Method for producing solid biomass fuel

Abstract

To provide a method of producing a biomass fuel that has sufficient water resistance and homogeneity and is prepared from biomass sources that can be easily grown or collected in commercial scale.SOLUTION: A method of producing a solid biomass fuel of this invention includes: (i) a step of obtaining biomass powders having an average particle diameter (D50) of 1000 μm to 6000 μm by pulverizing one or more kinds of biomass sources; (ii) a step of obtaining a biomass molded material by molding the biomass powders; and (iii) a step of obtaining the solid biomass fuel by heating the biomass molded material at 160°C to 420°C for 0.25 to 5 hours.SELECTED DRAWING: None

Description

[Technical field]

[0001] The present invention relates to a method for producing a solid biomass fuel, as well as to the solid biomass fuel produced by said method. Additionally, the present invention relates to a combustion method comprising combusting said solid biomass fuel to produce energy. [Background technology]

[0002] Coal-fired power generation is used in power plants and industrial processes around the world. Coal and other fossil fuels are non-renewable energy resources. Over the past few decades, there has been a push to reduce coal consumption by coal-fired power plants and use renewable energy resources instead.

[0003] Fuels derived from biomass are examples of renewable energy sources that can be used to replace or at least partially replace coal. Biomass-derived fuels can be burned in the presence of oxygen in a combustion process in a power plant to produce energy. Biomass-derived fuels can be burned in traditional power plants originally designed for burning coal, or biomass-derived fuels can be burned in power plants built specifically for biomass burning. Certain forms of biomass can be mixed with coal and burned in the same combustion process in a power plant. Such a process is known as coal co-firing of biomass. To be suitable for co-firing with coal, biomass-derived fuels typically must have certain characteristics, such as a certain level of quality and uniformity in terms of properties. For example, biomass fuels composed of particles of uniform size, density, moisture content, etc. are particularly desirable in co-firing processes. It is also desirable for biomass fuels to contain low levels of ash. The ash levels in biomass-derived fuels are typically higher than those found in coal.

[0004] Various methods for producing solid biomass fuel from biomass sources are known. WO 2014 / 087949 discloses a method for producing solid biomass fuel, in which a biomass source is steam exploded before being formed into biomass blocks and then heated to form a biomass fuel. The method aims to produce a biomass fuel that is easy to handle during storage and has a reduced chemical oxygen demand (COD) of the wastewater during storage. The biomass source used in this method is palm kernel shell.

[0005] WO 2016 / 056608 discloses a method for producing a solid biomass fuel that builds on the teachings of WO 2014 / 087949 and does not require a steam explosion step to produce the fuel. The method includes a molding step in which the biomass source is crushed before the biomass block is heated and compressed and molded into a biomass block. Biomass sources taught for use in the method are trees such as Douglas fir, hemlock, cedar, cypress, Scots pine, old almond tree, almond shells, acacia wood, acacia bark, walnut shells, sago palm, empty fruit bunches of palm, meranti and rubber.

[0006] A similar method is disclosed in WO 2017 / 175733, which includes a molding step in which a biomass source is crushed before being heated, compressed and molded into a biomass block. The method of WO 2017 / 175733 is directed to obtaining a biomass fuel that exhibits low degradability when exposed to storm water and achieves reduced COD in the wastewater. The biomass source used in this method is selected from rubber trees, acacia, meranti, eucalyptus, teak, and a mixture of larch, spruce and birch.

[0007] WO 2019 / 069849 aims to obtain a biomass fuel that is easy to transport and store and resistant to spontaneous combustion during storage. The biomass fuel is produced by a method including a molding step in which a biomass source is crushed before the biomass block is heated, compressed and molded into a biomass block. The biomass source for fuel production is selected from rubber trees, acacia trees, radiata pine, a mixture of larch, spruce and birch, as well as spruce, pine and fir.

[0008] WO 2019 / 069860 discloses an apparatus for producing biomass solid fuel. The apparatus includes a carbonization furnace for carbonizing a biomass molded product to obtain a biomass solid fuel. The apparatus further includes a yield calculation unit, a temperature measurement unit, and a control unit. The control unit controls the heat applied to the carbonization furnace based on the spontaneous combustion characteristics of the biomass fuel. The biomass molded product is formed by pulverizing a biomass source into pellets before the pellets are molded into the biomass molded product. The biomass source is selected from rubber tree, acacia, dipterocarp, radiata pine, a mixture of larch, spruce, and birch, or a mixture of spruce, pine, and fir.

[0009] WO 2018 / 181919 discloses a different method of producing solid biomass fuel than those discussed above. The method involves a hydrothermal carbonization step of biomass, where the biomass source is pressurized in hot water to carbonize the biomass. The method is reported to obtain a biomass fuel with high grindability, high yield and low production cost. The biomass source is selected from husks, palm kernel shells, coconut, bamboo, palm empty fruit bunches, apricots and eggplants.

[0010] WO 2017 / 175737 discloses a cooling device for cooling carbonized biomass. The device improves the cooling efficiency of semi-carbonized molded biomass. The device cools the biomass by spraying water. The cooler includes a vibrating plate and a spraying section for spraying water onto the plate. Biomass fuel is produced by the same method as discussed above. Biomass sources for producing biomass fuel are Douglas fir, hemlock, Himalayan cedar, cypress, Scots pine, old almond tree, almond shell, acacia wood, acacia bark, walnut shell, sago palm, empty palm fruit bunch, meranti and rubber tree.

[0011] Finally, WO 2014 / 050964 discloses a method for improving the grindability of biomass so that it can be ground with coal. The method involves increasing the moisture content of the ground wood biomass to 10-50%, so that the biomass has a moisture content of 0.55 g / cm before subjecting the biomass to torrefaction. 3 The method involves compacting the biomass to a density of at least 1000 MPa. Biomass sources include wood chips, bark, shavings, and sawdust.

[0012] The inventors of the present invention understand that the solid biomass fuels and their production methods discussed in the above documents have various problems associated with them. For example, the biomass sources described in the above texts are all typically plants and trees that occur only in nature and are not easy to cultivate and harvest on a commercial scale. The inventors understand that it would be advantageous to have a biomass source that can be easily grown and harvested on a commercial scale. It also understands that it would be advantageous to have a biomass source that can be grown and harvested so that the quality and specific characteristics of the biomass source can be controlled.

