 11.7 (1 / s) and a temperature drop rate of 0.1°C / s, to obtain a temperature change curve of the viscosity.

[0110] The viscosities at 80°C and 25°C can be determined by reading the viscosities at 80°C and 25°C, respectively, on the viscosity temperature curve. The phase transition point can be determined as the temperature at which the viscosity becomes 200 mPa s on the viscosity temperature curve.

[0111] From the viewpoint of improving ejection properties from an inkjet head, the average dispersed particle size of the pigment particles according to the present invention is preferably within a range of 50 to 150 nm, and the maximum particle size is preferably within a range of 300 to 1000 nm, and more preferably within a range of 80 to 130 nm.

[0112] The average dispersed particle size of pigment particles in the present invention means a value determined by dynamic light scattering using a Datasizer Nano ZSP manufactured by Malvern. Note that inks containing colorants have high concentrations and light is not transmitted through this measuring device, so the ink is diluted 200 times before measurement. The measurement temperature is room temperature (25°C).

[0113] [Printing method] The printing method of the present invention is a printing method using a thermosetting ink-jet ink, characterized in that the thermosetting ink contains a photopolymerizable compound, a thermosetting compound, and a photopolymerization initiator, the photopolymerization initiator is an acylphosphine-based initiator or an aminoacetophenone-based initiator, the content of which is within the range of 1 to 100 mmol / kg, and the printing method includes the following steps (1) to (3):

[0114] (1) A process in which a thermosetting inkjet ink is ejected from a nozzle and landed on a recording medium. (2) A step of pre-curing the deposited thermosetting inkjet ink by irradiating it with actinic rays in an atmosphere with an oxygen concentration in the range of 0.1 to 10.0% by volume. (3) Then, the partially cured thermosetting inkjet ink is heated to completely cure it.

[0115] As described above, in the present invention, the thermosetting property is improved by suppressing the temporary curing by light, and the adhesion to the substrate is improved. The amount of photopolymerization initiator is reduced to suppress the degree of polymerization during photocuring, but on the other hand, the curing property is reduced, and the surface tackiness is deteriorated, making it difficult to handle during the process (for example, double-sided printing or dust contamination). The above-mentioned thermosetting inkjet ink of the present invention solves this problem by containing a gelling agent, but even if the ink does not contain a gelling agent, it is possible to achieve both substrate adhesion and surface tackiness while maintaining high surface hardness by using a printing method in which the ink is provisionally cured by irradiating the ink with active light in an atmosphere having an oxygen concentration of 0.1 to 10.0% by volume, thereby increasing the surface curability while suppressing the degree of polymerization inside the ink.

[0116] The thermosetting inkjet ink described in the following printing method has the same composition as the thermosetting inkjet ink of the present invention described above, except that it does not need to contain a gelling agent. The thermosetting inkjet ink used in the printing method is also referred to as the "ink of the present invention."

[0117] The ink according to the present invention is preferably an ink for forming a solder resist pattern used on a printed circuit board.

[0118] <Step (1)> The step (1) is a step of ejecting a thermosetting inkjet ink from a nozzle and causing it to land on a recording medium. In the step (1), droplets of the ink according to the present invention are ejected from an inkjet head and caused to land on a substrate, which is a recording medium, such as a printed circuit board, at positions corresponding to the resist film to be formed, thereby forming a pattern.

[0119] The ejection method from the inkjet head may be either an on-demand method or a continuous method. The on-demand inkjet head may be of any of the following types: electro-mechanical conversion type, such as single cavity type, double cavity type, bender type, piston type, shear mode type, and shared wall type; and electro-thermal conversion type, such as thermal inkjet type and Bubble Jet (registered trademark) type (Bubble Jet is a registered trademark of Canon Inc.).

[0120] The ejection stability can be improved by ejecting the ink droplets from the inkjet head in a heated state. The temperature of the ink when ejected is preferably within a range of 40 to 100°C, and more preferably within a range of 40 to 90°C in order to further improve the ejection stability. In particular, it is preferable to eject the ink at an ink temperature such that the viscosity of the ink is within a range of 7 to 15 mPa·s, more preferably within a range of 8 to 13 mPa·s.

[0121] When using a sol-gel phase transition type ink containing a gelling agent, the temperature of the ink when filled into the inkjet head is preferably set to (gelation temperature + 10)°C to (gelation temperature + 30)°C of the ink in question. If the temperature of the ink inside the inkjet head is less than (gelation temperature + 10)°C, the ink will gel inside the inkjet head or on the nozzle surface, and the ink ejection properties are likely to decrease. On the other hand, if the temperature of the ink inside the inkjet head exceeds (gelation temperature + 30)°C, the ink will become too hot, which may cause the ink components to deteriorate.

