Abstract

Nitrogen oxides (NO x The present invention provides a selective catalytic reduction (SCR) catalyst composition that is effective in reducing NO at any temperature, particularly at low temperatures, compared to a Cu-chabazite reference catalyst composition. x The SCR catalyst composition of the present invention significantly increases the conversion of ethane to ethane. Also provided are catalyst articles, exhaust gas treatment systems, and methods for treating exhaust gas streams, each comprising the SCR catalyst composition of the present invention. The SCR catalyst composition is particularly useful for treating exhaust from lean-burn engines. [Selected figure] Figure 2a

Description

[Technical field]

[0001] The present invention relates generally to the field of exhaust gas treatment catalysts, and more particularly to the treatment of NO in engine exhaust. x The present invention relates to catalytic compositions capable of reducing emissions, catalytic articles coated with such compositions, emission treatment systems including such catalytic articles, and methods of their use. [Background technology]

[0002] Environmental regulations regarding internal combustion engine emissions are becoming increasingly stringent around the world.

[0003] Exhaust gas from vehicles powered by lean-burn diesel engines contains unburned hydrocarbons (HC), carbon monoxide (CO), and nitrogen oxides (NO x ), and emits exhaust gas emissions containing NO x "Lean" refers to the various chemical species of nitrogen oxides, including nitric oxide and nitrogen dioxide, among others. "Lean" refers to maintaining the air-to-fuel ratio in the combustion mixture supplied to such engines higher than stoichiometric so that the resulting exhaust gases are "lean", i.e., have a relatively high oxygen content. The air-to-fuel (A / F) ratio is the mass ratio of air to fuel present in a combustion process, such as an internal combustion engine. Lean-burn diesel engine operation provides users with superior fuel economy because they operate under fuel-lean conditions with a high air / fuel ratio. The exact proportion of air to fuel that results in stoichiometric conditions varies with the relative proportions of carbon and hydrogen in the fuel. The stoichiometric A / F ratio is determined by the relative proportions of carbon dioxide (CO) in hydrocarbon fuels. 2 ) and supports complete combustion into water.

[0004] Oxidation catalysts comprising precious metals such as platinum group metals (PGMs) dispersed on a refractory metal oxide support such as alumina are known for use in treating diesel engine exhaust to convert both HC and CO gaseous pollutants by catalyzing the oxidation of these pollutants to carbon dioxide and water. Such catalysts are commonly contained in units referred to as diesel oxidation catalysts (DOCs) and are placed in the exhaust flow path from diesel power generation systems to treat the exhaust before it is released into the atmosphere. Typically, diesel oxidation catalysts are formed on a ceramic or metallic substrate upon which one or more catalytic coating compositions are deposited. In addition to converting gaseous HC and CO emissions, oxidation catalysts containing PGMs also convert NO to NO. 2 Promotes oxidation to.

[0005] The NO formed by DOC was then 2 Contains NO x The components are typically converted to NO with a suitable reducing agent in the presence of a selective catalytic reduction (SCR) catalyst. x The components must be removed from the exhaust stream by reduction. The SCR process uses catalytic reduction of nitrogen oxides with a reducing agent (e.g., ammonia) in the presence of atmospheric oxygen, resulting in the formation of primarily nitrogen and steam: 4NO+4NH 3 +O 2 →4N 2 +6H 2 O (standard SCR reaction) 2NO 2 +4NH 3 →3N 2 +6H 2 O (slow SCR response) NO+NO 2 +NH 3 →2N 2 +3H 2 O (fast SCR reaction)

[0006] Current catalysts used in SCR processes include molecular sieves such as zeolites ion-exchanged with catalytic metals such as iron or copper. Useful SCR catalyst compositions are capable of reducing NO at temperatures above 200° C. and below 600° C. x It can effectively catalyze the reduction of exhaust components, resulting in reduced NO emissions even under low load conditions, which are typically associated with lower exhaust temperatures. x You can achieve the level.

[0007] Conventional gasoline engines with electronic fuel injection and intake systems provide a constantly changing mixture, cycling rapidly and continuously between lean and rich exhaust. Recently, to improve fuel economy, gasoline fueled engines have been designed to operate under lean conditions. Lean-burn gasoline direct injection (GDI) engines offer the fuel efficiency advantage of performing fuel combustion in excess air, thereby contributing to reduced greenhouse gas emissions.

[0008] Exhaust gas from vehicles powered by lean-burn gasoline engines is typically treated with a three-way catalyst (TWC), which is effective in mitigating CO and HC pollutants in the exhaust of engines operated under lean conditions. x emissions also need to be reduced to meet emission standards, but the TWC catalyst reduces NO emissions when a gasoline engine runs lean. x They are not effective in reducing emissions. The use of certain SCR catalysts for lean-burn gasoline engines poses challenges as such catalysts are expected to exhibit thermal stability at elevated temperatures under transient lean / rich conditions.

[0009] In the art, NO from an exhaust gas stream x There is a continuing need for effective SCR catalysts to efficiently and effectively mitigate emissions. Increasingly stringent emission regulations are driving the need to develop SCR catalysts with improved capabilities to manage NOx emissions while exhibiting sufficient high temperature thermal stability, especially under lean, low engine exhaust temperature conditions. Summary of the Invention

[0010] The present disclosure provides an improved selective catalytic reduction (SCR) catalyst composition and a comparison of the composition with a standard Cu-chabazite reference SCR catalyst composition to determine NO x The SCR catalyst composition of the present invention significantly increases NO conversion at any temperature, particularly at low temperatures. x Additionally provided are methods for preparing the disclosed SCR catalyst compositions, as well as catalytic articles, exhaust treatment systems, and methods for treating exhaust streams, each comprising the disclosed SCR catalyst compositions.

[0011] Thus, in one embodiment, a method for producing nitrogen oxides (NO ) from a lean-burn engine exhaust gas in the presence of a reductant is provided. x The present invention provides a selective catalytic reduction (SCR) catalyst composition effective for catalyzing the reduction of nitrous oxide, the catalyst composition comprising a first component comprising a porous refractory metal oxide support having a platinum group metal (PGM) and a base metal oxide deposited thereon, and a second component comprising a metal promoted zeolite, wherein the weight ratio of the first component to the second component is in the range of about 0.05 to about 0.5.

[0012] In some embodiments, the porous refractory metal oxide comprises silica, alumina, ceria, zirconia, a ceria-zirconia composite, titania, or a combination thereof. In some embodiments, the porous refractory metal oxide comprises silica in an amount of about 1 wt% to about 20 wt% and alumina in an amount of about 80 wt% to about 99 wt%. In some embodiments, the porous refractory metal oxide comprises silica in an amount of about 5 wt% and alumina in an amount of about 95 wt%.

[0013] In some embodiments, the PGMs are selected from platinum, palladium, rhodium, and combinations thereof.

[0014] In some embodiments, the base metal oxide is an oxide of Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Zn, Mo, Mo, Ag, Sn, or a combination thereof, In some embodiments, the base metal oxide is CuO.

[0015] In some embodiments, the zeolite has a structure type selected from AEI, AFT, AFV, AFX, AVL, CHA, DDR, EAB, EEI, ERI, IFY, IRN, KFI, LEV, LTA, LTN, MER, MWF, NPT, PAU, RHO, RTE, RTH, SAS, SAT, SAV, SFW, TSC, UFI, and combinations thereof. In some embodiments, the zeolite has a structure type selected from the group consisting of CHA and AEI.

[0016] In some embodiments, the metal is one or more of Cu, Co, Ni, La, Mn, Fe, V, Ag, Ce, Nd, Mo, Hf, Y, or W. In some embodiments, the metal is one or more of Cu, Fe, or Ce.

[0017] In some embodiments, the base metal oxide is present in an amount of from about 0.1 to about 20 weight percent of the porous refractory metal oxide support.

[0018] In some embodiments, the PGMs are present in an amount of from about 0.01 to about 20% by weight of the porous refractory metal oxide support.

[0019] In another embodiment, the method comprises the steps of: x The present invention provides an SCR article effective for catalyzing the reduction of carbon dioxide, the SCR article including a substrate having an inlet end and an outlet end defining an overall length, and having disposed thereon an SCR catalyst composition as disclosed herein.

[0020] In some embodiments, the SCR catalyst composition includes a first washcoat comprising a mixture of (a) a first component and (b) a second component, the first washcoat disposed on at least a portion of the length of the catalytic substrate, and a second washcoat comprising the second component, the second washcoat disposed on at least a portion of the length of the catalytic substrate.

[0021] In some embodiments, the first washcoat is disposed directly on the catalytic substrate and the second washcoat is disposed on at least a portion of the first washcoat. In some embodiments, the second washcoat is disposed directly on the catalytic substrate and the first washcoat is disposed on at least a portion of the second washcoat. In some embodiments, the first washcoat is disposed directly on the catalytic substrate from the inlet end for about 10% to about 50% of the total length and the second washcoat is disposed on at least a portion of the first washcoat. In some embodiments, the first washcoat is disposed directly on the catalytic substrate from the inlet end for about 10%, about 20%, about 30%, about 40%, or about 50% of the total length and the second washcoat is disposed on at least a portion of the first washcoat.

[0022] In some embodiments, the second washcoat is disposed directly on the catalytic substrate from the inlet end for about 50% to about 100% of the total length, and the first washcoat is disposed over at least a portion of the second washcoat. In some embodiments, the second washcoat is disposed directly on the catalytic substrate from the inlet end for about 50%, about 60%, about 70%, about 80%, about 90%, or about 100% of the total length, and the first washcoat is disposed over at least a portion of the second washcoat.

[0023] In some embodiments, the first washcoat is disposed directly on the catalyst substrate from the inlet end for about 20% to about 40% of the total length, and the second washcoat extends from the inlet end to the outlet end. In some embodiments, the first washcoat is disposed directly on the catalyst substrate from the inlet end for about 20%, about 25%, about 30%, about 35%, or about 40% of the total length, and the second washcoat extends from the inlet end to the outlet end. In some embodiments, the first washcoat is disposed directly on the catalyst substrate from the inlet end for about 33% of the total length, and the second washcoat extends from the inlet end to the outlet end.

[0024] In some embodiments, the first washcoat is disposed directly on the catalytic substrate from the outlet end for about 10% to about 50% of the total length, and the second washcoat is disposed over at least a portion of the first washcoat. In some embodiments, the first washcoat is disposed directly on the catalytic substrate from the outlet end for about 10%, about 20%, about 30%, about 40%, or about 50% of the total length, and the second washcoat is disposed over at least a portion of the first washcoat.

[0025] In some embodiments, the first washcoat is disposed directly on the catalyst substrate from the outlet end for about 20% to about 40% of the total length, and the second washcoat extends from the inlet end to the outlet end. In some embodiments, the first washcoat is disposed directly on the catalyst substrate from the outlet end for about 20%, about 25%, about 30%, about 35%, or about 40% of the total length, and the second washcoat extends from the inlet end to the outlet end. In some embodiments, the first washcoat is disposed directly on the catalyst substrate from the outlet end for about 33% of the total length, and the second washcoat extends from the inlet end to the outlet end.

