Fiber-reinforced composite material and its manufacturing method

Abstract

The present invention addresses the problem of developing and providing a fiber-reinforced composite that contains bagworm moth silk threads as reinforcing fibers, and is isotropic in terms of elastic modulus and strength.　Provided is a fiber-reinforced composite containing, as reinforcing fibers, a nonwoven fabric comprising bagworm moth silk threads.

Description

[Technical field]

[0001] The present invention relates to a fiber-reinforced composite material comprising a nonwoven fabric containing bagworm silk as a reinforcing fiber, and a method for producing the same. [Background technology]

[0002] Fiber-reinforced composite materials, which are made by combining reinforcing fibers and a base material, are lightweight materials with high strength and elastic modulus, as typified by carbon fiber-reinforced plastics (CFRP) and glass fiber-reinforced plastics (GFRP). Such high strength and elastic modulus are largely based on the mechanical properties of reinforcing fibers such as carbon fiber, glass fiber, and aramid fiber. For example, it is known that carbon fiber has mechanical properties about 10 times that of iron in terms of specific strength, which is the strength divided by the mass of the material (Non-Patent Document 1). Due to such mechanical properties, fiber-reinforced composite materials are used in various fields, including sports and leisure goods, automobiles, houses, buildings, and aircraft, as alternative materials to metals.

[0003] However, all conventional reinforcing fibers used in fiber-reinforced composite materials have a common property of being "inelastic." This property is the main cause of "brittleness" and "peeling" at the interface between the reinforcing fiber and the matrix in fiber-reinforced composite materials. Peeling from the reinforcing fiber in fiber-reinforced composite materials is a serious problem, especially when the matrix is ​​flexible.

[0004] Therefore, attempts have been made to solve this problem by using fibers that have elongation properties in addition to high strength and elastic modulus as next-generation reinforcing fibers in fiber-reinforced composite materials. For example, spider silk (often referred to as "spider silk" in this specification), which has extremely high toughness and elongation properties, is currently attracting attention as a next-generation reinforcing fiber (Non-Patent Document 2).

[0005] However, when spider silk is actually used as a reinforcing fiber, there are many problems to be solved in terms of mass productivity and production costs. For example, it is difficult to mass-breed spiders like silkworms, and it is not possible to directly mass-produce spider silk. Therefore, mass production of spider silk is not easy, resulting in a problem of high production costs. The problem of mass production of spider silk is currently being solved by recombinant gene technology using E. coli and silkworms (Patent Document 1 and Non-Patent Document 3). However, this method involves new problems. Since the E. coli and silkworms used in the production of spider silk are recombinant, they can only be cultured and bred in facilities equipped with the required equipment. Therefore, a large-scale production facility is required to produce a commercial-level amount. In addition, the maintenance costs are also enormous. Furthermore, since the spider silk protein obtained from E. coli is liquid, an increase in the number of manufacturing steps is unavoidable in converting it into fiber. Therefore, when using spider silk as a reinforcing fiber, even if the mass production problem can be solved, the production cost problem remains unsolved.

[0006] Against this technical background, the present inventors have developed a technology for producing fiber-reinforced composite materials that use silk spun by basket worms (also known as "bag worms") (often referred to as "bagworm silk" in this specification) as the reinforcing fiber instead of spider silk (Patent Document 2).

[0007] Bagworms are a general term for the larvae of moths belonging to the family Psychidae in the order Lepidoptera. The silk spun by these insects has a good balance between strength and elongation, and has mechanical properties superior to silkworm silk and spider silk. For example, the elastic modulus of bagworm silk from the brown bagworm moth (Eumeta minuscula) is 3.5 times that of silkworm silk and 2.5 times that of spider silk from the orb spider (Nephila clavata) (Non-Patent Documents 4 and 5). Furthermore, the present inventors have revealed that bagworm silk from the giant bagworm moth (Eumeta japonica) has similar mechanical properties when compared with silkworm silk and spider silk derived from the orb spider (Patent Document 3). For example, the elastic modulus was about five times that of silkworm silk and more than three times that of spider silk. Furthermore, its breaking strength was more than three times that of silkworm silk and about twice that of spider silk, and its breaking elongation was more than 1.3 times that of silkworm silk and almost equal to that of spider silk. In particular, its toughness was more than four times that of silkworm silk and more than 1.7 times that of spider silk, making it one of the toughest natural fibers. In fact, fiber-reinforced composite materials using bagworm silk as the reinforcing fiber had a higher elastic modulus than the polymer matrix alone, and when long-fiber bagworm silk was used, the problem of low breaking elongation, which was a challenge to solve with CFRP and GFRP, was significantly improved.

[0008] Furthermore, bagworms can be mass-reared like silkworms, and have the advantage of being easier to rear and manage than silkworms. For example, silkworms feed only on fresh leaves (mulberry leaves) of species belonging to the genus Morus, so the rearing area and rearing period depend on the source of mulberry leaves and the period when the leaves open, whereas bagworms are polyphagous and have low specificity for food leaves, so they can feed on the leaves of various tree species. Therefore, food leaves are easy to obtain and they can be reared in any area. Also, unlike mulberry, which is a deciduous tree, evergreen tree leaves can also be used as food leaves, so food leaves can be supplied throughout the year. Furthermore, bagworms are smaller in body size than silkworms and can be easily reared in large numbers, so they can be reared in large numbers even in a small rearing space. Therefore, rearing costs can be significantly reduced. In addition, bagworm silk can be directly extracted from bagworms, so special production facilities for the creation and maintenance of genetically modified organisms are not necessarily required. In addition, because there is no need to convert the fibers, the number of production steps is reduced. Therefore, bagworm silk can solve not only the mass production problem, but also the production cost problem that remained unsolved with spider silk. [Prior art documents] [Patent documents]

[0009] [Patent Document 1] WO2012 / 165477 [Patent Document 2] Patent application 2017-170648 [Patent Document 3] Patent Publication 2018-197415 [Non-patent literature]

[0010] [Non-Patent Document 1] Toru Hiramatsu, An Easy-to-Understand Introduction to Carbon Fiber Composites, Nikkan Kogyo Shimbun, 2015, Chapter 1. [Non-Patent Document 2] Mathijsen D., 2016, Reinforced Plastics, 60: 38-44. [Non-Patent Document 3] Kuwana Y, et al., 2014, PLoS One, DOI: 10.1371 / journal. pone.0105325 [Non-Patent Document 4] Shigeyoshi Osaki, 2002, Sen-i-Gakkaishi Journal (Fibers and Industry), 58: 74-78 [Non-Patent Document 5] Gosline JM et al., 1999, J. Exp. Biol. 202, 3295-3303 Summary of the Invention [Problem to be solved by the invention]

[0011] By using bagworm silk as a reinforcing fiber, the inventors have succeeded in developing a fiber-reinforced composite material with high strength, elastic modulus, and elongation properties not found in conventional products (Patent Application No. 2017-170648). On the other hand, if the strength and elastic modulus of a fiber-reinforced composite material are isotropic, the range of applications of the fiber-reinforced composite material can be further expanded.

