Energy-efficient pyrometallurgical process for processing lithium-ion batteries
The two-stage smelting process addresses the inefficiencies in recovering Ni and Co from batteries by utilizing the chemical energy of waste batteries, achieving home smelting with low Al and C content, and producing high-purity alloys and clean slags.
Patent Information
- Application Number
- JP2023572897
- Authority / Receiving Office
- JP · JP
- Patent Type
- Patents
- Current Assignee / Owner
- Priority Date
- 2021-05-26
- Filing Date
- 2022-05-24
- Publication Date
- 2025-04-14
- Estimated Expiration
- 2042-05-24
AI Technical Summary
Current processes for recovering Ni and Co from batteries are inefficient in terms of energy conservation and often produce slags with high heavy metal content, making them unsuitable for reuse.
A two-stage smelting process that optimizes energy requirements by utilizing the chemical energy of waste batteries, where the first step involves oxidizing carbon to CO2 to generate heat, and the second step involves reducing slag to produce a clean alloy and depleted slag.
This process allows for home smelting even with low Al and C content in batteries, reduces energy consumption, and produces high-purity alloys and clean slags, thereby addressing the inefficiencies and environmental concerns of existing methods.
Smart Images

Figure 0007661535000001 
Figure 0007661535000002 
Figure 0007661535000003
Abstract
Description
[Technical field]
[0001] The present invention relates to a process for recovering valuable metals such as Ni and Co from batteries and other sources. Ni-Co alloys and slags are produced. [Background technology]
[0002] Electric vehicles have seen unprecedented growth in recent years, driven especially by new legislation in Europe and China designed to gradually reduce the CO2 footprint of vehicles and limit air pollution in cities. This growth is expected to continue for the coming decades. The adoption of electric vehicles depends heavily on the performance of the batteries used to store the electrical energy. To obtain the highest energy density while controlling costs, lithium-ion batteries are used. Many of these batteries contain cathodes based on the transition metals Ni, Mn and Co, and are therefore also known as NMC batteries. With the growth of the electric mobility market, the demand for these metals is expected to increase significantly.
[0003] The demand for Ni and Co may even exceed the world's production capacities. Co is particularly critical since it is currently only produced as a by-product of the Ni and Cu industries. The Ni market is significantly larger than the Co market. Most of the Ni goes into the production of stainless steels, where purity is relatively unimportant. However, there is already a shortage of high-purity Ni and Co metals or compounds. In view of the above, the recovery of Ni and Co from used batteries is an attractive proposition.
[0004] Many smelting processes have been proposed that allow the recovery of metals from waste batteries. Such processes generally produce an alloy and a slag. The alloy, if sufficiently pure, may be suitable for example for the preparation of cathode materials for lithium-ion batteries, thus closing the loop. The slag, if sufficiently depleted of heavy metals, may be suitable for use in the construction industry or for safe disposal.
[0005] However, it is difficult to obtain pure alloys and highly depleted slag while conserving energy.
[0006] In Europe, the Classification, Labelling and Packaging (CLP) law EC No 1272 / 2008 requires labelling of all slags with more than 0.1% of either Ni or Co as potentially hazardous materials, requiring end users of the material to carry out a risk analysis: this prevents or even prohibits the reuse of such slags in most known applications.
[0007] When smelting metallurgical charges containing Co and / or Ni, the slag will typically contain more heavy metals than the above limits. This is illustrated, for example, by Elwert et al. (World of Metallurgy-Erzmetall, GDMB-Medienverlag, Clausthal-Zellerfeld, Vol. 65, no. 3, 163-171, 2012), who discuss three typical slags and their detailed phase compositions.
[0008] By increasing the reduction level, it is possible to further reduce the total Ni and Co content of the slag to less than 0.1%. However, these reduction reactions are endothermic and, more importantly, require reducing agents that are mostly carbon-based. The required reduction level involves the combustion of C to CO rather than CO2. This severely limits the enthalpy available for heating and melting the metallurgical charge, necessitating the use of additional heating means.
[0009] WO2018073145 teaches the addition of Co-containing materials, such as batteries, to a Cu or Ni converter. The charge essentially comprises matte, i.e. metal sulfides. As is typical in converters, smelting heat is generated by the oxidation of S to SO2. The enthalpy of this reaction is used to smelt a limited portion of the batteries with the sulfide charge.
