Capped Alkoxylated Alcohols

Abstract

The present invention relates to a compound having a narrow weight distribution and containing between 1 and 6 carbon atoms, a linear or branched alkyl group, a phenyl group, a benzyl group, and a carboxy functional group -COO - C3-C groups capped at the terminal portion with a group selected from a hydrocarbon group having a saccharide unit and a group having a saccharide unit 22 The present invention relates to a composition comprising a mixture of alcohol alkoxylates. The present invention also relates to a process for preparing said composition and to its use as a surfactant, in particular as a low foaming surfactant.

Description

[Technical field]

[0001] The present invention relates to the general field of alkoxylated alcohols, and more specifically to capped alkoxylated alcohols, methods for their preparation and also their use as surfactants. [Background technology]

[0002] It is now known that alcohol alkoxylates represent a group of compounds offering a wide range of properties with multiple uses as solvents, hydrotropes or surfactants, etc. As such, they constitute a class of compounds that show real industrial advantages for a great many fields of application.

[0003] Traditionally, alcohol alkoxylates are synthesized with the aid of basic catalysis, for example using potassium hydroxide, also called "potassium hydroxide catalysis" or "KOH catalysis". However, for about ten years, another type of catalyst has been presented that can be used with certain reactants and under certain conditions to obtain alkoxylates. This is the type of catalyst of double metal cyanides, also called DMC catalysts.

[0004] Already in the 1960s, patent US3359331 dealt with the ethoxylation of alcohols using catalysts based on tin and antimony, which were used in relatively large quantities in the reaction medium at temperatures below 70 °C and pressures close to atmospheric pressure. Catalysts of this type were so unstable that they could not function properly in conventional reactors, where there was a risk of deactivating the catalyst.

[0005] Many years later, reputable researchers published a study on the comparative kinetics of ethoxylation and propoxylation of 1-octanol and 2-octanol by KOH catalysis (di Serio M. et al., Ind. Eng. Chem. Res., (1996) 35, 3848-3853). The authors concluded that KOH catalysis was not satisfactory and encouraged the development of more efficient catalysts.

[0006] More recently, International Application WO2009000852 described a method for the alkoxylation of various compounds with mobile H, including alcohols, by DMC catalysis. This document teaches the need to add oxypropylene (OP) and / or oxybutylene (OB) blocks to the starting substrate before oxyethylene (OE) blocks can be grafted by DMC catalysis. The majority of the substrates are alcohols of the Neodol type (multibranched alcohols obtained by the Fischer-Tropsch process) and primary type. Moreover, the catalyst concentration used is high, about 3% by weight with respect to the starting product.

[0007] Similarly, International Application WO2012005897 discloses DMC-catalyzed alkoxylation of alcohols that involves first the addition of an OP block, followed only by the addition of an OE block.

[0008] The lack of large amounts of alcohol alkoxylates currently commercially available suggests that DMC catalysis would be difficult to carry out industrially today, especially with respect to alcohol-type substrates, but this type of catalysis may make it possible to obtain alkoxylates with entirely remarkable properties, in particular terminally capped (or end-capped) alcohol alkoxylates.

[0009] Some end-capped alkoxylates have already been described, for example those with benzyl ends in patent EP2205711 or those with carboxylic acid ends as described in international application WO2004037960.

[0010] It is well known that alkoxylation reactions give rise to mixtures of alkoxylation products containing different numbers of alkoxyl groups, and the number of alkoxyl units in the mixture of alkoxylation products most often follows a more or less broad or more or less narrow Gaussian distribution, generally characterized by the full width at half maximum of the Gaussian curve, generally statistically quantified by the 2σ value. [Prior art documents] [Patent documents]

[0011] [Patent Document 1] U.S. Pat. No. 3,359,331 [Patent Document 2] International Publication No. 2009 / 000852 [Patent Document 3] International Publication No. 2012 / 005897 [Patent Document 4] European Patent Application Publication No. 2205711 [Patent Document 5] International Publication No. 2004 / 037960 [Non-patent literature]

[0012] [Non-Patent Document 1] di Serio M. et al., Ind.Eng.Chem.Res., (1996) 35, 3848-3853 Summary of the Invention

[0013] It has now been found, quite surprisingly, that it is possible to prepare industrially in a particularly simple manner end-capped alkoxylates which exhibit entirely advantageous properties in terms of the physicochemical properties as well as the application properties.

[0014] Thus, according to a first aspect, the present invention relates to a composition comprising a mixture of end-capped alcohol alkoxylates, the composition comprising: the alcohol contains from 3 to 22, preferably from 5 to 22, more preferably from 5 to 20 and very particularly preferably from 5 to 18 carbon atoms, the weight distribution of the alkoxylates follows a monomodal distribution, the peak width value (2σ) of which is less than 7, preferably less than 6, advantageously less than 5 and more preferably less than 4, - The terminal portion is a straight or branched alkyl group containing 1 to 6 carbon atoms, a phenyl group, a benzyl group, or a carboxy-COO - It is capped with a group selected from a hydrocarbon group having a functional group and a group having a saccharide unit. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0015] Preferably, the end caps of the alcohol alkoxylates are selected from methyl, ethyl, propyl, butyl and benzyl groups, as well as alkylcarboxyl-COOH groups and their salts. Among the salts of the carboxyl functional groups which may be envisaged, to mention only the major ones, there may be mentioned the salts well known to those skilled in the art, in particular the metal, alkali metal, alkaline earth metal or ammonium salts. The sodium, potassium, calcium and ammonium salts are particularly preferred salts.