[0012] Therefore, an objective of the present invention is to develop and provide a fiber-reinforced composite material that contains bagworm silk as a reinforcing fiber and has isotropy in elastic modulus and strength. [Means for solving the problem]

[0013] In order to solve the above problems, the inventors of the present invention have conducted extensive research and have succeeded in producing a fiber-reinforced composite material with isotropic strength, elastic modulus, and elongation by using bagworm silk, particularly long-fiber bagworm silk, and a nonwoven fabric with random fiber orientation as the reinforcing fiber. The present invention is based on the above research results and provides the following invention. (1) A nonwoven fabric containing bagworm silk. (2) A fiber-reinforced composite material comprising a polymer matrix and a nonwoven fabric incorporating bagworm silk. (3) The fiber-reinforced composite material described in (2), wherein the bagworm silk comprises long fiber silk. (4) A fiber-reinforced composite material according to (2) or (3), wherein the nonwoven fabric contains organic fibers other than bagworm silk, inorganic fibers, or a combination thereof. (5) The fiber-reinforced composite material according to (4), wherein the organic fiber is silkworm silk and / or spider silk. (6) The fiber-reinforced composite material according to any one of (2) to (5), wherein the polymer matrix is ​​a resin, glue, starch, agar, or a combination thereof. (7) A fiber-reinforced composite material according to any one of (2) to (6), in which the mass fraction of bagworm silk in the fiber-reinforced composite material is 0.5% by mass to 50% by mass. This specification includes the disclosures of Japanese Patent Application No. 2019-046521, which is the priority basis of this application. Effect of the Invention

[0014] According to the fiber-reinforced composite material of the present invention, it is possible to provide a fiber-reinforced composite material having high strength, elastic modulus, and elongation properties, and these physical properties are isotropic. [Brief description of the drawings]

[0015] [Figure 1] FIG. 1 shows the stress-strain curves of a BSNF / EVA composite material (a) and EVA resin alone (b) cut in the 0° direction. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0016] 1. Fiber-reinforced composite materials 1-1. Overview The first aspect of the present invention is a fiber-reinforced composite material. The fiber-reinforced composite material of the present invention is characterized in that a nonwoven fabric containing bagworm silk is used as a reinforcing fiber substrate. According to the present invention, it is possible to provide a fiber-reinforced composite material that has high strength, elastic modulus, and elongation properties not found in conventional CFRP or GFRP, and that has isotropic physical properties.

[0017] 1-2.Definition Terms frequently used in this specification are defined below. "Fiber-reinforced composite material" refers to a material in which two or more different materials, i.e., the reinforcing fibers and the matrix, are combined together in an integrated manner without being fused to each other.

[0018] In this specification, the term "reinforcing fiber" refers to a fiber substrate in a fiber-reinforced composite material. Generally, a reinforcing fiber is a reinforcing material that imparts strength to a fiber-reinforced composite material, but in this specification, the term "reinforcing fiber" refers to a reinforcing material that imparts at least one of strength, elastic modulus, and elongation to the fiber-reinforced composite material.

[0019] In this specification, the term "base material" is also referred to as "matrix" and refers to a supporting substrate in a fiber-reinforced composite material. In a fiber-reinforced composite material, the base material is usually the side to which strength is imparted. However, in the reinforcing fibers in this specification, not only the reinforcing fibers themselves can be reinforcing agents, but the base material can also be a reinforcing material that imparts strength to the reinforcing fibers as a filler that fills between the reinforcing fibers. In other words, in the fiber-reinforced composite material of the present invention, each component material enhances the respective advantages and / or complements each other's disadvantages. As a result, a fiber-reinforced composite material with new properties not present in the original materials can be obtained.

[0020] As used herein, the term "polymer matrix" refers to a base material made of an organic polymer and / or an inorganic polymer.

[0021] In this specification, "silk thread" refers to a protein thread spun by insect larvae and adults for the purposes of nesting, moving, fixing, spinning cocoons, capturing food, etc. "Silkworm silk thread" spun by silkworms when spinning cocoons is a typical silk thread. However, when simply referring to silk thread in this specification, it means bagworm silk thread unless otherwise specified. As mentioned above, bagworm silk thread is silk thread spun by bagworms, and more specifically, there is bagworm silk thread for scaffolding (referred to as "scaffolding silk thread" in this specification) and bagworm silk thread for nesting (referred to as "nest silk thread" in this specification). "Scaffolding silk thread" is silk thread spun by bagworms prior to moving, and functions as a scaffold to prevent them from falling off branches, leaves, etc. when moving. "Nest silk" refers to the silk that makes up the nest, and is spun to bind together leaf and branch pieces, and to create a comfortable environment for the inner walls of the nest, which are the living area. Generally, scaffold silk is thicker and mechanically stronger than nest silk.

[0022] Silk yarn includes single fibers, spun fibers, spun silk yarns, and aggregate fibers. A "single fiber" is a filament (monofilament) thread, which is the smallest unit constituting silk yarn, and refers to fiber components such as fibroin protein obtained by removing coating components such as sericin protein from spun fibers described later. A single fiber is usually obtained by subjecting spun fibers to a refining process. A "spun fiber" refers to silk thread spun by an insect. For example, the spun fiber of a bagworm is composed of a difilament in which a pair of single fibers is bonded with a coating component. A "spun silk yarn" refers to a spun yarn obtained by spinning short fiber silk yarn described later. A "aggregated fiber" is a fiber composed of multiple silk fiber bundles, also called a multifilament. In this specification, an aggregate fiber is composed of a single fiber, spun fiber, spun silk yarn, or a combination thereof. The term "aggregated fiber" as used herein includes fibers composed only of silk threads derived from the same species, such as bagworm silk threads, and mixed fibers composed of multiple types of silk threads of different origins, such as bagworm silk threads and silkworm silk threads, or bagworm silk threads and spider silk threads. The term "aggregated fiber" includes not only twisted fibers, but also non-twisted fibers.