[0013] In addition, the biomass sources described in the above documents are all composed of wood and similar materials, which have been found by the inventors of the present invention to form particles having a low degree of uniformity when subjected to conventional milling techniques known in the art. Furthermore, milling biomass sources is made expensive by the nature of wood and wood-like materials being difficult to mill. The inventors of the present invention have realized that it would be advantageous to have a biomass source that is more easily milled by conventional milling techniques known in the art and that forms particles of a more uniform size when milled.

[0014] In addition, it has been found by the inventors that solid biomass fuels prepared from the biomass sources and by the methods discussed in the above text do not have sufficient waterproof properties. Waterproof properties are important for solid biomass fuels, since they need to be dry (or at least dry enough) when used in a combustion process (by itself or when co-firing with coal). Biomass fuels are frequently exposed to moisture (such as rainwater) during storage or transportation. Therefore, biomass fuels with increased waterproofing capabilities are desirable.

[0015] The inventors have also realised that the biomass fuel production methods described in the above text do not provide fuel with sufficient quality and homogeneity. In particular, the methods discussed above do not provide sufficient control over the density of the biomass during the shaping step. [Prior art documents] [Patent documents]

[0016] [Patent Document 1] International Publication No. 2014 / 087949 Brochure [Patent Document 2] International Publication No. 2016 / 056608 Brochure [Patent Document 3] International Publication No. 2017 / 175733 Brochure [Patent Document 4] International Publication No. 2019 / 069849 Brochure [Patent Document 5] International Publication No. 2019 / 069860 Brochure [Patent Document 6] International Publication No. 2018 / 181919 Brochure [Patent Document 7] International Publication No. 2017 / 175737 Brochure [Patent Document 8] International Publication No. 2014 / 050964 Brochure Summary of the Invention [Problem to be solved by the invention]

[0017] The present invention addresses the problems discussed above associated with the prior art methods. It has been surprisingly discovered by the inventors of the present invention that certain biomass sources useful for obtaining solid biomass fuels can be grown and harvested on a commercial scale. By doing so, a well-established and consistent biomass source for fuel production can be obtained in a growing cycle. In addition, growing and harvesting said biomass source on a commercial scale allows for control of the quality and homogeneity of the biomass source, for example, by cultivation and breeding techniques. In addition, it has been found that said biomass source is more easily pulverized than the trees and woody sources considered in the prior art methods, resulting in reduced processing costs. It has also been found that the biomass source used in the present invention obtains greater homogeneity when pulverized compared to the biomass source used in the prior art. In addition to the above, the inventors of the present invention have also found that biomass fuels with improved waterproofing properties can be provided by modifying the forming and / or heating steps of the present method. Control of the forming and heating steps in the present method has also been found to improve the quality and homogeneity of the solid biomass fuel product, as well as impart certain physical characteristics that are rather highly favorable for use in combustion methods. The inventors have discovered that the properties of the biomass source, together with the particular features of the grinding, shaping and heating steps, act to produce a superior biomass fuel product for use in combustion processes than those known in the art. [Means for solving the problem]

[0018] According to a first aspect of the present invention, (i) pulverizing one or more biomass sources to obtain a biomass powder having an average particle size (D50) of 1000 μm to 6000 μm; (ii) molding the biomass powder to obtain a biomass molded product; (iii) heating the biomass molded article at a temperature of 160° C. to 420° C. for 0.25 to 5 hours to obtain a solid biomass fuel; Including, A method for producing a solid biomass fuel is provided, wherein the one or more biomass sources include (i) seeds of the Fabaceae family, (ii) a mixture of straw, rice husk and coconut shell, or (iii) a mixture of acacia mangium, albizia chinensis and hevea brasiliensis.

[0019] Preferably, the one or more biomass sources include the species Calliandra calothyrsus. In one embodiment, the one or more biomass sources may consist essentially of, or even entirely of, Calliandra calothyrsus. In another embodiment, the one or more biomass sources include Calliandra carothyrsus and further include Acacia mangium, Albizia chinensis, Hevea brasiliensis, straw, rice husk, or coconut shell. In some embodiments, the one or more biomass sources may include, or consist essentially of, i) Calliandra carothyrsus, Acacia mangium, Albizia chinensis, and Hevea brasiliensis, or ii) Calliandra carothyrsus, straw, rice husk, and coconut shell.

[0020] The step of heating the biomass molded article is preferably carried out for 0.5 to 3 hours.

[0021] The step of heating the biomass molded article includes heating the biomass molded article at a temperature of 180°C to 350°C, preferably at a temperature of 210°C to 280°C.

[0022] Preferably, the step of heating the molded biomass article comprises heating the molded biomass article so as to induce torrefaction of the molded biomass article.

[0023] Preferably, the method further comprises the step of drying the biomass powder prior to the step of shaping the biomass powder to obtain a biomass shaped article.

[0024] Preferably, the method includes the step of cooling the solid biomass fuel after the heating step.

[0025] The step (ii) of molding the biomass powder may comprise adapting the molding step such that the density of the biomass article is controlled. Preferably, adapting the molding step such that the density of the biomass article is controlled comprises controlling the compression ratio of a mold used in said molding step.

[0026] Step (iii) of heating the biomass article is typically adapted to control the homogeneity of the solid biomass fuel. Preferably, adapting step (iii) to control the homogeneity of the solid biomass product comprises carrying out step (iii) in an apparatus that rotates the biomass article during heating. More preferably, adapting step (iii) to control the homogeneity of the solid biomass product comprises controlling the speed or direction of rotation of the solid biomass product, optionally the biomass article is rotated in both counterclockwise and clockwise directions in the apparatus.

[0027] The bulk density of the produced solid biomass fuel, determined according to DIN EN 15103, is typically between 0.6 kg / l and 0.8 kg / l, preferably between 0.6 kg / l and 0.75 kg / l, most preferably between 0.6 and 0.7 kg / l.