[0010] WO2011035915 describes a high-temperature process for the treatment of waste lithium-ion batteries, producing Co-, Ni-, and Cu-containing alloys and slags. Energy is provided by the oxidation of Al and C in such batteries, which corresponds to an autogenous smelting process. To ensure such an autogenous process, WO2011035915 teaches that the percentage of waste batteries in the total charge must be higher than 153%-3.5(Al+0.6C), where Al and C are the weight % of Al and C in the batteries. The main source of Al in the batteries comes from the packaging material. Autogenous smelting according to its disclosure can only be achieved if batteries are primarily present in the total charge and if they contain high concentrations of Al and / or C.
[0011] Recently, new designs of battery packs with the so-called cell-to-pack technology (CTP) have become prominent on the market. Battery packs using this technology are characterized by a significantly lower Al content. The above formula mathematically requires the addition of more than 100% batteries in the charge. Home smelting is therefore not possible for such Al-poor batteries.
[0012] Other processes are available for smelting this type of battery. For example, in WO2016023778, an electric plasma is used to provide the additional energy required for smelting the battery. Naturally, the additional energy results in higher costs. A further drawback of this process is the higher impurity levels in the alloy. This is also seen in WO2011035915.
[0013] A two-stage smelting process for recovering metals from waste lithium-ion batteries is known from EP 2 677 048. It teaches the formation of an impure alloy in a strong reducing first step, followed by purification in an oxidative second step. The first step is neither energy-efficient nor autogenous. [Prior art documents] [Patent documents]
[0014] [Patent Document 1] International Publication No. 2018 / 073145 [Patent Document 2] International Publication No. 2011 / 035915 [Patent Document 3] International Publication No. 2016 / 023778 [Patent Document 4] European Patent Application Publication No. 2677048 [Non-patent literature]
[0015] [Non-Patent Document 1] Elwert et al., World of Metallurgy-Erzmetall, GDMB-Medienverlag, Clausthal-Zellerfeld, Vol.65, no.3, 163-171, 2012 Summary of the Invention [Problem to be solved by the invention]
[0016] The present invention discloses an alternative two-stage smelting process that optimizes energy requirements. The smelting conditions allow home smelting in the first step even when the Al and C content of waste batteries is low. [Means for solving the problem]
[0017] This result is achieved by better utilizing the chemical energy of the waste batteries. For this reason, the process conditions in the first smelting step are selected to oxidize C to CO2. This is in contrast to known processes, where strong reducing conditions mean that C is oxidized only to CO. In fact, the oxidation to CO2 is much more exothermic and provides the energy necessary to melt the complete charge, even if it contains other components than the waste batteries.
[0018] Due to the oxidative conditions of the first step, some Ni and Co go into the slag. Therefore, a second step of reductive slag cleaning is required. This second step is carried out only on the slag, which is preferably kept in a liquid state and requires only a minimal amount of energy. Therefore, the total energy requirement for the combination of the two steps is more advantageous than a single-step smelting process.
[0019] According to a first embodiment, the recovery of valuable metals from a metallurgical charge comprising a slag former and a lithium-ion battery or a derivative thereof comprising Co, Ni, metallic Al, and C comprises the following steps; - providing a metallurgical smelting furnace equipped with means for injecting an O2-containing gas into the liquid; - defining an oxidation level Ox characterizing the oxidative smelting conditions according to the following equation: Ox = pCO2 / (pCO + pCO2), where 0.1 < Ox < 1, and pCO and pCO2 are the partial pressures of CO and CO2 in contact with the melt; - preparing a metallurgical charge comprising a weight fraction Bf of a lithium-ion battery or a derivative thereof according to the following equation: 1 > Bf > 0.3 / ((1 + 3.5*Ox)*C) + 2.5*Al), where Ox is the oxidation level, and Al and C are the respective weight fractions of metallic Al and C in the battery or a derivative thereof; - oxidatively smelting the metallurgical charge by injecting an O2-containing gas into the melt to reach the defined oxidation level Ox, thereby obtaining a first alloy having most of the Ni and a first slag containing the remaining Ni and Co; - a liquid / liquid separation step of the first alloy from the first slag; and - reductively smelting the first slag using a heat source and a reducing agent to maintain a reduction potential ensuring the reduction of Ni and Co, thereby producing a second alloy and a second slag containing less than 1 wt%, preferably less than 0.5%, more preferably less than 0.1% Ni.
