Rare earth aluminate sintered body and method for producing same

Abstract

To provide a rare earth aluminate sintered body having high emission properties and a method for producing the same.SOLUTION: A rare earth aluminate sintered body contains rare earth aluminate phosphor crystal phases and voids, where the rare earth aluminate phosphor crystal phases of 90% or more in number have the absolute maximum length ranging from 0.4 μm or more to 1.3 μm or less, and the voids of 90% or more in number have the absolute maximum length ranging from 0.1 μm or more to 1.2 μm or less.SELECTED DRAWING: Figure 6

Description

[Technical field]

[0001] The present disclosure relates to a rare earth aluminate sintered body and a method for producing the same. [Background technology]

[0002] There is known a light emitting device that includes a light emitting diode (LED) or a laser diode (LD) and a wavelength conversion member containing a phosphor that converts the wavelength of light emitted from the LED or LD. Such light emitting devices are used as light sources for, for example, in-vehicle lighting, general lighting, backlights for liquid crystal display devices, projectors, etc.

[0003] As an example of a wavelength conversion member provided in a light emitting device, Patent Document 1 discloses a single-phase ceramic conversion member obtained by sintering a phosphor raw material containing an oxide. [Prior art documents] [Patent documents]

[0004] [Patent Document 1] JP 2017-197774 A Summary of the Invention [Problem to be solved by the invention]

[0005] There is a demand for wavelength conversion members with further improved light emission characteristics. Therefore, an object of the present disclosure is to provide a rare earth aluminate sintered body having improved luminescent properties and a method for producing the same. [Means for solving the problem]

[0006] The first aspect is a rare earth aluminate sintered body which contains a rare earth aluminate phosphor crystal phase and voids, in which 90% or more of the rare earth aluminate phosphor crystal phase has an absolute maximum length measured under the measurement conditions described below in a range of 0.4 μm or more and 1.3 μm or less, and 90% or more of the voids has an absolute maximum length measured under the measurement conditions described below in a range of 0.1 μm or more and 1.2 μm or less. Measurement conditions The absolute maximum length is defined as the distance between the two most distant points on the outline of one of the rare earth aluminate phosphor crystal phases or the voids included in the measurement range on the surface or cross section of the rare earth aluminate sintered body.

[0007] The second aspect is to add at least one rare earth element Ln selected from the group consisting of Y, La, Lu, Gd and Tb. 1 oxide particles containing Ce, oxide particles containing Al, and at least one element M selected from Ga and Sc as required. 1 The present invention includes the steps of: preparing a slurry-like raw material mixture by mixing oxide particles containing Ln into a liquid; drying the raw material mixture to obtain a raw material mixture powder; molding the raw material mixture powder to obtain a molded body; and sintering the molded body at a temperature range of 1300° C. to 1800° C. to obtain a sintered body. 1 The oxide particles containing Ce, the oxide particles containing Al, and the element M 1 At least one oxide particle selected from the oxide particles containing 2 The present invention relates to a method for producing a rare earth aluminate sintered body having a rare earth aluminate sintering ratio of 0.1 to 0.5. Effect of the Invention

[0008] According to the present disclosure, it is possible to provide a method for producing a rare earth aluminate sintered body having improved luminescence properties. [Brief description of the drawings]

[0009] [Figure 1]FIG. 1 is a flow chart of a method for producing a rare earth aluminate sintered body. [Diagram 2] FIG. 2 is a flow chart of a method for producing a rare earth aluminate sintered body. [Diagram 3] FIG. 3 is a diagram showing a schematic configuration of an example of a light emitting device. [Figure 4] FIG. 4 is a plan view showing a schematic configuration of an example of a phosphor device including a rare earth aluminate sintered body. [Diagram 5] FIG. 5 is a side view showing a schematic configuration of an example of a phosphor device. [Figure 6] FIG. 6 is an SEM image of the rare earth aluminate sintered body according to Example 1. [Figure 7] FIG. 7 is an SEM image of the rare earth aluminate sintered body according to Example 3. [Figure 8] FIG. 8 is an SEM image of the rare earth aluminate sintered body according to Example 5. [Figure 9] FIG. 9 is an SEM image of the rare earth aluminate sintered body according to Example 8. [Figure 10] FIG. 10 is an SEM image of the rare earth aluminate sintered body according to Comparative Example 1. [Figure 11] FIG. 11 is an SEM image of the rare earth aluminate sintered body according to Comparative Example 4. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0010] The rare earth aluminate sintered body and the manufacturing method thereof according to the present invention will be described below based on the embodiments. However, the embodiments shown below are merely examples for embodying the technical idea of ​​the present invention, and the present invention is not limited to the rare earth aluminate sintered body and the manufacturing method thereof. The relationship between the color name and the chromaticity coordinate, and the relationship between the wavelength range of light and the color name of monochromatic light are in accordance with JIS Z8110.

[0011] Rare earth aluminate sintered body The rare earth aluminate sintered body contains a rare earth aluminate phosphor crystal phase and voids, and in the measurement range, 90% or more of the rare earth aluminate phosphor crystal phases have an absolute maximum length in the range of 0.4 μm or more and 1.3 μm or less, and 90% or more of the voids have an absolute maximum length in the range of 0.1 μm or more and 1.2 μm or less.

[0012] Absolute maximum length measurement conditions The absolute maximum length of a rare earth aluminate phosphor crystal phase or void is defined as the distance between the two most distant points on the outline of one rare earth aluminate phosphor crystal phase or void included in the measurement range on the surface or cross section of the rare earth aluminate sintered body. In a SEM image obtained by photographing the surface or cross section of the rare earth aluminate sintered body with a scanning electron microscope (SEM), 2 The measurement range is an area where the distance between the two most distant points on the contour of one rare earth aluminate phosphor crystal phase or void in this measurement range can be measured as the absolute maximum length. In this way, the number-based distribution of the absolute maximum lengths of the individual rare earth aluminate phosphor crystal phases included in the measurement range of the surface or cross section of the rare earth aluminate sintered body can be obtained, and the ratio of the number of rare earth aluminate phosphor crystal phases whose absolute maximum length is in the range of 0.4 μm to 1.3 μm to the total number of rare earth aluminate phosphor crystal phases can be obtained. Also, the number-based distribution of the absolute maximum lengths of the individual voids included in the measurement range of the surface or cross section of the rare earth aluminate sintered body can be obtained, and the ratio of the number of voids whose absolute maximum length is in the range of 0.1 μm to 1.2 μm to the total number of voids can be obtained.

[0013] When the number of rare earth aluminate phosphor crystal phases having an absolute maximum length in the range of 0.4 μm or more and 1.3 μm or less within the measurement range of the rare earth aluminate sintered body is 90% or more, the rare earth aluminate phosphor crystal phases having an absolute maximum length of 0.4 μm or more and 1.3 μm or less are contained in large numbers, and the rare earth aluminate sintered body contains many small crystal phases. When the rare earth aluminate sintered body contains many small crystal phases of the rare earth aluminate phosphor crystal phase, the spread of light can be suppressed when incident light is wavelength-converted by the rare earth aluminate phosphor crystal phase and emitted, and the light can be extracted forward.

[0014] The absolute maximum length of the rare earth aluminate phosphor crystal phase in the rare earth aluminate sintered body measured under the above-mentioned measurement conditions is preferably within the range of 0.4 μm to 2.3 μm. Even if the rare earth aluminate phosphor crystal phase with an absolute maximum length of 2.3 μm is contained in the rare earth aluminate sintered body, if the rare earth aluminate phosphor crystal phase with an absolute maximum length of 0.4 μm to 1.3 μm is contained in 90% or more by number, the spread of the emitted light can be suppressed and the light emission characteristics can be improved. It is more preferable that the rare earth aluminate sintered body has 100% by number of rare earth aluminate phosphor crystal phases with an absolute maximum length of 0.4 μm to 1.3 μm, more preferably 99.0% or less, more preferably 98.0% or less, preferably 91.0% or more, and more preferably 92.0% or more.