[0028] The mechanical durability of the produced solid biomass fuels, determined according to DIN EN 15210-1, is typically 95% or more, 96% or more, 97% or more, or 98% or more.

[0029] In some embodiments of this method, the one or more biomass sources and the solid biomass fuel are: (i) the one or more biomass sources include Calliandra carothyrus, and the solid biomass fuel has a bulk density of 0.64 kg / l to 0.66 kg / l and a mechanical durability of 96% or more; (ii) the one or more biomass sources include a mixture of Calliandra carothyrus, Acacia mangium, Albizia chinensis, and Hevea brasiliensis, and the bulk density of the solid biomass fuel is between 0.67 kg / l and 0.69 kg / l and the mechanical durability is greater than or equal to 98%; (iii) the one or more biomass sources include a mixture of Calliandra carotylus, straw, rice husk and coconut shell, and the bulk density of the solid biomass fuel is between 0.61 kg / l and 0.63 kg / l and the mechanical durability is 95% or more; (iv) the one or more biomass sources include a mixture of straw, rice husk and coconut shell, and the bulk density of the solid biomass fuel is between 0.60 kg / l and 0.62 kg / l and the mechanical durability is 95% or more; or (v) the one or more biomass sources include a mixture of Acacia mangium, Albizia chinensis and Hevea brasiliensis, and the bulk density of the biomass solid fuel is between 0.66 kg / l and 0.68 kg / l and the mechanical durability is 97% or more; The bulk density is determined in accordance with DIN EN 15103, the mechanical durability in accordance with DIN EN 15210-1.

[0030] Typically, the total dry sulfur content of the produced biomass solid fuel is less than or equal to 0.05 wt%, preferably less than or equal to 0.03 wt%, most preferably less than or equal to 0.02 wt%, the total dry sulfur content being determined in accordance with DIN EN 15289.

[0031] Typically, the total dry hydrogen content of the produced biomass solid fuel is 5 wt% or more, preferably 5 wt% to 10 wt%, more preferably 5 wt% to 7 wt%, the total dry hydrogen content being determined in accordance with DIN EN 15104.

[0032] Typically, the total dry oxygen content of the produced biomass solid fuel is 34 wt% or more, preferably 34 wt% to 40 wt%, more preferably 34 wt% to 38 wt%, the total dry oxygen content being determined in accordance with DIN EN 15296.

[0033] Typically, the total dry carbon content of the produced biomass solid fuel is 50 wt% or more, preferably 53 wt% to 60 wt%, more preferably 53 wt% to 58 wt%, the total dry carbon content being determined in accordance with DIN EN 15104.

[0034] Typically, the total dry nitrogen content of the produced biomass solid fuel is less than 0.3 wt%, preferably less than 0.25 wt%, more preferably less than 0.2 wt%, the total dry nitrogen content being determined in accordance with DIN EN 15104.

[0035] Typically, the solid biomass fuel produced is waterproof for up to 20 days, preferably up to 30 days, and more preferably up to 40 days.

[0036] Typically, the chemical oxygen demand (COD) of the solid biomass fuel produced, when immersed in water, is 5000 ppm or less, preferably 4000 ppm or less, most preferably 3000 ppm or less, where the chemical oxygen demand is determined in accordance with GB / 11914-89.

[0037] Typically, the fixed carbon content of the produced solid biomass fuel is 25 wt% or more, preferably 25 wt% to 35 wt%, more preferably 25 wt% to 32 wt%, the fixed carbon content being determined in accordance with DIN EN 51734.

[0038] Typically the ash content of the solid biomass fuel produced is less than 5 wt%, preferably less than 2.5 wt%, most preferably less than 2 wt%, the ash content being determined according to DIN EN 14775 at 550° C.

[0039] Typically, the moisture content of the solid biomass fuel produced is less than 5 wt%, preferably less than 2.5 wt%, most preferably less than 2 wt%; the moisture content is determined according to DIN EN 14774.

[0040] Typically, the volatile matter content of the solid biomass fuel produced is between 60 wt% and 80 wt%, more preferably between 60 wt% and 70 wt%, the volatile matter content being determined in accordance with DIN EN 15148.

[0041] Typically, the calorific value of the solid biomass fuel produced is between 5000 kcal / kg dry mass and 7000 kcal / kg dry mass, the calorific value being determined in accordance with DIN EN 14918.

[0042] Typically, the bulk density of the biomass moulded article is A and the bulk density of the solid biomass fuel is B, with B / A being 0.55 to 1, the bulk density being determined in accordance with DIN EN 15103.

[0043] According to a second aspect of the invention there is provided a solid biomass fuel obtainable or obtainable by a process according to the first aspect of the invention.

[0044] According to a third aspect of the present invention, there is provided a solid biomass fuel derived from one or more biomass sources, the one or more biomass sources comprising: (i) legume seeds; (ii) a mixture of straw, rice husk and coconut shell; or (iii) a mixture of Acacia mangium, Albizia chinensis and Hevea brasiliensis.

[0045] Preferably, the one or more biomass sources comprise the species Calliandra carothyrus. In one embodiment, the one or more biomass sources consist essentially of, or even consist of, Calliandra carothyrus.

[0046] In another embodiment, the one or more biomass sources include Calliandra carothyrus and further include Acacia mangium, Albizia chinensis, Hevea brasiliensis, straw, rice husk, or coconut shell. In some embodiments, the one or more biomass sources may include, consist essentially of, or consist of i) Calliandra carothyrus, Acacia mangium, Albizia chinensis, and Hevea brasiliensis, or ii) Calliandra carothyrus, straw, rice husk, and coconut shell.

[0047] The bulk density of the solid biomass fuel, determined in accordance with DIN EN 15103, is typically between 0.6 kg / l and 0.8 kg / l, preferably between 0.6 kg / l and 0.75 kg / l, most preferably between 0.6 and 0.7 kg / l.

[0048] The mechanical durability of solid biomass fuels, determined in accordance with DIN EN 15210-1, is typically 95% or more, 96% or more, 97% or more, or 98% or more.

