Abstract

To provide a novel fluorine-containing polymer useful for a water and oil repellent agent.SOLUTION: A novel fluorine-containing polymer has a repeating unit derived from a fluorine-containing monomer (f) having Rf1 or Rf2, where Rf1 is -CF3, -CF2H, or -CFH2; Rf2 is -CF2-, or -CFH-; and Rf1 and Rf2 are not parts of a 2≤C fluoroalkyl group, and -CH2-CF2-CH2-.SELECTED DRAWING: None

Description

[Technical field]

[0001] The present disclosure relates to a fluorine-containing polymer. [Background technology]

[0002] It is known that certain non-fluorinated polymers can impart oil resistance when used for surface treatment of substrates (Patent Document 1). [Prior art documents] [Patent documents]

[0003] [Patent Document 1] International Publication No. 2020-054856 Summary of the Invention [Problem to be solved by the invention]

[0004] An object of the present disclosure is to provide a new fluorine-containing polymer. [Means for solving the problem]

[0005] The present disclosure includes the following aspects: [Section 1] R f1 or R f2 A fluorine-containing polymer having a repeating unit derived from a fluorine-containing monomer (f) having the following formula: R f1 is -CF3, -CF2H, or -CFH2, R f2 is -CF2- or -CFH-, R f1 and R f2 is a fluoropolymer that is not a part of a fluoroalkyl group having 2 or more carbon atoms or -CH2-CF2-CH2-. [Section 2] R f1 is an oxygen atom or a nitrogen atom; R f2Item 2. The fluorine-containing polymer according to item 1, wherein at least one of the adjacent positions is an oxygen atom or a nitrogen atom. [Section 3] R f1 is CF3-, R f2 is -CF2-, Item 3. The fluorine-containing polymer according to item 1 or 2. [Section 4] 4. The fluorine-containing polymer according to any one of items 1 to 3, wherein the fluorine-containing monomer (f) is an acrylic monomer or an allyl monomer. [Section 5] Fluorine-containing monomer (f) is R f1 , or R f1 or R f2 Item 5. The fluorine-containing polymer according to any one of items 1 to 4, which contains a hydrocarbon group having 2 to 40 carbon atoms, comprising: [Section 6] Item 6. The fluorine-containing polymer according to any one of items 1 to 5, which does not have a fluoroalkyl group having 2 or more carbon atoms. [Section 7] The fluorine-containing monomer (f) is formula: CH2=C(-X f )-Y f -Z f α wherein each symbol represents independently at each occurrence: X f is a hydrogen atom, a monovalent organic group, or a halogen atom, Y f is Y f1 and Y f2 is a 1+α valent group consisting of one or more groups selected from the group consisting of Y f1 is a group consisting of one or more selected from the group consisting of a direct bond, -O-, -C(=O)-, -C(=NR')-, -S-, -S(=O)2-, -NR'-, -C(OR')R'-, -C(OR')(-)2, -N(-)2 (R' is a hydrogen atom or a monovalent organic group); Y f2 is a group consisting of one or more groups selected from the group consisting of aliphatic groups and aromatic groups, Z f is R f1 , or R f1 or R f2 is a hydrocarbon group having 2 to 40 carbon atoms, α is 1 to 3.] Item 7. The fluorine-containing polymer according to any one of items 1 to 6, which is a compound represented by the following formula: [Section 8] Z f R f1 Item 8. The fluorine-containing polymer according to item 7, [Section 9] The fluorine-containing monomer (f) is represented by the formula: CH2=C(-X f )-C(=O)-Y f11 -(Y f21 -Y f12 ) β -Y f22 -Y f13 -Z f or CH2=C(-X f )-CH2-Y f11 -(Y f21 -Y f12 ) β -Y f22 -Y f13 -Z f wherein each symbol represents independently at each occurrence: X f is a hydrogen atom, a monovalent organic group, or a halogen atom, Y f11 is -O- or -NH-, Y f21 is a group consisting of one or more groups selected from the group consisting of aliphatic groups and aromatic groups, Y f12 is a group consisting of one or more selected from the group consisting of -O-, -C(=O)-, -C(=NR')-, -S-, -S(=O)2-, -NR'-, and -C(OR')R'- (R' is a hydrogen atom or a monovalent organic group), β is 0 to 3; Y f22 is a group consisting of one or more groups selected from the group consisting of aliphatic groups and aromatic groups, Y f13 is -O-, -OC(=O)-O-, -OC(=O)-NR'-, -NR'-, -NR'-C(=O)-O-, -NR'-C(=O)-NR'-, -C(=O)-O-, -C(=O)-NR'-, or -SONR'- (R' is a hydrogen atom or a monovalent organic group). Z f is R f1 , or R f1 or R f2 It is a hydrocarbon group having 2 to 40 carbon atoms. 9. The fluorine-containing polymer according to any one of items 1 to 8, which is a compound represented by the following formula: [Section 10] Y f22 is the formula -Y f221 -Y f222 - [In the formula, Y f221 is a direct bond or a hydrocarbon group having 2 to 40 carbon atoms, Y f222 is a direct bond or a phenylene group. is a group represented by Y f13 is -O- or -NR'- (R' is a hydrogen atom or a monovalent organic group), β is 0 or 1; Z f is R f1 Item 10. The fluorine-containing polymer according to item 9, [Section 11] A repeating unit derived from a monomer (a) having a hydrocarbon group having 6 to 40 carbon atoms, A repeating unit derived from a hydrophilic group-containing monomer (b), A repeating unit derived from an ionic group-containing monomer (c), Repeat units derived from halogenated olefin monomer (d), and Crosslinking monomer (e) Item 10. The fluorine-containing polymer according to any one of items 1 to 9, having one or more of the following: [Section 12] The fluorine-containing monomer (f) is represented by the formula: CH2=C(-X f )-C(=O)-Y f11 -(Y f21 -Y f12 ) β -Y f22 -Y f13 -Z f wherein each symbol represents independently at each occurrence: X f is a hydrogen atom, a monovalent organic group, or a halogen atom, Y f11 is -O- or -NH-, Y f21 is a group consisting of one or more groups selected from the group consisting of aliphatic groups and aromatic groups, Y f12 is a group consisting of one or more selected from the group consisting of -O-, -C(=O)-, -C(=NR')-, -S-, -S(=O)2-, -NR'-, and -C(OR')R'- (R' is a hydrogen atom or a monovalent organic group), β is 0 to 3; Y f22 is a group consisting of one or more groups selected from the group consisting of aliphatic groups and aromatic groups, Y f13 is -O-, -OC(=O)-O-, -OC(=O)-NR'-, -NR'-, -NR'-C(=O)-O-, -NR'-C(=O)-NR'-, -C(=O)-O-, -C(=O)-NR'-, or -SONR'- (R' is a hydrogen atom or a monovalent organic group). Z f is -CF3. A compound represented by the formula: Item 12. The fluorine-containing polymer according to any one of items 1 to 11, which has a repeating unit derived from a monomer (a) having a hydrocarbon group having 6 or more and 40 or less carbon atoms. [Section 13] Item 13. A dispersion comprising the fluorine-containing polymer according to any one of items 1 to 12 and a liquid medium. [Section 14] Item 13. A water- and oil-repellent agent comprising the fluorine-containing polymer according to any one of items 1 to 12. [Section 15] Item 15. The water / oil repellent according to item 14, which is for use in textile products or paper products. [Section 16] Item 16. A method for producing a treated substrate, comprising treating the substrate with the water / oil repellent according to item 14 or 15. [Section 17] Item 17. The method according to item 16, wherein the substrate is a textile product or a paper product. [Section 18] Item 13. A product having the fluorine-containing polymer according to any one of items 1 to 12 adhered thereto. Effect of the Invention

[0006] According to the present disclosure, a new fluorinated polymer can be provided. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0007] <Terminology> As used herein, the term "n-valent group" refers to a group having n bonds, i.e., a group that forms n bonds. The term "n-valent organic group" refers to an n-valent group containing carbon. Such an organic group is not particularly limited, but may be a hydrocarbon group or a derivative thereof. The derivative of a hydrocarbon group refers to a group having one or more N, O, S, Si, amide, sulfonyl, siloxane, carbonyl, carbonyloxy, halogen, etc. at the end or molecular chain of the hydrocarbon group.

[0008] As used herein, the term "hydrocarbon group" refers to a group containing carbon and hydrogen, which is a group obtained by removing a hydrogen atom from a hydrocarbon. Such a hydrocarbon group is not particularly limited, but includes, for example, C 1-40 Examples of the hydrocarbon group include an aliphatic hydrocarbon group and an aromatic hydrocarbon group. The "aliphatic hydrocarbon group" may be linear, branched, or cyclic, and may be saturated or unsaturated. The hydrocarbon group may contain one or more ring structures. The hydrocarbon group may be substituted with one or more substituents, if explicitly stated.

[0009] In this specification, when a term (symbol) that may occur multiple times in a chemical structure is defined, the definition applies independently at each occurrence, unless otherwise stated, regardless of whether "independently at each occurrence," "independently of each other," "independently of each other," or similar expressions are explicitly stated.

[0010] It should be understood that the chemical structures illustrated herein do not encompass chemical structures that would be recognized by those of ordinary skill in the art as being chemically impossible or extremely unstable.

[0011] <Fluorine-containing polymer> The fluorine-containing polymer in the present disclosure is R f1 or R f2 The fluorine-containing polymer has a repeating unit derived from a fluorine-containing monomer (f) having the following formula:

[0012] [Characteristics of Fluorine-containing Polymer] The fluoropolymer of the present disclosure is capable of adhering to a substrate and imparting liquid repellency (for example, oil repellency, water repellency, oil resistance, water resistance) to the substrate.

[0013] The HD (n-hexadecane) contact angle of the fluoropolymer may be 10° or more, 15° or more, 25° or more, 35° or more, 40° or more, 45° or more, 55° or more, or 65° or more, preferably 30° or more, and may be 100° or less, 90° or less, or 75° or less. When the fluoropolymer has an HD contact angle equal to or greater than the above lower limit, it can impart good liquid repellency (particularly oil repellency) to the substrate. The HD contact angle is the static contact angle of the fluoropolymer with respect to a spin-coated film, and is obtained by dropping 2 μL of HD onto the spin-coated film and measuring the contact angle 1 second after the drop lands.

[0014] The water contact angle of the fluoropolymer may be 35° or more, 40° or more, 45° or more, 50° or more, 55° or more, 65° or more, 75° or more, 85° or more, 90° or more, or 100° or more, and may be 160° or less, 140° or less, 130° or less, 120° or less, 110° or less, 100° or less, or 90° or less. When the fluoropolymer has a water contact angle of the above lower limit or more, it can impart good liquid repellency (particularly water repellency) to the substrate. The water contact angle is the static contact angle of the fluoropolymer with respect to the spin-coated film, and is obtained by dropping 2 μL of water on the spin-coated film and measuring the contact angle 1 second after the drop lands.

[0015] The weight average molecular weight of the fluorine-containing polymer may be 3000 or more, 5000 or more, 10000 or more, 30000 or more, 100000 or more, 300000 or more, or 500000 or more; and may be 5000000 or less, 3000000 or less, 1000000 or less, 750000 or less, 500000 or less, 300000 or less, 100000 or less, 75000 or less, 50000 or less, 30000 or less, 100000 or less, or 5000 or less.

[0016] The melting point or glass transition point (e.g., melting point) of the fluorine-containing polymer may be 0° C. or higher, 20° C. or higher, 30° C. or higher, 35° C. or higher, 40° C. or higher, 45° C. or higher, 50° C. or higher, or 55° C. or higher, and may be 200° C. or lower, 150° C. or lower, 100° C. or lower, 80° C. or lower, or 70° C. or lower. The melting point is usually 30° C. or higher, preferably 40° C. or higher, for example, 75° C. or higher.

[0017] The fluoropolymer is preferably a compound having carbon of bio-based origin. The bio-based degree is measured in accordance with ASTM D6866. The bio-based degree of the fluoropolymer may be 20% or more, preferably 30% or more, more preferably 50% or more, even more preferably 60% or more, even more preferably 70% or more, and most preferably 80% or more or 90% or more, for example 100%. A high bio-based degree means that the amount of fossil resource-based materials, such as petroleum, used is small, and from this viewpoint, the higher the bio-based degree of the fluoropolymer, the more preferable it is.

[0018] In the present disclosure, the fluorine-containing polymer has the above-mentioned Rf 1 or Rf 2 On the other hand, the fluorine-containing polymer in the present disclosure may not have any one selected from the group consisting of a fluoroalkyl group having 8 or more carbon atoms, a perfluoroalkyl group having 8 or more carbon atoms, a fluoroalkyl group having 4 or more carbon atoms, a perfluoroalkyl group having 4 or more carbon atoms, a fluoroalkyl group having 2 or more carbon atoms, and a perfluoroalkyl group having 2 or more carbon atoms. The fluorine-containing polymer in the present disclosure can impart liquid repellency to a substrate even if it does not contain these fluorine-containing groups. In this specification, the fluoroalkyl group may mean a group in which one or more hydrogen atoms in each carbon atom of an alkyl group are substituted with a fluorine atom.

[0019] [R f1 and R f2 〕 The fluorine-containing polymer is R f1 or R f2 For example, R f1 where R f1 and R f2 is not a part of a fluoroalkyl group having 2 or more carbon atoms. f2 may not be part of -CH2-CF2-CH2-.

[0020] R f1 R is -CF3, -CF2H, or -CFH2, preferably -CF3. f1The adjacent position of may be an oxygen atom or a nitrogen atom.

[0021] R f2 is -CF2- or -CFH-, preferably -CF2-. f2 At least one of the adjacent positions may be an oxygen atom or a nitrogen atom.

[0022] [(f) Fluorine-containing monomer] The fluorine-containing polymer has repeating units derived from a fluorine-containing monomer (f).

[0023] The fluorine-containing monomer (f) is R f1 or R f2 R f1 and R f2 is as explained above.

[0024] [Structure of monomer (f)] The fluorine-containing monomer (f) is formula: CH2=C(-X f )-Y f -Z f α wherein each symbol represents independently at each occurrence: X f is a hydrogen atom, a monovalent organic group, or a halogen atom, Y f is Y f1 and Y f2 is a 1+α valent group consisting of one or more groups selected from the group consisting of Y f1 is a group consisting of one or more selected from the group consisting of a direct bond, -O-, -C(=O)-, -C(=NR')-, -S-, -S(=O)2-, -NR'-, -C(OR')R'-, -C(OR')(-)2, -N(-)2 (R' is a hydrogen atom or a monovalent organic group); Y f2 is a group consisting of one or more groups selected from the group consisting of aliphatic groups and aromatic groups, Z f is R f1 , or Rf1 or R f2 is a hydrocarbon group having 2 to 40 carbon atoms, α is 1 to 3.] The compound may be represented by the formula:

[0025] R f1 For example, Z f may be included in R f2 is, for example, an organic group, Y f2 , Z f , R f2 may be included in the

[0026] The fluorine-containing monomer (f) has an ethylenically unsaturated polymerizable group and may be an acrylic monomer or an allyl monomer.

[0027] (X f ) X f is a hydrogen atom, a monovalent organic group, or a halogen atom. Here, the monovalent organic group may be an aliphatic group or aromatic group having 1 to 30 carbon atoms (e.g., 1 to 20, 1 to 10, or 1 to 4 carbon atoms) (e.g., a substituted or unsubstituted alkyl group (e.g., a methyl group), a substituted or unsubstituted benzyl group, or a substituted or unsubstituted phenyl group). The halogen atom may be any halogen except a fluorine atom. X f may be a hydrogen atom, a methyl group or a chlorine atom.

[0028] (Y f ) Y f is Y f1 and Y f2 is a 1+α valent group consisting of one or more groups selected from the group consisting of Y f1 is a group consisting of one or more selected from the group consisting of a direct bond, -O-, -C(=O)-, -C(=NR')-, -S-, -S(=O)2-, -NR'-, -C(OR')R'-, -C(OR')(-)2, -N(-)2 (R' is a hydrogen atom or a monovalent organic group); Y f2 is a group composed of one or more members selected from the group consisting of aliphatic groups and aromatic groups.

[0029] Y f The molecular weight may be 10 or more, 50 or more, 100 or more, 200 or more, 300 or more, 500 or more, or 750 or more; and may be 3000 or less, 2500 or less, 2000 or less, 1500 or less, 1000 or less, 750 or less, 500 or less, 300 or less, 200 or less, 100 or less, or 50 or less.

[0030] In the following, Y f1 and Y f2 This article explains:

[0031] ○ Y f1 Y f1 is a non-hydrocarbon linker.

[0032] Y f1 is a direct bond or a divalent or higher group. f1 The valence of Y may be 2 to 4, 2 to 3, or 2. f1 is preferably not only a direct bond.

[0033] Y f1 The molecular weight may be 10 or more, 50 or more, 100 or more, 200 or more, 300 or more, or 500 or more, and may be 1000 or less, 750 or less, 500 or less, 300 or less, 200 or less, 100 or less, or 50 or less.

[0034] Y f1 is composed of one or more selected from the group consisting of -O-, -C(=O)-, -S(=O)2-, -NR'-, -C(OR')R'-, and -C(OR')(-)2 (wherein R' in each occurrence is independently a hydrogen atom or a monovalent organic group).

[0035] R' is a hydrogen atom or a monovalent organic group. The organic group may be, for example, an aliphatic group or aromatic group having 1 to 30 carbon atoms (e.g., 1 to 20, 1 to 10, or 1 to 4 carbon atoms) (e.g., a substituted or unsubstituted alkyl group, a substituted or unsubstituted benzyl group, or a substituted or unsubstituted phenyl group). The same may be true for other R's in this specification.

[0036] Y f1 Examples include: direct binding, -O-, -OC(=O)-, -OC(=O)-O-, -OC(=O)-NR'-, -NR'-, -NR'-C(=O)-, -NR'-C(=O)-O-, -NR'-C(=O)-NR'-, -C(=O)-, -C(=O)-O-, -C(=O)-NR'-, -SO2-, -SO2NR'-, -C(OR')R'-, -C(OR')(-)2 etc. (wherein R' in each occurrence is independently a hydrogen atom or a monovalent organic group.) Examples include:

[0037] ○ Y f2 Y f2 may be a group composed of one or more groups selected from the group consisting of aliphatic groups and aromatic groups.

[0038] Y f2 is a divalent or higher group. f2 The valency of may be, for example, 2 to 4, 2 to 3, or 2.

[0039] Y f2may have 1 or more, 2 or more, 3 or more, 4 or more, 6 or more, 8 or more, 10 or more, 12 or more, 14 or more, 16 or more, or 18 or more; and may be 40 or less, 35 or less, 30 or less, 25 or less, 20 or less, 15 or less, 10 or less, or 5 or less.

[0040] Y f2 The molecular weight may be 10 or more, 50 or more, 100 or more, 200 or more, 300 or more, or 500 or more, and may be 2000 or less, 1500 or less, 1000 or less, 750 or less, 500 or less, 300 or less, 200 or less, 100 or less, or 50 or less.

[0041] Y f2 is a group consisting of one or more groups selected from the group consisting of aliphatic groups and aromatic groups, and Y f2 may consist of only aliphatic groups, may consist of only aromatic groups, or may consist of a combination of aliphatic and aromatic groups. f2 Y itself may be an aliphatic group or an aromatic group. f2 Y may be a hydrocarbon group or a non-hydrocarbon group (including heteroatoms). f2 may be linear, branched or cyclic.

[0042] Y f2 may be a linker of a hydrocarbon ring which may have a substituent, a hydrocarbon aromatic ring which may have a substituent, or a heterocyclic ring which may have a substituent, or a combination thereof. For example, Y f2 may be composed of one or more selected from the group consisting of optionally substituted di- to tetravalent aliphatic hydrocarbon groups having 1 to 20 carbon atoms, optionally substituted di- to tetravalent aromatic hydrocarbon rings, and optionally substituted di- to tetravalent heterocycles.

[0043] The di- to tetravalent aliphatic hydrocarbon group having 1 to 20 carbon atoms may be a cyclic, branched, or straight chain hydrocarbon group. The di- to tetravalent aliphatic hydrocarbon group having 1 to 20 carbon atoms may be a saturated or unsaturated (e.g., saturated) aliphatic hydrocarbon group. The number of carbon atoms in the aliphatic hydrocarbon group having 1 to 20 carbon atoms may be 1 or more, 2 or more, 3 or more, 4 or more, 6 or more, 8 or more, or 10 or more, and may be 15 or less, 10 or less, or 5 or less. The valence of the aliphatic hydrocarbon group may be 2 or more, 3 or more, or 4, or 4 or less, 3 or less, or 2.

[0044] The aliphatic hydrocarbon group may have a substituent. Examples of the substituent include -OR', -N(R')2, -COOR', and halogen atoms (wherein R' is independently a monovalent organic group at each occurrence). The substituent may or may not have active hydrogen. The number of the substituents may be 6 or less, 5 or less, 4 or less, 3 or less, 2 or less, 1 or less, or 0. In the aliphatic hydrocarbon group having a substituent, the amount of carbon atoms relative to the amount of carbon atoms and heteroatoms may be 70 mol% or more, 80 mol% or more, 90 mol% or more, 95 mol% or more, or 99 mol% or more, preferably 75 mol% or more, and may be 95 mol% or less, 90 mol% or less, 85 mol% or less, or 80 mol% or less.

[0045] Examples of divalent to tetravalent hydrocarbon aromatic rings include groups obtained by removing 2 to 4 hydrogen atoms from a hydrocarbon aromatic ring such as benzene, naphthalene, anthracene, phenanthrene, tetracene (naphthacene), pentacene, pyrene, and coronene. The number of ring-constituting atoms of the hydrocarbon aromatic ring is 3 to 20, 4 to 16, or 5 to 12, and preferably 5 to 12. The valence of the hydrocarbon aromatic ring may be 2 or more, 3 or more, or 4, and may be 4 or less, 3 or less, or 2.

[0046] The aromatic hydrocarbon ring may have a substituent. Examples of the substituent include -R', -OR', -N(R')2, -COOR', and halogen atoms (wherein R' is independently a hydrogen atom or a monovalent organic group at each occurrence). The substituent may or may not have active hydrogen. The number of the substituents may be 6 or less, 5 or less, 4 or less, 3 or less, 2 or less, 1 or less, or 0. In the aromatic hydrocarbon ring having a substituent, the amount of carbon atoms relative to the amount of carbon atoms and heteroatoms may be 70 mol% or more, 80 mol% or more, 90 mol% or more, 95 mol% or more, or 99 mol% or more, preferably 75 mol% or more, and the amount of carbon atoms relative to the amount of carbon atoms and heteroatoms may be 95 mol% or less, 90 mol% or less, 85 mol% or less, or 80 mol% or less.

[0047] The divalent to tetravalent heterocycle may be an aliphatic group or an aromatic group. Examples of the divalent to tetravalent heterocycle include groups obtained by removing 2 to 4 hydrogen atoms from pyridine, pyrazine, pyrimidine, pyridazine, triazine, quinoline, isoquinoline, quinazoline, cinnoline, phthalazine, quinoxaline, pyrrole, indole, furan, benzofuran, thiophene, benzothiophene, pyrazole, imidazole, benzimidazole, triazole, oxazole, benzoxazole, thiazole, benzothiazole, isothiazole, benzisothiazole, pyrrolidine, piperidine, piperazine, imidazolidine, thiazoline, etc. The number of ring-constituting atoms of the heterocycle is 3 to 20, 4 to 16, or 5 to 12, and preferably 5 to 12. The valence of the heterocycle may be 2 or more, 3 or more, or 4, and may be 4 or less, 3 or less, or 2.