[0015] The absolute maximum length of the cumulative frequency of 50% in the particle size distribution of the number-based absolute maximum length of the rare earth aluminate phosphor crystal phase is preferably in the range of 0.4 μm to 0.9 μm, and may be in the range of 0.45 μm to 0.9 μm. When the absolute maximum length of the cumulative frequency of 50% in the particle size distribution of the number-based absolute maximum length of the rare earth aluminate phosphor crystal phase is in the range of 0.4 μm to 0.9 μm, the spread of light is more suppressed when the light incident on the rare earth aluminate sintered compact is wavelength-converted by the rare earth aluminate phosphor crystal phase and emitted. The absolute maximum length of the cumulative frequency of 50% in the particle size distribution of the number-based absolute maximum length of the rare earth aluminate phosphor crystal phase can be obtained from the particle size distribution of the number-based absolute maximum length of the rare earth aluminate phosphor sintered compact described above.

[0016] When the number of voids having an absolute maximum length in the range of 0.1 μm or more and 1.2 μm or less, included in the measurement range of the rare earth aluminate sintered body, is 90% or more, when light incident on the rare earth aluminate sintered body is scattered by the voids, the spread of the light is suppressed and the light can be extracted forward.

[0017] The voids in the rare earth aluminate sintered body measured by the above-mentioned measuring method may include voids having an absolute maximum length in the range of 0.1 μm to 3.0 μm, or may include voids having an absolute maximum length in the range of 0.2 μm to 2.3 μm, as long as the number of voids having an absolute maximum length in the range of 0.1 μm to 1.2 μm is 90% or more. The voids can moderately scatter the light incident on the rare earth aluminate sintered body and suppress the spread of the emitted light. The rare earth aluminate sintered body is more preferably 100% by number of voids having an absolute maximum length in the range of 0.1 μm to 1.2 μm, more preferably 99% or less, more preferably 98% or less, preferably 90.2% or more, and more preferably 90.5% or more.

[0018] The absolute maximum length of the cumulative frequency of 50% in the particle size distribution of the absolute maximum length based on the number of voids is preferably in the range of 0.3 μm to 0.8 μm. When the absolute maximum length of the cumulative frequency of 50% in the particle size distribution of the absolute maximum length based on the number of voids in the rare earth aluminate sintered body is in the range of 0.3 μm to 0.8 μm, the light incident on the rare earth aluminate sintered body can be appropriately scattered and the spread of light when emitted can be suppressed. The absolute maximum length of the cumulative frequency of 50% in the particle size distribution of the absolute maximum length based on the number of voids in the rare earth aluminate sintered body can be obtained from the particle size distribution based on the number of absolute maximum lengths of the voids described above.

[0019] The relative density of the rare earth aluminate sintered body is preferably 92% or more, more preferably 93% or more, and even more preferably 94% or more, and may be 99% or less, or may be 98% or less. The rare earth aluminate sintered body is formed only from the rare earth aluminate sintered body and voids. When the relative density of the rare earth aluminate sintered body is within the range of 85% to 99%, the excitation light incident on the rare earth aluminate sintered body can be efficiently scattered by the voids, and the scattered light can be efficiently wavelength-converted by the rare earth aluminate phosphor crystal phase, and the wavelength-converted light can be emitted from the same surface as the surface into which the excitation light is incident.

[0020] The relative density of the rare earth aluminate sintered body can be calculated from the apparent density and true density of the rare earth aluminate sintered body by the following formula (1).

[0021]

number

[0022] The apparent density of the rare earth aluminate sintered body is the mass of the rare earth aluminate sintered body divided by the volume of the rare earth aluminate sintered body, and can be calculated by the following formula (2). The true density of the rare earth aluminate sintered body can be the true density of the rare earth aluminate phosphor.

[0023]

number

[0024] The porosity of the rare earth aluminate sintered body is the remainder obtained by subtracting the relative density of the rare earth aluminate sintered body from 100%, and is preferably in the range of 1% to 8%. If necessary, the porosity of the rare earth aluminate sintered body can be calculated by the following formula (3).

[0025]

number

[0026] The rare earth aluminate phosphor crystal phase preferably has a composition represented by the following formula (I). (Ln 1 1-n Ce n )3(Al 1-m M 1 m ) 5k O 12 (I) In the above formula (I), Ln 1 is at least one rare earth element selected from the group consisting of Y, La, Lu, Gd and Tb, M 1 is at least one element selected from Ga and Sc, and m, n, and k are numbers that satisfy 0≦m≦0.02, 0.002≦n≦0.017, and 0.95≦k≦1.05, respectively. However, the variables m, n, and k in the formula (I) are Ln 1 This is the number when the sum of the molar ratio of A and the molar ratio of Ce is 3. In this specification, the molar ratio refers to the molar ratio of each element in 1 mole of the chemical composition of the phosphor.

[0027] In the composition represented by the above formula (I), Ln 1is at least one rare earth element selected from the group consisting of Y, Gd, Lu and Tb, and may contain two or more rare earth elements. Ce is an activator element for the rare earth aluminate phosphor crystal phase, and the product of the variables n and 3 represents the molar ratio of Ce in the composition represented by formula (I). The variable n is more preferably 0.002 or more and 0.016 or less (0.002≦n≦0.016), and even more preferably 0.003 or more and 0.015 or less (0.003≦n≦0.015). In the composition represented by formula (I), the product of the variables m, 5 and k represents the molar ratio of element M 1 The molar ratio of element M 1 may not be included in the composition represented by formula (I), that is, m may be 0. In the composition represented by formula (I), in order to convert the wavelength to a desired color tone, the variable m may be 0.00001 or more and 0.02 or less (0.00001≦m≦0.02), or 0.00005 or more and 0.018 or less (0.00005≦m≦0.018). In the composition represented by formula (I), the product of the variable k and 5 is the sum of Al and the element M. 1 The variable k is more preferably 0.96 or more and 1.03 or less (0.96≦k≦1.03), and further preferably 0.97 or more and 1.02 or less (0.97≦k≦1.02).

[0028] In the rare earth aluminate sintered body, the rare earth aluminate phosphor crystal phase preferably contains Lu in its composition, the rare earth aluminate crystal phase has an absolute maximum length in the range of 0.4 μm to 2.3 μm, and the voids preferably have an absolute maximum length in the range of 0.1 μm to 2.3 μm. When the absolute maximum length is within such a range, the spread of light can be suppressed when the incident light is wavelength-converted by the rare earth aluminate phosphor crystal phase and emitted.

[0029] When the rare earth aluminate phosphor crystal phase contains Lu in its composition, it preferably has a composition represented by the following formula (Ia). (Lu 1-q-n Ln 2 q Ce n )3(Al 1-m M1 m ) 5k O 12 (Ia) In the above formula (Ia), Ln 2 is at least one rare earth element selected from the group consisting of La, Gd and Tb, M 1 is at least one element selected from Ga and Sc, and q, m, n, and k are numbers that satisfy 0≦q≦0.9, 0≦m≦0.02, 0.002≦n≦0.017, and 0.95≦k≦1.05, respectively. However, the variables m, n, and k in the formula (Ia) are the molar ratio of Lu and Ln based on analytical values. 2 The sum of the molar ratio of A and the molar ratio of Ce is 3.

[0030] The rare earth aluminate sintered body can be used as a reflective wavelength conversion member in which the incident surface (first main surface) into which the excitation light is incident and the exit surface (first main surface) from which the wavelength-changed light is emitted are the same surface. When the rare earth aluminate sintered body is used as a reflective wavelength conversion member in which the incident surface of the excitation light and the exit surface of the light are the same surface, there is no limitation on the thickness of the rare earth aluminate sintered body, and when the rare earth aluminate sintered body is a plate-shaped body, the plate thickness is preferably in the range of 90 μm to 250 μm, more preferably in the range of 100 μm to 240 μm.

[0031] In the rare earth aluminate sintered body, the rare earth aluminate phosphor crystal phase contains Y in its composition, and the absolute maximum length of the rare earth aluminate phosphor crystal phase is preferably in the range of 0.4 μm to 2.1 μm, and the absolute maximum length of the void is preferably in the range of 0.1 μm to 3.0 m. When the absolute maximum length is within such a range, a desired luminescent color can be obtained, and the spread of light can be suppressed when the incident light is wavelength-converted by the rare earth aluminate phosphor crystal phase and emitted.

