Water-soluble film with low coefficient of friction

Abstract

The present disclosure provides a water-soluble film comprising a mixture of water-soluble polyvinyl alcohol, a plasticizer, and starch, wherein (a) the starch comprises hydroxypropylated starch in an amount of about 5 phr to about 30 phr, (b) the starch comprises modified starch having a degree of modification of greater than about 2% in an amount of about 2.5 phr to about 30 phr, (c) the starch is unmodified starch having an amylose content of about 20% to about 80%, or (d) the starch comprises hydroxypropylated starch having an amylose content of about 23% to about 95%, and the polyvinyl alcohol comprises unmodified polyvinyl alcohol or anionically modified polyvinyl alcohol, with the proviso that the anionic modifier is not an acrylate. The present disclosure further provides a sealed article comprising the water-soluble film in the form of a pouch defining an internal pouch volume.

Description

[Technical Field]

[0001] The present disclosure relates generally to water-soluble films and related packets. More specifically, the present disclosure relates to polyvinyl alcohol-based water-soluble films that can demonstrate a low coefficient of friction and therefore a reduced tendency to stick to surfaces such as converters and other water-soluble films. [Background technology]

[0002] Water-soluble polymer films are commonly used as packaging materials to simplify the dispersion, pouring, dissolution, and administration of the delivered material. Consumers can add the pouched composition directly to a mixing container, such as a bucket, sink, or any container suitable for holding water. Advantageously, this eliminates the need for consumers to measure the composition while providing accurate dosing. Pouched compositions can also reduce the mess that would otherwise be associated with dispensing materials from a product container, such as pouring or scooping the material. In short, dissolvable pre-measured polymer film pouches offer convenience for consumers to use in a variety of applications.

[0003] However, water-soluble films prepared from water-soluble polymers can stick to the surfaces on which they are formed (or converted, for example, into pouches) and / or to other water-soluble films. This problem can occur particularly when films are formed into pouches and the pouches are stored together in secondary packaging. Anti-blocking agents have been used to reduce the stickiness of water-soluble films to prevent them from sticking to manufacturing surfaces and to each other during storage. However, including anti-blocking agents, especially at higher loading levels, generally has a detrimental effect on the mechanical properties of the resulting film. In particular, the tensile strength of the water-soluble film is generally reduced, resulting in difficulty in processing the film into single-dose pouches. Alternative solutions include dusting the film with talc, starch, or similar particles, but the dusting process is generally tedious, resulting in wasted powder material and machine downtime.

[0004] Therefore, there is a need in the art for a water-soluble film that can be formed into a water-soluble package and that maintains water solubility with a reduced tendency to stick to other water-soluble films. Summary of the Invention

[0005] One aspect of the present disclosure provides a water-soluble film comprising a mixture of water-soluble polyvinyl alcohol, a plasticizer, and a starch, wherein the polyvinyl alcohol is present in an amount of about 20% to about 95% by weight based on the total weight of the film, and the starch comprises hydroxypropylated starch present in an amount ranging from about 5 phr to about 30 phr.

[0006] A related aspect of the present disclosure provides a sealed article comprising a water-soluble film in the form of a pouch defining an interior pouch volume, wherein the water-soluble film comprises a mixture of water-soluble polyvinyl alcohol, a plasticizer, and a starch, wherein the polyvinyl alcohol is present in an amount of about 20% to about 95% by weight based on the total weight of the film, and the starch comprises hydroxypropylated starch present in an amount ranging from about 5 phr to about 30 phr.

[0007] Another aspect of the present disclosure provides a water-soluble film comprising a mixture of water-soluble polyvinyl alcohol, a plasticizer, and a modified starch, wherein the polyvinyl alcohol is present in an amount of about 20% by weight to about 95% by weight based on the total weight of the film, and the modified starch has a degree of modification greater than about 2% and is present in an amount ranging from about 2.5 phr to about 30 phr.

[0008] A related aspect of the present disclosure provides a sealed article comprising a water-soluble film in the form of a pouch defining an interior pouch volume, wherein the water-soluble film comprises a mixture of water-soluble polyvinyl alcohol, a plasticizer, and a modified starch, wherein the polyvinyl alcohol is present in an amount of about 20% to about 95% by weight based on the total weight of the film, and the modified starch has a degree of modification greater than about 2% and is present in an amount ranging from about 2.5 phr to about 30 phr.

[0009] Another aspect of the present disclosure provides a water-soluble film comprising a mixture of water-soluble polyvinyl alcohol, a plasticizer, and unmodified starch, wherein the polyvinyl alcohol is present in an amount of about 20% to about 95% by weight based on the total weight of the film, and the starch has an amylose content in the range of about 20% to about 80%.

[0010] A related aspect of the present disclosure provides a sealed article comprising a water-soluble film in the form of a pouch defining an interior pouch volume, wherein the water-soluble film comprises a mixture of water-soluble polyvinyl alcohol, a plasticizer, and a non-modified starch, wherein the polyvinyl alcohol is present in an amount of about 20% to about 95% by weight based on the total weight of the film, and the starch has an amylose content in the range of about 20% to about 80%.

[0011] Another aspect of the present disclosure provides a water-soluble film comprising a mixture of water-soluble polyvinyl alcohol, a plasticizer, and a hydroxypropyl-modified starch, wherein the polyvinyl alcohol is present in an amount of about 20% to about 95% by weight based on the total weight of the film, the starch has an amylose content in the range of about 23% to about 95%, and the polyvinyl alcohol comprises unmodified polyvinyl alcohol or an anionically modified polyvinyl alcohol copolymer, with the proviso that the anionic modifier is not an acrylate.

[0012] A related aspect of the present disclosure provides a sealed article comprising a water-soluble film in the form of a pouch defining an interior pouch volume, wherein the water-soluble film comprises a mixture of water-soluble polyvinyl alcohol with a plasticizer and a hydroxypropyl-modified starch, wherein the polyvinyl alcohol is present in an amount of about 20% to about 95% by weight based on the total weight of the film, the starch has an amylose content in the range of about 23% to about 95%, and the polyvinyl alcohol comprises unmodified polyvinyl alcohol or an anionically modified polyvinyl alcohol copolymer, with the proviso that the anionic modifier is not an acrylate.

[0013] Another aspect of the present disclosure provides a sealed article comprising a water-soluble film in the form of a pouch defining an interior pouch volume, wherein the water-soluble film is defined according to any aspect or embodiment described herein.

[0014] It is contemplated that the optional features of the compositions described herein, including but not limited to, components and composition ranges thereof, may be selected from the various aspects, embodiments, and examples provided herein. For example, the embodiments and formulation techniques described in Examples 6-45 may be combined with any of the additional features provided in the description herein.

[0015] Further aspects and advantages will become apparent to those skilled in the art from a consideration of the following detailed description. While the films and pouches of the present disclosure are susceptible to embodiment in a variety of forms, the following description includes specific embodiments, with the understanding that the disclosure is illustrative and is not intended to limit the invention to the specific embodiments described herein. [Brief explanation of the drawings]

[0016] To further facilitate understanding of the present invention, two drawings are attached hereto.

[0017] [Figure 1]Rendering of amylose and amylopectin is shown. [Figure 2] An example of an apparatus for measuring the coefficient of friction of a film test piece is shown below. DETAILED DESCRIPTION OF THE INVENTION

[0018] One aspect of the present disclosure provides a water-soluble film comprising a mixture of water-soluble polyvinyl alcohol, a plasticizer, and a starch, wherein the polyvinyl alcohol is present in an amount of about 20% to about 95% by weight based on the total weight of the film, and the starch comprises hydroxypropylated starch present in an amount ranging from about 5 phr to about 30 phr.

[0019] Films according to this embodiment can be surprisingly designed to provide a combination of: (1) excellent ability to be converted (convertibility) using automated equipment at high starch loadings into pouches characterized by a tensile strength ranging from about 45 MPa to about 60 MPa according to the Tensile Strength Test described below; (2) excellent water solubility characterized by a cold water (10°C) dissolution time of 100 seconds or less according to MSTM-205; and (3) good film-to-film anti-stick properties characterized by a relatively low gloss-to-gloss static coefficient of friction (COF) of about 5 or less, as measured by the Coefficient of Friction Test described below.

[0020] A related aspect of the present disclosure provides a sealed article comprising a water-soluble film in the form of a pouch defining an interior pouch volume, wherein the water-soluble film comprises a mixture of water-soluble polyvinyl alcohol, a plasticizer, and a starch, wherein the polyvinyl alcohol is present in an amount of about 20% to about 95% by weight based on the total weight of the film, and the starch comprises hydroxypropylated starch present in an amount ranging from about 5 phr to about 30 phr.

[0021] In embodiments, the hydroxypropylated starch has an amylose content ranging from about 65% to about 95%. As used herein, and unless otherwise specified, amylose percentage refers to the weight percentage based on the total weight of amylose and amylopectin in a starch having about 12% water by weight, which essentially consists of water, amylose, and amylopectin. For example, a starch having an amylose content of 65% has an amylopectin content of 35%. As shown in Figure 1, amylose comprises a linear, helical polymer of α-D-glucose units linked via α(1→4) glycosidic bonds, while amylopectin comprises a hyperbranched polymer of glucose units linked linearly via (1→4) glycosidic bonds, with branches occurring at α(1→6) bonds, e.g., every 24 to 30 glucose units. Without intending to be bound by theory, it is believed that typical modified starches (e.g., hydroxypropylated, hydroxyethylated, or acetate-modified starches) have modifications (e.g., hydroxypropyl, hydroxyethyl, or acetate groups) randomly or substantially randomly distributed throughout both the amylose and amylopectin chains. In one aspect, modified starches for use herein (e.g., hydroxypropylated or hydroxyethylated starches) will have modifications randomly distributed throughout both the amylose and amylopectin chains. In an alternative aspect, modified starches for use herein (e.g., hydroxypropylated or hydroxyethylated starches) will have modifications non-randomly distributed throughout both the amylose and amylopectin chains.

[0022] In embodiments, the hydroxypropylated starch may have a degree of modification ranging from about 4% to about 8%. As used herein, and unless otherwise specified, the degree of starch modification is in weight percent. Starch modification may also be characterized as a degree of substitution (DS) ranging from 0 to 3, where a DS of 0 means that no OH groups are modified on each glucose ring, and a DS of 3 means that all three OH groups on each glucose ring are modified. In embodiments, the hydroxypropylated starch may have a DS ranging from about 0.05 to about 0.4, or from about 0.1 to about 0.3, or about 0.1, about 0.2, about 0.3, or about 0.4. In embodiments, the starch is present in an amount ranging from about 6 phr to about 16 phr. In embodiments, the starch is present in an amount ranging from about 6 phr to about 10 phr. In embodiments, the starch is present in the water-soluble film in an amount ranging from about 12 phr to about 16 phr. In embodiments, the water-soluble film has a tensile strength of at least 40 MPa as determined by the tensile strength test described herein. In embodiments, the polyvinyl alcohol comprises a polyvinyl alcohol selected from the group consisting of a polyvinyl alcohol homopolymer, a polyvinyl alcohol copolymer having anionic modification, and combinations of the foregoing.

[0023] In embodiments, the water-soluble film has a gloss-to-gloss (GG) static coefficient of friction of about 5 or less, or from about 0.1 to about 5, or from about 0.5 to about 5, as determined by the Coefficient of Friction Test described herein. The glossy side of a water-soluble film refers to the air side of the water-soluble film cast onto a casting surface. The matte side of a water-soluble film refers to the cast side of the water-soluble film cast onto a casting surface. In embodiments, the water-soluble film is characterized by a reduced GG static coefficient of friction compared to an equivalent film formulation that does not contain starch. The lower the GG static coefficient of friction, the less likely the film (or a pouch formed therefrom) will stick to the surface on which it is formed (or converted, e.g., into a pouch) and / or other water-soluble films. As used herein, "gloss-to-gloss static coefficient of friction" refers to the static coefficient of friction between the glossy sides of two water-soluble films having the same formulation. As used herein, "gloss-to-matte static coefficient of friction" refers to the static coefficient of friction between the glossy side and the matte side of two water-soluble films having the same formulation. As used herein, "matte-to-matte static coefficient of friction" refers to the static coefficient of friction between the matte sides of two water-soluble films with the same formulation. The coefficient of friction described herein is the gloss-to-gloss static coefficient of friction. The gloss-to-gloss static coefficient of friction is typically higher than the gloss-to-matte static coefficient of friction and the matte-to-matte coefficient of friction for a given cast water-soluble film. Without intending to be bound by theory, blown films are not cast on a casting surface, and all sides of a blown film can be considered the air side or "glossy" side; therefore, the gloss-to-gloss static coefficient of friction of a cast film is believed to represent the static coefficient of friction of a blown film with the same film composition as the cast film.

[0024] In embodiments, the sealed article includes a composition contained in the internal pouch volume. In embodiments, the composition contained in the internal pouch volume is a detergent composition. In embodiments, the detergent composition includes a surfactant, a bleaching agent, an enzyme, a fragrance, a dye or colorant, a solvent, and combinations thereof.

[0025] Another aspect of the present disclosure provides a water-soluble film comprising a mixture of water-soluble polyvinyl alcohol, a plasticizer, and a modified starch, wherein the polyvinyl alcohol is present in an amount of about 20% by weight to about 95% by weight based on the total weight of the film, and the modified starch has a degree of modification greater than about 2% and is present in an amount ranging from about 2.5 phr to about 30 phr.

[0026] Films according to this embodiment can be surprisingly designed to provide a combination of: (1) excellent ability to be converted (convertibility) using automated equipment at high starch loadings into pouches characterized by a tensile strength ranging from about 45 MPa to about 60 MPa according to the Tensile Strength Test described below; (2) excellent water solubility characterized by a cold water (10°C) dissolution time of 100 seconds or less according to MSTM-205; and (3) good film-to-film anti-stick properties characterized by a gloss-to-gloss static coefficient of friction (COF) of about 5 or less or relatively low, as measured by the Coefficient of Friction Test described below.

[0027] A related aspect of the present disclosure provides a sealed article comprising a water-soluble film in the form of a pouch defining an interior pouch volume, wherein the water-soluble film comprises a mixture of water-soluble polyvinyl alcohol, a plasticizer, and a modified starch, wherein the polyvinyl alcohol is present in an amount of about 20% to about 95% by weight based on the total weight of the film, and the modified starch has a degree of modification greater than about 2% and is present in an amount ranging from about 2.5 phr to about 30 phr.

[0028] In embodiments, the modified starch has a degree of modification of about 4% to about 8%. In embodiments, the modified starch has an amylose content ranging from about 65% to about 95%. In embodiments, the modified starch includes a hydroxyalkyl modification, where the alkyl has a chain length of 3 or more carbons, or 3 to 8 carbons, or 3 to 5 carbons, or 3 carbons. As used herein, "alkyl" refers to linear and branched saturated hydrocarbon groups containing 1 to 30 carbon atoms, e.g., 1 to 20 carbon atoms, or 1 to 10 carbon atoms. Non-limiting examples of alkyl groups include methyl, ethyl, n-propyl, isopropyl, n-butyl, sec-butyl (2-methylpropyl), t-butyl (1,1-dimethylethyl), 3,3-dimethylpentyl, and 2-ethylhexyl. Unless otherwise specified, alkyl groups can be unsubstituted or substituted. As used herein, "hydroxyalkyl" refers to an alkyl group substituted with a hydroxyl group. Non-limiting examples of hydroxyalkyl groups include hydroxymethyl, hydroxyethyl, hydroxypropyl, hydroxybutyl, and the like.

[0029] In embodiments, the polyvinyl alcohol comprises a polyvinyl alcohol selected from the group consisting of polyvinyl alcohol homopolymer, polyvinyl alcohol copolymer with anionic modification, and combinations of the foregoing. In embodiments, the starch is present in an amount ranging from about 6 phr to about 16 phr. In embodiments, the starch is present in an amount ranging from about 6 phr to about 10 phr. In embodiments, the starch is present in an amount ranging from about 12 phr to about 16 phr. In embodiments, the water-soluble film has a tensile strength of at least about 40 MPa and up to about 60 MPa, as determined by the Tensile Strength Test described herein. In embodiments, the water-soluble film has a GG static coefficient of friction of about 5 or less, or from about 0.1 to about 5, or from about 0.5 to about 5, or from about 0.1 to about 3, or from about 0.1 to about 2, as determined by the Coefficient of Friction Test described herein. In embodiments, the water-soluble film is characterized by a reduced GG static coefficient of friction compared to an equivalent film formulation without starch.