[0026] In some embodiments, the second washcoat is disposed directly on the catalytic substrate from the outlet end to about 50% to about 100% of the total length, and the first washcoat is disposed over at least a portion of the second washcoat.

[0027] In some embodiments, a first washcoat is placed directly on the catalytic substrate covering 100% of its length and a second washcoat is placed on the first washcoat covering 100% of its length. In some embodiments, a second washcoat is placed directly on the catalytic substrate covering 100% of its length and a first washcoat is placed on the second washcoat covering 100% of its length.

[0028] In some embodiments, the SCR article has a zoned configuration, where a first washcoat is disposed on the catalyst substrate from the inlet end for about 10% to about 50% of the total length, and a second washcoat is disposed on the catalyst substrate from the outlet end for about 50% to about 90% of the total length. In some embodiments, the SCR article has a zoned configuration, where a first washcoat is disposed on the catalyst substrate from the outlet end for about 10% to about 50% of the total length, and a second washcoat is disposed on the catalyst substrate from the inlet end for about 50% to about 90% of the total length.

[0029] In some embodiments, the weight ratio of the porous refractory metal oxide to the zeolite in the first washcoat is about 0.1 to about 10. In some embodiments, the weight ratio of the porous refractory metal oxide to the zeolite in the first washcoat is about 0.2 to about 5. In some embodiments, the weight ratio of the porous refractory metal oxide to the zeolite in the first washcoat is about 0.2, about 0.25, about 0.3, about 0.4, about 0.5, about 0.6, about 0.7, about 0.8, about 0.9, about 1, about 2, about 3, about 4, or about 5.

[0030] In some embodiments, the PGM component is Pt, the base metal oxide is copper oxide, the zeolite has a chabazite structure and is promoted with copper, the porous refractory metal oxide is alumina containing 5% silica, the Pt is present in an amount of about 2.9% by weight of the porous refractory metal oxide, and the copper oxide is present in an amount of about 10% by weight of the porous refractory metal oxide.

[0031] In some embodiments, the substrate is a honeycomb substrate. In some embodiments, the honeycomb substrate is a metal, ceramic, silicon carbide, cordierite, or aluminum titanate. In some embodiments, the honeycomb substrate is a metal or ceramic. In some embodiments, the honeycomb substrate is a flow-through substrate or a wall-flow filter (also called SCR over filter, SCRoF).

[0032] In some embodiments, NO x Effective reduction of NO is at temperatures above about 150° C. and below about 700° C. In some embodiments, NO x Effective reduction of NO is at temperatures between about 200° C. and about 600° C. In some embodiments, NO x The conversion of NO is increased by at least 10% at 200° C. as compared to a baseline catalytic article having only a copper-chabazite washcoat disposed on a substrate. In some embodiments, the NO x The conversion of is increased by at least 40% at 200° C. as compared to a baseline catalytic article having only a copper-chabazite washcoat disposed on a substrate.

[0033] In a further aspect, an exhaust gas treatment system is provided that includes a lean-burn engine generating an exhaust gas stream and an SCR article as disclosed herein. In some embodiments, the exhaust gas treatment system further includes one or more of a diesel oxidation catalyst (DOC), a soot filter, a urea injection component, an ammonia oxidation catalyst (AMOX), a low temperature NOx absorbent (LT-NA), and a lean NOx trap (LNT).

[0034] These and other features, aspects, and advantages of the present disclosure will become apparent upon reading the following detailed description in conjunction with the accompanying drawings, which are briefly described below. The present invention includes any combination of two, three, four, or more of the above-described embodiments, and any combination of two, three, four, or more features or elements described in this disclosure, regardless of whether such features or elements are explicitly combined in the description of a particular embodiment herein. It is intended that this disclosure be read as a whole such that separable features or elements of the disclosed invention should be considered combinable in any of its various aspects and embodiments, unless the context clearly indicates otherwise. Other aspects and advantages of the present invention will become apparent hereinafter. [Brief description of the drawings]

[0035] To provide an understanding of embodiments of the present invention, reference is made to the accompanying drawings. Reference numerals refer to components of exemplary embodiments of the present invention. The drawings are merely examples and should not be construed as limiting the present invention. The disclosure described herein is illustrated by way of example, and not by way of limitation, in the accompanying figures. For simplicity and clarity of the figures, the illustrated features have not necessarily been drawn to scale. For example, the dimensions of some features may be exaggerated relative to other features for clarity. Furthermore, where considered appropriate, reference labels have been repeated among the figures to indicate corresponding or similar elements. [Figure 1a] FIG. 1 is a perspective view of a wall-flow filter substrate. [Figure 1b] FIG. 2 is a cross-sectional view of a portion of a wall-flow filter substrate. [Figure 2a] FIG. 1 illustrates three possible coating configurations according to certain embodiments. [Figure 2b] FIG. 1 illustrates three possible coating configurations according to certain embodiments. [Figure 2c] FIG. 1 illustrates three possible coating configurations according to certain embodiments. [Diagram 3] 1 is a schematic diagram of an embodiment of an emissions treatment system in which the SCR catalyst article of the present invention is utilized. [Figure 4] FIG. 1 is a schematic diagram of one embodiment of a zoning design and coating sequence. [Diagram 5] FIG. 1 is a schematic diagram of one embodiment of a zoning design and coating sequence. [Figure 6] 1 is a graphical representation of NOx conversion and N2O formation results as a function of temperature for fresh and aged SCR catalyst articles, in accordance with certain embodiments. [Figure 7a] 1 is a graphical representation of NOx conversion results at 200° C. for a fresh SCR catalyst article, according to certain embodiments. [Figure 7b] 1 is a graphical representation of NOx conversion results at 200° C. for a fresh SCR catalyst article, according to certain embodiments. [Figure 8a] 1 is a graphical representation of NOx conversion results at 500° C. for a fresh SCR catalyst article, in accordance with certain embodiments. [Figure 8b] 1 is a graphical representation of NOx conversion results at 500° C. for a fresh SCR catalyst article, in accordance with certain embodiments. [Figure 9a] 1 is a graphical representation of peak N2O formation results at 200-300° C. for a fresh SCR catalyst article, according to certain embodiments. [Figure 9b] 1 is a graphical representation of peak N2O formation results at 200-300° C. for a fresh SCR catalyst article, according to certain embodiments. [Figure 10a] 1 is a graphical representation of NOx conversion results at 200° C. for an aged SCR catalyst article, according to certain embodiments. [Figure 10b] 1 is a graphical representation of NOx conversion results at 200° C. for an aged SCR catalyst article, according to certain embodiments. [Figure 11a] 1 is a graphical representation of NOx conversion results at 500° C. for an aged SCR catalyst article, according to certain embodiments. [Figure 11b] 1 is a graphical representation of NOx conversion results at 500° C. for an aged SCR catalyst article, according to certain embodiments. [Figure 12a] 1 is a graphical representation of peak N2O formation results at 200-300° C. for an aged SCR catalyst article, according to certain embodiments. [Figure 12b] 1 is a graphical representation of peak N2O formation results at 200-300° C. for an aged SCR catalyst article, according to certain embodiments. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0036] The present disclosure provides a method for reducing NO x The present invention provides an advanced selective catalytic reduction (SCR) catalyst composition and article that significantly increases the conversion of NO 3 at any temperature, particularly at low temperatures. x Additionally provided are methods for preparing the disclosed SCR catalyst compositions, as well as catalytic articles, exhaust treatment systems, and methods for treating exhaust streams, each comprising the disclosed SCR catalyst compositions.

[0037] Before describing some exemplary embodiments of the invention, it is to be understood that the invention is not limited to the details of construction or process steps set forth in the following description as the invention is capable of other embodiments and of being practiced or carried out in various ways.

[0038] definition The articles "a" and "an" herein refer to one or more than one (e.g., at least one) of the grammatical object. All ranges cited herein are inclusive. The term "about" used throughout is used to express and account for small variations. For example, "about" may mean that a numerical value may vary by ±5%, ±4%, ±3%, ±2%, ±1%, ±0.5%, ±0.4%, ±0.3%, ±0.2%, ±0.1%, or ±0.05%. All numerical values ​​are modified by the term "about", whether or not expressly stated. A numerical value modified by the term "about" includes the specific identified value. For example, "about 5.0" includes 5.0. The recitation of ranges of values ​​herein is intended only to serve as a shorthand method of individually referring to each individual value falling within the range, unless otherwise indicated herein, and each individual value is incorporated herein as if it were individually recited herein.

[0039] The term "catalyst" refers to a material that promotes a chemical reaction. A catalyst includes a "catalytically active species" and a "support" that carries or supports the active species. For example, zeolite particles can be a support for base metal catalytic species.

[0040] Catalytically active species are also called "promoters" because they accelerate a chemical reaction.

[0041] As used herein, the term "promoted" refers to a component that is intentionally added, for example, to the molecular sieve material, as opposed to an inherent impurity in the molecular sieve. The molecular sieve may be promoted, for example, with copper (Cu) and / or iron (Fe), although other catalytic metals such as manganese, cobalt, nickel, cerium, platinum, palladium, rhodium, or combinations thereof, may be used.

[0042] As used herein, "impregnated" or "impregnation" refers to the infiltration of the porous structure of the support material with a catalytic material.

[0043] As used herein, the term "support" or "support material" refers to any high surface area material, usually a metal oxide material, onto which a catalytic precious metal is applied. The term "on a support" means "dispersed on," "incorporated in," "impregnated in," "impregnated on," "implanted on," "deposited on," or otherwise associated.

[0044] The terms "catalytic article" or "catalyst article" refer to a component used to promote a desired reaction. The catalytic article includes a "substrate" having at least one catalytic coating disposed thereon.

[0045] In general, the term "effective" means, for example, from about 35% to 100% effective, e.g., from about 40%, about 45%, about 50% or about 55%, to about 60%, about 65%, about 70%, about 75%, about 80%, about 85%, about 90% or about 95% on a weight or molar basis with respect to a defined catalytic activity or storage / release activity.

[0046] The term "exhaust stream" or "exhaust gas stream" refers to any combination of flowing gases that may contain solid or liquid particulate matter. The stream is, for example, the exhaust of a lean-burn engine, which includes gaseous components and may contain certain non-gaseous components such as liquid droplets, solid particles, etc. The exhaust gas stream of a combustion engine generally contains products of combustion (CO 2 and H 2 O), products of incomplete combustion (carbon monoxide (CO) and hydrocarbons (HC), oxides of nitrogen (NO x ), combustible and / or carbonaceous particulate matter (soot), and unreacted oxygen and nitrogen.

