Method and device for extrusion molding of pipes with different thicknesses having solid portions

Abstract

In the present invention, when manufacturing a different-thickness pipe having a solid portion, there are performed: a first step for inserting a cylindrical material that is hollow on the proximal-end side and solid on the distal-end side into a large-inside-diameter portion of a container hole, bringing the distal-end side of the material into contact with a decreasing-inside-diameter portion of the container hole, bringing a sleeve into contact with the proximal-end-side end of the material, inserting a mandrel into the hollow hole in the material, and fixing the inter-distal-end distance, which is the distance between the distal end of the sleeve and the distal end of the mandrel, at a prescribed distance; a second step for causing the mandrel and the sleeve to advance in the extrusion direction, while maintaining the inter-distal-end distance, during a period until the distal end of the mandrel reaches the decreasing-inside-diameter portion of the container hole, whereby the material is pressed into the small-inside-diameter portion via the decreasing-inside-diameter portion of the container hole; and a third step for continuing to advance the sleeve and the mandrel while maintaining the inter-distal-end distance. It is thereby possible to reduce the incidence of defects such as cracks and / or material accumulation without requiring a material having a complex shape.

Description

[Technical field]

[0001] The present invention relates to an extrusion molding method and an extrusion molding apparatus for a pipe having a solid portion and a different thickness. [Background technology]

[0002] In the technical field, for example, there is known a differential thickness pipe (also called a "butted pipe" or "butted tube") in which a thick-walled portion is formed in a portion in the axial direction of the pipe for the purpose of achieving a desired mechanical strength in the thick-walled portion while reducing the weight of the thin-walled portion (portion other than the thick-walled portion). Such a differential thickness pipe that is hollow over its entire length can be integrally formed by extrusion molding from a cylindrical blank tube, as disclosed in Patent Document 1 (Japanese Patent No. 6933762), for example.

[0003] In addition, there is a need to apply a differential thickness pipe in the field of shafts, etc., but it may be required to provide a solid portion having a predetermined length in the axial direction at one end side, rather than making it hollow over the entire length. For example, from the viewpoint of reducing manufacturing costs, it is desirable to integrally mold such a differential thickness pipe having a solid portion by extrusion molding. However, such a differential thickness pipe having a solid portion cannot be molded by the above-mentioned method.

[0004] Meanwhile, in this technical field, a method is known for manufacturing a bottomed hollow metal product, which is a pipe with a thickness difference that has a solid portion at one end, although its axial length is short, by extrusion molding. For example, Patent Document 2 (JP Patent Publication 49-035497) discloses a method for manufacturing a bottomed hollow metal product by combining a piercing and compression process in which a punch is inserted into a substantially cylindrical solid material to form a hollow hole, and a subsequent process in which a separate punch is used to press the bottom of the hollow hole while extruding the entire material to form a hollow portion (a portion with a thickness difference) and a solid portion (a bottom portion).

[0005] Furthermore, Patent Document 3 (JP Patent Publication 58-048264) discloses a method in which a material having a flange and a hollow hole (and bottom) in a specified positional relationship is formed in advance in a forging process, and in the next process the bottom of the hollow hole is pressed with the tip of a center punch to form an intermediate material with corners, and in the next process the end portion opposite the bottom of the intermediate material is pressed with a sleeve punch to form a hollow portion (differential thickness portion) and a solid portion (bottom).

[0006] However, in all of the above-mentioned methods, it is necessary to prepare a material having a relatively complicated shape that meets certain requirements. In addition, the bottomed hollow metal products manufactured by these methods are so-called "bottomed tubular members" and do not correspond to the above-mentioned differential thickness pipes having a solid portion with a predetermined length in the axial direction. Furthermore, in the latter method, there is a problem that the pressing force of the center punch cannot be set strong because cracks are likely to occur at the boundary between the bottom and the side wall of the material during the process of pressing the bottom of the hollow hole with the tip of the center punch to give it a corner. [Prior art documents] [Patent documents]

[0007] [Patent Document 1] Patent No. 6933762 [Patent Document 2] Special Publication No. 49-035497 [Patent Document 3] Special Publication No. 58-048264 Summary of the Invention [Problem to be solved by the invention]

[0008] Therefore, taking into consideration the problems in the prior art as described above, the present inventor conducted an experiment based on the technology described in Patent Document 1 in which a material having a hollow portion and a solid portion was pressed into a container (die) having a small inner diameter portion at the tip side to reduce the diameter while a mandrel (core metal) was inserted into the hollow hole of the material, thereby extruding a differential thickness pipe having a solid portion. However, it was confirmed that when the bottom of the hollow hole of the material (the top of the solid portion) was pressed in the extrusion direction by the tip of the mandrel, a crack was likely to occur around the entire circumference at the boundary between the bottom of the hollow hole and the side wall portion, as exemplified by the thick solid line in Figure 6(a).

[0009] On the other hand, if extrusion molding is performed while maintaining a space between the tip of the mandrel and the bottom of the hollow hole in order to prevent the occurrence of cracks as described above, as shown by the black semicircle in Figure 6(b) , as the material is compressed radially inward, the material (forming material) of the material plastically flows toward the space, creating a material pool all around the space, making it impossible to achieve the desired hollow shape.

[0010] In other words, there is a need in the art for a method and apparatus for manufacturing a variable thickness pipe having a solid portion that can reduce the occurrence of defects such as cracks and / or material pockets as described above without requiring material with a complex shape. [Means for solving the problem]

[0011] Based on the above findings, the inventor conducted further intensive research and discovered that the above problem can be solved by appropriately controlling the positional relationship between the tip of the mandrel and the bottom of the hollow hole in the material, as well as the movement of the sleeve and mandrel.

[0012] Specifically, the present invention Solid part The method for extruding a pipe having a different thickness (hereinafter, sometimes referred to as the "method of the present invention") is to extrude a material having a predetermined shape in an extrusion molding device. Solid partThe extrusion molding method is a method for forming a pipe having a different thickness by extrusion processing. The extrusion molding apparatus includes a mandrel having a predetermined shape, a sleeve having a predetermined shape, a container having a container hole which is a through hole having a predetermined shape, and a mandrel inserted into the container hole. and sleeve and a drive mechanism configured to push the

[0013] The material is a member that is composed of a first hollow portion and a first solid portion, and has a cylindrical outer shape with a first outer diameter that is a predetermined outer diameter as a whole. The first hollow portion is a cylindrical portion that has a first wall thickness that is a predetermined thickness, in which a first hollow hole that is a cylindrical space that opens to an end face on the base end side that is the upstream side in the extrusion direction and has a first inner diameter that is a predetermined inner diameter is formed. The first solid portion is a cylindrical portion that is located between the end face on the tip end side that is the downstream side in the extrusion direction and the first hollow portion.

[0014] The differential thickness pipe is a member consisting of a second hollow portion, a third hollow portion, a fourth hollow portion, and a second solid portion. The second hollow portion is a cylindrical portion having a first outer diameter and a first wall thickness. The third hollow portion is a tubular portion adjacent to the tip side of the second hollow portion, in which the outer diameter changes from the first outer diameter to a second outer diameter, which is a predetermined outer diameter smaller than the first outer diameter, from the base end side to the tip side, and the wall thickness changes from the first wall thickness to a second wall thickness, which is a predetermined wall thickness smaller than the first wall thickness. The fourth hollow portion is a cylindrical portion adjacent to the tip side of the third hollow portion, having a second outer diameter and a second wall thickness. The second solid portion is a cylindrical portion located between the end portion on the tip side and the fourth hollow portion, and having a second outer diameter. Furthermore, a second hollow hole, which is a cylindrical space having a first inner diameter and opens to the end face on the base end side, is continuously formed from the second hollow portion to the fourth hollow portion.

