Viral mimetic nanoparticles

Abstract

The present invention relates to nanoparticles comprising a nanomaterial and at least a first ligand and a second ligand tethered to the nanoparticle. The present invention further relates to nanoparticles for use as pharmaceuticals or diagnostic agents. The present invention also relates to nanoparticles for use in methods for preventing or treating diseases selected from diabetic nephropathy, glomerulonephritis, glomerular VEGF A dysregulation, endothelial VEGF A dysregulation, diabetic retinopathy, rheumatoid arthritis, age-related macular degeneration, and cancers such as breast cancer. Furthermore, the present invention relates to methods for preparing nanoparticles.

Description

[Technical Field]

[0001] Field of Invention The present invention relates to nanomaterials and nanoparticles comprising at least a first ligand and a second ligand. The present invention further relates to nanoparticles for use as pharmaceutical or diagnostic agents. The present invention also relates to nanoparticles for use in methods of preventing or treating diseases selected from diabetic nephropathy, glomerulonephritis, glomerular VEGF A dysregulation, endothelial VEGF A dysregulation, diabetic retinopathy, rheumatoid arthritis, age-related macular degeneration, and cancer such as breast cancer. Furthermore, the present invention relates to methods for preparing nanoparticles. [Background technology]

[0002] Background of the Invention Numerous nanomaterials have been developed over the past few years as carriers for drug therapy or diagnostic methods. Ligands that bind to cell receptors have been anchored to their surface to give them the ability to identify target cells with sufficient specificity in vivo. However, simply following this old framework has proven insufficient for unquestionable cell identification, although it increases the avidity of nanomaterials. Currently, even nanomaterials presenting several different ligands for hetero-polyvalent binding are unable to distinguish between different cell types.

[0003] In contrast, viruses are nanoparticles (NPs) with ultimate target cell specificity. Unlike synthetic biomedical nanomaterials, viruses employ a sequential, multi-step recognition process for cell identification. Since many current nanoparticle-based approaches lack sufficient specificity, leveraging viral targeting strategies may be a viable option to overcome this limitation. Therefore, it may be possible to specifically target cells by mimicking the sequential recognition strategies of viruses such as influenza A virus using nanomaterials. In particular, viral target cell recognition is likely to be advantageous in vivo if the particles undergo surface modification resulting from protein adsorption.

[0004] In particular, the initial step of viral adhesion to the cell membrane, which increases the density of viral particles on the cell surface without causing particle uptake, is lacking in current nanoparticle design strategies. This initial adhesion to glycolipids and glycoproteins or specific receptors has been found to be essential for viral infectivity. Furthermore, if particles are subjected to clearance after reaching the target tissue, those particles become unsuitable for drug delivery purposes. In the case of mesangia, early reports have shown that small particles with a diameter of 70±25 nm or less penetrated glomerular endothelial windowings with a diameter of approximately 80–100 nm. However, these particles have undergone mesangial clearance. This problem with known nanoparticles, which are often rapidly cleared from tissue, can be overcome if the nanoparticles are internalized by target cells in the target tissue.

[0005] Maslanka Figueroa et al.[1] relate to polymer nanoparticles containing angiotensin-I as a ligand.

[0006] Sah et al.[2] relate to block copolymers and drug-containing nanoparticles. The present invention aims to provide nanomaterials with a virus-mimicking cell identification mechanism for addressing cells in vitro and in vivo. Furthermore, an object of the present invention is to provide nanoparticles that enable effective accumulation of the nanoparticles in target tissue in vivo. A further object of the present invention is to provide a drug delivery system that enables the delivery of drugs or diagnostic agents to target tissue. [Prior art documents] [Non-patent literature]

[0007] [Non-Patent Document 1] Maslanka Figueroa et al., Proc. Natl. Acad. Sci. (2019)201902563 [Non-Patent Document 2] Sah E. et al., Journal of Nanomaterials, Volume 2015, Article ID 794601 [Overview of the project] [Means for solving the problem]

[0008] Summary of the Invention The elements of the present invention are described below. These elements are enumerated in the specific embodiments, but it should be understood that these elements may be combined in any manner and in any number to create further embodiments. The various examples and preferred embodiments described should not be construed as limiting the invention to only the embodiments explicitly described. This description should be understood as supporting and encompassing embodiments that combine two or more of the explicitly described embodiments, or combine one or more of the explicitly described embodiments with any number of disclosed and / or preferred elements. Furthermore, any permutation and combination of all elements described in this application should be considered disclosed by the description of this application unless the context indicates otherwise.