[0047] As used herein, the terms "upstream" and "downstream" refer to relative directions relative to the flow of engine exhaust gas stream from the engine toward the tailpipe, with the engine being at the upstream location and the tailpipe and any pollution reduction articles, such as filters and catalysts, being downstream of the engine. The inlet end of the substrate is synonymous with the "upstream" end or the "front" end. The outlet end is synonymous with the "downstream" end or the "rear" end. The upstream zone is upstream of the downstream zone. The upstream zone may be closer to the engine or manifold and the downstream zone may be further away from the engine or manifold.

[0048] The term "in fluid communication" is used to refer to articles that are located on the same exhaust line, i.e., a common exhaust flow passes through articles that are in fluid communication with each other. Articles in fluid communication may be adjacent to each other in the exhaust line. Alternatively, articles in fluid communication may be separated by one or more articles, also referred to as "washcoated monoliths."

[0049] "Platinum group metal (PGM)" refers to any PGM (Ru, Rh, Os, Ir, Pd, Pt, and / or Au). Reference to a PGM allows for the presence of the PGM in any valence state. For example, a PGM may be in a metallic form with a zero valence, or the PGM may be in an oxide form. Terms such as "platinum (Pt) component," "rhodium (Rh) component," "palladium (Pd) component," "iridium (Ir) component," "ruthenium (Ru) component," and the like refer to the respective platinum group metal compounds, complexes, and the like, which decompose or otherwise convert to a catalytically active form, typically a metal or metal oxide, upon calcination or use of the catalyst.

[0050] As used herein, "base metal oxide" refers to NO x or is catalytically active for the reduction of NO xThe term "base metal oxide" refers to an oxide compound containing a transition metal or lanthanide (e.g., vanadium (V), tungsten (W), titanium (Ti), copper (Cu), iron (Fe), cobalt (Co), nickel (Ni), chromium (Cr), manganese (Mn), cerium (Ce), lanthanum (La), praseodymium (Pr), zinc (Zn), niobium (Nb), zirconium (Zr), molybdenum (Mo), tin (Sn), silver (Ag), gold (Au), or a combination thereof, that promotes another catalytic component to be more active for the reduction of base metal. Base metal oxides include, among others, Base metal oxides include oxides of copper, silver, iron, manganese, tin, cobalt, nickel, and combinations thereof. For ease of reference herein, the concentrations of base metal materials or base metal oxide materials are reported in terms of elemental metal concentration rather than oxide form. The total concentration of base metals in the base metal oxide component (e.g., copper, manganese, nickel, cobalt, iron, and combinations thereof) can vary, but will typically be about 1% to about 50% by weight based on the weight of the porous support, e.g., the refractory oxide support material (e.g., about 1% to about 50% by weight based on the refractory oxide support).

[0051] "Support" in the context of a catalytic material or catalytic washcoat refers to a material that receives metals (e.g., PGMs) by precipitation, association, dispersion, impregnation, or other suitable methods. Exemplary supports include porous refractory metal oxide supports as described herein below.

[0052] The term "high surface area refractory metal oxide support" specifically refers to support particles having pores greater than 20 Å and a broad pore distribution. High surface area refractory metal oxide supports, such as alumina support materials also referred to as "gamma alumina" or "activated alumina", typically have a surface area of ​​60 square meters per gram ("m 2 / g), often exceeding about 200m 2 / g of fresh material. Such activated aluminas are typically mixtures of gamma and delta phases of alumina, but may also contain significant amounts of eta, kappa, and theta alumina phases.

[0053] As used herein, the term "BET surface area" refers to 2 The pore size and pore volume have their usual meaning as for the Brunauer, Emmett, Teller method for determining surface area by adsorption. 2 This can be determined using adsorption or desorption experiments.

[0054] As used herein, the term "molecular sieve", such as zeolites and other zeolitic framework materials (e.g., isomorphously substituted materials), refers to materials in particulate form that can support catalytic metal components. Molecular sieves are materials based on an extensive three-dimensional network of oxygen ions that generally contain tetrahedral sites and have a substantially uniform pore distribution with pore sizes of 20 angstroms (Å) or less.

[0055] Molecular sieves may be zeolitic (zeolite) or non-zeolitic. Both zeolitic and non-zeolitic molecular sieves may have the chabazite crystal structure, also referred to as the CHA structure by the International Zeolite Society. Zeolitic chabazite has the approximate formula Ca 6 [Al 12 S 24 O 72 ]. 40 H 2O (i.e., hydrated calcium aluminum silicate). Three synthetic forms of zeolite chabazite are described in "Zeolite Molecular Sieves," by DW Breck, published in 1973 by John Wiley & Sons, which is incorporated herein by reference. The three synthetic forms reported by Breck are zeolite KG, described in J. Chem. Soc., p. 2822 (1956), Barrer et. Al., zeolite D, described in British Patent No. 868,846 (1961), and zeolite R, described in U.S. Pat. No. 3,030,181. The synthesis of SSZ-13, another synthetic form of zeolite chabazite, is described in U.S. Pat. No. 4,544,538. The synthesis of silicoaluminophosphate 34 (SAPO-34), a synthetic form of a non-zeolitic molecular sieve having the chabazite crystal structure, is described in U.S. Patent Nos. 4,440,871 and 7,264,789. A method for making yet another synthetic non-zeolitic molecular sieve having the chabazite structure, SAPO-44, is described, for example, in U.S. Patent No. 6,162,415.

[0056] Molecular sieves include small pore, medium pore, and large pore molecular sieves or combinations thereof. The pore size is defined by the ring size. Small pore molecular sieves contain channels defined by up to eight tetrahedral atoms. Medium pore molecular sieves contain channels defined by 10-membered rings. Large pore molecular sieves contain channels defined by 12-membered rings. As used herein, the term "small pore" refers to pore openings smaller than about 5 Å (angstroms), for example, on the order of about 3.8 Å.

[0057] Exemplary small pore molecular sieves include framework types ACO, AEI, AEN, AFN, AFT, AFX, ANA, APC, APD, ATT, CDO, CHA, DDR, DFT, EAB, EDI, EPI, ERI, GIS, GOO, IHW, ITE, ITW, LEV, KFI, MER, MON, NSI, OWE, PAU, PHI, RHO, RTH, SAT, SAV, SIV, THO, TSC, UEI, UFI, VNI, YUG, ZON, and mixtures or intergrowths thereof.

[0058] The phrase "eight-ring" zeolite refers to molecular sieves with eight-ring pore openings and double six-ring secondary structural units, and with a cage-like structure resulting from the connection of the double six-ring building units by four rings. Synthetic eight-ring small pore molecular sieves (e.g., with CHA structure) can be prepared by mixing a silica source, an alumina source, and a structure directing agent under alkaline aqueous conditions. Typical silica sources include various types of fumed silica, precipitated silica, and colloidal silica, as well as silicon alkoxides. Typical alumina sources include boehmite, pseudoboehmite, aluminum salts such as aluminum sulfite or sodium aluminate, and aluminum alkoxides. Sodium hydroxide is typically added to the reaction mixture. A typical structure directing agent for this synthesis is adamantyltrimethylammonium hydroxide, although other amines and / or quaternary ammonium salts may be substituted or added. The reaction mixture is heated in a pressure vessel with stirring to obtain a crystalline product. Typical reaction temperatures range from about 100°C to about 200°C, for example, from about 135°C to about 170°C. Typical reaction times are between 1 hour and 30 days, and in some embodiments, from 10 hours to 3 days. At the end of the reaction, the pH is optionally adjusted to 6-10, for example, 7-7.5, and the product is filtered and washed with water. Any acid, such as nitric acid, can be used to adjust the pH. Optionally, the product can be centrifuged. Organic additives can be used to aid in handling and isolation of the solid product. Spray drying is an optional step in the processing of the product. The solid product is heat treated in air or nitrogen. Alternatively, each gas treatment can be applied in various orders or a mixture of gases can be applied. Typical calcination temperatures are from about 400°C to about 850°C. Molecular sieves having the CHA structure can be prepared according to the methods disclosed, for example, in U.S. Pat. Nos. 4,544,538 and 6,709,644.

[0059] Exemplary medium pore molecular sieves include framework types AEL, AFO, AHT, BOF, BOZ, CGF, CGS, CHI, DAC, EUO, FER, HEU, IMF, ITH, ITR, JRY, JSR, JST, LAU, LOV, MEL, MFI, MFS, MRE, MTT, MVY, MWW, NAB, NAT, NES, OBW, PAR, PCR, PON, PUN, RRO, RSN, SFF, SFG, STF, STI, STT, STW, SVR, SZR, TER, TON, TUN, UOS, VSV, WEI, WEN, and mixtures or intergrowths thereof.

[0060] Exemplary large pore molecular sieves include skeletal types AFI, AFR, AFS, AFY, ASV, ATO, ATS, BEA, BEC, BOG, BPH, BSV, CAN, CON, CZP, DFO, EMT, EON, EZT, FAU, GME, GON, IFR, ISV, ITG, IWR, IWS, IWV, IWW, JSR, LTF, LTL, MAZ, MEI, MOR, MOZ, MSE, MTW, NPO, OFF, OKO, OSI, RON, RWY, SAF, SAO, SBE, SBS, SBT, SEW, SFE, SFO, SFS, SFV, SOF, SOS, STO, SSF, SSY, USI, UWY, VET, and mixtures or intergrowths thereof.

[0061] As used herein, the term "zeolite" refers to a specific example of a molecular sieve that further contains silicon and aluminum atoms. Generally, zeolites are a type of molecular sieve that is composed of corner-sharing TO 4 It is defined as an aluminosilicate with an open three-dimensional framework structure composed of tetrahedra, where T is Al or Si, or optionally P. The anionic framework charge-balancing cations are loosely associated with the framework oxygens, and the remaining pore volume is filled with water molecules. Non-framework cations are generally exchangeable and water molecules are removable.

[0062] Aluminosilicate zeolite structures do not contain phosphorus or other metals isomorphously substituted in the framework. That is, "aluminosilicate zeolites" excludes aluminophosphate materials such as SAPO, AlPO, and MeA1PO materials, while the broader term "zeolite" includes aluminosilicates and aluminophosphates. For purposes of this disclosure, SAPO, A1PO, and MeA1PO materials are considered non-zeolitic molecular sieves.

[0063] Zeolites are mainly composed of (SiO 4 ) / AlO 4 They can be distinguished according to the shape of the pores formed by a robust network of tetrahedra. The entrances to the pores are formed from 6, 8, 10, or 12 ring atoms for the atoms forming the entrance opening. Zeolites are crystalline materials with fairly uniform pore sizes, ranging from about 3 to 10 angstroms in diameter, depending on the type of zeolite and the type and amount of cations contained in the zeolite lattice.

[0064] Zeolites are made up of SiO molecules that are linked together by common oxygen atoms to form a three-dimensional network. 4 / AlO 4 The silica to alumina ("SAR") molar ratio of the zeolite can vary over a wide range, but is generally greater than or equal to 2. For example, the zeolite can have a SAR of from about 5 to about 1000.

