Method for making a film comprising nanocellulose and a film comprising nanocellulose

Abstract

The present invention relates to a method for making a film comprising nanocellulose, the method comprising: providing a suspension comprising 50-100% by weight of nanocellulose based on total dry weight; forming a fibrous web of the suspension on a non-porous support; providing a press fabric having a web-side first surface and an opposite second surface, the press fabric including a woven first fabric layer disposed within the press fabric as a layer providing the web-side first surface, such that the press fabric has a woven surface structure on the web-side first surface; applying the web-side surface of the press fabric in direct contact with the web; wet-pressing the web by directing the web disposed between the press fabric and the non-porous support through a press apparatus; and drying the dewatered web to form the film. The present invention further relates to a film made from the method.

Description

[Technical Field]

[0001] The present invention relates to a method for producing a film comprising nanocellulose. Furthermore, the present invention relates to a film comprising nanocellulose that can be obtained by this method. [Background technology]

[0002] Films containing large amounts of nanocellulose, such as microfibrillated cellulose (MFC), are known to have good strength and oxygen barrier properties. This is described, for example, by Syverud, "Strength and barrier properties of MFC films," Cellulose 2009 16:75-85, in which MFC films with basis weights of 15 to 30 gsm were fabricated and their strength and barrier properties were investigated.

[0003] However, during the preparation of nanocellulose films, it is not easy to dehydrate and prepare films at high speed and with high energy efficiency due to the unique properties of nanocellulose. For example, nanocellulose is associated with very good water retention, which provides high dehydration resistance.

[0004] When a nanocellulose film is used, for example, as a barrier, it is critical that the film be free of pinholes or other defects that would adversely affect its barrier properties. It can also be important that the surface of the nanocellulose film is smooth.

[0005] The wet-laid technique can be used to produce nanocellulose films, i.e., to dewater a furnish containing nanocellulose on a wire. However, it is difficult to produce nanocellulose films with good barrier properties and at high production rates by the wet-laid technique, especially when finer grades of nanocellulose are utilized. It is easy to obtain wire marks, which will adversely affect the barrier and optical properties of the film. Furthermore, when using a wire, it is difficult to obtain good retention of the small fibrils present in the furnish.

[0006] It is also possible to produce nanocellulose films using film casting, i.e., casting a film onto a non-porous support, such as a plastic or metal support, followed by slow drying, e.g., by evaporative drying. Casting methods have been shown to produce nanocellulose films with very smooth surfaces and good barrier properties. However, this method is uneconomical, slow, and inefficient for commercial-scale production. This is due, among other things, to the difficulty of efficiently increasing the solids content of the cast film; i.e., rapid removal of water or wastewater is difficult without disrupting film (and network) formation. Most importantly, the low solids content at the time of application (casting) combined with evaporative drying results in high energy consumption.

[0007] Therefore, there is room for improved methods for the preparation of nanocellulose films with good barrier properties, such as oxygen barrier properties. Summary of the Invention

[0008] It is an object of the present invention to provide an improved method for efficiently producing films comprising nanocellulose with good barrier properties, such as oxygen barrier properties, which method eliminates or mitigates at least some of the drawbacks of prior art methods.

[0009] The invention is defined by the accompanying independent claims. Embodiments are set out in the accompanying dependent claims and the following description.

[0010] The present invention provides a method for producing a film comprising nanocellulose, comprising: Providing a suspension comprising 50% to 100% nanocellulose by weight based on total dry weight; forming a fibrous web of the suspension on a non-porous support, the formed fibrous web having a dry content of 1 to 25% by weight; providing a press fabric having a web-side first surface and an opposite second surface, said press fabric including at least a woven first fabric layer, said woven first fabric layer being woven with a plurality of yarns, said woven first fabric layer being disposed within said press fabric as a layer providing said web-side first surface such that said press fabric has a woven surface structure on said web-side first surface; applying the web-side first surface of the press fabric directly to the fibrous web; wet-pressing the fibrous web by directing the fibrous web disposed between the press fabric and the non-porous support through a press apparatus to form a dewatered web; drying the dewatered web to form said film; The present invention relates to a method, including:

[0011] Surprisingly, it has been found that it is possible to dewater a web comprising a large amount of nanocellulose formed on a non-porous support by applying a web-side first surface of a press fabric comprising a woven first fabric layer in contact with the web before leading the web through a press apparatus, the woven first fabric layer being disposed within the press fabric as a layer providing the web-side first surface such that the press fabric has a woven surface structure on the web-side first surface.

[0012] It has therefore surprisingly been found that it is possible to dewater a web comprising a large amount of nanocellulose formed on a non-porous support by applying the woven surface structure of a press fabric in direct contact with the fibrous web before leading the web through a press apparatus.It has therefore surprisingly been found that it is possible to dewater a web comprising a large amount of nanocellulose and to produce a film by a method according to the present disclosure, i.e., it is possible to obtain a continuous film by a method according to the present disclosure.

[0013] More specifically, it has been surprisingly found that the method according to the present disclosure makes it possible to dewater webs containing large amounts of nanocellulose without the fibrous web becoming partially or completely attached to the press fabric, thereby preventing the formation of holes, pinholes, or other damage to the fibrous web. In this way, it is therefore possible to efficiently dewater the fibrous web, which leads to the production of films with good barrier properties and at the same time increases the dewatering rate.

[0014] As mentioned above, the first fabric layer is woven, i.e., is a woven first fabric layer. The woven first fabric layer does not include a batting (i.e., batting material) or other filler material.

[0015] Additionally, as noted above, the woven first fabric layer is disposed on the press fabric as a layer providing the web-side first surface, such that the press fabric has a woven surface structure on the web-side first surface. Accordingly, no core surface layer (or other surface layer) is disposed on the surface of the first fabric layer that constitutes the web-side first surface of the press fabric. However, one or more core surface layers (or other surface layers) may be disposed on the surface of the first fabric layer opposite the web-side first surface.