[0048] The heterocycle may have a substituent. Examples of the substituent include -R', -OR', -N(R')2, -COOR', and halogen atoms (wherein R' is independently a hydrogen atom or a monovalent organic group at each occurrence). The substituent may or may not have active hydrogen. The number of the substituents may be 6 or less, 5 or less, 4 or less, 3 or less, 2 or less, 1 or less, or 0. In the heterocycle having a substituent, the amount of carbon atoms relative to the amount of carbon atoms and heteroatoms may be 60 mol% or more, 70 mol% or more, 80 mol% or more, 90 mol% or more, 95 mol% or more, or 99 mol% or more, for example, 65 mol% or more, and 95 mol% or less, 90 mol% or less, 85 mol% or less, 80 mol% or less, or 70 mol% or less.

[0049] Y f2 Examples include: -Ali- -Cy- -Ali(-)2 -Cy(-)2 (-)2Ali- (-)2Cy- (-)2Ali(-)2 (-)2Cy(-)2 -Ali-Cy- -Cy-Ali- -Cy-Ali-Cy- -Ali-Cy-Ali- [In the formula, Ali is an aliphatic hydrocarbon group having 1 to 20 carbon atoms, and Cy is a hydrocarbon aromatic ring or heterocycle.] etc.

[0050] Y f2 Examples of specific examples include: -(CH2) p - (p is 1 to 20, for example, 1 to 10), a linear hydrocarbon group having 1 to 40 carbon atoms, for example 1 to 10 unsaturated bonds; a hydrocarbon group having a branched structure and having 1 to 40 carbon atoms, for example 1 to 10 carbon atoms; -(CH2) q-Cy-(CH2) r -(q and r each independently represent an integer of 0 to 20, for example, 1 to 10, and Cy represents a hydrocarbon aromatic ring or a heterocycle). etc.

[0051] ○ Y f Example Y f In the following, R' is independently a hydrogen atom or a monovalent organic group in each occurrence. f α The group adjacent to is Y f1 It may be.

[0052] Y f An example of this is Y f If is bivalent, -Y f1 -, -Y f1 -Y f2 -, -Y f1 -Y f2 -Y f1 -, -Y f1 -Y f2 -Y f1 -Y f2 -, -Y f2 -, -Y f2 -Y f1 -, -Y f2 -Y f1 -Y f2 -, -Y f2 -Y f1 -Y f2 -Y f1 -, etc.

[0053] Y f An example of this is Y f If is trivalent, -Y f1 (-)2, -Y f1 -Y f2 (-)2, -Y f1 -(Y f2 -)2, -Y f1 -Y f2 -Y f1 (-)2, -Y f1 -Y f2 (-Y f1 -)2, -Y f1 -(Y f2 -Yf1 -)2、-And f1 -AND f2 -AND f1 -AND f2 (-)2、-And f1 -AND f2 -AND f1 -(AND f2 -) 2、 -AND f1 -AND f2 -(AND f1 -AND f2 -) 2、 -AND f1 -(AND f2 -AND f1 -AND f2 -)2; (-)2Y f1 -,(-)2Y f1 -AND f2 -,(-AND f1 )2Y f2 -,(-)2Y f1 -AND f2 -AND f1 -,(-AND f1 )2-And f2 -AND f1 -,(-AND f1 -AND f2 )2-And f1 -,(-)2Y f1 -AND f2 -AND f1 -AND f2 -,(-AND f1 )2-And f2 -AND f1 -AND f2 -,(-AND f1 -AND f2 )2-And f1 -AND f2 -,(-AND f1 -AND f2 -AND f1 )2-And f2 -; -AND f2 (-)2、-And f2 -AND f1 (-)2、-And f2 -(AND f1 -)2、-And f2 -AND f1 -AND f2 (-)2、-And f2 -AND f1 (-ANDf2 -), 2, -Y f2 -(Y f1 -Y f2 -), 2, -Y f2 -Y f1 -Y f2 -Y f1 (-), 2, -Y f2 -Y f1 -Y f2 -(Y f1 -) 2、 -Y f2 -Y f1 -(Y f2 -Y f1 -) 2、 -Y f2 -(Y f1 -Y f2 -Y f1 )2; (-)2Y f2 -, (-)2Y f2 -Y f1 -, (-Y f2 )2Y f1 -, (-)2Y f2 -Y f1 -Y f2 -, (-Y f2 )2 - Y f1 -Y f2 -, (-Y f2 -Y f1 )2 - Y f2 -, (-)2Y f2 -Y f1 -Y f2 -Y f1 -, (-Y f2 )2 - Y f1 -Y f2 -Y f1 -, (-Y f2 -Y f1 )2 - Y f2 -Y f1 -, (-Y f2 -Y f1 -Y f2 )2 - Y f1 - etc. can be mentioned.

[0054] Y f As an example of, Y f when it is tetravalent, -Y f1 (-), 3, -Y f1 -Y f2(-)3、-And f1 -(AND f2 -)3、-And f1 -AND f2 -AND f1 (-)3、-And f1 -AND f2 (-AND f1 -)3、-And f1 -(AND f2 -AND f1 -)3、-And f1 -AND f2 -AND f1 -AND f2 (-)3、-And f1 -AND f2 -AND f1 -(AND f2 -) 3、 -AND f1 -AND f2 -(AND f1 -AND f2 -) 3、 -AND f1 -(AND f2 -AND f1 -AND f2 -)3; (-)2Y f1 (-)2, (-)2Y f1 -AND f2 (-)2、(-Y f1 )2Y f2 (-)2, (-)2Y f1 -AND f2 -AND f1 (-)2、(-Y f1 )2-And f2 -AND f1 (-)2、(-Y f1 -AND f2 )2-And f1 (-)2, (-)2Y f1 -AND f2 -AND f1 -AND f2 (-)2、(-Y f1 )2-And f2 -AND f1 -AND f2 (-)2、(-Y f1 -AND f2 )2-And f1 -AND f2 (-)2、(-Y f1 -AND f2 -AND f1 )2-Andf2 (-)2; (-)3Y f1 -,(-)3Y f1 -AND f2 -,(-AND f1 )3Y f2 -,(-)3Y f1 -AND f2 -AND f1 -,(-AND f1 )3-And f2 -AND f1 -,(-AND f1 -AND f2 )3-And f1 -,(-)3Y f1 -AND f2 -AND f1 -AND f2 -,(-AND f1 )3-And f2 -AND f1 -AND f2 -,(-AND f1 -AND f2 )3-And f1 -AND f2 -,(-AND f1 -AND f2 -AND f1 )3-And f2 -; -AND f2 (-)3、-And f2 -AND f1 (-)3、-And f2 -(AND f1 -)3、-And f2 -AND f1 -AND f2 (-)3、-And f2 -AND f1 (-AND f2 -)3、-And f2 -(AND f1 -AND f2 -)3、-And f2 -AND f1 -AND f2 -AND f1 (-)3、-And f2 -AND f1 -AND f2 -(AND f1 -) 3、 -AND f2 -AND f1 -(AND f2 -AND f1 -) 3、 -ANDf2 -(AND f1 -AND f2 -AND f1 -)3; (-)2Y f2 (-)2, (-)2Y f2 -AND f1 (-)2、(-Y f2 )2Y f1 (-)2, (-)2Y f2 -AND f1 -AND f2 (-)2、(-Y f2 )2-And f1 -AND f2 (-)2、(-Y f2 -AND f1 )2-And f2 (-)2, (-)2Y f2 -AND f1 -AND f2 -AND f1 (-)2、(-Y f2 )2-And f1 -AND f2 -AND f1 (-)2、(-Y f2 -AND f1 )2-And f2 -AND f1 (-)2、(-Y f2 -AND f1 -AND f2 )2-And f1 (-)2; (-)3Y f2 -,(-)3Y f2 -AND f1 -,(-AND f2 )3Y f1 -,(-)3Y f2 -AND f1 -AND f2 -,(-AND f2 )3-And f1 -AND f2 -,(-AND f2 -AND f1 )3-And f2 -,(-)3Y f2 -AND f1 -AND f2 -AND f1 -,(-AND f2 )3-And f1 -AND f2 -AND f1 -,(-AND f2-Y f1 )3-Y f2 -Y f1 -, (-Y f2 -Y f1 -Y f2 )3-Y f1 --etc.

[0055] Y f Preferred examples of -Y f1 -, -Y f1 -Y f2 -, -Y f1 -Y f2 -Y f1 -, -Y f1 -Y f2 (-)2, -(Y f1 )2-Y f2 -(where Y f2 is trivalent), -(Y f1 )2Y f2 (-)2 (where Y f2 is tetravalent), -Y f2 -, -Y f2 -Y f1 -, -Y f2 -Y f1 -Y f2 -, -Y f2 -Y f1 (-)2, -(Y f2 )2-Y f1 -(where Y f1 is trivalent), -(Y f2 )2Y f1 (-)2 (where Y f1 is tetravalent) etc.

[0056] (Z f ) Z f is R f1 , or R f1 or R f2 A hydrocarbon group having 2 to 40 carbon atoms, such as R f1 R f1 or R f2The hydrocarbon group containing R may be an aromatic hydrocarbon group or an aliphatic hydrocarbon group, and is preferably an aliphatic hydrocarbon group, particularly preferably a saturated aliphatic hydrocarbon group (alkyl group). f1 or R f2 The hydrocarbon group containing R is branched or linear, and more preferably linear. f1 or R f2 The hydrocarbon group containing R may be saturated or unsaturated. f1 or R f2 The hydrocarbon group containing R is preferably a saturated aliphatic hydrocarbon group (alkyl group). f1 or R f2 The number of carbon atoms in the hydrocarbon group including may be 2 or more, 4 or more, 6 or more, 8 or more, 10 or more, 12 or more, 14 or more, 16 or more, 18 or more, 20 or more, or 22 or more, and is preferably 10 or more, 12 or more, 14 or more, or 16 or more, and may be 40 or less, 35 or less, 30 or less, 25 or less, 20 or less, 15 or less, or 10 or less, and is preferably 30 or less, 25 or less, or 20 or less.

[0057] (α) α is 1 to 3 (1, 2, or 3), for example, 1 or 2, for example, 1.

[0058] [Example of monomer (f)] The fluorine-containing monomer (f) is represented by the formula: CH2=C(-X f )-C(=O)-Y f11 -(Y f21 -Y f12 ) β -Y f22 -Y f13 -Z f or CH2=C(-X f )-CH2-Y f11 -(Y f21 -Y f12 ) β -Y f22 -Y f13 -Z f wherein each symbol represents independently at each occurrence: X fis a hydrogen atom, a monovalent organic group, or a halogen atom, Y f11 is -O- or -NH-, Y f21 is a group consisting of one or more groups selected from the group consisting of aliphatic groups and aromatic groups, Y f12 is a group consisting of one or more selected from the group consisting of -O-, -C(=O)-, -C(=NR')-, -S-, -S(=O)2-, -NR'-, and -C(OR')R'- (R' is a hydrogen atom or a monovalent organic group), β is 0 to 3; Y f22 is a group consisting of one or more groups selected from the group consisting of aliphatic groups and aromatic groups, Y f13 is -O-, -OC(=O)-O-, -OC(=O)-NR'-, -NR'-, -NR'-C(=O)-O-, -NR'-C(=O)-NR'-, -C(=O)-O-, -C(=O)-NR'-, or -SONR'- (R' is a hydrogen atom or a monovalent organic group). Z f is R f1 , or R f1 or R f2 It is a hydrocarbon group having 2 to 40 carbon atoms. The compound may be represented by the formula:

[0059] X f may be a hydrogen atom, a monovalent organic group, or a halogen atom, as described above.

[0060] Y f11 may be -O- or -NH-.

[0061] Y f21 may be a group consisting of one or more groups selected from the group consisting of aliphatic groups and aromatic groups, f2 The same explanation can be applied. However, Y f21 is a divalent group.

[0062] Yf12 may be a group consisting of one or more selected from the group consisting of -O-, -C(=O)-, -C(=NR')-, -S-, -S(=O)2-, -NR'-, and -C(OR')R'-, and f1 The same explanation can be applied. However, Y f12 is a divalent group.

[0063] β may be 0-3 (0, 1, 2, or 3), for example 0-2, in particular 0-1.

[0064] Y f22 may be a group consisting of one or more groups selected from the group consisting of aliphatic groups and aromatic groups, 2 The same explanation can be applied. However, Y f22 is a divalent group. Y f22 is the formula -Y f221 -Y f222 - [In the formula, Y f221 is a direct bond or a hydrocarbon group having 2 to 40 carbon atoms, Y f222 is a direct bond or a phenylene group. Here, the hydrocarbon group may be an aromatic hydrocarbon group or an aliphatic hydrocarbon group, and may be an aliphatic hydrocarbon group, particularly a saturated aliphatic hydrocarbon group (alkyl group). The hydrocarbon group may be branched or linear, for example linear. The hydrocarbon group may be saturated or unsaturated. The hydrocarbon group may be a saturated aliphatic hydrocarbon group (alkyl group). The number of carbon atoms in the hydrocarbon group may be 2 or more, 4 or more, 6 or more, 8 or more, 10 or more, 12 or more, 14 or more, 16 or more, 18 or more, 20 or more, or 22 or more.

[0065] Y f13 may be -O-, -OC(=O)-O-, -OC(=O)-NR'-, -NR'-, -NR'-C(=O)-O-, -NR'-C(=O)-NR'-, -C(=O)-O-, -C(=O)-NR'-, or -SONR'- (R' is a hydrogen atom or a monovalent organic group).f13 is, for example, --O-- or --NR'--.

[0066] Z f is R f1 , or R f1 or R f2 As described above, R f1 It is.

[0067] In one embodiment, Y f22 is the formula -Y f221 -Y f222 - [In the formula, Y f221 is a direct bond or a hydrocarbon group having 2 to 40 carbon atoms, Y f222 is a direct bond or a phenylene group. It may be a group represented by the following formula: Here, Y f13 is -O- or -NR'- (R' is a hydrogen atom or a monovalent organic group), and β can be 0 or 1. Z f is R f1 It may be.

[0068] [Specific examples of monomer (f)] Specific examples of the monomer (f) include compounds obtained by reacting a compound having an ethylenically unsaturated polymerizable group (e.g., (meth)acrylic chloride, 2-((meth)acryloyloxy)ethyl isocyanate, (meth)acrylic acid glycidyl, allyl glycidyl ether, α-ethyl glycidyl acrylate, crotonyl glycidyl ether, (iso)crotonic acid glycidyl ether, (3,4-epoxycyclohexyl)methyl (meth)acrylate, (meth)acrylic acid chloride, (meth)acrylic chloride, (meth)acrylamide, (meth)acrylic acid, N,N-dimethylaminoethyl (meth)acrylate, 2-hydroxyethyl (meth)acrylate, allylamine, allyl alcohol, etc.) with the following reactive compounds: Acid halide G(O=)CY f -Z f α Acid anhydride O(C(=O)-Y f -Z f α )2 Carboxylic acid HO(O=)CY f -Z f α Isocyanate O=C=NY f -Z f α Thioisocyanate S=C=NY f -Z f α Epoxy (CH2OCH)CH2O-Y f -Z f α Halide GY f -Z f α Amine H2N-Y f -Z f α Hydroxy HO-Y f -Z f α [In the formula, Y f , Z f , α is as defined above, and G is a halogen atom (e.g., F, Cl, Br, or I). In addition, the above formula is Y f -Z f α The terminal functional group adjacent to (G(O=)C, etc.) is -Y f Although it is expressed as not included in -, part of the structure of the functional group of the terminal (e.g., (O=)C) is f It is also possible to re-express the statement as being incorporated into the

[0069] Examples of the reactive compound include: Trifluoromethoxyalkyl carboxylic acids, trifluoromethoxyalkyl carboxylic acid halides, Trifluoromethoxybenzoic acid, trifluoromethoxybenzoic acid halide, Trifluoromethoxyphenylacetic acid, Trifluoromethoxyphenylacetic acid halide, trifluoromethoxyalkylamines, trifluoromethoxyaniline, trifluoromethoxyalkyl alcohols, trifluoromethoxyphenol, Trifluoromethoxyalkyl isocyanate CF3-O-CF2-R 2 -OH CF3-OR 1 -O-CF2-R 2 -OH CF3-OR 1 -CF2-OR 2 -OH CF3-O-Ph-O-CF2-R 2 -OH CF3-O-Ph-CF2-OR 2 -OH R 3 -O-CF2-R 2 -OH R 3 -CF2-OR 2 -OH (Here, R1 to R3 are independently a hydrocarbon group having 1 to 40 carbon atoms.) Examples include:

[0070] More specific examples of the monomer (f) include (for example, in the formula given in the above specific examples) -Y f -Z f α but -Ali-OR f1 , -Ali-Cy-OR f1 , -Ali-Cy-Ali-OR f1 , -Cy-OR f1 , -Cy-Ali-OR f1 , -Cy-Ali-Cy-ORf1 , -Ali-N(R')-R f1 , -Ali-Cy-N(R')-R f1 , -Ali-Cy-Ali-N(R')-R f1 , -Cy-N(R')-R f1 , -Cy-Ali-N(R')-R f1 , -Cy-Ali-Cy-N(R')-R f1 , [In the formula, Ali is an aliphatic hydrocarbon group having 1 to 20 carbon atoms, Cy is a hydrocarbon aromatic ring or a heterocycle, and R' is a hydrogen atom or an organic group. f1 is -CF3, -CF2H, or -CFH2. It is a compound wherein

[0071] More specific examples of the monomer (f) include (for example, in the formula given in the above specific examples) -Y f -Z f α but -(CH2) n -OR f1 , -(CH2) n -Cy-OR f1 , -(CH2) n -Cy-(CH2) n -OR f1 , -Cy-OR f1 , -Cy-(CH2) n -OR f1 , -Cy-(CH2) n -Cy-OR f1 , -(CH2) n -N(R')-R f1 , -(CH2) n -Cy-N(R')-R f1 , -(CH2) n-Cy-(CH2)nN(R')-R f1 , -Cy-N(R')-R f1 , -Cy-(CH2) n -N(R')-R f1 , -Cy-(CH2) n -Cy-N(R')-R f1 , [In the formula, n is an integer of 1 to 40, Cy is a hydrocarbon aromatic ring or a heterocycle, R' is a hydrogen atom or an organic group, and R f1 is -CF3, -CF2H, or -CFH2. Certain compounds and the like can be mentioned.

[0072] [Example of a method for producing monomer (f)] The method for producing the monomer (f) is not limited, and any known method can be used.

[0073] Compounds containing hydroxyl groups and olefins (111): HO-R j33 A compound containing a trifluoromethoxy group may be synthesized using -CH=CH2 as a raw material. j33 is an alkylene group, for example, a C1-30 alkylene group.

[0074] Examples of the olefin group-containing compound include 3-hydroxypropene, 4-hydroxy-1-butene, 5-hydroxy-1-pentene, 6-hydroxy-1-hexene, 7-hydroxy-1-heptene, 8-hydroxy-1-octene, 9-hydroxy-1-nonene, 10-hydroxy-1-decene, 11-hydroxy-1-undecene, 12-hydroxy-1-dodecene, 13-hydroxy-1-tridecene, 14-hydroxy-1-tetradecene, 15-hydroxy-1-pentadecene, 16-hydroxy-1-hexadecene, 17-hydroxy-1-heptadecene, 18-hydroxy-1-octadecene, 19-hydroxy-1-nonadecene, 20-hydroxy-1-icosene, 21-hydroxy-1-henicosene, 24-hydroxy-1-tetracosene, and 30-hydroxy-1-triacontene.

[0075] The hydroxyl group of compound (111) is reacted with carbon disulfide in the presence of a base such as sodium hydride, and iodomethane is added to give the xanthate ester (112): HCS-C(=S)-OR. j33 -COOR j32 Here, R j32 is a lower alkyl group, for example, a methyl group, an ethyl group, a propyl group, a butyl group, or a tert-butyl group, specifically, a methyl group or a tert-butyl group. The above xanthate ester (102) is reacted with hydrogen fluoride pyridine and 1,3-dibromo-5,5-dimethylhydantoin to obtain the desired trifluoromethoxy group-containing compound (113): FCO-R j33 Obtain -CH=CH2.

[0076] Alternatively, the hydroxyl group of compound (111) can be reacted with arylsulfonic acid trifluoromethyl ester in the presence of cesium fluoride, tetrabutylammonium bromide, or the like in an aprotic polar solvent such as NMP, DMF, or HMPA (hexamethylphosphoric acid triamide) to give the desired trifluoromethoxy group-containing compound (113): FCO-R j33 -CH=CH2 can be obtained.

[0077] The obtained F3CO-R j33 -CH=CH2 can be used as monomer (f).

[0078] The obtained F3CO-R j33 -CH=CH2 is F3CO-R according to the standard method. j33It may be converted to CH2CH2-OH and reacted with a compound having an ethylenically unsaturated polymerizable group. For example, a (meth)acrylate monomer can be synthesized by reaction with (meth)acrylic acid. A (meth)acrylate monomer containing a urethane group can be synthesized by reaction with a (meth)acrylate containing an isocyanate group. A fluorine-containing acrylate may be obtained by reacting an alcohol with methyl acrylate in the presence of a basic catalyst (e.g., calcium hydroxide).

[0079] Here, F3CO-R j33 Another method for producing CH2CH2-OH is to react silver triflate, potassium fluoride, 1-(chloromethyl)-4-fluoro-4-diazoniabicyclo[2.2.2]octane, a salt of tetrafluoroborate, and benzyloxy alcohol (e.g., benzyloxyethanol), and reduce the resulting product (e.g., [2-(trifluoromethoxy)ethoxy]methyl]benzene) with hydrogen under a palladium catalyst, as described in WO2020 / 168011Al, etc. j33 CH2CH2-OH can further be reacted with (meth)acrylic acid to synthesize a (meth)acrylate monomer. By reacting with a (meth)acrylate containing an isocyanate group, a (meth)acrylate monomer containing a urethane group can be synthesized. A fluorine-containing acrylate can be obtained by reacting an alcohol with methyl acrylate in the presence of a basic catalyst (e.g., calcium hydroxide).

[0080] The obtained F3CO-R j33 -CH=CH2 is F3CO-R according to the standard method j33 By converting it to CH2C(=O)-OH, amidating it with aminoethanol, and then reacting it with (meth)acrylic acid, a (meth)acrylate monomer containing an amide group can be synthesized.

[0081] (a) Hydrocarbon Group-Containing Monomer The fluorine-containing polymer may have a repeating unit derived from a monomer (a) having a hydrocarbon group having 6 or more and 40 or less carbon atoms.

[0082] The hydrocarbon group of the monomer (a) may be an aromatic hydrocarbon group or an aliphatic hydrocarbon group, and is preferably an aliphatic hydrocarbon group, particularly a saturated aliphatic hydrocarbon group (alkyl group). The hydrocarbon group is branched or linear, and more preferably linear. The hydrocarbon group may be saturated or unsaturated. The hydrocarbon group is preferably a saturated aliphatic hydrocarbon group (alkyl group). The number of carbon atoms in the hydrocarbon group may be 6 or more, 8 or more, 10 or more, 12 or more, 14 or more, 16 or more, 18 or more, 20 or more, or 22 or more, preferably 10 or more, 12 or more, 14 or more, or 16 or more, and may be 40 or less, 35 or less, 30 or less, 25 or less, 20 or less, 15 or less, or 10 or less, and preferably 30 or less, 25 or less, or 20 or less.

[0083] The monomer (a) may contain an amide group, a urea group, or a urethane group. The hydrocarbon monomer may be a combination of a hydrocarbon monomer having an amide group, a urea group, or a urethane group and a hydrocarbon monomer not having an amide group, a urea group, or a urethane group. By including such a group in the monomer (a), the effect of the present disclosure can be well achieved.