[0009] In a first aspect, the present invention relates to nanomaterials and nanoparticles comprising at least a first ligand and a second ligand, - The first ligand can mediate the attachment of the nanoparticles to target cells, - The second ligand can mediate the internalization of the nanoparticles into the target cells, Preferably, the nanomaterial includes polyethylene glycol (PEG), polylactic acid (PLA), poly(lactic acid-coglycolic acid) (PLGA), oxazoline-derived polymers, poly(amino acids), polysaccharides, phospholipids, sphingolipids, cholesterol, PEG-lipids, block copolymers, such as PEG-PLA or PEG-poly-caprolactone, inorganic substances, such as gold or qdot materials, and any combination thereof. Regarding nanoparticles.

[0010] In one embodiment, the first ligand is a non-agonist agent that binds to GPCRs, such as angiotensin II receptor type 1 (AT1r), human neuropeptide Y1 receptor, and CXC chemokine receptor type 4, and / or an agent that binds to glycoproteins and / or glycolipids on the surface of target cells, such as heparan sulfate, sialycoprotein, ganglioside, and mannose receptors, preferably EXP3174 or telmisartan.

[0011] In one embodiment, the second ligand is any of the following: i) preferably an integrin, such as αVβ3 integrin or αVβ5 integrin, selected from RGD, a cyclic RGD-peptide having the sequence of SEQ ID NO: 1, and derivatives thereof; ii) an agonist agent that binds to a GPCR, such as AT1r, preferably activated angiotensin-II; iii) an ectoenzyme, such as legumain, membrane matrix metalloproteinase, and angiotensin-converting enzyme (ACE), preferably angiotensin-I; and / or iv) an agent that binds to a transferrin receptor.

[0012] In one embodiment, the nanoparticles further comprise a therapeutic agent, preferably either pirfenidone or synaciguat.

[0013] In one embodiment, the first ligand and the second ligand are each coupled to the nanomaterial, preferably each to a block copolymer chain of the nanomaterial.

[0014] In one embodiment, the nanomaterial comprises more than one block copolymer chain, the first ligand is coupled to a first block copolymer chain of the nanomaterial, the second ligand is coupled to a second block copolymer chain of the nanomaterial, and the first block copolymer chain is longer than the second block copolymer chain, preferably at least 1.5 times the length of the second block copolymer chain, and more preferably at least 3 times the length of the second block copolymer chain.

[0015] In one embodiment, the first block copolymer chain comprises PEG in the range of 1k to 20k, preferably 1k to 10k, and / or PLA in the range of 5k to 40k, preferably 10k to 20k, and optionally the first block copolymer chain comprises PEG 5k -PLA 10k The second block copolymer chain is PEG 2k -PLA 10k That is the case.

[0016] In one embodiment, the second ligand is enzymatically activated before the internalization of the nanoparticles into the target cells.

[0017] In one embodiment, the target cells are selected from mesangial cells, endothelial cells such as retinal endothelial cells, B cells, T cells, macrophages, dendritic cells, and tumor cells.

[0018] In one embodiment, the particles have a size of 5 nm to 1000 nm, preferably 10 nm to 150 nm, and more preferably 20 nm to 100 nm.

[0019] In one embodiment, the ratio of the first ligand to the second ligand is in the range of 2:1 to 1:2, preferably 1:1.

[0020] In one embodiment, the particles have particle avidity to a targeted receptor of 1 pM to 100 nM, preferably 50 pM to 1 nM.

[0021] In one embodiment, the nanomaterial comprises PEG, and the particles have a ligand density of at least 5%, preferably at least 15%, and more preferably at least 25% ligand / PEG.

[0022] In a further embodiment, the present invention relates to nanoparticles as defined in any of the above embodiments for use as pharmaceutical or diagnostic agents.

[0023] In a further embodiment, the present invention relates to nanoparticles as defined in any of the above embodiments for use in methods for preventing or treating diseases selected from diabetic nephropathy, glomerulonephritis, glomerular VEGF A dysregulation, endothelial VEGF A dysregulation, diabetic retinopathy, rheumatoid arthritis, age-related macular degeneration, and cancers such as breast cancer.

[0024] In a further embodiment, the present invention relates to a method for preparing nanoparticles, a) Preferably, one or more nanomaterials comprising polyethylene glycol (PEG), polylactic acid (PLA), poly(lactic acid-coglycolic acid) (PLGA), oxazoline-derived polymers, poly(amino acids), polysaccharides, phospholipids, sphingolipids, cholesterol, PEG-lipids, block copolymers, e.g., PEG-PLA or PEG-poly-caprolactone, inorganic substances, e.g., gold or qdot materials, and combinations thereof, as well as a therapeutic agent, in any order; b) A step of preparing a block copolymer from one or more of the nanomaterials as needed; c) Preferably, one or more steps involve coupling a first ligand and a second ligand to each other by DCC / NHS coupling or EDC / NHS coupling; d) A step of providing a therapeutic agent, preferably a lipophilic therapeutic agent, if one has not already been provided in step a); e) Preparing and obtaining nanoparticles using a ligand coupled to the nanomaterial and the therapeutic agent, preferably by nanoprecipitation. This includes methods.

