Nonaqueous electrolyte secondary battery and method of manufacturing positive electrode plate for nonaqueous electrolyte secondary battery

Abstract

To suppress high-rate deterioration caused by an insulating protective layer and suppress peeling of the insulating protective layer from a positive electrode current collector foil.SOLUTION: A lithium ion secondary battery includes a positive electrode plate, a negative electrode plate, a separator, and a nonaqueous electrolyte. The positive electrode plate includes a positive electrode current collector 31, a positive electrode composite material layer, and an insulating protective layer provided adjacent to the positive electrode composite material layer. The value of (insulator particles) / (insulator particles+binder) of the insulation protective layer is 75 [wt.%] or more and 85 [wt.%] or less, and the thickness TI of the insulating protective layer is 3.0 [μm] or more and 15 [μm] or less. The porosity PI of the insulating protective layer 34 is 42[%] or more and 55[%] or less. The value of (one-sided thickness TI of the insulating protective layer) / (thickness TP of the positive electrode composite layer) is set to be 0.12 or more and 0.80 or less.SELECTED DRAWING: Figure 4

Description

[Technical field]

[0001] The present invention relates to a nonaqueous electrolyte secondary battery and a method for manufacturing a positive electrode plate for the nonaqueous electrolyte secondary battery, and more particularly to a nonaqueous electrolyte secondary battery and a method for manufacturing a positive electrode plate for the nonaqueous electrolyte secondary battery that suppresses high-rate degradation. [Background technology]

[0002] Non-aqueous electrolyte secondary batteries such as lithium ion secondary batteries are preferably used as high-output power sources for vehicles because they are lightweight and can provide high energy density. In such non-aqueous electrolyte secondary batteries, a storage element in which a positive electrode and a negative electrode are insulated by a separator or the like is provided with a wound electrode body in which the positive electrode mixture layer is laminated and wound in an elliptical cylindrical shape in one battery case. In general, the positive electrode and the negative electrode of such an electrode body are designed so that the width dimension of the negative electrode mixture layer is wider than the width dimension of the positive electrode mixture layer. Therefore, the negative electrode mixture layer faces the positive electrode current collector with exposed metal through the separator. In this case, a short circuit does not usually occur due to the presence of the separator. However, heat may be generated by short circuiting through the separator due to metal precipitation in the negative electrode or penetration of metal fine powder.

[0003] For the purpose of preventing such short circuits, for example, Patent Document 1 discloses the following invention. That is, the positive electrode includes a positive current collector foil, an insulating protection layer containing an insulating material, and a positive electrode composite layer containing a positive electrode active material. The invention discloses an invention in which a positive electrode composite layer and an insulating protection layer are formed on at least one surface of the positive current collector foil of the positive electrode plate.

[0004] By providing such an insulating protective layer, the metal plate constituting the positive electrode current collector is covered with an insulator, and even if metallic Li precipitates or foreign matter such as metal powder enters, it is possible to effectively prevent a short circuit with the negative electrode composite layer through the separator.

[0005] Furthermore, Patent Document 1 discloses a configuration in which the overlapped portion of the insulating protection layer is covered by the overlapping portion of the positive electrode mixture layer, thereby preventing the insulating protection layer from peeling off from the positive electrode current collector foil. [Prior art documents] [Patent documents]

[0006] [Patent Document 1] JP 2017-157471 A Summary of the Invention [Problem to be solved by the invention]

[0007] In non-aqueous electrolyte secondary batteries, electrolyte migration occurs when charging and discharging at a high rate. If the non-aqueous electrolyte cannot migrate sufficiently due to an insulating protective layer in the cell battery, the concentration of the non-aqueous electrolyte becomes uneven. This can cause battery deterioration, known as "high-rate deterioration." However, the invention described in Patent Document 1 does not disclose any recognition of this problem.

[0008] Furthermore, although the insulating protection layer is prevented from peeling off from the positive electrode current collector foil at the overlapping portion with the positive electrode mixture layer, no configuration is disclosed for preventing the insulating protection layer itself from peeling off. The problem to be solved by the nonaqueous electrolyte secondary battery and the method for producing a positive electrode plate for a nonaqueous electrolyte secondary battery of the present invention is to suppress high-rate deterioration caused by the insulating protective layer and to suppress peeling of the insulating protective layer from the positive electrode current collector foil. [Means for solving the problem]

[0009] In order to solve the above problems, the non-aqueous electrolyte secondary battery of the present invention includes a positive electrode plate, a negative electrode plate, a separator that insulates the positive electrode plate and the negative electrode plate, and a non-aqueous electrolyte. The positive electrode plate includes a positive electrode current collector, a positive electrode mixture layer that is provided on at least one part of the surface of the positive electrode current collector and contains positive electrode active material particles and a conductor, and an insulating protection layer that is provided on another part of the surface of the positive electrode current collector and is adjacent to the positive electrode mixture layer and contains insulating particles and a binder, the insulating protection layer has a mass composition such that a value of (insulating particles) / (insulating particles+binder) is 75 [wt%] or more and 85 [wt%] or less, and the one-side thickness T of the insulating protection layer is I is 3.0 [μm] or more and 15 [μm] or less, and the porosity P of the insulating protective layer is I is 42[%] or more and 55[%] or less, and (one-sided thickness of the insulating protective layer T I ) / (Thickness of one side of the positive electrode composite layer T P ) is 0.12 or more and 0.80 or less.

[0010] The thickness of the insulating protective layer on one side T I ) / (Thickness of one side of the positive electrode composite layer T P ) is 0.12 or more and 0.60 or less, and the density D P is 2.2 [g / cm 3 ] or more, 3.0[g / cm 3 ] or less, and the porosity P P may be set to 30% or more and 50% or less.

[0011] The conductor of the positive electrode mixture layer is desirably a conductive material with an aspect ratio of 30 or more, and the conductor can suitably be carbon nanotubes or carbon nanofibers. Density of the insulating protective layer D I to 1.2 [g / cm 3 ] or more, 1.6[g / cm 3 ] or less, and the peel strength can be 10 [N] or more.

[0012] It is also preferable that the positive electrode mixture layer overlaps the insulating protection layer at a boundary portion where the positive electrode mixture layer and the insulating protection layer are adjacent to each other. The insulating particles may be made of boehmite or alumina.

[0013] In the method for producing a positive electrode plate for a non-aqueous electrolyte secondary battery of the present invention, the positive electrode plate includes a positive electrode plate, a negative electrode plate, a separator for insulating the positive electrode plate and the negative electrode plate, and a non-aqueous electrolyte, the positive electrode plate includes a positive electrode current collector, a positive electrode mixture layer that is provided on at least one part of the surface of the positive electrode current collector and contains positive electrode active material particles and a conductor, and an insulating protection layer that is provided on another part of the surface of the positive electrode current collector and is adjacent to the positive electrode mixture layer and contains insulator particles and a binder. the positive electrode current collector is coated simultaneously with an insulating protective paste containing positive electrode active material particles, a conductor, a binder, and a solvent, and a positive electrode composite paste containing positive electrode active material particles, a conductor, a binder, and a solvent, to form the positive electrode composite layer, the insulating protective layer adjacent to the positive electrode composite layer, and a boundary portion where the positive electrode composite layer and the insulating protective layer overlap; a positive electrode composite layer pressing step of pressing the positive electrode composite layer; and a boundary portion and insulating protective layer pressing step of simultaneously pressing the insulating protective layer and the boundary portion.

[0014] It is preferable that, in the boundary portion, the insulating protection layer is formed on the positive electrode current collector, and the positive electrode mixture layer is formed on top of the insulating protection layer. The boundary portion and insulating protection layer pressing step can use a roller press using a stepped roll having different radii that presses the insulating protection layer and the boundary portion but does not press the positive electrode mixture layer.

