Plated steel sheet having thin aluminum alloy plating and plating method thereof

Abstract

The present invention relates to a plated steel sheet having a thin aluminum alloy plating and a plating method therefor. The plated steel sheet of the present invention is used for hot stamping. The plated steel sheet has a plating thickness of 5 μm to 14 μm, and the aluminum alloy plating includes an FeAlSi inhibition layer adjacent to the base steel sheet and an Al alloy layer outside the FeAlSi inhibition layer. The thickness of the FeAlSi inhibition layer is 60% or less of the plating thickness, and is 1.5 μm to 6.0 μm. Kirkendall voids located within 2 μm into the base steel from the interface between the FeAlSi inhibition layer and the base steel have a diameter of 2.5 μm or less, and the number of Kirkendall voids with a diameter of 0.5 μm or more and 2.5 μm or less does not exceed 15 per 35 μm. The present invention also discloses a plating method for applying a thin aluminum alloy plating to a base steel sheet for hot stamping. This method can eliminate missing plating, and hot stamped parts obtained using the plated steel sheet have excellent resistance spot welding performance.

Description

[Technical field]

[0001] The present invention relates to a plated steel sheet having a thin aluminum alloy plating and a plating method thereof. [Background technology]

[0002] In recent years, with the increasingly stringent requirements in energy and environmental protection, collision prevention regulations, and passenger passive safety, hot stamping processes are increasingly applied in the design and manufacture of automotive parts. In order to improve the strength and toughness of hot stamped parts formed by aluminum-silicon plated plates, Patent Document 1 (China Patent Application Publication No. 108588612) proposes to obtain hot stamped parts using plates with thin plating, in which the initial plating thickness of the plated steel sheet before hot stamping is 3 μm to 19 μm. However, it has been found that the production of plates with thin plating is prone to problems during production, such as large variations in the plating thickness, unstable production, and localized no plating.

[0003] In addition, during hot stamping, the plated steel sheet blank is first heated to 880°C to 960°C and held there, so that Fe in the base steel and Al in the initial plating diffuse to form an Fe-Al intermetallic compound on the plating side, and a high Al content interdiffusion layer is formed between the base steel and the Fe-Al intermetallic compound layer. The diffusion rate of Fe into the plating to form the Fe-Al intermetallic compound is much faster than the diffusion rate of Al into the base material, so if the diffusion continues, a large amount of Fe will diffuse into the plating, and the vacancies in the interdiffusion layer cannot be filled in time, forming Kirkendall voids. The locations where these Kirkendall voids exist have high electrical resistance, so that sparks are likely to fly during the welding process, leading to a decrease in welding performance. Patent Document 1 found that the use of a thin initial plating can suppress interdiffusion during hot stamping to a certain extent. Therefore, compared with a thick initial plating, the thin initial plating is expected to suppress the formation and growth of Kirkendall voids during hot stamping to a certain extent, resulting in improved resistance spot welding performance of hot stamped parts.

[0004] However, the inventors of the present application have discovered that even with thin initial platings, the resistance spot welding performance still requires further improvement. [Prior art documents] [Patent documents]

[0005] [Patent Document 1] China Patent Application Publication No. 108588612 Summary of the Invention [Problem to be solved by the invention]

[0006] The present invention has been made in consideration of the above problems existing in the prior art. One object of the present invention is to provide a plated steel sheet having a thin aluminum alloy plating for hot stamping, which can eliminate non-plating and enable hot stamped parts obtained by the plated steel sheet to have excellent resistance spot welding performance. [Means for solving the problem]

[0007] In order to achieve the above object, the aluminum alloy plating on at least one side of the plated steel sheet of the present invention has a plating thickness of 5 μm to 14 μm, the aluminum alloy plating includes an FeAlSi inhibition layer adjacent to the base steel and an Al alloy layer outside the FeAlSi inhibition layer, and the thickness of the FeAlSi inhibition layer is 60% or less of the plating thickness, i.e., 1.5 μm to 6.0 μm. Within 2 μm into the base steel from the interface between the FeAlSi inhibition layer and the base steel, the diameter of Kirkendall voids is 2.5 μm or less, and the number of Kirkendall voids having a diameter of 0.5 μm or more and 2.5 μm or less does not exceed 15 per 35 μm, preferably does not exceed 10 per 35 μm, and more preferably does not exceed 5 per 35 μm.

[0008] By reducing the thickness of the FeAlSi inhibition layer, no plating situations are eliminated, the variation in plating thickness is reduced, production stability is improved, and fewer and smaller Kirkendall voids in the base steel near the interface are formed, which helps to further suppress the formation of large voids during hot stamping, thereby improving the resistance spot welding performance of the subsequently formed hot stamped component.

[0009] Preferably, the plating thickness of the aluminum alloy plating on at least one side is 6 μm to 13 μm, and the thickness of the FeAlSi inhibition layer is 50% or less of the plating thickness, i.e., 1.5 μm to 5.0 μm. Within 2 μm from the interface to the inside of the base steel, the diameter of the Kirkendall voids is 2.5 μm or less, and the number of Kirkendall voids having a diameter of 0.5 μm or more and 2.5 μm or less does not exceed 13 per 35 μm, more preferably the diameter of the Kirkendall voids is 2.0 μm or less, and the number of Kirkendall voids having a diameter of 0.5 μm or more and 2.0 μm or less does not exceed 15 per 35 μm, preferably does not exceed 10 per 35 μm, and more preferably does not exceed 5 per 35 μm.