[0016] In some embodiments, the plurality of yarns of the woven first fabric layer comprises polymeric yarns. Thus, the woven first fabric layer may comprise a woven structure woven with a plurality of polymeric yarns.

[0017] The plurality of yarns may comprise polymer yarns of at least one synthetic polymer selected from the group of synthetic polymers consisting of polyamide, polyurethane, polyester, polyaramid, polyimide, polyolefin, polyetherketone, polypropylene, polyethylene terephthalate (PET), polyether, polybutylene terephthalate (PBT), polyurea, and copolymers thereof.

[0018] In some embodiments, the plurality of polymeric yarns includes at least yarns of a first synthetic polymer selected from the group of synthetic polymers consisting of polyamide, polyurethane, polyester, polyaramid, polyimide, polyolefin, polyetherketone, polypropylene, polyethylene terephthalate (PET), polyether, polybutylene terephthalate (PBT), polyurea, and copolymers thereof. For example, the plurality of polymeric yarns may include polyester yarns or polypropylene yarns.

[0019] In some embodiments, the plurality of polymer yarns includes at least yarns of a first synthetic polymer and yarns of a second synthetic polymer, wherein the first and second synthetic polymers are selected from the group of synthetic polymers consisting of polyamide, polyurethane, polyester, polyaramid, polyimide, polyolefin, polyetherketone, polypropylene, polyethylene terephthalate (PET), polyether, polybutylene terephthalate (PBT), polyurea, and copolymers thereof. For example, the plurality of polymer yarns may include polyester yarns and polypropylene yarns.

[0020] For example, at least 80% of the yarns, preferably at least 90% of the yarns, may be polyester or polypropylene yarns.

[0021] The use of synthetic polymer yarns can further improve the smoothness of the formed film, and can also be beneficial to the durability and / or elasticity of the press fabric. In some embodiments, the weave of the woven first fabric layer is a satin weave, a plain weave, or a twill weave.

[0022] In some embodiments, the plurality of yarns are multifilament yarns. The use of multifilament yarns can improve the smoothness of the surface of the woven first fabric layer that is applied in direct contact with the fibrous web (i.e., the web-side first surface of the press fabric).

[0023] In some embodiments, the woven first fabric layer is woven with yarns having a denier of less than 6000, preferably less than 5000, and most preferably less than 4000, and the woven first fabric layer is woven with yarns having a denier of less than 5 cm -1 More than 10cm, preferably -1 More than 15cm, preferably -1 More than 20cm, most preferably -1 With a weft density exceeding 20cm -1 More than 30cm, preferably -1 More than 40cm, preferably -1 The use of yarns having a denier within a specific range and the use of weft and warp densities within the specific ranges respectively implies that a tightly woven structure of the woven first fabric layer is obtained, i.e., a tightly woven surface structure of the web surface of the press fabric is also obtained.

[0024] Particularly at the beginning of pressing, the nanocellulose-containing fibrous web is in a gel-like state and exhibits shear-thinning behavior. The dense surface structure of the press fabric described above has been found to improve the prevention of materials in the fibrous web from penetrating the pores and openings of the press fabric. This further prevents the fibrous web from partially or completely adhering to the press fabric and causing holes, pinholes, or other damage to the fibrous web. Furthermore, once the fibrous web adheres to the press fabric, it can be partially or completely separated from the support at the point where the press fabric should be separated from the fibrous web. Therefore, the use of a dense surface structure according to the above can further improve the barrier properties of the produced film, while also further improving the efficiency of dewatering the fibrous web.

[0025] In some embodiments, a support device is disposed on the second surface of the press fabric. The support device includes one or more batting layers and / or one or more support fabrics and / or one or more press felts. For example, the support device may be comprised of a press felt. The inclusion of a support device can provide the press fabric device with associated improved strength, elasticity, resilience, compressibility, and water retention capacity.

[0026] In some embodiments, the fibrous web is formed by casting, such as cast coating. Surprisingly, it has been found that the method according to the present disclosure can increase the dehydration of the cast-coated suspension on the support. Therefore, the method according to the present disclosure can rapidly produce a good barrier film by casting.

[0027] In some embodiments, the pressure used in the press is between 0.1 and 150 bar. Preferably, the pressure used in the press is gradually increased during processing in the press. By gradually or stepwise increasing the pressure in the press, dewatering of the web is improved, i.e., a web with a higher dry content can be produced without destroying the barrier properties of the final film.

[0028] The press apparatus is preferably a belt press or extended shoe press design, and the non-porous support is preferably a metal support, such as a metal belt. Alternatively, the non-porous support can be a polymer / plastic support.

[0029] The wet fibrous web is preferably heated before contacting the press fabric. In this manner, the temperature and solids content of the fibrous web are increased, further improving subsequent dewatering of the fibrous web. In some embodiments, the wet fibrous web has a temperature of 10 to 99°C when it enters the wet-pressing section. Increasing the temperature of the wet fibrous web can reduce the viscosity of water, which aids in dewatering. By increasing the solids content of the wet web before the wet-pressing section, the surface of the wet fibrous web that contacts the first web-side surface of the press fabric, or the entire fibrous web, becomes more viscous, reducing or preventing its penetration into the pores of the press fabric.

[0030] In some embodiments, the fibrous web has a dry content of 3 to 25% by weight when it enters the wet pressing step.

[0031] In some embodiments, the fibrous web has a dry content of 15 to 80% by weight after dewatering in the press apparatus.

[0032] In some embodiments, a step of pre-drying the fibrous web is performed before the step of applying the web-side first surface of the press fabric in direct contact with the fibrous web. In some embodiments, the step of pre-drying the fibrous web comprises drying the fibrous web by heating so that the dry content of the fibrous web increases by at least 1% by weight by evaporation before the step of applying the web-side first surface of the press fabric in direct contact with the fibrous web. Thus, in these embodiments, the fibrous web is pre-dried after formation of the fibrous web on the non-porous support but before applying the press fabric. For example, heating may be performed by heating the non-porous support, i.e., a heated non-porous support may be utilized in the pre-drying step.

