Non-aqueous electrolyte secondary battery

Abstract

The purpose of the present invention is to provide a non-aqueous electrolytic secondary battery in which electrical connection between an exposed surface of a negative current collector at the outermost periphery of an electrode assembly and the inner surface of an outer can is ensured. A non-aqueous electrolytic secondary battery according to an embodiment of the present disclosure is provided with a wound electrode assembly. A negative electrode (12) comprises a sheet-like negative current collector (40) having a negative electrode mixture layer (42) formed on a surface thereof, and includes a double-side coating portion in which the negative electrode mixture layer (42) is formed on both sides of the negative current collector (40), and a single-side coating portion in which the negative electrode mixture layer (42B) is formed on one side of the negative current collector. At least a part of the single-side coating portion is disposed at the outermost periphery of the electrode assembly. At least a part of an exposed surface of the negative current collector in the single-side coating portion is in contact with the inner surface of an outer can. The charge expansion ratio of the negative electrode mixture layer (42B) in the single-side coating portion is greater than the charge expansion ratio of the negative electrode mixture layer (42A) in the double-side coating portion.

Description

[Technical field]

[0001] The present disclosure relates to a non-aqueous electrolyte secondary battery. [Background technology]

[0002] Conventionally, nonaqueous electrolyte secondary batteries have been widely used in which a wound electrode body, in which a strip-shaped positive electrode and a strip-shaped negative electrode are wound with a separator interposed therebetween, is housed in an outer can. In such wound batteries, the electrodes (positive electrode and negative electrode) of the electrode body each have a composite layer containing an active material and a binder on both sides of a metal current collector, and the positive electrode and the negative electrode are wound with a separator interposed therebetween. In addition, a separator is usually disposed on the outermost periphery of the electrode body, the positive electrode is connected to a sealing body serving as a positive electrode side external terminal by a positive electrode lead, and the negative electrode is connected to an outer can serving as a negative electrode side external terminal by a negative electrode lead. In such a battery, the current from the strip-shaped negative electrode is concentrated in the negative electrode lead, so that the internal resistance is likely to be large.

[0003] Patent Document 1 discloses that a negative electrode is arranged on the outermost periphery of an electrode body, the negative electrode composite layer on the outer peripheral surface at this position is omitted, and the negative electrode current collector is exposed as a one-sided coated portion, and the negative electrode current collector is brought into direct contact with the inner surface of an outer can for electrical connection. [Prior art documents] [Patent documents]

[0004] [Patent Document 1] International Publication No. 2012 / 042830 Summary of the Invention [Problem to be solved by the invention]

[0005] Here, if the clearance between the electrode body and the inner surface of the outer can is narrowed in order to ensure that the exposed surface of the negative electrode current collector is in contact with the inner surface of the outer can, insertion failure is likely to occur during battery manufacturing, resulting in reduced productivity. In addition, since the negative electrode mixture layer expands during charging, it is possible to use this expansion during charging to strengthen the electrical connection between the negative electrode current collector and the inner surface of the outer can. However, with this method, the expansion and contraction of the negative electrode mixture layer due to charging and discharging becomes significant, and deterioration due to cycles is likely to increase, such as peeling between the active material and the current collector, or isolation of the active material that no longer contributes to charging and discharging.

[0006] The present disclosure provides a nonaqueous electrolyte secondary battery that sets a large charge expansion rate for a negative electrode composite layer in a single-sided coated portion, at least a portion of which is located on the outermost periphery, thereby suppressing defects during assembly and deterioration due to charge / discharge cycles, while ensuring electrical connection between the exposed surface of the negative electrode current collector on the outermost periphery of the electrode body and the inner surface of the outer casing can. [Means for solving the problem]

[0007] a negative electrode mixture layer formed on a surface of a sheet-shaped positive electrode current collector; a negative electrode mixture layer formed on a surface of a sheet-shaped negative electrode current collector; the negative electrode mixture layer including a chargeable and dischargeable negative electrode active material and a binder; the negative electrode includes a double-sided coated portion in which a negative electrode mixture layer is formed on both surfaces of the negative electrode current collector; and a single-sided coated portion in which a negative electrode mixture layer is formed on one surface of the negative electrode current collector; at least a portion of the single-sided coated portion is disposed on the outermost periphery of the electrode assembly; at least a portion of an exposed surface of the negative electrode current collector in the single-sided coated portion is in contact with an inner surface of the outer can; and a charging expansion coefficient of the negative electrode mixture layer in the single-sided coated portion is greater than a charging expansion coefficient of the negative electrode mixture layer in the double-sided coated portion. Effect of the Invention

[0008] The nonaqueous electrolyte secondary battery according to the present disclosure can ensure a clearance between the electrode body and the inner surface of the outer can during assembly and can reduce the charge expansion rate of the entire negative electrode mixture layer, thereby making it possible to achieve good electrical connection between the exposed surface of the negative electrode current collector and the inner surface of the outer can while suppressing the occurrence of defects during assembly and deterioration due to charge / discharge cycles. [Brief description of the drawings]