[0025] In one embodiment, the obtaining step in step e) includes obtaining nanoparticles having a polydispersity index of 0.01 to 0.5, preferably 0.01 to 0.3, and more preferably 0.01 to 0.1.

[0026] In this embodiment, the nanoparticles, the nanomaterial, the therapeutic agent, the block copolymer, the first ligand, and the second ligand are as defined above.

[0027] In a further embodiment, the present invention relates to a pharmaceutical composition comprising the nanoparticles defined above and a pharmaceutically acceptable excipient.

[0028] In a further embodiment, the present invention relates to a method for preventing or treating a disease, comprising the step of administering an effective amount of nanoparticles and / or a pharmaceutical composition to a patient in need thereof.

[0029] In this embodiment, the disease, the nanoparticles, and the pharmaceutical composition are as defined above.

[0030] In a further embodiment, the present invention relates to the use of nanoparticles in the manufacture of pharmaceuticals for the treatment of diseases.

[0031] In this embodiment, the nanoparticles and the disease are as defined above.

[0032] In a further embodiment, the present invention relates to the use of nanoparticles in the manufacture of diagnostic agents for the diagnosis and / or prognosis of diseases.

[0033] In this embodiment, the nanoparticles and the disease are as defined above.

[0034] Detailed explanation Poor availability in target tissues due to harmful physicochemical properties is a common cause of drug failure. Viruses overcome this limitation by embedding their nucleic acids in nanoscale particles and directing them to their target cells with high specificity. While nanotechnology provides a large number of nanocarriers for drug delivery, their ability to identify target cells without doubt has remained mediocre. We hereby demonstrate that particles with virus-like ability to identify cells through three consecutive checks for cellular identity have a superior ability to identify mesangial cells in vivo compared to conventional nanoparticles. In mice, this resulted in 15-fold higher accumulation in the renal mesangium and subsequent massive cellular uptake. The present invention provides a remarkably effective tool for delivering drugs into target tissues, and this tool is suitable for use in the treatment of various diseases, such as diabetic nephropathy, for which no drug therapy currently exists.

[0035] The inventors designed particles containing, for example, EXP3174, an angiotensin-II type 1 receptor (AT1R) ligand, in the NP corona to mediate receptor adhesion (Figure 1A). As a G protein-coupled receptor (GPCR) antagonist, this has the crucial advantage that binding does not induce cellular NP uptake but only membrane binding, thus preventing particle uptake by off-target cells possessing only AT1R.

[0036] As a second recognition criterion, the inventors have given particles the ability to search the cell surface for the presence of angiotensin-converting enzyme (ACE), which recognizes angiotensin-I (Ang-I), a proligand in the particle corona, and converts it to the active ligand angiotensin-II (Ang-II).

[0037] In the third recognition step, ligands such as Ang-II bind to targets such as AT1R and, as agonists, induce cellular uptake of the particles upon receptor binding. The entire process of target cell recognition can be best illustrated using a flowchart (Figure 1B). The particles were tested in vitro for their target receptor avidity and target cell specificity. Furthermore, we evaluated how the simultaneous presentation of two ligands directed toward the same receptor—an antagonist that promotes cell membrane binding and an agonist that supports intracellular uptake—affects the ability of the NPs to mediate cellular uptake. Finally, we demonstrated that particles with such a virus-mimicking triple recognition strategy were superior to conventional NPs in terms of reaching mesangial cells in vivo.

[0038] Since NPs are typically distributed throughout organisms by passive transport mechanisms, their appearance in specific tissues is a matter of their physicochemical properties. However, the proportion of particles accumulating in a target tissue can be increased if they can actively interact with target cells. To identify the identity of cells, it is not sufficient to provide NPs with ligands that bind to their respective receptors. The particles of the present invention clearly demonstrate that a strategy for stepwise cell identification, particularly one comprising a first ligand for mediating adhesion to target cells and a second ligand for mediating the internalization of nanoparticles into target cells, is more advantageous.

[0039] Using a virus as a template, the inventors designed a NP capable of performing a sequence of successive "if-then-else" decisions. In each single step, the NP searches a cell for the presence of a receptor or ectoenzyme, with the help of a ligand or substrate. If successful, the next identification step follows; otherwise (else), the particle "determines" that the cell cannot be a target cell. Similar to viruses, this helps avoid NP uptake by "wrong" cell types.

