Secondary battery

Abstract

A secondary battery according to one embodiment of the present invention includes an electrode assembly, an electrode lead attached to the electrode assembly, a case that houses the electrode assembly, a lead film that is formed to enclose a portion of an outer surface of the electrode lead and is interposed between the electrode lead and the case, a vent region formed in at least a portion of the case, and a vent member that is inserted into the vent region and includes linear low-density polyethylene having a comonomer having six or more carbon atoms.

Description

[Technical field]

[0001] This application claims priority to Korean Patent Application No. 10-2021-0049378 filed on April 15, 2021 and Korean Patent Application No. 10-2021-0150951 filed on November 4, 2021.

[0002] The present invention relates to a secondary battery, and more particularly to a secondary battery provided with a vent member. [Background technology]

[0003] Secondary batteries can be applied to a wide variety of products and have excellent electrical properties such as high energy density. Secondary batteries are widely used not only in portable devices but also in electric vehicles (EVs) and hybrid electric vehicles (HEVs) that are powered by electricity. Secondary batteries can significantly reduce the use of fossil fuels and do not produce by-products in the energy consumption process, so they are attracting attention as a new energy source that is environmentally friendly and improves energy efficiency.

[0004] Currently widely used secondary batteries include lithium ion batteries, lithium polymer batteries, nickel cadmium batteries, nickel hydrogen batteries, and nickel zinc batteries.

[0005] A secondary battery generally has a structure in which an electrode assembly including at least one unit cell having a positive electrode / separator / negative electrode structure is housed in a laminate sheet case in which an outer layer, a metal barrier layer, and a sealant layer are laminated in this order, and the electrode assembly is sealed by fusing the sealant resin of the sealant layer.

[0006] In conventional secondary batteries, the battery may catch fire due to various reasons such as a short circuit inside the secondary battery, overcharging or over-discharging, temperature control, etc. When this happens, the temperature inside the secondary battery rises rapidly, and a thermal propagation phenomenon occurs in which heat is transferred to adjacent cells, causing the flames to grow in size.

[0007] When a thermal runaway phenomenon occurs, i.e., when the temperature inside the secondary battery rises, in order to minimize damage to the electrodes caused by gas, a directional venting characteristic that exhausts gas in one direction is required. However, conventional secondary batteries have the disadvantage that it is difficult to induce the exhaust of gas in a specific direction.

[0008] SUMMARY OF THE PRESENTLY PREFERRED EMBODIMENTS Accordingly, an object of the present invention is to provide a secondary battery having improved safety by directing gas discharge in a specific direction. Summary of the Invention [Problem to be solved by the invention]

[0009] Therefore, an object of the present invention is to provide a secondary battery capable of inducing gas discharge in a specific direction, thereby improving safety. [Means for solving the problem]

[0010] In order to solve the above problems, according to one aspect of the present invention, there is provided a secondary battery having the following features.

[0011] The first aspect is An electrode assembly; an electrode lead attached to the electrode assembly; a case that accommodates the electrode assembly therein; a lead film formed so as to enclose a part of an outer surface of the electrode lead and interposed between the electrode lead and the case; a vent area formed in at least a portion of the case; a vent member inserted in the vent region, the vent member comprising a linear low density polyethylene having a comonomer having 6 or more carbon atoms; The present invention relates to a secondary battery including the above.

[0012] A second aspect is the secondary battery according to the first aspect, The vent member may comprise a linear low density polyethylene having a comonomer having 6 to 8 carbon atoms.

[0013] A third aspect is the secondary battery according to the first or second aspect, The case may include a seal portion formed to seal the electrode assembly. The seal portion may include a sealant resin, The linear low density polyethylene having a comonomer having 6 or more carbon atoms of the vent member may have a melting point lower than that of the sealant resin.

[0014] A fourth aspect is the secondary battery according to any one of the first to third aspects, The vent member can be melted at 100°C to 120°C to vent gas.

[0015] A fifth aspect is the secondary battery according to the fourth aspect, The vent member is capable of venting a vent gas at a pressure of 1.5 atm or greater.

[0016] A sixth aspect is the secondary battery according to any one of the first to fifth aspects, The vent member may have a maximum seal strength of less than 6 kgf / 15 mm at 100° C. or higher.

[0017] A seventh aspect is the secondary battery according to any one of the first to sixth aspects, The vent member may have an average seal strength of less than 4.5 kgf / 15 mm at 100° C. or higher.

[0018] An eighth aspect is the secondary battery according to any one of the first to seventh aspects, The vent member may have a maximum seal strength at room temperature to 60°C of 6 kgf / 15 mm or more.

[0019] A ninth aspect is the secondary battery according to any one of the first to eighth aspects, The vent member may have an average seal strength at room temperature to 60°C of 4.5 kgf / 15 mm or more.

[0020] A tenth aspect is the secondary battery according to any one of the first to ninth aspects, The linear low-density polyethylene having a comonomer having 6 or more carbon atoms may be polymerized in the presence of a metallocene catalyst.

[0021] An eleventh aspect is the secondary battery according to any one of the first to tenth aspects, Based on 100% by weight of the linear low-density polyethylene having a comonomer having 6 or more carbon atoms, the content of the comonomer having 6 or more carbon atoms may be 15% by weight or less.

[0022] A twelfth aspect is the secondary battery according to any one of the first to eleventh aspects, The linear low density polyethylene having a comonomer having 6 or more carbon atoms may have a polydispersity index (PDI) of 4 or less.

[0023] A thirteenth aspect is the secondary battery according to any one of the third to twelfth aspects, The difference between the crystallization temperature of the sealant resin and the crystallization temperature of the linear low density polyethylene having a comonomer having 6 or more carbon atoms may be 10° C. or less.

