Abstract

To provide a molding device allowed to cure an aggregate mixture by a microwave without preventing the aggregate mixture from drying / curing.SOLUTION: A molding device 100 according to an embodiment comprises a pattern 10 that has a lower die 11 and an upper die 12 to be matched together at a parting plane 13 and forms a cavity 14 to charge an aggregate mixture for molding therein and a microwave irradiator 20 that irradiates an aggregate mixture W charged in the cavity 14 with a microwave. The pattern 10 is porous at, at least, an inner face of the cavity 14 and the parting plane 13.SELECTED DRAWING: Figure 2

Description

[Technical field]

[0001] The present invention relates to a mold making apparatus. [Background technology]

[0002] Patent Document 1 discloses a method for molding a foundry mold in which a model is filled with foundry sand (aggregate mixture) made of a mixture of a soluble binder and refractory particles (particulate aggregate), and the foundry sand is hardened by irradiating it with microwaves in a reduced pressure atmosphere. The steam generated when the foundry sand hardens is released to the outside from the closed part of the model. [Prior art documents] [Patent documents]

[0003] [Patent Document 1] JP 2004-098160 A [Patent Document 2] International Publication No. 2005 / 023457 Summary of the Invention [Problem to be solved by the invention]

[0004] When using a mold model divided into two parts, the steam generated when the aggregate mixture is heated passes through the dividing surface (parting surface) of the model and is discharged outside the model. In microwave mold-making methods, models made of ceramics or resin are used. Models made of such materials are not heated by microwaves, so the steam cools at the parting surface and condensation forms on the parting surface. This prevents the steam from being discharged outside the model, which may hinder the drying of the aggregate mixture.

[0005] In addition, in Patent Document 1, the aggregate mixture is heated under a reduced pressure atmosphere. However, when the mixture is heated under a reduced pressure atmosphere, the dehydration condensation reaction of the binder such as water glass may not proceed due to the low temperature.

[0006] The present invention has been made in consideration of these problems, and an object of the present invention is to provide a mold making apparatus that is capable of hardening an aggregate mixture by microwaves without interfering with the drying and hardening of the aggregate mixture. [Means for solving the problem]

[0007] A mold making apparatus according to one embodiment includes a model in which a first mold and a second mold are mated at a parting surface to form a cavity into which an aggregate mixture for mold making can be filled, and a microwave irradiation device that irradiates microwaves to the aggregate mixture filled in the cavity, and at least the inner cavity surface and the parting surface of the model are porous.

[0008] A mold making apparatus according to another embodiment includes a model in which a first mold and a second mold are mated at a parting surface to form a cavity into which an aggregate mixture for mold making can be filled, and a microwave irradiation device that irradiates microwaves to the aggregate mixture filled in the cavity, and a hollowed-out portion is formed on the inner surface of the cavity of the model and on the back side of the parting surface. Effect of the Invention

[0009] According to the present invention, it is possible to provide a mold making device that is capable of hardening an aggregate mixture by microwaves without interfering with the drying and hardening of the aggregate mixture. [Brief description of the drawings]

[0010] [Figure 1] FIG. 1 is a diagram showing the configuration of a mold making apparatus according to a first embodiment. [Diagram 2] FIG. 2 is an enlarged view of part A in FIG. [Diagram 3] FIG. 2 is a diagram illustrating the mold-making process. [Figure 4] FIG. 2 is a diagram illustrating the mold-making process. [Diagram 5] FIG. 2 is a diagram illustrating the mold-making process. [Figure 6] FIG. 2 is a diagram illustrating the mold-making process. [Figure 7] FIG. 2 is a diagram illustrating the mold-making process. [Figure 8] FIG. 2 is a diagram illustrating the mold-making process. [Figure 9] FIG. 11 is a diagram showing the configuration of a mold making apparatus according to a second embodiment. [Figure 10] FIG. 11 is a diagram showing the configuration of a mold making apparatus according to a third embodiment. [Figure 11] 1A to 1C are diagrams illustrating problems with the mold making device of the comparative example. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0011] Hereinafter, an embodiment of the present invention will be described with reference to the drawings. For clarity of explanation, the following description and drawings are omitted and simplified as appropriate. In each drawing, the same elements are given the same reference numerals, and duplicate explanations are omitted as necessary. Note that the invention according to the claims is not limited to the following embodiments, and all of the configurations described in the embodiments are not necessarily essential as means for solving the problem.