[0033] In some embodiments, the method further comprises smoothing the dewatered web in a smoothing press.

[0034] The present invention further relates to a film comprising nanocellulose obtainable by the above method.

[0035] In some embodiments, the films obtained by the methods of the present disclosure, when uncoated and having a basis weight of 10 to 60 gsm, have a pinhole density of ≦1 pinhole / m according to EN 13676:2001. 2 It has.

[0036] The film obtained by the method of the present disclosure has a viscosity of 10 cc / m at 23°C and 50% RH (relative humidity) in accordance with ASTM D-3985. 2 / 24h less than 5cc / m 2 / 24h, most preferably less than 3cc / m 2The film obtained by the method of the present disclosure may have an oxygen transmission rate (OTR) value of less than 1 / 24 h. The film obtained by the method of the present disclosure may have a basis weight of 10 to 60 gsm, preferably 15 to 50 gsm, when dry, and a thickness of 10 to 60 μm, preferably 15 to 50 μm, when dry. The film obtained by the method of the present disclosure may have a transparency of greater than 80% according to DIN 53147. As a result, the method of the present disclosure makes it possible to produce thin films containing large amounts of nanocellulose with good oxygen barrier properties, such as oxygen barrier films. DETAILED DESCRIPTION OF THE INVENTION

[0037] 1. A method for making a film comprising nanocellulose, comprising: Providing a suspension comprising 50% to 100% nanocellulose by weight based on total dry weight; forming a fibrous web of the suspension on a non-porous support, the formed fibrous web having a dry content of 1 to 25% by weight; providing a press fabric having a web-side first surface and an opposite second surface, said press fabric including at least a woven first fabric layer, said woven first fabric layer being woven with a plurality of yarns, said woven first fabric layer being disposed within said press fabric as a layer providing said web-side first surface such that said press fabric has a woven surface structure on said web-side first surface; applying the web-side first surface of the press fabric directly to the fibrous web; wet-pressing the fibrous web by directing the fibrous web disposed between the press fabric and the non-porous support through a press apparatus to form a dewatered web; drying the dewatered web to form said film; A method is provided, comprising:

[0038] It has surprisingly been found that it is possible to dewater a web containing a large amount of nanocellulose formed on a non-porous support in an improved manner by applying a press fabric comprising a woven surface structure to a web-side surface in direct contact with the web and subsequently directing the web through a press apparatus. As described above, the press fabric comprises at least a woven first fabric layer, the woven first fabric layer being woven with a plurality of yarns, the woven first fabric layer being disposed on the press fabric as a layer providing a web-side first surface such that the press fabric has the woven surface structure on its web-side first surface. The web-side first surface of the press fabric, i.e., the woven surface structure, is applied in direct contact with the fibrous web, and the fibrous web disposed between the press fabric and the non-porous support is directed through a press apparatus.

[0039] The method according to the invention allows for good and very efficient dewatering of webs and the production of films with good barrier properties from the dewatered fibrous webs. Surprisingly, it has been found that the use of a press fabric with a woven surface structure on the web-side surface followed by treatment in a press device allows for the dewatering of webs containing large amounts of nanocellulose at high production rates (e.g., compared to the use of evaporative drying) without compromising the barrier properties of the web or the produced film.

[0040] Furthermore, it has surprisingly been found that the woven surface structure of the press fabric (and the remainder of the woven first fabric layer) does not adversely affect the dewatering efficiency of the press fabric, i.e., it allows water to pass through so that the nanocellulose web is successfully dewatered during the pressing action.

[0041] It has also surprisingly been found that clogging of the woven surface structure of the press fabric (and the remainder of the woven first fabric layer) by nanocellulose is limited or avoided. Thus, nanocellulose fibrils are at least substantially transferred into the press fabric, allowing dewatering of the fibrous web without clogging the press fabric. Avoiding clogging of the press fabric implies reduced cleaning requirements for the press fabric.

[0042] Dewatering webs containing large amounts of nanocellulose is one of the most challenging process steps for producing films with good barrier properties, i.e., for producing products with a limited number of defects, such as pinholes or other irregularities, that would affect the barrier properties of the product. Therefore, it is important that the dewatering is performed well to avoid poor barrier properties. Therefore, it has been very difficult to increase the production speed of the dewatering step for webs containing large amounts of nanocellulose without reducing the barrier properties.

[0043] As mentioned above, the suspension contains 50% to 100% by weight, preferably 70% to 100% by weight, of nanocellulose based on the total dry weight. Thus, the film made from the dehydrated fiber web contains a large amount of nanocellulose, preferably 70% to 100% by weight, which is related to the amount of nanocellulose in the film itself before the final coating layer is added.

[0044] As described above, the fibrous web is formed on a non-porous support, on which the fibrous web is guided through a press. Preferably, the fibrous web is formed on the support by casting a suspension onto the support, for example, by cast coating. However, alternatively, the fibrous web can be formed on the support by any other conventional coating technique in the art, such as blade, spray, rod, or curtain coating.

[0045] It has surprisingly been found that the method according to the present disclosure makes it possible to increase the dehydration of the suspension cast on the support, and therefore allows for the rapid production of smooth, good barrier films by casting.

[0046] Thus, the methods disclosed herein allow for higher operating speeds on the casting line, reduced casting line dryer lengths, and significant energy savings in drying energy consumption, while still providing good barrier properties (i.e., not degrading) in the produced film.

[0047] It is important to apply the suspension to the support so that a uniform fibrous web is formed, meaning that the fibrous web is as uniform as possible and has as uniform a thickness as possible. The thickness of the applied fibrous web can be, for example, 40 to 6,000 μm, 60 to 3,000 μm, 70 to 2,000 μm, or 100 to 2,000 μm at the time of application. The formed fibrous web has a dry content of 1 to 25 wt. %, preferably 2 to 20 wt. %, and most preferably 3 to 15 wt. % at the time of formation (i.e., during application to the support or immediately after application to the support).