[0084] The monomer (a) having a hydrocarbon group having 6 to 40 carbon atoms is formula: CH2=C(-X a )-C(=O)-Y a (R a ) k [In the formula, R a are each independently a hydrocarbon group having 6 to 40 carbon atoms, X a is a hydrogen atom, a monovalent organic group, or a halogen atom, Y ais a group (excluding hydrocarbon groups) composed of at least one selected from divalent to tetravalent hydrocarbon groups having one carbon atom (particularly, -CH2-, -CH=), -CH4-, -O-, -C(=O)-, -S(=O)2- and -NH-; k is 1 to 3. It is preferable that the monomer is represented by the following formula:

[0085] X a X may be a hydrogen atom, a methyl group, a halogen atom other than a fluorine atom, a substituted or unsubstituted benzyl group, or a substituted or unsubstituted phenyl group. a Examples of X are a hydrogen atom, a methyl group, a chlorine atom, a bromine atom, an iodine atom, and a cyano group. a is preferably a hydrogen atom, a methyl group, or a chlorine atom. a is particularly preferably a hydrogen atom.

[0086] Y a is a divalent to tetravalent group. Y a is preferably a divalent group. Y a is preferably a group (excluding hydrocarbon groups) composed of at least one selected from a hydrocarbon group having one carbon atom, -CH-, -O-, -C(=O)-, -S(=O)2-, and -NH-. Examples of the hydrocarbon group having one carbon atom include -CH2-, -CH= having a branched structure, and -C≡ having a branched structure.

[0087] Y a -Y'-, -Y'-Y'-, -Y'-C(=O)-, -C(=O)-Y'-, -Y'-C(=O)-Y'-, -Y'-R'-, -Y'-R'-Y'- , -Y'-R'-Y'-C(=O)-, -Y'-R'-C(=O)-Y'-, -Y'-R'-Y'-C(=O)-Y'-, or -Y'-R'-Y'-R'- [In the formula, Y' is a direct bond, -O-, -NH- or -S(=O)2-; R' is -(CH2) m - (wherein m is an integer of 1 to 5) or -C6H4- (phenylene group). It may be.

[0088] Y a Specific examples of are -O-, -NH-, -O-C(=O)-, -C(=O)-NH-, -NH-C(=O)-, -O-C(=O)-NH-, -NH-C(=O)-O-, -NH-C(=O)-NH-, -O-C6H4-, -O-(CH2) m -O-, -NH-(CH2) m -NH-, -O-(CH2) m -NH-, -NH-(CH2) m -O-, -O-(CH2) m -O-C(=O)-, -O-(CH2) m -C(=O)-O-, -NH-(CH2) m -O-C(=O)-, -NH-(CH2) m -C(=O)-O-, -O-(CH2) m -O-C(=O)-NH-, -O-(CH2) m -NH-C(=O)-O-, -O-(CH2) m -C(=O)-NH-, -O-(CH2) m -NH-C(=O)-, -O-(CH2) m -NH-C(=O)-NH-, -O-(CH2) m -O-C6H4-, -O-(CH2) m -NH-S(=O)2-, -O-(CH2) m -S(=O)2-NH-, -NH-(CH2) m -O-C(=O)-NH-, -NH-(CH2) m -NH-C(=O)-O-, -NH-(CH2) m -C(=O)-NH-, -NH-(CH2) m -NH-C(=O)-, -NH-(CH2) m -NH-C(=O)-NH-, -NH-(CH2) m -O-C6H4-, -NH-(CH2) m -NH-C6H4-, -NH-(CH2) m -NH-S(=O)2-, or -NH-(CH2) m -S(=O)2-NH- [wherein, m is 1 to 5, particularly 2 or 4].

[0089] Y a -O-, -NH-, -O-(CH2) m -OC(=O)-, -O-(CH2) m -NH-C(=O)-, -O-(CH2) m -OC(=O)-NH-, -O-(CH2) m -NH-C(=O)-O-, -O-(CH2) m -NH-C(=O)-NH-, -O-(CH2) m -NH-S(=O)2-, -O-(CH2) m -S(=O)2-NH-, -NH-(CH2) m -NH-S(=O)2- or -NH-(CH2) m -S(=O)2-NH- [In the formula, m is an integer of 1 to 5, particularly 2 or 4.] It is preferable that Y a is -O- or -O-(CH2) m -NH-C(=O)-, especially -O-(CH2) m It is more preferably -NH-C(=O)-.

[0090] R a is preferably a linear or branched hydrocarbon group. The hydrocarbon group may particularly be a linear hydrocarbon group. The hydrocarbon group is preferably an aliphatic hydrocarbon group, particularly a saturated aliphatic hydrocarbon group, especially an alkyl group. The number of carbon atoms in the hydrocarbon group is preferably 12 to 30, for example 16 to 26 or 15 to 26, particularly 18 to 22 or 17 to 22.

[0091] Examples of monomer (a) are: Formula (a1): CH2=C(-X a1 )-C(=O)-Y a1 -R a1 [In the formula, R a1 is a hydrocarbon group having 6 to 40 carbon atoms, X a1 is a hydrogen atom, a monovalent organic group, or a halogen atom, Y a1is -O- or -NH-.] A monomer represented by the formula: Formula (a2): CH2=C(-X a2 )-C(=O)-Y a21 -Z(-Y a22 -R a2 ) n [In the formula, R a2 are each independently a hydrocarbon group having 6 to 40 carbon atoms, X a2 is a hydrogen atom, a monovalent organic group, or a halogen atom, Y a21 is -O- or -NH-, Y a22 each independently represents a direct bond or a group consisting of at least one selected from -O-, -C(=O)-, -S(=O)2-, -NH-, and -CH2-; Z is a direct bond or a divalent or trivalent hydrocarbon group having 1 to 5 carbon atoms; n is 1 or 2. It is a monomer represented by the formula:

[0092] ((a1) Monomer) The monomer (a1) has the formula: CH2=C(-X a1 )-C(=O)-Y a1 -R a1 [In the formula, R a1 is a hydrocarbon group having 6 to 40 carbon atoms, X a1 is a hydrogen atom, a monovalent organic group, or a halogen atom, Y a1 is -O- or -NH-.] It is a compound represented by the formula:

[0093] The monomer (a1) is Y a1 a long chain acrylate ester monomer in which Y is -O-; a1 is a long chain acrylamide monomer in which is -NH-. R a1R is preferably an aliphatic hydrocarbon group, particularly a saturated aliphatic hydrocarbon group, and especially an alkyl group. a1 In the above formula, the hydrocarbon group preferably has 12 to 30 carbon atoms, for example, 16 to 26 carbon atoms, and particularly preferably 18 to 22 carbon atoms. X a1 may be a hydrogen atom, a methyl group, a halogen atom other than a fluorine atom, a substituted or unsubstituted benzyl group, or a substituted or unsubstituted phenyl group, and is preferably a hydrogen atom, a methyl group, or a chlorine atom.

[0094] Preferred specific examples of long chain acrylate ester monomers are lauryl (meth)acrylate, stearyl (meth)acrylate, icosyl (meth)acrylate, behenyl (meth)acrylate, stearyl alpha chloroacrylate, icosyl alpha chloroacrylate, and behenyl alpha chloroacrylate. Specific preferred examples of the long-chain acrylamide monomer are stearyl (meth)acrylamide, icosyl (meth)acrylamide, and behenyl (meth)acrylamide.

[0095] ((a2) Monomer) The monomer (a2) is a monomer different from the monomer (a1). The monomer (a2) is a (meth)acrylate or (meth)acrylamide having at least one group selected from -O-, -C(=O)-, -S(=O)2-, -NH-, or -CH2-. The monomer (a2) has the formula: CH2=C(-X a2 )-C(=O)-Y a21 -Z(-Y a22 -R a2 ) n [In the formula, R a2 are each independently a hydrocarbon group having 6 to 40 carbon atoms, X a2 is a hydrogen atom, a monovalent organic group, or a halogen atom, Y a21 is -O- or -NH-, Y a22each independently represents a direct bond or a group consisting of at least one selected from -O-, -C(=O)-, -S(=O)2-, -NH-, and -CH2-; Z is a direct bond or a divalent or trivalent hydrocarbon group having 1 to 5 carbon atoms; n is 1 or 2. The compound may be represented by the formula: Y a22 And / or Z may not be a direct bond. a22 and Z may not simultaneously be a direct bond.

[0096] R a2 R is preferably an aliphatic hydrocarbon group, particularly a saturated aliphatic hydrocarbon group, and especially an alkyl group. a2 In the above formula, the hydrocarbon group preferably has 12 to 30 carbon atoms, for example, 16 to 26 or 15 to 26, and particularly preferably 18 to 22 or 17 to 22 carbon atoms.

[0097] X a2 may be a hydrogen atom, a methyl group, a halogen atom other than a fluorine atom, a substituted or unsubstituted benzyl group, or a substituted or unsubstituted phenyl group, and is preferably a hydrogen atom, a methyl group, or a chlorine atom.

[0098] Y a22 -Y'-, -Y'-Y'-, -Y'-C(=O)-, -C(=O)-Y'-, -Y'-C(=O)-Y'-, -Y'-R'-, -Y'-R'-Y'- , -Y'-R'-Y'-C(=O)-, -Y'-R'-C(=O)-Y'-, -Y'-R'-Y'-C(=O)-Y'-, or -Y'-R'-Y'-R'- [In the formula, each Y' is independently a direct bond, -O-, -NH-, or -S(=O)2-, R' is -(CH2) m -(m is an integer of 1 to 5), a linear hydrocarbon group having an unsaturated bond of 1 to 5 carbon atoms, a hydrocarbon group having a branched structure of 1 to 5 carbon atoms, or -(CH2) l -C6H4-(CH2) l - (each 1 is independently an integer of 0 to 5, and -C6H4- is a phenylene group). may be

[0099] Y a22 Specific examples of are direct bonding, -O-, -NH-, -O-C(=O)-, -C(=O)-O-, -C(=O)-NH-, -NH-C(=O)-, -NH-S(=O)2-, -S(=O)2-NH-, -O-C(=O)-NH-, -NH-C(=O)-O-, -NH-C(=O)-NH-, -O-C6H4-, -NH-C6H4-, -O-(CH2) m -O-, -NH-(CH2) m -NH-, -O-(CH2) m -NH-, -NH-(CH2) m -O-, -O-(CH2) m -O-C(=O)-, -O-(CH2) m -C(=O)-O-, -NH-(CH2) m -O-C(=O)-, -NH-(CH2) m -C(=O)-O-, -O-(CH2) m -O-C(=O)-NH-, -O-(CH2) m -NH-C(=O)-O-, -O-(CH2) m -C(=O)-NH-, -O-(CH2) m -NH-C(=O)-, -O-(CH2) m -NH-C(=O)-NH-, -O-(CH2) m -O-C6H4-, -NH-(CH2) m -O-C(=O)-NH-, -NH-(CH2) m -NH-C(=O)-O-, -NH-(CH2) m -C(=O)-NH-, -NH-(CH2) m -NH-C(=O)-, -NH-(CH2) m -NH-C(=O)-NH-, -NH-(CH2) m -O-C6H4-, -NH-(CH2) m -NH-C6H4- [In the formula, m is an integer from 1 to 5.] is

[0100] Y a22is preferably -O-, -NH-, -OC(=O)-, -C(=O)-O-, -C(=O)-NH-, -NH-C(=O)-, -NH-S(=O)2-, -S(=O)2-NH-, -OC(=O)-NH-, -NH-C(=O)-O-, -NH-C(=O)-NH-, -O-C6H4-. Y a22 It is more preferable that Y is -NH-C(=O)-, -C(=O)-NH-, -OC(=O)-NH-, -NH-C(=O)-O- or -NH-C(=O)-NH-. a22 does not have to be a direct bond.

[0101] Z is a direct bond or a divalent or trivalent hydrocarbon group having 1 to 5 carbon atoms, and may have a straight-chain structure or a branched structure. The carbon number of Z is preferably 2 to 4, particularly 2. Specific examples of Z are a direct bond, -CH2-, -CH2CH2-, -CH2CH2CH2-, -CH2CH2CH2CH2-, -CH2CH2CH2CH2CH2-, -CH2CH= having a branched structure, -CH2(CH-)CH2- having a branched structure, -CH2CH2CH= having a branched structure, -CH2CH2CH2CH2CH= having a branched structure, -CH2CH2(CH-)CH2- having a branched structure, and -CH2CH2CH2CH= having a branched structure. Z does not have to be a direct bond.

[0102] Monomer (a2) is CH2=C(-X a2 )-C(=O)-O-(CH2) m -NH-C(=O)-R a2 , CH2=C(-X a2 )-C(=O)-O-(CH2) m -OC(=O)-NH-R a2 , CH2=C(-X a2 )-C(=O)-O-(CH2) m -NH-C(=O)-OR a2 , CH2=C(-X a2 )-C(=O)-O-(CH2) m -NH-C(=O)-NH-R a2 [wherein R a2 and Xa2 has the same meaning as above.] Monomer (a2) is CH2=C(-X a2 )-C(=O)-O-(CH2) m -NH-C(=O)-R a2 It is particularly preferred that:

[0103] Monomer (a2) can be produced by reacting a hydroxyalkyl (meth)acrylate or a hydroxyalkyl (meth)acrylamide with a long-chain alkyl isocyanate, such as lauryl isocyanate, myristyl isocyanate, cetyl isocyanate, stearyl isocyanate, oleyl isocyanate, or behenyl isocyanate. Alternatively, the monomer (a2) can be produced by reacting a (meth)acrylate having an isocyanate group in the side chain, such as 2-methacryloyloxyethyl methacrylate, with a long-chain alkylamine or a long-chain alkyl alcohol. Examples of long-chain alkylamines include laurylamine, myristylamine, cetylamine, stearylamine, oleylamine, and behenylamine. Examples of long-chain alkyl alcohols include lauryl alcohol, myristyl alcohol, cetyl alcohol, stearyl alcohol, oleyl alcohol, and behenyl alcohol.

[0104] Preferred examples of the monomer (a) are as follows: Stearyl (meth)acrylate, behenyl (meth)acrylate, stearyl alpha chloroacrylate, behenyl alpha chloroacrylate; Stearyl (meth)acrylamide, behenyl (meth)acrylamide;

[0105] TIFF0007633577000001.tif2453

[0106] TIFF0007633577000002.tif2253 TIFF0007633577000003.tif2152 TIFF0007633577000004.tif2155

[0107] TIFF0007633577000005.tif2357 TIFF0007633577000006.tif2256 TIFF0007633577000007.tif2156

[0108] TIFF0007633577000008.tif2051 TIFF0007633577000009.tif2054 TIFF0007633577000010.tif2352 TIFF0007633577000011.tif2659

[0109] TIFF0007633577000012.tif2046

[0110] TIFF0007633577000013.tif2249 [In the above formula, n is a number from 6 to 40, and m is a number from 1 to 5.] The compound of the above formula is an acryl compound in which the α-position is a hydrogen atom, but specific examples may be methacryl compounds in which the α-position is a methyl group and α-chloroacryl compounds in which the α-position is a chlorine atom.

[0111] The monomer (a2) has the formula: R a22 -C(=O)-NH-R a23 -OR a21 [In the formula, R a21 represents an organic residue having an ethylenically unsaturated polymerizable group, R a22 is a hydrocarbon group having 6 to 40 carbon atoms, R a23 is a hydrocarbon group having 1 to 5 carbon atoms.] It is preferable that the monomer is an amide group-containing monomer represented by the following formula:

[0112] R a21 is an organic residue having an ethylenically unsaturated polymerizable group, and is not particularly limited as long as it has a carbon-carbon double bond. a211 =CH2, -CHR a211 =CH2, -CH2CHR a211 Examples of the organic residue include an ethylenically unsaturated polymerizable group such as ═CH2. a211 is a hydrogen atom or an alkyl group having 1 to 4 carbon atoms. a21 R may have various organic groups other than the ethylenically unsaturated polymerizable group, such as organic groups of chain hydrocarbons, cyclic hydrocarbons, polyoxyalkylene groups, polysiloxane groups, etc., and these organic groups may be substituted with various substituents. a21 is -C(=O)CR a211 It is preferred that =CH2.

[0113] R a22 R is a hydrocarbon group having 6 to 40 carbon atoms, preferably an alkyl group, and examples thereof include chain hydrocarbon groups and cyclic hydrocarbon groups. Among these, a chain hydrocarbon group is preferred, and a linear saturated hydrocarbon group is particularly preferred. a22 The number of carbon atoms is 6 or more and 40 or less, preferably 11 to 27, and particularly preferably 15 to 23.

[0114] R a23 R is a hydrocarbon group having 1 to 5 carbon atoms, preferably an alkyl group. The hydrocarbon group having 1 to 5 carbon atoms may be either linear or branched and may have an unsaturated bond, but is preferably linear. a23 The number of carbon atoms in R is preferably 2 to 4, and more preferably 2. a23 is preferably an alkylene group.

[0115] The amide group-containing monomer is R a22 There is only one type (e.g., R a22 (Only compounds with 17 carbon atoms) or R a22is a combination of multiple a22 A compound having 17 carbon atoms, R a22 and a compound having 15 carbon atoms.

[0116] An example of an amide group-containing monomer is a carboxylic acid amide alkyl (meth)acrylate. Specific examples of the amide group-containing monomer include palmitic acid amidoethyl (meth)acrylate, stearic acid amidoethyl (meth)acrylate, behenic acid amidoethyl (meth)acrylate, myristic acid amidoethyl (meth)acrylate, lauric acid amidoethyl (meth)acrylate, isostearic acid ethyl amido (meth)acrylate, oleic acid ethyl amido (meth)acrylate, tertiary butyl cyclohexyl caproic acid amidoethyl (meth)acrylate, adamantane carboxylic acid ethyl amido (meth)acrylate, naphthalene carboxylic acid amidoethyl (meth)acrylate, anthracene carboxylic acid amidoethyl (meth)acrylate, palmitic acid amidopropyl (meth)acrylate, stearic acid amidopropyl (meth)acrylate, palmitic acid amidoethyl vinyl ether, stearic acid amidoethyl vinyl ether, palmitic acid amidoethyl allyl ether, stearic acid amidoethyl allyl ether, or mixtures thereof.

[0117] The amide group-containing monomer is preferably stearamidoethyl (meth)acrylate. The amide group-containing monomer may be a mixture containing stearamidoethyl (meth)acrylate. In the mixture containing stearamidoethyl (meth)acrylate, the amount of stearamidoethyl (meth)acrylate may be, for example, 40% by weight or more, 50% by weight or more, 60% by weight or more, or 70% by weight or more, and may be 90% by weight or less, 80% by weight or less, or 70% by weight or less, based on the weight of the entire amide group-containing monomer. The remaining monomer may be, for example, palmitamidoethyl (meth)acrylate.

[0118] In the monomer (a), the amount of monomer (a2) may be 10% by weight or more, 20% by weight or more, 30% by weight or more, 40% by weight or more, 50% by weight or more, 60% by weight or more, 70% by weight or more, or 80% by weight or more, and is preferably 30% by weight or more.

[0119] [(b) Hydrophilic group-containing monomer] The fluorine-containing polymer may contain a hydrophilic group-containing monomer (b). The monomer (b) is a monomer other than the monomer (a) and has a hydrophilic group. The hydrophilic group is preferably an oxyalkylene group (the alkylene group has 2 to 6 carbon atoms), particularly preferably an oxyethylene group. In particular, the monomer (b) is preferably an oxyalkylene (meth)acrylate, for example, polyalkylene (or monoalkylene) glycol mono(meth)acrylate and / or polyalkylene (or monoalkylene) glycol di(meth)acrylate, polyalkylene (or monoalkylene) glycol mono(meth)acrylamide.

[0120] The monomer (b) is formula: CH2=CX b C(=O)-Y b -(R b O) n -A b [In the formula, X b is a hydrogen atom or a methyl group, Y b is -O- or -NH-, R b are each independently an alkylene group having 2 to 6 carbon atoms, A b is a hydrogen atom, an unsaturated or saturated hydrocarbon group having 1 to 22 carbon atoms, or CH2=CX b C(=O)-Yes, n is an integer from 1 to 90. It is preferable that the oxyalkylene (meth)acrylate is represented by the following formula:

[0121] An example of the monomer (b) is a monomer having the formula: CH2=CX b C(=O)-O-(R b O) n -A bi (b1) and CH2=CX b C(=O)-O-(R b O) n -C(=O)CX b =CH2(b2), CH2=CX b C(=O)-NH-(R b O) n -A bi (b3) [In the formula, X b are each independently a hydrogen atom or a methyl group, A bi each independently represents a hydrogen atom or an unsaturated or saturated hydrocarbon group having 1 to 22 carbon atoms, R b are each independently an alkylene group having 2 to 6 carbon atoms, n is an integer between 1 and 90 It is.] It is preferable that the formula is represented by the following formula:

[0122] n may be, for example, 1 to 50, particularly 1 to 30, and especially 1 to 15 or 2 to 15. Alternatively, n may be, for example, 1. R b may be a linear or branched alkylene group, for example of the formula -(CH2) x -or-(CH2) x1 -(CH(CH3)) x2 -[In the formula, x1 and x2 are 0 to 6, for example, 2 to 5, and the sum of x1 and x2 is 1 to 6. -(CH2) x1 - and - (CH(CH3)) x2 The order of - is not limited to the depicted formula and may be random. -(R b O) n In -, R may be two or more types (for example, two to four types, particularly two types), and -(R b O) n- is, for example, -(R 1 O) n1 -and-(R 2 O) n2 -[wherein, R 1 and R 2 are different from each other and are alkylene groups having 2 to 6 carbon atoms, n1 and n2 are numbers of 1 or more, and the sum of n1 and n2 is 2 to 90.

[0123] R in formulas (b1), (b2) and (b3) b In particular, R is preferably an ethylene group, a propylene group or a butylene group, and more preferably a butylene group. b R may be a combination of two or more alkylene groups. In that case, it is preferable that at least one of R is an ethylene group, a propylene group, or a butylene group. b Examples of the combination include an ethylene group / propylene group combination, an ethylene group / butylene group combination, and a propylene group / butylene group combination. The monomer (b) may be a mixture of two or more kinds. In that case, at least one of the monomers (b) is a mixture of R b is preferably an ethylene group, a propylene group, or a butylene group. In addition, when using a polyalkylene glycol di(meth)acrylate represented by formula (b2), it is not preferable to use it alone as the monomer (b), but it is preferable to use it in combination with the monomer (b1). In that case, it is also preferable to keep the compound represented by formula (b2) to less than 30% by weight of the monomer (b) used.