[0049] In some embodiments, the method, the one or more biomass sources, and the solid biomass fuel are as follows. (i) the one or more biomass sources include Calliandra carothyrus, and the solid biomass fuel has a bulk density of 0.64 kg / l to 0.66 kg / l and a mechanical durability of 96% or more; (ii) the one or more biomass sources include a mixture of Calliandra carothyrus, Acacia mangium, Albizia chinensis, and Hevea brasiliensis, and the bulk density of the solid biomass fuel is between 0.67 kg / l and 0.69 kg / l and the mechanical durability is greater than or equal to 98%; (iii) the one or more biomass sources include a mixture of Calliandra carotylus, straw, rice husk and coconut shell, and the bulk density of the solid biomass fuel is between 0.61 kg / l and 0.63 kg / l and the mechanical durability is 95% or more; (iv) the one or more biomass sources include a mixture of straw, rice husk and coconut shell, and the bulk density of the solid biomass fuel is between 0.60 kg / l and 0.62 kg / l and the mechanical durability is 95% or more; or (v) the one or more biomass sources include a mixture of Acacia mangium, Albizia chinensis and Hevea brasiliensis, and the bulk density of the biomass solid fuel is between 0.66 kg / l and 0.68 kg / l and the mechanical durability is 97% or more; The bulk density is determined in accordance with DIN EN 15103, the mechanical durability in accordance with DIN EN 15210-1.

[0050] Typically, the total dry sulfur content of the biomass solid fuel is not more than 0.05 wt%, preferably not more than 0.03 wt%, most preferably not more than 0.02 wt%, the total dry sulfur content being determined in accordance with DIN EN 15289.

[0051] Typically, the total dry hydrogen content of the biomass solid fuel is 5 wt% or more, preferably 5 wt% to 10 wt%, more preferably 5 wt% to 7 wt%, the total dry hydrogen content being determined in accordance with DIN EN 15104.

[0052] Typically, the total dry oxygen content of the biomass solid fuel is 34 wt% or more, preferably 34 wt% to 40 wt%, more preferably 34 wt% to 38 wt%, the total dry oxygen content being determined in accordance with DIN EN 15296.

[0053] Typically, the total dry carbon content of the biomass solid fuel is 50 wt% or more, preferably 53 wt% to 60 wt%, more preferably 53 wt% to 58 wt%, the total dry carbon content being determined in accordance with DIN EN 15104.

[0054] Typically, the total dry nitrogen content of the biomass solid fuel is less than 0.3 wt.%, preferably less than 0.25 wt.%, more preferably less than 0.2 wt.%, the total dry nitrogen content being determined in accordance with DIN EN 15104.

[0055] Typically, solid biomass fuels are waterproof for up to 20 days, preferably up to 30 days, and more preferably up to 40 days.

[0056] Typically, the chemical oxygen demand (COD) of the solid biomass fuel when immersed in water is less than 5000 ppm, preferably less than 4000 ppm, most preferably less than 3000 ppm, where the chemical oxygen demand is determined in accordance with GB / 11914-89.

[0057] Typically, the fixed carbon content of the produced solid biomass fuel is 25 wt% or more, preferably 25 wt% to 35 wt%, more preferably 25 wt% to 32 wt%, the fixed carbon content being determined in accordance with DIN EN 51734.

[0058] Typically the ash content of the solid biomass fuel produced is less than 5 wt%, preferably less than 2.5 wt%, most preferably less than 2 wt%, the ash content being determined according to DIN EN 14775 at 550° C.

[0059] Typically, the moisture content of the solid biomass fuel produced is less than 5 wt%, preferably less than 2.5 wt%, most preferably less than 2 wt%; the moisture content is determined according to DIN EN 14774.

[0060] Typically, the volatile matter content of the solid biomass fuel produced is between 60 wt% and 80 wt%, more preferably between 60 wt% and 70 wt%, the volatile matter content being determined in accordance with DIN EN 15148.

[0061] Typically, the calorific value of the solid biomass fuel produced is between 5000 kcal / kg dry mass and 7000 kcal / kg dry mass, the calorific value being determined in accordance with DIN EN 14918.

[0062] Typically, the bulk density of the biomass moulded article is A and the bulk density of the solid biomass fuel is B, the ratio B / A being 0.55 to 1, the bulk density being determined in accordance with DIN EN 15103.

[0063] According to a fourth aspect of the invention there is provided a method of combustion comprising combusting a solid biomass fuel according to the second and third aspects of the invention to produce energy.

[0064] In one embodiment, the solid biomass fuel is co-combusted and combusted with a fossil fuel. Preferably, the fossil fuel comprises coal.

[0065] In one embodiment, the method has PM1.0 emissions of less than 175 mg / kg, preferably less than 150 mg / kg.

[0066] According to a fifth aspect of the invention there is provided the use of a solid biomass fuel according to the second and third aspects of the invention as a fuel in a combustion process.

[0067] Preferably, the combustion method comprises co-firing a solid biomass fuel with a fossil fuel. Preferably, the fossil fuel is coal.

[0068] In one embodiment, the method has PM1.0 emissions of less than 175 mg / kg, preferably less than 150 mg / kg.

[0069] According to a sixth aspect of the present invention, there is provided use of one or more biomass sources comprising (i) legume seeds, (ii) a mixture of straw, rice husk and coconut shell, or (iii) a mixture of Acacia mangium, Albizia chinensis and Hevea brasiliensis for producing solid biomass fuel.

[0070] Preferably, the one or more biomass sources are as described above according to the first and third aspects of the invention.

[0071] Preferably, the use comprises the use of one or more biomass sources in a method according to the first aspect of the invention.

