Flexible pouches using post-consumer resins

Abstract

The present disclosure provides a flexible pouch. In one embodiment, the flexible pouch includes a first layer structure and a second layer structure. Each layer structure includes (i) an inner liner and (ii) an outer sheath. The first layer structure is superimposed on the second layer structure such that the inner liners face each other. The first layer structure superimposed on the second layer structure defines a common peripheral edge. Each inner liner is composed of a flexible film of a polymeric material. Each outer sheath is composed of a post-consumer recycled (PCR) polymeric material. The PCR polymeric material has a GI200 value greater than 50. The flexible pouch includes a peripheral seal. The peripheral seal extends along at least a portion of the common peripheral edge. The peripheral seal seals the first layer structure to the second layer structure.

Description

[Background technology]

[0001] Social, political, and economic pressures are driving the industry to utilize post-consumer polymeric materials (PCR). The environmental hazards posed by plastic waste are well known. Large-scale societal efforts have been adopted to reclaim and reuse plastic materials, commonly known as post-consumer polymeric materials (PCR). Efforts to reprocess PCR and reincorporate it into usable consumer goods continue to grow.

[0002] In flexible film applications, the inherent variability of PCR makes its use in high performance liquid flexible packaging difficult. The fundamental disposal aspect of PCR means that PCR suffers from unpleasant odors, which can contribute to unpleasant tastes when in contact with food. These drawbacks of PCR make it difficult to use in food contact applications.

[0003] In liquid packaging, the package structure serves two fundamental roles. For example, a flexible pouch for holding a liquid must hold the liquid contents without leakage and with a failure rate of less than 1 leakage per 100,000 flexible packages. Another challenge facing flexible packaging is that in addition to holding the liquid contents, the flexible pouch must have sufficient structural integrity to survive the supply chain. In other words, the flexible pouch must have adequate structure, integrity, and strength to withstand the rigors and stresses of processing, filling, warehousing, distribution, merchandising, and consumer use.

[0004] The art recognizes the need for a flexible pouch that contains PCR and has the ability to function as a flexible pouch, i.e., one that is leak-proof and strong enough to survive and function through the supply chain. Summary of the Invention

[0005] Applicants have discovered a package configuration that is leak-proof and supports liquid contents, which also utilizes PCR.

[0006] The present disclosure provides a flexible pouch. In one embodiment, the flexible pouch includes a first layer structure and a second layer structure. Each layer structure includes (i) an inner liner and (ii) an outer sheath. The first layer structure is superimposed on the second layer structure such that the inner liners face each other. The first layer structure superimposed on the second layer structure defines a common peripheral edge. Each inner liner is composed of a flexible film of a polymeric material. Each outer sheath is composed of a post-consumer recycled (PCR) polymeric material. The PCR polymeric material has a GI200 value greater than 50. The flexible pouch includes a peripheral seal. The peripheral seal extends along at least a portion of the common peripheral edge. The peripheral seal seals the first layer structure to the second layer structure. [Brief explanation of the drawings]

[0007] [Figure 1] FIG. 1 is a top plan view of a flexible pouch in an exploded configuration according to an embodiment of the present disclosure.

[0008] definition Any references to the Periodic Table of the Elements are to the table as published in 1990-1991 by CRC Press, Inc. References to groups of elements in this table are to the new notation for numbering groups.

[0009] For purposes of United States patent practice, the contents of any referenced patent, patent application, or publication are incorporated by reference in their entirety (or the equivalent United States version thereof is so incorporated by reference), particularly with respect to the disclosure of definitions (to the extent not inconsistent with any definitions specifically provided in this disclosure) and general knowledge in the art.

[0010] Numerical ranges disclosed herein include all values ​​from the lower limit to the upper limit, inclusive. For ranges containing explicit numbers (e.g., 1 or 2, or 3 to 5, or 6, or 7), any subrange between any two explicit numbers (e.g., 1 to 2, 2 to 6, 5 to 7, 3 to 7, 5 to 6, etc.) is also included.

[0011] Unless stated to the contrary or customarily stated otherwise in the art, or unless otherwise indicated by context, all parts and percentages are by weight and all test methods are current as of the filing date of this disclosure.

[0012] As used herein, the term "blend" or "polymer blend" refers to a blend of two or more polymers. Such blends may or may not be miscible (not phase separated at the molecular level). Such blends may or may not be phase separated. Such blends may or may not contain one or more domain configurations as determined from transmission electron spectroscopy, light scattering, X-ray scattering, and other methods known in the art.

[0013] The term "composition" refers to a mixture of materials that comprise the composition, as well as reaction products and decomposition products formed from the materials of the composition.

[0014] The terms "comprising," "including," "having," and their derivatives are not intended to exclude the presence of any additional component, step, or procedure, whether specifically disclosed or not. For the avoidance of doubt, all compositions claimed through the use of the term "comprising" may include any additional additive, adjuvant, or compound, whether polymeric or not, unless stated to the contrary. In contrast, the term "consisting essentially of" excludes any other component, step, or procedure from the scope of any succeeding description, except those that are not essential to operability. The term "consisting of" also excludes any component, step, or procedure not specifically delineated or listed. The term "or," unless otherwise stated, refers to the listed members individually as well as in any combination. The use of the singular includes the use of the plural, and vice versa.