[0124] Specific examples of the monomer (b) include, but are not limited to, the following: CH2=CHCOO-CH2CH2O-H CH2=CHCOO-CH2CH2CH2O-H CH2=CHCOO-CH2CH(CH3)OH CH2=CHCOO-CH(CH3)CH2O-H CH2=CHCOO-CH2CH2CH2CH2O-H <h2 style=";text-align:left;direction:ltr">CH2=CHCOO-CH2CH2CH(CH3)OH<h2 style=";text-align:left;direction:ltr"> <h2 style=";text-align:left;direction:ltr"> CH2=CHCOO-CH2CH(CH3)CH2O-H<h2 style=";text-align:left;direction:ltr"> <h2 style=";text-align:left;direction:ltr"> CH2=CHCOO-CH(CH3)CH2CH2O-H<h2 style=";text-align:left;direction:ltr"> <h2 style=";text-align:left;direction:ltr"> CH2=CHCOO-CH2CH(CH2CH3)OH<h2 style=";text-align:left;direction:ltr"> <h2 style=";text-align:left;direction:ltr"> CH2=CHCOO-CH2C(CH3)2O-H<h2 style=";text-align:left;direction:ltr"> <h2 style=";text-align:left;direction:ltr"> CH2=CHCOO-CH(CH2CH3)CH2O-H<h2 style=";text-align:left;direction:ltr"> <h2 style=";text-align:left;direction:ltr"> CH2=CHCOO-C(CH3)2CH2O-H<h2 style=";text-align:left;direction:ltr"> <h2 style=";text-align:left;direction:ltr"> CH2=CHCOO-CH(CH3)CH(CH3)OH<h2 style=";text-align:left;direction:ltr"> <h2 style=";text-align:left;direction:ltr"> CH2=CHCOO-C(CH3)(CH2CH3)OH<h2 style=";text-align:left;direction:ltr"> <h2 style=";text-align:left;direction:ltr"> CH2=CHCOO-(CH2CH2O)2-H<h2 style=";text-align:left;direction:ltr"> <h2 style=";text-align:left;direction:ltr"> CH2=CHCOO-(CH2CH2O)4-H<h2 style=";text-align:left;direction:ltr"> <h2 style=";text-align:left;direction:ltr"> CH2=CHCOO-(CH2CH2O)5-H<h2 style=";text-align:left;direction:ltr"> <h2 style=";text-align:left;direction:ltr"> CH2=CHCOO-(CH2CH2O)6-H<h2 style=";text-align:left;direction:ltr"> <h2 style=";text-align:left;direction:ltr"> CH2=CHCOO-(CH2CH2O)5-CH3<h2 style=";text-align:left;direction:ltr"> <h2 style=";text-align:left;direction:ltr"> CH2=CHCOO-(CH2CH2O)9-CH3<h2 style=";text-align:left;direction:ltr"> <h2 style=";text-align:left;direction:ltr"> CH2=CHCOO-(CH2CH2O)<h2 style=";text-align:left;direction:ltr"> 23 <h2 style=";text-align:left;direction:ltr"> -CH3<h2 style=";text-align:left;direction:ltr"> <h2 style=";text-align:left;direction:ltr"> CH2=CHCOO-(CH2CH2O)<h2 style=";text-align:left;direction:ltr"> 90 <h2 style=";text-align:left;direction:ltr"> -CH3<h2 style=";text-align:left;direction:ltr"> <h2 style=";text-align:left;direction:ltr">

[0125] <h2 style=";text-align:left;direction:ltr"> <h2 style=";text-align:left;direction:ltr"> CH2=CHCOO-(CH2CH(CH3)O)9-H<h2 style=";text-align:left;direction:ltr"> <h2 style=";text-align:left;direction:ltr"> CH2=CHCOO-(CH2CH(CH3)O)9-CH3<h2 style=";text-align:left;direction:ltr"> <h2 style=";text-align:left;direction:ltr"> CH2=CHCOO-(CH2CH(CH3)O)<h2 style=";text-align:left;direction:ltr"> 12 <h2 style=";text-align:left;direction:ltr"> -CH3<h2 style=";text-align:left;direction:ltr"> <h2 style=";text-align:left;direction:ltr"> CH2=CHCOO-(CH2CH2O)5-(CH2CH(CH3)O)2-H<h2 style=";text-align:left;direction:ltr"> <h2 style=";text-align:left;direction:ltr"> CH2=CHCOO-(CH2CH2O)5-(CH2CH(CH3)O)3-CH3<h2 style=";text-align:left;direction:ltr"> <h2 style=";text-align:left;direction:ltr"> CH2=CHCOO-(CH2CH2O)8-(CH2CH(CH3)O)6-CH2CH(C2H5)C4H9<h2 style=";text-align:left;direction:ltr"> CH2=CHCOO-(CH2CH2O) 23 -OOC(CH3)C=CH2 CH2=CHCOO-(CH2CH2O) 20 -(CH2CH(CH3)O)5-CH2-CH=CH2

[0126] CH2=CHCOO-(CH2CH2O)9-H CH2=C(CH3)COO-CH2CH2O-H CH2=C(CH3)COO-CH2CH2CH2O-H CH2=C(CH3)COO-CH2CH(CH3)O-H CH2=C(CH3)COO-CH(CH3)CH2O-H CH2=C(CH3)COO-CH2CH2CH2CH2O-H CH2=C(CH3)COO-CH2CH2CH(CH3)O-H CH2=C(CH3)COO-CH2CH(CH3)CH2O-H CH2=C(CH3)COO-CH(CH3)CH2CH2O-H CH2=C(CH3)COO-CH2CH(CH2CH3)O-H CH2=C(CH3)COO-CH2C(CH3)2O-H CH2=C(CH3)COO-CH(CH2CH3)CH2O-H CH2=C(CH3)COO-C(CH3)2CH2O-H CH2=C(CH3)COO-CH(CH3)CH(CH3)O-H CH2=C(CH3)COO-C(CH3)(CH2CH3)O-H CH2=C(CH3)COO-(CH2CH2O)2-H CH2=C(CH3)COO-(CH2CH2O)4-H CH2=C(CH3)COO-(CH2CH2O)5-H CH2=C(CH3)COO-(CH2CH2O)6-H CH2=C(CH3)COO-(CH2CH2O)9-H CH2=C(CH3)COO-(CH2CH2O)5-CH3 CH2=C(CH3)COO-(CH2CH2O)9-CH3 CH2=C(CH3)COO-(CH2CH2O) 23 -CH3 CH2=C(CH3)COO-(CH2CH2O) 90 -CH3 CH2=C(CH3)COO-(CH2CH(CH3)O)9-H

[0127] CH2=C(CH3)COO-(CH2CH(CH3)O)9-CH3 CH2=C(CH3)COO-(CH2CH(CH3)O) 12 -CH3 CH2=C(CH3)COO-(CH2CH2O)5-(CH2CH(CH3)O)2-H CH2=C(CH3)COO-(CH2CH2O)5-(CH2CH(CH3)O)3-CH3 CH2=C(CH3)COO-(CH2CH2O)8-(CH2CH(CH3)O)6-CH2CH(C2H5)C4H9 CH2=C(CH3)COO-(CH2CH2O) 23 -OOC(CH3)C=CH2 CH2=C(CH3)COO-(CH2CH2O) 20 -(CH2CH(CH3)O)5-CH2-CH=CH2

[0128] CH2=CH-C(=O)-NH-CH2CH2O-H CH2=CH-C(=O)-NH-CH2CH2CH2O-H CH2=CH-C(=O)-NH-CH2CH(CH3)O-H CH2=CH-C(=O)-NH-CH(CH3)CH2O-H CH2=CH-C(=O)-NH-CH2CH2CH2CH2O-H CH2=CH-C(=O)-NH-CH2CH2CH(CH3)O-H CH2=CH-C(=O)-NH-CH2CH(CH3)CH2O-H CH2=CH-C(=O)-NH-CH(CH3)CH2CH2O-H CH2=CH-C(=O)-NH-CH2CH(CH2CH3)OH CH2=CH-C(=O)-NH-CH2C(CH3)2O-H CH2=CH-C(=O)-NH-CH(CH2CH3)CH2O-H CH2=CH-C(=O)-NH-C(CH3)2CH2O-H CH2=CH-C(=O)-NH-CH(CH3)CH(CH3)OH CH2=CH-C(=O)-NH-C(CH3)(CH2CH3)OH CH2=CH-C(=O)-NH-(CH2CH2O)2-H CH2=CH-C(=O)-NH-(CH2CH2O)4-H CH2=CH-C(=O)-NH-(CH2CH2O)5-H CH2=CH-C(=O)-NH-(CH2CH2O)6-H CH2=CH-C(=O)-NH-(CH2CH2O)9-H CH2=CH-C(=O)-NH-(CH2CH2O)5-CH3 CH2=CH-C(=O)-NH-(CH2CH2O)9-CH3 CH2=CH-C(=O)-NH-(CH2CH2O) 23 -CH3 CH2=CH-C(=O)-NH-(CH2CH2O) 90 -CH3

[0129] CH2=CH-C(=O)-NH-(CH2CH(CH3)O)9-H CH2=CH-C(=O)-NH-(CH2CH(CH3)O)9-CH3 CH2=CH-C(=O)-NH-(CH2CH(CH3)O) 12 -CH3 CH2=CH-C(=O)-NH-(CH2CH2O)5-(CH2CH(CH3)O)2-H CH2=CH-C(=O)-NH-(CH2CH2O)5-(CH2CH(CH3)O)3-CH3 CH2=CH-C(=O)-NH-(CH2CH2O)8-(CH2CH(CH3)O)6-CH2CH(C2H5)C4H9

[0130] CH2=C(CH3)-C(=O)-NH-CH2CH2O-H CH2=C(CH3)-C(=O)-NH-CH2CH2CH2O-H CH2=C(CH3)-C(=O)-NH-CH2CH(CH3)OH CH2=C(CH3)-C(=O)-NH-CH(CH3)CH2O-H CH2=C(CH3)-C(=O)-NH-CH2CH2CH2CH2O-H CH2=C(CH3)-C(=O)-NH-CH2CH2CH(CH3)OH CH2=C(CH3)-C(=O)-NH-CH2CH(CH3)CH2O-H CH2=C(CH3)-C(=O)-NH-CH(CH3)CH2CH2O-H CH2=C(CH3)-C(=O)-NH-CH2CH(CH2CH3)OH CH2=C(CH3)-C(=O)-NH-CH2C(CH3)2O-H CH2=C(CH3)-C(=O)-NH-CH(CH2CH3)CH2O-H CH2=C(CH3)-C(=O)-NH-C(CH3)2CH2O-H CH2=C(CH3)-C(=O)-NH-CH(CH3)CH(CH3)OH CH2=C(CH3)-C(=O)-NH-C(CH3)(CH2CH3)OH CH2=C(CH3)-C(=O)-NH-(CH2CH2O)2-H CH2=C(CH3)-C(=O)-NH-(CH2CH2O)4-H CH2=C(CH3)-C(=O)-NH-(CH2CH2O)5-H CH2=C(CH3)-C(=O)-NH-(CH2CH2O)6-H CH2=C(CH3)-C(=O)-NH-(CH2CH2O)9-H CH2=C(CH3)-C(=O)-NH-(CH2CH2O)5-CH3 CH2=C(CH3)-C(=O)-NH-(CH2CH2O)9-CH3 CH2=C(CH3)-C(=O)-NH-(CH2CH2O) 23 -CH3 CH2=C(CH3)-C(=O)-NH-(CH2CH2O) 90 -CH3

[0131] CH2=C(CH3)-C(=O)-NH-(CH2CH(CH3)O)9-H CH2=C(CH3)-C(=O)-NH-(CH2CH(CH3)O)9-CH3 CH2=C(CH3)-C(=O)-NH-(CH2CH(CH3)O) 12 -CH3 CH2=C(CH3)-C(=O)-NH-(CH2CH2O)5-(CH2CH(CH3)O)2-H CH2=C(CH3)-C(=O)-NH-(CH2CH2O)5-(CH2CH(CH3)O)3-CH3 CH2=C(CH3)-C(=O)-NH-(CH2CH2O)8-(CH2CH(CH3)O)6-CH2CH(C2H5)C4H9

[0132] As the monomer (b), X 2 is a hydrogen atom. The monomer (b) is particularly preferably hydroxyethyl acrylate, hydroxypropyl acrylate, hydroxybutyl acrylate, or hydroxyethyl acrylamide.

[0133] [(c) Ionic Group-Containing Monomer] The fluorine-containing polymer may contain an ionic group-containing monomer (c). The monomer (c) is a monomer other than the monomer (a) and the monomer (b). The monomer (c) is preferably a monomer containing an olefinic carbon-carbon double bond and an ionic group (particularly, an acrylic monomer). The ionic group is an anionic group and / or a cationic group.

[0134] Examples of the monomer having an anionic group include a monomer having a carboxyl group, a sulfonic acid group, or a phosphoric acid group.Specific examples of the monomer having an anionic group include (meth)acrylic acid, crotonic acid, maleic acid, fumaric acid, itaconic acid, citraconic acid, vinylsulfonic acid, (meth)allylsulfonic acid, styrenesulfonic acid, (meth)acrylate phosphate, vinylbenzenesulfonic acid, acrylamido tertiary butylsulfonic acid, and the like, or salts thereof.

[0135] Salts of anionic groups include alkali metal salts, alkaline earth metal salts, or ammonium salts, such as methylammonium salts, ethanolammonium salts, and triethanolammonium salts.

[0136] In the monomer having a cationic group, examples of the cationic group are amino groups, preferably tertiary amino groups and quaternary amino groups. In the tertiary amino group, the two groups bonded to the nitrogen atom are preferably the same or different and are an aliphatic group (particularly an alkyl group) having 1 to 5 carbon atoms, an aromatic group (aryl group) having 6 to 20 carbon atoms, or an araliphatic group having 7 to 25 carbon atoms (particularly an aralkyl group, for example, a benzyl group (C6H5-CH2-)). In the quaternary amino group, the three groups bonded to the nitrogen atom are preferably the same or different and are an aliphatic group (particularly an alkyl group) having 1 to 5 carbon atoms, an aromatic group (aryl group) having 6 to 20 carbon atoms, or an araliphatic group having 7 to 25 carbon atoms (particularly an aralkyl group, for example, a benzyl group (C6H5-CH2-)). In the tertiary amino group and the quaternary amino group, the remaining group bonded to the nitrogen atom may have a carbon-carbon double bond. The cationic group may be in the form of a salt.

[0137] The cationic group that is a salt is a salt with an acid (organic acid or inorganic acid). Organic acids, such as carboxylic acids having 1 to 20 carbon atoms (particularly monocarboxylic acids such as acetic acid, propionic acid, butyric acid, and stearic acid) are preferred. Dimethylaminoethyl (meth)acrylate and diethylaminoethyl (meth)acrylate and salts thereof are preferred.

[0138] Specific examples of the monomer having a cationic group are as follows. CH2=CHCOO-CH2CH2-N(CH3)2 and its salts (e.g. acetate) CH2=CHCOO-CH2CH2-N(CH2CH3)2 and its salts (e.g. acetate) CH2=C(CH3)COO-CH2CH2-N(CH3)2 and its salts (e.g. acetate) CH2=C(CH3)COO-CH2CH2-N(CH2CH3)2 and its salts (e.g. acetate salts) CH2=CHC(O)N(H)-CH2CH2CH2-N(CH3)2 and its salts (e.g. acetate) CH2=CHCOO-CH2CH2-N(-CH3)(-CH2-C6H5) and its salts (e.g. acetate) CH2=C(CH3)COO-CH2CH2-N(-CH2CH3)(-CH2-C6H5) and its salts (e.g. acetate) CH2=CHCOO-CH2CH2-N + (CH3)3Cl - CH2=CHCOO-CH2CH2-N + (-CH3)2(-CH2-C6H5)Cl - CH2=C(CH3)COO-CH2CH2-N + (CH3)3Cl - CH2=CHCOO-CH2CH(OH)CH2-N + (CH3)3Cl - CH2=C(CH3)COO-CH2CH(OH)CH2-N + (CH3)3Cl - CH2=C(CH3)COO-CH2CH(OH)CH2-N + (-CH2CH3)2(-CH2-C6H5)Cl - CH2=C(CH3)COO-CH2CH2-N + (CH3)3Br - CH2=C(CH3)COO-CH2CH2-N + (CH3)3I - CH2=C(CH3)COO-CH2CH2-N + (CH3)3O - SO3CH3 CH2=C(CH3)COO-CH2CH2-N + (CH3)(-CH2-C6H5)2Br -

[0139] The ionic group-containing monomer (c) is preferably methacrylic acid, acrylic acid, or dimethylaminoethyl methacrylate, and more preferably methacrylic acid or dimethylaminoethyl methacrylate.

[0140] (d) Halogenated olefin monomers The fluorine-containing polymer may have a repeating unit derived from a halogenated olefin monomer (d). The halogenated olefin monomer may not have a fluorine atom. The halogenated olefin monomer is preferably an olefin having 2 to 20 carbon atoms substituted with 1 to 10 chlorine atoms, bromine atoms or iodine atoms. The halogenated olefin monomer is preferably a chlorinated olefin having 2 to 20 carbon atoms, particularly preferably an olefin having 2 to 5 carbon atoms and having 1 to 5 chlorine atoms. Specific preferred examples of the halogenated olefin monomer are vinyl halides, such as vinyl chloride, vinyl bromide, vinyl iodide, and vinylidene halides, such as vinylidene chloride, vinylidene bromide, and vinylidene iodide. Vinyl chloride or vinylidene chloride is preferred because it enhances water repellency (particularly durability of water repellency). The presence of a repeating unit derived from a halogenated olefin monomer enhances the washing durability of the fluorine-containing polymer.

[0141] [(e) Crosslinkable monomer] In the fluorine-containing polymer, the crosslinkable monomer has at least two reactive groups and / or ethylenically unsaturated double bonds (preferably (meth)acrylate groups), and the crosslinkable monomer (e) may be a monomer that does not contain fluorine atoms. It may be a compound that does not contain fluorine atoms. The crosslinkable monomer (e) may be a compound that has at least two ethylenically unsaturated double bonds (preferably (meth)acrylate groups), or a compound that has at least one ethylenically unsaturated double bond and at least one reactive group. Examples of the reactive group include a hydroxyl group, an epoxy group, a chloromethyl group, a blocked isocyanate group, an amino group, a carboxyl group, and the like.

[0142] The crosslinking monomer may be a mono(meth)acrylate, di(meth)acrylate or di(meth)acrylamide having a reactive group.

[0143] An example of the crosslinkable monomer is a vinyl monomer having a reactive group. The vinyl monomer may be a compound having a polymerizable carbon-carbon double bond (>C=C<), and may be a monomer containing a vinyl group, a vinylene group, a vinylidene group, an acryloyl group, a methacryloyl group, or a derivative group thereof.

[0144] Examples of crosslinkable monomers include, but are not limited to, diacetone (meth)acrylamide, 3-chloro-2-hydroxypropyl (meth)acrylate, 2-acetoacetoxyethyl (meth)acrylate, butadiene, isoprene, chloroprene, vinyl monochloroacetate, vinyl methacrylate, glycidyl (meth)acrylate, 1,4-butanediol di(meth)acrylate, 1,6-hexanediol di(meth)acrylate, 1,9-nonanediol di(meth)acrylate, and neopentyl glycol di(meth)acrylate.

[0145] [(g) Cyclic Hydrocarbon Group-Containing Monomer] The fluorine-containing polymer may have a cyclic hydrocarbon group-containing monomer. The cyclic hydrocarbon group-containing monomer is a monomer having a cyclic hydrocarbon group, and may be a monomer having one ethylenically unsaturated double bond and a cyclic hydrocarbon group.

[0146] The cyclic hydrocarbon group-containing monomer preferably has a (meth)acrylic group as the ethylenically unsaturated double bond, and may, for example, have a (meth)acrylate group or a (meth)acrylamide group as the ethylenically unsaturated double bond.

[0147] The cyclic hydrocarbon group may be alicyclic or aromatic, preferably alicyclic. The cyclic hydrocarbon group may be saturated or unsaturated, preferably saturated. The cyclic hydrocarbon group may be a monocyclic group, a polycyclic group, or a bridged ring group, preferably a bridged ring group. The cyclic hydrocarbon group may have a chain group (e.g., a straight-chain or branched-chain hydrocarbon group).

[0148] The cyclic hydrocarbon group may have 4 or more, 6 or more, or 8 or more carbon atoms, and may have 30 or less, 26 or less, 22 or less, 18 or less, or 14 or less carbon atoms.

[0149] Specific examples of cyclic hydrocarbon groups include cyclohexyl, t-butylcyclohexyl, adamantyl, 2-methyl-2-adamantyl, 2-ethyl-2-adamantyl, bornyl, isobornyl, norbornyl, dicyclopentanyl, dicyclopentenyl, benzyl, phenyl, naphthyl, 2-t-butylphenyl, residues in which one or more hydrogen atoms have been removed from these groups (e.g., cyclohexylene, adamantylene, phenylene, naphthylene, etc.), and groups which are substitution products thereof.

[0150] Specific examples of the cyclic hydrocarbon group-containing monomer include cyclohexyl (meth)acrylate, t-butylcyclohexyl (meth)acrylate, benzyl (meth)acrylate, styrene, α-methylstyrene, p-methylstyrene, isobornyl (meth)acrylate, dicyclopentanyl (meth)acrylate, dicyclopentenyl (meth)acrylate, dicyclopentanyloxyethyl (meth)acrylate, tricyclopentanyl (meth)acrylate, adamantyl (meth)acrylate, 2-methyl-2-adamantyl (meth)acrylate, 2-ethyl-2-adamantyl (meth)acrylate, and compounds in which these acrylates are substituted with acrylamide. These may be used alone or in combination of two or more.

[0151] [(h) Other monomers] The other monomers are not limited to these examples, and include acrylonitrile, organosiloxane-containing (meth)acrylates, short-chain alkyl (meth)acrylates, vinyl acetate, vinyl alkyl ethers, etc. The other monomers (d) may be used alone or in combination of two or more.

[0152] [Polymer Composition] The combination of the monomers (a) to (h) constituting the repeating units of the fluorine-containing polymer is not particularly limited, and examples are as follows (brackets are omitted): f f+a f+b f+c f+a+b f+a+b+c f+a+c f+a+d f+a+b+c+d f+a+b+c+d+e f+a+b+c+d+e+g Further, another monomer (h) may be used in combination with the above combination. The fluorine-containing polymer preferably contains a repeating unit derived from the monomer (f) and a repeating unit derived from the monomer (a). In the case of a textile product, the monomers preferably include a combination of the monomers (a), (d), (e) and (g). In the case of a paper product, the monomers preferably include a combination of the monomers (a), (b) and (c).

[0153] The amount of the repeating units derived from the monomer (f) may be 1% by weight or more, 5% by weight or more, 10% by weight or more, 20% by weight or more, 30% by weight or more, 40% by weight or more, 50% by weight or more, 60% by weight or more, 70% by weight or more, 80% by weight or more, or 90% by weight or more, and may be 95% by weight or less, 85% by weight or less, 75% by weight or less, 65% by weight or less, 55% by weight or less, 45% by weight or less, 35% by weight or less, 25% by weight or less, 15% by weight or less, or 5% by weight or less, based on the fluoropolymer.

[0154] The amount of the repeating units derived from the monomer (a) may be 1% by weight or more, 5% by weight or more, 10% by weight or more, 20% by weight or more, 30% by weight or more, 40% by weight or more, 50% by weight or more, 60% by weight or more, 70% by weight or more, 80% by weight or more, or 90% by weight or more, and may be 95% by weight or less, 85% by weight or less, 75% by weight or less, 65% by weight or less, 55% by weight or less, 45% by weight or less, 35% by weight or less, 25% by weight or less, 15% by weight or less, or 5% by weight or less, based on the fluoropolymer. The amount of the repeating units derived from monomer (a) may be, relative to 100 parts by weight of the amount of the repeating units derived from monomer (f), 0.01 parts by weight or more, 0.1 parts by weight or more, 1 part by weight or more, 3 parts by weight or more, 5 parts by weight or more, 10 parts by weight or more, 15 parts by weight or more, 20 parts by weight or more, 50 parts by weight or more, 75 parts by weight or more, 100 parts by weight or more, 300 parts by weight or more, 500 parts by weight or more, 1000 parts by weight or more, or 3000 parts by weight or less, 2000 parts by weight or less, 1000 parts by weight or less, 750 parts by weight or less, 500 parts by weight or less, 300 parts by weight or less, 200 parts by weight or less, 100 parts by weight or less, 50 parts by weight or less, 30 parts by weight or less, 10 parts by weight or less, or 1 part by weight or less.

