Method for treating waste gypsum board and fluidized bed calciner used therefor

Abstract

To calcine gypsum granules obtained by pulverizing a waste gypsum board into hemihydrate gypsum and / or anhydrous type III gypsum instead of anhydrous type II gypsum, and to enable steady operation of a calciner used.CONSTITUTION: The present invention calcines gypsum granules obtained by pulverizing a waste gypsum board and changes same to hemihydrate gypsum and / or anhydrite type III. Gypsum granules are fed into a fluid tank from a feeding port to the fluid tank of a calcination device by a feeding device, and gypsum granules after calcination are discharged from a discharging port from the fluid tank by a discharging device. The amount of gypsum granules inside the fluid tank is kept within a predetermined range by controlling the feeding device and the discharging device.SELECTED DRAWING: Figure 2

Description

[Technical Field]

[0001] This invention relates to a method for treating waste gypsum boards and a fluidized bed calciner used therein. [Background technology]

[0002] The inventors have proposed a method for recovering gypsum from waste gypsum board (for example, Patent Document 1: WO2012 / 176688). First, the waste gypsum board is crushed using a crusher and then calcined using a calciner to convert the gypsum dihydrate contained in the waste gypsum board into gypsum hemihydrate. Gypsum hemihydrate has high hydration properties, so when it is converted into a gypsum slurry, gypsum particles can be precipitated in a crystallization tank. Then, the gypsum particles are separated from the gypsum slurry using a solid-liquid separator, allowing gypsum to be recovered from the waste gypsum board. Anhydrous type III gypsum may be used instead of gypsum hemihydrate, and the form of the precipitated gypsum particles can be controlled to gypsum dihydrate, gypsum hemihydrate, etc. by controlling the temperature of the crystallization tank. [Prior art documents] [Patent documents]

[0003] [Patent Document 1] WO2012 / 176688 Summary of the Invention [Problem to be solved by the invention]

[0004] Fluidized-bed calciners offer a high level of heat transfer efficiency. In a fluidized-bed calciner, hot air is introduced from the bottom of the fluidized bed, and the granules are heated by the hot air. The granules move while flowing from the inlet to the outlet. An example of a fluidized-bed calciner is shown in Figure 4. Powder is introduced into one end of the fluidized bed in the longitudinal direction, and the calcined powder is discharged from the other end. A dispersion plate 77 with multiple openings is installed at the bottom of the fluidized bed, through which hot air is blown in, heating and fluidizing the powder, and the air is exhausted from the top of the fluidized bed. A dam plate 76 is installed at the outlet side, and the amount of powder in the fluidized bed is controlled by raising and lowering the dam plate 76.

[0005] However, when a fluidized bed calciner is used to calcinate gypsum granules made from crushed waste gypsum board, problems arise. The gypsum granules made from crushed waste gypsum board have a wide particle size distribution. This is because the gypsum granules have a tendency to stick together due to binders such as starch contained in the gypsum board. Furthermore, when the waste gypsum board gets wet, such as from rain, the gypsum granules become more sticky. For these reasons, it is difficult to classify the gypsum granules into a narrow particle size range.

[0006] When calcining gypsum granules with a wide particle size distribution in a fluidized bed calciner equipped with a barrier plate 76, if the calciner is operated at a wind speed that causes large particles to exceed the barrier plate 76, small particles are dispersed into the exhaust line 79 in a short time, accounting for 40 to 60 mass% of the gypsum granules introduced. Because these particles are discharged from the calciner in a short time, some remain in the gypsum dihydrate form at the time of introduction. Note that the form of gypsum suitable for crystallization is hemihydrate or anhydrous type III. The dispersed particles into the exhaust line 79 are collected using a bag filter. The particles collected by the bag filter are combined with the calcined gypsum discharged from the outlet 80. The residual gypsum dihydrate content of the gypsum after the combination must be 5 mass% or less. If this percentage is exceeded, the average particle size of the gypsum dihydrate produced in the crystallization process decreases. Under the above conditions, the amount of dispersion is high, resulting in a residual gypsum dihydrate content of 10 mass% or more.

[0007] On the other hand, if the wind speed is reduced to reduce the amount of small particles flying away, the large particles will not pass through the weir plate and will remain in the calciner. As the amount of retained material increases, the operation of the fluidized bed becomes unstable and eventually becomes inoperable. Furthermore, the retained gypsum becomes anhydrous Type II, which is not suitable for crystallization.

[0008] We also considered providing a discharge port below the dam board 76 to discharge large gypsum particles. However, because the gypsum particles produced by crushing waste gypsum boards have low fluidity, it was not possible to discharge the gypsum particles at the desired rate, even if a discharge port was provided. As a result, it was not possible to sufficiently prevent the large gypsum particles from converting into anhydrous type II gypsum, and it was also difficult to operate the calciner steadily.

[0009] An object of the present invention is to provide a method for calcining gypsum granules obtained by crushing waste gypsum boards into hemihydrate and / or anhydrous type III gypsum instead of anhydrous type II gypsum, and to enable steady operation of the calciner used. Another object of the present invention is to provide a fluidized-tank calciner suitable for these purposes. [Means for solving the problem]

[0010] In the method for treating waste gypsum board of this invention, gypsum particles obtained by crushing waste gypsum board are calcined to convert them into hemihydrate gypsum and / or anhydrous type III gypsum. The method for treating waste gypsum board of this invention is characterized in that the gypsum particles are introduced into the fluidization tank of a calciner through an inlet to the fluidization tank by a feeding device, the calcined gypsum particles are discharged from an outlet of the fluidization tank by a discharging device, and the amount of gypsum particles in the fluidization tank is maintained within a predetermined range by controlling the feeding device and the discharging device.

[0011] The calciner of this invention is for calcining gypsum granules derived from waste gypsum board. The calciner of this invention is characterized by comprising a fluidized bed, an inlet equipped with a device for feeding gypsum granules, an outlet equipped with a device for discharging gypsum granules, and a controller that controls the inlet and discharge devices to maintain the amount of gypsum granules in the fluidized bed within a predetermined range. Note that in this specification, descriptions regarding the method for treating waste gypsum board, particularly descriptions regarding calcination, also apply directly to fluidized bed calciners.

[0012] In this invention, since no weir plate is provided, the flow of large particles can be achieved only by lateral movement on the dispersion plate. The amount of small gypsum particles that leave the fluidization tank as gypsum dihydrate can be reduced if the air volume required for lateral movement is sufficient. For example, the residual gypsum dihydrate rate in the gypsum after calcination can be reduced to less than 5% by mass.

[0013] In this invention, the amount of gypsum granules in the fluidization tank is adjusted by increasing or decreasing the amount of gypsum charged to and discharged from the fluidization tank, rather than by adjusting the height of the weir plate. For example, to increase the amount of gypsum granules in the fluidization tank, the amount charged is increased or the amount discharged is decreased. After a predetermined amount of gypsum granules is reached, the amount charged and the amount discharged are adjusted to be the same, and steady-state operation is performed. The amount of gypsum granules in the fluidization tank can be measured by, for example, the pressure difference above and below the dispersion plate. Keeping the amount of gypsum charged constant and increasing or decreasing the amount discharged is also included in controlling the charging device and discharge device.

[0014] Preferably, hot air is blown into the fluidization tank through a dispersion plate at the bottom, and the blown-in hot air is exhausted from an exhaust port at the top of the fluidization tank. The width of the fluidization tank is made larger at the top than at the bottom. The flow rate of the hot air decreases at the top of the fluidization tank, causing mainly small particle size gypsum suspended in the hot air to settle, thereby restricting the small particle size gypsum from being discharged from the fluidization tank in a short period of time.

[0015] Preferably, the dispersion plate is tilted downward from the inlet side to the outlet side, which moves all of the gypsum in the fluidization tank toward the outlet side, preventing large particle size gypsum from remaining in the fluidization tank for a long period of time.

[0016] Preferably, a cyclone is provided in the exhaust line from the fluidization tank. Of the small gypsum particles scattered in the exhaust line, relatively large ones are collected by the cyclone and returned to the fluidization tank. The repaired gypsum particles aggregate and grow as they circulate through the cyclone and fluidization tank, so they no longer scatter from the exhaust line. [Brief explanation of the drawings]

[0017] [Figure 1] FIG. 1 is a diagram showing an outline of a method for recovering gypsum from waste gypsum board in an embodiment. [Figure 2] Schematic cross-sectional view of a fluidized bed calciner used in the examples, taken along a plane perpendicular to the feed direction. [Figure 3] Schematic cross-sectional view of the fluidized bed calciner of FIG. 2 along a vertical plane in the width direction. [Figure 4]Schematic cross-sectional view of a fluidized bed calciner of a comparative example DETAILED DESCRIPTION OF THE INVENTION

[0018] Examples for carrying out the present invention are shown below. The scope of the present invention should be determined based on the claims, taking into account the description in the specification and well-known techniques in this field, and in accordance with the understanding of those skilled in the art. The scope of the present invention is not limited by the examples. [Example]

[0019] An embodiment is shown in Figures 1 to 3. Figure 1 shows the process from waste gypsum board to the recovery of gypsum. In pretreatment process 2, waste gypsum board (not shown) is fed into crusher 10 through inlet 11 and roughly crushed. The crushed pieces are processed through sieve 16, and the crushed pieces that pass through the sieve are fed to sorting conveyor 18, where foreign matter such as metal, wood chips, and mortar is visually removed. The gypsum granules that pass through the sieve are fed into fine crusher 30 (described below). A fixed-volume conveyor 20 transports the crushed pieces, from which foreign matter has been removed, in predetermined amounts. A magnetic separator 25 is installed near the fixed-volume conveyor 20, and magnetically removes magnetic material such as metal foreign matter. The crushed pieces are then fed to fine crusher 30, where they are crushed into gypsum granules of a size suitable for calcination and crystallization, and stored in silo 40.

[0020] In the next calcination step 4, the gypsum granules are calcined in a fluidized bed calciner 50 to convert the dihydrate gypsum into hemihydrate and / or anhydrous type III gypsum.

[0021] In the crystallization step 6, the hemihydrate and / or anhydrous type III gypsum obtained by calcination is mixed with a gypsum slurry or the like in a mixer, and gypsum particles such as gypsum dihydrate are precipitated in a crystallization tank. In the filtration step 8, the gypsum slurry is extracted from the crystallization tank, paper powder and the like are removed using a sieve, and the remaining slurry is subjected to solid-liquid separation using a filter to recover gypsum powder such as gypsum dihydrate. The liquid component after solid-liquid separation is mixed with industrial water and circulated to the mixer.

[0022] A fluidized-bed calciner 50 (hereinafter referred to as "calciner 50") used in the calcination step will be described with reference to Figures 2 and 3. Calciner 50 has a bottom plate 51 and a top plate 52, and hot air, for example, at about 300°C, is supplied by an air supply blower 53b from an air supply port 53 provided in bottom plate 51. A dispersion plate 54 is provided above bottom plate 51, and hot air is blown in through openings in dispersion plate 54. Preferably, dispersion plate 54 is inclined downward at an angle θ from the inlet side to the outlet side. The angle θ is, for example, 0.5° to 5°, and preferably 1° to 3°. The space between dispersion plate 54 and top plate 52 is the fluidized bed.

[0023] Gypsum granules are charged through charging port 55 and discharged through discharge port 56. To maintain a constant pressure inside the fluidization tank, a rotary valve 57 is provided at charging port 55, and a rotary valve 58 is also provided at discharge port 56, allowing charging and discharging while mechanically isolating the tank from the outside air. Any device other than rotary valves 57 and 58 may be used as long as it can charge or discharge while isolating the tank from the outside air and can control the amount charged (discharged), such as a double damper.

[0024] The amount of gypsum 70 in the calciner 50 is measured from the difference in pressure measured by pressure sensors 59a and 59b. Pressure sensor 59a measures the pressure of the hot air between the bottom plate 51 and the dispersion plate 54. Pressure sensor 59b measures the pressure of the hot air between the gypsum 70 and the top plate 52. The difference between these pressures indicates the pressure lost by the hot air as it passes through the gypsum 70, and represents the amount of gypsum 70. Any sensor can be used as long as it can measure the amount of gypsum 70.

[0025] An exhaust line 61 is connected to the top plate 52, and its outlet is connected to the cyclone 60. The airflow to the top of the cyclone 60 is treated by a bag filter 63 and exhausted from an exhaust port 62 by an exhaust blower 62b. A rotary valve (not shown) is also connected to the bag filter 63 for discharging the collected gypsum particles, and the collected gypsum particles are discharged without being returned to the calciner, and are combined with the gypsum from the discharge port 56. The gypsum granules collected by the cyclone 60 are returned to the fluidization tank using a rotary valve 64.

[0026] As shown in Figure 3, the fluidized bed has three side walls 65, 66, and 67, and the upper part of the fluidized bed is wider than the lower part, so the flow rate of the hot air is slower at the upper part of the fluidized bed.

[0027] Reference numeral 71 denotes an inclined plate in front of the discharge port 56. A controller 72 estimates the amount of gypsum 70 in the fluidization tank based on signals S1 and S2 from pressure sensors 59a and 59b, and controls rotary valves 57 and 58 based on control signals P1 and P2.

[0028] Examples of the size of the calciner 50 are shown below. The hot air is, for example, about 300°C at the air inlet 63 and about 150°C at the inlet of the exhaust line 61, and the flow rate of the hot air in the fluidization tank is, for example, about 1 to 2 m / s. The target heating temperature of the gypsum 70 is, for example, about 130°C. The distribution plate 54 is, for example, 5 m long and 1 m wide, the height from the distribution plate 54 to the top plate 52 is, for example, 3 m, the thickness of the accumulated gypsum 70 is, for example, 200 mm to 400 mm, the amount of gypsum in the fluidization tank is, for example, 600 to 1200 kg, and the average residence time of the gypsum in the fluidization tank is about 20 minutes to 40 minutes.

[0029] The operation of the calciner 50 will now be described. The controller 72 controls the rotary valves 57 and 58 so as to keep the amount of gypsum 70 in the fluidization tank constant. Because the discharge of the gypsum particles is controlled by the rotary valve 58, not by a weir plate, the gypsum particles only need to flow from right to left in FIG. 2 and do not need to overcome the weir plate. This makes it possible to reduce the difference in residence time between large and small gypsum particles.

[0030] Since the gypsum particles can be moved horizontally, the amount of hot air supplied can be reduced, thereby reducing the amount of gypsum particles scattered into the exhaust line 61. This also reduces the amount of small-diameter gypsum particles that reach the bag filter 63 as gypsum dihydrate.

[0031] Because the distribution plate 54 is inclined toward the outlet at an inclination angle θ, the gypsum 70 moves toward the outlet. Because the fluidization tank is wider at the top, the flow rate of the hot air decreases at the top of the fluidization tank, causing small floating gypsum particles to settle. This prevents small gypsum particles from reaching the discharge outlet 56 in a short time and further reduces the amount of gypsum dispersed into the exhaust line 61. By discharging the gypsum through the rotary valve 58 without installing a weir plate, by inclining the distribution plate 54, and by widening the top of the fluidization tank, large and small gypsum particles can be discharged from the fluidization tank with approximately the same retention time. Of these three elements, the essential element is discharging the gypsum through the rotary valve 58 without installing a weir plate.

[0032] The cyclone 60 captures gypsum fines in the exhaust line. The captured gypsum fines aggregate and grow in size, for example, in the cyclone and fluidized bed. This reduces the amount of gypsum fines that reach the bag filter 63. [Explanation of symbols]

[0033] 2 Pretreatment process 4. Calcination process 6 Crystallization process 8. Filtration process 10 Crusher 11 Inlet 16 Sieve 18 Sorting conveyor 20 Fixed-quantity conveyor 25 Magnetic separator 30 Fine crusher 32 Magnetic separation pipe 40 Silo 50 Fluidized bed calciner 51 Bottom plate 52 Top plate 53 Air supply port 53b Intake air blower 54 Dispersion plate 55 Inlet 56 Outlet 57, 58, 64 Rotary valve 59a,b Pressure sensor 60 Cyclone 61 Exhaust line 62 Exhaust port 62b Exhaust Blower 63 Bag filter 65,66,67 side wall 70 plaster 71 Inclined plate 72 Controller 76 Weir plate 77 Dispersion plate 78 Powder 79 Exhaust line 80 Outlet θ Tilt angle P1, P2 control signal S1, S2 sensor signal

Claims

1. A method for treating waste gypsum board, comprising calcining gypsum particles obtained by crushing waste gypsum board to convert them into hemihydrate gypsum and / or anhydrous type III gypsum, The gypsum granules are charged into the fluidized bed tank of the calciner through a charging port by a charging device, and The calcined gypsum granules are discharged from a discharge port of the fluidized bed by a discharge device. Furthermore, by controlling the charging device and the discharging device, the amount of gypsum granules in the fluidization tank is kept within a predetermined range, Hot air is blown into the fluidized bed through a dispersion plate at the bottom of the fluidized bed, By inclining the dispersion plate downward from the inlet side to the outlet side, the gypsum particles are easily moved to the outlet side, The method for treating waste gypsum boards is further characterized in that the fluidization tank is not equipped with a dam board.

2. The hot air blown into the fluidized bed is exhausted from an exhaust port at the top of the fluidized bed, The method for treating waste gypsum boards according to claim 1, further comprising the step of making the width of the fluidization tank larger at the upper part than at the lower part, thereby reducing the flow rate of the hot air at the upper part of the fluidization tank and allowing the gypsum floating in the hot air to settle.

3. 3. The method for treating waste gypsum board according to claim 1, wherein an exhaust line equipped with a cyclone is connected to the fluidization tank, and a portion of the gypsum particles scattered in the exhaust line is collected by the cyclone and returned to the fluidization tank.

4. A calciner for calcining gypsum granules derived from waste gypsum board, a flow tank; an inlet equipped with a gypsum granule injector; a discharge port provided with a gypsum granule discharge device; a controller that controls the charging device and the discharging device to keep the amount of gypsum granules in the fluidization tank within a predetermined range; and The fluidized bed is provided with a dispersion plate at the bottom for blowing hot air, and the dispersion plate is inclined downward from the inlet side to the outlet side to facilitate the movement of the gypsum granules toward the outlet side. The fluidized bed calciner is further characterized in that the fluidized bed is not provided with a weir plate.