[0009] [Figure 1] FIG. 1 is an axial cross-sectional view of a cylindrical secondary battery as one example of the embodiment. [Diagram 2] FIG. 2 is a perspective view of a wound electrode body included in the secondary battery shown in FIG. [Diagram 3] FIG. 3 is a front view showing a positive electrode constituting an electrode assembly according to an embodiment in a developed state. [Figure 4A] FIG. 4A is a front view showing a negative electrode constituting an electrode assembly according to an embodiment in a developed state. [Figure 4B] FIG. 4B is a longitudinal cross-sectional view showing a negative electrode constituting an electrode assembly according to an embodiment in a developed state. [Diagram 5] FIG. 5 is a radial cross-sectional view (cross-sectional view seen from the axial direction) of a negative electrode in the vicinity of the outermost periphery of an electrode body according to one example of the embodiment. [Figure 6] FIG. 6 is a radial cross-sectional view (cross-sectional view seen from the axial direction) of a part in the vicinity of the outermost periphery of an electrode body according to one example of the embodiment. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0010] Hereinafter, an example of an embodiment of a cylindrical, wound nonaqueous electrolyte secondary battery according to the present disclosure will be described in detail with reference to the drawings. In the following description, specific shapes, materials, values, directions, etc. are examples for facilitating understanding of the present invention, and can be appropriately changed according to the specifications of the cylindrical secondary battery. In addition, in the following description, when multiple embodiments and modified examples are included, it is assumed from the beginning that the characteristic parts of these are appropriately combined and used.

[0011] "Overall Configuration" FIG. 1 is an axial cross-sectional view of a wound type secondary battery 10, which is an example of an embodiment. Although the secondary battery 10 shown in FIG. 1 has a cylindrical shape, it may have a square tube shape or the like as long as it is wound. In the secondary battery 10 shown in FIG. 1, an electrode body 14 and a non-aqueous electrolyte (not shown) are housed in an outer can 15. The electrode body 14 has a wound structure in which a positive electrode 11 and a negative electrode 12 are wound with a separator 13 interposed therebetween. As a non-aqueous solvent (organic solvent) for the non-aqueous electrolyte, carbonates, lactones, ethers, ketones, esters, etc. can be used, and two or more of these solvents can be mixed and used. When two or more solvents are mixed and used, it is preferable to use a mixed solvent containing a cyclic carbonate and a chain carbonate. For example, ethylene carbonate (EC), propylene carbonate (PC), butylene carbonate (BC), etc. can be used as the cyclic carbonate, and dimethyl carbonate (DMC), ethyl methyl carbonate (EMC), diethyl carbonate (DEC), etc. can be used as the chain carbonate. LiPF6, LiBF4, LiCF3SO3, etc., and mixtures thereof can be used as the electrolyte salt of the non-aqueous electrolyte. The amount of electrolyte salt dissolved in the non-aqueous solvent can be, for example, 0.5 to 2.0 mol / L. For convenience of explanation, the sealing body 16 side will be described as the "upper" and the bottom side of the exterior can 15 as the "lower".

[0012] The opening end of the outer can 15 is closed with the sealing body 16, so that the inside of the secondary battery 10 is sealed. Insulating plates 17, 18 are provided above and below the electrode body 14, respectively. The positive electrode lead 19 extends upward through the through hole of the insulating plate 17 and is welded to the underside of the filter 22, which is the bottom plate of the sealing body 16. In the secondary battery 10, the cap 26, which is the top plate of the sealing body 16 and is electrically connected to the filter 22, serves as the positive electrode terminal. On the other hand, the negative electrode lead 20 extends to the bottom side of the outer can 15 through the through hole of the insulating plate 18 and is welded to the inner side surface of the bottom of the outer can 15. In the secondary battery 10, the outer can 15 serves as the negative electrode terminal.

[0013] As described below, the negative electrode current collector 40 of the one-sided coated portion 46 (see Figures 4A and 4B) is exposed at the outermost periphery of the electrode body 14, and the exposed surface of this negative electrode current collector 40 contacts the inner surface of the outer can 15, electrically connecting the negative electrode 12 and the outer can 15.

[0014] The exterior can 15 is, for example, a metallic exterior can having a cylindrical shape with a bottom. A gasket 27 is provided between the exterior can 15 and the sealing body 16, which electrically insulates the exterior can 15 and the sealing body 16 and ensures the sealing of the inside of the secondary battery 10. The exterior can 15 has a grooved portion 21 that supports the sealing body 16 and is formed, for example, by pressing the side portion from the outside. The grooved portion 21 is preferably formed in an annular shape along the circumferential direction of the exterior can 15, and supports the sealing body 16 on its upper surface.