[0048] The support (substrate) on which the fibrous web is formed is a non-porous support. It preferably has a smooth surface and can be a polymer / plastic support or a metal support. Preferably, the support is a metal support, i.e., the support is made of metal. For example, the metal support is a metal belt. The metal support is preferably heated to a temperature above 30°C, preferably between 30 and 150°C, more preferably between 45 and 150°C, and even more preferably between 60 and 100°C, before or immediately after the web is applied to the support. It has been found that by increasing the temperature on the support, and therefore on the applied web, it is possible to further increase the efficiency of dewatering the web in the press device.

[0049] By press fabric is meant a fabric that is permeable and allows water to be removed from the web by absorbing the water or by allowing the water to be removed through the fabric.

[0050] As noted above, the press fabric utilized in the methods of the present disclosure includes a web-facing first surface and an opposing second surface. The web-facing first surface of the press fabric is the surface of the press fabric intended to contact the fibrous web to be dewatered.

[0051] The press fabric further includes at least a woven first fabric layer, i.e., a woven first fabric layer. The woven first fabric layer does not include a batting (i.e., batting material) or other filler material. Thus, the woven structure of the first fabric layer is a woven structure without batting or other filler material. Therefore, the surface structure of the woven first fabric layer that is applied in direct contact with the fibrous web does not include batting or other filler material. The woven first fabric layer is arranged in the press fabric as a layer that provides a web-side first surface so that the press fabric has a woven surface structure on the web-side first surface. Thus, the woven first fabric layer constitutes the layer of the press fabric that provides the web-side surface structure, i.e., it is arranged so that one of its surfaces constitutes the web-side first surface, which is the outer surface of the press fabric that is arranged to contact the fibrous web.

[0052] Thus, the press fabric may be comprised of one layer, i.e., a woven first fabric layer. Thus, in one embodiment, the press fabric is comprised of a woven first fabric layer. In this embodiment, the woven first fabric layer provides both the web-side first surface and the opposite second surface of the press fabric, i.e., the web-side first surface of the press fabric is comprised of one surface of the woven first fabric layer, and the opposite second surface of the press fabric is comprised of the other opposite surface of the woven first fabric layer.

[0053] Alternatively, however, the press fabric may include one or more additional fabric layers and / or one or more batting layers in addition to the first fabric layer. In that case, the layers of the press fabric may be interwoven or arranged in a laminated or composite structure. In that case, the one or more additional fabric layers and / or one or more batting layers are arranged so that the woven first fabric layer is placed as the outermost layer, i.e., to provide the web-side first surface. One or more of the additional fabric layers may have the same properties as the woven first fabric layer. Alternatively, the one or more additional fabric layers may have different properties from the first fabric layer and may be of any suitable press fabric material. One or more of the additional fabric layers may be a woven layer, but alternatively, may have a woven or nonwoven base with a batting of synthetic batting material. If the one or more additional fabric layers are woven, they may have different properties from the woven first fabric layer, for example, a different weave and / or be of a different material.

[0054] The woven first fabric layer is woven with a plurality of yarns, which may include or consist of polymeric yarns. Thus, it may be woven with a plurality of polymeric yarns, i.e., it may comprise or consist of a woven structure woven with a plurality of polymeric yarns.

[0055] Furthermore, the polymer yarns can be yarns of one or more synthetic polymers. Thus, the woven first textile layer can be woven with yarns of one or more synthetic polymers, i.e., the woven first textile layer can include or consist of a woven structure of yarns of one or more synthetic polymers. For example, the woven first textile layer can be woven with yarns of only one type of synthetic polymer. However, alternatively, the woven first textile layer can be woven with yarns of two or more (e.g., three, four, five) different synthetic polymers, i.e., at least yarns of a first synthetic polymer and yarns of a second synthetic polymer.

[0056] The synthetic polymer can be any known suitable synthetic polymer used in paper machine clothing yarns. For example, the synthetic polymer can be selected from the group of synthetic polymers consisting of polyamide, polyurethane, polyester, polyaramid, polyimide, polyolefin, polyetherketone, polypropylene, polyethylene terephthalate (PET), polyether, polybutylene terephthalate (PBT), polyurea, and copolymers thereof. Preferably, the synthetic polymer is polyester or polypropylene. Alternatively, cotton or rayon can be used as the yarn material.

[0057] Thus, the woven first fabric layer may be woven with, for example, polyester or polypropylene yarns. Alternatively, the woven first fabric layer may be woven with, for example, a combination of polyester and polypropylene yarns, a combination of polyester and yarns of one or more other synthetic polymers from the group above, or a combination of polypropylene and yarns of one or more other synthetic polymers from the group above. For example, at least 80% of the yarns, preferably at least 90% of the yarns, are polyester or polypropylene yarns.

[0058] The woven first fabric layer may be woven with longitudinal and weft yarns. The weave of the woven first fabric layer may be of any suitable weave, such as a satin weave, a plain weave, or a twill weave.

[0059] The woven first fabric layer may be woven in an endless fashion, or may be woven flat and joined, or may be made into an endless form using seams or other techniques known in the art for placing fabrics in an endless form.

[0060] Preferably, the plurality of yarns of the woven first fabric layer are multifilament yarns. The filaments of the individual multifilament yarns are preferably of the same material, e.g., the same synthetic polymer, such that each individual yarn contains only one material, e.g., one synthetic polymer. However, alternatively, the filaments of the individual multifilament yarns can be of two or more different materials, e.g., two or more different synthetic polymers. Further alternatively, the yarns of the woven first fabric layer can be monofilament yarns.

[0061] In one embodiment, the weave of the woven first fabric layer is a satin weave, and at least 80% of the yarns, preferably at least 90% of the yarns, are polyester or polypropylene yarns. Thus, in this embodiment, at least 80% of the yarns, or at least 90% of the yarns, or 100% of the yarns can be polyester. Alternatively, at least 80% of the yarns, or at least 90% of the yarns, or 100% of the yarns can be polypropylene. Still alternatively, at least 80% of the yarns, or at least 90% of the yarns, or 100% of the yarns can be either polyester or polypropylene (i.e., there are polyester yarns and polypropylene yarns). In this embodiment, the yarns are preferably multifilament yarns.