[0040] As an example, a receptor belonging to the GPCR family, e.g., AT1R, was used for the decision-making particle. When the cell identity is detected using a ligand, e.g., a GPCR antagonist, e.g., EXP3174 or telmisartan, the positive outcome of this interaction is that the particle binds to the cell surface and remains there. If the subsequent interaction is not positive, there is clearly a risk that the particle will remain on off-target cells. However, in this case, as can be expected, due to the thermodynamic equilibrium between the free and bound particles, the decrease in the concentration of free particles over time in vivo shifts the equilibrium so that the particle dissociates from the "wrong" target over time. In contrast, when the cell identity is detected using an agonist for the same GPCR, e.g., Ang-II, the positive response of the cell is particle internalization. Therefore, by carefully selecting the target and ligand types for interaction, the particles can be given a logic that may enable the identification of even more hidden target cells than the exemplary targets investigated in this study. An example is a localized ocular application in retinal tissue, where, for instance, by specifically targeting endothelial cells, the particles may be able to distinguish between more than 60 existing cell types.

[0041] The terms “nanoparticles” and “NP,” as used herein, refer to nanomaterial structures comprising a first ligand and a second ligand. In particular, nanoparticles are nanoobjects in which all three external dimensions are nanoscale, e.g., liposomes, polymer nanoparticles, micelles, lipid nanocapsules, inorganic nanoparticles, e.g., gold nanoparticles or Qdots. In one embodiment, nanoparticles offer excellent biocompatibility and a highly tunable composition. Nanoparticles can be produced from a wide range of materials, e.g., polymers, biomolecules, and metals. In one embodiment, the nanoparticles of the present invention are, for example, virus-mimicking nanoparticles capable of delivering a drug into target tissue in the mesangium of the kidney. In one embodiment, the nanoparticles comprise pirfenidone and / or synaciguat and are for use in the treatment of diabetic nephropathy. In one embodiment, the nanoparticles of the present invention comprise a biodegradable block copolymer comprising PEG and PLA. In one embodiment, the first and second ligands are covalently coupled to the nanoparticles via DCC / NHS or EDC / NHS. In one embodiment, the block copolymer is dissolved in acetonitrile and mixed with PLGA (70 / 30, m / m) to obtain a polymer mixture. In one embodiment, nanoparticles are prepared using nanoprecipitation by injecting the polymer mixture into an aqueous phase in droplet form. In one embodiment, the nanoparticles of the present invention accumulate in target tissues such as kidney tissue within a very short time after administration of the nanoparticles, i.e., <1 hour.

[0042] In one embodiment, the nanoparticles of the present invention are very small, i.e., <80 nm, and due to their small size, they can rapidly escape from the bloodstream through fenestrated endothelium and accumulate in target tissues such as mesangial tissue. In one embodiment, the nanoparticles further comprise a therapeutic agent, preferably either pirfenidone or synacigat. In one embodiment, the particles have a size of 5 nm to 1000 nm, preferably 10 nm to 150 nm, more preferably 20 nm to 100 nm. In one embodiment, the particle size is measured using dynamic light scattering, particle scattering diffusometry, nanoparticle tracking analysis, atomic force microscopy, or transmission electron microscopy, preferably dynamic light scattering or transmission electron microscopy. The particle size is determined by the diameter of a spherical particle with respect to any linear segment passing through the center of the spherical particle and whose endpoint is on the spherical particle. For non-spherical particles, the diameter is with respect to the longest linear segment passing through the center of the non-spherical particle and whose endpoint is on the particle. In one embodiment, the average diameter is with respect to the average diameter of the nanoparticles contained in a batch of nanoparticles. In one embodiment, the particles of the present invention have a polydispersity index of 0.01 to 0.5, preferably 0.01 to 0.3, more preferably 0.01 to 0.1. In one embodiment, the polydispersity index is measured using dynamic light scattering, particle scattering-diffusion spectroscopy, nanoparticle tracking analysis, atomic force microscopy, or transmission electron microscopy, preferably dynamic light scattering or transmission electron microscopy. In one embodiment, the terms “nanoparticles” and “particles” are used interchangeably. In one embodiment, the nanoparticles of the present invention are for use in pharmaceuticals. In one embodiment, the nanoparticles have a zeta potential that is positive, negative, or neutral, for example, between -20mV and 0mV, or between -15mV and -5mV. In one embodiment, the nanoparticles include at least one core containing nanomaterial and optionally a polymer and / or linker on its surface, wherein the first ligand and the second ligand are coupled to the polymer and / or linker. In one embodiment, the particles have a polymer core.

