Multilayer curable compositions containing 1,1-diactivated vinyl compound products and related methods

Abstract

To provide a multilayer coating.SOLUTION: There is provided a multilayer coating containing a polymerization reaction product of a 1,1-double activated vinyl compound. There is also provided a method for coating a base material with a curable composition containing the 1,1-double activated vinyl compound. There is also provided an article coated with the composition. The multilayer coating includes a first coating layer coated on at least a part of the base material and a second coating layer coated on at least a part of the first coating layer. Both the first coating layer and the second coating layer independently contain polymer resins. When being cured, the first coating layer and / or the second coating layer contain the 1,1-double activated vinyl compound, its multifunctional form or a polymerization reaction product of a combination thereof.SELECTED DRAWING: None

Description

[Background technology]

[0001] 2. Background of the Invention The curable compositions can be applied to a wide variety of substrates to provide color and / or other visual effects, corrosion resistance, adhesion, sealing, abrasion resistance, chemical resistance, and the like. For example, multilayer coatings often include a basecoat layer that provides color and / or other visual effects, and a topcoat layer, which sometimes includes a clearcoat layer, to provide an abrasion and scratch protection layer. For multilayer coatings applied to metal substrates, such as automotive substrates, a primer layer and / or a surface passivation layer may be applied to the bare metal substrate, for example, under the overlying basecoat and topcoat. Typically, each layer of the multilayer coating is dehydrated and / or cured separately under different conditions, such as, for example, different ignition and / or baking temperatures, to form the final multilayer coating. Summary of the Invention [Means for solving the problem]

[0002] Summary of the Invention The multi-layer coating comprises a first coating layer applied over at least a portion of a substrate, and a second coating layer applied over at least a portion of the first coating layer. Both the first coating layer and the second coating layer independently comprise a polymeric resin. The first coating layer and / or the second coating layer, when cured, comprise a polymerization reaction product of a 1,1-diactivated vinyl compound, or a multifunctional form thereof, or a combination thereof.

[0003] A method for coating a substrate includes applying a first coating layer over at least a portion of the substrate, applying a second coating layer over at least a portion of the first coating layer, and curing the first coating layer and / or the second coating layer. Both the first coating layer and the second coating layer independently comprise a polymeric resin. The first coating layer and / or the second coating layer, when cured, comprises a polymerization reaction product of a 1,1-diactivated vinyl compound, or a multifunctional form thereof, or a combination thereof.

[0004] It will be understood that the invention described herein is not necessarily limited to the examples outlined in this Summary. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0005] Detailed Description of the Invention "Curable composition" as used herein refers to a composition having one or more components that can participate in a cure transformation. The composition may change its physical properties over a period of time as a result of chemical and / or physical processes. The curable composition may cure at room temperature or lower temperatures, or may require exposure to elevated temperatures or other condition(s), such as temperatures above room temperature, to initiate and / or accelerate the cure transformation. Once (and during) the curable composition is applied to a surface, the curing reaction may proceed to provide a cured composition. The cured composition produces a tack-free surface over a period of time, hardens, and then fully cures. The composition is considered fully cured when there is no further increase in hardness. The curable composition provided by the present disclosure may be applied directly onto the surface of a substrate as a single layer (often referred to as a monocoat) or multiple layers, and / or over an underlayer such as a primer, by any suitable method.

[0006] The curable compositions provided by the present disclosure can be used, for example, in sealants, coatings, adhesives, encapsulants, and embedding compositions. A sealant refers to a composition capable of producing a film that is resistant to operating conditions such as moisture and temperature and capable of at least partially blocking the permeation of materials such as water, fuel, and other liquids and gases. A sealant can be used to seal surfaces, smooth surfaces, fill gaps, seal joints, seal openings, and other features. A coating refers to a curable composition deposited on an article that serves to protect the article and / or improve the appearance of the coated article. Examples include pigmented coatings that provide color to freestanding structures such as automobiles, aircraft, ships, or metal cans, buildings, or bridges. An encapsulant refers to a curable composition that is applied to at least a portion of a material to increase durability and / or adjust the functional life of the material. An example of an encapsulant is a polymeric ethyl vinyl acetate film used to cover a portion of a photovoltaic module to protect the module from harsh environmental elements. "Putty" or "embedding composition" refers to a curable composition that is applied to a surface as a filler to smooth surface irregularities and / or improve appearance. Examples of putty applications include, but are not limited to, repairing scratches, holes, deformations, and dents in automotive parts. Other examples of putty applications include filling cracks in wood products, fixing glass, and / or smoothing architectural surfaces, especially walls and ceilings. Adhesives refer to a curable composition that is utilized to bond two or more substrate materials together. For example, structural adhesives may be used to bond automotive or industrial parts together. As used in this disclosure, the phrase "curable composition layer" is meant to include sealants, coatings, adhesives, encapsulants, and embedding composition layers that may be applied over a substrate or over other curable composition layers. For convenience and / or illustrative purposes, the present disclosure may refer to a single or multiple "coating composition layers."However, it should be understood that use of the phrase "coating composition layer" is used herein for illustrative purposes only and includes the various other sealant, adhesive, encapsulant, and potting composition layers that are contemplated as possible alternatives. Thus, except as described in the examples of the present invention, the phrase "coating composition layer" may be used synonymously to mean any other curable composition layer contemplated herein, such as sealant, coating, adhesive, encapsulant, and potting composition layers, as determined by one of ordinary skill in the art.

[0007] As used herein, particularly in relation to coating layers or films, the terms "on," "on top," "over," and variations thereof (e.g., "applied over," "formed over," "deposited over," "provided over," "located over," etc.) mean applied, formed, deposited, provided, or otherwise located over the surface of the substrate, but not necessarily in contact with the substrate. For example, a coating layer "applied over" a substrate does not exclude the presence of one or more other coating layers of the same or different composition located between the applied coating layer and the substrate. Similarly, a second coating layer "applied over" a first coating layer does not exclude the presence of one or more other coating layers of the same or different composition located between the applied second coating layer and the applied first coating layer.

[0008] As used herein, the terms "polymer" and "polymeric" refer to prepolymers, oligomers, and both homopolymers and copolymers. As used herein, "prepolymer" refers to a polymer precursor that can be further reacted or polymerized through one or more reactive groups to form a higher molecular weight or crosslinked state.

[0009] Furthermore, as used herein, a "first coating layer" or a "second coating layer" can include one or more coating applications separately to form either a first or second coating layer. Thus, a "coating layer" does not exclude the presence of one or more other coating applications of the same or different composition forming the layer, as specified herein. For example, if the first coating layer is a basecoat layer, it is contemplated that one, two, or more basecoat applications can be used together to form a "first coating layer". Similarly, it is contemplated that a clearcoat can have one, two, or more clearcoat applications to form a "second coating layer".

[0010] As used herein, the prefix "multi / poly" refers to two or more. For example, a "polyfunctional" molecule (whether a polymer, monomer, or other compound) contains two or more reactive functional groups, such as hydroxyl groups, amine groups, mercapto groups, carbamate groups, etc. More specifically, "polyol" refers to a compound containing two or more hydroxyl groups, "polyamine" refers to a compound containing two or more amine groups, "polythiol" refers to a compound containing two or more mercapto groups, and "polycarbamate" refers to a compound containing two or more carbamate groups.

[0011] A polyfunctional compound such as a polyol, polyamine, polythiol, or polycarbamate may be a polymer, but may not be a polymer, e.g., may comprise a non-polymeric compound. A polymeric polyol, a polymeric polyamine, a polymeric polythiol, or a polymeric polycarbamate each comprises two or more pendant and / or terminal hydroxyl, amine, mercapto, or carbamate functional groups on the polymer molecule. A "pendant group" refers to a group that includes a side branch from the side of the polymer backbone and does not include a part of the polymer backbone, while a "terminal group" refers to a group on the end of the polymer backbone and includes a part of the polymer backbone.

[0012] Furthermore, the terms polyol, polyamine, polythiol, and polycarbamate can encompass compounds that contain a combination of various types of functional groups.For example, a compound that contains two or more hydroxyl groups and two or more carbamate groups can be called a polyol, polycarbamate, or polyol / polycarbamate.Furthermore, polyol, polyamine, polythiol, and polycarbamate compounds can contain either or both neutral functional groups (hydroxyl, amine, mercapto, or carbamate) and / or salts of ionized forms of the functional groups (e.g., alkoxide salts, ammonium salts, etc.).

[0013] As used herein, the term "1,1-diactivated vinyl compound" refers to a compound that includes a vinyl group having two electron-withdrawing groups (EWGs) covalently bonded to one of the pi-bonded carbons and no substituent covalently bonded to the other pi-bonded carbon (i.e., -EWG-C(=CH2)-EWG-), where the electron-withdrawing groups independently include a halogen group, a haloalkyl group, a carbonyl-containing group (e.g., an ester, an amide, an aldehyde, a ketone, an acyl halide, a carboxylic acid / carboxylate group), a cyano group, a sulfonate group, an ammonium group, a quaternary amine group, or a nitro group. The term "multifunctional form" refers to a compound that includes two covalently bonded groups within a molecule. For example, dialkyl methylene malonate is an example of a 1,1-diactivated vinyl compound, and dialkyl methylene malonate is an example of a 1,1-diactivated vinyl compound. The transesterification adducts of alkyl methylene malonates and polyols are an example of multifunctional forms of dialkyl methylene malonates.

[0014] The multi-layer coating described herein contains at least two coating layers, both of which independently comprise a polymeric resin, and at least one of the coating layers comprises a polymerization reaction product of a 1,1-diactivated vinyl compound, or a multifunctional form thereof, or a combination thereof. Thus, the two coating layers can comprise the same polymeric resin or different polymeric resins, provided that at least one of the two coating layers comprises a polymerization reaction product. The polymerization reaction product can comprise the polymeric resin of one or more coating layers that contains the polymerization reaction product alone, or one or more coating layers can further comprise one or more different additional polymeric resins and / or other multifunctional compounds.

[0015] The 1,1-diactivated vinyl compound can include methylene dicarbonyl compounds, dihalovinyl compounds, dihaloalkyl disubstituted vinyl compounds, or cyanoacrylate compounds, or any multifunctional form thereof, or any combination thereof. Examples of 1,1-diactivated vinyl compounds and their multifunctional forms that can be used to formulate the curable composition to form one or more coating layers in a multilayer coating are described in U.S. Patent Nos. 8,609,885, 8,884,051, 9,108,914, 9,181,365 and 9,221,739, which are incorporated herein by reference. Further examples of 1,1-diactivated vinyl compounds and multifunctional forms thereof that can be used to formulate curable compositions to form one or more coating layers in multilayer coatings are described in U.S. Patent Application Publication Nos. 2014 / 0288230, 2014 / 0329980, and 2016 / 0068618, which are incorporated herein by reference.

[0016] The coating layer can include a polymerization reaction product of a 1,1-diactivated vinyl compound including methylene malonate, or a multifunctional form thereof, or a combination thereof. Methylene malonate can be represented by the general formula (I): [ka] where R and R' can be the same or different and can represent almost any substituent or side chain, such as a substituted or unsubstituted alkyl or aryl group. For example, the coating layer can include a polymerization reaction product of a dialkyl methylene malonate, a diaryl methylene malonate, a multifunctional form of a dialkyl methylene malonate, or a multifunctional form of a diaryl methylene malonate, or any combination thereof.

[0017] Multifunctional forms of methylene malonate can include transesterified adducts of methylene malonate and polyols. Thus, multifunctional forms of methylene malonate can be represented by the general formula (II): [ka] (wherein n is greater than 1, X is a polyol residue, and each R may be the same or different as described above). As used herein, the term "residue" refers to a group derived from the respective compound. For example, in the above formula, X is an n-valent group derived from a polyol by transesterification with methylene malonate and n hydroxyl groups of said polyol. Similarly, a polymer containing the residue of a particular compound can be obtained by polymerizing said compound. In some cases, a multifunctional form of methylene malonate can include a transesterification adduct of methylene malonate and a diol, and thus has the general formula (III): [ka] where X is a diol residue and R and R' may be the same or different as previously described.

[0018] Suitable polyols for producing transesterification adducts with methylene malonate include, for example, polymeric polyols (e.g., polyether polyols, polyester polyols, acrylic polyols, and polycarbonate polyols) and monomeric polyols (e.g., alkane polyols, including alkane diols such as 1,5-pentanediol and 1,6-hexanediol). Transesterification adducts can be formed by reaction of methylene malonate with polyols in a suitable reaction medium in the presence of a catalyst. Examples of transesterification adducts of methylene malonate and polyols that can be used in the curable composition are described in U.S. Patent Application Publication No. 2014 / 0329980 and U.S. Patent No. 9,416,091, which are incorporated herein by reference. Furthermore, the concentration of the transesterification adduct can be affected by the ratio of reactants and / or distillation or evaporation of the reaction medium.

[0019] In some examples, a coating layer of a multi-layer coating can include a polymerization reaction product of dimethyl methylene malonate (D3M), a multifunctional form of D3M, or both. In some examples, a coating layer of a multi-layer coating can include a polymerization reaction product of diethyl methylene malonate (DEMM), a multifunctional form of DEMM, or both. A multifunctional form of D3M or DEMM can include a transesterification adduct of D3M or DEMM and a polyol, such as 1,5-pentanediol or 1,6-hexanediol.

[0020] In some examples, the coating layers of the multi-layer coating include the polymerization reaction product of a combination of dialkyl methylene malonate and multi-functional forms of dialkyl methylene malonate. The coating layers of the multi-layer coating can include, for example, DEMM and polymerization reaction products of multifunctional forms of DEMM including transesterified adducts of DEMM and at least one polyol. DEMM can be transesterified with a polyol including, for example, an alkanediol such as 1,5-pentanediol or 1,6-hexanediol.

[0021] In some examples, the curable composition used to form the coating layer of the multilayer coating can include (in addition to the 1,1-diactivated vinyl compound, or multifunctional forms thereof, or combinations thereof) a polyol, a polyamine, a polythiol, or a polycarbamate, or any combination thereof. Without being bound by any theory, it is believed that the vinyl groups in the 1,1-diactivated vinyl compound and / or multifunctional forms thereof can react via a Michael addition mechanism with hydroxyl groups, amine groups, mercapto groups, and / or carbamate groups in the polyol, polyamine, polythiol, and / or polycarbamate resin, or other compounds (i.e., multifunctional polymer resins or multifunctional monomeric compounds), thereby forming stable covalent linkages. Furthermore, the 1,1-diactivated vinyl compounds and / or their multifunctional forms can undergo self-polymerization reactions, thereby forming polymerization reaction products that can be covalently bonded to multifunctional polymer resins or multifunctional monomer compounds via linkages formed by Michael addition reactions with hydroxyl, amine, mercapto, and / or carbamate groups. Thus, the 1,1-diactivated vinyl compounds and / or their multifunctional forms can function as crosslinkers / curing agents for multifunctional polymer resins or multifunctional monomer compounds. In some examples, the 1,1-diactivated vinyl compounds and / or their multifunctional forms can provide multiple curing mechanisms, including both Michael addition reactions and polymerization reactions, to crosslink and cure the multifunctional polymer resins or multifunctional monomer compounds.