[0065] As used herein, the term "substrate" refers to a monolithic material onto which the catalyst composition, i.e., catalytic coating, is disposed, typically in the form of a washcoat. In one or more embodiments, the substrate is a flow-through monolith and a monolithic wall-flow filter. The washcoat is formed by preparing a slurry containing a particular solids content (e.g., 30% to 90% by weight) of catalyst in a liquid, which is then coated onto the substrate and dried to provide a washcoat layer.

[0066] Reference to a "monolithic substrate" means a single structure that is homogeneous and continuous from the inlet to the outlet.

[0067] "Washcoat" has its usual meaning in the art of a thin, adherent coating of material (e.g., catalyst) applied to a "substrate", e.g., a honeycomb flow-through monolith substrate or a filter substrate that is sufficiently porous to allow the passage of the gas stream to be treated. As used herein and as described in Heck, Ronald and Farrauto, Robert, Catalytic Air Pollution Control, New York: Wiley-Interscience, 2002, pp. 18-19, a washcoat layer comprises a compositionally distinct layer of material disposed on the surface of a monolithic substrate or an underlying washcoat layer. A substrate can comprise one or more washcoat layers, each of which may differ in some respect (e.g., its physical properties, such as particle size or crystal phase, may differ) and / or may have different chemical catalytic functions.

[0068] The terms "on" and "over" with respect to coating layers may be used synonymously. The term "directly on" means in direct contact. The disclosed articles, in certain embodiments, are referred to as including one coating layer "on" a second coating layer, and such language is intended to encompass embodiments having intervening layers, where direct contact between the coating layers is not required (i.e., "on" is not equivalent to "directly on").

[0069] "NO x " The term NO or NO 2 This refers to nitrogen oxide compounds such as:

[0070] "Selective catalytic reduction" (SCR) is the catalytic reduction of nitrogen oxides using a reducing agent in the presence of a suitable amount of oxygen to form primarily nitrogen and water vapor (steam). The reducing agent can be, for example, a hydrocarbon, hydrogen, and / or ammonia. The SCR reaction in the presence of ammonia occurs according to the following three reactions (Equations 1-3): 4NO+4NH 3 +O 2 → 4N 2 +6H 2 O (Formula 1) NO+NO 2 +2NH 3 → 2N 2 +3H 2 O (formula 2) 6NO 2 +8NH 3 → 7N 2 +12H 2 O (formula 3)

[0071] "TWC" refers to the function of three-way conversion, where hydrocarbons, carbon monoxide, and nitrogen oxides are converted substantially simultaneously. Gasoline engines typically operate under near-stoichiometric reaction conditions that oscillate or slightly perturb between fuel-rich and fuel-lean air-fuel (A / F) ratios (·=1±~0.01). The use of "stoichiometric" herein refers to gasoline engine conditions, including oscillations or perturbations of near-stoichiometric A / F ratios. TWC catalysts contain an oxygen storage component (OSC), such as ceria or ceria-zirconia (see below), that has multiple valence states capable of retaining and releasing oxygen under a variety of air-fuel ratios. NO x Under rich conditions, when CO and HC are reduced, the OSC provides a small amount of oxygen to consume unreacted CO and HC. Similarly, under lean conditions, when CO and HC are oxidized, the OSC provides excess oxygen and / or NO x As a result, HC, CO, and NO are produced even in the presence of an atmosphere that oscillates between fuel-rich and fuel-lean air-fuel ratios. xThe conversions are all simultaneous (or essentially simultaneous). Typically, the TWC catalyst comprises one or more platinum group metals, e.g., palladium and / or rhodium, optionally platinum; an oxygen storage component; and optionally a promoter and / or stabilizer. Under rich conditions, the TWC catalyst can produce ammonia.

[0072] "OSC" refers to an element that has a multivalent oxidation state and is capable of reacting with oxygen (O 2 ) or NO x or can react vigorously with oxidizing agents such as CO, HC, or hydrogen (H 2 The term "oxygen storage component" refers to an oxygen storage component, which is an entity that reacts with a reducing agent such as lanthanum, yttrium, zirconium, etc. Examples of suitable oxygen storage components include ceria and praseodymia. Delivery of the OSC to the washcoat layer can be achieved, for example, by using mixed oxides. For example, ceria can be delivered as a mixed oxide of cerium and zirconium, and / or a mixed oxide of cerium, zirconium, and neodymium. For example, praseodymia can be delivered as a mixed oxide of praseodymium and zirconium, and / or a mixed oxide of praseodymium, cerium, lanthanum, yttrium, zirconium, and neodymium.

[0073] "DOC" refers to a diesel oxidation catalyst that converts hydrocarbons and carbon monoxide in the exhaust gas of a diesel engine. Typically, a DOC includes one or more platinum group metals, such as palladium and / or platinum; a support material, such as alumina; a zeolite for HC storage; and optionally a promoter and / or stabilizer.

[0074] "LNT" is a platinum group metal, ceria, and NO under lean conditions. x and a catalyst containing an alkaline earth trap material suitable for absorbing lean NO. x Under rich conditions, NO x is released and reduced to nitrogen.

[0075] "CSF" refers to a catalyzed soot filter that is a wall-flow monolith. Wall-flow filters consist of alternating inlet and outlet channels, where the inlet channels are plugged at the outlet end and the outlet channels are plugged at the inlet end. The soot-carrying exhaust gas stream that enters the inlet channels is forced through the filter wall before exiting the outlet channels. In addition to soot filtering and regeneration, CSFs also filter CO and HC to CO 2 and H 2 Oxidize NO to NO 2 to promote downstream SCR catalysis or to promote oxidation of soot particles at lower temperatures. When located after the LNT catalyst, the CSF 2 S oxidation function and H during LNT desulfurization process 2 S emissions can be suppressed.

[0076] "SCRoF" refers to an SCR catalyst composition coated directly onto a wall-flow filter.

[0077] "GDI" refers to a gasoline direct injection gasoline engine operating under lean-burn conditions.

[0078] "AMO x " refers to a selective ammonia oxidation catalyst, which is a catalyst containing one or more metals (typically, but not limited to, Pt) and a SCR catalyst suitable for converting ammonia to nitrogen.

[0079] All parts and percentages are by weight unless otherwise stated. Weight percent (wt %) is based on the total composition, excluding volatile materials, i.e., dry solids, unless otherwise stated.

[0080] All methods described herein can be performed in any suitable order unless otherwise indicated herein or clearly contradicted by context. The use of any and all examples or exemplary language (e.g., "etc.") provided herein is intended only to better describe the materials and methods and does not limit the scope unless otherwise claimed. No language in the specification should be construed as indicating any non-claimed element as essential to the practice of the disclosed materials and methods.

[0081] All U.S. patent applications, published patent applications, and patents referenced herein are hereby incorporated by reference.

[0082] I. Catalyst composition The present disclosure relates to a method for reducing NO from lean-burn engine exhaust gas in the presence of a reductant. x A selective catalytic reduction (SCR) catalyst composition effective for catalyzing the reduction of nitrous oxide, the catalyst composition comprising a first component comprising a porous refractory metal oxide support having a platinum group metal (PGM) and a base metal oxide deposited thereon, and a second component comprising a metal promoted zeolite, the first component and the second component having a weight ratio of the first component to the second component ranging from about 0.05 to about 0.5. In some embodiments, the weight ratio is from about 0.05, about 0.06, about 0.07, about 0.08, about 0.09, or about 0.1 to about 0.2, about 0.3, about 0.4, or about 0.5.

[0083] The porous refractory metal oxide support materials on which the catalytically active PGM and base metal oxides are deposited exhibit chemical and physical stability at elevated temperatures, such as those associated with gasoline or diesel engine exhaust. Exemplary porous refractory metal oxides include alumina, silica, zirconia, titania, ceria, praseodymia, tin oxide, and the like, as well as physical mixtures or chemical combinations thereof, e.g., atomically doped combinations, e.g., high surface area or activated compounds, e.g., activated alumina.

[0084] Porous refractory metal oxides that may be suitable for use in supporting the PGM components and base metal oxides include alumina, titania, zirconia; a mixture of alumina with one or more of titania, zirconia, and ceria; ceria coated on alumina; or titania coated on alumina. The porous refractory metal oxides may include oxides or mixed oxides, such as silica-alumina, aluminosilicates that may be amorphous or crystalline, alumina-zirconia, alumina-chromia, alumina-ceria, etc. The porous refractory metal oxides are in particular gamma alumina, silica-alumina, ceria coated on alumina, titania coated on alumina, or zirconia coated on alumina. Metal oxide combinations include silica-alumina, ceria-zirconia, praseodymia-ceria, alumina-zirconia, alumina-ceria-zirconia, lanthana-alumina, lanthana-zirconia-alumina, baria-alumina, baria-lanthana-alumina, baria-lanthana-neodymia-alumina, and alumina-ceria. Exemplary aluminas include large pore boehmite, gamma-alumina, and delta / theta alumina. Useful commercially available aluminas used as starting materials in the exemplary process include activated aluminas, such as high bulk density gamma-alumina, low or medium bulk density large pore gamma-alumina, and low bulk density large pore boehmite and gamma-alumina. In some embodiments, the porous refractory metal oxide comprises silica, alumina, ceria, zirconia, ceria-zirconia composite, titania, or combinations thereof.

[0085] The SCR catalyst composition can include any of the porous refractory metal oxides described above in any amount. For example, the porous refractory metal oxide in the SCR catalyst composition can be from about 1 wt%, about 5 wt%, about 10 wt%, about 15 wt%, about 20 wt%, about 25 wt%, about 30 wt%, or about 35 wt%, to about 50 wt%, about 55 wt%, about 60 wt%, about 65 wt%, or about 70 wt%, based on the total dry weight of the catalyst composition. The porous refractory metal oxide can include, for example, about 10 to about 99 wt% alumina, about 15 to about 95 wt% alumina, or about 20 to about 85 wt% alumina. In some embodiments, the porous refractory metal oxide includes silica in an amount of about 1 wt% to about 20 wt%, and alumina in an amount of about 80 wt% to about 99 wt%.

[0086] In some embodiments, the PGM is selected from platinum, palladium, rhodium, and combinations thereof. The PGM can be dispersed on the porous refractory metal oxide support, for example, by dispersing a soluble precursor thereon (e.g., palladium nitrate). Alternatively, the PGM is provided in the composition in particulate form, such as fine particles on the order of 1 to 15 nanometers or less in diameter, as opposed to being dispersed on the support. The amount of PGM deposited on the porous refractory metal oxide support can vary. In some embodiments, the PGM is present in an amount of about 0.01 to about 20% by weight of the porous refractory metal oxide support. In some embodiments, the PGMs are present at about 0.01, about 0.02, about 0.03, about 0.04, about 0.05, about 0.06, about 0.07, about 0.08, about 0.09, or about 0.1, to about 0.5, about 1.0, or about 2.0, about 5.0, about 10.0, or about 20 wt.% of the porous refractory metal oxide support.