[0122] The method for heating the ink is not particularly limited. For example, at least one of an ink supply system such as an ink tank constituting the head carriage, a supply pipe, and an anterior ink tank immediately before the head, a pipe with a filter, and a piezo head can be heated by a panel heater, a ribbon heater, or warm water.

[0123] The amount of ink droplets ejected is preferably within the range of 2 to 20 pL in terms of recording speed and image quality.

[0124] The printed circuit board is not particularly limited, but examples thereof include copper-clad laminates for high frequency circuits made of materials such as paper phenol, paper epoxy, glass cloth epoxy, glass polyimide, glass cloth / non-woven epoxy, glass cloth / paper epoxy, synthetic fiber epoxy, fluorine-polyethylene-PPO-cyanate ester, and the like, and are preferably copper-clad laminates of all grades (FR-4, etc.), as well as polyimide films, PET films, glass substrates, ceramic substrates, wafer plates, stainless steel plates, etc.

[0125] <Step (2)> In the step (2), the deposited thermosetting inkjet ink is irradiated with actinic rays in an atmosphere having an oxygen concentration in the range of 0.1 to 10.0% by volume to provisionally cure the ink. In the step (2), the deposited ink in the step (1) is irradiated with actinic rays to provisionally cure the ink.

[0126] The actinic ray can be selected from, for example, an electron beam, an ultraviolet ray, an α ray, a γ ray, an X-ray, and the like, and is preferably an ultraviolet ray. The ultraviolet light can be irradiated at a wavelength of 395 nm using, for example, a water-cooled LED manufactured by Phoseon Technology Co., Ltd. By using an LED as the light source, it is possible to prevent poor curing of the ink caused by the ink melting due to the radiant heat of the light source.

[0127] The ultraviolet irradiation is performed such that the peak illuminance of the ultraviolet light having a wavelength in the range of 370 to 410 nm on the surface of the resist film is preferably 0.5 to 10 W / cm 2 within the range of 1 to 5 W / cm 2 From the viewpoint of suppressing the radiation heat from being irradiated to the ink, the amount of light irradiated to the resist film is set to 500 mJ / cm 2 It is preferable that it is less than 1000 .mu.m.

[0128] In this process, the deposited ink is irradiated with actinic rays in an atmosphere having an oxygen concentration in the range of 0.1 to 10.0% by volume, thereby curing the ink. From the viewpoint of enhancing the curability of the ink, it is preferable to irradiate the ink with actinic rays for 0.001 to 300 seconds after the ink has landed, and from the viewpoint of forming a higher definition image, it is more preferable to irradiate the ink with actinic rays for 0.001 to 60 seconds.

[0129] The oxygen concentration is within the range of 0.1 to 10.0% by volume. From the viewpoint of making blooming less likely to occur, the oxygen concentration is preferably within the range of 0.5 to 8.0% by volume, and more preferably within the range of 0.5 to 6.0% by volume.

[0130] <Step (3)> In the step (3), the temporarily cured thermosetting inkjet ink is heated to completely cure it. After the temporarily curing in the step (2), the ink is further heated to completely cure it.

[0131] The heating method is preferably, for example, placing the product in an oven set at a temperature within the range of 110 to 180° C. for 10 to 60 minutes.

[0132] The thermosetting inkjet ink can be used not only as an ink for forming the above-mentioned solder resist pattern, but also as an adhesive, sealant, circuit protectant, etc. for electronic components. EXAMPLES

[0133] The present invention will be specifically described below with reference to examples, but the present invention is not limited thereto. In the following examples, unless otherwise specified, the operations were performed at room temperature (25°C). Furthermore, unless otherwise specified, "%" and "parts" mean "% by mass" and "parts by mass", respectively.

[0134] [Example 1] <Preparation of Yellow Pigment Dispersion> Dispersant 1 and Dispersant 2 below and the dispersion medium were placed in a stainless steel beaker, heated on a hot plate at 65°C for 1 hour while stirring and dissolving, cooled to room temperature, and then the pigment below was added, placed in a glass bottle together with 200 g of zirconia beads with a diameter of 0.5 mm and sealed. This was dispersed in a paint shaker until the desired particle size was reached, and the zirconia beads were then removed.