[0043] The term "viromitous," as used herein, refers to an approach in which a viral cell-targeting approach is mimicked. The viral-mimicking particles of the present invention are internalized by target cells by a recognition process having at least two sequential steps. In such a two-step process, the first step is that a first ligand on the particle, e.g., EXP3174 or telmisartan, binds to a target expressed on the target cell, e.g., an angiotensin receptor on mesangial cells. Subsequently, the particle is internalized into the target cell, which is mediated by a second ligand that binds to a target on the target cell, e.g., activated angiotensin II or a cyclic amino acid sequence (cycloArg-Gly-Asp-D-Phe-Lys; SEQ ID NO: 1), thereby initiating endocytosis of the particle. In one embodiment, the sequential presentation of the first and second ligands is achieved by i) stereocontrol mediated by the use of a longer linker, e.g., a longer PEG-PLA chain, for the first ligand compared to a shorter linker, e.g., a shorter PEG-PLA chain, used for the second ligand, and / or ii) an activation step, e.g., the conversion of angiotensin I to angiotensin II, which requires the second ligand to be activated so that it can mediate internalization. In one embodiment, the sequential presentation of ligands allows for a 15-fold higher accumulation of nanoparticles in target cells, such as mesangial cells, compared to conventional particles without ligand modification. In one embodiment, the particles have a particle avidity to a targeted receptor of 1 pM to 100 nM, preferably 50 pM to 1 nM. In one embodiment, the nanoparticles of the present invention are for use as pharmaceutical or diagnostic agents. In one embodiment, the nanoparticles of the present invention are for use in methods of preventing or treating diseases selected from diabetic nephropathy, glomerulonephritis, glomerular VEGF A dysregulation, endothelial VEGF A dysregulation, diabetic retinopathy, rheumatoid arthritis, age-related macular degeneration, and cancers such as breast cancer. In one embodiment, the terms “nanoparticles,” “virus-mimicking particles,” and “decision-executing nanoparticles” are used interchangeably.

[0044] The term “nanomaterial,” as used herein, refers to a material having any external dimensions on the nanoscale, or having an internal or surface structure on the nanoscale. In one embodiment, the nanomaterial preferably includes polyethylene glycol (PEG), polylactic acid (PLA), poly(lactic acid-coglycolic acid) (PLGA), oxazoline-derived polymers, poly(amino acids), polysaccharides, phospholipids, sphingolipids, cholesterol, PEG-lipids, e.g., DPSE-PEG and PEG-stearic acid, block copolymers, e.g., PEG-PLA or PEG-poly-caprolactone, inorganic substances, e.g., gold or qdot materials, and any combination thereof. In one embodiment, the first ligand and the second ligand are each coupled to the nanomaterial, preferably each to a block copolymer chain of the nanomaterial. In one embodiment, the nanomaterial comprises more than one block copolymer chain, the first ligand is coupled to a first block copolymer chain of the nanomaterial, the second ligand is coupled to a second block copolymer chain of the nanomaterial, and the first block copolymer chain is longer than the second block copolymer chain, preferably at least 1.5 times longer, and more preferably at least 3 times longer. In one embodiment, the first block copolymer chain comprises PEG in the range of 1k to 20k, preferably 1k to 10k, and / or PLA in the range of 5k to 40k, preferably 10k to 20k. In one embodiment, the PEG chain of the first block copolymer chain is longer than the PEG chain of the second block copolymer chain. In one embodiment, one ligand is coupled to one PEG molecule. The term "k," as used herein, refers to a kilodalton (kDa) with respect to polymer chains, e.g., block copolymer chains, PEG and / or PLA. For example, PEG in the range of 1k to 20k is PEG in the range of 1kDa to 20kDa, e.g., PEG 5kDa Regarding this, in one embodiment, PEG 5k -PLA10k and PEG 2k -PLA 10k is, respectively, PEG 5kDa -PLA 10kDa and PEG 2kDa -PLA 10kDa relates to. In one embodiment, the first block copolymer chain is PEG 5k -PLA 10k and the second block copolymer chain is PEG 2k -PLA 10k . In one embodiment, the nanomaterial comprises the total amount of PEG(PEG 総 ), and the particles have a ligand density of at least 5%, preferably at least 15%, more preferably at least 25% ligand / PEG 総 . The term "ligand" includes both the first ligand and the second ligand. In one embodiment, the ligand density of ligand / PEG is ≦ 50%.