[0020] By "slag former" is meant, for example, one or more of CaO, Al2O3, and SiO2. Other slag formers known to those skilled in the art may also be present. The slag forming compounds may be added as such or may be obtained in situ from easily oxidized metals present in the charge.
[0021] "Lithium ion batteries or derived products" means new batteries or pre-processed battery materials such as waste batteries, used batteries, production scrap, shredded or separated, etc. However, said products may still contain significant amounts of Co, Ni, metallic Al, and C.
[0022] A "major portion" of an element means greater than 50% by weight of the amount of the element present in the metallurgical charge.
[0023] The minimum value of 0.1 for the oxidation level Ox is determined by the need to generate a sufficient amount of CO2 to heat and melt the metallurgical charge, since the generation of CO alone is generally not sufficient. The upper limit of less than 1 corresponds to the avoidance of extreme oxidizing conditions that would prevent a large part of the Ni from going to the alloy in the smelting step. Here we assume that CO and CO2 are in contact with the melt, thereby ensuring control of the redox conditions.
[0024] The step of defining the oxidation Ox level by the battery percentage Bf must result in a condition following the formula above. Based on the battery composition, it must be verified that the calculated value of Bf is physically feasible, i.e. Bf<1. If not, a higher Ox up to a value less than 1 should be defined.
[0025] The above operating conditions have been found to be valid for battery fractions Bf greater than 0.3: below this value, the battery may not be able to provide enough energy to enable home smelting of the entire metallurgical charge.
[0026] Clean slag is important from an economic and environmental perspective. The 1 wt% and 0.5 wt% limits for Ni are based on economic aspects, while 0.1% represents the generally accepted upper limit for reusing slag in other useful applications.
[0027] If the criteria of the formula are met, the order of the step of defining the oxidation level Ox and the step of preparing the metallurgical charge is not important. Thus, starting from a given battery fraction Bf, the minimum oxidation level Ox can be determined. This reverse order is the purpose of the second embodiment.
[0028] According to a second embodiment, the recovery of valuable metals from a metallurgical charge comprising a slag former and a lithium-ion battery or a derivative thereof comprising Co, Ni, metallic Al, and C comprises the following steps: - providing a metallurgical smelting furnace equipped with means for injecting an O2-containing gas into the liquid; - preparing the metallurgical charge using the weight fraction Bf of the lithium-ion battery or a derivative thereof in the metallurgical charge; - defining an oxidation level Ox characterizing the oxidation smelting conditions according to the following formula: Ox = pCO2 / (pCO + pCO2)>(((0.3 / Bf - 2.5*Al) / C) - 1) / 3.5, where 0.1 < Ox < 1, pCO and pCO2 are the partial pressures of CO and CO2 in contact with the melt, and Al and C are the respective weight fractions of metallic Al and C in the battery or a derivative thereof; - oxidizing and smelting the metallurgical charge by injecting an O2-containing gas into the melt to reach the defined oxidation level Ox, thereby obtaining a first alloy having most of the Ni and a first slag containing the remaining Ni and Co; - a liquid / liquid separation step of the first alloy from the first slag; and - reducing and smelting the first slag using a heat source and a reducing agent and maintaining a reduction potential that ensures reduction of Ni and Co, thereby producing a second alloy and a second slag containing less than 1 wt. %, preferably less than 0.5%, more preferably less than 0.1% Ni.
[0029] In this embodiment, the oxidation level Ox is determined after preparing the charge. It is necessary to verify that the calculated value of Ox that allows the desired oxidation and home smelting conditions is compatible with the oxidation level Ox<1.
[0030] It can be shown that the equation for determining Bf starting from Ox and the equation for determining Ox starting from Bf are equivalent.
[0031] Applying the formula of the first or second embodiment results in self-charging, which means that the oxidation smelting step can be carried out using only the energy contained in the battery or its derivatives, without the need to add additional energy as fuel, coke or other carbon sources, or as residual reactive compounds of the metallurgical charge.
[0032] However, in practical operation, small amounts of energy may be provided for various reasons, e.g., to compensate for very high heat losses in certain furnaces. Such small amounts should preferably be limited to less than 50%, more preferably less than 10%, of the total energy requirement of the first smelting step.
[0033] The type of furnace and the exact operating temperature are not critical, but should be such that the metallurgical charge can be completely smelted and the first alloy and first slag obtained. Commonly known furnaces operating at temperatures such as 1350°C to 1800°C are suitable for smelting charges containing lithium-ion batteries or their derivatives. As shown in the examples below, temperatures above 1450°C are preferred to ensure melting of a wide range of charge materials, while temperatures below 1550°C are preferred to limit energy consumption.