[0015] An "ethylene-based polymer" is a polymer containing greater than 50 weight percent (wt%) polymerized ethylene monomers (based on the total amount of polymerizable monomers), and may optionally contain at least one comonomer. Ethylene-based polymers include ethylene homopolymers and ethylene copolymers (meaning units derived from ethylene and one or more comonomers). The terms "ethylene-based polymer" and "polyethylene" may be used interchangeably. Non-limiting examples of ethylene-based polymers (polyethylenes) include low-density polyethylene (LDPE) and linear polyethylene. Non-limiting examples of linear polyethylene include linear low-density polyethylene (LLDPE), ultra-low-density polyethylene (ULDPE), very low-density polyethylene (VLDPE), multicomponent ethylene-based copolymers (EPE), ethylene / α-olefin multiblock copolymers (also known as olefin block copolymers (OBC)), substantially linear or linear plastomers / elastomers, and high-density polyethylene (HDPE). Generally, polyethylene can be produced in gas-phase fluidized-bed reactors, liquid-phase slurry process reactors, or liquid-phase solution process reactors using heterogeneous catalyst systems such as Ziegler-Natta catalysts, or homogeneous catalyst systems containing Group 4 transition metals and ligand structures such as metallocene, nonmetallocene metal centers, heteroaryl, heteroatom aryloxy ethers, and phosphinimine. Combinations of heterogeneous and / or homogeneous catalysts can also be used in either single-reactor or dual-reactor configurations.

[0016] "Ethylene plastomer / elastomer" refers to a polymer that contains units derived from ethylene and at least one C3-C 10These are substantially linear or linear ethylene / α-olefin copolymers containing a uniform distribution of short chain branches comprising units derived from α-olefin comonomers. The ethylene plastomer / elastomers have a density of 0.860 g / cc to 0.917 g / cc. Non-limiting examples of ethylene plastomer / elastomers include AFFINITY™ plastomers and elastomers (available from The Dow Chemical Company), EXACT™ plastomers (available from ExxonMobil Chemical), Tafmer™ (available from Mitsui), Nexlene™ (available from SK Chemicals Co.), and Lucene™ (available from LG Chem Ltd.).

[0017] "High density polyethylene" (or "HDPE") is a polymer consisting of ethylene homopolymer or at least one C4-C6 10 An ethylene / α-olefin copolymer with an α-olefin comonomer or a C4-C8 α-olefin comonomer has a density of 0.940 g / cc, or 0.945 g / cc, or 0.950 g / cc, or 0.953 g / cc to 0.955 g / cc, or 0.960 g / cc, or 0.965 g / cc, or 0.970 g / cc, or 0.975 g / cc, or 0.980 g / cc. HDPE can be a unimodal or multimodal copolymer. A "unimodal ethylene copolymer" is an ethylene / C4-C8 copolymer having one distinct peak in gel permeation chromatography (GPC) indicating a molecular weight distribution. 10 It is an α-olefin copolymer. A "multimodal ethylene copolymer" is an ethylene / C4-C copolymer that has at least two distinct peaks in the GPC showing the molecular weight distribution. 10It is an α-olefin copolymer. Multimodal includes copolymers with two peaks (bimodal) and copolymers with three or more peaks. Non-limiting examples of HDPE include DOW™ high density polyethylene (HDPE) resin (available from The Dow Chemical Company), ELITE™ reinforced polyethylene resin (available from The Dow Chemical Company), CONTINUUM™ bimodal polyethylene resin (available from The Dow Chemical Company), LUPOLEN™ (available from LyondellBasell), and HDPE products from Borealis, Ineos, and ExxonMobil.

[0018] An "interpolymer" is a polymer prepared by the polymerization of at least two different monomers. This generic term includes copolymers, which are commonly used to refer to polymers prepared from two different monomers, and polymers prepared from three or more different monomers, such as terpolymers, tetrapolymers, etc.

[0019] "Linear low density polyethylene (or "LLDPE")" refers to a polymer that contains units derived from ethylene and at least one C3-C6 10 LLDPE is a linear ethylene / α-olefin copolymer containing a heterogeneous distribution of short chain branches, including units derived from α-olefins or C4-C8 α-olefin comonomers. LLDPE, in contrast to conventional LDPE, is characterized by little, if any, long chain branching. LLDPE has a density of 0.910 g / cc to less than 0.940 g / cc. Non-limiting examples of LLDPE include TUFLIN™ linear low density polyethylene resin (available from The Dow Chemical Company), DOWLEX™ polyethylene resin (available from The Dow Chemical Company), and MARLEX™ polyethylene (available from Chevron Phillips).

[0020] "Low density polyethylene" (or "LDPE") refers to ethylene homopolymer or to a polymer having a density between 0.915 g / cc and 0.940 g / cc and at least one C3-C6 long chain branch containing a broad MWD. 10 It consists of ethylene / α-olefin copolymers containing α-olefins or C4-C8 α-olefins. LDPE is typically produced by high-pressure free-radical polymerization (tubular reactor or autoclave using a free-radical initiator). Non-limiting examples of LDPE include MarFlex™ (Chevron Phillips), LUPOLEN™ (LyondellBasell), and LDPE products from Borealis, Ineos, ExxonMobil, and others.

[0021] "Multicomponent ethylene-based copolymers" (or "EPEs") are copolymers containing units derived from ethylene and at least one C3-C6 copolymer, such as those described in patent documents U.S. Pat. Nos. 6,111,023, 5,677,383, and 6,984,695. 10 The EPE resins contain units derived from an α-olefin or a C4 to C8 α-olefin comonomer. The EPE resins have a density of 0.905 g / cc to 0.962 g / cc. Non-limiting examples of EPE resins include ELITE™ reinforced polyethylene (available from The Dow Chemical Company), ELITE AT™ advanced technology resin (available from The Dow Chemical Company), SURPASS™ polyethylene (PE) resin (available from Nova Chemicals), and SMART™ (available from SK Chemicals Co.).

[0022] An "olefin-based polymer" or "polyolefin" is a polymer that contains more than 50 weight percent polymerized olefin monomers (based on the total amount of polymerizable monomers) and may optionally include at least one comonomer. Non-limiting examples of olefin-based polymers include ethylene-based polymers or propylene-based polymers.