[0032] When the rare earth aluminate phosphor crystal phase contains Y in its composition, it preferably has a composition represented by the following formula (Ib). (Y 1-p-n Ln 3p Ce n )3(Al 1-m M 1 m ) 5k O 12 (Ib) In the above formula (Ib), Ln 3 is at least one rare earth element selected from the group consisting of La, Gd and Tb, M 1 is at least one element selected from Ga and Sc, and p, m, n, and k are numbers that satisfy the following conditions: 0≦p≦0.9, 0≦m≦0.02, 0.002≦n≦0.017, and 0.95≦k≦1.05, respectively. However, the variables m, n, and k in the above formula (Ib) are the molar ratio of Y and Ln 3 The sum of the molar ratio of A and the molar ratio of Ce is 3.

[0033] In the rare earth aluminate sintered body formed in a plate shape, when the incident surface on which the excitation light is incident and the exiting surface from which the light is emitted are the same surface, the light diameter of the exiting light is preferably less than 100%, more preferably 95% or less, and even more preferably 94% or less, when the light diameter of the incident light is 100%. In this way, if the light diameter of the exiting light emitted from the same surface as the incident surface is less than 100% of the light diameter of the incident light, the spread of the exiting light is suppressed, and the light emitted from the rare earth aluminate sintered body can be concentrated at a target position. The light diameter of the incident light incident on one surface of the rare earth aluminate sintered body is the light diameter of the light emitted from the light source. The light diameter of the incident light can be measured, for example, by a color luminance meter. The light diameter of the incident light is preferably in the range of 0.1 mm to 5 mm, more preferably in the range of 0.5 mm to 4 mm. The light diameter of the outgoing light emitted from the same surface of the rare earth aluminate sintered body as the surface to which the incident light was incident can be measured by measuring the emission luminance of the light emitted from the rare earth aluminate sintered body with a color luminance meter, taking the position showing the maximum luminance in the obtained emission spectrum as the center (measurement center), measuring the distance (mm) from the measurement center to two positions where the luminance in the emission spectrum is 30 / 100 of the maximum luminance (hereinafter sometimes referred to as "30 / 100 luminance") as absolute values, and measuring the sum of the absolute values ​​of the distance (mm) from the measurement center to two positions where the luminance in the emission spectrum is 30 / 100 of the maximum luminance, as the light diameter of the outgoing light.

[0034] Method for producing rare earth aluminate sintered body At least one rare earth element selected from the group consisting of Y, La, Lu, Gd and Tb. 1 oxide particles containing Ce, oxide particles containing Al, and at least one element M selected from Ga and Sc as required. 1The present invention includes the steps of: preparing a slurry-like raw material mixture by mixing oxide particles containing Ln into a liquid; drying the raw material mixture to obtain a raw material mixture powder; molding the raw material mixture powder to obtain a molded body; and sintering the molded body at a temperature range of 1300° C. to 1800° C. to obtain a sintered body. 1 The oxide particles containing Ce, the oxide particles containing Al, and the element M 1 At least one oxide particle selected from the oxide particles containing 2 / g or more.

[0035] FIG. 1 is a flow chart showing an example of a method for producing a rare earth aluminate sintered body. The method for producing a rare earth aluminate sintered body will be described with reference to FIG. 1. The method for producing a rare earth aluminate sintered body includes preparing a slurry-like raw material mixture S101 by mixing raw material particles with a liquid, drying the slurry-like raw material mixture to obtain a raw material mixture powder S102, molding the raw material mixture powder S103, and firing the molded body to obtain a sintered body S104. FIG. 2 is a flow chart showing another example of a method for producing a rare earth aluminate phosphor sintered body. The preparation of the raw material mixture S101 may include preparing a slurry-like raw material mixture S101a and stirring the slurry-like raw material mixture S101b. The drying S102 may include drying S102a to dry the slurry-like raw material mixture to obtain a raw material mixture powder, and dry grinding and mixing S102b of the obtained raw material mixture powder. The molding S103 may include molding S103a of the raw material mixture powder, and heating and degreasing S103b of heating the molded body at a temperature lower than the sintering temperature to degrease it. The method for producing a rare earth aluminate sintered body may also include an annealing treatment S105 after sintering S104. The method for producing a rare earth aluminate sintered body may also include a process S106 of cutting the obtained sintered body to a desired size or thickness, and may further include a surface treatment S107 of the sintered body.

[0036] Preparation of raw material mixture The raw material is at least one rare earth element selected from the group consisting of Y, La, Lu, Gd and Tb. 1 oxide particles containing Ce, oxide particles containing Al, and at least one element M selected from Ga and Sc as required. 1 The rare earth element Ln 1 Specific examples of oxide particles containing the above include yttrium oxide particles, lanthanum oxide particles, lutetium oxide particles, gadolinium oxide particles, and terbium oxide particles. Other examples of oxide particles include cerium oxide particles, aluminum oxide particles, gallium oxide particles, and scandium oxide particles.

[0037] Rare Earth Elements Ln 1 oxide particles containing Ce, oxide particles containing Al, and optionally an element M 1 The oxide particles, including those mentioned above, have a specific surface area of ​​5 m2 measured by the BET method. 2 / g or more. Oxide particles with a large specific surface area are oxide particles with a small particle size, and can form a rare earth aluminate phosphor crystal phase with the above-mentioned absolute maximum length in a specific range by firing. 1 oxide particles containing Ce, oxide particles containing Al, and oxide particles containing element M 1 The specific surface area of ​​the oxide particles containing 150 m2 was measured by the BET method. 2 The upper limit of the specific surface area measured by the BET method varies depending on the type of oxide particles. The specific surface area of ​​oxide particles containing Ce measured by the BET method is 130 m 2 / g or less is acceptable, and 125m 2 / g or less. Rare earth element Ln 1 oxide particles containing Al, and oxide particles containing element M 1 The specific surface area of ​​oxide particles containing 2 / g or less is acceptable, and 50m 2If the specific surface area of ​​the oxide particles is too large, they will not disperse uniformly in the raw material mixture, and a homogeneous rare earth aluminate phosphor crystal phase may not be formed in the rare earth aluminate sintered body.

[0038] The oxides contained in the raw material mixture are preferably blended in a molar ratio that results in the composition represented by formula (I), the composition represented by formula (Ia), or the composition represented by formula (Ib).

[0039] The raw material may further contain rare earth aluminate phosphor particles. When the raw material contains rare earth aluminate phosphor particles, the specific surface area of ​​the raw material rare earth aluminate phosphor particles measured by the BET method is 5 m 2 / g or more. The rare earth aluminate phosphor particles having a large specific surface area can form a rare earth aluminate phosphor crystal phase having a small absolute maximum length in a specific range as described above together with other raw material oxide particles by firing. The rare earth aluminate phosphor particles as raw materials have a specific surface area of ​​6 m or more as measured by the BET method. 2 / g or more, and 15m 2 / g or less, 2 If the specific surface area of ​​the raw material rare earth aluminate phosphor particles is too large, it is difficult to uniformly disperse the raw material particles in the raw material mixture, and it may be difficult to form a homogeneous rare earth aluminate phosphor crystal phase in the rare earth aluminate sintered compact.

[0040] When the oxides contained in the raw material mixture are blended, for example, in a molar ratio that results in the composition represented by formula (I), it is preferable that the rare earth aluminate phosphor particles as the raw material have the composition represented by formula (I).

[0041] When the raw material mixture contains rare earth aluminate phosphor particles, rare earth aluminate phosphor particles, rare earth element Ln 1 oxide particles containing Ce, oxide particles containing Al, and optionally an element M 1The mass ratio of the rare earth aluminate phosphor particles is preferably in the range of 10 mass% to 90 mass%, more preferably in the range of 15 mass% to 80 mass%, and even more preferably in the range of 30 mass% to 70 mass% relative to 100 mass% of the total of the oxide particles including the above. The mass ratio of the raw material rare earth aluminate phosphor particles is in the range of 10 mass% to 90 mass% relative to 100 mass% of the total of the raw material rare earth aluminate phosphor particles and the above-mentioned oxide particles, and at least one particle selected from the rare earth aluminate phosphor particles and each oxide particle, or both the rare earth aluminate phosphor particles and each oxide particle, has a specific surface area of ​​5 m by BET method. 2 / g or more, a rare earth aluminate phosphor crystal phase having a small absolute maximum length in a specific range can be formed.