[0062] In one embodiment, the weave of the woven first fabric layer is a plain weave, and at least 80% of the yarns, preferably at least 90% of the yarns, are polyester or polypropylene yarns. Thus, in this embodiment, at least 80% of the yarns, or at least 90% of the yarns, or 100% of the yarns can be polyester. Alternatively, at least 80% of the yarns, or at least 90% of the yarns, or 100% of the yarns can be polypropylene. Still alternatively, at least 80% of the yarns, or at least 90% of the yarns, or 100% of the yarns can be either polyester or polypropylene (i.e., there are polyester yarns and polypropylene yarns). In this embodiment, the yarns are preferably multifilament yarns.

[0063] Preferably, the yarn denier, weft density, and warp density of the woven first fabric layer are selected to provide a tightly woven structure. For example, the woven first fabric layer may be woven with yarns having a denier of less than 6000, preferably less than 5000, and more preferably less than 4000. Preferably, the denier is greater than 10, and most preferably greater than 20. The weft density is greater than 5 cm -1 More than 10cm, preferably -1 More than 15cm, preferably -1 More than 20cm, most preferably -1 The warp density may be greater than 20cm -1 More than 30cm, preferably -1 Over, most preferably 40cm -1 The use of yarns having a denier within a specific range and the use of weft and warp densities within a specific range respectively implies that a dense woven structure can be obtained, i.e., a dense surface structure can also be obtained on the web side surface.

[0064] The thickness of the woven first fabric layer can be, for example, 0.05 to 2 mm, or preferably 0.1 to 1 mm.

[0065] For example, the basis weight of the woven first fabric layer is 30 to 1900 g / m 2 or 60 to 1400 g / m 2 It can be said that:

[0066] Additionally, a support device may be disposed on the second surface of the press fabric. The support device may be disposed on the second surface of the press fabric before, after, or as the press fabric is applied to contact the fibrous web. In some embodiments, the support device is attached to the second surface of the press fabric, such as in a laminated or composite structure. The support device may include one or more batting layers and / or a support fabric and / or one or more press felts. The one or more support fabrics may correspond to the press fabrics described above, i.e., the press fabric including the woven first fabric layer, or may have different properties. The support fabric may be comprised of any suitable fabric. If there are two or more support fabrics, they may be the same or different.

[0067] By press felt is meant a felt that is permeable and allows water to be removed from the web by absorbing the water or by allowing the water to be removed through the felt. Any known press felt can be used, for example, a press felt used to dewater paper or paperboard webs. The press felt may have a woven or nonwoven base with a core of batting material, for example, a synthetic batting material.

[0068] In one embodiment, the support device comprises a press felt, i.e., the press felt is disposed on or attached to the second surface of the press fabric. In one embodiment, the support device comprises a support fabric and a press felt, the press felt being preferably disposed as the outermost layer.

[0069] The press fabric is preferably applied to the fibrous web at least 20 cm away, i.e., in direct contact with the fibrous web, before it is guided through the press. The press fabric is preferably applied to the fibrous web at a distance of 20 cm to 5 meters, and even more preferably 50 cm to 3 meters, before it is guided through the press. It is preferable that no external pressure is applied to the press fabric when it is applied to the fibrous web before it is guided through the press. It may be possible to wrap the support, fibrous web, and press fabric around a roll and thus generate a small dewatering pressure, but it is important not to use too much pressure, and pressure from the use of nip rolls cannot be used. Combining the use of a press fabric according to the present disclosure at a certain distance before increasing dewatering in the press can improve web dewatering and further suppress clogging of the press fabric by nanocellulose fibrils migrating into the press fabric. Additionally, it may be possible to increase the pressure used in the press and increase the speed of the dewatering process.

[0070] The term "pressing device" refers to a device that forms a nip through which the fibrous web is guided and thus pressed and dewatered. The pressing device preferably includes an extended nip, and the pressing device is preferably a belt press. The belt press includes a metal belt and a roll, and the dewatering of the web is performed by applying the web and a press fabric between the metal belt and the roll. It may be preferable to increase the length of the nip by treating the fibrous web in the belt press over a distance of at least 20% of the diameter of the belt press roll. It has been found that the nip length for dewatering the fibrous web can be increased without reducing the barrier properties of the film made from the web, and the dewatering rate can also be increased. The pressing device may include two or more nips.

[0071] The pressure used in the pressing device is preferably 0.1 to 150 bar, preferably 0.5 to 100 bar, even more preferably 1 to 60 bar, and even more preferably 1 to 50 bar. It may be preferable to gradually increase the pressure in the pressing device. It is preferable to use a pressure between 0.5 and 10 bar at the start of the pressing device, gradually increasing the pressure to 5 to 20 bar, then optionally further increasing the pressure to 10 to 20 bar, and then optionally increasing the pressure to 20 to 50 bar. The increased pressure may be performed in the same pressure nip, e.g., an extended nip, or the pressing device may include two or more nips.

[0072] The web is preferably guided through the pressing device at a speed of at least 20 m / min for wet pressing, preferably greater than 100 m / min, and even more preferably greater than 200 m / min. It has been found that the present invention allows for increased production speeds for dewatering fibrous webs containing large amounts of nanocellulose, while still providing good barrier properties for the resulting film. Thus, since dewatering is often the most difficult process step for producing nanocellulose films with good barrier properties, the overall film production speed can also be improved, making it possible to produce nanocellulose films with good barrier properties in a much more cost-effective manner.

[0073] One or more press sections having press devices can be utilized. Thus, two or more press fabrics according to the present disclosure can be utilized, such as two press fabrics in different press sections. When two or more press fabrics are utilized, the different press fabrics can be the same or different. For example, a first press fabric can have low water permeability, and a second press fabric can have high water absorption properties.