[0045] The term “first ligand,” as used herein, refers to a ligand capable of mediating the attachment of nanoparticles to target cells. In one embodiment, the first ligand merely initiates the binding of particles to target cells, but does not initiate the internalization of particles into the target cells, and subsequent binding of a second ligand to the target cells is required to initiate the internalization of the particles into the target cells. In one embodiment, the first ligand is covalently or noncovalently coupled to the nanoparticles. In one embodiment, the first ligand is any biomolecule that induces the binding of nanoparticles to target cells, such as antibodies or their antigen-binding fragments, peptides, aptamers, DNA nanostructures, receptor ligands, and receptors. In one embodiment, the first ligand is a non-agonist agent that binds to GPCRs, such as angiotensin II receptor type 1 (AT1r), human neuropeptide Y1 receptor, and CXC chemokine receptor type 4, and / or an agent that binds to glycoproteins and / or glycolipids on the surface of target cells, such as heparan sulfate, sialycoprotein, ganglioside, and mannose receptors, preferably EXP3174 or telmisartan. In one embodiment, the non-agonist agent that binds to GPCRs induces particle binding to target cells but does not induce particle internalization into target cells, such as endocytosis. In one embodiment, the first ligand and / or the second ligand bind to a target that is not ubiquitously expressed but is predominantly expressed on target cells in target tissue. In one embodiment, the first ligand and / or the second ligand is K DIt binds to the target structure on the target cell with an affinity of <100 nM. In one embodiment, the first ligand and / or the second ligand have a molecular weight of <1500 Da. In one embodiment, the terms “target” and “target structure” are used interchangeably. In one embodiment, the term “target structure” refers to a protein, peptide, nucleic acid, saccharide, glycolipid, and / or glycoprotein presented on the surface of the target cell. In one embodiment, the first ligand is any AT1R antagonist having a free carboxylic acid residue for functionalization. In one embodiment, the first ligand is a selective AT1 antagonist, e.g., EXP3174 (losartan carboxylic acid) or telmisartan, which are potent and selective AT1 antagonists, or, if necessary, their bioactive derivatives. In one embodiment, the “biologically active derivative” has the same biological function as EXP3174 or telmisartan, e.g., the same binding function and / or therapeutic function.

[0046] The term "non-agonist agent," as used herein, refers to an agent that does not have an agonist effect on a target structure, preferably an agent that does not have an effect on the target structure that mediates its internalization into target cells, and that binds to the target structure.

[0047] The term “second ligand,” as used herein, refers to a ligand capable of mediating the internalization of nanoparticles into target cells. In one embodiment, binding of the second ligand to a target structure, e.g., a receptor on a target cell, initiates the internalization of nanoparticles into the target cell. In one embodiment, the target structure on the target cell is any structure typically expressed on the surface of the target cell, e.g., a surface molecule, a receptor, and / or a biomarker. In one embodiment, the target structure on the target cell is a molecule typically overexpressed in cells in a pathological state compared to healthy cells. In one embodiment, the first and second ligands target the same target structure on the target cell, or target different target structures on the target cell. In one embodiment, the second ligand is covalently or noncovalently coupled to the nanoparticles. In one embodiment, the second ligand is any biomolecule that induces the internalization of nanoparticles into the target cell, e.g., an antibody or its antigen-binding fragment, a peptide, an aptamer, a DNA nanostructure, a receptor ligand, and a receptor. In one embodiment, the second ligand is any of the following: i) preferably selected from RGD, cyclic RGD-peptides having the sequence of SEQ ID NO: 1, and derivatives thereof, a drug that binds to an integrin, e.g., αVβ3 integrin; ii) an agonist drug that binds to a GPCR, e.g., AT1r, preferably activated angiotensin-II; iii) a drug that binds to an ectoenzyme, e.g., regmine, membrane matrix metalloproteinase, and angiotensin-converting enzyme (ACE), preferably angiotensin-I; and / or iv) a drug that binds to a transferrin receptor. In one embodiment, the second ligand is enzymatically activated before the internalization of the nanoparticles into the target cells; for example, angiotensin-I is activated to angiotensin-II by ACE before the binding of the second ligand to AT1r and the internalization of the particles into the target cells. In one embodiment, the enzymatic activation of the second ligand is carried out by an ectoenzyme on the surface of a target cell, preferably the enzymatic activation includes enzymatic cleavage of the second ligand, thereby providing an activated second ligand.In alternative embodiments, the second ligand is not enzymatically activated before mediating internalization. In one embodiment, the ratio of the first ligand to the second ligand is in the range of 2:1 to 1:2, preferably 1:1. In one embodiment, the second ligand binds to the target cell after the first ligand has bound to the target cell. In one embodiment, the sequential binding of the first and second ligands to the target cell increases the specificity for the target cell.

[0048] In one embodiment, when the second ligand targets AT1r, angiotensin-I as the second ligand is preferred over angiotensin-II as the second ligand, because the intermediate step of enzymatic activation of angiotensin-I to angiotensin-II allows for increased specificity of the nanoparticles. In one embodiment, when the first ligand is EXP3174 and the second ligand is angiotensin-II, or angiotensin-I activated to angiotensin-II, both the first and second ligands bind to the same target structure on the target cell, namely AT1R. In this embodiment, the first ligand, EXP3174, binds to AT1R as an antagonist, and the second ligand, angiotensin-II, binds to AT1R as an agonist after enzymatic activation as needed. After binding of the first ligand, e.g., EXP3174, there is still an AT1R binding site available for the second ligand. In one embodiment, the binding site of the target bound by the first ligand and the binding site of the target bound by the second ligand are different binding sites, or they are the same binding site but are bound sequentially.

[0049] In one embodiment, the second ligand is shielded from binding to the target cell by i) steric hindrance, for example, by a block copolymer chain or linker of the second ligand that is shorter than the block copolymer chain or linker of the first ligand, and / or by the need for enzymatic activation of the second ligand before the second ligand can mediate internalization.

