Method for producing cycloolefin

Abstract

The present invention provides a method for producing a cycloolefin by causing a partial hydrogenation reaction of a monocyclic aromatic hydrocarbon by means of hydrogen in the presence of a ruthenium catalyst in an aqueous zinc sulfate solution, wherein: the aqueous zinc sulfate solution contains dimethylamine; and the partial hydrogenation reaction is performed, while setting the nitrogen concentration in the aqueous zinc sulfate solution to 0.5 mg / L to 3,000 mg / L or setting the acetic acid concentration in the aqueous zinc sulfate solution to 1 × 10-3 mg / L to 100 mg / L.

Description

[Technical Field]

[0001] The present invention relates to a method for producing cycloolefins. [Background technology]

[0002] Cycloolefins, particularly cyclohexenes, have been widely used as intermediates for industrial organic chemical products. Various methods are known for producing cycloolefins, among which a method of partially hydrogenating monocyclic aromatic hydrocarbons using a ruthenium catalyst as a raw material is common. Many techniques have been proposed to improve the yield of cycloolefins, such as by changing the type of catalyst component or carrier, or by adding metal salts to the reaction system. Among these, methods using a reaction system in which water and zinc coexist have been shown to result in a relatively high yield of cycloolefins.

[0003] For example, (1) a method has been proposed in which monocyclic aromatic hydrocarbons are partially reduced with hydrogen in the presence of water, using hydrogenation catalyst particles containing metallic ruthenium as a main component and having an average crystal size of 20 nm or less, and the reaction is carried out under neutral or acidic conditions in the coexistence of at least one solid basic zinc salt (excluding basic zinc sulfate) (see, for example, Patent Document 1). Also proposed is (2) a method in which monocyclic aromatic hydrocarbons are partially reduced with hydrogen under neutral or acidic conditions in the presence of water and at least one zinc compound, using a catalyst in which particles containing metallic ruthenium as a main component and having an average crystallite size of 3 to 20 nm are supported on a carrier (see, for example, Patent Document 2). Furthermore, (3) as a catalyst for producing cycloolefins, a catalyst has been proposed which uses zirconia as a carrier and is composed of particles having an average primary particle size in the range of 3 to 50 nm and an average secondary particle size in the range of 0.1 to 30 μm (see, for example, Patent Document 3).

[0004] When attempting to industrially carry out a method for producing cycloolefins by partially reducing monocyclic aromatic hydrocarbons as raw materials with hydrogen using a ruthenium catalyst, it is necessary to minimize the frequency of catalyst replacement, which hinders efficient production. For this reason, it is preferable that the catalyst can be used for a long period of time. However, it is known that the activity of a catalyst decreases when it is used for a long period of time. Causes of this decrease in catalyst activity have been reported to include physical changes (e.g., sintering) of the active sites of the catalyst itself due to the reaction environment (temperature, reaction heat), the accumulation of poisoning substances (e.g., sulfur compounds, foreign metals, etc.), and the interaction between hydrogen and ruthenium.

[0005] For example, with regard to catalyst poisoning, (1) an example of poisoning by sulfur compounds (see, for example, Patent Document 4) and (2) an example of poisoning by the material of the reactor (see, for example, Patent Document 5) are known. Furthermore, (3) a method of removing nickel eluted from the reactor, which is considered to be a poisoning substance, from the reaction system (see, for example, Patent Document 6), (4) a method of suppressing the adverse effects of the chloride ion concentration in the reaction solution (see, for example, Patent Document 7), and (5) a method of using a catalyst in a reaction system in which the chloride content in the catalyst is reduced to 0.04 parts by mass or less per part by mass of ruthenium (see, for example, Patent Document 8) have been disclosed.

[0006] Proposed methods for regenerating a ruthenium catalyst whose activity has decreased due to the interaction between hydrogen and the catalyst include a method of contacting the catalyst with oxygen in the liquid phase (see, for example, Patent Document 9), a method of maintaining the catalyst under a hydrogen partial pressure lower than the hydrogen partial pressure in the hydrogenation reaction and at a temperature not lower than 50°C lower than the temperature in the hydrogenation reaction (see, for example, Patent Document 10), and a method having a step of contacting the catalyst with oxygen in the liquid phase and a step of maintaining the catalyst under a hydrogen partial pressure lower than the hydrogen partial pressure in the hydrogenation reaction and at a temperature not lower than 50°C lower than the temperature in the hydrogenation reaction (see, for example, Patent Document 11).Furthermore, a method and apparatus for performing the same have been proposed in which a portion of the catalyst is continuously or intermittently withdrawn from a continuous reaction, regenerated, and returned to a reactor where a partial hydrogenation reaction is carried out (see, for example, Patent Document 12). It is also known that the selectivity of cycloolefins changes over time when the catalyst is used for a long period of time. To avoid this, methods have been proposed in which the reaction is carried out while changing the concentration of metal sulfate in the aqueous phase (see, for example, Patent Document 13), and in which sulfuric acid is added to the reaction system (see, for example, Patent Document 14). [Prior art documents] [Patent documents]

[0007] [Patent Document 1] Patent No. 2115581 [Patent Document 2] Patent No. 2138012 [Patent Document 3] Patent No. 4777891 [Patent Document 4] Patent No. 1849859 [Patent Document 5] Patent No. 2892233 [Patent Document 6] Patent No. 5254338 [Patent Document 7] Patent No. 5147053 [Patent Document 8] Patent No. 3125913 [Patent Document 9] Patent No. 2634828 [Patent Document 10] Patent No. 2886563 [Patent Document 11] Patent No. 3841226 [Patent Document 12] Patent No. 4397468 [Patent Document 13] Patent No. 4033980 [Patent Document 14] Patent No. 4025407 Summary of the Invention [Problem to be solved by the invention]

[0008] However, none of the above-mentioned prior art documents describes at all that nitrogen-containing components contained in the aqueous zinc sulfate solution in the reactor affect the reactivity of the catalyst when monocyclic aromatic hydrocarbons are subjected to a partial hydrogenation reaction with hydrogen.

[0009] Nitrogen-containing components enter the reactor contained in monocyclic aromatic hydrocarbons and hydrogen, which are raw materials for producing cycloolefins, or through the monocyclic aromatic hydrocarbons recycled from the product separation and purification process after the partial hydrogenation reaction.

[0010] Nitrogen-containing components derived from raw materials are contained in the raw materials used to produce monocyclic aromatic hydrocarbons and hydrogen, and may also be contaminated from chemicals used in the process of separating and refining raw materials, lubricants for equipment, etc. In addition, in the production of cycloolefins, nitrogen-containing components that enter the reactor via recycled monocyclic aromatic hydrocarbons are caused by the extraction agent used in the process after the hydrogenation step and the components generated by the decomposition of the extraction agent being mixed with the recycled monocyclic aromatic hydrocarbons.

[0011] In the partial hydrogenation reaction of monocyclic aromatic hydrocarbons, a commonly known method is to adjust the reaction conversion rate to highly selectively increase the production ratio of the target product, and if the reaction conversion rate is low, an operation is carried out in which unreacted monocyclic aromatic hydrocarbons are recycled and returned to the reactor where the partial hydrogenation reaction is carried out again. At this time, in the process of separating and purifying the product of the partial hydrogenation reaction from the unreacted monocyclic aromatic hydrocarbons, the extraction solvent used and decomposition products of the extraction solvent are mixed into the recycled monocyclic aromatic hydrocarbons and are then re-entered into the reactor for the partial hydrogenation reaction.

[0012] As described above, when nitrogen-containing components enter the reactor for the partial hydrogenation reaction, they come into contact with the catalyst in the hydrogenation reaction field and further react with the aqueous zinc sulfate solution, causing problems such as a decrease in the partial hydrogenation activity for monocyclic aromatic hydrocarbons and the selectivity for cycloolefins. On the other hand, there have been no reports on the influence of the amount of nitrogen-containing components in the hydrogenation reaction field on the hydrogenation reaction, and no solutions have been proposed.

[0013] Furthermore, none of the above-mentioned prior art documents describes at all that the concentration of acetic acid in the aqueous zinc sulfate solution in the reactor affects the reactivity of the partial hydrogenation reaction when monocyclic aromatic hydrocarbons are subjected to a partial hydrogenation reaction with hydrogen.

[0014] In the partial hydrogenation reaction of monocyclic aromatic hydrocarbons, it is necessary to appropriately adjust the reaction conversion of monocyclic aromatic hydrocarbons in order to recover the target product, cycloolefins, with high selectivity and to increase productivity. In this case, a method is generally used in which unreacted monocyclic aromatic hydrocarbons are separated and recovered from the reaction products and then recycled to the partial hydrogenation reactor again.

[0015] On the other hand, the reaction products of the partial hydrogenation reaction, including by-products, have boiling points similar to those of the monocyclic aromatic hydrocarbons that are the raw material. Therefore, a predetermined extractant is used for separation and recovery. Depending on the state of separation and recovery, the extractant or components formed by decomposition of the extractant may be mixed into the reactor together with the monocyclic aromatic hydrocarbons that are being recycled.

[0016] Acetic acid is generated in small amounts in the separation and recovery column of the partial hydrogenation reaction product as a decomposition product of dimethylacetamide, which is highly effective in separating and purifying the monocyclic aromatic hydrocarbons used as raw materials, the cycloolefins used as products, and the cycloparaffins used as by-products. This acetic acid is mixed with the recycled monocyclic aromatic hydrocarbons and enters the reactor for the subsequent partial hydrogenation reaction.

[0017] As described above, when acetic acid enters the reactor for the partial hydrogenation reaction, it acts on the catalyst in the hydrogenation reaction field, causing a problem of decreasing the selectivity for cycloolefins.

[0018] Therefore, an object of the present invention is to provide a method for stably producing cycloolefins by suppressing a decrease in the selectivity for cycloolefins in the partial hydrogenation reaction of monocyclic aromatic hydrocarbons. [Means for solving the problem]

[0019] The present inventors have found that, when monocyclic aromatic hydrocarbons are subjected to a partial hydrogenation reaction, by controlling the nitrogen concentration in an aqueous zinc sulfate solution, it is possible to significantly suppress a decrease in catalyst activity and a decrease in selectivity in the partial hydrogenation reaction, thereby solving the above-mentioned problems of the conventional techniques, and have thus completed the present invention. Furthermore, the present inventors have found that, when monocyclic aromatic hydrocarbons are subjected to a partial hydrogenation reaction, by controlling the concentration of acetic acid in an aqueous zinc sulfate solution within a specific numerical range, it is possible to significantly suppress a decrease in catalyst selectivity in the partial hydrogenation reaction, thereby solving the above-mentioned problems of the conventional techniques, and have thus completed the present invention. That is, the present invention is as follows.

[0020] [1] A method for producing cycloolefins by partially hydrogenating monocyclic aromatic hydrocarbons with hydrogen in an aqueous zinc sulfate solution in the presence of a ruthenium catalyst, comprising: The zinc sulfate aqueous solution contains dimethylamine, The nitrogen concentration in the zinc sulfate aqueous solution is 0.5 to 3000 mg / L. A method for producing cycloolefins. [2] a nitrogen concentration in the zinc sulfate aqueous solution containing the ruthenium catalyst is adjusted to 0.5 to 3000 mg / L by replacing a part of the zinc sulfate aqueous solution with a new zinc sulfate aqueous solution, and then the partial hydrogenation reaction of the monocyclic aromatic hydrocarbon is carried out. The method for producing cycloolefin according to [1] above. [3] The nitrogen concentration contained in the monocyclic aromatic hydrocarbons is 0.003 to 35 mg / L. The method for producing a cycloolefin according to [1] or [2] above. [4] The ratio of the nitrogen mass to the ruthenium catalyst mass in the zinc sulfate aqueous solution is 5×10 -6 ~8×10 -2 The method for producing cycloolefin according to any one of [1] to [3] above, wherein the reaction rate is 1000 sq. ft. / min. [5] The nitrogen concentration in the zinc sulfate aqueous solution is set to 0.5 to 1500 mg / L, The nitrogen concentration in the monocyclic aromatic hydrocarbon is set to 0.01 to 16 mg / L, The ratio of the mass of nitrogen to the mass of the ruthenium catalyst in the aqueous zinc sulfate solution is 1×10 -5 ~5×10 -2 As a double, carrying out a partial hydrogenation reaction; The method for producing a cycloolefin according to any one of [1] to [4] above. [6] the concentration of dimethylamine in the zinc sulfate aqueous solution is 1.7 to 9900 mg / L; the concentration of dimethylamine in the monocyclic aromatic hydrocarbon is 0.01 to 115 mg / L; The ratio of the mass of dimethylamine to the mass of the ruthenium catalyst in the zinc sulfate aqueous solution is 2×10 -5 ~0.26 times The method for producing a cycloolefin according to any one of [1] to [5] above. [7] a reaction step of partially hydrogenating the monocyclic aromatic hydrocarbon with hydrogen in the aqueous zinc sulfate solution; an extraction step of extracting the unreacted monocyclic aromatic hydrocarbons with a solvent containing a nitrogen-containing compound after the reaction step; a water washing step in which the extracted monocyclic aromatic hydrocarbons are brought into contact with water in an amount of 0.05 to 1 volume times; a recycling step of subjecting the water-washed monocyclic aromatic hydrocarbons to the reaction step; , and In the reaction step, the content of dimethylamine in the zinc sulfate aqueous solution is 40 to 1700 mg / L, and the ratio of the mass of dimethylamine to the mass of the ruthenium catalyst is 8 × 10 -4 ~6×10 -2 Double, to control, The method for producing a cycloolefin according to any one of [1] to [6] above. [8] A method for producing cycloolefins by partially hydrogenating monocyclic aromatic hydrocarbons with hydrogen in an aqueous zinc sulfate solution in the presence of a ruthenium catalyst, comprising: The concentration of acetic acid in the zinc sulfate aqueous solution was 1 × 10 -3 ~100mg / L and perform partial hydrogenation reaction. A method for producing cycloolefins. [9] By replacing a part of the zinc sulfate aqueous solution with a new zinc sulfate aqueous solution, the concentration of acetic acid in the zinc sulfate aqueous solution in which the ruthenium catalyst is present is increased to 1×10 -3 ~100mg / L and carry out partial hydrogenation of monocyclic aromatic hydrocarbons. The method for producing a cycloolefin according to [8] above.

[10] The concentration of acetic acid contained in the monocyclic aromatic hydrocarbon is 1×10 -4 ~5mg / L The method for producing a cycloolefin according to [8] or [9] above.

[11] The ratio of the mass of acetic acid to the mass of the ruthenium catalyst in the aqueous zinc sulfate solution is 3×10 -9 ~2.5×10 -3 It is in the double range, The method for producing a cycloolefin according to any one of [8] to

[10] above.

[12] a reaction step of partially hydrogenating the monocyclic aromatic hydrocarbon with hydrogen in the aqueous zinc sulfate solution; an extraction step of extracting the unreacted monocyclic aromatic hydrocarbons with a solvent containing a nitrogen-containing compound after the reaction step; a water washing step in which the extracted monocyclic aromatic hydrocarbons are brought into contact with water in an amount of 0.05 to 1 volume times; a recycling step of subjecting the water-washed monocyclic aromatic hydrocarbons to the reaction step; , and In the reaction step, the ratio of the mass of acetic acid to the mass of the ruthenium catalyst in the zinc sulfate aqueous solution is 1×10 -6 ~5×10 -4 Double, to control, The method for producing a cycloolefin according to any one of [8] to

[11] above.

[13] the ruthenium catalyst is a zirconia-containing ruthenium catalyst; a step of regenerating a part or all of the zirconia-containing ruthenium catalyst, Reusing the regenerated zirconia-containing ruthenium catalyst; The method for producing a cycloolefin according to any one of [1] to

[12] above.

[14] the ruthenium catalyst is a zirconia-containing ruthenium catalyst; The zinc concentration in the zirconia-containing ruthenium catalyst is 0.5 to 3.5 mass%. The method for producing a cycloolefin according to any one of [1] to

[13] above.

[15] The monocyclic aromatic hydrocarbon is The alkyl group may be selected from the group consisting of benzene, toluene, and benzene substituted with an alkyl group having 1 to 4 carbon atoms. The method for producing a cycloolefin according to any one of [1] to

[14] above.

[16] The concentration of acetic acid in the zinc sulfate aqueous solution is 1×10 -3 mg / L to 100 mg / L, The method for producing a cycloolefin according to any one of [1] to [7] above. [Effects of the Invention]

[0021] According to the present invention, a decrease in cycloolefin selectivity can be effectively suppressed, and cycloolefins can be produced stably and efficiently for a long period of time. DETAILED DESCRIPTION OF THE INVENTION

[0022] Hereinafter, an embodiment of the present invention (hereinafter referred to as "the present embodiment") will be described in detail. It should be noted that the following embodiments are merely examples for explaining the present invention, and the present invention is not limited to the following embodiments. The present invention can be practiced by appropriately modifying it within the scope of its gist.

[0023] [Method for producing cycloolefins] The method for producing a cycloolefin of the present embodiment (hereinafter, may be simply referred to as the present embodiment) relates to a method for producing a cycloolefin by subjecting a monocyclic aromatic hydrocarbon to a partial hydrogenation reaction with hydrogen in an aqueous zinc sulfate solution in the presence of a ruthenium catalyst. In a first embodiment, the zinc sulfate aqueous solution contains dimethylamine, and the nitrogen concentration in the zinc sulfate aqueous solution is set to a predetermined numerical range. In the second embodiment, the concentration of acetic acid in the aqueous zinc sulfate solution is set to a predetermined range. Hereinafter, the methods for producing cycloolefins according to the first and second embodiments will be described.

[0024] [Method for producing cycloolefin according to the first embodiment] In a first embodiment, the aqueous zinc sulfate solution contains dimethylamine, and the nitrogen concentration in the aqueous zinc sulfate solution is 0.5 to 3000 mg / L. According to the first embodiment, the catalytic activity of the partial hydrogenation reaction and the selectivity to cycloolefins can be maintained at high levels, and the catalytic activity and the selectivity to cycloolefins can be maintained at high levels even after catalyst regeneration. By stabilizing the catalytic activity and selectivity, the number of complicated operations such as replacing the catalyst or adding unused catalyst during long-term cycloolefin production can be reduced, a decrease in cycloolefin selectivity can be effectively suppressed, and cycloolefins can be produced efficiently and stably over a long period of time.

[0025] (monocyclic aromatic hydrocarbons) In the method for producing a cycloolefin according to the first embodiment, a monocyclic aromatic hydrocarbon is used as a raw material. Examples of monocyclic aromatic hydrocarbons include, but are not limited to, benzene, toluene, and benzene substituted with an alkyl group having 1 to 4 carbon atoms, such as xylene.

[0026] (hydrogen pressure) In the first embodiment, the hydrogen pressure when the partial hydrogenation reaction is carried out with hydrogen is generally 1 to 20 MPa, and preferably 2 to 7 MPa. By setting the hydrogen pressure to 1 MPa or more, it is possible to ensure sufficient selectivity to cycloolefins, and by setting the hydrogen pressure to 20 MPa or less, it is possible to control the pressure of hydrogen and monocyclic aromatic hydrocarbons supplied to the reactor to a practically preferable level, thereby reducing the load on equipment associated with an increase in pressure and enabling the supply of hydrogen and monocyclic aromatic hydrocarbons in proportion to the hydrogen consumption, thereby enabling efficient operation.

[0027] (Reaction temperature) The temperature during the partial hydrogenation reaction is generally 50 to 250°C, preferably 100 to 200°C. A reaction temperature of 50°C or higher ensures a sufficient reaction rate. A reaction temperature of 250°C or lower suppresses the growth of the average crystallite size of ruthenium in the ruthenium catalyst (sintering), thereby reducing the decrease in catalytic activity.

[0028] (Ruthenium catalyst) In the first embodiment, a partial hydrogenation reaction of monocyclic aromatic hydrocarbons is carried out in the presence of a ruthenium catalyst. The ruthenium catalyst is preferably a catalyst containing metallic ruthenium obtained by previously reducing various ruthenium compounds. Examples of the ruthenium compound include, but are not limited to, halides such as chlorides, bromides, and iodides, nitrates, sulfates, and hydroxides, and various complexes containing ruthenium, such as ruthenium carbonyl complexes, ruthenium acetylacetonate complexes, ruthenocene complexes, ruthenium ammine complexes, and ruthenium hydride complexes, and compounds derived from such complexes. These ruthenium compounds may be used alone or in combination of two or more.

[0029] Examples of methods for reducing these ruthenium compounds include catalytic reduction using hydrogen, carbon monoxide, or the like, and chemical reduction using formalin, sodium borohydride, potassium borohydride, hydrazine, or the like. Of these reduction methods, the preferred methods are catalytic reduction with hydrogen and chemical reduction with sodium borohydride. In the case of catalytic reduction with hydrogen, reduction activation is carried out usually at 50 to 450°C, preferably 100 to 400°C, and more preferably 100 to 250°C. A reduction temperature of 50°C or higher allows reduction at a rate sufficient for practical use, while a temperature of 450°C or lower can suppress ruthenium aggregation and prevent adverse effects on activity and selectivity. This reduction may be carried out in either the gas phase or the liquid phase, but liquid phase reduction is preferred. In the case of chemical reduction using sodium borohydride, the reduction temperature is preferably 100°C or lower, and typically 10°C to 80°C. The ruthenium catalyst charged during the partial hydrogenation reaction may be in the form of a ruthenium compound that does not contain metallic ruthenium. In this case, the ruthenium compound is preferably a compound such as a hydroxide that does not contain chloride ions.