[0012] Embodiment 1. FIG. 1 is a schematic diagram showing the structure of a mold molding apparatus according to the first embodiment. As shown in FIG. 1, the mold molding apparatus 100 according to the first embodiment includes a model 10 and a microwave irradiation device 20. The model 10 includes a lower mold 11 and an upper mold 12. The lower mold 11 and the upper mold 12 are mated at a parting surface 13 to form a cavity 14 that can be filled with an aggregate mixture W for mold molding. Either the lower mold 11 or the upper mold 12 may be a fixed type, and the other may be a movable type. Here, an example in which a cavity is formed using two molds, the lower mold 11 and the upper mold 12, is shown, but the cavity may be formed by mating more than two molds.

[0013] The microwave irradiation device 20 irradiates microwaves to the aggregate mixture W filled in the cavity 14. By irradiating microwaves, the aggregate mixture W is heated and hardened. In the casting method using microwaves, a metal mold cannot be used as the model 10, and a model 10 made of ceramics or resin is used. For the resin model, for example, synthetic resins such as polystyrene resin, silicon resin, urethane resin, and epoxy resin can be used.

[0014] A method for making a mold using such a model 10 will be described with reference to Figures 3 to 8. Figures 3 to 8 are diagrams illustrating each step of making a mold. First, as shown in Figure 3, an aggregate mixture containing granular aggregate, one or more types of water-soluble binder, and water is mixed.

[0015] The particulate aggregate may be one or more selected from silica sand, alumina sand, olivine sand, chromite sand, zircon sand, mullite sand, various artificial aggregates, etc. The one or more water-soluble binders are binders that harden by evaporating water. It is preferable to use a water-soluble binder that is water-soluble at room temperature. In addition, a water-soluble binder that is dissolved in water after being heated and mixed with water and then cooled to room temperature may also be used.

[0016] In the example shown in Fig. 3, a water glass binder is used as the water-soluble binder, which is prepared by dissolving, for example, glassy silicate of lithium, sodium and / or potassium in water. The water glass may have a molar ratio SiO2 / M2O of, for example, 1.5 to 3.5. Note that M2O is the sum of the masses of lithium, sodium and potassium in the binder calculated as oxides.

[0017] Next, as shown in FIG. 4, the aggregate mixture is mixed by stirring. Then, the aggregate mixture is filled into the cavity 14 of the model 10, which is a space for molding a casting mold. As shown in FIG. 5, a blow head 30 for storing the kneaded aggregate mixture W is disposed above the upper mold 12 of the model 10. A blow plate 31 of the blow head 30 is provided with a plurality of blow nozzles 32 for discharging the aggregate mixture W. The blow nozzles 32 are inserted into the nozzle insertion holes of the upper mold 12. The aggregate mixture W stored in the blow head 30 is discharged from the blow nozzles 32 by pressurized air toward the cavity surface of the lower mold 11. As a result, the cavity 14 of the model 10 is filled with the aggregate mixture W, as shown in FIG. 6.

[0018] Thereafter, the moisture in the filled aggregate mixture W is evaporated to harden the aggregate mixture W, and a mold is formed. As shown in Fig. 7, microwaves are irradiated to the aggregate mixture W filled in the cavity 14 by a microwave irradiation device 20 under atmospheric pressure. When microwaves are irradiated, the moisture in the aggregate mixture W is selectively heated, and turns into steam, which is discharged to the outside of the model 10. At this time, the water glass binder in the aggregate mixture W is dried and hardened.

[0019] Then, as shown in Fig. 8, the mold M is removed from the mold-making space. The method may further include a step of adding a crosslinking agent to the aggregate mixture and reacting the crosslinking agent before or after the step of removing the mold. Such a mold-making method is described in, for example, Patent Document 2.