[0023] A "polymer" is a compound prepared by polymerizing monomers, whether of the same or different types, that provide multiple and / or repeating "units" or "mer units" that, in polymerized form, constitute the polymer. Thus, the generic term "polymer" encompasses the term "homopolymer," which is commonly used to refer to a polymer prepared from only one type of monomer, and the term "copolymer," which is commonly used to refer to a polymer prepared from at least two types of monomer. It also encompasses all forms of copolymers, e.g., random, block, etc. The terms "ethylene / α-olefin polymer" and "propylene / α-olefin polymer" refer to the aforementioned copolymers prepared from polymerizing ethylene or propylene with one or more additional polymerizable α-olefin monomers, respectively. While polymers are often referred to as "made of" one or more specific monomers, "based on" a particular monomer or monomer type, "containing" a particular monomer content, etc., it is noted that in this context, the term "monomer" is understood to refer to the polymerized residue of a particular monomer, not to the unpolymerized species. Generally, polymers herein are referred to in terms of "units" that are the polymerized form of the corresponding monomers.

[0024] A "propylene-based polymer" is a polymer containing more than 50 weight percent polymerized propylene monomers (based on the total amount of polymerizable monomers) and may optionally include at least one comonomer. Propylene-based polymers include propylene homopolymers and propylene copolymers (meaning units derived from propylene and one or more comonomers). The terms "propylene-based polymer" and "polypropylene" may be used interchangeably. Non-limiting examples of suitable propylene copolymers include propylene impact copolymers and propylene random copolymers.

[0025] "Ultra-low density polyethylene (or "ULDPE")" and "very low density polyethylene (or "VLDPE")" are each polyethylenes containing units derived from ethylene and at least one C3-C 10 They are linear ethylene / α-olefin copolymers containing a heterogeneous distribution of short chain branches, including units derived from α-olefin comonomers. ULDPE and VLDPE have densities ranging from 0.885 g / cc to 0.915 g / cc, respectively. Non-limiting examples of ULDPE and VLDPE include ATTANE™ ultra-low density polyethylene resins (available from The Dow Chemical Company) and FLEXOMER™ very low density polyethylene resins (available from The Dow Chemical Company).

[0026] Test Method Density is measured according to ASTM D792, Method B. Results are reported in grams per cubic centimeter (g / cc).

[0027] Differential Scanning Calorimetry (DSC). Differential scanning calorimetry (DSC) can be used to measure the melting, crystallization, and glass transition behavior of polymers over a wide temperature range. For example, a TA Instruments Q1000 DSC equipped with a refrigerated cooling system (RCS) and an autosampler is used to perform this analysis. A nitrogen purge gas flow rate of 50 ml / min is used during testing. Each sample is melt-pressed into a thin film at approximately 175°C, and the molten sample is then air-cooled to room temperature (approximately 25°C). A 3-10 mg, 6 mm diameter specimen is extracted from the cooled polymer, weighed, placed in a light (approximately 50 mg) aluminum pan, and crimped shut. Analysis is then performed to determine its thermal properties.

[0028] The thermal behavior of the sample is determined by ramping the sample temperature to generate a heat flow vs. temperature profile. First, the sample is rapidly heated to 180°C and held isothermal for 3 minutes to remove its thermal history. Next, the sample is cooled to -40°C at a cooling rate of 10°C / min and held isothermal at -40°C for 3 minutes. The sample is then heated to 180°C at a heating rate of 10°C / min (this is the "second heat" ramp). A cooling curve and a second heating curve are recorded. The cooling curve is analyzed by setting a baseline endpoint from the onset of crystallization to -20°C. The heating curve is analyzed by setting a baseline endpoint from -20°C to the end of melting. The values ​​determined are the extrapolated onset of melting, Tm, and the extrapolated onset of crystallization, Tc. The heat of fusion (H) (in joules per gram) is f ), and the % crystallinity of the polyethylene sample calculated using the following equation: % crystallinity = ((H f ) / 292 J / g) x 100. The glass transition temperature, Tg, is determined from a DSC heating curve with an increased liquid heat capacity over half of the sample, as described in Bernhard Wunderlich, The Basis of Thermal Analysis, in Thermal Characterization of Polymeric Materials 92, 278-279 (Edith A. Turi ed., 2d ed. 1997). Baselines are drawn below and above the glass transition region and extrapolated through the Tg region. The temperature at which the heat capacity of the sample is midway between these baselines is the Tg.

[0029] GI200 is defined as the sum of the areas of all gels with a diameter greater than 200 microns. GI200 is determined using an OCS FSA-100 line gel counter, consisting of an illumination unit, a CCD detector, and an image processor with gel counter software version 5.0.4.6, available from OCS Optical Control Systems GmbH, or equivalent. The strips are 24.6 cm 3 film, or 0.324 m for a 76 μιη film thickness 225 pieces are analyzed, with the definition:

[0030] Gel count: Gel count is the number of gels detected by a gel camera. The counted gels are further classified into the following categories based on the area of ​​the measured circle equivalent diameter: less than 100 microns, 100-150 microns, 150-200 microns, 200-400 microns, 400-800 microns, 800-1600 microns, and more than 1600 microns. GI200 is the number of gels counted by the number of gels detected by a gel camera. The number of gels counted ... 3 Gel per film 1200 mm 2 The gel diameter is determined as the diameter of a circle with an equivalent area. One analysis cycle is 24.6 cm 3 of film is inspected. The corresponding area is 0.324 m for a film thickness of 76 microns. 2 and 0.647 m for a 38 micron film thickness. 2 Alternatively, gel ppm is measured using the technique described above, and GI200 is approximately gel ppm divided by 3.