[0034] A further embodiment according to any of the foregoing is characterized by the use of only an auto-oxidation smelting step, i.e., the energy contained in the battery or its derivatives.
[0035] Liquid / liquid separation of alloy and slag is very common in the metallurgical industry and is achieved, for example, by so-called "tapping" the liquid phase from a furnace.
[0036] In a further embodiment according to any of the foregoing, the slag is maintained in a liquid state between the steps of liquid / liquid separation and reduction smelting.
[0037] This ensures that the energy expended to heat and melt the charge in the first smelting step is maximized. Once the slag cools and solidifies, additional energy is required to remelt it in the reduction smelting step. This extra energy is often acceptable, especially when the amount of first slag is significantly less than the total amount of metallurgical charge.
[0038] In a further embodiment according to any of the foregoing, the O2-containing gas is enriched air or pure O2.
[0039] This embodiment results in less heat loss than when air is used as the O2 containing gas.
[0040] In a further embodiment according to any of the foregoing, Ox<0.98, preferably Ox<0.95.
[0041] These conditions correspond to somewhat reduced oxidation levels, which may still be adequate to ensure home smelting while improving the direct Ni and Co yields in the first alloy.
[0042] In a further embodiment according to any of the foregoing, the slag formers include, by weight, up to 50% CaO, up to 55% Al2O3, and up to 65% SiO2.
[0043] Using these guidelines, one skilled in the art can readily obtain a slag with a sufficiently low viscosity at operating temperatures to allow decantation and phase separation. The slag formers may be added as is or may be generated in situ by oxidation of metals present in the charge, such as Si or Al.
[0044] In a further embodiment according to any of the foregoing, the process comprises a step of transferring the separated first slag to a second furnace suitable for carrying out a step of reduction smelting, thereby obtaining a second Ni- and Co-containing alloy and a depleted second slag.
[0045] Thus, the smelting step can be carried out either batchwise with intermediate tapping of the Ni-Co alloy or in two different furnaces.
[0046] In a further embodiment according to any of the foregoing, the second furnace is an electric furnace.
[0047] Electric furnaces are well suited when high temperatures and strong reducing conditions are required.
[0048] In a further embodiment according to any of the foregoing, the process includes liquid / liquid separation of the second alloy from the second slag.
[0049] This second alloy is then further processed by hydrometallurgy to separate and purify the metals, which refers to a leaching step, preferably carried out after atomizing the alloy.
[0050] In a further embodiment according to any of the foregoing, the process comprises recycling the separated second alloy, preferably in liquid state, to the oxidative smelting of the metallurgical charge.
[0051] This embodiment provides good overall yields of Ni and Co in the first alloy even if the direct yield to the first alloy is low.
[0052] In a further embodiment according to any of the foregoing, the process comprises the steps of: - spraying a first alloy; and - dissolving the atomized alloy under acidic conditions, thereby obtaining a metal-containing solution suitable for further hydrometallurgical refining.
[0053] The oxidation level of the first step is defined by the parameter Ox, i.e. the ratio of pCO2 to (pCO+pCO2). In practice, this level results in most of the Ni going into the first alloy. The residual Ni goes into the first slag, at a concentration of more than 2% by weight, preferably more than 5%. This residual slagged Ni, together with the slagged Co, is recovered in the second alloy.
[0054] According to the above embodiment, the oxidizing operating conditions of the first step result in the production of a large amount of a relatively pure first alloy of Ni and Co, containing little or no other metals such as Si, Fe, or Mn. These conditions allow for the complete oxidation of at least a portion of the C to CO2 and produce the energy required to melt the charge.
[0055] The reducing operating conditions of the second step ensure complete recovery of Ni and Co in a small amount of the second alloy, which can be further processed or recycled to the first step, ensuring an excellent overall yield of Ni and Co. This second step produces a clean second slag with less than 1 wt.% Ni. No significant energy is required beyond compensation for heat losses, especially if the first slag is kept liquid.
[0056] Too strong reducing conditions in the second step have no significant adverse effects, but may result in alloys containing undesirably high amounts of Si and Mn. Si is associated with filtration problems in the hydrometallurgical processing of the alloy, and may therefore create problems during downstream processing of the alloy. Reduction of Mn requires additional energy in the second step and is therefore undesirable beyond the production of clean slag.