[0087] In some embodiments, the base metal oxide is an oxide of Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Zn, Mo, Mo, Ag, Sn, or a combination thereof. In a particular embodiment, the base metal oxide is CuO. The amount of base metal oxide deposited on the porous refractory metal oxide support can vary. In some embodiments, the base metal oxide is present in an amount of about 0.1 to about 20% by weight of the porous refractory metal oxide support. In some embodiments, the base metal oxide is present in an amount of about 0.1, about 0.2, about 0.3, about 0.4, about 0.5, about 0.6, about 0.7, about 0.8, about 0.9, or about 1 to about 2, about 5, about 10, or about 20% by weight of the porous refractory metal oxide support.

[0088] The structure type of the metal promoted zeolite can be varied. In some embodiments, the zeolite has a structure type selected from AEI, AFT, AFV, AFX, AVL, CHA, DDR, EAB, EEI, ERI, IFY, IRN, KFI, LEV, LTA, LTN, MER, MWF, NPT, PAU, RHO, RTE, RTH, SAS, SAT, SAV, SFW, TSC, UFI, and combinations thereof. In some embodiments, the zeolite has a structure type selected from the group consisting of CHA and AEI.

[0089] Zeolite-promoting metals are generally base metals (e.g., transition metals or lanthanides). In some embodiments, the zeolite-promoting metal is one or more of Cu, Co, Ni, La, Mn, Fe, V, Ag, Ce, Nd, Mo, Hf, Y, or W. In particular embodiments, the zeolite-promoting metal is one or more of Cu, Fe, or Ce. In particular embodiments, the zeolite-promoting metal is Cu. Reference to "metal" in this context contemplates the presence of the metal in any valence state. For example, the zeolite-promoting metal may be in a metallic form with a valence of zero, or the metal may be in an oxide form. Generally, the zeolite-promoting metal will be present in an oxide form.

[0090] The catalyst composition may be prepared by mixing a binder, such as ZrO, which is derived from a suitable precursor, such as zirconyl acetate or any other suitable zirconium precursor, such as zirconyl nitrate. 2 The binder may be prepared using a binder such as a zirconyl acetate binder. Zirconyl acetate binders provide coatings that remain uniform and intact after heat aging, for example, when the catalyst is exposed to high temperatures of at least about 600°C, e.g., about 800°C or higher and high water vapor environments of about 5% or higher. Other potentially suitable binders include, but are not limited to, alumina and silica. Alumina binders include aluminum oxide, aluminum hydroxide, and aluminum oxyhydroxide. Colloidal forms of aluminum salts and alumina may also be used. Silica binders include SiO such as silicates and colloidal silica. 2 The binder composition may include any combination of zirconia, alumina, and silica.

[0091] Other exemplary binders include bohemite, gamma-alumina, or delta / theta alumina, as well as silica sol. Binders, when present, are generally used in an amount of about 1-5 wt.% total washcoat loading. Alternatively, the binder can be zirconia- or silica-based, e.g., zirconium acetate, zirconia sol, or silica sol. When present, alumina binders are typically used in an amount of about 0.05 g / in 3 ~Approx. 1g / in 3 is used in amounts of

[0092] Methods for Making SCR Compositions In accordance with the present disclosure, the SCR catalyst composition is generally prepared by providing a first component comprising a porous refractory metal oxide support having a platinum group metal (PGM) and a base metal oxide deposited thereon, and by providing a second component comprising a metal promoted zeolite, wherein the weight ratio of the first component to the second component is within the range of about 0.05 to about 0.5.

[0093] To prepare metal-promoted zeolites according to various embodiments of the present invention, metals (e.g., copper, iron, cerium, etc.) are ion-exchanged into the zeolite. Such metals are generally alkali metals or NH 4 Ion-exchanged into zeolites (e.g., NH by methods known in the art, as disclosed in Bleken, F. et al. Topics in Catalysis 2009, 52, 218-228, which is incorporated herein by reference). 4 (Can be prepared by ion exchange).

[0094] The preparation of metal-promoted zeolites typically involves an ion exchange process between a particulate form of the zeolite and a metal precursor solution. For example, a copper salt may be used to provide the copper. When copper acetate is used to provide the copper, the copper concentration of the liquid copper solution used in the copper ion exchange is in a range of about 0.01 to about 0.4 molar, more specifically in a range of about 0.05 to about 0.3, even more specifically in a range of about 0.1 to about 0.25 molar, even more specifically in a range of about 0.125 to about 0.25 molar, even more specifically in a range of about 0.15 to about 0.225 molar, even more specifically in a range of from 0.2 to 0.5 molar. In certain embodiments, the metal, such as copper, is selected from the group consisting of an alkali metal or NH 4 -chabazite to form Cu-chabazite. Additionally, metal ions can be introduced by using solid metal oxides as metal precursors and by introducing protons or NH of zeolite as zeolite precursors in a gas stream or slurry environment. 4 By using the form, it may be exchanged into zeolites. In this case, high temperatures may be required to facilitate the exchange process. In the case of solid-state exchange, a certain moisture level in the gas stream may also be beneficial.

[0095] To further promote SCR of nitrogen oxides, in some embodiments, the zeolite can be promoted with more than one metal (e.g., copper in combination with one or more other metals). When more than one metal is included in the metal-promoted zeolitic material, multiple metal precursors (e.g., copper and iron precursors) can be ion-exchanged simultaneously or separately. In certain embodiments, a second metal can be exchanged into a zeolitic material first promoted with a first metal (e.g., a second metal can be exchanged into a zeolitic material promoted with copper).

[0096] II. Catalytic articles In another embodiment, the method comprises the steps of: x The present invention provides an SCR article effective for catalyzing the reduction of carbon dioxide, the SCR article including a substrate having an inlet end and an outlet end defining an overall length, and having disposed thereon an SCR catalyst composition as disclosed herein.

[0097] Base material In one or more embodiments, the catalytic composition is disposed on a substrate to form a catalytic article. Catalytic articles including the substrate are typically used as part of an exhaust gas treatment system (including, but not limited to, catalytic articles including the SCR compositions disclosed herein). Useful substrates are three-dimensional, having a length, diameter, and volume similar to a cylinder. The shape does not necessarily have to be the same as a cylinder. The length is the axial length defined by the inlet and outlet ends.

[0098] According to one or more embodiments, the substrate for the disclosed composition(s) can be composed of any material typically used to prepare automotive catalysts, and will typically include a metal or ceramic honeycomb structure. The substrate typically provides a plurality of walls to which the washcoat composition is applied and adhered, thereby acting as a support for the catalyst composition.

[0099] The ceramic substrate may be made from any suitable heat-resistant material, such as cordierite, cordierite-α-alumina, aluminum titanate, silicon titanate, silicon carbide, silicon nitride, zircon-mullite, spodumene, alumina-silica-magnesia, zircon silicate, sillimanite, magnesium silicate, zircon, petalite, α-alumina, aluminosilicates, and the like.

[0100] The substrate may also be metallic and include one or more metals or metal alloys. Metallic substrates may include any metallic substrate, such as those with openings or "punches out" in the channel walls. Metallic substrates may be used in a variety of shapes, such as pellets, compressed metallic fibers, corrugated sheets, or monolith forms. Particular examples of metallic substrates include heat-resistant base metal alloys, particularly alloys in which iron is a substantial or major component. Such alloys may contain one or more of nickel, chromium, and aluminum, the sum of which may advantageously include at least about 15% by weight (weight percent) of the alloy, in each case based on the weight of the substrate, for example, about 10-25% by weight chromium, about 1-8% by weight aluminum, and 0-about 20% by weight nickel. Examples of metallic substrates include those with straight channels, those with protruding blades along the axial channels to disrupt gas flow and open gas flow communication between the channels, and those with blades as well as holes to enhance gas transport between the channels and allow radial gas transport throughout the monolith.

[0101] Any suitable substrate for the catalytic article disclosed herein may be used, such as a monolithic substrate of the type having fine, parallel gas flow passages extending from the inlet or outlet face of the substrate through which the passages are open for fluid to flow (flow-through substrate). Another suitable substrate is of the type having a plurality of fine, substantially parallel gas flow passages extending along the longitudinal axis of the substrate, typically with each passage blocked at one end of the substrate body and alternating passages blocked at the opposite end face ("wall-flow filter"). Flow-through and wall-flow substrates are also taught, for example, in International Publication No. WO2016 / 070090, which is incorporated herein by reference in its entirety.

[0102] In some embodiments, the catalytic substrate comprises a honeycomb substrate in the form of a wall-flow filter or a flow-through substrate. In some embodiments, the substrate is a wall-flow filter. In some embodiments, the substrate is a flow-through substrate. Flow-through substrates and wall-flow filters will be discussed further below.

[0103] Flow-Through Substrate In some embodiments, the substrate is a flow-through substrate (e.g., a monolithic substrate, including a flow-through honeycomb monolithic substrate). A flow-through substrate has fine, parallel gas flow passages extending from the inlet end to the outlet end of the substrate such that the flow passages are open to fluid flow. The flow passages, which are essentially straight-line paths from the fluid inlet to the fluid outlet, are defined by walls on or within which catalytic coatings are disposed such that gas flowing through the flow passages contacts the catalytic material. The flow passages of the flow-through substrate are thin-walled channels and can be of any suitable cross-sectional shape and size, such as trapezoidal, rectangular, square, sinusoidal, hexagonal, elliptical, circular, etc. The flow-through substrate can be ceramic or metallic, as described above.

[0104] The flow-through substrate may be, for example, about 50 in 3 ~About 1200in3 volume of about 60 cells per square inch (cpsi) to about 500 cpsi or up to about 900 cpsi, for example, a cell density (inlet opening) of about 200 to about 400 cpsi, and a wall thickness of about 50 to about 200 microns or about 400 microns.

[0105] Wall Flow Filter Substrate In some embodiments, the substrate is a wall-flow filter, which generally has a plurality of fine, substantially parallel gas flow passages extending along the longitudinal axis of the substrate. Typically, each passage is blocked at one end of the substrate body, and an alternate passage is blocked at the opposite end face. Such monolithic wall-flow filter substrates can contain up to about 900 or more passages (or "cells") per square inch of cross section, although only a few may be used. For example, the substrate may have about 7 to 600, more commonly about 100 to 400 cells per square inch ("cpsi"). The cells may have rectangular, square, circular, elliptical, triangular, hexagonal, or other polygonal cross sections. Wall-flow filter substrates can be ceramic or metallic, as described above.