[0023] "Nonwoven fabric" refers to a material formed into a sheet by intertwining fibers without weaving them. The shape of the nonwoven fabric itself is not limited, and may be any shape such as cloth, paper, cotton, leather, etc. According to the nonwoven fabric terminology of Japanese Industrial Standards (JIS) L0222, nonwoven fabric is defined as "a fiber sheet, web, or batt in which the fibers are oriented in one direction or randomly and are bonded to each other by entanglement and / or fusion and / or adhesion, excluding paper, woven fabric, knitted fabric, tufted fabric, and crepe felt." In principle, the nonwoven fabric used in the present invention also conforms to this definition. However, in this specification, felt is exceptionally included in the nonwoven fabric.

[0024] In this specification, "isotropic" means that the physical properties are not dependent on the direction. For example, if the fiber-reinforced composite material has a planar shape such as a sheet, it means that it exhibits the same strength, elastic modulus, and elongation in any direction on the plane. If the fiber-reinforced composite material has a three-dimensional shape, it means that it exhibits the same strength, elastic modulus, and elongation in any direction in three-dimensional space. In addition, in this specification, "isotropic" means that it has isotropic properties. On the other hand, the fact that the physical properties depend on the direction is called "anisotropic", and the fact that it has such properties is called "anisotropy". For example, in a sheet-shaped fiber-reinforced composite material, if the physical properties in an arbitrary direction on the plane are different from the physical properties in the direction perpendicular to that direction, the fiber-reinforced composite material is said to be anisotropic.

[0025] 1-3.Configuration 1-3-1. Components The fiber-reinforced composite material of the present invention contains reinforcing fibers and a polymer matrix as essential components. Each component will be described below. (1) Reinforced Fiber The fiber-reinforced composite material of the present invention contains a nonwoven fabric as a reinforcing fiber as an essential component fiber, and may contain one or more different fibers other than the nonwoven fabric as optional component fibers.

[0026] Furthermore, the nonwoven fabric is characterized in that it contains bagworm silk, and the nonwoven fabric itself can be one embodiment of the present invention. Each of the constituent fibers will be described below.

[0027] (1-1) Nonwoven fabric The nonwoven fabric is an essential component fiber as a reinforcing fiber in the fiber-reinforced composite material of the present invention. The greatest feature of the present invention is that the nonwoven fabric contains bagworm silk.

[0028] Bagworm silk is silk spun by bagworms. As mentioned above, bagworms are a general term for the larvae of moths belonging to the Psychidae family of the Lepidoptera order. Moths of the Psychidae family are distributed all over the world, and all larvae (bagworms) live in nests made of natural materials such as leaves and branches woven together with the silk they spun themselves throughout their entire larval stage. The nests are bag-like and can be spindle-shaped, cylindrical, conical, or other shapes that can encase the entire body. Bagworms usually hide in these nests, and are always with them when feeding or moving, and as a rule, pupation also takes place in the nest.

[0029] The type of bagworm moth from which the bagworm silk used for the nonwoven fabric is derived is not important. For example, the Psychidae family includes genera such as Acanthopsyche, Anatolopsyche, Bacotia, Bambalina, Canephora, Chalioides, Dahlica, Diplodoma, Eumeta, Eumasia, Kozhantshikovia, Mahasena, Nipponopsyche, Paranarychia, Proutia, Psyche, Pteroma, Siederia, Striglocyrbasia, Taleporia, Theriodopteryx, and Trigonodoma, and the species may belong to any of the genuses. Specific examples of bagworm species include Eumeta japonica, Eumeta minuscula, and Nipponopsyche fuscescens. In addition, the age of the larvae (bagworms) can be any age from the first to the final stage. In addition, both males and females are included. However, if the goal is to obtain thicker and longer bagworm silk threads, larger bagworms are preferred. For example, within the Psychidae family, larger species are preferred. Therefore, from the perspective of obtaining thicker and longer bagworm silk threads, Psilocybe aeruginosa and Psilocybe nigricans are suitable species of bagworms to be used in the present invention. Furthermore, within the same species, final instar larvae are more preferred, and females, which are larger in size, are more preferred.

[0030] The bagworm silk used in the nonwoven fabric may be either scaffold silk or nest silk, or a mixture of the two.

[0031] The length of the bagworm silk thread used in the nonwoven fabric does not matter. It may be short fibers (short fiber silk thread), long fibers (long fiber silk thread), or a combination of both. However, in order to achieve the isotropy of strength, elastic modulus, and elongation that is the objective of the present invention, it is preferable to contain long fibers. In other words, only long fibers or a combination of long fibers and short fibers is preferable.

[0032] In this specification, "short fiber" refers to silk threads whose major axis length is 1.0 mm or more and less than 1 m, 1.5 mm or more and less than 80 cm, 2 mm or more and less than 60 cm, 2.5 mm or more and less than 50 cm, 3 mm or more and less than 40 cm, 3.5 mm or more and less than 30 cm, 4 mm or more and less than 20 cm, 4.5 mm or more and less than 10 cm, and 5.0 mm or more and less than 5 cm. Specific examples of short fibers include spun fiber fragments less than 1 m long derived from scaffold silk threads or nest silk threads, and single fiber fragments obtained by refining them.