[0057] Based on the observed behavior of Co, Ni and Mn, one skilled in the art could easily control the degree of reduction by adding reducing agents such as coal or natural gas.
[0058] The invention is illustrated in the following examples.
[0059] Example 1 The metallurgical charge according to Table 1 is prepared using 500 kg of batteries, 80 kg of limestone and 20 kg of silica. A cylindrical furnace lined with 200 mm magnesia-chrome bricks and having a diameter of 1 m is used.
[0060] Charge is added continuously to the furnace at a rate of 500 kg battery / h, maintaining a bath temperature of 1450°C without the need for additional coke, natural gas, or electrical energy. Heat is provided at a rate of 77 Nm 3 The fuel is supplied by oxidation of Al and C in the cell using submerged O injection at a rate of 100000 / h. These conditions correspond to a ratio of CO2 to (CO+CO2) of 0.30.
[0061] After one hour, the alloy (1.1) is allowed to cool and the slag (1.1) is tapped from the furnace. This slag weighs 188 kg and is still liquid and fed to a second furnace. An electric furnace is used for this second step.
[0062] [Table 1]
[0063] The electric furnace is operated at a temperature of 1500 °C and 3.5 kg of coke is added to the slag as a reducing agent. A net power of 30 kWh is supplied to the electric furnace to maintain the temperature of the bath.
[0064] After 1 hour of reduction and after decantation, the slag (1.2) and alloy (1.2) are tapped from the furnace and allowed to cool. A detailed material balance is given in Table 2.
[0065] [Table 2]
[0066] Example 2 (Comparison) The metallurgical charge according to Table 3 is prepared using 500 kg of batteries, 80 kg of limestone and 20 kg of silica. A cylindrical furnace lined with 200 mm magnesia-chrome bricks and having a diameter of 1 m is used.
[0067] The charge is added continuously to the furnace at a rate of 500 kg battery / h while maintaining a bath temperature of 1450 °C without the need for additional coke, natural gas, or electrical energy. To reach the desired degree of reduction for high metal yields, 42 Nm 3 / hour O2 is injected. The conditions applied correspond to a CO2 to (CO+CO2) ratio of 0.0, i.e. essentially only CO and no CO2 present. A net power of 220 kWh is required to maintain the desired temperature.
[0068] After 1 hour of reduction and after decantation, the slag (2) and alloy (2) are tapped from the furnace and allowed to cool. The detailed material balance is given in Table 3.
[0069] [Table 3]
[0070] Comparing Example 1 and Example 2 The first alloy (1.1) produced in Example 1 contains fewer impurities than the alloy (2) of Comparative Example 2. This is especially true for C and Mn, whose concentrations in Example 1 are below the detection limit of 0.1% compared to 1.2% C and 6.6% Mn. This is also true for Fe, whose concentration in the first alloy (1.1) is 4% compared to 6.6% in the alloy (2) according to the comparative example. The high purity obtained according to Example 1 makes any hydrometallurgical follow-up processing of the alloy easier and cheaper.
[0071] Furthermore, the electrical energy required over both steps is also different between Example 1 and Example 2. In Example 1, only 30 kWh of energy is required to carry out the reduction process, compared to 220 kWh in Comparative Example 2. The two-step smelting process of Example 1 required only 14% of the electrical energy according to Comparative Example 2.
[0072] It is noted that the use of larger, industrial-scale furnaces would result in even lower specific electrical energy requirements for the reduction step. As the furnace area to volume ratio increases, heat losses decrease, providing even greater benefits.
[0073] Example 3 A metallurgical charge according to Table 4 is prepared using 500 kg of batteries, 80 kg of limestone and 20 kg of silica, as well as 500 kg of slag and 100 kg of alloy, e.g. obtained from other battery recycling operations. A cylindrical furnace lined with 200 mm magnesia-chrome bricks and having a diameter of 1 m is used.
[0074] [Table 4]
[0075] Charge is added continuously to the furnace at a rate of 500 kg battery / h, maintaining a bath temperature of 1450°C without the need for additional coke, natural gas, or electrical energy. Heat is added at 140 Nm 3 / h O2 is used to supply the oxidation of Al and C from the battery. These conditions correspond to a ratio of CO2 to (CO+CO2) of 0.85.