[0031] The melt flow rate (MFR) is measured in g / 10 min according to ASTM D1238 (230°C / 2.16 kg).

[0032] Melt index (MI) (I2) in g / 10 min is measured according to ASTM D1238 (190°C / 2.16 kg).

[0033] Yellowness Index (YI) of granular and pelletized polyethylene is achieved using a Hunter Color FlexEZ™ spectrometer in accordance with ASTM procedure D6290, Standard Test Method for Color Determination of Plastic Pellets, and E313, Standard Practice for Calculating Yellowness and Whiteness Indices from Instrumentally Measured Color Coordinates. DETAILED DESCRIPTION OF THE INVENTION

[0034] The present disclosure provides a flexible pouch. In one embodiment, the flexible pouch includes a first layer structure and a second layer structure. Each layer structure includes (i) an inner liner and (ii) an outer sheath. The first layer structure is superimposed on the second layer structure such that the inner liners face each other. The first layer structure superimposed on the second layer structure defines a common peripheral edge. Each inner liner is composed of a flexible film of a polymeric material. Each outer sheath is composed of a post-consumer recycled (PCR) polymeric material. The PCR polymeric material has a GI200 value greater than 50. The flexible pouch includes a peripheral seal. The peripheral seal extends along at least a portion of the common peripheral edge. The peripheral seal seals the first layer structure to the second layer structure.

[0035] The flexible pouch includes a first layer structure and a second layer structure. As used herein, the term "layer structure" refers to a structure comprised of at least two distinct structures: (i) an inner liner and (ii) an outer sheath. The inner liner and outer sheath are each flexible, flat, and individual sheet-like articles comprised of extruded or cast thermoplastic material, each having a consistent, uniform thickness of between 0.25 millimeters (mm) and 6.35 mm (250 mils).

[0036] Each layered component (i.e., the inner liner and outer sheath) can be composed of a single polymeric material or a blend of two or more polymeric materials, and each layered component has either a monolayer or multilayer configuration (coextruded multilayer and / or laminated multilayer).

[0037] The first layer structure is superimposed on the second layer structure with the inner liners facing each other. The first layer structure superimposed on the second layer structure defines a common peripheral edge. The common peripheral edge defines the peripheral shape of the flexible pouch. The peripheral shape of the flexible pouch can be polygonal (e.g., triangular, square, rectangular, rhombus, pentagonal, hexagonal, heptagonal, octagonal, etc.) or oval (e.g., oval, elliptical, or circular).

[0038] The first layer structure and the second layer structure each include an inner liner. The first layer structure includes a first inner liner. The second layer structure includes a second inner liner. Each inner liner is made of a flexible film made of a polymer material. Each inner liner is elastic, flexible, deformable, and pliable.

[0039] In one embodiment, each inner liner is a flexible multilayer film having at least three layers. The flexible multilayer film has an A / B / A layer structure. Layer A is a sealant layer comprised of LLDPE. Layer B is an abuse layer comprised of an ethylene-based polymer. The A / B / A flexible multilayer film has a layer volume of 20 / 60 / 20, and the flexible multilayer film has a thickness of 10 or 20 microns to 40 or 80 microns.

[0040] In one embodiment, each inner liner flexible multilayer film has an A / B / C / B / A layer structure. Layer A is a sealant layer comprised of LLDPE. Layer B is a tie layer comprised of a maleic anhydride-grafted ethylene-based polymer or polymer blend. Layer C is a barrier layer such as polyamide or ethylene-vinyl alcohol (EVOH). The A / B / C / B / A flexible multilayer film has a layer volume of 15 / 5 / 60 / 5 / 15, and the flexible multilayer film has a thickness from 10 microns or 20 microns to 40 microns or 80 microns. The barrier layer may function to prevent oxygen and / or fragrance transmission.

[0041] The first layer structure and the second layer structure each include an outer sheath. The first layer structure includes a first outer sheath. The second layer structure includes a second outer sheath. Each outer sheath is composed of a post-consumer recycled (PCR) polymer material. The PCR used to make the outer sheaths has a GI200 value of greater than 50.

[0042] The term "post-consumer resin" or "PCR" refers to polymeric materials previously used in consumer or industrial packaging. In other words, PCR is waste plastic. PCR is typically collected from recycling programs and recycling plants. PCR typically requires additional cleaning and processing before it can be reintroduced into the manufacturing line. PCR may include one or more of the following: ethylene-based polymers, propylene-based polymers, polyesters, poly(vinyl chloride), polystyrene, acrylonitrile butadiene styrene, polyamides, ethylene vinyl alcohol, ethylene vinyl acetate, or polyvinyl chloride. PCR may contain one or more contaminants. The contaminants may be the result of the use of the polymeric material before it is modified for reuse. In some embodiments, the contaminants may include paper, ink, food residue, or other recycled materials in addition to the polymer resulting from the recycling process. PCR is understood to include post-industry recycled (PIR) resins.

[0043] PCR differs from virgin polymeric materials. Because PCR has undergone an initial heating and molding process, PCR is not a "virgin" polymeric material. A "virgin polymeric material" is a polymeric material that has not undergone or been subjected to a heating or molding process. PCR resins have different physical, chemical, and flow properties compared to virgin polymeric resins.

[0044] In one embodiment, the PCR is polyethylene-PCR. Non-limiting examples of sources of polyethylene-PCR include HDPE packaging, such as bottles (milk jugs, juice containers), and LDPE / LLDPE packaging, such as films. Polyethylene-PCR also contains residues from its original use, such as paper, adhesives, inks, nylon, ethylene vinyl alcohol (EVOH), polyamide (PA), polyethylene terephthalate (PET), and other odor-causing agents.