[0050] The term "capable of mediating adhesion," as used herein, refers to the ability of a first ligand to bind to a target cell. The first ligand is capable of mediating adhesion; that is, it induces the binding of nanoparticles to the target cell, preferably by targeting a target structure on the target cell. In one embodiment, the binding of the first ligand to the target cell does not induce the internalization of nanoparticles into the target cell. In one embodiment, further interaction is required for the internalization of nanoparticles into the target cell, i.e., an interaction between a second ligand and the target cell, preferably including a second ligand that targets the same or a different target structure on the target cell as the target structure of the first ligand. In one embodiment, the first and second ligands may bind to the same target structure but to different sites on the target structure, e.g., an agonist binding site and an antagonist binding site.

[0051] The term "capable of mediating internalization," as used herein, refers to the ability of a second ligand to induce the internalization of nanoparticles into target cells. In one embodiment, the second ligand binds to a target structure on the target cell, thereby initiating the internalization of nanoparticles into the target cell. In one embodiment, the ability to induce internalization may include the ability to be activated, for example, by enzymatic activation, before inducing internalization. In one embodiment, the internalization involves either receptor-mediated endocytosis, clathrin-coated pits, and / or caveolae.

[0052] The term “target cells,” as used herein, refers to cells involved in a pathological condition, i.e., a disease. In one embodiment, treatment of the disease involves targeting the cells involved in the disease using the nanoparticles of the present invention. In one embodiment, the nanoparticles of the present invention function as a drug delivery system for transporting a drug to the target cells. In one embodiment, the target cells are selected from mesangial cells, endothelial cells, such as retinal endothelial cells, and tumor cells.

[0053] The term “therapeutic agent,” as used herein, refers to any substance intended for a medical treatment. In one embodiment, the therapeutic agent is contained in the particle body, i.e., core, of the nanoparticles, for example, inside the nanoparticles, and / or throughout the particle nanomaterial, and / or is coupled to the nanoparticles using a linker. In one embodiment, the therapeutic agent is a lipophilic therapeutic agent and is encapsulated and / or contained within the particle body. In one embodiment, the therapeutic agent is non-covalently or covalently coupled to the particles, for example, by a cleavable linker. In one embodiment, the therapeutic agent may be covalently or non-covalently coupled to any component of the nanoparticles. In one embodiment, the therapeutic agent is an antifibrotic agent or a chemotherapeutic agent. In one embodiment, the therapeutic agent is either pirfenidone or synacigat. The term “particle body,” as used herein, refers to the primary supporting structure of a particle. For example, the particle body may refer to the lipid bilayer of a liposome, or the core structure of a polymer and / or solid lipid particle. In one embodiment, the nanoparticles of the present invention are loaded with a therapeutic agent for specifically treating target cells, such as mesangial cells, with the therapeutic agent. In one embodiment, the therapeutic agent loaded into the particles, for example, pirfenidone or synaciguat, is dissolved in a polymer phase, incorporated into the particles during the preparation of the particle polymer core, and / or dissolved in an aqueous phase contained by the particles, for example, an aqueous phase contained by liposomes, and / or dissolved in a lipid phase contained by the particles, for example, a lipid phase contained by liposomes. Pirfenidone is a TGF-beta antagonist and has been proposed as a candidate for treating mesangial-associated pathological fibrosis. Synaciguat (BAY 58-2667) is a soluble guanylate cyclase (sGC) activator and has been proposed for treating diabetic nephropathy. In one embodiment, the therapeutic agent pirfenidone or synaciguat is efficiently incorporated into the polymeric core of the nanoparticles without significantly altering the properties of the particles, which is possible due to the lipophilic properties of the therapeutic agent.In one embodiment, the nanoparticles are for use in the treatment of diabetic nephropathy, and the therapeutic agent is an antifibrotic agent. In another embodiment, the nanoparticles are for use in the treatment of cancer, and the therapeutic agent is a chemotherapeutic agent.

[0054] The present invention further relates to compositions comprising the nanoparticles of the present invention and pharmaceutically acceptable excipients. The nanoparticles of the present invention may be mixed with appropriate auxiliary substances and / or additives to obtain pharmaceutically acceptable compositions. Such substances include pharmaceutically acceptable substances that increase the stability, solubility, biocompatibility, or biological half-life of the nanoparticles, or substances that need to be included for application in a particular route, for example, for intravenous solutions, sprays, bandages®, or pills. The present invention also relates to compositions comprising the nanoparticles of the present invention for use in pharmaceuticals, for example, for use in methods of preventing or treating diseases selected from diabetic nephropathy, glomerulonephritis, glomerular VEGF A dysregulation, endothelial VEGF A dysregulation, diabetic retinopathy, rheumatoid arthritis, age-related macular degeneration, and cancers such as breast cancer.