[0135] Dispersant 1: EFKA7701 (BASF) 5.6 parts by mass Dispersant 2: Solsperse 22000 (manufactured by Lubrizol Japan) 0.4 parts by mass Dispersion medium: Dipropylene glycol diacrylate (containing 0.2% UV-10) 80.6 parts by mass Pigment: PY185 (BASF, Paliotol Yellow D1155) 13.4 parts by mass

[0136] <Preparation of Cyan Pigment Dispersion> The yellow pigment dispersion was prepared in the same manner as in the preparation of the yellow pigment dispersion, except that the dispersant, dispersion medium and pigment were changed as shown below.

[0137] Dispersant: EFKA7701 (BASF) 7 parts by weight Dispersion medium: Dipropylene glycol diacrylate (containing 0.2% UV-10) 70 parts by mass Pigment: PB15:4 (Dainichi Seika Chemicals, Chromofine Blue 6332JC) 23 parts by mass

[0138] <Photopolymerizable compound> As the photopolymerizable compound, the following compounds were used. A1: Tripropylene glycol diacrylate (molecular weight 300) A2: Trimethylolpropane triacrylate (molecular weight 296) A3: Neopentyl glycol diacrylate (molecular weight 212) a4: 2PO modified neopentyl glycol diacrylate (molecular weight 328)

[0139] <Thermosetting compounds> As the thermosetting compound, the following compounds were used. (Blocked isocyanate (aliphatic polyisocyanate)) b1: trixeneBI7982 (LANXESS) (molecular weight 793) b2: trixeneBI7961 (LANXESS) (molecular weight 793) b3: EA-1010N (bisphenol A type epoxy acrylate) (manufactured by Shin-Nakamura Chemical Co., Ltd.) (molecular weight 400) b4:YD-127 (manufactured by Nippon Steel & Sumikin Chemical Co., Ltd.) (molecular weight 793)

[0140] (Aliphatic Epoxides) b5: 4-Hydroxybutyl acrylate glycidyl ether (BMI-1000, manufactured by Nippon Kasei Co., Ltd.) (molecular weight 793)

[0141] (Compounds containing maleimide groups) b6: 4,4'-diphenylmethane bismaleimide (BMI-1000, manufactured by Daiwa Chemical Industry Co., Ltd.) (molecular weight 793)

[0142] <Photopolymerization initiator> As the photopolymerizable compound, the following compounds were used. (Acylphosphine initiator) c1: Omnirad TPO H (manufactured by IGM) (molecular weight 348) c2: Omnirad 819 (manufactured by IGM) (molecular weight 419) (Aminoacetophenone initiator) c3: Omnirad 907 (manufactured by IGM) (molecular weight 279) c4: Omnirad 379 (manufactured by IGM) (molecular weight 381) (Thioxanthone initiator) c5: 2-isopropylthioxanthone (ITX: molecular weight 254) c6: 2,4-diethylthioxanthone (DETX: molecular weight 268)

[0143] <Gelling agent> The gelling agents used were as follows: d1: Distearyl ketone (molecular weight 507) d2: Behenyl behenate (molecular weight 199)

[0144] <Preparation of Inkjet Ink> In addition to 3.0 g of the yellow pigment dispersion and 1.0 g of the cyan pigment dispersion, the ink compositions shown in Tables I to II below were added to prepare inkjet inks, which were then filtered through a 3 μm Teflon (registered trademark) membrane filter manufactured by ADVATEC Co., Ltd. The 80° C. viscosity and gel phase transition temperature of each ink were measured using a viscoelasticity measuring device MCR300 manufactured by Physica Co., Ltd. with a shear rate of 1000 (1 / s).

[0145] Here, the gel phase transition temperature refers to the temperature at which the complex viscosity becomes 1 Pa or more in a viscoelasticity curve obtained by changing the temperature at a cooling rate of 0.1°C / s, a strain of 5%, an angular frequency of 10 radian / s, and a cooling rate of 0.1°C / s.

[0146] The viscosity of the ink of the present invention at 25° C. is in the range of 1 to 1×10 4 In contrast, the inks in the comparative examples all had a viscosity of less than 1 Pa·s. Furthermore, the gel phase transition temperatures of the inks of the present invention were all within the range of 40 to 100° C., but the gel phase transition phenomenon was not observed in the inks of the comparative examples.

[0147] <Inkjet pattern formation> Each of the prepared inkjet inks was loaded into an inkjet recording device having an inkjet recording head equipped with a piezoelectric inkjet nozzle. Using this device, a pattern was formed on a copper-clad laminate for printed wiring boards (FR-4, thickness 1.6 mm, size 150 mm x 95 mm).