[0106] Referring to FIG. 1a, an exemplary wall-flow filter substrate is cylindrical and has a cylindrical outer surface with a diameter D and an axial length L. FIG. 1b is a perspective view of an exemplary wall-flow filter. A cross-sectional view of a monolithic wall-flow filter substrate section is illustrated in FIG. 1b, showing alternating blocked and open flow channels (cells). Blocked or blocked ends 100 alternate with open flow channels 101, with each opposing end being open and blocked, respectively. The filter has an inlet end 102 and an outlet end 103. Arrows across the porous cell walls 104 represent exhaust gas flow entering the open cell ends, diffusing through the porous cell walls 104, and exiting the open outlet cell ends. The blocked ends 100 prevent gas flow and promote diffusion through the cell walls. Each cell wall will have an inlet side 104a and an outlet side 104b. The flow channels are surrounded by cell walls.

[0107] The wall flow filter article substrate may be, for example, about 50 cm 3 , about 100in 3 , about 200in 3 , about 300in 3 , about 400in 3 , about 500in 3 , about 600in 3 , about 700in 3 , about 800in 3 , about 900in 3 , or about 1000in 3 From about 1500in 3 , about 2000in 3 , about 2500in 3 , about 3000in 3 , about 3500in 3 , about 4000in 3 , about 4500in 3 , or about 5000in 3 Wall-flow filter substrates typically have a wall thickness of from about 50 microns to about 2000 microns, for example, from about 50 microns to about 450 microns, or from about 150 microns to about 400 microns.

[0108] The walls of the wall-flow filter are porous and generally have a wall porosity of at least about 40% or at least about 50% and an average pore size of at least about 10 microns before the functional coating is placed. For example, the wall-flow filter article substrate in some embodiments will have a porosity of ≧40%, ≧50%, ≧60%, ≧65%, or ≧70%. For example, the wall-flow filter article substrate will have a wall porosity of about 50%, about 60%, about 65%, or about 70% to about 75% and an average pore size of about 10 or about 20 to about 30 microns or about 40 microns before the catalytic coating is placed. The terms "wall porosity" and "substrate porosity" are synonymous and interchangeable. Porosity is the ratio of void volume (or pore volume) divided by the total volume of the substrate material. Pore size and pore size distribution are typically determined by Hg porosimetry measurements.

[0109] Substrate Coating Process To produce the SCR catalytic articles of the present disclosure, a substrate as described herein is coated with the SCR catalytic composition as disclosed herein. The coating is a "catalytic coating composition" or a "catalytic coating." "Catalyst composition" and "catalytic coating composition" are synonymous.

[0110] Generally, a catalyst composition is prepared and coated onto a substrate. The method can include mixing a catalyst composition generally disclosed herein (or one or more components of the catalyst composition) with a solvent (e.g., water) to form a slurry for coating the catalyst substrate. In addition to the catalyst composition (i.e., porous refractory metal oxide, PGM, base metal oxide, zeolite, and metal), the slurry can optionally contain various additional components. Exemplary additional components include, but are not limited to, binders as described herein above, such as additives for controlling the pH and viscosity of the slurry. The additional components can include hydrocarbon (HC) storage components (e.g., zeolite), associative thickeners, and / or surfactants (including anionic, cationic, nonionic, or amphoteric surfactants). A typical pH range for the slurry is from about 3 to about 6. Acidic or basic species may be added to the slurry to adjust the pH. For example, in some embodiments, the pH of the slurry is adjusted by the addition of an aqueous solution of acetic acid.

[0111] The slurry can be milled to reduce particle size and improve particle mixing and formation of a homogenous material. Milling can be accomplished in a ball mill, continuous mill, or other similar equipment, and the solids content of the slurry can be, for example, about 20-60% by weight, more specifically, about 20-40% by weight. In one embodiment, the slurry after milling has a D of about 1 to about 40 microns, preferably 2 to about 20 microns, and more preferably about 4 to about 15 microns. 90 It is characterized by its particle size.

[0112] The catalyst composition may typically be applied in the form of one or more washcoats containing the SCR catalyst composition components as disclosed herein. The washcoat is formed by preparing a slurry containing a particular solids content (e.g., about 10 to about 60 wt%) of the catalyst composition (or one or more components of the catalyst composition) in a liquid vehicle, which is then applied to the substrate using any washcoat technique known in the art, dried and calcined to provide a coating layer. If multiple coatings are applied, the substrate is dried and / or calcined after each washcoat is applied and / or after a desired number of multiple washcoats are applied. In one or more embodiments, the catalytic material(s) are applied to the substrate as a washcoat.

[0113] After calcination, the catalyst loading obtained by the above washcoat technique can be determined by calculating the difference between the coated and uncoated weights of the substrate. As will be apparent to those skilled in the art, the catalyst loading can be modified by changing the rheology of the slurry. Furthermore, the coating / drying / calcining process to produce a washcoat layer (coating layer) can be repeated as necessary to build up the coating to a desired loading level or thickness, meaning that two or more washcoats can be applied.

[0114] The catalytic coating can include one or more coating layers, at least one of which includes the catalytic composition or one or more components of the catalytic composition. The catalytic coating can include one or more thin, adherent coating layers disposed on and adhered to at least a portion of the substrate. The overall coating includes the individual "coating layers."

[0115] In some embodiments, the catalytic article may include the use of one or more catalytic layers, as well as a combination of one or more catalytic layers. The catalytic material may be present only on the inlet side, only on the outlet side, on both the inlet and outlet sides of the substrate wall, or the wall itself may be composed entirely or partially of catalytic material. The catalytic coating may be on the substrate wall surface and / or within the pores of the substrate wall, i.e., "in" and / or "on" the substrate wall. Thus, the phrase "washcoat disposed on the substrate" means on any surface, e.g., on the wall surface and / or on the pore surface.

[0116] The washcoat(s) can be applied such that the different coating layers are in direct contact with the substrate. Alternatively, one or more "undercoats" can be present, such that the catalytic coating layer or at least a portion of the coating layer is not in direct contact with the substrate (rather, it is in contact with the undercoat). One or more "overcoats" can also be present such that at least a portion of the coating layer(s) is not directly exposed to the gas stream or atmosphere (rather, it is in contact with the overcoat).

[0117] Alternatively, the catalyst composition may be present in a top coating layer overlying the bottom coating layer. The catalyst composition may be present in the top and bottom layers. Any one layer may extend over the entire axial length of the substrate, for example, the bottom layer may extend over the entire axial length of the substrate, and the top layer may also extend over the bottom layer over the entire axial length of the substrate. Each of the top and bottom layers may extend from either the inlet end or the outlet end.

[0118] For example, both the bottom coating layer and the top coating layer can extend from the same substrate end, the top layer partially or completely overlaying the bottom layer, and the bottom layer can extend a partial or full length of the substrate, and the top layer can extend a partial or full length of the substrate. Alternatively, the top layer can overlay a portion of the bottom layer. For example, the bottom layer can extend the full length of the substrate, and the top layer can extend about 10%, about 20%, about 30%, about 40%, about 50%, about 60%, about 70%, about 80%, or about 90% of the substrate length from either the inlet or outlet end.

[0119] Alternatively, the bottom layer can extend from either the inlet end or the outlet end up to about 10%, about 15%, about 25%, about 30%, about 40%, about 45%, about 50%, about 55%, about 60%, about 65%, about 70%, about 75%, about 80%, about 85%, or about 95% of the length of the substrate, and the top layer can extend from either the inlet end or the outlet end up to about 10%, about 15%, about 25%, about 30%, about 40%, about 45%, about 50%, about 55%, about 60%, about 65%, about 70%, about 75%, about 80%, about 85%, or about 95% of the length of the substrate, where at least a portion of the top layer overlays the bottom layer. This "overlay" zone may extend, for example, from about 5% to about 80% of the length of the substrate, such as about 5%, about 10%, about 20%, about 30%, about 40%, about 50%, about 60, or about 70%.

[0120] In some embodiments, the SCR catalyst composition disclosed herein disposed on a substrate disclosed herein includes a first washcoat comprising a mixture of (a) a porous refractory metal oxide support having a PGM component and a base metal oxide deposited thereon, and (b) a zeolite promoted with a metal component, where the first washcoat is disposed over at least a portion of the length of the catalyst substrate, and a second washcoat comprising a zeolite promoted with a metal component, where the second washcoat is disposed over at least a portion of the length of the catalyst substrate.

[0121] In some embodiments, the first washcoat is disposed directly on the catalytic substrate and the second washcoat is disposed over at least a portion of the first washcoat. In some embodiments, the second washcoat is disposed directly on the catalytic substrate and the first washcoat is disposed over at least a portion of the second washcoat. In some embodiments, the first washcoat is disposed directly on the catalytic substrate from the inlet end for about 10% to about 50% of the total length and the second washcoat is disposed over at least a portion of the first washcoat. In some embodiments, the second washcoat is disposed directly on the catalytic substrate from the inlet end for about 50% to about 100% of the total length and the first washcoat is disposed over at least a portion of the second washcoat. In some embodiments, the first washcoat is disposed directly on the catalytic substrate from the inlet end for about 20% to about 40% of the total length and the second washcoat extends from the inlet end to the outlet end. In some embodiments, the first washcoat is disposed directly on the catalyst substrate from the outlet end to about 10% to about 50% of the total length, and the second washcoat is disposed over at least a portion of the first washcoat. In some embodiments, the first washcoat is disposed directly on the catalyst substrate from the outlet end to about 20% to about 40% of the total length, and the second washcoat extends from the inlet end to the outlet end. In some embodiments, the second washcoat is disposed directly on the catalyst substrate from the outlet end to about 50% to about 100% of the total length, and the first washcoat is disposed over at least a portion of the second washcoat. In some embodiments, the first washcoat is disposed directly on the catalyst substrate covering 100% of the total length, and the second washcoat is disposed over the first washcoat covering 100% of the total length. In some embodiments, the second washcoat is disposed directly on the catalytic substrate with 100% coverage of the entire length, and the first washcoat is disposed on the second washcoat with 100% coverage of the entire length.

[0122] The catalytic coating can advantageously be "zoned" and include zoned catalytic layers, i.e., the catalytic coating contains different compositions across the axial length of the substrate. This can also be described as "laterally zoned." For example, a layer can extend from the inlet end toward the outlet end and can extend up to about 10%, about 20%, about 30%, about 40%, about 50%, about 60%, about 70%, about 80%, or about 90% of the substrate's length. Another layer can extend from the outlet end toward the inlet end and can extend up to about 10%, about 20%, about 30%, about 40%, about 50%, about 60%, about 70%, about 80%, or about 90% of the substrate's length. Different coating layers may be adjacent to each other and not overlay each other. Alternatively, different layers may overlay portions of each other to provide a third "intermediate" zone. The intermediate zone can extend, for example, from about 5% to about 80% of the length of the substrate, such as about 5%, about 10%, about 20%, about 30%, about 40%, about 50%, about 60, or about 70%.

[0123] The zones of the present disclosure are defined by the relationship of the coating layers. There are several possible zoning configurations with respect to different coating layers. For example, there can be an upstream zone and a downstream zone, there can be an upstream zone, an intermediate zone, and a downstream zone, there can be four different zones, etc. When two layers are adjacent and do not overlap, there are upstream and downstream zones. When two layers overlap to some extent, there are upstream, downstream, and intermediate zones. For example, when a coating layer extends over the entire length of the substrate and a different coating layer extends a certain length from the exit end and overlays a portion of the first coating layer, there are upstream and downstream zones.