[0155] The amount of the repeating units derived from the monomer (b) may be 1% by weight or more, 5% by weight or more, 10% by weight or more, 20% by weight or more, 30% by weight or more, 40% by weight or more, 50% by weight or more, 60% by weight or more, 70% by weight or more, 80% by weight or more, or 90% by weight or more, and may be 95% by weight or less, 85% by weight or less, 75% by weight or less, 65% by weight or less, 55% by weight or less, 45% by weight or less, 35% by weight or less, 25% by weight or less, 15% by weight or less, or 5% by weight or less, based on the fluoropolymer. The amount of the repeating units derived from monomer (b) may be, relative to 100 parts by weight of the amount of the repeating units derived from monomer (f), 0.01 parts by weight or more, 0.1 parts by weight or more, 1 part by weight or more, 3 parts by weight or more, 5 parts by weight or more, 10 parts by weight or more, 15 parts by weight or more, 20 parts by weight or more, 50 parts by weight or more, 75 parts by weight or more, 100 parts by weight or more, 300 parts by weight or more, 500 parts by weight or more, 1000 parts by weight or more, or 3000 parts by weight or less, 2000 parts by weight or less, 1000 parts by weight or less, 750 parts by weight or less, 500 parts by weight or less, 300 parts by weight or less, 200 parts by weight or less, 100 parts by weight or less, 50 parts by weight or less, 30 parts by weight or less, 10 parts by weight or less, or 1 part by weight or less.

[0156] The amount of the repeating units derived from the monomer (c) may be 1% by weight or more, 5% by weight or more, 10% by weight or more, 20% by weight or more, 30% by weight or more, 40% by weight or more, 50% by weight or more, 60% by weight or more, 70% by weight or more, 80% by weight or more, or 90% by weight or more, and may be 95% by weight or less, 85% by weight or less, 75% by weight or less, 65% by weight or less, 55% by weight or less, 45% by weight or less, 35% by weight or less, 25% by weight or less, 15% by weight or less, or 5% by weight or less, based on the fluorine-containing polymer. The amount of the repeating units derived from monomer (c) may be, relative to 100 parts by weight of the amount of the repeating units derived from monomer (f), 0.01 parts by weight or more, 0.1 parts by weight or more, 1 part by weight or more, 3 parts by weight or more, 5 parts by weight or more, 10 parts by weight or more, 15 parts by weight or more, 20 parts by weight or more, 50 parts by weight or more, 75 parts by weight or more, 100 parts by weight or more, 300 parts by weight or more, 500 parts by weight or more, 1000 parts by weight or more, or 3000 parts by weight or less, 2000 parts by weight or less, 1000 parts by weight or less, 750 parts by weight or less, 500 parts by weight or less, 300 parts by weight or less, 200 parts by weight or less, 100 parts by weight or less, 50 parts by weight or less, 30 parts by weight or less, 10 parts by weight or less, or 1 part by weight or less.

[0157] The amount of the repeating units derived from the monomer (d) may be 1% by weight or more, 5% by weight or more, 10% by weight or more, 20% by weight or more, 30% by weight or more, 40% by weight or more, 50% by weight or more, 60% by weight or more, 70% by weight or more, 80% by weight or more, or 90% by weight or more, and may be 95% by weight or less, 85% by weight or less, 75% by weight or less, 65% by weight or less, 55% by weight or less, 45% by weight or less, 35% by weight or less, 25% by weight or less, 15% by weight or less, or 5% by weight or less, based on the fluoropolymer. The amount of the repeating units derived from monomer (d) may be, relative to 100 parts by weight of the amount of the repeating units derived from monomer (f), 0.01 parts by weight or more, 0.1 parts by weight or more, 1 part by weight or more, 3 parts by weight or more, 5 parts by weight or more, 10 parts by weight or more, 15 parts by weight or more, 20 parts by weight or more, 50 parts by weight or more, 75 parts by weight or more, 100 parts by weight or more, 300 parts by weight or more, 500 parts by weight or more, 1000 parts by weight or more, or 3000 parts by weight or less, 2000 parts by weight or less, 1000 parts by weight or less, 750 parts by weight or less, 500 parts by weight or less, 300 parts by weight or less, 200 parts by weight or less, 100 parts by weight or less, 50 parts by weight or less, 30 parts by weight or less, 10 parts by weight or less, or 1 part by weight or less.

[0158] The amount of the repeating units derived from the monomer (e) may be 1% by weight or more, 5% by weight or more, 10% by weight or more, 20% by weight or more, 30% by weight or more, 40% by weight or more, 50% by weight or more, 60% by weight or more, 70% by weight or more, 80% by weight or more, or 90% by weight or more, and may be 95% by weight or less, 85% by weight or less, 75% by weight or less, 65% by weight or less, 55% by weight or less, 45% by weight or less, 35% by weight or less, 25% by weight or less, 15% by weight or less, or 5% by weight or less, based on the fluoropolymer. The amount of the repeating units derived from monomer (e) may be, relative to 100 parts by weight of the amount of the repeating units derived from monomer (f), 0.01 parts by weight or more, 0.1 parts by weight or more, 1 part by weight or more, 3 parts by weight or more, 5 parts by weight or more, 10 parts by weight or more, 15 parts by weight or more, 20 parts by weight or more, 50 parts by weight or more, 75 parts by weight or more, 100 parts by weight or more, 300 parts by weight or more, 500 parts by weight or more, 1000 parts by weight or more, or 3000 parts by weight or less, 2000 parts by weight or less, 1000 parts by weight or less, 750 parts by weight or less, 500 parts by weight or less, 300 parts by weight or less, 200 parts by weight or less, 100 parts by weight or less, 50 parts by weight or less, 30 parts by weight or less, 10 parts by weight or less, or 1 part by weight or less.

[0159] The amount of the repeating units derived from the monomer (g) may be 1% by weight or more, 5% by weight or more, 10% by weight or more, 20% by weight or more, 30% by weight or more, 40% by weight or more, 50% by weight or more, 60% by weight or more, 70% by weight or more, 80% by weight or more, or 90% by weight or more, and may be 95% by weight or less, 85% by weight or less, 75% by weight or less, 65% by weight or less, 55% by weight or less, 45% by weight or less, 35% by weight or less, 25% by weight or less, 15% by weight or less, or 5% by weight or less, based on the fluoropolymer. The amount of the repeating units derived from monomer (g) may be, relative to 100 parts by weight of the amount of the repeating units derived from monomer (f), 0.01 parts by weight or more, 0.1 parts by weight or more, 1 part by weight or more, 3 parts by weight or more, 5 parts by weight or more, 10 parts by weight or more, 15 parts by weight or more, 20 parts by weight or more, 50 parts by weight or more, 75 parts by weight or more, 100 parts by weight or more, 300 parts by weight or more, 500 parts by weight or more, 1000 parts by weight or more, or 3000 parts by weight or less, 2000 parts by weight or less, 1000 parts by weight or less, 750 parts by weight or less, 500 parts by weight or less, 300 parts by weight or less, 200 parts by weight or less, 100 parts by weight or less, 50 parts by weight or less, 30 parts by weight or less, 10 parts by weight or less, or 1 part by weight or less.

[0160] The amount of repeating units derived from monomer (h) may be 1% by weight or more, 5% by weight or more, 10% by weight or more, 20% by weight or more, 30% by weight or more, 40% by weight or more, 50% by weight or more, 60% by weight or more, 70% by weight or more, 80% by weight or more, or 90% by weight or more, and may be 95% by weight or less, 85% by weight or less, 75% by weight or less, 65% by weight or less, 55% by weight or less, 45% by weight or less, 35% by weight or less, 25% by weight or less, 15% by weight or less, or 5% by weight or less, based on the fluoropolymer. The amount of the repeating units derived from monomer (h) may be, relative to 100 parts by weight of the amount of the repeating units derived from monomer (f), 0.01 parts by weight or more, 0.1 parts by weight or more, 1 part by weight or more, 3 parts by weight or more, 5 parts by weight or more, 10 parts by weight or more, 15 parts by weight or more, 20 parts by weight or more, 50 parts by weight or more, 75 parts by weight or more, 100 parts by weight or more, 300 parts by weight or more, 500 parts by weight or more, 1000 parts by weight or more, or 3000 parts by weight or less, 2000 parts by weight or less, 1000 parts by weight or less, 750 parts by weight or less, 500 parts by weight or less, 300 parts by weight or less, 200 parts by weight or less, 100 parts by weight or less, 50 parts by weight or less, 30 parts by weight or less, 10 parts by weight or less, or 1 part by weight or less.

[0161] [Polymerization method] The fluorine-containing polymer can be produced by a known polymerization method, and the polymerization reaction conditions can be selected arbitrarily. Examples of such polymerization methods include solution polymerization, suspension polymerization, emulsion polymerization, and condensation polymerization.

[0162] In solution polymerization, a method is adopted in which a monomer is dissolved in an organic solvent in the presence of a polymerization initiator, and after nitrogen substitution, the mixture is heated and stirred at a temperature in the range of 30 to 120°C for 1 to 10 hours. Examples of the polymerization initiator include azobisisobutyronitrile, benzoyl peroxide, di-t-butyl peroxide, lauryl peroxide, cumene hydroperoxide, t-butyl peroxypivalate, and diisopropyl peroxydicarbonate. The polymerization initiator is used in an amount of 0.01 to 20 parts by weight, for example, 0.01 to 10 parts by weight, relative to 100 parts by weight of the monomer.

[0163] The organic solvent is inactive to the monomers and dissolves them, and may be, for example, an ester (e.g., an ester having 2 to 40 carbon atoms, specifically, ethyl acetate, butyl acetate), a ketone (e.g., a ketone having 2 to 40 carbon atoms, specifically, methyl ethyl ketone, diisobutyl ketone, methyl isobutyl ketone), or an alcohol (e.g., an alcohol having 1 to 40 carbon atoms, specifically, ethanol, butanol, isopropyl alcohol). Specific examples of the organic solvent include acetone, chloroform, HCHC225, isopropyl alcohol, cyclohexane, benzene, toluene, xylene, petroleum ether, tetrahydrofuran, 1,4-dioxane, methyl ethyl ketone, methyl isobutyl ketone, diisobutyl ketone, ethyl acetate, butyl acetate, 1,1,2,2-tetrachloroethane, 1,1,1-trichloroethane, trichloroethylene, perchloroethylene, tetrachlorodifluoroethane, trichlorotrifluoroethane, and the like. The organic solvent is used in an amount of 10 to 3000 parts by weight, for example, 50 to 2000 parts by weight, based on 100 parts by weight of the total of the monomers.

[0164] In emulsion polymerization, a method is adopted in which a monomer is emulsified in water in the presence of a polymerization initiator and an emulsifier, and after nitrogen substitution, the monomer is polymerized by stirring at a temperature in the range of 50 to 80°C for 1 to 20 hours. As the polymerization initiator, water-soluble initiators such as benzoyl peroxide, lauroyl peroxide, t-butyl perbenzoate, 1-hydroxycyclohexyl hydroperoxide, 3-carboxypropionyl peroxide, acetyl peroxide, azobisisobutylamidine dihydrochloride, sodium peroxide, potassium persulfate, and ammonium persulfate, and oil-soluble initiators such as azobisisobutyronitrile, benzoyl peroxide, di-t-butyl peroxide, lauryl peroxide, cumene hydroperoxide, t-butyl peroxypivalate, and diisopropyl peroxydicarbonate are used. The polymerization initiator is used in the range of 0.01 to 10 parts by weight relative to 100 parts by weight of the monomer.

[0165] In order to obtain a polymer aqueous dispersion having excellent shelf stability, it is desirable to polymerize the monomer by dispersing it in water into fine particles using an emulsifier capable of applying strong crushing energy such as a high-pressure homogenizer or an ultrasonic homogenizer. As the emulsifier, various anionic, cationic or nonionic emulsifiers can be used, and are used in the range of 0.5 to 20 parts by weight per 100 parts by weight of the monomer. It is preferable to use an anionic and / or nonionic and / or cationic emulsifier. When the monomers are not completely compatible with each other, it is preferable to add a compatibilizer that can sufficiently make these monomers compatible, such as a water-soluble organic solvent or a low molecular weight monomer. The addition of a compatibilizer can improve emulsifiability and copolymerizability.

[0166] The water-soluble organic solvent may be the organic solvent described above. For example, acetone, methyl ethyl ketone, ethyl acetate, propylene glycol, dipropylene glycol monomethyl ether, dipropylene glycol, tripropylene glycol, ethanol, etc. may be used in an amount of 1 to 50 parts by weight, for example, 10 to 40 parts by weight, based on 100 parts by weight of water. In addition, the low molecular weight monomer may be methyl methacrylate, glycidyl methacrylate, 2,2,2-trifluoroethyl methacrylate, etc., may be used in an amount of 1 to 50 parts by weight, for example, 10 to 40 parts by weight, based on 100 parts by weight of the total amount of the monomers.

[0167] In the polymerization, a chain transfer agent may be used. The molecular weight of the polymer can be changed depending on the amount of the chain transfer agent used. Examples of the chain transfer agent include mercaptan group-containing compounds such as lauryl mercaptan, thioglycol, and thioglycerol (particularly alkyl mercaptans (e.g., having 1 to 40 carbon atoms)), and inorganic salts such as sodium hypophosphite and sodium hydrogen sulfite. The amount of the chain transfer agent used may be in the range of 0.01 to 10 parts by weight, for example, 0.1 to 5 parts by weight, based on 100 parts by weight of the total amount of the monomers.

[0168] <Water and oil repellent> The water / oil repellent in the present disclosure imparts liquid repellency (water repellency, oil repellency, oil resistance, and / or water resistance) to a substrate (e.g., a fiber substrate, a paper substrate), and can function as at least one selected from the group consisting of a water repellent, an oil repellent, an oil resistance agent, and a water resistance agent. The water / oil repellent in the present disclosure can effectively impart oil resistance (oil repellency) and / or water resistance (water repellency) to the substrate, and can, for example, effectively impart both oil resistance and water resistance.

[0169] [Fluorine-containing polymer] The water / oil repellent of the present disclosure includes the above-mentioned fluoropolymer. The fluoropolymer itself may be used as the water / oil repellent, or may be used in combination with other components as described below.

[0170] The water and oil repellent in the present disclosure is Rf 1 or Rf 2 The water- and oil-repellent agent of the present disclosure may not have any of the following: a compound having a fluoroalkyl group having 8 or more carbon atoms, a compound having a perfluoroalkyl group having 8 or more carbon atoms, a compound having a fluoroalkyl group having 4 or more carbon atoms, a compound having a perfluoroalkyl group having 4 or more carbon atoms, a compound having a fluoroalkyl group having 2 or more carbon atoms, and a compound having a perfluoroalkyl group having 2 or more carbon atoms. The water- and oil-repellent agent of the present disclosure may impart liquid repellency to a substrate even if it does not contain these fluorine compounds. In this specification, the fluoroalkyl group may mean a group in which one or more hydrogen atoms in each carbon atom of an alkyl group are substituted with a fluorine atom.

[0171] [Amount of fluorine-containing polymer] The amount of the fluorine-containing polymer in the water / oil repellent may be 0.01% by weight or more, 0.03% by weight or more, 0.5% by weight or more, 1% by weight or more, 3% by weight or more, 5% by weight or more, 10% by weight or more, 20% by weight or more, 30% by weight or more, and may be 60% by weight or less, 50% by weight or less, 40% by weight or less, 30% by weight or less, 20% by weight or less, 10% by weight or less, 5% by weight or less, or 3% by weight or less. The fluorine-containing polymer itself may be used as the water / oil repellent.

[0172] [Other water and oil repellent ingredients] The water- and oil-repellent agent of the present disclosure may contain other water- and oil-repellent components. As the other water- and oil-repellent agent, a known water- and oil-repellent agent can be used, for example, a non-fluorine water- and oil-repellent agent component. Examples of non-fluorine water- and oil-repellent agents include, for example, acrylic polymers described in WO / 2020 / 054856, WO / 2017 / 159754, WO / 2020 / 162547, etc., polyurethanes as described in JP-T-2016-524628, JP-T-2017-533976, JP-T-2017-504730, WO / 2021 / 132170, WO / 2021 / 132172, etc., natural product modifications as described in WO / 2022 / 065382, and WO / 2022 / 065385, etc., but are not limited thereto.

[0173] [Amount of other water and oil repellent ingredients] The amount of other water / oil repellent components may be, relative to 100 parts by weight of the fluoropolymer, 0.01 part by weight or more, 0.1 part by weight or more, 1 part by weight or more, 3 parts by weight or more, 5 parts by weight or more, 10 parts by weight or more, 15 parts by weight or more, 20 parts by weight or more, 50 parts by weight or more, 75 parts by weight or more, or 100 parts by weight or more, and may be 500 parts by weight or less, 300 parts by weight or less, 200 parts by weight or less, 100 parts by weight or less, 30 parts by weight or less, 20 parts by weight or less, 10 parts by weight or less, 5 parts by weight or less, 3 parts by weight or less, or 1 part by weight or less.

[0174] [Dispersant] The water / oil repellent of the present disclosure may contain a dispersant.

[0175] The dispersant is selected from an organic dispersant and an inorganic dispersant. At least one type may be used. The dispersant may be non-anionic, and may be at least one type selected from a nonionic dispersant, a cationic dispersant, an amphoteric dispersant, and an inorganic dispersant. The water / oil repellent may not contain an anionic dispersant.

[0176] As the dispersant, an organic dispersant and an inorganic dispersant may be used separately, or an organic dispersant and an inorganic dispersant may be used in combination.

[0177] An organic dispersant may be used as the dispersant. The organic dispersant can be classified into a nonionic dispersant, an anionic dispersant, a cationic dispersant, and an amphoteric dispersant, and the organic dispersant may mean a surfactant.

[0178] The dispersant may be fluorine-free.

[0179] [Nonionic dispersant] The dispersant may include a nonionic dispersant. The nonionic dispersant may be a nonionic surfactant.

[0180] The nonionic dispersant may be a low molecular weight or a high molecular weight. The molecular weight may be 100 or more, 500 or more, 1000 or more, 2000 or more, 4000 or more, or 6000 or more, and may be 100000 or less, 50000 or less, 25000 or less, 10000 or less, 7500 or less, 5000 or less, 2500 or less, 1000 or less, 750 or less, or 250 or less.

[0181] Examples of nonionic dispersants include ethers, esters, ester ethers, alkanolamides, polyols and amine oxides.

[0182] An example of an ether is a compound having an oxyalkylene group (preferably a polyoxyethylene group).

[0183] An example of the ester is an ester of an alcohol and a fatty acid. An example of the alcohol is a monohydric to hexahydric (particularly dihydric to pentahydric) alcohol (e.g., an aliphatic alcohol) having 1 to 50 carbon atoms (particularly 10 to 30 carbon atoms). An example of the fatty acid is a saturated or unsaturated fatty acid having 2 to 50 carbon atoms, particularly 5 to 30 carbon atoms.

[0184] An example of the ester ether is a compound in which an alkylene oxide (particularly ethylene oxide) is added to an ester of an alcohol and a fatty acid. An example of the alcohol is a monohydric to hexahydric (particularly dihydric to pentahydric) alcohol (e.g., aliphatic alcohol) having 1 to 50 carbon atoms (particularly 3 to 30 carbon atoms). An example of the fatty acid is a saturated or unsaturated fatty acid having 2 to 50 carbon atoms, particularly 5 to 30 carbon atoms.

[0185] An example of an alkanolamide is formed from a fatty acid and an alkanolamine. The alkanolamide may be a monoalkanolamide or a dialkanolamine. An example of a fatty acid is a saturated or unsaturated fatty acid having 2 to 50 carbon atoms, particularly 5 to 30 carbon atoms. The alkanolamine may be an alkanol having 2 to 50 carbon atoms, particularly 5 to 30 carbon atoms, having 1 to 3 amino groups and 1 to 5 hydroxyl groups.

[0186] The polyol may be a di- to penta-hydric alcohol having 10 to 30 carbon atoms. The amine oxide may be an oxide (eg, having 5 to 50 carbon atoms) of an amine (secondary amine or preferably tertiary amine).

[0187] The nonionic dispersant is preferably a nonionic dispersant having an oxyalkylene group (preferably a polyoxyethylene group). The number of carbon atoms in the alkylene group in the oxyalkylene group is preferably 2 to 10. The number of oxyalkylene groups in the molecule of the nonionic dispersant is generally preferably 2 to 100.

[0188] The nonionic dispersant is selected from the group consisting of ethers, esters, ester ethers, alkanolamides, polyols and amine oxides, and is preferably a nonionic dispersant having an oxyalkylene group.

[0189] The nonionic dispersant may be an alkylene oxide adduct of a linear and / or branched aliphatic (saturated and / or unsaturated) group, a polyalkylene glycol ester of a linear and / or branched fatty acid (saturated and / or unsaturated), a sorbitan ester of a linear and / or branched fatty acid (saturated and / or unsaturated), a glycerin ester of a linear and / or branched fatty acid (saturated and / or unsaturated), a polyglycerin ester of a linear and / or branched fatty acid (saturated and / or unsaturated), a sucrose ester of a linear and / or branched fatty acid (saturated and / or unsaturated), a polyoxyethylene (POE) / polyoxypropylene (POP) copolymer (random copolymer or block copolymer), an alkylene oxide adduct of acetylene glycol, and the like. Among these, those in which the structure of the alkylene oxide adduct portion and the polyalkylene glycol portion is polyoxyethylene (POE) or polyoxypropylene (POP) or a POE / POP copolymer (which may be a random copolymer or a block copolymer) are preferred. Additionally, the nonionic dispersant need not contain aromatic groups.

[0190] The nonionic dispersant has the formula: R 1 O-(CH2CH2O) p -(R 2 O) q -R 3 [In the formula, R 1 is an alkyl group having 1 to 22 carbon atoms or an alkenyl group or acyl group having 2 to 22 carbon atoms, R 2 each is independently the same or different and is an alkylene group having 3 or more carbon atoms (e.g., 3 to 10), R 3 is a hydrogen atom, an alkyl group having 1 to 22 carbon atoms, or an alkenyl group having 2 to 22 carbon atoms, p is a number equal to or greater than 2, q is a number equal to or greater than 0. The compound may be represented by the formula:

[0191] R 1R preferably has 8 to 20 carbon atoms, particularly preferably 10 to 18 carbon atoms. 1 Preferred specific examples include a lauryl group, a tridecyl group, and an oleyl group. R 2 Examples are a propylene group and a butylene group. In the nonionic dispersant, p may be a number of 3 or more (for example, 5 to 200). q may be a number of 2 or more (for example, 5 to 200). That is, -(R 2 O) q may form a polyoxyalkylene chain. The nonionic dispersant may be a polyoxyethylene alkylene alkyl ether containing a hydrophilic polyoxyethylene chain and a hydrophobic oxyalkylene chain (particularly a polyoxyalkylene chain) in the center. Examples of the hydrophobic oxyalkylene chain include an oxypropylene chain, an oxybutylene chain, and a styrene chain, and among these, an oxypropylene chain is preferred.

[0192] Examples of nonionic dispersants include ethylene oxide and hexylphenol, isooctatylphenol, hexadecanol, oleic acid, alkanes (C 12 -C 16 ) Thiol, Sorbitan Mono Fatty Acid (C7-C 19 ) or alkyl(C 12 -C 18 ) amines, etc., sorbitan fatty acid esters, glycerin fatty acid esters, polyglycerin fatty acid esters, sucrose fatty acid esters, propylene glycol fatty acid esters, polyoxyethylene alkyl ethers, polyoxyethylene polyoxypropylene alkyl ethers, polyoxyethylene glycerin fatty acid esters, polyoxyethylene sorbitan fatty acid esters, lecithin derivatives, etc.