[0033] In this specification, "long fiber" refers to silk threads having a fiber length of 1 m or more, 2 m or more, preferably 3 m or more, more preferably 4 m or more, 5 m or more, 6 m or more, 7 m or more, 8 m or more, 9 m or more, or 10 m or more. The fiber length may be obtained by spinning short fibers as in spun silk, but it is preferable that the fiber length is the length of a continuous fiber, that is, the length of a filament thread such as a single fiber or a spun fiber. In the case of silkworms, cocoons are spun by continuous spinning, so it is relatively easy to obtain long fiber silk threads of filament threads by refining the cocoons and spinning them. However, in the case of bagworms, they pupate in the nest, which is the habitat of the larvae, and therefore do not spin cocoons before pupation like silkworms. In addition, bagworm nests are generally expanded as they grow from the first instar, so new and old silk threads are mixed in the nest. In addition, at one end of the long axis of the bagworm nest, there is an opening that exposes part of the bagworm head and thorax to move and feed, and at the other end there is an excretion hole for excreting feces, etc. In other words, since there are always two holes, the silk thread is cut and discontinuous within the nest. In this way, the bagworm nest itself is composed of relatively short silk threads entangled. Therefore, it is not possible to obtain long fiber silk threads of filament threads from the nest by normal methods. In this way, in the case of bagworm silk threads, it has been technically impossible to obtain filament threads of 1m or more due to the unique ecology of bagworms. The present inventors have succeeded in solving this problem using the method disclosed in JP 2018-197415 A.

[0034] There is no particular limitation on the method for producing the nonwoven fabric used as the reinforcing fiber in the fiber-reinforced composite material of the present invention. The nonwoven fabric may be produced by a known method using the short fibers and / or long fibers of the bagworm silk as the material.

[0035] A typical method for producing a nonwoven fabric includes a fleece forming step of collecting fibers and a fiber bonding step of bonding the collected fibers.

[0036] For example, the dry method, wet method, spunbond method, meltblown method, flash spinning method, etc. are known for the fleece formation process, and any of these methods may be used. The dry method is a method in which fibers are oriented in a certain direction or randomly by air flow or the like to form a fiber accumulation layer. The wet method is a method in which short fibers are dispersed in a liquid and spun up with a net to form a fiber accumulation layer. The spunbond method, meltblown method, and flash spinning method are all direct spinning methods in which molten raw materials are discharged from a nozzle, spun, and accumulated in a sheet shape. Although this method is generally applied to chemical fibers, since recombinant bagworm silk protein can be operated in a liquid state, this method can also be used to form a fleece.

[0037] Known fiber bonding processes include thermal bonding, chemical bonding, needle punching, and hydroentanglement, and any of these may be used. The thermal bonding method is a method in which fleece mixed with low-melting point heat-fusible fibers is thermally compressed to bond the fibers together. The chemical bonding method is a method in which fleece is impregnated or sprayed with an emulsion adhesive resin, and then heated and dried to bond the intersections of the fibers. The needle punch method is a method in which a fleece is repeatedly pierced with a needle that moves up and down at high speed to entangle the fibers. The hydroentanglement method is a method in which a high-pressure water stream is sprayed in a columnar shape onto the fleece to entangle the fibers.

[0038] In addition, in the case of bagworm silk, nonwoven fabrics can be produced by a method of harvesting silk specific to bagworms. For example, the simplest method of producing nonwoven fabrics made of bagworm silk is to obtain it from bagworm nests. As mentioned above, bagworm nests are made of short fibers of bagworm silk entangled together, so the nests themselves are constructed as nonwoven fabrics. Therefore, nonwoven fabrics made of bagworm silk can be obtained by cutting open a bagworm nest, spreading it out flat, and removing the nest material leaves and twigs. However, since it is almost impossible to completely remove the nest material from bagworm silk, impurities are inevitably mixed into the nonwoven fabrics obtained by this method. In reinforcing fibers, the presence of such impurities can cause a decrease in the quality and physical properties of fiber-reinforced composite materials, and may offset the advantages of using bagworm silk as a reinforcing fiber, so it is not originally preferable.

[0039] In addition, a nonwoven fabric made of bagworm silk can be produced using, for example, the silk harvesting method disclosed in Japanese Patent Application No. 2018-078522, but is not limited thereto. In this method, one or more bagworms are placed on a solvent-soluble or heat-fusible substrate, and the scaffold silk is spun onto the substrate surface until a thin film can be formed. The substrate itself is then dissolved in a solvent that does not damage, denature, or dissolve the bagworm silk, or is heated and melted at a temperature that does not damage, denature, or melt the bagworm silk, and the substrate components and the spun scaffold silk can be separated to obtain a nonwoven fabric made of a thin film of scaffold silk.

[0040] The solvent-soluble substrate used in this method includes a water-soluble substrate (water-soluble material) composed of a substance soluble in water or an aqueous solution, and a low-polarity solvent-soluble substrate composed of a substance soluble in a low-polarity solvent. All substrates are solid in a dry environment, that is, under standard conditions (15°C to 25°C and atmospheric pressure conditions) and at a humidity of 50% or less, preferably 40% or less, 30% or less, 20% or less, or 10% or less. Examples of water-soluble substrates include gelatin, starch, and pullulan, and examples of low-polarity solvent-soluble substrates include polystyrene, vinyl acetate, cellulose acetate, acrylic resin, and polycarbonate.

[0041] The heat-fusible substrate is a substrate that is in a solid state under standard conditions and can be easily melted and turned into a liquid state by heating. The melting point of the heat-fusible substrate may be lower than the temperature at which the bagworm silk thread is damaged, thermally denatured, or melted. Since the bagworm silk thread begins to thermally decompose at temperatures above 260°C, the melting point may be at least 260°C or lower. However, in order to reduce heating costs and not expose the bagworm silk thread to higher temperatures than necessary, a range of, for example, 40°C to 100°C, 45°C to 98°C, 50°C to 95°C, 55°C to 90°C, 60°C to 85°C, 65°C to 80°C, or 70°C to 75°C is appropriate.

[0042] In addition, a nonwoven fabric made of bagworm silk can be obtained using the silk harvesting method disclosed in Japanese Patent Application No. 2017-251904. This method utilizes the bagworm's habit of quickly starting nesting behavior using nesting material to protect and keep warm when a naked bagworm is taken out of its nest and given nesting material. After giving a solvent-soluble or heat-soluble substance as nesting material to a naked bagworm and allowing it to build a nest, the nesting material is dissolved in a solvent that does not damage, denature, or dissolve the bagworm silk, or is melted by heating at a temperature that does not damage, denature, or melt the bagworm silk, and the dissolved nesting material and the bagworm silk are separated to obtain the remaining nest silk as a nonwoven fabric. Although there are differences between the scaffold silk and the nest silk in the above-mentioned Japanese Patent Application No. 2018-078522, the conditions such as the base material components, solvent, and melting temperature are basically the same as those in the above-mentioned Japanese Patent Application No. 2018-078522.