[0030] In embodiments, the sealed article includes a composition contained in the internal pouch volume. In embodiments, the composition contained in the internal pouch volume is a detergent composition. In embodiments, the detergent composition includes a surfactant, a bleaching agent, an enzyme, a fragrance, a dye or colorant, a solvent, and combinations thereof.

[0031] Another aspect of the present disclosure provides a water-soluble film comprising a mixture of water-soluble polyvinyl alcohol, a plasticizer, and unmodified starch, wherein the polyvinyl alcohol is present in an amount of about 20% to about 95% by weight based on the total weight of the film, and the starch has an amylose content in the range of about 20% to about 80%.

[0032] Films according to this embodiment can be surprisingly designed to provide a combination of: (1) excellent water solubility, characterized by a cold water (10° C.) dissolution time of 100 seconds or less according to MSTM-205; (2) excellent film-to-film anti-stick properties, characterized by a relatively low gloss-to-gloss static coefficient of friction (COF) of about 1 or less, as measured by the Coefficient of Friction Test described below; and (3) good ability to be converted at high starch loadings using automated equipment (convertibility) into pouches characterized by a tensile strength in the range of about 40 MPa to about 60 MPa according to the Tensile Strength Test described below.

[0033] A related aspect of the present disclosure provides a sealed article comprising a water-soluble film in the form of a pouch defining an interior pouch volume, wherein the water-soluble film comprises a mixture of water-soluble polyvinyl alcohol, a plasticizer, and a non-modified starch, wherein the polyvinyl alcohol is present in an amount of about 20% to about 95% by weight based on the total weight of the film, and the starch has an amylose content in the range of about 20% to about 80%.

[0034] In embodiments, the polyvinyl alcohol is present in the water-soluble film in an amount of about 85% to about 95% by weight, based on the total weight of the film. In embodiments, the unmodified starch is present in an amount ranging from about 2 phr to about 30 phr. In embodiments, the unmodified starch is present in an amount ranging from about 2 phr to about 5 phr. In embodiments, the water-soluble film has a GG static coefficient of friction of about 1 or less. In embodiments, the water-soluble film is characterized by a reduced gloss-to-gloss static coefficient of friction compared to an equivalent film formulation without starch.

[0035] In embodiments, the sealed article includes a composition contained in the internal pouch volume. In embodiments, the composition contained in the internal pouch volume is a detergent composition. In embodiments, the detergent composition includes a surfactant, a bleaching agent, an enzyme, a fragrance, a dye or colorant, a solvent, and combinations thereof.

[0036] Another aspect of the present disclosure provides a water-soluble film comprising a mixture of water-soluble polyvinyl alcohol, a plasticizer, and a hydroxypropyl-modified starch, wherein the polyvinyl alcohol is present in an amount of about 20% to about 95% by weight based on the total weight of the film, the starch has an amylose content in the range of about 23% to about 95%, and the polyvinyl alcohol comprises unmodified polyvinyl alcohol or an anionically modified polyvinyl alcohol copolymer, with the proviso that the anionic modifier is not an acrylate.

[0037] Films according to this embodiment can be surprisingly designed to provide a combination of: (1) excellent ability to be converted (convertibility) at high starch loadings using automated equipment into pouches characterized by a tensile strength in the range of about 45 MPa to about 60 MPa according to the Tensile Strength Test described below; (2) excellent water solubility characterized by a cold water (10°C) dissolution time of 100 seconds or less; and (3) good film-to-film anti-stick properties characterized by a relatively low gloss-to-gloss static coefficient of friction (COF) of about 5 or less, as measured by the Coefficient of Friction Test described below.

[0038] A related aspect of the present disclosure provides a sealed article comprising a water-soluble film in the form of a pouch defining an interior pouch volume, wherein the water-soluble film comprises a mixture of water-soluble polyvinyl alcohol with a plasticizer and a hydroxypropyl-modified starch, wherein the polyvinyl alcohol is present in an amount of about 20% to about 95% by weight based on the total weight of the film, the starch has an amylose content in the range of about 23% to about 95%, and the polyvinyl alcohol comprises unmodified polyvinyl alcohol or an anionically modified polyvinyl alcohol copolymer, with the proviso that the anionic modifier is not an acrylate or an alkyl acrylate.

[0039] In embodiments, the starch is present in an amount ranging from about 5 phr to about 12 phr. In embodiments, the water-soluble film has a GG static coefficient of friction of about 5 or less, or from about 0.1 to about 5, or from about 0.5 to about 5, or from about 0.1 to about 3, or from about 0.1 to about 2. In embodiments, the starch has an amylose content ranging from about 50% to about 95% by weight. In embodiments, the hydroxypropyl-modified starch includes greater than 2% hydroxypropyl-modified starch, e.g., 2.1% to 8% hydroxypropyl-modified starch. In embodiments, the hydroxypropyl-modified starch includes from about 4% to about 8% hydroxypropyl-modified starch. In embodiments, the water-soluble film is characterized by a reduced gloss-to-gloss static coefficient of friction compared to an equivalent film formulation without starch.

[0040] In embodiments, the sealed article includes a composition contained in the internal pouch volume. In embodiments, the composition contained in the internal pouch volume is a detergent composition. In embodiments, the detergent composition includes a surfactant, a bleaching agent, an enzyme, a fragrance, a dye or colorant, a solvent, and combinations thereof.

[0041] To be considered a water-soluble film according to the present disclosure, the film must be about 1.5 mils (about 0.038 mm) thick and dissolve in water at a temperature of 20°C (68°F) in 300 seconds or less according to MonoSol Test Method MSTM-205.

[0042] "Comprising," as used herein, refers to various components, ingredients, or steps that may be used in conjunction in the practice of the present disclosure. Thus, the term "comprising" encompasses the more restrictive terms "consisting essentially of" and "consisting of." The compositions may include, consist essentially of, or consist of any of the required and optional elements disclosed herein. For example, a thermoformable packet may "consist essentially of" a film as described herein due to the use of the film's thermoforming characteristics, while including a non-thermoformable film (e.g., a lid portion) and optional indicia on the film, e.g., by inkjet printing. The inventions illustratively disclosed herein may be suitably practiced in the absence of any element or step not specifically disclosed herein.

[0043] Unless otherwise specified, all percentages, parts, and ratios referred to herein are based on the total dry weight of the film compositions of the present disclosure or the total weight of the packeted compositions, as the case may be, and all measurements are made at about 25° C. Unless otherwise specified, all such weights pertaining to listed ingredients are based on the active level and, therefore, do not include carriers or by-products that may be included in commercially available materials.

[0044] All ranges described herein include all possible subset ranges and any combination of such subset ranges. By default, ranges include the stated endpoints unless otherwise stated. When a range of values ​​is provided, it is understood that each intervening value between the upper and lower limits of that range, and any other stated or intervening value within that stated range, is encompassed within the present disclosure. The upper and lower limits of these smaller ranges may independently be included within the smaller ranges, and are also encompassed within the present disclosure, subject to any specifically excluded limit within the stated range. If a stated range includes one or both of these limits, ranges excluding either or both of these included limits are also considered to be part of the present disclosure.

[0045] For example, for any numerical value described herein as a parameter of a described object or as part of a range associated with the described object, alternatives forming part of the description are expressly contemplated as being functionally equivalent ranges surrounding the particular numerical value (e.g., for a dimension disclosed as "40 mm," another embodiment contemplated is "about 40 mm"). Similarly, values ​​described by "about" expressly include the specific value itself as an alternative embodiment (e.g., for an endpoint described as "about 40," an alternative embodiment contemplated is "40").

[0046] As used herein, the terms packet(s) and pouch(es) should be considered interchangeable. In certain embodiments, the terms packet(s) and pouch(es) are used to refer to a container made using a film and preferably a sealed container that seals a material therein, for example, in the form of a metered-dose delivery system, respectively. Sealed pouches can be made by any suitable method, including processes and features such as heat sealing, solvent bonding, and adhesive sealing (e.g., using a water-soluble adhesive).

[0047] As used herein, and unless otherwise stated, the terms "weight percent (wt.%)" and "weight percent (wt%)" are intended to refer to the composition of a particular element in "dry" (anhydrous) parts by weight of the entire film, including residual moisture in the film (if applicable), or parts by weight of the total composition contained within the pouch (if applicable).

[0048] As used herein, and unless otherwise stated, the term "PHR" ("phr") is intended to refer to parts of a specified component composition per hundred parts of water-soluble polymeric resin (whether PVOH or other polymeric resin, but not including starch) in a water-soluble film.

[0049] The film can be made by any suitable method, including solvent casting. The film can be used to form a container (pouch) by any suitable process, including vertical form-fill-seal (VFFS), rotary drum horizontal form-fill-seal, or thermoforming, and, for example, solvent or heat sealing a film layer around the perimeter of the container. The pouch can be used, for example, to contain materials delivered to bulk water.

[0050] In any embodiment, the water-soluble pouch may contain (enclose) a composition within a defined internal volume of the pouch. The composition may be selected from liquids, solids, or combinations thereof. As used herein, "liquid" includes free-flowing liquids as well as pastes, gels, foams, and mousses. Non-limiting examples of liquids include detergent compositions such as light-duty and heavy-duty liquid detergent compositions, powder detergent compositions, hand-washing and / or dishwashing detergents, hard surface cleaning compositions, fabric softeners, detergent gels commonly used in laundry, bleaches and laundry additives, shaving creams, skin care, hair care compositions (shampoos and conditioners), and body washes. Such detergent compositions may include surfactants, bleaches, enzymes, fragrances, dyes or colorants, solvents, and combinations thereof. Optionally, the detergent composition is selected from the group consisting of laundry detergents, dishwashing detergents, hard surface cleaning compositions, fabric softener compositions, shaving creams, skin care, hair care compositions (shampoos and conditioners), and body washes, and combinations thereof.

[0051] Further non-limiting examples of liquids include agricultural compositions, automotive compositions, aviation compositions, food and nutritional compositions, industrial compositions, livestock compositions, marine compositions, medical compositions, commercial compositions, military and paramilitary compositions, office compositions, and non-household care compositions, including recreational and park compositions, pet compositions, water treatment compositions (including cleaning and detergent compositions applicable to any such use). In an embodiment, the composition contained in the inner pouch volume is a detergent composition.

[0052] Gas, e.g., suspended bubbles, or solids, e.g., particles, can be contained within the liquid. As used herein, "solids" includes, but is not limited to, powders, agglomerates, and mixtures thereof. Non-limiting examples of solids include granules, microcapsules, beads, noodles, and pearls. Solid compositions may provide technical benefits, including, but not limited to, cleaning benefits, pre-treatment benefits, and / or aesthetic effects, such as fragrance-containing microcapsules or enzyme-containing microcapsules.

[0053] The films, pouches, and related methods of making and using are considered to include embodiments that further include any combination of one or more of the additional optional elements, features, and steps described below (including those shown in the examples), unless otherwise noted.

[0054] Water-soluble film The water-soluble films described herein comprise a polyvinyl alcohol (PVOH) resin, a modified polyvinyl alcohol resin, or a combination thereof. In embodiments, the PVOH comprises a PVOH resin selected from the group consisting of a PVOH homopolymer, a PVOH copolymer with anionic modification, and combinations of the foregoing. The films can have any suitable thickness, with a film thickness of about 76 microns (μm) being typical and specifically contemplated. Other values ​​and ranges contemplated include a range of about 5 to about 200 μm, or about 20 to about 100 μm, or about 40 to about 90 μm, or about 50 to about 80 μm, or about or about 60 to about 65 μm, e.g., values ​​of 65 μm, 76 μm, and 88 μm.

[0055] PVOH resin The films described herein include one or more PVOH polymers to make up the PVOH resin content of the film, and may include PVOH copolymers.

[0056] Polyvinyl alcohol is a synthetic resin commonly prepared by alcoholysis of polyvinyl acetate, a process commonly referred to as hydrolysis or saponification. Fully hydrolyzed PVOH, in which substantially all acetate groups have been converted to alcohol groups, is a strongly hydrogen-bonded, highly crystalline polymer that is soluble only in hot water above about 140°F (about 60°C). If a sufficient number of acetate groups remain after hydrolysis of polyvinyl acetate, i.e., the PVOH polymer is partially hydrolyzed, the polymer is less hydrogen-bonded and less crystalline, and is generally soluble in cold water below about 50°F (about 10°C). Thus, the partially hydrolyzed polymer is a vinyl alcohol-vinyl acetate copolymer, commonly referred to as PVOH, even though it is a PVOH copolymer.

[0057] As used herein, the term "homopolymer" generally includes polymers having a single type of monomer repeat unit (e.g., a polymer chain consisting of, or essentially consisting of, a single monomer repeat unit). In the specific case of PVOH, the term "homopolymer" (or "PVOH homopolymer" or "PVOH polymer") further includes copolymers having a distribution of vinyl alcohol and vinyl acetate monomer units depending on the degree of hydrolysis (e.g., a polymer chain consisting of, or essentially consisting of, vinyl alcohol and vinyl acetate monomer units). In the limiting case of 100% hydrolysis, PVOH homopolymer can include true homopolymers having only vinyl alcohol units.

[0058] The viscosity (μ) of PVOH polymers is determined by measuring freshly made solutions using a Brookfield LV viscometer with a UL adapter, as described in British Standard EN ISO 15023-2:2006 Annex E Brookfield test method. It is international practice to state the viscosity of a 4% aqueous polyvinyl alcohol solution at 20°C. All viscosities specified in centipoise (cP) herein should be understood to refer to the viscosity of a 4% aqueous polyvinyl alcohol solution at 20°C, unless otherwise specified. Similarly, when a resin is described as having (or not having) a particular viscosity, it is intended that the specified viscosity is the average viscosity of a resin essentially having the corresponding molecular weight distribution, unless otherwise specified.

[0059] When the PVOH resin is a PVOH polymer blend, the resin has a weighted logarithmic average viscosity

number

number

number

[0060] For reference, the water-soluble film has a 4% solution viscosity at 20°C.

number

number

number

number

[0061] The PVOH resin may have a degree of hydrolysis (DH or DH) of at least 80%, 84%, or 85%, and up to about 99.7%, 98%, 96%, or 80%, e.g., in the range of about 84% to about 90%, or 85% to 88%, or 86.5%, or 85% to 99.7%, about 88% to 98%, or 90% to 96%, e.g., 90%, 91%, 92%, 93%, 94%, 95%, or 96%, or in the range of 87 to 93. As used herein, degree of hydrolysis is expressed as the mole percentage of vinyl acetate units converted to vinyl alcohol units.

[0062] Further, when the PVOH resin is a PVOH resin blend, the weighted arithmetic mean degree of hydrolysis is from about 80% to about 99.7%, from about 85% to about 98%, or from about 87 to about 93%, or from about 96 to 98%, e.g., about 85%, or about 86%, or about 87%, or about 87.5%, or about 88%, or about 88.5%, or about 89%, or about 89.5%, or about 90%, or about 91%, or about 92%, or about 93%, or about 94%, or about 95%, or about 96%, or about 96.5%, or about 97%, or about 97.5%, or about 98%.

number

number

number

[0063] The water-soluble film may include a PVOH copolymer, which may be a PVOH terpolymer containing vinyl alcohol monomer units, vinyl acetate monomer units (i.e., when not fully hydrolyzed), and a single type of anionic monomer unit (e.g., when the single type of monomer unit may include the equivalent acid form, salt form, and optionally ester form of the anionic monomer unit). In some embodiments, the PVOH copolymer may include two or more types of anionic monomer units. General classes of anionic monomer units that may be used in PVOH copolymers include vinyl polymerized units corresponding to monocarboxylic acid vinyl monomers, esters and anhydrides thereof, dicarboxylic acid monomers having a polymerizable double bond, esters and anhydrides thereof, and alkali metal salts of any of the foregoing. Examples of suitable anionic monomer units include vinyl polymerized units corresponding to vinyl anionic monomers, including vinyl acetic acid, maleic acid, monoalkyl maleates, dialkyl maleates, maleic anhydride, fumaric acid, monoalkyl fumarates, dialkyl fumarates, fumaric anhydride, itaconic acid, monoalkyl itaconates, dialkyl itaconates, itaconic anhydride, citraconic acid, monoalkyl citraconic acid, dialkyl citraconic acid, citraconic anhydride, mesaconic acid, monoalkyl mesaconic acid, dialkyl mesaconic acid, mesaconic anhydride, glutaconic acid, monoalkyl glutaconates, dialkyl glutaconates, glutaconic anhydride, alkyl acrylates, alkyl alkacrylates, vinyl sulfonic acids, alkali metal salts of the foregoing, esters of the foregoing, and combinations of the foregoing. In embodiments, the anionic monomer units are not acrylates or alkyl alkacrylates.