[0193] The proportion of the polyoxyethylene block may be 5 to 80% by weight, for example 30 to 75% by weight, particularly 40 to 70% by weight, based on the molecular weight of the nonionic dispersant (copolymer). The average molecular weight of the nonionic dispersant is generally 300 to 5,000, for example, 500 to 3,000. The nonionic dispersant may be a single type or a mixture of two or more types. The nonionic dispersant may be a mixture of a compound having an HLB (hydrophilic-hydrophobic balance) of less than 15 (particularly 5 or less) and a compound having an HLB of 15 or more.

[0194] [Cationic dispersants] The dispersant may contain a cationic dispersant. The cationic dispersant may be a cationic surfactant. The cationic dispersant may be a low molecular weight type (e.g., molecular weight of 2000 or less, particularly 10000 or less) or a high molecular weight type (e.g., molecular weight of 2000 or more). The cationic dispersant may be a compound that does not have an amide group.

[0195] The cationic dispersant may be a low molecular weight or a high molecular weight. The molecular weight may be 100 or more, 500 or more, 1000 or more, 2000 or more, 4000 or more, or 6000 or more, and may be 100000 or less, 50000 or less, 25000 or less, 10000 or less, 7500 or less, 5000 or less, 2500 or less, 1000 or less, 750 or less, or 250 or less.

[0196] The cationic dispersant may be an amine salt, a quaternary ammonium salt, or an oxyethylene adduct ammonium salt.Specific examples of the cationic dispersant include, but are not limited to, amine salt-type dispersants such as alkylamine salts, amino alcohol fatty acid derivatives, polyamine fatty acid derivatives, and imidazoline, and quaternary ammonium salt-type dispersants such as alkyl trimethyl ammonium salts, dialkyl dimethyl ammonium salts, alkyl dimethyl benzyl ammonium salts, pyridinium salts, alkyl isoquinolinium salts, benzalkonium chloride, and benzethonium chloride.

[0197] Preferred examples of the cationic dispersant are R 21 -N + (-R 22 )(-R23 )(-R 24 )X - [In the formula, R 21 , R 22 , R 23 and R 24 is a hydrocarbon group having 1 to 40 carbon atoms, X is an anionic group. It is a compound represented by the formula: R 21 , R 22 , R 23 and -R 24 Specific examples of X include alkyl groups (e.g., methyl, butyl, stearyl, and palmityl groups). Specific examples of X include halogens (e.g., chlorine) and acids (e.g., hydrochloric acid and acetic acid). The cationic dispersant is particularly preferably a monoalkyltrimethylammonium salt (alkyl having 4 to 40 carbon atoms).

[0198] The cationic dispersant is preferably an ammonium salt. The cationic dispersant has the formula: R 1 p -N + R 2 q X - [In the formula, R 1 is C12 or higher (e.g. C 12 ~C 50 ) linear and / or branched aliphatic (saturated and / or unsaturated) groups, R 2 is H or a C1-4 alkyl group, a benzyl group, a polyoxyethylene group (the number of oxyethylene groups is, for example, 1 (particularly 2, particularly 3) to 50); (CH3, C2H5 are particularly preferred), X is a halogen atom (for example), a C1-C4 fatty acid base, p is 1 or 2, q is 2 or 3, and p+q=4. R 1 may have 12 to 50 carbon atoms, for example, 12 to 30 carbon atoms.

[0199] Specific examples of cationic dispersants include dodecyltrimethylammonium acetate, trimethyltetradecylammonium chloride, hexadecyltrimethylammonium bromide, trimethyloctadecylammonium chloride, (dodecylmethylbenzyl)trimethylammonium chloride, benzyldodecyldimethylammonium chloride, methyldodecyldi(hydropolyoxyethylene)ammonium chloride, benzyldodecyldi(hydropolyoxyethylene)ammonium chloride, and N-[2-(diethylamino)ethyl]oleamide hydrochloride.

[0200] [Anionic dispersant] The dispersant may comprise an anionic dispersant. The anionic dispersant may be an anionic surfactant. The dispersant may be free of an anionic dispersant.

[0201] The anionic dispersant may be a low molecular weight or a high molecular weight. The molecular weight may be 100 or more, 500 or more, 1000 or more, 2000 or more, 4000 or more, or 6000 or more, and may be 100000 or less, 50000 or less, 25000 or less, 10000 or less, 7500 or less, 5000 or less, 2500 or less, 1000 or less, 750 or less, or 250 or less.

[0202] Examples of anionic dispersants include alkyl ether sulfates, alkyl sulfates, alkenyl ether sulfates, alkenyl sulfates, olefin sulfonates, alkanesulfonates, saturated or unsaturated fatty acid salts, alkyl or alkenyl ether carboxylates, α-sulfonic fatty acid salts, N-acylamino acid type dispersants, phosphoric acid mono- or diester type dispersants, and sulfosuccinic acid esters.

[0203] [Amphoteric dispersant] The dispersant may comprise an amphoteric dispersant, which may be an amphoteric surfactant.

[0204] The amphoteric dispersant may be of low molecular weight or high molecular weight. The molecular weight may be 100 or more, 500 or more, 1000 or more, 2000 or more, 4000 or more, or 6000 or more, and may be 100000 or less, 50000 or less, 25000 or less, 10000 or less, 7500 or less, 5000 or less, 2500 or less, 1000 or less, 7500 or less, or 250 or less.

[0205] Examples of amphoteric dispersants include alanines, imidazolinium betaines, amido betaines, and betaine acetate. Specific examples include lauryl betaine, stearyl betaine, lauryl carboxymethyl hydroxyethyl imidazolinium betaine, lauryl dimethylamino acetate betaine, and fatty acid amidopropyl dimethylamino acetate betaine.

[0206] [Inorganic dispersant] The dispersant may comprise an inorganic dispersant.

[0207] The average primary particle size of the inorganic dispersant may be 5 nm or more, 30 nm or more, 100 nm or more, 1 μm or more, 10 μm or more, or 25 μm or more, and may be 100 μm or less, 50 μm or less, 10 μm or less, 1 μm or less, 500 nm or less, or 300 nm or less. The average primary particle size can be measured, for example, by observation with a microscope (scanning electron microscope or transmission electron microscope). The inorganic dispersant may be a hydrophilic particle.

[0208] Examples of inorganic dispersants include polyvalent metal phosphates such as tricalcium phosphate, magnesium phosphate, aluminum phosphate, zinc phosphate, and hydroxyapatite; carbonates such as calcium carbonate and magnesium carbonate; silicates such as calcium metasilicate; sulfates such as calcium sulfate and barium sulfate; and hydroxides such as calcium hydroxide, magnesium hydroxide, and aluminum hydroxide.

[0209] [Amount of dispersant] The amount of the dispersant may be, relative to 100 parts by weight of the fluoropolymer, 0.01 part by weight or more, 0.1 part by weight or more, 1 part by weight or more, 3 parts by weight or more, 5 parts by weight or more, 10 parts by weight or more, 15 parts by weight or more, 20 parts by weight or more, 50 parts by weight or more, 75 parts by weight or more, or 100 parts by weight or more, and may be 500 parts by weight or less, 300 parts by weight or less, 200 parts by weight or less, 100 parts by weight or less, 30 parts by weight or less, 20 parts by weight or less, 10 parts by weight or less, 5 parts by weight or less, 3 parts by weight or less, or 1 part by weight or less.

[0210] [Liquid medium] The water- and oil-repellent agent in the present disclosure may include a liquid medium. The liquid medium may be water, an organic solvent, or a mixture of water and an organic solvent. The water- and oil-repellent agent may be a dispersion or a solution. The water- and oil-repellent agent in the present disclosure may be a water-dispersed type and may include at least water.

[0211] Examples of the organic solvent include esters (e.g., esters having 2 to 40 carbon atoms, specifically, ethyl acetate, butyl acetate), ketones (e.g., ketones having 2 to 40 carbon atoms, specifically, methyl ethyl ketone, diisobutyl ketone), alcohols (e.g., alcohols having 1 to 40 carbon atoms, specifically, isopropyl alcohol), aromatic solvents (e.g., toluene and xylene), and petroleum solvents (e.g., alkanes having 5 to 10 carbon atoms, specifically, naphtha, kerosene). The organic solvent is preferably a water-soluble organic solvent. The water-soluble organic solvent may contain a compound having at least one hydroxyl group (e.g., alcohol, polyols such as glycol-based solvents, ethers of polyols (e.g., monoethers), etc.). These may be used alone or in combination of two or more.

[0212] [Amount of liquid medium] The amount of the liquid medium may be, relative to 1 part by weight of the fluoropolymer, 1 part by weight or more, 3 parts by weight or more, 5 parts by weight or more, 10 parts by weight or more, 20 parts by weight or more, 30 parts by weight or more, 40 parts by weight or more, 50 parts by weight or more, 100 parts by weight or more, 200 parts by weight or more, 300 parts by weight or more, 500 parts by weight or more, or 1000 parts by weight or more, and may be 3000 parts by weight or less, 2000 parts by weight or less, 1000 parts by weight or less, 500 parts by weight or less, 200 parts by weight or less, 175 parts by weight or less, 150 parts by weight or less, 125 parts by weight or less, 100 parts by weight or less, 80 parts by weight or less, 60 parts by weight or less, 40 parts by weight or less, 20 parts by weight or less, or 10 parts by weight or less.

[0213] The amount of water may be 1 part by weight or more, 3 parts by weight or more, 5 parts by weight or more, 10 parts by weight or more, 20 parts by weight or more, 30 parts by weight or more, 40 parts by weight or more, 50 parts by weight or more, 100 parts by weight or more, 200 parts by weight or more, 300 parts by weight or more, 500 parts by weight or more, or 1000 parts by weight or more, and may be 3000 parts by weight or less, 2000 parts by weight or less, 1000 parts by weight or less, 500 parts by weight or less, 200 parts by weight or less, 175 parts by weight or less, 150 parts by weight or less, 125 parts by weight or less, 100 parts by weight or less, 80 parts by weight or less, 60 parts by weight or less, 40 parts by weight or less, 20 parts by weight or less, or 10 parts by weight or less, relative to 1 part by weight of the fluoropolymer.

[0214] The amount of the organic solvent may be 1 part by weight or more, 3 parts by weight or more, 5 parts by weight or more, 10 parts by weight or more, 20 parts by weight or more, 30 parts by weight or more, 40 parts by weight or more, 50 parts by weight or more, 100 parts by weight or more, 200 parts by weight or more, 300 parts by weight or more, 500 parts by weight or more, or 1000 parts by weight or more, and may be 3000 parts by weight or less, 2000 parts by weight or less, 1000 parts by weight or less, 500 parts by weight or less, 200 parts by weight or less, 175 parts by weight or less, 150 parts by weight or less, 125 parts by weight or less, 100 parts by weight or less, 80 parts by weight or less, 60 parts by weight or less, 40 parts by weight or less, 20 parts by weight or less, or 10 parts by weight or less, relative to 1 part by weight of the fluoropolymer.

[0215] 〔silicone〕 The water / oil repellent of the present disclosure may contain silicone (polyorganosiloxane). By containing silicone, it is possible to obtain good texture and durability in addition to good liquid repellency.

[0216] As the silicone, known silicones can be used, and examples of silicones include polydimethylsiloxane and modified silicones (amino-modified, epoxy-modified silicone, carboxy-modified silicone, methylhydrogen silicone, etc.). The silicone may be a silicone wax having wax-like properties. These may be used alone or in combination of two or more.

[0217] The weight average molecular weight of the silicone may be 1,000 or more, 10,000 or more, or 50,000 or more, and may be 500,000 or less, 250,000 or less, 100,000 or less, or 50,000 or less.

[0218] [Amount of silicone] The amount of silicone may be, relative to 100 parts by weight of the fluoropolymer, 0.1 part by weight or more, 1 part by weight or more, 3 parts by weight or more, 5 parts by weight or more, 10 parts by weight or more, 15 parts by weight or more, 20 parts by weight or more, 50 parts by weight or more, 75 parts by weight or more, or 100 parts by weight or more, and may be 500 parts by weight or less, 300 parts by weight or less, 200 parts by weight or less, 100 parts by weight or less, 50 parts by weight or less, 40 parts by weight or less, 30 parts by weight or less, 20 parts by weight or less, 10 parts by weight or less, or 5 parts by weight or less.

[0219] 〔wax〕 The water / oil repellent in the present disclosure may contain a wax. By containing a wax, it is possible to impart good liquid repellency to the substrate.

[0220] Examples of waxes include paraffin wax, microcrystalline wax, Fischer-Tropsch wax, polyolefin wax (polyethylene wax, polypropylene wax, etc.), oxidized polyolefin wax, silicone wax, animal and vegetable wax, mineral wax, etc. Paraffin wax is preferred. Specific examples of compounds constituting the wax include normal alkanes (e.g., tricosane, tetracosane, pentacosane, hexacosane, heptacosane, octacosane, nonacosane, triacontane, hentriacontane, dotriacontane, tritriacontane, tetratriacontane, pentatriacontane, hexatriacontane), and normal alkenes (e.g., 1-eicosene, 1-docosene, 1-tricosene, 1-tetracosene, 1-pentacosene, 1-hexacosene, 1-heptacosene, 1-octacosene, 1-nonacosene, 1-triacontene, 1-hentriacontene, 1-dotriacontene, 1-tritriacontene, 1-tetratriacontene, 1-pentatriacontene, 1-hexatriacontene). The carbon number of the compound constituting the wax is preferably 20 to 60, for example, 25 to 45. The molecular weight of the wax may be from 200 to 2000, for example, from 250 to 1500, or from 300 to 1000. These may be used alone or in combination of two or more.

[0221] The melting point of the wax may be 40° C. or more, 50° C. or more, 55° C. or more, 60° C. or more, 65° C. or more, or 70° C. or more, preferably 55° C. or more, more preferably 60° C. or more, and may be 200° C. or less, 150° C. or less, 130° C. or less, 120° C. or less, 110° C. or less, 100° C. or less, 80° C. or less, or 50° C. or less, preferably 120° C. or less. The melting point of the wax is measured in accordance with JIS K 2235-1991.

[0222] [Amount of wax] The amount of the wax may be, relative to 100 parts by weight of the fluoropolymer, 0.1 part by weight or more, 1 part by weight or more, 3 parts by weight or more, 5 parts by weight or more, 10 parts by weight or more, 15 parts by weight or more, 20 parts by weight or more, 50 parts by weight or more, 75 parts by weight or more, or 100 parts by weight or more, and may be 500 parts by weight or less, 300 parts by weight or less, 200 parts by weight or less, 100 parts by weight or less, 50 parts by weight or less, 40 parts by weight or less, 30 parts by weight or less, 20 parts by weight or less, 10 parts by weight or less, or 5 parts by weight or less.

[0223] [Organic acid] The water- and oil-repellent agent of the present disclosure may contain an organic acid. As the organic acid, a known one may be used. As the organic acid, carboxylic acid, sulfonic acid, sulfinic acid, etc. are preferably mentioned, and carboxylic acid is particularly preferable. As the carboxylic acid, formic acid, acetic acid, propionic acid, butyric acid, oxalic acid, succinic acid, glutaric acid, adipic acid, malic acid, citric acid, etc. are mentioned, and formic acid or acetic acid is particularly preferable. In the present disclosure, the organic acid may be used alone or in combination of two or more kinds. For example, formic acid and acetic acid may be used in combination.

[0224] [Amount of organic acid] The amount of the organic acid may be 0.1 parts by weight or more, 1 part by weight or more, 3 parts by weight or more, 5 parts by weight or more, 10 parts by weight or more, 15 parts by weight or more, 20 parts by weight or more, 50 parts by weight or more, 75 parts by weight or more, or 100 parts by weight or more, and may be 500 parts by weight or less, 300 parts by weight or less, 200 parts by weight or less, 100 parts by weight or less, 50 parts by weight or less, 40 parts by weight or less, 30 parts by weight or less, 20 parts by weight or less, 10 parts by weight or less, or 5 parts by weight or less, relative to 100 parts by weight of the fluoropolymer. The amount of the organic acid may be adjusted so that the pH of the water / oil repellent is 3 to 10, for example, 5 to 9, particularly 6 to 8. The water / oil repellent may be acidic (pH 7 or less, for example, 6 or less).

[0225] [Hardening agent] The water / oil repellent of the present disclosure may contain a curing agent (an active hydrogen reactive compound or an active hydrogen-containing compound).

[0226] The curing agent (crosslinking agent) in the water / oil repellent can cure the fluorine-containing polymer well. The curing agent may be an active hydrogen reactive compound or an active hydrogen-containing compound that reacts with the active hydrogen or active hydrogen reactive group of the fluorine-containing polymer. Examples of the active hydrogen reactive compound are isocyanate compounds, epoxy compounds, chloromethyl group-containing compounds, carboxyl group-containing compounds, and hydrazide compounds. Examples of the active hydrogen-containing compound are hydroxyl group-containing compounds, amino group-containing compounds, carboxyl group-containing compounds, ketone group-containing compounds, hydrazide compounds, and melamine compounds.

[0227] The curing agent may include an isocyanate compound. The isocyanate compound may be a polyisocyanate compound. The polyisocyanate compound is a compound having two or more isocyanate groups in one molecule. The polyisocyanate compound acts as a crosslinking agent. Examples of the polyisocyanate compound include aliphatic polyisocyanates, alicyclic polyisocyanates, araliphatic polyisocyanates, aromatic polyisocyanates, and derivatives of these polyisocyanates. The isocyanate compound may be a blocked isocyanate compound (e.g., a blocked polyisocyanate compound). The blocked isocyanate compound is a compound in which the isocyanate group of the isocyanate compound is masked with a blocking agent to suppress the reaction.

[0228] Examples of aliphatic polyisocyanates are trimethylene diisocyanate, tetramethylene diisocyanate, hexamethylene diisocyanate, pentamethylene diisocyanate, 1,2-propylene diisocyanate, 1,2-butylene diisocyanate, 2,3-butylene diisocyanate, 1,3-butylene diisocyanate, 2,4,4- or 2,2,4-trimethylhexamethylene diisocyanate, 2,6-di ... Aliphatic diisocyanates such as cyanatomethyl caproate, and aliphatic triisocyanates such as lysine ester triisocyanate, 1,4,8-triisocyanatooctane, 1,6,11-triisocyanatoundecane, 1,8-diisocyanato-4-isocyanatomethyloctane, 1,3,6-triisocyanatohexane, 2,5,7-trimethyl-1,8-diisocyanato-5-isocyanatomethyloctane, etc. These may be used alone or in combination of two or more.

[0229] Examples of alicyclic polyisocyanates include alicyclic diisocyanates and alicyclic triisocyanates. Specific examples of alicyclic polyisocyanates include 1,3-cyclopentene diisocyanate, 3-isocyanatomethyl-3,5,5-trimethylcyclohexyl isocyanate (isophorone diisocyanate), and 1,3,5-triisocyanatocyclohexane. These may be used alone or in combination of two or more.

[0230] Examples of the araliphatic polyisocyanate are araliphatic diisocyanate and araliphatic triisocyanate.Specific examples of the araliphatic polyisocyanate are 1,3- or 1,4-xylylene diisocyanate or a mixture thereof, 1,3- or 1,4-bis(1-isocyanato-1-methylethyl)benzene (tetramethylxylylene diisocyanate) or a mixture thereof, and 1,3,5-triisocyanatomethylbenzene.These may be used alone or in combination of two or more.

[0231] Examples of aromatic polyisocyanates are aromatic diisocyanates, aromatic triisocyanates, and aromatic tetraisocyanates. Specific examples of aromatic polyisocyanates are m-phenylene diisocyanate, p-phenylene diisocyanate, 4,4'-diphenyl diisocyanate, 1,5-naphthalene diisocyanate, 2,4'- or 4,4'-diphenylmethane diisocyanate or a mixture thereof, 2,4- or 2,6-tolylene diisocyanate or a mixture thereof, triphenylmethane-4,4',4''-triisocyanate, and 4,4'-diphenylmethane-2,2',5,5'-tetraisocyanate. These may be used alone or in combination of two or more.

[0232] Examples of the polyisocyanate derivatives include various derivatives of the above-mentioned polyisocyanate compounds, such as dimers, trimers, biurets, allophanates, carbodiimides, uretdione, uretoimine, isocyanurates, iminooxadiazinedione, etc. These may be used alone or in combination of two or more.

[0233] These polyisocyanates can be used alone or in combination of two or more. As the polyisocyanate compound, it is preferable to use a blocked polyisocyanate compound (blocked isocyanate), which is a compound in which the isocyanate group of the polyisocyanate compound is blocked with a blocking agent. It is preferable to use a blocked polyisocyanate compound because it is relatively stable even in a solution and can be used in the same solution as the water / oil repellent agent.

[0234] The blocking agent blocks free isocyanate groups. When the blocked polyisocyanate compound is heated to, for example, 100°C or higher, for example, 130°C or higher, the isocyanate group is regenerated and can easily react with the hydroxyl group. Examples of the blocking agent include phenol-based compounds, lactam-based compounds, aliphatic alcohol-based compounds, and oxime-based compounds. The polyisocyanate compounds can be used alone or in combination of two or more kinds.

[0235] The epoxy compound is a compound having an epoxy group. Examples of the epoxy compound include epoxy compounds having a polyoxyalkylene group, such as polyglycerol polyglycidyl ether and polypropylene glycol diglycidyl ether; and sorbitol polyglycidyl ether. The chloromethyl group-containing compound is a compound having a chloromethyl group. An example of the chloromethyl group-containing compound is chloromethyl polystyrene. The carboxyl group-containing compound is a compound having a carboxyl group. Examples of the carboxyl group-containing compound include (poly)acrylic acid and (poly)methacrylic acid.

[0236] Specific examples of the ketone group-containing compound include (poly)diacetone acrylamide and diacetone alcohol. Specific examples of the hydrazide compound include hydrazine, carbohydrazide, adipic acid hydrazide, and the like. Specific examples of the melamine compound include melamine resins and methyl etherified melamine resins.

[0237] [Amount of hardener] The amount of the curing agent may be, relative to 100 parts by weight of the fluoropolymer, 0.1 part by weight or more, 1 part by weight or more, 3 parts by weight or more, 5 parts by weight or more, 10 parts by weight or more, 15 parts by weight or more, 20 parts by weight or more, 50 parts by weight or more, 75 parts by weight or more, or 100 parts by weight or more, and may be 500 parts by weight or less, 300 parts by weight or less, 200 parts by weight or less, 100 parts by weight or less, 50 parts by weight or less, 40 parts by weight or less, 30 parts by weight or less, 20 parts by weight or less, 10 parts by weight or less, or 5 parts by weight or less.