[0016] According to another embodiment, the end caps of the alcohol alkoxylates are selected from optionally functionalized alkylene carboxyls and their salts, typical non-limiting examples being represented by sulfosuccinic acid groups, in particular the sodium, potassium, calcium and ammonium sulfosuccinates.

[0017] According to yet another embodiment, the end cap of the alcohol alkoxylate is selected from groups having one sugar unit, such as glucose (for a monoglucoside), or two or more sugar units (for an alkyl polyglucoside, also known as "APG").

[0018] As mentioned above, the alcohols used as starting substrates for the alkoxylation reaction contain from 3 to 22, preferably from 5 to 22, more preferably from 5 to 20 and very particularly preferably from 5 to 18 carbon atoms. The carbon atoms may be linear, branched or partly or completely cyclic chains. According to a preferred embodiment, the alcohols are 45 g.mol -1 ~300g.mol -1 , preferably 70 g.mol -1 ~250g.mol -1 , more preferably 80 g.mol -1 ~200g.mol -1 The weight-average molar mass ranges from 0.1 to 1.0.

[0019] The alcohol used as starting substrate can be of any type and of any origin. In general, the alcohol is a primary or secondary alcohol. The alcohol can be of petroleum origin or of biological origin, for example of vegetable or animal origin. For obvious reasons of environmental protection, biological alcohols are preferred. Also, for the requirements of the present invention, it is preferred to use secondary alcohols.

[0020] When the alcohol is a primary alcohol, it may be selected from linear or branched primary alcohols, for example linear or branched primary alcohols containing from 8 to 14 carbon atoms, such as 1-octanol, 1-nonanol, 1-decanol, 1-undecanol, 1-dodecanol, 1-tridecanol or 1-tetradecanol, in particular alcohols having 10 carbon atoms such as Exxal™ 10 or alcohols having 13 carbon atoms such as Exxal™ 13 (sold by Exxon Mobile).

[0021] When the alcohol is a secondary alcohol, it can be selected from linear or branched secondary alcohols containing 3 to 22 carbon atoms and optionally containing one or more aromatic groups, representative of which are phenolic alcohols such as cardanol. According to a very particularly preferred embodiment, the secondary alcohol contains 3 to 22 carbon atoms, quite advantageously 3 to 14 carbon atoms, more preferably 6 to 12 carbon atoms. More preferably, the secondary alcohol is selected from 2-octanol and 4-methyl-2-pentanol, and very particularly preferably, the secondary alcohol is 2-octanol.

[0022] The alkoxylated repeating units are selected from ethylene oxide units, propylene oxide units and butylene oxide units, and combinations thereof.

[0023] In the sense of the present invention, the term "ethylene oxide unit" is understood to mean a unit resulting from ethylene oxide after opening of the oxirane ring. In the sense of the present invention, the term "propylene oxide unit" is understood to mean a unit resulting from propylene oxide after opening of the oxirane ring. In the sense of the present invention, the term "butylene oxide unit" is understood to mean a unit resulting from butylene oxide after opening of the oxirane ring.

[0024] According to one embodiment of the invention, the capped alcohol alkoxylates comprise a sequence comprising one or more units selected from ethylene oxide units, propylene oxide units, butylene oxide units and combinations thereof, the units being distributed randomly, alternatingly or in blocks.

[0025] According to another embodiment of the invention, the capped alcohol alkoxylate comprises ethylene oxide units and a sequence comprising one or more units selected from ethylene oxide units, propylene oxide units, butylene oxide units and combinations thereof, which units can be distributed randomly, alternatingly or in blocks, and at least one propylene oxide or butylene oxide unit is present in the sequence.

[0026] According to another preferred embodiment, the capped alcohol alkoxylate comprises at least one ethylene oxide unit and at least one propylene oxide unit distributed alternatingly, randomly or in blocks.

[0027] According to yet another preferred embodiment, the capped alcohol alkoxylate comprises at least one ethylene oxide unit and at least one butylene oxide unit distributed alternatingly, randomly or in blocks.

[0028] Another embodiment of the present invention relates to capped alcohol alkoxylates containing at least one propylene oxide unit and at least one butylene oxide unit distributed in an alternating, random or block manner.

[0029] The number of repeat units is generally between 1 and 100, preferably between 2 and 100, more preferably between 3 and 100, in particular between 3 and 80, more particularly between 3 and 75, preferably between 3 and 50 (limits included).

[0030] According to a preferred embodiment of the present invention, the number of repeating units is between 1 and 75, preferably between 2 and 75, more preferably between 3 and 75, in particular between 4 and 75, more particularly between 5 and 75, preferably between 6 and 75, more preferably between 7 and 75, preferably between 8 and 75, more preferably between 9 and 75 and very preferably between 10 and 75 (limits included).

[0031] According to another preferred embodiment, the number of repeating units is between 1 and 50, preferably between 2 and 50, more preferably between 3 and 50, in particular between 4 and 50, more particularly between 5 and 50, preferably between 6 and 50, more preferably between 7 and 50, preferably between 8 and 50, more preferably between 9 and 50 and very preferably between 10 and 50 (limits included).

[0032] According to yet another preferred embodiment, the number of repeating units is between 1 and 30, preferably between 2 and 20, more preferably between 3 and 20, advantageously between 3 and 15 (limits included).

[0033] In the compositions of the present invention, the capped alcohol alkoxylates are present according to a monomodal weight distribution, following the normal laws of statistical distribution. According to a very specific embodiment of the present invention, the composition of secondary alkoxylates exhibits a narrow monomodal weight distribution.