[0124] For example, the article may include (a) a porous refractory metal oxide support having a PGM component and a base metal oxide deposited thereon; and (b) an upstream zone including a first washcoat layer comprising a mixture of a PGM component and a zeolite promoted with a metal component, and a downstream zone including a second washcoat layer comprising a zeolite promoted with a metal component.

[0125] Alternatively, the upstream zone can include the second washcoat layer and the downstream zone can include the first washcoat layer.

[0126] In some embodiments, the first washcoat is disposed on the catalyst substrate from the inlet end for about 10% to about 50% of the total length, and the second washcoat is disposed on the catalyst substrate from the outlet end for about 50% to about 90% of the total length. In some embodiments, the first washcoat is disposed on the catalyst substrate from the outlet end for about 10% to about 50% of the total length, and the second washcoat is disposed on the catalyst substrate from the inlet end for about 50% to about 90% of the total length.

[0127] In some embodiments, the weight ratio of the porous refractory metal oxide to the zeolite in the first washcoat is from about 0.1 to about 10. In some embodiments, the weight ratio of the porous refractory metal oxide to the zeolite in the first washcoat is from about 0.2 to about 5. In some embodiments, the weight ratio of the porous refractory metal oxide to the zeolite in the first washcoat is about 0.25.

[0128] 2a, 2b, and 2c show some possible coating layer configurations with two coating layers. Shown is the substrate wall 200 on which coating layers 201 (top coat) and 202 (bottom coat) are disposed. This is a simplified view, and in the case of a porous wall-flow substrate, the pores and the coatings attached to the pore walls are not shown, nor are the plugged ends shown. In FIG. 2a, the bottom coating layer 202 extends about 50% of the substrate length from the outlet, and the top coating layer 201 extends more than 50% of the substrate length from the inlet, overlaying a portion of layer 202, providing an upstream zone 203, an intermediate overlay zone 205, and a downstream zone 204. In FIG. 2b, coating layers 201 and 202 each extend the entire length of the substrate, with the top layer 201 overlaying the bottom layer 202. The substrate in FIG. 2b does not contain a zoned coating configuration. Figure 2c illustrates a zoned configuration having coating layer 202 extending approximately 50% of the substrate length from the outlet to form downstream zone 204, and coating layer 201 extending approximately 50% of the substrate length from the inlet to provide upstream zone 203. Figures 2a, 2b, and 2c may be useful in illustrating coating compositions on wall-through substrates or flow-through carriers.

[0129] The SCR articles disclosed herein are capable of reducing NO from lean-burn engine exhaust gas in the presence of a reductant. x The current article is effective at catalyzing the reduction of NO over a range of temperatures. x In some embodiments, the NO xの Effective reduction occurs at temperatures above about 150° C. and below about 700° C. In some embodiments, NO x Effective reduction of NO is at temperatures between about 200° C. and about 600° C. In some embodiments, NO x The conversion of NO is increased by at least 10% at 200° C. as compared to a baseline catalytic article having only a copper-chabazite washcoat disposed on a substrate. In some embodiments, the NO xThe conversion of NO is increased by 40% or more at 200° C. as compared to a baseline catalytic article having only a copper-chabazite washcoat disposed on a substrate. In some embodiments, x The conversion of NO is increased by 10% at 200° C. compared to a baseline catalytic article having only a copper-chabazite washcoat disposed on a substrate. In some embodiments, NO x Nitrogen (N 2 ) and water is increased by 15%, 20%, 25%, 30%, 40%, 50%, 60%, 70%, 80% or more at 200° C. compared to a baseline catalytic article having only a copper-chabazite washcoat disposed on a substrate.

[0130] III. Exhaust Gas Treatment System In a further aspect, an exhaust gas treatment system is provided that includes a lean-burn engine that generates an exhaust gas stream and an SCR article as disclosed herein. The engine can be, for example, a diesel engine that operates under combustion conditions with more air than is required for stoichiometric combustion, i.e., lean conditions. In other embodiments, the engine can be a lean-burn gasoline engine, or an engine associated with a stationary power source (e.g., a generator or a pumping station). The exhaust gas treatment system generally contains two or more catalytic articles disposed downstream of the engine in fluid communication with the exhaust gas stream. The system can contain, for example, a selective catalytic reduction catalyst (SCR) as disclosed herein, a diesel oxidation catalyst (DOC), and one or more articles that contain a reductant injector, a soot filter, an ammonia oxidation catalyst (AMOx), or a lean NOx trap (LNT). An article that contains a reductant injector is a reduction article. The reduction system includes a reductant injector and / or a pump and / or a reservoir, and the like. The treatment system can further include a soot filter and / or an ammonia oxidation catalyst. The soot filter may be uncatalyzed or catalyzed (CSF). For example, the treatment system may include, from upstream to downstream, a DOC-containing item, a CSF, a urea injector, an SCR item, and an AMOx-containing item. A lean NOx trap (LNT) may also be included.

[0131] The relative placement of the various catalytic components present within the emission treatment system can vary. In the present exhaust gas treatment systems and methods, the exhaust gas stream is received into the article(s) or treatment system by entering at an upstream end and exiting at a downstream end. The inlet end of the substrate or article is synonymous with the "upstream" end or "front" end. The outlet end is synonymous with the "downstream" end or "rear" end. The treatment system is generally downstream of and in fluid communication with the internal combustion engine.

[0132] One exemplary emission treatment system is illustrated in FIG. 3, which shows a schematic diagram of an emission treatment system 20. As shown, the emission treatment system may include multiple catalyst components in series downstream of an engine 22, such as a lean-burn gasoline engine. At least one of the catalyst components will be an SCR catalyst of the present invention as described herein. The catalyst composition of the present invention may be combined with a number of additional catalyst materials and may be in various positions relative to the additional catalyst materials. Although FIG. 3 illustrates five catalyst components 24, 26, 28, 30, 32 in series, the total number of catalyst components may vary, and five components are merely one example.

[0133] Without limitation, Table 1 presents various exhaust gas treatment system configurations of one or more embodiments. Note that each catalyst is connected to the next catalyst via an exhaust conduit such that the engine is upstream of catalyst A, which is upstream of catalyst B, which is upstream of catalyst C, which is upstream of catalyst D, and which is upstream of catalyst E (if present). References in the table to components A-E may be cross-referenced with the same designations in FIG. 3.

[0134] The LNT catalysts listed in Table 1 are x It can be any catalyst conventionally used as a trap, typically a base metal oxide (BaO, MgO, CeO 2 ) and platinum group metals (e.g., Pt and Rh) for catalytic oxidation and reduction of NO x The present invention includes a sorbent composition.

[0135] The LT-NA catalysts listed in Table 1 produce NO at low temperatures (<250°C). x (e.g. NO or NO 2 The catalyst can be any catalyst that can adsorb NO 2 and release it into the gas stream at high temperatures (>250°C). X Generally, N is generated on the downstream SCR or SCRoF catalyst. 2 and H 2O. Typically, the LT-NA catalyst comprises a Pd-promoted zeolite or a Pd-promoted refractory metal oxide.

[0136] References to SCR in the tables refer to an SCR catalyst, which may include the SCR catalyst composition of the present invention. References to SCRoF (i.e., SCR on filter) refer to a particulate or soot filter (e.g., a wall-flow filter) that may include the SCR catalyst composition of the present invention. If both an SCR and an SCRoF are present, one or both could include the SCR catalyst of the present invention, or one of the catalysts could include a conventional SCR catalyst (e.g., an SCR catalyst with a conventional metal loading level).

[0137] References to AMOx in the tables refer to an ammonia oxidation catalyst that may be provided downstream of the catalyst of one or more embodiments of the present invention to remove any leaking ammonia from the exhaust gas treatment system. In certain embodiments, the AMOx catalyst may include a PGM component. In one or more embodiments, the AMOx catalyst may include a bottom coat having PGMs and a top coat having SCR functionality.

[0138] As will be appreciated by one of skill in the art, in the configurations listed in Table 1, any one or more of components A, B, C, D, or E can be disposed on a particulate filter, such as a wall-flow filter, or on a flow-through honeycomb substrate. In one or more embodiments, the engine exhaust system includes one or more catalyst compositions mounted in a location near the engine (direct-coupled location, CC), with an additional catalyst composition in an underbody location (underfloor location, UF). In one or more embodiments, the exhaust gas treatment system may further include a urea injection component. [Table 1]

[0139] How to treat engine exhaust Another aspect of the present invention relates to a method for treating an exhaust gas stream from a lean-burn engine, particularly a lean-burn gasoline or diesel engine. The method can include placing an SCR catalyst article according to one or more embodiments of the present invention downstream of the engine and flowing the engine exhaust gas stream over the catalyst. In one or more embodiments, the method further includes placing an additional catalyst component downstream of the engine, as described above. The catalyst composition, article, system, and method are suitable for treating exhaust gas streams from internal combustion engines, such as gasoline, light diesel, and heavy diesel engines. The catalyst composition is also suitable for treating emissions from stationary industrial processes, removing harmful or toxic substances from indoor air, or catalyzing chemical reaction processes.

[0140] It will be readily apparent to those skilled in the relevant art that suitable modifications and adaptations to the compositions, methods, and applications described herein can be made without departing from the scope of any embodiment or aspect thereof. The compositions and methods provided are exemplary and are not intended to limit the scope of the claimed embodiments. All of the various embodiments, aspects, and options disclosed herein can be combined in all variations. The scope of the compositions, formulations, methods, and processes described herein includes all actual or potential combinations of the embodiments, aspects, options, examples, and preferences herein. All patents and publications cited herein are incorporated by reference for their specific teachings, as described, unless other specific statements of incorporation are specifically provided.

[0141] The present invention will now be described with reference to the following examples. Before describing certain exemplary embodiments of the invention, it should be understood that the invention is not limited to the details of construction or process steps set forth in the following description. The invention is capable of other embodiments and of being practiced or carried out in various ways.

[0142] experiment Aspects of the present invention are more fully illustrated by the following examples, which are presented to describe particular aspects of the invention and are not to be construed as limiting the invention. EXAMPLES

[0143] Preparation of SCR Compositions and Articles (SCRoF) An example of a selective catalytic reduction (SCR) catalyst composition (SCRoF Article) according to certain embodiments disclosed herein disposed on a filter substrate was prepared by washcoating SCR catalytic components onto a highly porous SiC filter substrate. The SiC substrate had a porosity of 63%, an average pore size of 23 μm, and 300 cells / in 2 The substrates were square segments (34 mm x 34 mm x 152 mm) with a cell density of 0.01 mm and a wall thickness of 0.3 mm. The substrates had an asymmetric cell design, with large openings for the inlet channels and small openings for the outlet channels. This type of cell design therefore allowed the filter to retain more ash compared to a symmetric design without excessively increasing the back pressure on the filter.