[0043] Furthermore, a nonwoven fabric made of bagworm silk can be obtained by the silk harvesting method disclosed in Japanese Patent Application No. 2018-158762. In this method, one or more bagworms are placed on a substrate and allowed to spin the scaffold silk threads until a thin film can be formed on the substrate surface. A wetting liquid is then sprayed or applied to the bagworm silk threads spun onto the substrate surface to separate the substrate from the bagworm silk threads, thereby obtaining a nonwoven fabric made of a thin film of the scaffold silk threads.

[0044] The wetting liquid used in this method is a pure substance or mixture that has a melting point below 20°C and a boiling point between 30°C and 300°C under atmospheric pressure, that is in a liquid state at least between 20°C and 30°C, and that does not damage, denature, or dissolve the fibroin protein, which is the fiber component of bagworm silk. Examples of this include ethanol, an aqueous solution, or an organic solvent.

[0045] The silk harvesting methods described in the above three applications make it possible to obtain nonwoven fabrics made of pure bagworm silk that are completely free of impurities such as dead leaves, dead branches, and other nesting materials. This means that it is possible to impart only the advantages of bagworm silk as a reinforcing fiber to a fiber-reinforced composite material, without causing a deterioration in the quality or physical properties of the fiber-reinforced composite material.

[0046] The nonwoven fabric of the present invention may be made of one or more kinds of bagworm silk threads. For example, it may be made of only bagworm silk threads derived from the giant bagworm moth, or it may be made of two kinds of bagworm silk threads derived from the giant bagworm moth and the brown bagworm moth. The manufacturing method of a nonwoven fabric made of multiple kinds of bagworm silk threads may basically be the same as the manufacturing method of a nonwoven fabric made of one kind of bagworm silk thread. For example, it can be manufactured by spinning the bagworms of the giant bagworm moth and the brown bagworm moth on the same substrate. Bagworm silk threads generally have the above-mentioned physical properties in common regardless of the species they are derived from, but depending on the species, there may be differences in their characteristics, such as silk threads with a particularly high elastic modulus, silk threads with high breaking strength, or silk threads with high toughness. When the physical properties differ between species, the bagworm silk threads of those species can be combined to enhance each other's advantages and complement each other's disadvantages.

[0047] In addition, the nonwoven fabric of the present invention may further contain one or more other fibers different from bagworm silk within a range that does not impair the effects of the present invention. For example, organic fibers or inorganic fibers can be mentioned. Organic fibers include natural plant fibers such as cotton and hemp, which are mainly composed of cellulose, silk obtained from insects such as domestic silkworms such as silkworms or wild silkworms, which are the larvae of moths of the Saturniidae family, and natural animal fibers such as spider silk, and chemically synthesized fibers such as aramid, polyamide (including nylon), polyester, polyethylene, acrylic, and rayon. Inorganic fibers include carbon fibers, glass fibers, metal fibers (stainless steel, titanium, copper, aluminum, nickel, iron, tungsten, molybdenum, etc.), and amorphous fibers (ceramic fibers, rock wool, etc.).

[0048] By combining bagworm silk with other fibers to make a nonwoven fabric, a synergistic effect between the fibers can be obtained. For example, carbon fiber and glass fiber boast extremely high strength and elastic modulus, but have low toughness and are brittle because they lack elongation properties. On the other hand, bagworm silk has high strength and elastic modulus, but does not reach those of carbon fiber or glass fiber. However, bagworm silk has elongation properties that carbon fiber and glass fiber do not have. Therefore, by combining bagworm silk with carbon fiber and / or glass fiber to make a nonwoven fabric, it is possible to take advantage of the advantages of both and complement each other's disadvantages. By using a nonwoven fabric combining bagworm silk with carbon fiber and / or glass fiber as a reinforcing fiber, a fiber-reinforced composite material with extremely high strength and elastic modulus and elongation properties can be produced.

[0049] When the nonwoven fabric of the present invention contains other fibers in addition to bagworm silk, the content of bagworm silk in the reinforcing fibers when used in a fiber-reinforced composite material is not limited. For example, the content of bagworm silk in the reinforcing fibers may be 1% by mass or more, 3% by mass or more, 5% by mass or more, 8% by mass or more, 10% by mass or more, 15% by mass or more, 20% by mass or more, 25% by mass or more, 30% by mass or more, 35% by mass or more, 40% by mass or more, 45% by mass or more, 50% by mass or more, 55% by mass or more, 60% by mass or more, 65% by mass or more, 70% by mass or more, 75% by mass or more, 80% by mass or more, 85% by mass or more, 90% by mass or more, 92% by mass or more, 95% by mass or more, 97% by mass or more, 98% by mass or more, or 99% by mass or more.

[0050] (1-2) Other fibers The reinforcing fibers constituting the fiber-reinforced composite material of the present invention may include, in addition to the nonwoven fabric, one or more different fibers as optional constituent fibers.

[0051] The composition of the fibers other than the nonwoven fabric that can be used as reinforcing fibers basically conforms to that of the fibers constituting the nonwoven fabric. That is, in addition to one or more types of short and / or long fibers of bagworm silk, it can contain organic fibers such as natural plant fibers, natural animal fibers, and chemically synthesized fibers, and / or inorganic fibers such as carbon fibers, glass fibers, metal fibers, and amorphous fibers. In the fiber-reinforced composite material, these fibers can be in any shape other than the nonwoven fabric. For example, in addition to a simple string shape (thread shape), woven fabric, knitted fabric, or sheet shape such as paper, or a combination thereof can be mentioned.

[0052] When the reinforcing fibers constituting the fiber-reinforced composite material of the present invention include one or more other fibers in addition to the nonwoven fabric, the content of the other fibers in the reinforcing fibers is not limited. However, since the nonwoven fabric is the main reinforcing fiber component in the fiber-reinforced composite material of the present invention, it is preferable that the content of the nonwoven fabric is higher in principle. For example, it is preferable that the content of the other fibers is 1 mass% or less, 3 mass% or less, 5 mass% or less, 8 mass% or less, 10 mass% or less, 15 mass% or less, 20 mass% or less, 25 mass% or less, 30 mass% or less, 35 mass% or less, 40 mass% or less, 45 mass% or less, or less than 50 mass% in mass fraction.