[0238] [Other ingredients] The water and oil repellent may contain other components in addition to the above components. Examples of other components include polysaccharides, paper strength agents, flocculants, retention improvers, coagulants, binder resins, slip prevention agents, sizing agents, paper strength agents, PVA, penetrating agents, organic acids, pigments, fillers, antistatic agents, preservatives, ultraviolet absorbers, antibacterial agents, deodorants, fragrances, etc. These may be used alone or in combination of two or more. In addition to the above-mentioned components, other components include other water and / or oil repellents, dispersants, texture adjusters, softeners, flame retardants, paint fixing agents, anti-wrinkle agents, drying speed adjusters, crosslinking agents, film-forming agents, compatibilizers, antifreeze agents, viscosity adjusters, UV absorbers, antioxidants, pH adjusters, insect repellents, defoamers, shrink prevention agents, laundry wrinkle prevention agents, shape retention agents, drape retention agents, ironing improvers, whitening agents, whitening agents, fabric softening clay, dye transfer inhibitors such as polyvinylpyrrolidone, polymer dispersants, dirt removers, scum dispersants, fluorescent whitening agents such as 4,4-bis(2-sulfostyryl)biphenyl disodium (Ciba Specialty Chemicals' Chinopearl CBS-X), dye fixatives, and discoloration inhibitors such as 1,4-bis(3-aminopropyl)piperazine. The following can be blended: stain removers, enzymes such as cellulase, amylase, protease, lipase, keratinase, etc. as fiber surface modifiers, foam inhibitors, silk protein powders, their surface modified products or emulsified dispersions (e.g., K-50, K-30, K-10, A-705, S-702, L-710, FP series (Idemitsu Petrochemicals), hydrolyzed silk liquid (Jomo), Silkgen G Soluble S (Ichimaru Falcos)), stain prevention agents (e.g., nonionic polymer compounds consisting of alkylene terephthalate and / or alkylene isophthalate units and polyoxyalkylene units (e.g., FR627 manufactured by GOO Chemical Industry Co., Ltd., SRC-1 manufactured by Clariant Japan, etc.), etc. These may be used alone or in combination of two or more.

[0239] [Polysaccharide] Examples of polysaccharides include starch, xanthan gum, karaya gum, welan gum, guar gum, pectin, tamarind gum, carrageenan, chitosan, gum arabic, locust bean gum, cellulose, alginic acid, agar, dextran, cellulose, carboxymethylcellulose, hydroxyethylcellulose, hydroxypropylcellulose, chitin nanofiber, cellulose nanofiber, pullulan, etc. The polysaccharide may be a substituted modified polysaccharide, in particular a modified polysaccharide into which a hydroxyl group or a cationic group has been introduced.

[0240] [Paper strength agents, flocculants, retention aids or coagulants] Examples of paper strength enhancers, flocculants, retention improvers or coagulants include styrene polymers (styrene / maleic acid polymers, styrene / acrylic acid polymers), urea-formaldehyde polymers, polyethyleneimine, melamine-formaldehyde polymers, polyamidoamine-epichlorohydrin polymers, polyacrylamide polymers, polyamine polymers, polydiallyldimethylammonium chloride, alkylamine-epichlorohydrin condensates, condensates of alkylene dichlorides and polyalkylene polyamines, dicyandiamide-formaldehyde condensates, dimethyldiallylammonium chloride polymers, and olefin / maleic anhydride polymers.

[0241] [Sizing agent] Examples of sizing agents include cellulose-reactive sizing agents, e.g., rosin-based sizing agents such as rosin-based soaps, rosin-based emulsions / dispersions, cellulose-reactive sizing agents, e.g., emulsions / dispersions of acid anhydrides such as alkyl and alkenyl succinic anhydrides (ASA), alkenyl and alkyl ketene dimers (AKD) and polymers, and anionic, cationic and amphoteric polymers of ethylenically unsaturated monomers, e.g., copolymers of styrene and acrylates.

[0242] [Antistatic agent] Examples of the antistatic agent include cationic antistatic agents having cationic functional groups such as quaternary ammonium salts, pyridinium salts, and primary, secondary, and tertiary amino groups; anionic antistatic agents having anionic functional groups such as sulfonates, sulfates, phosphonates, and phosphates; amphoteric antistatic agents such as alkylbetaines and their derivatives, imidazolines and their derivatives, alanines and their derivatives, nonionic antistatic agents such as aminoalcohols and their derivatives, glycerin and its derivatives, and polyethylene glycols and its derivatives. The antistatic agent may be an ion-conductive polymer obtained by polymerizing or copolymerizing monomers having these cationic, anionic, or amphoteric ion-conductive groups. These may be used alone or in combination of two or more.

[0243] [Preservatives] The preservatives are mainly used to enhance the preservative and bactericidal power and maintain the preservative properties during long-term storage. Examples of the preservatives include isothiazolone organic sulfur compounds, benzisothiazolone organic sulfur compounds, benzoic acids, 2-bromo-2-nitro-1,3-propanediol, etc.

[0244] [Ultraviolet absorber] An ultraviolet absorber is a drug that has an ultraviolet protection effect, and is a component that absorbs ultraviolet light and converts it into infrared light, visible light, etc. Examples of ultraviolet absorbers include aminobenzoic acid derivatives, salicylic acid derivatives, cinnamic acid derivatives, benzophenone derivatives, azole compounds, 4-t-butyl-4'-methoxybenzoylmethane, etc.

[0245] [Antibacterial agents] Antibacterial agents are components that have the effect of suppressing the growth of bacteria on fibers and further suppressing the generation of unpleasant odors resulting from the decomposition products of microorganisms. Examples of antibacterial agents include cationic bactericides such as quaternary ammonium salts, bis-(2-pyridylthio-1-oxide) zinc, polyhexamethylene biguanidine hydrochloride, 8-oxyquinoline, polylysine, etc.

[0246] [Deodorant] Examples of deodorants include cluster dextrin, methyl-β-cyclodextrin, 2-hydroxypropyl-β-cyclodextrin, monoacetyl-β-cyclodextrin, acylamidopropyldimethylamine oxide, and aminocarboxylic acid metal complexes (zinc complex of trisodium methylglycinediacetate described in WO 2012 / 090580).

[0247] [Amount of other ingredients] The amount or total amount of the other components may be, relative to 100 parts by weight of the fluoropolymer, 0.1 part by weight or more, 1 part by weight or more, 3 parts by weight or more, 5 parts by weight or more, 10 parts by weight or more, 15 parts by weight or more, 20 parts by weight or more, 50 parts by weight or more, 75 parts by weight or more, or 100 parts by weight or more, and may be 500 parts by weight or less, 300 parts by weight or less, 200 parts by weight or less, 100 parts by weight or less, 50 parts by weight or less, 40 parts by weight or less, 30 parts by weight or less, 20 parts by weight or less, 10 parts by weight or less, or 5 parts by weight or less.

[0248] <Manufacturing method of treated textile or paper products> The method for producing a product treated with a water / oil repellent according to the present disclosure includes a treatment step of treating a substrate with the water / oil repellent described above.

[0249] "Treatment" means that the water / oil repellent is applied to a substrate by immersion, spraying, coating, or the like. The treatment causes the fluorine-containing polymer, which is the active ingredient of the water / oil repellent, to adhere to the inside and / or surface of the substrate. Here, the adhesion may be physical or chemical, and for example, the fluorine-containing polymer may be physically or chemically (by reacting with) a hydroxyl group of the substrate (fiber, paper, glass, etc.).

[0250] [Base material] The substrate to be treated with the water / oil repellent agent of the present disclosure is not limited, but is preferably a textile product or a paper product, in particular a paper product.

[0251] The water- and oil-repellent agent of the present disclosure provides liquid repellency to a substrate (e.g., a fiber substrate, a paper substrate) and can function as at least one selected from the group consisting of a water repellent, an oil repellent, an oil-resistant agent, and a water-resistant agent. The substrate treated with the water- and oil-repellent agent of the present disclosure is, for example, oil-resistant paper or water-resistant paper.

[0252] Examples of the substrate for textile products include natural fibers of animal and vegetable origin such as cotton, hemp, wool, silk, etc., synthetic fibers such as polyamide, polyester, polyvinyl alcohol, polyacrylonitrile, polyvinyl chloride, polypropylene, etc., semi-synthetic fibers such as rayon, acetate, etc., inorganic fibers such as glass fiber, carbon fiber, asbestos fiber, etc., or mixtures of these fibers. Textile products include woven fabrics, knitted fabrics and nonwoven fabrics, clothing forms (e.g., water-repellent clothing, e.g., raincoats), and carpets, but the treatment may be performed on fibers, yarns, and intermediate textile products (e.g., slivers or rovings) before being made into cloth.

[0253] Examples of the substrate for paper products include paper made of bleached or unbleached chemical pulp such as kraft pulp or sulfite pulp, bleached or unbleached high-yield pulp such as groundwood pulp, mechanical pulp or thermomechanical pulp, waste paper pulp such as recycled newsprint, recycled magazine paper, recycled corrugated cardboard or deinked recycled paper, containers made of paper, molded articles made of paper, etc. Specific examples of paper products include food packaging materials, food containers, gypsum board base paper, coated base paper, medium-quality paper, general liners and cores, neutral pure white roll paper, neutral liners, rust-proof liners and metal interleaving paper, kraft paper, neutral printing and writing paper, neutral coated base paper, neutral PPC paper, neutral heat-sensitive paper, neutral pressure-sensitive base paper, neutral inkjet paper and neutral information paper, molded paper (molded containers), etc., and suitable examples include food packaging materials and food containers.

[0254] Substrates to be treated with the water and oil repellent of the present disclosure are not limited to textile products or paper products, but also include stone, filters (e.g., electrostatic filters), dust masks, fuel cell components (e.g., gas diffusion electrodes and gas diffusion supports), glass, wood, leather, fur, asbestos, bricks, cement, metals and oxides, ceramic products, plastics, painted surfaces, and plaster.

[0255] When the substrate is glass, the glass product to be manufactured may be an optical member. The surface (outermost layer) of the glass substrate may have some layer (or film), such as a hard coat layer or an anti-reflection layer. The anti-reflection layer may be either a single-layer anti-reflection layer or a multi-layer anti-reflection layer. Examples of inorganic substances that can be used for the anti-reflection layer include SiO2, SiO, ZrO2, TiO2, TiO, Ti2O3, Ti2O5, Al2O3, Ta2O5, CeO2, MgO, Y2O3, SnO2, MgF2, WO3, etc. These inorganic substances may be used alone or in combination of two or more of them (for example, as a mixture). When a multi-layer anti-reflection layer is used, it is preferable to use SiO2 and / or SiO for the outermost layer. When the product to be manufactured is an optical glass part for a touch panel, a transparent electrode, such as a thin film using indium tin oxide (ITO) or indium zinc oxide, may be provided on a part of the surface of the substrate (glass). In addition, the substrate may have an insulating layer, an adhesive layer, a protective layer, a decorative frame layer (I-CON), an atomizing film layer, a hard coating film layer, a polarizing film, a phase difference film, and a liquid crystal display module, etc., depending on its specific specifications, etc.

[0256] [Processing method] The water- and oil-repellent agent of the present disclosure can be applied to a substrate as a treatment agent (particularly a surface treatment agent) by a conventionally known method. The treatment method may be a method in which the water- and oil-repellent agent of the present disclosure is dispersed and diluted in an organic solvent or water as necessary, and attached to the inside and / or surface of the substrate by a known method such as dip coating, spray coating, foam coating, etc., and then dried. After drying, a product is obtained to which the solid components of the water- and oil-repellent agent are attached. If necessary, it may be applied together with a suitable crosslinking agent and cured. The water- and oil-repellent agent of the present disclosure may be used in combination with various additives such as water- and / or oil-repellent agents, slip prevention agents, antistatic agents, texture adjusters, softeners, antibacterial agents, flame retardants, paint fixing agents, anti-wrinkle agents, drying speed adjusters, crosslinking agents, film-forming assistants, compatibilizers, antifreeze agents, viscosity adjusters, ultraviolet absorbers, antioxidants, pH adjusters, insect repellents, and defoamers. Examples of various additives may be the same as those described above in "other components". The concentration of the water / oil repellent in the treatment agent to be contacted with the substrate may be changed appropriately depending on the application, but may be 0.01 to 10% by weight, for example, 0.05 to 5% by weight.

[0257] The water- and oil-repellent agent can be applied to the substrate by any of the methods known for treating substrates with liquids. The substrate may be immersed in the water- and oil-repellent agent, or the solution may be applied or sprayed onto the substrate. The treated substrate is preferably dried and cured by heating to develop liquid repellency. The heating temperature may be, for example, 100°C to 200°C, 100°C to 170°C, or 100°C to 120°C. In the present disclosure, good performance can be obtained even with low-temperature heating (for example, 100°C to 140°C). In the present disclosure, the heating time may be 5 seconds to 60 minutes, for example, 30 seconds to 3 minutes. When the substrate is paper, the agent may be coated on the paper, or the solution may be applied or sprayed onto the paper, or the agent may be mixed with the pulp slurry before papermaking and treated. The treatment may be an external addition treatment or an internal addition treatment. Alternatively, the water- and oil-repellent agent may be applied to the textile product by a cleaning method, for example, by washing application or dry cleaning method.

[0258] [Processing of paper products] Examples of the paper substrate include paper, paper containers, paper molded articles (e.g., pulp molds), etc. The fluorine-containing polymer of the present disclosure adheres well to the paper substrate.

[0259] The paper can be produced by a conventional papermaking method, for example, an internal treatment method in which the water- and oil-repellent agent is added to the pulp slurry before papermaking, or an external treatment method in which the water- and oil-repellent agent is applied to the paper after papermaking.

[0260] The size press for external additive treatment can be divided into the following types according to the coating method: One application method is a so-called pond-type two-roll size press, in which a coating liquid (size liquid) is supplied to a nip formed by passing paper between two rubber rolls, a coating liquid pool called a pond is created, and the paper is passed through this coating liquid pool to apply the size liquid to both sides of the paper. Other application methods are a gate roll type in which the size liquid is applied by a surface transfer type, and a rod metering size press. In a pond-type two-roll size press, the size liquid is likely to penetrate into the inside of the paper, and in a surface transfer type, the size liquid component is likely to remain on the surface of the paper. In the surface transfer type, the coating layer is more likely to remain on the surface of the paper than in a pond-type two-roll size press, and the coating layer formed on the surface is larger than in a pond-type two-roll size press. In the present disclosure, performance can be imparted to the paper even when the former pond-type two-roll size press is used. The paper thus treated can exhibit excellent oil resistance, water resistance, etc. by optionally accompanying a heat treatment that can take a temperature range of up to 300°C, for example up to 200°C, particularly 80°C to 180°C, depending on the properties of the paper, after simple drying at room temperature or high temperature.

[0261] The internal addition treatment method may mean a treatment method of adding a water- and oil-repellent agent to a pulp slurry before papermaking. The internal addition treatment method may include, but is not limited to, one or more of the following steps: adding a water- and oil-repellent agent to a pulp slurry and stirring and mixing it; suctioning and dehydrating the pulp composition prepared in the above step through a mesh body of a predetermined shape to deposit the pulp composition to form a pulp mold intermediate; and molding and drying the pulp mold intermediate with a heated mold to obtain paper, a paper container, or a paper molded product. The treated paper may be heat-treated, depending on the properties of the paper, after simple drying at room temperature or at a high temperature. The temperature of the heat treatment may be 150°C or higher, 180°C or higher, or 210°C or higher, and may be 300°C or lower, 250°C or lower, or 200°C or lower, and may be particularly 80°C to 180°C. By performing heat treatment in such a temperature range, excellent oil resistance and water resistance can be exhibited.

[0262] The present disclosure can be used in gypsum board base paper, coated base paper, medium quality paper, general liners and cores, neutral pure white roll paper, neutral liners, rust-proof liners and metal interleaving paper, kraft paper, etc. It can also be used in neutral printing and writing paper, neutral coated base paper, neutral PPC paper, neutral thermal paper, neutral pressure-sensitive base paper, neutral inkjet paper, and neutral information paper.

[0263] Pulp raw materials include bleached or unbleached chemical pulp such as kraft pulp or sulfite pulp, groundwood pulp, mechanical pulp, or thermomechanical pulp. Any of bleached or unbleached high-yield pulp, recycled newspaper, magazine, corrugated cardboard, deinked recycled paper, etc. may be used. Mixtures of the above pulp raw materials with synthetic fibers such as asbestos, polyamide, polyimide, polyester, polyolefin, polyvinyl alcohol, etc. may also be used.

[0264] The water resistance of paper can be improved by adding a sizing agent. Examples of the sizing agent include cationic sizing agents, anionic sizing agents, and rosin-based sizing agents (e.g., acidic rosin-based sizing agents, neutral rosin-based sizing agents). The amount of the sizing agent may be 0.01 to 5% by weight based on the pulp.

[0265] If necessary, the paper may contain additives used in the manufacture of paper, such as paper strength enhancers such as starch, modified starch, carboxymethyl cellulose, and polyamide polyamine-epichlorohydrin resin, flocculants, fixing agents, retention improvers, dyes, fluorescent dyes, slime control agents, and defoamers, to the extent that they are commonly used. Starch and modified starch are preferably used. If necessary, water and oil repellents can be applied to the paper using starch, polyvinyl alcohol, dyes, coating colors, anti-slip agents, etc., using a size press, gate roll coater, bill blade coater, calendar, etc.

[0266] In the case of external addition, the amount of the fluorine-containing polymer contained in the coating layer is 0.01 to 2.0 g / m 2 , especially 0.1 to 1.0 g / m 2 The coating layer is preferably formed from a water / oil repellent and starch and / or modified starch. The solid content of the water / oil repellent for paper in the coating layer is preferably 2 g / m 2 It is preferable that: In the case of internal addition, it is preferable to mix the water / oil repellent with the pulp so that the amount of the water / oil repellent is 0.01 to 50 parts by weight or 0.01 to 30 parts by weight, for example 0.01 to 10 parts by weight, and particularly 0.2 to 5.0 parts by weight, per 100 parts by weight of the pulp forming the paper.

[0267] In the case of external addition, oil resistance can also be imparted to paper by using a so-called pond-type two-roll size press process in which the treatment solution is pooled between rolls and the base paper is passed through the treatment solution between the rolls at any roll speed and nip pressure.

[0268] In the external addition treatment, the paper substrate may contain additives such as sizing agents, paper strength agents, flocculants, retention agents, or coagulants. The additives may be nonionic, cationic, anionic, or amphoteric. The ionic charge density of the additives may be -10000 to 10000 μeq / g, preferably -4000 to 8000 μeq / g, and more preferably -1000 to 7000 μeq / g. The additives (e.g., sizing agents, paper strength agents, flocculants, retention agents, or coagulants, etc., such as solids or active ingredients) can generally be used in an amount of 0.1 to 10% by weight (e.g., 0.2 to 5.0% by weight) based on the pulp. In the case of a paper substrate containing a cationic additive (e.g., sizing agents, paper strength agents, flocculants, retention agents, or coagulants), the water and oil repellent may be anionic, and in the case of a paper substrate containing an anionic additive, the water and oil repellent may be cationic, but is not limited thereto.

[0269] In the internal addition treatment, it is preferable to make a pulp slurry having a pulp concentration of 0.5 to 5.0% by weight (for example, 2.5 to 4.0% by weight). Additives (for example, sizing agents, paper strength agents, flocculants, retention agents, coagulants, etc.) and fluorine-containing compounds can be added to the pulp slurry. Examples of additives (e.g., sizing agents, paper strength agents, flocculants, retention agents or coagulants) are alkylketene dimers, alkenyl succinic anhydrides, styrene polymers (styrene / maleic acid polymers, styrene / acrylic acid polymers), urea-formaldehyde polymers, polyethyleneimine, melamine-formaldehyde polymers, polyamidoamine-epichlorohydrin polymers, polyacrylamide polymers, polyamine polymers, polydiallyldimethylammonium chloride, alkylamine-epichlorohydrin condensates, condensates of alkylene dichlorides and polyalkylenepolyamines, dicyandiamide-formaldehyde condensates, dimethyldiallylammonium chloride polymers, and olefin / maleic anhydride polymers.

[0270] In the internal addition treatment, the paper substrate may contain additives such as sizing agents, paper strength agents, flocculants, retention agents, or coagulants. The additives may be nonionic, cationic, anionic, or amphoteric. The ionic charge density of the additives may be -10000 to 10000 μeq / g, preferably -4000 to 8000 μeq / g, and more preferably -1000 to 7000 μeq / g. The additives (e.g., sizing agents, paper strength agents, flocculants, retention agents, or coagulants, etc., e.g., solids or active ingredients) can generally be used in an amount of 0.1 to 10% by weight (e.g., 0.2 to 5.0% by weight) based on the pulp. In the case of a paper substrate containing a cationic additive (e.g., sizing agents, paper strength agents, flocculants, retention agents, or coagulants), the water and oil repellent may be anionic, and in the case of a paper substrate containing an anionic additive, the water and oil repellent may be cationic, but is not limited thereto.

[0271] The oil resistance (KIT method) of treated paper products can be measured according to TAPPI T-559cm-02. Here, the paper products may be products that have been treated with external additives. The KIT test liquid is a test liquid made by mixing castor oil, toluene, and heptane in the ratios shown in the table below. A drop of the test liquid shown in the table is placed on the paper, and the state of oil penetration is observed after 15 seconds. The highest oil resistance score given by the KIT test liquid that shows no penetration is regarded as the oil resistance. The higher the number of the KIT test liquid, the higher the oil resistance. JPEG0007633577000014.jpg78133

[0272] The high-temperature oil resistance of the treated paper product can be measured as follows. Here, the paper product may be an internally treated product. 100 ml of corn oil at 65°C is poured into a pulp-molded product formed on a container, and after leaving it for 30 minutes, the corn oil is removed and the degree of oil penetration into the pulp mold is evaluated according to the following criteria. 4: Almost no oil stains are visible on the inside of the bottom of the container. 3: No oil stains on the outside of the container bottom 2: Oil stains are visible on less than 5% of the outer area of ​​the container bottom 1: Oil stains are visible on 5% to less than 50% of the outer area of ​​the container bottom 0: Oil stains are visible on more than 5% of the outer area of ​​the container bottom

[0273] The high-temperature water resistance of the treated paper product can be measured as follows. Here, the paper product may be an internally treated product. 100 ml of 80°C hot water is poured into a pulp molded product formed on a container, and after leaving it for 30 minutes, the hot water is removed and the degree of oil penetration into the pulp mold is evaluated according to the following criteria. 4: Almost no oil stains are visible on the inside of the bottom of the container. 3: No oil stains on the outside of the container bottom 2: Oil stains are visible on less than 5% of the outer area of ​​the container bottom 1: Oil stains are visible on 5% to less than 50% of the outer area of ​​the container bottom 0: Oil stains are visible on more than 5% of the outer area of ​​the container bottom

[0274] [Pretreatment of textile products] The textile product may be pretreated before being treated with the water / oil repellent of the present disclosure. By pretreating the textile product, excellent fastness can be imparted to the textile product after treatment with the water / oil repellent.

[0275] Examples of pretreatments of textile products include cationization treatment by reaction with a reactive quaternary ammonium salt, anionization treatment such as sulfonation, carboxylation, and phosphation, and acetylation treatment, benzoylation treatment, carboxymethylation treatment, grafting treatment, tannic acid treatment, and polymer coating treatment after anionization treatment.

[0276] The method for pretreating a textile product is not limited, and the textile product can be pretreated by a conventionally known method. The pretreatment liquid may be dispersed and diluted in an organic solvent or water as necessary, and applied to the inside and / or surface of the textile product by a known method such as dip coating, spray coating, foam coating, etc., and then dried. The pH and temperature of the pretreatment liquid may be adjusted depending on the desired degree of treatment. As an example of the method for pretreating a textile product, a method for pretreating a textile product with the above-mentioned treatment agent will be described in detail.

[0277] The pretreatment method for textile products is to add -SO3M to the fibers. 1 (In the formula, M 1 represents a monovalent cation), -COOM 2 (In the formula, M 2 represents a monovalent cation), and -OP(O)(OX 1 )(OX 2 )(wherein, X 1 and X 2 each independently represents a hydrogen atom or an alkyl group having 1 to 22 carbon atoms) (hereinafter, also referred to as "specific functional groups").

[0278] M 1 Examples of M include H, K, Na, and ammonium ion which may have a substituent. 2 Examples of X include H, K, Na, and ammonium ion which may have a substituent. 1 Or X 2 When is an alkyl group, it is preferably an alkyl group having 1 to 22 carbon atoms, and more preferably an alkyl group having 4 to 12 carbon atoms.