[0030] When a ruthenium catalyst not containing metallic ruthenium is charged during the partial hydrogenation reaction, it is preferable to use a ruthenium hydroxide-supported carrier prepared by supporting the above-mentioned ruthenium compound on a carrier and treating the carrier with an alkali such as sodium hydroxide, or to use a mixture of ruthenium hydroxide and a dispersant obtained by adding an alkali such as sodium hydroxide to a mixture containing the dispersant and the above-mentioned ruthenium compound.

[0031] Furthermore, the ruthenium compound may be a ruthenium-based compound obtained by adding other metals or metal compounds, such as zinc, chromium, molybdenum, tungsten, manganese, cobalt, nickel, iron, copper, gold, platinum, boron, lanthanum, cerium, or compounds of these metals, before or after reduction of the ruthenium compound. When such other metals or metal compounds are used, the atomic ratio relative to ruthenium atoms is usually selected within the range of 0.001 to 20. Among the other metals and metal compounds, zinc and zinc compounds are preferred. Zinc and zinc compounds are preferably added before or during the reduction of the ruthenium compound, and the amount added is preferably 0.001 to 2 times the mass of zinc relative to ruthenium. Furthermore, from the viewpoint of catalytic activity and cycloolefin selectivity, it is more preferred to use 0.005 to 1 times the mass of zinc relative to ruthenium.

[0032] Examples of methods for preparing ruthenium-based catalysts containing such other metals or metal compounds include: (1) a method in which a ruthenium compound and the other metal or metal compound are supported on a carrier and then reduced; (2) a method in which an alkali such as sodium hydroxide is added to a solution containing a ruthenium compound and the other metal or metal compound, thereby precipitating the ruthenium compound and the other metal, etc. together as an insoluble salt and reducing the precipitate; (3) a method in which an insoluble ruthenium compound is supported on a carrier as needed, and this ruthenium compound is reduced in a liquid phase containing the other metal compound, etc.; and (4) a method in which both the ruthenium compound and the other metal compound are reduced in a state where they are dissolved in a liquid phase.

[0033] In the method for producing a cycloolefin according to the first embodiment, the catalyst may be supported on a carrier. The carrier is not particularly limited, but examples thereof include oxides, composite oxides, hydroxides, and poorly water-soluble metal salts of metals such as magnesium, aluminum, silicon, calcium, titanium, vanadium, chromium, manganese, cobalt, iron, nickel, copper, zinc, zirconium, hafnium, tungsten, and boron, as well as compounds or mixtures of two or more of these chemically or physically combined. Among these, zirconium oxide (zirconia) and zirconium hydroxide are preferred as the carrier, and zirconium oxide (zirconia) is particularly preferred because of its excellent physical stability under reaction conditions, such as specific surface area. The average particle size of zirconium oxide is preferably 0.05 to 30 μm, more preferably 0.05 to 10 μm. The specific surface area is preferably 20 to 200 μm. 2 / g, and the average pore diameter is preferably between 1 and 50 nm. The method for supporting ruthenium on the carrier is not particularly limited, but examples thereof include adsorption, ion exchange, immersion, coprecipitation, and drying. The amount of the carrier used is not particularly limited, but is usually 1 to 1000 times by mass relative to ruthenium. In particular, when zirconium oxide (zirconia) is used as the carrier, it is preferable to use 1 to 100 times by mass relative to ruthenium, and more preferably 2 to 20 times by mass. In the method for producing cycloolefins according to the first embodiment, it is preferable to use a zirconia-containing ruthenium catalyst in the partial hydrogenation reaction of monocyclic aromatic hydrocarbons. When using a zirconia-containing ruthenium catalyst, the support is zirconia, or when no support is used as described below, zirconium is used as a dispersant, which is oxidized to form zirconia, which is combined with ruthenium to form a catalyst.

[0034] Furthermore, even when ruthenium is used as is without being supported on a carrier, it is preferable to use, as a dispersant, an oxide, composite oxide, hydroxide, or poorly water-soluble metal salt of a metal such as magnesium, aluminum, silicon, calcium, titanium, vanadium, chromium, manganese, cobalt, iron, nickel, copper, zinc, zirconium, hafnium, tungsten, barium, or boron, or a compound or mixture of two or more of these chemically or physically combined.

[0035] Furthermore, the average crystallite diameter of the metallic ruthenium in the ruthenium catalyst used in the first embodiment is preferably 20 nm or less. If the average crystallite diameter is 20 nm or less, the catalyst has a suitable surface area, so there are a sufficient number of active sites, which is preferable, and the catalytic activity is improved. In addition, the lower limit of this average crystallite diameter is theoretically larger than the crystal unit, and in reality it is 1 nm or more.

[0036] (Zinc sulfate aqueous solution) In the cycloolefin production method of the first embodiment, the partial hydrogenation reaction of monocyclic aromatic hydrocarbons is carried out in an aqueous zinc sulfate solution. In other words, the use of water is an essential requirement. The amount of water varies depending on the reaction format. The amount of water is preferably 0.5 to 20 times by mass relative to the monocyclic aromatic hydrocarbon raw material. This range allows high cycloolefin selectivity to be maintained without increasing the reactor size. More preferably, the amount of water is 1 to 10 times by mass relative to the monocyclic aromatic hydrocarbon used. In either case, it is necessary for the amount of water present in the reaction system to be such that an organic liquid phase (oil phase) composed mainly of the raw materials and the product and water are in a phase-separated state, i.e., a two-phase liquid state consisting of an oil phase and an aqueous phase. The "major component" referred to here refers to the component that accounts for the largest proportion, in terms of moles, of the components constituting the liquid phase.

[0037] In the first embodiment, the reaction system is carried out in an aqueous solution of zinc sulfate, and zinc sulfate must be present in the aqueous phase in a dissolved state, at least partially or entirely.

[0038] <Zinc sulfate and metal sulfates> In the production method of the first embodiment, the reaction system may contain other metal sulfates in addition to zinc sulfate. Other metal sulfates include sulfates of iron, nickel, cadmium, gallium, indium, magnesium, aluminum, chromium, manganese, cobalt, copper, etc. Two or more of these may be used in combination, or a double salt containing such a metal sulfate may be used. The content of zinc sulfate in the aqueous zinc sulfate solution is set to a concentration of 1×10 in the aqueous phase from the viewpoint of enhancing catalytic activity and cycloolefin selectivity. -3 The concentration is preferably from 0.1 to 2.0 mol / L, more preferably from 0.1 to 1.0 mol / L, and even more preferably from 0.4 to 0.9 mol / L. The concentration of metal sulfates other than zinc sulfate is preferably set appropriately depending on the type of metal component.

[0039] <Metal salts> Furthermore, in the reaction system in the method for producing cycloolefin of the first embodiment, the following metal salts may be present, as in conventional methods. Examples of the metal salts include nitrates, oxides, hydroxides, acetates, and phosphates of Group 1 metals such as lithium, sodium, and potassium in the periodic table, Group 2 metals such as magnesium and calcium (Group numbers are based on the IUPAC Inorganic Chemistry Nomenclature Revised Edition (1989)), and metals such as zinc, manganese, cobalt, copper, cadmium, lead, arsenic, iron, gallium, germanium, vanadium, chromium, silver, gold, platinum, nickel, palladium, barium, aluminum, and boron. Two or more of these may be used in combination chemically and / or physically. However, metal chlorides are not preferred because the chloride ion concentration in the aqueous phase adversely affects the long-term performance of the catalyst. As metal salts and metal oxides other than chlorides, zinc compounds such as zinc hydroxide and zinc oxide are preferred. In particular, double salts containing zinc hydroxide, such as those of the general formula (ZnSO4), m (Zn(OH)2) n A double salt represented by the formula (I) where m:n=1:0.01 to 1:100 is preferred. The amount of the metal salt used is not particularly limited as long as the aqueous phase is kept acidic or neutral. -5 ~1×10 5 The metal salts may be present anywhere in the reaction system, and the entire amount does not necessarily have to be dissolved in the aqueous phase.

[0040] <pH of the aqueous phase of zinc sulfate solution> The pH of the aqueous phase of the zinc sulfate solution used in the method for producing cycloolefins of the first embodiment is preferably acidic or neutral at 7.0 or less, from the viewpoint of enhancing catalytic activity and cycloolefin selectivity.

[0041] <Chloride ion concentration> In the cycloolefin production method of the first embodiment, as described above, chloride ions dissolved in the water of the reaction system may adversely affect the long-term performance of the catalyst. Therefore, the chloride ion concentration is preferably 300 mg / L or less, more preferably 200 mg / L or less, and even more preferably 100 mg / L or less. The chloride ion concentration is the concentration of chlorine Cl2, hypochlorous acid HClO, and hypochlorite ion ClO - The free residual chlorine, which exists in equilibrium with the ammonium ions present in the water, reacts with the combined residual chlorine, which exists in the form of chloramines, and the Cl - The sum of the concentrations of all chlorine present in the form of chlorine atoms and ions, including all chloride ions present in the form of chlorine atoms and ions. By keeping the chloride ion concentration at 300 mg / L or less, in the first embodiment, it is possible to effectively suppress a decrease in activity and a decrease in cycloolefin selectivity when the ruthenium catalyst is used for a long period of time. The reason why chloride ions dissolved in water reduce the reaction activity and cycloolefin selectivity of the ruthenium catalyst is not entirely clear, but the following is thought to be the cause. In the presence of chloride ions, ruthenium dissolves in water and re-reduction occurs. This promotes sintering of ruthenium, causing a decrease in catalyst activity. At the same time, the interaction between ruthenium and the coexisting metal or metal compound changes. Since this metal or metal compound plays an important role in cycloolefin selectivity, it is presumed that cycloolefin selectivity also decreases.

[0042] In the first embodiment, the concentration of chloride ions dissolved in the aqueous phase in which the ruthenium catalyst is present can be controlled to 300 mg / L or less by controlling the chloride ion concentrations of each component present in the aqueous phase. Specifically, by controlling the chloride ion concentration contained in the water, catalyst, dispersant, metal sulfate, metal salt, monocyclic aromatic hydrocarbon, and hydrogen supplied to the reaction system to a certain value or less, the chloride ion concentration dissolved in the water can be controlled to 300 mg / L or less. In the first embodiment, in addition to supplying the monocyclic aromatic hydrocarbon and hydrogen to the reaction field, it is effective to newly supply water in an amount equivalent to the amount of water that flows out of the reaction field together with the reaction solution. The chloride ion content of the newly supplied water is preferably 20 mg / L or less, more preferably 10 mg / L or less, and even more preferably 5 mg / L or less. Methods for controlling the chloride ion content in newly supplied water to fall within the above range include, for example, treating the water with an ion exchange resin, purifying the water by distillation, and the like.

[0043] <Electrical conductivity of water supplied to the reaction field> Furthermore, the electrical conductivity of the water supplied to the reaction field is preferably 0.5 μS / cm or less, more preferably 0.3 μS / cm or less, when expressed in terms of commonly used electrical conductivity, from the viewpoint of maintaining high catalytic activity and cycloolefin selectivity.

[0044] <Nitrogen concentration in zinc sulfate aqueous solution> In the method for producing cycloolefin of the first embodiment, the nitrogen concentration in the aqueous zinc sulfate solution is set to the range of 0.5 to 3000 mg / L. The nitrogen concentration in the aqueous zinc sulfate solution refers to the concentration of nitrogen-containing components calculated as the nitrogen atom content. The nitrogen concentration in the aqueous zinc sulfate solution can be measured by the method described in the Examples below. Nitrogen-containing components contaminated in the aqueous zinc sulfate solution include impurities of monocyclic aromatic hydrocarbons and hydrogen, which are raw materials for producing cycloolefins, substances generated in the process of separating and purifying the raw materials, lubricants of chemicals and equipment used, and extractants and decomposition components of the extractants used in the process of separating and purifying the product after the partial hydrogenation reaction step, which are contaminated in the recycled monocyclic aromatic hydrocarbons. Nitrogen-containing components that are entrained in the aqueous zinc sulfate solution along with the monocyclic aromatic hydrocarbons and hydrogen used as raw materials include monoethanolamine, ammonia, pyrrole, pyridine, quinoline, etc. In addition, examples of the extractant and decomposition products of the extractant that enter the reactor through the recycled monocyclic aromatic hydrocarbons include dimethylacetamide and dimethylamine. The zinc sulfate aqueous solution used in the method for producing a cycloolefin according to the first embodiment contains dimethylamine. Further examples of nitrogen-containing components that dissolve in the zinc sulfate aqueous solution include monoethanolamine, ammonia, and dimethylacetamide.

[0045] In the first embodiment, the influence of the nitrogen concentration in the reaction system for partially hydrogenating monocyclic aromatic hydrocarbons on the reactivity of the partial hydrogenation reaction of monocyclic aromatic hydrocarbons was extensively studied, and it was found that nitrogen-containing components react with an aqueous zinc sulfate solution, which further changes the physical properties of the catalyst and affects the reactivity. Therefore, it was decided to control the nitrogen concentration in the aqueous zinc sulfate solution, the nitrogen concentration in the monocyclic aromatic hydrocarbons, and the ratio of the nitrogen mass to the catalyst mass.

[0046] In the first embodiment, in consideration of the influence of nitrogen-containing components on the partial hydrogenation reaction of monocyclic aromatic hydrocarbons, the total nitrogen concentration in the aqueous zinc sulfate solution is set to a range of 0.5 to 3000 mg / L. When the nitrogen concentration in the aqueous zinc sulfate solution is 3000 mg / L or less, the decrease in the reaction activity of the ruthenium catalyst can be suppressed, and the decrease in selectivity can be prevented. The reason why the concentration of nitrogen dissolved in the aqueous zinc sulfate solution affects the reduction in the reaction activity and selectivity of the ruthenium catalyst is thought to be as follows. Many nitrogen-containing components entering the reaction field are alkaline, causing zinc salting out in the zinc sulfate aqueous solution. The salted-out zinc acts on the ruthenium catalyst, modifying the reaction sites of the ruthenium catalyst and reducing its reaction activity. It is also possible that nitrogen-containing components act as poisons to the ruthenium catalyst, reducing selectivity. Furthermore, for stable production of cycloolefins, a procedure is required to suppress the reduction in the reaction activity of the ruthenium catalyst. A method is employed to remove the salted-out zinc, which reduces catalytic activity. Specifically, sulfuric acid is added to the reaction field of the zinc sulfate aqueous solution to dissolve the salted-out zinc and suppress the reduction in reaction activity. However, while the added sulfuric acid acts on the ruthenium catalyst and restores the reduced activity, it also causes deterioration of the original ruthenium catalyst itself, resulting in a reduction in selectivity.

[0047] From the above, the nitrogen concentration in the zinc sulfate aqueous solution should be kept at 3000 mg / L or less, preferably 1500 mg / L or less, more preferably 1000 mg / L or less, and even more preferably 650 mg / L or less.

[0048] An effective method for suppressing the nitrogen concentration dissolved in the zinc sulfate aqueous solution to 3000 mg / L or less is to suppress the concentration of nitrogen-containing components in the raw materials used in the production of cycloolefins, including the monocyclic aromatic hydrocarbons to be recycled. It is preferable that the concentration of nitrogen-containing components entering the reactor via monocyclic aromatic hydrocarbons or hydrogen as raw materials is sufficiently reduced in a raw material purification step. Also, for nitrogen-containing components entering the reactor via recycled monocyclic aromatic hydrocarbons, it is preferable to reduce the concentration of nitrogen-containing components in the monocyclic aromatic hydrocarbons by distillation purification or to add a nitrogen-containing component removal step in the separation and recovery of monocyclic aromatic hydrocarbons and the extractant used as the nitrogen-containing components.

[0049] However, there is a limit to how much the nitrogen concentration in the zinc sulfate aqueous solution can be reduced. In view of the fact that the scale of the equipment for removing nitrogen-containing components becomes large, the energy load for operating the equipment increases, and the economic burden also increases, it is practically preferable to control the nitrogen concentration in the zinc sulfate aqueous solution at 0.5 mg / L or more. By setting the nitrogen concentration at 15 mg / L or more, the energy load and economic burden for operating the equipment for removing nitrogen can be further reduced.

[0050] (Partial replacement of zinc sulfate aqueous solution) The nitrogen concentration in the aqueous zinc sulfate solution is due to nitrogen-containing components entering from the raw materials, including the recycled monocyclic aromatic hydrocarbons, but not all of the nitrogen-containing components are accumulated in the aqueous zinc sulfate solution, and some are extracted to the outside of the reactor system together with the reaction products. In other words, the nitrogen concentration in the aqueous zinc sulfate solution can be reduced by suppressing the nitrogen-containing components entering the reaction field. On the other hand, in order to reduce the amount of nitrogen-containing components entering from the raw materials, including the recycled monocyclic aromatic hydrocarbons, it is necessary to take measures such as increasing the load on the purification process of each raw material or adding a nitrogen-containing component removal process. Furthermore, when the nitrogen concentration in the zinc sulfate aqueous solution in the reaction field increases, even if the nitrogen-containing components gradually escape outside the reactor system along with the reaction product, it takes a long time to reduce the nitrogen concentration in the zinc sulfate aqueous solution. Therefore, we investigated methods for reducing the nitrogen concentration in the zinc sulfate aqueous solution in the reaction field and found that partially replacing the zinc sulfate aqueous solution with a new zinc sulfate aqueous solution with a lower nitrogen concentration is effective. By reducing the nitrogen concentration once increased in the zinc sulfate aqueous solution by replacing it with a new zinc sulfate aqueous solution, the reactivity that was reduced due to the influence of the nitrogen concentration can be restored. In other words, even if the nitrogen concentration in the zinc sulfate aqueous solution temporarily deviates from the appropriate range of 0.5 to 3000 mg / L, the nitrogen concentration can be returned to the above appropriate range by replacing a part of the zinc sulfate aqueous solution with a new zinc sulfate aqueous solution as described above.

[0051] (Nitrogen concentration in monocyclic aromatic hydrocarbons) In the method for producing a cycloolefin according to the first embodiment, the nitrogen concentration contained in the monocyclic aromatic hydrocarbon is preferably in the range of 0.003 to 35 mg / L. In this case, the monocyclic aromatic hydrocarbons include both the monocyclic aromatic hydrocarbons used as raw materials at the beginning of the production process and the monocyclic aromatic hydrocarbons that are recycled.

[0052] Nitrogen-containing components that enter the reaction site from the raw material monocyclic aromatic hydrocarbons include components derived from the original raw material, nitrogen-containing components produced during the separation and refinement process, and nitrogen-containing components that are mixed in from the chemicals used and lubricants in equipment, etc. Furthermore, after the partial hydrogenation reaction step, the monocyclic aromatic hydrocarbons recycled from the product separation and purification steps enter the reactor, including the extractant used in the step after the hydrogenation step and components formed by decomposition of the extractant.

[0053] Nitrogen-containing components are impurities in monocyclic aromatic hydrocarbons, so removing or reducing the amount of impurities requires adjusting the equipment and operating conditions for separation and purification. To remove nitrogen-containing components with different boiling points by distillation purification, it is necessary to design a distillation column and apply operating conditions that will achieve the target nitrogen concentration in the monocyclic aromatic hydrocarbons. Furthermore, methods for reducing and removing impurities other than distillation purification require equipment that can reduce and remove nitrogen-containing components using adsorbents or extract and remove nitrogen-containing components from monocyclic aromatic hydrocarbons. Methods for reducing and removing nitrogen-containing components using adsorbents include using an adsorption tower filled with adsorbents such as activated alumina, silica-alumina, smectite, and zeolite. Furthermore, when reducing and removing nitrogen-containing components that dissolve in water, a method using a water washing tower, such as submerging monocyclic aromatic hydrocarbons in water, is effective. Furthermore, when nitrogen-containing components are generated during the process of raw material refining or recycling, it is necessary to take measures such as suppressing the factors that cause their generation and minimizing the contamination of monocyclic aromatic hydrocarbons with nitrogen-containing components. For example, when the nitrogen-containing components are thermal decomposition products, it is effective to take measures such as lowering the temperature at the site where the nitrogen-containing components are generated, or when the nitrogen-containing components are hydrolysis products, suppressing the contamination with water.

[0054] By controlling the nitrogen concentration in all monocyclic aromatic hydrocarbons entering the reaction field of the zinc sulfate aqueous solution to 35 mg / L or less, it becomes easy to control the nitrogen concentration in the zinc sulfate aqueous solution to 3000 mg / L or less, and a decrease in the reactivity of the partial hydrogenation reaction can be prevented. That is, the nitrogen concentration in all monocyclic aromatic hydrocarbons is preferably 35 mg / L or less, more preferably 16 mg / L or less, and even more preferably 10 mg / L or less. Furthermore, lowering the nitrogen concentration in total monocyclic aromatic hydrocarbons to less than 0.003 mg / L increases the equipment costs for reducing and removing nitrogen-containing components and increases the operational and analytical management burdens of managing trace nitrogen-containing components at low concentrations. Therefore, the lower limit of the nitrogen concentration in total monocyclic aromatic hydrocarbons is preferably set to 0.003 mg / L or more, and more preferably to 0.01 mg / L or more from the viewpoint of reducing the management burden.