[0053] (2) Polymer matrix The polymer matrix refers to a base material made of an organic polymer and / or an inorganic polymer, and the polymer matrix used in the fiber-reinforced composite material of the present invention means either or both of an organic polymer and an inorganic polymer. The organic polymer referred to here includes natural polymers and synthetic polymers.

[0054] Natural polymers are polymers that exist in nature, such as proteins, polysaccharides, and natural resins. Specific examples of proteins include glue (including collagen and gelatin). Specific examples of polysaccharides include starch, cellulose, mannan, agar, and the like. Specific examples of natural resins include lacquer, rosin, latex (natural rubber), and shellac.

[0055] Synthetic polymers are polymers obtained by linking monomers through a condensation reaction or an addition polymerization reaction, and examples of such polymers include synthetic resins and synthetic rubbers.

[0056] Synthetic resins are also called plastics. The synthetic resin used as the polymer matrix in the fiber-reinforced composite material of the present invention may be any of a thermosetting resin, a thermoplastic resin, or a combination thereof. Examples of the thermosetting resin include epoxy resin, unsaturated polyester resin, vinyl ester resin, and phenolic resin. Examples of the thermoplastic resin include polyethylene, polypropylene, polyester, polystyrene, polyvinyl chloride, methacrylic resin, fluororesin, polycarbonate, polyurethane, aromatic polyether ketone resin, and polyphenylene sulfide resin.

[0057] Examples of synthetic rubber include butadiene rubber, chloroprene rubber, styrene butadiene rubber, isoprene rubber, ethylene propylene rubber, nitrile rubber, silicone rubber, acrylic rubber, fluororubber, and urethane rubber.

[0058] (3) Component ratio The blending ratio of the reinforcing fiber and the polymer matrix in the fiber-reinforced composite material of the present invention is not particularly limited. Usually, the reinforcing fiber may be blended at a ratio that can impart high strength, high elastic modulus, elongation, etc., which are the target properties of the reinforcing fiber, to the polymer matrix, which is the base material. In the fiber-reinforced composite material of the present invention, a blending ratio that can impart elongation, which is a property of bagworm silk, to the polymer matrix in addition to high strength and high elastic modulus is preferable. Specifically, the mass fraction of bagworm silk relative to the total dry mass of the fiber-reinforced composite material is 0.5% by mass to 50% by mass, 0.8% by mass to 40% by mass, 1% by mass to 35% by mass, 1.5% by mass to 30% by mass, 2% by mass to 28% by mass, or 3% by mass to 25% by mass.

[0059] 1-3-2. Structure The structure of the fiber-reinforced composite material of the present invention, i.e., the arrangement of the reinforcing fibers and the polymer matrix in the fiber-reinforced composite material, is not particularly limited. For example, a prepreg in which a nonwoven fabric, which is the main reinforcing fiber, is impregnated with a liquid polymer matrix, and a state in which a plurality of prepregs are laminated so that the orientation of the reinforcing fibers is different and integrated into a structure, etc., can be mentioned. In addition to the above structure, a state in which reinforcing fibers other than the nonwoven fabric are dispersed in the polymer matrix layer and / or on its surface can also be mentioned. Note that the above-mentioned prepreg is originally an intermediate material of the fiber-reinforced composite material, but is included in the fiber-reinforced composite material in this specification.

[0060] 1-4.Effects The fiber-reinforced composite material of the present invention incorporates a nonwoven fabric containing bagworm silk as a reinforcing fiber, making it possible to provide a fiber-reinforced composite material that has a well-balanced and high value of strength, elastic modulus, and elongation that is not found in conventional CFRP or GFRP, and in which these physical properties are isotropic.

[0061] 1-5.Applications The fiber-reinforced composite material of the present invention can be used in various fields including the applications of conventional fiber-reinforced composite materials. For example, sports and leisure (golf shafts, rackets, fishing rods, bicycle parts, etc.), housing (bathtubs, septic tanks, etc.), civil engineering and construction (earthquake-resistant reinforcement materials, lightweight building materials, wall and floor reinforcement materials, truss structural materials, etc.), transportation equipment (automobiles, ships, airplanes, helicopters, high-pressure hydrogen tanks, etc.), industrial equipment (casings, home appliance parts, printed circuit boards, wind power generation blades, etc.), and space-related (rockets, artificial satellites, etc.). In particular, the fiber-reinforced composite material of the present invention has high strength and elastic modulus, as well as properties of "elongation" and "toughness" that are not found in conventional fiber-reinforced composite materials such as CFRP and GFRP, and furthermore, these physical properties are isotropic, so that it is suitable for use in material fields that require elongation in addition to strength and elastic modulus.

[0062] Furthermore, when the reinforcing fibers are animal fibers such as bagworm silk or bagworm silk and silkworm silk, and the polymer matrix is ​​natural organic polymers such as collagen and gelatin, a fiber-reinforced composite material with high biocompatibility is obtained, which can be used in the medical field as a tissue regeneration substrate or blood vessel regeneration substrate.

[0063] Furthermore, nonwoven fabrics containing the bagworm silk of the present invention can be used as medical materials (masks, wound dressings, anti-adhesion membranes, artificial skin, etc.), filters, industrial materials (wall coverings and decorative materials, etc.), and beauty salon materials (packaging materials, etc.).

[0064] 2. Fiber-reinforced composite material manufacturing method 2-1. Overview A second aspect of the present invention is a method for producing a fiber-reinforced composite material. The method of the present invention is a method for producing and / or molding the fiber-reinforced composite material according to the first aspect. According to the production method of the present invention, a fiber-reinforced composite material containing bagworm silk can be easily produced and molded.

[0065] 2-2. Method The manufacturing method of the fiber-reinforced composite material of the present invention is basically the same as that of conventional fiber-reinforced composites, except that bagworm silk is used as the reinforcing fiber. For example, when using long bagworm silk as the reinforcing fiber, the manufacturing method usually used for CFRP or GFRP can be used as is. There are various manufacturing methods known, and an appropriate method can be selected depending on the purpose such as the application and shape.

[0066] For example, a method for producing a prepreg may involve impregnating a nonwoven fabric of reinforced fibers containing bagworm silk, or additionally woven fabrics, knitted fabrics, paper, etc. selected as reinforcement fibers, with a suitable polymer matrix. If the polymer matrix is ​​a thermosetting resin, the result is a semi-cured prepreg in which polymerization is incomplete. On the other hand, if the polymer matrix is ​​a thermoplastic resin or a natural polymer such as collagen, the result is a cured prepreg in which polymerization is complete.