[0024] A fourteenth aspect is the secondary battery according to the thirteenth aspect, The crystallization temperature of the linear low-density polyethylene having a comonomer having 6 or more carbon atoms may be 90°C to 115°C.

[0025] A fifteenth aspect is the secondary battery according to any one of the first to fourteenth aspects, The linear low-density polyethylene having a comonomer having 6 or more carbon atoms may have a melting point of 100°C to 130°C.

[0026] A sixteenth aspect is the secondary battery according to any one of the first to fifteenth aspects, The linear low-density polyethylene having a comonomer having 6 or more carbon atoms may have a weight average molecular weight of 100,000 g / mol to 400,000 g / mol.

[0027] A seventeenth aspect is the secondary battery according to any one of the third to sixteenth aspects, The vent area may be located at the seal.

[0028] An eighteenth aspect is the secondary battery according to the seventeenth aspect, The vent area may be located in a seal on a corner side of the case.

[0029] A nineteenth aspect is the secondary battery according to any one of the first to eighteenth aspects, The secondary battery may be a pouch-type secondary battery.

[0030] A twentieth aspect is the secondary battery according to any one of the first to nineteenth aspects, The vent member may have a maximum seal strength at 100°C to 120°C of less than 6 kgf / 15 mm.

[0031] A twenty-first aspect is the secondary battery according to any one of the first to twentieth aspects, The vent member may have an average seal strength at 100°C to 120°C of less than 4.5 kgf / 15 mm.

[0032] A twenty-second aspect is the secondary battery according to any one of the first to twenty-first aspects, Based on 100% by weight of the linear low density polyethylene, the content of the comonomer having 6 or more carbon atoms may be 5% by weight to 15% by weight.

[0033] A twenty-third aspect is the secondary battery according to any one of the first to twenty-second aspects, The linear low density polyethylene may have a polydispersity index (PDI) of 1-4.

[0034] A twenty-fourth aspect is the secondary battery according to any one of the first to twenty-third aspects, The vent member may have a maximum seal strength of less than 3 kgf / 15 mm at 120° C. or higher.

[0035] A twenty-fifth aspect is the secondary battery according to any one of the first to twenty-fourth aspects, The vent member may have an average seal strength of less than 2 kgf / 15 mm at 120° C. or higher. Effect of the Invention

[0036] The secondary battery according to an embodiment of the present invention includes a vent member including a linear low-density polyethylene having a comonomer having 6 or more carbon atoms, which allows gas to be discharged to the vent region, thereby improving the safety of the battery. [Brief description of the drawings]

[0037] The following drawings attached to this specification illustrate preferred embodiments of the present invention and, together with the detailed description of the invention described below, serve to further understand the technical ideas of the present invention. Therefore, the present invention should not be interpreted as being limited only to the matters depicted in such drawings.

[0038] [Figure 1] 1 is an exploded perspective view of a secondary battery according to an embodiment of the present invention; [Diagram 2] 1 is a plan view showing a secondary battery according to an embodiment of the present invention; [Diagram 3] 4A and 4B are diagrams illustrating a state in which venting occurs in a secondary battery according to an embodiment of the present invention. [Figure 4] FIG. 4 is a plan view showing a secondary battery according to another embodiment of the present invention. [Diagram 5] FIG. 13 is a plan view showing a secondary battery according to still another embodiment of the present invention. [Figure 6] FIG. 13 is a plan view showing a secondary battery according to still another embodiment of the present invention. [Figure 7] FIG. 13 is a plan view showing a secondary battery according to still another embodiment of the present invention. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0039] Hereinafter, a preferred embodiment of the present invention will be described in detail with reference to the accompanying drawings. Prior to this, the terms and words used in the specification and claims should not be interpreted as being limited to their ordinary or dictionary meanings, but should be interpreted as having meanings and concepts according to the technical ideas of the present invention, in accordance with the principle that the inventor himself can appropriately define the concepts of terms in order to best describe the invention.

[0040] Therefore, it should be understood that the embodiment described in this specification and the configurations shown in the drawings are merely the most preferred embodiment of the present invention and do not represent the entire technical idea of ​​the present invention, and that there may be various equivalents and modifications that can be substituted therefor at the time of this application.

[0041] According to one aspect of the present invention, there is provided a secondary battery comprising: an electrode assembly having an electrode lead attached thereto; a case housing the electrode assembly therein; a lead film formed to enclose a portion of an outer surface of the electrode lead and interposed between the electrode lead and the case; a vent region formed in at least a portion of the case; and a vent member inserted in the vent region and including a linear low-density polyethylene having a comonomer having 6 or more carbon atoms.

[0042] 1 and 2 show a secondary battery according to one embodiment of the present invention.

[0043] The secondary battery 10 comprises an electrode assembly 12 to which an electrode lead 11 is attached, and a case 13 .

[0044] The electrode assembly 12 includes a positive electrode plate, a negative electrode plate, and a separator. The electrode assembly 12 may be formed by stacking the positive electrode plate and the negative electrode plate in this order with the separator interposed therebetween.

[0045] The positive electrode plate may include a positive electrode current collector made of a metal thin plate having excellent electrical conductivity, for example, an aluminum (Al) foil, and a positive electrode active material layer coated on at least one side of the positive electrode current collector. The positive electrode plate may also include a positive electrode tab made of a metal material, for example, an aluminum (Al) material, at one end. The positive electrode tab may protrude from one end of the positive electrode plate. The positive electrode tab may be welded to one end of the positive electrode plate, or may be attached using a conductive adhesive.