[0055] The nitrogen concentration in the monocyclic aromatic hydrocarbons can be measured by the method described in the Examples below. The nitrogen concentration contained in the monocyclic aromatic hydrocarbons can be controlled to fall within the above-mentioned range by carrying out a denitrification step, such as refining the monocyclic aromatic hydrocarbons used as raw materials or distilling and refining the monocyclic aromatic hydrocarbons to be recycled.

[0056] (Ratio of nitrogen mass of nitrogen-containing component to ruthenium catalyst mass) In the first embodiment of the cycloolefin production method, the ratio of the nitrogen mass of the nitrogen-containing component to the ruthenium catalyst mass in the zinc sulfate aqueous solution is 5×10 -6 ~8×10 -2It is preferable to set the range to 1×10. -5 ~5×10 -2 times, and more preferably 1.5×10 -5 ~3×10 -2 It's double. The ratio of the mass of nitrogen to the mass of the ruthenium catalyst in the aqueous zinc sulfate solution can be calculated by withdrawing the aqueous zinc sulfate solution containing the ruthenium catalyst in a completely mixed state from the hydrogenation reaction field, filtering, washing with water and drying, weighing the solid ruthenium catalyst and measuring the nitrogen concentration in the filtrate by the method described later in the Examples, and determining the masses of both components. The ratio of the mass of nitrogen to the mass of ruthenium catalyst can be controlled within the above range by reducing the nitrogen concentration in the aqueous zinc sulfate solution or by adjusting the amount of ruthenium catalyst added.

[0057] In a first embodiment, a ruthenium catalyst is used as a catalyst for producing cycloolefins by the partial hydrogenation reaction of monocyclic aromatic hydrocarbons. In an aqueous zinc sulfate solution, ruthenium adsorbs monocyclic aromatic hydrocarbons and hydrogen and desorbs them as cycloolefins. During this process, if a nitrogen-containing component enters the aqueous zinc sulfate solution, the zinc in the aqueous zinc sulfate solution solidifies as zinc hydroxide or a double salt of zinc sulfate and zinc hydroxide. This zinc hydroxide or double salt of zinc sulfate and zinc hydroxide covers the reactive sites of ruthenium, inhibiting the partial hydrogenation reaction and reducing the reaction activity. On the other hand, to stably produce cycloolefins, it is necessary to take measures such as adding sulfuric acid to the zinc sulfate aqueous solution to reduce the zinc, which causes a decrease in activity. While adding sulfuric acid to the reaction field can restore decreased activity, the zinc in the catalyst, which was originally designed to adsorb monocyclic aromatic hydrocarbons and hydrogen to ruthenium and to promote the desorption of cycloolefins, is also dissolved by the addition of sulfuric acid, reducing the selectivity to cycloolefins. Therefore, it is necessary to reduce the ratio of nitrogen mass to ruthenium catalyst mass within a range that does not inhibit the reaction of the ruthenium catalyst. From the above viewpoint, in the zinc sulfate aqueous solution, the ratio of the nitrogen-containing component to the ruthenium catalyst mass is 8 × 10 -2 It is preferable to adjust the amount of nitrogen-containing components so that the ratio is 5×10 or less. -2 It is more preferable to set it to 3×10 or less. -2 It is more preferable to set it to 100 times or less.

[0058] The ratio of the nitrogen mass of the nitrogen-containing component to the ruthenium catalyst mass in the zinc sulfate aqueous solution is 5 x 10 -6 Maintaining the concentration below 2x would require an increase in the number of facilities required to reduce and remove nitrogen-containing components, and would also require a large operational burden and analytical management burden to maintain low concentrations of trace nitrogen-containing components, in terms of refining and separating raw materials, including recycling. In addition, the presence of a small amount of nitrogen-containing components in the zinc sulfate aqueous solution, to the extent that there is no effect of a decrease in the activity of the ruthenium catalyst and the need for control of sulfuric acid addition, may contribute to the stabilization of cycloolefin selectivity due to the effect of zinc salting out in small amounts. Therefore, the ratio of the nitrogen mass to the ruthenium catalyst mass in the zinc sulfate aqueous solution is 5 × 10 -6 It is preferable not to reduce it less than 1×10 -5 It is preferable not to reduce it below 1.5 x 10 -5 It is even more preferable not to do less than twice as much.

[0059] As described above, in the first embodiment, the nitrogen concentration in the zinc sulfate aqueous solution is set to 0.5 to 1500 mg / L, the nitrogen concentration in the monocyclic aromatic hydrocarbon is set to 0.01 to 16 mg / L, and the ratio of the nitrogen mass to the ruthenium catalyst mass in the zinc sulfate aqueous solution is set to 1×10 -5 ~5×10 -2 Alternatively, it is preferable to carry out a partial hydrogenation reaction of monocyclic aromatic hydrocarbons to produce cycloolefins. This makes it possible to maintain high catalytic activity in the partial hydrogenation reaction of monocyclic aromatic hydrocarbons and high selectivity for cycloolefins, stabilize the performance of the ruthenium catalyst, reduce the number of complicated operations such as replacing or adding ruthenium catalyst when producing cycloolefins over a long period of time, effectively suppress a decrease in cycloolefin selectivity, and enable stable and efficient production of cycloolefins over a long period of time.

[0060] (Nitrogen-containing components) In this embodiment, the nitrogen-containing components that indicate the nitrogen concentration in the aqueous zinc sulfate solution include substances that enter the reaction system contained in monocyclic aromatic hydrocarbons and hydrogen, which are raw materials for producing cycloolefins, as well as substances that enter the reaction system through recycled monocyclic aromatic hydrocarbons. Such substances include components such as dimethylamine, dimethylacetamide, monoethanolamine, ammonia, pyrrole, pyridine, and quinoline.

[0061] According to the investigations and studies of the present inventors, it has been found that among these nitrogen-containing components, dimethylamine is contained in large amounts in aqueous zinc sulfate solutions. In the method for producing a cycloolefin according to the first embodiment, the aqueous zinc sulfate solution contains dimethylamine. The dimethylamine is a decomposition product of dimethylacetamide, which is used as an extraction solvent in the product separation and purification process after undergoing a partial hydrogenation reaction process. Dimethylamine is formed through hydrolysis or thermal decomposition with the minute amount of water carried into the product separation and purification process, and is mixed with the recycled monocyclic aromatic hydrocarbons and enters the aqueous zinc sulfate solution in the hydrogenation reaction system. Furthermore, when dimethylacetamide is hydrolyzed, acetic acid is produced in addition to dimethylamine. This acetic acid acts as a catalyst to promote the decomposition of dimethylacetamide, leading to an increase in dimethylamine. Furthermore, dimethylacetamide that enters the hydrogenation reaction system may be hydrolyzed in the zinc sulfate aqueous solution to form dimethylamine. Due to these effects, dimethylamine accounts for a large proportion of the nitrogen-containing components contained in the zinc sulfate aqueous solution. As described above, in the first embodiment, it is important to control the concentration of dimethylamine in the aqueous zinc sulfate solution.

[0062] (Concentration of dimethylamine in zinc sulfate aqueous solution) In the method for producing a cycloolefin according to the first embodiment, the concentration of dimethylamine in the aqueous zinc sulfate solution to which the ruthenium catalyst is added is preferably in the range of 1.7 to 9900 mg / L, more preferably in the range of 1.7 to 4950 mg / L, even more preferably in the range of 1.7 to 3300 mg / L, still more preferably in the range of 40 to 1700 mg / L, and even more preferably in the range of 80 to 1000 mg / L. By keeping the dimethylamine concentration in the zinc sulfate aqueous solution at 1.7 mg / L or higher, it is possible to reduce the load on the equipment and operation, as well as to maintain stable ruthenium catalyst performance, while by keeping it at 9,900 mg / L or lower, it is possible to prevent a decrease in ruthenium catalyst activity and cycloolefin selectivity. The concentration of dimethylamine in the aqueous zinc sulfate solution can be measured by the method described in the Examples below. The concentration of dimethylamine in the aqueous zinc sulfate solution can be controlled within the above-mentioned range by adjusting the distillation separation performance of dimethylamine that enters the reactor through the recycled monocyclic aromatic hydrocarbons, adjusting the conditions of the equipment that removes nitrogen components in the monocyclic aromatic hydrocarbons before they enter the reactor, adjusting the conditions of the extraction and separation step that is the source of dimethylamine, or by withdrawing the aqueous zinc sulfate solution containing dimethylamine from the reaction system and replenishing the reactor with fresh aqueous zinc sulfate solution, for example.

[0063] (Dimethylamine concentration in monocyclic aromatic hydrocarbons) Furthermore, the concentration of dimethylamine in all monocyclic aromatic hydrocarbons entering the reaction field of the zinc sulfate aqueous solution, including the recycled monocyclic aromatic hydrocarbons, is preferably in the range of 0.01 to 115 mg / L, more preferably in the range of 0.04 to 52 mg / L, and even more preferably in the range of 0.04 to 33 mg / L. By keeping the dimethylamine concentration in the monocyclic aromatic hydrocarbons at 0.01 mg / L or higher, it is possible to reduce the load on the equipment and operation, as well as to maintain stable ruthenium catalyst performance. By keeping the concentration at 115 mg / L or lower, it is possible to suppress an increase in the dimethylamine concentration in the zinc sulfate aqueous solution. The concentration of dimethylamine in the monocyclic aromatic hydrocarbon can be measured by the method described in the Examples below. The concentration of dimethylamine in the monocyclic aromatic hydrocarbons can be controlled within the above-mentioned range by adjusting the conditions for separating and purifying the monocyclic aromatic hydrocarbons, adjusting the conditions of the dimethylamine removal equipment, or adjusting the conditions of the extraction and separation step that is the source of dimethylamine.

[0064] (ratio of dimethylamine mass to ruthenium catalyst mass) Furthermore, the ratio of the mass of dimethylamine to the mass of the ruthenium catalyst in the zinc sulfate aqueous solution is 2 × 10 -5 The range of 0.26 times is preferable, and 4 × 10 -5 A range of 0.16 times or less is more preferable, and a range of 5×10 -5 A range of 0.1 times or less is more preferable, and a range of 8×10 -4 ~6×10 -2 A range of 1×10 is more preferable. -3 ~4×10 -2 It is more preferable that the range is 2 times. The ratio of the mass of ruthenium catalyst to the mass of dimethylamine is 2 × 10 -5By setting the ratio to 0.26 or more, the effect of stabilizing the ruthenium catalyst performance can be obtained, in addition to the effect of reducing the load on the equipment and operation, and the effect of stabilizing the ruthenium catalyst activity and cycloolefin selectivity can be obtained by setting the ratio to 0.26 or less. The ratio of the mass of dimethylamine to the mass of the ruthenium catalyst can be measured by the method described in the Examples below. The ratio of the mass of dimethylamine to the mass of the ruthenium catalyst can be controlled within the above range by taking measures to reduce the amount of dimethylamine in the aqueous zinc sulfate solution or by adjusting the amount of ruthenium catalyst added.

[0065] (Acetic acid concentration in zinc sulfate aqueous solution) In the method for producing cycloolefin according to the first embodiment, the concentration of acetic acid in the aqueous zinc sulfate solution is 1×10 -3 It is preferable to set the range to 100 mg / L. Acetic acid is subjected to a partial hydrogenation reaction step, and the product is separated. The acetic acid then enters the reactor via monocyclic aromatic hydrocarbons recycled from the subsequent purification step of monocyclic aromatic hydrocarbons for recycling. The reaction liquid after the partial hydrogenation reaction contains partially hydrogenated cycloolefins, fully hydrogenated cycloalkanes, and unreacted monocyclic aromatic hydrocarbons. To separate this reaction liquid, dimethylacetamide is used as a known extractant. When dimethylacetamide is used as an extractant, acetic acid is generated as a decomposition product. If this product cannot be sufficiently separated in the purification process of the recycled monocyclic aromatic hydrocarbons, the acetic acid will be mixed into the partial hydrogenation reaction field together with the recycled monocyclic aromatic hydrocarbons. By keeping the acetic acid concentration in the zinc sulfate aqueous solution, which is the reaction field, at 100 mg / L or less, the decrease in the reaction selectivity of the catalyst can be suppressed. The acetic acid concentration in the zinc sulfate aqueous solution is preferably 75 mg / L or less, and more preferably 50 mg / L or less. The effect of acetic acid on the catalyst's reaction selectivity is thought to be due to its adverse effect on the adsorption and desorption of the raw materials, monocyclic aromatic hydrocarbons and cycloolefins, on the catalyst. In the reaction field, monocyclic aromatic hydrocarbons dissolved in the aqueous phase (aqueous zinc sulfate solution) are partially hydrogenated on the catalyst, converted to cycloolefins, and desorbed from the catalyst. The presence of acetic acid may modify the catalyst surface, promoting the reaction of monocyclic aromatic hydrocarbons in the oil phase and leading to an increase in cycloalkanes. It may also make it more difficult for the reaction products to desorb from the catalyst surface in the aqueous phase until they are converted from cycloolefins to cycloalkanes. The concentration of acetic acid in the aqueous zinc sulfate solution can be measured by the method described in the Examples below.

[0066] The concentration of acetic acid in an aqueous zinc sulfate solution can be measured by ion chromatography (IC). One method for controlling the acetic acid concentration in the aqueous zinc sulfate solution to 100 mg / L or less is to keep the acetic acid concentration contained in the recycled monocyclic aromatic hydrocarbons low. In the separation of the monocyclic aromatic hydrocarbons to be recycled from the extractant, it is effective to reduce the concentration of acetic acid in the monocyclic aromatic hydrocarbons to be recycled by appropriately setting the distillation purification conditions. In addition, since acetic acid is a decomposition product of dimethylacetamide used as the extractant, it is effective to prevent water, which promotes decomposition, from entering the extraction separation process where dimethylacetamide is present, and to avoid excessively high temperatures in the separation process.

[0067] However, there is a practical limit to the reduction of the acetic acid concentration in the zinc sulfate aqueous solution. Considering the equipment load for purification and separation and the load on operating conditions, the acetic acid concentration in the zinc sulfate aqueous solution is limited to 1 × 10 -3 It is preferable to control it at 1×10 mg / L or more. -2 If it is more than mg / L, it will be easier to manage.

[0068] In the first embodiment, the acetic acid in the aqueous zinc sulfate solution comes from the raw materials including the recycled monocyclic aromatic hydrocarbons, but not all of the incoming acetic acid accumulates in the aqueous zinc sulfate solution, and some of it is extracted to the outside of the reactor system together with the reaction product. In other words, by reducing the amount of acetic acid coming into the reaction field, the acetic acid concentration in the aqueous zinc sulfate solution can be reduced. On the other hand, reducing the amount of acetic acid coming from raw materials, including recycled monocyclic aromatic hydrocarbons, requires increasing the load on the separation and purification process of recycled monocyclic aromatic hydrocarbons and taking measures to prevent the decomposition of the extractant, dimethylacetamide. Furthermore, it takes time to gradually remove the acetic acid that has entered the zinc sulfate aqueous solution along with the reaction products, thereby reducing the amount of acetic acid. Therefore, an effective method for reducing the acetic acid concentration in the zinc sulfate aqueous solution in the reaction field is to replace part of the zinc sulfate aqueous solution with a new zinc sulfate aqueous solution that does not contain acetic acid. The reactivity that was reduced by the influence of acetic acid can be recovered by reducing the acetic acid concentration that once increased in the zinc sulfate aqueous solution by replacing it with a new zinc sulfate aqueous solution. -3 Even if the acetic acid concentration falls outside the appropriate range of up to 100 mg / L, the replacement operation can return the acetic acid concentration to the above appropriate range.

[0069] (Acetic acid concentration in monocyclic aromatic hydrocarbons) In the method for producing cycloolefin of the first embodiment, the concentration of acetic acid contained in the monocyclic aromatic hydrocarbon is 1×10 -4 It is preferable to set it in the range of up to 5 mg / L. In this case, the monocyclic aromatic hydrocarbons include both the monocyclic aromatic hydrocarbons used at the beginning of the production process and the monocyclic aromatic hydrocarbons that are recycled. The acetic acid in the monocyclic aromatic hydrocarbons can be reduced and controlled to fall within the above-mentioned range by suppressing its generation in the extraction and separation step, by performing separation and purification to remove or reduce the amount of acetic acid generated as an impurity of the monocyclic aromatic hydrocarbons, by reducing and removing the acetic acid using an adsorbent, by washing the monocyclic aromatic hydrocarbons with water, or the like. By specifying the acetic acid concentration in the monocyclic aromatic hydrocarbon to 5 mg / L or less, the rate at which the acetic acid concentration in the zinc sulfate aqueous solution gradually increases can be suppressed, and a decrease in the performance of the partial hydrogenation reaction can be prevented. That is, the concentration of acetic acid in the monocyclic aromatic hydrocarbon is preferably 5 mg / L or less, more preferably 3 mg / L or less, and even more preferably 1.5 mg / L or less. On the other hand, the concentration of acetic acid in monocyclic aromatic hydrocarbons is 1×10 -4 Lowering the concentration below 10 mg / L increases the operational and analytical loads required to reduce and remove acetic acid and maintain low concentrations. -4 It is preferable to set the concentration to 1×10 mg / L or more. -3 By setting the concentration at mg / L or higher, the operational load and analytical load for separation and purification can be reduced. The concentration of acetic acid contained in monocyclic aromatic hydrocarbons can be determined by adding water to the aromatic hydrocarbon sample to be measured to concentrate and extract it, and then measuring the extracted water using ion chromatography. Alternatively, samples with a concentration of 1 mg / L or more can be analyzed using gas chromatography (GC).

[0070] (ratio of acetic acid mass to ruthenium catalyst mass) In the first embodiment of the cycloolefin production method, the ratio of the mass of acetic acid to the mass of the ruthenium catalyst in the zinc sulfate aqueous solution is 3 × 10 -9 ~2.5×10 -3 It is preferable to set the range to 1×10. -8 ~2×10 -3 times, and more preferably 1×10 -7 ~1.5×10 -3 times, and more preferably 1×10 -6 ~5×10 -4 times, and even more preferably 3×10 -6 ~5×10 -4 The ratio of the mass of acetic acid to the mass of the ruthenium catalyst in the aqueous zinc sulfate solution can be calculated as the ratio of the total solid catalyst concentration (mg / L) in the reaction solution to the amount of acetic acid (mg / L) in the aqueous zinc sulfate solution.

[0071] In the first embodiment, a ruthenium catalyst is used as a catalyst for producing cycloolefins by partial hydrogenation of monocyclic aromatic hydrocarbons. In the zinc sulfate aqueous solution, ruthenium adsorbs monocyclic aromatic hydrocarbons and hydrogen and desorbs them as cycloolefins. During this process, if acetic acid enters the zinc sulfate aqueous solution, the reactivity of the ruthenium catalyst is inhibited. Therefore, the amount of acetic acid is preferably within a range that does not affect the inhibition of the ruthenium catalyst reaction. It is preferable to control the acetic acid concentration in the zinc sulfate aqueous solution as the acetic acid present in the reaction field, the acetic acid concentration contained in the recycled monocyclic aromatic hydrocarbons, and the acetic acid concentration per catalyst. If the acetic acid concentration in the zinc sulfate aqueous solution or the acetic acid concentration per catalyst rises above the preferred range, the reactivity of the ruthenium catalyst can be restored by replacing the zinc sulfate aqueous solution in the reaction field to return it to the preferred range.

[0072] (Preferred mode of the method for producing cycloolefin in the first embodiment) In the method for producing cycloolefin according to the first embodiment, a reaction step of partially hydrogenating the monocyclic aromatic hydrocarbon with hydrogen in the aqueous zinc sulfate solution; an extraction step of extracting the unreacted monocyclic aromatic hydrocarbons with a solvent containing a nitrogen-containing compound after the reaction step; a water washing step in which the extracted monocyclic aromatic hydrocarbons are brought into contact with water in an amount of 0.05 to 1 volume times; a recycling step of subjecting the water-washed monocyclic aromatic hydrocarbons to the reaction step; , and In the reaction step, the content of dimethylamine in the zinc sulfate aqueous solution is 40 to 1700 mg / L, and the ratio of the mass of dimethylamine to the mass of the ruthenium catalyst is 8 × 10 -4 ~6×10 -2 It is preferable to control the temperature to twice as high as possible. This makes it possible to maintain high catalytic activity in the partial hydrogenation reaction and high cycloolefin selectivity, and also to maintain high catalytic activity and cycloolefin selectivity even after catalyst regeneration. By stabilizing the catalytic activity, the number of complicated operations such as replacing the catalyst or adding unused catalyst during long-term cycloolefin production can be reduced, and a decrease in cycloolefin selectivity can be effectively suppressed, allowing cycloolefins to be produced efficiently and stably over a long period of time. The dimethylamine content in the aqueous zinc sulfate solution can be controlled within the above-mentioned range by adjusting the distillation separation performance of dimethylamine that enters the reactor through the recycled monocyclic aromatic hydrocarbons, adjusting the conditions of the equipment that removes nitrogen components from the monocyclic aromatic hydrocarbons before they enter the reactor, adjusting the conditions of the extraction and separation step that is the source of dimethylamine, or by withdrawing the aqueous zinc sulfate solution containing dimethylamine from the reaction system and replenishing the reactor with fresh aqueous zinc sulfate solution, for example. The volume of water to be contacted in the water washing step is preferably 0.05 to 0.8 times, more preferably 0.08 to 0.6 times, the volume of the monocyclic aromatic hydrocarbon. The ratio of the mass of dimethylamine to the mass of the ruthenium catalyst can be controlled within the above range by taking measures to reduce the amount of dimethylamine in the aqueous zinc sulfate solution or by adjusting the amount of ruthenium catalyst added.

[0073] [Method for producing cycloolefin according to the second embodiment] The method for producing a cycloolefin of the second embodiment (hereinafter, may be simply referred to as the present embodiment) relates to a method for producing a cycloolefin by subjecting a monocyclic aromatic hydrocarbon to a partial hydrogenation reaction with hydrogen in an aqueous zinc sulfate solution in the presence of a ruthenium catalyst. In a second embodiment, the concentration of acetic acid in the zinc sulfate aqueous solution is 1×10 -3 The concentration is adjusted to 100 mg / L and a partial hydrogenation reaction is carried out. According to the second embodiment, the catalytic activity of the partial hydrogenation reaction and the selectivity to cycloolefins can be maintained at high levels, and the catalytic activity and the selectivity to cycloolefins can be maintained at high levels even after catalyst regeneration. By stabilizing the catalytic performance, the number of complicated operations such as replacing the catalyst or adding unused catalyst during long-term cycloolefin production can be reduced, a decrease in cycloolefin selectivity can be effectively suppressed, and cycloolefins can be produced efficiently and stably over a long period of time.

[0074] (monocyclic aromatic hydrocarbons) In the method for producing cycloolefins according to the second embodiment, monocyclic aromatic hydrocarbons are used as raw materials. Examples of monocyclic aromatic hydrocarbons include, but are not limited to, benzene, toluene, and benzene substituted with an alkyl group having 1 to 4 carbon atoms, such as xylene, and the same ones as in the first embodiment described above can be used.

[0075] (hydrogen pressure) In the second embodiment, from the same viewpoint as in the first embodiment described above, the hydrogen pressure when carrying out the partial hydrogenation reaction with hydrogen is generally 1 to 20 MPa, and preferably 2 to 7 MPa.

[0076] (Reaction temperature) The temperature during the partial hydrogenation reaction is generally 50 to 250°C, preferably 100 to 200°C, from the same viewpoint as in the first embodiment described above.

[0077] (Ruthenium catalyst) In a second embodiment, a partial hydrogenation reaction of monocyclic aromatic hydrocarbons is carried out in the presence of a ruthenium catalyst. The ruthenium catalyst is preferably a catalyst containing metallic ruthenium obtained by reducing various ruthenium compounds in advance, and the same ruthenium catalyst as that used in the first embodiment described above can be used.

[0078] (Zinc sulfate aqueous solution) In the second embodiment of the cycloolefin production method, the partial hydrogenation reaction of monocyclic aromatic hydrocarbons is carried out in an aqueous zinc sulfate solution. The same materials as those used in the first embodiment can be used as the aqueous zinc sulfate solution. In the second embodiment, the acetic acid concentration in the aqueous zinc sulfate solution is specified to fall within a predetermined range. The acetic acid concentration will be described later.

[0079] <Acetic acid concentration in zinc sulfate aqueous solution> In the second embodiment of the cycloolefin production method, the acetic acid concentration in the zinc sulfate aqueous solution is 1×10 -3 The range should be ~100mg / L. Acetic acid enters the reactor through the monocyclic aromatic hydrocarbons used as raw materials, particularly through the monocyclic aromatic hydrocarbons recycled from the purification process of monocyclic aromatic hydrocarbons that are separated as products after passing through a partial hydrogenation reaction process. The reaction liquid after the partial hydrogenation reaction contains partially hydrogenated cycloolefins, fully hydrogenated cycloalkanes, and unreacted monocyclic aromatic hydrocarbons. To separate this reaction liquid, dimethylacetamide is used as a known extractant. When dimethylacetamide is used as an extractant, acetic acid is generated as a decomposition product. If this product cannot be sufficiently separated in the purification process of the recycled monocyclic aromatic hydrocarbons, the acetic acid will be mixed into the partial hydrogenation reaction field together with the recycled monocyclic aromatic hydrocarbons. By keeping the acetic acid concentration in the zinc sulfate aqueous solution, which is the reaction field, at 100 mg / L or less, the decrease in the reaction selectivity of the catalyst can be suppressed. The acetic acid concentration in the zinc sulfate aqueous solution is preferably 75 mg / L or less, and more preferably 50 mg / L or less. Regarding the effect of acetic acid on the reaction selectivity of the catalyst, it is thought to have a negative effect on the adsorption and desorption of the raw material monocyclic aromatic hydrocarbons and cycloolefins on the catalyst. In the hydrogenation reaction field, monocyclic aromatic hydrocarbons dissolved in the aqueous phase, i.e., an aqueous zinc sulfate solution, are partially hydrogenated on the catalyst, converted to cycloolefins, and then desorbed from the catalyst. The presence of acetic acid may modify the catalyst surface, promoting the reaction of monocyclic aromatic hydrocarbons in the oil phase and leading to an increase in cycloalkanes. It is also thought that the presence of acetic acid may make it more difficult for the reaction products to desorb from the catalyst surface in the aqueous phase until they are converted from cycloolefins to cycloalkanes. The concentration of acetic acid in the aqueous zinc sulfate solution can be measured by the method described in the Examples below.

[0080] The concentration of acetic acid in an aqueous zinc sulfate solution can be measured by ion chromatography (IC). One method for suppressing the acetic acid concentration in the aqueous zinc sulfate solution to 100 mg / L or less is to suppress the acetic acid concentration contained in the monocyclic aromatic hydrocarbons to be recycled. In the separation process of recycled monocyclic aromatic hydrocarbons and the extractant, it is effective to reduce the concentration of acetic acid in the recycled monocyclic aromatic hydrocarbons by appropriately setting the distillation purification conditions. In addition, to reduce the acetic acid generated in the distillation purification, it is also effective to use a purification column for the extractant dimethylacetamide, which discharges acetic acid together with other impurities from the extraction separation process, or to use a water washing column to reduce the acetic acid in the recycled monocyclic aromatic hydrocarbons. Furthermore, because acetic acid is a decomposition product of dimethylacetamide used as an extractant, it is also effective to prevent water, which promotes decomposition, from entering the extraction separation process where dimethylacetamide is present, and to take measures to avoid excessively raising the temperature in the separation process.

[0081] However, there is a practical limit to the reduction of the acetic acid concentration in the zinc sulfate aqueous solution. Considering the equipment load for purification and separation and the load on operating conditions, the acetic acid concentration in the zinc sulfate aqueous solution is limited to 1 × 10 -3 It is preferable to control it at 1×10 mg / L or more. -2If it is more than mg / L, it will be easier to manage.

[0082] (Partial replacement of zinc sulfate aqueous solution) In the first embodiment, the acetic acid in the aqueous zinc sulfate solution is introduced from the raw materials including the recycled monocyclic aromatic hydrocarbons, but not all of the introduced acetic acid is accumulated in the aqueous zinc sulfate solution, and some of the acetic acid is extracted to the outside of the reactor system together with the reaction product. In other words, by reducing the amount of acetic acid introduced into the reaction field, the acetic acid concentration in the aqueous zinc sulfate solution can be reduced. On the other hand, reducing the acetic acid content of raw materials, including recycled monocyclic aromatic hydrocarbons, requires increasing the load on the separation and purification process of recycled monocyclic aromatic hydrocarbons and preventing the decomposition of the extractant, dimethylacetamide. Furthermore, it takes time to gradually reduce the acetic acid, once it has entered the zinc sulfate aqueous solution, along with the reaction products. Therefore, an effective method for reducing the acetic acid concentration in the zinc sulfate aqueous solution in the reaction field is to replace part of the zinc sulfate aqueous solution with a new zinc sulfate aqueous solution, i.e., a zinc sulfate aqueous solution that does not contain acetic acid. The reactivity that was reduced by the influence of acetic acid can be recovered by reducing the acetic acid concentration that once increased in the zinc sulfate aqueous solution by replacing it with a new zinc sulfate aqueous solution. -3 Even if the acetic acid concentration falls outside the appropriate range of up to 100 mg / L, the replacement operation can return the acetic acid concentration to the above appropriate range.

[0083] (Acetic acid concentration in monocyclic aromatic hydrocarbons) In the second embodiment of the cycloolefin production method, the concentration of acetic acid contained in the monocyclic aromatic hydrocarbon is 1×10 -4 It is preferable to set it in the range of up to 5 mg / L. In this case, the monocyclic aromatic hydrocarbons include both the monocyclic aromatic hydrocarbons used at the beginning of the production process and the monocyclic aromatic hydrocarbons that are recycled. The acetic acid in the monocyclic aromatic hydrocarbons can be reduced and controlled to fall within the above-mentioned range by suppressing its generation in the extraction and separation step of the recycled monocyclic aromatic hydrocarbons, by performing separation and purification to remove or reduce the generated acetic acid as an impurity of the monocyclic aromatic hydrocarbons, by reducing and removing it using an adsorbent, by washing the monocyclic aromatic hydrocarbons with water, or the like. By specifying the acetic acid concentration in the monocyclic aromatic hydrocarbon to be 5 mg / L or less, a gradual increase in the acetic acid concentration in the aqueous zinc sulfate solution in the presence of a ruthenium catalyst can be prevented, and the acetic acid concentration in the aqueous zinc sulfate solution can be set to 100 mg / L or less, thereby preventing a decrease in the performance of the partial hydrogenation reaction. That is, the concentration of acetic acid in the monocyclic aromatic hydrocarbon is preferably 5 mg / L or less, more preferably 3 mg / L or less, and even more preferably 1.5 mg / L or less. On the other hand, the concentration of acetic acid in monocyclic aromatic hydrocarbons is 1×10 -4 Lowering the concentration below 10 mg / L increases the operational and analytical loads required to reduce and remove acetic acid and maintain low concentrations. -4 It is preferable to set the concentration to 1×10 mg / L or more. -3 By setting the concentration at mg / L or more, the operational load and analytical load for separation and purification can be further reduced. The concentration of acetic acid in the monocyclic aromatic hydrocarbon can be measured by the method described in the Examples below.

[0084] (ratio of acetic acid mass to ruthenium catalyst mass) In the method for producing a cycloolefin according to the second embodiment, a ruthenium catalyst is used as a catalyst for producing a cycloolefin by a partial hydrogenation reaction of a monocyclic aromatic hydrocarbon. In a second embodiment, the ratio of the mass of acetic acid to the mass of the ruthenium catalyst in the aqueous zinc sulfate solution is 3×10 -9 ~2.5×10 -3 It is preferable to set the range to 1×10. -8 ~2×10 -3 times, and more preferably 1×10 -7 ~1.5×10 -3 times 1 x 10 -6 ~5×10-4 Double is even more preferable. The ratio of the mass of acetic acid to the mass of the ruthenium catalyst can be calculated by the method described in the Examples below.

[0085] The partial hydrogenation reaction of monocyclic aromatic hydrocarbons is carried out in an aqueous zinc sulfate solution by a ruthenium catalyst adsorbing monocyclic aromatic hydrocarbons and hydrogen to form cycloolefins, which are then desorbed from the catalyst. If acetic acid enters the aqueous zinc sulfate solution during this reaction, it inhibits the adsorption and desorption properties of the ruthenium catalyst, resulting in a decrease in reactivity. Therefore, the concentration of acetic acid in the aqueous zinc sulfate solution is preferably within a range that does not have an effect on inhibiting the reaction of the ruthenium catalyst, and it is necessary to control the concentration of acetic acid in the aqueous zinc sulfate solution, which is the reaction field, the concentration of acetic acid contained in the recycled monocyclic aromatic hydrocarbons, and the ratio of the mass of acetic acid to the mass of the ruthenium catalyst. If the acetic acid concentration in the aqueous zinc sulfate solution or the ratio of the mass of acetic acid to the mass of the ruthenium catalyst exceeds the preferred range, the reactivity of the ruthenium catalyst can be restored by replacing the aqueous zinc sulfate solution in the reaction field to return it to the preferred range.

[0086] (Preferable Mode of the Method for Producing Cycloolefin in the Second Embodiment) In the method for producing cycloolefin according to the second embodiment, a reaction step of partially hydrogenating the monocyclic aromatic hydrocarbon with hydrogen in the aqueous zinc sulfate solution; an extraction step of extracting the unreacted monocyclic aromatic hydrocarbons with a solvent containing a nitrogen-containing compound after the reaction step; a water washing step in which the extracted monocyclic aromatic hydrocarbons are brought into contact with water in an amount of 0.05 to 1 volume times; a recycling step of subjecting the water-washed monocyclic aromatic hydrocarbons to the reaction step; , and In the reaction step, the ratio of the mass of acetic acid to the mass of the ruthenium catalyst in the zinc sulfate aqueous solution is 1×10 -6 ~5×10 -4It is preferable to control the temperature to twice as high as possible. This makes it possible to maintain high catalytic activity in the partial hydrogenation reaction and high cycloolefin selectivity, and also to maintain high catalytic activity and cycloolefin selectivity even after catalyst regeneration. By stabilizing the catalytic activity, the number of complicated operations such as replacing the catalyst or adding unused catalyst during long-term cycloolefin production can be reduced, and a decrease in cycloolefin selectivity can be effectively suppressed, allowing cycloolefins to be produced efficiently and stably over a long period of time. The volume of water to be contacted in the water washing step is preferably 0.05 to 0.8 times, more preferably 0.08 to 0.6 times, the volume of the monocyclic aromatic hydrocarbon. The ratio of the mass of acetic acid to the mass of the ruthenium catalyst in the aqueous zinc sulfate solution can be controlled within the above range by replacing the aqueous zinc sulfate solution in the reaction field.

[0087] [Regeneration of ruthenium catalyst] In the cycloolefin production methods of the first and second embodiments, a part or all of the ruthenium catalyst can be regenerated and reused. By regenerating and reusing a part or all of the ruthenium catalyst, it is possible to suppress the decrease in catalytic activity and cycloolefin selectivity. By regenerating a part or all of the ruthenium catalyst, it is possible to remove components that may poison the catalytic reaction surface, and to regenerate the activity of the catalyst that has deteriorated after use. The ruthenium catalyst to be regenerated is preferably a zirconia-containing ruthenium catalyst from the viewpoint of increasing the regeneration efficiency and extending the catalyst life.

[0088] In the cycloolefin production methods of the first and second embodiments, examples of substances whose amounts in the aqueous zinc sulfate solution need to be controlled include nitrogen-containing components, particularly dimethylamine, and acetic acid, which are thought to be involved in the generation of substances that reduce reaction performance and to poison or alter the catalytic reaction surface. In particular, when the partial hydrogenation reaction of monocyclic aromatic hydrocarbons is carried out continuously, substances that poison or alter the ruthenium catalyst present in the aqueous zinc sulfate solution tend to bind strongly to the surface of the ruthenium catalyst over time, making it difficult to desorb or remove. In addition, the agglomeration of the ruthenium catalyst components also progresses gradually, and if the poisoning or altering substances are present there, they tend to be incorporated into the agglomeration of the ruthenium catalyst components, making it increasingly difficult to desorb or remove them from the catalyst surface. By performing catalyst regeneration treatment, it is possible to detach and remove substances that are strongly bound to the catalyst surface and that poison or alter the catalyst, as described above, thereby suppressing catalyst agglomeration, redispersing the agglomerated catalyst components, and separating the substances that poison or alter the catalyst from the catalyst surface, thereby suppressing a decrease in catalyst activity and cycloolefin selectivity.

[0089] The amount of ruthenium catalyst to be regenerated may be all or a portion, and can be selected appropriately depending on the production line. Furthermore, the catalyst regeneration method can be carried out either batchwise or continuously.

[0090] Regenerating the entire catalyst has the following advantages: That is, when the reaction is carried out in a batch system, it is preferable to regenerate the entire amount, from the viewpoint that the activity and selectivity of the catalyst after regeneration can be easily controlled by understanding the relationship between the regeneration conditions, the activity of the catalyst after regeneration, and the cycloolefin selectivity through basic experiments. On the other hand, regenerating a portion of the catalyst has the following advantages. When a part of the catalyst is regenerated, the regenerated catalyst and the unregenerated catalyst are mixed and reused. With regard to catalyst activity and cycloolefin selectivity, a state in which optimal amounts of hydrogen and metal ions are adsorbed on ruthenium is preferable, and mixing a catalyst that has been regenerated, which involves a rapid change on ruthenium, with a catalyst that has not been regenerated can create a state in which hydrogen and metal ions are adsorbed on ruthenium in a relatively mild manner, which is preferable from the viewpoint of maintaining a good balance between activity and cycloolefin selectivity during long-term catalyst use.

[0091] When cycloolefins are produced by a batch reaction, the aforementioned portion preferably represents 5 to 80% by mass of the catalyst used in the reaction. More preferably, it is 10 to 60% by mass. Furthermore, in a continuous reaction, it is practical to vary the amount of catalyst regenerated depending on the degree of deterioration in catalytic performance per hour. For example, it is preferable that 5 to 80% by mass of the entire catalyst be regenerated within 24 hours. More preferably, it is 10 to 60% by mass.

[0092] There is no particular limitation on the method of extracting part or all of the catalyst from the continuous reaction, subjecting it to regeneration treatment, and returning it to the reactor for the partial hydrogenation reaction. For example, in the case of a continuous reaction, the continuous reaction may be stopped once, the oil phase may be removed, and the entire liquid phase containing the catalyst may be regenerated, and then the partial hydrogenation reaction may be resumed. Alternatively, the liquid phase containing the catalyst may be partially extracted without stopping the continuous reaction, and recharged into the reactor for the partial hydrogenation reaction while being regenerated. Examples of an apparatus and operation method for continuously withdrawing a liquid phase containing a catalyst, regenerating it, and refilling it include the method disclosed in Japanese Patent No. 4397468 and an apparatus comprising a partial hydrogenation reactor, a jacketed cooler, and a jacketed activation treatment vessel.

[0093] As a method for regenerating the ruthenium catalyst, a known method can be used. For example, there are (1) a method in which the catalyst is contacted with oxygen in a liquid phase, and (2) a method in which the catalyst is maintained under a hydrogen partial pressure lower than the hydrogen partial pressure in the hydrogenation reaction and at a temperature not lower than 50°C lower than the temperature during the partial hydrogenation reaction. In the first method (1) of contacting the catalyst with oxygen in the liquid phase, the liquid phase state can be a state in which the ruthenium catalyst is dispersed in a suitable liquid in the form of a slurry, and although the amount of liquid can be small, it is necessary that at least the surface of the catalyst is covered with the liquid. The liquid used can be any liquid that does not adversely affect the ruthenium catalyst or its carrier, and is preferably water. When the catalyst is brought into contact with oxygen in the liquid phase, the oxygen source may be oxygen gas, a gas containing molecular oxygen such as air, or a compound that releases nascent oxygen such as hydrogen peroxide. Oxygen gas may be used as is, but it is preferable to use it after diluting it with a suitable inert gas for ease of operation.

[0094] The oxygen concentration in the liquid phase is usually 1 x 10 converted to standard oxygen gas. -7 ~1 NmL / mL, preferably 1 × 10 -5 When the oxygen concentration is in this range, the treatment time can be kept relatively short, and irreversible changes due to rapid oxidation of the ruthenium on the catalyst surface can be prevented.

[0095] Oxygen may be supplied directly to the liquid phase in a slurry state. The most preferred method of supplying oxygen is to disperse the ruthenium catalyst in water and supply an oxygen-containing gas to the dispersion. This method is preferred because it is easy to operate.

[0096] The operation for restoring the activity of the ruthenium catalyst can be carried out under any of reduced pressure, normal pressure, and elevated pressure. It is also possible to apply pressure to increase the oxygen concentration in the liquid phase. The operating temperature for contacting the catalyst with oxygen can be in the range of 0 to 300°C, preferably 30 to 200°C, and more preferably 50 to 150°C. The operation time may be appropriately determined depending on the degree of decrease in activity of the catalyst to be treated and the desired degree of activity recovery, and is usually from several minutes to several days.

[0097] The second method, (2) regeneration of the catalyst by maintaining the catalyst under a hydrogen partial pressure lower than that in the hydrogenation reaction and at a temperature not lower than 50°C lower than that during the partial hydrogenation reaction, can be carried out in either the gas phase or the liquid phase. The hydrogen partial pressure may be lower than the hydrogen partial pressure in the partial hydrogenation reaction. However, if the difference between the two hydrogen partial pressures is small, a long period of time may be required for activity recovery. Therefore, the hydrogen partial pressure is preferably half or less of the hydrogen partial pressure in the partial hydrogenation reaction, and more preferably zero or close to zero. The operating temperature at which the catalyst is maintained is not lower than 50° C. below the temperature during the partial hydrogenation reaction, preferably not lower than 40° C. below, and more preferably not lower than 30° C. below. The operating temperature may exceed the temperature during the partial hydrogenation reaction, but if it is too high, there is a risk of irreversible changes occurring in the active sites of the catalyst, so it is preferable to select an upper limit of the operating temperature that is appropriate for the characteristics of the catalyst. For the ruthenium catalyst fine particles used in the first and second embodiments, it is preferable to maintain the catalyst at a temperature not exceeding 250°C, more preferably not exceeding 200°C, from the viewpoint of preventing physical denaturation of the catalyst. On the other hand, if the temperature is below a temperature 50°C lower than the temperature during the hydrogenation reaction, a significantly long treatment time may be required to restore activity. The retention time may be appropriately selected depending on the degree of activity decline of the catalyst to be treated and the target degree of activity recovery, but is usually several minutes to several days.

[0098] When the two ruthenium catalyst regeneration methods (1) and (2) described above are combined, either method may be performed first. Preferably, the method (1) of contacting the catalyst with oxygen in the liquid phase is performed first. In order to perform such an activity recovery operation, it is preferable to separate and remove in advance from the ruthenium catalyst any organic matter coexisting with the catalyst resulting from the partial hydrogenation reaction. Here, the organic matter coexisting with the catalyst refers to the raw material monocyclic aromatic hydrocarbons, reaction products, by-products, impurities, etc.

[0099] The ruthenium catalyst whose activity has been restored is washed and dried as appropriate to give it a preferred form, and then reused in the partial hydrogenation reaction of monocyclic aromatic hydrocarbons.

[0100] By extracting a part or all of the ruthenium catalyst and carrying out only the regeneration treatment, it is possible to recover to some extent the cycloolefin activity and selectivity of the catalyst whose performance has deteriorated, but this may not always be sufficient. In addition to the regeneration treatment of the ruthenium catalyst, by maintaining the concentrations of nitrogen-containing components dissolved in the zinc sulfate aqueous solution, particularly dimethylamine and acetic acid, within appropriate ranges, it is possible to effectively suppress the deterioration of the activity and cycloolefin selectivity of the ruthenium catalyst. In addition, since the regeneration performance of the ruthenium catalyst can be improved, high catalytic activity and cycloolefin selectivity can be maintained even after the regeneration treatment.

[0101] In addition to the regeneration treatment of the ruthenium catalyst, the mechanism of suppressing catalyst deterioration by maintaining the concentrations of nitrogen-containing components, particularly dimethylamine and acetic acid, within appropriate ranges is thought to be that if the concentrations of each component exceed the appropriate ranges, it becomes difficult to desorb and remove the nitrogen-containing components and acetic acid from the catalyst surface during the catalyst regeneration treatment.It is also thought that poisoning substances that were once desorbed from the catalyst surface during the catalyst regeneration treatment may be re-adsorbed onto the catalyst surface, causing a decrease in reaction performance again.

[0102] That is, even when extracting a part or all of the ruthenium catalyst for regeneration treatment, the nitrogen-containing components dissolved in the zinc sulfate aqueous solution are preferably in the range of 0.5 to 3000 mg / L, the dimethylamine is preferably in the range of 1.7 to 9900 mg / L, and the acetic acid concentration is preferably 1×10 -3 It is preferable to set the range to 100 mg / L. By maintaining the concentration of each component within an appropriate range, poisoning substances and substances that alter the ruthenium catalyst can be easily desorbed and removed from the catalyst surface, thereby suppressing a decrease in catalyst activity and selectivity not only in the short term but also in the long term.

[0103] [Zinc concentration in zirconia-containing ruthenium catalyst] In the first and second embodiments, the zinc concentration in the ruthenium catalyst is preferably maintained in the range of 0.5 to 3.5 mass%, more preferably 0.5 to 2.5 mass%, and even more preferably 0.5 to 1.8 mass%. The zinc concentration in the ruthenium catalyst can be measured by the method described in the Examples below. When the zinc concentration is set within the above range, a zirconia-containing ruthenium catalyst is particularly preferred from the viewpoint of improving the stability of the zinc concentration during the reaction and stabilizing the reactivity of the catalyst.

[0104] Nitrogen-containing components, dimethylacetamide, and dimethylamine, which enter the reaction field of the zinc sulfate aqueous solution, are alkaline and cause zinc salting out when they enter the zinc sulfate aqueous solution. The salted-out zinc covers the reaction sites of the ruthenium catalyst, reducing the reaction activity. One method for removing zinc, which causes a decrease in catalytic activity, is to add sulfuric acid to an aqueous zinc sulfate solution to dissolve the zinc that has salted out, thereby suppressing the decrease in activity. Furthermore, regeneration treatment of the catalyst can also reduce the amount of zinc adsorbed on the ruthenium surface, thereby suppressing the decrease in catalytic activity. On the other hand, adding sulfuric acid to an aqueous zinc sulfate solution or regenerating the catalyst also reduces the amount of zinc in the catalyst, which has the effect of increasing selectivity. From the above-mentioned viewpoint, in the first and second embodiments, it is preferable that the concentration of zinc in the ruthenium catalyst solid content be within the above-mentioned range. If the zinc concentration is lowered below 0.5% by mass, the selectivity to cycloolefins decreases, whereas if it exceeds 3.5% by mass, the activity decreases, and the zinc concentration is too high, which tends to inhibit the reaction and decrease the selectivity to cycloolefins.

[0105] That is, in a reaction field where nitrogen-containing components, dimethylacetamide, and dimethylamine enter an aqueous zinc sulfate solution, when sulfuric acid is added or the catalyst is regenerated, it is preferable to appropriately control the zinc concentration contained in the ruthenium catalyst from the viewpoint of stably maintaining the activity of the catalyst and the selectivity for cycloolefins. [Example]

[0106] Hereinafter, the present embodiment will be described in more detail with reference to specific examples and comparative examples, but the present invention is not limited to the following examples and comparative examples in any way. The methods for evaluating various physical properties are as follows.

[0107] [First Example] (Nitrogen concentration in zinc sulfate aqueous solution, nitrogen concentration in monocyclic aromatic hydrocarbons, ratio of nitrogen mass to zirconia-containing ruthenium catalyst mass) The nitrogen concentrations in the zinc sulfate aqueous solution and the monocyclic aromatic hydrocarbons were measured by the chemiluminescence method using a TS-2100V total nitrogen automatic analyzer manufactured by Nitto Seiko Analytech Co., Ltd. (formerly Mitsubishi Chemical Analytech Co., Ltd.). The ratio of the mass of nitrogen to the mass of the zirconia-containing ruthenium catalyst was determined as the ratio of the mass concentration of the total nitrogen to the mass concentration of the total solid catalyst in the aqueous zinc sulfate solution (total nitrogen concentration in the aqueous zinc sulfate solution / mass concentration of the total solid catalyst in the aqueous zinc sulfate solution). Specifically, the reaction solution, the aqueous zinc sulfate solution, and the zirconia-containing ruthenium catalyst were withdrawn from the reaction system in a completely mixed state and allowed to stand for separation, and the total nitrogen concentration in the aqueous zinc sulfate solution was measured using the above-mentioned analyzer. The mass concentration of the zirconia-containing ruthenium catalyst was determined as the solid concentration in the aqueous zinc sulfate solution after filtration and drying, thereby calculating the ratio of the mass of nitrogen to the mass of the zirconia-containing ruthenium catalyst.

[0108] (Dimethylamine concentration in zinc sulfate aqueous solution, dimethylamine concentration in monocyclic aromatic hydrocarbon, ratio of dimethylamine mass to zirconia-containing ruthenium catalyst mass) The concentration of dimethylamine in the aqueous zinc sulfate solution was measured using an IC-2010 ion chromatograph manufactured by Toso Techno Systems. The concentration of dimethylamine in the monocyclic aromatic hydrocarbons was measured using a gas chromatograph equipped with a Shimadzu GC-2014 FID detector. The ratio of the mass of dimethylamine to the mass of the zirconia-containing ruthenium catalyst was calculated from the measured concentration of dimethylamine in the aqueous zinc sulfate solution extracted from the reaction system and the solids concentration of the zirconia-containing ruthenium catalyst, in the same manner as in calculating the nitrogen concentration per catalyst.

[0109] (Zinc concentration in zirconia-containing ruthenium catalyst) The zinc concentration in the zirconia-containing ruthenium catalyst was measured using a Rigaku ZSX Primus II fluorescence analyzer. In analyzing small samples, the zirconia-containing ruthenium catalyst was dissolved in hydrochloric acid used for measuring hazardous metals, and the zinc concentration dissolved in the liquid was measured using a Hitachi High-Tech Science SPS3520UV-DD ICP device.

[0110] (average crystallite size of ruthenium) The average crystallite size of ruthenium was determined by Scherrer's equation from the broadening of the diffraction peak of ruthenium metal at a diffraction angle (2θ) of 44° obtained using an XRD-6100 X-ray diffractometer manufactured by Shimadzu Corporation.

[0111] (Benzene conversion and cyclohexene selectivity) A catalyst and hydrogen were charged into a 1L high-pressure autoclave reactor, and a predetermined amount of benzene was added all at once as a monocyclic aromatic hydrocarbon while the temperature and hydrogen pressure were set. Reaction evaluation was carried out using the batch method under the specified reaction temperature and hydrogen pressure. A batch reaction, also known as a batch reaction, involves placing an aqueous zinc sulfate solution containing a catalyst into an autoclave, and then adding the raw material benzene once at the start of the reaction under set temperature, pressure, and time conditions, and then recovering the entire amount once the reaction is complete. After adding benzene, a portion of the reaction liquid was extracted and analyzed using a gas chromatograph (Shimadzu GC-2014) equipped with an FID detector. Based on the experimental concentration analysis values, the reaction conversion rate and selectivity over time were calculated using the following calculation formulas (1) and (2). Furthermore, the selectivity at a conversion rate of 50% was calculated by plotting the analytical data. In addition, a 4L continuous tank reactor (CSTR) was charged with the catalyst, and benzene and hydrogen were continuously introduced to evaluate the reaction progress using a continuous flow method. In a continuous flow reaction, the raw material benzene is continuously introduced into the reactor, and the reaction product is continuously removed from the reactor, allowing the reaction to be carried out continuously under constant conditions over a long period of time. By controlling the temperature, pressure, catalyst amount, and benzene flow rate, the benzene conversion rate can be adjusted, and the cyclohexene selectivity can be determined. In this example, the benzene conversion was set to approximately 50%, and the reaction solution was analyzed using a gas chromatograph (GC-2014, manufactured by Shimadzu Corporation) equipped with an FID detector, as in the batch process. Based on the experimental concentration analysis values, the benzene conversion and cyclohexene selectivity were calculated using the following calculation formulas (1) and (2). Although the reaction performance in a continuous-tank reactor is theoretically lower than the reaction selectivity required in a batch reactor, industrial production is carried out in this continuous-tank reaction format due to its high production efficiency. Because the evaluation values ​​for each method differ, examples of batch-type evaluations are summarized in Table 1, and examples using a continuous flow method are summarized in Table 2.

[0112]

number

[0113]

number

[0114] Example 1-1 (Catalyst Preparation) 20 g of ruthenium chloride hydrate (containing 40% by mass of ruthenium) and 8 g of zinc chloride were dissolved in 500 mL of distilled water heated to 80°C while stirring. 100 mL of 5N aqueous sodium hydroxide solution was added, and stirring was continued at 80°C for another 2 hours, resulting in a black precipitated solid. The liquid containing the solid was cooled and filtered, and the recovered solid was placed in 500 mL of 1N aqueous sodium hydroxide solution and subjected to alkali washing and filtration three times. This was then washed with 500 mL of distilled water and filtered five times. The solid was then added to a measuring cylinder containing a previously prepared zinc sulfate aqueous solution, and the resulting solution was adjusted to a zinc sulfate concentration of 0.62 mol / L. This solution was then placed in a 1 L autoclave. 45 g of zirconia powder was then added, and the 1 L autoclave was set up. The temperature and pressure were increased while stirring, and the reduction treatment was carried out at 150°C under hydrogen at 5 MPa for 5 hours. The 1L autoclave was then cooled, and the liquid containing the ruthenium catalyst containing reduced zirconia was transferred to a beaker. After allowing to stand, the supernatant was removed by decantation. Distilled water was then added, and the mixture was stirred, allowed to stand, decanted, and the supernatant was replaced. This procedure was repeated five times, yielding 52.8g of wet ruthenium catalyst containing zirconia in dry weight equivalent. The average crystallite size of ruthenium in the zirconia-containing ruthenium catalyst was 4.6 nm.

[0115] (Partial hydrogenation of benzene) 280 mL of a liquid containing 12 g of the zirconia-containing ruthenium catalyst in terms of dry mass, adjusted to a dimethylamine concentration of 45 mg / L and a zinc sulfate concentration of 0.62 mol / L, was charged into a 1 L autoclave. The inside of the autoclave was replaced with hydrogen while stirring, and after the temperature was raised to 145°C, hydrogen was further injected and maintained at a total pressure of 5 MPa for 22 hours to carry out pre-reaction treatment of the catalyst slurry. Next, the pressure in the autoclave was temporarily reduced to 3 MPa, and then 140 mL of benzene was injected together with hydrogen, and the reaction was carried out under a total pressure of 5 MPa with high-speed stirring. The benzene conversion and cyclohexene selectivity were determined by withdrawing the reaction mixture over time and analyzing the composition of the liquid phase by gas chromatography. After the reaction, the reaction product and catalyst slurry were removed from the autoclave, and the nitrogen concentration in the aqueous zinc sulfate solution, the ratio of the nitrogen mass to the mass of the charged zirconia-containing ruthenium catalyst, and the zinc concentration in the zirconia-containing ruthenium catalyst were measured. The analytical values ​​and the selectivity to cyclohexene when the benzene conversion rate was 50% are shown in Table 1 below.

[0116] Example 1-2 A 1-liter autoclave was charged with 280 mL of a solution containing 12 g (in terms of dry mass) of the zirconia-containing ruthenium catalyst prepared in Example 1-1 and 1.15 g of 40 mass % dimethylamine, and adjusted to a zinc sulfate concentration of 0.62 mol / L. The inside of the autoclave was replaced with hydrogen while stirring, and after the temperature was raised to 145°C, hydrogen was further injected and maintained at a total pressure of 5 MPa for 22 hours to carry out pre-reaction treatment of the catalyst slurry. The autoclave was then cooled, depressurized, and opened, and 0.52 g of 96% by mass sulfuric acid was added. Hydrogen was again injected and the mixture was stirred at 145°C and a total pressure of 5 MPa for 1 hour. After the pressure in the autoclave was temporarily reduced to 3 MPa, 140 mL of benzene was injected together with hydrogen, and the mixture was reacted at a total pressure of 5 MPa with high-speed stirring. The benzene conversion and cyclohexene selectivity were determined by withdrawing the reaction mixture over time and analyzing the composition of the liquid phase by gas chromatography. After the reaction, the reaction product and catalyst slurry were removed from the autoclave, and the nitrogen concentration in the aqueous zinc sulfate solution, the ratio of the nitrogen mass to the catalyst mass charged, and the zinc concentration in the zirconia-containing ruthenium catalyst were measured. The analytical values ​​and the selectivity to cyclohexene when the benzene conversion rate was 50% are shown in Table 1 below.

[0117] Examples 1-3 280 mL of a solution containing 12 g (in terms of dry mass) of the zirconia-containing ruthenium catalyst prepared in Example 1-1 and 3.03 g of 40% by mass dimethylamine and adjusted to a zinc sulfate concentration of 0.62 mol / L was charged into a 1-L autoclave. The inside of the autoclave was replaced with hydrogen while stirring, and after the temperature was raised to 145°C, hydrogen was further injected and maintained at a total pressure of 5 MPa for 22 hours to carry out pre-reaction treatment of the catalyst slurry. The autoclave was then cooled, depressurized, and opened, and 1.5 g of 96% by mass sulfuric acid was added. Hydrogen was again injected and the mixture was stirred at 145°C and a total pressure of 5 MPa for 1 hour. After the pressure in the autoclave was temporarily reduced to 3 MPa, 140 mL of benzene was injected together with hydrogen and the mixture was reacted at a total pressure of 5 MPa with high-speed stirring. The benzene conversion and cyclohexene selectivity were determined by withdrawing the reaction mixture over time and analyzing the composition of the liquid phase by gas chromatography. After the reaction, the reaction product and catalyst slurry were removed from the autoclave, and the nitrogen concentration in the aqueous zinc sulfate solution, the ratio of the nitrogen mass to the catalyst mass charged, and the zinc concentration in the zirconia-containing ruthenium catalyst were measured. The analytical values ​​and the selectivity to cyclohexene when the benzene conversion rate was 50% are shown in Table 1 below.

[0118] Examples 1-4 280 mL of a solution containing 12 g (in terms of dry mass) of the zirconia-containing ruthenium catalyst prepared in Example 1-1 and 6.08 g of 40 mass % dimethylamine, adjusted to a zinc sulfate concentration of 0.62 mol / L, was charged into a 1 L autoclave. The inside of the autoclave was replaced with hydrogen while stirring, and after the temperature was raised to 145°C, hydrogen was further injected and maintained at a total pressure of 5 MPa for 22 hours to carry out pre-reaction treatment of the catalyst slurry. The autoclave was then cooled, depressurized, and opened, and 2.81 g of 96% by mass sulfuric acid was added. Hydrogen was again injected and the mixture was stirred at 145°C and a total pressure of 5 MPa for 1 hour. After the pressure in the autoclave was temporarily reduced to 3 MPa, 140 mL of benzene was injected together with hydrogen, and the mixture was reacted at a total pressure of 5 MPa with high-speed stirring. The benzene conversion and cyclohexene selectivity were determined by withdrawing the reaction mixture over time and analyzing the composition of the liquid phase by gas chromatography. After the reaction, the reaction product and catalyst slurry were removed from the autoclave, and the nitrogen concentration in the aqueous zinc sulfate solution, the ratio of the nitrogen mass to the catalyst mass charged, and the zinc concentration in the zirconia-containing ruthenium catalyst were measured. The analytical values ​​and the selectivity to cyclohexene when the benzene conversion rate was 50% are shown in Table 1 below.

[0119] Comparative Example 1-1 A zirconia-containing ruthenium catalyst prepared in the same manner as in Example 1-1 was recovered in an amount of 53.1 g in terms of dry mass. 280 mL of a solution containing 12 g of the zirconia-containing ruthenium catalyst and 19.56 g of 40 mass % dimethylamine and adjusted to a zinc sulfate concentration of 0.62 mol / L was charged into a 1 L autoclave. The inside of the autoclave was replaced with hydrogen while stirring, and after the temperature was raised to 145°C, hydrogen was further injected and maintained at a total pressure of 5 MPa for 22 hours to carry out pre-reaction treatment of the catalyst slurry. The autoclave was then cooled, depressurized, and opened, and 8.73 g of 96% by mass sulfuric acid was added. Hydrogen was again injected and the mixture was stirred at 145°C and a total pressure of 5 MPa for 1 hour. After the pressure in the autoclave was temporarily reduced to 3 MPa, 140 mL of benzene was injected together with hydrogen and the mixture was reacted at a total pressure of 5 MPa with high-speed stirring. The benzene conversion and cyclohexene selectivity were determined by withdrawing the reaction mixture over time and analyzing the composition of the liquid phase by gas chromatography. After the reaction, the reaction product and catalyst slurry were removed from the autoclave, and the nitrogen concentration in the aqueous zinc sulfate solution, the ratio of the nitrogen mass to the catalyst mass charged, and the zinc concentration in the zirconia-containing ruthenium catalyst were measured. The analytical values ​​and the selectivity to cyclohexene when the benzene conversion rate was 50% are shown in Table 1 below.

[0120] Comparative Example 1-2 The zirconia-containing ruthenium catalyst and the reaction liquid reacted in Example 1-4 were removed from the autoclave, and the aromatic hydrocarbon components in the reaction liquid were removed. Nitrogen was then passed through the catalyst slurry to treat it to the extent that the odor of aromatic hydrocarbons was no longer noticeable. 240 mL of the catalyst slurry in a completely mixed state was taken, and 10.67 g of 40% by mass dimethylamine was added thereto, followed by charging into a 1 L autoclave. The inside of the autoclave was replaced with hydrogen while stirring, and after the temperature was raised to 145°C, hydrogen was further injected and maintained at a total pressure of 5 MPa for 22 hours to carry out pre-reaction treatment of the catalyst slurry. The autoclave was then cooled, depressurized, and opened, and 4.71 g of 96% by mass sulfuric acid was added. Hydrogen was again injected and the mixture was stirred at 145°C and a total pressure of 5 MPa for 1 hour. After the pressure in the autoclave was temporarily reduced to 3 MPa, 120 mL of benzene was injected together with hydrogen and the mixture was reacted at a total pressure of 5 MPa with high-speed stirring. The benzene conversion and cyclohexene selectivity were determined by withdrawing the reaction mixture over time and analyzing the composition of the liquid phase by gas chromatography. After the reaction, the reaction product and catalyst slurry were removed from the autoclave, and the nitrogen concentration in the aqueous zinc sulfate solution, the ratio of the nitrogen mass to the catalyst mass in the reactor, and the zinc concentration in the zirconia-containing ruthenium catalyst were measured. The analytical values ​​and the selectivity to cyclohexene when the benzene conversion rate was 50% are shown in Table 1 below.

[0121] Comparative Examples 1-3 The zirconia-containing ruthenium catalyst and the reaction liquid reacted in Comparative Example 1-2 were removed from the autoclave, and the aromatic hydrocarbon components in the reaction liquid were removed. Nitrogen was then passed through the catalyst slurry to treat it to the extent that the odor of aromatic hydrocarbons was no longer noticeable. 220 mL of the catalyst slurry in a completely mixed state was taken, and 0.061 g of 96 mass % sulfuric acid was added thereto, followed by charging into a 1 L autoclave. Hydrogen was again injected and the mixture was stirred at 145°C and a total pressure of 5 MPa for 1 hour. The pressure in the autoclave was then temporarily reduced to 3 MPa, after which 110 mL of benzene was injected together with hydrogen and the mixture was reacted at a total pressure of 5 MPa with high-speed stirring. The benzene conversion and cyclohexene selectivity were determined by withdrawing the reaction mixture over time and analyzing the composition of the liquid phase by gas chromatography. After the reaction, the reaction product and catalyst slurry were removed from the autoclave, and the nitrogen concentration in the aqueous zinc sulfate solution, the ratio of the nitrogen mass to the catalyst mass in the reactor, and the zinc concentration in the zirconia-containing ruthenium catalyst were measured. The analytical values ​​and the selectivity to cyclohexene when the benzene conversion rate was 50% are shown in Table 1 below.

[0122] Examples 1-5 The zirconia-containing ruthenium catalyst and the reaction liquid reacted in Comparative Example 1-1 were removed from the autoclave, and the aromatic hydrocarbon components in the reaction liquid were removed. Nitrogen was then passed through the catalyst slurry to treat it to the extent that the odor of aromatic hydrocarbons was no longer noticeable. 240 mL of the catalyst slurry in a completely mixed state was sampled and allowed to stand to allow the catalyst solids to settle, after which 140 mL of the supernatant was removed and a new 0.62 mol / L aqueous zinc sulfate solution was added to make up the total volume to 280 mL. Next, the catalyst slurry was stirred for 5 minutes, allowed to stand to allow the catalyst solids to settle, and then 180 mL of the supernatant was removed, and a new 0.62 mol / L aqueous zinc sulfate solution was added to make up to 280 mL. This operation was repeated twice. Then, 280 mL of the treated catalyst slurry was placed in a 1 L autoclave, and the inside of the autoclave was replaced with hydrogen while stirring. After heating to 145°C, further hydrogen was injected and maintained at a total pressure of 5 MPa for 22 hours to pretreat the catalyst. Next, the pressure in the autoclave was temporarily reduced to 3 MPa, and then 140 mL of benzene was injected together with hydrogen, and the reaction was carried out under a total pressure of 5 MPa with high-speed stirring. The benzene conversion and cyclohexene selectivity were determined by withdrawing the reaction mixture over time and analyzing the composition of the liquid phase by gas chromatography. After the reaction, the reaction product and catalyst slurry were removed from the autoclave, and the nitrogen concentration in the aqueous zinc sulfate solution, the ratio of the nitrogen mass to the catalyst mass in the reactor, and the zinc concentration in the zirconia-containing ruthenium catalyst were measured. The analytical values ​​and the selectivity to cyclohexene when the benzene conversion rate was 50% are shown in Table 1 below.

[0123] [Table 1]

[0124] Examples 1-6 A continuous tank reactor was charged with 1200 mL of a solution having a zinc sulfate concentration of 0.62 mol / L, and containing 50 g, in terms of dry mass, of a zirconia-containing ruthenium catalyst prepared in the same manner as in Example 1-1. This continuous-tank reactor has an oil-water separator as an auxiliary vessel, and its inner surface is coated with Teflon (registered trademark). Next, benzene containing 0.1 mg / L of dimethylamine was fed to the continuous tank reactor at 1.2 L / hr at 145°C under a hydrogen pressure of 5 MPa to continuously carry out a partial hydrogenation reaction of benzene. During this process, water was supplied so that the composition of the aqueous phase containing the zirconia-containing ruthenium catalyst in the reaction system was always constant, and the reaction product consisting of benzene, cyclohexene, and cyclohexane was continuously removed from the oil-water separation tank. The volume ratio of the aqueous phase to the oil phase in the reactor was kept constant at aqueous phase:oil phase=2:1. The reaction liquid coming out of the oil-water separation tank 22 hours after the start of the reaction was sampled, and the composition of the liquid phase was analyzed by gas chromatography to determine the conversion rate of benzene and the selectivity for cyclohexene. Following sampling of the reaction liquid, catalyst slurry was collected from a catalyst sampling line installed in the tank reactor, and the nitrogen concentration in the aqueous zinc sulfate solution, the ratio of the nitrogen mass to the catalyst mass in the reactor, and the zinc concentration contained in the zirconia-containing ruthenium catalyst were measured. The analytical values, benzene conversion and cyclohexene selectivity are shown in Table 2 below.

[0125] Examples 1-7 The reaction in Example 1-6 was continued, and the reaction liquid coming out of the oil-water separation tank 116 hours after the start of the reaction was sampled, and the composition of the liquid phase was analyzed by gas chromatography to determine the benzene conversion and cyclohexene selectivity. As a result, the reaction results were a benzene conversion of 45.7% and a cyclohexene selectivity of 78.8%. Since the benzene conversion rate had decreased with respect to the reaction results after a reaction time of 22 hours, the benzene supply rate was reduced with the benzene conversion rate at 50% as a guideline, and after ensuring a stabilization time of 2 hours, the reaction liquid was sampled again and the reaction results were determined. Further, the catalyst slurry was sampled, and the nitrogen concentration in the aqueous zinc sulfate solution, the ratio of the nitrogen mass to the catalyst mass in the reactor, and the zinc concentration contained in the zirconia-containing ruthenium catalyst were measured. The analytical values, benzene conversion and cyclohexene selectivity are shown in Table 2 below.

[0126] Examples 1-8 A continuous tank reactor was charged with 1200 mL of a solution containing 50 g, in dry mass equivalent, of a zirconia-containing ruthenium catalyst prepared in the same manner as in Example 1-1, and adjusted to a zinc sulfate concentration of 0.62 mol / L. Next, benzene containing 10 mg / L of dimethylamine was fed to the continuous tank reactor at 1.2 L / hr at 145°C under a hydrogen pressure of 5 MPa, and a continuous partial hydrogenation reaction of benzene was carried out. Twenty hours after the start of the reaction, 0.3 g of 96% by mass sulfuric acid was added to the reactor through the water supply line used to replenish the reaction system. After 22 hours, the reaction liquid emerging from the oil-water separation tank was sampled, and the composition of the liquid phase was analyzed by gas chromatography. From the results, the benzene conversion rate and cyclohexene selectivity were determined. Following sampling of the reaction solution, catalyst slurry was collected from a catalyst sampling line installed in the continuous tank reactor, and the nitrogen concentration in the aqueous zinc sulfate solution, the ratio of the nitrogen mass to the catalyst mass in the reactor, and the zinc concentration contained in the zirconia-containing ruthenium catalyst were measured. The analytical values, benzene conversion and cyclohexene selectivity are shown in Table 2 below.

[0127] Examples 1-9 The reaction of Example 1-8 was continued, and 24 hours after the start of the reaction, 600 mL of catalyst slurry containing the reaction liquid was extracted from the continuous tank reactor, while 400 mL of catalyst slurry containing zinc sulfate, which was the same as that initially charged in Example 1-8, was charged into the continuous tank reactor. The catalyst slurry containing the extracted reaction liquid was treated to remove aromatic hydrocarbon components, and nitrogen was then passed through the catalyst slurry until the odor of aromatic hydrocarbons was no longer noticeable. Next, the mixture was brought into contact with nitrogen containing 7% by volume of oxygen at 70°C for 1 hour, and then the atmosphere was replaced with nitrogen and then with hydrogen. Thereafter, the temperature was raised to 140° C., and stirring was carried out for 4 hours while maintaining the pressure inside the system at 0.5 MPa under a hydrogen atmosphere, and the entire amount of the catalyst slurry was used to carry out an operation for restoring catalytic activity. While the reaction was being continued in this manner, the operation of withdrawing 400 mL of catalyst slurry from the reactor and returning the slurry to the reactor after the catalyst activity recovery operation was continued once a day as described above. To the catalyst slurry that had been subjected to the activity recovery operation, 0.41 g of 96 mass % sulfuric acid was added, and the mixture was returned to the reactor. The reaction liquid coming out of the oil-water separation tank 118 hours after the start of the reaction was sampled, and the composition of the liquid phase was analyzed by gas chromatography to determine the conversion rate of benzene and the selectivity for cyclohexene. Following sampling of the reaction solution, catalyst slurry was collected from a catalyst sampling line installed in the continuous tank reactor, and the nitrogen concentration in the aqueous zinc sulfate solution, the ratio of the nitrogen mass to the catalyst mass in the reactor, and the zinc concentration contained in the zirconia-containing ruthenium catalyst were measured. The analytical values, benzene conversion and cyclohexene selectivity are shown in Table 2 below.

[0128] Examples 1-10 A continuous tank reactor was charged with 1200 mL of a solution containing 50 g, in dry mass equivalent, of a zirconia-containing ruthenium catalyst prepared in the same manner as in Example 1-1, and adjusted to a zinc sulfate concentration of 0.62 mol / L. Next, benzene containing 50 mg / L of dimethylamine was fed to the continuous tank reactor at 1.2 L / hr at 145°C under a hydrogen pressure of 5 MPa, and a partial hydrogenation reaction of benzene was carried out continuously. Twenty hours after the start of the reaction, 1.5 g of 96% by mass sulfuric acid was added to the reactor through the water supply line used to replenish the reaction system. After 22 hours, the reaction liquid emerging from the oil-water separation tank was sampled, and the composition of the liquid phase was analyzed by gas chromatography. From the results, the benzene conversion rate and cyclohexene selectivity were determined. Following sampling of the reaction solution, catalyst slurry was collected from a catalyst sampling line installed in the continuous tank reactor, and the nitrogen concentration in the aqueous zinc sulfate solution, the ratio of the nitrogen mass to the catalyst mass in the reactor, and the zinc concentration contained in the zirconia-containing ruthenium catalyst were measured. The analytical values, benzene conversion and cyclohexene selectivity are shown in Table 2 below.

[0129] Examples 1-11 The reaction of Example 1-10 was continued, and 24 hours after the start of the reaction, the catalyst slurry containing the reaction solution was extracted from the 600 mL continuous tank reactor, while 400 mL of the catalyst slurry containing zinc sulfate, which was the same as that initially charged in Example 1-10, was charged into the tank-type flow reactor. The catalyst slurry containing the extracted reaction liquid was treated to remove aromatic hydrocarbon components, and nitrogen was then passed through the catalyst slurry until the odor of aromatic hydrocarbons was no longer noticeable. Next, the mixture was brought into contact with nitrogen containing 7% by volume of oxygen at 70°C for 1 hour, and then the atmosphere was replaced with nitrogen and then with hydrogen. Thereafter, the temperature was raised to 140° C., and stirring was carried out for 4 hours while maintaining the pressure inside the system at 0.5 MPa under a hydrogen atmosphere, and the entire amount of the catalyst slurry was used to carry out an operation for restoring catalytic activity. While the reaction was being continued in this manner, the operation of withdrawing 400 mL of catalyst slurry from the reactor and returning the slurry to the reactor after the catalyst activity recovery operation was continued once a day as described above. After the activity recovery operation, 2.1 g of 96 mass % sulfuric acid was added to the catalyst slurry, and the mixture was returned to the reactor. The reaction liquid coming out of the oil-water separation tank 118 hours after the start of the reaction was sampled, and the composition of the liquid phase was analyzed by gas chromatography. From the results, the conversion rate of benzene and the selectivity and reaction selectivity of cyclohexene were determined. Following sampling of the reaction solution, catalyst slurry was collected from a catalyst sampling line installed in the continuous tank reactor, and the nitrogen concentration in the aqueous zinc sulfate solution, the ratio of the nitrogen mass to the catalyst mass in the reactor, and the zinc concentration contained in the zirconia-containing ruthenium catalyst were measured. The analytical values, benzene conversion and cyclohexene selectivity are shown in Table 2 below.

[0130] Examples 1-12 A continuous tank reactor was charged with 1200 mL of a solution containing 50 g, in dry mass equivalent, of a zirconia-containing ruthenium catalyst prepared in the same manner as in Example 1-1, and adjusted to a zinc sulfate concentration of 0.62 mol / L. Next, benzene containing 100 mg / L of dimethylamine was fed to the continuous tank reactor at 1.2 L / hr at 145°C under a hydrogen pressure of 5 MPa, and a continuous partial hydrogenation reaction of benzene was carried out. Twenty hours after the start of the reaction, 3 g of 96% by mass sulfuric acid was added to the reactor through the water supply line used to replenish the reaction system. After 22 hours, the reaction liquid emerging from the oil-water separation tank was sampled, and the composition of the liquid phase was analyzed by gas chromatography. From the results, the benzene conversion rate and cyclohexene selectivity were determined. Following sampling of the reaction solution, catalyst slurry was collected from a catalyst sampling line installed in the continuous tank reactor, and the nitrogen concentration in the aqueous zinc sulfate solution, the ratio of the nitrogen mass to the catalyst mass in the reactor, and the zinc concentration contained in the zirconia-containing ruthenium catalyst were measured. The analytical values, benzene conversion and cyclohexene selectivity are shown in Table 2 below.

[0131] Examples 1-13 The reaction of Example 1-12 was continued, and 24 hours after the start of the reaction, the catalyst slurry containing the reaction liquid was extracted from the 600 mL continuous tank reactor, while 400 mL of the catalyst slurry containing zinc sulfate similar to that initially charged in Example 1-10 was charged into the continuous tank reactor. The catalyst slurry containing the extracted reaction liquid was treated to remove aromatic hydrocarbon components, and nitrogen was then passed through the catalyst slurry until the odor of aromatic hydrocarbons was no longer noticeable. Next, the mixture was brought into contact with nitrogen containing 7% by volume of oxygen at 50°C for 1 hour, and then the atmosphere was replaced with nitrogen and then with hydrogen. Thereafter, the temperature was raised to 140° C., and stirring was carried out for 4 hours while maintaining the pressure inside the system at 0.5 MPa under a hydrogen atmosphere, and the entire amount of the catalyst slurry was used to carry out an operation for restoring catalytic activity. While the reaction was being continued in this manner, the operation of withdrawing 400 mL of catalyst slurry from the reactor and returning the slurry to the reactor after the catalyst activity recovery operation was continued once a day as described above. After the activity recovery operation, 4 g of 96% by mass sulfuric acid was added to the catalyst slurry, and the mixture was returned to the reactor. The reaction liquid coming out of the oil-water separation tank 118 hours after the start of the reaction was sampled, and the composition of the liquid phase was analyzed by gas chromatography to determine the conversion rate of benzene and the selectivity for cyclohexene. Following sampling of the reaction solution, catalyst slurry was collected from a catalyst sampling line installed in the continuous tank reactor, and the nitrogen concentration in the aqueous zinc sulfate solution, the ratio of the nitrogen mass to the catalyst mass in the reactor, and the zinc concentration contained in the zirconia-containing ruthenium catalyst were measured. The analytical values, benzene conversion and cyclohexene selectivity are shown in Table 2 below.

[0132] Comparative Examples 1-4 The reaction in Example 1-13 was continued, and the operation of withdrawing 400 mL of the catalyst slurry containing the reaction liquid and returning 400 mL of the slurry that had been subjected to the operation for restoring catalytic activity to the reactor was continued once a day. To the catalyst slurry that had been subjected to the activity recovery operation, 3.26 g of 96 mass % sulfuric acid was added, and the mixture was returned to the reactor. The reaction liquid coming out of the oil-water separation tank 310 hours after the start of the reaction was sampled, and the composition of the liquid phase was analyzed by gas chromatography to determine the conversion rate of benzene and the selectivity for cyclohexene. Following sampling of the reaction solution, catalyst slurry was collected from a catalyst sampling line installed in the continuous tank reactor, and the nitrogen concentration in the aqueous zinc sulfate solution, the ratio of the nitrogen mass to the catalyst mass in the reactor, and the zinc concentration contained in the zirconia-containing ruthenium catalyst were measured. The analytical values, benzene conversion and cyclohexene selectivity are shown in Table 2 below.

[0133] Comparative Examples 1-5 A continuous tank reactor was charged with 1200 mL of a solution containing 50 g, in dry mass equivalent, of a zirconium ruthenium catalyst prepared in the same manner as in Example 1-1, and adjusted to a zinc sulfate concentration of 0.62 mol / L. Next, benzene containing 200 mg / L of dimethylamine was fed to the continuous tank reactor at 1.2 L / hr at 145°C under a hydrogen pressure of 5 MPa, and a continuous partial hydrogenation reaction of benzene was carried out. 24 hours after the start of the reaction, 600 mL of catalyst slurry containing the reaction liquid was extracted from the continuous tank reactor, and 400 mL of catalyst slurry containing zinc sulfate similar to that initially charged in Example 1-1 was charged into the continuous tank reactor. The catalyst slurry containing the extracted reaction liquid was treated to remove aromatic hydrocarbon components, and nitrogen was then passed through the catalyst slurry until the odor of aromatic hydrocarbons was no longer noticeable. Next, the mixture was brought into contact with nitrogen containing 7% by volume of oxygen at 50°C for 1 hour, and then the atmosphere was replaced with nitrogen and then with hydrogen. Thereafter, the temperature was raised to 140° C., and stirring was carried out for 4 hours while maintaining the pressure inside the system at 0.5 MPa under a hydrogen atmosphere, and the entire amount of the catalyst slurry was used to carry out an operation for restoring catalytic activity. While the reaction was being continued in this manner, the operation of withdrawing 400 mL of catalyst slurry from the reactor and returning the slurry to the reactor after the catalyst activity recovery operation was continued once a day as described above. The catalyst slurry after the activity recovery operation was added with 8.1 g of 96% by mass sulfuric acid and returned to the reactor, and this operation was carried out three times in total. The reaction liquid coming out of the oil-water separation tank 118 hours after the start of the reaction was sampled, and the composition of the liquid phase was analyzed by gas chromatography to determine the conversion rate of benzene and the selectivity for cyclohexene. Following sampling of the reaction solution, catalyst slurry was collected from a catalyst sampling line installed in the continuous tank reactor, and the nitrogen concentration in the aqueous zinc sulfate solution, the ratio of the nitrogen mass to the catalyst mass in the reactor, and the zinc concentration contained in the zirconia-containing ruthenium catalyst were measured. The analytical values, benzene conversion and cyclohexene selectivity are shown in Table 2 below.

[0134] Examples 1-14 The reaction of Comparative Example 1-5 was continued, and the benzene was switched to benzene with a dimethylamine concentration of 0.1 mg / L 120 hours after the start of the reaction. Furthermore, 400 mL of the catalyst slurry containing the reaction solution was withdrawn, and 400 mL of the slurry that had been subjected to the catalyst activity recovery operation was returned to the reactor. This operation was continued once a day. The catalyst slurry returned to the reactor 120 hours after the start of the reaction was treated until the nitrogen concentration in the liquid extracted from the reactor was undetectable. Specifically, similar to Comparative Example 1-5, the catalyst slurry was treated to the extent that the odor of aromatic hydrocarbon components was undetectable, followed by oxygen-containing nitrogen treatment. The process of decantation at room temperature, removal of the supernatant, and addition of a freshly prepared 0.62 mol / L aqueous zinc sulfate solution was repeated to reduce the nitrogen concentration. Subsequently, 400 mL of the treated catalyst slurry was heated to 140°C and stirred for 4 hours while maintaining the system pressure at 0.5 MPa under a hydrogen atmosphere. The recovered catalyst slurry was secured and used when adding the catalyst. The reaction liquid coming out of the oil-water separation tank 310 hours after the start of the reaction was sampled, and the composition of the liquid phase was analyzed by gas chromatography to determine the conversion rate of benzene and the selectivity for cyclohexene. Following sampling of the reaction liquid, catalyst slurry was collected from a catalyst sampling line installed in the tank reactor, and the nitrogen concentration in the aqueous zinc sulfate solution, the ratio of the nitrogen mass to the catalyst mass in the reactor, and the zinc concentration contained in the zirconia-containing ruthenium catalyst were measured.

[0135] The analytical values, benzene conversion and cyclohexene selectivity are shown in Table 2 below.

[0136] [Table 2]

[0137] [Second Example] (acetic acid concentration) <Acetic acid concentration in zinc sulfate aqueous solution> The acetic acid concentration in the zinc sulfate aqueous solution was measured using a Tosoh Technosystems IC-2010 ion chromatograph. However, when the acetic acid concentration was 1 mg / L or less, the amount was determined by subtracting the amount of acetic acid that was not retained in the aqueous zinc sulfate solution due to dissolution in the monocyclic aromatic hydrocarbons and the reaction liquid from the amount of acetic acid added to the aqueous zinc sulfate solution. Specifically, it was calculated using the following formula. (Amount of acetic acid in zinc sulfate solution) = (Amount of acetic acid entering zinc sulfate solution) - (Amount of acetic acid leaving zinc sulfate solution) In the above formula, (the amount of acetic acid entering the aqueous zinc sulfate solution) refers to the amount of acetic acid in the monocyclic aromatic hydrocarbon such as benzene as the raw material. Also, (the amount of acetic acid leaving the aqueous zinc sulfate solution) refers to the amount of acetic acid in the oil phase (monocyclic aromatic hydrocarbon reaction solution) after the reaction.

[0138] <Concentration of acetic acid in monocyclic aromatic hydrocarbons and monocyclic aromatic hydrocarbon reaction liquid (oil phase after reaction)> The concentrations of monocyclic aromatic hydrocarbons (benzene) and acetic acid in the reaction solution of monocyclic aromatic hydrocarbons were measured using a Shimadzu GC-2014 gas chromatograph. When the monocyclic aromatic hydrocarbon and acetic acid concentrations in the reaction solution were 0.5 ppm or less, water was added to the measurement sample, followed by extraction and concentration, and the measurement sample was analyzed based on a calibration curve based on the distribution ratio.

[0139] (ratio of acetic acid mass to zirconia-containing ruthenium catalyst mass) The ratio of the mass of acetic acid to the mass of the zirconia-containing ruthenium catalyst was calculated as the ratio of the total solid catalyst concentration (mg / L) in the reaction liquid to the acetic acid concentration (mg / L) in the aqueous zinc sulfate solution. Specifically, the reaction liquid, the aqueous zinc sulfate solution, and the catalyst were withdrawn from the reaction system in a completely mixed state and allowed to stand for separation. The acetic acid concentration in the aqueous zinc sulfate solution was measured using the above-mentioned analyzer, and the catalyst was determined as a solid concentration in an aqueous sulfate solution by filtration and drying treatment, and the ratio of the mass of acetic acid to the mass of the catalyst was calculated from this.

[0140] (Zinc concentration in catalyst solids) The zinc concentration in the catalyst solids was measured using a Rigaku ZSX Primus II fluorescence analyzer. When analyzing small samples, the catalyst solids were dissolved using hydrochloric acid for measuring hazardous metals, and the zinc concentration dissolved in the liquid was measured using an ICP device, SPS3520UV-DD, manufactured by Hitachi High-Tech Science.

[0141] (average crystallite size of ruthenium) The average crystallite size of ruthenium was determined by Scherrer's equation from the broadening of the diffraction peak of ruthenium metal at a diffraction angle (2θ) of 44° obtained using an XRD-6100 X-ray diffractometer manufactured by Shimadzu Corporation.

[0142] (Benzene conversion and cyclohexene selectivity) A catalyst and hydrogen were charged into a 1L high-pressure autoclave reactor, and a predetermined amount of benzene was added all at once as a monocyclic aromatic hydrocarbon while the temperature and hydrogen pressure were set. Reaction evaluation was carried out using the batch method under the specified reaction temperature and hydrogen pressure. A batch reaction, also known as a batch reaction, involves placing a zinc sulfate solution containing a catalyst into an autoclave, adding the raw material benzene once at the start of the reaction under set temperature, pressure, and time settings, and recovering the entire amount once the reaction is complete. After adding the benzene, a portion of the reaction liquid was withdrawn and analyzed using a gas chromatograph (Shimadzu GC-2014) equipped with an FID detector. Based on the experimental concentration analysis values, the reaction conversion and selectivity over time were calculated using the following calculation formulas (1) and (2). The analytical data was then plotted to determine the selectivity at a conversion rate of 50%. In addition, a reaction evaluation was performed using a flow method in which a 4L tank-type flow reactor was charged with the catalyst, and benzene and hydrogen were continuously added to observe the reaction progress. In a flow method reaction, raw material benzene is continuously added to the reactor and the reaction product is continuously removed from the reactor, allowing the reaction to be carried out continuously under constant conditions over a long period of time. By controlling the temperature, pressure, amount of catalyst, and benzene flow rate, the benzene conversion rate can be adjusted and the cyclohexene selectivity can be determined. In this example, the benzene conversion was set to approximately 50%, and the reaction solution was analyzed using a gas chromatograph (GC-2014, manufactured by Shimadzu Corporation) equipped with an FID detector, as in the batch process. Based on the experimental concentration analysis values, the benzene conversion and cyclohexene selectivity were calculated using the following calculation formulas (3) and (4). Although the reaction performance in a continuous-tank reactor is theoretically lower than the reaction selectivity required in a batch reactor, industrial production is carried out in this continuous-tank reaction format due to its high production efficiency. Because the evaluation values ​​for each method differ, examples of batch-type evaluations are summarized in Table 3, and examples using a continuous flow method are summarized in Table 4.

[0143]

number

[0144]

number

[0145] Example 2-1 (Catalyst Preparation) 20 g of ruthenium chloride hydrate (containing 40% ruthenium by mass) and 8 g of zinc chloride were dissolved in 500 mL of distilled water heated to 80°C while stirring. 100 mL of 5N aqueous sodium hydroxide solution was added, and stirring was continued at 80°C for another 2 hours, resulting in a black precipitated solid. The liquid containing the solid was cooled and filtered, and the recovered solid was placed in 500 mL of 1N aqueous sodium hydroxide solution and subjected to alkali washing and filtration three times. This was then washed with 500 mL of distilled water and filtered five times. The solid was then added to a measuring cylinder containing a previously prepared aqueous zinc sulfate solution, and the resulting solution was adjusted to a zinc sulfate concentration of 0.62 mol / L. This solution was then placed in a 1 L autoclave. 45 g of zirconia powder was then added, and the 1 L autoclave was set up. The temperature and pressure were increased while stirring, and the reduction treatment was carried out at 150°C under hydrogen at 5 MPa for 5 hours. The 1L autoclave was then cooled, and the liquid containing the ruthenium catalyst containing reduced zirconia was transferred to a beaker. After allowing to stand, the supernatant was removed by decantation. Distilled water was then added, and the mixture was stirred, allowed to stand, decanted, and the supernatant was replaced. This procedure was repeated five times, yielding 53.1g of wet ruthenium catalyst containing zirconia in dry mass equivalent. The average crystallite size of ruthenium in the zirconia-containing ruthenium catalyst was 5.1 nm.

[0146] (Partial hydrogenation of benzene) 280 mL of a liquid containing 12 g of the zirconia-containing ruthenium catalyst in terms of dry mass, 5 mg / L of acetic acid, and a catalyst slurry adjusted to a zinc sulfate concentration of 0.62 mol / L was charged into a 1 L autoclave. The inside of the autoclave was replaced with hydrogen while stirring, and after the temperature was raised to 145°C, hydrogen was further injected and maintained at a total pressure of 5 MPa for 22 hours to carry out pre-reaction treatment of the catalyst slurry. Next, the pressure in the autoclave was temporarily reduced to 3 MPa, and then 140 mL of benzene was injected together with hydrogen, and the reaction was carried out under a total pressure of 5 MPa with high-speed stirring. During the reaction, the reaction liquid was withdrawn from the autoclave over time, and the composition of the liquid phase was analyzed by gas chromatography to determine the benzene conversion and cyclohexene selectivity. In addition, the reaction product and catalyst slurry after the reaction were withdrawn from the autoclave, and the acetic acid concentration in the aqueous zinc sulfate solution, the ratio of the mass of acetic acid to the mass of the charged zirconia-containing ruthenium catalyst, and the zinc concentration contained in the zirconia-containing ruthenium catalyst were measured. The analytical values ​​and the selectivity to cyclohexene when the benzene conversion rate was 50% are shown in Table 3 below.

[0147] Example 2-2 A 1-L autoclave was charged with 280 mL of a catalyst slurry containing 12 g, in terms of dry mass, of the zirconia-containing ruthenium catalyst prepared in Example 2-1, adjusted to an acetic acid concentration of 80 mg / L and a zinc sulfate concentration of 0.62 mol / L. The inside of the autoclave was replaced with hydrogen while stirring, and after the temperature was raised to 145°C, hydrogen was further injected and maintained at a total pressure of 5 MPa for 22 hours to carry out pre-reaction treatment of the catalyst slurry. Next, the pressure in the autoclave was temporarily reduced to 3 MPa, and then 140 mL of benzene was injected together with hydrogen, and the reaction was carried out under a total pressure of 5 MPa with high-speed stirring. The benzene conversion and cyclohexene selectivity were determined by withdrawing the reaction mixture over time and analyzing the composition of the liquid phase by gas chromatography. After the reaction, the reaction product and catalyst slurry were removed from the autoclave, and the acetic acid concentration in the aqueous zinc sulfate solution, the ratio of the mass of acetic acid to the mass of the charged catalyst, and the zinc concentration in the zirconia-containing ruthenium catalyst were measured. The analytical values ​​and the selectivity to cyclohexene when the benzene conversion rate was 50% are shown in Table 3 below.

[0148] Comparative Example 2-1 A 1-L autoclave was charged with 280 mL of a catalyst slurry containing 12 g, in terms of dry mass, of the zirconia-containing ruthenium catalyst prepared in Example 2-1, with an acetic acid concentration of 120 mg / L and adjusted to a zinc sulfate concentration. The inside of the autoclave was replaced with hydrogen while stirring, and after the temperature was raised to 145°C, hydrogen was further injected and maintained at a total pressure of 5 MPa for 22 hours to carry out pre-reaction treatment of the catalyst slurry. Next, the pressure in the autoclave was temporarily reduced to 3 MPa, and then 140 mL of benzene was injected together with hydrogen, and the reaction was carried out under a total pressure of 5 MPa with high-speed stirring. The benzene conversion and cyclohexene selectivity were determined by withdrawing the reaction mixture over time and analyzing the composition of the liquid phase by gas chromatography. After the reaction, the reaction product and catalyst slurry were removed from the autoclave, and the acetic acid concentration in the aqueous zinc sulfate solution, the ratio of the mass of acetic acid to the mass of the charged catalyst, and the zinc concentration in the zirconia-containing ruthenium catalyst were measured. The analytical values ​​and the selectivity to cyclohexene when the benzene conversion rate was 50% are shown in Table 3 below.

[0149] Comparative Example 2-2 A 1-L autoclave was charged with 280 mL of a catalyst slurry containing 12 g, in terms of dry mass, of the zirconia-containing ruthenium catalyst prepared in Example 2-1, adjusted to an acetic acid concentration of 230 mg / L and a zinc sulfate concentration of 0.62 mol / L. The inside of the autoclave was replaced with hydrogen while stirring, and after the temperature was raised to 145°C, hydrogen was further injected and maintained at a total pressure of 5 MPa for 22 hours to carry out pre-reaction treatment of the catalyst slurry. Next, the pressure in the autoclave was temporarily reduced to 3 MPa, and then 140 mL of benzene was injected together with hydrogen, and the reaction was carried out under a total pressure of 5 MPa with high-speed stirring. The benzene conversion and cyclohexene selectivity were determined by withdrawing the reaction mixture over time and analyzing the composition of the liquid phase by gas chromatography. After the reaction, the reaction product and catalyst slurry were removed from the autoclave, and the acetic acid concentration in the aqueous zinc sulfate solution, the ratio of the mass of acetic acid to the mass of the charged catalyst, and the zinc concentration in the zirconia-containing ruthenium catalyst were measured. The analytical values ​​and the selectivity to cyclohexene when the benzene conversion rate was 50% are shown in Table 3 below.

[0150] Comparative Example 2-3 The zirconia-containing ruthenium catalyst and the reaction liquid reacted in Example 2-2 were removed from the autoclave, and the aromatic hydrocarbon components in the reaction liquid were removed. Nitrogen was then passed through the catalyst slurry to treat it to the extent that the odor of aromatic hydrocarbons was no longer noticeable. 240 mL of the catalyst slurry in a completely mixed state was taken, and 10 mL of a separately prepared aqueous solution in which the acetic acid concentration was adjusted to 2.01 g / L and the zinc sulfate concentration was adjusted to 0.62 mol / L was added, and the mixture was placed in a 1 L autoclave. The inside of the autoclave was purged with hydrogen while stirring, and after heating to 145°C, further hydrogen was injected and maintained at a total pressure of 5 MPa for 22 hours, thereby carrying out a reaction pretreatment of the catalyst slurry. Next, the pressure in the autoclave was temporarily reduced to 3 MPa, and then 140 mL of benzene was injected together with hydrogen, and the reaction was carried out under a total pressure of 5 MPa with high-speed stirring. The benzene conversion and cyclohexene selectivity were determined by withdrawing the reaction mixture over time and analyzing the composition of the liquid phase by gas chromatography. After the reaction, the reaction product and catalyst slurry were removed from the autoclave, and the acetic acid concentration in the aqueous zinc sulfate solution, the ratio of the mass of acetic acid to the mass of the charged catalyst, and the zinc concentration in the zirconia-containing ruthenium catalyst were measured. The analytical values ​​and the selectivity to cyclohexene when the benzene conversion rate was 50% are shown in Table 3 below.

[0151] Example 2-3 The zirconia-containing ruthenium catalyst and the reaction liquid reacted in Comparative Example 2-2 were removed from the autoclave, and the aromatic hydrocarbon components in the reaction liquid were removed. Nitrogen was then passed through the catalyst slurry to treat it to the extent that the odor of aromatic hydrocarbons was no longer noticeable. 240 mL of the catalyst slurry in a completely mixed state was sampled and allowed to stand to allow the catalyst solids to settle, after which 140 mL of the supernatant was removed and a new 0.62 mol / L aqueous zinc sulfate solution was added to make up the total volume to 280 mL. Next, the catalyst slurry was stirred for 5 minutes, allowed to stand to allow the catalyst solids to settle, and then 180 mL of the supernatant was removed. A new 0.62 mol / L aqueous zinc sulfate solution was added to make up to 280 mL, and this operation was repeated twice. Then, 280 mL of the treated catalyst slurry was placed in a 1 L autoclave, and the inside of the autoclave was replaced with hydrogen while stirring. After heating to 145°C, further hydrogen was injected and maintained at a total pressure of 5 MPa for 22 hours to pretreat the catalyst. Next, the pressure in the autoclave was temporarily reduced to 3 MPa, and then 140 mL of benzene was injected together with hydrogen, and the reaction was carried out under a total pressure of 5 MPa with high-speed stirring. The benzene conversion and cyclohexene selectivity were determined by withdrawing the reaction mixture over time and analyzing the composition of the liquid phase by gas chromatography. After the reaction, the reaction product and catalyst slurry were removed from the autoclave, and the acetic acid concentration in the aqueous zinc sulfate solution, the ratio of the mass of acetic acid to the mass of the charged catalyst, and the zinc concentration in the zirconia-containing ruthenium catalyst were measured. The analytical values ​​and the selectivity to cyclohexene when the benzene conversion rate was 50% are shown in Table 3 below.

[0152] [Table 3]

[0153] [Example 2-4] A continuous tank reactor was charged with 1200 mL of a solution having a zinc sulfate concentration of 0.62 mol / L, containing 50 g, in terms of dry mass, of a zirconia-containing ruthenium catalyst prepared in the same manner as in Example 2-1. This continuous-tank reactor has an oil-water separator as an auxiliary vessel, and its inner surface is coated with Teflon (registered trademark). Next, benzene, which had been previously adjusted to have an acetic acid concentration of 0.01 mg / L, was fed to the continuous tank reactor at 1.2 L / hr at 145°C under a hydrogen pressure of 5 MPa to continuously carry out a partial hydrogenation reaction of benzene. During this process, water was supplied so that the composition of the aqueous phase containing the zirconia-containing ruthenium catalyst in the reaction system was always constant, and the reaction product consisting of benzene, cyclohexene, and cyclohexane was continuously removed from the oil-water separation tank. The volume ratio of the aqueous phase to the oil phase in the reactor was kept constant at aqueous phase:oil phase=2:1. The reaction liquid coming out of the oil-water separation tank 22 hours after the start of the reaction was sampled, and the composition of the liquid phase was analyzed by gas chromatography to determine the conversion rate of benzene and the selectivity for cyclohexene. Furthermore, following sampling of the reaction solution, catalyst slurry was collected from a catalyst sampling line installed in the continuous tank reactor, and the acetic acid concentration in the aqueous zinc sulfate solution, the ratio of the acetic acid mass to the catalyst mass in the reactor, and the zinc concentration contained in the zirconia-containing ruthenium catalyst were measured. The analytical values, benzene conversion and cyclohexene selectivity are shown in Table 4 below.

[0154] Example 2-5 The reaction of Example 2-4 was continued, and 24 hours after the start of the reaction, 600 mL of catalyst slurry containing the reaction solution was extracted from the tank-type flow reactor, while a 400 mL catalyst slurry containing zinc sulfate similar to that initially charged in Example 2-4 was charged into a continuous tank-type reactor. The catalyst slurry containing the extracted reaction liquid was treated to remove aromatic hydrocarbon components, and nitrogen was then passed through the catalyst slurry until the odor of aromatic hydrocarbons was no longer noticeable. Next, the mixture was brought into contact with nitrogen containing 7% by volume of oxygen at 70°C for 1 hour, and then the atmosphere was replaced with nitrogen and then with hydrogen. Thereafter, the temperature was raised to 140° C., and stirring was carried out for 4 hours while maintaining the pressure inside the system at 0.5 MPa under a hydrogen atmosphere, and the entire amount of the catalyst slurry was used to carry out an operation for restoring catalytic activity. While the reaction was being continued in this manner, the operation of withdrawing 400 mL of catalyst slurry from the reactor and returning the slurry to the reactor after the catalyst activity recovery operation was continued once a day as described above. The reaction liquid coming out of the oil-water separation tank 118 hours after the start of the reaction was sampled, and the composition of the liquid phase was analyzed by gas chromatography to determine the conversion rate of benzene and the selectivity for cyclohexene. Furthermore, following sampling of the reaction solution, catalyst slurry was collected from a catalyst sampling line installed in the continuous tank reactor, and the acetic acid concentration in the aqueous zinc sulfate solution, the ratio of the acetic acid mass to the catalyst mass in the reactor, and the zinc concentration contained in the zirconia-containing ruthenium catalyst were measured. The analytical values, benzene conversion and cyclohexene selectivity are shown in Table 4 below.

[0155] [Example 2-6] A continuous tank reactor was charged with 1200 mL of a solution having a zinc sulfate concentration of 0.62 mol / L, containing 50 g, in terms of dry mass, of a zirconia-containing ruthenium catalyst prepared in the same manner as in Example 2-1. Next, benzene, which had been adjusted in advance to have an acetic acid concentration of 0.5 mg / L, was fed to the continuous tank reactor at 1.2 L / hr at 145°C under a hydrogen pressure of 5 MPa, and a partial hydrogenation reaction of benzene was carried out continuously. During this process, water was supplied so that the composition of the aqueous phase containing the zirconia-containing ruthenium catalyst in the reaction system was always constant, and the reaction product consisting of benzene, cyclohexene, and cyclohexane was continuously removed from the oil-water separation tank. The volume ratio of the aqueous phase to the oil phase in the reactor was kept constant at aqueous phase:oil phase=2:1. The reaction liquid coming out of the oil-water separator 22 hours after the start of the reaction was sampled, and the composition of the liquid phase was analyzed by gas chromatography to determine the reaction selectivity. Following sampling of the reaction solution, catalyst slurry was collected from a catalyst sampling line installed in the continuous tank reactor, and the acetic acid concentration in the aqueous zinc sulfate solution, the ratio of the mass of acetic acid to the mass of the catalyst in the reactor, and the concentration of zinc contained in the zirconia-containing ruthenium catalyst were measured. The analytical values, benzene conversion and cyclohexene selectivity are shown in Table 4 below.

[0156] [Example 2-7] The reaction of Example 2-6 was continued, and 24 hours after the start of the reaction, 600 mL of catalyst slurry containing the reaction liquid was extracted from the continuous tank reactor, while 400 mL of catalyst slurry containing zinc sulfate similar to that initially charged in Example 2-4 was charged into the continuous tank reactor. The catalyst slurry containing the extracted reaction liquid was treated to remove aromatic hydrocarbon components, and nitrogen was then passed through the catalyst slurry until the odor of aromatic hydrocarbons was no longer noticeable. Next, the mixture was brought into contact with nitrogen containing 7% by volume of oxygen at 70°C for 1 hour, and then the atmosphere was replaced with nitrogen and then with hydrogen. Thereafter, the temperature was raised to 140° C., and stirring was carried out for 4 hours while maintaining the pressure inside the system at 0.5 MPa under a hydrogen atmosphere, and the entire amount of the catalyst slurry was used to carry out an operation for restoring catalytic activity. While the reaction was being continued in this manner, the operation of withdrawing 400 mL of catalyst slurry from the reactor and returning the slurry to the reactor after the catalyst activity recovery operation was continued once a day as described above. The reaction liquid coming out of the oil-water separation tank 118 hours after the start of the reaction was sampled, and the composition of the liquid phase was analyzed by gas chromatography to determine the conversion rate of benzene and the selectivity for cyclohexene. Following sampling of the reaction liquid, catalyst slurry was collected from a catalyst sampling line installed in the tank reactor, and the acetic acid concentration in the aqueous zinc sulfate solution, the ratio of the acetic acid mass to the catalyst mass in the reactor, and the zinc concentration contained in the zirconia-containing ruthenium catalyst were measured. The analytical values, benzene conversion and cyclohexene selectivity are shown in Table 4 below.