[0144] Two types of slurries were coated on the substrates sequentially, one containing Pt and the other containing Cu-CHA. The main components of the Pt-containing slurry were a Pt amine precursor and a copper nitrate solution on an alumina-based support (5% SiO 2 The Pt-CuO powders were prepared by sequential impregnation of ZnO-doped alumina (Pt-CuO powders) with ZnO-doped alumina (Pt-CuO powders). After each impregnation, a calcination treatment (500°C / 2h) was applied. Some Pt-CuO powders were further calcined at 800°C for 4h. A detailed description of the supported Pt-CuO powders is shown in Table 2. [Table 2]

[0145] Table 3 provides the coating design of SCRoF articles according to certain embodiments of the present disclosure, coated with a Pt-containing slurry as the first coating. The reference sample for this group of articles was a Cu-CHA only formulation (S0) without the Pt component. Articles S1-S10 contained various formulations of Pt-containing powder as part of the first coat slurry. Articles S9 and S10 contained Al in the first coat. 2 O 3 While the first of the articles S1-S8 contained Pt-containing slurry, articles S1-S8 also contained some Cu-CHA in their first coat. The Pt-containing slurry covered 33% of the filter length from the outlet face. The second coats of S1-S10 were the same (e.g., Cu-CHA coated from the inlet end and covering 100% of the filter). After each coating, a baking (450° C. for 1 hour) step was performed. The washcoat zoning design and coating sequence of articles S1-S10 are illustrated in FIG. 4. [Table 3]

[0146] Table 4 shows the coating design of the SCRoF article according to certain embodiments, where a Pt-containing slurry was coated as the second coat (S11-S20). Cu-CHA was first coated on the filter substrate from the inlet end with 100% coverage. The second coat was a Pt-containing coat, consisting of Pt-CuO powder (shown in Table 2) and either Cu-CHA or Al. 2 O 3 The second coat was applied from the exit end and covered 33% of the length. Articles S11-S20 are mirror designs of Articles 1-10. The washcoat zoning designs and coating sequences of Articles S11-S20 are shown in FIG. 5. [Table 4]

[0147] Example 2. Evaluation of catalytic articles The catalyst article identified above was tested in a steady-state laboratory reactor capable of flowing 200 L / min of gas. The reaction feedstock had a GHSV of 60,000 h -1 500 ppm NO, 550 ppm NH 3 , (NH 3 / NO x = 1.1), 500 ppm CO, 10% O 2、 5% CO 2 , 5%H 2 O, the rest N 2 The catalyzed filter article samples were first heated at 200° C. for 30 minutes to remove NO and NH 3 The mixture was then equilibrated with the main feed gas that did not contain NO and NH. 3 were added sequentially to the system at 200°C with equilibration times of 15 and 25 minutes, respectively. With full reactive feed, the reactor inlet temperature was ramped from 200 to 500°C at 2.5°C / min. All catalyst articles were prepared fresh (as prepared) and after aging (10% H in air). 2 The results are shown in Figures 6-12 and discussed below.

[0148] FIG. 6 illustrates exemplary test results obtained for catalyst article S1, showing NO as a function of reaction temperature. x Conversion and N 2 The graph shows NO formation at 200 and 500 °C for clarity. x Conversion and peak N 2 Only O formation is compared for articles S0 to S20 in Figs.

[0149] 7a and 7b show the NO x The conversion is compared to a zeolite-only control (S0). For the samples with Pt in the first coat (S1-S10), all samples, except for S9 and S10, had higher NO2 (by 8-19%) than the control. xIn the case of the articles with Pt in the second coat (S11-20), two samples (S14 and S16) showed high NO x Although the conversion was shown, the other samples were comparable to or lower (S19 and S20) than the reference (S0).

[0150] As shown in Figures 8a and 8b, the NO x The conversions were comparable to each other and to the reference S0 (87-90%).

[0151] 9a and 9b show the peaks N 2 O formation. The much higher peak N 2 O formation was observed for S20, S2, S19, S6, and S10 (95–52 ppm) relative to S0 (8 ppm). The other products showed slightly higher N 2 O formation was demonstrated.

[0152] 10a and 10b show the NO 3 at 200 °C for S1-S10 and S11-S20, respectively, after hydrothermal aging at 800 °C for 16 h. x Two articles (S7 and S9) showed much higher NO conversion than the reference S0 (25%). x Conversion (70% and 62%, respectively) of NO was demonstrated. All other articles demonstrated slightly higher NO x The conversion was 29-36%.

[0153] 11a and 11b show NO 2 at 500° C. for aged catalyst articles S1-S10 and S11-S20, respectively. x The results show that the conversion of 1,2-dichlorophenyl 1,3-dichlorophenyl 1,4-dichlorophenyl 1,5-dichlorophenyl 1,6-dichlorophenyl 1,7-dichlorophenyl 1,8-dichlorophenyl 1,9 ...x The transformation was shown.

[0154] 12a and 12b show peaks N for aged catalyst articles S1-S10 and S11-S20, respectively. 2 O formation. Very high N 2 O formation was observed in S10, S19, and S20 (69–116 ppm), with slightly higher N in S7 and S9 (21 and 36 ppm). 2 O was observed, and N was observed for all other items. 2 O formation was comparable to S0 (5-7 ppm).

[0155] Overall, considering all the performance data, article S7 showed the most favorable profile. Without wishing to be bound by theory, it is believed that typically Pt is too strong an oxidizing component and NH 3 N 2 O and NO x As a result, NO x Conversion is reduced and N 2 It is believed that the oxidation function of Pt may be mitigated while providing sufficient oxidation activity for in situ NO oxidation by impregnating and immobilizing Cu and Pt on the same support.

Claims

1. NO from lean-burn engine exhaust in the presence of a reductant ｘ a selective catalytic reduction (SCR) article effective to catalyze the reduction of The SCR catalyst composition comprises: a first component comprising a porous refractory metal oxide support having deposited thereon a platinum group metal (PGM) and a base metal oxide; a second component comprising a metal promoted zeolite; a weight ratio of said first component to said second component ranges from about 0.05 to about 0.5; and The SCR catalyst composition comprises: a first washcoat comprising a mixture of (a) the first component and (b) the second component, the first washcoat being disposed over at least a portion of a length of the catalytic substrate; a second washcoat comprising the second component, the second washcoat disposed on at least a portion of a length of the catalytic substrate.

2. 10. The SCR article of claim 1, wherein the first washcoat is disposed directly on the catalytic substrate and the second washcoat is disposed over at least a portion of the first washcoat.

3. 10. The SCR article of claim 1, wherein the second washcoat is disposed directly on the catalytic substrate and the first washcoat is disposed over at least a portion of the second washcoat.

4. 2. The SCR article of claim 1, wherein the first washcoat is disposed directly on the catalytic substrate from the inlet end to about 10% to about 50% of the overall length, and the second washcoat is disposed over at least a portion of the first washcoat.

5. 2. The SCR article of claim 1, wherein the second washcoat is disposed directly on the catalytic substrate from the inlet end to about 50% to about 100% of the overall length, and the first washcoat is disposed over at least a portion of the second washcoat.

6. 2. The SCR article of claim 1, wherein the first washcoat is disposed directly on the catalytic substrate from the inlet end to about 20% to about 40% of the overall length, and the second washcoat extends from the inlet end to the outlet end.

7. 2. The SCR article of claim 1, wherein the first washcoat is disposed directly on the catalytic substrate from the outlet end to about 10% to about 50% of the overall length, and the second washcoat is disposed over at least a portion of the first washcoat.

8. 2. The SCR article of claim 1, wherein the first washcoat is disposed directly on the catalytic substrate from the outlet end to about 20 to about 40% of the overall length, and the second washcoat extends from the inlet end to the outlet end.

9. 2. The SCR article of claim 1, wherein the second washcoat is disposed directly on the catalytic substrate from the outlet end to about 50% to about 100% of the overall length, and the first washcoat is disposed over at least a portion of the second washcoat.

10. 2. The SCR article of claim 1, wherein the first washcoat is disposed directly on the catalytic substrate covering 100% of the overall length and the second washcoat is disposed on the first washcoat covering 100% of the overall length.

11. 2. The SCR article of claim 1, wherein the second washcoat is disposed directly on the catalytic substrate covering 100% of the overall length and the first washcoat is disposed on the second washcoat covering 100% of the overall length.

12. 10. The SCR article of claim 1 having a zoned configuration, wherein the first washcoat is disposed on the catalytic substrate from the inlet end to about 10% to about 50% of the total length, and the second washcoat is disposed on the catalytic substrate from the outlet end to about 50% to about 90% of the total length.

13. 10. The SCR article of claim 1 having a zoned configuration, wherein the first washcoat is disposed on the catalytic substrate from the outlet end to about 10% to about 50% of the total length, and the second washcoat is disposed on the catalytic substrate from the inlet end to about 50% to about 90% of the total length.

14. 2. The SCR article of claim 1, wherein the weight ratio of porous refractory metal oxide to zeolite in the first washcoat is from about 0.1 to about 10.

15. 2. The SCR article of claim 1, wherein the first washcoat has a weight ratio of porous refractory metal oxide to zeolite of about 0.2 to about 5.

16. 7. The SCR article of claim 6, wherein the PGM is Pt, the base metal oxide is copper oxide, the zeolite has a chabazite structure and is promoted with copper, the porous refractory metal oxide is alumina containing 5% silica, the Pt is present in an amount of about 2.9% by weight of the porous refractory metal oxide, and the copper oxide is present in an amount of about 10% by weight of the porous refractory metal oxide.

17. The SCR article of claim 1 , wherein the substrate is a honeycomb substrate.

18. 20. The SCR article of claim 17, wherein the honeycomb substrate is a metal, ceramic, silicon carbide, cordierite, or aluminum titanate.

19. 20. The SCR article of claim 17, wherein the honeycomb substrate is a flow-through substrate or a wall-flow filter.

20. NO ｘ The SCR article of claim 1, wherein effective reduction of is at a temperature greater than about 150°C and less than about 700°C.

21. NO ｘ The SCR article of claim 16, wherein effective reduction of is at a temperature of about 200°C to about 600°C.

22. NO ｘ 10. The SCR article of claim 1, wherein the conversion of is increased by at least 10% at 200° C. as compared to a baseline catalytic article having only a copper-chabazite washcoat disposed on the substrate.

23. An exhaust gas treatment system comprising: a lean-burn engine generating an exhaust gas stream; and the SCR article of claim 1.

24. Diesel Oxidation Catalyst (DOC), soot filter, urea injection component, ammonia oxidation catalyst (AMOX), low temperature NO ｘ Absorbent (LT-NA) and Lean NO ｘ24. The exhaust gas treatment system of claim 23, further comprising one or more of the following: a trap (LNT).