[0010] Preferably, the plating thickness of the aluminum alloy plating on at least one side is 7 μm to 12 μm, and the thickness of the FeAlSi inhibition layer is 40% or less of the plating thickness, i.e., 2.45 μm to 3.95 μm. Within 2 μm from the interface into the base steel, the diameter of the Kirkendall voids is 2.5 μm or less, and the number of Kirkendall voids having a diameter of 0.5 μm or more and 2.5 μm or less does not exceed 13 per 35 μm, more preferably, the diameter of the Kirkendall voids is 2.0 μm or less, and the number of Kirkendall voids having a diameter of 0.5 μm or more and 2.0 μm or less does not exceed 15 per 35 μm, preferably does not exceed 10 per 35 μm, and more preferably does not exceed 5 per 35 μm.

[0011] Smaller and fewer Kirkendall voids further improve the resistance spot welding performance of the subsequently formed hot stamped component.

[0012] Unless otherwise stated, the plating thickness, the thickness of the FeAlSi inhibit layer, and the thickness of the Al alloy layer herein are each the average of at least three corresponding measurements.

[0013] In order to meet the requirements of the hot stamping process regarding the hardenability of the steel sheet, i.e. to form a martensite dominated microstructure in the hot stamped part and to reach a strength of 900MPa to 2200MPa, the base steel sheet contains the following components by weight: 0.05% to 0.45% C, 0.5% to 10% Mn, 0% to 0.01% B, 0% to 0.4% Nb+Ti+V, 0.01% to 2% Si, 0.01% to 2% Al, 0.01% to 5% Cr+Ni+Mo+Cu, with 0% to 2% Cr, 0% to 2% Ni, 0% to 2% Mo and 0% to 2% Cu, with the balance being Fe and unavoidable impurity elements.

[0014] Preferably, the base steel sheet contains the following components by weight: 0.09 to 0.39% C, 0.6 to 3.5% Mn, 0 to 0.004% B, 0 to 0.4% Nb+Ti+V, 0.01 to 2% Si, 0.01 to 2% Al, 0.01 to 5% Cr+Mo+Ni+Cu, with 0 to 2% Cr, 0 to 2% Ni, 0 to 2% Mo, and 0 to 2% Cu, with the balance being Fe and unavoidable impurity elements.

[0015] More preferably, to obtain a hot stamped part with a predominantly martensite microstructure and a strength reaching 1400 MPa to 2100 MPa, the base steel sheet contains the following composition by weight: 0.18 to 0.39% C, 0.6 to 3.5% Mn, 0 to 0.004% B, 0.05 to 0.3% Nb+Ti+V, 0.01 to 2% Si, 0.01 to 2% Al, 0.01 to 5% Cr+Mo+Ni+Cu, with 0 to 2% Cr, 0 to 2% Ni, 0 to 2% Mo and 0 to 2% Cu, with the balance being Fe and unavoidable impurity elements.

[0016] Preferably, the thickness of the base steel sheet is from 0.5 mm to 3.0 mm.

[0017] Another object of the present invention is to provide a plating method for applying a thin aluminum alloy plating to a base steel sheet for hot stamping, which can eliminate unplated areas and enable a hot stamped part obtained from the plated steel sheet to have excellent resistance spot welding performance.

[0018] In order to achieve the above object, in the plating method of the present invention, the plating solution contains, by weight, 9% to 12% Si and 4% or less Fe, with the remainder being Al and unavoidable impurities.

[0019] Preferably, the Si content in the plating solution is between 9.2% and 11.2% by weight.

[0020] The plating method according to the present invention comprises: a) subjecting a base steel sheet to pretreatment before plating; b) heating the pretreated base steel sheet, and then cooling the base steel sheet to a predetermined temperature within a range of 610°C to 650°C, preferably 620°C to 645°C, more preferably 625°C to 639°C, and even more preferably 625°C to 635°C; c) immersing the base steel sheet cooled to the predetermined temperature in step b) in a heated plating solution for 2 to 7 seconds to perform hot-dip plating, wherein the temperature of the plating solution is higher than the predetermined temperature and is maintained at 630°C to 670°C, preferably 640°C to 660°C; d) removing excess plating solution from at least one surface by air knife purging after the base steel sheet is removed from the plating solution and before the plating solution solidifies on at least one surface, thereby controlling the plating thickness on at least one surface; e) cooling the steel sheet to room temperature to obtain a plated steel sheet having a thin aluminum alloy plating.

[0021] The plating method can be carried out in a continuous hot-dip plating process. The steps of pretreating the base steel sheet include, for example, degreasing, water washing, rust removal, hot water washing, auxiliary plating, drying, etc. In the process of hot-dip aluminum plating on the steel sheet, the heating of the base steel sheet can be carried out by induction heating, heating furnace and other methods. Preferably, the temperature of the plating solution is 5°C to 20°C higher, more preferably 7°C to 15°C higher than the predetermined temperature of the steel sheet entering the plating solution (i.e., the temperature of the steel sheet entering the pot). In step e), the cooling rate of the steel sheet is preferably 5°C / s or higher. Moreover, a person skilled in the art will understand that any range or any value within the above range is applicable to the present invention. For example, the predetermined temperature can be taken from any range within the range of 610°C to 650°C, or any specific value within the range of 610°C to 650°C, any range such as 610°C to 620°C, 635°C to 650°C, and 635°C to 645°C, or any value such as 612°C, 614°C, 616°C, 618°C, 620°C, 622°C, 624°C, 626°C, 628°C, 630°C, 632°C, 634°C, 636°C, 638°C, 640°C, 642°C, 644°C, 646°C, 648°C, etc.