[0072] Preferably the solid biomass fuel is as described above according to the first and third aspects of the invention. [Brief description of the drawings]

[0073] The invention will now be described, by way of example, with reference to the accompanying drawings in which: [Figure 1] 1 is a graph depicting compression ratio on the x-axis against yield of biomass extrusions produced by the method of the present invention on the y-axis, the biomass source being Calliandra carotylus. [Diagram 2] 1 is a graph depicting the compression ratio on the x-axis against the density kg / l of biomass extrusions produced by the method of the present invention on the y-axis, the biomass source being Calliandra carothyrus. [Diagram 3] 1 is a photograph of a biomass fuel product of the present invention. [Figure 4] 1 is a graph depicting the bulk density of several products of the present invention. [Diagram 5] 1 is a graph depicting the durability of several products of the present invention. [Figure 6] 1 is a graph depicting the sulfur content of several products of the present invention. [Figure 7] 1 is a graph depicting the oxygen content of several products of the present invention. [Figure 8] 1 is a graph depicting the carbon content of several products of the present invention. [Figure 9] 1 is a graph depicting the nitrogen content of several products of the present invention. [Figure 10]1 is a graph depicting the carbon content of several products of the present invention. [Figure 11] 1 is a graph depicting the charcoal content of several products of the present invention. [Figure 12] 1 is a graph depicting the moisture content of several products of the present invention. [Figure 13] 1 is a graph depicting the volatile content of several products of the present invention. [Figure 14] 1 is a graph depicting PM1.0 emissions of several products of the present invention. [Figure 15] FIG. 1 shows the results of testing the product of the present invention in a climate chamber. [Figure 16] FIG. 13 shows further test results of the product of the present invention in a climate chamber. [Figure 17] FIG. 1 shows the results of apparent moisture content of some products of the invention after testing in a climatic chamber. [Figure 18] FIG. 13 shows further test results of the product of the present invention in a climate chamber. [Figure 19] 1 is a diagram of a compression mold that can be used in the molding step of the method of the present invention. [Figure 20] 1 is a diagram of a compression mold that can be used in the molding step of the method of the present invention. [Figure 21] FIG. 1 illustrates various physical and chemical properties of solid biomass fuel pellets of the present invention. [Figure 22] FIG. 1 illustrates various physical and chemical properties of solid biomass fuel pellets of the present invention. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0074] Biomass Sources The one or more biomass sources used according to the present invention may be any of those discussed above. In a rather preferred embodiment, the one or more biomass sources comprise, consist essentially of, or consist of Calliandra carotylus. When the one or more biomass sources include Calliandra carotylus and one or more additional biomass sources, the one or more biomass sources can contain any particular amount of Calliandra carotylus, such as 5 wt% to 95 wt%. Typically, when the one or more biomass sources include Calliandra carotylus and one or more additional biomass sources, Calliandra carotylus is present in an amount of 50 wt% to 90 wt% of the one or more biomass sources. When the one or more biomass sources include or consist of a mixture of straw, rice husk and coconut shell, or a mixture of Acacia mangium, Albizia chinensis and Hevea brasiliensis, each component of the one or more biomass sources can be present in any suitable amount, such as an amount of 5 wt% to 95 wt%. Each of the one or more biomass sources discussed above can be obtained or harvested by routine methods known in the art.

[0075] As discussed above, it has been found that the biomass source(s) used in the present invention can be grown and harvested on a commercial scale, and that greater control can be obtained over the quality and specific characteristics of the biomass source compared to the woody materials used in the prior art. The use of said materials also avoids the environmental damage associated with the use of trees, which requires deforestation and the like. It has also been surprisingly found that the use of the biomass source(s) used in the present invention is more easily ground than said previously used materials, reducing costs in the grinding process. The use of the materials of the present invention also provides a more uniform particle size mix when ground than said previously used materials. Without being limited by theory, it is believed that this imparts advantageous properties to the final solid fuel product, such as greater homogeneity and continuity of the biomass fuel product. This is desirable for combustion processes for a number of reasons.

[0076] Biomass fine grinding The biomass source can be pulverized into a biomass powder by standard techniques known in the art. The biomass source can be pulverized such that the biomass powder has an average particle size (D50) of 1000 μm to 6000 μm. As discussed above, it has been found that pulverizing certain biomass sources for use in the present invention advantageously results in biomass powders having a smaller particle size distribution than that provided by grinding conventional known biomass sources.

[0077] Molding of biomass powder The biomass powder is molded to obtain a biomass molded product. The molding step can be carried out in any molding device known in the art and by biomass molding techniques known in the art, which may include an extrusion system. Preferably, the molding step is carried out in a compression mold. Preferably, the compression mold includes a molded product exit port. The molding step can be carried out using the device described in Chinese Patent No. 105435708.

[0078] Preferably, the forming step comprises forming the biomass powder into pellets. Thus, in a preferred embodiment, the biomass molded article comprises biomass pellets.

[0079] While it is known to mold biomass powder to produce biomass molded articles, the present inventors have surprisingly discovered that adapting the molding step to control the density of the biomass molded articles produced therefrom within a particular range imparts advantageous properties to the final solid biomass fuel product. In particular, controlling the molding step to provide a bulk density of the biomass molded articles within the range of 0.9-1.6 kg / l has been found to provide advantageous properties to the final solid biomass fuel product. Preferably, the molding step is controlled to provide a bulk density of the biomass molded articles within the range of 1.1 kg / l-1.25 kg / l.

[0080] The molding step can be controlled by various methods. If the molding method involves the use of a compression mold, the density is controlled using a compression ratio of 3.8 to 6.5. Typically, the lower the compression ratio, the lower the density of the biomass molded product. However, the higher the compression ratio, the lower the yield of the biomass molded product.

[0081] The compression ratio of a compression mold having a molded product exit port may be defined as the ratio of the length of the molded product exit port to the diameter.

[0082] Figures 19 and 20 show examples of compression moulds that can be used in accordance with the present invention. Biomass powder is inserted inside the mould before being squeezed from inside the mould under pressure to exit the mould product exit port shown in the figure. The compression ratio is shown in the figure as the ratio of the length to the diameter of the product exit port.

[0083] In the method of the present invention, preferably, the step (ii) of molding the biomass powder includes adapting the molding step so that the density of the biomass molded product is controlled within the range of 1.1 kg / l to 1.25 kg / l. Preferably, the density is controlled using a compression mold and by controlling the compression ratio of the compression mold. More preferably, the compression ratio is 3.8 to 6.5.