[0067] In addition, the main molding methods include a sheet winding molding method, a press molding method, an autoclave molding method, a resin transfer molding (RTM) molding method, a vacuum resin transfer molding (VaRTM) molding method, a sheet molding compound (SMC) molding method, a vacuum bag molding method, a hand lay-up molding method, and a fiber placement molding method.

[0068] The "sheet winding molding method" is a molding method in which prepregs are wound around a rotating mold (mandrel) while being impregnated with a polymer matrix, and then de-cored after hardening. The "press molding method" is a molding method in which compounds and prepregs are placed in a mold and pressurized and heated to form the mold. The "autoclave molding method" is a molding method in which prepregs are layered in a mold, covered with a bag, and the air and volatile substances present in the autoclave are vacuum removed, and then pressurized and heated to form the mold. The "RTM molding method" is also called the resin injection molding method, and is a method in which molten thermosetting resin is introduced under low pressure into a closed system in which a preform of reinforcing fibers is placed in a mold, and the mold is removed after heat hardening. The "VaRTM molding method" is a type of RTM method in which a closed system in which reinforcing fibers are layered is evacuated, a thermosetting resin is introduced, and the mold is removed after heat hardening. The "SMC molding method" is a molding method in which sheet-like materials consisting of reinforcing fibers and a polymer matrix are layered and molded. The "vacuum bag molding method" is a method in which a laminate sealed with a sealed film is subjected to a vacuum and compression molding is performed at atmospheric pressure. The "hand lay-up molding method" is a method in which prepregs are manually laminated in a mold and then cured and molded. And the "fiber placement molding method" is a method in which prepregs processed into a tape form or tows impregnated with a polymer matrix are laminated in various three-dimensional molds and then cured and molded. The specific methods for these molding methods are all known in the field of fiber-reinforced composite materials, and these may be used as a reference.

[0069] 2-3. Manufacturing process The manufacturing process of the method for manufacturing a fiber-reinforced composite material of the present invention includes a contacting step as an essential step, and optionally includes a molding step, a curing step, and a demolding step. Each step will be specifically described below.

[0070] (1) Contact process The "contact step" is a step of contacting the reinforcing fiber with the polymer matrix. The contact method is not particularly limited as long as the two components can be directly contacted. The reinforcing fiber may be dispersed, immersed, or impregnated in a dissolved liquid polymer matrix, or a fiber bundle or sheet of the reinforcing fiber may be sandwiched between sheets of the polymer matrix as in the SMC molding method.

[0071] The above-mentioned prepreg is made by impregnating a sheet made of reinforcing fibers with a polymer matrix, and the manufacturing process is composed of only a contact process.

[0072] (2) Molding process "Forming" refers to the process of forming the reinforcing fibers and / or polymer matrix, which are the components of the fiber-reinforced composite material, into a desired shape. This is an optional process and can be performed according to various manufacturing methods.

[0073] In this process, a mold such as a die is used, and molding is performed according to the mold. Reinforcing fibers or prepregs can also be laminated and molded as necessary. The order of the molding process and the contact process described above varies depending on the manufacturing method and is not limited. For example, in the above-mentioned filament winding molding method, sheet winding molding method, press molding method, autoclave molding method, hand layup molding method, fiber placement molding method, etc., the molding process is performed after the contact process. On the other hand, in the RTM molding method and VaRTM molding method, after molding a preform of reinforcing fibers in a mold, the polymer matrix is ​​introduced into the mold, so the contact process is performed after the molding process. It may be performed according to each manufacturing method.

[0074] (3) Curing process The "curing step" refers to a step for promoting and / or completing the polymerization reaction of the polymer matrix after the previous step. This step hardens the polymer matrix and completes the fiber-reinforced composite material. The curing step may include a heating step and / or a cooling step.

[0075] The "heating step" is a step in which the polymer matrix is ​​heated to promote and / or complete the polymerization reaction. This step is performed when a thermosetting resin is used for the polymer matrix. On the other hand, when the polymer matrix is ​​a thermoplastic resin or a natural polymer, the polymerization is released by heating and the matrix softens or dissolves, so this step can be considered as the contacting step or the molding step.

[0076] The heating temperature is not particularly limited. It varies depending on the type of polymer matrix used, but it may be usually performed in the range of 20°C to 250°C, 23°C to 200°C, 25°C to 180°C, 27°C to 150°C, or 30°C to 120°C. The heating time is related to the heating temperature, and generally the lower the temperature, the longer the time, and the higher the temperature, the shorter the time. It may be usually performed in the range of 0.5 hours to 48 hours, 1 hour to 42 hours, 1.5 hours to 36 hours, 2 hours to 30 hours, 2.5 hours to 24 hours, or 3 hours to 18 hours.

[0077] The "cooling step" is a step in which the heated polymer matrix is ​​cooled or hardened by cooling. When a thermosetting resin is used for the polymer matrix, the cooling step is performed to cool the fiber-reinforced composite material after the thermosetting reaction is completed in the heating step. When a thermoplastic resin or a natural polymer is used for the polymer matrix, the polymerization reaction is accelerated and / or completed by cooling, and the fiber-reinforced composite material is completed by hardening the polymer matrix.

[0078] The cooling temperature is not limited. Although it varies depending on the type of polymer matrix used, it may be usually performed at 260°C or less, 200°C or less, 180°C or less, 150°C or less, 120°C or less, 100°C or less, 90°C or less, 80°C or less, 70°C or less, 60°C or less, 50°C or less, 40°C or less, 35°C or less, 30°C or less, 27°C or less, 25°C or less, 23°C or less, 20°C or less, 18°C ​​or less, 15°C or less, or 10°C or less. The lower limit temperature is not particularly limited, but it is usually about 4°C, 0°C, -10°C, -15°C, or -20°C. The cooling time may be in the range of 0.1 to 1 hour, 0.2 to 0.9 hours, 0.3 to 0.8 hours, 0.4 to 0.7 hours, or 0.5 to 0.6 hours.