[0034] In this specification and claims, weight distribution is determined by analysis by gas chromatography and flame ionization detection (FID) on standard columns well known to those skilled in the art, where the various components of the composition being analyzed are separated by increasing the boiling point and by increasing the molar mass with each addition of an alkylene oxide unit. Weight distribution corresponds to the surface area percentage which is considered to be equivalent to the percentage by weight, assuming that the products are of the same chemical nature and therefore have the same response factors.

[0035] Quite surprisingly, it has been found that this very particularly narrow monomodal distribution of capped alcohol alkoxylates present in the composition according to the invention can be obtained using alkoxylation reaction in the presence of a specific catalyst that allows very good control of the alkoxylation reaction, in particular in the presence of a catalyst of double metal cyanide (DMC) type.Other known catalysts that allow access to a mixture of alkoxylates with a narrow distribution can also be used, such as acid catalysts of BF3 derivative type, calcium-based basic catalysts, hydrotalcite type catalysts, etc., in a non-limiting manner.However, for the requirements of the present invention, DMC type catalysts as described above are preferred.

[0036] This is because it has been observed that in the presence of such specific "narrow range" catalysts, the weight distribution of the alkoxylates is narrow, much narrower than when basic catalysts of the potassium hydroxide catalyst type are used.

[0037] In addition to obtaining compositions with a very broad weight distribution, it is known that reactions for the alkoxylation of substrates by conventional routes (base catalysis), especially when the substrate is an alcohol, and very particularly when the alcohol is a secondary alcohol, result in very high residual amounts of unreacted substrate.

[0038] Capping reactions carried out on such compositions with broad distributions and significant residual amounts can present implementation difficulties (reaction media that can be viscous, difficult to handle, produce poor yields, etc.) and can therefore lead in certain cases to capped alkoxylate compositions with less acceptable, indeed even poor, application properties, which perhaps explains why such capped alkoxylates have not been industrially developed so far.

[0039] On the other hand, and this is one of the very particular advantages of the present invention, the capped alcohol alkoxylates, and very specifically the capped secondary alkoxylates described herein, show a narrow distribution and, quite unexpectedly, a significant improvement in application performance qualities.In particular, when the compositions according to the invention are used as surfactants, a reduced foaming effect and better cleaning performance properties can be observed compared to the known compositions available on the market today.

[0040] It is also possible to obtain the compositions according to the invention by carrying out the above-mentioned capping reaction directly on narrow range alkoxylates that are already commercially available. Among these narrow range alkoxylates, mention may be made, for example, of Berol® sold by Nouryon.

[0041] Some of the capped alcohol alkoxylates described in this invention are novel and, as such, are within the scope of the present invention.

[0042] Thus, according to another aspect, the present invention relates to a composition comprising a mixture of capped 2-octanol alkoxylates having a narrow weight distribution with a peak width value (2σ) of less than 7, preferably less than 6, more preferably less than 5, and completely preferably less than 4.

[0043] More specifically, the present invention relates to a linear or branched alkyl group having 1 to 6 carbon atoms, a phenyl group, a benzyl group, a carboxy-COO group, etc. - The present invention relates to a composition comprising a 2-octanol alkoxylate capped with a group selected from a hydrocarbon group having a functional group and a group having a sugar unit.

[0044] Even more specifically, the present invention relates to a composition comprising: - 2-octanol ethoxylated and then capped with propylene oxide; - 2-octanol ethoxylated and then capped with butylene oxide; - 2-octanol which has been ethoxylated and / or propoxylated and then capped with an alkyl group, in particular an alkyl group selected from the group consisting of methyl, ethyl, propyl or butyl, or a benzyl group; - After ethoxylation and / or propoxylation, the carboxyl (-(CH2) n -COOH, where n is an integer between 1 and 5 inclusive, optionally an alkali metal, alkaline earth metal or ammonium, preferably Na + , K + or NH4 + 2-octanol capped with

[0045] According to a very particularly preferred embodiment, the present invention relates to a composition comprising: - 2-Octanol 2-15OE 1OP, - benzyl-capped 2-octanol 2-15OE, - methyl-capped 2-octanol 2-15OE, - Ethyl-capped 2-octanol 2-15OE, - Propyl-capped 2-octanol 2-15OE, -Butyl-capped 2-octanol 2-15OE, - 2-octanol capped with CH2-COOH 2-15OE, - 2-Octanol 2-15OE 1-15OB, - 2-Octanol 2-15OE 1-15OP, - 2-Octanol 1-6OE 1-15OP.

[0046] Another subject of the invention is a process for the preparation of a composition according to the invention defined above, comprising the following successive steps: a) reacting an alcohol with one or more alkylene oxides selected from ethylene oxide, propylene oxide, butylene oxide and mixtures thereof in the presence of at least one alkoxylation catalyst of the narrow range type, preferably of the DMC type, b) reacting the product resulting from step (a) with one or more compounds capable of end-capping.

[0047] The alkoxylation in step a) can be carried out with one or more alkylene oxides simultaneously, sequentially or alternatingly, depending on the sequence of alkoxylated units desired in the final composition.

[0048] The alkylene oxide used in the process of the invention can be of various origins, in particular "mass-balanced" alkylene oxide, in particular biobased "mass-balanced" ethylene oxide, "mass-balanced" alkylene oxide. Advantageously, the ethylene oxide used is biobased, for example, it can be obtained by oxidation of biobased ethylene derived from the dehydration of bioethanol, itself derived from corn starch, lignocellulosic materials, for example agricultural wastes such as sugar cane bagasse.

[0049] As indicated above, the alkoxylation reaction is carried out in the presence of a catalyst which leads to a narrow weight distribution of the resulting alkoxylates, preferably with the smallest possible residual amount of alcohol. Perfectly suitable catalysts belong to the group of double metal cyanide (DMC) type catalysts.