[0015] The sealing body 16 includes a filter 22, a lower valve body 23, an insulating member 24, an upper valve body 25, and a cap 26, which are stacked in this order from the electrode body 14 side. Each member constituting the sealing body 16 has, for example, a disk shape or a ring shape, and each member except the insulating member 24 is electrically connected to each other. The lower valve body 23 and the upper valve body 25 are connected to each other at their respective centers, and the insulating member 24 is interposed between their respective peripheral edges. When the internal pressure of the battery increases due to abnormal heat generation, for example, the lower valve body 23 breaks, which causes the upper valve body 25 to swell toward the cap 26 and move away from the lower valve body 23, thereby cutting off the electrical connection between them. When the internal pressure further increases, the upper valve body 25 breaks, and gas is discharged from the opening 26a of the cap 26.

[0016] "Electrode body configuration" Next, the electrode body 14 will be described with reference to FIG. 2. FIG. 2 is a perspective view of the electrode body 14. As described above, the electrode body 14 has a wound structure in which the positive electrode 11 and the negative electrode 12 are wound in a spiral shape with the separator 13 interposed therebetween. The positive electrode 11, the negative electrode 12, and the separator 13 are all formed in a strip shape, and are wound in a spiral shape around a winding core arranged along the winding axis 28, so that they are alternately stacked in the radial direction of the electrode body 14. In the radial direction, the winding axis 28 side is called the inner circumferential side, and the opposite side is called the outer circumferential side. In the electrode body 14, the longitudinal direction of the positive electrode 11 and the negative electrode 12 is the winding direction, and the strip width direction of the positive electrode 11 and the negative electrode 12 is the axial direction. The positive electrode lead 19 extends in the axial direction from approximately the center in the radial direction between the center and the outermost circumference at the upper end of the electrode body 14. Furthermore, the negative electrode lead 20 extends in the axial direction from the vicinity of the winding axis 28 at the lower end of the electrode body 14 .

[0017] A porous sheet having ion permeability and insulating properties is used for the separator 13. Specific examples of the porous sheet include a microporous thin film, a woven fabric, and a nonwoven fabric. The material of the separator 13 is preferably an olefin resin such as polyethylene or polypropylene. The thickness of the separator 13 is, for example, 10 μm to 50 μm. The separator 13 tends to be thinner as the capacity and output of the battery increase. The separator 13 has a melting point of, for example, about 130° C. to 180° C.

[0018] "Positive electrode composition" Next, FIG. 3 is a front view showing the positive electrode 11 constituting the electrode body 14 in an expanded state.

[0019] The positive electrode 11 has a strip-shaped positive electrode current collector 30 and a positive electrode composite layer 32 formed on the positive electrode current collector 30. The positive electrode composite layer 32 is formed on at least one of the inner and outer circumferential sides of the positive electrode current collector 30. For the positive electrode current collector 30, for example, a foil of a metal such as aluminum, or a film having such a metal disposed on its surface layer, is used. A suitable positive electrode current collector 30 is a foil of a metal mainly composed of aluminum or an aluminum alloy. The thickness of the positive electrode current collector 30 is, for example, 10 μm to 30 μm.

[0020] The positive electrode composite material layer 32 is preferably formed over the entire area of both surfaces of the positive electrode current collector 30, excluding the positive electrode current collector exposed portions 34 described later. The positive electrode composite material layer 32 preferably contains a positive electrode active material, a conductive agent, and a binder. The positive electrode composite material layer 32 is formed by applying a positive electrode composite material slurry containing a positive electrode active material, a conductive agent, a binder, and a solvent such as N-methyl-2-pyrrolidone (NMP) onto both surfaces of the positive electrode current collector 30 and drying it (positive electrode composite material layer forming step). Thereafter, the positive electrode composite material layer 32 is compressed.

[0021] Examples of the positive electrode active material include lithium-containing transition metal oxides containing transition metal elements such as Co, Mn, and Ni. The lithium-containing transition metal oxide is not particularly limited, but is preferably a composite oxide represented by the general formula Li 1+x MO2 (wherein -0.2 < x ≦ 0.2 and M includes at least one of Ni, Co, Mn, and Al).

[0022] Examples of the conductive agent contained in the positive electrode composite material layer 32 include carbon materials such as carbon black (CB), acetylene black (AB), ketjen black, and graphite.

[0023] Examples of the binder contained in the positive electrode composite material layer 32 include fluorine-based resins such as polytetrafluoroethylene (PTFE) and polyvinylidene fluoride (PVdF), polyacrylonitrile (PAN), polyimide (PI), acrylic resins, and polyolefin resins. When preparing the positive electrode composite material slurry with an aqueous solvent, styrene-butadiene rubber (SBR), nitrile rubber (NBR), CMC or its salt, polyacrylic acid or its salt, polyvinyl alcohol, etc. can be used. From the viewpoint of the flexibility of the positive electrode 11, rubber-based resins having a molecular structure in which double bonds and single bonds are repeated, such as SBR and NBR, are preferable as the binder. These may be used alone or in combination of two or more. The content of the binder in the positive electrode composite material layer 32 is 0.5 mass% to 10 mass%, preferably 1 mass% to 5 mass%.