[0046] The negative electrode plate may include a negative electrode current collector made of a conductive metal thin plate, for example, copper (Cu) foil, and a negative electrode active material layer coated on at least one side of the negative electrode current collector. The negative electrode plate may also include a negative electrode tab formed of a metal material, for example, nickel (Ni) material, at one end. The negative electrode tab may protrude from one end of the negative electrode plate. The negative electrode tab may be welded to one end of the negative electrode plate, or may be attached using a conductive adhesive.

[0047] The separator is located between the positive electrode plate and the negative electrode plate to electrically insulate the positive electrode plate and the negative electrode plate from each other. The separator may be formed as a porous membrane so that lithium ions can pass between the positive electrode plate and the negative electrode plate. The separator may include a porous membrane using, for example, polyethylene (PE), polypropylene (PP), or a composite film thereof.

[0048] The separator may have an inorganic coating layer on its surface, which may have a structure in which inorganic particles are bound and fixed together by a binder, and a pore structure is formed by the interstitial volume between the particles.

[0049] The electrode assembly 12 may be a jelly roll type (wound type) electrode assembly having a structure in which long sheet-like positive and negative electrode plates are wound with a separator between them, a stack type (lamination type) electrode assembly in which a number of positive and negative electrode plates cut into units of a predetermined size are stacked in this order with a separator between them, a stack / folding type electrode assembly having a structure in which a bi-cell or full cell in which positive and negative electrode plates of a predetermined unit are stacked with a separator between them is wound up, or the like.

[0050] The case 13 serves to accommodate the electrode assembly 12 .

[0051] In one embodiment of the present invention, the case 13 may include a receiving portion 13a for receiving the electrode assembly 12, and a seal portion 13b formed to seal the electrode assembly 12, as shown in FIG.

[0052] The sealing portion 13b may include a sealant resin, and the sealant resin may be fused along the outer circumferential surface of the receiving portion 13a to seal the electrode assembly 12.

[0053] In one embodiment of the present invention, the case 13 may be provided in the form of a film having a multi-layer structure including an outer layer for protection from external impact, a metal barrier layer for blocking moisture, and a sealant layer for sealing the case.

[0054] The outer layer may include a polyester-based film using poly(ethylene terephthalate) (PET), polybutylene terephthalate, polyethylene naphthalate, polybutylene naphthalate, copolymer polyester, polycarbonate, nylon, or the like, and may be configured as a single layer or multiple layers.

[0055] The metal barrier layer may include aluminum, copper, or the like.

[0056] The sealant layer may include a sealant resin and may be configured as a single layer or multiple layers.

[0057] The sealant resin may include polypropylene (PP), acid modified polypropylene (PPa), random polypropylene, ethylene propylene copolymer, or two or more of these. The ethylene propylene copolymer may include, but is not limited to, ethylene propylene rubber, ethylene-propylene block copolymer, etc.

[0058] In one embodiment of the present invention, the case 13 may be in the form of a pouch.

[0059] The pouch-shaped case 13 may include an upper pouch and a lower pouch. When the case 13 includes an upper pouch and a lower pouch, the upper pouch and the lower pouch are arranged so that their sealant resins face each other, and then the facing sealant resins are fused to each other by heat and pressure to seal the battery.

[0060] The fusion of the seal portion 13b may be by heat fusion, ultrasonic fusion, or the like, but is not particularly limited as long as it is capable of fusion of the seal portion 13b.

[0061] In some embodiments, the sealed portion 13b may be four-sided sealed or three-sided sealed at the periphery of the case 13. In the three-sided sealed structure, the upper pouch and the lower pouch are formed from a single pouch sheet, and then the boundary surface between the upper pouch and the lower pouch is folded so that the storage portions 13a formed in the upper pouch and the lower pouch overlap, and the periphery of the remaining three sides excluding the folded portion is sealed.

[0062] The electrode lead 11 may be housed in the case 13 such that a portion of the electrode lead 11 is exposed to the outside of the case 13, as shown in FIG.

[0063] A secondary battery 10 according to one embodiment of the present invention includes a lead film 14 .

[0064] The lead film 14 wraps a part of the outer surface of the electrode lead 11 and is interposed between the electrode lead 11 and the case 13. For example, the lead film 14 can be interposed between the electrode lead 11 and a seal portion 13b of the case 13 at a portion where the electrode lead 11 protrudes or extends from the case 13 to assist in bonding the electrode lead 11 to the case 13.

[0065] 1 and 2, a secondary battery 10 according to an embodiment of the present invention may include a vent area (not shown) formed in at least a portion of the case 13, and a vent member 15 may be inserted into the vent area. When a thermal runaway phenomenon occurs, the vent member 15 may improve the safety of the battery by inducing the discharge of gas in a specific direction.

[0066] The vent member 15 and the case 13 may be overlapped using heat fusion. In another example, the vent member 15 and the case 13 may be overlapped using an adhesive such as glue. In yet another example, the vent member 15 and the case 13 may be physically connected to each other using a clip or the like. In yet another example, at least a portion of the vent member 15 may be embedded in a film that constitutes the case 13, for example, in a sealant resin.

[0067] The vent member 15 contains a linear low density polyethylene having a comonomer with a carbon number of 6 or more. Since the vent member 15 contains a linear low density polyethylene having a comonomer with a carbon number of 6 or more, the vent member 15 has excellent sealing ability for the case 13 in a normal temperature range, for example, room temperature to 60°C, but at high temperatures, for example, 100°C or higher, the seal strength of the case into which the vent member 15 is inserted is reduced, thereby realizing or inducing venting.