[0148] The ink supply system consists of an ink tank, ink flow path, a sub-ink tank just before the inkjet recording head, piping with a metal filter, and a piezo head. The ink is heated to 90°C from the ink tank to the head. A heater is also built into the piezo head, and the ink temperature inside the recording head is heated to 90°C. The piezo head has a nozzle diameter of 22μm, and the heads with a nozzle resolution of 360dpi are arranged in a staggered pattern to form a nozzle row of 720dpi.

[0149] Using this inkjet device, a voltage was applied so that a dot with a droplet volume of 6.0 pl was formed. A solid pattern of 20 mm × 50 mm and a comb pattern with lines and spaces of 100 μm were printed on the substrate, each with a thickness of 20 μm. Then, the pattern was illuminated with an LED lamp (395 nm, 8 W / cm) manufactured by Phoseon Technology. 2 , water cooled unit) at 500mJ / cm 2The ink layer was temporarily cured by irradiating the ink so that the ink layer was cured. The ink layer was then placed in an oven set at 150°C for 60 minutes for full curing, and a print sample was obtained.

[0150] [evaluation] <Adhesion to substrate> For the solid pattern print sample, the cured film was cut into a grid pattern according to the cross-cut method of JIS K5600, adhesive tape was attached, and the peeled state of the cured film was observed by peeling it off, and the adhesion residual rate was calculated by the following method and evaluated according to the following criteria. Here, the adhesion residual rate is calculated by using the number of squares created by cutting as the denominator and the number of squares remaining after tape peeling as the numerator. (standard) 6: Adhesion remaining rate 100% 5: Adhesion remaining rate: 90% or more but less than 100% 4: Adhesion remaining rate: 70% or more but less than 90% 3: Adhesion remaining rate: 50% to less than 70% 2: Adhesion residual rate: 25% to less than 50% 1: Residual adhesion rate less than 25%

[0151] <Surface tackiness> The solid pattern print sample was subjected to a 4 cm rub test in accordance with the method described in "JIS Standard K5701-1 6.2.3 Rub Resistance Test". 2 A piece of coated paper for printing cut to the size required was placed on the image and rubbed with a load of 500 g. The degree of decrease in image density was then visually observed and evaluated according to the following criteria. The results are shown in Table 3.

[0152] (standard) 4: Even after rubbing more than 50 times, no change in the image or coloring of the coated printing paper was observed. 3: Even after rubbing more than 50 times, no change in the image is observed, but discoloration of the printing coated paper is observed. 2: After 50 rubs, a decrease in image density is observed, but this is within the acceptable range for practical use. 1: When rubbed less than 50 times, a clear decrease in image density was observed, and the quality was not suitable for practical use.

[0153] <Pencil hardness> The pencil hardness of the surface of the solid pattern print sample was measured according to the method described in "JIS Standard K-5400." The evaluation was performed according to the following criteria. (standard) 5: Pencil hardness 6H or higher 4: Pencil hardness 5H 3: Pencil hardness 4H 2: Pencil hardness 3H 1: Pencil hardness 2H or less The results are shown in Tables I and II.

[0154] [Table 1]

[0155] [Table 2]

[0156] As shown in Tables I and II, the thermosetting inkjet ink of the present invention is superior to the inks of the comparative examples in substrate adhesion, surface hardness, and surface tackiness.

[0157] [Example 2] <Preparation of Inkjet Ink> In addition to 3.0 g of the yellow pigment dispersion and 1.0 g of the cyan pigment dispersion, the ink compositions shown in Tables III to V below were added to prepare inkjet inks, which were then filtered through a 3 μm Teflon membrane filter manufactured by ADVATEC.

[0158] <Inkjet pattern formation> Each of the prepared inkjet inks was loaded into an inkjet recording device having an inkjet recording head equipped with a piezoelectric inkjet nozzle. Using this device, a pattern was formed on a copper-clad laminate for printed wiring boards (FR-4, thickness 1.6 mm, size 150 mm x 95 mm).

[0159] The ink supply system consists of an ink tank, ink flow path, a sub-ink tank just before the inkjet recording head, piping with a metal filter, and a piezo head. The ink is heated to 90°C from the ink tank to the head. A heater is also built into the piezo head, and the ink temperature inside the recording head is heated to 90°C. The piezo head has a nozzle diameter of 22μm, and the heads with a nozzle resolution of 360dpi are arranged in a staggered pattern to form a nozzle row of 720dpi.