[0064] In embodiments, the anionic monomer units are vinyl acetate, alkyl acrylate, maleic acid, monoalkyl maleate, dialkyl maleate, monomethyl maleate, dimethyl maleate, maleic anhydride, fumaric acid, monoalkyl fumarate, dialkyl fumarate, monomethyl fumarate, dimethyl fumarate, fumaric anhydride, itaconic acid, monomethyl itaconate, dimethyl itaconate, itaconic anhydride, citraconic acid, monoalkyl citraconic acid, dialkyl citraconic acid, citraconic anhydride, mesaconic acid, monoalcohol mesaconic acid alkyl, dialkyl mesaconic acid, mesaconic anhydride, glutaconic acid, monoalkyl glutaconic acid, dialkyl glutaconic acid, glutaconic anhydride, vinyl sulfonic acid, alkyl sulfonate, ethylene sulfonic acid, 2-acrylamido-1-methylpropanesulfonic acid, 2-acrylamido-2-methylpropanesulfonic acid, 2-methylacrylamido-2-methylpropanesulfonic acid, 2-sulfoethyl acrylate, alkali metal salts of the foregoing, esters of the foregoing, and combinations of the foregoing. In embodiments, the anionic monomer units are vinyl acetic acid, maleic acid, monoalkyl maleates, dialkyl maleates, monomethyl maleate, dimethyl maleate, maleic anhydride, fumaric acid, monoalkyl fumarate, dialkyl fumarate, monomethyl fumarate, dimethyl fumarate, fumaric anhydride, itaconic acid, monomethyl itaconate, dimethyl itaconate, itaconic anhydride, citraconic acid, monoalkyl citraconic acid, dialkyl citraconic acid, citraconic anhydride, mesaconic acid, monomesaconic acid The alkyl acrylate or alkyl acrylate copolymer is selected from the group consisting of alkyl acrylate, alkyl acrylate, alkyl acrylate copolymer ...In embodiments, the anionic monomer unit is selected from the group consisting of maleic acid, monoalkyl maleates, dialkyl maleates, monomethyl maleate, dimethyl maleate, maleic anhydride, fumaric acid, monoalkyl fumarate, dialkyl fumarate, monomethyl fumarate, dimethyl fumarate, fumaric anhydride, itaconic acid, monomethyl itaconate, dimethyl itaconate, itaconic anhydride, citraconic acid, monoalkyl citraconic acid, dialkyl citraconic acid, citraconic anhydride, mesaconic acid, monoalkyl mesaconic acid, dialkyl mesaconic acid, mesaconic anhydride, glutaconic acid, monoalkyl glutaconic acid, dialkyl glutaconic acid, glutaconic anhydride, alkali metal salts of the foregoing, esters of the foregoing, and combinations of the foregoing. In embodiments, the anionic monomer unit is not an acrylate or an alkyl alkacrylate.

[0065] In one class of embodiments, the PVOH is a carboxyl-modified copolymer. In another aspect, the PVOH can be modified with a dicarboxyl-type monomer. In one class of these embodiments, the α-carbons of both carbonyls are bonded to unsaturated bonds (e.g., maleic acid, fumaric acid). In another class of these embodiments, the α-carbons of both carbonyls are bonded to unsaturated bonds, which are further substituted, for example, with methyl branches (e.g., citraconic acid, mesaconic acid). In another class of these embodiments, the β-carbon of one carbonyl and the α-carbon of the other carbonyl are connected to unsaturated bonds (e.g., itaconic acid, cis-glutaconic acid, trans-glutaconic acid). Monomers that provide alkyl carboxyl groups are contemplated. Maleic-type (e.g., including maleic acid, dialkyl maleate (including dimethyl maleate), monoalkyl maleate (monomethyl maleate), or maleic anhydride) comonomers are particularly contemplated.

[0066] In embodiments, the anionic monomer unit comprises a monomer derived from maleic acid. The maleic acid-derived monomer can be one or more of maleic acid, monoalkyl maleates, dialkyl maleates, monomethyl maleate, dimethyl maleate, maleic anhydride, alkali metal salts of the foregoing (e.g., sodium, potassium, or other alkali metal salts), esters of the foregoing (e.g., methyl, ethyl, or other C1-C4 or C6 alkyl esters), and combinations thereof (e.g., multiple types of anionic monomers or equivalent forms of the same anionic monomer). For example, the maleic acid-derived monomer can include one or more monoalkyl maleates, dialkyl maleates, and alkali metal salts thereof (e.g., sodium salts). Similarly, the anionic monomer can include one or more monomethyl maleate, dimethyl maleate, and alkali metal salts thereof (e.g., sodium salts).

[0067] The solvent used for saponifying polyvinyl acetate to polyvinyl alcohol is typically methanol, which may remain in the resulting PVOH powder even after drying. Dissolving PVOH releases methanol into the atmosphere. Therefore, it is desirable to reduce the residual methanol content in PVOH powder to less than 3 wt. %, or even less than 1 wt. Methods for removing volatile organic compounds include supplying a water-containing gas during the drying step to replace the volatile organic compounds in the PVOH polymer with water. However, PVOH modified with monoesters, diesters, or anhydrides of ethylenically unsaturated dicarboxylic acids has a high affinity for water, and the use of water-gas results in dissolution of the powder particle surface and particle agglomeration, making PVOH difficult to process. Alternatively, prolonged heating at high temperatures has been used to remove residual methanol. However, such high temperatures promote crosslinking between the PVOH hydroxyl moieties and the monoester, diester, and / or anhydride units, resulting in insoluble components.

[0068] To reduce the amount of residual methanol in the PVOH copolymer, the saponified copolymer is washed in a methanol / methyl acetate mixture having a methyl acetate content of about 45% by volume or more, 60% by volume or more, or 70% by volume or more. For example, the PVOH gel obtained after the saponification step can be triturated with methanol / methyl acetate in a ratio of 15 / 85 (v / v).

[0069] Additionally, to reduce the amount of methanol, the particle size of the final PVOH resin can be reduced so that more than 95% by weight passes through a 1.0 mm sieve, or more than 30% passes through a 500 micron sieve, or more than 45% passes through a 500 micron sieve. If the particle size of the final PVOH resin is too large, it becomes difficult to volatilize the methanol.

[0070] For PVOH copolymers containing monoesters, diesters, or anhydrides of ethylenically unsaturated dicarboxylic acids, the amount of insoluble components can be reduced by controlling the ratio of lactone ring formation to copolymer modification through partial saponification. The ratio of lactone ring formation to copolymer modification can be represented by formula (Q): 0.05≦Y / X<0.98(Q) wherein X is the copolymer modification and Y is the lactone ring formation. To reduce the amount of insoluble material, Y / X is about 0.80 or less, about 0.60 or less, or about 0.40 or less.

[0071] When the PVOH resin comprises a PVOH copolymer containing an anionic monomer, the incorporation level of one or more anionic monomer units in the PVOH copolymer is not particularly limited. In embodiments, the one or more anionic monomer units are present in the PVOH copolymer in an amount ranging from about 1 mol % to 10 mol %, or from 1.5 mol % to about 8 mol %, or from about 2 mol % to about 6 mol %, or from about 3 mol % to about 5 mol %, or from about 1 mol % to about 4 mol % (e.g., at least 1.0, 1.5, 2.0, 2.5, 3.0, 3.5, or 4.0 mol %, and / or up to about 3.0, 4.0, 4.5, 5.0, 6.0, 8.0, or 10 mol %) in various embodiments.

[0072] The water-soluble film may contain at least about 20%, 30%, 40%, 55%, 50%, 60%, 65%, 70%, 75%, 80%, 85%, or 90% by weight of a PVOH resin or resin blend, and / or up to about 60%, 70%, 80%, 90%, 95%, or 99% by weight of the PVOH resin or resin blend, based on the total weight of the film. In embodiments, the PVOH resin or resin blend is present in the film in an amount of about 20% to about 95% by weight, based on the total weight of the film. In embodiments, the PVOH resin or resin blend is present in the film in an amount of about 60% to about 95% by weight, based on the total weight of the film. In embodiments, the PVOH resin or resin blend is present in the film in an amount of about 85% to about 95% by weight, based on the total weight of the film.

[0073] In an embodiment, the PVOH resin comprises a blend of PVOH polymers. In an embodiment, the PVOH resin blend comprises an anionically modified PVOH polymer. In a refinement of the foregoing embodiment, the PVOH resin blend further comprises a second PVOH polymer selected from a second anionically modified PVOH polymer or a PVOH homopolymer. In an embodiment in which the PVOH resin blend comprises two anionically modified PVOH polymers, the two anionically modified PVOH polymers can have the same anionically modified or different anionically modified. For example, the two anionically modified PVOH polymers can each be a maleic acid modified polymer. Furthermore, the two anionically modified PVOH polymers can be, for example, a maleic acid modified polymer and an acetate modified polymer. In an embodiment in which the two anionically modified PVOH polymers have the same anionically modified, at least one property selected from viscosity, degree of hydrolysis, and / or degree of anionically modified can differ between the two anionically modified PVOH polymers.

[0074] starch The water-soluble films described herein comprise starch and / or modified starch, non-limiting examples of modified starches include ethylated starch, hydroxyethylated starch, propylated starch, hydroxypropylated starch, and acetate-modified starch.

[0075] The starch may be provided in an amount of at least about 2 phr, 2.5 phr, 5 phr, 6 phr, 7 phr, 10 phr, 12 phr, 15 phr, 20 phr, or 22 phr and / or up to about 5 phr, 10 phr, 12 phr, 16 phr, 20 phr, 22 phr, 24 phr, 26 phr, or 30 phr, based on the total amount of PVOH resin. For example, the starch can be provided in an amount ranging from about 2.5 phr to about 30 phr, or from about 5 phr to about 30 phr, or from about 5 phr to about 30 phr, or from about 5 phr to about 15 phr, or from about 6 phr to about 10 phr, or from about 12 phr to about 16 phr, or from about 2 phr to about 5 phr, or from about 5 phr to about 12 phr, or about 2 phr, about 2.5 phr, about 3 phr, about 7 phr, about 8 phr, about 9 phr, about 13 phr, about 14 phr, about 16 phr, about 20 phr, about 22 phr, about 24 phr, about 25 phr, or about 26 phr.

[0076] The starch can have an amylose content of at least about 20%, about 23%, about 25%, about 30%, about 40%, about 50%, about 60%, about 65%, or about 75% and / or up to about 60%, about 70%, about 80%, about 85%, or about 95%, e.g., in the range of about 65% to about 95%, or about 75% to about 85%, or about 20% to about 80%, or about 25% to about 70%, or about 30% to about 70%, or about 40% to about 60%, or about 23% to about 95%.

[0077] Sources of starch having an amylose content of about 20% to about 80% include acorns, apples, arrowroot, barley, ester lilies, elm trees, white wood, iris tubers, corn, amylomaize, oats, peas, potatoes, sago, and wheat.Sources of starch having an amylose content of about 23% to about 95% include acorns, apples, ester lilies, iris tubers, corn, amylomaize, oats, peas, sago, and wheat.

[0078] Determination of amylose content can be achieved by iodine complex formation, as discussed in Amylose and Amylopectin Content of Starches Determined by their Iodine Complex Formation, F.L. Bates, D. French, and R.E. Rundle, J. Am. Chem. Soc., 1943, 65(2), pp. 142-148.

[0079] High amylose starches containing less than 45% amylopectin are more suitably measured using a modified potentiometric iodine method as outlined in U.S. Patent No. 5,300,145, incorporated herein by reference, at column 8, line 14 to column 9, line 68. High amylose starches having amylose contents greater than 55%, greater than 70%, and greater than 89% are embodiments encompassed herein.

[0080] The amylopectin present in the starches suitable herein may include a high molecular weight fraction, a medium molecular weight fraction, and a low molecular weight fraction. The molecular weight fractions may be determined by gel permeation chromatography, as discussed in Shi, Y., Capitani, T., Trzasko, P., and Jeffoat, R., Journal of Cereal Science 27 (1998) 289-299. High amylose starches having an amylopectin content including all three weight fractions are embodiments included herein. For example, high amylose starches may include a high molecular weight fraction of amylopectin of 2 to 32% (e.g., 31.1%), a medium molecular weight fraction of linear and branched (a mixture of amylopectin and amylose) of 59 to 71% (e.g., 59.5%), and a low molecular weight fraction (amylose) of 9 to 27% (e.g., 9.4%).

[0081] The average particle size of the starch in its solid state should not exceed 6 microns. For example, the starch can be provided in a range of about 1 to about 6 microns, about 1 to about 5.5 microns, about 1.5 to about 5 microns, about 2 to about 5 microns, about 2 to about 4 microns, about 3 to about 5 microns, or about 3 to about 4 microns, e.g., about 1, 2, 3, 4, 5, or 6 microns. While not intending to be bound by theory, it is believed that increasing the average particle size of the starch beyond 6 microns adversely affects the physical properties of the resulting film, such as tensile strength and elongation. It is common knowledge in the art that, in the presence of water and heat, starch increases in size to a certain extent by swelling (e.g., about 6 to about 8 microns) and then degrades over time. Therefore, as used herein, the "average particle size" of starch refers to the dry particles of the starch raw material. Methods for determining the average particle size of dry starch are known in the art.

[0082] When starch in water is heated to a temperature below its gelatinization temperature, the starch will swell. When starch in water is heated to a temperature above its gelatinization temperature, the starch will decompose and form a gel. The gelatinization temperature of a given starch depends on various properties of the starch, including, but not limited to, the type of plant from which the starch is derived, the degree of cross-linking in the starch, the degree of starch modification, and the level of amylose content. In embodiments, the starch has a gelatinization temperature higher than the temperature at which the water-soluble film ingredients are mixed in water. In embodiments, the gelatinization temperature of the starch in water is greater than about 75°C, greater than about 80°C, greater than about 85°C, greater than about 90°C, or greater than about 95°C, and up to about 300°C, up to about 250°C, 200°C, or 150°C, for example, from about 80°C to about 200°C, or from about 85°C to about 150°C. The presence of other chemicals in the aqueous solution can affect the gelatinization properties of the starch.

[0083] The starch may have a degree of modification of at least about 2%, about 4%, about 5%, or about 6% and / or up to about 4%, about 6%, about 7%, or about 8%, e.g., greater than about 2%, or in the range of about 2% to about 8%, about 4% to about 8%, or about 5% to about 7%.

[0084] In embodiments, two or more starches may be used together to form a starch blend. The starch blend may include a combination of two unmodified starches, two modified starches, or an unmodified and a modified starch. For example, two or more unmodified starches may be blended together to achieve an average amylose content of about 20% to about 95%, or about 40% to about 60%. Surprisingly, it has been found that when a mixture of starches is used, each starch in the blend independently affects the properties of the final film in the same way as if each starch were used alone. Thus, each starch in the blend may independently have a degree of modification, gelatinization temperature, particle size, and / or amylose content, as described herein.

[0085] In embodiments, the starch comprises hydroxypropylated starch and is present in the water-soluble film in an amount ranging from about 5 phr to about 30 phr, optionally from about 6 phr to about 10 phr, or from about 12 phr to about 16 phr. Optionally, the hydroxypropylated starch has an amylose content ranging from about 65% to about 95%, or from about 75% to about 85%. Optionally, the hydroxypropylated starch has a degree of modification of from about 4% to about 8%, or from about 5% to about 7%. In embodiments, a water-soluble film comprising hydroxypropylated starch and having a thickness of about 76 microns has a cold water solubility of less than about 90 seconds as measured by MSTM-205.

[0086] Without intending to be bound by theory, one skilled in the art would expect the mechanical properties (e.g., tensile strength and tear strength) of a film to decrease as the amount of starch present in the film increases. As demonstrated below, when unmodified starch is present in a water-soluble film at a PVOH resin to starch ratio of about 80:20 or greater (i.e., about 25 phr starch) (e.g., 70:30), the tensile strength and tear strength of the film are dramatically reduced relative to those of an equivalent water-soluble film containing starch at a PVOH resin to starch ratio of less than 80:20, e.g., 97:3.

[0087] Advantageously, it has been surprisingly discovered that the mechanical properties of films containing hydroxypropylated starch are maintained (i.e., do not significantly decrease) as the amount of hydroxypropylated starch present in the film increases over a range of about 2.5 phr to about 30 phr. In embodiments, water-soluble films contain hydroxypropylated starch present in an amount ranging from about 5 phr to about 30 phr, and the films have tensile strengths of at least about 40 MPa, or at least about 45 MPa to about 60 MPa. Without intending to be bound by theory, it is believed that when the modified starch is a hydroxyalkyl-modified starch in which the alkyl contains 3 or more carbon atoms, e.g., 3 to 8 carbon atoms, the hydroxyalkyl chains disrupt the helical structure of amylose, allowing the amylose to more closely associate with the polyvinyl alcohol chains, providing the resulting film with increased mechanical strength relative to films containing unmodified starch.