[0068] 3 is a diagram showing a state in which a vent occurs in a secondary battery according to an embodiment of the present invention, in particular, a cross-sectional view showing a vent member in a secondary battery according to an embodiment of the present invention.

[0069] Referring to Fig. 3, at a temperature at which the battery normally operates, the vent member serves to seal the case from the outside. If the temperature of the battery rises excessively due to abnormal operation of the battery, the vent member melts and the seal strength of the portion where the vent member is inserted decreases. Therefore, gas can be discharged from this portion. For example, when the pressure of gas inside the battery is applied to the interface between the vent member and the battery case, a gap is formed between the vent member and the battery case, and gas can be discharged from there.

[0070] In one embodiment of the present invention, the vent member 15 may contain linear low-density polyethylene having a comonomer having 6 to 8 carbon atoms.

[0071] In one embodiment of the present invention, the linear low density polyethylene having a comonomer with 6 or more carbon atoms may have a melting point lower than that of the sealant resin. When the linear low density polyethylene having a copolymer with 6 or more carbon atoms has a melting point lower than that of the sealant resin, the linear low density polyethylene can melt faster than the sealant resin at high temperatures. The seal strength of the portion into which the vent member 15 is inserted is further reduced compared to the seal strength of the case portion containing other sealant resins, so that the vent characteristics are more easily realized.

[0072] In one embodiment of the present invention, the linear low-density polyethylene having a comonomer with six or more carbon atoms may have a melting point of 100° C. to 130° C., or 105° C. to 125° C., or 110° C. to 120° C. When the melting point of the linear low-density polyethylene having a comonomer with six or more carbon atoms falls within the above-mentioned range, the seal strength of the portion of case 13 into which vent member 15 is inserted decreases at high temperatures, for example, 100° C. or higher, making it easier to achieve vent characteristics.

[0073] The melting point of the linear low-density polyethylene having a comonomer having 6 or more carbon atoms can be measured using a differential scanning calorimeter (DSC). For example, the temperature of the sample is raised from 30°C to 280°C at 10°C / min, maintained at 280°C for 10 minutes, cooled to 30°C at 10°C / min, and maintained at 30°C for 10 minutes. The temperature of the sample is then raised from 30°C to 280°C at 10°C / min, and maintained at 280°C for 10 minutes to measure the melting point.

[0074] In one embodiment of the present invention, the vent member 15 can vent at 100° C. to 120° C., and can discharge or exhaust gas from the receiving portion to the outside of the battery. In particular, the vent member 15 can vent at 100° C. to 120° C. and at a pressure of 1.5 atm or more. Since the vent member 15 vents within the above-mentioned temperature range and / or the above-mentioned pressure condition, the battery can be sealed when the battery operates normally, and gas can be discharged only when the battery operates abnormally.

[0075] In one embodiment of the present invention, the vent member 15 may have a maximum seal strength of less than 6 kgf / 15 mm, less than 5 kgf / 15 mm, or less than 4.5 kgf / 15 mm at 100° C. or higher. In one embodiment of the present invention, the vent member 15 may have a maximum seal strength of less than 6 kgf / 15 mm, less than 5 kgf / 15 mm, or less than 4.5 kgf / 15 mm at 100° C. to 120° C. In one embodiment of the present invention, the vent member 15 may have a maximum seal strength of less than 3 kgf / 15 mm, less than 2 kgf / 15 mm, less than 1 kgf / 15 mm, or less than 0.5 kgf / 15 mm at 120° C. or higher. When the vent member 15 satisfies the above-mentioned seal strength in the above-mentioned temperature range, the seal strength of the portion of the case 13 into which the vent member 15 is inserted is reduced at high temperatures, for example, 100° C. or higher, and the vent characteristics are more easily realized.

[0076] Furthermore, in one embodiment of the present invention, the vent member 15 may have a maximum seal strength of 6 kgf / 15 mm or more, 8 kgf / 15 mm or more, or 10 kgf / 15 mm or more at room temperature to 60° C. If the vent member 15 satisfies the above-mentioned seal strength in the above-mentioned temperature range, even if the vent member 15 is inserted, when the battery operates normally, the portion of the case 13 into which the vent member 15 is inserted has excellent seal strength, making it easy to ensure the hermeticity of the battery.

[0077] In one embodiment of the present invention, the vent member 15 may have a maximum seal strength of less than 6 kgf / 15 mm at 100° C. or higher, and the vent member 15 may have a maximum seal strength of 6 kgf / 15 mm or higher at room temperature to 60° C. When the vent member 15 satisfies the above-mentioned seal strength, the seal strength of the portion of the case 13 into which the vent member 15 is inserted decreases at high temperatures, for example, 100° C. or higher, making it easier to realize the vent characteristics. When the battery operates normally, the case 13 has excellent seal strength, making it easier to ensure the hermeticity of the battery.

[0078] In one embodiment of the present invention, the vent member 15 may have an average seal strength of less than 4.5 kgf / 15 mm or less than 3 kgf / 15 mm at 100° C. or more. In one embodiment of the present invention, the vent member 15 may have an average seal strength of less than 4.5 kgf / 15 mm or less than 3 kgf / 15 mm at 100° C. to 120° C. In one embodiment of the present invention, the vent member 15 may have an average seal strength of less than 2 kgf / 15 mm, less than 1 kgf / 15 mm, or less than 0.5 kgf / 15 mm at 120° C. or more. When the vent member 15 satisfies the above-mentioned seal strength in the above-mentioned temperature range, the seal strength of the portion of the case 13 into which the vent member 15 is inserted is reduced at high temperatures, for example, 100° C. or more, and the vent characteristics are more easily realized.