[0076] After one hour, the formed alloy (3.1) is tapped from the furnace and allowed to cool. A total of 922 kg of slag (3.1) is tapped and fed, while still liquid, to a second furnace. An electric furnace is used for this step.
[0077] The electric furnace is operated at a temperature of 1500°C and 45 kg of coke are added to the slag. After 1 hour of reduction and after decantation, the alloy (3.2) and slag (3.2) are tapped from the furnace and allowed to cool. A detailed material balance is given in Table 5. To maintain the bath temperature, a net power of 190 kWh is supplied to the electric furnace.
[0078] [Table 5]
[0079] This example shows that the process allows self-operation even when a significant amount of the charge contains other components besides the battery. However, a higher oxidation degree is required: 0.85 in example 3 compared to 0.30 in example 1. This results in a first alloy (3.1) that is rich in Ni and depleted in Fe. This specification is advantageous. However, the yields of Ni and Co in the first smelting step are lower. This lower yield can be fully compensated by recycling the alloy from the second smelting step to the first smelting step.
[0080] Example 4 Lithium ion batteries having the compositions shown in Table 6 are smelted in accordance with the present invention in a 1 meter diameter cylindrical furnace lined with 200 mm magnesia chrome bricks.
[0081] A metallurgical charge is prepared containing 180 kg of limestone and 150 kg of silica as fluxes and containing 500 kg of lithium ion batteries.
[0082] The mixture is added continuously to the furnace at a rate of 500 kg batteries / h and a bath temperature of 1350 °C is maintained without the need for coke, natural gas, or electrical energy. Energy is provided by oxidation of Al and C from the batteries using submerged O2 injection. 91 Nm 3 / hour O2 is injected. These conditions correspond to a CO2 / (CO+CO2) ratio of 0.45.
[0083] After 1 hour, the phase is tapped from the furnace. The alloy (4.1) is allowed to cool. The slag (4.1), weighing 400 kg, is fed, while still liquid, to a second furnace. An electric furnace is used for this second step.
[0084] [Table 6]
[0085] After the first step, the slag is separated and transferred to an electric furnace where a temperature of 1500°C is applied and 10 kg of coke is added per hour along with 400 kg of slag. After 1 hour of reduction and decantation, the alloy and slag are tapped from the furnace and allowed to cool. The detailed material balance is given in Table 7.
[0086] [Table 7]
[0087] Example 5 The metallurgical charge according to Table 8 is prepared using 500 kg of lithium-ion batteries, 100 kg of limestone and 40 kg of silica. A cylindrical furnace with a diameter of 1 m lined with 200 mm magnesia-chrome bricks is used.
[0088] Charge is added continuously to the furnace at a rate of 500 kg battery / h while maintaining a bath temperature of 1550°C without the need for additional coke, natural gas, or electrical energy. Heat is added at a rate of 77 Nm 3 The fuel is supplied by oxidation of Al and C in the cell using submerged O injection at a rate of 100000 / h. These conditions correspond to a ratio of CO to (CO+CO) of 0.30.
[0089] After one hour, the alloy (5.1) is allowed to cool and the slag (5.1) is tapped from the furnace. This slag weighs 188 kg and, while still liquid, is fed to a second furnace. An electric furnace is used for this second step.
[0090] [Table 8]
[0091] The electric furnace is operated at a temperature of 1500°C and 3.5 kg of coke is added to the slag as a reducing agent.
[0092] After 1 hour of reduction and after decantation, the slag (5.2) and alloy (5.2) are tapped from the furnace and allowed to cool. A detailed material balance is given in Table 9.
[0093] [Table 9]
[0094] Conclusion: Examples 4 and 5 show in-house processes with different temperatures of the first smelting step.
[0095] Battery composition and oxidation level, Ox=pCO2 / (pCO+pCO2) 1>Bf>0,3 / ((1+3.5*Ox)*C)+2.5*Al) Use to compare the spent battery fraction of the feed to the minimum battery fraction (Bf) required for home smelting.
[0096] Example 4 has a cell fraction of 60%, while 59% is required for home smelting. Thus, Example 4 shows the minimum required cell fraction for home smelting for a given cell composition and selected oxidation level. The process is operated at 1350°C, sufficient to keep both the slag and alloy liquid.
[0097] Example 5 has a cell fraction of 78%, whereas home smelting requires 69%. Thus, Example 5 uses a cell fraction higher than the minimum required for home smelting, and the process is operated at 1550°C.