[0022] Multifunctional polymer resins that can be formulated and used to form one or more coating layers in a multilayer coating and crosslinked and cured with 1,1-diactivated vinyl compounds and / or multifunctional forms thereof include polymer resins containing pendant and / or terminal hydroxyl, amine, mercapto, and / or carbamate groups, such as polyether polyols, polyester polyols, acrylic polyols, polycarbonate polyols, polyether polyamines, polyester polyamines, acrylic polyamines, polycarbonate polyamines, polyether polythiols, polyester polythiols, acrylic polythiols, polycarbonate polythiols, polyether polycarbamates, polyester polycarbamates, acrylic polycarbamates, polycarbonate polycarbamates, and any combinations thereof. Additional multifunctional polymer resins that can be formulated into the curable compositions and crosslinked and cured using 1,1-diactivated vinyl compounds and / or their multifunctional forms include any multifunctional polymer resin incorporating hydroxyl, amine, mercapto, or carbamate groups, or any combination thereof, including, for example, polyester resins, polyurethane resins, polyurea resins, polyether resins, polythioether resins, polycarbonate resins, polycarbamate resins, epoxy resins, phenolic resins, and aminoplast resins (urea-formaldehyde and / or melamine-formaldehyde).

[0023] In addition to or instead of the multifunctional polymer resin, multifunctional monomeric compounds can be incorporated into the curable composition and crosslinked and cured using 1,1-diactivated vinyl compounds and / or multifunctional forms thereof. When polyol compounds are used, they can be the same or different from the polyol compounds used to form the transesterified adducts described above. Examples of monomeric polyol compounds include glycols, e.g. Examples of suitable hydroxyl-containing polyfunctional monomeric compounds include, but are not limited to, ethylene glycol, diethylene glycol, triethylene glycol, 1,2-propylene glycol, 1,3-butylene glycol, tetramethylene glycol, hexamethylene glycol, neopentyl glycol, pentaerythritol, and any combination thereof. Other suitable hydroxyl-containing polyfunctional monomeric compounds include, but are not limited to, 1,5-pentanediol, 1,6-hexanediol, cyclohexanedimethanol, 2-ethyl-1,6-hexanediol, 1,4-butanediol, 1,3-propanediol, trimethylolpropane, 1,2,6-hexanetriol, glycerol, and any combination thereof. Additionally, monomeric amino alcohols that can be incorporated into the curable composition and crosslinked and cured using 1,1-diactivated vinyl compounds and / or polyfunctional forms thereof include, but are not limited to, ethanolamine, propanolamine, butanolamine, and any combination thereof.

[0024] Examples of monomeric polyamine compounds that can be incorporated into the curable compositions used to form one or more coating layers in a multilayer coating and crosslinked and cured using 1,1-diactivated vinyl compounds and / or multifunctional forms thereof include, but are not limited to, diamines such as ethylenediamine, hexamethylenediamine, 1,2-propanediamine, 2-methyl-1,5-penta-methylenediamine, 2,2,4-trimethyl-1,6-hexanediamine, isophoronediamine, diaminocyclohexane, xylylenediamine, 1,12-diamino-4,9-dioxadodecane, and any combination thereof. Other suitable monomeric and polymeric polyamine compounds include polyetheramines such as Jeffamine® products available from Huntsman Chemical Company.

[0025] Examples of monomeric and polymeric polythiol compounds that can be incorporated into the curable compositions used to form one or more coating layers in a multilayer coating and crosslinked and cured using 1,1-diactivated vinyl compounds and / or multifunctional forms thereof include, for example, resins and compounds produced by esterification of polyols with mercapto organic acids. Examples of suitable polyols include the polyols mentioned above, and examples of suitable mercapto organic acids include thioglycolic acid and mercaptopropionic acid. Examples of monomeric polythiol compounds include glyceryl dithioglycolate, glyceryl trithioglycolate, glycol dimercaptoacetate, pentaerythritol tetramercaptoacetate, glycol di-(3-mercaptopropionate), pentaerythritol tetra(3-mercaptoproprionate), dipentaerythritol hexa(3-mercaptopropionate). Other suitable monomeric and polymeric polythiol compounds include, but are not limited to, trimethylolpropane tris-(thioglycolate), pentaerythritol tetrakis-(thioglycolate), ethylene glycol dithioglycolate, trimethylolpropane tris-(β-thiopropionate), pentaerythritol tetrakis-(β-thiopropionate), dipentaerythritol poly(β-thiopropionate), and any combination thereof. Other suitable monomeric and polymeric polythiol compounds include, but are not limited to, trimethylolpropane tris-(thioglycolate), pentaerythritol tetrakis-(β-thiopropionate), dipentaerythritol poly(β-thiopropionate), and any combination thereof. These include Thiocure® products available from Fabrik GmbH & Co. KG.

[0026] Examples of monomeric and polymeric polycarbamate compounds that can be incorporated into curable compositions used to form one or more coating layers in multilayer coatings and crosslinked and cured with 1,1-diactivated vinyl compounds and / or multifunctional forms thereof include, for example, resins and compounds produced by transcarbamylation of polyols with alkyl carbamates (i.e., transesterification of alkyl carbamates with polyols).

[0027] The curable composition used to form one or more coating layers in a multilayer coating can further include an activator in addition to the 1,1-diactivated vinyl compound, or a multifunctional form thereof, or a combination thereof. As used herein, the term "activator" refers to a compound or other agent that can initiate and / or catalyze (i) the polymerization of the 1,1-diactivated vinyl compound or a multifunctional form thereof, and / or (ii) the addition reaction between the 1,1-diactivated vinyl compound or a multifunctional form thereof and a polyfunctional component (e.g., a polyol, a polyamine, a polythiol, and / or a polycarbamate resin or compound). The term "activator" includes (1) the active form of an activator compound, and (2) a latent precursor form of an activator compound that can be converted from the latent precursor form to the active form (e.g., by exposure to heat, electromagnetic radiation, pressure, or an effective amount of a chemical coactivator). Additionally, latent precursor forms of activator compounds that can be converted to active forms include activators associated with volatile or otherwise removable neutralizing or inhibitor compounds that, when applied as a coating layer, can evaporate or otherwise be removed from the hardenable composition, thereby activating the activator.

[0028] The activator may include a base. As used herein, the term "base" refers to an electronegative compound or functional group capable of initiating anionic polymerization of 1,1-diactivated vinyl compounds. Suitable activators include organic bases (e.g., amine-containing compounds and carboxylates), inorganic bases (e.g., hydroxide salts, carbonates, and metal oxides), organometallic compounds, and any combination thereof. Suitable activators also include polymers that contain pendant and / or terminal amine, carboxylate, or other base functional groups capable of initiating anionic polymerization of 1,1-diactivated vinyl compounds.

[0029] In some examples, the activator comprises a strong base (pH greater than 9 in water at 25° C.), a medium base (pH 8-9 in water at 25° C.), or a weak base (pH greater than 7 to 8 in water at 25° C.), or any combination thereof. Activators include, for example, sodium acetate; potassium acetate; acid salts of sodium, potassium, lithium, copper, or cobalt; tetrabutylammonium fluoride, chloride, or hydroxide; amines, including primary, secondary, and tertiary amines; amides; acid salts bound to polymers; benzoates; 2,4-pentanedionates; sorbates; propionates; secondary aliphatic amines; piperidene, piperazine, N-methylpiperazine, dibutylamine, morpholine, diethylamine, pyridine, triethylamine, tripropylamine, triethylenediamine, N,N-dimethylpiperazine, butylamine, pentylamine, hexylamine, heptylamine, nonylamine, butyl ... nylamine, decylamine; 1,4-diazabicyclo[2.2.2]octane (DABCO); 1,1'-iminobis-2-propanol (DIPA); 1,2-cyclohexanamine; 1,3-cyclohexanedimethaneamine; 2-methylpentamethylenediamine; 3,3-iminodipropylamine; triacetonediamine (TAD); salts of amines with organic monocarboxylic acids; piperidine acetate; metal salts of lower monocarboxylic acids; copper(II) acetate, copper(II) acetate monohydrate, potassium acetate, zinc acetate, zinc chloracetate, magnesium chloroacetate, magnesium acetate; salts of acid-containing polymers; salts of polyacrylic acid copolymers; and any combination thereof.

[0030] In some examples, the curable composition used to form one or more coating layers in the multilayer coating may include a tertiary amine activator, such as DABCO, 2-(dimethylamino)ethanol (DMAE / DMEA), 2-piperazin-1-ylethylamine, N,N,N',N'-tetrakis(2-hydroxypropyl)ethylenediamine, 2-[2-(dimethylamino)ethoxy]ethanol, 1-[bis[3 ... N,N,N',N'',N''-Pentamethyldiethylenetriamine, N,N,N',N'-Tetraethyl-1,3-propanediamine, N,N,N',N'-Tetramethyl-1,4-butanediamine, N,N,N',N'-Tetramethyl-1,6-hexanediamine, 1,4,8,11-Tetramethyl-1,4,8,11-tetraazacyclotetradecane, 1,3,5-trimethyl It can include hexahydro-1,3,5-triazine, methyl dicocoamine, 1,8-diazabicycloundec-7-ene (DBU), 1,5 diazabicyclo-[4,3,0]-non-5-ene (DBN), 1,1,3,3-tetramethylguanidine, 1,5,7-triazabicyclo[4.4.0]dec-5-ene, 7-methyl-1,5,7-triazabicyclo[4.4.0]dec-5-ene, or any combination thereof, etc. In some examples, the tertiary amine activator includes a bicyclic guanidine compound or a substituted derivative thereof, such as 1,5,7-triazabicyclo[4.4.0]dec-5-ene, or 7-methyl-1,5,7-triazabicyclo[4.4.0]dec-5-ene, or any substituted derivative thereof, or any combination thereof, etc.

[0031] The activator may include an ionic liquid. As used herein, the term "ionic liquid" refers to a salt having a melting point temperature of less than 100° C. at 1 atmosphere pressure. Ionic liquids may be in a liquid state at room temperature (approximately 23° C.) and atmospheric pressure. Ionic liquids include a cation in ionic association with an anion. The cation may be, for example, a heterocyclic nitrogen-containing organic cation, such as an imidazolium cation, a pyrazolium cation, a pyrrolidinium cation, a pyridinium cation, a pyrazinium cation, or a pyrimidinium cation (including derivatives thereof), or other cations, such as C 1 ~C 32 Tetraalkylphosphonium cation, C 1 ~C 32 Tetraalkylammonium cation or C 1 ~C 32The anion may include, for example, a halide (F - , Cl - , Br - , I - ), formate, acetate, nitrate, phosphate, sulfonate, tetrafluoroborate, hexfluorophosphate, triflate (trifluoromethanesulfonate), bis(trifluoromethylsulfonyl)imide, tosylate, alkylsulfonate anion (e.g., methylsulfonate), alkylsulfate anion, carboxylate anion, or phthalate anion.

[0032] Ionic liquid activators used in the compositions, coatings, and methods described herein can include any combination of the aforementioned cations and anions that initiate and / or catalyze (i) the polymerization of 1,1-diactivated vinyl compounds or multifunctional forms thereof, and / or (ii) the addition reaction between 1,1-diactivated vinyl compounds or multifunctional forms thereof and polyfunctional components (e.g., polyols, polyamines, polythiols, and / or polycarbamate resins or compounds).

[0033] The ionic liquid activator has the formula: [ka] (In the formula, R 1 and R 2 are each independently C1 to C 12 is an alkyl group, R 3 , R 4 , and R 5 are each independently hydrogen or C1-C 12 is an alkyl group, and X - In some examples, R can include an imidazolium salt of 1 and R 2 are C1 to C 12 is an alkyl group, R3 , R 4 , and R 5 are each a hydrogen atom. In some examples, R 1 , R 2 , and R 3 are C1 to C 12 is an alkyl group, R 4 and R 5 are each hydrogen atoms.

[0034] The ionic liquid activator has the formula: [ka] (In the formula, R 1 and R 2 are each independently C1 to C 12 is an alkyl group, R 3 , R 4 , and R 5 are each independently hydrogen or C1-C 12 is an alkyl group, and X - In some examples, R can include a pyrazolium salt of 1 and R 2 are C1 to C 12 is an alkyl group, R 3 , R 4 , and R 5 are each a hydrogen atom. In some examples, R 1 , R 2 , and R 3 are C1 to C 12 is an alkyl group, R 4 and R 5 are each hydrogen atoms.

[0035] The ionic liquid activator has the formula: [ka] (In the formula, R 1 is C1~C 12 is an alkyl group, R 2 are each independently C1 to C 12is an alkyl group, n is 0 to 5, and X - is an anion).

[0036] The ionic liquid activator has the formula: [ka] (In the formula, R 1 is C1~C 12 is an alkyl group, R 2 are each independently C1 to C 12 is an alkyl group, n is 0 to 4, and X - is an anion).

[0037] The ionic liquid activator has the formula: [ka] (In the formula, R 1 , R 2 , R 3 , and R 4 are each independently C1 to C 12 is an alkyl group, and X - is an anion).

[0038] The anion (X - ) can be, for example, a halide (F - , Cl - , Br - , I - ), formate, acetate, nitrate, phosphate, sulfonate, tetrafluoroborate, hexafluorophosphate, triflate (trifluoromethanesulfonate), bis(trifluoromethylsulfonyl)imide, tosylate, alkylsulfonate anions (e.g., methylsulfonate), alkylsulfate anions, carboxylate anions, or phthalate anions.

[0039] The ionic liquid activators used in the compositions, coatings, and methods described herein can include any combination of the aforementioned cations and anions, and can also include combinations of any two or more ionic liquids each independently comprising the aforementioned cations and anions.

[0040] The curable composition may contain an amount of activator ranging from a non-zero amount to 10%, 5%, 2%, 1%, 0.5%, or 0.1% by weight of the total composition, or any subrange subsumed within such range. The activator may be kept separate (e.g., in a separate container) from the 1,1-diactivated vinyl compound or its multifunctional form until about sufficient time has elapsed to apply the curable composition across a substrate to prevent premature curing of the curable composition. The activator may then be mixed with all of the other components of the curable composition and applied across the substrate using a suitable application technique (e.g., spraying, electrostatic spraying, dipping, rolling, brushing, troweling, electrocoating, etc.). In other examples described below, an activator can be applied over and / or under the layer of the hardenable composition to (1) activate an addition reaction between a multifunctional component and a 1,1-diactivated vinyl compound or multifunctional forms thereof, and / or (2) activate a polymerization reaction between a 1,1-diactivated vinyl compound or multifunctional forms thereof.

[0041] In some cases, the activator can constitute a metal oxide layer on the metal substrate to which the curable composition is applied. For example, a chromium oxide film on a stainless steel substrate, an aluminum oxide film on an aluminum or aluminum oxide substrate, or a titanium oxide film on a titanium or titanium alloy substrate can function as an activator in a coating layer applied over such substrates.

[0042] Further examples of activating agents and activation methods that can be used in conjunction with one or more coating layers in a multi-layer coating are described in US Pat. No. 9,181,365, which is incorporated herein by reference.