[0022] The plated steel sheet obtained by the plating method of the present invention has a plating thickness of 5 μm to 14 μm, preferably 6 μm to 13 μm, more preferably 7 μm to 12 μm, and the thickness of the FeAlSi inhibition layer in the plating is 60% or less of the plating thickness and in the range of 1.5 μm to 6 μm, preferably 50% or less of the plating thickness and in the range of 1.5 μm to 5.0 μm, more preferably 40% or less of the plating thickness and in the range of 2.45 μm to 3.95 .... Within 2 μm inward, the diameter of the Kirkendall voids is 2.5 μm or less, and the number of Kirkendall voids having a diameter of 0.5 μm or more and 2.5 μm or less does not exceed 15 per 35 μm, preferably does not exceed 13 per 35 μm, more preferably does not exceed 5 per 35 μm, and even more preferably the diameter of the Kirkendall voids is 2.0 μm or less, and the number of Kirkendall voids having a diameter of 0.5 μm or more and 2.0 μm or less does not exceed 15 per 35 μm, preferably does not exceed 10 per 35 μm, and more preferably does not exceed 5 per 35 μm.

[0023] In the method of the present invention, the temperature of the plating solution in an aluminum pot and the temperature of the steel sheet entering the aluminum pot are reduced, the Si content in the plating solution is increased, and the residence time of the steel sheet in the plating solution is shortened. The synergistic effect of these factors suppresses interdiffusion between Fe in the substrate and Al in the plating, on the one hand, the resulting plating has a stable plating thickness with no plating, and on the other hand, suppresses the formation of Kirkendall voids in the substrate steel near the interface between the FeAlSi inhibition layer and the substrate steel, resulting in fewer voids and smaller diameters, thereby improving the resistance spot welding performance of the hot stamped part formed by the plated steel sheet. [Brief description of the drawings]

[0024] [Figure 1]FIG. 11 is a SEM photograph of a local plating form of a plated steel sheet according to a fifth embodiment of the present invention. [Diagram 2] FIG. 11 is a SEM photograph of a local plating form of a plated steel sheet according to Comparative Example 4. [Diagram 3] FIG. 4 is a photograph of a typical non-plating defect in the plated steel sheet according to Comparative Example 4. [Figure 4] FIG. 11 is a metallurgical microscope photograph of the local plating morphology of the sample plated steel sheets of Example 5 and Comparative Example 4 after hot stamping. [Diagram 5] FIG. 13 is a diagram showing the results of a spot welding performance test of the sample plated steel sheets of Example 5 and Comparative Example 4 after hot stamping. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0025] The present invention will be described in more detail below with reference to exemplary embodiments. The following embodiments or experimental data are intended to exemplify the present invention. It will be apparent to those skilled in the art that the present invention is not limited to these embodiments or experimental data.

[0026] The present invention provides a plated steel sheet for hot stamping and a plating method thereof.

[0027] In the hot dip aluminizing process, an alloying reaction occurs between Fe in the surface of the base steel and Al and Si in the plating solution, forming an FeSiAl intermetallic compound alloy layer, i.e., an FeAlSi inhibition layer, on the surface of the base steel. The formation of the FeAlSi inhibition layer on the surface of the base steel significantly reduces the interdiffusion of Fe and Al. There is an Al alloy layer on the outside of the FeAlSi inhibition layer, the thickness of which can be adjusted by air knife purging. When producing a thin plated sheet, if the Al alloy layer in the plating is too thin for a given plating thickness, it will lead to problems such as unstable plating thickness of the steel sheet during continuous production and frequent occurrence of localized non-plating phenomena, so the Al alloy layer should not be too thin. Therefore, in order to ensure a sufficient thickness of the Al alloy layer, it is necessary to obtain a thin FeAlSi inhibition layer on the surface of the steel sheet during plating.

[0028] Also, in the prior art, compared with the heating process of hot stamping, the temperature of the steel sheet before entering the plating solution is below 700°C, and the hot-dipping time is only a few seconds, so it is generally believed that the diffusion of alloying elements in the hot-dipping process is slow and the Kirkendall effect does not occur. However, after thorough investigation, the inventors of the present invention found that in the hot-dipping process, the outside of the steel substrate is liquid aluminum, so Fe atoms can still react quickly with Al and Si in the liquid aluminum to form intermetallic compounds (FeAlSi inhibition layer). The Kirkendall effect is essentially caused by the diffusion rate of Fe to the outside being much faster than the diffusion rate of Al into the iron substrate, and the existence of a few micrometers of FeAlSi inhibition layer in the plating formed by hot-dipping fully suggests that the phenomenon of Fe diffusion to the outside does indeed exist in the hot-dipping process, that is, Kirkendall voids can be formed. Through extensive microscopic observation, the inventors have found that a large number of Kirkendall voids do indeed exist within 2 μm into the substrate steel from the interface between the FeAlSi inhibition layer and the substrate steel, and are difficult to notice because their size is much smaller than the size of the voids after hot stamping. The present invention has found that the thicker the FeAlSi inhibition layer is, the more Fe diffuses to the outside, making it easier for Kirkendall voids to form. Therefore, by reducing the thickness of the FeAlSi inhibition layer, the diffusion of Fe elements in the substrate steel to the outside can be reduced, thereby reducing the formation of Kirkendall voids.

[0029] On the other hand, the present invention has found that in the subsequent hot stamping process, the Kirkendall effect voids formed in the hot dip plating process tend to grow quite rapidly, significantly increasing the resistance of the plating during spot welding, causing sparks to fly during welding, and seriously affecting the resistance spot welding performance of the hot stamped parts. Therefore, in order to ensure the resistance spot welding performance of the final parts, the present invention aims to achieve the objective of suppressing the formation of Kirkendall voids by controlling the hot dip plating conditions.

[0030] Therefore, the method of the present invention aims to obtain a thin FeAlSi inhibition layer and suppress the formation of Kirkendall voids in the base steel near the interface between the FeAlSi inhibition layer and the base steel, thereby improving the stability of the plating thickness, eliminating no plating situations, and improving the resistance spot welding performance of parts subsequently formed by hot stamping the plated steel sheet.