[0015] The boundary portion and insulating protection layer pressing step may be performed by applying tension to the positive electrode current collector to press the insulating protection layer and the boundary portion against the stepped roll. Effect of the Invention

[0016] The nonaqueous electrolyte secondary battery and the method for manufacturing a positive electrode plate for a nonaqueous electrolyte secondary battery of the present invention have the effect of suppressing high-rate deterioration caused by the insulating protective layer and suppressing peeling of the insulating protective layer from the positive electrode current collector. [Brief description of the drawings]

[0017] [Figure 1] 1 is a perspective view showing an outline of the configuration of a lithium ion secondary battery according to an embodiment of the present invention; [Diagram 2] FIG. 2 is a schematic diagram showing the configuration of a wound electrode body of the present embodiment. [Diagram 3] FIG. 2 is a schematic partial cross-sectional view showing the laminated configuration of an electrode body of a lithium ion secondary battery. [Figure 4] 4 is a schematic diagram showing a boundary portion B between a positive electrode composite layer and an insulating protection layer in a coating step of the present embodiment, the boundary portion B being an enlarged view of a portion A in FIG. 3. FIG. [Diagram 5] 4 is a flowchart showing a method for manufacturing a positive electrode plate according to the present embodiment. [Figure 6] FIG. [Figure 7] FIG. 2 is a schematic perspective view showing a first nozzle and a second nozzle including a cross section seen from a CC portion of a coating machine. [Figure 8] FIG. 4 is a schematic diagram showing the state of the electrode body 12 after completion of the coating step (S3). [Figure 9] FIG. 13 is a schematic diagram showing a positive electrode mixture layer pressing step (S5). [Figure 10] FIG. 11 is a schematic perspective view showing the boundary portion and the insulating protective layer pressing step (S6). [Figure 11] FIG. 11 is a schematic cross-sectional view showing the boundary portion and the insulating protective layer at the start of a pressing step (S6). [Figure 12] 10A to 10C are schematic cross-sectional views showing the boundary portion and the action in the insulating protective layer pressing step (S6). [Figure 13] 1 is a table showing the results of an experimental example. [Figure 14] FIG. 2 is a schematic diagram showing an electrode body of the present embodiment. [Figure 15]FIG. 1 is a schematic diagram showing an electrode body of the prior art. [Figure 16] 1 is a schematic diagram showing a state in which an insulating protective layer with an excessively large porosity PI causes a foreign object short circuit. [Figure 17] 1 is a schematic diagram showing an insulating protective layer having a small porosity PI according to the present embodiment. [Figure 18] FIG. 2 is a schematic diagram showing an insulating protective layer that has fallen off because the porosity PI is too large or the thickness TI is too thin. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0018] (Outline of this embodiment) The method for producing a nonaqueous electrolyte secondary battery and a positive electrode plate of the present invention will be described with reference to one embodiment of a method for producing a lithium ion secondary battery 1 and a positive electrode plate thereof with reference to FIGS.

[0019] <Previous issues> Fig. 15 is a schematic diagram showing a conventional electrode body 12. As described in the conventional technology, by providing insulating protective layers 34 adjacent to both ends of a positive electrode mixture layer 32 as shown in Fig. 15, it was possible to suppress micro-short circuits.

[0020] However, in the lithium ion secondary battery 1, when charging and discharging are performed at a high rate, the electrolyte moves. In this case, as shown in FIG. I However, the thickness T of the positive electrode mixture layer 32 P In such a conventional configuration, the movement of the electrolyte is hindered by the insulating protective layer 34 in the cell battery, causing uneven concentration. This causes the battery to deteriorate, which is known as "high-rate deterioration."

[0021] 14 is a schematic diagram showing the electrode body 12 of the present embodiment. In the electrode body 12 of the lithium ion secondary battery 1 of the present embodiment, the thickness T I The thickness T of the positive electrode mixture layer 32 P By making it thinner, the non-aqueous electrolyte 13 can move more easily.

[0022] <Porosity P[%]> Here, the porosity P [%] is a measure of the amount of space including interparticle voids, etc. Since the porosity P [%] is generally proportional to the permeability coefficient, in this embodiment, it is used as an index showing the efficiency with which the electrolyte 13 in the cell flows to the positive electrode mixture layer 32.

[0023] On the other hand, the porosity P [%] also serves as an index of the distance between the positive electrode active material particles 32b in the positive electrode mixture layer 32. The porosity P [%] can be measured, for example, by the immersion method, in which a porous sample is immersed in a liquid with good wetting properties and the pores are saturated with the liquid. Alternatively, an optical method can be used to determine the material area and the area of ​​visible pores through microscopic observation of the sample cross section. Furthermore, it can be measured by the mercury intrusion method, in which mercury, which has a strong surface tension, is forced into minute pores, and the amount of intrusion is measured against the amount of pressure applied from the outside to determine the distribution of pore diameters and pore volume.

[0024] <Changes in void ratio P [%] during pressing process> In the positive electrode mixture layer 32, the decrease in porosity P [%] reduces the distance between the positive electrode active material particles 32b in the positive electrode mixture layer 32, improving the conductive path and enhancing the battery performance.

[0025] However, in the invention described in Patent Document 1, the insulating protective layer 34 is also pressed and compressed, so that the distance between the insulating particles 34b in the insulating protective layer 34 is reduced. This reduces the porosity P [%]. When the porosity P [%] decreases, the efficiency of exchange of the electrolyte 13 in the positive electrode mixture layer 32 decreases. This causes unevenness in the concentration of the electrolyte 13 in the battery, particularly during high-rate charging and discharging, which causes the battery to deteriorate, i.e., the so-called "high-rate deterioration."

[0026] FIG. 16 shows the thickness T P Thinner thickness T I When the insulating protective layer 34 is formed in the above-mentioned manner, the porosity P I 4 shows the case where the insulating protective layer 34 is excessively large. Porosity PI This is a schematic diagram showing a state in which the strength decreases and a foreign object short circuit occurs when the porosity P I The higher the porosity P, the easier the electrolyte migration becomes. I If the thickness becomes too large, for example, if a metal with a sharp edge such as copper (Cu) is mixed in, the foreign matter may break through the insulating protective layer 34, causing a short circuit.

[0027] FIG. 17 shows the porosity P I FIG. 1 is a schematic diagram showing an insulating protective layer 34 having a small porosity P I This prevents excessive increase in the strength of the insulating protective layer 34. Since the strength of the insulating protective layer 34 is high, insulation can be maintained even if metal with sharp edges, such as copper (Cu), is mixed in.

[0028] Furthermore, as described above, the thickness T I is thinned and the porosity P I The movement of the nonaqueous electrolyte 13 was improved under the condition that the lower limit was set. Even if the mechanical strength of the insulating protective layer 34 is increased to ensure the insulating properties, a problem will occur if the insulating protective layer 34 peels off.

[0029] Figure 18 shows the porosity P I is too large, or the thickness T I 1 is a schematic diagram showing an insulating protective layer 34 that has fallen off due to being too thin, etc. Even if the above conditions are satisfied, if the insulating protective layer 34 peels off from the positive electrode current collector 31, a part of the insulating protective layer 34 may become a foreign body. Therefore, in this embodiment, in order to solve the problem of the insulating protective layer 34 peeling off, it was necessary to determine the conditions.

[0030] In order to solve these multiple problems simultaneously, the inventors have analyzed through many experiments a configuration that solves these problems simultaneously by changing various conditions. <Specific conditions in this embodiment> The present inventors have found through experiments that the following numerical ranges are suitable for each purpose.

[0031] <(thickness T of the insulating protective layer 34 on one side I ) / (thickness T of positive electrode mixture layer 32 P )> In order to prevent high-rate deterioration, the insulating protective layer 34 of this embodiment has a thickness T I The thickness is 15 μm or less. I / D P By setting the value of D to 0.12 to 0.80, a gap is secured so as not to impede the movement of the nonaqueous electrolyte 13. I / D P The value is more preferably 0.1 to 0.6.

[0032] <Porosity P of the insulating protective layer 34 I > In addition, to prevent high rate deterioration, the porosity P I is kept below 55% so as not to impede the movement of electrolytes.

[0033] On the other hand, in order to ensure the insulation of the insulating protective layer 34, the porosity P I The mechanical strength is ensured by setting the thickness at 42% or more. <Density D of the insulating protective layer 34 I > The thickness T of the insulating protective layer 34 on one side I Therefore, the density D of the insulating protective layer 34 is set to 1. I to 1.2 [g / cm 3 ] or more.

[0034] On the other hand, in order to promote the movement of the electrolyte, the density D I to 1.6 [g / cm 3 ] below. <One-side thickness T of the insulating protective layer 34 I > In order to ensure the strength of the insulating protective layer 34, the thickness T I was set to 3.0 μm or more.

[0035] <Composition of insulating protective layer 34> In order to prevent the insulating protective layer 34 from peeling off from the positive electrode current collector 31, the value of (insulating particles 34b) / (insulating particles 34b+binder 34c) in the mass composition of the insulating protective layer 34 is set to 85% or less. Therefore, sufficient binder 34c prevents the insulating protective layer 34 from peeling off from the positive electrode current collector 31.