[0079] In one embodiment of the present invention, the vent member 15 may have an average seal strength of 4.5 kgf / 15 mm or more, or 5 kgf / 15 mm or more, or 6 kgf / 15 mm or more, or 7 kgf / 15 mm or more at room temperature to 60° C. If the vent member 15 satisfies the above-mentioned seal strength in the above-mentioned temperature range, even if the vent member 15 is inserted, when the battery operates normally, the portion of the case 13 into which the vent member 15 is inserted has excellent seal strength, making it easy to ensure the hermeticity of the battery.

[0080] In one embodiment of the present invention, the vent member 15 may have an average seal strength of less than 4.5 kgf / 15 mm at 100° C. or higher, and an average seal strength of 4.5 kgf / 15 mm or higher at room temperature to 60° C. When the vent member 15 has the above-mentioned seal strength in the above-mentioned temperature range, the seal strength of the portion of the case 13 into which the vent member 15 is inserted decreases at high temperatures, for example, 100° C. or higher, and the vent characteristics are easily realized. In addition, when the battery operates normally, the vent member 15 has excellent seal strength and is easy to ensure the hermeticity of the battery.

[0081] The sealing strength of the vent member 15 according to the temperature was measured by dividing the part of the case 13 into which the vent member 15 was inserted by 15 mm in width and 5 mm in length. cm After cutting into pieces, both ends are spread 180° and held using a Universal Testing Machine (UTM) jig, and a tensile test is performed at a speed of 5 mm / min to measure.

[0082] In this case, the maximum seal strength means the maximum value at which the case 13 breaks, and the average seal strength means the average value when the case 13 stretches by 8 mm at 4.5 kgf / 15 mm if the maximum seal strength is 4.5 kgf / 15 mm or more, and means the average value when the case 13 stretches by 8 mm at the maximum seal strength if the maximum seal strength is less than 4.5 kgf / 15 mm.

[0083] In one embodiment of the present invention, the linear low-density polyethylene having a comonomer having 6 or more carbon atoms may be one polymerized in the presence of a metallocene catalyst. When the linear low-density polyethylene having a comonomer having 6 or more carbon atoms is polymerized in the presence of a metallocene catalyst, it may be more advantageous in terms of seal strength and physical properties than when it is polymerized in the presence of a Ziegler-Natta catalyst.

[0084] In one embodiment of the present invention, the content of the comonomer having 6 or more carbon atoms in the linear low density polyethylene having a comonomer having 6 or more carbon atoms may be 15% by weight or less, or 12% by weight or less, or 11.8% by weight or less, or 10% by weight or less, or 9% by weight or less, or 8% by weight or less, or 7.6% by weight or less, based on 100% by weight of the linear low density polyethylene having a comonomer having 6 or more carbon atoms. At the same time, the content of the comonomer having 6 or more carbon atoms may be 5% by weight or more, or 7.6% by weight or more, or 8% by weight or more, or 9.0% by weight or more, or 10% by weight or more, or 11.8% by weight or more, or 12% by weight or more, based on 100% by weight of the linear low density polyethylene having a comonomer having 6 or more carbon atoms. When the content of the comonomer having 6 or more carbon atoms satisfies the above-mentioned range, the packing density between molecules is reduced, which makes it easier to prevent the problem of low seal strength when the battery operates normally.

[0085] The content of the comonomer having 6 or more carbon atoms can be measured by H-NMR. For example, about 10 mg of a sample is completely dissolved in about 0.6 mL of trichloroethylene solvent using a heat gun, and then sampled in a nuclear magnetic resonance (NMR) tube and measured by H-NMR.

[0086] In one embodiment of the present invention, the weight average molecular weight of the linear low density polyethylene having a comonomer having 6 or more carbon atoms may be 100,000 g / mol to 400,000 g / mol, or 200,000 g / mol to 350,000 g / mol, or 230,000 g / mol to 300,000 g / mol. When the weight average molecular weight of the linear low density polyethylene having a comonomer having 6 or more carbon atoms satisfies the above-mentioned range, the sealing strength can be further improved when the battery operates normally.

[0087] In one embodiment of the present invention, the polydispersity index (PDI) of the linear low density polyethylene having a comonomer having 6 or more carbon atoms may be 4 or less, or 3.8 or less, or 3.796 or less, or 3.5 or less, or 3.023 or less, or 3 or less, or 2.7 or less, or 2.674 or less. The polydispersity index (PDI) may be 1.0 or more. When the polydispersity index of the linear low density polyethylene having a comonomer having 6 or more carbon atoms satisfies the above-mentioned range, the molecular weight distribution is narrow, and the sealing strength and physical properties when the battery normally operates are further improved.

[0088] The weight average molecular weight and polydispersity index of the linear low density polyethylene having a comonomer having 6 or more carbon atoms may be measured by gel permeation chromatography (GPC) under the following conditions.

[0089] -Column: Tosoh HLC-8321 GPC / HT -Solvent: Trichlorobenzene (TCB) + 0.04% butylated hydroxytoluene (BHT) (dried with 0.1% CaCl2) -Flow rate: 1.0ml / min -Sample concentration: 1.5mg / ml -Injection volume: 300μl -Column temperature: 160°C -Detector: Refractive index (RI) detector -Standard: Polystyrene (corrected to a cubic function)

[0090] In one embodiment of the present invention, the crystallization temperature of the sealant resin may be approximately the same as that of the linear low-density polyethylene having a comonomer with 6 or more carbon atoms. For example, the difference between the crystallization temperature of the sealant resin and that of the linear low-density polyethylene having a comonomer with 6 or more carbon atoms may be 10° C. or less, or 5° C. or less. The difference between the crystallization temperature of the sealant resin and that of the linear low-density polyethylene having a comonomer with 6 or more carbon atoms may be 0.1° C. or more. When the difference between the crystallization temperature of the sealant resin and that of the linear low-density polyethylene having a comonomer with 6 or more carbon atoms satisfies the above-mentioned range, the fusion characteristics of the sealant resin and the linear low-density polyethylene having a comonomer with 6 or more carbon atoms during normal operation of the battery are further improved.