[0074] The fibrous web is preferably heated before the press fabric is applied to contact it. In this way, the temperature and solids content of the fibrous web are increased, further improving subsequent dewatering of the fibrous web. The increased heat may be applied using any known method. The fibrous web is preferably heated to a temperature of 10 to 99°C, preferably 50 to 95°C.

[0075] The dry content of the fibrous web before entering the wet pressing step is preferably 3 to 25 wt%, more preferably 4 to 20 wt%, and most preferably 5 to 15 wt%. The dry content of the fibrous web after dewatering in the pressing device is preferably 15 to 80 wt%, more preferably 20 to 60 wt%.

[0076] After dewatering in the press, the dewatered web is dried to form a film. Drying the dewatered web may include drying and / or further dewatering in any conventional manner, such as by additional pressing or conventional cylinder drying, by using vacuum, and / or by using hot air, so that the web has a suitable dry content. The film preferably has a dry content of more than 95% by weight. It may also be possible to process the dewatered web in any manner known to those skilled in the art, for example, to make a film by calendering.

[0077] After dewatering in the press device, a smoothing press can be optionally used to remove press fabric markings on the dewatered web and thus improve smoothness. The smoothing press can be a non-felt nip. Smoothing with the smoothing press can be performed before the drying step, i.e., the dewatered web can be smoothed before drying. Alternatively, smoothing with the smoothing press can be performed between drying substeps of the drying step. For example, the drying step can include a first drying substep and a second drying substep, and smoothing can be performed between the first drying substep and the second drying substep.

[0078] The film provided after drying of the dewatered web is 10 cc / m at 23°C and 50% RH in accordance with ASTM D-3985. 2 / 24h less than 5cc / m 2 / 24h, most preferably less than 3cc / m 2 The film may have an oxygen transmission rate (OTR) value of less than 1 / 24h. The basis weight of the dry film provided may be 10 to 60 gsm, preferably 15 to 50 gsm. The thickness of the dry film provided may be 10 to 60 μm, preferably 15 to 50 μm, when dry. The thickness of the film may be selected depending on the required properties. The formed film is preferably a thin, translucent or transparent film with high smoothness and good barrier properties (e.g., gas / oxygen, fragrance, light, etc.).

[0079] The press fabric may be washed and dewatered after being conducted through the press apparatus and separated from the dewatered web.

[0080] A step of pre-drying the fibrous web may be performed before the step of applying the web-side first surface of the press fabric directly to the fibrous web. Thus, a step of pre-drying the fibrous web can be performed after the fibrous web is formed on the support but before applying the press fabric. Depending on the dry content, a pre-drying step may be necessary. For example, if the dry content is 1 to 25 wt. %, or 3 to 15 wt. %, or 3 to 10 wt. %, a pre-drying step may be necessary. For example, pre-drying can be performed by evaporation, hot air impingement drying, IR, microwave, thermal heating, or any other method known in the art.

[0081] For example, the step of pre-drying the fibrous web may include drying the fibrous web by heating so that the dry content of the fibrous web increases by at least 1% by weight by evaporation before applying the web-side first surface of the press fabric in direct contact with the fibrous web. The fibrous web is then pre-dried after formation of the fibrous web on a non-porous support but before applying the press fabric. For example, heating may be performed by heating the non-porous support, i.e., a heated non-porous support may be utilized in the pre-drying step.

[0082] By film is meant herein a thin substrate having good gas, fragrance or grease or oil barrier properties, preferably oxygen barrier properties, such as oxygen barrier properties according to the OTR values ​​mentioned above.

[0083] In addition to nanocellulose, the suspension, and therefore the resulting film, may also contain longer cellulose fibers, hardwood fibers or softwood fibers, preferably kraft pulp softwood fibers. The film may also contain other additives, such as pigments, plasticizers, wetting agents, viscosity modifiers, carboxymethyl cellulose (CMC), retention chemicals, and starch. The film may also contain minerals, such as clay, preferably bentonite. It may be preferable for the film to contain 1 to 50% by weight, more preferably 2 to 30% by weight, of bentonite. It has been found that by increasing the bentonite content of the film, it is possible to increase the dry content of the web. Additives may be included in the suspension used to form the fibrous web, or they may be added to the fibrous web after formation.

[0084] The method of the present disclosure may further include a step of peeling the formed film from the substrate after the drying step, preferably at a dryness of less than 20%, to form a free-standing film. Therefore, the method of the present disclosure may be a method for producing a free-standing nanocellulose film.

[0085] As mentioned above, the support on which the fibrous web is formed can be a metal or plastic support, and the method may then further comprise peeling the formed film from the support to provide a free-standing nanocellulose film.

[0086] The present invention also relates to a film comprising nanocellulose obtained by the above method. The film preferably has a viscosity of 10 cc / m at 23°C and 50% RH according to ASTM D-3985. 2 / 24h less than 5cc / m 2 / 24h, most preferably less than 3cc / m 2 The film preferably has an oxygen transmission rate (OTR) value of less than 1 / 24h. The film preferably has a basis weight of 10 to 60 gsm, more preferably 15 to 50 gsm, when dry. The film preferably has a thickness of 10 to 60 μm, more preferably 15 to 50 μm, when dry. The film thickness can be selected depending on the required properties. The film according to the present invention is preferably a thin, translucent or transparent film with high smoothness and good barrier properties (e.g., gas / oxygen, fragrance, light, etc.). The film may have a transparency of more than 80% according to DIN 53147. Preferably, the film, when uncoated and having a basis weight of 10 to 60 gsm, has a pinhole count of ≦1 pinhole / m according to EN 13676:2001. 2 It has.

[0087] The free-standing films obtained by the method according to the present disclosure may be applied to the surface of any paper or paperboard product.