[0043] In some cases, but not necessarily, when the curable composition used to form one or more coating layers in a multilayer coating includes both (1) a 1,1-diactivated vinyl compound, or a multifunctional form thereof, or a combination thereof, and (2) a polyol, polyamine, polythiol, or polycarbamate, or any combination thereof, the curable composition can further include an acid accelerator. In some cases, the acid accelerator can include a strong acid. As used herein, the term "strong acid" refers to an acid having a pK in water of less than -1.74. a A protonic acid is an acid that has at least one proton (H + ) means an acid having a molecular weight of 100 to 2000. Strong acid accelerators that can be incorporated into the curable composition include, for example, strong inorganic acids and strong organic acids. Suitable strong inorganic acids include, for example, mineral acids (e.g., hydrochloric acid, perchloric acid, sulfuric acid, and nitric acid) and heteropoly acids (e.g., phosphotungstic acid, phosphomolybdic acid, tungstosilicic acid, and silicomolybdic acid). Suitable strong organic acids include, for example, sulfonic acids (e.g., p-toluenesulfonic acid, methanesulfonic acid, and dodecylbenzenesulfonic acid). Any combination of strong acids (e.g., a mixture of sulfonic acid and heteropolyacid) can also be incorporated into the curable composition.

[0044] Without wishing to be bound by any theory, it is believed that the acid can function as a Lewis acid in the hardenable composition, complexing with the 1,3-dicarbonyl motif, thereby facilitating a Michael addition reaction between the functional groups on the multifunctional component and the vinyl groups on the 1,1-diactivated vinyl compound and / or its multifunctional form. Thus, the strong acid component in the hardenable composition can shift the crosslinking and curing reaction from the self-polymerization of the 1,1-diactivated vinyl compound and / or its multifunctional form to a Michael addition reaction that forms a covalent linkage between the multifunctional component and the 1,1-diactivated vinyl compound and / or its multifunctional form.

[0045] In some cases, but not necessarily, when the curable composition used to form one or more coating layers in a multi-layer coating includes an activator, the curable composition can further include an extender. As used herein, the term "extender" refers to a compound or other agent that can reduce the reaction rate of (i) the polymerization of 1,1-diactivated vinyl compounds or their multifunctional forms, and / or (ii) the addition reaction between 1,1-diactivated vinyl compounds or their multifunctional forms and polyfunctional components (e.g., polyols, polyamines, polythiols, and / or polycarbamate resins or compounds). Thus, the extender functions to extend the pot life of the curable composition and can be used in combination with an activator and / or an acid accelerator as described above to control the pot life and cure response of the curable composition used to form one or more coating layers in a multi-layer coating.

[0046] The extenders used in the compositions, coatings, and methods described herein can include, for example, carboxylic anhydride compounds and / or carboxylic acid compounds. Suitable carboxylic anhydride compounds include, for example, unsaturated anhydrides, such as maleic anhydride, citraconic anhydride, itaconic anhydride, aconitic anhydride, bicyclo[2.2.2]oct-7-ene-2,3,5,6-tetracarboxylic dianhydride, crotonic anhydride, 1-cyclopentene-1,2-dicarboxylic anhydride, methacrylic anhydride, or any combination thereof. Suitable carboxylic anhydride compounds also include, for example, saturated anhydrides, such as saturated homologs of any of the aforementioned unsaturated anhydrides (e.g., succinic anhydride). Suitable carboxylic anhydride compounds include, for example, short chain (e.g., C2-C 20 ) Saturated and unsaturated carboxylic acids, such as oxalic acid, acetic acid, propionic acid, octanoic acid, stearic acid, isostearic acid, benzoic acid, citric acid, (meth)acrylic acid, crotonic acid, isocrotonic acid, vinylacetic acid, 2-pentenoic acid, 3-pentenoic acid, allylacetic acid, maleic acid, fumaric acid, These include fatty acids such as oleic acid, citraconic acid, itaconic acid, aconitic acid, saturated and unsaturated fatty acids (eg, palmitoleic acid, vaccenic acid, and / or oleic acid), and any combination thereof.

[0047] Alternatively or additionally, the extender used in the compositions, coatings, and methods described herein can include, for example, anhydride-containing vinyl polymers and / or carboxylic acid-containing vinyl polymers. As used herein, the term "vinyl polymer" refers to any polymer produced by an addition reaction between carbon-carbon double bonds. Anhydride-containing vinyl polymers can be produced from monomer mixtures that include ethylenically unsaturated carboxylic acid anhydrides, such as maleic anhydride, citraconic anhydride, itaconic anhydride, aconitic anhydride, bicyclo[2.2.2]oct-7-ene-2,3,5,6-tetracarboxylic dianhydride, crotonic anhydride, 1-cyclopentene-1,2-dicarboxylic anhydride, methacrylic anhydride, or any combination thereof. Anhydride-containing vinyl polymers can be produced from monomer mixtures that further include ethylenically unsaturated monomers, such as, for example, styrene and its derivatives, vinyl acetate, vinyl chloride, (meth)acrylic acid esters, and the like. Anhydride-containing vinyl polymers suitable for use as extenders in the compositions, coatings, and methods described herein are described, for example, in U.S. Pat. No. 4,798,745, column 7, line 27 to column 8, line 3 and column 10, line 40 to column 12, line 59, which is incorporated herein by reference.

[0048] Carboxylic acid-containing vinyl polymers suitable for use as extenders in the compositions, coatings, and methods described herein can be produced from monomer mixtures containing ethylenically unsaturated carboxylic acids, such as, for example, (meth)acrylic acid, crotonic acid, isocrotonic acid, vinyl acetic acid, 2-pentenoic acid, 3-pentenoic acid, allyl acetic acid, maleic acid, fumaric acid, citraconic acid, itaconic acid, aconitic acid, saturated and unsaturated fatty acids (e.g., palmitoleic acid, vaccenic acid, and / or oleic acid), and any combination thereof. Carboxylic acid-containing vinyl polymers can be produced from monomer mixtures further containing ethylenically unsaturated monomers, such as, for example, styrene and its derivatives, vinyl acetate, vinyl chloride, (meth)acrylate esters, and the like. Additionally, vinyl polymers containing both carboxylic acid groups and carboxylic acid anhydride groups can be used as extenders in the compositions, coatings, and methods described herein. Such vinyl polymers can be produced from monomer mixtures containing both ethylenically unsaturated carboxylic acids and ethylenically unsaturated carboxylic acid anhydrides, as previously described.

[0049] In some examples, the curable composition used to form one or more coating layers in the multi-layer coating can include any combination of (1) 1,1-diactivated vinyl compounds, or multifunctional forms thereof, or combinations thereof, and (2) acid accelerators, activators, and / or extenders, as described above. The curable composition used to form one or more coating layers in the multi-layer coating can further include (3) polyols, polyamines, polythiols, or polycarbamates, or any combinations thereof. The curable composition used to form one or more coating layers in the multi-layer coating can further include additional materials, such as additional resins, solvents, reactive diluents, colorants, and the like. As used herein, "colorant" means any substance that imparts color and / or other opacity effects and / or other visual effects to the curable composition, especially when applied over a substrate and cured. The colorant can be added to the curable composition in any suitable form, such as separate particles, dispersions, solutions, and / or flakes. A single colorant or a mixture of two or more colorants can be incorporated into the curable compositions used to form one or more coating layers in the multilayer coatings described herein.

[0050] Exemplary colorants include pigments (organic or inorganic), dyes, and tints, such as those used in the paint industry and / or listed by the Dry Color Manufacturers Association (DCMA), as well as special effect compositions. Colorants can include, for example, finely divided solid powders that are insoluble but wettable under the conditions of use. Colorants can be organic or inorganic and can be agglomerated or non-agglomerated. Colorants can be incorporated into the curable composition by the use of a grinding vehicle, such as an acrylic grinding vehicle, the use of which is well known to those skilled in the art.

[0051] Exemplary pigments and / or pigment compositions include, but are not limited to, carbazole dioxazine crude pigments, azo, monoazo, diazo, naphthol AS, salt type (flake), benzimidazolone, isoindolinone, isoindoline and polycyclic phthalocyanine, quinacridone, perylene, perinone, diketopyrrolopyrrole, thioindigo, anthraquinone, indanthrone, anthrapyrimidine, flavanthrone, pyranthrone, anthanthrone, dioxazine, triarylcarbonium, quinophthalone pigment, diketopyrrolopyrrole red ("DPPBO red"), titanium dioxide, carbon black, and any mixtures thereof. The terms "pigment" and "coloring filler" can be used interchangeably. Exemplary dyes include those that are soluble in organic solvents and / or water, such as, but are not limited to, phthalo green or blue, iron oxide, bismuth vanadate, anthraquinone, perylene, and quinacridone.

[0052] Exemplary tinting agents include, but are not limited to, pigments dispersed in a water-based or water-miscible carrier, such as AQUA-CHEM 896 (available from Degussa, Inc.), and CHARISMA COLORANTS and MAXITONER INDUSTRIAL COLORANTS (available from Accurate Dispersions Division of Eastman Chemical Company).

[0053] The colorant optionally incorporated into the curable composition can also include a special effect composition or pigment. As used herein, "special effect composition or pigment" refers to a composition or pigment that interacts with visible light to provide an appearance effect other than or in addition to a continuous, unchanging color. Exemplary special effect compositions and pigments include those that provide one or more appearance effects such as reflection, pearlescence, metallic luster, texture, phosphorescence, fluorescence, photochromism, photosensitivity, thermochromism, goniochromism, and / or color change. Examples of special effect compositions can include transparent coated mica and / or synthetic mica, coated silica, coated alumina, aluminum flake, transparent liquid crystal pigment, liquid crystal coating, and any combination thereof.

[0054] Other examples of materials that can be incorporated into the curable compositions include plasticizers, anti-wear particles, antioxidants, hindered amine light stabilizers, UV light absorbers and stabilizers, surfactants, flow and surface control agents, thixotropic agents, solvents and co-solvents, reactive diluents, catalysts, reaction inhibitors, and other adjuvants customary in the paint and coatings industry.

[0055] The invention described herein includes using a curable composition as described above to produce a multi-layer coating. For example, a method for coating a substrate may include applying a first coating layer over at least a portion of the substrate, applying a second coating layer over at least a portion of the first coating layer, and applying a second coating layer over at least a portion of the first coating layer. and curing the first and / or second coating layers. The curing of the first and second coating layers can be performed sequentially or simultaneously with or without intermediate flash, drying, or dehydration steps. The first and / or second coating layers both independently comprise a polymeric resin. The first and / or second coating layers, when cured, comprise a polymerization reaction product of a 1,1-diactivated vinyl compound, or a multifunctional form thereof, or a combination thereof. The first and / or second coating layers, when cured, can also comprise an addition reaction product of a 1,1-diactivated vinyl compound, or a multifunctional form thereof, or a combination thereof, with a polyol, a polyamine, a polythiol, or a polycarbamate.

[0056] "Addition reaction product" refers to an adduct formed by the reaction of a 1,1'-diactivated vinyl compound and / or its multifunctional form with a nucleophile (e.g., an amine, a thiol or an alcohol and / or their polymeric forms). Without being bound by any theory, the addition reaction product can be obtained by adding a nucleophile to a conjugated double bond ("Michael addition reaction") or by replacing the alcohol of an ester of a 1,1-diactivated vinyl ester with another alcohol (transesterification reaction), an amine, a thiol and / or their polymeric forms. For example, reaction of an amine can result in an amide product, and reaction with a thiol can result in a thioester product. "Polymerous addition product" refers to the product of a polymerization reaction in which multiple reactants react repeatedly. Without being bound by any theory, the polymeric addition product can be obtained via various reaction mechanisms such as anionic polymerization, condensation polymerization, chain growth or radical polymerization. For example, primary amines can be reacted with 1,1'-diethylmethylenemalonate (DEMM) via anionic polymerization to form polymeric DEMM.

[0057] The first coating layer and / or the second coating layer can include a curable composition having any of the aforementioned features or characteristics in any combination. For example, the 1,1-diactivated vinyl compound can include a methylene dicarbonyl compound, a dihalovinyl compound, a dihaloalkyl disubstituted vinyl compound, or a cyanoacrylate compound, or any multifunctional form thereof, or any combination thereof. The curable composition forming the coating layer can include an activator (e.g., an amine, e.g., a tertiary amine such as DABCO or DMAE / DMEA, or an ionic liquid). The curable composition forming the coating layer can include an accelerator (e.g., a strong acid, e.g., a sulfonic acid and / or a heteropoly acid), which further includes a polyol, a polyamine, a polythiol, or a polycarbamate, which can include, in particular, in some examples, a multifunctional polymer resin, or a multifunctional monomer compound, or a combination thereof. The curable composition forming the coating layer can include an extender (e.g., an anhydride-containing vinyl polymer).

[0058] As mentioned above, the hardenable composition used to form one or more coating layers in the multi-layer coating can include any combination of acid accelerators, activator compounds, and / or extenders. Without being bound by any theory, the presence of acid accelerators and / or activator compounds and / or extenders in the hardenable composition can affect the final coating properties by modulating the cure kinetics and / or extent of the Michael addition reaction to the self-polymerization of the 1,1-diactivated vinyl compound and / or its multifunctional form. In some examples, the acid catalyst can include the aforementioned "strong acids" and / or weaker acids. Suitable weaker acids that can be incorporated into the hardenable composition include, for example, inorganic weak acids and organic weak acids. In this context, a weak acid is defined as having a pKa in the range of -1.3 to 7 in water at 25°C. Suitable inorganic weak acids include, for example, sulfamic acid, phosphoric acid, hypochlorous acid, and boric acid. Suitable weak organic acids include, for example, carboxylic acids such as oxalic acid, acetic acid, propionic acid, octanoic acid, stearic acid, isostearic acid, benzoic acid, and citric acid.

[0059] As used herein, the terms "cure" and "curing" refer to the progression of a liquid curable composition from a liquid state to a cured state, and include physical drying of the curable composition via evaporation of a solvent or carrier (e.g., a thermoplastic curable composition) and / or chemical crosslinking of components in the curable composition (e.g., a thermoset curable composition). In this regard, the term "cured" as used herein refers to a state of the liquid curable composition where a film or layer formed from the liquid curable composition is at least dry to the touch.

[0060] In some examples, curing the first coating layer and / or the second coating layer can include spraying an activator solution over and / or under at least a portion of the first coating layer and / or the second coating layer. The activator solution can include an activator (as described above) dissolved or otherwise dispersed in a liquid carrier. The activator solution can include an activator compound, such as an amine activator (e.g., a tertiary amine compound, such as DABCO or DMAE / DMEA), dissolved in an aqueous or organic solvent (e.g., an ester solvent, such as n-butyl acetate). The activator solution can be sprayed or otherwise applied over the substrate and the applied curable composition over the pre-applied activator solution. Alternatively, or in addition, the activator solution can be sprayed or otherwise applied over a pre-applied layer or film of the curable composition. The activator solution can initiate a polymerization reaction and / or a Michael addition reaction at the interface of the applied curable composition layer or film, and can migrate into the layer or film to further initiate the curing reaction.

[0061] In some examples, the curing of the first coating layer can be initiated by an activator compound present in the second coating layer, or the curing of the second coating layer can be initiated by an activator compound present in the first coating layer. For example, the first coating layer can include an activator compound, and the curing of the second coating layer can include activating a polymerization reaction and / or an addition reaction in the second coating layer by the activator compound in the first coating layer. In this manner, the activator compound in the first coating layer can initiate a polymerization reaction and / or a Michael addition reaction in the second coating layer at the interface between the two layers. Also, the activator compound in the first coating layer can migrate through the interface to the second coating layer to further initiate a curing reaction. In this example, the chemical composition of the first coating layer can be such that the activator does not function to initiate a crosslinking or other curing reaction in the first coating layer, but does initiate a curing reaction in the second coating layer when the second coating layer is applied over the first coating layer and in contact with it.