[0015] The mandrel is a cylindrical member that is coaxially and axially slidably fitted into the sleeve and has a third outer diameter that is a predetermined outer diameter corresponding to the first inner diameter. The sleeve is a cylindrical member that is coaxially and axially slidably fitted into the mandrel and has a second inner diameter and a first outer diameter that are predetermined inner diameters corresponding to the third outer diameter.

[0016] The container bore comprises a large inner diameter portion, a small inner diameter portion, and a reduced inner diameter portion. The large inner diameter portion is formed on the base end side and has a third inner diameter that is an inner diameter corresponding to the first outer diameter. The small inner diameter portion is formed on the tip end side and has a fourth inner diameter that is an inner diameter corresponding to the second outer diameter. The reduced inner diameter portion is formed between the large inner diameter portion and the small inner diameter portion and has an inner diameter that decreases from the third inner diameter to the fourth inner diameter as it approaches the small inner diameter portion.

[0017] The method of the present invention includes the following first to third steps. The first step is a step of inserting a raw material into the large inner diameter portion of the container hole, abutting the tip end of the raw material into the reduced diameter portion of the container hole, abutting the base end of the raw material with a sleeve, inserting a mandrel into a first hollow hole in the raw material, and fixing the tip-to-tip distance, which is the relative distance in the extrusion direction between the tip end of the sleeve and the tip end of the mandrel, to a predetermined first distance. The second step is a step of advancing the sleeve and mandrel in the extrusion direction while maintaining the tip-to-tip distance at a first distance, thereby forcing the material through the reduced inner diameter portion of the container hole and into the smaller inner diameter portion, thereby performing an extrusion process, and continuing to advance the sleeve and mandrel until the tip end of the mandrel reaches the base end of the reduced inner diameter portion of the container hole at the first point in time. The third step is a step of advancing the sleeve and the mandrel in the extrusion direction while maintaining the tip-to-tip distance at the first distance after the first point in time.

[0018] The present invention also provides a method for producing a medicament for the treatment of a pulmonary artery disease by carrying out the above-mentioned method. Solid part A pipe having a different thickness is formed. Solid part The present invention also relates to an extrusion molding apparatus for a pipe having a different thickness (hereinafter, sometimes referred to as the "apparatus of the present invention"). Effect of the Invention

[0019] By carrying out the method of the present invention including the above-mentioned first to third steps in the apparatus of the present invention having the above-mentioned configuration, it is possible to produce a material having a simple structure. Solid part In other words, according to the present invention, it is possible to provide a manufacturing method and a manufacturing device for a differential thickness pipe having a solid portion, which can reduce the occurrence of defects such as cracks and / or material pools without requiring a material having a complex shape.

[0020] Other objects, features and attendant advantages of the present invention will become readily apparent from the following description of the embodiments of the present invention which are given with reference to the accompanying drawings. [Brief description of the drawings]

[0021] [Figure 1] FIG. 1 is a schematic cross-sectional view showing an example of the configuration of a raw material that is the basis of the material used in an extrusion molding method (first method) for a differential thickness pipe having a solid portion according to a first embodiment of the present invention, the material, and a differential thickness pipe having a solid portion molded from the material. [Diagram 2] FIG. 2 is a schematic cross-sectional view showing an example of the configuration of a mandrel, a sleeve, and a container used in a first method. [Diagram 3] 4 is a flowchart illustrating a flow of first to third steps executed in a first method. [Figure 4] This is a schematic cross-sectional view showing an example of the shape of the raw material and the differential thickness pipe at the end of the first step and at the start and end of the third step performed in the first method, and the positional relationship between the mandrel, sleeve, and container and the raw material and the differential thickness pipe. [Diagram 5] FIG. 2 is a schematic cross-sectional view showing an example of the positional relationship between the bottom of the first hollow hole in the material and the mandrel near the bottom of the first hollow hole at the start of the second step included in an extrusion molding method (second method) for a differential thickness pipe having a solid portion according to a second embodiment of the present invention. [Figure 6]1 is a schematic cross-sectional view illustrating a problem observed when attempting to extrude a pipe having a solid portion with a different thickness based on the prior art. FIG. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0022] First Embodiment Hereinafter, a method for extrusion molding a differential thickness pipe having a solid portion according to a first embodiment of the present invention (hereinafter, sometimes referred to as a "first method") will be described with reference to the drawings.

[0023] <composition> The first method is to extrude a material having a predetermined shape in an extrusion molding device. Solid part The extrusion molding method is a method for forming a pipe having a different thickness by extrusion processing. The extrusion molding apparatus includes a mandrel having a predetermined shape, a sleeve having a predetermined shape, a container having a container hole which is a through hole having a predetermined shape, and a mandrel inserted into the container hole. and sleeve and a drive mechanism configured to push the mandrel into the container hole. The basic configuration of such an extrusion molding device is well known to those skilled in the art, so a detailed explanation will be omitted, but the components including the mandrel, sleeve, and container are made of materials having properties (e.g., mechanical strength and durability) that can withstand processing conditions such as the load acting on the components in the extrusion process described below. and sleeve The driving mechanism for pushing the material into the extrusion process can be appropriately selected from various driving mechanisms known in the art according to the properties (e.g., mechanical strength, hardness, etc.) of the material constituting the material to be extruded. Typically, a press machine such as a hydraulic press machine is used as the driving mechanism.

[0024] 1A, 1B, and 1C are schematic cross-sectional views showing an example of the configuration of an original material 11, a material 21, and a differential thickness pipe 31 having a solid portion formed from the material 21, which are used in the first method. As shown in FIG. 1B, the material 21 is a member having a cylindrical outer shape consisting of a first hollow portion PH1 and a first solid portion PS1 and having a first outer diameter DO1, which is a predetermined outer diameter as a whole. The first hollow portion PH1 is a cylindrical portion having a first wall thickness T1, in which a first hollow hole HH1 is formed as a cylindrical space having a first inner diameter DI1, which is a predetermined inner diameter, and opens to an end face on the base end side, which is the upstream side in the extrusion direction. The first solid portion PS1 is a cylindrical portion located between the end face on the tip side, which is the downstream side in the extrusion direction, and the first hollow portion PH1.

[0025] As described above, the raw material 21 has a relatively simple structure, and therefore can be easily manufactured by forming the first hollow hole HH1 in the raw material 11, which is a cylindrical member having a first outer diameter DO1 as exemplified in (a) of Fig. 1. The specific method for forming the first hollow hole HH1 in the raw material 11 is not particularly limited, but the first hollow hole HH1 can be easily formed in the raw material 11 by a method such as cutting.

[0026] The material constituting the raw material 11 is not particularly limited as long as it can be formed into a desired shape by plastic deformation in the extrusion process. Typically, the material constituting the raw material 11 is a metal such as lead, tin, aluminum, copper, zirconium, titanium, molybdenum, vanadium, niobium, and steel.

[0027] As illustrated in FIG. 1(c), the differential thickness pipe 31 is a member consisting of a second hollow portion PH2, a third hollow portion PH3, a fourth hollow portion PH4, and a second solid portion PS2. The second hollow portion PH2 is a cylindrical portion having a first outer diameter DO1 and a first wall thickness T1. The third hollow portion PH3 is a cylindrical portion adjacent to the tip side of the second hollow portion PH2, the outer diameter of which changes from the first outer diameter DO1 to a second outer diameter DO2, which is a predetermined outer diameter smaller than the first outer diameter DO1, from the base end side to the tip side, and the wall thickness of which changes from the first wall thickness T1 to a second wall thickness T2, which is a predetermined wall thickness smaller than the first wall thickness T1. The fourth hollow portion PH4 is a cylindrical portion adjacent to the tip side of the third hollow portion PH3, and has a second outer diameter DO2 and a second wall thickness T2. The second solid portion PS2 is a cylindrical portion located between the distal end and the fourth hollow portion PH4 and having a second outer diameter DO2. Furthermore, a second hollow hole HH2, which is a cylindrical space having a first inner diameter DI1 and opens to the proximal end face, is continuously formed from the second hollow portion PH2 to the fourth hollow portion PH4.