[0050] Optionally, the product resulting from step (a) can be isolated, but this is not necessary, especially since the residual content of reactant alcohol is very low and can be neglected.

[0051] The alcohol used in step a) of the process of the invention may be any alcohol known to the person skilled in the art, in particular as described above, the alcohol being selected from primary and secondary alcohols, preferably secondary alcohols, preferably 2-octanol and methylisobutylcarbinol, the preferred alcohol being 2-octanol.

[0052] 2-octanol presents very particular advantages in several respects, in particular because it is derived from a bio-based product that does not compete with human or animal food products. Furthermore, 2-octanol has a high boiling point, is biodegradable and presents a good ecotoxicological profile.

[0053] According to a preferred embodiment, an alcohol is used in step a) after drying, according to conventional techniques well known to those skilled in the art, so that the water content in said secondary alcohol is less than or equal to 200 ppm, preferably less than or equal to 100 ppm.

[0054] Preferably, the catalyst that can be used in the alkoxylation reaction of step a) of the process of the present invention can be any narrow range catalyst known to those skilled in the art, in particular a catalyst of the double metal cyanide (DMC) type. When the catalyst is of the double metal cyanide type, it can be of any nature known to those skilled in the art, for example as described in patents US6429342, US6977236 and PL398518. In particular, the catalyst used comprises zinc hexacyanocobaltate and one or more ligands, for example the catalyst sold by Covestro under the name Arcol® or the catalyst sold by Mexeo under the name MEO-DMC®.

[0055] Advantageously, the content of double metal cyanide type catalyst ranges from 1 ppm to 1000 ppm, preferably from 1 ppm to 500 ppm, preferably from 2 ppm to 300 ppm and more preferably from 5 ppm to 200 ppm relative to the content of the starting alcohol.

[0056] The reaction can be carried out under all temperature and pressure conditions known to those skilled in the art, and according to a preferred embodiment, the reaction temperature during the alkoxylation step (a) is generally between 80° C. and 200° C., preferably between 100° C. and 180° C. The reaction pressure during step (a) can range from 0.01 MPa to 3 MPa, preferably from 0.02 MPa to 2 MPa.

[0057] Preferably, the process according to the invention comprises a step of removal of residual oxides used in the alkoxylation and / or capping steps, more particularly of ethylene oxide, propylene oxide, butylene oxide and mixtures thereof used in the process according to the invention. This step can therefore be carried out after step (a) and / or after step (b), preferably after step a).

[0058] In the sense of the present invention, the term "residual oxides" is understood to mean unreacted oxides. Preferably, said step of removing the residual oxides is carried out by cooking, i.e. by maintaining a temperature ranging from 70°C to 170°C, preferably from 100°C to 160°C, in order to consume the residual oxides, and / or by a step of stripping under a flow of inert gas. Alternatively, said stripping step can be carried out under reduced pressure.

[0059] Preferably, after the removal step, the content by weight of residual oxides is generally less than or equal to 0.05%, preferably less than or equal to 0.01%, more preferably less than or equal to 0.001%, based on the total weight of the capped or uncapped alkoxylate, depending on whether this removal step is carried out before or after step b).

[0060] The end-capping or capping reaction (step b) is carried out in a conventional manner according to any method known to the skilled artisan, with or without a catalyst, for example as described in documents EP2205711 and WO2004037960. Generally, this capping reaction is carried out in a basic medium (for example KOH or NaOH) or in the presence of a catalyst of the narrow range type mentioned above, in particular of the DMC type, after the formation of an alkoxide, especially when the capping is carried out with an alkylene oxide. Typically, the alkoxylate or mixture of alkoxylates is reacted in the form of an alkoxide with a halide (for example an alkyl halide, a benzyl halide, an ω-halogenated carboxylic acid halide, etc.) or with an alkylene oxide. The reaction medium is then neutralized, the salts formed are filtered off and the expected product is recovered. If one chooses to carry out the capping reaction in the presence of a catalyst of the narrow range type, in particular of the DMC type, it is advantageous to use the same catalyst as that used in step a) (indeed, even without adding fresh catalyst) and to use the catalyst used in step a).

[0061] The process according to the invention can be carried out batchwise, semi-continuously or continuously. The skilled artisan knows how to adapt the process for the preparation of the compositions according to the invention according to the desired distribution of the sequence of alkoxylates: random, alternating or block.

[0062] Furthermore, the method according to the invention shows the advantage of synthesizing capped alcohol alkoxylates under good safety conditions, so that it can be carried out on an industrial scale, since the operating conditions with respect to temperature and pressure are controlled thanks to the method according to the invention, in particular the exothermicity of the reaction can be controlled very easily.

[0063] The capped alcohol alkoxylate composition can in most cases be used as is upon leaving the reactor without the need to provide other steps such as purification, distillation, etc. Conventional operations such as filtration, drying, purification, etc. can be carried out as necessary.

[0064] Finally, a subject of the present invention is the use of the capped alcohol alkoxylates according to the invention as surfactants in compositions, in particular as surfactants with low foaming power (low-foaming surfactants).

[0065] This is because the compositions of the invention, which are characterized by a particularly narrow weight distribution, exhibit very advantageous application properties in terms of performance.Moreover, the compositions of the invention exhibit a completely advantageous biodegradability profile, especially for low levels of alkoxylation (<8 units).