[0084] It has been surprisingly found that controlling the density of the biomass extrusions during the molding step results in a final biomass fuel product with increased waterproofing capabilities. Preferably, solid biomass fuel products made from biomass extrusions having a density in the range of 1.1 kg / l to 1.25 kg / l are sufficiently waterproof for up to 20 days, preferably up to 30 days.

[0085] FIG. 1 is a graph depicting compression ratio on the x-axis against yield of biomass extrusions produced by the method of the present invention on the y-axis, the biomass source being Calliandra carothyrus.

[0086] FIG. 2 is a graph depicting the compression ratio on the x-axis against the density kg / l of the biomass extrusions produced by the method of the present invention on the y-axis, the biomass source being Calliandra carothyrus.

[0087] Heating of biomass molded products The biomass molded article is heated to produce a solid biomass fuel. The heating is carried out at a temperature between 160°C and 420°C for a period of 0.25 to 5 hours. Preferably, the step of heating the biomass molded article is carried out for a period of 0.5 to 3 hours. Preferably, the step of heating the biomass molded article includes heating the biomass molded article at a temperature between 180°C and 350°C, more preferably at a temperature between 210°C and 280°C.

[0088] As discussed above, preferably the biomass shaped article comprises pellets when heated by heating step (iii) of the method of the present invention.

[0089] Preferably, the step (iii) of heating the biomass molded article comprises heating the biomass molded article under conditions that induce torrefaction of the biomass molded article. Torrefaction is a mild pyrolysis method in which the heating is carried out under a low oxygen atmosphere, such as an atmosphere with an oxygen content of less than 10%. Suitable conditions and methods of torrefaction are known in the art. Thus, preferably, the step (iii) of heating the biomass molded article comprises torrefaction. The use of biomass molded articles comprising pellets is advantageous over conventional known torrefaction methods in which a pulverized biomass source, such as wood chips, is subjected to torrefaction without being directly pulverized into pellets. Pellets are generally much denser than wood chips, meaning that they contain more energy per unit volume. The lower volume saves the energy requirements of the torrefaction heating device. Thus, the use of pellets is more economical. The heating step can be carried out in any suitable device known in the art for heating biomass molded articles to produce solid biomass fuel products. For example, the heating step can be carried out by use of the equipment and operating conditions disclosed in European Patent Application No. 3287509A1.

[0090] Preferably, the heating step (iii) of the biomass article is adapted to control the homogeneity of the solid biomass fuel, and optionally, adapting step (iii) to control the homogeneity of the solid biomass product comprises performing step (iii) in an apparatus in which the biomass article is rotated as it is heated, and optionally, adapting step (iii) to control the homogeneity of the solid biomass product comprises controlling the speed or direction of rotation of the solid biomass product, and optionally, the biomass article is rotated in both counterclockwise and clockwise directions in the apparatus. The homogeneity of the biomass product is also optimized by the heating temperature and time discussed above.

[0091] If the method of the invention comprises a cooling step after the heating step of the biomass, the cooling step may comprise rotating the biomass. The biomass may be rotated in a suitable apparatus such as the apparatus disclosed in European Patent Application No. 3287509A1. Preferably, the heating step (iii) and the step of cooling the biomass both comprise rotating the biomass. If the biomass is rotated in either the cooling step or the heating step, the biomass may be rotated in different directions, such as both clockwise and counterclockwise in successive cycles.

[0092] The term "homogeneity" of a solid biomass fuel product is used to refer to a solid biomass fuel product that has constant or similar properties across each particle of the solid biomass fuel and across multiple particles within a bulk sample of the solid biomass fuel product, such as, but not limited to, the density of the particle, the ease of combustion of the particle, the chemical composition of the particle, and the water resistance characteristics of the particle. Homogeneity is a highly desirable property for a biomass fuel to be used in a combustion process.

[0093] It has also been found by the inventors that controlling the heating step in the manner discussed above additionally aids in obtaining a solid biomass fuel product having improved waterproofing properties compared to prior art biomass fuels.

[0094] Solid Biofuel Products The solid biomass fuel product can have any of the physical characteristics discussed above.

[0095] As discussed above, the biomass solid fuel of the present invention preferably comprises pellets. The pellets can be of any suitable size. Preferably, the pellets have a diameter of 3 mm to 100 mm, more preferably 5 mm to 8 mm. Preferably, the pellets have a length of 20 mm to 60 mm, more preferably 30 mm to 50 mm. As discussed above, it has surprisingly been found that the solid biomass fuel product of the present invention has improved waterproof properties compared to solid biomass fuel products made by the prior art methods. This is believed to be due to the control of the forming and / or heating steps discussed above. It has been found by the inventors that the prior art biomass fuels are sufficiently waterproof for only up to 10 days. In contrast, it has been found that the solid biomass fuel product of the present invention is sufficiently waterproof for up to 20 days, preferably 30 days, more preferably 40 days.

[0096] The waterproofing properties of solid biomass fuels were determined according to standard tests from the Energy Research Centre of the Netherlands (ECN) and are detailed further below.

[0097] The moisture content of the biomass solid fuel of the present invention can also be determined by standard ECN test methods. The moisture content of the solid biomass fuel of the present invention is typically 5-9 wt%, preferably 6-8 wt%, more preferably 6-7 wt%.

[0098] The solid biomass fuel of the present invention has also been found to have unexpectedly high mechanical durability. The mechanical durability is typically greater than 95%. This is advantageous because it has been found that biomass pellets with a mechanical durability of 95% or more can be stored outdoors for up to two months without damage. In contrast, biomass pellets with a mechanical durability of less than 95% are typically damaged by rainfall and cannot be stored outdoors. Thus, high mechanical durability is an additional advantage of the biomass pellets of the present invention.

[0099] An additional benefit associated with the high durability of solid biomass fuel particles is that if the pellets are broken by any force, they will break up into larger pieces than pellets with lower mechanical durability, minimizing any risk of dust explosions.

[0100] Combustion Method The products of the invention can be used in a variety of different combustion processes. The suitability of the products for use in a particular process will be apparent to those skilled in the art. For example, the biomass fuels of the invention can be used in a power plant combustion process or in an industrial process per se. Alternatively, the biomass products of the invention can be used in a combustion process together with an additional fuel, such as coal, in a co-combustion process.