[0028] In the differential thickness pipe 31 illustrated in FIG. 1(c), the rate of change in the outside diameter of the third hollow portion PH3 increases from the base end side to the tip end side, and the contour of the outside diameter of the third hollow portion PH3 is a curved line that is convex outward in the radial direction. However, the pattern of the change in the outside diameter of the third hollow portion PH3 from the first outside diameter DO1 to the second outside diameter DO2 is not limited to this. For example, the contour of the outside diameter of the third hollow portion PH3 may be a curved line that is concave outward in the radial direction, or the rate of change in the outside diameter of the third hollow portion PH3 may be constant from the base end to the tip end, and the contour of the outside diameter of the third hollow portion PH3 may be a straight line.

[0029] In the differential thickness pipe 31 illustrated in FIG. 1(c), the bottom (end on the tip side) of the second hollow hole HH2 has a conical shape. However, the shape of the bottom of the second hollow hole HH2 is not limited to this, and can be various shapes depending on, for example, the use of the differential thickness pipe 31. For example, the shape of the bottom of the second hollow hole HH2 may be a plane perpendicular to the axial direction of the differential thickness pipe 31, or may be a curved surface (e.g., a spherical surface) that is convex toward the tip side. Such a shape of the bottom of the second hollow hole HH2 can be achieved, for example, by making the shape of the end on the tip side of the mandrel a shape corresponding to the shape of the bottom of the second hollow hole HH2.

[0030] 2(a) and 2(b) are schematic cross-sectional views showing an example of the configuration of the mandrel 41, sleeve 51, and container 61 used in the first method, respectively. As shown in FIG. 2(a), the mandrel 41 is a cylindrical member that is coaxially and axially slidably fitted into the sleeve 51 and has a third outer diameter DO3 that is a predetermined outer diameter corresponding to the first inner diameter DI1 that is the inner diameter of the first hollow portion PH1 of the material 21. The sleeve 51 is coaxially and axially slidably fitted into the mandrel 41 and has a second inner diameter DI2 that is a predetermined inner diameter corresponding to the third outer diameter DO3 that is the outer diameter of the mandrel 41, and a first outer diameter DO1 that is the outer diameter of the material 21.

[0031] Although not shown in FIG. 2, the base end portions of mandrel 41 and sleeve 51 may be provided with a structure and / or mechanism suitable for driving by a driving mechanism provided in the extrusion molding device and / or for attachment and detachment from the driving mechanism.

[0032] As illustrated in FIG. 2B, the container hole HC1 formed in the container 61 is composed of a large inner diameter portion PDIL, a small inner diameter portion PDIS, and an inner diameter decreasing portion PDIT. The large inner diameter portion PDIL is a portion formed on the base end side and has a third inner diameter DI3 that is an inner diameter corresponding to the first outer diameter DO1 that is the outer diameter of the blank 21. The small inner diameter portion PDIS is a portion formed on the tip end side and has a fourth inner diameter DI4 that is an inner diameter corresponding to the second outer diameter DO2 that is the outer diameter of the fourth hollow portion PH2 and the second solid portion PS2 of the differential thickness pipe 31. The inner diameter decreasing portion PDIT is a portion formed between the large inner diameter portion PDIL and the small inner diameter portion PDIS and the inner diameter decreases from the third inner diameter DI3 to the fourth inner diameter DI4 as it approaches the small inner diameter portion PDIS from the large inner diameter portion PDIL.

[0033] In the container 61 illustrated in Fig. 2(b), the large inner diameter portion PDIL is made up of two members, the inner diameter reduced portion PDIT and the most proximal portion of the small inner diameter portion PDIS are integrally formed with one member, and the remaining portion of the small inner diameter portion PDIS is made up of two members. That is, the container 61 illustrated in Fig. 2(b) is made up of five members as a whole. However, the configuration of the container 61 is not limited to this, and may be made up of one member as a whole, or may be made up of three members as a whole, with the large inner diameter portion PDIL, the small inner diameter portion PDIS, and the inner diameter reduced portion PDIT each being made up of one member.

[0034] The first method, as illustrated by the flow chart of FIG. 3, includes the following first to third steps.

[0035] The first process executed in step S01 is a process of inserting a raw material into the large inner diameter portion of the container hole, abutting the tip end of the raw material against the reduced inner diameter portion of the container hole, abutting the base end of the raw material with a sleeve, inserting a mandrel into a first hollow hole of the raw material, and fixing the tip-to-tip distance, which is the relative distance in the extrusion direction between the tip end of the sleeve and the tip end of the mandrel, to a predetermined first distance. That is, in the first process, the raw material, the mandrel, the sleeve, and the container are set in predetermined positions.

[0036] The second process executed in step S02 is a process of advancing the sleeve and mandrel in the extrusion direction while maintaining the tip-to-tip distance at the first distance, thereby forcing the material into the small inner diameter portion through the reduced inner diameter portion of the container hole, and continuing to advance the sleeve and mandrel until the first time point at which the tip-to-tip end of the mandrel reaches the base end of the reduced inner diameter portion of the container hole. That is, in the second process, the mandrel and sleeve are driven in cooperation to maintain the tip-to-tip distance at the first distance, and the sleeve and mandrel are advanced in the extrusion direction until the tip-to-tip end of the mandrel reaches the base end of the reduced inner diameter portion of the container hole. This results in extrusion from the first solid portion of the material to the second solid portion of the differential thickness pipe.

[0037] The third step performed in step S03 is a step of advancing the sleeve and mandrel in the extrusion direction while maintaining the tip-to-tip distance at the first distance even after the first time point. That is, even in the third step, which is a step performed after the first time point, the tip-to-tip distance is maintained at the first distance by cooperative driving of the mandrel and sleeve, and the sleeve and mandrel are advanced in the extrusion direction, thereby performing extrusion from a part on the tip side of the first hollow portion of the material to the third hollow portion and the fourth hollow portion of the differential thickness pipe. Note that the part of the first hollow portion of the material that was not subjected to extrusion in the third step becomes the second hollow portion of the differential thickness pipe.

[0038] Fig. 4(a) is a schematic cross-sectional view showing an example of the shape of the blank 21 at the end of the first step and the positional relationship between the blank 21 and the mandrel 41, sleeve 51, and container 61. In Fig. 4, in order to simplify the drawing, only some of the reference symbols given to the respective parts shown in Figs. 1 and 2 are shown. However, in the following explanation of Fig. 4, the reference symbols shown in Figs. 1 and 2 will be used for accuracy, so please refer to Figs. 1 and 2 as necessary.

[0039] As illustrated in Fig. 4(a), the blank 21 is inserted into the large inner diameter portion PDIL of the container hole HC1, and the tip end of the blank 21 abuts against the reduced inner diameter portion PDIT of the container hole HC1. This holds the blank 21 at a predetermined position inside the container hole HC1. A sleeve 51 abuts against the base end of the blank 21, and a mandrel 41 is inserted into a first hollow hole HH1 formed in the blank 21. Furthermore, the sleeve 51 and the mandrel 41 are arranged so that a tip-to-tip distance DT, which is the relative distance in the extrusion direction between the tip end of the sleeve 51 and the tip end of the mandrel 41, is a predetermined first distance D1 (i.e., DT = D1).

[0040] Then, in a second step subsequent to the first step (not shown), the mandrel 51 and the sleeve 41 are driven in a coordinated manner to advance the sleeve 51 and the mandrel 41 in the extrusion direction (the downward direction in FIG. 4) while maintaining the tip-to-tip distance DT at the first distance D1. As a result, the first solid portion PS1 of the raw material 21 is pushed from the tip side through the inner diameter reduced portion PDIT of the container hole HC1 into the small inner diameter portion PDIS, and the first solid portion PS1 of the raw material 21 is extruded into the second solid portion PS2 of the differential thickness pipe 31.