[0160] Using this inkjet device, a voltage was applied so that a dot with a droplet volume of 6.0 pl was formed. A solid pattern of 20 mm × 50 mm and a comb pattern with lines and spaces of 100 μm were printed on the substrate, each with a thickness of 20 μm. Then, the pattern was illuminated with an LED lamp (395 nm, 8 W / cm) manufactured by Phoseon Technology. 2 , water cooled unit) at 500mJ / cm 2 The ink layer was temporarily cured by irradiation so as to become

[0161] However, unlike Example 1, the oxygen concentration was controlled to 3.0% by volume during irradiation with the actinic rays.

[0162] The oxygen concentration was measured by placing a gas supply nozzle between the inkjet head and the light source, as shown in Figure 2 of WO 2017 / 164164, connecting a nitrogen gas generator (N2 IMPACT, manufactured by Kofloc Corporation) at a pressure of 0.5 MPa s, and flowing nitrogen (N2) gas. Thereafter, the coating was placed in an oven set at 150° C. for 60 minutes for full curing, to obtain a print sample.

[0163] The obtained print sample was evaluated in the same manner as in Example 1. The results obtained are shown in Tables III to V.

[0164] [Table 3]

[0165] [Table 4]

[0166] [Table 5]

[0167] As shown in Tables III to V, according to the printing method of the present invention, even without containing a gelling agent, the surface curing property is increased by using a printing method in which actinic rays are irradiated in an atmosphere with a low oxygen concentration to cause temporary curing, while the degree of polymerization inside is suppressed, making it possible to achieve both substrate adhesion and surface tackiness while maintaining high surface hardness, and it is clear that the ink is superior in substrate adhesion, surface hardness and surface tackiness compared to the inks of the comparative examples. [Industrial Applicability]

[0168] The thermosetting inkjet ink of the present invention can form a coating film having excellent substrate adhesion, high surface hardness, and favorable surface tackiness, and can therefore be used publicly as a solder resist for printed circuit boards.

Claims

1. A thermosetting inkjet ink containing a thermosetting compound, The composition contains a photopolymerizable compound, a thermosetting compound, a photopolymerization initiator, and a gelling agent, The photopolymerization initiator is an acylphosphine-based initiator or an aminoacetophenone-based initiator, and the content thereof is within the range of 1 to 100 mmol / kg; and A thermosetting inkjet ink characterized by undergoing a sol-gel phase transition depending on temperature.

2. 2. The thermosetting inkjet ink according to claim 1, wherein the thermosetting compound is a blocked isocyanate in which a polyisocyanate is blocked with a blocking agent.

3. 3. The thermosetting ink-jet ink of claim 2, wherein the polyisocyanate is an aliphatic polyisocyanate.

4. 4. The thermosetting inkjet ink according to claim 1, wherein the content of the photopolymerization initiator is within a range of 1 to 70 mmol / kg.

5. 5. The thermosetting inkjet ink according to claim 1, further comprising a thioxanthone-based initiator in an amount within a range of 40 to 400 mmol / kg as a photopolymerization initiator.

6. 5. The thermosetting inkjet ink according to claim 1, further comprising a thioxanthone-based initiator in an amount within the range of 100 to 400 mmol / kg as a photopolymerization initiator.

7. A printing method using a thermosetting inkjet ink, comprising the steps of: the thermosetting inkjet ink contains a photopolymerizable compound, a thermosetting compound, and a photopolymerization initiator; The photopolymerization initiator is an acylphosphine-based initiator or an aminoacetophenone-based initiator, and the content thereof is within the range of 1 to 100 mmol / kg; and A printing method comprising the following steps (1) to (3): (1) A process of ejecting a thermosetting inkjet ink from a nozzle and landing it on a recording medium. (2) A step of pre-curing the deposited thermosetting inkjet ink by irradiating it with actinic rays in an atmosphere having an oxygen concentration in the range of 0.1 to 10.0% by volume. (3) Then, the temporarily cured thermosetting inkjet ink is heated to completely cure it.

8. 8. The printing method according to claim 7, wherein the thermosetting compound is a blocked isocyanate obtained by blocking a polyisocyanate with a blocking agent.

9. 9. The printing method according to claim 8, wherein the polyisocyanate is an aliphatic polyisocyanate.

10. 10. The printing method according to claim 7, wherein the content of the photopolymerization initiator is within a range of 1 to 70 mmol / kg.

11. The printing method according to any one of claims 7 to 10, characterized in that the photopolymerization initiator further contains a thioxanthone-based initiator in an amount within a range of 40 to 400 mmol / kg.

12. The printing method according to any one of claims 7 to 10, characterized in that the photopolymerization initiator further contains a thioxanthone-based initiator in an amount within a range of 100 to 400 mmol / kg.

13. 13. The printing method according to claim 7, wherein the thermosetting ink-jet ink contains a gelling agent.

Images