[0036] On the other hand, to ensure insulation, the value of (insulating particles 34b) / (insulating particles 34b+binder 34c) is set to 75% or more. Therefore, the insulating particles 34b, which have high hardness, prevent the intrusion of even metallic foreign objects, ensuring sufficient insulation.

[0037] <Peel strength> The insulating protective layer 34 has a porosity P I Decrease the density again to D I Even if the strength of the insulating protective layer 34 itself is increased by increasing the peel strength, if peeled off, the insulating protective layer 34 itself may become a foreign object. Therefore, it is more preferable to set the peel strength to 10 [N] or more. In order to increase the peel strength, it is possible to achieve this by selecting an appropriate binder 34c or by setting the value of (insulating particles 34b) / (insulating particles 34b+binder 34c) to 85 [%] or less.

[0038] <Density D of the positive electrode mixture layer 32 P > Density D of the positive electrode mixture layer 32 P [g / cm 3 ] is 2.2 [g / cm 3 By setting the density of the positive electrode active material particles 32b to be equal to or greater than 1, the density of the positive electrode active material particles 32b is increased, thereby ensuring the battery performance.

[0039] In addition, the density D of the positive electrode mixture layer 32 P [g / cm 3 ] is 3.0 [g / cm 3 ] or less, which facilitates the movement of electrolytes. <Porosity P of the positive electrode mixture layer 32 P > Porosity P of the positive electrode mixture layer 32P By making the ratio 50[%] or less, the density of the positive electrode active material particles 32b is increased, thereby ensuring the battery performance.

[0040] Porosity P of the positive electrode mixture layer 32 P By setting the content to 30% or more, the electrolyte can move more easily. <Aspect ratio> Porosity P of the positive electrode mixture layer 32 P In order to improve the aspect ratio of the conductor 32c, the aspect ratio is preferably 30 or more. Here, the "aspect ratio" refers to the ratio of the length and diameter of the fiber. If the aspect ratio is 30 or more, an effective conductive network can be formed even with a small mass, so the amount of the conductor added to the positive electrode mixture layer 32 can be reduced to increase the porosity P P As the conductor 32c having such characteristics, for example, carbon nanotubes (CNT) or carbon nanofibers (CNF) may be used.

[0041] (Configuration of this embodiment) <Configuration of lithium-ion secondary battery 1> 1 is a perspective view showing the outline of the configuration of a lithium ion secondary battery 1 according to the present embodiment. Next, the configuration of the lithium ion secondary battery 1 according to the present embodiment will be described.

[0042] As shown in FIG. 1, the lithium ion secondary battery 1 is configured as a cell battery. The lithium ion secondary battery 1 includes a rectangular parallelepiped battery case 11 having an opening on the upper side. An electrode body 12 is housed inside the battery case 11. A nonaqueous electrolyte 13 is filled into the battery case 11 through a filling hole. The battery case 11 is made of a metal such as an aluminum alloy, and forms a sealed battery container. The lithium ion secondary battery 1 also includes a positive electrode external terminal 14 and a negative electrode external terminal 15 used for charging and discharging power. The shapes of the positive electrode external terminal 14 and the negative electrode external terminal 15 are not limited to those shown in FIG. 1.

[0043] <Electrode body 12> 2 is a schematic diagram showing the configuration of a wound electrode assembly 12. The electrode assembly 12 is formed by winding a large number of negative electrode plates 2 and positive electrode plates 3, with separators 4 arranged between them, flatly. The negative electrode plates 2 have a negative electrode composite layer 22 formed on a negative electrode current collector 21 that serves as a base material. A negative electrode connection part 23 is provided at one end in a width direction W (winding axis direction) perpendicular to the winding direction (winding direction L), where the negative electrode composite layer 22 is not formed and the negative electrode current collector 21 is exposed.

[0044] In the positive electrode plate 3, a positive electrode composite layer 32 is formed on a positive electrode collector 31 serving as a base material. As shown in Fig. 2, a positive electrode connection part 33 is provided on the other end side (opposite to the negative electrode connection part 23) in a width direction W (winding axis direction) perpendicular to the direction in which the positive electrode collector 31 is wound (winding direction L). No positive electrode composite layer 32 is formed on the positive electrode connection part 33, and the metal of the positive electrode collector 31 is exposed.

[0045] In this embodiment, an insulating protective layer 34 is provided adjacent to an end of the positive electrode mixture layer 32 and facing the negative electrode mixture layer 22. The insulating protective layer 34 is provided so as to cover the exposed positive electrode current collector 31.

[0046] <Layer structure of electrode body 12> 3 is a schematic partial cross-sectional view showing the laminated configuration of the electrode body 12 of the lithium-ion secondary battery 1. As shown in FIG. 2, the electrode body 12 of the lithium-ion secondary battery 1 basically comprises a negative electrode plate 2, a positive electrode plate 3, and a separator 4.

[0047] The negative electrode plate 2 includes a negative electrode mixture layer 22 on both sides of a negative electrode current collector 21 serving as a negative electrode base material. One end of the negative electrode current collector 21 serves as a negative electrode connection portion 23 where the metal is exposed. The positive electrode plate 3 includes a positive electrode mixture layer 32 on both sides of a positive electrode current collector 31 serving as a positive electrode base material. The other end of the positive electrode current collector 31 serves as a positive electrode connection portion 33 where the metal is exposed.

[0048] The negative electrode plate 2 and the positive electrode plate 3 are stacked with a separator 4 interposed therebetween to form a laminate. This laminate is wound in the longitudinal direction around a winding axis, and formed into a flat wound electrode body 12.

[0049] In this embodiment, an insulating protective layer 34 is provided on the positive electrode current collector 31 adjacent to the positive electrode connection portion 33 side of the positive electrode mixture layer 32. In the case where there is no insulating protective layer 34 as in the conventional case, the positive electrode current collector 31 is exposed from the end a on the positive electrode connection portion 33 side of the positive electrode mixture layer 32 to the positive electrode side. In this case, the positive electrode current collector 31 and the negative electrode mixture layer 22 face each other through the separator 4 from the end a to the end b on the positive electrode side of the negative electrode mixture layer 22. At this time, metal fine powder may be mixed in this position, or dendrites of metal Li may grow in the negative electrode mixture layer 22. If these penetrate the separator 4, a short circuit may occur between the negative electrode mixture layer 22 and the positive electrode current collector 31, which may cause heat generation or self-discharge. Therefore, in this embodiment, the insulating protective layer 34 is provided from the end a to the end c beyond the end b. This insulating protective layer 34 can suppress such a short circuit.

[0050] <Nonaqueous electrolyte 13> As shown in FIG. 1, the nonaqueous electrolyte 13 is filled in a battery container formed by a battery case 11. The nonaqueous electrolyte 13 of the lithium ion secondary battery 1 is a composition in which a lithium salt is dissolved in an organic solvent. Examples of the lithium salt include LiClO4, LiPF6, LiAsF6, LiBF4, and LiSO3CF3. Examples of the organic solvent include cyclic carbonates such as ethylene carbonate, propylene carbonate, butylene carbonate, and trifluoropropylene carbonate, chain carbonates such as diethyl carbonate, dimethyl carbonate, ethyl methyl carbonate, and dipropyl carbonate, ether compounds such as tetrahydrofuran, 2-methyltetrahydrofuran, and dimethoxyethane, sulfur compounds such as ethyl methyl sulfone and butane sultone, and phosphorus compounds such as triethyl phosphate and trioctyl phosphate. One or more of these can be mixed and used as the nonaqueous electrolyte. The composition of the nonaqueous electrolyte 13 is not limited to this.

[0051] <Components of electrode body 12> Next, the negative electrode plate 2, the positive electrode plate 3, and the separator 4, which are the components that make up the electrode assembly 12, will be described.

[0052] In this embodiment, the "average diameter" refers to the median diameter (D 50 Average particle size (50% volume average particle size) refers to the average particle size in the range of approximately 1 μm or more, which can be determined by the laser diffraction / light scattering method. In addition, average particle size in the range of approximately 1 μm or less can be determined by the dynamic light scattering (DLS) method. The average particle size based on the DLS method can be measured in accordance with JIS Z 8828:2013.

[0053] <Negative electrode plate 2> The negative electrode plate 2 is constituted by forming a negative electrode mixture layer 22 on both sides of a negative electrode current collector 21, which is a negative electrode base material. In this embodiment, the negative electrode current collector 21 is made of Cu foil. The negative electrode current collector 21 serves as a base for the aggregate of the negative electrode mixture layer 22, and also functions as a current collecting member that collects electricity from the negative electrode mixture layer 22. In this embodiment, the negative electrode active material is a material capable of absorbing and releasing lithium ions, and a powdered carbon material made of graphite or the like is used.