[0091] In one embodiment of the present invention, the crystallization temperature of the linear low density polyethylene having a comonomer having 6 or more carbon atoms may be 90° C. to 115° C., or 95° C. to 110° C., or 100° C. to 110° C., or 105° C. to 110° C. When the crystallization temperature of the linear low density polyethylene having a comonomer having 6 or more carbon atoms satisfies the above-mentioned range, the fusion properties of the sealant resin and the linear low density polyethylene having a comonomer having 6 or more carbon atoms are further improved.

[0092] In one embodiment of the present invention, the difference between the crystallization temperature of the sealant resin and the crystallization temperature of the linear low-density polyethylene having a comonomer having 6 or more carbon atoms may be 10°C or less, and the crystallization temperature of the linear low-density polyethylene having a comonomer having 6 or more carbon atoms may be 90°C to 115°C.

[0093] The crystallization temperature can be measured using a differential scanning calorimeter (DSC). For example, the temperature of the sample can be raised from 30°C to 280°C at 10°C / min, then maintained at 280°C for 10 minutes, cooled to 30°C at 10°C / min, and then maintained at 30°C for 10 minutes. The temperature of the sample can then be raised from 30°C to 280°C at 10°C / min, and then maintained at 280°C for 10 minutes to measure the crystallization temperature.

[0094] In one embodiment of the present invention, the vent member 15 may have various shapes to facilitate gas flow toward the vent region. For example, the vent member 15 may be in the form of a film.

[0095] The vent member 15 may be formed to have a predetermined thickness of a pre-set size.

[0096] In one embodiment of the present invention, as shown in Figures 1 and 2, a vent member 15 may be located at the seal.

[0097] 2, the vent member 15 may be located in a seal portion on a corner side of the case. For example, the vent member 15 may be located on a corner side of the seal portion where the electrode lead 11 is exposed to the outside. Specifically, the vent member 15 may be located in a seal portion next to the electrode lead 11, excluding the area between the electrode leads 11. When the vent member 15 is located on the corner side of the seal portion where the electrode lead 11 is exposed to the outside, the amount of gas discharged toward the electrode lead 11 can be minimized, and the safety of the battery can be further improved.

[0098] In one embodiment of the present invention, when seal portion 13b is sealed on three sides, the folded side of the case and one end of vent member 15 may be in close proximity.

[0099] Also, the vent member 15 may be inserted into the case 13 to different insertion lengths or to control the vent pressure and position depending on the design. Here, the insertion length of the vent member means the maximum distance between one end and the other end of the vent member based on the protruding direction of the electrode lead.

[0100] 4, the insertion length of the vent member 15 may be smaller than the width of the seal portion 13b. For example, the insertion length of the vent member 15 may be less than about 50% of the width of the seal portion 13b. Here, the width of the seal portion 13b means the maximum distance between one end and the other end of the seal portion 13b based on the protruding direction of the electrode lead 11.

[0101] 5, the insertion length of the vent member 15 may be greater than the width of the seal portion 13b. For example, the vent member 15 may be inserted so as to be exposed to the outside of the case 13 through the housing portion 13a.

[0102] In one embodiment of the present invention, the vent member 15 may further include an adhesive layer for even smoother placement.

[0103] FIG. 6 is a plan view showing a secondary battery according to still another embodiment of the present invention.

[0104] Referring to FIG. 6, the vent member 15 may be located in the sealing portion except the sealing portion where the electrode lead 11 is exposed to the outside.

[0105] FIG. 7 is a plan view showing a secondary battery according to still another embodiment of the present invention.

[0106] 7, the vent member 15 may be located in a seal portion where the electrode lead 11 is exposed to the outside. For example, the vent member 15 may be located in a seal portion between the electrode leads 11.

[0107] The secondary battery according to one embodiment of the present invention includes a vent member including a linear low-density polyethylene having a comonomer having six or more carbon atoms, which reduces the seal strength at high temperatures to more smoothly and quickly realize a directional vent that can discharge gas in a specific direction, and minimizes damage to electrodes caused by gas when a thermal runaway phenomenon occurs, i.e., when the internal temperature of the secondary battery rises.

[0108] In one embodiment of the present invention, the secondary battery may be a cylindrical, square, or pouch-type secondary battery, and in particular, the secondary battery may be a pouch-type secondary battery.

[0109] The present invention will be described in more detail below with reference to examples to aid in the understanding of the present invention. However, the examples according to the present invention can be modified into various other forms, and the scope of the present invention should not be construed as being limited to the following examples. The examples of the present invention are provided to more completely explain the present invention to those having average knowledge in the art.

[0110] Example 1

[0111] The upper pouch and the lower pouch, in which polyethylene terephthalate / aluminum foil / polypropylene resin were laminated in this order, were arranged so that the polypropylene resin faced each other, and then an electrode assembly, in which a positive electrode / separator / negative electrode were laminated in this order, was housed therein.