[0041] Furthermore, the second outer diameter DO2, which is the outer diameter of the second solid portion PS2 of the thickness-differential pipe 31, is smaller than the first outer diameter DO1, which is the outer diameter of the first solid portion PS1 of the material 21 (DO2 < DO1). That is, the cross-sectional area of the second solid portion PS2 of the thickness-differential pipe 31 is smaller than the cross-sectional area of the first solid portion PS1 of the material 21. Therefore, the length of the second solid portion PS2 of the thickness-differential pipe 31 extruded from the first solid portion PS1 of the material 21 in the extrusion direction is larger than the length of the first solid portion PS1 of the material 21 in the extrusion direction (details will be described later).

[0042] Incidentally, from the viewpoint of avoiding problems such as the occurrence of cracks as exemplified in FIG. 6(a), for example, at least at the second time point which is the start point of the extrusion direction in the second step, although the end portion on the base end side of the material 21 is pressed by the sleeve 51 in the extrusion direction, it is preferable that the bottom of the first hollow hole HH1 is not pressed by the mandrel 41. Such a state can be achieved, for example, by not bringing the bottom of the first hollow hole HH1 of the material 21 into contact with the mandrel 41 at the second time point or by providing a gap having a predetermined size between the bottom of the first hollow hole HH1 of the material 21 and the end portion on the tip side of the mandrel 41 at the second time point (details will be described later).

[0043] However, although not shown, depending on, for example, the materials constituting the material, the mandrel, the sleeve and / or the container, and the conditions of the extrusion process such as the pressing load and / or the pressing speed, etc., a so-called "settling phenomenon" may occur as the extrusion process progresses. In this case, due to the plastic flow of the material constituting the material and / or the elastic deformation of the container, etc., the material expands outward in the radial direction and contracts in the axial direction, and the bottom of the first hollow hole formed in the material is slightly displaced toward the base end side. Therefore, even if there is a gap between the bottom of the first hollow hole of the material and the end portion on the tip side of the mandrel at the second time point, the gap may disappear or shrink due to the above-described settling phenomenon.

[0044] As the extrusion process proceeds, the tip end of the mandrel 41 eventually reaches the base end of the inner diameter reduced portion PDIT of the container hole HC1. The period up to the first point in time when the tip end of the mandrel 41 reaches the base end of the inner diameter reduced portion PDIT of the container hole HC1 corresponds to the second step, and the period after the first point in time corresponds to the third step.

[0045] FIG. 4B is a schematic cross-sectional view showing an example of the shape of the blank 21 immediately after the end of the second step, i.e., immediately after the start of the third step, and the positional relationship between the blank 21 and the mandrel 41, sleeve 51, and container 61. In the third step, the sleeve 51 and mandrel 41 continue to move in the extrusion direction while maintaining the tip-to-tip distance DT at the first distance D1 even after the first time point. As a result, the first hollow portion PH1 of the blank 21 is pushed from the tip side into the small inner diameter portion PDIS through the inner diameter reduction portion PDIT of the container hole HC1, and extrusion processing is performed from a part of the tip side of the first hollow portion PH1 of the blank 21 into the fourth hollow portion PH4 and the third hollow portion PH3 of the differential thickness pipe 31. Also, as described above, the part of the first hollow portion PH1 of the blank 21 that was not subjected to the extrusion processing in the third step becomes the second hollow portion PH2 of the differential thickness pipe 31.

[0046] Furthermore, the second outer diameter DO2, which is the outer diameter of the fourth hollow portion PH4 of the differential wall pipe 31, is smaller than the first outer diameter DO1, which is the outer diameter of the first hollow portion PH1 of the material 21 (DO2 < DO1). Also, the inner diameter of the second hollow hole HH2 of the differential wall pipe 31 is maintained as the first inner diameter DI1, which is the inner diameter of the first hollow portion PH1 of the material 21, by the mandrel 41. That is, the cross-sectional area of the fourth hollow portion PH4 of the differential wall pipe 31 is smaller than the cross-sectional area of the first hollow portion PH1 of the material 21. On the other hand, although the outer diameter of the third hollow portion PH3 of the differential wall pipe 31 changes from the first outer diameter DO1 to the second outer diameter DO2, which is smaller than the first outer diameter DO1, from the base end side toward the tip end side as described above, the inner diameter of the third hollow portion PH3 of the differential wall pipe 31 is also maintained as the first inner diameter DI1 by the mandrel 41. That is, the cross-sectional area of the third hollow portion PH3 of the differential wall pipe 31 is also smaller than the cross-sectional area of the first hollow portion PH1 of the material 21. Therefore, the lengths in the extrusion direction of the fourth hollow portion PH4 and the third hollow portion PH3 of the differential wall pipe 31 extruded from the first hollow portion PH1 of the material 21 are larger than the length in the extrusion direction of the portion of the first hollow portion PH1 of the material 21 to which the extrusion process is applied (details will be described later).

[0047] Therefore, as shown in the region surrounded by the thick broken line in Fig. 4(b), when the extrusion process from the first hollow portion PH1 of the material 21 to the fourth hollow portion PH4 and the third hollow portion PH3 of the differential wall pipe 31 is started in the third step, the bottom of the first hollow hole of the material and the end portion on the tip end side of the mandrel begin to separate from each other.

[0048] Fig. 4(c) is a schematic cross-sectional view showing an example of the shape of the differential wall pipe 31 at the end of the third step and the positional relationship between the mandrel 41, the sleeve 51, the container 61, and the differential wall pipe 31. As illustrated in Fig. 4(c), by performing the above-described first to third steps, the differential wall pipe 31 including the second hollow portion PH2, the third hollow portion PH3, the fourth hollow portion PH4, and the second solid portion PS2 having the desired shape can be easily formed from the material 21 having a simple shape.

[0049] In the second step included in the first method, as described above, the tip-to-tip distance DT, which is the relative distance in the extrusion direction between the tip end of the sleeve and the tip end of the mandrel, is maintained at a predetermined first distance D1, while the sleeve 51 and the mandrel 41 are advanced in the extrusion direction, thereby forcing the first solid portion PS1 of the raw material 21 into the small inner diameter portion PDIS through the reduced inner diameter portion PDIT of the container hole HC1, thereby performing extrusion processing from the first solid portion PS1 of the raw material 21 to the second solid portion PS2 of the differential thickness pipe 31.

[0050] On the other hand, in the third step, as described above, the bottom of the first hollow in the raw material and the end portion on the tip side of the mandrel are separated from each other. That is, in the third step, the mandrel 41 does not contribute to the extrusion process, but has the function of maintaining the cross-sectional shape of the second hollow HH2 formed in the differential thickness pipe 31 the same as that of the first hollow HH1 formed in the raw material 21 during the process in which a part on the tip side of the first hollow portion PH1 of the raw material 21 changes into the fourth hollow portion PH4 and the third hollow portion PH3 of the differential thickness pipe 31.

[0051] Here, the length in the extrusion direction (the same as the axial direction of the raw material 21) of each portion of the raw material 21 and the differential thickness pipe 31 mentioned above will be described in detail below. However, in the following description, for the purpose of facilitating understanding, it is assumed that the shapes of the bottoms of the first hollow hole HH1 formed in the raw material 21 and the second hollow hole HH2 formed in the differential thickness pipe 31 are both planes perpendicular to the axial direction. Therefore, it goes without saying that if the shapes of these bottoms are not planes perpendicular to the axial direction, corrections will be required according to the shapes.