[0054] The negative electrode plate 2 is produced, for example, by kneading a negative electrode active material, a solvent, and a binding material (binder), applying the kneaded negative electrode mixture paste to the negative electrode current collector 21, and drying it. <Positive electrode plate 3> The positive electrode plate 3 is composed of a positive electrode current collector 31, and a positive electrode mixture layer 32 and an insulating protective layer 34 that are applied to the positive electrode current collector 31.

[0055] <Positive electrode current collector 31> A positive electrode mixture layer 32 is formed on both sides of a positive electrode current collector 31, which is a positive electrode base material, to form a positive electrode plate 3. In this embodiment, the positive electrode current collector 31 is made of an Al foil. The positive electrode current collector 31 serves as a base for the aggregate of the positive electrode mixture layer 32, and also functions as a current collecting member that collects electricity from the positive electrode mixture layer 32.

[0056] First, the positive electrode base material constituting the positive electrode current collector 31 is exemplified as an Al foil, but may be made of a conductive material made of a metal having good conductivity. As the conductive material, for example, a material containing aluminum or a material containing an aluminum alloy may be used. The configuration of the positive electrode current collector 31 is not limited to this.

[0057] <Positive electrode mixture layer 32> Fig. 4 is an enlarged schematic diagram of a portion indicated by portion A in Fig. 3, showing a boundary portion B between the positive electrode mixture layer 32 and the insulating protective layer 34 in the coating step (S3) of this embodiment. The positive electrode mixture layer 32 will be described with reference to Fig. 4. The positive electrode mixture layer 32 is formed by coating a positive electrode mixture paste 32a on a positive electrode current collector 31 and drying the coating. The positive electrode mixture layer 32 contains, in addition to positive electrode active material particles 32b, a conductor 32c, a binder 32d, and additives such as a dispersant.

[0058] <Positive electrode mixture paste 32a> The positive electrode mixture paste 32a is prepared by adding a solvent 32e to additives such as a conductor 32c, a binder 32d, and a dispersant in addition to positive electrode active material particles 32b. The positive electrode mixture layer 32 is formed by applying the positive electrode mixture paste 32a to the positive electrode current collector 31 in a coating step (S3) shown in FIG. 4. The positive electrode mixture layer 32 is then dried and fixed in a drying step (S4). The positive electrode mixture paste 32a shown in FIG. 4 contains the solvent 32e. However, in the positive electrode mixture layer 32 after the drying step (S4), the solvent 32e has volatilized and disappeared.

[0059] <Composition of Positive Electrode Active Material Particles 32b> The primary particles of the positive electrode active material particles 32b contain a lithium transition metal oxide having a layered crystal structure. The lithium transition metal oxide contains one or more predetermined transition metal elements in addition to Li. The transition metal element contained in the lithium transition metal oxide is preferably at least one of Ni, Co, and Mn. A suitable example of the lithium transition metal oxide is a lithium transition metal oxide containing all of Ni, Co, and Mn.

[0060] The positive electrode active material particles 32b may additionally contain one or more elements in addition to the transition metal element (i.e., at least one of Ni, Co, and Mn). As the additional element, any element belonging to Group 1 (alkali metals such as sodium), Group 2 (alkaline earth metals such as magnesium and calcium), Group 4 (transition metals such as titanium and zirconium), Group 6 (transition metals such as chromium and tungsten), Group 8 (transition metals such as iron), Group 13 (boron which is a semi-metal element or a metal such as aluminum), and Group 17 (halogens such as fluorine) of the periodic table can be included.

[0061] In a preferred embodiment, the positive electrode active material particles 32b may have a composition (average composition) represented by the following general formula (1). Li1+xNiyCozMn(1-y-z)MAαMBβO2…(1) In the above formula (1), x can be a real number satisfying 0 ≦ x ≦ 0.2. y can be a real number satisfying 0.1 < y < 0.6. z can be a real number satisfying 0.1 < z < 0.6. MA is at least one metal element selected from W, Cr, and Mo, and α is a real number satisfying 0 < α ≦ 0.01 (typically 0.0005 ≦ α ≦ 0.01, for example 0.001 ≦ α ≦ 0.01). MB is one or more elements selected from the group consisting of Zr, Mg, Ca, Na, Fe, Zn, Si, Sn, Al, B, and F, and β can be a real number satisfying 0 ≦ β ≦ 0.01. β may be substantially 0 (i.e., an oxide substantially free of MB). In the chemical formula indicating the layered lithium transition metal oxide, for convenience, the composition ratio of O (oxygen) is shown as 2. However, this numerical value should not be strictly interpreted and some composition variations (typically included in the range of 1.95 or more and 2.05 or less) can be tolerated.

[0062] <Conductor 32c> The conductor 32c is a material for forming a conductive path in the positive electrode mixture layer 32. By mixing an appropriate amount of a conductor into the positive electrode mixture layer 32, the conductivity inside the positive electrode can be increased, and the charge / discharge efficiency and output characteristics of the battery can be improved. As the conductor 32c in this embodiment, for example, a carbon material such as carbon nanotube (CNT) or carbon nanofiber (CNF) can be used. In addition, a string-shaped conductor with an aspect ratio of 30 or more is used.

[0063] <Binding material 32d> For example, polyvinylidene fluoride (PVdF), polytetrafluoroethylene (PTFE), polyacrylic acid, polyacrylate, or the like can be used for the binder 32d.

[0064] <Configuration of insulating protective layer 34> 2, the positive electrode plate 3 has a positive electrode mixture layer 32 formed on a positive electrode current collector 31, and an insulating protection layer 34 formed adjacent to the positive electrode mixture layer 32 and at a position facing an end of the negative electrode mixture layer 22 on the positive electrode current collector 31. The insulating protection layer 34 has insulating particles 34b fixed in a dispersed state by a binder 32d. The insulating protection layer 34 is formed by applying an insulating protection paste 34a to the surface of the positive electrode current collector 31 along the end of the positive electrode mixture layer 32 and drying it.

[0065] <Insulating protective paste 34a> The insulating protection paste 34a is a paste in which a binder 34c is added with a solvent 34d to make it liquid, and the insulating particles 34b are dispersed in the paste. A dispersant is also added to disperse the insulating particles 34b evenly within the paste.

[0066] The insulating protective layer 34 is formed by applying an insulating protective paste 34a to the positive electrode current collector 31 in a coating step (S3) shown in Fig. 6, and then drying and fixing the paste in a drying step (S4). The insulating protective paste 34a shown in Fig. 5 contains a solvent 32e. However, in the insulating protective layer 34 after the drying step (S4), the solvent 32e has volatilized and disappeared.

[0067] <Insulating particle 34b> The insulating particles 34b are disposed between the negative electrode mixture layer 22 and the positive electrode current collector 31 to provide electrical insulation. Examples of the insulating particles 34b include ceramics obtained by sintering metal oxides, which have high insulating properties and hardness sufficient to prevent the intrusion of foreign matter. Specifically, particles of boehmite or alumina are used. In this embodiment, boehmite is used.

[0068] <Boehmite> Boehmite is an aluminum hydroxide (γ-AlO(OH)) mineral and a component of the aluminum ore bauxite. It exhibits a vitreous to pearlescent luster, a Mohs hardness of 3-3.5, and a specific gravity of 3.00-3.07. It has high insulating, heat-resistant, and hardness properties, and industrially it can be used as an inexpensive flame-retardant additive for fire-resistant polymers.

[0069] Boehmite has the chemical composition AlO(OH) or Al2O3·H2O, and is generally a chemically stable alumina monohydrate produced by heating or hydrothermally treating alumina trihydrate in air. Boehmite has a high dehydration temperature of 450-530°C, and by adjusting the production conditions, it can be controlled into various shapes such as plate-like boehmite, needle-like boehmite, and hexagonal plate-like boehmite. In addition, the aspect ratio and particle size can be controlled by adjusting the production conditions.

[0070] Various methods for producing boehmite have been proposed, but the most common method is to hydrothermally treat aluminum hydroxide, a raw material derived from bauxite. This method includes a stirring and mixing step of a slurry of aluminum hydroxide, a reaction promoter (metal compound), and water. It also includes a hydrothermal treatment step of wet curing while heating in a steam atmosphere in a pressure vessel. It also includes the steps of dehydrating the reaction product, washing with water, filtering, and drying.