[0112] Next, a linear low-density polyethylene having a comonomer having 6 carbon atoms polymerized in the presence of a metallocene catalyst (Exxon Mobil Corporation, Exceed) was placed between the polypropylene resin. TM After inserting a vent member including a vent hole (not shown) into the battery, the battery was heat-sealed to produce a secondary battery.

[0113] Example 2

[0114] Linear low-density polyethylene having a comonomer with 6 carbon atoms polymerized in the presence of a metallocene catalyst (LG Chem, Lucene TM A secondary battery was produced in the same manner as in Example 1, except that a vent member containing SP311) was inserted between the polypropylene resin.

[0115] Example 3

[0116] Linear low-density polyethylene with a comonomer having 8 carbon atoms polymerized in the presence of a metallocene catalyst (Dow, Elite TM A secondary battery was manufactured in the same manner as in Example 1, except that a vent member containing 5401GT was inserted between the polypropylene resin.

[0117] Comparative Example 1

[0118] The upper pouch and the lower pouch, in which polyethylene terephthalate / aluminum foil / polypropylene resin were laminated in this order, were arranged so that the polypropylene resin faced each other, and then an electrode assembly, in which a positive electrode / separator / negative electrode were laminated in this order, was housed therein.

[0119] Next, the polypropylene resin was heat-sealed to manufacture a secondary battery.

[0120] Comparative Example 2

[0121] A secondary battery was manufactured in the same manner as in Example 1, except that a vent member containing linear low-density polyethylene having a comonomer having a carbon number of 4 polymerized in the presence of a Ziegler-Natta catalyst was inserted between the polypropylene resin.

[0122] Comparative Example 3

[0123] A secondary battery was manufactured in the same manner as in Example 1, except that a vent member containing high density polyethylene (SABIC HDPEF04660) was inserted between the polypropylene resin.

[0124] Evaluation example 1: Evaluation of the physical properties of the resin used in the vent material

[0125] The melting points, comonomer contents, weight average molecular weights, polydispersity indexes, and crystallization temperatures of the resins used in the vent members of Examples 1 to 3 and Comparative Example 2 (referred to as "vent resins" in this specification) and the sealant resin used in Comparative Example 1 were measured and are shown in Table 1 below.

[0126] (1) Measurement of melting point and crystallization temperature

[0127] The melting points and crystallization temperatures of the sealant resin used in Comparative Example 1 and the vent resins used in the vent members of Examples 1 to 3 and Comparative Example 2 were measured by the following method.

[0128] Using a differential scanning calorimeter (DSC), the temperature of the sample was raised from 30° C. to 280° C. at 10° C. / min, then maintained at 280° C. for 10 minutes, cooled to 30° C. at 10° C. / min, and maintained at 30° C. for 10 minutes. The temperature of the sample was then raised from 30° C. to 280° C. at 10° C. / min, then maintained at 280° C. for 10 minutes, and the melting point and crystallization temperature were measured.

[0129] (2) Measurement of comonomer content

[0130] The comonomer contents of the sealant resin used in Comparative Example 1 and the vent resins used in the vent members of Examples 1 to 3 and Comparative Example 2 were measured using H-NMR.

[0131] About 10 mg of a sample was completely dissolved in about 0.6 mL of trichloroethylene solvent using a heat gun, and then sampled in an NMR tube and measured using H-NMR.

[0132] (3) Measurement of weight average molecular weight and polydispersity index

[0133] The weight average molecular weight and polydispersity index of the sealant resin used in Comparative Example 1 and the vent resin used in the vent members of Examples 1 to 3 and Comparative Example 2 were measured by gel permeation chromatography (GPC) under the following conditions.

[0134] -Column: Tosoh HLC-8321 GPC / HT -Solvent: Trichlorobenzene (TCB) + 0.04% butylated hydroxytoluene (BHT) (dried with 0.1% CaCl2) -Flow rate: 1.0ml / min -Sample concentration: 1.5mg / ml -Injection volume: 300μl -Column temperature: 160°C -Detector: Refractive index (RI) detector -Standard: Polystyrene (corrected to a cubic function)

[0135] [Table 1]

[0136] Evaluation example 2: Measurement of seal strength as a function of temperature

[0137] In the secondary batteries manufactured in Examples 1 to 3 and Comparative Examples 2 to 3, the case of the portion where the vent member was inserted was cut to a width of 15 mm and a length of 5 cm at the temperature described below, and then both ends were spread 180° and held using a UTM jig, and a tensile test was performed at a speed of 5 mm / min. The seal strength of the case at this time is shown in Table 2 below.

[0138] In the secondary battery manufactured in Comparative Example 1, the case of the sealed portion was cut to a width of 15 mm and a length of 5 cm at the temperature below, and then both ends were spread 180° and held using a UTM jig, and a tensile test was performed at a speed of 5 mm / min. The seal strength of the case at this time is shown in Table 2 below.

[0139] In this case, the maximum seal strength means the maximum value at which the case breaks, and the average seal strength means the average value when the case stretches by 8 mm at 4.5 kgf / 15 mm if the maximum seal strength is 4.5 kgf / 15 mm or more, and means the average value when the case stretches by 8 mm at the maximum seal strength if the maximum strength is less than 4.5 kgf / 15 mm.

[0140] [Table 2]

[0141] As is clear from Table 2 above, it was confirmed that the maximum seal strength and average seal strength at room temperature to 60°C of the case part into which the vent member was inserted in the secondary batteries manufactured in Examples 1 to 3 were approximately the same as the maximum seal strength and average seal strength at room temperature to 60°C of the case of the secondary battery manufactured in Comparative Example 1. It was also confirmed that the maximum seal strength and average seal strength at 100°C or higher of the case part into which the vent member was inserted in the secondary batteries manufactured in Examples 1 to 3 were significantly lower than the maximum seal strength and average seal strength at 100°C or higher of the case of the secondary battery manufactured in Comparative Example 1.