[0101] Advantageously, the products of the present invention have been found to result in very low PM1.0 emissions compared to other biomass fuels known in the art. In addition, the PM1.0 emissions of the present process are lower than processes involving coal fuels.

[0102] Advantageously, it has been found that the improved physical properties of the biomass fuel of the present invention make it particularly suitable for co-firing with coal. For example, the improved quality and homogeneity of the product allows the biomass fuel of the present invention to be particularly well co-firing with coal. The improved waterproof properties of the biomass fuel of the present invention also mean that the biomass is particularly well co-firing with coal, and that the waterproof properties make it easier to store and transport. EXAMPLES

[0103] The method of the present invention was carried out. The biomass source was only Calliandra carothyrus. The temperature of the heating step was 220°C-280°C for 0.5-3.5 hours, and then cooled to obtain solid biomass fuel.

[0104] A photograph of the solid product is shown in FIG. EXAMPLES

[0105] The method of the present invention was carried out. The biomass sources were Calliandra carothyrus in an amount of 70 wt%, Acacia mangium in an amount of 10 wt%, Eucalyptus (Albizia chinensis) in an amount of 10 wt%, and rubber tree (Hevea brasiliensis) in an amount of 10 wt%.

[0106] The temperature of the heating step was 220°C-280°C for 0.5-3.5 hours, and then cooled to obtain solid biomass fuel. EXAMPLES

[0107] The method of the present invention was carried out. The biomass sources were Calliandra carothyrus in an amount of 70 wt%, straw in an amount of 10 wt%, rice husk in an amount of 10 wt%, and coconut shell in an amount of 10 wt%.

[0108] The temperature of the heating step was 220°C-280°C for 0.5-3.5 hours, and then cooled to obtain solid biomass fuel. EXAMPLES

[0109] The method of the present invention was carried out. The biomass sources were straw in an amount of 40 wt%, rice husk in an amount of 10 wt% and coconut shell in an amount of 50 wt%.

[0110] The temperature of the heating step was 220°C-280°C for 0.5-3.5 hours, and then cooled to obtain solid biomass fuel. EXAMPLES

[0111] The method of the present invention was carried out. The biomass sources were Acacia mangium in an amount of 30 wt%, Albizia chinensis in an amount of 30 wt%, and rubber tree (Hevea brasiliensis) in an amount of 40 wt%.

[0112] The temperature of the heating step was 220°C-280°C for 0.5-3.5 hours, and then cooled to obtain solid biomass fuel.

[0113] Characterization of solid biomass fuels for Examples 1-5 The bulk density kg / l of the solid biomass fuels produced in Examples 1 to 5 is shown in Figure 4. The bulk density was determined using DIN EN 15103 to be 0.643 kg / l.

[0114] The durability of the solid biomass fuels produced in Examples 1 to 5 is shown in Figure 5. The durability was determined according to DIN EN 15210-1.

[0115] The sulfur content of the solid biomass fuels produced in Examples 1 to 5 is shown in Figure 6. The sulfur content was determined according to DIN EN 15289.

[0116] The oxygen content of the solid biomass fuels produced in Examples 1 to 5 is shown in Figure 7. The oxygen content was determined according to DIN EN 15296.

[0117] The carbon contents of the biomass solid fuels produced in Examples 1 to 5 are shown in Figure 8. The carbon contents were determined in accordance with DIN EN 15104.

[0118] The nitrogen contents of the biomass solid fuels produced in Examples 1 to 5 are shown in Figure 9. The nitrogen contents were determined in accordance with DIN EN 15104.

[0119] The fixed carbon contents of the biomass solid fuels produced in Examples 1 to 5 are shown in Figure 10. The fixed carbon contents were determined in accordance with DIN EN 51734.

[0120] The ash content of the biomass solid fuels produced in Examples 1 to 5 is shown in Figure 11. The ash content is determined according to DIN EN 14775 at 550°C.

[0121] The moisture contents of the biomass solid fuels produced in Examples 1 to 5 are shown in Figure 12. The moisture contents were determined in accordance with DIN EN 14774-2.

[0122] The volatile matter contents of the solid biomass fuels produced in Examples 1 to 5 are shown in FIG.

[0123] The PM1.0 emission levels of the biomass solid fuels produced in Examples 1 to 5 are shown in Figure 14. The PM1.0 emission levels are determined according to the standard method of the ECN testing institute in Germany.

[0124] In the above diagram, the product of Example 1 is designated A, Example 2 is designated B, Example 3 is designated C, Example 4 is designated D, and Example 5 is designated E. EXAMPLES

[0125] The solid biomass fuel of Example 1 was tested in a climate chamber experiment and exposed to the climate chamber for 10 days. The test is an ECN standard test for evaluating the moisture content of biomass fuel particles.

[0126] The results of this test are shown in Figure 15. The results in Figure 15 show that after approximately 14 days of exposure under conditions of 27°C and 90% relative humidity, the equilibrium moisture uptake of the biomass pellets stabilized at 6-7 wt%, which is a low moisture content for torrefied biomass pellets, indicating that the biomass pellets have high hydrophobicity and high waterproofing properties compared to biomass solid fuels known in the art.

[0127] In a second experiment in a climate chamber, the biomass solid fuel was immersed in water for 15 minutes and then exposed to a temperature of 27°C in the climate chamber. After immersion in water, the moisture content of the sample was 90 wt%. After 10 days of exposure in the climate chamber, the moisture content of the fuel stabilized at approximately 7.6%. The results are shown in Figures 16 and 18. Submersion of the pellets in water did not affect the equilibrium moisture content reached after 10 days. EXAMPLES

[0128] The climate chamber experiment was repeated for the products of Examples 2-5.

[0129] Figure 17 shows the apparent moisture content of the products of Examples 1 to 5. It can be seen that the apparent moisture content and the measured moisture content of the biomass pellets are very similar.

[0130] In Figures 15-18, the y-axis values ​​are weight percent moisture of the biomass pellets. EXAMPLES

[0131] 21 and 22 show various physical and chemical properties of the solid biomass fuel pellets of the present invention.