[0071] <Particle size of insulating particles 34b> As mentioned above, the average particle size [μm(D 50If the average particle diameter [μm(D 50 ) is set to 1 to 3 μm.

[0072] <Binding material 34c> The binder 34c may be, for example, polyvinylidene fluoride (PVdF), polytetrafluoroethylene (PTFE), polyacrylic acid, polyacrylate, or the like.

[0073] <Separator 4> The separator 4 may be a porous resin sheet made of a resin such as polyethylene (PE) or polypropylene (PP) for holding the non-aqueous electrolyte solution 13 between the positive electrode plate 3 and the negative electrode plate 2. Such a porous resin sheet may have a single-layer structure using various materials alone, or a multi-layer structure combining various materials.

[0074] <Method of Manufacturing Positive Electrode Plate 3> 5 is a flowchart showing a method for manufacturing the positive electrode plate 3 of this embodiment. The method for manufacturing the positive electrode plate 3 of this embodiment will be described with reference to FIG.

[0075] <Positive electrode composite paste manufacturing process (S1)> First, the positive electrode composite paste 32a is produced, as described above in detail. <Insulating protection paste manufacturing process (S2)> Additionally, the insulating protective paste 34a is produced, the details of which have already been described.

[0076] <Coating process (S3)> Next, the coating step (S3) will be described. The coating step (S3) is a step of simultaneously coating the positive electrode composite paste 32a produced in the positive electrode composite paste production step (S1) and the insulating protective paste 34a produced in the insulating protective paste production step (S2) on predetermined positions of the positive electrode current collector 31.

[0077] <Configuration of Coating Machine 5> Fig. 6 is a perspective view showing a coating process. Fig. 7 is a schematic perspective view showing a first nozzle 53 and a second nozzle 55 including a cross section seen from a CC portion of the coater 5. The coater 5 will be described with reference to Figs. 6 and 7.

[0078] As shown in FIG. 6, the coating machine 5 includes a stage 57 serving as a base. The stage 57 includes a positioning guide 58 for transporting the positive electrode current collector 31 made of Al foil formed in a long strip shape before cutting. The positive electrode current collector 31 is drawn from a supply reel (not shown) and transported on the stage 57 by a transport means. A gate-shaped die nozzle 51 is provided at the end of the stage 57 on the upstream side in the transport direction of the positive electrode current collector 31, in a direction perpendicular to the transport direction, so as to straddle the positive electrode current collector 31. The die nozzle 51 includes a first die 52 for storing the positive electrode composite paste 32a. The first die 52 is a space provided at a position corresponding to the position where the positive electrode composite layer 32 is formed. The positive electrode composite paste 32a is supplied from a supply means (not shown) and stored in the first die 52. The second die 54 is a space provided at a position corresponding to the position where the insulating protective layer 34 is formed. The insulating protective paste 34a is supplied from a supplying means (not shown) and stored in the second die 54. The first die 52 and the second die 54 are adjacent to each other and aligned in the same straight line.

[0079] First nozzle 53 is a nozzle that communicates from the lower part of first die 52 to a position on stage 57 where positive electrode mixture layer 32 of positive electrode current collector 31 is to be formed. When the internal pressure of first die 52 is increased by a pressurizing means (not shown), a predetermined amount of positive electrode mixture paste 32a is discharged from first nozzle 53 to the position where positive electrode mixture layer 32 of positive electrode current collector 31 is to be formed.

[0080] The second nozzle 55 is a nozzle that communicates from the lower part of the second die 54 to a position on the stage 57 where the insulating protective layer 34 of the positive electrode current collector 31 is to be formed. When the internal pressure of the second die 54 is increased by a pressurizing means (not shown), a predetermined amount of the insulating protective paste 34a is discharged from the second nozzle 55 to the position where the insulating protective layer 34 of the positive electrode current collector 31 is to be formed.

[0081] As shown in FIG. 7, the first nozzle 53 and the second nozzle 55 are separated from each other. The positive electrode composite paste 32a discharged from the first nozzle 53 and the insulating protection paste 34a discharged from the second nozzle 55 are brought into contact with each other so as to be in close contact with each other immediately after discharge. In the contacted state, the positive electrode composite paste 32a is applied to the positive electrode current collector 31 at a position where the positive electrode composite layer 32 is to be formed. In addition, in the contacted state, the insulating protection paste 34a is applied to the positive electrode current collector 31 at a position where the insulating protection layer 34 is to be formed. Thereafter, the surfaces of the positive electrode composite layer 32 and the insulating protection layer 34 formed by application are shaped by the roller 56. Note that since the insulating protection layer 34 is thinner than the positive electrode composite layer 32, only the positive electrode composite layer 32 is shaped.

[0082] <Electrode body 12 after coating process (S3)> FIG. 8 shows the state of the electrode body 12 after the coating step (S3) is completed. As shown in FIG. 8, an insulating protective layer 34 is coated on a part of a positive electrode current collector 31. Then, a positive electrode mixture layer 32 is coated so as to be adjacent to the insulating protective layer 34. At this time, the positive electrode mixture layer 32 is coated so as to overlap the insulating protective layer 34 at its end. This overlapping portion of the positive electrode mixture layer 32 and the insulating protective layer 34 is called a boundary portion B. Here, the thickness to which the positive electrode mixture layer 32 is coated is called a thickness T P The thickness of the insulating protective layer 34 is called thickness T I These thicknesses T P and thickness T I The thickness of the positive electrode mixture layer 32 at this stage is called thickness T P1 Let us assume that.

[0083] Air bubbles are likely to form at the boundary between positive electrode mixture layer 32 and insulating protection layer 34 in boundary portion B. Such air bubbles can cause peeling from this portion, so it is desirable to remove them.

[0084] <Drying process (S4)> As described above, the drying step (S4) is performed in a state in which the positive electrode mixture paste 32a and the insulating protection paste 34a are mixed together after the coating step (S3) to generate the mixed layer M. The drying step (S4) causes the solvent 32e of the positive electrode mixture layer 32 to volatilize, and the paste-like positive electrode mixture layer 32 becomes a solid and does not mix with the insulating protection layer 34. The solvent 34d of the insulating protection layer 34 also volatilizes, and the paste-like insulating protection layer 34 becomes a solid and does not mix with the positive electrode mixture layer 32. The mixture is stable in this state.

[0085] <Positive electrode composite layer pressing process (S5)> 9 is a schematic diagram showing the positive electrode composite layer pressing step (S5). When the drying step (S4) is completed, the positive electrode composite layer 32 and the insulating protection layer 34 shown in FIG. 8 have already reached a certain hardness. From the state shown in FIG. 8, the positive electrode composite layer pressing step (S5) uses a pressing machine (not shown) to shape the layer into a flat surface of a predetermined thickness. Even after the drying step (S4), the thickness T of the insulating protection layer 34 remains constant. I is the thickness T of the positive electrode mixture layer 32 P As shown in FIG. 9, the press roll 71 of the press machine 7 used in the positive electrode composite layer pressing step (S5) presses the entire positive electrode plate 3 after the drying step (S4). At this time, the thickness T of the insulating protective layer 34 is 100 mm, as shown in FIG. I is the thickness T of the positive electrode mixture layer 32 P1 Since the positive electrode mixture layer 32 is thinner, the press roll 71 is pressed against the entire positive electrode mixture layer 32. At this time, the gap of the press roll 71 is set to a value equal to the thickness T P1 The thickness T of the insulating protective layer 34 is smaller than the thickness T of the insulating protective layer 34. P2 Therefore, in the positive electrode mixture layer pressing step (S5), only positive electrode mixture layer 32 is pressed. As a result, positive electrode mixture layer 32 has a thickness T P2 In addition, a portion of insulating protection layer 34 at boundary portion B is also pressed together with positive electrode mixture layer 32.

[0086] On the other hand, no load is applied from the press roll 71 to the other parts of the insulating protective layer 34 . <Boundary and insulating protection layer pressing process (S6)> 10 is a schematic perspective view showing the boundary portion and insulating protective layer pressing step (S6). In the boundary portion and insulating protective layer pressing step (S6), a constant tension is applied to the long positive electrode plate from a reel (not shown) in which it is housed, and the long positive electrode plate is pressed against a stepped roll 81 of a press machine 8 for pressing the boundary portion and the insulating protective layer.