[0066] The capped alcohol alkoxylates with a narrow weight distribution make these compositions, for example, perfectly suitable for a great many fields of application, such as, but not limited to, for detergents, for cosmetics, for the flotation of ores, as lubricants, in particular for metalworking fluids, as emulsifiers, as adjuvants for bitumen applications, as wetting agents, as solvents, as coalescents, as processing aids, for deinking, as gas hydrate agglomeration inhibitors, in enhanced oil recovery, in corrosion protection, in hydraulic fracturing, in soil bioremediation, in agrochemicals (e.g. coatings for granular products, in particular fertilizers and plant protection products), and also as hydrotropes, antistatic agents, paint adjuvants, textile adjuvants, for polyols, for the manufacture of battery electrodes and electrolytes, to mention only the main fields of application, but without limitation.

[0067] Another subject of the present invention is a formulation comprising at least one composition of capped alcohol alkoxylates as defined above and one or more aqueous, organic or aqueous / organic solvents selected from water, alcohols, glycols, polyols, mineral oils, vegetable oils, waxes, etc., alone or as mixtures of two or more of the following, in all proportions:

[0068] The formulations according to the invention may also contain one or more additives and fillers well known to those skilled in the art, such as, for example but not limited to, anionic, cationic, amphoteric or nonionic surfactants, rheology modifiers, demulsifiers, deposit inhibitors, antifoaming agents, dispersants, pH control agents, colorants, antioxidants, preservatives, corrosion inhibitors, biocides and other additives, such as sulfur, boron, nitrogen or phosphorus products. The nature and amounts of the additives and fillers may vary within wide proportions depending on the nature of the application envisaged and can be easily adjusted by those skilled in the art.

[0069] The invention will now be illustrated by the following non-limiting examples. EXAMPLES

[0070] The 2-octanol (CAS RN123-96-6) used was Oleris® (purity >99%), a “purified” grade of 2-octanol sold by Arkema France.

[0071] Example A: Comparison between KOH and DMC catalysis To illustrate the narrow distribution effect obtained with DMC catalysis, in comparison with basic potassium hydroxide catalysis, tests of the alkoxylation of 2-octanol at a ratio of 1 mole of 2-octanol per 2 moles of propylene oxide are carried out under the same operating conditions, one with KOH catalyst and the other with DMC catalyst.

[0072] In both cases the 2-octanol is dried beforehand (less than 1000 ppm for KOH and less than 200 ppm for DMC). The amount of catalyst is equal to 2500 ppm KOH on the one hand and 100 ppm DMC on the other hand. The reaction is carried out in an autoclave at a temperature between 130 and 170 °C and a pressure between 0.15 and 0.6 MPa. The results of the weight distribution of the alkoxylate compounds, measured by gas chromatography and expressed as a percentage of the surface area of ​​the peak of each alkoxylate, are given in Table 1 below.

[0073] [Table 1]

[0074] In this example, it can be seen that for DMC catalysis the distribution is generally centered around a number of OP units equal to 2. It is also noted that the residual amount of alcohol (number of OP=0) is significantly lower for DMC catalysis than for KOH catalysis.

[0075] Furthermore, the calculated 2σ value for the values ​​resulting from base catalysis is 5.0, whereas the calculated 2σ value for the values ​​resulting from DMC catalysis is 2.9.

[0076] [Example 1: Synthesis of 2-octanol 6OE 4OP in DMC catalysis] 750 g (5.76 mol) of 2-octanol, dried to less than 200 ppm moisture, and 0.11 g (150 ppm) of DMC catalyst Arcol® are charged into a clean and dry 4 L autoclave. The reactor is closed, purged with nitrogen and checked for leak tightness under pressure. The reactor is pressurized with nitrogen. The reaction medium is started by bringing it to 90° C., with stirring. 30 g of ethylene oxide are introduced at 120° C. When the start of the reaction is observed, the remaining ethylene oxide is introduced, ie a total of 1520 g (34.56 mol), at a temperature of about 140° C., over a period of 2 hours and 50 minutes. At the end of the addition, the temperature is maintained for 30 minutes and then the residual ethylene oxide is removed with nitrogen. The reactor is cooled to 80° C. and the expected products, namely 2-octanol 6OE(I OH : 138 mg KOH / g, 77 Hz coloring) Take out 1000 g.

[0077] 20 g of propylene oxide are introduced into the 1270 g (3.22 mol) of 2-octanol 6OE remaining in the reactor at a temperature of 130° C. When the start of the reaction is observed, the remaining propylene oxide, i.e. a total of 747 g (12.9 mol), is introduced over a period of 55 minutes at a temperature of about 140° C. At the end of the addition, the temperature is maintained for 30 minutes and then the residual propylene oxide is removed with nitrogen.

[0078] At the end of the reaction, 2015 g of clear 2-octanol 6OE 4OP is collected at 50° C. (I OH : 86 mg KOH / g, 10 Hz coloration).

[0079] Example 2: Synthesis of 2-octanol 6OE 4OB by DMC catalysis 500 g (3.84 mol) of 2-octanol, dried to less than 200 ppm moisture, and 0.075 g (150 ppm) of DMC catalyst Arcol® are charged into a clean and dry 4 L autoclave. The reactor is closed, purged with nitrogen and checked for leak tightness under pressure. The reactor is pressurized with nitrogen. The reaction medium is started by bringing it to 90° C., with stirring. At a temperature of 120° C., 25 g of ethylene oxide are introduced. When the start of the reaction is observed, the remaining ethylene oxide, i.e. 1015 g (23 mol) in total, is introduced at a temperature of about 140° C., over a period of 2 hours. At the end of the addition, the temperature is maintained for 30 minutes and then the residual butylene oxide is removed with nitrogen. The reactor is cooled to 80° C. and the product, i.e. 2-octanol 6OE(I OH 1000 g of butylene oxide (coloring: 140 mg KOH / g and 50 Hz) are removed. 20 g of butylene oxide are introduced into the 513 g (1.3 mol) of 2-octanol 6OE remaining in the reactor at a temperature of 130° C. When the start of the reaction is observed, the remaining butylene oxide is introduced over 45 minutes, i.e. 375 g (5.2 mol) in total, at a temperature of about 140° C. At the end of the addition, the temperature is maintained for 30 minutes and then the residual butylene oxide is removed with nitrogen.