[0088] Nanocellulose films can also be part of flexible packaging materials, such as self-standing pouches or bags, which can be transparent or translucent. Thus, nanocellulose films according to the present disclosure can be used as bagging materials for boxes when packaging dry foods such as cereals. Furthermore, nanocellulose films according to the present disclosure can be used as packaging substrates, as laminate materials for paper, paperboard, or plastic, and / or as substrates for disposable electronic devices. Nanocellulose films can also be included, for example, in closures, lids, or labels. Nanocellulose films can be incorporated into any type of packaging, such as boxes, bags, packaging films, cups, containers, trays, bottles, etc.

[0089] Nanocellulose comprises partially or fully fibrillated cellulose or lignocellulose fibers. The liberated fibrils have diameters less than 1000 nm, although the actual fibril diameter or particle size distribution and / or aspect ratio (length / width) depend on the source and production method. The smallest fibrils are called elementary fibrils and have a diameter of about 2 to 4 nm (see, for example, Chinga-Carrasco, G., Cellulose fibers, nanofibrils and microfibrils: The morphological sequence of MFC components from plant physiology and fiber technology point of view, Nanoscale research letters 2011, 6:417), but aggregated forms of elementary fibrils, also defined as microfibrils, are generally the main product obtained when making MFCs, for example, by using an extended purification process or a pressure drop cracking process (Fengel, D., Ultrastructural behavior of cell wall polysaccharides, Tappi J., March 1970, Vol. 53, No. 3).

[0090] Nanocellulose has various synonyms, such as cellulose microfibrils, fibrillated cellulose, nanofibrillated cellulose (NFC), fibril aggregates, nanoscale cellulose fibrils, cellulose nanofibers, cellulose nanofibrils, cellulose microfibers, cellulose fibrils, cellulose nanofilaments, microfibril cellulose, microfibrillated cellulose (MFC), microfibril aggregates, and cellulose microfibril aggregates.

[0091] Various methods exist for making nanocellulose, such as single-pass or multi-pass refining, pre-hydrolysis or enzymatic treatment followed by purification or high-shear disintegration or liberation of fibrils.

[0092] To make nanocellulose production energy-efficient and sustainable, one or several pretreatment steps are usually required. Therefore, the cellulose fibers of the pulp used may be pretreated, for example, enzymatically or chemically, to hydrolyze or swell the fibers or reduce the amount of hemicellulose or lignin. Cellulose fibers may also be chemically modified before fibrillation, so that the cellulose molecules contain functional groups other than (or more than) those found in original or native cellulose. Such groups include, among others, carboxymethyl (CM), aldehyde and / or carboxyl groups (cellulose obtained by N-oxyl-mediated oxidation, e.g., "TEMPO"), quaternary ammonium (cationic cellulose), or phosphoryl groups. After modification or oxidation by one of the above methods, it is easier to break down the fibers into nanocellulose or nanofibril-sized fibrils.

[0093] Nanocellulose may contain some hemicellulose, the amount of which depends on the plant source. Mechanical disintegration of the fibers is carried out using appropriate equipment, such as refiners, grinders, homogenizers, colloidal grinders, friction grinders, single- or twin-screw extruders, ultrasonic sonicators, fluidizers such as microfluidizers, macrofluidizers, or fluidizer-type homogenizers. Depending on the nanocellulose production method, the product may also contain fines present in wood fiber or papermaking processes, or nanocrystalline cellulose, or other chemicals. The product may also contain varying amounts of micron-sized fiber particles that are not efficiently fibrillated.

[0094] Nanocellulose can be made from wood cellulose fibers, both from hardwood and softwood fibers. It can also be made from agricultural fibers, such as microbial sources, straw pulp, bamboo, bagasse, or other non-wood fiber sources. It is preferably made from pulp, including pulp from virgin fibers, such as mechanical pulp, chemical pulp, and / or thermomechanical pulp. It can also be made from shredded or recycled paper. The term nanocellulose includes real nanocellulose and BNC (bacterial nanocellulose). Nanocellulose can also be obtained from plant fibers, such as sugar beet or potato-based nanocellulose.

[0095] The above definition of nanocellulose includes, but is not limited to, the definition of nanocellulose in the ISO / TS20477:2017 standard. [Example]

[0096] Four different press fabric systems were provided according to the following: The press felts utilized in some of the press fabric systems were conventional paper machine press felts.

[0097] Press cloth device 1: Polyester multifilament yarn on the web side (breathability 125 l / dm 2 Minutes, warp density 120cm -1 , Weft density: 40cm -1, 5 harness satin weave) 107g / m 2 A press fabric apparatus comprising a single layer of satin fabric (0.18 mm thick) and a conventional paper machine press felt on the backside.

[0098] Press cloth device 2: Polyester multifilament yarn on the web side (calendered, breathable 2L / dm 2 Minutes, thread density 14cm -1 , plain weave) 800g / m 2 A press fabric apparatus containing a single layer of filter fabric (0.85 mm thick).

[0099] Press cloth device 3: Polypropylene multifilament yarn (calendered, breathable 2L / dm 2 Minutes, thread density 14cm -1 , plain weave) 585g / m 2 A press fabric apparatus containing a single layer of filter fabric (0.80 mm thick).

[0100] Press cloth device 4: Polypropylene multifilament yarn on the web side (calendered, breathable 2L / dm 2 Minutes, thread density 14cm -1 , plain weave) 585g / m 2 A press fabric apparatus comprising a single layer of filter fabric (0.80 mm thick) and a conventional paper machine press felt on the backside.

[0101] A suspension containing 87% nanocellulose and 13% sorbitol based on the total dry weight was cast onto a metal support to form a fibrous web. The dry content of the suspension during casting was 3-3.5%. The dry content of the formed fibrous web was increased from 3-3.5% to 5.5-8.5% by hot air impingement drying in the pre-drying step.

[0102] The formed, pre-dried fibrous web was then wet-pressed onto a metal support in different experiments (Experiments 1-6) by applying the web side of each of the press fabric devices described above to contact the web. The web and each press fabric device were pressed in a static laboratory press. As seen in Table 1 below, the experiments utilized different solids contents of the web when each press fabric device was applied to (i.e., brought into contact with) the web and wet-pressing began ("Starting Solids Content"). Additionally, as seen in Table 1 below, the experiments utilized different maximum pressures during the press pulse ("Maximum Pressure (bar)") and different solids contents after wet-pressing (dewatering) in the press device ("Final Solids Content").