[0024] The positive electrode 11 is provided with a positive electrode current collector exposed portion 34 where the surface of the positive electrode current collector 30 is exposed. The positive electrode current collector exposed portion 34 is a portion to which the positive electrode lead 19 is connected, and is a portion where the surface of the positive electrode current collector 30 is not covered with the positive electrode mixture layer 32. The positive electrode current collector exposed portion 34 is formed wider in the longitudinal direction than the positive electrode lead 19. The positive electrode current collector exposed portion 34 is preferably provided on both sides of the positive electrode 11 so as to overlap in the thickness direction of the positive electrode 11. The positive electrode lead 19 is joined to the positive electrode current collector exposed portion 34 by, for example, ultrasonic welding.

[0025] In the example shown in FIG. 3, a positive electrode current collector exposed portion 34 is provided in the center of the longitudinal direction of the positive electrode 11 over the entire length in the strip width direction. The positive electrode current collector exposed portion 34 may be formed at the beginning or end of the positive electrode 11, but from the viewpoint of current collection, it is preferable to provide it at a position approximately equidistant from the beginning and end. By connecting the positive electrode lead 19 to the positive electrode current collector exposed portion 34 provided at such a position, when the electrode body 14 is wound, the positive electrode lead 19 is arranged to protrude upward from the end face in the strip width direction at the radial middle position of the electrode body 14. The positive electrode current collector exposed portion 34 is provided, for example, by intermittent application in which the positive electrode composite slurry is not applied to a part of the positive electrode current collector 30.

[0026] "Negative electrode composition" FIG. 4A is a front view showing the negative electrode 12 constituting the electrode body 14 in an expanded state, and FIG. 4B is a longitudinal cross-sectional view showing the negative electrode 12 constituting the electrode body 14 in an expanded state.

[0027] In the electrode body 14, the negative electrode 12 is formed to be larger than the positive electrode 11 in order to prevent lithium deposition in the negative electrode 12. Specifically, the length of the negative electrode 12 in the strip width direction (axial direction) is larger than the length of the positive electrode 11 in the strip width direction. In addition, the length of the negative electrode 12 in the longitudinal direction is larger than the length of the positive electrode 11 in the longitudinal direction. As a result, when wound into the electrode body 14, at least the portion of the positive electrode 11 where the positive electrode mixture layer 32 is formed is disposed opposite the portion of the negative electrode 12 where the negative electrode mixture layer 42 is formed, with the separator 13 interposed therebetween.

[0028] 4A and 4B, the negative electrode 12 has a strip-shaped negative electrode current collector 40 and a negative electrode composite layer 42 formed on both sides of the negative electrode current collector 40. For the negative electrode current collector 40, for example, a foil of a metal such as copper, or a film having such a metal disposed on its surface layer, is used. The thickness of the negative electrode current collector 40 is, for example, 5 μm to 30 μm.

[0029] The negative electrode mixture layer 42 is preferably formed on the entire area of ​​both sides of the negative electrode current collector 40, except for a negative electrode current collector exposed portion 44 and a single-side coated portion 46, which will be described later. The negative electrode mixture layer 42 preferably contains a negative electrode active material and a binder. The negative electrode mixture layer 42 is formed by applying a negative electrode mixture slurry containing a negative electrode active material, a binder, and a solvent such as water to both sides of the negative electrode current collector 40 and drying the slurry (negative electrode mixture layer forming step). Thereafter, the negative electrode mixture layer 42 is compressed.

[0030] 4A and 4B, a negative electrode current collector exposed portion 44 is provided at the beginning end in the longitudinal direction of the negative electrode 12 over the entire length of the current collector in the strip width direction. The negative electrode current collector exposed portion 44 is a portion to which the negative electrode lead 20 is connected, and is a portion of the surface of the negative electrode current collector 40 that is not covered by the negative electrode mixture layer 42. The negative electrode current collector exposed portion 44 is formed to be wider in the longitudinal direction than the width of the negative electrode lead 20. The negative electrode current collector exposed portions 44 are preferably provided on both sides of the negative electrode 12 so as to overlap in the thickness direction of the negative electrode 12.

[0031] In this embodiment, the negative electrode lead 20 is joined to the surface on the inner circumferential side of the negative electrode current collector 40 by, for example, ultrasonic welding. One end of the negative electrode lead 20 is disposed in the negative electrode current collector exposed portion 44, and the other end extends downward from the lower end of the negative electrode current collector exposed portion 44. The negative electrode current collector exposed portion 44 is provided, for example, by intermittent application in which the negative electrode composite slurry is not applied to a part of the negative electrode current collector 40.