[0062] Alternatively, the second coating layer can include an activator compound, and curing the first coating layer includes activating a polymerization and / or addition reaction in the first coating layer with the activator compound in the second coating layer. In this manner, the activator compound in the second coating layer can initiate a polymerization and / or Michael addition reaction in the first coating layer at the interface between the two layers. Also, the activator compound in the second coating layer can migrate through the interface to the first coating layer to initiate further curing reactions. In this example, the chemical composition of the second coating layer is such that the activator does not function to initiate crosslinking or other curing reactions in the second coating layer, but rather acts to crosslink and / or crosslink the first coating layer or the second coating layer. The composition may be such that when a coating layer is applied in contact with it, it actually initiates a curing reaction in the first coating layer. Activators present in either the first or second coating layer that initiate a crosslinking or other curing reaction in the other coating layer can include activator compounds such as amine activators (e.g., tertiary amine compounds such as DABCO or DMAE / DMEA).

[0063] In some examples, the first and / or second coating layers can be applied over at least a portion of a bare substrate or a previously applied coating (e.g., a primer coating) using application techniques such as spraying, electrostatic spraying, dipping, rolling, brushing, electrocoating, and the like. Once applied, the first and second coating layers can be dehydrated and / or cured. As mentioned above, curing of the first and second coating layers can be performed sequentially (i.e., the first coating layer is cured before the second coating layer is applied) or simultaneously, with or without intermediate flash, drying, or dehydration steps. For example, the first coating layer can be applied and dehydrated, the second coating layer can be applied over the dehydrated first coating layer, and both the first and second coating layers can be baked or otherwise treated to cure the multilayer system. The specific curing conditions of the coating layers are based at least in part on the chemical formulation of the curable composition that forms the layer. In some examples, the first coating layer and / or the second coating layer can be dehydrated and / or cured, independently or together, at a temperature ranging from ambient temperature (about 20°C to 25°C) to 500°C, or any subrange encompassed therein, such as ambient to 200°C, ambient to 150°C, ambient to 140°C, ambient to 130°C, ambient to 120°C, ambient to 100°C, ambient to 90°C, ambient to 80°C, ambient to 60°C, or ambient to 50°C.

[0064] As mentioned above, the 1,1-diactivated vinyl compound and / or its multifunctional form can undergo a polymerization reaction (e.g., anionic polymerization initiated by an amine or other alkaline activator compound). Thus, after curing, at least one of the cured first coating layer and / or the cured second coating layer can include a polymerization reaction product of the 1,1-diactivated vinyl compound and / or its multifunctional form. The 1,1-diactivated vinyl compound and / or its multifunctional form can include a dialkyl methylene malonate, a diaryl methylene malonate, a multifunctional form of a dialkyl methylene malonate, or a multifunctional form of a diaryl methylene malonate, or any combination thereof.

[0065] Furthermore, as mentioned above, the 1,1-diactivated vinyl compound and / or its multifunctional form can function as a crosslinker / curing agent for the multifunctional polymer resin or multifunctional monomer compound. Again, without being bound by any theory, it is believed that the vinyl group(s) in the 1,1-diactivated vinyl compound and / or its multifunctional form can react with the hydroxyl, amine, mercapto, and / or carbamate groups in the multifunctional polymer resin or multifunctional monomer compound via a Michael addition mechanism, thereby forming stable covalent linkages. Thus, after curing, at least one of the cured first coating layer and / or the cured second coating layer can include the polymerization and addition reaction products of (1) a polyol, polyamine, polythiol, or polycarbamate, or any combination thereof, and (2) the 1,1-diactivated vinyl compound and / or its multifunctional form. The 1,1-diactivated vinyl compound and / or multifunctional forms thereof may be a dialkyl methylene malonate, a diaryl methylene malonate, a multifunctional form of a dialkyl methylene malonate, or a multifunctional form of a diaryl methylene malonate, or any of these. The present invention may include any combination of the above.

[0066] In some examples, after curing, at least one of the cured first coating layer and / or the cured second coating layer can include a polymerization reaction product of dialkyl methylene malonate and / or a multifunctional form of dialkyl methylene malonate. The multifunctional form of dialkyl methylene malonate can include a transesterification adduct of dialkyl methylene malonate and at least one polyol. The transesterification adduct of dialkyl methylene malonate and at least one polyol can include a transesterification adduct of dialkyl methylene malonate and a diol (e.g., an alkane diol, such as 1,5-pentane diol or 1,6-hexane diol). In some examples, after curing, at least one of the cured first coating layer and / or the cured second coating layer can also include an addition reaction product of (1) a polyol, a polyamine, a polythiol, or a polycarbamate, or any combination thereof, with (2) a dialkyl methylene malonate and a multifunctional form of the dialkyl methylene malonate. The dialkyl methylene malonate and / or the multifunctional form of the dialkyl methylene malonate can include, for example, dimethyl methylene malonate (D3M) or diethyl methylene malonate (DEMM).

[0067] The invention described herein includes a multilayer coating comprising a coating layer formed from the curable composition described above. For example, the multilayer coating can include a first coating layer applied over at least a portion of a substrate, and a second coating layer applied over at least a portion of the first coating layer. The first coating layer and the second coating layer both independently comprise a polymeric resin. The first coating layer and / or the second coating layer can include a polymerization reaction product of a 1,1-diactivated vinyl compound, or a multifunctional form thereof, or a combination thereof. The first coating layer and / or the second coating layer can further include an addition reaction product of (1) a polyol, a polyamine, a polythiol, or a polycarbamate, or any combination thereof, and (2) a 1,1-diactivated vinyl compound, or a multifunctional form thereof, or a combination thereof.

[0068] In instances where only the first or second coating layer is formed from a curable composition comprising a 1,1-diactivated vinyl compound and / or a multifunctional form thereof (and optionally a multifunctional resin or compound), the other coating layer may be formed from a different curable composition comprising any useful formulation. Other types of curable compositions that may be used with a curable composition comprising a 1,1-diactivated vinyl compound, or a multifunctional form thereof, or combinations thereof to produce a multilayer coating include, for example, polyurethane-based coating compositions, polyurea-based coating compositions, acrylic-based coating compositions, epoxy-based coating compositions, polyester-based coating compositions, polyether-based coating compositions, polythioether-based coating compositions, polyamide-based coating compositions, polycarbonate-based coating compositions, polycarbamate-based coating compositions, and aminoplast-based coating compositions (including coating compositions comprising urea-formaldehyde and / or melamine-formaldehyde resins).

[0069] In some examples, the first coating layer comprises a thermosetting resin including a polyester resin, a polyurethane resin, a polyurea resin, a polyether resin, a polythioether resin, a polycarbonate resin, a polycarbamate resin, an epoxy resin, a phenolic resin, or an aminoplast resin, or any combination thereof, and the second coating layer comprises a polymerization reaction product of a 1,1-diactivated vinyl compound, or a multifunctional form thereof, or a combination thereof. The second coating layer can comprise a clearcoat layer.

[0070] Curable compositions containing 1,1-diactivated vinyl compounds, or multifunctional forms thereof, or combinations thereof, can be used in combination with other coating chemistries to form other coating layers of a multilayer coating system to form basecoats, topcoats, tiecoats, etc. As used herein, the term "basecoat" refers to a coating layer that is deposited on a primer and / or directly on a substrate, and optionally includes a component (e.g., pigment) that affects color and / or provides other visual effects. As used herein, the term "topcoat" refers to a coating layer that is deposited over another coating layer, such as a basecoat. A topcoat is often, but not always, a "clearcoat," which as used herein refers to a coating layer that appears at least substantially transparent or appears completely transparent. As used herein, the term "substantially transparent" refers to a coating in which the surface beyond the coating is at least partially visible to the naked eye when viewed through the coating. As used herein, the term "completely transparent" refers to a coating in which the surface beyond the coating is completely visible to the naked eye when viewed through the coating. A clearcoat can include colorants, such as pigments, provided that the colorants do not interfere with the desired transparency of the clearcoat layer. In some instances, the clearcoat layer does not include an added colorant, such as a pigment. As used herein, the term "tie coat" means a coating layer that is positioned between two other coating layers, such as a coating layer that is positioned between a basecoat layer and a topcoat layer.

[0071] The multi-layer coating described herein can include a primer coating layer, which can correspond to the first coating layer. As used herein, "primer coating layer" refers to an undercoat that can be deposited on a substrate to prepare the surface for applying a protective or decorative coating system. The primer coating layer can be formed as the first coating layer over at least a portion of the substrate, and a second coating layer (e.g., a base coat) can be formed over at least a portion of the primer coating layer. Thus, the multi-layer coating of the present invention can include a primer coating layer, and one or more of a base coat layer and a top coat layer.

[0072] The first coating layer, including the primer coating layer, can be formed from a coating composition that includes a film-forming resin, such as a cationic-based resin, an anionic-based resin, and / or any of the additional film-forming resins described above. The coating composition used to form the primer coating composition can include a corrosion inhibitor, particularly in coating formulations intended for use on metal substrates. As used herein, "corrosion inhibitor" refers to a component that reduces the rate or severity of surface corrosion on metal or metal alloy substrates. The first coating layer can also be a direct gloss coating. Direct gloss coating, in this context, refers to a colored topcoat layer that has a glossy or matte finish.

[0073] The corrosion inhibitors may include, but are not limited to, an alkali metal component, an alkaline earth metal component, a transition metal component, or any combination thereof. The term "alkali metal" refers to Group 1 elements of the Periodic Table of Chemical Elements (International Union of Pure and Applied Chemistry (IUPAC)), including, for example, cesium (Cs), francium (Fr), lithium (Li), potassium (K), rubidium (Rb), and sodium (Na). The term "alkaline earth metal" refers to Group 2 elements of the Periodic Table of Chemical Elements (IUPAC), including, for example, barium (Ba), beryllium (Be), calcium (Ca), magnesium (Mg), and strontium (Sr). The term "transition metal" refers to Group 3 elements of the Periodic Table of Chemical Elements (IUPAC), including, for example, barium (Ba), beryllium (Be), calcium (Ca), magnesium (Mg), and strontium (Sr). , refers to Groups 3-12 of the Periodic Table of the Chemical Elements (IUPAC), which includes, for example, titanium (Ti), zirconium (Zr), chromium (Cr), and zinc (Zn), among various other elements. Examples of inorganic components that can function as corrosion inhibitors in the primer coating composition include magnesium oxide, magnesium hydroxide, magnesium carbonate, magnesium phosphate, magnesium silicate, zinc oxide, zinc hydroxide, zinc carbonate, zinc phosphate, zinc silicate, zinc powder, and combinations thereof.

[0074] The components of the primer coating composition can be selected to form an electrodepositable coating composition. As used herein, the term "electrodepositable coating composition" refers to a coating composition that can be deposited on a conductive substrate under the influence of an applied electric potential. Examples of electrodepositable coating compositions include anionic and cationic electrodepositable coating compositions, such as epoxy or polyurethane-based coatings, such as those electrodepositable coatings described in U.S. Pat. No. 4,933,056, column 2, lines 48 to 5, line 53; U.S. Pat. No. 5,530,043, column 1, lines 54 to 4, line 67; U.S. Pat. No. 5,760,107, column 2, lines 11 to 9, line 60; and U.S. Pat. No. 5,820,987, column 3, lines 48 to 10, line 63, each of which is incorporated herein by reference. Suitable electrodepositable coating compositions also include those commercially available from PPG Industries, Inc., such as the POWERCRON® series of anodic and cathodic epoxy and acrylic coatings, ED-6060C, ED-6280, ED-6465, and ED-7000.

[0075] As previously mentioned, the primer coating composition can be directly deposited as a first coating layer over at least a portion of the substrate, followed by application of a second coating layer. Alternatively, the first coating layer can be deposited over the cured primer coating layer, where the first coating layer functions as a basecoat layer, and the second coating layer can be deposited over the first coating layer, where the second coating layer functions as a topcoat layer or a tiecoat layer (if a subsequent layer is applied over the second coating layer). Once the primer coating composition has been applied to at least a portion of the substrate, an overcoating layer, whether a basecoat or a topcoat, can be applied after the primer coating layer has dehydrated and / or cured. The primer coating composition can be dehydrated and / or cured, for example, at a temperature of 175°C to 205°C, to form the primer coating layer.

[0076] When a curable composition including a 1,1-diactivated vinyl compound, or a multifunctional form thereof, or a combination thereof, is used to form a basecoat layer or a tiecoat layer, the multilayer coating can include a topcoat layer formed from a different curable composition, such as a curable composition formulated to produce an isocyanate crosslinked polyurethane clearcoat. Further examples of topcoat layers that can be used with the multilayer coating of the present invention include those described in U.S. Pat. No. 4,650,718, column 1, lines 62 to 10, line 16; U.S. Pat. No. 5,814,410, column 2, lines 23 to 9, line 54; and U.S. Pat. No. 5,891,981, column 2, lines 22 to 12, line 37, each of which is incorporated herein by reference. Suitable topcoat coating compositions that can be used to form a topcoat layer over a coating layer comprising the reaction product of a 1,1-diactivated vinyl compound, or multifunctional forms thereof, or combinations thereof, also include those commercially available from PPG Industries, Inc. under the trademarks NCT®, DIAMOND COAT®, and CERAMICLEAR®.

[0077] As mentioned above, at least one of the first coating layer and / or the second coating layer in the multilayer coating of the present invention can include a polymerization reaction product of a 1,1-diactivated vinyl compound, or a multifunctional form thereof, or a combination thereof. The first coating layer and / or the second coating layer can further include an addition reaction product of (1) a polyol, a polyamine, a polythiol, or a polycarbamate, or any combination thereof, and (2) a 1,1-diactivated vinyl compound, or a multifunctional form thereof, or a combination thereof. As mentioned above, the 1,1-diactivated vinyl compound can include, for example, a methylene dicarbonyl compound, a dihalovinyl compound, a dihaloalkyl disubstituted vinyl compound, or a cyanoacrylate compound, or any multifunctional form thereof, or any combination thereof.

[0078] In some examples of multi-layer coatings, the first coating layer and / or the second coating layer can include a polymerization reaction product of dialkyl methylene malonate, diaryl methylene malonate, a multifunctional form of dialkyl methylene malonate, or a multifunctional form of diaryl methylene malonate, or any combination thereof. For example, the first coating layer and / or the second coating layer can include a polymerization reaction product of diethyl methylene malonate and a multifunctional form of diethyl methylene malonate. The multifunctional form of diethyl methylene malonate can include a transesterification adduct of diethyl methylene malonate and at least one polyol. The transesterification adduct of diethyl methylene malonate and at least one polyol can include a transesterification adduct of diethyl methylene malonate and a diol (e.g., an alkane diol, such as 1,5-pentane diol or 1,6-hexane diol).

[0079] In some examples of multi-layer coatings, the first coating layer and / or the second coating layer may be formed from a curable composition that includes an accelerator (e.g., a strong acid, such as a sulfonic acid and / or a heteropoly acid) and / or an activator (e.g., an amine, such as a tertiary amine such as DABCO or DMAE / DMEA, or an ionic liquid) and / or an extender (e.g., an anhydride-containing vinyl polymer). In some examples, the first coating layer includes an activator compound that activates a polymerization reaction in the second coating layer when the second coating layer is applied over the first coating layer. In other examples, the second coating layer includes an activator compound that activates a polymerization reaction in the first coating layer when the second coating layer is applied over the first coating layer.