[0080] At the end of the reaction, 880 g of clear 2-octanol 6OE 4OB is recovered at 50° C. (I OH : 81 mg KOH / g and 20 Hz coloration).

[0081] [Example 3: Synthesis of 2-octanol 13OE benzyl ether in DMC catalysis] 500 g (3.84 mol) of 2-octanol, dried to less than 200 ppm moisture, and 0.075 g (150 ppm) of DMC catalyst Arcol® are charged into a clean and dry 4 L autoclave. The reactor is closed, purged with nitrogen and checked for leak tightness under pressure. The reactor is pressurized with nitrogen. The reaction medium is started by bringing it to 90° C., with stirring. 30 g of ethylene oxide are introduced at 120° C. When the start of the reaction is observed, the remaining ethylene oxide, i.e. 2200 g (50 mol) in total, is introduced over 3 hours at a temperature of about 140° C. At the end of the addition, the temperature is maintained for 30 minutes and then the residual ethylene oxide is removed with nitrogen. The reactor is cooled to 80° C. and 2700 g of product, i.e. 2-octanol 13OE(I OH The product is a white solid at ambient temperature.

[0082] 2106 g (3 mol) of the 2-octanol 13OE obtained above and 10 g of water are charged into a 4 L glass reactor equipped with a mechanical stirrer, heating means, a dropping funnel for the introduction of solids and an inerting system with nitrogen. The reaction medium is brought to 90 ° C while being sparged with nitrogen to deoxygenate the reaction medium. Nitrogen is then introduced into the head space of the reactor and 132 g (3.3 mol) of sodium hydroxide beads are added, i.e. a 15% excess. The medium is then brought to 100 ° C-105 ° C, the pressure is reduced to about 300 mbar and the water is distilled off. The criterion for stopping is a water content of less than 1.5%. The reaction medium is then returned to 70 ° C and then 342 g (2.7 mol) of benzyl chloride are added over a period of about 60 minutes. The temperature is maintained at 120 ° C for 5 hours. After returning to 70 ° C, the reaction medium is neutralized with 37% hydrochloric acid until a pH of 7 is reached. The water is distilled off under reduced pressure to precipitate the sodium chloride formed, which is filtered to recover 2300 g of benzyl-capped 2-octanol 13OE.

[0083] Example 4: Synthesis of 2-octanol 9OE ether carboxylic acid in DMC catalysis 500 g (3.84 mol) of 2-octanol, dried to less than 200 ppm moisture, and 0.075 g (150 ppm) of DMC catalyst Arcol® are charged into a clean and dry 4 L autoclave. The reactor is closed, purged with nitrogen and checked for leak tightness under pressure. The reactor is pressurized with nitrogen. The reaction medium is started by bringing it to 90° C., with stirring. At a temperature of 120° C., 25 g of ethylene oxide are introduced. When the start of the reaction is observed, the remaining ethylene oxide is introduced, i.e., a total of 1520 g (34.56 mol), at a temperature of about 140° C., over 2 hours and 30 minutes. At the end of the addition, the temperature is maintained for 30 minutes and then the residual ethylene oxide is removed with nitrogen. The reactor is cooled to 80° C. and 2010 g of product is obtained, i.e., 2-octanol 9OE(I OH : 105 mg KOH / g, colored 35 Hz) is taken out.

[0084] 1578 g (3 mol) of 2-octanol 9OE obtained above are charged into a 3 L glass reactor equipped with a mechanical stirrer, heating means, a dropping funnel for introducing solids and an inerting system with nitrogen. The reaction medium is brought to 50° C. while being sparged with nitrogen in order to deoxygenate the reaction medium. Nitrogen is then introduced into the head space of the reactor and 126 g (3.15 mol) of sodium hydroxide beads are added. Water is distilled off under reduced pressure. 367 g (3.15 mol) of sodium monochloroacetate are then added at 50° C. At the end of the reaction, the reaction medium is neutralized with 37% hydrochloric acid. 1610 g of 2-octanol 9OE ether carboxylic acid are recovered.

[0085] Example 5: Synthesis of 1-decanol 5OE by basic KOH catalysis 500 g (3.16 mol) of biobased 1-decanol (sold by Ecogreen), dried to less than 1000 ppm moisture, and 1.5 g (3000 ppm) of potassium hydroxide (KOH) catalyst as pellets are charged into a clean and dry 4 L autoclave. The reactor is closed, purged with nitrogen and checked for leak tightness under pressure. The reactor is pressurized with nitrogen. The reaction medium is started by bringing it to 90° C., with stirring. 30 g of ethylene oxide are introduced at 120° C. When the start of the reaction is observed, the remaining ethylene oxide, i.e. 695 g (15.8 mol) in total, is introduced at a temperature of about 140° C., over a period of 1 hour. At the end of the addition, the temperature is maintained for 30 minutes and then the residual ethylene oxide is removed with nitrogen. The reactor is cooled to 80° C. and 1180 g of crude product 1-decanol 5OE is removed and neutralized with acetic acid (I OH : 153 mg KOH / g, coloring at 385 Hz).