[0088] Without intending to be bound by theory, it is believed that for water-soluble films containing starch, the GG static coefficient of friction decreases as the amount of starch in the film increases. In embodiments, the water-soluble film contains from about 5 phr to about 30 phr of hydroxypropylated starch, and the film has a GG static coefficient of friction of about 5 or less, about 3 or less, about 2 or less, or about 1 or less. In embodiments, the water-soluble film contains from about 5 phr to about 30 phr of hydroxypropylated starch, and the film is characterized by a reduced gloss-to-gloss static coefficient of friction compared to an equivalent film formulation without starch.

[0089] In embodiments, the starch comprises a modified starch having a degree of modification greater than about 2%, wherein the modified starch is present in an amount ranging from about 2.5 phr to about 30 phr, optionally from about 6 phr to about 16 phr, or from about 6 phr to about 10 phr, or from about 12 phr to about 16 phr. Optionally, the degree of modification is from about 4% to about 8%, or from about 5% to about 7%. Optionally, the modified starch has an amylose content ranging from about 65% to about 95%, or from about 75% to about 85%. Optionally, the modified starch comprises a hydroxyalkyl modification, wherein the alkyl has a chain length of 3 or more carbon atoms. In embodiments, a water-soluble film having a thickness of about 76 microns and comprising a modified starch having a degree of modification greater than about 2% has a cold water solubility of less than about 90 seconds as measured by MSTM-205.

[0090] Without intending to be bound by theory, it is believed that when the modified starch has a degree of modification greater than about 2%, the mechanical properties of films containing the modified starch are maintained (i.e., do not significantly decrease) as the amount of starch contained in the film increases over a range of about 2.5 phr to about 30 phr. In embodiments, a water-soluble film contains modified starch with a degree of modification greater than 2%, present in an amount ranging from about 2.5 phr to about 30 phr, and the film has a tensile strength of at least about 40 MPa, or at least about 45 MPa to about 60 MPa. Without intending to be bound by theory, it is believed that when the modified starch has a degree of modification greater than about 2%, for example, 4% to 8%, the modification disrupts the helical structure of amylose, allowing amylose to more closely associate with polyvinyl alcohol chains relative to films containing unmodified starch, providing the resulting film with increased mechanical strength relative to films containing unmodified starch.

[0091] In embodiments, the water-soluble film comprises modified starch having a degree of modification greater than about 2% in an amount ranging from about 2.5 phr to about 30 phr, and the film has a GG static coefficient of friction of about 5 or less, about 3 or less, about 2 or less, or about 1 or less. In embodiments, the water-soluble film comprises modified starch having a degree of modification greater than 2% in an amount ranging from about 2.5 phr to about 30 phr, and the film is characterized by a reduced gloss-to-gloss static coefficient of friction compared to an equivalent film formulation without the starch.

[0092] In embodiments, the water-soluble film comprises a non-modified starch having an amylose content ranging from about 20% to about 80%, optionally from about 25% to about 70%, from about 30% to about 70%, or from about 40% to about 60%. Optionally, the non-modified starch is present in an amount ranging from about 2 phr to about 30 phr, or from about 2 phr to about 5 phr. Advantageously, when the water-soluble film comprises a non-modified starch having an amylose content ranging from greater than about 20% to less than about 80%, the film has been found to have a GG static coefficient of friction of about 1 or less, even at lower starch loadings (e.g., from about 2 phr to about 5 phr). In embodiments, the water-soluble film comprises a non-modified starch having an amylose content ranging from about 20% to about 80%, optionally from about 25% to about 70%, from about 30% to about 70%, or from about 40% to about 60%, and the film is characterized by a reduced gloss-to-gloss static coefficient of friction compared to an equivalent film formulation without the starch.

[0093] In embodiments, the water-soluble film comprises a hydroxypropyl-modified starch having an amylose content ranging from about 23% to about 95%, and the PVOH resin comprises an unmodified polyvinyl alcohol, an anionically modified polyvinyl alcohol copolymer, provided that the anionic modifier is not an acrylate, or a combination thereof. Optionally, the hydroxypropylated starch is present in an amount ranging from about 5 phr to about 12 phr. Optionally, the hydroxypropylated starch has an amylose content ranging from about 50% to about 95%. Further optionally, the hydroxypropylated starch comprises greater than 2% hydroxypropyl modification, or from about 4% to about 8% hydroxypropyl modification. Without intending to be bound by theory, it is believed that the acrylate moieties negatively interact with the hydroxyalkyl-modified starch, resulting in a film with a high GG static coefficient of friction. In embodiments, water-soluble films comprising hydroxypropyl-modified starch having an amylose content ranging from about 23% to about 95% and PVOH resins comprising unmodified polyvinyl alcohol, anionically modified polyvinyl alcohol copolymers, provided that the anionic modifier is not an acrylate, or combinations thereof, have a gloss-to-gloss static coefficient of friction of about 5 or less. In embodiments, water-soluble films comprising hydroxypropyl-modified starch having an amylose content ranging from about 23% to about 95% and PVOH resins comprising unmodified polyvinyl alcohol, anionically modified polyvinyl alcohol copolymers, provided that the anionic modifier is not an acrylate, or combinations thereof, are characterized by a reduced gloss-to-gloss static coefficient of friction compared to equivalent film formulations that do not include starch.

[0094] Other water-soluble polymers In addition to the PVOH resin or resin blend, other water-soluble polymers for use may include, but are not limited to, vinyl alcohol-vinyl acetate copolymers, sometimes referred to as PVOH homopolymers, polyacrylates, water-soluble acrylate copolymers, polyvinylpyrrolidone, polyethyleneimine, pullulan, water-soluble natural polymers including, but not limited to, guar gum, acacia gum, xanthan gum, carrageenan, and starch (not previously described above), water-soluble polymer-modified starches (not previously described above), including, but not limited to, ethylated starch, and hydroxyethylated starch, and hydroxypropylated starch, copolymers of the foregoing, and combinations of any of the foregoing. Other water-soluble polymers include polyalkylene oxides, polyacrylamides, polyacrylic acids, and their salts, cellulose, cellulose ethers, cellulose esters, cellulose amides, polyvinyl acetates, polycarboxylic acids, and their salts, polyamino acids, polyamides, gelatin, methylcellulose, carboxymethylcellulose, and their salts, dextrin, ethylcellulose, hydroxyethylcellulose, hydroxypropylmethylcellulose, maltodextrin, polymethacrylates, and combinations of any of the foregoing. Such water-soluble polymers, whether PVOH or not, are commercially available from various suppliers. In embodiments, the water-soluble film does not contain polyacrylates, water-soluble acrylate copolymers, polyacrylic acids, or their salts.

[0095] The water-soluble film may contain other auxiliary and processing aids in amounts suitable for their intended purpose, such as, but not limited to, plasticizers, plasticizer compatibilizers, surfactants, lubricants, release agents, fillers, extenders, crosslinkers, anti-blocking agents, antioxidants, detackifying agents, anti-foaming agents, nanoparticles such as layered silicate-type nanoclays (e.g., sodium montmorillonite), bleaching agents (e.g., sodium disulfite, sodium bisulfite, etc.), bittering agents (e.g., denatonium salts such as denatonium benzoate, denatonium saccharide, and denatonium chloride; octaacetylsucrose; quinine; flavonoids such as quercetin and naringenin; and quassinoids such as quassin and brucine), and aversive agents such as pungency (e.g., capsaicin, piperine, allyl isothiocyanate, and resinferratoxin), as well as other functional ingredients. Embodiments including plasticizers are preferred. In embodiments, the water-soluble film includes a surfactant, antioxidant, bittering agent, soil release polymer, anti-redeposition aid, chelating agent, builder, fragrance, or combinations thereof, and the amounts of the adjuvants, individually or collectively, can be up to about 50%, 20%, 15%, 10%, 5%, 4% and / or at least 0.01%, 0.1%, 1%, or 5% by weight.

[0096] In processes such as solvent casting, in which water-soluble film components are added to a solvent and mixed or held at elevated temperatures, the composition may brown. Such browning is undesirable for most water-soluble film applications, where a transparent film is desired. Therefore, the methods and compositions described herein may further include adding bisulfite or disulfite to the composition in an amount ranging from about 0.10% to about 0.75% by weight, e.g., from about 0.4% to about 0.7% by weight, based on the weight of the resulting film, to prevent browning of the heated composition.

[0097] plasticizer Plasticizers are liquids, solids, or semi-solids that are added to materials (usually resins or elastomers) to make them softer, more flexible, and easier to process (by decreasing the glass transition temperature of the polymer). Polymers may alternatively be internally plasticized by chemically modifying the polymer or monomer. Additionally or alternatively, polymers may be externally plasticized by the addition of a suitable plasticizer.

[0098] Plasticizers include, but are not limited to, glycerol, diglycerin, sorbitol, ethylene glycol, diethylene glycol, triethylene glycol, dipropylene glycol, tetraethylene glycol, propylene glycol, polyethylene glycols up to 400 MW, neopentyl glycol, trimethylolpropane, polyether polyols, 2-methyl-1,3-propanediol (MPDiol®), ethanolamine, glycerol propylene oxide polymers (e.g., Voranol® available from The Dow Chemical Company), and the like. (商標) In embodiments, the plasticizer may include glycerol, propylene glycol, sorbitol, trimethylolpropane, polyethylene glycols up to 400 MW, glycerol propylene oxide polymers (e.g., Voranol available from The Dow Chemical Company, etc.), and mixtures thereof. (商標) In an embodiment, the plasticizer is selected from the group consisting of glycerol, sorbitol, 2-methyl-1,3-propanediol, xylitol, and combinations thereof.

[0099] The total amount of plasticizer can range from about 10% to about 45% by weight, or from 15% to about 35% by weight, or from about 20% to about 30% by weight, or from about 20% to about 45% by weight, e.g., about 25% by weight, based on the total film weight. In embodiments, the amount of plasticizer in the water-soluble film is expressed in parts per hundred (PHR) of total water-soluble polymer in the water-soluble film, e.g., at least 1 PHR, at least 5 PHR, at least 10 PHR, at least 15 PHR, at least 20 PHR, at least 25 PHR, at least 30 PHR, or at least 35 PHR. The total amount of plasticizer can be, for example, up to 40 PHR, 45 PHR, or 50 PHR. The total amount of plasticizer can range, for example, from about 1 PHR to about 40 PHR, or from about 10 PHR to about 40 PHR, or from about 30 PHR to about 50 PHR, or from about 32.5 PHR to about 42.5 PHR, or from about 35 PHR to about 45 PHR, or from about 35 PHR to about 40 PHR, or from more than 30 PHR to less than 45 PHR, or from 40 PHR to 50 PHR. The specific amount of plasticizer can be selected in certain embodiments based on the desired film plasticity and processability characteristics of the water-soluble film. At low plasticizer levels, the film may be brittle, difficult to process, or prone to breakage. At high plasticizer levels, the film may be too soft, weak, or difficult to process for the desired use.

[0100] surfactants Surfactants for use in water-soluble films are known in the art. Optionally, a surfactant is included to aid in dispersion of the resin solution during casting. Suitable surfactants may include nonionic, cationic, anionic, and zwitterionic classes. Suitable surfactants include, but are not limited to, polyoxyethylenated polyoxypropylene glycols, alcohol ethoxylates, alkylphenol ethoxylates, tertiary acetylene glycols, and alkanolamides (nonionic), polyoxyethylenated amines, quaternary ammonium salts, and quaternized polyoxyethylenated amines (cationic), as well as amine oxides, N-alkyl betaines, and sulfobetaines (zwitterionic). Other suitable surfactants include dioctyl sodium sulfosuccinate, lactylated fatty acid esters of glycerol and propylene glycol, lactyl esters of fatty acids, sodium alkyl sulfate, polysorbate 20, polysorbate 60, polysorbate 65, polysorbate 80, lecithin, acetylated fatty acid esters of glycerol and propylene glycol, and acetylated esters of fatty acids, and combinations thereof. In some embodiments, the surfactant is selected from the group consisting of polyoxyethylenated polyoxypropylene glycols, alcohol ethoxylates, alkylphenol ethoxylates, tertiary acetylenic glycols and alkanolamides, polyoxyethylenated amines, quaternary ammonium salts and quaternized polyoxyethylenated amines, amine oxides, N-alkylbetaines, sulfobetaines, and combinations thereof.

[0101] In various embodiments, the amount of surfactant in the water-soluble film ranges from about 0.1% to about 8.0% by weight, or from about 1.0% to about 7.0% by weight, or from about 3% to about 7% by weight, or from about 5% to about 7% by weight. In embodiments, the amount of plasticizer in the water-soluble film, expressed in parts per hundred parts of total water-soluble polymer in the water-soluble film (PHR), is present in the range of from about 0.5 phr to about 12 phr, from about 1.0 phr to about 11.0 phr, from about 3.0 phr to about 10.5 phr, or from about 1.0 phr to about 2.0 phr.

[0102] Suitable lubricants / release agents may include, but are not limited to, fatty acids and their salts, fatty alcohols, fatty esters, fatty amines, fatty amine acetates, and fatty amides. Preferred lubricants / release agents are fatty acids, fatty acid salts, and fatty amine acetates. In certain embodiments, the amount of lubricant / release agent in the water-soluble film may range from about 0.02% to about 1.5% by weight, optionally from about 0.1% to about 1% by weight.

[0103] Suitable fillers / bulking agents / anti-blocking agents / detackifying agents include, but are not limited to, cross-linked polyvinylpyrrolidone, cross-linked cellulose, microcrystalline cellulose, silica, metal oxides, calcium carbonate, talc, mica, stearic acid and its metal salts, such as magnesium stearate. Optionally, in addition to one of the specific starch components mentioned above, the water-soluble starch may contain additional unmodified or modified starches, such as, for example, hydroxypropylated starch present in an amount ranging from about 5 phr to about 30 phr, or modified starch having a degree of modification greater than about 2% and present in an amount ranging from about 2.5 phr to about 30 phr, or unmodified starch having an amylose content ranging from about 20% to about 80%, or hydroxypropyl-modified starch having an amylose content ranging from about 23% to about 95% when the polyvinyl alcohol comprises unmodified polyvinyl alcohol or an anionically modified polyvinyl alcohol copolymer, provided that the anionic modifier is not an acrylate. Preferred materials are starch, modified starch, and silica. In certain embodiments, the amount of filler / bulking agent / anti-blocking agent in the water-soluble film can range, for example, from about 1% to about 6% by weight, or from about 1% to about 4% by weight, or from about 2% to about 4% by weight, or from about 1 phr to about 6 phr, or from about 1 phr to about 4 phr, or from about 2 phr to about 4 phr. In embodiments, when starch or modified starch is included in the water-soluble film in addition to one of the specific starch components described above, the additional starch component will be provided in an amount of less than about 50% by weight, based on the total weight of all starches included in the film. Without intending to be bound by theory, it is believed that any benefits provided to the water-soluble films of the present disclosure by the inclusion of the above-described starch components are not affected by the inclusion of additional starch components that provide less benefit to the water-soluble film or no benefit at all to the water-soluble film.

[0104] The water-soluble film may further have a residual moisture content of at least 4% by weight, preferably in the range of about 4 to about 10% by weight, as measured by Karl Fischer titration.

[0105] Film production method One contemplated class of embodiments is characterized in that the water-soluble film of the water-soluble packet is formed, for example, by solvent casting. Processes for solvent casting of PVOH are known in the art. For example, in a film-forming process, polyvinyl alcohol polymer and secondary additives are dissolved in a solvent, typically water, metered onto a surface, and subsequently dried (or forced dried) to form a cast film, which is then removed from the casting surface. The process can be carried out batchwise, but is more efficiently carried out in a continuous process. For example, water or solvent is heated to a temperature in the range of about 80-90°C, and the plasticizer, starch, and secondary additives are added to the water or solvent first, followed by the surfactant. The mixture is stirred until a homogeneous mixture is formed. The film-forming resin is then added to the mixture and mixed at about 80-90°C until homogeneous.

[0106] In forming a continuous film of polyvinyl alcohol, it is conventional to meter a solution of the solution onto a moving casting surface, such as a continuously moving metal drum or belt, causing the solvent to be substantially removed from the liquid, thereby forming a self-supporting cast film, which is then stripped from the casting surface.

[0107] Optionally, the water-soluble film can be a self-supporting film consisting of one layer or multiple similar layers.