[0032] A single-sided coated portion 46 in which a negative electrode composite layer 42 is formed only on the inner peripheral surface of a negative electrode current collector 40 is provided at the terminal end of the negative electrode 12 arranged on the outermost peripheral side of the electrode body 14, and the negative electrode current collector 40 is exposed on the outer peripheral surface of the single-sided coated portion 46. The negative electrode composite layer 42 (42B) in the single-sided coated portion 46 is set to have a larger charge expansion coefficient than the negative electrode composite layer 42 (42A) in the double-sided coated portion.

[0033] The negative electrode current collector 40 exposed at the one-side coated portion 46 is in contact with the inner surface of the exterior can 15 (see FIG. 1 ), and the negative electrode 12 and the exterior can 15 are electrically connected to each other separately from the negative electrode lead 20. The negative electrode current collector exposed portion 44 and the one-side coated portion 46 may be provided, for example, by intermittent application in which the negative electrode composite slurry is not applied to a part of the negative electrode current collector 40.

[0034] The negative electrode active material is not particularly limited as long as it can reversibly absorb and release lithium (Li) ions. For example, carbon materials such as natural graphite and artificial graphite, metals that can be alloyed with lithium such as silicon (Si) and tin (Sn), or alloys and oxides containing these can be used.

[0035] Examples of the binder contained in the negative electrode mixture layer 42 include fluorine-based resins such as polytetrafluoroethylene (PTFE) and polyvinylidene fluoride (PVdF), polyacrylonitrile (PAN), polyimide (PI), acrylic resins, and polyolefin resins. When preparing the negative electrode mixture slurry using an aqueous solvent, styrene butadiene rubber (SBR), nitrile rubber (NBR), CMC or a salt thereof, polyacrylic acid or a salt thereof, polyvinyl alcohol, and the like can be used. From the viewpoint of flexibility of the negative electrode 12, the binder is preferably a rubber-based resin having a molecular structure in which double bonds and single bonds are repeated, such as SBR or NBR. These may be used alone or in combination of two or more. The content of the binder in the negative electrode mixture layer 42 is 0.5% by mass to 10% by mass, and preferably 1% by mass to 5% by mass.

[0036] "Configuration of the electrode body near the outermost periphery" 5 is a radial cross-section (cross-section seen from the axial direction) of the vicinity of the outermost periphery of negative electrode 12 (positive electrode 11 and separator 13 are omitted). As shown in FIG. 5, negative electrode mixture layer 42 is not present on the outer periphery side of the outermost negative electrode 12, and negative electrode current collector 40 is exposed.

[0037] 6 is a radial cross-section (cross-section seen from the axial direction) of a portion near the outermost periphery of the electrode body 14. Thus, the negative electrode 12 is located inside the exterior can 15, and the negative electrode current collector 40 is exposed on the outer periphery side of the negative electrode 12, with the exposed surface of the negative electrode current collector 40 in contact with the inner surface of the exterior can 15. The positive electrode 11, in which the positive electrode mixture layer 32 is formed on both sides of the positive electrode current collector 30, is located on the inner periphery side of the negative electrode 12, with the separator 13 interposed therebetween. The negative electrode 12 is then located on the inner periphery side of the positive electrode 11, with the separator 13 interposed therebetween.

[0038] The negative electrode mixture layer 42 (42B) in the single-sided coated portion 46 located on the outermost periphery of the electrode body 14 has properties different from the negative electrode mixture layer 42 (42A) in the double-sided coated portion located more inward. That is, in the negative electrode 12 of the nonaqueous electrolyte secondary battery of this embodiment, the negative electrode mixture layer 42B in the single-sided coated portion 46 has a larger charge expansion coefficient than the negative electrode mixture layer 42A in the double-sided coated portion.

[0039] "Charging expansion rate of negative electrode mixture layer" In this embodiment, the charge expansion coefficient of negative electrode mixture layer 42 (42B) in single-side coated portion 46 is increased, and the following method is exemplified for this purpose. (1) Increasing the proportion of active materials with a large charging expansion rate. (2) Increasing the particle size of the active material that has a large charging expansion rate. (3) Reducing the binder content.

[0040] Examples of negative electrode active materials with a large charging expansion rate include silicon materials containing Si and tin materials containing Sn. Although silicon materials and tin materials are not necessarily required, in this embodiment, it is preferable that the negative electrode composite layer 42 (42B) contains a silicon material. Examples of silicon materials include Si, Si oxide, and lithium silicate. As Si oxide, for example, a composite in which Si particles are dispersed in a SiO2 phase can be used. It is preferable to use a silicon material together with a carbon material.