[0279] The fibers containing the specific functional groups (hereinafter, sometimes referred to as "functional group-containing fibers") can be prepared, for example, by the following method. (i) A compound having the specific functional group is attached to a fiber material. The attachment of the compound may be in a state where a part of the compound is chemically bonded to a part of the fiber to the extent that a sufficient amount of the specific functional group remains. (ii) A fiber is prepared in which the specific functional group is directly introduced into the material constituting the fiber.

[0280] In the case of (i), for example, a functional group-containing fiber can be obtained by a functional group introduction step in which a fiber material is treated with a pretreatment liquid containing one or more compounds having the specific functional group.

[0281] The material of the fiber material is not particularly limited, and examples thereof include natural fibers such as cotton, hemp, silk, wool, etc., semi-synthetic fibers such as rayon, acetate, etc., synthetic fibers such as polyamide (nylon, etc.), polyester, polyurethane, polypropylene, etc., and composite fibers, blended fibers, etc. The form of the fiber material may be any of fibers (tow, sliver, etc.), yarn, knitted fabric (including interwoven fabric), woven fabric (including interwoven fabric), nonwoven fabric, etc.

[0282] In this embodiment, from the viewpoint of improving the water repellency of the obtained textile product, it is preferable to use textile materials containing polyamide and polyester as raw materials, and in particular, it is preferable to use nylons such as nylon 6 and nylon 6,6, polyesters such as polyethylene terephthalate (PET), polytrimethyl terephthalate, and polylactic acid, and mixed fibers containing these.

[0283] Above -SO3M 1 As the compound having the formula (I), a phenol-based polymer can be used. As such a phenol-based polymer, for example, one containing at least one compound represented by the following general formula can be mentioned.

[0284] JPEG0007633577000015.jpg4678 [where, X 2 Ha-SO3M 3 (In the formula, M 3 represents a monovalent cation) or a group represented by the following general formula, and n is an integer of 20 to 3000.

[0285] JPEG0007633577000016.jpg2661 [In the formula, M 4 represents a monovalent cation.

[0286] The above M 3 Examples of the cation include H, K, Na, and ammonium ion which may have a substituent.

[0287] The above M 4Examples of the cation include H, K, Na, and ammonium ion which may have a substituent.

[0288] The compound represented by the above general formula may be, for example, a formalin condensate of phenolsulfonic acid or a formalin condensate of sulfonated bisphenol S.

[0289] Above - COOM 2 Examples of compounds having the formula include polycarboxylic acid polymers.

[0290] As the polycarboxylic acid polymer, for example, a polymer synthesized by a conventionally known radical polymerization method using acrylic acid, methacrylic acid, maleic acid, or the like as a monomer, or a commercially available product can be used.

[0291] Examples of the method for producing a polycarboxylic acid polymer include a method in which a radical polymerization initiator is added to an aqueous solution of the above-mentioned monomer and / or its salt, and the mixture is heated and reacted at 30 to 150° C. for 2 to 5 hours. At this time, an alcohol such as methanol, ethanol, isopropyl alcohol, or an aqueous solvent such as acetone may be added to the aqueous solution of the above-mentioned monomer and / or its salt. Examples of the radical polymerization initiator include persulfates such as potassium persulfate, sodium persulfate, and ammonium persulfate, redox-based polymerization initiators such as combinations of persulfates and sodium bisulfite, hydrogen peroxide, and water-soluble azo-based polymerization initiators. These radical polymerization initiators may be used alone or in combination of two or more. Furthermore, during radical polymerization, a chain transfer agent (e.g., octyl thioglycolate) may be added for the purpose of adjusting the degree of polymerization.

[0292] In addition to the above monomers, copolymerizable monomers can be used in the radical polymerization. Examples of the copolymerizable monomers include vinyl monomers such as ethylene, vinyl chloride, and vinyl acetate, acrylamide, acrylates, and methacrylates. The acrylates and methacrylates are preferably those having a hydrocarbon group having 1 to 3 carbon atoms which may have a substituent such as a hydroxyl group. Examples of such acrylates or methacrylates include methyl acrylate, methyl methacrylate, ethyl acrylate, ethyl methacrylate, 2-hydroxyethyl acrylate, 2-hydroxyethyl methacrylate, propyl acrylate, and propyl methacrylate. These copolymerizable monomers may be used alone or in combination of two or more.

[0293] The carboxyl group in the polycarboxylic acid polymer may be free or may be neutralized with an alkali metal, an amine compound, etc. Examples of the alkali metal include sodium, potassium, and lithium, and examples of the amine compound include ammonia, monoethanolamine, diethanolamine, and triethanolamine.

[0294] The weight average molecular weight of the polycarboxylic acid polymer is preferably from 1,000 to 20,000, and more preferably from 3,000 to 15,000, from the viewpoint of improving the water repellency of the resulting textile product.

[0295] As the polycarboxylic acid polymer, commercially available products such as "Neocrystal 770" (product name, manufactured by Nicca Chemical Co., Ltd.) and "Ceropol PC-300" (product name, manufactured by Sanyo Chemical Industries, Ltd.) can be used.

[0296] Above -OP(O)(OX 1 )(OX 2 ) is exemplified by a phosphate ester compound represented by the following general formula: JPEG0007633577000017.jpg3243[where, X 1 Or X 2 is the same as above, and X3 represents an alkyl group having 1 to 22 carbon atoms.

[0297] As the phosphate ester compound, phosphate monoesters, diesters and triesters, in which the alkyl ester moiety is an alkyl group having 1 to 22 carbon atoms, and mixtures thereof can be used.

[0298] From the viewpoint of improving the water repellency of the resulting textile product, it is preferable to use lauryl phosphate and decyl phosphate.

[0299] As the phosphate ester compound, for example, a commercially available product such as "Phosphanol ML-200" (product name, manufactured by Toho Chemical Industry Co., Ltd.) can be used.

[0300] The pretreatment liquid containing one or more compounds having the specific functional group may be, for example, an aqueous solution of the above-mentioned compounds. The pretreatment liquid may also contain an acid, an alkali, a surfactant, a chelating agent, etc.

[0301] Examples of the method for treating the textile material with the pretreatment liquid include padding, immersion, spraying, and coating. Examples of padding include a method using a padding device described on pages 396-397 of Textile Dyeing and Processing Dictionary (published by Nikkan Kogyo Shimbun, 1963) and pages 256-260 of Color Dyeing Chemistry III (published by Jikkyo Publishing Co., Ltd., 1975). Examples of coating include a method using a coating machine described on pages 473-477 of Dyeing and Finishing Equipment Directory (published by Sen-sha, 1981). Examples of immersion include a method using a batch-type dyeing machine described on pages 196-247 of Dyeing and Finishing Equipment Directory (published by Sen-sha, 1981), and a liquid flow dyeing machine, air flow dyeing machine, drum dyeing machine, winch dyeing machine, washer dyeing machine, cheese dyeing machine, etc. can be used. Examples of the spray treatment include an air spray in which the treatment liquid is sprayed in the form of a mist using compressed air, and a method using an air spray of a liquid pressure atomization type. The treatment conditions, such as the concentration of the treatment liquid and the heat treatment after application, can be appropriately adjusted in consideration of various conditions such as the purpose and performance. In addition, when the pretreatment liquid contains water, it is preferable to dry the pretreatment liquid after it is applied to the fiber material in order to remove the water. There is no particular limit to the drying method, and either a dry heat method or a wet heat method may be used. There is also no particular limit to the drying temperature, and for example, drying may be performed at room temperature to 200°C for 10 seconds to several days. If necessary, heat treatment may be performed at a temperature of 100 to 180°C for about 10 seconds to 5 minutes after drying.

[0302] When the textile material is to be dyed, the treatment with the pretreatment liquid may be carried out before dyeing or in the same bath as the dyeing. However, when reduction soaping is carried out, there is a risk that the compound having the specific functional group (e.g., a phenolic polymer compound, etc.) adsorbed during the process may fall off, so it is preferable to carry out the treatment after reduction soaping after dyeing.

[0303] The treatment temperature in the immersion treatment can be 60 to 130° C. The treatment time can be 5 to 60 minutes.

[0304] In the functional group introduction step using a pretreatment liquid, the amount of the compound having the specific functional group attached is preferably 1.0 to 7.0 parts by weight per 100 parts by weight of the textile material. Within this range, durable water repellency and texture can be simultaneously achieved at high levels.

[0305] The pH of the pretreatment liquid may be adjusted to less than 7, for example, to a range of 3 to 5. The pH can be adjusted using a pH adjuster such as acetic acid or malic acid.

[0306] In the pretreatment solution, a salt may be used in combination in order to effectively adsorb the compound having the specific functional group to the fiber material by the salting-out effect. Examples of the salt that can be used include sodium chloride. Examples of suitable salts include sodium carbonate, ammonium sulfate, and sodium sulfate.

[0307] In the functional group introduction step using the pretreatment liquid, it is preferable to remove the compound having the specific functional group that has been treated in excess. An example of a removal method is washing with water. By removing the compound sufficiently, it is possible to prevent the development of water repellency in the subsequent water repellent treatment from being hindered, and in addition, the texture of the obtained textile product is improved. In addition, it is preferable to thoroughly dry the obtained functional group-containing fiber before contacting it with the above-mentioned treatment agent.

[0308] (ii) An example of a fiber in which the specific functional group is directly introduced into the material constituting the fiber is cationic dyeable polyester (CD-PET).

[0309] From the viewpoint of improving the water repellency of the resulting textile product, the functional group-containing fiber preferably has a surface zeta potential of −100 to −0.1 mV, more preferably −50 to −1 mV. The zeta potential of the fiber surface can be measured, for example, by a zeta potential / particle size measuring system ELSZ-1000ZS (manufactured by Otsuka Electronics Co., Ltd.).

[0310] Although the embodiments have been described above, it will be understood that various changes in form and details are possible without departing from the spirit and scope of the claims. EXAMPLES

[0311] The present disclosure will be described in detail below with reference to examples, but the present disclosure is not limited to these examples.

[0312] <Manufacturing method> [Synthesis Example 1] Put 7.0g of 4-trifluoromethoxyaniline, 4.0g of triethylamine, and 35ml of THF into a 100ml three-neck flask equipped with a stirrer, an inert gas inlet, a reflux condenser, and a thermometer, place it in an ice bath, and stir. Then, insert a 50ml dropping funnel containing 4.2g of acrylic acid chloride and 15ml of THF into the flask, and drop the solution in the dropping funnel at a rate of one drop every 5 seconds to start the reaction. After the drop is complete, remove the ice bath, place a water bath, and react at 40℃ for 3 hours. After the reaction was completed, 40 mL of water and 20 mL of ethyl acetate were added, and the organic layer was extracted using a separatory funnel. The extracted organic layer was dried over magnesium sulfate, and then the solvent was distilled off to obtain 7.5 g (yield 82%) of Monomer 1 as a white solid.

[0313] [Synthesis Example 2] Monomer 2 was obtained as a pale yellow solid (7.2 g, yield 72%) in the same manner as in the synthesis of Monomer 1, except that 7.0 g of 4-trifluoromethoxyaniline was replaced with 7.0 g of 4-methoxyaniline.

[0314] [Production Example 1] The mixture obtained in Synthesis Example 1 was placed in a 200 ml four-neck flask equipped with a stirrer, an inert gas inlet, a reflux condenser, and a thermometer. Monomer 1 10g, Stearamidoethyl acrylate 5g, Stearyl acrylate 4.5g, 2,3-dihydroxypropyl methacrylate 0.5g, Toluene 21g, Lauryl mercaptan 0.02g, Toluene 2g After replacing the atmosphere with nitrogen, a polymerization reaction was carried out at 70° C. for 12 hours or more with stirring to obtain a toluene solution of a polymer.

[0315] [Comparative Manufacturing Example 1] The same procedure as in Production Example 1 was repeated, except that 10 g of Monomer 1 was used instead of 7.7 g of Monomer 2.

[0316] [Production Example 2] In a 500ml plastic container 10 g of Monomer 1 obtained in Synthesis Example 1, Stearyl acrylate 14.5g Isobornyl methacrylate 5.0g Diacetone acrylamide 0.5g, Tripropylene glycol 8.5g, Stearyl trimethyl ammonium chloride 1g, Sorbitan Monostearate 0.5g, Polyoxyethylene lauryl ether (EO:21. EO represents the number of ethylene oxide units) 1.25 g, Pure water 114g, The mixture was heated to 80°C, stirred at 2000 rpm for 1 minute with a homomixer, and then emulsified and dispersed with ultrasonic waves for 15 minutes. The emulsified dispersion was transferred to a 500 ml four-neck flask equipped with a nitrogen inlet tube, thermometer, stirring rod, and reflux tube, and after replacing with nitrogen, 9 g of an aqueous solution containing 0.05 g of lauryl mercaptan and 1.25 g of 2,2-azobis(2-amidinopropane) dihydrochloride was added and reacted at 60°C for 5 hours to obtain an aqueous dispersion of a polymer.

[0317] [Comparative Manufacturing Example 2] The same procedure as in Production Example 2 was repeated, except that 10 g of Monomer 1 was used instead of 7.7 g of Monomer 2.

[0318] <Processing solution preparation method> [Solvent-based] The solution prepared in Production Example 1 was diluted with toluene to prepare 200 g of each of treatment solutions 1 and 2 so that the solid content concentrations were 1.0 and 2.0%. Furthermore, the solution prepared in Comparative Production Example 1 was diluted with toluene to prepare 200 g each of Treatment Solutions 3 and 4 so that the solid content concentrations were 1.0 and 2.0%. [Water system] The solution prepared in Production Example 2 was diluted with water to prepare 200 g of each of Treatment Solutions 5 and 6 so that the solid content concentrations were 1.0 and 2.0%. Furthermore, the solution prepared in Comparative Production Example 2 was diluted with water to prepare 200 g each of Treatment Solutions 7 and 8 so as to have solid concentrations of 1.0 and 2.0%. A list of the treatment solutions is shown in Table 1.

[0319] <Evaluation of treated fabric> [Method of treatment for fabric] Two types of fabric were used: nylon fabric and PET fabric. [Solvent-based] The two types of fabrics were placed in a 500ml plastic bottle containing 200g of the prepared treatment solution, and the plastic bottle was shaken for 10 seconds to allow the treatment solution to adhere to the fabric. After removing the fabric from the treatment solution, the fabric was placed in a centrifuge and spun at 1000rpm for 30 seconds. The fabric was then dried at room temperature for 24 hours and then heated at 160℃ for 2 minutes. [Water-based] Two types of fabric were immersed in the treatment solution, passed through a mangle, and heat-treated at 160°C for 2 minutes to obtain aqueous test fabrics. [Water repellency test] The water repellency of the treated fabrics was evaluated by visually evaluating the wet state according to the spray method of JIS-L-1092 (AATCC-22) based on the following criteria. The evaluation results are expressed by a water repellency number as shown in the table below. The higher the score, the better the water repellency. The results are shown in Table 2. ◎(100): No moisture or water droplets on the surface ○ (90): Does not wet the surface, but shows small water droplets adhering to it △(80): Shows wetting of small individual water droplets on the surface × (70 or less): More than half of the surface is wet, and partial penetration is observed [Oil repellency test] A drop of a 10 / 90 IPA / water solution was placed on the treated fabric, and the condition after 30 seconds was visually evaluated according to the following criteria. The results are shown in Table 3. ◎: The droplets do not soak in and maintain their round shape. ○: The droplets are barely absorbed and are maintained. △: Some of the droplets have soaked in, but the droplets remain. ×: The droplet has completely soaked in and the stain has spread

[0320] <Evaluation of treated paper> [Preparation of treated paper] Water resistance (Cobb value) 52g / m 2 , basis weight 45g / m 2 , density 0.60g / m 3 Treatment solutions 1 to 8 were applied three times to the thin paper using a Baker-type applicator with a gap set to 0 mil, and then annealed at 140° C. for 1 minute to create treated paper. [KIT test (oil resistance)] Measurements were made using the 3M Kit Test (TAPPI T-559cm-02). The 3M Kit Test method involves placing a test oil containing a mixture of castor oil, toluene, and heptane on the surface of treated paper, wiping the test oil off after 15 seconds, and evaluating the presence or absence of oil stains on the treated paper. Tests were conducted using test oils with kit numbers 1 to 6, and the highest kit number that showed no stains was used as the evaluation result for oil resistance. The evaluation results are shown in Table 4.

[0321] Table 1: List of processing fluids TIFF0007633577000018.tif56155

[0322] Table 2: Water repellency evaluation of treated fabrics TIFF0007633577000019.tif39155

[0323] Table 3: Oil repellency evaluation of treated fabrics TIFF0007633577000020.tif39155

[0324] Table 4: Oil resistance evaluation of treated paper TIFF0007633577000021.tif64155

Claims

1. Formula: CH 2 =C(-X f )-Y f -Z f α wherein each symbol represents independently at each occurrence: X f is a hydrogen atom, a monovalent organic group, or a halogen atom; Y f is a 1+α-valent group consisting of one or more selected from the group consisting of Y f1 and Y f2 , provided that it contains at least one Y f2 ; Y f1 is a group consisting of one or more groups selected from the group consisting of a direct bond, -O-, -C(=O)-, -C(=NR')-, -S-, -S(=O) 2 -, -NR'-, -C(OR')R'-, -C(OR')(-) 2 and -N(-) 2 (R' is a hydrogen atom or a monovalent organic group); Y f2 is a group composed of one or more selected from the group consisting of di- to tetravalent aliphatic hydrocarbon groups having 1 to 20 carbon atoms, di- to tetravalent hydrocarbon aromatic rings which may have a substituent, and di- to tetravalent heterocycles which may have a substituent; Z f is R f1 , or a hydrocarbon group containing R f1 or R f2 and having 2 to 40 carbon atoms; α is 1 to 3. A fluorine-containing polymer having a repeating unit derived from a fluorine-containing monomer (f) represented by the following formula: R ｆ１ Ha-CF ３ , -CF ２ H, or -CFH ２ and R ｆ２ Ha-CF ２ - or -CFH-, R ｆ１ and R ｆ２ is a fluoroalkyl group having 2 or more carbon atoms and -CH ２ -CF ２ -CH ２ - A water and oil repellent agent containing a fluorine-containing polymer that is not a part of the above.

2. The R ｆ１ is an oxygen atom or a nitrogen atom; The R ｆ２ The water / oil repellent according to claim 1 , wherein at least one of the adjacent positions is an oxygen atom or a nitrogen atom.

3. The R ｆ１ is CF ３ - and The R ｆ２ Ha-CF ２ - is, The water and oil repellent according to claim 1 or 2.

4. 3. The water / oil repellent according to claim 1 or 2, wherein the fluorine-containing monomer (f) is an acrylic monomer or an allyl monomer.

5. The fluorine-containing monomer (f) is R ｆ１ , or R ｆ１ Or R ｆ２ The water / oil repellent according to claim 1 or 2, which comprises a hydrocarbon group having 2 to 40 carbon atoms, comprising:

6. The water / oil repellent according to claim 1 or 2, which does not have a fluoroalkyl group having two or more carbon atoms.

7. The water / oil repellent according to claim 1, wherein Y f2 is a hydrocarbon group. The water and oil repellent according to claim 1 or 2.

8. Z ｆ R ｆ１ The water / oil repellent according to claim 7,

9. The fluorine-containing monomer (f) is represented by the formula: CH 2 =C(-X ｆ )-C(=O)-Y ｆ１１ -(Y ｆ２１ -Y ｆ１２ ) β -Y ｆ２２ -Y ｆ１３ -Z ｆ 、or CH 2 (-X) ｆ )-CH ２ -Y ｆ１１ -(Y ｆ２１ -Y ｆ１２ ) β -Y ｆ２２ -Y ｆ１３ -Z ｆ wherein each symbol represents independently at each occurrence: X ｆ is a hydrogen atom, a monovalent organic group, or a halogen atom, Y ｆ１１ is —O— or —NH—, Y ｆ２１ is a group consisting of one or more groups selected from the group consisting of aliphatic groups and aromatic groups, Y ｆ１２ are -O-, -C(=O)-, -C(=NR')-, -S-, -S(=O) ２ A group consisting of one or more selected from the group consisting of -, -NR'-, and -C(OR')R'- (R' is a hydrogen atom or a monovalent organic group); β is 0 to 3; Y ｆ２２ is a group consisting of one or more groups selected from the group consisting of aliphatic groups and aromatic groups, Y ｆ１３ is -O-, -OC(=O)-O-, -OC(=O)-NR'-, -NR'-, -NR'-C(=O)-O-, -NR'-C(=O)-NR'-, -C(=O)-O-, -C(=O)-NR'-, or -SO ２ NR'- (R' is a hydrogen atom or a monovalent organic group). Z ｆ is R ｆ１ , or R ｆ１ Or R ｆ２ is a hydrocarbon group having 2 to 40 carbon atoms. The water / oil repellent according to claim 1 or 2, which is a compound represented by the following formula:

10. Y ｆ２２ is the formula -Y ｆ２２１ -Y ｆ２２２ - [In the formula, Y ｆ２２１ is a direct bond or a hydrocarbon group having 2 to 40 carbon atoms, Y ｆ２２２ is a direct bond or a phenyl group. is a group represented by Y ｆ１３ is -O- or -NR'- (R' is a hydrogen atom or a monovalent organic group), β is 0 or 1; Z ｆ is R ｆ１ The water / oil repellent according to claim 9 ,

11. A repeating unit derived from a monomer (a) having a hydrocarbon group having 6 to 40 carbon atoms, A repeating unit derived from a hydrophilic group-containing monomer (b), A repeating unit derived from an ionic group-containing monomer (c), Repeat units derived from halogenated olefin monomer (d), and Crosslinkable monomer (e) The water / oil repellent according to claim 1 or 2, comprising one or more of the following:

12. The fluorine-containing monomer (f) is represented by the formula: CH 2 (-X) ｆ )-C(=O)-Y ｆ１１ -(Y ｆ２１ -Y ｆ１２ ) β -Y ｆ２２ -Y ｆ１３ -Z ｆ wherein each symbol represents independently at each occurrence: X ｆ is a hydrogen atom, a monovalent organic group, or a halogen atom, Y ｆ１１ is —O— or —NH—, Y ｆ２１ is a group consisting of one or more groups selected from the group consisting of aliphatic groups and aromatic groups, Y ｆ１２ are -O-, -C(=O)-, -C(=NR')-, -S-, -S(=O) ２ A group consisting of one or more selected from the group consisting of -, -NR'-, and -C(OR')R'- (R' is a hydrogen atom or a monovalent organic group); β is 0 to 3; Y ｆ２２ is a group consisting of one or more groups selected from the group consisting of aliphatic groups and aromatic groups, Y ｆ１３ is -O-, -OC(=O)-O-, -OC(=O)-NR'-, -NR'-, -NR'-C(=O)-O-, -NR'-C(=O)-NR'-, -C(=O)-O-, -C(=O)-NR'-, or -SO ２ NR'- (R' is a hydrogen atom or a monovalent organic group). Z ｆ is -CF ３ It is.] A compound represented by the formula:

3. The water / oil repellent according to claim 1 or 2, wherein the fluorine-containing polymer has a repeating unit derived from a monomer (a) having a hydrocarbon group having from 6 to 40 carbon atoms.

13. The water / oil repellent according to claim 1 or 2, which is a dispersion containing a liquid medium.

14. The water- and oil-repellent agent according to claim 1 or 2, which is for use in textile products or paper products.

15. A method for producing a treated substrate, comprising treating the substrate with the water / oil repellent according to claim 1 or 2.

16. The method according to claim 15, wherein the substrate is a textile product or a paper product.

17. A product having the water / oil repellent according to claim 1 or 2 adhered thereto.