[0108] Residual moisture content

[0109] The water-soluble film may further have a residual moisture content of at least 4% by weight, preferably in the range of about 4 to about 10% by weight, as measured by Karl Fischer titration.

[0110] Pouch / Packet The water-soluble films disclosed herein are useful for making sealed articles in the form of pouches that define an internal pouch volume that contains a composition therein. For example, in embodiments in which the compartment contains a degassed solid, the "sealed article" includes a sealed compartment with a vent. The pouch composition can take any form, such as a powder, gel, paste, liquid, tablet, or any combination thereof. The films are also useful in any other application in which improved wet processing and low cold water residue are desired.

[0111] The films described herein may also be used to make packets with two or more compartments, either made from the same film or in combination with films of other polymeric materials. The additional film can be obtained, for example, by casting, blow molding, extrusion, or extrusion-blow molding of the same or different polymeric materials as known in the art. In one type of embodiment, the polymer, copolymer, or derivative thereof suitable for use as the additional film is selected from polyvinyl alcohol, polyvinylpyrrolidone, polyalkylene oxide, polyacrylic acid, cellulose, cellulose ether, cellulose ester, cellulose amide, polyvinyl acetate, polycarboxylic acid and salt, polyamino acid or peptide, polyamide, polyacrylamide, maleic acid / acrylic acid copolymer, polysaccharides including starch and gelatin, natural gums such as xanthan gum, and carrageenan. For example, the polymer may be selected from polyacrylates and water-soluble acrylate copolymers, methylcellulose, sodium carboxymethylcellulose, dextrin, ethylcellulose, hydroxyethylcellulose, hydroxypropylmethylcellulose, maltodextrin, polymethacrylates, and combinations thereof, or may be selected from polyvinyl alcohol, polyvinyl alcohol copolymers and hydroxypropylmethylcellulose (HPMC), and combinations thereof. One contemplated embodiment is characterized by the polymer level in the packet material, for example, the PVOH copolymers mentioned above are at least 60% as described above.

[0112] The pouch of the present disclosure may include at least one sealed compartment. Thus, the pouch may include a single compartment or multiple compartments. The water-soluble pouch may be formed from two layers of water-soluble polymeric film sealed at their interfaces, or from a single film folded over and sealed on itself. One or both of the films may comprise the PVOH film described above. The film defines an internal pouch volume containing any desired composition for release into an aqueous environment. The composition is not particularly limited and may include, for example, any of the various compositions described below. In embodiments with multiple compartments, each compartment may contain the same and / or different compositions. The composition may, in turn, take any suitable form, including, but not limited to, a liquid, a solid, a compressed solid (tablet), and combinations thereof (e.g., a solid suspended in a liquid). In an embodiment, the pouch includes first, second, and third compartments, each containing a different first, second, and third composition, respectively.

[0113] The compartments of the multi-compartment pouch may be of the same or different size(s) and / or volume(s). The compartments of the present multi-compartment pouch may be separated or joined in any suitable manner. In embodiments, the second and / or third and / or subsequent compartments are superimposed on the first compartment. In embodiments, the second and / or third and / or subsequent compartments are oriented side-by-side or concentrically. The compartments may be packaged in series, with each compartment individually separable by a perforation. In this manner, each compartment may be individually torn by the end user from the remainder of the series.

[0114] The geometric shapes of the sections may be the same or different. In embodiments, the optional third section and subsequent sections each have a different geometric shape and shape compared to the first and second sections. In these embodiments, the optional third section and subsequent sections are arranged in a design on the first or second section. This design may be decorative, educational, or illustrative, for example, to illustrate a concept or instruction, and / or may be used to indicate the source of the product.

[0115] The pouches and / or packets of the present disclosure may comprise one or more different films. For example, in single-compartment embodiments, the packet may be made of one wall folded over on itself and sealed at the edges, or two walls sealed together at the edges. In multi-compartment embodiments, the packet may be made from one or more films, such that any given packet compartment may comprise walls made from a single film or multiple films having different compositions.

[0116] Pouches and packets can be made using any suitable equipment and method. For example, single-compartment pouches can be made using vertical form-fill, horizontal form-fill, or rotary drum-fill techniques commonly known in the art. Such processes can be either continuous or intermittent. The film can be moistened and / or heated to increase its malleability. The method can also involve the use of a vacuum to draw the film into a suitable mold. The vacuum to draw the film into the mold can be applied for about 0.2 to about 5 seconds, or about 0.3 to about 3, or about 0.5 to about 1.5 seconds once the film is resting on a horizontal portion of a surface. The vacuum can be such as to provide a low pressure, for example, in the range of 10 mbar to 1000 mbar, or in the range of 100 mbar to 600 mbar.

[0117] The molds from which the packets are made can have any shape, length, width, and depth depending on the required dimensions of the pouch. Molds can also vary in size and shape, if desired. For example, the volume of the final pouch can be about 5 ml to about 300 ml, or about 10 to 150 ml, or about 20 to about 100 ml, with the size of the mold adjusted accordingly.

[0118] Molding, sealing, and thermoforming A thermoformable film is a film that can be shaped through the application of heat and force.

[0119] Thermoforming a film is a process in which a film is heated, molded (e.g., into a mold), and then cooled so that the film will retain its shape, e.g., the shape of the mold. Heat may be applied using any suitable means. For example, the film may be directly heated by passing it under a heating element or through hot air before or once it is applied to a surface. Alternatively, the film may be indirectly heated, for example, by heating the surface or by applying a hot item to the film. In embodiments, the film is heated using infrared light. The film may be heated to a temperature ranging from about 50 to about 150°C, about 50 to about 120°C, about 60 to about 130°C, about 70 to about 120°C, or about 60 to about 90°C. Thermoforming can be performed by any one or more of the following processes: manual draping of heat-softened film over a mold, or forming the softened film against a mold by pressure (e.g., vacuum forming), or automatic high-speed indexing of a freshly extruded sheet having a precisely known temperature to a forming and trimming station, or automatic placement, plug forming and / or pneumatic stretching and pressure forming of the film.

[0120] Alternatively, the film may be moistened by any suitable means before or once it is applied to the surface, such as directly by spraying a wetting agent (including water, a solution of the film composition, a plasticizer for the film composition, or any combination of the foregoing) onto the film, or by wetting the surface, or indirectly by applying a wetting article to the film.

[0121] Once the film is heated and / or wetted, it can be drawn into a suitable mold, preferably using a vacuum. Filling of the formed film can be achieved by utilizing any suitable means. In embodiments, the most preferred method will depend on the product form and the required filling speed. In embodiments, the formed film is filled by an in-line filling technique. The filled, open packet is then sealed using a second film by any suitable method to form a pouch. This can be achieved in a continuous, constant motion while in a horizontal position. Sealing can be achieved by continuously feeding a second film, preferably a water-soluble film, over and over the open packet, and then preferably sealing the first and second films together, typically in the area between the molds and therefore between the packets.

[0122] Any suitable method of sealing the packet and / or its individual compartments may be utilized. Non-limiting examples of such means include heat sealing, solvent welding, solvent or wet sealing, and combinations thereof. Typically, only the area where the seal will be formed is treated with heat or solvent. Heat or solvent may be applied by any method, typically onto the sealant material, and typically only onto the area where the seal will be formed. When solvent or wet sealing or welding is used, it may be preferable to also apply heat. A preferred method of wet or solvent sealing / welding involves selectively applying solvent onto the areas between the dies or onto the sealant material, for example, by spraying or printing the solvent onto these areas, and then applying pressure onto these areas to form the seal. For example, sealing rolls and sealing belts (optionally also providing heat), as described above, may be used.

[0123] The formed pouch can then be cut by a cutting device. Cutting can be accomplished using any known method. It may also be preferable for cutting to be done in a continuous manner, preferably at a constant speed and preferably in a horizontal position. The cutting device may be, for example, a sharp article, or a hot article, or a laser, in the latter case, where the hot article or laser "burns" through the film / sealing area.

[0124] The different compartments of the multi-compartment pouch may be made together in a side-by-side or concentric manner, and the resulting joined-together pouch may or may not be separated by cutting. Alternatively, the compartments may be made separately.

[0125] In embodiments, pouches may be made according to a process including: a) forming a first compartment (as described above), b) forming recesses in some or all of the sealed compartments formed in step (a) to produce a second molded compartment superimposed on the first compartment, c) filling and sealing the second compartment with a third film, d) sealing the first, second, and third films, and e) cutting the films to produce a multi-compartment pouch. The recesses formed in step (b) may be achieved by applying a vacuum to the compartments prepared in step (a).

[0126] In embodiments, the second and / or third compartment(s) can be made in separate steps and then combined with the first compartment, as described in European Patent Application No. 08101442.5, or U.S. Patent Application Publication No. 2013 / 240388(A1), or WO2009 / 152031.

[0127] In embodiments, pouches may be made according to a process comprising the steps of: a) forming a first compartment using a first film in a first forming machine, optionally using heat and / or vacuum; b) filling the first compartment with a first composition; c) optionally filling the second compartment with a second composition; d) sealing the first and optional second compartments to the first film with a second film; and e) cutting the film to produce multi-compartment pouches.

[0128] In embodiments, pouches may be made according to a process comprising: a) forming a first compartment using a first film on a first forming machine, optionally using heat and / or vacuum; b) filling the first compartment with a first composition; c) deforming a second film on a second forming machine, optionally using heat and vacuum, to create a second and optionally third shaped compartment; d) filling the second and optionally third compartments; e) sealing the second and optionally third compartments using a third film; f) placing the sealed second and optionally third compartments onto the first compartment; g) sealing the first, second, and optionally third compartments; and h) cutting the film to produce a multi-compartment pouch.

[0129] The first and second forming machines may be selected based on their suitability for carrying out the above process. In an embodiment, the first forming machine is preferably a horizontal forming machine, and the second forming machine is preferably a rotary drum former, preferably located above the first forming machine.

[0130] It should be understood that by using an appropriate supply station, it may be possible to produce multi-compartment pouches incorporating a number of different or unique compositions and / or different or unique liquid, gel or paste compositions.

[0131] In embodiments, the film and / or pouch is sprayed or dusted with a suitable material, such as an active agent, a lubricant, an aversive agent, or a mixture thereof. In embodiments, the film and / or pouch is printed thereon, for example with an ink and / or an active agent.

[0132] Vertical form, fill and seal In embodiments, the water-soluble film of the present disclosure can be formed into a sealed article. In embodiments, the sealed article is a vertically formed, filled, and sealed article. The vertical form, fill, and seal (VFFS) process is a conventional, automated process. A VFFS includes an apparatus, such as an assembly machine, that wraps a single piece of film around a vertically oriented feed tube. The machine's heat sealing or another method secures opposing edges of the film together to create a side seal and create a hollow tube of film. The machine's heat sealing or another method then creates a bottom seal, thereby defining a container portion with an open top on which a top seal will later be formed. The machine introduces a specific amount of flowable product into the container portion through the open top end. Once the container contains the desired amount of product, the machine advances the film, for example, to another heat-sealing device to create the top seal. Finally, the machine advances the film to a cutter to cut the film just above the top seal to provide a filled package.

[0133] In operation, an assembly machine advances the film from the roll to form the package, so the film must be able to advance easily through the machine and not adhere to the machine assembly or be so weak that it breaks during processing.

[0134] The water-soluble film can be converted by VFFS in a Rovema VFFS machine or equivalent. Pouches / packets are prepared at a standard laboratory atmosphere of 78°F (approximately 25.5°C) and 24% relative humidity. Both unfilled and salt-filled bags are produced. Salt-containing bags are filled to a maximum fill level of 1.2 lbs (approximately 550g). The horizontal sealing temperature is 225°F (approximately 107°C), and the vertical sealing temperature varies as needed to produce a good seal, e.g., from about 255°F (approximately 124°C) to about 280°F (approximately 138°C).

[0135] Pouch contents The article (e.g., in the form of a pouch or packet) can contain various compositions, such as household care compositions (detergent compositions), or non-household care compositions. A multi-compartment pouch can contain the same or different compositions in each separate compartment. The composition is proximal to the water-soluble film. The composition may be less than about 10 cm, or less than about 5 cm, or less than about 1 cm from the film. Typically, the composition is adjacent to or in contact with the film. The film can be in the form of a pouch or compartment that contains the composition therein.

[0136] The inner film of the pouch can be utilized as a divider to keep compositions containing incompatible ingredients physically separated from one another. It is believed that such a divider can extend the useful life and / or reduce the physical instability of such ingredients. Additionally or alternatively, such a divider can provide an aesthetic benefit, as described in U.S. Patent Application No. 8,835,372.

[0137] In embodiments, the compositions may be selected from the group of light-duty and heavy-duty liquid detergent compositions, powder detergent compositions, hand and / or dishwashing detergents, hard surface cleaning compositions, fabric softeners, detergent gels commonly used in laundry, and detergent compositions as bleaches and laundry additives, shaving creams, skin care, hair care compositions (shampoos and conditioners), and body washes. Such detergent compositions may include surfactants, bleaches, enzymes, fragrances, dyes or colorants, solvents, and combinations thereof.

[0138] In embodiments, the compositions may be selected from the group of non-household care compositions, including agricultural compositions, automotive compositions, aviation compositions, food and nutritional compositions, industrial compositions, livestock compositions, marine compositions, medical compositions, commercial compositions, military and paramilitary compositions, office compositions, and recreational and park compositions, pet compositions, water treatment compositions (including cleaning and detergent compositions applicable to any such use).

[0139] In embodiments, the composition contained in the inner pouch volume is a detergent composition. Optionally, the detergent composition is selected from the group consisting of laundry detergent, dishwashing detergent, hard surface cleaning composition, fabric softener composition, shaving cream, skin care, hair care composition (shampoo and conditioner), body wash, and combinations thereof.

[0140] Non-limiting examples of useful non-household care compositions include agricultural compositions, automotive compositions, aircraft compositions, food and nutritional compositions, industrial compositions, livestock compositions, marine compositions, medical compositions, commercial compositions, military and paramilitary compositions, office compositions, recreational and park compositions, pet compositions, and water treatment compositions (including cleaning and detergent compositions applicable to any such use). The compositions used in the pouches can be in liquid, solid, or powder form. Liquid compositions can include solids. Solids can include powders or agglomerates such as microcapsules, beads, noodles, or one or more pearl-sized balls, or mixtures thereof. Such solid elements can provide technical benefits throughout the wash or as pre-treatment, delayed- or continuous-release components, and can additionally or alternatively provide aesthetic benefits (e.g., perfume microcapsules).

[0141] The compositions encapsulated by the films described herein, when liquid compositions, can have any suitable viscosity, depending on factors such as the ingredients to be incorporated and the purpose of the composition. In one embodiment, the composition has a viscosity of 20 s -1 and a temperature of 20°C, and a high shear viscosity value of 100 to 3,000 cP, or 300 to 2,000 cP, or 500 to 1,000 cP, and a 1 s -1The viscosity of the liquid has a low shear viscosity of 500 to 100,000 cP, or 1,000 to 10,000 cP, or 1,300 to 5,000 cP at a shear rate of 100°C and a temperature of 20°C. Methods for measuring viscosity are known in the art. Viscosity measurements according to the present invention are performed using a rotational rheometer, such as a TA Instruments AR550. This instrument includes a 40 mm 2° or 1° cone fixture with a gap of approximately 50 to 60 μm for isotropic liquids, or a 40 mm flat steel plate with a gap of 1,000 μm for liquids containing particles. Measurements are performed using a flow procedure that includes a calibration step, peak hold, and continuous ramp step. The calibration step involves setting the measurement temperature at 20°C, ramping for 10 s, and then ramping for 10 s. -1 The preshear included 10 seconds at a shear rate of 0.05 s and 60 seconds equilibration at the selected temperature. Peak hold was 0.05 s at 20 °C. -1 A shear rate of 0.1 to 1200 s was applied for 3 min with sampling every 10 s. Successive ramp steps were performed from 0.1 to 1200 s at 20 °C. -1 The flow is run for 3 minutes at a shear rate of 100 rpm to obtain a complete flow profile.

[0142] As mentioned above, the composition can be a non-household care composition.For example, the non-household care composition can be selected from agricultural compositions, automotive compositions, aviation compositions, food and nutrition compositions, industrial compositions, livestock compositions, marine compositions, medical compositions, commercial compositions, military and paramilitary compositions, office compositions, and recreational and park compositions, pet compositions, water treatment compositions (including cleaning compositions and detergent compositions applicable to any such use).