[0041] By increasing the charge expansion rate of the negative electrode mixture layer 42 (42B) in the one-side coated portion 46, the exposed surface of the outermost negative electrode current collector 40 and the inner surface of the outer can 15 are reliably in contact with each other during charging without excessively narrowing the clearance between the electrode body 14 and the inner surface of the outer can 15 when inserted into the outer can 15, ensuring good current collection. Although the negative electrode mixture layer 42 shrinks upon discharge, the initial expansion is greater than the subsequent shrinkage. Therefore, by performing an initial charge after the insertion of the electrode body 14, the outermost negative electrode current collector 40 can be brought into contact with the inner surface of the outer can, and good electrical contact can be maintained during subsequent charging and discharging.

[0042] In this embodiment, the entire single-sided coated portion 46 is disposed on the outermost periphery of the electrode body 14, but the range in which the single-sided coated portion 46 is disposed does not necessarily have to coincide with the outermost periphery of the electrode body 14. If at least a part of the single-sided coated portion 46 is disposed on the outermost periphery of the electrode body 14, at least a part of the exposed surface of the negative electrode current collector 40 can be sufficiently in contact with the inner surface of the outer can. For example, it is preferable that the single-sided coated portion 46 is disposed in a range of 50% or more of the circumferential length of the outermost periphery of the electrode body 14. In addition, a part of the single-sided coated portion 46 may be disposed so as to extend from the outermost periphery of the electrode body 14 to the winding start side. In this case, as shown in FIG. 6, since the inner periphery side of the positive electrode mixture layer 32 needs to face the outer periphery side of the negative electrode mixture layer 42 via the separator 13, the single-sided coated portion 46 is formed in a range not exceeding the position facing the end of the inner periphery side of the positive electrode mixture layer 32 from the end of the negative electrode 12. Therefore, the area where the negative electrode mixture layer 42 (42B) in the one-sided coated portion 46 faces the positive electrode mixture layer 32 is limited to one circumference or less, so even if the charge expansion rate of the negative electrode mixture layer 42 (42B) in the one-sided coated portion 46 is increased, peeling between the active material and the current collector and deterioration due to isolation of the active material are suppressed.

[0043] This makes it possible to suppress defects when inserting the electrode body 14 into the outer casing 15 and deterioration due to charge / discharge cycles, while ensuring that the exposed surface of the negative electrode current collector 40 is in contact with the inner surface of the outer casing 15, thereby ensuring good current collection properties. EXAMPLES

[0044] The present disclosure will be further described below with reference to examples, but the present disclosure is not limited to these examples.

[0045] [Preparation of negative electrode] (Negative electrode slurry 1: Si ratio 5.5 mass%, Si particle size 5 μm) Graphite and Si oxide were used as the negative electrode active material. Negative electrode slurry 1 was prepared by mixing 94.5 parts by mass of graphite, 5.5 parts by mass of Si oxide having an average particle size of 5.0 μm, 1 part by mass of carboxymethyl cellulose (CMC), 1 part by mass of styrene butadiene rubber (SBR), and water. That is, the content of the binder (CMC and SBR) relative to the negative electrode active material in negative electrode slurry 1 is 2% by mass. Note that the Si ratio and Si particle size in the present disclosure respectively mean the ratio and average particle size of the Si oxide in the negative electrode active material, and the average particle size is the median diameter (D50) based on volume.

[0046] (Negative electrode slurry 2: Si ratio 20 mass%, Si particle size 5 μm) Negative electrode slurry 2 was prepared by mixing 80.0 parts by mass of graphite, 20.0 parts by mass of Si oxide having an average particle size of 5.0 μm, 1 part by mass of carboxymethyl cellulose (CMC), 1 part by mass of styrene butadiene rubber (SBR), and water.

[0047] (Negative electrode slurry 3: Si ratio 5.5 mass%, Si particle size 1 μm) The Si oxide in the negative electrode slurry 1 was changed to one having an average particle size of 1 μm.

[0048] (Negative electrode slurry 4: Si ratio 5.5 mass%, Si particle size 15 μm) The Si oxide in the negative electrode slurry 1 was changed to one having an average particle size of 15 μm.

[0049] (Negative electrode slurry 5: Si ratio 5.5 mass%, Si particle size 20 μm) The Si oxide in the negative electrode slurry 1 was changed to one having an average particle size of 20 μm.

[0050] (Negative electrode slurry 6: Si ratio 5.5 mass%, Si particle size 5 μm, binder 1.5 mass%) The amount of styrene butadiene rubber (SBR) added in negative electrode slurry 1 was changed to 0.5 parts by mass. That is, the content of the binder (CMC and SBR) relative to the negative electrode active material in negative electrode slurry 6 was 1.5% by mass.

[0051] (Negative electrode coating) Two types of negative electrode slurries, one for double-sided coated areas and one for single-sided coated areas, were applied to the copper foil using a multi-layer die coater, switching the negative electrode slurry depending on the area to be coated. In other words, the negative electrode slurry for double-sided coated areas was applied to the areas to be double-sided coated, and the negative electrode slurry for single-sided coated areas was applied to the areas to be single-sided coated. The coating was then dried, rolled, and cut to the specified plate size to produce the negative electrode.