[0045] Non-limiting examples of suitable PCRs include those sold by Envision Plastics (North Carolina, USA) under the trade names EcoPrime™, PRISMA™, Natural HDPE PCR Resins, and Mixed Color and Black HDPE PCR Resins, as well as PCRs sold under the trade names KWR101-150, KWR101-150-M5-BLK, KWR101-150-M10 BLK, KWR102-8812 BLK, KWR102, KWR102LVW, KWR105, KW620, KWR102-M4, KWR-105M2, KWR105M4, and KWR621. Examples include PCRs sold by KW Plastics (Alabama, USA) under the designations FDA, KWR621-20-FDA, KW308A, KW621, KW621-T10, KW621-T20, KW622-20, KW622-35, KW627C, KW1250G, and KWBK10-NB.

[0046] In one embodiment, the outer sheath is composed of 100% PCR by weight, where the weight percentage is based on the total weight of the outer sheath.

[0047] In one embodiment, in addition to the PCR, the outer sheath may optionally include an olefin-based polymer. The olefin-based polymer may be a propylene-based polymer or an ethylene-based polymer. Non-limiting examples of propylene-based polymers include propylene copolymers, propylene homopolymers, and combinations thereof. In one embodiment, the propylene-based polymer is a propylene / α-olefin copolymer. Non-limiting examples of suitable α-olefins include C2 and C4-C 20 α-olefins or C4-C 10 The olefin-based polymer may be an α-olefin or a C4-C8 α-olefin. Representative α-olefins include ethylene, 1-butene, 1-pentene, 1-hexene, 1-heptene, and 1-octene. In one embodiment, the olefin-based polymer is a virgin olefin-based polymer.

[0048] In one embodiment, the propylene / α-olefin copolymer is a propylene / ethylene copolymer containing greater than 50 wt%, or 51 wt%, or 55 wt%, or 60 wt% to 70 wt%, or 80 wt%, or 90 wt%, or 95 wt%, or 99 wt% propylene-derived units, based on the weight of the propylene / ethylene copolymer. The propylene / ethylene copolymer contains the reciprocal amount of ethylene-derived units, or less than 50 wt%, or 49 wt%, or 45 wt%, or 40 wt% to 30 wt%, or 20 wt%, or 10 wt%, or 5 wt%, or 1 wt%, or 0 wt% ethylene-derived units, based on the weight of the propylene / ethylene copolymer.

[0049] In one embodiment, the olefin-based polymer is an ethylene-based polymer. The ethylene-based polymer can be an ethylene homopolymer or an ethylene / α-olefin copolymer.

[0050] In one embodiment, the ethylene-based polymer is an ethylene / α-olefin copolymer. Non-limiting examples of suitable α-olefins include C3-C 20 α-olefins or C4-C 10 Examples of α-olefins include propylene, 1-butene, 1-pentene, 1-hexene, 1-heptene, and 1-octene.

[0051] In one embodiment, the outer sheath contains 5%, or 20%, or 30%, or 40%, or 50% to 60%, or 70%, or 80%, or 95% by weight of PCR and the reciprocal of the virgin olefin-based polymer, or 95%, or 80%, or 70%, or 60%, or 50% to 40%, or 30%, or 20%, or 5% by weight of virgin olefin-based polymer. The weight percentages are based on the total weight of the outer sheath.

[0052] The outer sheath, comprised of PCR, has a GI200 value of greater than 50. In one embodiment, the PCR of the outer sheath has a GI200 value of 100, or 200, or 500-1000, or 5000, or 10,000. In further embodiments, the PCR has a GI200 value of 100-10,000, or 200-5000, or 300-1600, or 300-1000.

[0053] In one embodiment, the outer sheath is surface printed and / or coated with a high temperature lacquer to protect the ink or to provide thermal protection to the surface during the heat sealing process.

[0054] In one embodiment, each layer structure comprises 10 volume percent (vol%) to 90 volume% of the outer sheath and the reciprocal volume percent of the inner liner, or 90 volume% to 10 volume% of the inner liner, where the volume percent is based on the total volume of the layer structure.

[0055] In one embodiment, each layer structure comprises greater than 50% to 95% by volume of outer sheath and the reciprocal volume percent of inner liner, or less than 50% to 5% by volume of inner liner.

[0056] The flexible pouch includes a peripheral seal that extends along at least a portion of the common peripheral edge. In one embodiment, the peripheral seal extends along the entire common peripheral edge. The peripheral seal forms a storage compartment within the flexible pouch.

[0057] In one embodiment, the flexible pouch includes a fitment disposed between the first layer structure and the second layer structure along a peripheral seal that hermetically seals the fitment between the first layer structure and the second layer structure.

[0058] The peripheral seal seals or bonds the first layer structure to the second layer structure. The peripheral seal can be formed by ultrasonic sealing, heat sealing, adhesive sealing, or a combination thereof. The peripheral seal includes opposing sealing layers of each inner liner in direct contact with one another.

[0059] In one embodiment, the peripheral seal is formed by a heat sealing procedure. As used herein, the term "heat sealing" refers to the act of placing two layer structures between opposing heat sealing bars, moving the heat sealing bars toward each other to sandwich the layer structures, and applying heat and pressure to the layer structures, so that the opposing inner surfaces (sealing layers) of the layer structures come into contact, melt, form a heat seal, or weld, and the layer structures adhere to each other. Heat sealing includes structures and mechanisms suitable for moving the sealing bars toward and away from each other to perform the heat sealing procedure. As a result, the term "heat seal" as used herein refers to a weld formed between two layer structures subjected to a heat sealing process, where the weld is composed of melted polymer material from the first heat-sealed layer structure and also from the second heat-sealed layer structure, and the melted polymer material then solidifies.

[0060] In one embodiment, the peripheral seal comprises a heat seal between opposing inner liners. In a further embodiment, each inner liner is a flexible multilayer film having an A / B / A configuration. The heat seal is a weld formed between the A layer material of the first inner liner and the A layer material of the second inner liner.

[0061] In one embodiment, the peripheral seal comprises a heat seal between the outer sheath and its respective inner liner. The heat seal comprises a weld between the first inner liner and the first outer sheath. The heat seal also comprises a weld between the second inner liner and the second outer sheath.

[0062] In one embodiment, when the perimeter seal is viewed in cross section, it has the following layer structure: first outer sheath / first inner liner / second inner liner / second outer sheath, where " / " represents the interface of the layers. It is understood that there is a weld at each interface of the layers " / ".

[0063] In one embodiment, the peripheral seal includes a first outer sheath heat sealed to a first inner liner, a first inner liner heat sealed to a second inner liner, and a second inner liner heat sealed to a second outer sheath.

[0064] In one embodiment, the peripheral seal is the only seal, or is otherwise the only seal, between the inner liner and its respective outer sheath. There is no adhesive contact at the outer sheath / inner liner interface other than the peripheral seal. The inner surface of the outer sheath, other than the peripheral seal, contacts or directly contacts the outer surface of its respective inner liner, and direct contact is the absence or otherwise of adhesive contact. As used herein, the term "adhesive contact" refers to the contact and securing mechanism between films relative to one another. As used herein, the terms "direct contact" or "in direct contact," or similar terms, refer to a film layer configuration in which a first film layer is positioned directly adjacent to a second film layer, the first film layer contacts the second film layer, and there are no intervening layers and / or structures between the first and second film layers. In this manner, a gap or void exists between the inner liner and its respective outer sheath, except for the peripheral seal.

[0065] The peripheral seal seals the first layer structure to the second layer structure, and a gap between each outer sheath and its respective inner liner exists in areas of the flexible pouch where the peripheral seal does not extend. Stated differently, the gap exists at the outer sheath-inner liner interface, excluding the peripheral seal. The gap or void that exists at the outer sheath-inner liner interface between the outer sheath and inner liner in areas of the flexible pouch other than the peripheral seal is free of air, allowing movement and / or separation between the outer sheath and inner liner.

[0066] The flexible pouch has adhesion (compared to welds) only at the outer sheath / inner liner interface between the layer structure and at the liner / liner interface at the peripheral seal. In the flexible pouch, the interfaces of layers not disposed at the peripheral seal are free of adhesion. Gaps or voids exist at the outer sheath / inner liner interface. Gaps or voids exist between the inner liner / inner liner interfaces other than at the peripheral seal. Applicant has discovered that the gaps (i) advantageously provide a barrier between the outer sheath and its respective inner liner and (ii) also contribute to the drop strength of the flexible pouch.

[0067] In one embodiment, each layer structure includes a printed film. The printed film directly contacts the outer surface of the PCR sheath. The printed film covers the PCR sheath. Consequently, the printed film is the outermost layer of each layer structure and the flexible pouch. When the printed film is provided, the PCR sheath is not visible when an observer looks at the flexible pouch or is otherwise observed. Non-limiting examples of materials suitable for the printed film include ethylene-based polymers such as polyethylene terephthalate (PET), biaxially oriented polypropylene (BOPP), and HDPE.

[0068] When a printed film is provided, the peripheral seal of the flexible pouch includes a heat seal between the printed film and its respective PCR sheath, in addition to a heel seal between the PCR sheath and its respective inner liner. The heat seal includes a weld between the first inner liner and the first PCR sheath, and a weld between the PCR sheath and the first printed film. The heat seal also includes a weld between the second inner liner and the second PCR sheath, and a weld between the second PCR sheath and the second printed film.

[0069] When a printed film is provided, the peripheral seal when viewed in cross section has the following layer configuration: first printed film / first PCR sheath / first inner liner / second inner liner / second PCR sheath / second printed film, with " / " representing the layer interface. It is understood that there is a weld at each layer interface " / ".

[0070] In one embodiment, the flexible pouch contains a food product within the storage compartment. The food product is in direct contact with one or both of the inner liners. The food product does not contact the outer sheath. The gap at the outer sheath-inner liner interface provides an additional barrier between the PCR of the outer sheath and the food product within the storage compartment. The food product can be a solid and / or liquid substance. Non-limiting examples of suitable liquid food products include industrial cleaning chemicals, industrial additives, solvents, liquid soap, or food contents such as beverages, sauces, condiments (ketchup, mustard, mayonnaise), butter, and baby food. Non-limiting examples of suitable solid food products include industrial granules, powdered soap, salt crystals, or food-related products such as powdered sugar, grains, meat chunks, granulated solids, animal feed, and pet food.

[0071] The present disclosure provides another flexible pouch. In one embodiment, the flexible pouch includes a first layer structure and a second layer structure. Each layer structure includes a PCR layer, a foam layer, and a seal layer. The foam layer is disposed between the PCR layer and the seal layer. The PCR layer is the outermost layer. The seal layer is the innermost layer. The first layer structure and the second layer structure are superimposed on each other with the seal layers facing each other. The superimposed first layer structure and second layer structure define a common peripheral edge. The PCR has a GI200 value greater than 50. The flexible pouch includes a peripheral seal. The peripheral seal extends along at least a portion of the common peripheral edge. The peripheral seal seals the first layer structure to the second layer structure.

[0072] The foam layer can be a separate layer, or the foam layer can be integrated into the PCR layer.

[0073] In one embodiment, the foam layer is composed of foamed PCR, which may be the same as or different from the PCR of the outermost layer.

[0074] In one embodiment, each layer structure is a coextruded structure in which the PCR, foam, and inner layer are coextruded together. When the layer structure is a coextruded structure with a foam layer, each layer structure has the following layer configuration: outer PCR / foam / inner liner, where " / " represents the interface of the layers.

[0075] In one embodiment, the foam layer is generated in situ by utilizing or introducing a blowing agent into the polymeric material that is coextruded between the outer PCR layer and the inner liner layer during the coextrusion process. Each layer structure has the following layer configuration: outer PCR / (in situ) foam / inner liner, where " / " represents the interface of the layers.

[0076] By way of example, and not limitation, several embodiments of the present disclosure are described in detail below in the following examples. [Example]

[0077] The materials used in the examples are provided in Table 1 below. [Table 1]

[0078] A. Preparation of Inner Liner / Outer Sheath 1. Inner liner a. Inner liner structure—a three-layer multilayer film in which both outer layers are sealant layers and the core layer is a highly puncture-resistant polymer. A three-layer film with a layer structure A / B / A with a layer ratio of 20 / 60 / 20, where each A layer is a sealant layer composed of AFFINITY 1146G and the B layer is composed of LLDPE INNATE ST50, was prepared using a conventional blown film line. The total film thickness of the inner liner is 25 microns (1 mil).

[0079] b. Process for manufacturing the inner liner - An Alpine 7-layer extrusion line was used, where layers 1 and 2 were each 10% layers containing AFFINITY 1146G, layers 3, 4, and 5 were 20% layers containing INNATE ST50, and layers 6 and 7 were each 10% layers containing AFFINITY 1146G.

[0080] 2.Outer sheath a. PCR outer sheath—A monolayer film was produced using a conventional blown film process, with formulation-free polymers used to produce the desired film. In most cases, the PCR pellets were dried using an oven.

[0081] b. Drying of PCR Pellets - Approximately 50 pounds of PCR resin was each placed in a Conair Franklin "Closed Loop" Dehumidifying Dryer, a forced air oven dryer, for over 12 hours to remove moisture. The drying air temperature was set at 60°C (140°F). The dried PCR pellets were stored in moisture-proof bags until use.

[0082] c. Process for manufacturing the outer sheath—A LabTech 5-layer blown film extrusion line was used, with all extruder feeds filled with unmodified PCR pellets. The blow-up ratio was 2.5, and the final film thickness of each single-layer outer sheath was 150 microns (6 mils).

[0083] B. Pouch manufacturing An inner liner was cut to a rectangle measuring 28 cm (11 inches) by 51 cm (20 inches). An outer sheath was cut to a rectangle measuring 28 cm (11 inches) by 51 cm (20 inches). Two inner liners and two outer sheaths were stacked and aligned directly on top of each other with sealing layers A of the inner liners facing each other. The inner liners / outer sheaths were stacked and positioned to define a common peripheral edge according to the following order shown in Structure A below: Structural formula (A) i. Layer 1 (bottom layer) - outer sheath ii. Layer 2—Inner Liner Layer iii. Layer 3—Inner Liner Layer iv. Layer 4 (top layer) - outer sheath

[0084] An Impulse Heat Sealer was used to seal the inner liner and outer sheath of Structure A together, forming a peripheral seal along their common peripheral edge. The degree of sealing was adjusted with a dial until the inner liner / outer sheath were sealed together without burning at the sealing point. By forming the peripheral seal, Structure A was formed into a flexible pouch with a storage compartment and a non-sealed area along its common peripheral edge. The non-sealed area along the common peripheral edge is an opening for introducing contents into the storage compartment.

[0085] C. Filling flexible pouches The flexible pouch was filled with water through the opening shown in Figure 1. 5.5 kg of water was added to the flexible pouch so that the water was added between the two inner sealant layers. The design of the flexible pouch ensures that the water does not contact the outer sheath at any point. After filling was complete, the opening of the flexible pouch was sealed using a pressure-sensitive adhesive. The flexible pouch has no adhesive contact between the inner liner and outer sheath other than the perimeter seal and the opening seal.

[0086] Before testing, the flexible pouches were inspected for leaks, and only leak-free pouches were evaluated further.

[0087] D. Flexible Pouch Drop Test A Lansmont Bottle Drop Tester is used for the drop test. The Lansmont Bottle Drop Tester is equipped with a horizontal plate onto which the flexible pouch is placed. The flexible pouch will rest and hold its position in a horizontal position without the use of restraints.

[0088] The drop surface was a smooth metal surface. After each test, all water was removed from the metal surface. The actuator arm would drop out from under the flexible pouch faster than the acceleration rate, causing the pouch to fall onto the metal surface. After each drop, the flexible pouch was inspected. If there was any breach in the structure and water leakage occurred, the flexible pouch was considered to have failed.

[0089] E. Data Analysis To determine the usefulness of the flexible pouch having Structure A, a bag was formed having only the inner liner sealed together and tested by itself. The bag has Structure B below. Structure (B) i. Layer 1—Inner liner layer ii. Layer 2—Inner Liner Layer

[0090] Comparative Blank ID1 and Comparative Blank ID2 were each sealed flexible bags filled with water and having Structure B. For Comparative Blank ID1 and Comparative Blank ID2, each bag passed the drop test from a drop of 0.91 meters. However, when dropped from 1.22 meters, Comparative Blank ID1 and Comparative Blank ID2 each failed both times.