[0080] In some examples, the second coating layer comprises a polymerization reaction product of a 1,1-diactivated vinyl compound and / or a multifunctional form thereof (and optionally an addition reaction product of a multifunctional resin or compound with a 1,1-diactivated vinyl compound and / or a multifunctional form thereof), and the first coating layer is formed from a curable composition that cures when heated at a temperature of less than 500° C., less than 200° C., less than 150° C., less than 140° C., less than 130° C., less than 120° C., or less than 100° C. Curable compositions forming the first coating layer can include, for example, polyurethane-based coating compositions, polyurea-based coating compositions, acrylic-based coating compositions, epoxy-based coating compositions, polyester-based coating compositions, polyether-based coating compositions, polythioether-based coating compositions, polyamide-based coating compositions, polycarbonate-based coating compositions, polycarbamate-based coating compositions, and aminoplast-based coating compositions (including coating compositions comprising urea-formaldehyde and / or melamine-formaldehyde resins). In some examples, the first coating layer is formed from a curable composition that is free (i.e., substantially free) of melamine resins and formaldehyde condensates. The term "substantially free," as used herein, means that the described material is present, if at all, at incidental impurity levels, generally less than 1000 parts per million (ppm) by weight based on the weight of the total curable composition.

[0081] In some examples, the first coating layer comprises a polymerization reaction product of a 1,1-diactivated vinyl compound and / or a multifunctional form thereof (and optionally an addition reaction product of a multifunctional resin or compound with a 1,1-diactivated vinyl compound and / or a multifunctional form thereof), and the second coating layer comprises a clearcoat layer (e.g., an isocyanate-crosslinked polyurethane clearcoat layer).

[0082] In some examples, the first coating layer comprises a polymerization reaction product of a 1,1-diactivated vinyl compound and / or a multifunctional form thereof (and optionally an addition reaction product of a multifunctional resin or compound with a 1,1-diactivated vinyl compound and / or a multifunctional form thereof), and the first coating layer is applied directly onto the metal substrate. The first coating layer applied directly onto the metal substrate can further comprise a wetting agent. For example, the first coating layer applied directly onto the metal substrate can further comprise a polysiloxane-based wetting agent, such as a polyether-modified polydimethylsiloxane (e.g., poly(ethylene oxide)-polydimethylsiloxane and / or poly(propylene oxide)-polydimethylsiloxane), and the like.

[0083] The multi-layer coatings can be applied to a wide range of substrates, including vehicle components and components of freestanding structures, such as buildings, bridges, or other public infrastructure. More specific substrates include, but are not limited to, automotive substrates (e.g., body panels and other parts and components), industrial substrates, aircraft components, watercraft components, packaging substrates (e.g., food and beverage cans), wood floors and furniture, apparel, electronics (e.g., enclosures and circuit substrates), glass and transparencies, sporting goods (e.g., golf balls, etc.), appliances (e.g., dishwashers, clothes washers, clothes dryers). Substrates can be, for example, metallic or non-metallic. Metallic substrates include, but are not limited to, tin, steel (including, among others, electrogalvanized steel, cold-rolled steel, hot-dip galvanized steel), aluminum, aluminum alloys, zinc-aluminum alloys, steel coated with zinc-aluminum alloys, and aluminum-plated steel. Non-metallic substrates include polymeric, plastic, polyester, polyolefin, polyamide, cellulose, polystyrene, polyacrylic, poly(ethylene naphthalate), polypropylene, polyethylene, nylon, EVOH, polylactic acid, other "green" polymeric substrates, poly(ethylene terephthalate) (PET), polycarbonate, polycarbonate acrylobutadiene styrene (PC / ABS), polyamide, wood, veneer, wood composites, particle board, fiberboard, cement, concrete, brick, stone, paper, cardboard, fabric, leather (both synthetic and natural), glass or fiberglass composites, carbon fiber composites, mixed fiber (e.g., fiberglass and carbon fiber) composites, etc. The substrate may be a substrate that has already been treated in some manner, such as to impart visual and / or color effects, a protective pretreatment or primer coating layer, or other coating layers, etc.

[0084] The present invention further provides an article comprising a multi-layer coating formed from the curable composition described herein. For example, the multi-layer coating of the present invention is also suitable for use as a packaging coating. The application of various pretreatments and coatings to packaging is well established. Such treatments and / or coatings can be used, for example, in the case of metal cans, where the treatments and / or coatings are used to retard or inhibit corrosion, provide decorative coatings, facilitate handling during manufacturing, and the like. Coatings can be applied to the inside of such cans to prevent the contents from contacting the metal of the container. Coatings Applied to the Inside of Metal Cans can help prevent corrosion in the headspace of the can, which is the area between the product's fill line and the can's lid. Corrosion in the headspace is particularly problematic for food products with high salt content. Coatings can also be applied to the exterior of metal cans. Certain coatings of the present invention can be applied specifically for use with, for example, coiled metal stock for making can lids ("can end stock"), and coiled metal stock for making can caps and closures ("cap / closure stock"). Coatings designed for use on can end stock and cap / closure stock are typically flexible and extensible, since the pieces are typically cut and separated from the coiled metal stock after application. Coatings for cans that are subject to relatively rigorous temperature and / or pressure requirements should also be resistant to popping, corrosion, whitening and / or blistering.

[0085] Thus, the present invention is further directed to a package at least partially coated with any of the aforementioned multi-layer coatings. A "package" is anything that is used to contain another item, particularly for transportation from a point of manufacture to a consumer and for subsequent storage by the consumer. A package is therefore understood to be anything that is sealed to keep its contents from deteriorating until opened by the consumer. A "package" of the present invention is therefore distinct from a storage container or heat-resistant container in which a consumer makes and / or stores a food product, such containers only being capable of maintaining the freshness or integrity of the food product for a relatively short period of time. A package according to the present invention can be made from metal or non-metal, e.g., plastic or laminate, and can be of any form. One example of a suitable package is a laminate tube. Another example of a suitable package is a metal can. The term "metal can" includes any kind of metal can, container, or any kind of receptacle, or part thereof, that is sealed by a food / beverage manufacturer to minimize or eliminate damage to the contents until such package is opened by the consumer. An example of a metal can is a food can, and the term "food can(s)" is used herein to refer to a can, container, or any type of receptacle, or part thereof, used to hold any type of food and / or beverage. The term "metal can(s)" specifically includes food cans, It also specifically includes "can ends," including "easy open ends," which are typically separated from the can lid material and used in conjunction with food and beverage packaging. The term "metal cans" also specifically includes metal caps and / or or closures, such as bottle caps of any size, screw top caps and lids, lug caps, and the like. Metal cans can be used to hold other items as well, including, but not limited to, personal care products, bug sprays, spray paints, any other compounds suitable for packaging in an aerosol can. Cans can include "two-piece cans" and "three-piece cans" as well as ironed one-piece cans, such as those often found in applications involving aerosol products. Packages coated according to the present invention can include plastic bottles, plastic tubes, laminates, and flexible packaging, such as those made from PE, PP, PET, and the like. Such packaging can hold, for example, food, toothpaste, personal care products, and the like. The coating can be applied to the interior and / or exterior of the package.

[0086] In some examples, the multi-layer coatings prepared and used in accordance with the present invention may be substantially free, essentially free, and / or completely free of bisphenol A and epoxy compounds derived from bisphenol A ("BPA"), such as bisphenol A diglycidyl ether ("BADGE"). The term "substantially free," as used in this context, means that the coating composition contains less than 1000 parts per million (ppm) of any of the foregoing compounds, derivatives, or residues thereof. "Essentially free" means having less than 100 ppm, and "completely free" means less than 20 parts per billion (ppb). EXAMPLES

[0087] The following examples are intended to further illustrate the present invention. It is understood that the present invention described herein is not necessarily limited to the examples described in this section. In particular, the curable composition of the present disclosure can take various forms, including sealants, coatings, adhesives, encapsulants, and embedding compositions, as described in some of the following examples presented herein. Example 1A Coating layer comprising the polymerization product of a 1,1-diactivated vinyl compound on a metal substrate

[0088] A 1,1-diactivated vinyl compound (dimethylmethylenemalonate) and a polyether-modified polydimethylsiloxane (BYK-333 available from BYK-Chemie GmbH) were added to a 20 milliliter glass vial and stirred under ambient conditions until homogeneous. The dimethylmethylenemalonate and polyether-modified polydimethylsiloxane were combined together in the amounts provided in Table 1 to form a liquid coating composition. [Table 1]

[0089] The liquid coating compositions were applied directly onto 4" x 12" hot dip galvanized steel panels (available from ACT Test Panels LLC) using a 1.4 mil wire round drawdown bar to form a coating layer. The coating layers were tested for film drying and curing characteristics. Tack free time was measured as the amount of time required for the applied coating film to achieve a level of dryness such that a cotton ball was applied and removed without transferring the cotton fibers to the coating surface. The cotton ball was applied in the following manner: 1. Hold a cotton ball approximately 3 inches above the substrate panel in a horizontal position and drop the cotton ball onto the applied coating film. 2. Hold the substrate panel with the coating side facing up for 5±2 seconds to keep the cotton ball in contact with the coating film. After 3.5±2 seconds, the substrate panel is flipped coated side down. If the cotton ball falls off without leaving any fibers on the membrane, the coating is not sticky. b. If the cotton ball does not fall off or leaves fibers behind, repeat steps 1-3 at appropriate time intervals (e.g., every 15 minutes) until the coating is no longer tacky. The coating layer reached a tack-free state between 15 and 30 minutes under ambient conditions after application to the steel panels.

[0090] Also, an MEK double rub test was performed. With the MEK double rub test, double (back and forth) rubs are performed by hand with a rag soaked in methyl ethyl ketone (MEK) to record the number of double rubs required to dissolve the applied coating and thus make the substrate visible. The MEK double rub test was performed after about 24 hours under ambient conditions, measured from the time of coating application. Double rubs were performed up to 100 times and then discontinued. The coating layer was Withstood 100 MEK double rubs with no visible damage.

[0091] The relatively rapid drying of the applied coating layer and the development of MEK solvent resistance indicated the formation of a polymerized and crosslinked film with good intramembrane cohesion and adhesion to the underlying steel substrate. Example 1B A coating layer comprising the polymerization product of a 1,1-diactivated vinyl compound on a metal substrate.

[0092] A 1,1-diactivated vinyl compound (dimethylmethylenemalonate) and a polyether-modified polydimethylsiloxane (BYK-333 available from BYK-Chemie GmbH) were added to a 20 milliliter glass vial and stirred under ambient conditions until homogeneous. The dimethylmethylenemalonate and polyether-modified polydimethylsiloxane were combined together in the amounts provided in Table 2 to form a liquid coating composition. [Table 2]

[0093] The liquid coating compositions were applied directly onto 4" x 12" electrogalvanized steel panels (available from ACT Test Panels LLC) using a 1.4 mil wire round drawdown bar to form a coating layer. The coating layers were tested for film drying and curing characteristics. The time to tack-free was measured as previously described in Example 1A. The coating layers reached a tack-free state at times between 15 and 30 minutes under ambient conditions after application to the steel panels. MEK double rub testing was also performed as previously described in Example 1A (measured from the time of coating application and after approximately 24 hours under ambient conditions). The coating layers withstood 100 MEK double rubs without visible damage.

[0094] The relatively rapid drying of the applied coating layer and the development of MEK solvent resistance indicated the formation of a polymerized and crosslinked film with good intramembrane cohesion and adhesion to the underlying steel substrate. Example 1C A coating layer comprising the polymerization product of a 1,1-diactivated vinyl compound on a metal substrate.

[0095] A 1,1-diactivated vinyl compound (dimethylmethylenemalonate) and a polyether-modified polydimethylsiloxane (BYK-333 available from BYK-Chemie GmbH) were added to a 20 milliliter glass vial and stirred under ambient conditions until homogeneous. The dimethylmethylenemalonate and polyether-modified polydimethylsiloxane were combined together in the amounts provided in Table 3 to form a liquid coating composition. [Table 3]

[0096] The liquid coating compositions were applied directly onto 4" x 12" 6022 aluminum alloy panels (available from ACT Test Panels LLC) using a 1.4 mil wire round drawdown bar to form a coating layer. The coating layers were tested for film drying and curing characteristics. The time to tack-free was measured as previously described in Example 1A. The coating layers reached a tack-free state at times between 15 and 30 minutes under ambient conditions after application to the aluminum alloy panels. MEK double rub testing was also performed as previously described in Example 1A (measured from the time of coating application and after approximately 24 hours under ambient conditions). The coating layers withstood 100 MEK double rubs without visible damage.

[0097] The relatively rapid drying of the applied coating layer and the development of MEK solvent resistance indicated the formation of a polymerized and crosslinked film with good intrafilm cohesion and adhesion to the underlying aluminum alloy substrate. Example 2 A multilayer coating system comprising the polymerization product of a 1,1-diactivated vinyl compound.

[0098] A pigmented water-based basecoat composition (Envirobase High Performance T409 (black) available from PPG Industries, Inc.) was applied over a 4 inch by 12 inch cold rolled steel substrate panel pre-coated with ED-6060C electrocoat (electrocoat available from PPG Industries, Inc., and substrate panels available in pre-coated form from ACT Test Panels LLC). The basecoat layer was applied under ambient conditions by drawdown over the electrocoat on the substrate panel using a drawdown bar with a 1 mil gap. The applied basecoat layer was allowed to dry under ambient conditions for approximately 10-15 minutes until a matte appearance was observed.

[0099] A second coating composition was immediately applied over the dried basecoat layer to form a second coating layer. The second coating composition included a combination of 1,1-diactivated vinyl compounds and their multifunctional forms (a mixture of diethyl methylene malonate and a transesterified adduct of diethyl methylene malonate and 1,6-hexanediol, as described in US Patent Application Publication No. 2014 / 0329980). The second coating layer was applied under ambient conditions by drawdown over the dried basecoat layer using a drawdown bar with a 3 mil gap. The second coating layer maintained visible gloss under ambient conditions and was tack-free within 5 minutes of application over the basecoat layer (measured using the cotton ball method as described above in Example 1A). Also, immediately after reaching a tack-free state (approximately 5 minutes after application of the second coating layer), MEK double rub testing was performed as described above in Example 1A. The second coating layer survived 100 MEK double rubs with no visible damage.

[0100] Prior to application of the second coating layer, the second coating composition has a water-like viscosity. The coating exhibited a high viscosity and gelled only upon contact of the liquid with the underlying basecoat layer. Without wishing to be bound by any theory, it is believed that residual amines in the dried basecoat layer acted as activator compounds to activate the anionic polymerization of diethyl methylene malonate and the transesterified adduct of diethyl methylene malonate and 1,6-hexanediol in the second coating layer. Example 3 A multilayer coating system comprising the polymerization product of a 1,1-diactivated vinyl compound.