[0087] FIG. 11 is a schematic cross-sectional view showing the start of the boundary and insulating protection layer pressing step (S6). As shown in FIG. 11, the stepped roll 81 has a cylindrical first surface 81a with the largest radius, a cylindrical third surface 81c with the smallest radius, and a truncated cone-shaped second surface 81b connecting the first surface 81a and the third surface 81c. The first surface 81a is located mainly facing the insulating protection layer 34. The second surface is located mainly facing the boundary B. The third surface is located mainly facing the positive electrode mixture layer 32 not including the boundary B. Of these, the third surface 81c is provided with a gap so as not to come into contact with the positive electrode mixture layer 32. Note that a surface perpendicular to the rotation axis is provided between the second surface 81b and the third surface 81c, forming a large gap so that the third surface 81c does not come into contact with the positive electrode mixture layer 32.

[0088] In other words, when tension is applied to the positive electrode collector 31 of the long positive electrode plate 3 relative to the stepped roll 81, the boundary portion B and the insulating protective layer 34 of the positive electrode plate 3 are sandwiched between the tensioned positive electrode collector 31 and the stepped roll 81, and the boundary portion B and the insulating protective layer 34 are pressed.

[0089] 12 is a schematic diagram showing the action in the boundary portion and insulating protective layer pressing step (S6). As shown in FIG. 12, tension is applied to the positive electrode collector 31, so that the positive electrode plate 3 is pressed against the stepped roll 81 by the positive electrode collector 31. Then, the first surface 81a brings the insulating protective layer 34 into close contact with the positive electrode collector 31. At the same time, the second surface 81b brings the boundary portion B into close contact with the positive electrode collector 31. As a result, the insulating protective layer 34 is compressed by the first surface 81a, and the thickness T of the insulating protective layer 34 is reduced. I [μm] is adjusted to a specified thickness. I As the density D I [g / cm3 In addition, boundary portion B is compressed by second surface 81b, and thickness T P [μm] and the thickness T of the insulating protective layer 34 I At the same time, the porosity P P As the density D P [g / cm 3 At the same time, the porosity P I As the density D I [g / cm 3 Furthermore, air bubbles 36 (see FIG. 8) that have occurred at the boundary between positive electrode mixture layer 32 and insulating protection layer 34 at boundary portion B disappear.

[0090] In the boundary and insulating protection layer pressing step (S6), tension is applied to the long positive electrode current collector 31 wound on a storage reel (not shown), and the positive electrode plate 3 is pressed against the stepped roll 81. As in the positive electrode composite layer pressing step (S6) shown in FIG. 9, when the positive electrode plate 3 placed on the hard and flat stage 57 is pressed against the hard press roll 71, if there are irregularities on the surface of the positive electrode plate 3, the shape of the press roll 71 is strongly transferred. On the other hand, in the boundary and insulating protection layer pressing step (S6), tension is applied to the positive electrode current collector 31, and the positive electrode plate 3 is pressed against the stepped roll 81. At this time, the positive electrode current collector 31 is a thin metal foil made of Al or an Al alloy, and is therefore easily bent. For this reason, it deforms according to the shapes of the positive electrode composite layer 32 and the insulating protection layer 34 on the surface of the positive electrode plate 3, and the entire positive electrode composite layer 32 and the insulating protection layer 34 can be evenly pressed against the stepped roll 81.

[0091] In the above-described boundary and insulating protective layer pressing step (S6), the strength of the pressing is adjusted to thereby reduce the thickness T I [μm], porosity P I [%], density D I [g / cm 3 In addition, the thickness T P [μm], porosity P P [%], density DP [g / cm 3 ] can be adjusted.

[0092] <Cutting process (S7)> In the boundary and insulating protection layer pressing step (S6), when the thickness, porosity, and density are adjusted to the desired values, the manufacture of the positive electrode composite layer 32 and the insulating protection layer 34 is completed, and in the cutting step (S6), they are cut to a length that matches the electrode body 12. In this way, the positive electrode plate 3 is completed.

[0093] <Manufacturing method for vehicle battery packs> When the positive electrode plate 3 is completed by such a manufacturing method of the positive electrode plate 3, it is stacked with the negative electrode plate 2 in multiple stages via the separator 4 and wound to manufacture the electrode body 12. Thereafter, the electrode body 12 is fitted with the positive electrode external terminal 14 and the negative electrode external terminal 15 via the lid of the battery case 11. Then, the electrode body 12 is housed in the battery case 11, and the lid is airtightly joined by laser welding or the like. After a drying process, the nonaqueous electrolyte 13 is filled and sealed in a liquid injection process. Then, a cell battery is completed through conditioning such as initial charging, OCV inspection, internal resistance inspection, and aging. A plurality of cell batteries are stacked to form an assembled battery. Furthermore, a plurality of assembled batteries are housed in a battery pack, and a control device for monitoring and controlling charging and discharging is installed, and the battery is completed as an in-vehicle lithium-ion secondary battery.

[0094] (Action of this embodiment) <Experimental Example> 13 is a table showing the results of an experimental example. The lithium ion secondary battery 1 of this embodiment has the configuration as described above. Experiments were conducted to compare Examples 1 to 4 configured in this manner with Comparative Examples 1 to 6 that do not have the configuration of this embodiment as described above.

[0095] <Conditions for the Lithium-Ion Secondary Battery 1 of the Present Embodiment> First, the conditions of the invention for the lithium ion secondary battery 1 of this embodiment are shown as "standard". Thickness T of the insulating protective layer 34 I [μm] is 3 to 20 [μm].

[0096] Porosity P of the insulating protective layer 34 I [%] is greater than or equal to 42[%] and less than or equal to 55[%]. The mass composition [wt%] of the insulating protective layer 34 is (insulating particles 34b) / (insulating particles 34b+binder 34c) is 75 wt% or more and 85 wt% or less. In the case of the binder 34c, the value of (binder 34c) / (insulating particles 34b+binder 34c) is 15 wt% or more and 25 wt% or less.

[0097] (Thickness of the insulating protective layer on one side T I [μm]) / (Thickness of the positive electrode composite layer on one side T P [μm]) is 0.12 or more and 0.80 or less. The resistance increase rate (internal resistance DC-IR) is 1.15 or less.

[0098] The insulating protective layer 34 does not fall off from the positive electrode current collector 31. - There is no short circuit caused by foreign objects. <Example 1> In the first embodiment, the thickness T of the insulating protective layer 34 I [μm] is 3 [μm], porosity P I The ratio of the insulating particles 34b and the binder 34c is 85 wt% and 15 wt%, respectively. I / Thickness T P is 0.15.

[0099] The evaluation results were: the resistance increase rate was 1.15, which was below the standard; there was no loss of the insulating protective layer; and there was no short circuit due to foreign matter. <Example 2> In the second embodiment, the thickness T I [μm] is 6 [μm], porosity P I The ratio of the insulating particles 34b and the binder 34c is 85 wt% and 15 wt%, respectively. I / Thickness T P is 0.2.

[0100] The evaluation results were: the resistance increase rate was 1.10, which was below the standard; there was no loss of the insulating protective layer; and there was no short circuit due to foreign matter. <Example 3> In the third embodiment, the thickness T I [μm] is 10 [μm], porosity P I The ratio of the insulating particles 34b and the binder 34c is 80 wt% and 20 wt%, respectively. I / Thickness T P is 0.4.

[0101] The evaluation results were: the resistance increase rate was 1.10, which was below the standard; there was no loss of the insulating protective layer; and there was no short circuit due to foreign matter. <Example 4> In the fourth embodiment, the thickness T I [μm] is 15[μm], porosity P I The ratio of the insulating particles 34b and the binder 34c is 80 wt% and 20 wt%, respectively. I / Thickness T P is 0.8.

[0102] The evaluation results showed that the resistance increase rate was 1.13, which was below the standard, there was no loss of the insulating protective layer, and there was no short circuit due to foreign matter. <Comparative Example 1> Comparative Example 1 is a comparative example in which the insulating protective layer 34 is not provided.

[0103] The evaluation result was that the resistance increase rate was 1.12, and that there was a foreign object short circuit. In other words, there was a problem with the occurrence of a foreign object short circuit. <Comparative Example 2> In Comparative Example 2, the thickness T I [μm] is 2 [μm], porosity P I The ratio of the insulating particles 34b and the binder 34c is 80 wt% and 20 wt%, respectively. I / Thickness T P is 0.12.

[0104] In this example, the thickness T I[μm] is 2 [μm], which is less than the standard value of 3. The evaluation results showed that the resistance increase rate was 1.10, there was no loss of the insulating protective layer, and there was a foreign object short circuit. In other words, the problem was the occurrence of a foreign object short circuit.