[0031] The plating solution used in the present invention contains, by weight, 9% to 12% Si, up to 4% Fe, Al or Al alloys and the balance consisting of unavoidable impurities.

[0032] Preferably, the Si content in the plating solution is between 9.2% and 11.2% by weight.

[0033] The plating method for a plated steel sheet for hot stamping according to the present invention comprises the steps of: a) subjecting a base steel sheet to pretreatment before plating; b) heating the pretreated base steel sheet, and then cooling the base steel sheet to a predetermined temperature within a range of 610°C to 650°C, preferably 620°C to 645°C, more preferably 625°C to 639°C, and even more preferably 625°C to 635°C; c) immersing the base steel sheet cooled to the predetermined temperature in step b) in a heated plating solution for 2 to 7 seconds to perform hot-dip plating, during which the temperature of the plating solution is higher than the predetermined temperature and is maintained at 630°C to 670°C, preferably 640°C to 660°C; d) removing excess plating solution from at least one surface by air knife purging after the base steel sheet is removed from the plating solution and before the plating solution solidifies on at least one surface, thereby controlling the plating thickness on at least one surface; e) cooling the steel sheet to room temperature to obtain a plated steel sheet having a thin aluminum alloy plating.

[0034] In the above method, the step of pretreating the base steel sheet includes, for example, degreasing, water washing, rust removal, hot water cleaning, auxiliary plating, drying, etc. In step c), the temperature of the plating solution is preferably 5°C to 20°C, more preferably 7°C to 20°C higher than the predetermined temperature of the steel sheet entering the plating solution. In step e), the cooling rate of the steel sheet is preferably 5°C / s or more.

[0035] In the method of the present invention, a plating solution with a high Si content is selected. The higher the Si content in the plating solution, the lower the melting point of the plating solution, making it easier to lower the temperature of the plating solution, thereby suppressing the interdiffusion of Al atoms and Fe atoms, resulting in a FeAlSi inhibition layer with a reduced thickness, and slowing the formation and growth of Kirkendall voids near the surface of the base steel sheet during hot dip plating and when the plated steel sheet is hot stamped thereafter. Therefore, the Si content is 9% or more. However, if the Si content is too high, the resistivity of the alloyed layer in the plating of the steel sheet after hot stamping the plated steel sheet increases, and the welding performance of the hot stamped part formed by the plated steel sheet decreases, so the Si content should not be too high. Therefore, the Si content cannot exceed 12%. Preferably, the Si content in the present invention is 9.2% to 11.2%.

[0036] Next, the present invention proposes to suppress the formation of Kirkendall effect voids by lowering the temperature of the plating solution and the predetermined temperature of the steel sheet entering the plating solution (i.e., the temperature of the steel sheet entering the pot). As mentioned above, during the formation of the FeSiAl inhibition layer, Fe atoms in the base steel diffuse into the plating solution to form FeSiAl intermetallic compounds, while Al atoms diffuse into the Fe base material. The diffusion of Fe and Al atoms in the base material occurs based on a vacancy mechanism, i.e., diffusion is achieved by exchanging the positions of metal atoms and vacancies. When the rate of Al atoms entering the base material is not sufficient to compensate for the number of Fe atoms diffusing out of the base material, voids will form in the base material due to the agglomeration of vacancies. Therefore, by suppressing the thickness and growth rate of the FeAlSi inhibition layer, the formation of Kirkendall effect voids can be effectively suppressed. Since it is well known that temperature has a large effect on the diffusion rate, the formation of Kirkendall effect voids can be suppressed by lowering the temperature of the plating solution and the predetermined temperature of the steel sheet entering the plating solution. On the one hand, it is possible to lower the predetermined temperature of the steel sheet entering the plating solution. The difference in the diffusion rates of Fe and Al atoms increases at high temperatures, resulting in the formation of a larger number of Kirkendall voids of larger size. Experimental data shows that when the predetermined temperature of the steel sheet entering the plating solution is higher than 655°C, a larger number of Kirkendall voids of larger size are formed observably in the base steel near the interface. However, in order to ensure the galvanizability of the steel sheet during hot dip plating and to prevent problems such as no plating on the surface, the predetermined temperature of the steel sheet entering the plating solution should not be too low. Experimental data shows that when the predetermined temperature of the steel sheet entering the plating solution is lower than 610°C, serious no plating occurs. Therefore, according to the present invention, the predetermined temperature of the steel sheet entering the plating solution is designed to be 610°C to 650°C, preferably 620°C to 645°C, more preferably 620°C to 639°C, and even more preferably 625°C to 635°C.On the other hand, it is believed that lowering the temperature of the plating solution leads to the inhibition of the alloying reaction between Fe, Al and Si atoms to form a thin inhibition layer. However, correspondingly, in order to ensure the fluidity and uniformity of the plating solution, the temperature of the plating solution should not be too low. Therefore, the temperature of the plating solution is designed to be higher than the predetermined temperature, 630°C to 670°C, preferably 640°C to 660°C.

[0037] Furthermore, the present invention proposes to shorten the residence time of the steel sheet in the plating solution. First, if the residence time is too long, the continuous interdiffusion of Fe and Al will be promoted, the FeAlSi inhibition layer will become thick, and Kirkendall voids will be formed. Second, the production line has a limited length, and if the residence time is too long, the operation speed of the production line must be slowed down, which will affect production efficiency and increase costs. Therefore, the residence time of the steel sheet in the plating solution needs to be controlled to 2 to 7 seconds.

[0038] Finally, the thickness of the Al alloy layer is controlled by maintaining a high intensity purge of an air knife to obtain a steel sheet having a thin aluminum alloy plating. Thus, after the base steel sheet is removed from the plating solution, before the plating solution on at least one side solidifies, excess plating solution on the at least one side is removed by air knife purging to control the plating thickness on the at least one side. The steel sheet is then cooled to room temperature, preferably at a cooling rate of 5°C / s or more, to obtain a plated steel sheet having a thin aluminum alloy plating.