[0101] A coating composition comprising a combination of 1,1-diactivated vinyl compounds and their multifunctional forms (a mixture of diethyl methylene malonate and a transesterified adduct of diethyl methylene malonate and 1,6-hexanediol as described in US Patent Application Publication No. 2014 / 0329980) was applied over a 4" x 12" cold rolled steel substrate panel pre-coated with ED-6060C electrocoat (electrocoat available from PPG Industries, Inc., and substrate panel available in pre-coated form from ACT Test Panels LLC). The coating layer was applied under ambient conditions by drawdown over the electrocoat on the substrate panel using a drawdown bar with a 3 mil gap. The coating composition exhibited a water-like viscosity and did not gel upon liquid contact with the underlying electrocoat layer.

[0102] Eight grams of an activator solution of 1,4-diazabicyclo[2.2.2]octane (DABCO) in n-butyl acetate (0.3 wt % solution) was sprayed over the coating layer using a SATA Jet 4000 B HVLP equipped with a 1.3 mm nozzle at 10 psi. The coating layer became tack-free immediately upon spraying of the activator solution (measured using the cotton ball method described above in Example 1A). Also, within 5 minutes of spraying of the activator solution, a MEK double rub test was performed as described above in Example 1A. The coating layer withstood 100 MEK double rubs without visible damage.

[0103] As mentioned above, before and after the application of the coating layer, the coating composition exhibited a water-like viscosity and gelled only after the activator solution was sprayed over the applied coating layer. Without being bound by any theory, it is believed that the fully cured electrodeposition coating on the substrate panel did not gel upon application because (1) it did not contain any residual amine or other alkaline compound to activate the anionic polymerization of diethyl methylene malonate and the transesterified adduct of diethyl methylene malonate and 1,6-hexanediol in the second coating layer, or (2) any residual amine or other alkaline compound was insufficient in mobility, possibly due to the crosslinked state of the binder resin in the electrodeposition coating, to migrate to the surface of the cured electrodeposition coating or otherwise contact the coating layer applied over the electrodeposition coating. However, it is expected that an electrodeposition coating composition containing an amine or other alkaline compound may activate anionic polymerization in a coating composition containing 1,1-diactivated vinyl compounds and / or multifunctional forms thereof applied over such an electrodeposition coating layer prior to the curing of the electrodeposition coating layer. Example 4A A multilayer coating system comprising the polymerization product of a 1,1-diactivated vinyl compound.

[0104] The waterborne basecoat system containing the two coating layers was applied over 4 inch by 12 inch cold rolled steel substrate panels that had been pre-coated with ED-6465 electrocoat (PPG (electrocoatings available from ACT Industries, Inc., and substrate panels available in pre-coated form from ACT Test Panels LLC). The coating layers were applied under controlled conditions of 20-22°C temperature and 60-65% relative humidity. A first coating layer of the basecoat system (Basecoat A below) was sprayed over the electrocoat on the substrate panel using a Binks Model 95AR conventional air spray gun with a 1.8 millimeter nozzle at 60 psi. The first coating layer of the basecoat system was allowed to dry under ambient conditions for 5 minutes.

[0105] Basecoat A was a red pigmented basecoat composition suitable for use as a first basecoat layer in a multiple layer coating system, prepared in the following manner: Components 1-9 listed in Table 4 below were mixed with stirring to form an aqueous phase mixture. A red tinting agent (component 10) and a white tinting agent (component 11) were then added to the aqueous phase mixture. Components 12-18 were mixed to form an organic phase mixture and stirred for 15 minutes before being added to the aqueous phase mixture. After the aqueous and organic phase mixtures were mixed together, the pH of the combined mixture was adjusted to 8.6 using a 50% aqueous dimethylethanolamine solution. The resulting basecoat composition was aged for 24 hours under ambient conditions before the viscosity was adjusted with demineralized water. The high shear viscosity of the Basecoat A composition was adjusted to 95 cps at 1000 sec-1 using a Brookfield CAP 2000 viscometer equipped with spindle number 1. [Table 4-1] [Table 4-2]

[0106] A second coating layer of the basecoat system (Basecoat B) was sprayed over the dried first coating layer of the basecoat system using a Binks Model 95AR conventional air spray gun with a 1.8 millimeter nozzle at 60 psi. The second coating layer was sprayed in two successive coats without any intermediate drying between spray applications. The two coating layers of the basecoat system were then dried under ambient conditions for 5 minutes and then dehydrated at 70° C. for 7 minutes. The film thickness of the basecoat system (both coating layers) after dehydration was approximately 34-40 micrometers.

[0107] Basecoat B was a metallic red pigmented basecoat composition suitable for use as a second basecoat layer in a multi-layer coating system, prepared in the following manner: Components 1-12, listed in Table 5 below, were mixed with stirring to form an aqueous phase mixture. Components 13 and 14 were then mixed separately for approximately 20 minutes until the mixture was clear, and then added to the remainder of the aqueous phase components with stirring. Components 15-18 were mixed to form an organic phase mixture and stirred for 15 minutes before being added to the aqueous phase mixture. After the aqueous and organic phase mixtures were mixed together, the pH of the combined mixture was adjusted to 8.8 using 50% dimethylethanolamine. The resulting Basecoat B composition was aged for 24 hours under ambient conditions, after which the viscosity was adjusted with demineralized water. The high shear viscosity of the Basecoat B composition was adjusted to 80 cps at 1000 sec-1 using a Brookfield CAP 2000 viscometer equipped with spindle number 1. [Table 5]

[0108] A third coating composition was immediately applied over the dehydrated basecoat system to form a third coating layer. The third coating composition included a combination of 1,1-diactivated vinyl compounds and their multifunctional forms (a mixture of diethyl methylene malonate and the transesterified adduct of diethyl methylene malonate and 1,6-hexanediol, as described in US Patent Application Publication No. 2014 / 0329980). The third coating layer was applied under ambient conditions by drawdown over the dehydrated basecoat layer using a drawdown bar with a 2 mil gap. The substrate panel including the two-layer basecoat system and the overlying third coating layer was allowed to dry under ambient conditions for 10 minutes. Within 10 minutes of application, the third coating layer reached a tack-free state (measured using the cotton ball method previously described in Example 1A).

[0109] After flash drying for 10 minutes under ambient conditions, the substrate panel containing the two-layer basecoat system and the overlying third coating layer was baked at 150° C. for 30 minutes to cure the two-layer basecoat system. MEK double rub testing was performed on the cured multi-layer coating system as described above in Example 1A. The third coating layer (i.e., the multi-layer coating The top layer of the coating system withstood 100 MEK double rubs without visible damage or visible loss of gloss.

[0110] Prior to application of the third coating layer, the third coating composition had a water-like viscosity and gelled only upon liquid contact with the underlying basecoat layer. Without wishing to be bound by any theory, it is believed that residual dimethylethanolamine in the dried basecoat layer acted as an activator compound to activate the anionic polymerization of diethylmethylenemalonate and the transesterified adduct of diethylmethylenemalonate and 1,6-hexanediol in the second coating layer. Example 4B Comparative multi-layer coating system.

[0111] Example 4A was repeated, except that the third coating layer was applied after the two-layer basecoat system was baked and cured. More specifically, the water-based basecoat system including the two coating layers was applied over a 4" x 12" cold-rolled steel substrate panel that had been pre-coated with ED-6465 electrocoat (electrocoat available from PPG Industries, Inc., and substrate panel available in pre-coated form from ACT Test Panels LLC). The coating layers were applied under controlled conditions of temperature of 20-22°C and relative humidity of 60-65%. The first coating layer of the basecoat system (Basecoat A of Example 4A) was sprayed over the electrocoat on the substrate panel using a Binks Model 95AR conventional air spray gun with a 1.8 millimeter nozzle at 60 psi. The first coating layer of the basecoat system was allowed to dry for 5 minutes under ambient conditions.

[0112] A second coating layer of the basecoat system (Basecoat B of Example 4A) was sprayed over the dried first coating layer of the basecoat system using a Binks Model 95AR conventional air spray gun with a 1.8 millimeter nozzle at 60 psi. The second coating layer was sprayed in two successive coats without any intermediate drying between spray applications. The two coating layers of the basecoat system were then dried under ambient conditions for 5 minutes and then dehydrated at 70°C for 7 minutes. The film thickness of the basecoat system (both coating layers) after dehydration was approximately 34-40 micrometers. After dehydration for 7 minutes, the substrate panel containing the two-layer basecoat system was baked at 150°C for 30 minutes to cure the two-layer basecoat system.

[0113] A third coating composition was applied over the cured basecoat system to form a third coating layer. The third coating composition included a combination of 1,1-diactivated vinyl compounds and their multifunctional forms (a mixture of diethyl methylene malonate and a transesterified adduct of diethyl methylene malonate and 1,6-hexanediol, as described in US Patent Application Publication No. 2014 / 0329980). The third coating layer was applied under ambient conditions by drawdown over the cured basecoat layer using a drawdown bar with a 2 mil gap. The third coating layer did not gel and remained in a liquid state indefinitely after application to the cured basecoat system.

[0114] Without wishing to be bound by any theory, it is believed that curing the two-layer basecoat system by baking at 150°C for 30 minutes likely caused the dimethylethanolamine in the basecoat layer to volatilize and evaporate from the basecoat system. Furthermore, any residual dimethylethanolamine present in the cured basecoat system after baking may (1) activate the anionic polymerization of diethyl methylene malonate and the transesterification adduct of diethyl methylene malonate and 1,6-hexanediol in the third coating layer; or (2) was insufficiently mobile, possibly due to the crosslinked state of the binder resin in the system, to migrate to the surface of the cured basecoat system or otherwise contact a subsequently applied third coating layer. Thus, due to the basecoat system curing (crosslinking) prior to application of the third coating layer, the dimethylethanolamine in the basecoat composition was not able to function as an activator compound to activate the anionic polymerization of diethyl methylene malonate and the transesterification adduct of diethyl methylene malonate and 1,6-hexanediol in the third coating layer. Example 5A Multilayer coating systems containing polymerization products of 1,1-diactivated vinyl compounds

[0115] The low temperature cure basecoat was applied over 4" x 12" cold rolled steel substrate panels that had been precoated with ED-6465 electrocoat (electrocoat available from PPG Industries, Inc., and substrate panels available in precoated form from ACT Test Panels LLC). The basecoat compositions were prepared using the components listed in Table 6. [Table 6]

[0116] Basecoat compositions were prepared by mixing the components listed in Table 6 with a conventional mixing blade while avoiding foaming and entrapment of air bubbles. The latex components were pre-prepared as follows:

[0117] First, the polyurethane was prepared by charging the components listed in Table 7 into a four-neck round bottom flask equipped with a thermocouple, a mechanical stirrer, and a condenser. [Table 7]

[0118] The mixture was heated to 50°C and held for 15 minutes. Next, 601.0 parts by weight (grams) of isophorone diisocyanate was charged to the flask over 10 minutes and mixed for 15 minutes. After mixing, 39 parts by weight (grams) of butyl acrylate and 1.6 parts by weight (grams) of dibutyltin dilaurate (DBTDL) were charged to the flask and an immediate exotherm was observed. After the exotherm subsided, the mixture was heated to 90°C and held for 60 minutes. The mixture was cooled to 70°C and 538 grams of butyl acrylate and 94.0 grams of hexanediol diacrylate were charged to the flask. The resulting mixture was held at 60°C, dispersed in water and then cooled to ambient temperature to provide a polyurethane product.

[0119] The polyurethane product was used to produce a latex. The latex contained polyurethane-acrylic shell-core particles with urea linkages, urethane linkages, pendant carboxylic acid functional groups, and pendant keto functional groups on the polyurethane shell. The latex was prepared by charging the components listed in Table 8 into a four-neck round bottom flask equipped with a thermocouple, mechanical stirring device, and condenser. [Table 8] The mixture was heated to 70°C and held for 2 hours with a N2 blanket. After the mixture was heated, 1925 parts by weight (grams) of deionized water and 40 parts by weight (grams) of AEROSOL® OT-75 (surfactant available from Cytec Solvay Group) were charged to the flask and held at 50°C for 15 minutes. Next, 2600.0 parts by weight (grams) of the aforementioned polyurethane product were dispersed in the flask over a period of 20 minutes and mixed for an additional 15 minutes. Next, a mixture of 7.7 parts by weight (grams) of ammonium persulfate and 165 parts by weight (grams) of deionized water was charged to the flask over a period of 15 minutes. The temperature increased from 50°C to 80°C due to the heat of polymerization. The mixture was held at 75°C for an additional hour. After cooling to 40° C., 1.2 parts by weight (grams) of FOAMKILL® 649 (a non-silicone antifoam available from Crucible Chemical Company), 25 parts by weight (grams) of ACTICIDE® MBS (a 1,2-benzisothiazolin-3-one and 2-methyl-4-methyl-1,2-dione antifoam available from Thor GmbH) were added to the mixture. -isothiazolin-3-one mixture), and 55 parts by weight (grams) of deionized water were charged to the flask and mixed for an additional 15 minutes. The resulting latex had a solids content of 38.6% and an average particle size of 60 nm. The average particle size was determined with a Zetasize 3000HS according to the instructions in the Zetasize 3000HS manual.

[0120] A layer of the basecoat composition (Table 4 above) was applied under ambient conditions by drawdown over the electrocoat on the substrate panel using a drawdown bar with a 1 mil gap. The applied basecoat layer was dehydrated at 80° C. for 5 minutes. The resulting layer had a dry film thickness of about 27 micrometers.

[0121] A second coating composition was applied over the dehydrated basecoat layer to form a second coating layer over each panel. The second coating composition included a combination of 1,1-diactivated vinyl compounds and their multifunctional forms (a mixture of diethyl methylene malonate and a transesterified adduct of diethyl methylene malonate and 1,6-hexanediol, as described in U.S. Patent Application Publication No. 2014 / 0329980). The second coating layer was applied under ambient conditions by drawdown over the dehydrated basecoat layer using a drawdown bar with a 2 mil and 4 mil gap (corresponding to a dry film thickness of approximately 30-40 micrometers and 50-60 micrometers, respectively).

[0122] The cure response of the second coating layer was monitored under ambient conditions by measuring the time from application until the layer was dry to the touch (determined by manually touching the second coating layer with a gloved finger). Both the 30-40 μm and 50-60 μm DFT layers achieved a dry to the touch state under ambient conditions between 30 and 45 minutes after application. Additionally, 60 minutes after application of the second coating layer, measurements of the coating hardness were initiated using a standard HM2000 Fischer MicroHardness tester. The results are recorded in Table 9 (hardness is expressed in N / mm 2 (Recorded in units of . [Table 9]

[0123] Also, 60 minutes after the second coating layer is applied, a methyl ethyl ketone solvent double rub test is carried out as described above in Example 1A. The second coating layer withstands 100 methyl ethyl ketone double rubs without visible damage. Also, 5 days after the second coating layer is applied, an acetone solvent double rub test is carried out (this acetone double rub test is similar to the methyl ethyl ketone double rub test, except that acetone is used instead of methyl ethyl ketone). The second coating layer withstands 100 acetone double rubs without visible damage. Example 5B Comparative multi-layer coating system.

[0124] Example 5A was repeated, except that the coating composition containing the mixture of diethyl methylene malonate and the transesterified adduct of diethyl methylene malonate and 1,6-hexanediol was applied directly over a 4" x 12" cold rolled steel substrate panel pre-coated with ED-6670 electrocoat (electrocoat available from PPG Industries, Inc., and substrate panel available in pre-coated form from ACT Test Panels LLC). No intermediate basecoat was applied between the electrocoat layer and the coating layer containing the mixture of diethyl methylene malonate and the transesterified adduct of diethyl methylene malonate and 1,6-hexanediol. The applied coating layer remained in a liquid state 5 days after application.