[0103] After the wet pressing was completed, additional drying by hot air impingement was applied to form a nanocellulose film.

[0104] The number of pinholes in the web was counted by visual inspection after wet pressing (dewatering) and after final drying. Additionally, the presence of nanocellulose in each press fabric device after dewatering and final drying was determined by visual inspection. TIFF0007731365000001.tif63170

[0105] As can be seen from the results in Table 1, by utilizing a press fabric device with a woven layer on the web side (i.e., a woven surface structure on the web side), it was possible to apply pressure to reduce the amount of water in the cast-coated nanocellulose web and still produce a nanocellulose film with good barrier properties. Furthermore, clogging of the press fabric device was avoided.

[0106] In view of the above detailed description of the invention, other modifications and variations will be apparent to those skilled in the art, and it is evident, however, that such other modifications and variations can be made without departing from the spirit and scope of the invention.

Claims

1. 1. A method for making a film comprising nanocellulose, comprising: providing a suspension comprising 50% to 100% by weight of nanocellulose based on total dry weight; forming a fibrous web of the suspension on a non-porous support, the formed fibrous web having a dry content of 1 to 25% by weight; providing a press fabric having a web-side first surface and an opposite second surface, said press fabric including at least a woven first fabric layer, said woven first fabric layer being woven with a plurality of yarns, said woven first fabric layer being disposed within said press fabric as a layer providing said web-side first surface such that said press fabric has a woven surface structure on said web-side first surface; applying the web-side first surface of the press fabric in direct contact with the fibrous web; wet-pressing the fibrous web by directing the fibrous web disposed between the press fabric and the non-porous support through a press apparatus to form a dewatered web; drying the dewatered web to form said film; Including, the woven first fabric layer is woven with yarn having a denier of less than 6000, and the woven first fabric layer is －１ With a weft density exceeding 20cm －１ and a warp density of greater than 1000 .mu.m.

2. The method of claim 1 , wherein the plurality of threads comprises polymer threads.

3. 3. The method of claim 2, wherein the plurality of yarns comprises polymeric yarns of at least one synthetic polymer selected from the group of synthetic polymers consisting of polyamide, polyurethane, polyester, polyaramid, polyimide, polyolefin, polyetherketone, polypropylene, polyethylene terephthalate (PET), polyether, polybutylene terephthalate (PBT), polyurea, and copolymers thereof.

4. The method of claim 3 , wherein the plurality of polymeric yarns comprises polyester yarns or polypropylene yarns.

5. 4. The method of claim 3, wherein the plurality of polymeric yarns comprises at least yarns of a first synthetic polymer and yarns of a second synthetic polymer, the first and second synthetic polymers being selected from the group of synthetic polymers.

6. The method of claim 5 , wherein the plurality of polymeric yarns comprises polyester yarns and polypropylene yarns.

7. 7. The method of any one of claims 1 to 6, wherein at least 80% of the yarns are polyester yarns or polypropylene yarns.

8. 8. The method of claim 1, wherein the weave of the woven first fabric layer is a satin weave, a plain weave, or a twill weave.

9. 9. The method of claim 1, wherein the plurality of yarns are multifilament yarns.

10. The woven first fabric layer is woven with yarn having a denier of less than 5000, and the woven first fabric layer is woven with yarn having a denier of less than 10 cm －１ With a weft density exceeding 30cm －１ 10. The method according to claim 1, wherein the warp density is greater than 100%.

11. 11. The method of any one of claims 1 to 10, wherein a support device is disposed on the second surface of the press fabric, the support device comprising one or more support fabrics and / or one or more press felts.

12. 12. The method of claim 11, wherein the support device comprises a press felt.

13. 13. The method of any one of claims 1 to 12, wherein the fibrous web is formed by casting.

14. 14. The method according to any one of claims 1 to 13, wherein the pressure used in the pressing device is between 0.1 and 150 bar.

15. 15. The method of any one of claims 1 to 14, wherein the press device is a belt press.

16. 16. The method of any one of claims 1 to 15, wherein the non-porous support is a metal support or a plastic support.

17. The method of claim 16, wherein the metal support is a metal belt.

18. 18. The method according to any one of claims 1 to 17, wherein the fibrous web has a temperature of from 10 to 99°C when it enters the wet-pressing step.

19. 19. The method according to any one of the preceding claims, wherein the fibrous web has a dry content of 3 to 25% by weight when it enters the wet-pressing step.

20. 20. The method according to any one of the preceding claims, wherein the fibrous web has a dry content of 15 to 80% by weight after dewatering in the press device.

21. 21. The method of any one of claims 1 to 20, wherein the step of applying the web-side first surface of the press fabric in direct contact with the fibrous web is preceded by a step of pre-drying the fibrous web.

22. 22. The method of claim 21, wherein the step of pre-drying the fibrous web comprises drying the fibrous web by heating such that the dry content of the fibrous web increases by at least 1% by weight by evaporation prior to the step of applying the web-side first surface of the press fabric in direct contact with the fibrous web.

23. 23. The method of any one of claims 1 to 22, further comprising smoothing the dewatered web in a smoothing press.

24. The film has a pinhole density of ≦1 pinhole / m according to EN 13676:2001 ２ 24. The method of any one of claims 1 to 23, comprising:

25. The film was measured at 23°C and 50% RH in accordance with ASTM D-3985 at a rate of 10 cc / m ２ 25. The method of claim 24, wherein the composition has an oxygen transmission rate (OTR) value of less than 1 / 24h.

26. 26. The method of claim 24 or 25, wherein the film has a basis weight of 10 to 60 gsm when dry.

27. 27. The method of any one of claims 24 to 26, wherein the film has a thickness when dry of from 10 to 60 μm.