[0042] The raw material rare earth aluminate phosphor particles are preferably rare earth aluminate phosphor particles formed by a coprecipitation method, which makes it possible to produce rare earth aluminate phosphor particles having a large specific surface area.

[0043] The method of forming rare earth aluminate phosphor particles by the coprecipitation method includes, for example, preparing oxides containing constituent elements contained in the composition of rare earth aluminate or compounds that easily become oxides at high temperatures as raw materials, and weighing each compound so as to obtain the composition of rare earth aluminate while considering the stoichiometric ratio. Each compound weighed to obtain the composition of rare earth aluminate is dissolved in a solvent, and a precipitant is added to the solution to cause coprecipitation to obtain a coprecipitate. The oxide obtained by firing the coprecipitate and other raw materials as necessary, for example, oxides contained in the composition of rare earth aluminate, are weighed, and these raw materials are mixed in a wet or dry manner. A flux may be added to the raw materials. The mixture containing the oxide obtained by coprecipitation, other raw materials, and flux as necessary is fired to obtain rare earth aluminate phosphor particles formed by the coprecipitation method. Examples of compounds that easily become oxides at high temperatures include hydroxides, oxalates, carbonates, chlorides, nitrates, sulfates, etc., containing elements that constitute the composition of rare earth aluminate. The compound that easily becomes an oxide at high temperature may be a metal consisting of an element that constitutes the composition of the rare earth aluminate, for example, simple aluminum. The oxide may be the same as the oxide used in the raw material mixture described above. The solvent for dissolving the metal or each compound may be deionized water or the like. The precipitant may be oxalic acid or an oxalate, a carbonate, ammonium hydrogen carbonate, or the like. For example, an example of an oxalate is ammonium oxalate, and an example of a carbonate is ammonium carbonate.

[0044] Rare Earth Elements Ln 1 oxide particles containing Ce, oxide particles containing Al, and optionally an element M 1 The oxide particles containing Ln and, if necessary, rare earth aluminate phosphor particles are mixed with a liquid to obtain a slurry-like raw material mixture. By mixing each oxide particle and, if necessary, rare earth aluminate phosphor particles with a liquid, they are uniformly dispersed, and a rare earth aluminate sintered body having a homogeneous rare earth aluminate phosphor crystal phase can be produced. Examples of the liquid for dispersing the raw material include deionized water, water, and ethanol. The liquid is a liquid containing a rare earth element Ln1 oxide particles containing Ce, oxide particles containing Al, and optionally an element M 1 and, if necessary, rare earth aluminate phosphor particles, the total amount of the oxide particles containing the compound is preferably in the range of 10 parts by mass or more and 200 parts by mass or less, and may be in the range of 50 parts by mass or more and 150 parts by mass or less, relative to 100 parts by mass of the total amount of the oxide particles containing the compound and, if necessary, the rare earth aluminate phosphor particles.

[0045] The slurry-like raw material mixture may contain a dispersant to enhance dispersibility. For example, an organic dispersant may be used, and a cationic dispersant, an anionic dispersant, a nonionic dispersant, etc. may be used. When a dispersant is added to the raw material mixture, the rare earth element Ln 1 oxide particles containing Ce, oxide particles containing Al, and optionally an element M 1 The amount is preferably an amount that can be volatilized by subsequent heating and degreasing or firing, relative to the total amount (100 mass%) of the oxide particles containing the compound and, if necessary, the rare earth aluminate phosphor particles, and may be 10 mass% or less, 5 mass% or less, or 3 mass% or less.

[0046] Mixing The preparation of the raw material mixture may include stirring the obtained slurry raw material mixture. The slurry raw material mixture is preferably stirred for 2 hours or more and 40 hours or less at a stirring speed of 20 rpm or more and 250 rpm or less. By uniformly mixing the slurry raw material mixture, each oxide particle and, if necessary, rare earth aluminate phosphor particles are uniformly dispersed, and a small rare earth aluminate phosphor crystal phase having an absolute maximum length in a specific range is formed in the rare earth aluminate sintered body.

[0047] Drying The method for producing a rare earth aluminate sintered body may include drying the obtained slurry-like raw material mixture to obtain a raw material mixture powder. The drying temperature is preferably in the range of 50°C to 150°C, and the drying time is preferably 1 hour to 20 hours. By drying the slurry-like raw material mixture in which the raw materials are uniformly mixed, a raw material mixture powder in which each raw material is uniformly mixed can be obtained.

[0048] Dry grinding and mixing The method for producing a rare earth aluminate sintered body may include dry grinding and mixing in which the raw material mixture powder is ground and mixed. The dry grinding and mixing is preferably performed, for example, for 1 hour in a ball mill. It is not necessary for all particles in the raw material mixture powder to be ground, and only a portion of the particles may be ground and mixed. By performing dry grinding and mixing, aggregation of particles in the raw material mixture is suppressed.

[0049] molding The method for producing a rare earth aluminate sintered body includes forming the obtained raw material mixture powder to obtain a molded body. The method for forming the raw material mixture powder can employ known methods such as press molding. Examples of press molding methods include die press molding and cold isostatic pressing (CIP) method, the term of which is defined in JIS Z2500:2000, No.2109. In addition, molding may be performed by uniaxial compression. As a molding method, two types of methods may be adopted to adjust the shape of the molded body, for example, CIP may be performed after die press molding, or CIP may be performed after uniaxial compression by the roller bench method. As for CIP, it is preferable to press the molded body by cold isostatic pressing using water as a medium.

[0050] The pressure during die press molding or uniaxial compression molding is preferably in the range of 5 MPa to 50 MPa, more preferably 5 MPa to 30 MPa. If the pressure during die press molding or uniaxial compression molding is in the above range, the molded body can be shaped into a desired shape.

[0051] The pressure in the CIP is preferably in the range of 50 MPa to 200 MPa, more preferably in the range of 50 MPa to 180 MPa. When the pressure in the CIP is in the range of 50 MPa to 200 MPa, a molded body can be formed that can give a rare earth aluminate sintered body having a relative density of 90% or more and a porosity of 1% to 10% by firing.

[0052] Heat degreasing The method for producing a rare earth aluminate sintered body may include heating the molded body to remove the dispersant and the like and degreasing the molded body. When degreasing by heating, it is preferable to include heating in the air or nitrogen atmosphere within a range of 500°C to 1000°C. By heating in the air or nitrogen atmosphere within a range of 500°C to 1000°C, the amount of carbon contained in the molded body is reduced, and a decrease in luminous flux due to the inclusion of carbon can be suppressed.

[0053] Firing The method for producing a rare earth aluminate sintered body includes sintering the obtained molded body at a temperature in the range of 1300° C. to 1800° C. to obtain a sintered body.

[0054] The sintering temperature of the molded body is in the range of 1300° C. to 1800° C., preferably in the range of 1400° C. to 1790° C., and more preferably in the range of 1450° C. to 1780° C. If the sintering temperature is 1300° C. or higher, the specific surface area is large, and the uniformly mixed raw materials react to obtain a sintered body containing a rare earth aluminate phosphor crystal phase and voids whose absolute maximum length is in a specific range.

[0055] The sintering of the molded body is preferably carried out in an oxygen-containing atmosphere. The oxygen content in the atmosphere is preferably 5% by volume or more, more preferably 10% by volume or more, and even more preferably 15% by volume or more. The molded body may be sintered in an air atmosphere (oxygen content of 20% by volume or more). In an atmosphere with an oxygen content of less than 1% by volume, the surface of the oxide is difficult to melt, and the oxides are difficult to melt together to form a crystal structure having a rare earth aluminate composition, and it may be difficult to obtain a sintered body having voids. The amount of oxygen in the atmosphere may be measured, for example, by the amount of oxygen flowing into a sintering device, and may be measured at a temperature of 20°C and atmospheric pressure (101.325 kPa).

[0056] Annealing The method for producing a rare earth aluminate sintered body may include annealing the obtained sintered body in a reducing atmosphere. By annealing the obtained sintered body in a reducing atmosphere, cerium, which is an oxidized activation element contained in the crystal phase of the sintered body, is reduced, and the decrease in wavelength conversion efficiency and the decrease in luminous efficiency in each crystal phase can be suppressed. The reducing atmosphere may be an atmosphere containing at least one rare gas selected from the group consisting of helium, neon, and argon, or nitrogen gas, and hydrogen gas or carbon monoxide gas, and more preferably contains at least argon or nitrogen gas, and hydrogen gas or carbon monoxide gas. The annealing treatment may be performed after processing.