[0086] Example 6: Synthesis of 1-decanol 5OE by DMC catalysis 500 g (3.16 mol) of biobased 1-decanol (ex Ecogreen), dried to less than 200 ppm moisture, and 0.075 g (150 ppm) of DMC catalyst (ex Mexeo) are charged into a clean and dry 4 L autoclave. The reactor is closed, purged with nitrogen and checked for leak tightness under pressure. The reactor is pressurized with nitrogen. The reaction medium is started by bringing it to 90° C., with stirring. At a temperature of 120° C., 35 g of ethylene oxide are introduced. When the start of the reaction is observed, the remaining ethylene oxide, i.e. 695 g (15.8 mol) in total, is introduced at a temperature of about 140° C., over a period of 1 hour. At the end of the addition, the temperature is maintained for 30 minutes and then the residual ethylene oxide is removed with nitrogen. The reactor is cooled to 80° C. and 1185 g of product, i.e. 1-decanol 5OE(I OH : 145 mg KOH / g and 23 Hz coloration) is taken out.

[0087] The weight distribution of the alkoxylate compounds as a percentage of the surface area of ​​each alkoxylate peak, as determined by gas chromatography, is shown below in Table 2.

[0088] [Table 2]

[0089] The calculated 2σ value for the values ​​obtained from base catalysis is 7.3, whereas the calculated 2σ value for the values ​​obtained from DMC catalysis is 3.7.

[0090] Example 7: Potassium hydroxide (KOH) catalyzed synthesis of benzylated 1-decanol 13OE Step a): Ethoxylation 500 g (3.16 mol) of biobased 1-decanol (sold by Ecogreen), dried to less than 1000 ppm moisture, and 1.5 g (3000 ppm) of solid KOH are charged to a clean and dry 4 L autoclave. The reactor is closed, purged with nitrogen and checked for leak tightness under pressure. The reactor is pressurized with nitrogen. The reaction medium is started by bringing it to 90° C., with stirring. 30 g of ethylene oxide are introduced at 120° C. When the start of the reaction is observed, the remaining ethylene oxide, i.e. 1807 g (41 mol) in total, is introduced at a temperature of about 140° C., over a period of 2 hours and 40 minutes. At the end of the addition, the temperature is maintained for 30 minutes and then the residual ethylene oxide is removed with nitrogen. The reactor is cooled to 80° C. and 2281 g of product, i.e. 1-decanol 13OE(I OH : 77 mg KOH / g, 480 Hz color on the molten product. The product is a white solid at ambient temperature.

[0091] Step b): Capping 2000 g (2.74 mol) of 1-decanol 13OE obtained in the previous step and 10 g of water are charged into a 4 L glass reactor equipped with a mechanical stirrer, heating means, a dropping funnel for the introduction of solids and an inerting system with nitrogen. The reaction medium is brought to 90 ° C while purging with nitrogen to deoxygenate the reaction medium. Nitrogen is then introduced into the head space of the reactor and then 120 g (3 mol) of sodium hydroxide beads are added. The medium is then brought to 100 ° C-105 ° C, the pressure is reduced to about 30 kPa and the water is distilled off. The criterion for stopping is a water content of less than 1.5%. The reaction medium is then returned to 70 ° C. 329 g (2.6 mol) of benzyl chloride are then added over a period of about 60 minutes. The temperature is maintained at 120 ° C for 5 hours. After returning to 70 ° C, the reaction medium is neutralized with 37% hydrochloric acid until a pH of 7 is reached. The water is distilled off under reduced pressure and the sodium chloride formed is precipitated. The latter is filtered off to recover 2195 g of benzyl-capped 1-decanol 13OE.

[0092] Example 8: Synthesis of DMC-catalyzed benzylated 1-decanol 13OE Step a): Ethoxylation 500 g (3.16 mol) of biobased 1-decanol, dried to less than 200 ppm moisture, and 0.075 g (150 ppm) of DMC catalyst, Arcol®, are charged into a clean and dry 4 L autoclave. The reactor is closed, purged with nitrogen and checked for leak tightness under pressure. The reactor is pressurized with nitrogen. The reaction medium is started by bringing it to 90° C., with stirring. At a temperature of 120° C., 35 g of ethylene oxide are introduced. When the start of the reaction is observed, the remaining ethylene oxide, i.e. 1807 g (41 mol) in total, is introduced at a temperature of about 140° C., over 2 hours and 40 minutes. At the end of the addition, the temperature is maintained for 30 minutes and then the residual ethylene oxide is removed with nitrogen. The reactor is cooled to 80° C. and 2290 g of product, i.e. 1-decanol 13OE(I OH : 75 mg KOH / g, 30 Hz coloring on the molten product. The product is a white solid at ambient temperature.

[0093] Step b): Capping 2190 g (3 mol) of the 1-decanol 13OE obtained above and 10 g of water are charged into a 4 L glass reactor equipped with a mechanical stirrer, heating means, a dropping funnel for the introduction of solids and an inerting system with nitrogen. The reaction medium is brought to 90 ° C while sparging with nitrogen to deoxygenate the reaction medium. Nitrogen is then introduced into the head space of the reactor and 132 g (3.3 mol) of sodium hydroxide beads are added. The medium is then brought to 100 ° C-105 ° C, the pressure is reduced to about 30 kPa and the water is distilled off. The criterion for stopping is a water content of less than 1.5%. The reaction medium is then brought back to 70 ° C and 366 g (2.9 mol) of benzyl chloride are added over a period of about 60 minutes. The temperature is maintained at 120 ° C for 5 hours. After returning to 70 ° C, the reaction medium is neutralized with 37% hydrochloric acid until a pH of 7 is reached. The water is distilled off under reduced pressure and the sodium chloride formed is precipitated. The latter is filtered off to recover 2390 g of benzyl-capped 1-decanol 13OE.