[0143] In some embodiments, the composition comprises a pesticide, such as one or more insecticides, fungicides, herbicides, pesticides, acaricides, repellents, attractants, defoliants, plant growth regulators, fertilizers, bactericides, micronutrients, and trace elements. Suitable pesticides and secondary agents are described in U.S. Patent Nos. 6,204,223 and 4,681,228, and European Patent No. EP 0 989 803 (A1). For example, suitable herbicides include paraquat salts (e.g., paraquat dichloride or paraquat bis(methyl sulfate), diquat salts (e.g., diquat dibromide or diquat alginate), and glyphosate or its salts or esters (e.g., glyphosate isopropylammonium, glyphosate sesquisodium, or glyphosate trimesium, also known as sulfosate). Pairs of incompatible crop protection chemicals may be used in separate chambers, as described, for example, in U.S. Pat. No. 5,558,228. Examples of incompatible crop protection chemical pairs that may be used include bensulfuron methyl and molinate, 2,4-D and thifensulfuron methyl, 2,4-D and methyl 2-[[[[N-4-methoxy-6-methyl-1,3,5-triazin-2-yl]methyl ... ]-N-methylamino]carbonyl]amino]-sulfonyl]benzoate, 2,4-D and metsulfuron methyl, maneb or mancozeb and benomyl, glyphosate and metsulfuron methyl, tralomethrin and any organophosphate such as monocrotophos or dimethoate, bromoxynil and N-[[4,6-dimethoxypyrimidin-2-yl]-amino]carbonyl]-3-(ethylsulfonyl)-2-pyridine-sulfonamide, bromoxynil and methyl 2-[[[[(4-methyl-6-methoxy)-1,3,5-triazin-2-yl)amino]carbonyl]amino]sulfonyl]benzoate, bromoxynil and methyl 2-[[[[N-(4-methoxy-6-methyl-1,3,5-triazin-2-yl)-N-methylamino]carbonyl]amino]-sulfonyl]benzoate.In another related type of embodiment, the composition may include one or more seeds, optionally together with soil, and optionally together with one or more additional components selected from mulch, sand, peat moss, water jelly crystals, and fertilizer, including, for example, embodiments of the type described in U.S. Pat. No. 8,333,033.

[0144] In another type of embodiment, the composition is a water treatment agent. Such agents include aggressive oxidizing chemicals, such as those described in U.S. Patent Application Publication No. 2014 / 0110301 and U.S. Patent No. 8,728,593. For example, sanitizing agents can include hypochlorites, such as sodium hypochlorite, calcium hypochlorite, and lithium hypochlorite, and chlorinated isocyanurates, such as dichloroisocyanuric acid (also known as "dichlor" or dichloro-s-triazinetrione, 1,3-dichloro-1,3,5-triazinane-2,4,6-trione) and trichloroisocyanuric acid (also known as "trichlor" or 1,3,5-trichloro-1,3,5-triazinane-2,4,6-trione). Salts and hydrates of the disinfecting compounds are also contemplated. For example, dichloroisocyanuric acid can be provided as sodium dichloroisocyanurate, sodium dichloroisocyanurate dihydrate, among others. Bromine-containing disinfectants may also be suitable for use in unit-dose packaging applications, including 1,3-dibromo-5,5-dimethylhydantoin (DBDMH), 2,2-dibromo-3-nitrilopropionamide (DBNPA), dibromocyanoacetic acid amide, 1-bromo-3-chloro-5,5-dimethylhydantoin, and 2-bromo-2-nitro-1,3-propanediol, among others. The oxidizing agent may be one described in U.S. Patent No. 7,476,325, such as potassium hydrogen peroxymonosulfate. The composition may also be a pH-adjusting chemical, such as that described in U.S. Patent Application Publication No. 2008 / 0185347, which may include, for example, acidic and alkaline components that effervescently effervescently adjust the pH of water upon contact with the composition. Suitable components include sodium bicarbonate, sodium bisulfate, potassium hydroxide, sulfamic acid, organic carboxylic acids, sulfonic acids, and potassium dihydrogen phosphate. The buffer blend may include, for example, boric acid, sodium carbonate, glycolic acid, and oxone monopersulfate.

[0145] The water treatment agent may be or may include a flocculant, such as those described in U.S. Patent Application Publication No. 2014 / 0124454. The flocculant can include a polymeric flocculant, such as polyacrylamide, polyacrylamide copolymers, such as diallyldimethylammonium chloride (DADMAC), dimethylaminoethyl acrylate (DMAEA), dimethylaminoethyl methacrylate (DMAEM), 3-methylamidopropyltrimethylammonium chloride (MAPTAC) or acrylamide copolymers of acrylic acid, cationic polyacrylamide, anionic polyacrylamide, neutral polyacrylamide, polyamine, polyvinylamine, polyethyleneimine, polydimethyldiallylammonium chloride, polyoxyethylene, polyvinyl alcohol, polyvinylpyrrolidone, polyacrylic acid, polyphosphoric acid, polystyrene sulfonic acid, or any combination thereof. The flocculant can be selected from chitosan acetate, chitosan lactate, chitosan adipate, chitosan glutamate, chitosan succinate, chitosan malate, chitosan citrate, chitosan fumarate, chitosan hydrochloride, and combinations thereof. The water treatment composition can include one or more phosphate-removing materials selected from, for example, zirconium compounds, rare earth lanthanide salts, aluminum compounds, iron compounds, or any combination thereof.

[0146] The composition may be, for example, a limescale removal composition as described in US Patent Application No. 2006 / 0172910, such as citric acid, or maleic acid, or sulfates thereof, or any mixture thereof.

[0147] Various other types of compositions are contemplated for use in the packets described herein, including particulates such as feathers, as described, for example, in US RE29059 E; superabsorbent polymers, as described, for example, in US Patent Application Publication Nos. 2004 / 0144682 and 2006 / 0173430; pigments and stains, as described, for example, in US Patent Application Publication Nos. 3,580,390 and 2011 / 0054111; brazing fluxes (e.g., alkali metal fluoroaluminates, alkali metal fluorosilicates, and alkali metal fluorozincates), as described, for example, in US Patent Application Publication No. 8,163,104; food products (e.g., coffee powder or dried soup), as described, for example, in US Patent Application Publication No. 2007 / 0003719; and wound dressings, as described, for example, in US Patent No. 4,466,431.

[0148] Dissolution and Disintegration Test (MSTM 205) Films can be characterized or tested for dissolution and disintegration times according to methods known in the art, MonoSol Test Method 205 (MSTM 205), see, e.g., U.S. Patent No. 7,022,656.

[0149] Equipment and materials: 1.600mL beaker 2. Magnetic Stirrer (Labline Model No. 1250 or equivalent) 3. Magnetic stirring bar (5cm) 4.Thermometer (0~100℃±1℃) 5. Template, stainless steel (3.8cm x 3.2cm) 6. Timer (0-300 seconds, accuracy to the second) 7. Polaroid 35mm slide mount (or equivalent) 8. MonoSol 35mm Slide Mount Holder (or equivalent) 9. Distilled water

[0150] For each film tested, three specimens are cut from the film sample using a stainless steel template (i.e., 3.8 cm x 3.2 cm specimens). If cut from a film web, specimens should be cut from equally spaced areas of the web along the cross direction of the web. Each specimen is then analyzed using the following procedure. 1. Lock each specimen into a separate 35mm slide mount. 2. Fill a beaker with 500 mL of distilled water. Measure the temperature of the water with a thermometer and, if necessary, heat or cool the water to maintain a temperature of 20°C (approximately 68°F). 3. Record the height of the water column. Place a magnetic stirrer on the base of the holder. Place the beaker on the magnetic stirrer, add a magnetic stir bar to the beaker, turn the stirrer on, and adjust the stirring speed until a vortex develops approximately one-fifth the height of the water column. Record the depth of the vortex. 4. Secure the 35mm slide to the alligator clamp on the 35mm slide holder so that the long end of the slide mount is parallel to the water surface. The holder's depth adjuster should be mounted so that when dropped, the end of the clip is 0.6 cm below the water surface. One of the short sides of the slide mount should be next to the side of the beaker, and the other should be positioned directly above the center of the stir bar, so that the film surface is perpendicular to the water flow. 5. In one motion, drop the secured slide and clip into the water and start the timer. Disintegration occurs when the film breaks. Once all visible film has been released from the slide mount, lift the slide out of the water while continuing to monitor the solution for undissolved film fragments. Dissolution occurs when all film fragments are no longer visible and the solution is clear.

[0151] Results should include the following: complete sample identification, individual and average disintegration and dissolution times, and the water temperature at which the sample was tested.

[0152] The film disintegration time (I) and film dissolution time (S) can be corrected to a standard or reference film thickness using the exponential algorithm shown below in Equation 1 and Equation 2, respectively. I 修正された =I 測定された / (reference thickness / measured thickness) 1.83 [1] S 修正された =S 測定された / (reference thickness / measured thickness) 1.93 [2]

[0153] Tensile Strength Test Films characterized or tested for tensile strength according to a tensile strength test are analyzed as follows. The procedure involves determining tensile strength according to ASTM D882 ("Standard Test Method for Tensile Properties of Thin Plastic Sheeting") or equivalent. An INSTRON® tensile testing device (Model 5544 Tensile Tester or equivalent) is used to collect film data. A minimum of three specimens, each cut with a reliable cutting tool to ensure dimensional stability and repeatability, are tested in the machine direction (MD) (if applicable) for each measurement. Testing is conducted in a standard laboratory atmosphere of 23±2.0°C and 35±5% relative humidity. For tensile strength determination, a 1-inch-wide (2.54 cm) sample is prepared from a single film sheet having a thickness of 3.0±0.15 mils (or 76.2±3.8 μm). The sample is then transferred to the INSTRON® tensile tester for testing while minimizing exposure to the 35% relative humidity environment. Prepare and calibrate a tensile tester equipped with a 500 N load cell according to the manufacturer's instructions. Install the correct grips and faces (INSTRON® grips with rubber-coated, 25 mm wide faces, model number 2702-032, or equivalent). Attach the sample to the tensile tester and analyze to determine the tensile strength (i.e., the stress required to break the film).

[0154] Suitable behavior of films according to the present disclosure is indicated by a tensile strength value (in the machine direction (MD)) of at least about 40 MPa as measured by a tensile strength test. In various embodiments, the films have a tensile strength value of at least 40 MPa and / or up to about 60 MPa (e.g., about 40, about 45, about 60, about 55, or about 60 MPa).

[0155] Tear Strength Test This method involves determining the average force (grams / mil) of specimen thickness required to propagate a tear through a specific length of polyvinyl alcohol (PVOH) film. The force (grams) required to propagate a tear through the film is measured using a precisely calibrated pendulum device. Under the action of gravity, the pendulum swings through an arc, tearing the specimen from a pre-cut slit. The specimen is held stationary on one side and secured to the pendulum on the other side. The energy loss of the pendulum swing is indicated by a needle on a scale. The scale reading is a function of the force required to tear the specimen. This method provides a value for ranking the relative tear resistance of PVOH films. Water-soluble films were evaluated for tear propagation resistance of polyvinyl alcohol films using an Elmendorf Tearing Tester Model 1#40043 according to the standard test method MSTM 107RD.

[0156] The water-soluble films were conditioned at a temperature of about 23°C + / - 3°C (73°F + / - 5°F) and a relative humidity of about 35% + / - 5% for at least 8 hours prior to testing. Testing was conducted in a standard laboratory atmosphere of 23°C + / - 3°C (73°F + / - 5°F) and a relative humidity of about 35% + / - 5%. The average tear force in grams-force per mil was calculated as follows: Tear force, g / mil = (increased weight g / 100) x scale index Film thickness in mills

[0157] Suitable behavior of films according to the present disclosure is indicated by a tear strength value (in the machine direction (MD)) of at least about 800 g / mil, as measured by a tear strength test. In various embodiments, the films have a tear strength value (MD) of at least 500 g / mil and / or up to about 2000 g / mil (e.g., about 500, about 800, about 1000, about 1200, or about 1500 g / mil).

[0158] Friction Coefficient Test The coefficient of friction method tests the friction of two pieces of material rubbed against each other and measures the force required to move one piece of material relative to the other. Both the force to start the sled (static friction) and the force to keep the sled moving (kinetic friction) are measured by a load cell using ASTM D1894 "Friction Testing of Plastic Film and Sheeting."

[0159] This method is (登録商標) Use a Coefficient of Friction Test Fixture Model 2810-005 or equivalent, or a representative diagram shown in Figure 2, and an Instron® Tester Model #5543 or equivalent.

[0160] The test apparatus includes a friction fixture 10 upon which rests a friction sled 12 having a film sample 14 secured thereon. Sled 12 is attached to an upper grip 18 via a pull cord 20 that engages a pulley 22 secured to the friction fixture 10. A lower coupling 24 secures the test fixture to an Instron® testing machine (not shown).

[0161] Instron (登録商標)According to the Blue Hill program on methods, "The system searches for the maximum value between the start and end values ​​of a particular channel; determines the first data point above or below it as a percentage of the maximum value and assigns this point as the first peak; determines the coefficient of static friction using the following equation: Static friction = first peak / sled weight; calculates the average load in the region from the first peak to the end value using the following equation: Average load = energy / change in elongation; determines the coefficient of kinetic friction using the following equation: Kinetic friction = average load / sled weight."

[0162] The specimens to form the test area should consist of samples having dimensions of 5 inches by 5 inches square (12.7 cm by 12.7 cm square) on the sled and 5 inches by 8 inches square (12.7 cm by 20.3 cm) on the face. Film thickness is not expected to affect the static COF, but films may have a thickness of 3.0 ± 0.10 mils (or 76.2 ± 2.5 μm). Samples may be cut, for example, using a razor blade and an appropriately sized template. When applicable, samples should be cut with the long dimension parallel to the machine direction of the cast film. Also, when applicable, the 5 inch by 5 inch sample orientation should be kept in mind and oriented during testing so that the direction in which the sled is pulled is parallel to the machine direction of the film sample.

[0163] The specimens should be conditioned at 75°F ± 5°F and 35% ± 5% relative humidity for at least 8 hours prior to testing, and the test will be conducted under the same temperature and relative humidity conditions.

[0164] COF equipment installation procedure 1. Instron (登録商標) Remove the clevis pin from the lower jaw of the Friction Coefficient Test Fixture Model 2810-005 and remove the lower jaw. 2. Remove the clevis pin from the upper jaw and remove the upper jaw. 3.Instron (登録商標) Place the lower coupling of the friction fixture onto the base adapter of the testing machine model #5543. 4. Attach with clevis pins. 5. Slide the loop on one end of the pull cord onto the upper clevis pin and replace it with the locking clip. 6. Calibration of Tester Model #5543 7. Slip the loop on the other end of the pull cord through the hook on the friction sled. 8. Check that the pulley can rotate freely. 9. Move the sled until there is no slack in the pull cord and it is aligned with the groove around the pulley. 10. Ensure there is enough travel space to pull the friction sled along the full 50 mm of the test without the sled hitting the pulley. (登録商標) Place the moving crosshead (upper hard) of the friction coefficient test fixture model 2810-005. 11. Hold the cord taut while the crosshead is moving. 12. Use the JOG control on the Instron #5543 control panel to set the extension limit so that the far end of the friction sled does not extend beyond the backplane of the friction fixture (the plane furthest from the pulley that is perpendicular to the axis of motion). Press the GL button to set the travel limit. This will prevent the friction sled from colliding with the pulley during testing and ensure that the coefficient of friction of the sample is measured properly. 13. The test fixture is now ready for testing. Specimen placement procedure 1. Place the surface sample in the aluminum friction fixture in the appropriate orientation. 2. Pull the surface sample firmly over the edge of the aluminum surface and tape the sample to the bottom side of the friction fixture. 3. It is important to tape along the edge of the friction jig farthest from the coupling to avoid sticking the sled to the surface. 4. Make sure the material is taut but not stretched. 5. Wrap the 5x5 inch sample around the friction sled so that the machine direction of the film is parallel to the direction the sled is pulled. 6. Tape the edge of the tip that overlaps the top of the sled, making sure there is no excess material that will stick to the surface sample. 7. Tape the other edge of the sample to the friction sled, ensuring that the sample is taut on the contact surface to be measured. 8. Ensure that no tape is pinched between the target surface on the sled and the target surface on the friction fixture. 9. The sample on the friction surface and the sample on the friction sled must be taut so that there are no wrinkles or bulges that would cause errors in the COF measurement. 10. Inspect the sled to ensure that no foreign objects are touching the surface being tested. 11. Attach the sled to the pull cord, place the sled very lightly and gently on the friction table to prevent any unnatural sticking between the two specimens, and begin the test immediately. 12. Ensure that the sled, when fully extended, fits completely over the specimen placed on the rub fixture and does not touch the tape or extend beyond the edge of the rub fixture. Conducting a COF test 1. Test at least three specimens for each required orientation (e.g., air side to air side or band side to band side). 2. For the air side to band side test combination, the air side orientation of the film shall be the film sample placed on the aluminum test surface, and the band side for testing shall include the material wrapped around the sled. 3. Always wear powder-free, moisture-proof gloves while handling film specimens, as powder and moisture may impair the accuracy of the test. 4. Cut the sample as described above, for example using a template. 5. Place the friction sled encased in the first specimen at the end of the friction fixture farthest from the pulley. 6. Make sure the pull cord is taut. 7. From the test screen, open the Coefficient of Friction test titled "COF.im ptf". 8. Click the start button on the screen to begin the test. 9. Once the test specimen has been run, click OK to return the friction sled to its starting position, replace the film specimen in the friction sled and fixture, and repeat the test.