[0142] In this way, the secondary batteries equipped with the vent members manufactured in Examples 1 to 3 can ensure an appropriate seal strength when the battery operates normally, but can release gas through the vent member with weakened seal strength when the battery becomes hot due to an abnormal phenomenon. In contrast, the secondary battery manufactured in Comparative Example 1 can ensure an appropriate seal strength when the battery operates normally, but can release gas in unspecified directions and cause chain fires of the battery when the battery becomes hot due to an abnormal phenomenon.

[0143] The maximum and average seal strengths at room temperature to 60° C. of the case parts into which the vent members were inserted in the secondary batteries manufactured in Comparative Examples 2 and 3 were significantly lower than the maximum and average seal strengths at room temperature to 60° C. of the case parts into which the vent members were inserted in the secondary batteries manufactured in Examples 1 to 3, and the seal strength was too low to be measured at temperatures above 100° C. From this, it was confirmed that the secondary batteries manufactured in Comparative Examples 2 and 3 were unable to ensure an appropriate seal strength when the batteries were operating normally. [Explanation of symbols]

[0144] 10 Secondary battery 11 Electrode Lead 12 Electrode assembly 13 cases 13a Storage section 13b Seal part 14 Lead Film 15 Venting material

Claims

1. An electrode assembly; an electrode lead attached to the electrode assembly; a case that accommodates the electrode assembly therein; a vent area formed in at least a portion of the case; a vent member inserted in the vent region, the vent member comprising a linear low density polyethylene having a comonomer having six or more carbon atoms; Including, the case includes a seal portion formed to seal the electrode assembly, The seal portion includes a sealant resin, The linear low density polyethylene having a comonomer having 6 or more carbon atoms of the vent member has a melting point lower than that of the sealant resin, The vent member has a maximum seal strength of less than 6 kgf / 15 mm at 100° C. or higher and a maximum seal strength of 6 kgf / 15 mm or higher at room temperature to 60° C.

2. 2. The secondary battery according to claim 1, wherein the vent member comprises a linear low density polyethylene having a comonomer having 6 to 8 carbon atoms.

3. 2. The secondary battery according to claim 1, wherein the vent member is melted at 100° C. to 120° C. to vent gas.

4. The secondary battery according to claim 3 , wherein the vent member vents gas at a pressure of 1.5 atm or more.

5. The secondary battery according to claim 1 , wherein the vent member has an average seal strength of less than 4.5 kgf / 15 mm at 100° C. or higher.

6. 2. The secondary battery according to claim 1, wherein the vent member has an average seal strength of 4.5 kgf / 15 mm or more at room temperature to 60°C.

7. 2. The secondary battery according to claim 1, wherein the linear low-density polyethylene having a comonomer having 6 or more carbon atoms is polymerized in the presence of a metallocene catalyst.

8. 2. The secondary battery according to claim 1, wherein the content of the comonomer having 6 or more carbon atoms is 15% by weight or less, based on 100% by weight of the linear low-density polyethylene having a comonomer having 6 or more carbon atoms.

9. 2. The secondary battery according to claim 1, wherein the linear low density polyethylene having a comonomer having 6 or more carbon atoms has a polydispersity index (PDI) of 4 or less.

10. 2. The secondary battery according to claim 1, wherein the difference between the crystallization temperature of the sealant resin and the crystallization temperature of the linear low-density polyethylene having a comonomer having 6 or more carbon atoms is 10° C. or less.

11. The secondary battery according to claim 10, wherein the linear low-density polyethylene having a comonomer having 6 or more carbon atoms has a crystallization temperature of 90°C to 115°C.

12. 2. The secondary battery according to claim 1, wherein the linear low-density polyethylene having a comonomer having 6 or more carbon atoms has a melting point of 100° C. to 130° C.

13. 2. The secondary battery according to claim 1, wherein the linear low-density polyethylene having a comonomer having 6 or more carbon atoms has a weight average molecular weight of 100,000 g / mol to 400,000 g / mol.

14. The secondary battery of claim 1 , wherein the vent area is located in the seal portion.

15. The secondary battery according to claim 14 , wherein the vent area is located in a seal portion on a corner side of the case.

16. The secondary battery according to claim 1 , wherein the secondary battery is a pouch-type secondary battery.

17. 2. The secondary battery according to claim 1, wherein the vent member has a maximum seal strength of less than 6 kgf / 15 mm at 100° C. to 120° C.

18. 2. The secondary battery according to claim 1, wherein the vent member has an average seal strength of less than 4.5 kgf / 15 mm at 100° C. to 120° C.

19. 2. The secondary battery according to claim 1, wherein the content of the comonomer having 6 or more carbon atoms is 5% by weight to 15% by weight, based on 100% by weight of the linear low-density polyethylene having a comonomer having 6 or more carbon atoms.

20. 2. The secondary battery according to claim 1, wherein the linear low-density polyethylene having a comonomer having 6 or more carbon atoms has a polydispersity index (PDI) of 1 to 4.

21. The secondary battery according to claim 1 , wherein the vent member has a maximum seal strength of less than 3 kgf / 15 mm at 120° C. or higher.

22. The secondary battery according to claim 1 , wherein the vent member has an average seal strength of less than 2 kgf / 15 mm at 120° C. or higher.

23. The secondary battery according to claim 1 , further comprising a lead film formed to enclose a portion of an outer surface of the electrode lead and interposed between the electrode lead and the case.