[0052] The second hollow portion PH2, the third hollow portion PH3, and the fourth hollow portion PH4 of the differential thickness pipe 31 are formed from the first hollow portion PH1 of the raw material 21, and the second solid portion PS2 of the differential thickness pipe 31 is formed from the first solid portion PS1 of the raw material 21. Therefore, the following relationships are established between the axial length of each portion of the raw material 21 (hereinafter, may be simply referred to as "length") and the axial length of each portion of the differential thickness pipe 31.

[0053] First, the length (LPH2) of the second hollow portion PH2 of the differential thickness pipe 31 is the length of the portion that has not been subjected to extrusion processing and remains in an unprocessed state as the raw material 21 at the time when the third step is completed. Therefore, as long as it is shorter than the length (LPH1) of the first hollow portion PH1 of the raw material 21, LPH2 can be set to any size depending on the timing of completing the third step.

[0054] Next, the length (LPH3) of the third hollow portion PH3 of the differential thickness pipe 31 is automatically determined by the length (LPDIT) of the inner diameter reduced portion PDIT of the container hole HC1 formed in the container 61. Therefore, by adjusting the LPDIT in the container hole HC1 formed in the container 61, the LPH3 can be set to any size.

[0055] Next, the length (LPH4) of the fourth hollow portion PH4 of the differential thickness pipe 31 can be calculated by subtracting the volume (VPH2+VPH3) of the material constituting the second hollow portion PH2 and the third hollow portion PH3 of the differential thickness pipe 31 from the volume (VPH1) of the material constituting the first hollow portion PH1 of the blank 21, and dividing the remaining volume by the area (APH4) of the annular cross section of the fourth hollow portion PH4. Therefore, in order to obtain a desired LPH4, it is necessary to configure the blank 21, the differential thickness pipe 31, and the container hole HC1 formed in the third container 61 so that the following formula (1) is established. Note that VPH1, VPH2, and APH4 can be expressed by the following formulas (2) to (4). Note that VPH3 changes depending on the pattern of change in the outer diameter of the third hollow portion PH3 (i.e., the shape of the outline), so it is necessary to calculate it according to the shape of the third hollow portion PH3.

[0056]

number

[0057] The relationship between the length (LPS1) of the first solid portion PS1 of the blank 21 and the length (LPS2) of the solid portion PS2 of the differential thickness pipe 31 can be expressed by the following formula (5).

[0058]

number

[0059] Therefore, in order to obtain the desired LPS2, it is necessary to determine the length (LPS1) of the first solid portion of the material 21 in accordance with the first outer diameter DO1 of the material 21 and the second outer diameter DO2 of the differential thickness pipe 31 so that the following equation (6) is satisfied.

[0060]

number

[0061] <effect> As described above, by carrying out the first method including the first to third steps in the extrusion molding apparatus including the mandrel, sleeve, and container having the above-mentioned configurations, it is possible to extrude a material having a simple structure. Solid part The first method is a method for manufacturing a pipe with a solid portion having a thickness that can reduce the occurrence of defects such as cracks and / or solid portions without requiring a material with a complex shape.

[0062] Such a differential thickness pipe having a solid portion is useful as a part that is required to achieve a desired mechanical strength in the thick portion while reducing the weight of the thin portion (portion other than the thick portion). Also, for example, if a differential thickness pipe having a solid portion as described above is used as a shaft-type part that requires an oil stopper, a plug for the oil stopper becomes unnecessary, which increases the freedom in design and reduces manufacturing costs.

[0063] Second Embodiment Hereinafter, a method for extrusion molding a differential thickness pipe having a solid portion according to a second embodiment of the present invention (hereinafter, sometimes referred to as a "second method") will be described with reference to the drawings.

[0064] As described above, in the first method, the tip-to-tip distance, which is the relative distance in the extrusion direction between the tip end of the sleeve and the tip end of the mandrel, is maintained at a predetermined first distance, while the sleeve and the mandrel are advanced in the extrusion direction, so that the material is pushed into the small inner diameter portion through the reduced inner diameter portion of the container hole, thereby performing the extrusion process. As a result, in the third step in which a part on the tip side of the first hollow portion PH1 of the material 21 is extruded into the fourth hollow portion PH4 and the third hollow portion PH3 of the differential thickness pipe 31, the bottom of the first hollow hole of the material and the tip end of the mandrel are separated from each other. That is, in the third step, the mandrel does not contribute to the extrusion process, but has the function of maintaining the cross-sectional shape of the hollow hole in the process in which the first hollow hole formed in the material changes into the second hollow hole formed in the differential thickness pipe 31.

[0065] As a result, Solid part In other words, according to the first method, a pipe with a thickness difference having a solid portion can be easily manufactured while reducing the occurrence of defects such as cracks and / or solid portions, without requiring a material with a complex shape.

[0066] However, as described above, depending on the materials constituting the raw material, the mandrel, the sleeve, and / or the container, and the extrusion conditions such as the pressing load and / or the pressing speed, the so-called "upsetting phenomenon" may occur at the time when the raw material starts to be pushed into the small inner diameter part through the reduced inner diameter part of the container hole formed in the container (i.e., at the start of the extrusion process). In this case, the raw material expands radially outward and contracts axially due to the plastic flow of the material constituting the raw material and / or the elastic deformation of the container, and the bottom of the first hollow hole formed in the raw material is slightly displaced toward the base end. As a result, the tip end of the mandrel is pressed toward the base end by the bottom of the first hollow hole, and the reaction of this applies stress to the bottom of the first hollow hole, which may cause a crack to occur at the boundary between the bottom of the first hollow hole and the side wall part.

[0067] <composition> Therefore, the second method is the above-mentioned first method, characterized in that at least at a second time point, which is a start time point of the extrusion processing in the second step, the bottom of the first hollow hole of the material is not in contact with the mandrel. Solid part The present invention relates to an extrusion molding method for a pipe having a different thickness.

[0068] Fig. 5 is a schematic cross-sectional view showing an example of the positional relationship between the bottom of the first hollow hole HH1 in the raw material 21 and the mandrel near the bottom of the first hollow hole in the raw material at the start of the second step included in the second method, and is an enlarged view of the area surrounded by the thick dashed line in (a) of Fig. 4. As illustrated in Fig. 5, in the second method, at least at the time when the sleeve 51 (not shown) and the mandrel 41 start to move in the extrusion direction (second time point), the bottom of the first hollow hole HH1 in the raw material 21 is not in contact with the mandrel 41. Specifically, in the example shown in Fig. 5, a gap G is provided between the bottom of the first hollow hole HH1 in the raw material 21 and the mandrel 41.

[0069] As a result, even if the upsetting phenomenon occurs at the start of extrusion in the second step and the bottom of the first hollow hole formed in the material is displaced toward the base end as described above, the possibility of the bottom of the hollow hole pressing against the tip of the mandrel can be reduced. As a result, the risk of cracks occurring at the boundary between the bottom of the first hollow hole and the side wall portion due to the reaction of the pressing of the bottom of the first hollow hole against the tip of the mandrel can be reduced.

[0070] In the raw material 21 illustrated in FIG. 5, the bottom (end portion on the tip side) of the first hollow hole HH1 has a conical shape. Therefore, in the example illustrated in FIG. 5, the distance between the average position in the axial direction of the bottom surface of the first hollow hole HH1 of the raw material 21 and the tip surface of the mandrel 41 is adopted as the gap G between the bottom of the first hollow hole HH1 of the raw material 21 and the mandrel 41. However, the shape of the bottom of the first hollow hole HH1 is not limited to this, and can be various shapes depending on, for example, the use of the differential thickness pipe 31 and / or the shape of the end portion on the tip side of the mandrel. For example, the shape of the bottom of the first hollow hole HH1 may be a plane perpendicular to the axial direction of the raw material 21, or may be a curved surface (for example, a spherical surface) that is convex toward the tip side.