[0094] [Example 9: Synthesis of 2-octanol 3OE disodium sulfosuccinate monoester] 393 g (1.5 mol) of 2-octanol 3OE prepared by DMC catalysis as described in WO2019092366 are charged into a 2 L glass reactor equipped with stirrer and a system for introducing solids.

[0095] The reaction medium is brought to a temperature between 60 and 70 ° C and then 154 g (1.57 mol) of maleic anhydride are gradually introduced while maintaining this temperature and stirring. After the addition, this temperature is maintained at 70 ° C for 1 hour. The degree of esterification is then checked by quantitative determination. Then 816 g of a 20% aqueous solution of sodium hydrogen sulfite (i.e. 1.57 mol) are run in while stirring at a temperature between 75 and 90 ° C. After the addition, the reaction medium is maintained at 90 ° C. When the reaction is complete, the reaction medium is cooled, the pH is adjusted by adding sodium hydroxide solution and the reactor is emptied.

[0096] Example 10: Synthesis of 2-octanol 3OE monoglucoside 655 g (2.5 mol) of 2-octanol 3OE prepared by DMC catalysis as described in WO2019092366, 90 g (0.5 mol) of glucose and 7.45 g of para-toluenesulfonic acid, i.e. 1% of the reaction medium, are charged into a 1 L glass reactor equipped with a stirrer, a dropping funnel, an electric heating system and a vacuum setting system.

[0097] The medium is brought to 115° C. under an inert atmosphere while stirring. The assembly is then gradually placed under reduced pressure up to a value of 30 mmHg (i.e. 4 kPa). The water formed is distilled off and collected in a cold trap. The reaction is continued for about 7 hours until all the glucose is converted.

[0098] Cooling is performed and the catalyst is neutralized with sodium hydroxide. Excess ethoxylated alcohol can be recovered by vacuum distillation using WFSP (swept film short path) technology.

Claims

1. 1. A composition comprising a mixture of end-capped alcohol alkoxylates, the composition comprising: the alcohol is a secondary alcohol containing from 3 to 14 carbon atoms, the weight distribution of the alkoxylates follows a monomodal distribution, the peak width value (2σ) of which is less than 7; The terminal portion is a straight or branched alkyl group having 1 to 6 carbon atoms, a phenyl group, a benzyl group, a carboxy-COO group, － Capped with a group selected from a hydrocarbon group having a functional group and a group having a sugar unit; composition.

2. 2. The composition of claim 1, wherein the end cap of the alcohol alkoxylate is selected from a methyl group, an ethyl group, a propyl group, a butyl group, or a benzyl group, a carboxyl-COOH group and its salts, an alkylene carboxyl group and its salts which may be functionalized.

3. The composition according to claim 1 or 2, wherein the secondary alcohol is selected from 2-octanol and 4-methyl-2-pentanol.

4. The composition according to any one of claims 1 to 3, wherein the secondary alcohol is 2-octanol.

5. 5. The composition of any one of claims 1 to 4, wherein the capped alcohol alkoxylate comprises a sequence comprising one or more units selected from ethylene oxide units, propylene oxide units, butylene oxide units, and combinations thereof, the units being distributed randomly, alternatingly, or in blocks.

6. Linear or branched alkyl having 1 to 6 carbon atoms, phenyl group, benzyl group, carboxy-COO － 6. The composition according to any one of claims 1 to 5, comprising a mixture of 2-octanol alkoxylates capped with a group selected from a hydrocarbon group having a functional group and a group having a sugar unit.

7. The composition of any one of claims 1 to 6, comprising: - 2-octanol which has been ethoxylated and / or propoxylated and then capped with an alkyl or benzyl group; - After ethoxylation and / or propoxylation, the carboxyl (-(CH ２ ) ｎ 2-Octanol capped with --COOH, where n is an integer between 1 and 5, inclusive, optionally in the form of an alkali metal, alkaline earth metal or ammonium salt.

8. The composition of any one of claims 1 to 7, comprising: - benzyl capped 2-octanol 2-15OE, - methyl-capped 2-octanol 2-15OE, - ethyl capped 2-octanol 2-15OE, - propyl-capped 2-octanol 2-15OE, - butyl-capped 2-octanol 2-15OE, -CH ２ -COOH capped 2-octanol 2-15OE.

9. A process for the preparation of a composition according to any one of claims 1 to 8, comprising the successive steps of: a) reacting an alcohol with one or more alkylene oxides selected from ethylene oxide, propylene oxide, butylene oxide and mixtures thereof in the presence of at least one alkoxylation catalyst of the narrow range type; b) reacting the product resulting from step (a) with one or more compounds capable of end-capping.

10. Use of a composition according to any one of claims 1 to 8 as a surfactant.

11. 11. Use according to claim 10 in detergents, in cosmetics, for ore flotation, as a lubricant, as an emulsifier, as an adjuvant in bitumen applications, as a wetting agent, as a solvent, as a coalescent, as a processing aid, as a gas hydrate agglomeration inhibitor, for deinking, in enhanced oil recovery, in corrosion protection, in hydraulic fracturing, in soil bioremediation, in pesticides, as a hydrotrope, an antistatic agent, a paint adjuvant, a textile adjuvant or for the manufacture of electrodes and electrolytes for batteries.

12. A formulation comprising at least one composition according to any one of claims 1 to 8 and one or more aqueous, organic or aqueous / organic solvents selected from water, alcohols, glycols, polyols, mineral oils, vegetable oils, waxes and others, alone or as a mixture of two or more in all proportions.