[0039] Also, preferably, a relatively high temperature of the plating solution to ensure the platability is compatible with a low predetermined temperature of the steel sheet entering the plating solution to ensure a low reaction rate at the interface and to reduce the formation of Kirkendall voids. The present invention particularly points out that plating is performed under the condition that the predetermined temperature is lower than the temperature of the plating solution. Preferably, the predetermined temperature is 5°C or more lower than the temperature of the plating solution, so that the platability is ensured while the reaction rate at the interface is slowed down, resulting in a reduction in Kirkendall voids. On the other hand, if the difference between the temperature of the steel sheet and the temperature of the plating solution is too large, the temperature of the plating solution becomes unstable, so the temperature difference is designed not to exceed 20°C in the present invention. Preferably, the temperature difference is 7°C to 15°C.

[0040] According to the above-mentioned method of the present invention, a plated steel sheet having a thin aluminum alloy plating for hot stamping can be obtained. The thickness of the plated steel sheet is 0.5 mm to 3.0 mm. On any surface of the steel sheet, the plating thickness of the aluminum alloy plating is 5 μm to 14 μm, preferably 6 μm to 13 μm, more preferably 7 μm to 12 μm.

[0041] The above aluminum alloy plating is a FeAlSi inhibition layer adjacent to a base steel, the FeAlSi inhibition layer having a thickness of 1.5 μm to 6 μm at 60% or less of the plating thickness, preferably 1.5 μm to 5 μm at 50% or less of the plating thickness, more preferably 2.45 μm to 3.95 μm at 40% or less of the plating thickness, and within 2 μm into the base steel from the interface between the FeAlSi inhibition layer and the base steel, Kirkendall voids have a diameter of 2.5 μm or less and a diameter of 0.5 μm or more an FeAlSi inhibition layer in which the number of Kirkendall voids having diameters of 0.5 μm or more and 2.0 μm or less does not exceed 13 per 35 μm, preferably does not exceed 10 per 35 μm, more preferably does not exceed 5 per 35 μm, and even more preferably the diameter of the Kirkendall voids is 2.0 μm or less, and the number of Kirkendall voids having diameters of 0.5 μm or more and 2.0 μm or less does not exceed 13 per 35 μm, preferably does not exceed 10 per 35 μm, and more preferably does not exceed 5 per 35 μm; and an Al alloy layer on the outer side of the FeAlSi inhibition layer.

[0042] The FeAlSi inhibition layer is a compound layer of FeSiAl alloy formed by the reaction between Al and Si atoms in the plating solution and Fe atoms in the surface of the steel sheet when the steel sheet is immersed in the plating solution, and is mainly composed of Fe2SiAl7, and the mass ratio of Si element to the sum of Si element and Al element is higher than 0.12 and higher than the Si content in the plating solution. The thickness of the Al alloy layer is adjusted by an air knife to obtain different thicknesses of the aluminum-silicon plating.

[0043] In order to meet the requirements of the hot stamping process regarding the hardenability of the steel sheet, i.e. to form a martensite dominated microstructure in the hot stamped part and to reach a strength of 900 MPa to 2200 MPa, the base steel sheet contains the following components by weight: 0.05% to 0.45% C, 0.5% to 10% Mn, 0% to 0.01% B, 0% to 0.4% Nb+Ti+V, 0.01% to 2% Si, 0.01% to 2% Al, and 0.01% to 5% Cr+Ni+Mo+Cu, with 0% to 2% Cr, 0% to 2% Ni, 0% to 2% Mo, and 0% to 2% Cu, as well as unavoidable impurity elements.

[0044] In the plated steel sheet of the present invention, the base steel near the interface between the FeAlSi inhibition layer and the base steel has a small amount of Kirkendall voids with small diameter, which helps reduce the formation of large size voids in the plating of the hot stamped parts during hot stamping, thereby ensuring that the parts have good resistance spot welding performance. When the plating thickness is set, a thin FeAlSi inhibition layer means a thicker Al alloy layer, which is beneficial for air knife control, improves the stability of the plating thickness, and prevents the occurrence of no plating phenomenon.

[0045] As an example, the tested base steel sheet has the composition shown in Table 1, and the corresponding manufacturing process is as follows:

[0046] a) Steelmaking: melting according to the composition in Table 1 by vacuum induction furnace, electric furnace or converter, and using continuous casting technology to produce cast billets, or directly using continuous casting and rolling process of thin slabs. b) Hot rolling: the billet is heated to 1120°C to 1280°C and hot rolled, the total rolling reduction of the hot rolling is 50% or more, and final rolling is performed at a temperature of 800°C or more to obtain a hot rolled steel sheet, which is rolled at a temperature of 700°C or less to form a hot rolled steel strip, and the hot rolled strip is pickled to remove oxide scale generated during the hot rolling process. c) Cold rolling: The pickled hot rolled strip is cold rolled at a rolling ratio of 30% to 70% to obtain a cold rolled steel strip of 1.4 mm.

[0047] [Table 1]

[0048] The obtained base steel sheet is plated according to the plating process presented in Table 2. The target plating thickness is 8 μm to 12 μm, and the plating solution contains, by weight, 9% to 12% Si, 4% or less Fe, and the balance consisting of Al or Al alloy and unavoidable impurities. The plating process in Table 2 comprehensively considers the effects of hot-dip plating process parameters, such as the temperature of the plating solution, the predetermined temperature of the steel sheet entering the plating solution (i.e., the temperature of the steel sheet entering the pot), the temperature difference between the plating solution and the steel sheet, the hot-dip plating time, and the Si content in the plating solution.

[0049] [Table 2]

[0050] After the above plating process, the surface quality of the steel strip is macro-inspected to detect the non-plated state of the surface. The non-plated state of the surface includes all the states of the exposed base steel sheet and the exposed FeAlSi inhibition layer. Meanwhile, the plating thickness and the thickness of the FeAlSi inhibition layer within the plating thickness are determined as follows: Five positions, 1 / 6, 1 / 3, 1 / 2, 2 / 3, and 5 / 6 of the steel strip, are selected, and the thickness of the FeAlSi inhibition layer and the plating thickness are measured by a scanning electron microscope (SEM), and the average value of the measurement results of the five positions is calculated together with the deviation.

[0051] A method for determining the number of Kirkendall voids: Within the field of view of the SEM, count Kirkendall voids within a 35 μm length range along the surface of the base steel and measure their diameters. A method for determining the diameter of Kirkendall voids: Within the same field of view, measure the longest and shortest diameters of the voids, and use half the sum of the two diameters as the diameter of the void.

[0052] The statistical results for the plating structure, macroscopic surface, and the number of Kirkendall voids are shown in Table 3.

[0053] [Table 3]

[0054] With reference to the first to eighth embodiments, when the target coating thickness is 8 to 12 μm, the thickness of the FeAlSi inhibition layer obtained according to the method of the present invention is controlled to be about 2.9 to 4.1 μm, the thickness of the Al alloy layer is controlled to be about 5.1 to 8 μm, and the FeAlSi inhibition layer accounts for about 29% to 45% of the coating thickness. In this case, the coating thickness of the steel sheet is thin, but the FeAlSi inhibition layer is relatively thin, so that the thickness of the Al alloy layer is also adjusted by air knife purging, so that the control of the target coating thickness in the production process can be easily achieved, there is no no-coating phenomenon, and the variation in the final coating thickness is small. In addition, the maximum diameter of the Kirkendall voids near the interface between the base steel and the coating is 2 μm or less, and the number of the Kirkendall voids generally does not exceed 13 per 35 μm, which is easy to improve the resistance spot welding performance of the coated steel sheet after hot stamping. For example, a comparison of the data for embodiment 5 and embodiment 8 shows that the difference between the temperature of the plating solution and the temperature of the steel sheet entering the pot was 7° C. for embodiment 5, and the difference was 5° C. for embodiment 8. The number of Kirkendall voids for embodiment 8 was 8 per 35 μm, and the number of Kirkendall voids for embodiment 5 was 5 per 35 μm. It can be seen that an appropriate temperature difference results in a further reduction in the formation of Kirkendall voids.

[0055] 1 is an SEM photograph of the local plating morphology of the plated steel sheet according to embodiment 5 of the present invention. The plating thickness was about 9.0 μm, the thickness of the FeAlSi inhibition layer was about 3.2 μm, the diameter of the Kirkendall voids was 2.5 μm or less, and the number of Kirkendall voids having a diameter in the range of 0.5 μm to 2.5 μm was about 5 per 35 μm.

[0056] 2 is an SEM photograph of the local plating morphology of the plated steel sheet according to Comparative Example 4. The plating thickness was about 8.6 μm, the thickness of the FeAlSi inhibition layer was about 6.7 μm, and the number of Kirkendall voids having diameters ranging from 0.5 μm to 2.5 μm was about 29 per 35 μm.

[0057] The parameters of the plating process for embodiment 5 and comparative example 4 differ only in the temperature of the steel sheet entering the pot, and the temperature of the steel sheet entering the pot in comparative example 4 was significantly higher. Therefore, the higher Kirkendall voids and thicker FeAlSi inhibition layer in comparative example 4 are caused by the higher temperature of the steel sheet entering the pot. It can be seen that a high temperature of the steel sheet entering the pot is not desirable.

[0058] Figure 3 is a photo of a typical non-coating defect of the plated steel sheet according to Comparative Example 4. It can be clearly seen that serious non-coating occurs in several places. This is because, compared with embodiment 5, the higher temperature of the steel sheet entering the pot in Comparative Example 4 accelerates the diffusion, so that the generated FeAlSi inhibition layer becomes thicker and the Al alloy layer becomes thinner accordingly. As a result, the requirements for air knife purging become higher and the difficulties in control increase, which leads to non-coating.

[0059] Each comparative example shows different degrees of non-plating and has a large amount of Kirkendall voids with large size. This is because the Si content in the aluminum plating solution is too low in Comparative Example 1, the residence time of the steel sheet in the aluminum plating solution is too long in Comparative Example 2, the temperature of the steel sheet entering the pot is too high in Comparative Example 4, and the temperature of the plating solution is too high in Comparative Example 6. All the above four situations lead to the thickness of the finally obtained FeAlSi inhibition layer being thick, reaching 6.6 μm to 7.5 μm. As a result, the thickness of the Al alloy layer is thin, the measurement results of the thickness are significantly different depending on the position, the thickness uniformity is poor, the final plating thickness is obviously uneven, and there is a local non-plating, which affects the production stability of the steel sheet. In addition, in the above four cases, the number of Kirkendall voids with a diameter of 0.5 μm to 2.5 μm in the substrate steel near the interface between the substrate steel and the FeAlSi inhibition layer is large, reaching 17 to 29 per 35 μm. These large Kirkendall voids weaken the resistance spot welding performance of the resulting hot stamped parts. Thus, low Si content, long dwell time, high temperature of the steel sheet entering the pot, and high temperature of the plating solution all promote diffusion and result in the formation of more and larger Kirkendall voids. Therefore, all the four factors need to be controlled simultaneously to suppress the formation of Kirkendall voids under their synergistic effects.

[0060] Also, in Comparative Example 3, due to the low temperature of the steel sheet entering the pot, the surface temperature of the steel sheet is close to the solidification point of the Al-Si alloy. As a result, the steel sheet has poor galvanic properties, which leads to the occurrence of no-plating problems in many places. The large deviation also suggests that the thickness of the obtained FeAlSi inhibition layer and the plating thickness are quite uneven. In Comparative Example 5, the temperature of the plating solution is too low, so the fluidity and uniformity of the plating solution are poor. This also leads to poor plating quality, uneven plating thickness (large deviation), and locally existing no-plating phenomenon.

[0061] Considering the above and the data shown in Tables 2 and 3, it can be seen that the Si content in the coating solution, the temperature of the steel sheet entering the pot, the temperature of the coating solution, and the hot-dip coating time all significantly affect the thickness uniformity of the coating, non-coating, and the formation of Kirkendall voids. Any condition that exceeds the specified range will result in uneven coating thickness, non-coating, or the formation and growth of more Kirkendall voids, weakening the performance of the product. The synergistic effect of the range of the Si content in the coating solution, the range of the temperature of the steel sheet entering the pot, the range of the temperature of the coating solution, and the range of the hot-dip coating time selected in the present invention not only eliminates non-coating situations, but also reduces the number of large-sized Kirkendall voids, improving the yield of the coated steel sheet.

[0062] Therefore, the resistance spot welding performance of the hot stamped part formed later is also affected by the synergistic effect of the Si content in the plating solution, the temperature of the steel sheet entering the pot, the temperature of the plating solution, and the hot dip plating time. The following is an explanation of the effect of the plating process on the resistance spot welding performance of the hot stamped part, using only embodiment 5 and comparative example 4 as an example. In embodiment 5 and comparative example 4, the thin plate with a thin plating was subjected to simulated hot stamping. The heating process was performed in a laboratory tube furnace. The heating temperature was 930°C and was held as it is for 240 seconds. The heated sample plate was then removed and placed in a hot stamping simulation device and cooled to 100°C or less within 8 to 10 seconds. The plating morphology of the obtained hot stamped sample plate was observed, and the results are shown in FIG. 4.

[0063] As can be seen from FIG. 4, under the same hot stamping conditions, the final plating thickness in embodiment 5 is about 20 μm, the thickness of the interdiffusion layer is about 8.55 μm, while the final plating thickness in comparative example 4 is about 16.42 μm, and the thickness of the interdiffusion layer is about 9.83 μm. In addition, the Kirkendall voids in comparative example 4 are distributed substantially linearly. This corresponds to the data in Table 3, where the number of initial Kirkendall voids with diameters of 0.5 μm to 2.5 μm in embodiment 5 and comparative example 4 is 5 per 35 μm and 29 per 35 μm, respectively, the maximum diameter in embodiment 5 is 0.65 μm, and the maximum diameter of the initial voids in comparative example 4 is 1.71 μm. Since comparative example 4 originally had more Kirkendall voids with larger sizes, the voids in comparative example 4 are obviously more serious after undergoing the same hot stamping process.

[0064] A resistance spot welding experiment was carried out on the obtained hot stamped panel. The welding method and evaluation criteria refer to AWS D8.9M:2012 standard. Single pulse welding was selected. The welding parameters are as follows: diameter of electrode cap end face 7 mm, electrode pressure 5.5 kN, electrode preload time 400 ms, current application time 360 ​​ms, and post-current holding time 200 ms. FIG. 5 shows the spot welding evaluation results of two plated steel sheets after hot stamping. As can be seen from FIG. 5, the weldable current range for spot welding the hot stamped sample sheet in embodiment 5 was 1.2 kA, and the minimum welding current at which spatter occurred was 7.8 kA. Meanwhile, the weldable current range for spot welding the hot stamped sample sheet in comparative example 4 was 0.8 kA, and the minimum welding current at which spatter occurred was 7.4 kA. Obviously, the weldable current range of the hot stamped sample sheet in comparative example 4 is narrower, and the current at which spatter occurs is smaller. From the experimental results, it can be seen that the large amount of Kirkendall voids in Comparative Example 4 increases the contact resistance of the plating, and sparks easily occur even with a small welding current during spot welding, resulting in a reduction in the weldable current range of the steel sheet. On the other hand, the plated steel sheet (embodiment 5) obtained according to the present invention, which has fewer and smaller Kirkendall voids, improves the resistance spot welding performance of the hot stamped component.

[0065] In summary, the plating thickness of the aluminum alloy plating of the plated steel sheet of the present invention is 5 μm to 14 μm, and the thickness of the FeAlSi inhibition layer is 1.5 μm to 6 μm, which is 60% or less of the plating thickness. Within 2 μm from the interface between the FeAlSi inhibition layer and the base steel into the base steel, the diameter of the Kirkendall voids is 2.5 μm or less, and the number of Kirkendall voids with a diameter of 0.5 μm or more and 2.5 μm or less does not exceed 15 per 35 μm. The aluminum alloy plated steel sheet having the above plating characteristics can be a hot stamped part with excellent resistance spot welding performance. The plating method for producing the plated steel sheet of the present invention ensures the uniformity of the plating thickness, avoids the occurrence of non-plating on the surface, and at the same time suppresses the formation of large-sized Kirkendall voids, thereby ensuring good resistance spot welding performance of the hot stamped part.

[0066] The above embodiments and experimental data are intended to illustratively illustrate the present invention. It will be apparent to those skilled in the art that the present invention is not limited to these embodiments, and various modifications are possible without departing from the scope of protection of the present invention.

Claims

1. A plated steel sheet having an aluminum alloy plating for hot stamping, comprising a base steel sheet and the aluminum alloy plating applied to at least one surface of the base steel sheet, the base steel sheet contains the following components by weight: 0.05% to 0.45% C, 0.5% to 10% Mn, 0% to 0.01% B, 0% to 0.4% Nb+Ti+V, 0.01% to 2% Si, 0.01% to 2% Al, and 0.01% to 5% Cr+Ni+Mo+Cu, where 0% to 2% Cr, 0% to 2% Ni, 0% to 2% Mo, and 0% to 2% Cu, with the balance being Fe and unavoidable impurity elements; The plating thickness of the aluminum alloy plating is 5 μm to 14 μm, The aluminum alloy plating includes an FeAlSi inhibition layer adjacent to the base steel, and an Al alloy layer outside the FeAlSi inhibition layer, the thickness of the FeAlSi inhibition layer is 60% or less of the plating thickness, and the thickness of the FeAlSi inhibition layer is 1.5 μm to 6 μm; A plated steel sheet, wherein within 2 μm from an interface between the FeAlSi inhibit layer and the base steel into the base steel, Kirkendall voids have a diameter of 2.5 μm or less, and the number of Kirkendall voids having a diameter of 0.5 μm or more and 2.5 μm or less does not exceed 15 per 35 μm.

2. 2. The plated steel sheet according to claim 1, wherein the base steel sheet comprises the following components by weight: 0.09 to 0.39% C, 0.6 to 3.5% Mn, 0 to 0.004% B, 0 to 0.4% Nb+Ti+V, 0.01 to 2% Si, 0.01 to 2% Al, and 0.01 to 5% Cr+Mo+Ni+Cu, where 0 to 2% Cr, 0 to 2% Ni, 0 to 2% Mo, and 0 to 2% Cu, with the balance consisting of Fe and unavoidable impurity elements.

3. 2. The plated steel sheet according to claim 1, wherein the base steel sheet comprises the following components by weight: 0.18 to 0.39% C, 0.6 to 3.5% Mn, 0 to 0.004% B, 0.05 to 0.25% Nb+Ti+V, 0.01 to 2% Si, 0.01 to 2% Al, and 0.01 to 5% Cr+Mo+Ni+Cu, where 0 to 2% Cr, 0 to 2% Ni, 0 to 2% Mo, and 0 to 2% Cu, with the balance consisting of Fe and unavoidable impurity elements.

4. 2. The plated steel sheet according to claim 1, wherein the aluminum alloy plating has a plating thickness of 6 μm to 13 μm, the FeAlSi inhibition layer has a thickness of 50% or less of the plating thickness, and the FeAlSi inhibition layer has a thickness of 1.5 μm to 5 μm.

5. 2. The plated steel sheet according to claim 1, wherein the aluminum alloy plating has a plating thickness of 7 μm to 12 μm, the FeAlSi inhibition layer has a thickness of 40% or less of the plating thickness, and the FeAlSi inhibition layer has a thickness of 2.45 μm to 3.95 μm.

6. 6. The plated steel sheet according to claim 1, wherein within 2 μm from the interface between the FeAlSi inhibit layer and the base steel into the interior of the base steel, the number of Kirkendall voids having a diameter of 0.5 μm or more and 2.5 μm or less does not exceed 13 per 35 μm.

7. 6. The plated steel sheet according to claim 1, wherein within 2 μm from the interface between the FeAlSi inhibit layer and the base steel into the interior of the base steel, the number of Kirkendall voids having a diameter of 0.5 μm or more and 2.5 μm or less does not exceed 10 per 35 μm.

8. 6. The plated steel sheet according to claim 1, wherein within 2 μm from the interface between the FeAlSi inhibit layer and the base steel into the interior of the base steel, the Kirkendall voids have a diameter of 2.0 μm or less, and the number of Kirkendall voids having a diameter of 0.5 μm or more and 2.0 μm or less does not exceed 10 per 35 μm.

9. The plated steel sheet according to any one of claims 1 to 5, wherein the base steel sheet has a thickness of 0.5 mm to 3.0 mm.

10. A plating method for applying a thin aluminum alloy plating to at least one surface of a base steel sheet for hot stamping, comprising the steps of: a) subjecting the base steel sheet to a pretreatment process prior to plating; b) heating the pre-treated steel sheet and then cooling the steel sheet to a predetermined temperature within a range of 610°C to 650°C; c) immersing the base steel sheet cooled to the predetermined temperature in step b) in a heated plating solution for 2 to 7 seconds to perform hot-dip plating, the plating solution having a composition of 9.2% to 12% Si by weight and the balance consisting of Al or Al alloy and unavoidable impurities, and during the step, the temperature of the plating solution is maintained at 630°C to 670°C, which is higher than the predetermined temperature; d) removing excess plating solution on the at least one surface of the base steel sheet by air knife purging after the base steel sheet is removed from the plating solution and before the plating solution solidifies on the at least one surface of the base steel sheet, thereby controlling the thickness of the thin aluminum alloy plating on the at least one surface to 5 μm to 14 μm; e) cooling the base steel sheet to room temperature to obtain a plated steel sheet having the thin aluminum alloy plating; 13. A method according to claim 12, wherein the base steel sheet comprises the following components by weight: 0.05 to 0.45% C, 0.5 to 10% Mn, 0 to 0.01% B, 0 to 0.4% Nb+Ti+V, 0.01 to 2% Si, 0.01 to 2% Al, and 0.01 to 5% Cr+Ni+Mo+Cu, where 0 to 2% Cr, 0 to 2% Ni, 0 to 2% Mo, and 0 to 2% Cu, with the balance being Fe and unavoidable impurity elements.

11. 11. The method of claim 10, wherein the predetermined temperature is within the range of 620°C to 639°C, and the temperature of the plating solution is 5°C to 20°C higher than the predetermined temperature.

12. 11. The method of claim 10, wherein the predetermined temperature is within the range of 625°C to 635°C, and the temperature of the plating solution is 7°C to 15°C higher than the predetermined temperature.

Images