[0071] <effect> As described above, according to the second method, even if the upsetting phenomenon occurs at the start of the extrusion process in the second step and the bottom of the first hollow hole formed in the material is displaced toward the base end, the possibility of the bottom of the hollow hole pressing against the tip of the mandrel can be reduced. As a result, the risk of cracks occurring at the boundary between the bottom and the sidewall of the first hollow hole due to the reaction of the bottom of the first hollow hole pressing against the tip of the mandrel can be reduced.

[0072] Third Embodiment Hereinafter, a method for extrusion molding a differential thickness pipe having a solid portion according to a third embodiment of the present invention (hereinafter, sometimes referred to as the "third method") will be described with reference to the drawings.

[0073] As described above, in the second method, the bottom of the first hollow hole in the raw material is not in contact with the mandrel at least at the time when the sleeve and mandrel start to move in the extrusion direction (the second time point). Therefore, according to the second method, even if the upsetting phenomenon occurs at the start of the extrusion process in the second step and the bottom of the first hollow hole formed in the raw material is displaced toward the base end, the possibility of the bottom of the hollow hole pressing against the tip of the mandrel can be reduced. As a result, the risk of cracks occurring at the boundary between the bottom of the first hollow hole and the side wall portion due to the reaction of the bottom of the first hollow hole pressing against the tip of the mandrel can be reduced.

[0074] However, if the gap G (initial gap) between the bottom of the first hollow of the raw material and the mandrel at the second time point is too small, it may not be possible to sufficiently reduce the risk of cracks occurring at the boundary between the bottom and the side wall of the first hollow. Therefore, it is considered desirable to set the initial gap to be sufficiently large in order to sufficiently reduce the risk of cracks occurring at the boundary between the bottom and the side wall of the first hollow. However, as a result of further research by the present inventor, it was found that even if the initial gap is too large, it may not be possible to sufficiently reduce the risk of cracks occurring at the boundary between the bottom and the side wall of the first hollow, depending on, for example, the materials constituting the raw material, the mandrel, the sleeve, and / or the container, and the extrusion processing conditions, such as the pressing load and / or the pressing speed. In other words, there is a suitable range for the initial gap to sufficiently reduce the risk of cracks occurring at the boundary between the bottom and the side wall of the first hollow.

[0075] <composition> Therefore, a third method is the above-mentioned second method, characterized in that the initial length, which is the length of the initial gap in the extrusion direction, is equal to or longer than a predetermined first length and is shorter than a predetermined second length that is longer than the first length. Solid part The initial gap is a gap between the bottom of the first hollow hole of the material and the end of the mandrel on the tip side at the second point in time.

[0076] The first length can be determined based on the magnitude of dimensional change of the material during a period from the second time point to a third time point, which is the time point when the tip end of the material starts to enter the portion of the container hole with a reduced inner diameter. Preferably, the first length can be determined based on the magnitude of displacement of the bottom of the first hollow hole toward the base end during a period from the second time point to the third time point. The magnitude of such dimensional change of the material, such as the displacement of the bottom of the first hollow hole toward the base end, can be determined, for example, by verification in advance through a preliminary experiment and / or a computer simulation such as a flow analysis.

[0077] On the other hand, the second length is a predetermined length from the second point (a predetermined length from the point when the tip end of the mandrel passes through the reduced inner diameter portion of the container hole). Time 4 The second length can be set to a predetermined length equal to or less than the maximum length at which the material constituting the blank does not flow into the first gap, which is the gap between the bottom of the first hollow hole of the blank and the end of the mandrel on the tip side, during the period from the first hollow hole of the blank to the end of the mandrel on the tip side. This second length can also be specified, for example, by verification in advance by a preliminary experiment and / or a computer simulation such as a flow analysis.

[0078] <effect> As described above, in the third method, the initial gap is set in a suitable range to sufficiently reduce the risk of cracks occurring at the boundary between the bottom and sidewall of the first hollow hole at the time (second time point) when the sleeve and mandrel start to move in the extrusion direction. As a result, the third method makes it possible to more reliably reduce the risk of cracks occurring at the boundary between the bottom and sidewall of the first hollow hole in the material.

[0079] Fourth Embodiment As described at the beginning of this specification, the present invention relates not only to the extrusion molding method of a pipe having a different thickness and a solid portion, including the above-mentioned first to third methods, but also to an extrusion molding device of a pipe having a different thickness and a solid portion. Therefore, the extrusion molding device of a pipe having a different thickness and a solid portion according to various embodiments of the present invention will be described below.

[0080] First, an extrusion molding apparatus for a differential thickness pipe according to a fourth embodiment of the present invention (hereinafter, sometimes referred to as a "fourth apparatus") will be described.

[0081] <composition> A fourth device includes a mandrel having a predetermined shape, a sleeve having a predetermined shape, a container having a container hole which is a through hole having a predetermined shape, and a mandrel inserted into the container hole. and sleeve and a drive mechanism configured to push the mandrel into the container. As described above, the basic configuration of such an extrusion molding device is well known to those skilled in the art, and components such as the mandrel, sleeve, and container are made of materials having properties (e.g., mechanical strength, durability, etc.) that can withstand processing conditions such as the load acting on the components in the above-mentioned extrusion processing.

[0082] The fourth device performs the first to third steps listed below to produce a material having a predetermined shape. Solid part The pipe is configured to be molded by extrusion processing.

[0083] The first step is a step of inserting a raw material into the large inner diameter portion of the container hole, abutting the tip end of the raw material into the reduced diameter portion of the container hole, abutting the base end of the raw material with a sleeve, inserting a mandrel into a first hollow hole in the raw material, and fixing the tip-to-tip distance, which is the relative distance in the extrusion direction between the tip end of the sleeve and the tip end of the mandrel, to a predetermined first distance. The second step is a step of advancing the sleeve and mandrel in the extrusion direction while maintaining the tip-to-tip distance at a first distance, thereby forcing the material through the reduced inner diameter portion of the container hole and into the smaller inner diameter portion, thereby performing an extrusion process, and continuing to advance the sleeve and mandrel until the tip end of the mandrel reaches the base end of the reduced inner diameter portion of the container hole at the first point in time. The third step is a step of advancing the sleeve and the mandrel in the extrusion direction while maintaining the tip-to-tip distance at the first distance after the first point in time.

[0084] The details of the first to third steps have already been described in the description of the first method, and therefore will not be described here.

[0085] As already explained with reference to Fig. 1, the blank 21 is a member having a cylindrical shape consisting of a first hollow portion PH1 and a first solid portion PS1 and having a first outer diameter DO1, which is a predetermined outer diameter, as a whole. The first hollow portion PH1 is a cylindrical portion having a first wall thickness T1, in which a first hollow hole HH1, which is a cylindrical space having a first inner diameter DI1, which is a predetermined inner diameter, is formed and opens to an end face on the base end side, which is the upstream side in the extrusion direction. The first solid portion PS1 is a cylindrical portion located between the end face on the tip end side, which is the downstream side in the extrusion direction, and the first hollow portion PH1.

[0086] The differential thickness pipe 31 is a member consisting of a second hollow portion PH2, a third hollow portion PH3, a fourth hollow portion PH4, and a second solid portion PS2. The second hollow portion PH2 is a cylindrical portion having a first outer diameter DO1 and a first wall thickness T1. The third hollow portion PH3 is a tubular portion adjacent to the tip side of the second hollow portion PH2, the outer diameter of which changes from the first outer diameter DO1 to a second outer diameter DO2, which is a predetermined outer diameter smaller than the first outer diameter DO1, from the base end side to the tip side, and the wall thickness of which changes from the first wall thickness T1 to a second wall thickness T2, which is a predetermined wall thickness smaller than the first wall thickness T1. The fourth hollow portion PH4 is a cylindrical portion adjacent to the tip side of the third hollow portion PH3, the second outer diameter DO2 and the second wall thickness T2. The second solid portion PS2 is a columnar portion located between the tip side end and the fourth hollow portion PH4, and has a second outer diameter DO2. Furthermore, a second hollow hole HH2, which is a cylindrical space that opens to the end face on the base end side and has a first inner diameter DI1, is formed continuously from the second hollow portion PH2 to the fourth hollow portion PH4.