[0157] [Example 2-8] A continuous tank reactor was charged with 1200 mL of a solution having a zinc sulfate concentration of 0.62 mol / L, containing 50 g, in terms of dry mass, of a zirconia-containing ruthenium catalyst prepared in the same manner as in Example 2-1. Next, benzene, which had been previously adjusted to contain 1 mg / L of acetic acid, was fed to the continuous tank reactor at 1.2 L / hr at 145°C under a hydrogen pressure of 5 MPa, and a partial hydrogenation reaction of benzene was carried out continuously. During this process, water was supplied so that the composition of the aqueous phase containing the zirconia-containing ruthenium catalyst in the reaction system was always constant, and the reaction product consisting of benzene, cyclohexene, and cyclohexane was continuously removed from the oil-water separation tank. The volume ratio of the aqueous phase to the oil phase in the reactor was kept constant at aqueous phase:oil phase=2:1. The reaction liquid coming out of the oil-water separation tank 22 hours after the start of the reaction was sampled, and the composition of the liquid phase was analyzed by gas chromatography to determine the conversion rate of benzene and the selectivity for cyclohexene. Furthermore, following sampling of the reaction solution, catalyst slurry was collected from a catalyst sampling line installed in the continuous tank reactor, and the acetic acid concentration in the aqueous zinc sulfate solution, the ratio of the acetic acid mass to the catalyst mass in the reactor, and the zinc concentration contained in the zirconia-containing ruthenium catalyst were measured. The analytical values, benzene conversion and cyclohexene selectivity are shown in Table 4 below.

[0158] Example 2-9 The reaction of Example 2-8 was continued, and 24 hours after the start of the reaction, 600 mL of catalyst slurry containing the reaction liquid was extracted from the continuous tank reactor, while 400 mL of catalyst slurry containing zinc sulfate similar to that initially charged in Example 2-8 was charged into the continuous tank reactor. The catalyst slurry containing the extracted reaction liquid was treated to remove aromatic hydrocarbon components, and nitrogen was then passed through the catalyst slurry until the odor of aromatic hydrocarbons was no longer noticeable. Next, the mixture was brought into contact with nitrogen containing 7% by volume of oxygen at 50°C for 1 hour, and then the atmosphere was replaced with nitrogen and then with hydrogen. Thereafter, the temperature was raised to 140° C., and stirring was carried out for 4 hours while maintaining the pressure inside the system at 0.5 MPa under a hydrogen atmosphere, and the entire amount of the catalyst slurry was used to carry out an operation for restoring catalytic activity. While the reaction was being continued in this manner, the operation of withdrawing 400 mL of catalyst slurry from the reactor and returning the slurry to the reactor after the catalyst activity recovery operation was continued once a day as described above. The reaction liquid coming out of the oil-water separation tank 118 hours after the start of the reaction was sampled, and the composition of the liquid phase was analyzed by gas chromatography to determine the conversion rate of benzene and the selectivity for cyclohexene. Furthermore, following sampling of the reaction solution, catalyst slurry was collected from a catalyst sampling line installed in the continuous tank reactor, and the acetic acid concentration in the aqueous zinc sulfate solution, the ratio of the acetic acid mass to the catalyst mass in the reactor, and the zinc concentration contained in the zirconia-containing ruthenium catalyst were measured. The analytical values, benzene conversion and cyclohexene selectivity are shown in Table 4 below.

[0159] Example 2-10 A continuous tank reactor was charged with 1200 mL of a solution having a zinc sulfate concentration of 0.62 mol / L, containing 50 g, in terms of dry mass, of a zirconia-containing ruthenium catalyst prepared in the same manner as in Example 2-1. Next, benzene, which had been previously adjusted to contain 4 mg / L of acetic acid, was fed to the continuous tank reactor at 1.2 L / hr at 145°C under a hydrogen pressure of 5 MPa, and a partial hydrogenation reaction of benzene was carried out continuously. During this process, water was supplied so that the composition of the aqueous phase containing the zirconia-containing ruthenium catalyst in the reaction system was always constant, and the reaction product consisting of benzene, cyclohexene, and cyclohexane was continuously removed from the oil-water separation tank. The volume ratio of the aqueous phase to the oil phase in the reactor was kept constant at aqueous phase:oil phase=2:1. Twenty hours after the start of the reaction, 0.55 g of 96% by mass sulfuric acid was added to the reactor through the water supply line used to replenish the reaction system. After 22 hours, the reaction liquid emerging from the oil-water separation tank was sampled, and the composition of the liquid phase was analyzed by gas chromatography. From the results, the benzene conversion rate and cyclohexene selectivity were determined. Furthermore, following sampling of the reaction solution, catalyst slurry was collected from a catalyst sampling line installed in the continuous tank reactor, and the acetic acid concentration in the aqueous zinc sulfate solution, the ratio of the acetic acid mass to the catalyst mass in the reactor, and the zinc concentration contained in the zirconia-containing ruthenium catalyst were measured. The analytical values, benzene conversion and cyclohexene selectivity are shown in Table 4 below.

[0160] Comparative Example 2-4 A continuous tank reactor was charged with 1200 mL of a solution having a zinc sulfate concentration of 0.62 mg / L, including 50 g, in terms of dry mass, of a zirconia-containing ruthenium catalyst prepared in the same manner as in Example 2-1. Next, benzene, which had been previously adjusted to contain 6 mg / L of acetic acid, was fed to the continuous tank reactor at 145°C under a hydrogen pressure of 5 MPa at a rate of 1.2 L / hr, and a continuous partial hydrogenation reaction of benzene was carried out. During this process, water was supplied so that the composition of the aqueous phase containing the zirconia-containing ruthenium catalyst in the reaction system was always constant, and the reaction product consisting of benzene, cyclohexene, and cyclohexane was continuously removed from the oil-water separation tank. The volume ratio of the aqueous phase to the oil phase in the reactor was kept constant at aqueous phase:oil phase=2:1. The reaction liquid coming out of the oil-water separation tank 22 hours after the start of the reaction was sampled, and the composition of the liquid phase was analyzed by gas chromatography to determine the conversion rate of benzene and the selectivity for cyclohexene. Furthermore, following sampling of the reaction solution, catalyst slurry was collected from a catalyst sampling line installed in the continuous tank reactor, and the acetic acid concentration in the aqueous zinc sulfate solution, the ratio of the acetic acid mass to the catalyst mass in the reactor, and the zinc concentration contained in the zirconia-containing ruthenium catalyst were measured. The analytical values, benzene conversion and cyclohexene selectivity are shown in Table 4 below.

[0161] Comparative Example 2-5 The reaction of Comparative Example 2-4 was continued, and 24 hours after the start of the reaction, 600 mL of catalyst slurry containing the reaction liquid was extracted from the continuous tank reactor, while 400 mL of catalyst slurry containing zinc sulfate similar to that initially charged in Example 2-8 was charged into the continuous tank reactor. The catalyst slurry containing the extracted reaction liquid was treated to remove aromatic hydrocarbon components, and nitrogen was then passed through the catalyst slurry until the odor of aromatic hydrocarbons was no longer noticeable. Next, the mixture was brought into contact with nitrogen containing 7% by volume of oxygen at 50°C for 1 hour, and then the atmosphere was replaced with nitrogen and then with hydrogen. Thereafter, the temperature was raised to 140° C., and stirring was carried out for 4 hours while maintaining the pressure inside the system at 0.5 MPa under a hydrogen atmosphere, and the entire amount of the catalyst slurry was used to carry out an operation for restoring catalytic activity. While the reaction was being continued in this manner, the operation of withdrawing 400 mL of catalyst slurry from the reactor and returning the slurry to the reactor after the catalyst activity recovery operation was continued once a day as described above. The reaction liquid coming out of the oil-water separation tank 118 hours after the start of the reaction was sampled, and the composition of the liquid phase was analyzed by gas chromatography to determine the conversion rate of benzene and the selectivity for cyclohexene. Furthermore, following sampling of the reaction solution, catalyst slurry was collected from a catalyst sampling line installed in the continuous tank reactor, and the acetic acid concentration in the aqueous zinc sulfate solution, the ratio of the acetic acid mass to the catalyst mass in the reactor, and the zinc concentration contained in the zirconia-containing ruthenium catalyst were measured. The analytical values, benzene conversion and cyclohexene selectivity are shown in Table 4 below.

[0162] Comparative Example 2-6 A continuous tank reactor was charged with 1200 mL of a solution having a zinc sulfate concentration of 0.62 mg / L, containing 50 g, in terms of dry mass, of a zirconia-containing ruthenium catalyst prepared in the same manner as in Example 2-1. Next, benzene, which had been previously adjusted to contain 10 mg / L of acetic acid, was fed to the continuous tank reactor at 1.2 L / hr at 145°C under a hydrogen pressure of 5 MPa, and a partial hydrogenation reaction of benzene was carried out continuously. During this process, water was supplied so that the composition of the aqueous phase containing the zirconia-containing ruthenium catalyst in the reaction system was always constant, and the reaction product consisting of benzene, cyclohexene, and cyclohexane was continuously removed from the oil-water separation tank. The volume ratio of the aqueous phase to the oil phase in the reactor was kept constant at aqueous phase:oil phase=2:1. The reaction liquid coming out of the oil-water separation tank 22 hours after the start of the reaction was sampled, and the composition of the liquid phase was analyzed by gas chromatography to determine the conversion rate of benzene and the selectivity for cyclohexene. Furthermore, following sampling of the reaction solution, catalyst slurry was collected from a catalyst sampling line installed in the continuous tank reactor, and the acetic acid concentration in the aqueous zinc sulfate solution, the ratio of the acetic acid mass to the catalyst mass in the reactor, and the zinc concentration contained in the zirconia-containing ruthenium catalyst were measured. The analytical values, benzene conversion and cyclohexene selectivity are shown in Table 4 below.

[0163] Example 2-11 The reaction of Comparative Example 2-6 was continued, and the acetic acid concentration was changed to benzene at 0.01 mg / L 24 hours after the start of the reaction. Furthermore, 400 mL of the catalyst slurry containing the reaction solution was withdrawn, and 400 mL of the slurry that had been subjected to the catalyst activity recovery operation was returned to the reactor. This operation was continued once a day. The catalyst slurry returned to the reactor 24 hours after the start of the reaction was treated until the concentration of acetic acid mixed in the liquid extracted from the reactor was undetectable. Specifically, similar to Comparative Example 5, the catalyst slurry was treated until the odor of aromatic hydrocarbon components was undetectable, and then the mixture was contacted with nitrogen containing 7% by volume of oxygen at 50°C for 1 hour. Next, the mixture was decanted at room temperature, the supernatant was removed, and a freshly prepared 0.62 mol / L aqueous zinc sulfate solution was added, and this procedure was repeated to reduce the acetic acid concentration. Then, 400 mL of the catalyst slurry that had been replaced with nitrogen and hydrogen was heated to 140°C and stirred for 4 hours while maintaining the system pressure at 0.5 MPa under a hydrogen atmosphere. The recovered catalyst slurry was secured and used when adding the catalyst. The reaction liquid coming out of the oil-water separation tank 118 hours after the start of the reaction was sampled, and the composition of the liquid phase was analyzed by gas chromatography to determine the conversion rate of benzene and the selectivity for cyclohexene. Following sampling of the reaction solution, catalyst slurry was collected from a catalyst sampling line installed in the continuous tank reactor, and the acetic acid concentration in the aqueous zinc sulfate solution, the ratio of the nitrogen mass to the catalyst mass in the reactor, and the zinc concentration contained in the zirconia-containing ruthenium catalyst were measured. The analytical values, benzene conversion and cyclohexene selectivity are shown in Table 4 below.

[0164] [Table 4]

[0165] Example 3-1 In this example, after the partial hydrogenation reaction of benzene, an extraction step was carried out in which cyclohexene and cyclohexane obtained by the reaction and unreacted benzene were extracted and separated using dimethylacetamide as an extractant. Furthermore, in the step of recovering benzene from a mixture of the extractant and unreacted benzene and returning the washed benzene to the reactor, the amounts of dimethylamine and acetic acid, which are decomposition products of dimethylacetamide generated in the extraction step, were reduced by washing the benzene with water as described above, and the dimethylamine and acetic acid were recycled to the partial hydrogenation reaction. In order to rapidly reproduce the conditions at the bottom of a benzene recovery column that recovers dimethylacetamide and unreacted benzene, 600 g of dimethylacetamide containing 5.027 g of water and 1.795 g of acetic acid was charged into a 1 L autoclave and heated at 200°C for 42 hours. 400 g of the treated liquid was collected, 1 kg of benzene was added, and distillation under reduced pressure at 80°C and 80 kPa was carried out. After 3 hours of reduced pressure distillation, 170 g of the initial distillate was recovered, and benzene was added to the recovered liquid to make 35 kg, producing a benzene adjusted liquid corresponding to the top of the benzene recovery column. The components of the benzene adjusted solution were analyzed, and the results were dimethylamine 46.9 mg / L and acetic acid 8.31 mg / L. The benzene adjusted solution was subjected to a water washing treatment using a water washing experimental device having a piping outer diameter of 150 mm, a height of 1000 mm, and a 500 mm thick packed bed of Pall rings with an outer diameter of 5 / 8 inch installed in the center of the device, while maintaining the liquid temperature at a constant 40°C. Water was fed downward from four nozzles installed in the upper part of the water-washing experimental apparatus at a total rate of 11.0 L / hr. Meanwhile, the benzene preparation solution was also fed upward from four nozzles installed in the lower part of the apparatus at a rate of 20.7 L / hr, and after contacting with water in an amount 0.53 times the volume of the benzene, the wash water was extracted from the lower part of the water-washing experimental apparatus, and 32.0 kg of washed benzene was recovered from the upper part of the water-washing experimental apparatus. Analysis of the benzene components after washing with water revealed 6.45 mg / L of dimethylamine and 0.82 mg / L of acetic acid. Subsequently, the benzene washed with water as described above was used to continuously carry out a partial hydrogenation reaction of benzene under the same conditions as in Example 1-6. Twenty hours after the start of the reaction, 0.2 g of 96% by mass sulfuric acid was added to the reactor through the supply line for water being replenished in the reaction system, and 22 hours later, the reaction liquid emerging from the oil-aqueous separation tank was sampled. The composition of the liquid phase was analyzed by gas chromatography, and the benzene conversion was found to be 50.6% and the cyclohexene selectivity was 75.4%. In addition, following the sampling of the reaction solution, catalyst slurry was collected from the catalyst sampling line installed in the continuous tank reactor. The dimethylamine concentration in the zinc sulfate aqueous solution was 137 mg / L, the nitrogen concentration was 51 mg / L, and the acetic acid concentration was 17 mg / L. The mass ratio of dimethylamine to the catalyst mass in the reactor was 3.2 × 10 -3 times, nitrogen mass ratio 1.2 x 10 -3 times, acetic acid mass ratio 4.2 x 10 -4 In addition to the fact that the catalyst yield doubled, the zinc concentration in the catalyst was measured and found to be 1.26 mass %.

[0166] This application is based on Japanese patent application (Patent Application No. 2022-125754) and Japanese patent application (Patent Application No. 2022-125785) filed with the Japan Patent Office on August 5, 2022, the contents of which are incorporated herein by reference. [Industrial Applicability]

[0167] The present invention has industrial applicability as a method for producing cycloolefins that efficiently produces cycloolefins with high selectivity over a long period of time while suppressing a decrease in the selectivity of cycloolefins.

Claims

1. A method for producing cycloolefins by partially hydrogenating monocyclic aromatic hydrocarbons with hydrogen in an aqueous zinc sulfate solution in the presence of a ruthenium catalyst, comprising: The zinc sulfate aqueous solution contains dimethylamine, The nitrogen concentration in the zinc sulfate aqueous solution is 0.5 to 3000 mg / L. A method for producing cycloolefins.

2. a part of the aqueous zinc sulfate solution is replaced with a new aqueous zinc sulfate solution, thereby adjusting the nitrogen concentration in the aqueous zinc sulfate solution containing the ruthenium catalyst to 0.5 to 3000 mg / L, and then the partial hydrogenation reaction of the monocyclic aromatic hydrocarbon is carried out. The method for producing cycloolefins according to claim 1 .

3. the nitrogen concentration contained in the monocyclic aromatic hydrocarbons is 0.003 to 35 mg / L; The method for producing cycloolefins according to claim 1 or 2.

4. The ratio of the nitrogen mass to the ruthenium catalyst mass in the zinc sulfate aqueous solution is 5 x 10 －６ ~8 x 10 －２ It is double, The method for producing cycloolefins according to claim 1 or 2.

5. The nitrogen concentration in the zinc sulfate aqueous solution is set to 0.5 to 1500 mg / L, The nitrogen concentration in the monocyclic aromatic hydrocarbon is set to 0.01 to 16 mg / L, The ratio of the mass of nitrogen to the mass of the ruthenium catalyst in the aqueous zinc sulfate solution is 1 x 10 －５ ~5 x 10 －２ As a double, carrying out a partial hydrogenation reaction; The method for producing cycloolefins according to claim 1 or 2.

6. the concentration of dimethylamine in the aqueous zinc sulfate solution is 1.7 to 9900 mg / L; the concentration of dimethylamine in the monocyclic aromatic hydrocarbon is 0.01 to 115 mg / L; The ratio of the mass of dimethylamine to the mass of the ruthenium catalyst in the zinc sulfate aqueous solution is 2 × 10 －５ ~0.26 times The method for producing cycloolefins according to claim 1 or 2.

7. a reaction step of partially hydrogenating the monocyclic aromatic hydrocarbon with hydrogen in the aqueous zinc sulfate solution; an extraction step of extracting the unreacted monocyclic aromatic hydrocarbons with a solvent containing a nitrogen-containing compound after the reaction step; a water washing step in which the extracted monocyclic aromatic hydrocarbons are brought into contact with water in an amount of 0.05 to 1 volume times; a recycling step of subjecting the water-washed monocyclic aromatic hydrocarbon to the reaction step; , and In the reaction step, the content of dimethylamine in the zinc sulfate aqueous solution is 40 to 1700 mg / L, and the ratio of the mass of dimethylamine to the mass of the ruthenium catalyst is 8×10 －４ ~6 x 10 －２ Double, to control, The method for producing cycloolefins according to claim 1 or 2.

8. A method for producing cycloolefins by partially hydrogenating monocyclic aromatic hydrocarbons with hydrogen in an aqueous zinc sulfate solution in the presence of a ruthenium catalyst, comprising: The concentration of acetic acid in the zinc sulfate aqueous solution was 1×10 －３ 100 mg / L or less and perform a partial hydrogenation reaction. A method for producing cycloolefins.

9. By replacing a part of the zinc sulfate aqueous solution with a new zinc sulfate aqueous solution, the concentration of acetic acid in the zinc sulfate aqueous solution in which the ruthenium catalyst is present is increased to 1×10 －３ 100 mg / L or less, and then a partial hydrogenation reaction of monocyclic aromatic hydrocarbons is carried out. The method for producing cycloolefins according to claim 8.

10. The concentration of acetic acid contained in the monocyclic aromatic hydrocarbon is 1×10 －４ ~5 mg / L The method for producing cycloolefins according to claim 8 or 9.

11. The ratio of the mass of acetic acid to the mass of the ruthenium catalyst in the aqueous zinc sulfate solution is 3 x 10 －９ ~2.5 x 10 －３ It is in the double range, The method for producing cycloolefins according to claim 8 or 9.

12. a reaction step of partially hydrogenating the monocyclic aromatic hydrocarbon with hydrogen in the aqueous zinc sulfate solution; an extraction step of extracting the unreacted monocyclic aromatic hydrocarbons with a solvent containing a nitrogen-containing compound after the reaction step; a water washing step in which the extracted monocyclic aromatic hydrocarbons are brought into contact with water in an amount of 0.05 to 1 volume times; a recycling step of subjecting the water-washed monocyclic aromatic hydrocarbon to the reaction step; , and In the reaction step, the ratio of the mass of acetic acid to the mass of the ruthenium catalyst in the zinc sulfate aqueous solution is 1×10 －６ ~5 x 10 －４ Double, to control, The method for producing cycloolefins according to claim 8 or 9.

13. the ruthenium catalyst is a zirconia-containing ruthenium catalyst; a step of regenerating a part or all of the zirconia-containing ruthenium catalyst, Reusing the regenerated zirconia-containing ruthenium catalyst; The method for producing cycloolefins according to claim 1 or 8.

14. the ruthenium catalyst is a zirconia-containing ruthenium catalyst; The zinc concentration in the zirconia-containing ruthenium catalyst is 0.5 to 3.5 mass%. The method for producing cycloolefins according to claim 1 or 8.

15. The monocyclic aromatic hydrocarbon is The alkyl group may be selected from the group consisting of benzene, toluene, and benzene substituted with an alkyl group having 1 to 4 carbon atoms. The method for producing cycloolefins according to claim 1 or 8.