[0091] To determine the usefulness of the flexible pouch having Structure A, a bag having only the outer sheath sealed together was formed and tested by itself. The bag having only the outer sheath has Structure C below. Structure (C) i. Layer 1 - Outer sheath layer ii. Layer 2 - Outer Sheath Layer

[0092] For comparative samples (CS) 1, 2, 3, and 4, an outer sheath was used to create a bag with the same dimensions as the flexible pouch. Drop test results for all comparative samples are provided in Table 2 below. [Table 2]

[0093] Comparative Blank Samples 1-4 in Table 2 above showed 100% failure at a 1.22 meter drop, and Comparative Blank Samples 3 and 4 showed 100% failure at a 0.91 meter drop. Comparative Samples (CS) 1-4 showed at least 50% failure at 1.22 meters.

[0094] The flexible pouches of invention examples (IE) 1, 2, 3, 4, and 5 all have the same inner liner, as shown in Table 1. The PCR resin of the outer sheath varies for each of IEs 1 to 5. Drop test results for invention examples 1, 2, 3, 4, and 5 are provided in Table 3 below. [Table 3]

[0095] From Table 2, flexible pouches CS1-4 each had a 50% breakage rate in the 1.22 meter drop test. In Table 3, inventive examples (IEs), IE1-5, each passed the 1.22 meter drop test 100%. IE4-5 each passed the drop test from 1.22 meters and also passed a subsequent drop test from 1.52 meters without breakage / leaking.

[0096] It is expressly intended that the present disclosure is not limited to the embodiments and examples contained herein, but includes modifications of these embodiments, including portions of the embodiments and combinations of elements of different embodiments, as falling within the scope of the following claims. The inventions described in the original claims of this application are set forth below. [1] A flexible pouch, A first layer structure and a second layer structure, each layer structure comprising: (i) an inner liner; and (ii) an outer sheath; the first layer structure is superimposed on the second layer structure such that the inner liners face each other, the first layer structure and the second layer structure defining a common peripheral edge; Each inner liner (i) is made of a flexible film made of a polymer material; A first layer structure and a second layer structure, each outer sheath (ii) being made of a post-consumer resin (PCR), said PCR having a GI200 value of greater than 50; a peripheral seal along at least a portion of the common peripheral edge, the peripheral seal sealing the first layer structure to the second layer structure; A flexible pouch comprising: [2] The flexible pouch according to [1], wherein the PCR has a GI200 value of 100 to 10,000. [3] The flexible pouch of [1] or [2], wherein the peripheral seal comprises a heat seal between opposing inner liners. [4] A flexible pouch according to any one of [1] to [3], wherein each layer structure comprises 10% by volume to 90% by volume of the outer sheath and 90% by volume to 10% by volume of the inner liner. [5] The flexible pouch according to any one of [1] to [4], wherein the peripheral seal comprises a heat seal between the outer sheath and its respective inner liner. [6] The flexible pouch according to [5], wherein the peripheral seal, when viewed in cross section, comprises a layer configuration of a first outer sheath, a first liner, a second liner, and a second outer sheath. [7] The peripheral seal is the outer sheath heat sealed to the first liner; the first liner heat sealed to the second liner; and [6] The flexible pouch according to [6], comprising the second liner heat-sealed to the second sheath. [8] The flexible pouch according to any one of [1] to [7], wherein each inner liner is a flexible multilayer film comprising at least three layers. [9] The flexible pouch according to any one of [1] to [8], wherein each layer structure includes a printed film.

[10] A flexible pouch according to any one of [1] to [9], wherein the peripheral seal is the only seal between the inner liner and its respective outer sheath.

[11] including an interface between the inner liner and its respective outer sheath;

[10] The flexible pouch according to

[10] , wherein a gap exists at the boundary surface except for the peripheral seal.

Claims

1. A flexible pouch comprising: a first layer structure and a second layer structure, each layer structure comprising: (i) an inner liner; and (ii) an outer sheath; the first layer structure is superimposed on the second layer structure with the inner liners facing each other, the first layer structure and the second layer structure defining a common peripheral edge; each inner liner (i) is made of a flexible film made of a polymeric material; the polymeric material is an ethylene-based polymer, and each of the inner liners (i) is a flexible multilayer film having at least three layers, having an A / B / A layer structure, the at least three layers including a sealant layer composed of an ethylene / α-olefin copolymer comprising ethylene and a C4 to C8 α-olefin comonomer; a first layer structure and a second layer structure, each outer sheath (ii) being composed of 100% by weight of post-consumer resin (PCR), said PCR having a GI200 value (unit: mm 2 ) of 300 to 1600; a peripheral seal along at least a portion of the common peripheral edge, the peripheral seal sealing the first layer structure to the second layer structure; an interface between said inner liner and its respective outer sheath; a gap present at the interface excluding the peripheral seal; Including, the peripheral seal is the only seal between the inner liner (i) and each outer sheath (ii), and there is no adhesive contact between each inner liner and each outer sheath other than the peripheral seal. Flexible pouch.

2. The flexible pouch of claim 1 , wherein the peripheral seal comprises a heat seal between opposing inner liners.

3. 3. The flexible pouch of claim 1, wherein each layer structure comprises 10% to 90% by volume of the outer sheath and 90% to 10% by volume of the inner liner.

4. The flexible pouch of any one of claims 1 to 3, wherein the peripheral seal comprises a heat seal between the outer sheath and its respective inner liner.

5. 5. The flexible pouch of claim 4, wherein the peripheral seal, when viewed in cross section, comprises a layered configuration of a first outer sheath, a first liner, a second liner, and a second outer sheath.

6. The peripheral seal is the outer sheath heat sealed to the first liner; the first liner heat sealed to the second liner; and The flexible pouch of claim 5 , comprising the second liner heat sealed to the second outer sheath.

7. The flexible pouch of any one of claims 1 to 6, wherein each inner liner is a flexible multi-layer film comprising at least three layers.

8. The flexible pouch according to any one of claims 1 to 7, wherein each layer structure comprises a printed film.