[0125] Without wishing to be bound by any theory, it is believed that the residual amines (e.g., dimethylethanolamine) in the dehydrated basecoat layer of Example 5A acted as activator compounds to activate the anionic polymerization of diethyl methylene malonate and the transesterified adduct of diethyl methylene malonate and 1,6-hexanediol in the second coating layer. However, in Example 5B, the cured electrocoat layer did not contain sufficient and / or sufficiently mobile amine compounds to activate anionic polymerization in the overlying coating layer. Example 6 A curable composition comprising a 1,1-diactivated vinyl compound and an ionic liquid activator, optionally a polythiol, and optionally an extender.

[0126] A composition was prepared that included a 1,1-diactivated vinyl compound and its multifunctional form (a combination of diethyl methylene malonate and a transesterified adduct of diethyl methylene malonate and 1,6-hexanediol). An ionic liquid was prepared that included an alkyl imidazolinium phthalate. A tetrafunctional polythiol was prepared that included pentaerythritol tetra(3-mercaptopropionate). An extender was prepared that included a vinyl polymer prepared using an ethylenically unsaturated carboxylic acid anhydride. The crosslinker composition (or unreacted diethyl methylene malonate), ionic liquid, polythiol, and extender were combined together in the amounts provided in Table 10 to form a curable composition. [Table 10]

[0127] The components of the curable compositions listed in Table 10 were mixed together in a vial at room temperature. The curable compositions were evaluated for gel time, and select formulations were evaluated for coating film drying and curing properties (time to tack-free), as well as solvent resistance (MEK double rub test). Gel time was measured as the time taken from combining all the components until the composition showed no visually observable flow when the vial containing the composition was inverted.

[0128] Coating films were prepared by applying the curable compositions listed in Table 10 over 10.16 cm x 30.18 cm cold rolled steel substrate panels precoated with ED-6060 electrocoat (electrocoat available from PPG Industries, Inc., and substrate panels available in precoated form from ACT Test Panels LLC). The coatings were applied by drawdown over the electrocoat on the substrate panels immediately after mixing using a drawdown bar with a 2-4 mil gap (50-102 micrometers). Time to tack-free was measured as the amount of time required for the coating to achieve a level of dryness such that application and removal of a cotton ball did not result in transfer of the cotton fibers to the coating surface. MEK double rubs (MEK DR) are recorded as the number of double rubs required to dissolve the coating and thus the substrate visible, up to a maximum of 100 MEK DRs, by performing double rubs by hand with a rag soaked in methyl ethyl ketone. The gel time, time to tack free, and MEK DR results are recorded in Table 11. [Table 11]

[0129] The gel and tack-free times for Samples A and B indicate that the ionic liquid polymerized both the DEMM and crosslinker compositions in the vial and was effective as a coating film applied onto the panel. Note that the fast gel and tack-free times for Samples A and B indicate rapid polymerization of the DEMM or DEMM crosslinker. Sample C was similar to Sample A, except that it further contained an extender that provided longer gel and tack-free times at ambient conditions. Sample C formed a tack-free coating upon brief baking (60° C. for 10 minutes), but did not withstand any MEK DR, which was expected since the reaction product is believed to be a non-crosslinked linear polymer formed from the anionic polymerization of the DEMM monomers. Sample D was similar to Sample B, except that it further contained an extender that provided longer gel and tack-free times at ambient conditions. Sample D, when briefly baked (60° C. for 10 minutes), formed a tack-free coating that withstood 100 MEK DRs and demonstrated the formation of a solvent-resistant crosslinked coating.

[0130] Sample E, which did not contain ionic liquid, exhibited a relatively slow reaction of the crosslinker composition with the polythiol, as indicated by the long gel time and time to tack-free. Sample F, which was similar to Sample E but contained added ionic liquid, exhibited a substantially more rapid reaction, as indicated by a gel time of less than 1 minute. In fact, the reaction of Sample F upon initial mixing was so rapid that it was not possible to apply the composition as a coating film onto a substrate panel before it became too viscous to apply. Sample G was similar to Sample F, except that it also contained an added extender. The gel time was moderate, at 10 minutes, with the addition of the extender, compared to Sample E, which was over 3 hours, and Sample F, which was less than 1 minute, thereby providing a more practical pot life for the composition.

[0131] These examples demonstrate the utility of ionic liquids to activate the cure of 1,1-diactivated vinyl compounds and their multifunctional forms, alone or in combination with multifunctional materials such as polyols, polyamines, polythiols, and / or polycarbamates. The use of extenders to control the reaction rate was also demonstrated, thereby providing control over pot life and cure response, promoting longer gel times that extend the usable application time of the composition, while still maintaining fairly rapid cure kinetics. Aspects of the invention

[0132] Aspects of the invention include, but are not limited to, the following numbered clauses. 1. a first curable composition layer applied over at least a portion of a substrate; and a second curable composition layer applied over at least a portion of the first curable composition layer; A multi-layer curable composition comprising: the first curable composition layer and the second curable composition layer both independently comprise a polymeric resin; the first curable composition layer and / or the second curable composition layer, when cured, comprise a polymerization reaction product of a 1,1-diactivated vinyl compound, or a multifunctional form thereof, or a combination thereof; Multilayer curable compositions. 2. The multilayer curable composition according to claim 1, wherein the 1,1-diactivated vinyl compound comprises a methylenedicarbonyl compound, a dihalovinyl compound, a dihaloalkyl disubstituted vinyl compound, or a cyanoacrylate compound, or any multifunctional form thereof, or any combination thereof. 3. The first curable composition layer and / or the second curable composition layer, when cured, comprises a polymerization reaction product of a dialkyl methylene malonate, a diaryl methylene malonate, a multifunctional form of a dialkyl methylene malonate, or a multifunctional form of a diaryl methylene malonate, or any combination thereof. The multilayer curable composition of claim 1 or 2. 4. The multi-layer curable composition according to claim 3, wherein the first curable composition layer and / or the second curable composition layer, when cured, comprises a polymerization reaction product of diethyl methylene malonate and a multifunctional form of diethyl methylene malonate, wherein the multifunctional form of diethyl methylene malonate comprises a transesterification adduct of diethyl methylene malonate and at least one polyol. 5. The multilayer curable composition according to claim 4, wherein the transesterification adduct of diethyl methylene malonate and at least one polyol comprises a transesterification adduct of diethyl methylene malonate and a diol. 6. The multilayer curable composition according to item 5, wherein the diol comprises 1,5-pentanediol and / or 1,6-hexanediol. 7. (i) the first curable composition layer comprises an activator compound that activates a polymerization reaction in the second coating layer when the second coating layer is applied over the first coating layer; or (ii) the second curable composition layer comprises an activator compound that activates a polymerization reaction in the first coating layer once the second curable composition is applied over the first curable composition layer; Item 7. The multilayer curable composition according to any one of items 1 to 6. 8. The multilayer curable composition according to claim 7, wherein the activator compound comprises a tertiary amine compound. 9. The multilayer curable composition according to paragraph 8, wherein the activator compound comprises 2-(dimethylamino)ethanol and / or 1,4-diazabicyclo[2.2.2]octane. 10. The multilayer curable composition of claim 7, wherein the activator compound comprises an ionic liquid. 11. The multilayer curable composition according to any one of claims 1 to 10, wherein the first curable composition layer comprises a curable composition that cures when heated at a temperature less than 500°C, and the second curable composition layer comprises the polymerization reaction product. 12. The multi-layer curable composition according to any one of the preceding claims, wherein the first coating layer does not contain a melamine resin or a formaldehyde condensate. 13. The first curable composition layer is made of an acrylic resin, a polyester resin, a polyurethane resin, a polyurea resin, a polyether resin, a polythioether resin, or a polycarbonate resin. Item 12. The multilayer coating of any one of items 1 to 11, wherein the second curable composition layer comprises a thermosetting resin comprising a polycarbamate resin, an epoxy resin, a phenolic resin, or an aminoplast resin, or any combination thereof, and the second curable composition layer comprises a clearcoat layer comprising the polymerization reaction product. 14. The multilayer coating of any one of claims 1 to 12, wherein the first curable composition layer comprises the polymerization reaction product, and the first curable composition layer is applied directly onto a metal substrate. 15. The multilayer curable composition of any one of claims 1 to 12, wherein the first curable composition layer comprises the polymerization reaction product, and the first curable composition layer is applied directly onto a non-metallic substrate. 16. The substrate according to any one of the preceding claims, wherein the substrate is polymeric. 17. The substrate according to any one of claims 1 to 16, wherein the non-metallic substrate is an automotive part. 18. The multilayer coating of any one of claims 1 to 13, wherein the substrate comprises an electrodeposited curable composition layer and the first curable composition layer is applied over the electrodeposited coating layer. 19. The multilayer curable composition of any one of the preceding claims, wherein the curable composition layer comprising the polymerization reaction product of the 1,1-diactivated vinyl compound, or a multifunctional form thereof, or a combination thereof, further comprises an extender. 20. The multilayer curable composition of claim 19, wherein the extender comprises an anhydride-containing vinyl polymer. 21. The multilayer curable composition of claim 20, wherein the anhydride-containing vinyl polymer comprises maleic anhydride monomer residues. 22. An article comprising the multi-layer curable composition of any one of paragraphs 1 to 21 deposited over a surface of the article. 23. The article of claim 22, wherein the article comprises a vehicle part or a free-standing structure. 24. A method for a curable composition substrate, comprising: applying a first layer of a curable composition over at least a portion of a substrate; applying a second curable composition layer over at least a portion of the first curable composition layer; and curing the first curable composition layer and / or the second curable composition layer, the first curable composition layer and the second curable composition layer both independently comprise a polymeric resin; the first curable composition layer and / or the second curable composition layer, when cured, comprise a polymerization reaction product of a 1,1-diactivated vinyl compound, or a multifunctional form thereof, or a combination thereof; method. 25. The method of claim 24, wherein the 1,1-diactivated vinyl compound comprises a methylene dicarbonyl compound, a dihalovinyl compound, a dihaloalkyl disubstituted vinyl compound, or a cyanoacrylate compound, or any multifunctional form thereof, or any combination thereof. 26. The method of claim 24 or 25, wherein the step of curing the first curable composition layer and / or the second curable composition layer comprises spraying an activator solution over and / or under at least a portion of the first curable composition layer and / or the second curable composition layer. 27. The method of claim 26, wherein the activator solution comprises a tertiary amine compound. 28. The method of claim 27, wherein the activator solution comprises 1,4-diazabicyclo[2.2.2]octane and / or 2-(dimethylamino)ethanol. 29. (i) The first curable composition layer includes an activator compound, and the step of curing the second curable composition layer includes initiating a polymerization reaction in the second curable composition layer. with the activator compound in the first hardenable composition layer; or (ii) the second curable composition layer comprises an activator compound, and the step of curing the first curable composition layer comprises activating a polymerization reaction in the first curable composition layer with the activator compound in the second curable composition layer; 29. The method according to any one of items 24 to 28. 30. The method of claim 29, wherein the activator compound comprises a tertiary amine compound. 31. The method of claim 30, wherein the activator compound comprises 2-(dimethylamino)ethanol and / or 1,4-diazabicyclo[2.2.2]octane. 32. The method of claim 29, wherein the activator compound comprises an ionic liquid. 33. The method of any one of paragraphs 24 to 32, wherein at least one of the first curable composition layer and / or the second curable composition layer, when cured, comprises a polymerization reaction product of a dialkyl methylene malonate, a diaryl methylene malonate, a multifunctional form of a dialkyl methylene malonate, or a multifunctional form of a diaryl methylene malonate, or a combination thereof. 34. The method of claim 33, wherein the first curable composition layer and / or the second curable composition layer comprises a polymerization reaction product of diethyl methylene malonate and a multifunctional form of diethyl methylene malonate, and the multifunctional form of diethyl methylene malonate comprises a transesterification adduct of diethyl methylene malonate and at least one polyol. 35. The method of claim 34, wherein the transesterification adduct of diethyl methylene malonate and at least one polyol comprises a transesterification adduct of diethyl methylene malonate and a diol. 36. The method of any one of claims 24 to 35, wherein the first curable composition layer comprises a curable composition that hardens when heated at a temperature less than 500°C, and the second curable composition layer comprises the polymerization reaction product. 37. The method of any one of claims 24 to 36, wherein the first curable composition layer does not contain a melamine resin or a formaldehyde condensate. 38. The method of any one of paragraphs 24 to 37, wherein the first curable composition layer, when cured, comprises a thermosetting resin comprising an acrylic resin, a polyester resin, a polyurethane resin, a polyurea resin, a polyether resin, a polythioether resin, a polycarbonate resin, a polycarbamate resin, an epoxy resin, a phenolic resin, or an aminoplast resin, or any combination thereof, and the second curable composition layer, when cured, comprises a clearcoat layer comprising the reaction product. 39. The method of any one of items 24 to 37, wherein the first curable composition layer comprises the polymerization reaction product when cured, and the first curable composition layer is applied directly onto a metal substrate. 40. The method according to any one of items 24 to 38, wherein the substrate comprises an electrodeposition curable composition layer, and the first coating layer is applied over the electrodeposition curable composition layer. 41. The method of any one of claims 24 to 40, wherein the curable composition layer comprising the polymerization reaction product of the 1,1-diactivated vinyl compound, or a multifunctional form thereof, or a combination thereof, further comprises an extender. 42. The method of claim 41, wherein the extender comprises an anhydride-containing vinyl polymer. 43. The method of claim 42, wherein the anhydride-containing vinyl polymer comprises maleic anhydride monomer residues.

[0133] Various features and characteristics are described herein to provide an understanding of the compositions, structure, production, function, and / or operation of the invention, including the disclosed compositions, coatings, and methods. The various features and characteristics of the invention described herein may be used interchangeably, regardless of whether such features and characteristics are expressly described herein in combination. It is understood that the features and characteristics may be combined in any suitable manner. The inventors and applicants expressly contemplate that such combinations of features and characteristics are within the scope of the invention described herein. Thus, the claims may be amended to recite any features and characteristics in any combination that are expressly or inherently described herein or otherwise expressly or inherently supported by the present specification. Furthermore, applicants reserve the right to amend the claims to categorically disclaim features and features that may exist in the prior art, even if they are not expressly described herein. Thus, any such amendments do not add new matter to the specification or claims, and are subject to the requirements of description, sufficiency of description, and additional matter, including those required by 35 U.S.C. 112(a) and 123(2) EPC.

[0134] Any numerical range recited herein describes any subrange of the same numerical precision (i.e., having the same number of specified digits) encompassed within the recited range. For example, a recited range of "1.0 to 10.0" describes any subrange between the recited minimum value of 1.0 and the recited maximum value of 10.0 (and inclusive), such as "2.4 to 7.6," even if the range "2.4 to 7.6" is not expressly recited in the body of the specification. Accordingly, the applicant reserves the right to amend this specification, including the claims, to expressly recite any subrange of the same numerical precision encompassed within the range expressly recited herein. Any such range is essentially described herein, such that any amendment to expressly recite any such subrange complies with the requirements of description, sufficiency of description, and additional matter, including those required by 35 U.S.C. § 112(a) and 123(2) EPC. In addition, unless expressly specified or otherwise required by context, any numerical parameter described herein (e.g., parameters expressing values, ranges, amounts, percentages, etc.) can be read as if preceded by the term "about", even if the term "about" is not expressly recited before a numerical value. Further, the numerical parameters described herein should be interpreted in light of the number of reported significant digits, numerical precision, and by applying ordinary rounding techniques. It is also understood that the numerical parameters described herein necessarily have the inherent variability characteristic of the underlying measurement technique used to determine the numerical value of the parameter.