[0087] 2, the mandrel 41 is a cylindrical member that is coaxially and axially slidably fitted into the sleeve 51 and has a third outer diameter DO3 that is a predetermined outer diameter corresponding to the first inner diameter DI1 that is the inner diameter of the first hollow portion PH1 of the raw material 21. The sleeve 51 is coaxially and axially slidably fitted into the mandrel 41 and has a second inner diameter DI2 that is a predetermined inner diameter corresponding to the third outer diameter DO3 that is the outer diameter of the mandrel 41, and a first outer diameter DO1 that is the outer diameter of the raw material 21.

[0088] The container hole HC1 formed in the container 61 is composed of a large inner diameter portion PDIL, a small inner diameter portion PDIS, and an inner diameter decreasing portion PDIT. The large inner diameter portion PDIL is a portion formed on the base end side and has a third inner diameter DI3 which is an inner diameter corresponding to the first outer diameter DO1 which is the outer diameter of the blank 21. The small inner diameter portion PDIS is a portion formed on the tip end side and has a fourth inner diameter DI4 which is an inner diameter corresponding to the second outer diameter DO2 which is the outer diameter of the fourth hollow portion PH2 and the second solid portion PS2 of the differential thickness pipe 31. The inner diameter decreasing portion PDIT is a portion formed between the large inner diameter portion PDIL and the small inner diameter portion PDIS and the inner diameter decreases from the third inner diameter DI3 to the fourth inner diameter DI4 as it approaches the small inner diameter portion PDIS from the large inner diameter portion PDIL.

[0089] As described above, the fourth apparatus is an extrusion molding apparatus for a differential thickness pipe having a solid portion, which corresponds to the above-mentioned first method. Therefore, the differential thickness pipe molded by the fourth apparatus, the raw material from which the differential thickness pipe is molded and the raw material from which the raw material is derived, and the mandrel, sleeve, and container constituting the fourth apparatus are clear from the above-mentioned explanation of the first method, and therefore will not be described here.

[0090] <effect> By carrying out the first to third steps in the fourth device having the above-mentioned configuration, a material having a simple structure can be produced. Solid partIn other words, the fourth apparatus is a manufacturing apparatus for a pipe with a solid portion and a thickness difference that can reduce the occurrence of defects such as cracks and / or solid portions without requiring a material with a complex shape.

[0091] Fifth Embodiment Next, an extrusion molding apparatus for a variable thickness pipe having a solid portion according to a fifth embodiment of the present invention (hereinafter, sometimes referred to as a "fifth apparatus") will be described.

[0092] <composition> The fifth device is the fourth device described above, characterized in that at least at a second time point, which is a start time point of the extrusion process in the second step, the bottom of the first hollow hole of the material is not in contact with the mandrel. Solid part The present invention relates to an extrusion molding apparatus for a pipe with different thicknesses.

[0093] As described above, the fifth apparatus is an extrusion molding apparatus for a pipe having a solid portion and a different thickness, which corresponds to the second method described above. Therefore, the details of the configuration and operation of the fifth apparatus are clear from the explanation of the second method, and therefore will not be explained here.

[0094] <effect> According to the fifth device, even if the upsetting phenomenon occurs at the start of the extrusion process in the second step and the bottom of the first hollow hole formed in the material is displaced toward the base end, the possibility of the bottom of the hollow hole pressing against the tip of the mandrel can be reduced. As a result, the risk of cracks occurring at the boundary between the bottom of the first hollow hole and the side wall portion due to the reaction of the pressing of the bottom of the first hollow hole against the tip of the mandrel can be reduced.

[0095] Sixth Embodiment Next, an extrusion molding apparatus for a variable thickness pipe having a solid portion according to a sixth embodiment of the present invention (hereinafter, sometimes referred to as a "sixth apparatus") will be described.

[0096] <composition> A sixth device is the fifth device described above, characterized in that an initial length, which is a length of the initial gap in the extrusion direction, is equal to or longer than a predetermined first length and is shorter than a predetermined second length longer than the first length. Solid part The extrusion molding method for producing a pipe with a differential thickness having the above structure is as follows: the initial gap is the gap between the bottom of the first hollow hole of the material at the second time point and the tip end of the mandrel. The first length can be determined based on the magnitude of the dimensional change of the material during the period from the second time point to a third time point, which is the time point when the tip end of the material starts to enter the portion of the container hole with a reduced inner diameter. The second length is determined based on the magnitude of the dimensional change of the material during the period from the second time point (which is a predetermined time point after the tip end of the mandrel passes through the portion of the container hole with a reduced inner diameter). Time 4 The length can be set to a predetermined length that is less than the maximum length at which the material constituting the raw material does not flow into the first gap, which is the gap between the bottom of the first hollow hole of the raw material and the tip end of the mandrel, during the period from

[0097] As described above, the sixth apparatus is an extrusion molding apparatus for a pipe having a solid portion and a different thickness, which corresponds to the third method described above. Therefore, the details of the configuration and operation of the sixth apparatus are clear from the explanation of the third method, and therefore will not be explained here.

[0098] <effect> In the sixth device, the initial gap is set in a suitable range to sufficiently reduce the risk of cracks occurring at the boundary between the bottom and the side wall of the first hollow hole at the time (second time point) when the sleeve and mandrel start to move in the extrusion direction. As a result, the sixth device can more reliably reduce the risk of cracks occurring at the boundary between the bottom and the side wall of the first hollow hole in the material.

[0099] For the purpose of explaining the present invention, several embodiments having specific configurations have been described above, sometimes with reference to the attached drawings. However, the scope of the present invention should not be construed as being limited to these exemplary embodiments, and it goes without saying that appropriate modifications can be made within the scope of the claims and the matters described in the specification. [Explanation of symbols]

[0100] 11...raw material, 21...material, 31...different thickness pipe, 41...mandrel, 51...sleeve, 61...container, DO1...first outer diameter, DO2...second outer diameter, DO3...third outer diameter, DI1...First inner diameter, DI2...Second inner diameter, DI3...Second inner diameter, DI4...Second inner diameter, HH1...first hollow hole, HH2...second hollow hole, T1...first wall thickness, T2...second wall thickness, PH1...first hollow part, PH2...second hollow part, PH3...third hollow part, PH4...fourth hollow part, PS1: first solid part; PS2: second solid part; HC1: container hole, PDIL: large inner diameter portion, PDIS: small inner diameter portion, PDIT: reduced inner diameter portion, and G...Void.