[0052] [Preparation of positive electrode] In N-methylpyrrolidone (NMP) solvent, LiNi 0.8 Co 0.15 Al 0.05 O2, acetylene black, a carbon conductive agent, and polyvinylidene fluoride (PVDF) with an average molecular weight of 1.1 million were mixed in a mass ratio of 95:2.5:2.5 using a mixer to prepare a positive electrode composite slurry with a solid content of 70%. The prepared slurry was applied to both sides of aluminum foil, dried, rolled, and then cut to the specified plate size to prepare a positive electrode plate.

[0053] [Preparation of electrolyte] Five parts by mass of vinylene carbonate (VC) was added to 100 parts by mass of a mixed solvent of ethylene carbonate (EC) and dimethyl carbonate (DMC) (volume ratio of EC:DMC=1:3), and 1 mol / L of LiPF6 was dissolved as a lithium salt to prepare an electrolyte solution as a non-aqueous electrolyte.

[0054] [Battery construction] The positive and negative electrodes were each provided with a lead terminal, and the electrodes were wound with a separator interposed therebetween to produce an electrode body. At this time, the one-sided coating portion of the negative electrode was disposed on the outermost periphery of the electrode body. The wound body was inserted into an exterior can, which is a battery container, and the negative electrode lead was welded to the bottom of the container. Next, the positive electrode lead was ultrasonically welded to a sealing body, the electrolyte was poured in, and the sealing body was crimped to seal the battery. The rated capacity of the produced battery was 2500mAh.

[0055] [DC resistance measurement] The battery was charged at a constant current of 0.5 It until the voltage reached 4.2 V. The battery was then charged at a constant voltage of 0.05 It at 4.2 V. The battery was then discharged at a constant current of 0.2 It until the voltage reached 2.5 V, and the discharge capacity was measured.

[0056] Based on the above discharge capacity results, the battery's depth of charge (SOC) was adjusted to 10%, and then the battery was discharged at a current of 1.0 It for 10 seconds, and the voltage change ΔV after 10 seconds had elapsed was measured. The direct current resistance (DCR) was calculated using the voltage change ΔV and the current value during discharge using the following formula. Note that It (A) = rated capacity (Ah) / 1 (h). DCR=ΔV / 1.0It

[0057] [Capacity retention rate measurement] The charge / discharge cycle was repeated 100 times under the same conditions as in the above-mentioned method for measuring the discharge capacity, and the capacity retention rate was calculated using the following formula. Capacity retention rate = (discharge capacity at 100th cycle / discharge capacity at 1st cycle) x 100

[0058] <Example 1> Slurry 1 was used as the slurry for the double-sided coated portion, and slurry 2 was used as the slurry for the single-sided coated portion.

[0059] <Comparative Example 1> Slurry 1 was used as the slurry for the double-sided coated area and the slurry for the single-sided coated area.

[0060] <Comparative Example 2> Slurry 2 was used as the slurry for the double-sided coated area and the slurry for the single-sided coated area.

[0061] <Example 2> Slurry 1 was used as the slurry for the double-sided coated portion, and slurry 4 was used as the slurry for the single-sided coated portion.

[0062] <Comparative Example 3> Slurry 4 was used as the slurry for the double-sided coated area and the slurry for the single-sided coated area.

[0063] <Example 3> Slurry 3 was used as the slurry for the double-sided coated portion, and slurry 1 was used as the slurry for the single-sided coated portion.

[0064] <Example 4> Slurry 4 was used as the slurry for the double-sided coated portion, and slurry 5 was used as the slurry for the single-sided coated portion.

[0065] <Example 5> Slurry 1 was used as the slurry for the double-sided coated portion, and slurry 6 was used as the slurry for the single-sided coated portion.

[0066] <Comparative Example 4> Slurry 6 was used as the slurry for the double-sided coated area and the slurry for the single-sided coated area.

[0067] [Experimental Results] Table 1 shows the DCR and capacity retention rate when the silicon material content ratio (Si ratio) in the negative electrode composite layer 42A of the double-sided coated portion located on the inner side of the outermost circumference and the negative electrode composite layer 42B of the single-sided coated portion 46 located on the outermost circumference is changed.

[0068] [Table 1]

[0069] The DCR is significantly reduced in Example 1 compared to Comparative Example 1. In this way, the DCR is reduced by increasing the Si ratio in the single-sided coated portion 46 arranged at the outermost periphery. Furthermore, Example 1 exhibits a capacity retention rate equivalent to that of Comparative Example 1, but Comparative Example 2 exhibits a significantly reduced DCR compared to Comparative Example 1, but the capacity retention rate is also reduced. In other words, by increasing the Si ratio in the single-sided coated portion 46 compared to the double-sided coated portion, it is possible to reduce the DCR while suppressing the decrease in the capacity retention rate.