[0105] <Comparative Example 3> In Comparative Example 3, the thickness T I [μm] is 4 [μm], porosity P I [%] is 63[%], the ratio of the insulating particles 34b and the binder 34c is 80[wt%] and 20[wt%], respectively, and the thickness T I / Thickness T P is 0.12.

[0106] In this example, the porosity P I [%] is 63[%], exceeding the standard value of 60[%]. The evaluation results showed that the resistance increase rate was 1.13, there was no loss of the insulating protective layer, and there was a foreign object short circuit. In other words, the problem was the occurrence of a foreign object short circuit.

[0107] <Comparative Example 4> In Comparative Example 4, the thickness T I [μm] is 4 [μm], porosity P I [%] is 52[%], the ratio of the insulating particles 34b and the binder 34c is 70[wt%] and 30[wt%], respectively, and the thickness T I / Thickness T P is 0.2.

[0108] In this example, the ratios of insulating particles 34b and binder 34c are 70 wt% and 30 wt%, respectively, with the insulating particles 34b falling short of the standard value of 75 wt% or more and the binder 34c exceeding the standard value of 25 wt% or less.

[0109] The evaluation results showed that the resistance increase rate was 1.13, there was no loss of the insulating protective layer, and there was a foreign object short circuit. In other words, the problem was the occurrence of a foreign object short circuit. <Comparative Example 5> In Comparative Example 5, the thickness T I[μm] is 25[μm], porosity P I The ratio of the insulating particles 34b and the binder 34c is 80 wt% and 20 wt%, respectively. I / Thickness T P is 0.9.

[0110] In this example, the thickness T I [μm] is 25 [μm], which exceeds the standard value of 20 [μm]. I / Thickness T P is 0.9, exceeding the standard value of 0.8. The evaluation results were: resistance increase rate 1.38, no loss of insulating protective layer, no foreign object short circuit. In other words, the resistance increase rate of 1.38 was problematic as it exceeded the standard value of 1.15.

[0111] <Comparative Example 6> In Comparative Example 6, the thickness T I [μm] is 30[μm], porosity P I The ratio of the insulating particles 34b and the binder 34c is 80 wt% and 20 wt%, respectively. I / Thickness T P is 1.2.

[0112] In this example, the thickness T I [μm] is 30 [μm], which exceeds the standard value of 20 [μm]. I / Thickness T P is 1.2, exceeding the standard value of 0.8. The evaluation results were: resistance increase rate 1.52, no loss of insulating protective layer, no foreign object short circuit. In other words, the resistance increase rate of 1.52 was problematic because it exceeded the standard value of 1.15.

[0113] <Comparative Example 7> In Comparative Example 7, the thickness T I [μm] is 15[μm], porosity P I [%] is 63[%], the ratio of the insulating particles 34b and the binder 34c is 85[wt%] and 15[wt%], respectively, and the thickness TI / Thickness T P is 0.6.

[0114] In this example, the porosity P I [%] is 63[%], exceeding the standard value of 60. The evaluation results showed that the resistance increase rate was 1.12, the insulating protective layer was removed, and a foreign object short circuit was generated. In other words, there were problems with the insulating protective layer being removed and the foreign object short circuit being generated.

[0115] <Comparative Example 8> In Comparative Example 8, the thickness T I [μm] is 15[μm], porosity P I The ratio of the insulating particles 34b and the binder 34c is 90 wt% and 10 wt%, respectively. I / Thickness T P is 0.6.

[0116] In this example, the ratios of insulating particles 34b and binder 34c are 90 wt% and 10 wt%, respectively, with the insulating particles 34b exceeding the standard value of 85 wt%, and the binder 34c being below the standard value of 15 wt%.

[0117] The evaluation results showed that the resistance increase rate was 1.12, the insulating protective layer was removed, and there was no foreign object short circuit. In other words, there was a problem with the insulating protective layer being removed. <Summary of Experimental Examples> First, it is seen from Comparative Examples 1 to 4 and 7 that the insulating protective layer 34 has an effect of suppressing short circuits caused by foreign objects. I [μm] is 3 [μm] or more, porosity P I It was found that the conditions were that the ratio of the insulating particles 34b and the binder 34c was 85 wt % or more and 15 wt % or less, respectively.

[0118] In addition, from Comparative Example 5 and Comparative Example 6, the thickness T P [μm] vs. thickness T of the insulating protective layer 34 IIt was found that the condition for suppressing the resistance increase rate to 1.15 times or less is a ratio of [μm] of 0.8 or less.

[0119] In addition, from Comparative Example 7 and Comparative Example 8, in order to suppress the dropping of the insulating protective layer 34, the porosity P I It was found that the conditions were that the ratio of the insulating particles 34b and the binder 34c was 85 wt % or less and 15 wt %, respectively.

[0120] (Effects of this embodiment) (1) According to the manufacturing method of the lithium ion secondary battery 1 and the positive electrode plate 3 of this embodiment, it is possible to suppress high-rate deterioration due to the insulating protective layer 34 and to suppress peeling of the insulating protective layer 34 from the positive electrode current collector 31.

[0121] (2) The mass composition of the insulating protective layer 34 is such that the value of (insulating particles 34b) / (insulating particles 34b+binder 34c) is 75 wt% or more. This has the effect of ensuring insulation against foreign matter.

[0122] In addition, the value of (insulating particles 34b) / (insulating particles 34b+binder 34c) is set to 85 wt % or less. This has the effect of suppressing peeling of the insulating protective layer 34 from the positive electrode current collector 31.

[0123] (3) Thickness T of one side of the insulating protective layer 34 I Therefore, it is possible to ensure insulation against foreign matter. In addition, the thickness T I This has the effect of facilitating the movement of electrolytes.

[0124] (4) Porosity P of the insulating protective layer 34 I If the porosity P of the insulating protective layer 34 is 42% or more, the electrolyte can be easily moved. IIf the ratio is 55% or less, the mechanical strength is increased, the insulating properties of the insulating protective layer 34 are improved, and peeling can be suppressed.

[0125] (5) (One-side thickness T of the insulating protective layer 34 I ) / (thickness T of positive electrode mixture layer 32 P If the value of ) is 0.12 or more, the thickness T I In addition, the thickness T I ) / (thickness T of positive electrode mixture layer 32 P ) is 0.80 or less, and further 0.60 or less, there is an effect that the movement of electrolytes becomes easy.

[0126] (6) Density D of the positive electrode composite layer P to 2.2 [g / cm 3 On the other hand, if the density is 3.0 [g / cm 3 ] or less, there is an effect that the movement of the electrolyte can be facilitated.

[0127] (7) Positive electrode mixture layer porosity P P If the porosity P of the positive electrode mixture layer is set to 30% or more, the electrolyte can be easily moved. P If the charge-discharge current is set to 50% or less, the battery capacity can be improved.

[0128] (8) When conductor 32c of positive electrode mixture layer 32 is made of a conductive material having an aspect ratio of 30 or more, a conductive network can be effectively formed with a small mass. (9) If the conductor 32c is a carbon nanotube or a carbon nanofiber, the conductor 32c can have a high aspect ratio.

[0129] (10) Density D of the insulating protective layer 34 I to 1.2 [g / cm 3 ] or more, the mechanical strength of the insulating protective layer 34 is increased, and peeling can be suppressed.3 ] or less, the movement of electrolytes is less likely to be hindered.

[0130] (11) If the peel strength is set to 10 [N] or more, peeling of the insulating protective layer 34 from the positive electrode current collector 31 can be suppressed. (12) At boundary portion B where positive electrode composite layer 32 and insulating protective layer 34 are adjacent to each other, if positive electrode composite layer 32 overlaps insulating protective layer 34, peeling of insulating protective layer 34 from positive electrode current collector 31 can be effectively prevented.

[0131] (13) When the insulating particles 34b are made of boehmite or alumina, it is possible to obtain high insulating properties and high mechanical strength. (14) In the manufacturing method of the positive electrode plate 3 of the lithium ion secondary battery 1 of this embodiment, the insulating protective paste 34a and the positive electrode composite paste 32a are simultaneously applied to the surface of the positive electrode current collector 31 in the coating step (S3). This makes it possible to form a boundary portion B where the positive electrode composite layer 32 overlaps the insulating protective layer 34. This has the effect of making the insulating protective layer 34 less likely to peel off.