Claims

1. (i) pulverizing one or more biomass sources to obtain a biomass powder having an average particle size (D50) of 1000 μm to 6000 μm; (ii) molding the biomass powder to obtain a biomass molded product; (iii) heating the biomass molded article at a temperature of 160° C. to 420° C. for 0.25 to 5 hours to obtain a solid biomass fuel; Including, 13. A method for producing a solid biomass fuel, wherein the one or more biomass sources comprise: (i) Calliandra carothyrus; or (ii) a mixture of straw, rice husk and coconut shell.

2. 2. The method of claim 1, wherein the one or more biomass sources comprise Calliandra carotylusus.

3. The method according to any one of claims 1 to 2, wherein the step of heating the biomass molded article is carried out for 0.5 to 3 hours, and / or the step of heating the biomass molded article comprises heating the biomass molded article at a temperature of 180 ° C to 350 ° C.

4. 4. The method of claim 1, wherein the step (ii) of molding the biomass powder comprises adapting the molding step to control the density of the biomass molded article, and wherein adapting the molding step to control the density of the biomass molded article comprises controlling a compression ratio of a mold used in the molding step.

5. 5. The method of any of claims 1 to 4, wherein step (iii) of heating the biomass article is adapted to control homogeneity of a solid biomass fuel, and wherein adapting step (iii) to control homogeneity of a solid biomass product comprises performing step (iii) in an apparatus that rotates the biomass article while heating.

6. 6. The method of claim 5, wherein adapting step (iii) to control the homogeneity of the solid biomass product comprises controlling a rotation speed or direction of the solid biomass product, and wherein the biomass article is rotated in an apparatus in both a counterclockwise and a clockwise direction.

7. 7. The method of any of claims 1 to 6, wherein the step (ii) of shaping the biomass powder comprises shaping the biomass powder using a compression mould, the shaping being adapted to control the density of the biomass mould using a compression ratio of the compression mould between 3.8 and 6.

5.

8. 8. The method according to claim 1, wherein the bulk density of the solid biomass fuel, determined according to DIN EN 15103, is between 0.6 kg / l and 0.8 kg / l and / or the mechanical durability of the solid biomass fuel, determined according to DIN EN 15210-1, is 95% or higher.

9. The method of claim 1, further defined by one of the following (i), (ii), (iii) or (iv): (i) the one or more biomass sources include Calliandra carothyrus, and the bulk density of the solid biomass fuel is between 0.64 kg / l and 0.66 kg / l and the mechanical durability is 96% or more; (ii) the one or more biomass sources comprise a mixture of Calliandra carothyrus, Acacia mangium, Albizia chinensis and Hevea brasiliensis, and the bulk density of the solid biomass fuel is between 0.67 kg / l and 0.69 kg / l, and the mechanical durability is 98% or more; (iii) the one or more biomass sources comprise a mixture of Calliandra carotylusus, straw, rice husk and coconut shell, the bulk density of the solid biomass fuel is between 0.61 kg / l and 0.63 kg / l and the mechanical durability is 95% or more; (iv) the one or more biomass sources comprise a mixture of straw, rice husk and coconut shell, the bulk density of the solid biomass fuel is between 0.60 kg / l and 0.62 kg / l, and the mechanical durability is 95% or more; The bulk density is determined in accordance with DIN EN 15103 and the mechanical durability is determined in accordance with DIN EN 15210-1.

10. The method according to any one of claims 1 to 9, wherein the solid biomass fuel is further defined by one or more of the following (i) to (v): (i) the total dry sulfur content of the solid biomass fuel is less than or equal to 0.05 wt.%, wherein the total dry sulfur content is determined in accordance with DIN EN 15289; (ii) the total dry hydrogen content of the solid biomass fuel is greater than or equal to 5 wt.%, wherein the total dry hydrogen content is determined in accordance with DIN EN 15104; (iii) the total dry oxygen content of the solid biomass fuel is greater than or equal to 34 wt.%, wherein the total dry oxygen content is determined in accordance with DIN EN 15296; (iv) the total dry carbon content of the solid biomass fuel is greater than or equal to 50 wt.%, wherein the total dry carbon content is determined in accordance with DIN EN 15104; (v) the total dry nitrogen content of the solid biomass fuel is less than 0.3 wt.%, wherein the total dry nitrogen content is determined in accordance with DIN EN 15104.

11. The method of any of claims 1 to 10, wherein the solid biomass fuel is waterproof for up to 30 days.

12. The method according to any one of claims 1 to 11, wherein the solid biomass fuel is further defined by one or more of the following (i) to (iv): (i) the chemical oxygen demand (COD) of the solid biomass fuel when immersed in water is less than or equal to 5000 ppm, the chemical oxygen demand being determined in accordance with GB / 11914-89; (ii) the fixed carbon content of the solid biomass fuel is greater than or equal to 25 wt%; (iii) the ash content of the solid biomass fuel is less than 5 wt%; and (iv) the volatile matter content of the solid biomass fuel is between 60 wt% and 80 wt%.

13. The method according to any one of claims 1 to 12, wherein the moisture content of the solid biomass fuel is less than 5 wt% or the calorific value of the solid biomass fuel is between 5000 kcal / kg dry mass and 7000 kcal / kg dry mass.

14. 1. A solid biomass fuel derived from one or more biomass sources including (i) Calliandra carotylusus, or (ii) a mixture of straw, rice husk and coconut shell, wherein the bulk density of the solid biomass fuel, determined according to DIN EN 15103, is between 0.6 kg / l and 0.8 kg / l, and the mechanical durability of the solid biomass fuel, determined according to DIN EN 15210-1, is 95% or more, and the calorific value of the solid biomass fuel is between 5000 kcal / kg dry mass and 7000 kcal / kg dry mass, wherein the calorific value is determined according to DIN EN 14918.

15. 20. A method of combustion comprising combusting the solid biomass fuel of claim 14 to produce energy.

16. 16. The method of claim 15, wherein the solid biomass fuel is co-combusted and combusted with a fossil fuel, such as coal, and the PM1.0 emissions are less than 175 mg / kg.