[0057] The annealing temperature is lower than the firing temperature and is preferably within the range of 1000°C to 1600°C. The annealing temperature is more preferably within the range of 1100°C to 1400°C. If the annealing temperature is lower than the firing temperature and within the range of 1000°C to 1600°C, the oxidized activator element cerium contained in the crystal phase of the sintered body can be reduced without reducing the voids in the sintered body, and the decrease in wavelength conversion efficiency and the decrease in luminous efficiency can be suppressed.

[0058] processing The method for producing a rare earth aluminate sintered body may include processing the obtained sintered body by cutting it into a desired size or thickness. The cutting method may be a known method, such as a method using a blade dicing, a laser dicing, or a wire saw.

[0059] Surface Treatment The method for producing a rare earth aluminate sintered body may further include surface treatment as described below. Surface treatment is performed on the surface of the obtained rare earth aluminate sintered body or the cut product obtained by cutting the rare earth aluminate sintered body. This surface treatment not only makes it possible to make the surface of the rare earth aluminate sintered body in an appropriate state in order to improve the luminescence characteristics of the rare earth aluminate sintered body, but also makes it possible to make the rare earth aluminate sintered body into a desired shape, size or thickness, in combination with the above-mentioned processing or alone. The surface treatment may be performed before or after cutting and processing the rare earth aluminate sintered body into a desired size or thickness. Examples of the surface treatment method include a sandblasting method, a mechanical grinding method, a dicing method, and a chemical etching method.

[0060] The above-mentioned manufacturing method can provide a rare earth aluminate sintered body that contains a rare earth aluminate phosphor crystal phase and voids, in which 90% or more of the rare earth aluminate phosphor crystal phase has an absolute maximum length in the range of 0.4 μm to 1.3 μm, and 90% or more of the voids has an absolute maximum length in the range of 0.1 μm to 1.2 μm. The rare earth aluminate phosphor crystal phase contained in the rare earth aluminate sintered body obtained by the above-mentioned manufacturing method preferably has a composition represented by formula (I), formula (Ia), or formula (Ib).

[0061] The obtained rare earth aluminate sintered body can be used as a wavelength conversion member in a light emitting device such as a light source for a projector by combining it with a light source.

[0062] Light-emitting device A light emitting device using the above-mentioned rare earth aluminate sintered body as a wavelength conversion member will be described below. The light emitting device includes a rare earth aluminate sintered body and an excitation light source.

[0063] The excitation light source is preferably a semiconductor light-emitting element made of an LED chip or an LD chip. The semiconductor light-emitting element can be a nitride-based semiconductor. By using a semiconductor light-emitting element as the excitation light source, a highly efficient light-emitting device with high linearity of output relative to input and high mechanical shock resistance can be obtained. The rare earth aluminate sintered body can convert the wavelength of light emitted from the semiconductor light-emitting element to form a light-emitting device that emits wavelength-converted mixed color light. The semiconductor light-emitting element is preferably one that emits light in a wavelength range of, for example, 350 nm or more and 500 nm or less. The rare earth aluminate sintered body preferably converts the wavelength of the excitation light from the semiconductor light-emitting element to emit an emission light having an emission peak wavelength in the range of 500 nm or more and less than 650 nm.

[0064] The excitation light source is more preferably a semiconductor laser. The excitation light emitted from the semiconductor laser as the excitation light source may be incident on the rare earth aluminate sintered body using a rare earth aluminate sintered body as a wavelength conversion member, and the light whose wavelength has been converted by the rare earth aluminate sintered body may be condensed, separated into red light, green light, and blue light by a plurality of optical systems such as a lens array, a polarization conversion element, and a color separation optical system, and modulated according to image information to form color image light. The excitation light emitted from the semiconductor laser as the excitation light source may be incident on the rare earth aluminate sintered body through an optical system such as a dichroic mirror or a collimating optical system.

[0065] FIG. 3 is a diagram showing a schematic configuration of an example of the light emitting device 100. The light emitting device 100 preferably includes an excitation light source 101, a collimating lens 102, three condenser lenses 103, 105, and 106, a dichroic mirror 104, a rod integrator 107, and a phosphor device 110 including a rare earth aluminate sintered body. The excitation light source 101 preferably uses a semiconductor laser. The excitation light source 101 may use a plurality of semiconductor lasers, or may be one in which a plurality of semiconductor lasers are arranged in an array or matrix. The collimating lens 102 may be a collimating lens array in which a plurality of collimating lenses are arranged in an array. The laser light emitted from the excitation light source 101 becomes approximately parallel light by the collimating lens 102, is collected by the condenser lens 103, passes through the dichroic mirror 104, and is further collected by the condenser lens 105. The laser light collected by the condenser lens 105 is wavelength-converted by the phosphor device 110 including a rare earth aluminate sintered body, and light having an emission peak wavelength in a desired wavelength range is emitted from the phosphor device 110. The wavelength-converted light emitted from the phosphor device 110 is collected by the condenser lens 106 and incident on the rod integrator 107, and light with improved uniformity of illuminance distribution in the illuminated area is emitted from the light emitting device 100. The light emitting device 100 including the rare earth aluminate sintered body can be used as a light source for a projector.

[0066] 4 is a plan view showing a schematic configuration of an example of a phosphor device. The phosphor device 110 includes at least a rare earth aluminate sintered body 111. The phosphor device 110 includes a disk-shaped rare earth aluminate sintered body 111, and may include a rotation mechanism 112 for rotating the rare earth aluminate sintered body 111. The rotation mechanism 112 is connected to a drive mechanism such as a motor, and can dissipate heat by rotating the rare earth aluminate sintered body 111.

[0067] 5 is a side view showing a schematic configuration of an example of a phosphor device. The phosphor device 110 may include a heat sink 113 in contact with the rare earth aluminate sintered body 111. The phosphor device 110 rotates the rare earth aluminate sintered body 111 using a rotation mechanism 112 to dissipate heat, and transfers heat generated in the rare earth aluminate sintered body 111 to the heat sink 113, so that the heat can be easily dissipated from the heat sink 113 to the outside of the phosphor device 110. EXAMPLES

[0068] The present invention will be described in more detail below with reference to examples, but the present invention is not limited to these examples.

[0069] Manufacturing example of rare earth aluminate phosphor particles (LAG phosphor particles by coprecipitation method) Lutetium chloride (LuCl3), cerium chloride (CeCl3), and aluminum chloride (AlCl3) are 2.987 Ce 0.013 AlO 12 The mixture was weighed out so that the composition was expressed by the formula: 2.987 Ce 0.013 AlO 12 This mixture was placed in an alumina crucible and fired in an air atmosphere at 1200 to 1600°C for 10 hours to obtain a fired product. The fired product was passed through a dry sieve to classify it, and Lu 2.987 Ce 0.013 AlO 12 The specific surface area of ​​the LAG phosphor particles (co-precipitated LAG phosphor particles) measured by the BET method was 8.8 m 2 / g.

[0070] Manufacturing example of rare earth aluminate phosphor particles (YAG phosphor particles by coprecipitation method) Yttrium chloride (YCl3), cerium chloride (CeCl3), and aluminum chloride (AlCl3) are 2.99 Ce0.01 AlO 12 The mixture was weighed out so that the composition was expressed by the formula: 2.99 Ce 0.01 AlO 12 This mixture was placed in an alumina crucible and fired in an air atmosphere at a temperature ranging from 1200°C to 1600°C for 10 hours to obtain a fired product. The fired product was classified by passing it through a dry sieve to obtain a mixture represented by the formula: 2.99 Ce 0.01 AlO 12 The YAG phosphor particles (co-precipitated YAG phosphor particles) having the composition shown in the following formula were prepared. The specific surface area of ​​the YAG phosphor particles (co-precipitated YAG phosphor particles) measured by the BET method was 8.0 m 2 / g.

[0071] Lutetium Oxide Lutetium oxide particles with a purity of lutetium oxide of 99% by mass were used.