Claims
1. 1. A process for recovering valuable metals from a metallurgical charge containing a slag former and a lithium ion battery or a derived product thereof containing Co, Ni, metallic Al, and C, comprising: - O 2 providing a metallurgical smelting furnace equipped with submerged injection means for contained gas; - Formula: Ox=pCO 2 / (pCO+pCO 2 ) Defining an oxidation level Ox characterizing the oxidation smelting conditions according to Wherein, 0.1<Ox<1, and pCO and pCO 2 is CO and CO in contact with the melt. 2 step; - Formula: 1>Bf>0.3 / ((1+3.5*Ox)*C)+2.5*Al) Preparing the metallurgical charge comprising a weight fraction Bf of a lithium ion battery or a derivative thereof according to where Ox is the oxidation level, and Al and C are the weight fractions of metallic Al and C, respectively, in the lithium ion battery or derivative thereof; - adding O to the melt to reach the defined oxidation level Ox 2 oxidatively smelting said metallurgical charge by injecting a containing gas, thereby obtaining a first alloy having a majority of Ni and a first slag containing the remaining Ni and Co; - liquid / liquid separation of said first alloy from said first slag; and - reducing and smelting said first slag using a heat source and a reducing agent and maintaining a reduction potential that ensures reduction of Ni and Co, thereby producing a second alloy, and a second slag containing less than 1 wt. % Ni. The process includes:
2. 1. A process for recovering valuable metals from a metallurgical charge containing a slag former and a lithium ion battery or a derived product thereof containing Co, Ni, metallic Al, and C, comprising: - O 2 providing a metallurgical smelting furnace equipped with submerged injection means for contained gas; - preparing the metallurgical charge using a weight fraction Bf of lithium ion batteries or derivatives thereof in the metallurgical charge; - Formula: Ox=pCO 2 / (pCO+pCO 2 )>(((0.3 / Bf-2.5*Al) / C)-1) / 3.5, Defining an oxidation level Ox characterizing the oxidation smelting conditions according to Wherein, 0.1<Ox<1, and pCO and pCO 2 is CO and CO in contact with the melt. 2 where Al and C are the respective weight fractions of metallic Al and C in said lithium ion battery or derivative thereof; - adding O to the melt to reach the defined oxidation level Ox 2 oxidatively smelting said metallurgical charge by injecting a containing gas, thereby obtaining a first alloy having a majority of Ni and a first slag containing the remaining Ni and Co; - liquid / liquid separation of said first alloy from said first slag; and - reducing and smelting said first slag using a heat source and a reducing agent and maintaining a reduction potential that ensures reduction of Ni and Co, thereby producing a second alloy, and a second slag containing less than 1 wt. % Ni. The process includes:
3. 3. The process of claim 1 or 2, wherein the oxidative smelting step is autogenous.
4. 3. The process of claim 1 or 2, wherein the first slag is maintained in a liquid state between the liquid / liquid separation step and the step of reduction smelting.
5. The above O 2 The gas contained is enriched air or pure O 2 3. The process according to claim 1 or 2,
6. 3. The process of claim 1 or 2, wherein Ox<0.
98.
7. The slag former is, by weight, up to 50% CaO, up to 55% Al 2 O 3 , and up to 65% SiO 2 3. The process according to claim 1 or 2, comprising:
8. 3. The process according to claim 1 or 2, further comprising a step of transferring the separated first slag to a second furnace suitable for carrying out a step of reduction smelting, thereby obtaining a second Ni- and Co-containing alloy and a depleted second slag.
9. The process of claim 8 wherein the second furnace is an electric furnace.
10. 3. The process of claim 1 or 2, further comprising liquid / liquid separation of the second alloy from the second slag.
11. 11. The process of claim 10, further comprising recycling the separated second alloy to a step of home smelting.
12. 3. The process of claim 1 or 2, further comprising the steps of: - atomizing said first alloy; and - Dissolving the atomized alloy in acidic conditions, thereby obtaining a metal-containing solution suitable for further hydrometallurgical refining.
Citation Information
Patent Citations
Method for recycling positive-negative electrode mixed material of waste ternary lithium-ion battery
CN111129632A
Valuable metal recovery method
EP2677048A1
Process for the valorization of metals from li-ion batteries
WO2011035915A1
Process for smelting lithium-ion batteries
WO2016023778A1
Process for recycling cobalt-bearing materials
WO2018073145A1