[0132] (15) The method includes a positive electrode composite layer pressing step (S5) for pressing the positive electrode composite layer 32, and a boundary portion and insulating protection layer pressing step (S6) for simultaneously pressing the insulating protection layer 34 and the boundary portion B. Therefore, the positive electrode composite layer 32, the insulating protection layer 34, and the boundary portion B can each be appropriately formed.

[0133] (16) The boundary portion and insulating protective layer pressing step (S6) is a roller press using stepped roll 81 having a step with a different radius that presses insulating protective layer 34 and boundary portion B while not pressing positive electrode composite layer 32. Therefore, insulating protective layer 34 and boundary portion B can be appropriately formed.

[0134] (17) In the boundary portion and insulating protective layer pressing step (S6), tension is applied to the positive electrode current collector 31, thereby pressing the insulating protective layer 34 and the boundary portion B against the stepped roll 81. Therefore, due to the flexibility of the positive electrode current collector 31, it is possible to flexibly and appropriately press the insulating protective layer 34 and the boundary portion B in accordance with their shapes.

[0135] (Modification) The above embodiment is an example of the present invention, and the present invention can be modified as follows.

[0136] (Modification) The above embodiment is an example of the present invention, and the present invention can be modified as follows.

[0137] In this embodiment, the positive electrode mixture layer 32 and the insulating protective layer 34 are formed on both sides of the positive electrode current collector 31, and the invention of this embodiment is implemented on both sides. However, the invention of this embodiment may be implemented on only one side of the positive electrode current collector 31. Furthermore, the positive electrode mixture layer 32 and the insulating protective layer 34 may be formed on only one side of the positive electrode current collector 31, and the invention of this embodiment may be implemented on that side.

[0138] In this embodiment, the lithium ion secondary battery 1, which is a plate-shaped cell battery for vehicle use, is exemplified as an example of a non-aqueous electrolyte secondary battery, but the present invention is not limited to this, and other shapes such as a cylindrical shape and other uses such as stationary use are also possible. The electrode body 12 is also not limited to a flat wound type, and may be a laminate of rectangular plate-shaped electrodes. The shapes of the positive electrode external terminal 14 and the negative electrode external terminal 15 are also not limited.

[0139] The drawings are for illustrating the present embodiment, and the dimensions and balance may be exaggerated for clarity, and the present invention is not limited to these drawings. The flowchart shown in Fig. 5 is an example of the present invention, and the steps may be added, deleted, changed in order, or interchanged. For example, the drying step (S4) may be performed after the positive electrode composite layer pressing step (S5).

[0140] Various numerical values ​​and ranges are merely examples and can be optimized and implemented by those skilled in the art. The compositions and material properties of the positive electrode composite paste 32a and the insulating protective paste 34a are merely examples of the present invention and may be optimized by those skilled in the art.

[0141] The “simultaneous coating” in the coating process (S3) does not necessarily have to be performed strictly simultaneously, and as long as the object of the present invention can be achieved, for example, the first nozzle 53 and the second nozzle 55 may be offset in the conveying direction.

[0142] The present embodiment is one embodiment of the present invention, and it goes without saying that those skilled in the art can add, delete, or modify the configuration without being limited to the embodiment, as long as it does not deviate from the scope of the claims. [Explanation of symbols]

[0143] W…Width direction (winding axis direction) W1: Pressing range W2: Pressing range A...part B...boundary part P I …(insulating protective layer) void ratio [%] P P ...(Positive electrode composite layer) porosity [%] D I …(insulating protective layer) density [g / cm 3 ] D P ...(Positive electrode composite layer) density [g / cm 3 ] T I …(insulating protective layer) thickness [μm] T P …(Positive electrode composite layer) thickness [μm] T P1…(Positive electrode composite layer) thickness [μm] T P2 …(Positive electrode composite layer) thickness [μm] 1...Lithium-ion secondary battery (non-aqueous electrolyte secondary battery) 11…Battery case 12...Electrode body 13...Nonaqueous electrolyte 14…Positive external terminal 15...Negative external terminal 2...Negative electrode plate 21...Negative electrode current collector 22...Negative electrode composite material layer 23...Negative electrode connection part 3…Positive electrode plate 31...Positive electrode current collector 32...Positive electrode mixture layer 32a…Positive electrode mixture paste 32b...Positive electrode active material particles 32c…Conductor 32d…Binding material 32e…Solvent 33…Positive electrode connection 34…Insulating protective layer 34a…Insulating protective paste 34b…Insulating particles 34c…Binding material 34d…Solvent 4…Separator 5…Coating machine 51…Die nozzle 52…First die 53…First nozzle 54…Second die 55…Second nozzle 57…Stage 58…Guide 7...Press machine (for the positive electrode composite layer pressing process) 71…Press roll 8... Press machine (for pressing the boundary and insulating protective layer) 81...Step roll

Claims

1. A battery comprising a positive electrode plate, a negative electrode plate, a separator for insulating the positive electrode plate and the negative electrode plate, and a non-aqueous electrolyte; the positive electrode plate includes a positive electrode current collector, a positive electrode mixture layer provided on at least one part of a surface of the positive electrode current collector and containing positive electrode active material particles and a conductor, and an insulating protection layer provided on another part of the surface of the positive electrode current collector and adjacent to the positive electrode mixture layer, the insulating protection layer containing insulator particles and a binder; the mass composition of the insulating protection layer is such that the value of (insulating particles) / (insulating particles+binder) is 75 wt % or more and 85 wt % or less; The thickness T of the insulating protective layer Ｉ is 3.0 [μm] or more and 15 [μm] or less, And the porosity P of the insulating protective layer Ｉ is 42% or more and 55% or less, (Thickness of the insulating protective layer on one side T Ｉ ) / (thickness of one side of the positive electrode mixture layer T Ｐ ) is 0.12 or more and 0.60 or less, Density D of the positive electrode mixture layer Ｐ is 2.2 [g / cm ３ ] or more, 3.0 [g / cm ３ ] or less, Porosity P of the positive electrode mixture layer Ｐ is 30% or more and 50% or less 2. A non-aqueous electrolyte secondary battery comprising:

2. 2. The nonaqueous electrolyte secondary battery according to claim 1, wherein the conductor of the positive electrode mixture layer has an aspect ratio of 30 or more.

3. 2. The nonaqueous electrolyte secondary battery according to claim 1, wherein the conductor is made of a carbon nanotube or a carbon nanofiber.

4. 2. The nonaqueous electrolyte secondary battery according to claim 1, wherein the positive electrode mixture layer overlaps the insulating protection layer at a boundary between the positive electrode mixture layer and the insulating protection layer.

5. 2. The nonaqueous electrolyte secondary battery according to claim 1, wherein the insulating particles are made of boehmite or alumina.

6. A battery comprising a positive electrode plate, a negative electrode plate, a separator for insulating the positive electrode plate and the negative electrode plate, and a non-aqueous electrolyte; The positive electrode plate includes a positive electrode current collector, a positive electrode mixture layer that is provided on at least one part of a surface of the positive electrode current collector and contains positive electrode active material particles and a conductor, and an insulating protective layer that is provided on another part of the surface of the positive electrode current collector and is adjacent to the positive electrode mixture layer and contains insulator particles and a binder, a coating step of simultaneously coating an insulating protection paste containing insulating particles, a binder, and a solvent, and a positive electrode composite paste containing positive electrode active material particles, a conductor, a binder, and a solvent on a surface of the positive electrode current collector to form the positive electrode composite layer, the insulating protection layer adjacent to the positive electrode composite layer, and a boundary portion where the positive electrode composite layer and the insulating protection layer overlap; a positive electrode mixture layer pressing step of pressing the positive electrode mixture layer; a boundary portion and insulating protection layer pressing step of simultaneously pressing the insulating protection layer and the boundary portion, a positive electrode current collector having a first insulating protection layer formed thereon, and a positive electrode mixture layer formed thereon, the positive electrode current collector having a first insulating protection layer formed thereon, the positive electrode mixture layer being formed on the first insulating protection layer.

7. 7. The method for manufacturing a positive electrode plate for a nonaqueous electrolyte secondary battery according to claim 6, wherein the boundary portion and insulating protection layer pressing step is performed by using a roller press having steps with different radii that press the insulating protection layer and the boundary portion but do not press the positive electrode mixture layer.

8. 8. The method for manufacturing a positive electrode plate for a nonaqueous electrolyte secondary battery according to claim 7, wherein the boundary portion and insulating protection layer pressing step presses the insulating protection layer and the boundary portion against the stepped roll by applying tension to the positive electrode current collector.

Images