[0072] Yttrium oxide The yttrium oxide particles used had a purity of 98 mass %.

[0073] Aluminum oxide Aluminum oxide particles with a purity of 99 mass % were used.

[0074] Cerium oxide Cerium oxide particles with a purity of 92 mass % were used.

[0075] specific surface area The specific surface areas of the yttrium oxide particles, aluminum oxide particles, cerium oxide particles, LAG phosphor particles, and YAG phosphor particles were measured by the BET method using a specific surface area measuring device (manufactured by Mountec Co., Ltd.).

[0076] Example 1 Preparation of raw material mixture BET specific surface area: 12 m2 / g lutetium oxide particles, specific surface area by BET method 11.8 m 2 / g aluminum oxide particles, specific surface area by BET method 125 m 2 / g of cerium oxide particles were prepared with a molar ratio of Lu, Al, and Ce contained in each oxide particle of Lu. 2.987 Ce 0.013 AlO 12 The specific surface area of ​​each oxide particle used, as determined by the BET method, is shown in Table 1. A raw material mixture was prepared by adding 4 parts by mass of a dispersant (Floren G-700, Kyoeisha Chemical Co., Ltd.) and further adding 50 parts by mass of ethanol to a total of 100 parts by mass of lutetium oxide particles, aluminum oxide particles, and cerium oxide particles.

[0077] Mixing The raw material mixture was stirred in a wet ball mill for 15 hours to prepare a slurry-like raw material mixture in which lutetium oxide particles, aluminum oxide particles, and cerium oxide particles were uniformly mixed.

[0078] Drying The obtained slurry-like raw material mixture was dried at 130° C. for 10 hours in an air atmosphere to obtain a raw material mixture powder.

[0079] molding The obtained raw material mixture powder was filled into a mold and subjected to a pressure of 5 MPa (51 kgf / cm 2 A cylindrical molded body with a diameter of 26 mm and a thickness of 10 mm was formed at a pressure of 176 MPa. The obtained molded body was placed in a packaging container and vacuum-packed, and then subjected to CIP at 176 MPa using a cold isostatic pressing device (manufactured by Kobe Steel, Ltd. (KOBELCO)) to obtain a molded body.

[0080] Heat degreasing The obtained green body was degreased by heating at 700° C. in a nitrogen atmosphere.

[0081] Firing The obtained molded body was sintered in a sintering furnace (manufactured by Marusho Denki Co., Ltd.) to obtain a rare earth aluminate sintered body. The sintering conditions were an air atmosphere (101.325 kPa, oxygen concentration: approximately 20% by volume), a temperature of 1600°C, and a sintering time of 6 hours.

[0082] Machining / Surface treatment The obtained rare earth aluminate sintered body was cut into an appropriate shape and size with a wire saw, and the surface of the cut piece was polished with a surface grinder, and finally, the rare earth aluminate sintered body of Example 1 having a plate thickness of 230 μm was obtained.

[0083] Example 2 A rare earth aluminate sintered body of Example 2 was obtained in the same manner as in Example 1, except that the lutetium oxide particles, aluminum oxide particles, and cerium oxide particles shown in Table 1 were used and the firing temperature was set to 1650°C.

[0084] Example 3 A rare earth aluminate sintered body of Example 3 was obtained in the same manner as in Example 1, except that the lutetium oxide particles, aluminum oxide particles, cerium oxide particles, and LAG phosphor particles shown in Table 1 were used in an amount of 30 mass% of the LAG phosphor particles relative to a total amount of 100 mass% of the lutetium oxide particles, aluminum oxide particles, cerium oxide particles, and LAG phosphor particles, and that the firing temperature was 1510° C. The specific surface area of ​​the LAG phosphor particles measured by the BET method was 8.8 m 2 / g.

[0085] Example 4 A rare earth aluminate sintered body of Example 4 was obtained in the same manner as in Example 1, except that the lutetium oxide particles, aluminum oxide particles, cerium oxide particles, and LAG phosphor particles shown in Table 1 were used, and the LAG phosphor particles were used in an amount of 30 mass% relative to 100 mass% of the total amount of the lutetium oxide particles, aluminum oxide particles, cerium oxide particles, and LAG phosphor particles, and the firing temperature was 1530°C.

[0086] Comparative Example 1 BET specific surface area: 3.5 m2 / g lutetium oxide particles, specific surface area by BET method 5.5 m 2 / g aluminum oxide particles, specific surface area by BET method 125 m 2 A rare earth aluminate sintered body of Comparative Example 1 was obtained in the same manner as in Example 1, except that cerium oxide particles of 0.1 g / g were used and the firing temperature was 1700°C.

[0087] Comparative Example 2 A rare earth aluminate sintered body of Comparative Example 2 was obtained in the same manner as in Comparative Example 1, except that the firing temperature was 1680°C.

[0088] Comparative Example 3 A rare earth aluminate sintered body of Comparative Example 3 was obtained in the same manner as in Comparative Example 1, except that the firing temperature was 1660°C.

[0089] Example 5 BET specific surface area: 20m 2 / g yttrium oxide particles, specific surface area by BET method 5.5 m 2 / g aluminum oxide particles, specific surface area by BET method 125 m 2 / g of cerium oxide particles were used, and the molar ratio of each element of Y, Al, and Ce contained in each oxide particle was Y 2.99 Ce 0.01 Al 5.1 O 12 The raw material mixture was prepared by adding 6 parts by mass of a dispersant and further adding 50 parts by mass of ethanol relative to 100 parts by mass of the total amount of yttrium oxide particles, aluminum oxide particles, and cerium oxide particles, and a rare earth aluminate sintered body was obtained in the same manner as in Example 1 except that the firing temperature was 1570°C.

[0090] Example 6 A rare earth aluminate sintered body of Example 6 was obtained in the same manner as in Example 5, except that the firing temperature was 1580°C.

[0091] Example 7 A rare earth aluminate sintered body of Example 7 was obtained in the same manner as in Example 5, except that the firing temperature was 1600°C.

[0092] Example 8 A rare earth aluminate sintered body of Example 8 was obtained in the same manner as in Example 5, except that the yttrium oxide particles, aluminum oxide particles, cerium oxide particles, and YAG phosphor particles shown in Table 2 were used in an amount of 30 mass% of the YAG phosphor particles relative to a total amount of 100 mass% of the yttrium oxide particles, aluminum oxide particles, cerium oxide particles, and YAG phosphor particles, and that the firing temperature was 1540° C. The specific surface area of ​​the YAG phosphor particles measured by the BET method was 8.0 m 2 / g.

[0093] Comparative Example 4 BET specific surface area: 2.1 m 2 / g yttrium oxide particles, specific surface area by BET method 5.5 m 2 / g aluminum oxide particles, specific surface area by BET method 125 m 2 A rare earth aluminate sintered body of Comparative Example 4 was obtained in the same manner as in Example 1, except that cerium oxide particles of 0.1 g / g were used and the firing temperature was 1640°C.

[0094] Comparative Example 5 A rare earth aluminate sintered body of Comparative Example 4 was obtained in the same manner as in Example 1, except that the firing temperature was 1650°C.

[0095] The following analyses were carried out on each of the rare earth aluminate sintered bodies of the Examples and Comparative Examples. The results are shown in Tables 1 and 2 and described below.

[0096] Relative Density The relative density of each rare earth aluminate sintered body of the examples and comparative examples was measured. The relative density of the rare earth aluminate sintered body of the examples and comparative examples was calculated by the above-mentioned formula (1). The apparent density of the rare earth aluminate sintered body was calculated by the above-mentioned formula (2). The true density of the rare earth aluminate sintered body was taken as the true density of the LAG phosphor or the true density of the YAG phosphor. The true density of the LAG phosphor was 6.69 g / cm 3 The true density of the YAG phosphor is 4.60 g / cm 3 It is.