[0079] (4) Demolding process The "demolding step" is a step of removing the fiber-reinforced composite material from the mold after the curing step. Specifically, in this step, the completed fiber-reinforced composite material is removed from the mold and mandrel used in the molding step. The demolding method may be a method known in the art. EXAMPLES

[0080] <Example 1: Production and properties of fiber-reinforced composite material containing nonwoven fabric of bagworm silk> (the purpose) We will create a fiber-reinforced composite material containing nonwoven fabric of bagworm silk as a reinforcing fiber and verify its physical properties.

[0081] (method) The bagworms used were larvae of the giant bagworm moth (bag length 10-15 mm) collected from a fruit orchard in Tsukuba City, Ibaraki Prefecture.

[0082] The bagworm silk nonwoven fabric was obtained in the following manner. Approximately 50 bagworms were released into a cubic breeding cage measuring approximately 20 cm in length, width, and height, and were raised for 7 days. The top plate of the breeding cage was made of acrylic and was removable. Bagworms have the tendency to move upwards, so they spend a long time on the underside of the cage top plate. As a result, multiple bagworms continue to spin their silk in a disorderly manner on the underside of the top plate, and after 7 days, a silk sheet consisting of accumulated bagworm silk (scaffold silk) was formed. This silk sheet was sprayed with 70% ethanol and then carefully peeled off from the top plate to obtain a nonwoven fabric (BSNF) derived from bagworm silk.

[0083] The polymer matrix used was ethylene-vinylacetate copolymer (EVA) resin.

[0084] For the EVA resin, we used hot gun adhesive resin (Taiyo Denki Sangyo Co., Ltd.). As a substitute for a metal mold, a circular mold with a diameter of about 80 mm was made from a 0.5 mm thick silicone rubber sheet, and after placing the EVA resin inside the mold, it was pressed at 100°C and about 2 MPa to produce two EVA resin sheets.

[0085] Next, a laminate (approximately 30 mm long and wide) consisting of 10 layers of bagworm silk nonwoven fabric (BSNF) as reinforcing fiber was sandwiched between the EVA resin sheets and pressed at approximately 2 MPa with two hot plates heated to 100°C. The laminate was then cooled to obtain a fiber-reinforced composite material (hereinafter referred to as "BSNF / EVA composite material") film consisting of BSNF and EVA resin with a thickness of approximately 270 μm. At the same time, a film of EVA resin alone (hereinafter referred to as "EVA resin") of the same thickness was also produced as a negative control by pressing only two EVA sheets without containing BSNF.

[0086] Next, strip-shaped test pieces with a width of about 1.5 mm and a length of about 20 mm were cut out from each film and subjected to mechanical testing. When cutting out the test pieces, first, an arbitrary direction of the nonwoven fabric was defined as the 0° direction, and the test pieces were cut out along the 0° direction. Next, test pieces were similarly cut out along angles (cut-out angles) of 30°, 60°, and 90° clockwise relative to the 0° direction. Finally, four types of test pieces with different cut-out angles from the film every 30° were obtained. In addition, the mass fraction of the reinforcing fibers relative to the total mass of the test pieces was calculated as the fiber content (mass%: wt%).

[0087] (Result 1) The mass fraction of reinforcing fibers relative to the total mass in each specimen of the BSNF / EVA composite was 4.3 wt%. The results of the mechanical tests on the test pieces of the BSNF / EVA composite material and the EVA resin are shown in Tables 1 and 2, respectively. The stress-strain curves of the test pieces cut in the 0° direction are shown in Figure 1.

[0088] [Table 1]

[0089] [Table 2]

[0090] In Tables 1 and 2, "elastic modulus" refers to the initial elastic modulus. This corresponds to the proportionality constant in the deformation range where the force and deformation are proportional when the sample is pulled, i.e., Hooke's law is satisfied, and is given as the slope of the initial gradient of the stress-strain curve. Generally, the larger the value, the smaller the deformation in response to tensile stress, and the harder the material is. Furthermore, "maximum strength" refers to the maximum stress immediately before breakage. Generally, the larger the value, the stronger the material can withstand. Furthermore, "strain" refers to the breaking elongation, which refers to the elongation until the sample breaks. Generally, the larger the value, the better the material can elongate.

[0091] (Result 2) For both EVA resin and BSNF / EVA composite material, almost no difference in the mechanical properties of elastic modulus and maximum strength due to the cut-out angle of the test pieces, i.e., anisotropy, was observed. Furthermore, the elastic modulus and maximum strength of the BSNF / EVA composite material were approximately twice as high as those of the EVA resin for all test pieces cut out at all cut-out angles. This indicates that the BSNF / EVA composite material is harder and stronger than the EVA resin. These results confirmed that by using bagworm silk nonwoven fabric as a reinforcing fiber, it is possible to give EVA resin hardness (high elastic modulus) and strength (high strength) isotropically.

[0092] Furthermore, the strain (elongation at break) of the BSNF / EVA composite material was approximately 40% for all test pieces with all cut-out angles measured. This result suggests that the problem of low elongation at break that occurs when carbon or glass fibers are used in fiber-reinforced composite materials can be significantly improved by using nonwoven fabric of bagworm silk.

[0093] In other words, it was revealed that by incorporating bagworm silk nonwoven fabric at a small content of approximately 4 wt% into a fiber-reinforced composite material, it was possible to isotropically and dramatically improve the mechanical properties of the polymer matrix, such as its strength and elastic modulus, while also imparting an extremely high elongation of approximately 40%, which is very high for a fiber-reinforced composite material. All publications, patents, and patent applications cited herein are hereby incorporated by reference in their entirety.

Claims

1. A fiber-reinforced composite material comprising a polymer matrix and a nonwoven fabric containing bagworm scaffold silk that is free of contaminants derived from nest materials.

2. The fiber-reinforced composite material of claim 1 , wherein the bagworm scaffold silk comprises long fiber silk.

3. The fiber-reinforced composite material of claim 1 or 2, wherein the nonwoven fabric further comprises organic fibers other than bagworm scaffold silk, inorganic fibers, or a combination thereof.

4. 4. The fiber-reinforced composite material according to claim 3, wherein the organic fibers are bagworm nest silk, silkworm silk and / or spider silk.

5. The fiber reinforced composite material according to any one of claims 1 to 4, wherein the polymer matrix is ​​a resin, a glue, a starch, an agar, or a combination thereof.

6. The fiber-reinforced composite material according to any one of claims 1 to 5, wherein the mass fraction of the bagworm scaffold silk in the fiber-reinforced composite material is 0.5% by mass to 50% by mass.