[0020] As described above, in the microwave irradiation process, the moisture in the aggregate mixture W turns into steam and is discharged to the outside of the model 10. FIG. 2 is an enlarged view of part A in FIG. 1. FIG. 2 shows the state when the aggregate mixture W filled in the cavity 14 is irradiated with microwaves under atmospheric pressure. In FIG. 2, the flow of steam is indicated by arrows. As shown in FIG. 2, the steam generated from the aggregate mixture W is discharged to the outside of the model 10 through the gap between the parting surface 13 of the lower mold 11 and the upper mold 12.

[0021] Here, the problems with the mold-making device of Patent Document 1 are explained. In Patent Document 1, microwaves are irradiated to the aggregate mixture under a reduced pressure atmosphere, thereby lowering the vaporization temperature (boiling point) of the binder and improving the problem of deformation of the model. Such a mold-making device requires a structure that prevents microwaves from leaking and a double sealed container that maintains a reduced pressure atmosphere, making the device expensive. In addition, it takes time because a process of repeatedly depressurizing and opening the sealed container is required every time before and after the microwave irradiation process. In addition, when the aggregate mixture is heated under a reduced pressure atmosphere, the temperature is low, so the dehydration condensation reaction of the water glass binder does not proceed, and the aggregate mixture cannot be sufficiently hardened.

[0022] FIG. 11 is a diagram for explaining the problems of a comparative example in which microwave irradiation is performed at atmospheric pressure without reducing the pressure. FIG. 11 shows the state when microwave irradiation is performed under atmospheric pressure on aggregate mixture W filled in cavity 4. In a casting molding method using microwaves, models (lower mold 1, upper mold 2) made of ceramics or resin are used as models. Since models made of such materials are not heated by microwaves, steam is cooled on the inner surface of cavity 4 and parting surface 3, and condensation occurs. If this condensation blocks the gap of parting surface 3, steam is trapped and drying of aggregate mixture W is hindered. In addition, the corners of aggregate mixture W are surrounded by cold models (lower mold 1, upper mold 2) and are difficult to heat, and drying is further delayed due to condensation.

[0023] To solve such problems, in the embodiment, at least the inner surface and parting surface 13 of the cavity 14 of the model 10 are porous. In the first embodiment, the entire model 10 is formed from a porous material. That is, the aggregate mixture W is filled into the space for casting (cavity 14) formed from the porous material.

[0024] The inner surface of the cavity 14 and the parting surface 13, which are made of a porous material, become warm by absorbing the hot steam generated from the aggregate mixture W (see FIG. 2). The steam generated from the water-soluble binder passes through the gaps in the parting surface 13, which is surrounded by the warm porous resin. As a result, no condensation occurs on the parting surface 13, and the steam is discharged outside the model. This makes it possible to prevent the drying of the aggregate mixture from being hindered.

[0025] As such a porous material, for example, a porous resin having pores smaller than the particle size of the granular aggregate can be used, which can prevent the pores of the porous material from becoming clogged with the granular aggregate.

[0026] Similarly, the inner surface of the cavity 14 also becomes warm by absorbing the hot steam generated from the aggregate mixture W. As a result, the surface of the aggregate mixture W, particularly the corners, are heated by the warm inner surface of the cavity 14. This makes it possible to advance the dehydration condensation reaction of the water glass binder and promote the hardening of the aggregate mixture W. Although the model 10 is formed from a porous material and therefore has thermal insulation properties, it does not absorb microwaves well and is therefore not heated to high temperatures. This makes it possible to suppress thermal deformation of the model 10.

[0027] Here, a comparison is made between a case where molding is performed using a model made of a non-porous resin and a case where molding is performed using a model made of a porous resin as in embodiment 1. In both cases, the formulation of the aggregate mixture, the kneading conditions, and the microwave irradiation conditions are the same.

[0028] When molding was done using a model made from non-porous resin, moisture remained on the surface of the mold, there were uncured areas, and water droplets (condensation) were observed on the parting surfaces of the model. In contrast, when molding was done using a model made from porous resin, the surface of the mold was free of moisture and had hardened, and no water droplets (condensation) were observed on the parting surfaces of the model.

[0029] Thus, according to embodiment 1, the inner surface and parting surface 13 of the cavity 14 of the model 10 are made of a porous material, thereby solving the problems of model deformation and steam, and enabling the aggregate mixture to harden by microwave heating in an atmospheric pressure environment.