[0097] Relative luminous flux (%) The rare earth aluminate sintered body of each Example and Comparative Example was irradiated with a laser beam having a wavelength of 450 nm from a laser diode so that the diameter of the incident beam was 2.2 mm, and the radiant flux of the light emitted from the same surface as the surface on which the laser beam was incident was measured with an integrating sphere. The radiant flux of Comparative Example 1 was set to 100%, and the radiant flux of each rare earth aluminate sintered body sample of Examples 1 to 4 and Comparative Examples 2 to 3 relative to the radiant flux of Comparative Example 1 was expressed as a relative luminous flux (%). The radiant flux of Comparative Example 4 was set to 100%, and the radiant flux of each rare earth aluminate sintered body sample of Examples 5 to 8 and Comparative Example 5 relative to the radiant flux of Comparative Example 4 was expressed as a relative luminous flux (%).

[0098] Beam diameter ratio (beam diameter of outgoing light / beam diameter of incoming light) Each rare earth aluminate sintered body of the examples and comparative examples was irradiated with a laser beam having a wavelength of 450 nm from a laser diode so that the diameter of the incident beam was 0.6 mm on the first main surface to which the laser beam was incident, and the diameter of the laser beam was defined as the diameter of the incident beam incident on the first main surface of the rare earth aluminate sintered body. The diameter of the outgoing beam emitted from the same surface as the first main surface to which the laser beam was incident was measured by measuring the emission luminance of the light emitted from the rare earth aluminate sintered body of each example and comparative example with a color luminance meter, setting the position showing the maximum luminance in the obtained emission spectrum as the center (measurement center), measuring the distance (mm) from the measurement center to two positions showing a luminance of 30 / 100 of the maximum luminance in the emission spectrum as an absolute value, and measuring the sum of the absolute values ​​of the distances (mm) from the measurement center to two positions showing a luminance of 30 / 100 of the maximum luminance from the maximum luminance as the diameter of the outgoing beam emitted from the first main surface. The beam diameter ratio of the beam diameter of the outgoing light from the first main surface, which is the same surface, to the beam diameter of the incident light incident on the first main surface was obtained. The beam diameter ratio of Comparative Example 1 was set to 100%, and the beam diameter ratios of the samples of the rare earth aluminate sintered bodies of Examples 1 to 4 and Comparative Examples 2 to 3 measured relative to the beam diameter ratio of Comparative Example 1 were expressed as relative beam diameter ratios (%). The beam diameter ratio of Comparative Example 4 was set to 100%, and the beam diameter ratios of the samples of the rare earth aluminate sintered bodies of Examples 5 to 8 and Comparative Example 5 measured relative to the beam diameter ratio of Comparative Example 4 were expressed as relative beam diameter ratios (%).

[0099] Light extraction efficiency (%) For each of the rare earth aluminate sintered bodies of the Examples and Comparative Examples, the measured relative luminous flux was divided by the relative beam diameter ratio to calculate the light extraction efficiency (%).

[0100] How to measure absolute maximum length In the SEM images obtained by photographing the surface or cross section of each rare earth aluminate sintered body of the examples and comparative examples with a scanning electron microscope (SEM), 2The area where the measurement range was determined was the area where the data size of the SEM image was 1280 × 960 pixels (vertical × horizontal), and one pixel was 0.09921875 μm. Therefore, the area of ​​the measurement range was calculated as 127 μm × 95.25 μm, which is 12096 μm. 2 The distance between the two most distant points on the contour of one rare earth aluminate phosphor crystal phase or void contained in this measurement range was taken as the absolute maximum length, and was measured using a Winroof2018 image analysis software device (manufactured by Mitani Shoji Co., Ltd.). The distribution of the absolute maximum length of each rare earth aluminate phosphor crystal phase contained in the measurement range was determined based on the number, and the ratio of the number of rare earth aluminate phosphor crystal phases having an absolute maximum length in the range of 0.4 μm to 1.3 μm to the total number of rare earth aluminate phosphor crystal phases was determined. In addition, the distribution of the absolute maximum length of the voids contained in the measurement range based on the number was determined, and for each of the rare earth aluminate sintered bodies of Examples 1 to 4 and Comparative Examples 1 to 3, the ratio of the number of voids having an absolute maximum length in the range of 0.1 μm to 1.2 μm to the total number of voids was determined. The number-based distribution of the absolute maximum length of the voids included in the measurement range was obtained, and for each of the rare earth aluminate sintered bodies of Examples 5 to 8 and Comparative Examples 4 to 5, the ratio of the number of voids with an absolute maximum length in the range of 0.1 μm to 1.2 μm to the total number of voids was obtained. In addition, the absolute maximum length (μm) at a cumulative frequency of 50%, the minimum value (μm) of the absolute maximum length, and the maximum value (μm) of the absolute maximum length were obtained from the number-based particle size distribution of the absolute maximum length of the rare earth aluminate phosphor crystal phase. In the particle size distribution of the number frequency for the absolute maximum length of the voids, the absolute maximum length (μm) at a cumulative frequency of 50%, the minimum value (μm) of the absolute maximum length, and the maximum value (μm) of the absolute maximum length were obtained.

[0101] SEM images A scanning electron microscope (SEM) was used to obtain SEM images of the surface of each rare earth aluminate sintered body of the examples and comparative examples. The SEM images shown in the figures were obtained at a magnification of 2000 times, and the SEM images used for measuring the absolute maximum length were obtained at a magnification of 1000 times in consideration of the accuracy of the analysis.

[0102] [Table 1]

[0103] [Table 2]

[0104] In the rare earth aluminate sintered bodies according to Examples 1 to 4, the number of rare earth aluminate phosphor crystal phases having an absolute maximum length in the range of 0.4 μm to 1.3 μm was 90% or more relative to the total number of rare earth aluminate phosphor crystal phases included in the measurement range. In addition, in the rare earth aluminate sintered bodies according to Examples 1 to 8, the number of voids having an absolute maximum length in the range of 0.1 μm to 1.2 μm was 90% or more relative to the total number of voids included in the measurement range. The relative light diameter ratios of the rare earth aluminate sintered bodies according to Examples 1 to 4 were all 95% or less, which was smaller than that of the rare earth aluminate sintered body of Comparative Example 1, and the spread of the emitted light was suppressed. In addition, the rare earth aluminate sintered bodies according to Examples 2 to 4 had a higher relative luminous flux than that of the rare earth aluminate sintered body of Comparative Example 1. The rare earth aluminate sintered bodies according to Examples 1 to 4 have higher light extraction efficiency than the rare earth aluminate sintered body of Comparative Example 1. The relative luminous flux is measured by measuring the light emitted from the same surface of the rare earth aluminate sintered body as the surface into which the light was incident, and the light that was spread out is also measured. The relative luminous flux of the rare earth aluminate sintered body according to Example 1 is lower than that of the rare earth aluminate sintered body of Comparative Example 1, but the light extraction efficiency in consideration of the luminous flux per unit area is significantly higher than that of Comparative Example 1.

[0105] In the rare earth aluminate sintered bodies according to Examples 5 to 8, the number of rare earth aluminate phosphor crystal phases having an absolute maximum length in the range of 0.4 μm to 1.3 μm was 90% or more of the total number of rare earth aluminate phosphor crystal phases included in the measurement range. In addition, in the rare earth aluminate sintered bodies according to Examples 5 to 8, the number of voids having an absolute maximum length in the range of 0.1 μm to 1.2 μm was 90% or more of the total number of voids included in the measurement range. The relative beam diameter ratios of the rare earth aluminate sintered bodies according to Examples 5, 6 and 8 were all smaller than the relative beam diameter ratio of the rare earth aluminate sintered body according to Comparative Example 4, and the spread of the emitted light was suppressed. In addition, the relative luminous fluxes of the rare earth aluminate phosphors according to Examples 5 to 8 were all equal to or higher than that of the rare earth aluminate sintered body according to Comparative Example 4. The rare earth aluminate sintered bodies of Examples 5 to 8 had higher light extraction efficiencies than the rare earth aluminate sintered body of Comparative Example 4. The rare earth aluminate sintered body of Example 5 had a relative luminous flux substantially equivalent to that of the rare earth aluminate sintered body of Comparative Example 4, but the light extraction efficiency in consideration of the luminous flux per unit area was higher than that of the rare earth aluminate sintered body of Comparative Example 4.