Claims

1. 1. An extrusion molding method for forming a differential thickness pipe having a solid portion from a material having a predetermined shape by extrusion processing in an extrusion molding apparatus including a mandrel having a predetermined shape, a sleeve having a predetermined shape, a container having a container hole which is a through hole having a predetermined shape, and a drive mechanism configured to push the mandrel and the sleeve into the container hole, the blank is a member having a cylindrical outer shape having a first outer diameter that is a predetermined outer diameter as a whole, the blank being made up of a first hollow portion that is a cylindrical portion having a first wall thickness and a first hollow hole that is a cylindrical space that opens into an end face on a base end side that is an upstream side in the extrusion direction and has a first inner diameter that is a predetermined inner diameter, and a first solid portion that is a cylindrical portion located between an end face on a tip end side that is a downstream side in the extrusion direction and the first hollow portion, the third hollow portion is a tubular portion adjacent to the tip side of the second hollow portion, the outer diameter of which changes from the first outer diameter to a second outer diameter that is a predetermined outer diameter smaller than the first outer diameter from the base end side to the tip side, and the wall thickness of which changes from the first wall thickness to a second wall thickness that is a predetermined wall thickness smaller than the first wall thickness; a fourth hollow portion is a tubular portion adjacent to the tip side of the third hollow portion, the second outer diameter and the second wall thickness; and a second solid portion is a cylindrical portion located between the tip side end and the fourth hollow portion and has the second outer diameter, and a second hollow hole is a cylindrical space that opens into an end face on the base end side and has the first inner diameter and is continuously formed from the second hollow portion to the fourth hollow portion, the mandrel is a cylindrical member that is coaxially fitted into the sleeve so as to be slidable in the axial direction and has a third outer diameter that is a predetermined outer diameter corresponding to the first inner diameter, the sleeve is a cylindrical member that is fitted coaxially around the mandrel and slidably in the axial direction, and has a second inner diameter that is a predetermined inner diameter corresponding to the third outer diameter, and the first outer diameter; the container hole comprises: a large inner diameter portion formed on the base end side and having a third inner diameter which is an inner diameter corresponding to the first outer diameter; a small inner diameter portion formed on the tip end side and having a fourth inner diameter which is an inner diameter corresponding to the second outer diameter; and an inner diameter decreasing portion formed between the large inner diameter portion and the small inner diameter portion and whose inner diameter decreases from the third inner diameter to the fourth inner diameter as the large inner diameter portion approaches the small inner diameter portion, a first step of inserting the raw material into the large inner diameter portion of the container hole, abutting the tip end of the raw material against the reduced inner diameter portion of the container hole, abutting the sleeve against the base end of the raw material, inserting the mandrel into the first hollow hole of the raw material, and fixing a tip-to-tip distance, which is a relative distance in the extrusion direction between the tip end of the sleeve and the tip end of the mandrel, to a predetermined first distance; a second step of advancing the sleeve and the mandrel in the extrusion direction while maintaining the tip-to-tip distance at the first distance by cooperatively driving the mandrel and the sleeve, thereby forcing the material into the small inner diameter portion through the reduced inner diameter portion of the container hole, and continuing to advance the sleeve and the mandrel until a first time point at which the tip end of the mandrel reaches the base end of the reduced inner diameter portion of the container hole; and a third step of advancing the sleeve and the mandrel in the extrusion direction while maintaining the tip-to-tip distance at the first distance even after the first point in time; Including, At least at a second time point, which is a start time point of the extrusion process in the second step, a bottom of the first hollow hole of the material is not in contact with the mandrel. A method for extrusion molding a pipe having a solid portion and a different thickness, comprising the steps of:

2. 2. A method for extruding a pipe having a solid portion according to claim 1, comprising the steps of: an initial length, which is a length in the extrusion direction of an initial gap, which is a gap between a bottom of the first hollow hole of the raw material and an end portion of the mandrel on the tip side at the second time point, is equal to or greater than a predetermined first length and is shorter than a predetermined second length which is longer than the first length; the first length is determined based on a magnitude of a dimensional change of the blank during a period from the second time point to a third time point at which the tip end of the blank starts to enter the reduced diameter portion of the container hole; the second length is set to a predetermined length equal to or less than a maximum length at which the material constituting the blank does not flow into a first gap, which is a gap between a bottom of the first hollow hole of the blank and an end portion of the mandrel on the tip side, during a period from the second time point to the first time point; A method for extrusion molding a pipe having a solid portion and a different thickness, comprising the steps of:

3. a mandrel having a predetermined shape, a sleeve having a predetermined shape, a container having a container hole which is a through hole having a predetermined shape, and a drive mechanism configured to push the mandrel and the sleeve into the container hole, The pipe is configured to be extruded to form a pipe having a solid portion from a material having a predetermined shape. An extrusion molding apparatus, the blank is a member having a cylindrical outer shape having a first outer diameter that is a predetermined outer diameter as a whole, the blank being made up of a first hollow portion that is a cylindrical portion having a first wall thickness and a first hollow hole that is a cylindrical space that opens into an end face on a base end side that is an upstream side in the extrusion direction and has a first inner diameter that is a predetermined inner diameter, and a first solid portion that is a cylindrical portion located between an end face on a tip end side that is a downstream side in the extrusion direction and the first hollow portion, the third hollow portion is a tubular portion adjacent to the tip side of the second hollow portion, the outer diameter of which changes from the first outer diameter to a second outer diameter that is a predetermined outer diameter smaller than the first outer diameter from the base end side to the tip side, and the wall thickness of which changes from the first wall thickness to a second wall thickness that is a predetermined wall thickness smaller than the first wall thickness; a fourth hollow portion is a tubular portion adjacent to the tip side of the third hollow portion, the second outer diameter and the second wall thickness; and a second solid portion is a cylindrical portion located between the tip side end and the fourth hollow portion and has the second outer diameter, and a second hollow hole is a cylindrical space that opens into an end face on the base end side and has the first inner diameter and is continuously formed from the second hollow portion to the fourth hollow portion, the mandrel is a cylindrical member that is coaxially fitted into the sleeve so as to be slidable in the axial direction and has a third outer diameter that is a predetermined outer diameter corresponding to the first inner diameter, the sleeve is a cylindrical member that is fitted coaxially around the mandrel and slidably in the axial direction, and has a second inner diameter that is a predetermined inner diameter corresponding to the third outer diameter, and the first outer diameter; the container hole comprises: a large inner diameter portion formed on the base end side and having a third inner diameter which is an inner diameter corresponding to the first outer diameter; a small inner diameter portion formed on the tip end side and having a fourth inner diameter which is an inner diameter corresponding to the second outer diameter; and an inner diameter decreasing portion formed between the large inner diameter portion and the small inner diameter portion and whose inner diameter decreases from the third inner diameter to the fourth inner diameter as the large inner diameter portion approaches the small inner diameter portion, a first step of inserting the raw material into the large inner diameter portion of the container hole, abutting the tip end of the raw material against the reduced inner diameter portion of the container hole, abutting the sleeve against the base end of the raw material, inserting the mandrel into the first hollow hole of the raw material, and fixing a tip-to-tip distance, which is a relative distance in the extrusion direction between the tip end of the sleeve and the tip end of the mandrel, to a predetermined first distance; a second step of advancing the sleeve and the mandrel in the extrusion direction while maintaining the tip-to-tip distance at the first distance by cooperatively driving the mandrel and the sleeve, thereby forcing the material into the small inner diameter portion through the reduced inner diameter portion of the container hole, and continuing to advance the sleeve and the mandrel until a first time point at which the tip end of the mandrel reaches the base end of the reduced inner diameter portion of the container hole; and a third step of advancing the sleeve and the mandrel in the extrusion direction while maintaining the tip-to-tip distance at the first distance even after the first point in time; The method is configured to form the differential thickness pipe by executing At least at a second time point, which is a start time point of the extrusion process in the second step, a bottom of the first hollow hole of the material is not in contact with the mandrel. An extrusion molding apparatus for a pipe having a solid portion and a different thickness, comprising:

4. 4. The extrusion molding apparatus for a pipe having a solid portion and a different thickness according to claim 3, an initial length, which is a length in the extrusion direction of an initial gap, which is a gap between a bottom of the first hollow hole of the raw material and an end portion of the mandrel on the tip side at the second time point, is equal to or greater than a predetermined first length and is shorter than a predetermined second length which is longer than the first length; the first length is determined based on a magnitude of a dimensional change of the blank during a period from the second time point to a third time point at which the tip end of the blank starts to enter the reduced diameter portion of the container hole; the second length is set to a predetermined length equal to or less than a maximum length at which the material constituting the blank does not flow into a first gap, which is a gap between a bottom of the first hollow hole of the blank and an end portion of the mandrel on the tip side, during a period from the second time point to the first time point; An extrusion molding apparatus for a pipe having a solid portion and a different thickness, comprising: