mirror

Abstract

To provide a mirror that hardly becomes chipped even when dropped.SOLUTION: A mirror according to the present invention comprises a mirror body which is formed in a polygonal shape in a plan view, and which has a first principal plane reflecting an image, a second principal plane on the opposite side of the first principal plane, and a peripheral edge surface for connecting the first and second principal planes. The peripheral edge surface has a plurality of first end surfaces, and a second end surface for connecting the first end surfaces adjacent to each other. The second end surface constitutes a first chamfered part that is formed at an outer edge of the mirror body in a plan view.SELECTED DRAWING: Figure 1

Description

[Technical Field]

[0001] The present invention relates to a mirror. [Background technology]

[0002] There are various types of mirrors, and for example, Patent Document 1 discloses an anticorrosion mirror. [Prior art documents] [Patent documents]

[0003] [Patent Document 1] Japanese Patent Application Laid-Open No. 2010-330 Summary of the Invention [Problem to be solved by the invention]

[0004] Because mirrors are made of glass plates, they must be handled carefully and may break or chip if dropped. The present invention has been made to solve the above problem, and aims to provide a mirror that is less likely to chip even if dropped. [Means for solving the problem]

[0005] Item 1. A mirror body is provided which is formed in a polygonal shape in a plan view and has a first main surface on which an image is reflected, a second main surface opposite to the first main surface, and a peripheral surface connecting the first main surface and the second main surface, the peripheral surface includes a plurality of first end faces and second end faces connecting adjacent first end faces, A mirror, wherein the second end surface constitutes a first chamfered portion formed on the outer edge of the mirror body in a plan view.

[0006] Item 2. The mirror according to item 1, wherein a second chamfer is formed between the first main surface and the peripheral surface.

[0007] Item 3. The mirror according to item 1 or 2, further comprising an anti-fogging layer covering at least a portion of the first main surface.

[0008] Item 4. The mirror according to Item 3, wherein the antifogging layer and the first main surface are chemically bonded.

[0009] Item 5. The mirror according to Item 3 or 4, further comprising an underlayer disposed between the antifogging layer and the first main surface.

[0010] Item 6. A second chamfered portion is formed between the first main surface and the peripheral surface, Item 6. The mirror according to any one of items 3 to 5, wherein the anti-fogging layer is arranged to cover the second chamfered portion.

[0011] Item 7. The mirror according to Item 6, wherein the antifogging layer is disposed so as to cover the peripheral surface.

[0012] Item 8. The mirror according to Item 7, wherein the anti-fogging layer has a pencil hardness of H to 2H.

[0013] Item 9. The mirror according to any one of Items 3 to 8, wherein the antifogging layer has a thickness of 2 to 12 μm.

[0014] Item 10. The mirror according to any one of Items 3 to 9, wherein the antifogging layer is not disposed in a peripheral region of a predetermined width extending from the periphery of the first main surface toward the center.

[0015] Item 11. The mirror according to any one of Items 3 to 9, wherein the entire first main surface is covered with the antifogging layer.

[0016] Item 12. The anti-fogging layer is arranged to cover the peripheral surface, Item 12. The mirror according to any one of items 3 to 11, wherein the thickness of the anti-fogging layer disposed on the peripheral surface is greater than the thickness of the anti-fogging layer disposed on the first main surface.

[0017] Item 13. The mirror according to any one of Items 3 to 12, wherein the anti-fogging layer has anti-fogging properties due to hydrophilicity.

[0018] Item 14. The mirror according to Item 13, wherein the anti-fogging layer further has anti-fogging properties due to water absorption.

[0019] Item 15. The mirror according to Item 11, wherein the antifogging layer is made of a material containing a water-absorbing resin as a main component.

[0020] Item 16. The mirror according to Item 15, wherein the water-absorbing resin contains at least one of an epoxy resin and a polyvinyl acetal resin.

[0021] Item 17. The mirror according to any one of Items 3 to 16, wherein the anti-fogging layer has a shatterproof function.

[0022] Item 18. The anti-fog mirror according to claim 17, wherein the anti-fog layer has a crosslinked structure formed by a hydrolyzable metal compound.

[0023] Item 19. The anti-fog mirror according to Item 18, wherein the hydrolyzable metal compound comprises silicon alkoxide.

[0024] Item 20. The anti-fog mirror according to any one of Items 17 to 19, wherein the adhesion of the anti-fog layer to the mirror body is Class 0 or 1 in a cross-cut test according to JIS K5600-5-6.

[0025] Item 21. An anti-fog mirror according to any one of Items 17 to 20, wherein a linear cut is formed on the second main surface of the mirror body with a cutter, a round rod placed on a horizontal plane is brought into contact with the anti-fog layer facing downward so as to correspond to the cut, and pressure is applied to both sides of the cut, so that when the mirror body is split, the anti-fog layer is not cut.

[0026] Item 22. The mirror according to any one of items 3 to 21, further comprising a protective film covering the anti-fogging layer.

[0027] Item 23. The protective film has a sheet-like substrate and an adhesive layer disposed on one surface of the substrate, the adhesive layer adheres the substrate to the anti-fogging layer; Item 23. The mirror according to item 22, wherein the peripheral edge of the substrate has an area where the adhesive layer is not disposed.

[0028] Item 24. The anti-fogging layer is arranged to cover the peripheral surface, Item 24. The mirror according to item 23, wherein the protective film is not adhered to at least a portion of the anti-fogging layer covering the peripheral surface.

[0029] Item 25. The mirror according to any one of Items 22 to 24, wherein the protective film is formed so as to protrude from the mirror body at the location where the first chamfered portion is formed.

[0030] Item 26. The mirror according to any one of Items 22 to 25, wherein the protective film has a bending strength of 96 to 131 MPa.

[0031] Item 27. The mirror according to any one of Items 22 to 26, wherein the thickness of the protective film is 30 to 90 μm.

[0032] Item 28. A mirror according to any one of items 22 to 27, wherein the protective film is configured to cover the anti-fogging layer in a divided state.

[0033] Item 29. The mirror body is a semi-metal layer laminated on one surface of the glass plate; a resin protective layer laminated on the semi-metal layer; an inorganic oxide layer made of an inorganic oxide laminated between the semi-metal layer and the protective layer; Item 29. The mirror according to any one of items 1 to 28, comprising:

[0034] Item 30. The mirror of claim 29, wherein the semimetal layer is primarily composed of Si or Ge.

[0035] Item 31. The mirror body is A glass plate and a metal layer laminated on one surface of the glass plate; a resin protective layer laminated on the metal layer; Item 29. The mirror according to any one of items 1 to 28, comprising:

[0036] Item 32. The other surface of the glass plate constitutes the first main surface, Item 32. The mirror according to item 31, wherein an anti-fogging layer is disposed so as to cover the first main surface.

[0037] Item 33. On the peripheral surface, Item 33. The mirror of item 31 or 32, further comprising a peripheral protective layer disposed to cover a first interface between the glass plate and the metal layer and a second interface between the metal layer and the protective layer.

[0038] Item 34. The other surface of the glass plate constitutes the first main surface, an anti-fogging layer is disposed so as to cover the first main surface; On the peripheral surface, a peripheral protective layer disposed to cover a first interface between the glass plate and the metal layer and a second interface between the metal layer and the protective layer; Item 32. The mirror according to item 31, wherein a portion of the anti-fogging layer covers the peripheral protective layer.

[0039] Item 35. The mirror according to Item 33 or 34, wherein the peripheral protective layer is formed from an ultraviolet curable resin.

[0040] Item 36. A mirror according to any one of Items 33 to 35, wherein an area not covered with the peripheral protective layer is provided on the edge surface of the glass plate that is exposed to the outside on the peripheral surface.

[0041] Item 37. Further provided with a shatterproof film that prevents fragments from scattering when the mirror body is broken, Item 37. The mirror according to any one of items 31 to 36, wherein the shatterproof film is arranged to cover the protective layer.

[0042] Item 38. The mirror according to any one of items 31 to 37, wherein the protective layer has multiple types of information printed on it.

[0043] Item 39. The mirror according to any one of Items 3 to 38, wherein the anti-fogging layer takes 30 seconds or more to form condensation. [Effects of the Invention]

[0044] According to the present invention, it is possible to make the device less likely to chip even if dropped. [Brief explanation of the drawings]

[0045] [Figure 1] 1 is a plan view showing an embodiment of a mirror according to the present invention. [Figure 2] FIG. 2 is a cross-sectional view of FIG. 1. [Figure 3] FIG. 10 is a cross-sectional view showing another example of a mirror according to the present invention. [Figure 4] FIG. 10 is a cross-sectional view showing another example of a mirror according to the present invention. [Figure 5] FIG. 10 is a cross-sectional view showing another example of a mirror according to the present invention. [Figure 6] FIG. 10 is a cross-sectional view showing another example of a mirror according to the present invention. [Figure 7] FIG. 1 is a schematic diagram of an apparatus for evaluating anti-fogging performance. [Figure 8] FIG. 10 is a cross-sectional view showing another example of a mirror according to the present invention. DETAILED DESCRIPTION OF THE INVENTION

[0046] Hereinafter, an embodiment of a mirror according to the present invention will be described with reference to the drawings. The mirror according to this embodiment includes a mirror body. Below, the mirror body will be described first, and then various additional elements, such as an anti-fogging layer, that are added to the mirror body will be described. <1. Overview of the mirror body> Fig. 1 is a plan view of the mirror body, and Fig. 2 is a cross-sectional view of the mirror body taken along line AA. As shown in Figs. 1 and 2, mirror body 1 has an outer shape that is rectangular in plan view, and has a first main surface 11 on which an image is reflected, a second main surface 12 opposite to first main surface 11, and a peripheral surface 13 that connects first main surface 11 and second main surface 12. However, the planar shape of mirror body 1 is not particularly limited, and it can be formed into a polygonal shape in addition to the rectangular shape shown in Fig. 1.

[0047] The peripheral surface 13 has four first end faces 131 and second end faces 132 connecting adjacent first end faces 131. The four first end faces 131 are end faces that form the four main sides of a rectangle, and adjacent first end faces 131 are perpendicular to each other. The second end faces 132 are connected to adjacent first end faces 131 so as to extend obliquely in a plan view. In other words, the second end faces 132 form a chamfered portion on the periphery of the mirror body 1 in a plan view. Hereinafter, the second end faces 132 may be referred to as a first chamfered portion.

[0048] 1 and 2, a chamfered portion 14 can be formed between the first main surface 11 and the peripheral surface 13, but this is not essential. Hereinafter, this chamfered portion 14 may be referred to as a second chamfered portion. The second chamfered portion 14 is formed in the glass plate 2 (described later) in cross section, and is connected to the first main surface 11 and the peripheral surface 13 so as to extend obliquely.

[0049] 2. Layer structure of the mirror body 2, the mirror body 1 has a glass plate 2 having a first surface (lower surface) and a second surface (upper surface), a metal layer 3 laminated on the first surface of the glass plate 2, and a protective layer 4 laminated so as to cover the metal layer 3, and the second surface of the glass plate 2 forms a first main surface 11. Below, each member constituting the mirror body 1 will be described.

[0050] <2-1. Glass plate> The glass plate 2 according to this embodiment can be a known glass plate, and can be formed of heat-absorbing glass, general clear glass, green glass, or UV green glass. Examples of clear glass, heat-absorbing glass, and soda-lime glass are shown below.

[0051] (clear glass) SiO2:70~73% by mass Al2O3:0.6~2.4% by mass CaO: 7~12% by mass MgO: 1.0~4.5% by mass RO: 13 to 15 mass% (R is an alkali metal) Total iron oxide converted to Fe2O3 (T-Fe2O3): 0.08 to 0.14 mass%

[0052] (heat-absorbing glass) The composition of the heat ray absorbing glass can be, for example, based on the composition of clear glass, with the ratio of total iron oxide (T-Fe2O3) converted to Fe2O3 being 0.4 to 1.3 mass%, the ratio of CeO2 being 0 to 2 mass%, and the ratio of TiO2 being 0 to 0.5 mass%, and the amount of the glass framework components (mainly SiO2 and Al2O3) reduced by the amount of the increase in T-Fe2O3, CeO2, and TiO2.

[0053] (soda-lime glass) SiO2: 65~80% by mass Al2O3: 0~5% by mass CaO: 5~15% by mass MgO: 2% by mass or more NaO: 10~18% by mass K2O: 0~5% by mass MgO+CaO: 5~15% by mass Na2O+K2O: 10~20% by mass SO3:0.05~0.3% by mass B2O3:0~5% by mass Total iron oxide (T-Fe2O3) converted to Fe2O3: 0.02 to 0.03 mass%

[0054] The thickness of the glass plate 2 according to this embodiment is not particularly limited, but is preferably 1 to 10 mm, and more preferably 3 to 8 mm, for example.

[0055] <2-2. Metal layer> The metal layer 3 is composed of a silver mirror film 31 and a copper film 32. That is, a known silver mirror film 31 that reflects an image is laminated on the first surface of the glass plate 2, and a copper film 32 is further laminated to cover this silver mirror film 31. The copper film 32 functions as a protective layer for the silver mirror film 31. However, the copper film 32 can be omitted and the metal layer can be formed only with the silver mirror film 31.

[0056] <2-3.Protective layer> Protective layer 4 is a layer that covers the copper film 32, and can be made of a resin material such as epoxy resin or acrylic silicone resin. In addition, various information about the mirror, such as the manufacturing location and date of the mirror, and information about the anti-fogging layer (described later), can be added to this protective layer 4 by printing or the like.

[0057] <2-4. Peripheral protective layer> The mirror body 1 is constructed by laminating a glass plate 2, a metal layer 3, and a protective layer 4 in this order, so the interface between these layers is exposed at the peripheral surface 13. Therefore, if moisture penetrates through these interfaces, the metal layer 3 may be deteriorated. Therefore, as shown in FIG. 3, a peripheral protective layer 5 can be provided to cover the peripheral surface 13 of the mirror body 1, if necessary. The peripheral protective layer 5 can be formed from a resin material, such as a UV-curable resin, a two-component epoxy resin, or a thermosetting resin. To facilitate lamination of the peripheral protective layer 5, as shown in FIG. 4, a diagonal cutout (which can also be a chamfered portion) can be formed in the cross section of the peripheral surface 13, and the peripheral protective layer 5 can be laminated to cover this cutout. In this case, the edge of the glass plate 2 may be exposed or covered with the peripheral protective layer 5, as shown in FIG. 4. The notch is formed so as to extend obliquely inward from the edge of the glass plate 2 toward the protective layer 4, and the interface between the glass plate 2, the metal layer 3, and the protective layer 4 is positioned in this notch.

[0058] <3. Anti-fogging layer> 5, an anti-fogging layer 7 can be laminated, if necessary, on the second main surface 12 of the glass plate 2 of the mirror body 1. The anti-fogging layer 7 will be described in detail below.

[0059] The anti-fogging layer 7 is not particularly limited as long as it has an anti-fogging effect on the glass plate 2, and any known anti-fogging layer can be used. Generally, anti-fogging layers 7 are classified into hydrophilic types that form a water film on the surface from water generated from water vapor, water-absorbent types that absorb water vapor, water-repellent and water-absorbent types that make it difficult for water droplets to condense on the surface, and water-repellent types that repel water droplets generated from water vapor, and any type of anti-fogging layer can be used. Below, an example of a water-repellent and water-absorbent anti-fogging layer will be described. [Organic-inorganic composite anti-fog layer] The organic-inorganic composite anti-fogging layer is a single-layer film or a laminated multi-layer film formed on the surface of the glass plate 2. The organic-inorganic composite anti-fogging layer contains at least a water-absorbing resin, a water-repellent group, and a metal oxide component. The anti-fogging layer 7 may further contain other functional components as necessary. Any type of water-absorbing resin may be used as long as it is a resin that can absorb and retain water. The water-repellent group can be supplied to the anti-fogging layer 7 from a metal compound having a water-repellent group (a water-repellent group-containing metal compound). The metal oxide component can be supplied to the anti-fogging layer 7 from a water-repellent group-containing metal compound or other metal compound, metal oxide fine particles, etc. Each component will be described below.

[0060] (Water absorbent resin) The water-absorbent resin is not particularly limited, and examples thereof include polyethylene glycol, polyether resins, polyurethane resins, starch resins, cellulose resins, acrylic resins, epoxy resins, polyester polyols, hydroxyalkyl cellulose, polyvinyl alcohol, polyvinyl pyrrolidone, polyvinyl acetal resins, polyvinyl acetate, etc. Among these, preferred are hydroxyalkyl cellulose, polyvinyl alcohol, polyvinyl pyrrolidone, polyvinyl acetal resins, polyvinyl acetate, epoxy resins, and polyurethane resins, more preferred are polyvinyl acetal resins, epoxy resins, and polyurethane resins, and particularly preferred is polyvinyl acetal resin.

[0061] Polyvinyl acetal resins can be obtained by acetalizing polyvinyl alcohol through a condensation reaction with an aldehyde. Acetalization of polyvinyl alcohol can be carried out using known methods, such as precipitation using an aqueous medium in the presence of an acid catalyst or dissolution using a solvent such as alcohol. Acetalization can also be carried out in parallel with the saponification of polyvinyl acetate. The degree of acetalization is preferably 2 to 40 mol%, more preferably 3 to 30 mol%, particularly preferably 5 to 20 mol%, and in some cases 5 to 15 mol%. The degree of acetalization can be measured, for example, by C-nuclear magnetic resonance spectroscopy. Polyvinyl acetal resins having a degree of acetalization within the above range are suitable for forming organic-inorganic composite anti-fogging layers with good water absorption and water resistance.

[0062] The average degree of polymerization of polyvinyl alcohol is preferably 200 to 4500, more preferably 500 to 4500. A high average degree of polymerization is advantageous for forming an organic-inorganic composite anti-fogging layer with good water absorption and water resistance, but if the average degree of polymerization is too high, the viscosity of the solution becomes too high, which may hinder film formation. The saponification degree of polyvinyl alcohol is preferably 75 to 99.8 mol%.

[0063] Examples of aldehydes to be condensed with polyvinyl alcohol include aliphatic aldehydes such as formaldehyde, acetaldehyde, butylaldehyde, hexylcarbaldehyde, octylcarbaldehyde, and decylcarbaldehyde. Other examples include benzaldehyde; 2-methylbenzaldehyde, 3-methylbenzaldehyde, 4-methylbenzaldehyde, and other alkyl-substituted benzaldehydes; chlorobenzaldehyde and other halogen-substituted benzaldehydes; substituted benzaldehydes in which hydrogen atoms are substituted with functional groups other than alkyl groups, such as hydroxy groups, alkoxy groups, amino groups, and cyano groups; and condensed aromatic ring aldehydes such as naphthaldehyde and anthraldehyde. Aromatic aldehydes with strong hydrophobicity are advantageous for forming an organic-inorganic composite anti-fogging layer with a low degree of acetalization and excellent water resistance. The use of an aromatic aldehyde is advantageous in that it allows the formation of a film with high water absorption while leaving many hydroxyl groups. The polyvinyl acetal resin preferably contains an acetal structure derived from an aromatic aldehyde, particularly benzaldehyde.

[0064] Examples of epoxy resins include glycidyl ether epoxy resins, glycidyl ester epoxy resins, glycidyl amine epoxy resins, alicyclic epoxy resins, etc. Among these, alicyclic epoxy resins are preferred.

[0065] The polyurethane resin may be a polyurethane resin composed of a polyisocyanate and a polyol, and the polyol is preferably an acrylic polyol or a polyoxyalkylene polyol.

[0066] The organic-inorganic composite anti-fogging layer contains a water-absorbing resin as its main component. In the present invention, the term "main component" refers to the component with the highest content by mass. From the viewpoints of film hardness, water absorbency, and anti-fogging properties, the content of the water-absorbing resin based on the weight of the organic-inorganic composite anti-fogging layer is preferably 50% by weight or more, more preferably 60% by weight or more, and particularly preferably 65% ​​by weight or more, and is 95% by weight or less, more preferably 90% by weight or less.

[0067] (water-repellent base) To fully obtain the above-mentioned effects of the water-repellent group, it is preferable to use a water-repellent group with high water repellency. The preferred water-repellent group is at least one selected from (1) linear or cyclic alkyl groups having 3 to 30 carbon atoms, and (2) linear or cyclic alkyl groups having 1 to 30 carbon atoms in which at least a portion of the hydrogen atoms has been substituted with fluorine atoms (hereinafter, sometimes referred to as "fluorine-substituted alkyl groups").

[0068] With regard to (1) and (2), the chain or cyclic alkyl group is preferably a chain alkyl group. The chain alkyl group may be a branched alkyl group, but is preferably a linear alkyl group. An alkyl group having more than 30 carbon atoms may cause the anti-fogging layer 7 to become cloudy. From the viewpoint of the balance between the anti-fogging properties, strength, and appearance of the film, the number of carbon atoms in the alkyl group is preferably 20 or less, more preferably 6 to 14. Particularly preferred alkyl groups are linear alkyl groups having 6 to 14 carbon atoms, particularly 6 to 12 carbon atoms, such as n-hexyl (6 carbon atoms), n-decyl (10 carbon atoms), and n-dodecyl (12 carbon atoms). With regard to (2), the fluorine-substituted alkyl group may be a group in which only a portion of the hydrogen atoms of a chain or cyclic alkyl group are substituted with fluorine atoms, or may be a group in which all of the hydrogen atoms of a chain or cyclic alkyl group are substituted with fluorine atoms, such as a linear perfluoroalkyl group. Fluorine-substituted alkyl groups have high water repellency, so sufficient effects can be obtained by adding a small amount. However, if the content of the fluorine-substituted alkyl group is too high, it may separate from other components in the coating liquid used to form the film.

[0069] (Hydrolyzable metal compounds with water-repellent groups) To incorporate water-repellent groups into the anti-fogging layer 7, a metal compound having a water-repellent group (water-repellent group-containing metal compound), particularly a metal compound having a water-repellent group and a hydrolyzable functional group or a halogen atom (water-repellent group-containing hydrolyzable metal compound) or its hydrolysate may be added to the coating liquid for forming the film. In other words, the water-repellent group may be derived from a water-repellent group-containing hydrolyzable metal compound. A suitable water-repellent group-containing hydrolyzable metal compound is a water-repellent group-containing hydrolyzable silicon compound represented by the following formula (I): RmSiY4-m (I) Here, R is a water-repellent group, i.e., a linear or cyclic alkyl group having 1 to 30 carbon atoms in which at least a portion of the hydrogen atoms may be substituted with fluorine atoms; Y is a hydrolyzable functional group or a halogen atom; and m is an integer of 1 to 3. The hydrolyzable functional group is, for example, at least one selected from an alkoxyl group, an acetoxy group, an alkenyloxy group, and an amino group, and is preferably an alkoxy group, particularly an alkoxy group having 1 to 4 carbon atoms. An example of an alkenyloxy group is an isopropenoxy group. The halogen atom is preferably chlorine. The functional groups exemplified here can also be used as the "hydrolyzable functional group" described below. m is preferably 1 to 2.

[0070] Upon completion of hydrolysis and polycondensation, the compound represented by formula (I) provides a component represented by formula (II): RmSiO(4-m) / 2 (II) where R and m are as defined above. After hydrolysis and polycondensation, the compound represented by formula (II) actually forms a network structure in the anti-fogging layer 7 in which silicon atoms are bonded to each other via oxygen atoms.

[0071] In this way, the compound represented by formula (I) undergoes hydrolysis or partial hydrolysis, and further undergoes at least partial polycondensation to form a network structure of siloxane bonds (Si-O-Si) in which silicon atoms and oxygen atoms are alternately connected and three-dimensionally spread. The silicon atoms in this network structure are connected to water-repellent groups R. In other words, the water-repellent groups R are fixed to the network structure of siloxane bonds via R-Si bonds. This structure is advantageous for uniformly dispersing the water-repellent groups R in the film. The network structure may contain silica components provided by silicon compounds other than the water-repellent group-containing hydrolyzable silicon compound represented by formula (I) (e.g., tetraalkoxysilane, silane coupling agent). When a silicon compound having no water-repellent groups but a hydrolyzable functional group or a halogen atom (water-repellent group-free hydrolyzable silicon compound) is blended with the water-repellent group-containing hydrolyzable silicon compound in the coating liquid for forming the anti-fogging layer 7, a network structure of siloxane bonds containing silicon atoms bonded to water-repellent groups and silicon atoms not bonded to water-repellent groups can be formed. With such a structure, it becomes easy to adjust the content of the water-repellent group and the content of the metal oxide component in the anti-fogging layer independently of each other.

[0072] The water-repellent group has the effect of improving the anti-fogging performance by increasing the water vapor permeability on the surface of the anti-fogging layer 7 containing the water-absorbent resin. Because the two functions of water absorption and water repellency are mutually exclusive, water-absorbent materials and water-repellent materials have traditionally been provided in separate layers. However, the water-repellent group eliminates uneven distribution of water near the surface of the anti-fogging layer, extending the time until condensation forms, and improving the anti-fogging performance of an anti-fogging layer having a single layer structure. The effects of this are explained below.

[0073] Water vapor that penetrates the anti-fogging layer 7 containing a water-absorbent resin forms hydrogen bonds with hydroxyl groups of the water-absorbent resin and is retained in the form of bound water. As the amount increases, the water vapor progresses from bound water to semi-bound water and finally to free water retained in the voids in the anti-fogging layer. In the anti-fogging layer 7, the water-repellent groups hinder the formation of hydrogen bonds and facilitate the dissociation of formed hydrogen bonds. With the same water-absorbent resin content, the number of hydrogen-bondable hydroxyl groups in the film remains the same, but the water-repellent groups slow the rate of hydrogen bond formation. Therefore, in the anti-fogging layer 7 containing water-repellent groups, water is ultimately retained in the film in one of the above forms, but before it is retained, it can diffuse as water vapor to the bottom of the film. Furthermore, once retained, water dissociates relatively easily and moves to the bottom of the film in the form of water vapor. As a result, the distribution of water retention across the film thickness is relatively uniform from near the surface to the bottom of the film. In other words, the entire thickness of the anti-fogging layer is effectively utilized to absorb water supplied to the film surface, which makes it difficult for water droplets to condense on the surface and improves anti-fogging properties. Furthermore, since water droplets are difficult to condense on the surface, the anti-fogging layer that has absorbed moisture has the characteristic of being difficult to freeze even at low temperatures.

[0074] On the other hand, in an anti-fogging layer that does not contain water-repellent groups, water vapor that penetrates into the film is very easily retained in the form of bound water, semi-bound water, or free water. Therefore, the penetrated water vapor tends to be retained near the surface of the film. As a result, the moisture content in the film is extremely high near the surface and rapidly decreases as it progresses toward the bottom of the film. In other words, although the bottom of the film can still absorb water, the film near the surface is saturated with moisture and condenses as water droplets, resulting in limited anti-fogging properties.

[0075] When a water-repellent group-containing hydrolyzable silicon compound (see formula (I)) is used to introduce a water-repellent group into the anti-fogging layer, a strong network structure of siloxane bonds (Si-O-Si) is formed. The formation of this network structure is advantageous not only from the viewpoint of improving abrasion resistance but also from the viewpoint of improving hardness, water resistance, etc.

[0076] The water-repellent groups should be added to the extent that the water contact angle on the surface of the anti-fogging layer is 70 degrees or more, preferably 80 degrees or more, and more preferably 90 degrees or more. The water contact angle is measured by dropping a 4 mg water droplet on the surface of the film. In particular, when methyl or ethyl groups, which have relatively weak water repellency, are used as the water-repellent groups, it is preferable to incorporate water-repellent groups in the anti-fogging layer in an amount that will result in a water contact angle in the above-mentioned range. There is no particular upper limit for this water droplet contact angle, but it is, for example, 150 degrees or less, for example, 120 degrees or less, or even 100 degrees or less. It is preferable that the water-repellent groups be uniformly incorporated into the anti-fogging layer so that the water droplet contact angle is in the above-mentioned range throughout the entire surface of the anti-fogging layer.

[0077] The anti-fogging layer preferably contains water-repellent groups in an amount of 0.05 parts by mass or more, preferably 0.1 parts by mass or more, more preferably 0.3 parts by mass or more, relative to 100 parts by mass of the water-absorbent resin, and in an amount of 10 parts by mass or less, preferably 5 parts by mass or less.

[0078] (inorganic oxides) The inorganic oxide is, for example, an oxide of at least one element selected from Si, Ti, Zr, Ta, Nb, Nd, La, Ce, and Sn, and includes at least an oxide of Si (silica). The organic-inorganic composite anti-fogging layer preferably contains at least 0.01 parts by weight of inorganic oxide per 100 parts by weight of the water-absorbent resin, more preferably at least 0.1 parts by weight, even more preferably at least 0.2 parts by weight, particularly preferably at least 1 part by weight, most preferably at least 5 parts by weight, in some cases at least 10 parts by weight, and if necessary at least 20 parts by weight, and preferably at most 50 parts by weight, more preferably at most 45 parts by weight, even more preferably at most 40 parts by weight, particularly preferably at most 35 parts by weight, most preferably at most 33 parts by weight, and in some cases at most 30 parts by weight. The inorganic oxide is a necessary component for ensuring the strength, particularly abrasion resistance, of the organic-inorganic composite anti-fogging layer, but if the inorganic oxide content is high, the anti-fogging properties of the organic-inorganic composite anti-fogging layer will decrease.

[0079] (Inorganic oxide fine particles) The organic-inorganic composite anti-fogging layer may further contain inorganic oxide fine particles as at least a portion of the inorganic oxide. The inorganic oxide constituting the inorganic oxide fine particles is, for example, an oxide of at least one element selected from Si, Ti, Zr, Ta, Nb, Nd, La, Ce, and Sn, preferably silica fine particles. Silica fine particles can be introduced into the organic-inorganic composite anti-fogging layer, for example, by adding colloidal silica. Inorganic oxide fine particles are excellent at transmitting stress applied to the organic-inorganic composite anti-fogging layer to the article supporting the organic-inorganic composite anti-fogging layer and also have high hardness. Therefore, the addition of inorganic oxide fine particles is advantageous from the perspective of improving the abrasion resistance of the organic-inorganic composite anti-fogging layer. Furthermore, the addition of inorganic oxide fine particles to the organic-inorganic composite anti-fogging layer forms fine voids where the fine particles are in contact with or adjacent to each other, making it easier for water vapor to be absorbed into the film through these voids. Therefore, the addition of inorganic oxide fine particles may be advantageous in improving anti-fogging properties. The inorganic oxide fine particles can be supplied to the organic-inorganic composite anti-fogging layer by adding pre-formed inorganic oxide fine particles to a coating liquid for forming the organic-inorganic composite anti-fogging layer.

[0080] If the average particle size of inorganic oxide particles is too large, the organic-inorganic composite anti-fogging layer may become cloudy. If the average particle size is too small, the particles may aggregate and become difficult to uniformly disperse. From this perspective, the average particle size of inorganic oxide particles is preferably 1 to 20 nm, more preferably 5 to 20 nm. Here, the average particle size of inorganic oxide particles is described in terms of primary particles. The average particle size of inorganic oxide particles is determined by measuring the particle sizes of 50 randomly selected particles through observation using a scanning electron microscope and adopting the average value. If the content of inorganic oxide particles is too high, the water absorption capacity of the organic-inorganic composite anti-fogging layer as a whole may decrease, potentially causing the organic-inorganic composite anti-fogging layer to become cloudy. The inorganic oxide particles are added in an amount of preferably 0 to 50 parts by weight, more preferably 2 to 30 parts by weight, even more preferably 5 to 25 parts by weight, and particularly preferably 10 to 20 parts by weight, per 100 parts by weight of the water-absorbent resin.

[0081] (Hydrolyzable metal compounds without water-repellent groups) The anti-fogging layer may contain a metal oxide component derived from a hydrolyzable metal compound that does not have a water-repellent group (a hydrolyzable compound that does not have a water-repellent group). A preferred hydrolyzable metal compound that does not have a water-repellent group is a hydrolyzable silicon compound that does not have a water-repellent group. The hydrolyzable silicon compound that does not have a water-repellent group is, for example, at least one silicon compound (that does not have a water-repellent group) selected from silicon alkoxide, chlorosilane, acetoxysilane, alkenyloxysilane, and aminosilane, and silicon alkoxide that does not have a water-repellent group is preferred. An example of an alkenyloxysilane is isopropenoxysilane.

[0082] The hydrolyzable silicon compound having no water-repellent group may be a compound represented by the following formula (III). SiY4 (III) As described above, Y is a hydrolyzable functional group, and is preferably at least one selected from an alkoxyl group, an acetoxy group, an alkenyloxy group, an amino group, and a halogen atom.

[0083] The hydrolyzable metal compound without a water-repellent group is hydrolyzed or partially hydrolyzed, and at least a portion of the hydrolyzed metal compound undergoes polycondensation to provide a metal oxide component in which a metal atom is bonded to an oxygen atom. This component firmly bonds the metal oxide fine particles to the water-absorbent resin, and can contribute to improving the abrasion resistance, hardness, water resistance, etc. of the anti-fogging layer. The metal oxide component derived from the hydrolyzable metal compound without a water-repellent group is preferably in the range of 0 to 40 parts by mass, preferably 0.1 to 30 parts by mass, more preferably 1 to 20 parts by mass, particularly preferably 3 to 10 parts by mass, and in some cases 4 to 12 parts by mass, per 100 parts by mass of the water-absorbent resin.

[0084] A preferred example of a hydrolyzable silicon compound having no water-repellent group is a tetraalkoxysilane, more specifically a tetraalkoxysilane having an alkoxy group having 1 to 4 carbon atoms. The tetraalkoxysilane is, for example, at least one selected from tetramethoxysilane, tetraethoxysilane, tetra-n-propoxysilane, tetraisopropoxysilane, tetra-n-butoxysilane, tetraisobutoxysilane, tetra-sec-butoxysilane, and tetra-tert-butoxysilane.

[0085] If the content of the metal oxide (silica) component derived from tetraalkoxysilane is too high, the anti-fogging properties of the anti-fogging layer may be reduced. One reason for this is that the flexibility of the anti-fogging layer is reduced, limiting the swelling and shrinkage of the film due to absorption and release of moisture. The metal oxide component derived from tetraalkoxysilane is added in an amount of 0 to 30 parts by mass, preferably 1 to 20 parts by mass, and more preferably 3 to 10 parts by mass, per 100 parts by mass of the water-absorbing resin.

[0086] Another preferred example of a hydrolyzable silicon compound having no water-repellent group is a silane coupling agent. The silane coupling agent is a silicon compound having different reactive functional groups. Preferably, a portion of the reactive functional groups is a hydrolyzable functional group. The silane coupling agent is, for example, a silicon compound having an epoxy group and / or an amino group and a hydrolyzable functional group. Preferred examples of the silane coupling agent include glycidyloxyalkyltrialkoxysilane and aminoalkyltrialkoxysilane. In these silane coupling agents, the alkylene group directly bonded to the silicon atom preferably has 1 to 3 carbon atoms. Since glycidyloxyalkyl groups and aminoalkyl groups contain functional groups (epoxy groups, amino groups) that exhibit hydrophilicity, they are not water-repellent as a whole, despite containing alkylene groups.

[0087] Silane coupling agents firmly bond the water-absorbent resin, which is an organic component, with inorganic components such as metal oxide particles, and can contribute to improving the abrasion resistance, hardness, and water resistance of the anti-fogging layer. However, if the content of the metal oxide (silica) component derived from the silane coupling agent is excessive, the anti-fogging properties of the anti-fogging layer will decrease and, in some cases, the anti-fogging layer will become cloudy. The metal oxide component derived from the silane coupling agent is added in an amount of 0 to 10 parts by mass, preferably 0.05 to 5 parts by mass, and more preferably 0.1 to 2 parts by mass, per 100 parts by mass of the water-absorbent resin.

[0088] (Crosslinked structure) The anti-fogging layer may contain a crosslinked structure derived from a crosslinking agent, preferably at least one crosslinking agent selected from an organoboron compound, an organotitanium compound, and an organozirconium compound. The introduction of a crosslinked structure improves the abrasion resistance, scratch resistance, and water resistance of the anti-fogging layer. From another perspective, the introduction of a crosslinked structure facilitates improving the durability of the anti-fogging layer without reducing its anti-fogging performance.

[0089] When a crosslinked structure derived from a crosslinking agent is introduced into an anti-fogging layer whose metal oxide component is a silica component, the anti-fogging layer may contain, as a metal atom, silicon as well as a metal atom other than silicon, preferably boron, titanium, or zirconium.

[0090] The type of crosslinking agent is not particularly limited as long as it can crosslink the water-absorbent resin used. Here, only examples of organic titanium compounds are given. The organic titanium compound is, for example, at least one selected from titanium alkoxides, titanium chelate compounds, and titanium acylates. Examples of titanium alkoxides include titanium tetraisopropoxide, titanium tetra-n-butoxide, and titanium tetraoctoxide. Examples of titanium chelate compounds include titanium acetylacetonate, titanium ethyl acetoacetate, titanium octylene glycol, titanium triethanolamine, and titanium lactate. Titanium lactate may be an ammonium salt (ammonium titanium lactate). Examples of titanium acylates include titanium stearate. A preferred organic titanium compound is a titanium chelate compound, particularly titanium lactate.

[0091] When the water-absorbing resin is polyvinyl acetal, the preferred crosslinking agent is an organic titanium compound, particularly titanium lactate.

[0092] Furthermore, when a crosslinked structure is formed by a hydrolyzable metal compound such as the silicon alkoxide described above, the adhesion between the anti-fogging layer 7 and the mirror body 1 is improved, and the anti-fogging layer 7 can exhibit shatterproof properties. The amount of silicon alkoxide added to the anti-fogging layer coating solution used to form the anti-fogging layer is 1 part by mass or more, preferably 1.5 parts by mass or more, and 50 parts by mass or less, preferably 30 parts by mass or less, per 100 parts by mass of the water-absorbent resin made of polyvinyl acetal or polyepoxy resin. If the amount of hydrolyzable metal compound added is small, the adhesion between the mirror body 1 and the anti-fogging layer 7 decreases, making the anti-fogging layer 7 more likely to peel off from the mirror body 1. On the other hand, if the amount of hydrolyzable metal compound added is large, the anti-fogging layer 7 becomes hard and therefore more likely to break when the mirror body 1 is broken. Therefore, the shatterproof properties of the anti-fogging layer 7 are reduced.

[0093] (Other optional ingredients) The anti-fogging layer may contain other additives. Examples of the additives include glycols such as glycerin and ethylene glycol, which have the function of improving anti-fogging properties. The additives may also be surfactants, leveling agents, ultraviolet absorbers, colorants, antifoaming agents, preservatives, etc.

[0094] (base layer) The anti-fogging layer 7 can be laminated directly on the glass plate 2, or an underlayer can be formed on the glass plate 2, and the anti-fogging layer 7 can be laminated on top of that. By laminating the anti-fogging layer 7 on the glass plate 2 via the underlayer in this way, the anti-fogging layer 7 can be made less likely to peel off. For the underlayer, a silane coupling agent or the like can be used, for example.

[0095] [Film thickness] The thickness of the organic-inorganic composite anti-fogging layer can be adjusted appropriately depending on the required anti-fogging properties and other factors. The thickness of the organic-inorganic composite anti-fogging layer is preferably 2 to 12 μm, more preferably 2 to 15 μm, and even more preferably 3 to 10 μm. A thickness of 2 μm or greater for the anti-fogging layer 7 provides sufficient anti-fogging effects. However, if the anti-fogging layer 7 is too thick, its edges become more visible, which is undesirable. To address this issue, for example, as shown in FIG. 6 , the anti-fogging layer 7 can be extended from the edge of the first main surface 11 to cover the second chamfered portion 14. Alternatively, it can be extended to cover all or part of the peripheral surface 13. In this way, even if the anti-fogging layer 7 is thick, its edges can be made invisible. Furthermore, if the anti-fogging layer 7 is too thick, unevenness in the layer thickness may distort the reflected image. Furthermore, since the anti-fogging layer 7 is formed from a resin material as described above and has birefringence, an excessively thick layer may blur the image.

[0096] It is also possible to provide both the peripheral protective layer and the anti-fogging layer described above. The order in which the anti-fogging layer 7 is formed is not particularly limited. However, for example, when the peripheral protective layer 5 shown in FIG. 4 is formed, it is preferable to form the anti-fogging layer 7 thereafter. This is because forming the anti-fogging layer 7 first may prevent the acidic solution contained in the anti-fogging layer solution from coming into contact with the interfaces of the components exposed at the peripheral surface 13 of the mirror body 1. To prevent this, it is preferable to form the peripheral protective layer 7 first. In this case, the anti-fogging layer 7 may be laminated on a portion of the peripheral protective layer 5. The peripheral surface 13 of the mirror body 1 may be completely covered by either the peripheral protective layer 5 or the anti-fogging layer 7, or may be partially exposed. For example, at least a portion of the edge of the glass plate 2 may be exposed.

[0097] However, if the anti-fogging layer 7 is extended to the peripheral surface 13 as described above, the thickness of the anti-fogging layer 7 formed on the peripheral surface 13 will be greater than the thickness of the anti-fogging layer 7 formed on the first main surface 11 due to surface tension. Considering productivity and cost, it is conceivable to form a large mirror body, laminate the anti-fogging layer on top of it, and then cut out mirrors of sizes that meet the requirements of various products. However, because the required specifications, such as anti-fogging performance, vary depending on the type of product, it is preferable to cut the mirror body to the required product size and then laminate the anti-fogging layer 7. This reduces unnecessary inventory and allows for the production of a wide variety of products.

[0098] [hardness] The hardness of the anti-fogging layer 7 is preferably, for example, H to 2H in terms of pencil hardness as defined by JIS K5600-5-4. This is because if the anti-fogging layer is too hard, sufficient anti-fogging performance cannot be obtained, whereas if it is too soft, durability is poor.

[0099] [Anti-fogging layer formation area] The anti-fogging layer 7 can be laminated over the entire glass plate 2 as described above. However, for example, when a frame is provided to support the mirror body 1, the anti-fogging layer 7 can be avoided from being formed in the area where the frame is attached. This is because the anti-fogging layer is easily damaged by the attachment of the frame. The area where the frame is provided can be, for example, an area approximately 5 mm inward from the periphery of the glass plate. Such an area can be formed, for example, by masking the periphery of the glass plate 2 when forming the anti-fogging layer 7.

[0100] The above-described anti-fogging layer is merely an example, and other known anti-fogging layers can be used, including various types such as the anti-fogging layer described in JP-A-2001-146585. By forming such an anti-fogging layer, the time until condensation occurs in the anti-fogging performance test described below can be set to 30 seconds or more, preferably 60 seconds or more, and more preferably 100 seconds or more.

[0101] The anti-fogging performance test can be performed as follows in an environment with a room temperature of 20 to 23°C and a humidity of 20 to 23% RH. First, as shown in Figure 7, a cylinder with an inner diameter of 80 mm and an axial length of 60 mm was prepared and placed above a water tank filled with water at 35°C. The distance between the top end of the cylinder and the water surface in the water tank was 100 mm. Next, the mirror on which the anti-fogging layer 7 was formed was stored at 20°C and 30% RH for 30 minutes or more, and then the cylinder was placed so that the top opening was closed. The anti-fogging layer 7 was oriented downward, facing the water. The time until the anti-fogging layer 7 became foggy was then measured.

[0102] <4. Protective film> The anti-fogging layer 7 can also be covered with a protective film. The protective film can be composed of a sheet-like substrate and an adhesive layer laminated on one side of the substrate. The adhesive layer can be attached to the anti-fogging layer to protect the anti-fogging layer 7. The protective film is removed when the mirror is used. The material from which the substrate is made is not particularly limited, but can be made of resin materials such as polyethylene terephthalate, polyvinyl chloride, polyvinylidene chloride, polycarbonate, and acrylic resins.

[0103] The adhesive layer may be any adhesive layer capable of fixing the substrate to the anti-fogging layer 7 with an appropriate strength. Specifically, adhesive layers may be used that have tackiness at room temperature, such as acrylic, rubber, or resins copolymerized with methacrylic and acrylic monomers and set to a desired glass transition temperature. Examples of acrylic monomers that can be used include methyl acrylate, ethyl acrylate, butyl acrylate, stearyl acrylate, and 2-ethylhexyl acrylate. Examples of methacrylic monomers that can be used include ethyl methacrylate, butyl methacrylate, isobutyl methacrylate, and stearyl methacrylate. Furthermore, when applying the adhesive by heat lamination or the like, organic substances that soften at the lamination temperature may be used. For example, in the case of a resin copolymerized with methacrylic and acrylic monomers, the glass transition temperature can be adjusted by changing the compounding ratio of the monomers.

[0104] The thickness of the protective film is not particularly limited, but can be, for example, 30 to 90 μm. If the protective film is too thin, it may not sufficiently protect the anti-fog layer 7 and may damage the anti-fog layer 7. On the other hand, if the protective film is too thick, it may be difficult to attach it to the anti-fog layer.

[0105] The flexural strength of the protective film is not particularly limited, but may be, for example, 96 to 131 MPa. If the flexural strength of the protective film is low, the protective film may adhere to the edge of the anti-fog layer 7, making it difficult to peel off. On the other hand, if the flexural strength of the protective film is high, it may be difficult to attach the protective film to the anti-fog layer 7.

[0106] The protective film can cover the anti-fog layer 7 in various ways. For example, it can be formed to have the same area as the anti-fog layer 7 and cover the entire anti-fog layer 7, or it can be formed so that the protective film 9 protrudes outward from the peripheral surface 13, as shown in FIG. 8. In this way, the protruding portion can be grasped and the protective film 9 can be easily peeled off. In this case, the protruding portion may be bent so that it fits along the peripheral surface. Furthermore, to reduce the protruding portion, only the portion corresponding to the second chamfered portion 14 can protrude.

[0107] The anti-fogging layer 7 may be covered with one protective film, or may be covered with a plurality of protective films. That is, the protective film may be divided.

[0108] <5. Shatterproof layer> To prevent fragments from scattering when the mirror breaks, a shatterproof layer can be laminated on the protective layer 4. The shatterproof layer can be made of a resin material such as polyester, polyethylene terephthalate, or polycarbonate, and can be fixed to the protective layer 4 with an adhesive.

[0109] <6. Features> The mirror described above can provide the following effects. (1) The first chamfered portion 132 formed on the mirror body 1 has the advantage that the mirror body 1 is less likely to chip when dropped. The second chamfered portion 14 also has the same effect. (2) By forming the anti-fogging layer 7, the glass plate 2 of the mirror body 1 can be prevented from fogging up. (3) By forming the anti-fogging layer 7 on the first main surface 11 of the mirror body 1, the anti-fogging layer 7 can absorb impacts from the first main surface 11 side. As a result, even if the glass plate 2 itself is broken, scattering of glass fragments can be suppressed. (4) As described above, the anti-fogging layer 7 can be formed from various materials. For example, if the anti-fogging layer 7 is formed from a material containing a water-absorbent resin as its main component, the anti-fogging layer 7 will have the ability to absorb water and expand and contract, thereby absorbing impact. As a result, the impact can be alleviated and breakage of the glass plate 2 can be suppressed. Furthermore, because the absorbent resin can expand and contract and is firmly bonded to the glass plate 2, even if the glass plate 2 is broken, scattering of glass fragments can be suppressed.

[0110] <7. Variations> Although the embodiments of the present invention have been described above, the present invention is not limited to the above embodiments, and various modifications are possible without departing from the spirit of the present invention. The following modifications can be combined as appropriate.

[0111] In the above embodiment, an example in which a metal layer and a protective layer are laminated in this order on a glass plate has been described. However, a semi-transparent reflective film can also be laminated instead. A semi-transparent reflective film functions as a half mirror. For example, a semi-transparent reflective film has a first layer laminated on the glass plate and a second layer laminated on the first layer. However, additional layers such as a third layer and a fourth layer can be provided as needed. When a metal reflective layer made of a metal or semi-metal is used as a layer constituting the semi-transparent reflective film, one or more units each consisting of a two-layer structure in which a low-refractive index layer or a high-refractive index layer is laminated directly on the metal reflective layer can be laminated, or one or more units each consisting of a low-refractive index layer and a high-refractive index layer laminated in this order on the metal reflective layer can be laminated. When a metal reflective layer is not used, one or more units each consisting of a low-refractive index layer and a high-refractive index layer laminated in this order can be laminated on a high-refractive index layer. The refractive index of the high-refractive index layer is preferably 1.6 or higher, and more preferably 1.8 or higher. The refractive index of the low refractive index layer is lower than this, and is preferably 1.6 or less, and more preferably 1.5 or less. The high refractive index layer and the low refractive index layer can also be formed by laminating one or more materials as long as the refractive index conditions are met.

[0112] Next, the materials of each layer of the semi-transmissive reflective film will be described. Each layer constituting the semi-transmissive reflective film can be formed of a layer made of a metal or semi-metal and a layer made of an inorganic metal oxide (inorganic oxide layer). For example, silicon (Si), germanium (Ge), SUS or another suitable metal or semi-metal, silicon dioxide (SiO2), tin oxide (SnO2), titanium dioxide (TiO2), or another suitable inorganic metal oxide can be appropriately selected so as to satisfy the above-mentioned refractive index range. For example, the refractive indices of silicon, silicon dioxide, tin oxide, titanium dioxide, SUS, Ag, Al, Cr, Mo, and Ti are approximately 4.4, approximately 1.4, approximately 1.8, approximately 2.2, approximately 2.4, approximately 0.14, approximately 1.4, approximately 2.4, approximately 3.6, and approximately 2.7, respectively. The layer configuration of the semi-transmissive reflective film is not particularly limited, but can be, for example, as follows. In addition, each layer can be appropriately doped with an additive to adjust the electrical resistance. Instead of Si in the first layer in Examples 2 and 3, Ag, Al, Cr, Ti, or Mo can also be used. [Table 1]

[0113] In Examples 1 and 3, a base layer of SiO2 can be provided between the first layer and the glass plate 2. Furthermore, the use of SUS can improve the visible light absorptance. When the visible light absorptance is improved, the total value of the visible light reflectance and the visible light transmittance decreases, making it easier to adjust the visible light reflectance and the visible light transmittance.

[0114] When a semi-transmitting reflective film is formed using an inorganic metal oxide containing the above-mentioned metal or semi-metal, the color tone does not change significantly when the semi-transmitting reflective film is viewed from a wide angle, making the mirror of the present invention suitable as an optical cover glass. However, because the metal reflective layer is easily scratched, it is preferable not to place it on the outermost surface of the mirror. Furthermore, providing an inorganic metal oxide layer can improve alkali resistance.

[0115] The thickness (physical thickness) of the semi-transmitting reflective film is preferably 3 to 300 nm, more preferably 5 to 250 nm. If the thickness of the semi-transmitting reflective film is less than 10 nm, it becomes difficult to control the film thickness, resulting in poor productivity. On the other hand, if the thickness exceeds 300 nm, costs may increase, the surface irregularities may become noticeable, and the haze ratio may increase, resulting in an unattractive appearance. The thicknesses of the layers constituting the semi-transmitting reflective film may be appropriately adjusted so that the film thickness of the semi-transmitting reflective film falls within the above-mentioned range, and are not particularly limited. For example, in Example 2, a semi-transmitting reflective film can be formed in which the first layer is 18 nm, the second layer is 85 nm, and the third layer is 65 nm. In Example 4, the thickness of the silicon layer can be approximately 18 nm, and the thickness of the silicon dioxide layer can be approximately 30 nm. Additionally, the thickness of the titanium dioxide layer in Examples 1 and 3 can be approximately 6 nm, and the thickness of the SUS layer in Example 5 can be approximately 8 nm.

[0116] Furthermore, in Example 2, in order to increase the reflection at the first layer, a low refractive index material can be laminated as the second layer and a high refractive index material can be laminated as the third layer. For example, as described above, if the first layer is 18 nm, the second layer is 85 nm, and the third layer is 65 nm, and the optical film thickness of the semi-transmissive reflective film is set to 135 nm ± 20 nm, the optical film thickness will be λ / 4 for the wavelength λ of incident light (center wavelength: 550 nm), thereby strengthening the reflection at the interface between the first and second layers. Materials other than those shown in Example 2 may be used as long as the film thickness and refractive index of each layer can be adjusted in this manner.

[0117] The visible light transmittance of the mirror provided with the semi-transparent reflective film is preferably 20% to 70% inclusive, more preferably 35% to 60% inclusive, and particularly preferably 35% to 50% inclusive. On the other hand, since the visible light reflectance of the mirror is in a trade-off relationship with the visible light transmittance, it is preferably 30% to 80% inclusive, more preferably 40% to 65% inclusive, and particularly preferably 50% to 65% inclusive.

[0118] The visible light transmittance and visible light reflectance of such a mirror can be adjusted by changing the material and film thickness of the semi-transmissive reflective film, and the material and thickness of the glass plate 2.

[0119] Next, a method for forming a semi-transmissive reflective film will be described. The method for forming a semi-transmissive reflective film is not particularly limited, but may be, for example, a so-called physical vapor deposition method such as sputtering or vacuum deposition, a spray method, or a chemical vapor deposition method (CVD method). In particular, when a CVD method is used, it is preferable to use an online CVD method. The online CVD method is a type of chemical vapor deposition method in which a material for a semi-transmissive reflective film is supplied from a coater onto the top surface of a glass ribbon that is above a molten tin bath and has a temperature of 615°C or higher during the float glass manufacturing process, and a semi-transmissive reflective film is formed by a thermal decomposition oxidation reaction.

[0120] To form each layer of the semi-transmissive reflective film, one material can be supplied from one coater, but if the layer is thick, one layer can be formed using two or more coaters. For example, in Example 4 above, if the silicon film thickness is 18 nm and the silicon dioxide film thickness is 30 nm, the semi-transmissive reflective film can be formed by preparing first to third coaters and supplying silicon from the first coater and silicon dioxide from the second and third coaters.

[0121] The SUS film is formed by sputtering, not CVD, and is preferably formed by sputtering to form a thin film of a material. [Example]

[0122] Examples of the present invention will be described below. However, the present invention is not limited to the following examples. In the following, the performance of the anti-fogging film will be evaluated.

[0123] (1) Preparation of the mirror for the example A mirror was prepared as a test sample as follows.

[0124] (i) Mirror body A mirror body was prepared in which the above-described semi-transmissive reflective film was laminated on the second main surface of a glass plate (soda lime silicate glass, thickness 3.1 mm, size 100×100 mm).

[0125] (ii) Anti-fog layer A solution containing 62.5 mass% of polyvinyl acetal resin (Sekisui Chemical Co., Ltd. "S-LEC KX-5," solid content 8 mass%, degree of acetalization 9 mol%, containing acetal structures derived from benzaldehyde), 1.04 mass% of tetraethoxysilane (TEOS, Shin-Etsu Chemical Co., Ltd. "KBE-04"), and 1.04 mass% of titanium lactate (Matsumoto Fine Chemical Co., Ltd. "Orgatix TC-310"; Ti(OH)2[OCH(CH3)COO A coating solution for forming an anti-fog layer was prepared by placing 1.21 mass% of a solution containing 44 mass% of [H]2 and made of a mixed solvent of 2-propanol and water, 17.79 mass% of an alcohol solvent ("Solmix AP-7" manufactured by Nippon Alcohol Industry Co., Ltd.), 17.44 mass% of purified water, 0.01 mass% of nitric acid as an acid catalyst, and 0.01 mass% of a leveling agent ("KP-341" manufactured by Shin-Etsu Chemical Co., Ltd.) in a glass container and stirring at room temperature (25°C) for 3 hours.

[0126] Next, the coating liquid was applied to the first main surface of the mirror body by flow coating at room temperature of 20°C and relative humidity of 30%. After drying for 10 minutes in the same environment, a (preliminary) heat treatment at 120°C was performed. Thereafter, a high-temperature, high-humidity treatment was performed using the above-mentioned atmosphere and time, and an additional heat treatment was performed using the same atmosphere and time to produce a mirror according to the example. The anti-fogging layer had a thickness of 3.9 μm.

[0127] The mirrors manufactured as described above were evaluated as follows. First, peeling of the anti-fogging layer was evaluated using the cross-cut method specified in JIS K5600-5-1. As a result, a rating of Class 0 was obtained (the edges of the cuts were completely smooth and there was no peeling at any of the grid holes). Therefore, it was found that the anti-fogging layer according to the example exhibited high adhesion to the mirror body. However, even a rating of Class 1 is considered acceptable for practical use.

[0128] Next, the shatterproof function was evaluated. First, a linear cut was made on the second main surface of the mirror body 1 using a glass cutter. Note that a wheel cutter or diamond cutter can also be used instead of the glass cutter. Next, a round rod with a diameter twice the thickness of the glass plate was placed on a horizontal surface. Next, a mirror was placed on the round rod with the anti-fogging layer facing downward. At this time, the round rod was brought into contact with the anti-fogging layer so that it corresponded to the cut (extending along the cut). Then, both sides of the cut on the second main surface of the mirror body were simultaneously pressed toward the horizontal surface to split the mirror body. When it was confirmed whether the anti-fogging layer had been cut, it was found not to have been cut. Therefore, it was found that the anti-fogging layer does not break even if the mirror body is broken, and therefore can prevent fragments of the broken mirror body from scattering. [Explanation of symbols]

[0129] 1 Mirror body 11 First main surface 12 Second main surface 13 Peripheral surface 132 First chamfer 14 Second chamfer 2 glass plates 3 metal layer 5 Protective layer 7 Anti-fog layer

Claims

1. a mirror body formed in a polygonal shape in a plan view, the mirror body having a first main surface on which an image is reflected, a second main surface opposite to the first main surface, and a peripheral surface connecting the first main surface and the second main surface; an anti-fogging layer; Equipped with the peripheral surface includes a plurality of first end faces and second end faces connecting adjacent first end faces, the second end surface constitutes a first chamfered portion formed on an outer edge of the mirror body in a plan view, a second chamfered portion is formed between the first main surface and the peripheral surface; A mirror, wherein the anti-fogging layer is formed by a coating film that covers at least a portion of the first main surface and the second chamfered portion.

2. The mirror according to claim 1 , wherein the anti-fogging layer and the first main surface are chemically bonded to each other.

3. The mirror according to claim 1 or 2, further comprising an underlayer disposed between the anti-fogging layer and the first main surface.

4. The mirror according to claim 1 , wherein the anti-fogging layer is disposed so as to cover the peripheral surface.

5. 5. The mirror according to claim 4, wherein the anti-fogging layer has a pencil hardness of H to 2H.

6. 6. The mirror according to claim 1, wherein the antifogging layer has a thickness of 2 to 12 μm.

7. 7. The mirror according to claim 1, wherein the anti-fogging layer is not disposed in a peripheral region of a predetermined width extending from the periphery of the first main surface toward the center.

8. The mirror according to claim 1 , wherein the entire first main surface is covered with the anti-fogging layer.

9. the anti-fogging layer is disposed so as to cover the peripheral surface, The mirror according to claim 1 , wherein the thickness of the anti-fogging layer disposed on the peripheral surface is greater than the thickness of the anti-fogging layer disposed on the first main surface.

10. 10. The mirror according to claim 1, wherein the anti-fogging layer has anti-fogging properties due to hydrophilicity.

11. The mirror according to claim 10, wherein the anti-fogging layer further has anti-fogging properties due to water absorption.

12. 11. The mirror according to claim 10, wherein the anti-fogging layer is made of a material containing a water-absorbing resin as a main component.

13. 13. The mirror according to claim 12, wherein the water-absorbing resin contains at least one of an epoxy resin and a polyvinyl acetal resin.

14. 14. The mirror according to claim 1, wherein the anti-fogging layer has a shatterproof function.

15. The mirror according to claim 14, wherein the anti-fogging layer has a cross-linked structure formed by a hydrolyzable metal compound.

16. 16. The mirror of claim 15, wherein the hydrolyzable metal compound comprises a silicon alkoxide.

17. 17. The mirror according to claim 14, wherein the adhesion of the anti-fogging layer to the mirror body is classified as 0 or 1 in a cross-cut test specified in JIS K5600-5-6.

18. A mirror as described in any one of claims 14 to 17, wherein a linear cut is formed on the second main surface of the mirror body with a cutter, a round rod placed on a horizontal plane is brought into contact with the anti-fogging layer facing downward to correspond to the cut, and pressure is applied to both sides of the cut, so that when the mirror body is split, the anti-fogging layer is not cut.

19. 19. The mirror of claim 1, further comprising a protective film covering the anti-fog layer.

20. The protective film has a sheet-like substrate and an adhesive layer disposed on one surface of the substrate, the adhesive layer adheres the substrate to the anti-fogging layer; The mirror according to claim 19, wherein the peripheral edge of the base has an area where the adhesive layer is not disposed.

21. the anti-fogging layer is disposed so as to cover the peripheral surface, 21. The mirror of claim 20, wherein the protective film is not adhered to at least a portion of the anti-fog layer covering the peripheral surface.

22. 22. The mirror according to claim 19, wherein the protective film is formed so as to protrude from the mirror body at a location where the first chamfered portion is formed.

23. 23. The mirror according to claim 19, wherein the protective film has a bending strength of 96 to 131 MPa.

24. The mirror according to any one of claims 19 to 23, wherein the thickness of the protective film is 30 to 90 µm.

25. 25. The mirror according to claim 19, wherein the protective film is configured to cover the anti-fogging layer in a state where the protective film is divided into a plurality of pieces.

26. The mirror body is A glass plate and a metal layer or a semi-metal layer laminated on one surface of the glass plate; a resin protective layer laminated on the metal layer or semi-metal layer; 26. The mirror according to claim 1, further comprising an inorganic oxide layer made of an inorganic oxide laminated between the metal layer or semi-metal layer and the protective layer.

27. 27. The mirror of claim 26, wherein the semi-metallic layer is based on Si or Ge.

28. The mirror body is A glass plate and a metal layer laminated on one surface of the glass plate; 26. The mirror according to claim 1, further comprising a protective layer made of resin laminated on the metal layer.

29. the other surface of the glass plate constitutes the first main surface, 30. The mirror of claim 28, wherein an anti-fog layer is disposed over the first major surface.

30. On the peripheral surface, 30. The mirror of claim 28 or 29, further comprising a peripheral protective layer disposed over a first interface between the glass plate and the metal layer and a second interface between the metal layer and the protective layer.

31. the other surface of the glass plate constitutes the first main surface, an anti-fogging layer is disposed so as to cover the first main surface; On the peripheral surface, a peripheral protective layer disposed to cover a first interface between the glass plate and the metal layer and a second interface between the metal layer and the protective layer; 29. The mirror of claim 28, wherein a portion of the anti-fog layer covers the peripheral protective layer.

32. 32. The mirror according to claim 30, wherein the peripheral protective layer is formed from an ultraviolet curable resin.

33. 33. The mirror according to claim 30, wherein an area not covered with the peripheral protective layer is provided on an end face of the glass plate that is exposed to the outside on the peripheral surface.

34. Further provided with a shatterproof film that prevents fragments from scattering when the mirror body is broken; 34. A mirror according to any one of claims 28 to 33, wherein the shatterproof film is disposed over the protective layer.

35. 35. The mirror of any one of claims 28 to 34, wherein the protective layer carries multiple types of information.

36. 36. The mirror according to claim 1, wherein the anti-fogging layer takes 30 seconds or more to form condensation.