[0030] Embodiment 2. Fig. 9 is a diagram showing the configuration of a mold making apparatus according to embodiment 2. In embodiment 2, similarly to embodiment 1, model 10 includes lower mold 11 and upper mold 12, and lower mold 11 and upper mold 12 are mated at parting surface 13 to form cavity 14. In the example shown in Fig. 9, model 10 has non-porous lower mold substrate 11A and upper mold substrate 12A. Porous material 15 is provided on the surfaces of lower mold substrate 11A and upper mold substrate 12A. Parting surface 13 and the inner surface of cavity 14 are formed from this porous material 15.

[0031] As the porous material, for example, a fiber structure including an air layer can be used. Referring to Fig. 9, the inner surface of the cavity 14 and the parting surface 13 formed of the porous material absorb hot steam generated from the aggregate mixture W and become warm. The steam generated from the water-soluble binder passes through the gaps of the parting surface 13 surrounded by the warm porous resin, so that condensation does not occur on the parting surface 13 and the steam is discharged to the outside of the model, making it possible to suppress the prevention of the drying of the aggregate mixture being hindered.

[0032] Embodiment 3. Fig. 10 is a diagram showing the configuration of a mold making apparatus according to embodiment 3. In embodiment 3, similarly to embodiment 1, model 10 includes lower die 11 and upper die 12, and lower die 11 and upper die 12 are mated at parting surface 13 to form cavity 14. In the example shown in Fig. 10, lower die 11 and upper die 12 of model 10 are made of non-porous resin, and hollowed-out portions 16 are formed on the inner surface of cavity 14 and on the back side of parting surface 13.

[0033] In the example shown in Fig. 10, the cavity 14 and the parting surface 13 of the upper mold 12 are hollowed out to form a recess that is open to the outside of the model. The thickness of the base material of this recess is thinner than that of the adjacent portions. The cavity 14 and the parting surface 13 of the lower mold 11 are hollowed out to form a hollow space.

[0034] The model 10 itself does not absorb microwaves well and is not heated to a high temperature, but by forming a lightening portion 16 on the inner surface of the cavity 14 of the model 10 and on the back side of the parting surface 13, the inner surface of the cavity 14 and the parting surface 13 are heated by steam generated from the water-soluble binder. This prevents condensation from forming on the parting surface 13 and allows the steam to be discharged outside the model. In addition, the heated inner surface of the cavity heats the aggregate mixture W, accelerating its hardening.

[0035] The present invention is not limited to the above-described embodiment, and can be modified as appropriate without departing from the spirit and scope of the present invention. [Explanation of symbols]

[0036] 100 Mold molding equipment 10 Model 11 Lower mold 11A Lower mold base material part 12 Upper mold 12A Upper mold base material part 13 Parting Surface 14 Cavity 15 Porous materials 20 Microwave irradiation device 30 Blow Head 31 Blow Plate 32 Blow nozzle W aggregate mixture M mold

Claims

1. a model in which the first and second dies are mated at a parting surface to form a cavity into which an aggregate mixture for casting can be filled; a microwave irradiation device that irradiates microwaves to the aggregate mixture filled in the cavity; Equipped with The model has a non-porous base portion; The cavity inner surface and the parting surface are formed of a porous material provided on the surface of the base material. Mold molding equipment.

2. The porous material is a porous resin having pores smaller than the particle size of the aggregate mixture. The mold making apparatus according to claim 1 .

3. The porous material is a fiber structure including an air layer. The mold making apparatus according to claim 1 .

4. a model in which the first and second dies are mated at a parting surface to form a cavity into which an aggregate mixture for casting can be filled; a microwave irradiation device that irradiates microwaves to the aggregate mixture filled in the cavity; Equipped with the model is formed from a non-porous material; A hollow portion is formed on the inner surface of the cavity and on the back side of the parting surface of the model. Mold molding equipment.

5. The mold making apparatus according to claim 4 , wherein the hollowed-out portion is concave and opens to the outside of the pattern.

6. The mold making apparatus according to claim 4 , wherein the model is hollow due to the formation of the recessed portion.

7. The microwave irradiation is carried out under atmospheric pressure. The mold making apparatus according to any one of claims 1 to 6.