[0070] Table 2 shows the DCR and capacity retention rate when the average particle diameter (Si particle diameter) of the silicon material is changed in the negative electrode composite layer 42A of the double-sided coated portion located on the inner side of the outermost circumference and in the negative electrode composite layer 42B of the single-sided coated portion 46 located on the outermost circumference.

[0071] [Table 2]

[0072] The DCR is significantly reduced in Example 2 compared to Comparative Example 1. In this way, the DCR is reduced by increasing the Si particle size in the single-sided coated portion 46 arranged at the outermost periphery. Furthermore, Example 2 exhibits a capacity retention rate equivalent to that of Comparative Example 1, but Comparative Example 3 exhibits a significantly reduced DCR compared to Comparative Example 1, but the capacity retention rate is also reduced. In other words, by increasing the Si particle size in the single-sided coated portion 46 compared to the double-sided coated portion, it is possible to reduce the DCR while suppressing the decrease in the capacity retention rate.

[0073] Table 3 shows the DCR and capacity maintenance rate when the binder content in negative electrode mixture layer 42A in the double-sided coated portion arranged on the inner side from the outermost periphery and in negative electrode mixture layer 42B arranged on the outermost periphery are changed.

[0074] [Table 3]

[0075] The DCR is significantly reduced in Example 5 compared to Comparative Example 1. In this way, the DCR is reduced by increasing the binder content of the single-sided coated portion 46 arranged at the outermost periphery. Furthermore, Example 5 exhibits a capacity retention rate equivalent to that of Comparative Example 1, but Comparative Example 4 exhibits a significantly reduced capacity retention rate compared to Comparative Example 1, although the DCR is significantly reduced. In other words, by increasing the binder content of the single-sided coated portion 46 compared to the double-sided coated portion, it is possible to reduce the DCR while suppressing the decrease in the capacity retention rate.

[0076] [result] From the above, it was found that when the charge expansion rate of the negative electrode composite layer 42 (42B) of the single-sided coated portion 46 arranged on the outermost periphery is made larger than that of the double-sided coated portion arranged more inward than the outermost periphery, it is possible to reduce the DCR while suppressing the decrease in capacity retention rate. [Explanation of symbols]

[0077] 10 secondary battery, 11 positive electrode, 12 negative electrode, 13 separator, 14 electrode body, 15 outer can, 16 sealing body, 17, 18 insulating plate, 19 positive electrode lead, 20 negative electrode lead, 21 grooved portion, 22 filter, 23 lower valve body, 24 insulating member, 25 upper valve body, 26 cap, 26a opening, 27 gasket, 28 winding shaft, 30 positive electrode current collector, 32 positive electrode composite layer, 34 positive electrode current collector exposed portion, 40 negative electrode current collector, 42 negative electrode composite layer, 44 negative electrode current collector exposed portion, 46 one-sided coating portion.

Claims

1. A nonaqueous electrolyte secondary battery comprising: a wound electrode assembly in which a strip-shaped positive electrode and a strip-shaped negative electrode are wound with a separator interposed therebetween; and an exterior can for accommodating the electrode assembly, The positive electrode has a positive electrode mixture layer formed on the surface of a sheet-shaped positive electrode current collector. The negative electrode has a negative electrode mixture layer formed on the surface of a sheet-shaped negative electrode current collector, the negative electrode mixture layer includes a chargeable / dischargeable negative electrode active material and a binder, The negative electrode is a double-sided coated section in which a negative electrode composite layer is formed on both sides of the negative electrode current collector; and a single-sided coated section in which a negative electrode composite layer is formed on one side of the negative electrode current collector, At least a part of the single-sided coated portion is disposed on the outermost periphery of the electrode body, at least a part of an exposed surface of the negative electrode current collector in the one-side coated portion is in contact with an inner surface of the outer can, a charging expansion coefficient of the negative electrode mixture layer in the one-side coated portion is greater than a charging expansion coefficient of the negative electrode mixture layer in the double-side coated portion.

2. 2. The nonaqueous electrolyte secondary battery according to claim 1, wherein the negative electrode mixture layer contains a silicon material as the negative electrode active material, and a ratio of the silicon material to the negative electrode active material in the one-sided coated portion is greater than a ratio of the silicon material to the negative electrode active material in the double-sided coated portion.

3. 3. The nonaqueous electrolyte secondary battery according to claim 1, wherein the negative electrode mixture layer contains a silicon material as the negative electrode active material, and an average particle diameter of the silicon material in the one-sided coated portion is larger than an average particle diameter of the silicon material in the both-sided coated portion.

4. 4. The nonaqueous electrolyte secondary battery according to claim 1, wherein the binder content in the single-sided coated portion is lower than the binder content in the double-sided coated portion.