[0135] The invention(s) described herein can comprise, consist of, or consist essentially of various features and characteristics described herein. The terms "comprise" (and any form of comprise, e.g., "comprises" and "comprising"), "have" (and any form of have, e.g., "has" and "having"), "include" (and any form of include, e.g., "includes" and "including"), and "contain" (and any form of contain, e.g., "contains" and "containing") are open-ended linking verbs. Thus, a composition, coating, or method that "comprises," "has," "includes," or "contains" one or more features and / or characteristics has those one or more features and / or characteristics, but is not limited to having only those one or more features and / or characteristics. Similarly, an element of a composition, coating, or method that "comprises," "has," "includes," or "contains" one or more features and / or characteristics has those one or more features and / or characteristics, but is not limited to having only those one or more features and / or characteristics, and can have additional properties and / or characteristics.

[0136] The grammatical articles "a", "an" and "the" as used herein, including the claims, are intended to include "at least one" or "one or more" unless otherwise specified. Thus, the articles are used herein to refer to one or more than one (i.e., "at least one") of the grammatical object of the article. For example, "a component" means one or more components, and therefore, more than one component is likely to be used or may be used in the practice of the compositions, coatings, and methods contemplated and described. Nevertheless, it is understood that the use of the terms "at least one" or "one or more" in some cases but not others does not give rise to any interpretation that the object of the grammatical articles "a", "an" and "the" is limited to only one by the inability to use those terms. Further, unless otherwise dictated by the context used, the use of a singular noun includes the plural and the use of a plural noun includes the singular.

[0137] Any patent, publication, or other document identified herein is incorporated herein by reference in its entirety unless otherwise specified, but only to the extent that the incorporated material does not contradict existing descriptions, definitions, descriptions, illustrations, or other disclosure material expressly set forth herein. Thus, to the extent necessary, the published disclosure set forth herein supersedes any conflicting material incorporated by reference. Any material or portion thereof that is incorporated herein by reference but contradicts existing definitions, descriptions, or other disclosure material set forth herein is incorporated only to the extent that it does not create a conflict between the incorporated material and the existing disclosure material. Applicant reserves the right to amend this specification to expressly recite any subject matter or portion thereof that is incorporated by reference. Amendments to this specification to add such incorporated subject matter are subject to the requirements of description, sufficiency of description, and additional matter, including those required by 35 U.S.C. § 112(a) and 123(2) EPC.

[0138] According to a preferred embodiment of the present invention, for example, the following is provided: (Section 1) a first curable composition layer applied over at least a portion of a substrate; and a second curable composition layer applied over at least a portion of the first curable composition layer; A multi-layer curable composition comprising: the first curable composition layer and the second curable composition layer both independently comprise a polymeric resin; the first curable composition layer and / or the second curable composition layer, when cured, comprise a polymerization reaction product of a 1,1-diactivated vinyl compound, or a multifunctional form thereof, or a combination thereof; Multilayer curable compositions. (Section 2) The multi-layer curable composition according to claim 1, wherein the 1,1-diactivated vinyl compound comprises a methylenedicarbonyl compound, a dihalovinyl compound, a dihaloalkyl disubstituted vinyl compound, or a cyanoacrylate compound, or any multifunctional form thereof, or any combination thereof. (Section 3) The multi-layer curable composition of claim 1, wherein the first curable composition layer and / or the second curable composition layer, when cured, comprises a polymerization reaction product of a dialkyl methylene malonate, a diaryl methylene malonate, a multifunctional form of a dialkyl methylene malonate, or a multifunctional form of a diaryl methylene malonate, or any combination thereof. (Section 4) The multi-layer curable composition of claim 3, wherein the first curable composition layer and / or the second curable composition layer, when cured, comprises a polymerization reaction product of diethyl methylene malonate and a multifunctional form of diethyl methylene malonate, the multifunctional form of diethyl methylene malonate comprising a transesterification adduct of diethyl methylene malonate and at least one polyol. (Section 5) 5. The multi-layer curable composition according to claim 4, wherein the transesterification adduct of diethyl methylene malonate and at least one polyol comprises a transesterification adduct of diethyl methylene malonate and a diol. (Section 6) 6. The multi-layer curable composition according to claim 5, wherein the diol comprises 1,5-pentanediol and / or 1,6-hexanediol. (Section 7) (i) the first curable composition layer comprises an activator compound that activates a polymerization reaction in the second curable composition layer when the second curable composition layer is applied over the first coating layer; or (ii) the second curable composition layer comprises an activator compound that activates a polymerization reaction in the first curable composition layer once the second curable composition layer is applied over the first curable composition layer; Item 1. The multilayer curable composition according to item 1. (Section 8) 8. The multi-layer curable composition according to claim 7, wherein the activator compound comprises a tertiary amine compound. (Section 9) 9. The multi-layer curable composition according to claim 8, wherein the activator compound comprises 2-(dimethylamino)ethanol and / or 1,4-diazabicyclo[2.2.2]octane. (Section 10) 8. The multi-layer curable composition according to claim 7, wherein the activator compound comprises an ionic liquid. (Section 11) Item 2. The multi-layer curable composition according to item 1, wherein the first curable composition layer comprises a curable composition that cures when heated at a temperature less than 500° C., and the second curable composition layer comprises the polymerization reaction product. (Section 12) Item 12. The multi-layer curable composition according to item 11, wherein the first curable composition layer does not contain a melamine resin or a formaldehyde condensate. (Section 13) Item 2. The multi-layer curable composition according to item 1, wherein the first curable composition layer comprises a thermosetting resin comprising an acrylic resin, a polyester resin, a polyurethane resin, a polyurea resin, a polyether resin, a polythioether resin, a polycarbonate resin, a polycarbamate resin, an epoxy resin, a phenolic resin, or an aminoplast resin, or any combination thereof, and the second curable composition layer comprises a clear coat layer comprising the polymerization reaction product. (Section 14) Item 2. The multi-layer curable composition according to item 1, wherein the first curable composition layer comprises the polymerization reaction product, and the first curable composition layer is applied directly onto a metal substrate. (Section 15) Item 1, wherein the first curable composition layer comprises the polymerization reaction product, and the first curable composition layer is applied directly onto a non-metallic substrate. (Section 16) Item 16. The substrate according to item 15, wherein the substrate is polymeric. (Section 17) Item 16. The substrate according to item 15, wherein the nonmetallic substrate is an automobile part. (Section 18) Item 2. The multi-layer curable composition according to item 1, wherein the substrate comprises an electrodeposition curable composition layer, and the first curable composition layer is applied over the electrodeposition curable composition layer. (Section 19) The multi-layer curable composition according to claim 1, wherein the curable composition layer comprising the polymerization reaction product of the 1,1-diactivated vinyl compound, or a multifunctional form thereof, or a combination thereof, further comprises an extender. (Section 20) 20. The multi-layer curable composition of claim 19, wherein the extender comprises an anhydride-containing vinyl polymer. (Section 21) 21. The multilayer curable composition of claim 20, wherein the anhydride-containing vinyl polymer comprises maleic anhydride monomer residues. (Section 22) 13. An article comprising the multi-layer curable composition of claim 1 deposited over a surface of the article. (Section 23) 23. The article of claim 22, wherein the article comprises a vehicle part or a self-supporting structure. (Section 24) 1. A method for a curable composition substrate, comprising: applying a first layer of a curable composition over at least a portion of a substrate; applying a second curable composition layer over at least a portion of the first curable composition layer; and curing the first curable composition layer and / or the second curable composition layer, the first curable composition layer and the second coating layer both independently comprise a polymeric resin; the first curable composition layer and / or the second curable composition layer, when cured, comprise a polymerization reaction product of a 1,1-diactivated vinyl compound, or a multifunctional form thereof, or a combination thereof; method. (Section 25) 25. The method of claim 24, wherein the 1,1-diactivated vinyl compound comprises a methylene dicarbonyl compound, a dihalovinyl compound, a dihaloalkyl disubstituted vinyl compound, or a cyanoacrylate compound, or any multifunctional form thereof, or any combination thereof. (Section 26) 25. The method of claim 24, wherein the step of curing the first curable composition layer and / or the second curable composition layer comprises applying an activator solution over and / or under at least a portion of the first curable composition layer and / or the second curable composition layer. (Section 27) 27. The method according to claim 26, wherein the activator solution comprises a tertiary amine compound. (Section 28) 28. The method according to claim 27, wherein the activator solution comprises 1,4-diazabicyclo[2.2.2]octane and / or 2-(dimethylamino)ethanol. (Section 29) (i) the first curable composition layer comprises an activator compound, and the step of curing the second curable composition layer comprises activating a polymerization reaction in the second curable composition layer with the activator compound in the first curable composition layer; or (ii) the second curable composition layer comprises an activator compound, and the step of curing the first curable composition layer comprises activating a polymerization reaction in the first curable composition layer with the activator compound in the second coating layer; 25. The method according to item 24 above. (Section 30) 30. The method of claim 29, wherein the activator compound comprises a tertiary amine compound. (Section 31) 31. The method of claim 30, wherein the activator compound comprises 2-(dimethylamino)ethanol and / or 1,4-diazabicyclo[2.2.2]octane. (Section 32) 30. The method of claim 29, wherein the activator compound comprises an ionic liquid. (Section 33) 25. The method of claim 24, wherein at least one of the first curable composition layer and / or the second curable composition layer, when cured, comprises a polymerization reaction product of a dialkyl methylene malonate, a diaryl methylene malonate, a multifunctional form of a dialkyl methylene malonate, or a multifunctional form of a diaryl methylene malonate, or a combination thereof. (Section 34) 34. The method of claim 33, wherein the first curable composition layer and / or the second curable composition layer comprises a polymerization reaction product of diethyl methylene malonate and a multifunctional form of diethyl methylene malonate, the multifunctional form of diethyl methylene malonate comprising a transesterification adduct of diethyl methylene malonate and at least one polyol. (Section 35) 35. The method of claim 34, wherein the transesterification adduct of diethyl methylene malonate and at least one polyol comprises a transesterification adduct of diethyl methylene malonate and a diol. (Section 36) 25. The method according to claim 24, wherein the first curable composition layer comprises a curable composition that cures when heated at a temperature less than 500° C., and the second coating layer comprises the polymerization reaction product. (Section 37) 37. The method according to claim 36, wherein the first curable composition layer does not contain a melamine resin or a formaldehyde condensate. (Section 38) 25. The method of claim 24, wherein the first curable composition layer, when cured, comprises a thermosetting resin comprising an acrylic resin, a polyester resin, a polyurethane resin, a polyurea resin, a polyether resin, a polythioether resin, a polycarbonate resin, a polycarbamate resin, an epoxy resin, a phenolic resin, or an aminoplast resin, or any combination thereof, and the second coating layer, when cured, comprises a clear coat layer comprising the polymerization reaction product. (Section 39) 25. The method of claim 24, wherein the first curable composition layer comprises the polymerization reaction product when cured, and the first curable composition layer is applied directly onto a metal substrate. (Section 40) 25. The method of claim 24, wherein the substrate comprises an electrodepositable curable composition layer, and the first curable composition layer is applied over the electrodepositable curable composition layer. (Section 41) 25. The method of claim 24, wherein the curable composition layer comprising the polymerization reaction product of the 1,1-diactivated vinyl compound, or a multifunctional form thereof, or a combination thereof, further comprises an extender. (Section 42) 42. The method of claim 41, wherein the extender comprises an anhydride-containing vinyl polymer. (Section 43) 43. The method of claim 42, wherein the anhydride-containing vinyl polymer comprises maleic anhydride monomer residues.

Claims

1. 1. A coating composition comprising a polyol, a polyamine, a polythiol, a polycarbamate, or any combination thereof, and, when cured, a polymerization reaction product of a dialkyl methylene malonate, a diaryl methylene malonate, a multifunctional form of a dialkyl methylene malonate, or a multifunctional form of a diaryl methylene malonate, and a Michael addition reaction product of said polyol, polyamine, polythiol, polycarbamate, or any combination thereof with a dialkyl methylene malonate, a diaryl methylene malonate, a multifunctional form of a dialkyl methylene malonate, or a multifunctional form of a diaryl methylene malonate, or a combination thereof.

2. 2. The coating composition of claim 1, wherein the coating composition, when cured, comprises a polymerization reaction product of diethyl methylene malonate and a multifunctional form of diethyl methylene malonate, wherein the multifunctional form of diethyl methylene malonate comprises a transesterification adduct of diethyl methylene malonate and at least one polyol.

3. 3. The coating composition of claim 2, wherein the transesterification adduct of diethyl methylene malonate and at least one polyol comprises a transesterification adduct of diethyl methylene malonate and a diol.

4. The coating composition of claim 3, wherein the diol comprises 1,5-pentanediol and / or 1,6-hexanediol.

5. The coating composition of any one of claims 1 to 4, further comprising an activator compound.

6. The coating composition of claim 5 , wherein the activator compound comprises a tertiary amine compound.

7. The coating composition of claim 6, wherein the activator compound comprises 2-(dimethylamino)ethanol and / or 1,4-diazabicyclo[2.2.2]octane.

8. The coating composition of claim 5 , wherein the activator compound comprises an ionic liquid.

9. The coating composition of any one of claims 1 to 8, wherein the coating composition cures when heated at a temperature less than 500°C.

10. 10. The coating composition of claim 9, wherein the coating composition is free of melamine resins and free of formaldehyde condensates.

11. 11. The coating composition of any one of claims 1 to 10, wherein the coating composition comprises a thermosetting resin comprising an acrylic resin, a polyester resin, a polyurethane resin, a polyurea resin, a polyether resin, a polythioether resin, a polycarbonate resin, a polycarbamate resin, an epoxy resin, a phenolic resin, or an aminoplast resin, or any combination thereof.

12. The coating composition of any one of claims 1 to 11, further comprising an extender.

13. The coating composition of claim 12 , wherein the extender comprises an anhydride-containing vinyl polymer.

14. 14. The coating composition of claim 13, wherein the anhydride-containing vinyl polymer comprises maleic anhydride monomer residues.

15. An article comprising the coating composition of any one of claims 1 to 14 deposited over a surface of the article.

16. The article of claim 15 , wherein the article is a metal substrate.

17. The article of claim 15 , wherein the article is a non-metallic substrate.

18. The article of claim 17 , wherein the non-metallic substrate is polymeric.

19. The article according to any one of claims 15 to 18, wherein the article is an automotive part.

20. 16. The article of any one of claims 15, wherein the article comprises an electrodepositable curable composition layer and the coating composition is applied over the electrodepositable curable composition layer.

21. The article of claim 20 , wherein the article comprises a vehicle part or a free-standing structure.

22. A coating layer produced by curing the coating composition according to any one of claims 1 to 14.

23. 1. A method for applying a curable composition to a substrate, comprising: Applying a curable composition according to any one of claims 1 to 14 over at least a portion of a substrate; and curing the curable composition to form a coating layer. A method comprising: