Cellulose fine fibers and their manufacturing method

Abstract

To provide a cellulose fine fiber whose dispersion has extremely high light transmittance and viscosity, and provide a method for producing the same.SOLUTION: Cellulose microfibers of this invention have a fiber width of 1 to 200 nm, a portion of the hydroxy groups of the cellulose fiber is substituted with a predetermined functional group, and an ester of phosphooxo acid is introduced, and the amount of the functional group introduced is more than 2.0 mmol per 1 g of cellulose fiber. Further, in producing this cellulose fine fiber, the cellulose fibers are added with the solution having a pH of less than 3.0, which contains an additive (A) containing at least one of phosphorus oxoacids and metal salts of phosphorus oxoacids and an additive (B) containing at least one of urea and an urea derivative, are heated, and fibrillated.SELECTED DRAWING: None

Description

[Technical field]

[0001] The present invention relates to cellulose fine fibers and a method for producing the same. [Background technology]

[0002] In recent years, nanotechnology, which aims to make a substance finer to the nanometer level and obtain new physical properties different from the conventional properties of the substance, has been attracting attention. For example, pulp, which is a cellulose-based raw material, is made into cellulose fine fibers (cellulose nanofibers) by chemical treatment, pulverization, etc. Since cellulose fine fibers have excellent strength, elasticity, thermal stability, etc., they are expected to be used in industrial applications such as filter materials, filter aids, base materials for ion exchangers, fillers for chromatography analysis instruments, fillers for compounding resins and rubbers, and as compounding agents for cosmetics such as lipsticks, powder cosmetics, and emulsion cosmetics. In addition, since cellulose fine fibers have excellent aqueous dispersibility, they are expected to be used in many applications such as viscosity retaining agents for foods, cosmetics, paints, etc., strengthening agents for food raw material doughs, moisture retaining agents, food stabilizers, low-calorie additives, and emulsion stabilization aids.

[0003] To obtain such cellulose fine fibers, there are methods for mechanically defibrating cellulosic raw materials using a high-pressure homogenizer, a high-speed rotary homogenizer, an ultrasonic homogenizer, etc. However, these methods require a large amount of energy to advance defibration, and also damage the cellulose fibers.

[0004] Therefore, Patent Document 1 proposes a method for producing cellulose fine fibers that causes less damage to the cellulose fibers, and states that commercially available blenders, mixers, etc. can be used to defibrate (agitate) the fibers. However, when using the method described in this document, the defibration time needs to be extended to increase the light transmittance and viscosity of the dispersion obtained by dispersing the cellulose fine fibers, and extending the defibration time increases the damage to the cellulose fibers. In particular, for applications such as food and cosmetics, it is considered an essential condition that the dispersion has high light transmittance, and the challenge of increasing light transmittance cannot be avoided in expanding the applications of cellulose fine fibers.

[0005] In addition, a method has been proposed for producing cellulose fine fibers in which, prior to defibration, "a polybasic acid anhydride is semi-esterified to some of the hydroxyl groups of cellulose to introduce carboxyl groups, thereby preparing polybasic acid semi-esterified cellulose" (see Patent Document 2).

[0006] Furthermore, as the method described in the same document is insufficient in terms of fineness, a method has been proposed in which "a fiber raw material containing cellulose is treated with at least one compound selected from phosphorus oxoacids or their salts" prior to defibration (see Patent Document 3). The document describes that the method described in the document produces fine fibrous cellulose having a fiber width of 1 to 1000 nm and into which phosphorus oxoacid groups have been introduced by substituting a portion of the hydroxyl groups of the cellulose constituting the fibers with a predetermined functional group. However, the present inventors have found that the dispersion of cellulose fine fibers obtained by the method described in the document leaves room for improvement in terms of light transmittance and viscosity. [Prior art documents] [Patent documents]

[0007] [Patent Document 1] JP 2010-216021 A [Patent Document 2] JP 2009-293167 A [Patent Document 3] JP 2013-127141 A Summary of the Invention [Problem to be solved by the invention]

[0008] The problem to be solved by the present invention is to provide cellulose fine fibers, which, when dispersed in a dispersion, have extremely high light transmittance and viscosity, and a method for producing the same. [Means for solving the problem]

[0009] The present inventors have conducted various studies on why the light transmittance and viscosity of the method of Patent Document 3 described above are insufficient. As a result, they have found that the key point is the amount (molar amount) of phosphorus oxoacid introduced per 1 g of cellulose fiber. In this regard, the document states that "the amount of phosphorus oxoacid groups introduced in the hydroxyl groups (-OH groups) of the cellulose, which is the raw material for fibers, is preferably 0.1 to 2.0 mmol, more preferably 0.2 to 1.5 mmol, per 1 g (mass) of fine fibrous cellulose." However, as shown in the examples described later, it is preferable that the amount of phosphorus oxoacid groups introduced exceeds 2.0 mmol. In the course of the study, the present inventors have also found that the amount of phosphorus oxoacid introduced is not sufficient simply by specifying the amount of phosphorus oxoacid added. The amount of phosphorus oxoacid groups actually introduced also depends on the production conditions. In addition, when using the method of Patent Document 3, the amount of phosphorus oxoacid groups that can be introduced in one reaction is thought to be up to 2.0 mmol / g at most, and this amount does not provide sufficient light transmittance or viscosity for the dispersion. If the amount of phosphorus oxoacid introduced by the method of Patent Document 3 is to exceed 2.0 mmol, the reaction must be repeated, and therefore it is thought that this document did not anticipate the introduction of an amount of phosphorus oxoacid exceeding 2.0 mmol in the first place.

[0010] Based on the above-mentioned various studies and findings, the following means for solving the above problems have been arrived at. (Means described in claim 1) The fiber width is 1 to 200 nm, A part of the hydroxyl groups of the cellulose fiber is substituted with a functional group represented by the following structural formula (1) to introduce an ester of phosphorus oxoacid, The amount of the functional group represented by the structural formula (1) introduced is more than 2.0 mmol per 1 g of cellulose fiber, and the axial ratio is 3 to 1,000,000. the law of nature , a part of the hydroxyl groups of the cellulose fibers is substituted with a carbamate group to introduce a carbamate; The amount of the carbamate group introduced is 0.69 to 2.34 mmol per 1 g of the cellulose fiber. The cellulose fine fibers are characterized by the following: [Structural formula (1)] [ka] In structural formula (1), a, b, m, and n are natural numbers. At least one of A1, A2, . . ., An and A' is O-, and the rest are R, OR, NHR, or none. R is a hydrogen atom, a saturated linear hydrocarbon group, a saturated branched hydrocarbon group, a saturated cyclic hydrocarbon group, an unsaturated linear hydrocarbon group, an unsaturated branched hydrocarbon group, an aromatic group, or a group derived from any of these. α is a cation consisting of an organic or inorganic substance.

[0011] (Means described in claim 2) The crystallinity is 50-100%. The cellulose fine fibers according to claim 1. (Means described in claim 3) The light transmittance of the dispersion (0.2% solids solution) is 50.0% or more. The cellulose fine fibers according to claim 1. (Means described in claim 4) The B-type viscosity of the dispersion when the concentration is 1 mass% (w / w) is 10 to 300,000 cps. The cellulose fine fibers according to claim 1.

[0012] (Means described in claim 5) A part of the hydroxyl groups of the cellulose fibers is substituted with a functional group represented by the following structural formula (2) to introduce an ester of phosphonic acid, The amount of the functional group represented by the structural formula (2) introduced is more than 2.0 mmol and not more than 3.4 mmol per 1 g of cellulose fiber. R , The cellulose fine fibers according to claim 1. [Structural formula (2)] [ka] In structural formula (2), α is none, R, or NHR. R is a hydrogen atom, a saturated linear hydrocarbon group, a saturated branched hydrocarbon group, a saturated cyclic hydrocarbon group, an unsaturated linear hydrocarbon group, an unsaturated branched hydrocarbon group, an aromatic group, or a group derived from any of these. β is a cation made of an organic or inorganic substance.

[0013] (Claim 6 (Means described in In producing the cellulose fine fibers according to claim 1, A solution having a pH of 2.0 or more and less than 3.0, which is composed of an additive (A) containing phosphonic acids and an additive (B) containing at least one of urea and a urea derivative, is added to cellulose fibers, and the fibers are heated and defibrated. A part of the hydroxyl groups of the cellulose fibers is replaced with a carbamate group to introduce a carbamate, The amount of the carbamate group introduced is 0.69 to 2.34 mmol per 1 g of the cellulose fiber. A method for producing cellulose fine fibers, comprising the steps of:

[0014]

[0015] (Claim 7 (Means described in A hydroxide salt is also added to the cellulose fibers, and the heating is performed at 100 to 160°C, and then the cellulose fibers are washed. Claim 6 The method for producing cellulose fine fibers according to claim 1. (Claim 8 (Means described in The amount of the additive (B) added is 0.5 to 10 mol per 1 mol of the additive (A). Claim 6 The method for producing cellulose fine fibers according to claim 1. Effect of the Invention

[0016] According to the present invention, there are provided cellulose fine fibers and a production method thereof, in which, when the cellulose fine fibers are made into a dispersion, the dispersion has extremely high light transmittance and viscosity. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0017] Next, an embodiment of the present invention will be described. Note that the embodiment is an example of the present invention.

[0018] (Cellulose Microfibers) The cellulose fine fibers of this embodiment have a fiber width of 1 to 200 nm, and some of the hydroxyl groups (-OH groups) of the cellulose fibers are replaced with functional groups shown in the following structural formula (1) to introduce (modify, modify) an ester of phosphorus oxoacid (esterification), and the amount of the functional groups shown in the following structural formula (1) introduced exceeds 2.0 mmol (preferably 2.1 mmol or more) per gram of cellulose fibers. More preferably, some of the hydroxyl groups of the cellulose fibers are replaced with carbamate groups to introduce carbamate (ester of carbamic acid).

[0019] [Structural formula (1)] [ka]

[0020] In structural formula (1), a, b, m, and n are natural numbers.

[0021] At least one of A1, A2, . . ., An and A' is O - and the rest is either R, OR, NHR, or none. R is any of a hydrogen atom, a saturated linear hydrocarbon group, a saturated branched hydrocarbon group, a saturated cyclic hydrocarbon group, an unsaturated linear hydrocarbon group, an unsaturated branched hydrocarbon group, an aromatic group, and derivatives thereof. α is a cation consisting of an organic or inorganic substance.

[0022] An ester of phosphorus oxoacid is a compound in which a hydroxyl group (-OH) and an oxo group (=O) are bonded to a phosphorus atom, and the hydroxyl group provides an acidic proton. An ester of phosphorus oxoacid has a high negative charge, and therefore, when an ester of phosphorus oxoacid is introduced, the repulsion between cellulose molecules becomes stronger, making it easier to defibrate cellulose fibers. Furthermore, when a carbamate is also introduced together with the ester of phosphorus oxoacid, the light transmittance and viscosity of the dispersion are significantly improved. In this regard, carbamate has an amino group. Therefore, when a carbamate is introduced, it interacts with the ester of phosphorus oxoacid. As a result, it is believed that when a carbamate is also introduced, the shear force of the dispersion increases and the viscosity improves.

[0023] As the phosphorus oxoacid ester to be introduced, a phosphonic acid ester is more preferable. When a phosphonic acid ester is introduced, yellowing is reduced, and the light transmittance of the dispersion in which the cellulose fine fibers are dispersed is increased. The viscosity of the dispersion is also increased. When a phosphonic acid ester is introduced, some of the hydroxyl groups (-OH groups) of the cellulose fibers are replaced with the functional group shown in the following structural formula (2).

[0024] [Structural formula (2)] [ka]

[0025] In structural formula (2), α is none, R, or NHR. R is a hydrogen atom, a saturated linear hydrocarbon group, a saturated branched hydrocarbon group, a saturated cyclic hydrocarbon group, an unsaturated linear hydrocarbon group, an unsaturated branched hydrocarbon group, an aromatic group, or a group derived from any of these. β is a cation made of an organic or inorganic substance.

[0026] The amount of phosphorus oxoacid ester or phosphonic acid ester introduced is more than 2.0 mmol, preferably 2.1 mmol or more, more preferably 2.2 mmol or more, per 1 g of cellulose fine fibers. Also, it is 3.4 mmol or less, preferably 3.2 mmol or less, more preferably 3.0 mmol or less. If the amount introduced is 2.0 mmol or less, the light transmittance and viscosity of the dispersion may not be sufficiently increased. On the other hand, if the amount introduced is more than 3.4 mmol, the cellulose fibers may dissolve in water.

[0027] The amount of phosphorus oxoacid ester introduced is a value evaluated based on elemental analysis, which is performed using X-Max 50 001 manufactured by Horiba, Ltd.

[0028] The amount of carbamate introduced is preferably 0.06 to 2.34 mmol, more preferably 0.15 to 1.28 mmol, and particularly preferably 0.39 to 1.02 mmol per 1 g of cellulose fine fibers. If the amount introduced is less than 0.06 mmol, the light transmittance and viscosity of the dispersion may not be sufficiently increased. On the other hand, if the amount introduced is more than 2.34 mmol, the cellulose fibers may dissolve in water. The amount of carbamate introduced was calculated by the Kjeldahl method.

[0029] The fiber width (average diameter of a single fiber) of the cellulose fine fibers is preferably 1 to 200 nm, more preferably 2 to 100 nm, and particularly preferably 3 to 50 nm. If the fiber width is less than 1 nm, the cellulose may dissolve in water and may lose the physical properties required for the cellulose fine fibers, such as strength, rigidity, and dimensional stability. On the other hand, if the fiber width exceeds 200 nm, the width becomes about 1 / 10 of the wavelength of visible light, and therefore, when the cellulose fine fibers are dispersed in water (when made into an aqueous dispersion), refraction and scattering of visible light may occur, and the light transmittance may be considered to be insufficient.

[0030] The fiber width of the cellulose fine fibers is measured using an electron microscope as follows. First, 100 ml of an aqueous dispersion of cellulose fine fibers with a solid content concentration of 0.01 to 0.1% by mass is filtered through a Teflon (registered trademark) membrane filter, and the solvent is replaced once with 100 ml of ethanol and three times with 20 ml of t-butanol. Next, the sample is freeze-dried and osmium-coated to obtain a sample. This sample is observed using an electron microscope SEM image at a magnification of 5,000 times, 10,000 times, or 30,000 times depending on the width of the fibers that constitute it. In this observation, two diagonal lines are drawn on the observed image, and three straight lines are arbitrarily drawn that pass through the intersections of the diagonal lines. Then, the widths of a total of 100 fibers that intersect with these three straight lines are visually measured. The median diameter of this measurement is taken as the fiber width.

[0031] The axial ratio (fiber length / fiber width) of the cellulose fine fibers is preferably 3 to 1,000,000, more preferably 6 to 340,000, and particularly preferably 10 to 340,000. If the axial ratio is less than 3, it can no longer be said to be fibrous. On the other hand, if the axial ratio exceeds 1,000,000, the viscosity of the dispersion (slurry) may become too high.

[0032] The crystallinity of the cellulose fine fibers is preferably 50 to 100%, more preferably 60 to 90%, and particularly preferably 65 to 85%. If the crystallinity is less than 50%, the strength and heat resistance may be insufficient. The crystallinity can be adjusted, for example, by selecting pulp fibers, pre-treating, defibrating, etc.

[0033] The crystallinity is a value measured by X-ray diffraction in accordance with JIS-K0131 (1996) "General Rules for X-ray Diffraction Analysis." Note that cellulose fine fibers have amorphous and crystalline portions, and the crystallinity refers to the proportion of the crystalline portion in the entire cellulose fine fibers.

[0034] The light transmittance of the dispersion of cellulose fine fibers (0.2% solids solution) is preferably 50.0% or more, more preferably 60.0% or more, and particularly preferably 70.0% or more. If the light transmittance is less than 50.0%, the light transmittance may be considered insufficient. The light transmittance of the cellulose fine fibers can be adjusted, for example, by selecting pulp fibers, pre-treating, defibrating, etc.

[0035] The light transmittance is a value obtained by measuring the light transmittance (transmittance of light of 350 to 880 nm) of a 0.2% (w / v) cellulose fine fiber dispersion using a Spectrophotometer U-2910 (Hitachi, Ltd.).

[0036] When the concentration of the cellulose fine fibers is 1% by mass (w / w), the dispersion preferably has a Brookfield viscosity of 10 to 300,000 cps, more preferably 1,000 to 200,000 cps, and particularly preferably 16,000 to 100,000 cps.

[0037] B-type viscosity is a value measured for an aqueous dispersion of cellulose microfibers with a solid content concentration of 1% in accordance with JIS-Z8803 (2011) "Method of measuring viscosity of liquids." B-type viscosity is the resistance torque when stirring a slurry, and the higher the viscosity, the more energy is required for stirring.

[0038] (Method of manufacturing cellulose fine fibers) In the manufacturing method of this embodiment, a solution of less than pH 3 containing additive (A) containing at least one of phosphorus oxoacids and phosphorus oxoacid metal salts, and preferably additive (B) containing at least one of urea and urea derivatives, is added to cellulose fibers, and heated to introduce phosphorus oxoacid esters, preferably phosphorus oxoacid esters and carbamates, into the cellulose fibers. The cellulose fibers into which the phosphorus oxoacid esters have been introduced are then defibrated to obtain cellulose fine fibers.

[0039] Preferably, hydroxide salts are also added to the cellulose fibers, and the cellulose fibers are washed after heating and prior to defibration.

[0040] (Cellulose fiber) As the cellulose fibers, for example, fibers derived from plants (plant fibers), fibers derived from animals, fibers derived from microorganisms, etc. can be used. These fibers can be used alone or in combination as necessary. However, as the cellulose fibers, it is preferable to use plant fibers, and it is more preferable to use pulp fibers, which are a type of plant fiber. When the cellulose fibers are pulp fibers, it is easy to adjust the physical properties of the cellulose fine fibers.

[0041] Examples of plant fibers that can be used include wood pulp made from broadleaf trees, coniferous trees, etc., non-wood pulp made from straw, bagasse, etc., and waste paper pulp (DIP) made from recycled waste paper, broke paper, etc. These fibers can be used alone or in combination.

[0042] Examples of wood pulp that can be used include chemical pulps such as hardwood kraft pulp (LKP) and softwood kraft pulp (NKP), mechanical pulp (TMP), and deionized paper pulp (DIP), etc. These pulps can be used alone or in combination.

[0043] The hardwood kraft pulp (LKP) may be bleached hardwood kraft pulp, unbleached hardwood kraft pulp, or semi-bleached hardwood kraft pulp. The softwood kraft pulp (NKP) may be bleached softwood kraft pulp, unbleached softwood kraft pulp, or semi-bleached softwood kraft pulp. The deionized paper pulp (DIP) may be magazine waste paper pulp (MDIP), newspaper waste paper pulp (NDIP), corrugated paper pulp (WP), or other deionized paper pulp.

[0044] (Additive (A)) The additive (A) includes at least one of phosphorus oxoacids and phosphorus oxoacid metal salts. As the additive (A), for example, phosphoric acid, ammonium dihydrogen phosphate, diammonium hydrogen phosphate, triammonium phosphate, ammonium pyrophosphate, ammonium polyphosphate, lithium dihydrogen phosphate, trilithium phosphate, dilithium hydrogen phosphate, lithium pyrophosphate, lithium polyphosphate, sodium dihydrogen phosphate, disodium hydrogen phosphate, trisodium phosphate, sodium pyrophosphate, sodium polyphosphate, potassium dihydrogen phosphate, dipotassium hydrogen phosphate, tripotassium phosphate, potassium pyrophosphate, potassium polyphosphate, phosphorous acid, sodium hydrogen phosphite, ammonium hydrogen phosphite, potassium hydrogen phosphite, sodium dihydrogen phosphite, sodium phosphite, lithium phosphite, potassium phosphite, magnesium phosphite, calcium phosphite, triethyl phosphite, triphenyl phosphite, pyrophosphorous acid and other phosphorous acid compounds can be used. These additives can be used alone or in combination. However, it is preferable to use phosphonic acids as part or all of the phosphorus oxoacids. The use of phosphonic acids prevents yellowing of the cellulose fibers, thus improving the light transmission of the dispersion.

[0045] When the additive (A) is added, the cellulose fibers may be in a dry state, a wet state, or a slurry state. The additive (A) may be in a powder state or an aqueous solution state. However, it is preferable to add the additive (A) in an aqueous solution state to the cellulose fibers in a dry state, since this ensures high reaction uniformity.

[0046] The amount of additive (A) added is preferably 1 to 10,000 g, more preferably 100 to 5,000 g, and particularly preferably 300 to 1,500 g, per kg of cellulose fiber. If the amount is less than 1 g, the effect of adding additive (A) may not be obtained. On the other hand, if the amount is more than 10,000 g, the effect of adding additive (A) may reach a plateau.

[0047] (Additive (B)) The additive (B) includes at least one of urea and a urea derivative. For example, urea, thiourea, biuret, phenylurea, benzylurea, dimethylurea, diethylurea, tetramethylurea, etc. can be used as the additive (B). These ureas or urea derivatives can be used alone or in combination. However, it is preferable to use urea.

[0048] When the additive (B) is heated, it decomposes into isocyanic acid and ammonia as shown in the following reaction formula (1). The isocyanic acid is highly reactive and forms hydroxyl groups of cellulose and carbamate as shown in the following reaction formula (2). Therefore, the addition of the additive (B) to cellulose fibers promotes the introduction of carbamate.

[0049] NH2-CO-NH2→ HN=C=O+NH3…(1) Cell-OH+HN=C=O → Cell-OC-NH2…(2) Note that Cell refers to a cellulose molecule.

[0050] The amount of additive (B) added is preferably 0.01 to 100 mol, more preferably 0.2 to 20 mol, and particularly preferably 0.5 to 10 mol, relative to 1 mol of additive (A). If the amount added is less than 0.01 mol, the introduction of carbamate may not proceed. On the other hand, if the amount added exceeds 100 mol, the effect of adding urea may reach a plateau.

[0051] (Other additives) In addition to the additives (A) and (B), it is preferable to add a hydroxide salt, particularly sodium hydroxide, to the cellulose fibers. The hydroxide salt functions as a pH adjuster and also makes it easier to defibrate the cellulose fibers due to the osmotic pressure effect.

[0052] (heating) The heating temperature when the cellulose fibers to which the additive (A) or (B) has been added is preferably 100 to 210°C, more preferably 100 to 200°C, and particularly preferably 100 to 160°C. If the heating temperature is 100°C or higher, the phosphorus oxoacid ester can be introduced. However, if the heating temperature exceeds 210°C, the cellulose may deteriorate rapidly, which may cause coloring or a decrease in viscosity. In addition, if the heating temperature exceeds 160°C, the B-type viscosity of the cellulose fine fibers may decrease, and the light transmittance may decrease.

[0053] The pH when the cellulose fiber to which the additive (A) or (B) is added is heated is preferably less than 3.0, more preferably 2.8 or less, and particularly preferably 2.5 or less. The lower the pH, the easier it is to introduce the phosphorus oxoacid ester or carbamate. However, if the pH is less than 2.1, the light transmittance and viscosity tend to decrease, and in particular, if the pH is less than 2.0, there is a risk that the deterioration of the cellulose fiber will progress rapidly. Therefore, the pH is preferably 2.0 or more, more preferably 2.1 or more.

[0054] The cellulose fibers to which the additive (A) or (B) has been added are preferably heated until the cellulose fibers are dried. Specifically, the cellulose fibers are dried until the moisture content of the cellulose fibers is preferably 10% or less, more preferably 0.1% or less, and particularly preferably 0.001% or less. Of course, the cellulose fibers may be in an absolutely dry state with no moisture.

[0055] The heating time of the cellulose fiber containing the additive (A) or the additive (B) is, for example, 1 to 1,440 minutes, preferably 10 to 180 minutes, and more preferably 30 to 120 minutes. If the heating time is too long, the introduction of the phosphorus oxoacid ester or carbamate may proceed too much. In addition, if the heating time is too long, the cellulose fiber may turn yellow.

[0056] As a device for heating the cellulose fiber to which the additive (A) or the additive (B) has been added, for example, a hot air dryer, a kiln, a heated kneader, a papermaking machine, a dry pulp machine, etc. can be used.

[0057] (Pretreatment) Prior to or after the introduction of the phosphorus oxoacid ester or carbamate into the cellulose fibers, the cellulose fibers may be subjected to a pretreatment such as beating, if necessary. By subjecting the pulp fibers to a pretreatment prior to defibration of the cellulose fibers, the number of defibrations can be significantly reduced, and the energy required for defibration can be saved.

[0058] The pretreatment of the cellulose fibers can be by physical or chemical means, preferably by physical and chemical means. The pretreatment by physical means and the pretreatment by chemical means can be carried out simultaneously or separately.

[0059] As a pretreatment by a physical method, beating is preferably adopted. When cellulose fibers are beaten, the cellulose fibers are cut into uniform pieces. Therefore, entanglement of the cellulose fibers with each other is prevented (agglomeration is prevented). From this viewpoint, beating is preferably performed until the freeness of the cellulose fibers becomes 700 ml or less, more preferably 500 ml or less, and particularly preferably 300 ml or less.

[0060] The freeness of the cellulose fiber is a value measured in accordance with JIS P8121-2 (2012). The beating can be carried out using, for example, a refiner or a beater.

[0061] Examples of pretreatments by chemical methods include hydrolysis of polysaccharides with acids (acid treatment), hydrolysis of polysaccharides with enzymes (enzyme treatment), swelling of polysaccharides with alkali (alkali treatment), oxidation of polysaccharides with oxidizing agents (oxidation treatment), reduction of polysaccharides with reducing agents (reduction treatment), etc. However, as pretreatments by chemical methods, enzyme treatment is preferred, and in addition, one or more treatments selected from acid treatment, alkali treatment, and oxidation treatment are more preferred. The alkali treatment will be described in detail below.

[0062] As a method of alkali treatment, for example, there is a method in which cellulose fibers to which an ester of phosphorus oxoacid or the like has been introduced are immersed in an alkaline solution.

[0063] The alkaline compound contained in the alkaline solution may be an inorganic alkaline compound or an organic alkaline compound. Examples of inorganic alkaline compounds include hydroxides of alkali metals or alkaline earth metals, carbonates of alkali metals or alkaline earth metals, and phosphorus oxoacid salts of alkali metals or alkaline earth metals. Examples of hydroxides of alkali metals include lithium hydroxide, sodium hydroxide, potassium hydroxide, and the like. Examples of hydroxides of alkaline earth metals include calcium hydroxide, and the like. Examples of carbonates of alkali metals include lithium carbonate, lithium hydrogen carbonate, potassium carbonate, potassium hydrogen carbonate, sodium carbonate, sodium hydrogen carbonate, and the like. Examples of carbonates of alkaline earth metals include calcium carbonate, and the like. Examples of phosphorus oxoacid salts of alkali metals include lithium phosphate, potassium phosphate, trisodium phosphate, disodium hydrogen phosphate, and the like. Examples of phosphates of alkaline earth metals include calcium phosphate, calcium hydrogen phosphate, and the like.

[0064] Examples of the organic alkali compound include ammonia, aliphatic amines, aromatic amines, aliphatic ammonium, aromatic ammonium, heterocyclic compounds, and their hydroxides, carbonates, phosphates, etc. Specific examples include ammonia, hydrazine, methylamine, ethylamine, diethylamine, triethylamine, propylamine, dipropylamine, butylamine, diaminoethane, diaminopropane, diaminobutane, diaminopentane, diaminohexane, cyclohexylamine, aniline, tetramethylammonium hydroxide, tetraethylammonium hydroxide, tetrapropylammonium hydroxide, tetrabutylammonium hydroxide, benzyltrimethylammonium hydroxide, pyridine, N,N-dimethyl-4-aminopyridine, ammonium carbonate, ammonium hydrogen carbonate, diammonium hydrogen phosphate, etc.

[0065] The solvent for the alkaline solution may be either water or an organic solvent, but is preferably a polar solvent (water, a polar organic solvent such as alcohol), and more preferably an aqueous solvent containing at least water.

[0066] The pH of the alkaline solution at 25° C. is preferably 9 or more, more preferably 10 or more, and particularly preferably 11 to 14. When the pH is 9 or more, the yield of cellulose fine fibers is high. However, when the pH exceeds 14, the handling property of the alkaline solution is deteriorated.

[0067] (Washing) The cellulose fibers into which the phosphorus oxoacid ester or the like has been introduced are preferably washed prior to defibration. By washing the cellulose fibers, by-products and unreacted substances can be washed away. Furthermore, if this washing is performed prior to the alkali treatment in the pretreatment, the amount of alkaline solution used in the alkali treatment can be reduced.

[0068] The cellulose fibers can be washed using, for example, water or an organic solvent.

[0069] (Defibrilization) The cellulose fibers to which esters of phosphorus oxyacids etc. have been introduced are defibrated (fine-processed) after washing. Through this defibration, the pulp fibers become microfibrillated and turn into fine cellulose fibers (cellulose nanofibers (CNF)).

[0070] When defibrating cellulose fibers, it is preferable to prepare the cellulose fibers in a slurry state. The solid content of this slurry is preferably 0.1 to 20 mass%, more preferably 0.5 to 10 mass%, and particularly preferably 1.0 to 5.0 mass%. When the solid content is within the above range, the cellulose fibers can be defibrated efficiently.

[0071] The cellulose fibers can be defibrated by using one or more means selected from homogenizers such as high-pressure homogenizers and high-pressure homogenizers, grinders, grinders, and other mill-type friction machines, refiners such as conical refiners and disk refiners, and various bacteria. However, the cellulose fibers are preferably defibrated by using a device or method that uses a water flow, particularly a high-pressure water flow, to finely disperse the cellulose fibers. This device or method results in very uniform dimensions and uniform dispersion of the resulting cellulose fine fibers. In contrast, for example, when a grinder that grinds between rotating grindstones is used, it is difficult to uniformly finely disperse the cellulose fibers, and in some cases, there is a risk that some fiber lumps will remain undisintegrated.

[0072] Grinders used to defibrate cellulose fibers include, for example, the Masscolloider manufactured by Masuko Sangyo Co., Ltd. Devices that use high-pressure water flow to pulverize materials include, for example, Starburst (registered trademark) manufactured by Sugino Machine Co., Ltd. and Nanovater (registered trademark) manufactured by Yoshida Kikai Kogyo Co., Ltd. High-speed rotary homogenizers used to defibrate cellulose fibers include the Clearmix-11S manufactured by M Technique Co., Ltd.

[0073] The present inventors have found that when cellulose fibers are defibrated using both a method of grinding between rotating grinding wheels and a method of refining with a high-pressure water jet, and the resulting fibers are observed under a microscope, the fibers obtained using the method of refining with a high-pressure water jet have a more uniform fiber width.

[0074] Defibration using a high-pressure water stream is preferably performed by pressurizing a dispersion of cellulose fibers with a pressure booster to, for example, 30 MPa or more, preferably 100 MPa or more, more preferably 150 MPa or more, and particularly preferably 220 MPa or more (high pressure condition), spraying it from a nozzle with a pore diameter of 50 μm or more, and reducing the pressure so that the pressure difference is, for example, 30 MPa or more, preferably 80 MPa or more, and more preferably 90 MPa or more (reduced pressure condition). The pulp fibers are defibrated by the cleavage phenomenon caused by this pressure difference. If the pressure of the high-pressure condition is low or the pressure difference from the high-pressure condition to the reduced pressure condition is small, the defibration efficiency decreases, and repeated defibration (spraying from the nozzle) becomes necessary to achieve the desired fiber width.

[0075] As a device for defibrating with a high-pressure water flow, it is preferable to use a high-pressure homogenizer. A high-pressure homogenizer is a homogenizer capable of ejecting a slurry of cellulose fibers at a pressure of, for example, 10 MPa or more, preferably 100 MPa or more. When cellulose fibers are treated with a high-pressure homogenizer, collisions between the cellulose fibers, pressure differences, microcavitation, etc., occur, and the cellulose fibers are effectively defibrated. Therefore, the number of defibration treatments can be reduced, and the production efficiency of cellulose fine fibers can be improved.

[0076] It is preferable to use a high-pressure homogenizer that causes the cellulose fiber slurry to collide in a straight line. Specifically, for example, a high-pressure homogenizer of the counter-collision type (MICROFLUIDIZER (registered trademark), wet jet mill) is used. In this device, two upstream flow paths are formed so that the pressurized cellulose fiber slurry collide in a counter-collision manner at the junction. The cellulose fiber slurry collides at the junction, and the collided cellulose fiber slurry flows out from the downstream flow path. The downstream flow path is provided perpendicular to the upstream flow path, and a T-shaped flow path is formed by the upstream flow path and the downstream flow path. When such a counter-collision type high-pressure homogenizer is used, the energy provided by the high-pressure homogenizer is converted to collision energy to the maximum extent, so that the cellulose fibers can be defibrated more efficiently.

[0077] The cellulose fibers are preferably defibrated so that the average fiber width, average fiber length, crystallinity, etc. of the resulting cellulose fine fibers have desired values ​​or evaluations. EXAMPLES

[0078] Next, an embodiment of the present invention will be described.

[0079] A test was conducted to produce cellulose fine fibers by adding phosphorus oxoacid (phosphonic acid), hydroxide salts (sodium hydroxide) and urea to cellulose fibers, heating and washing them, and then defibrating them. Bleached softwood kraft pulp was used as the cellulose fibers. Defibration was performed using a high-pressure homogenizer.

[0080] The amounts of phosphorus oxoacid, sodium hydroxide and urea added, the pH of these solutions (reagent A), the heating temperature and time, and the number of defibration passes were as shown in Table 1. The physical properties of the obtained cellulose fine fibers are shown in Table 2. The methods for evaluating B-type viscosity and light transmittance were as described above. Note that an amount of urea added of 0 mmol / g in Table 1 means "no addition," an amount of carbamate groups introduced of 0 mmol / g in Table 2 means "not introduced," and "-" in Comparative Example 3 means "not measured."

[0081] [Table 1]

[0082] [Table 2]

[0083] (Consideration) From Table 2, it can be seen that when the amount of phosphorus oxoacid groups introduced exceeds 2.0 mmol per 1 g of cellulose fiber, both the Brookfield viscosity and the light transmittance are improved. [Industrial Applicability]

[0084] INDUSTRIAL APPLICABILITY The present invention can be used as cellulose fine fibers and a method for producing the same.

Claims

1. The fiber width is 1 to 200 nm, A part of the hydroxyl groups of the cellulose fiber is substituted with a functional group represented by the following structural formula (1) to introduce an ester of phosphorus oxoacid, the amount of the functional group represented by the structural formula (1) introduced exceeds 2.0 mmol per 1 g of cellulose fiber, and the axial ratio is 3 to 1,000,000; a part of the hydroxyl groups of the cellulose fibers is substituted with a carbamate group to introduce a carbamate; The amount of the carbamate group introduced is 0.69 to 2.34 mmol per 1 g of the cellulose fiber. The cellulose fine fibers are characterized by the following: [Structural formula (1)] 【Chemistry 1】 In structural formula (1), a, b, m, and n are natural numbers. At least one of A1, A2, ..., An and A' is O-, and the rest are R, OR, NHR, or none. R is any of a hydrogen atom, a saturated linear hydrocarbon group, a saturated branched hydrocarbon group, a saturated cyclic hydrocarbon group, an unsaturated linear hydrocarbon group, an unsaturated branched hydrocarbon group, an aromatic group, and derivatives thereof. α is a cation composed of an organic or inorganic substance.

2. The crystallinity is 50 to 100%. The cellulose fine fibers according to claim 1.

3. The light transmittance of the dispersion (0.2% solids solution) is 50.0% or more. The cellulose fine fibers according to claim 1.

4. The B-type viscosity of the dispersion at a concentration of 1% by mass (w / w) is 10 to 300,000 cps. The cellulose fine fibers according to claim 1.

5. A part of the hydroxyl groups of the cellulose fibers is substituted with a functional group represented by the following structural formula (2) to introduce an ester of phosphonic acid, The amount of the functional group represented by the structural formula (2) introduced is more than 2.0 mmol and not more than 3.4 mmol per 1 g of cellulose fiber. The cellulose fine fibers according to claim 1. [Structural formula (2)] 【Chemistry 2】 In structural formula (2), α is none, R, or NHR. R is a hydrogen atom, a saturated linear hydrocarbon group, a saturated branched hydrocarbon group, a saturated cyclic hydrocarbon group, an unsaturated linear hydrocarbon group, an unsaturated branched hydrocarbon group, an aromatic group, or a group derived from any of these. β is a cation made of an organic or inorganic substance.

6. In producing the cellulose fine fibers according to claim 1, A solution having a pH of 2.0 or more and less than 3.0, which is composed of an additive (A) containing phosphonic acids and an additive (B) containing at least one of urea and a urea derivative, is added to cellulose fibers, and the fibers are heated and defibrated. A part of the hydroxyl groups of the cellulose fibers is replaced with a carbamate group to introduce a carbamate, The amount of the carbamate group introduced is 0.69 to 2.34 mmol per 1 g of the cellulose fiber. A method for producing cellulose fine fibers, comprising the steps of:

7. Hydroxide salts are also added to the cellulose fibers, and the heating is carried out at 100 to 160°C, and then the cellulose fibers are washed. The method for producing cellulose fine fibers according to claim 6.

8. The amount of the additive (B) added is 0.5 to 10 mol per 1 mol of the additive (A). The method for producing cellulose fine fibers according to claim 6.