[0165] The film may be characterized by a static COF in the range of 4.0 or less, or 2.0 or less, or 1.5 or less, or 1.25 or less, or 1.0 or less, e.g., 1.0, 0.9, 0.8, 0.7, 0.6 or less. In another embodiment, the static COF may be less than 4.0, or less than about 2.5, or less than 2, or less than 1.

[0166] In one or more embodiments, the films may be characterized as having a GG static COF of less than 5 and a tensile strength in the range of 40-60 MPa.

[0167] Water-soluble films according to the present disclosure may be better understood in view of the following examples, which are intended merely to illustrate the water-soluble films and are not meant to limit their scope in any way. [Example]

[0168] Example 1 Water-soluble films containing water-soluble polyvinyl alcohol, plasticizer, and modified starch were prepared. The film formulations contained a polyvinyl alcohol copolymer with approximately 4% maleic acid modification. Three film formulations further contained approximately 26 phr of plasticizer, approximately 1 phr total of trace amounts of processing aids, such as surfactants and antioxidants, and hydroxypropylated starch with an 80% amylose content and approximately 6% hydroxypropyl modification present at levels of approximately 2.66 phr (1a), approximately 7.98 phr (1b), or 23.94 phr (1c). These films contained approximately 77 wt% (1a), approximately 74 wt% (1b), and approximately 66 wt% (1c) PVOH resin, based on the total weight of the film. Three additional film formulations further contained, in addition to the PVOH resin, about 26 phr of plasticizer, a total of about 1 phr of trace amounts of processing aids, such as surfactants and antioxidants, and hydroxyethylated starch with an amylose content of about 20% and about 2% hydroxypropyl modification, present at levels of about 2.66 phr (1a), about 7.98 phr (1e), or 23.94 phr (1f). These films contained about 77 wt% (1d), about 74 wt% (1e), and about 66 wt% (1f) of PVOH resin by weight, based on the total weight of the film. Films having a thickness of about 75 microns were prepared. The films were tested for cold water solubility at 10°C according to MSTM-205, for tensile strength according to the Tensile Strength Test, and for coefficient of friction according to the Coefficient of Friction Test. Films that dissolved in 100 seconds or less are indicated in Table 1 with a (+), and films that dissolved in more than 100 seconds but less than or equal to 300 seconds are indicated in Table 1 below with a (*). Films that had a tensile strength of about 45 MPa or greater are indicated in Table 1 with a (+), films that had a tensile strength of less than about 45 MPa but at least about 40 MPa or greater are indicated in Table 1 below with a (*), and films that had a tensile strength less than 40 MPa are indicated in Table 1 below with a (-). Films that had a gloss-to-gloss static coefficient of friction of about 1 or less are indicated in Table 1 below with a (+), films that had a gloss-to-gloss coefficient of friction of greater than about 1 but less than about 5 are indicated in Table 1 below with a (*), and films that had a gloss-to-gloss coefficient of friction of greater than about 5 are indicated in Table 1 below with a (-). [Table 1]

[0169] Table 1 shows that films of the present disclosure comprising a mixture of water-soluble polyvinyl alcohol, a plasticizer, and hydroxypropylated starch present in an amount of about 5 phr to about 30 phr demonstrate good cold water solubility, good tensile strength, and an excellent coefficient of friction. Table 1 further shows that films of the present disclosure comprising a mixture of water-soluble polyvinyl alcohol, a plasticizer, and hydroxypropylated starch present in an amount less than about 5 phr demonstrate good cold water solubility, good tensile strength, and an acceptable coefficient of friction. Table 1 further shows that the tensile strength of water-soluble films comprising hydroxypropylated starch is maintained or improved as the starch loading increases from about 2.5 phr to about 24 phr, while the tensile strength of water-soluble films comprising hydroxyethylated starch decreases as the starch loading increases.

[0170] Table 1 shows that films of the present disclosure containing a mixture of water-soluble polyvinyl alcohol, plasticizer, and modified starch having a degree of modification greater than about 2% and present in an amount ranging from about 2.5 phr to about 30 phr demonstrate good cold water solubility, good tensile strength, and an acceptable coefficient of friction, and that when provided in a range of about 5 to about 30 phr, demonstrate a combination of good cold water solubility, good tensile strength, and excellent coefficient of friction. Table 1 further shows that water-soluble films containing modified starch having a degree of modification greater than about 2% and present at low loading levels, e.g., about 12 phr or less, demonstrate an increased coefficient of friction relative to films containing modified starch having a degree of modification greater than 2% at similar loading levels. Table 1 further shows that the tensile strength of water-soluble films containing modified starch having a degree of modification greater than about 2% is maintained or improved as the starch loading is increased from about 2.5 phr to about 24 phr, while the tensile strength of water-soluble films containing modified starch having a degree of modification less than about 2% decreases as the starch loading is increased.

[0171] Thus, Example 1 demonstrates a water-soluble film of the present disclosure comprising a mixture of water-soluble polyvinyl alcohol, a plasticizer, and a hydroxypropylated starch present in an amount of about 5 phr to about 30 phr, and a water-soluble film of the present disclosure comprising a mixture of water-soluble polyvinyl alcohol, a plasticizer, and a modified starch present in an amount ranging from about 5 phr to about 30 phr, having a degree of modification greater than about 2% and having good cold water solubility, good convertibility, and good film-to-film anti-stick properties as evidenced by a low GG coefficient of friction.

[0172] Example 2 Water-soluble films containing water-soluble polyvinyl alcohol, a plasticizer, and unmodified starch were prepared. The film formulation contained a polyvinyl alcohol copolymer with about 4% maleic acid modification. The film formulation further contained about 26 phr of plasticizer, a total of about 1 phr of trace amounts of processing aids, such as surfactants and antioxidants, and unmodified starch present at levels of about 2.66 phr (2a, 2d, 2g, 2j), about 7.98 phr (2b, 2e, 2h, 2k), or 23.94 phr (2c, 2f, 2i, 2l). Three films (2a, 2b, 2c) contained unmodified starch with 1% amylose content, three films (2d, 2e, 2f) contained unmodified starch with 25% amylose content, three films (2g, 2h, 2i) contained unmodified starch with 50% amylose content, and three films (2j, 2k, 2l) contained unmodified starch with 80% amylose content. These films contained approximately 77% by weight (2a, 2d, 2g, 2j), approximately 74% by weight (2b, 2e, 2h, 2k), and approximately 66% by weight (2c, 2c, 2f, 2i, 2l) of PVOH resin, based on the total weight of the film. Films with a thickness of approximately 75 microns were prepared. The films were tested for cold water solubility at 10°C according to MSTM-205, for tensile strength according to the Tensile Strength Test, and for coefficient of friction according to the Coefficient of Friction Test. Films that dissolved in 100 seconds or less are indicated in Table 2 with a (+), and films that dissolved in more than 100 seconds but less than 300 seconds are indicated in Table 2 below with a (*). Films that had a tensile strength of 45 MPa or greater are indicated in Table 2 with a (+), films that had a tensile strength of less than about 45 MPa but at least about 40 MPa or greater are indicated in Table 2 below with a (*), and films that had a tensile strength less than 40 MPa are indicated in Table 2 below with a (-). Films that had a gloss-to-gloss static coefficient of friction of about 1 or less are indicated in Table 2 below with a (+), films that had a gloss-to-gloss coefficient of friction of greater than about 1 but less than about 5 are indicated in Table 2 below with a (*), and films that had a gloss-to-gloss coefficient of friction of greater than about 5 are indicated in Table 2 below with a (-). [Table 2]

[0173] Table 2 shows that water-soluble films according to the present disclosure comprising a water-soluble polyvinyl alcohol, a plasticizer, and an unmodified starch having an amylose content ranging from about 20% to about 80% by weight demonstrate good tensile strength and coefficient of friction when the starch is provided at a low loading level (e.g., about 2 phr to about 5 phr) (2d, 2g). Table 2 further demonstrates that the tensile strength of water-soluble films according to the present disclosure comprising an unmodified starch having an amylose content ranging from about 20% to about 80% by weight decreases with increasing starch loading. Thus, Table 2 demonstrates that water-soluble films according to the present disclosure comprising a mixture of a water-soluble polyvinyl alcohol, a plasticizer, and an unmodified starch having an amylose content ranging from about 20% to about 80% by weight, present in an amount of about 5 phr to about 30 phr, have good convertibility and good film-to-film anti-stick properties as demonstrated by a low GG coefficient of friction.

[0174] Example 3 Water-soluble films containing different polyvinyl alcohol resins were prepared and tested for gloss-to-gloss static coefficient of friction. Each water-soluble film formulation contained polyvinyl alcohol resin in an amount of approximately 74% by weight based on the total weight of the film. The polyvinyl alcohol resins tested included a PVOH homopolymer (3a) with a viscosity of approximately 13 cP and a degree of hydrolysis of approximately 88, a PVOH homopolymer (3b) with a viscosity of approximately 23 CP and a degree of hydrolysis of approximately 88, a polyvinyl alcohol copolymer (3c) with 5% methyl acrylate modification, a polyvinyl alcohol copolymer (3d) with 4% maleic acid modification, a polyvinyl alcohol copolymer (3e) with approximately 2% maleic acid modification, and a polyvinyl alcohol copolymer with approximately 4% 2-acrylamido-2-methylpropanesulfonic acid modification. Each film formulation further contained approximately 26 phr of plasticizer, trace amounts of processing aids, such as surfactants and antioxidants, totaling approximately 1 phr, and starch present at a level of approximately 7.98 phr. The starches tested were unmodified starches (3a) with an amylose content of 50%. 1 ~3e 1 ), or hydroxypropyl-modified starch with an amylose content of about 80% (3a 2 ~3e 2 Films that had a gloss-to-gloss static coefficient of friction of about 1 or less are indicated in Table 3 with a (+), films that had a gloss-to-gloss coefficient of friction of greater than about 1 but less than about 5 are indicated in Table 3 with a (*), and films that had a gloss-to-gloss coefficient of friction of greater than about 5 are indicated in Table 3 with a (-). [Table 3]

[0175] Table 3 shows that the effect of unmodified starch on the gloss-to-gloss coefficient of friction was independent of the type of polyvinyl alcohol or the degree of modification of the polyvinyl alcohol copolymer. Table 3 further shows that hydroxypropylated starch provided acceptable coefficients of friction for all resin types except for methyl acrylate-modified PVOH. Thus, the effect of hydroxypropylated starch does not differ significantly between resin types, except for acrylate-modified PVOH.

[0176] Example 4 Water-soluble films with different starches were prepared and tested for tensile strength and tear strength according to the Tensile Strength Test and Tear Strength Test. Each water-soluble film formulation contained a maleic acid-modified polyvinyl alcohol copolymer in an amount of about 77% by weight based on the total weight of the film. The film formulations also contained about 26 phr of plasticizer, a total of about 1 phr of trace amounts of processing aids, such as surfactants and antioxidants, and starch present at a level of about 2.66 phr. The starches tested included unmodified starch with 1% amylose content (4a), acid-hydrolyzed starch with 1% amylose content (4b), unmodified starch with about 25% amylose content (4c), hydroxyethyl-modified starch with about 25% amylose content (4d), unmodified starch with 50% amylose content (4e), unmodified starch with 80% amylose content (4f), and hydroxypropyl-modified starch with 80% amylose content (4g). Tensile strength and tear strength values ​​are provided in Table 4 below. [Table 4]

[0177] Table 4 shows the tensile strength of the water-soluble film (approximately 45 to 55 N / mm 2) and tear strength (approximately 1300-2000 g / mil) were relatively consistent for all films. Thus, Table 4 demonstrates that amylose content and modification type do not significantly affect the mechanical properties of water-soluble films.

[0178] Example 5 Water-soluble films with different polyvinyl alcohol to starch ratios were prepared and tested for tensile and tear strength as described above. Each water-soluble film formulation contained a polyvinyl alcohol copolymer with maleic acid modification. The film formulations also contained approximately 26 phr of plasticizer, approximately 1 phr total of trace amounts of processing aids, such as surfactants and antioxidants, and unmodified starch with an amylose content of approximately 50%. The amount of PVOH provided in the resin based on the total weight of the film, and the PVOH:starch ratio, were 79 wt% PVOH and 100:0 (5a), 77 wt% and 97:3 (5b), 63 wt% and 80:20 (5c), 47 wt% and 60:40 (5d), or 32 wt% and 40:60 (5e). Films that had a tensile strength of about 45 MPa or greater are designated with a (+) in Table 2, films that had a tensile strength of less than about 45 MPa but greater than or equal to about 40 MPa are designated with a (*) in Table 2, and films that had a tensile strength of less than 40 MPa are designated with a (-) in Table 2 below. Films that had a tear strength of about 1500 g / mil or greater are designated with a (+) in Table 5, films that had a tensile strength of less than about 1500 g / mil but greater than or equal to about 500 g / mil are designated with a (+) in Table 5, and films that had a tensile strength less than 500 g / mil are designated with a (-) in Table 5 below. [Table 5]

[0179] Table 5 shows that when unmodified starch is present in a water-soluble film at a PVOH resin to starch ratio of about 80:20 or greater, the tensile strength and tear strength of the film are dramatically reduced relative to that of an equivalent water-soluble film containing starch at a PVOH resin to starch ratio of less than 80:20, e.g., 97:3.

[0180] Examples 6 to 45 Water-soluble films are prepared having different polyvinyl alcohols present in amounts of about 20% to 95% by weight, different starches present in amounts of about 2.5 to about 30 phr, plasticizers present in amounts of about 10% to about 45% by weight, surfactants present in amounts of about 0.1% to 8.0% by weight, bittering agents present in amounts of about 0.01% to 10% by weight, and bleaching agents present in amounts of 0.01% to 10% by weight. The film formulations are shown in Table 6 below. [Table 6-1] [Table 6-2] [Table 6-3] [Table 6-4] *Selected from one or more of the following: polyethylene glycol, sorbitol, trimethylolpropane, 2-methyl-1,3-propanediol, dulcitol, erythritol, glycerol propylene oxide polymer, hexylene glycol, propylene glycol, triethylene glycol, voranol, xylitol **Selected as one or more of the following: cationic, anionic, zwitterionic A is a PVOH terpolymer of alkyl acrylate monomers. B is a PVOH terpolymer of 2-acrylamido-2-methylpropanesulfonic acid monomer units. C is a PVOH terpolymer of 1.75 mole % monoalkyl maleate monomer units. D is a PVOH terpolymer with 4.00 mole % monoalkyl maleate monomer units. E is a PVOH homopolymer (viscosity 3; DH85). F is a PVOH homopolymer (viscosity 4; DH88). G is a PVOH homopolymer (viscosity 8; DH88). H is a PVOH homopolymer (viscosity 13; DH 88). I is a PVOH homopolymer (viscosity 15, DH79). J is a PVOH homopolymer (viscosity 23; DH 88). K is a PVOH homopolymer (viscosity 32, DH 88). L is a PVOH homopolymer (viscosity 40; DH 88). M is a PVOH homopolymer (viscosity 56, DH 98). N is Casco corn product (25% amylose, native) (ingredient). O is Hylon® V (50% amylose, native) (ingredient). P is Eco-Film® (80% amylose, hydroxypropylated, approximately 2.5% modified) (ingredient).

[0181] Thus, Examples 6-45 illustrate film formulations specifically contemplated for preparing water-soluble films according to the present disclosure.

[0182] Example 46 Pouches are prepared from the water-soluble films of Examples 1-45. Specifically, the pouches are formed from two layers of water-soluble polymeric film sealed at an interface, or by a single film folded over itself and sealed. In both methods, the film defines an inner pouch container sealed at a matte-matte interface, with the glossy side of the film forming the exterior of the pouch.