[0106] FIG. 6 is an SEM image of the surface of the rare earth aluminate sintered body according to Example 1, and FIG. 7 is an SEM image of the rare earth aluminate sintered body according to Example 3. FIG. 10 is an SEM image of the surface of the rare earth aluminate sintered body according to Comparative Example 1. It was confirmed that the rare earth aluminate sintered bodies according to Examples 1 and 3 have smaller individual rare earth aluminate phosphor crystal phases than the rare earth aluminate sintered body according to Comparative Example 1. The rare earth aluminate phosphor crystal phase of the rare earth aluminate sintered body according to Example 3 is smaller than the rare earth aluminate phosphor crystal phase of the rare earth aluminate sintered body according to Example 1, and it was confirmed that the rare earth aluminate sintered body using rare earth aluminate phosphor particles as a raw material has a smaller rare earth aluminate phosphor crystal phase.

[0107] FIG. 8 is an SEM image of the surface of the rare earth aluminate sintered body according to Example 5, and FIG. 9 is an SEM image of the rare earth aluminate sintered body according to Example 8. FIG. 11 is an SEM image of the surface of the rare earth aluminate sintered body according to Comparative Example 4. It was confirmed that the rare earth aluminate sintered bodies according to Examples 5 and 8 have smaller individual rare earth aluminate phosphor crystal phases than the rare earth aluminate sintered body according to Comparative Example 4. The rare earth aluminate phosphor crystal phase of the rare earth aluminate sintered body according to Example 8 is smaller than the rare earth aluminate phosphor crystal phase of the rare earth aluminate sintered body according to Example 5, and it was confirmed that the rare earth aluminate sintered body using rare earth aluminate phosphor particles as a raw material has a smaller rare earth aluminate phosphor crystal phase. [Industrial Applicability]

[0108] The rare earth aluminate sintered body according to the present disclosure can be used in combination with an excitation light source as a wavelength conversion member for vehicle-mounted or general lighting devices, backlights for liquid crystal display devices, and light sources for projectors. [Explanation of symbols]

[0109] 100: light emitting device, 101: excitation light source, 102: collimating lens, 103, 105 and 106: condenser lenses, 104: dichroic mirror, 107: rod integrator, 110: phosphor device, 111: rare earth aluminate sintered body, 112: rotation mechanism, 113: heat sink.

Claims

1. The rare earth aluminate phosphor includes a crystal phase of a rare earth aluminate phosphor and voids, and 90% or more of the rare earth aluminate phosphor has an absolute maximum length measured under the following measurement conditions within a range of 0.4 μm or more and 1.3 μm or less, and 90% or more of the voids has an absolute maximum length measured under the following measurement conditions within a range of 0.1 μm or more and 1.2 μm or less, The rare earth aluminate sintered body, wherein the rare earth aluminate phosphor crystal phase contains rare earth aluminate phosphor crystals having a composition represented by the following formula (I): (Ln 1 1-n Ce n ) 3 (Al 1-m M 1 m ) 5k O 12 (I) (In the formula (I), Ln 1 is at least one rare earth element selected from the group consisting of Y and Lu, M 1 is at least one element selected from the group consisting of Ga and Sc, and m, n, and k satisfy 0≦m≦0.02, 0.002≦n≦0.017, and 0.95≦k≦1.05, respectively.) Measurement conditions The distance between the two most distant points on the outline of one of the rare earth aluminate phosphor crystal phases or the voids included in the measurement range on the surface or cross section of the rare earth aluminate sintered body is defined as the absolute maximum length.

2. In a SEM image obtained by photographing the surface or cross section of the rare earth aluminate sintered body with a scanning electron microscope, an area of ​​12096 μm ２ The rare earth aluminate sintered body according to claim 1 , wherein the measurement range is a range in which

3. 3. The rare earth aluminate sintered body according to claim 1, wherein the absolute maximum length at 50% cumulative frequency in a particle size distribution of the absolute maximum length on a number basis of the rare earth aluminate phosphor crystal phase is within a range of 0.4 μm or more and 0.9 μm or less.

4. 4. The rare earth aluminate sintered body according to claim 1, which is formed only by the rare earth aluminate phosphor crystal phase and the voids.

5. 5. The rare earth aluminate sintered body according to claim 1, wherein the absolute maximum length at a cumulative frequency of 50% in a particle size distribution of the absolute maximum length based on the number of voids is within a range of 0.3 μm or more and 0.8 μm or less.

6. 6. The rare earth aluminate sintered body according to claim 1, wherein the rare earth aluminate phosphor crystal phase contains Lu in its composition, and the absolute maximum length of the rare earth aluminate crystal phase is in the range of 0.4 μm to 2.3 μm.

7. 7. The rare earth aluminate sintered body according to claim 1, wherein the rare earth aluminate phosphor crystal phase contains Lu in its composition, and the absolute maximum length of the voids is within a range of 0.1 μm to 2.3 μm.

8. The rare earth aluminate sintered body according to claim 6 or 7, wherein the rare earth aluminate phosphor crystal phase comprises a rare earth aluminate phosphor crystal phase having a composition represented by the following formula (Ia): (Lu 1-q-n Ln 2 q Ce n ) 3 (Al 1-m M 1 m ) 5k O 12 (Ia) (In the formula (Ia), Ln 2 is at least one rare earth element selected from the group consisting of La, Gd and Tb, M 1 is at least one element selected from Ga and Sc, and q, m, n and k are numbers satisfying q=0, 0≦m≦0.02, 0.002≦n≦0.017, 0.95≦k≦1.05, respectively, with the proviso that the variables m, n and k in the formula (Ia) are numbers when the sum of the molar ratio of Lu, the molar ratio of Ln 2 and the molar ratio of Ce based on analytical values ​​is 3.)

9. 7. The rare earth aluminate sintered body according to claim 1, wherein the rare earth aluminate phosphor crystal phase contains Y in its composition, and the absolute maximum length of the rare earth aluminate phosphor crystal phase is in the range of 0.4 μm to 2.1 μm.

10. 10. The rare earth aluminate sintered body according to claim 1, wherein the rare earth aluminate phosphor crystal phase contains Y in its composition, and the absolute maximum length of the voids is within a range of 0.1 μm to 3.0 μm.

11. The rare earth aluminate sintered body according to claim 9 or 10, wherein the rare earth aluminate phosphor crystal phase comprises a rare earth aluminate phosphor crystal phase having a composition represented by the following formula (Ib): (Y 1-p-n Ln 3 p Ce n ) 3 (Al 1-m M 1 m ) 5k O 12 (Ib) (In the formula (Ib), Ln 3 is at least one rare earth element selected from the group consisting of La, Gd and Tb, M 1 is at least one element selected from Ga and Sc, and p, m, n and k are numbers satisfying p=0, 0≦m≦0.02, 0.002≦n≦0.017, 0.95≦k≦1.05, respectively, with the proviso that the variables m, n and k in the formula (Ib) are numbers when the sum of the molar ratio of Y, the molar ratio of Ln 3 and the molar ratio of Ce based on analytical values ​​is 3.)

12. At least one rare earth element Ln selected from the group consisting of Y and Lu １ preparing a slurry-like raw material mixture by mixing oxide particles containing Ce, oxide particles containing Al, and oxide particles containing Al in a liquid; drying the raw material mixture to obtain a raw material mixture powder; forming the raw material mixture powder into a compact; sintering the molded body at a temperature in the range of 1300° C. to 1800° C. to obtain a sintered body; In preparing the raw material mixture, １ The specific surface area of ​​at least one oxide particle selected from the group consisting of oxide particles containing Ce, and oxide particles containing Al, as measured by a BET method, is 5 m ２ / g or more, A method for producing a rare earth aluminate sintered body, comprising the steps of: obtaining a rare earth aluminate sintered body containing a rare earth aluminate phosphor crystal phase having a composition represented by the following formula (I): (Ln 1 1-n Ce n ) 3 (Al 1-m M 1 m ) 5k O 12 (I) (In the formula (I), Ln 1 is at least one rare earth element selected from the group consisting of Y and Lu, M 1 is at least one element selected from the group consisting of Ga and Sc, and m, n, and k satisfy 0≦m≦0.02, 0.002≦n≦0.017, and 0.95≦k≦1.05, respectively.)

13. In preparing the raw material mixture, a specific surface area measured by the BET method is 5 m ２ The method for producing a rare earth aluminate sintered body according to claim 12, further comprising the step of: adding rare earth aluminate phosphor particles having a surface roughness of 1 / g or more to the raw material mixture.

Images