[0183] The prepared pouches are further filled with a composition comprising a liquid, powder, gel, or combination thereof, including ingredients such as surfactants, bleaches, enzymes, fragrances, dyes or colorants, and / or solvents (for liquid and gel compositions).

[0184] Example 47 The water-soluble film according to the present disclosure was thermoformed into a filled pouch using commercially available high-speed equipment.The pouch demonstrated practical and realistic results for reducing the coefficient of friction of the water-soluble film.In particular, while commercially available films with similar compositions but without the starch of the present disclosure require the application of powder (e.g., talc as described in U.S. Pat. No. 9,290,727) to prevent the formed pouches from sticking together during handling, the pouches made with the film according to the present invention did not require the application of powder to prevent the pouches from sticking together.The benefits observed were due to the film of the present disclosure having a reduced coefficient of friction.

[0185] The foregoing description is set forth for clarity of understanding only, and no unnecessary limitations should be understood therefrom, since modifications within the scope of the invention may be apparent to those skilled in the art.

[0186] All patents, publications, and references cited herein are incorporated by reference in their entirety. In the event of a conflict between the present disclosure and the incorporated patents, publications, and references, the present disclosure shall control. Another aspect of the present invention may be as follows. [1] A water-soluble film comprising a mixture of water-soluble polyvinyl alcohol, a plasticizer, and a starch, wherein the polyvinyl alcohol is present in an amount of about 20% by weight to about 95% by weight based on the total weight of the film, and the starch comprises hydroxypropylated starch present in an amount ranging from about 5 phr to about 30 phr. [2] The water-soluble film according to [1], wherein the hydroxypropylated starch has an amylose content in the range of about 65% to about 95%. [3] The water-soluble film according to [1] or [2], wherein the hydroxypropylated starch has a degree of modification of about 4% to about 8%. [4] The water-soluble film according to any one of [1] to [3] above, wherein the starch is present in an amount ranging from about 6 phr to about 10 phr. [5] The water-soluble film according to any one of [1] to [4], wherein the starch is present in an amount of about 8 phr, and a 76 micron film has a cold water solubility of less than about 90 seconds as measured by MSTM-205. [6] The water-soluble film according to any one of [1] to [3] above, wherein the starch is present in an amount ranging from about 12 phr to about 16 phr. [7] The water-soluble film according to any one of [1] to [6] above, wherein the film has a tensile strength of at least 40 MPa. [8] The water-soluble film according to any one of [1] to [7] above, wherein the film has a tensile strength of more than about 45 MPa. [9] The water-soluble film according to any one of [1] to [8], wherein the film has a gloss-to-gloss static friction coefficient of about 5 or less.

[10] The water-soluble film according to any one of [1] to [9] above, wherein the plasticizer is present in an amount ranging from about 1 phr to about 40 phr.

[11] The water-soluble film according to any one of [1] to

[10] above, wherein the plasticizer is selected from the group consisting of glycerol, propylene glycol, sorbitol, trimethylolpropane, polyethylene glycol, glycerol propylene oxide polymer, 2-methyl-1,3-propanediol, diglycerol, xylitol, and combinations thereof.

[12] The water-soluble film according to any one of [1] to

[11] , wherein the plasticizer is selected from the group consisting of 2-methyl-1,3-propanediol, sorbitol, glycerol, and combinations thereof.

[13] The water-soluble film according to any one of [1] to

[12] , further comprising a surfactant, an antioxidant, a bittering agent, a soil release polymer, an anti-redeposition agent, a chelating agent, a builder, a fragrance, or a combination of the above.

[14] The water-soluble film according to any one of [1] to

[13] , wherein the film is characterized by a reduced gloss-to-gloss static coefficient of friction compared to an equivalent film formulation that does not contain starch.

[15] The water-soluble film according to any one of [1] to

[14] , wherein the polyvinyl alcohol comprises a polyvinyl alcohol homopolymer, an anion-modified polyvinyl alcohol copolymer, or a combination of the above.

[16] A sealed article comprising the water-soluble film of any one of [1] to

[15] above in the form of a pouch defining an internal pouch volume.

[17] The sealed article according to

[16] , further comprising a composition contained in the internal pouch volume.

[18] The sealed article according to

[17] , wherein the composition is a detergent composition.

[19] The sealed article of

[18] , wherein the detergent composition is selected from the group consisting of laundry detergents, dishwashing detergents, hard surface cleaning compositions, fabric softener compositions, shampoos, body washes, and combinations thereof.

[20] A water-soluble film comprising a mixture of water-soluble polyvinyl alcohol, a plasticizer, and a modified starch, wherein the polyvinyl alcohol is present in an amount of about 20% by weight to about 95% by weight based on the total weight of the film, and the modified starch has a degree of modification greater than about 2% and is present in an amount ranging from about 2.5 phr to about 30 phr.

[21] The water-soluble film according to

[20] , wherein the modified starch has a degree of modification of about 4% to about 8%.

[22] The water-soluble film according to

[20] or

[21] , wherein the modified starch has an amylose content in the range of about 65% to about 95%.

[23] The water-soluble film according to any one of

[20] to

[22] , wherein the modified starch includes a hydroxyalkyl modification, and the alkyl has a chain length of 3 or more carbon atoms.

[24] The water-soluble film according to any one of

[20] to

[23] , wherein the polyvinyl alcohol comprises a polyvinyl alcohol selected from the group consisting of a polyvinyl alcohol homopolymer, an anion-modified polyvinyl alcohol copolymer, and a combination of the foregoing.

[25] The water-soluble film according to

[23] , wherein the polyvinyl alcohol comprises an anion-modified polyvinyl alcohol copolymer.

[26] The water-soluble film according to any one of

[20] to

[25] , wherein the starch is present in an amount ranging from about 6 phr to about 10 phr.

[27] The water-soluble film according to any one of

[20] to

[26] , wherein the starch is present in an amount of about 8 phr, and a 76 micron film has a cold water solubility of less than about 90 seconds as measured by MSTM-205.

[28] The water-soluble film according to any one of

[20] to

[25] , wherein the starch is present in an amount ranging from about 12 phr to about 16 phr.

[29] The water-soluble film according to any one of

[20] to

[28] above, wherein the film has a tensile strength of at least 40 MPa.

[30] The water-soluble film according to any one of

[20] to

[29] above, wherein the film has a tensile strength of more than about 45 MPa.

[31] The water-soluble film according to any one of

[20] to

[30] above, wherein the film has a gloss-to-gloss static friction coefficient of 5 or less.

[32] The water-soluble film according to any one of

[20] to

[31] above, wherein the plasticizer is present in an amount ranging from about 1 phr to about 40 phr.

[33] The water-soluble film according to any one of

[20] to

[32] , wherein the plasticizer is selected from the group consisting of glycerol, propylene glycol, sorbitol, trimethylolpropane, polyethylene glycol, glycerol propylene oxide polymer, 2-methyl-1,3-propanediol, diglycerol, xylitol, and combinations thereof.

[34] The water-soluble film according to any one of

[20] to

[33] , wherein the plasticizer is selected from the group consisting of 2-methyl-1,3-propanediol, sorbitol, glycerol, and combinations thereof.

[35] The water-soluble film according to any one of

[20] to

[34] , further comprising a surfactant, an antioxidant, a bittering agent, a soil release polymer, an anti-redeposition agent, a chelating agent, a builder, a fragrance, or a combination of the above.

[36] A water-soluble film according to any one of

[20] to

[35] , wherein the film is characterized by a reduced gloss-to-gloss static coefficient of friction compared to an equivalent film formulation that does not contain starch.

[37] A sealed article comprising the water-soluble film according to any one of

[20] to

[36] above in the form of a pouch defining an internal pouch volume.

[38] The sealed article according to

[37] , further comprising a composition contained in the internal pouch volume.

[39] The sealed article according to

[38] , wherein the composition is a detergent composition.

[40] The sealed article of

[39] , wherein the detergent composition is selected from the group consisting of laundry detergents, dishwashing detergents, hard surface cleaning compositions, fabric softener compositions, shampoos, body washes, and combinations thereof.

[41] A water-soluble film comprising a mixture of water-soluble polyvinyl alcohol, a plasticizer, and unmodified starch, wherein the polyvinyl alcohol is present in an amount of about 20% to about 95% by weight based on the total weight of the film, and the starch has an amylose content in the range of 20% to 80%.

[42] The water-soluble film according to

[41] , wherein the polyvinyl alcohol is present in an amount of about 60% by weight to about 95% by weight based on the total weight of the film.

[43] The water-soluble film according to

[41] or

[42] , wherein the polyvinyl alcohol is present in an amount of about 85% by weight to about 95% by weight based on the total weight of the film.

[44] The water-soluble film according to any one of

[41] to

[43] , wherein the starch is present in an amount ranging from about 2 phr to about 30 phr.

[45] The water-soluble film according to any one of

[41] to

[44] , wherein the starch is present in an amount ranging from about 2 phr to about 5 phr.

[46] The water-soluble film described in any one of

[41] to

[45] above, wherein the film has a gloss-to-gloss static friction coefficient of about 1.

[47] The water-soluble film according to any one of

[41] to

[46] , wherein the starch has an amylose content in the range of about 40% by weight to about 60% by weight.

[48] ​​The water-soluble film according to any one of

[41] to

[47] above, wherein the plasticizer is present in an amount ranging from about 1 phr to about 40 phr.

[49] The water-soluble film according to any one of

[41] to

[48] , wherein the plasticizer is selected from the group consisting of glycerol, propylene glycol, sorbitol, trimethylolpropane, polyethylene glycol, glycerol propylene oxide polymer, 2-methyl-1,3-propanediol, diglycerol, xylitol, and combinations thereof.

[50] The water-soluble film according to any one of

[41] to

[49] , wherein the plasticizer is selected from the group consisting of 2-methyl-1,3-propanediol, sorbitol, and glycerol.

[51] The water-soluble film according to any one of

[41] to

[50] , further comprising a surfactant, an antioxidant, a bittering agent, a soil release polymer, an anti-redeposition agent, a chelating agent, a builder, a fragrance, or a combination of the above.

[52] A water-soluble film according to any one of

[41] to

[51] , wherein the film is characterized by a reduced gloss-to-gloss static coefficient of friction compared to an equivalent film formulation that does not contain starch.

[53] A sealed article comprising the water-soluble film according to any one of

[41] to

[52] above in the form of a pouch defining an internal pouch volume.

[54] The sealed article of

[53] , further comprising a composition contained in the internal pouch volume.

[55] The sealed article according to

[54] , wherein the composition is a detergent composition.

[56] The sealed article of

[55] , wherein the detergent composition is selected from the group consisting of laundry detergents, dishwashing detergents, hard surface cleaning compositions, fabric softener compositions, shampoos, body washes, and combinations thereof.

[57] A water-soluble film comprising a mixture of water-soluble polyvinyl alcohol, a plasticizer, and a hydroxypropyl-modified starch, wherein the polyvinyl alcohol is present in an amount of about 20% by weight to about 95% by weight based on the total weight of the film, the starch has an amylose content in the range of 23% to 95%, and the polyvinyl alcohol comprises unmodified polyvinyl alcohol or an anionically modified polyvinyl alcohol copolymer, with the proviso that the anionic modifier is not an acrylate.

[58] The water-soluble film according to

[57] , wherein the polyvinyl alcohol is present in an amount of about 60% by weight to about 95% by weight based on the total weight of the film.

[59] The water-soluble film according to

[57] or

[58] , wherein the polyvinyl alcohol is present in an amount of about 85% by weight to about 95% by weight based on the total weight of the film.

[60] The water-soluble film according to any one of

[57] to

[59] , wherein the starch is present in an amount ranging from about 5 phr to about 12 phr.

[61] The water-soluble film described in any one of

[57] to

[60] above, wherein the film has a gloss-to-gloss static friction coefficient of about 5 or less.

[62] The water-soluble film described in any one of

[57] to

[61] above, wherein the starch has an amylose content in the range of about 50% by weight to about 95% by weight.

[63] The water-soluble film according to any one of

[57] to

[62] , wherein the hydroxypropyl-modified starch contains more than 2% hydroxypropyl modification.

[64] The water-soluble film according to any one of

[57] to

[63] , wherein the hydroxypropyl-modified starch contains about 4% to about 8% hydroxypropyl modification.

[65] The water-soluble film according to any one of

[57] to

[64] , wherein the plasticizer is present in an amount ranging from about 1 phr to about 40 phr.

[66] The water-soluble film described in any one of

[57] to

[65] , wherein the plasticizer is selected from the group consisting of glycerol, propylene glycol, sorbitol, trimethylolpropane, polyethylene glycol, glycerol propylene oxide polymer, 2-methyl-1,3-propanediol, diglycerol, xylitol, and combinations thereof.

[67] The water-soluble film described in any one of

[57] to

[66] above, wherein the plasticizer is selected from the group consisting of 2-methyl-1,3-propanediol, sorbitol, and glycerol.

[68] The water-soluble film according to any one of

[57] to

[67] , further comprising a surfactant, an antioxidant, a bittering agent, a soil release polymer, an anti-redeposition agent, a chelating agent, a builder, a fragrance, or a combination of the above.

[69] A water-soluble film described in any one of

[57] to

[68] , wherein the film is characterized by a reduced gloss-to-gloss static coefficient of friction compared to an equivalent film formulation that does not contain starch.

[70] A sealed article comprising the water-soluble film of any one of

[57] to

[69] above in the form of a pouch defining an internal pouch volume.

[71] The sealed article of

[70] , further comprising a composition contained in the internal pouch volume.

[72] The sealed article according to

[71] , wherein the composition is a detergent composition.

[73] The sealed article of

[72] , wherein the detergent composition is selected from the group consisting of laundry detergents, dishwashing detergents, hard surface cleaning compositions, fabric softener compositions, shampoos, body washes, and combinations thereof.

[74] The water-soluble film according to any one of [1] to

[15] ,

[20] to

[36] , 41 to 52, and 57 to 69, wherein the starch has an average particle size in the range of 1 micron to approximately 6 microns in a dry state.

[75] The water-soluble film according to any one of [1] to

[15] ,

[20] to

[36] , 41 to 52, 57 to 69, and 74, wherein the starch has a gelatinization temperature of more than 75°C and up to 300°C.

Claims

1. A water-soluble film comprising a mixture of a water-soluble polyvinyl alcohol copolymer having anionic modification, a plasticizer, and unmodified starch, wherein the polyvinyl alcohol copolymer having anionic modification is present in an amount of 60% to 95% by weight based on the total weight of the film, and the starch has an amylose content in the range of 40% to 60% and is present in an amount in the range of 2 phr to less than 5 phr.

2. 10. The water-soluble film of claim 1, wherein the film has a gloss-to-gloss static coefficient of friction of 1.

3. 3. The water-soluble film of claim 1, wherein the polyvinyl alcohol copolymer is present in an amount of 85% to 95% by weight based on the total weight of the film.

4. The water-soluble film of any one of claims 1 to 3, wherein the plasticizer is present in an amount ranging from 1 phr to 40 phr.

5. 5. The water-soluble film of claim 1, wherein the plasticizer is selected from the group consisting of glycerol, propylene glycol, sorbitol, trimethylolpropane, polyethylene glycol, glycerol propylene oxide polymer, 2-methyl-1,3-propanediol, diglycerol, xylitol, and combinations of the foregoing.

6. The water-soluble film of any one of claims 1 to 5, wherein the plasticizer is selected from the group consisting of 2-methyl-1,3-propanediol, sorbitol, glycerol, and combinations thereof.

7. 7. The water-soluble film of claim 1, further comprising a surfactant, an antioxidant, a bittering agent, a soil release polymer, an anti-redeposition agent, a chelating agent, a builder, a fragrance, or a combination of the foregoing.

8. 8. The water-soluble film of any one of claims 1 to 7, wherein the film is characterized by a reduced gloss-to-gloss static coefficient of friction compared to an equivalent film formulation that does not contain starch.

9. 9. The water-soluble film according to claim 1, wherein the starch has an average particle size in the range of 1 micron to 6 microns in a dry state.

10. 10. The water-soluble film according to claim 1, wherein the starch has a gelatinization temperature of more than 75°C and up to 300°C.

11. A sealed article comprising the water-soluble film of any one of claims 1 to 10 in the form of a pouch defining an internal pouch volume.

12. 12. The sealed article of claim 11, further comprising a composition contained within the interior pouch volume.

13. The sealed article of claim 12, wherein the composition is a detergent composition.

14. 14. The sealed article of claim 13, wherein the detergent composition is selected from the group consisting of laundry detergents, dishwashing detergents, hard surface cleaning compositions, fabric softener compositions, shampoos, body washes, and combinations thereof.