[0055] The nanoparticles of the present invention utilize a novel virus-mimicking recognition principle for target cells such as mesangial cells, which results in highly efficient accumulation of the nanoparticles in target tissues such as mesangia. In one embodiment, the nanoparticles are combined with a suitable therapeutic agent, i.e., the therapeutic agent is incorporated into and / or ligated to the nanoparticles, enabling targeted treatment of target cells in target tissues, e.g., mesangial cells in mesangia. In one embodiment, the nanoparticles containing the therapeutic agent are used to prevent or treat diabetic nephropathy. In one embodiment, the nanoparticles of the present invention enable targeting of target cells using a recognition process having at least two steps. In one embodiment, the nanoparticles of the present invention comprise a selective AT1 antagonist, e.g., EXP3174, as a first ligand, and further comprise a therapeutic agent, preferably pirfenidone and / or synaciguat. In one embodiment, the nanoparticles of the present invention are EXPcRGD nanoparticles, i.e., nanoparticles comprising EXP3174 as a first ligand and cRGD, particularly cRGDfK, as a second ligand, or the nanoparticles are EXPAng-I nanoparticles, i.e., nanoparticles comprising EXP3174 as a first ligand and Ang-I as a second ligand. In one embodiment, the EXPcRGD nanoparticles and / or EXPAng-I nanoparticles further comprise a therapeutic agent, preferably pirfenidone and / or synaciguat. In one embodiment, the nanoparticles further comprise a therapeutic agent which is a nanoparticle comprising a selective AT1 antagonist, such as EXP3174, as a first ligand, preferably EXPcRGD nanoparticles, and synaciguat. In one embodiment, the nanoparticles comprise or comprise nanomaterials comprising PLGA and / or PEG-PLA.

[0056] The term “administer,” as used herein, refers to the administration of a drug, for example, the nanoparticles of the present invention and / or the pharmaceutical compositions of the present invention, which may be achieved by any method that allows the drug to reach target cells. These methods include, for example, injection, oral ingestion, inhalation, nasal delivery, topical administration, deposition, implantation, suppositories, or any other method of administration that provides access to target cells by the nanoparticles. Injection may refer to intravenous, intradermal, subcutaneous, intramuscular, or intraperitoneal injection. Implantation may refer to the insertion of an implantable drug delivery system containing the nanoparticles of the present invention, and / or a hydrogel containing nanoparticles, in particular a hydrogel that gels in situ and releases the nanoparticles with a delay, and is injected subcutaneously and / or intraperitoneally. Suppositories include glycerin suppositories. Inhalation refers to the administration of nanoparticles using an aerosol in an inhaler, either alone or attached to an absorbable carrier. The nanoparticles may be suspended in a liquid, for example, in colloidal form.

[0057] "Effective dose" is the amount of nanoparticles or pharmaceutical composition that alleviates the symptoms found for a disease and / or condition.

[0058] The term “patient” as used herein refers to a human or animal, preferably a mammal. Treatment of a patient means, for example, preventing, treating, reducing the symptoms of, or curing a disease or condition, such as cancer or diabetic nephropathy.

[0059] The term “block copolymer,” as used herein, refers to a polymer containing two or more homo- or copolymer subunits linked by covalent bonds. It may include intermediate non-repeating subunits that form junction blocks. Block copolymers are composed of blocks of different polymerized monomers. The term “block copolymer chain” refers to a chain of block copolymers.

[0060] The terms “DCC / NHS coupling” and “EDC / NHS coupling,” as used herein, refer to a coupling reaction. A common method for synthesizing an NHS-activated molecule is to mix the NHS with, for example, a desired carboxylic acid and a small amount of an organic base in an anhydrous solvent. A coupling reagent, for example, dicyclohexylcarbodiimide (DCC) or ethyl(dimethylaminopropyl)carbodiimide (EDC), is then added to form a highly reactive activated intermediate. In one embodiment, a first ligand and a second ligand are coupled to the nanomaterial in at least two steps. In one embodiment, the first ligand and the second ligand are coupled to the nanomaterial via a linker, via a fusion protein and / or via PEG.

[0061] The inventors hereby successfully demonstrate that virus-mimicking NPs that double / triple-check cell identity enable enhanced NP accumulation in targeted microclavic cells (MCs) in vivo. By combining an antagonistic ligand that mimics the initial cell attachment of viruses with an enzyme-mediated target cell recognition process, the particles exhibited exceptionally high in vitro target avidity, along with exceptional target cell specificity. The inventors also demonstrate that simultaneous hetero-polyvalent binding of the agonist and antagonist anchored to the particle to the same GPCR remarkably leads to particle uptake. Overall, non-specific, size-mediated passive targeting is insufficient to achieve satisfactory particle accumulation in MCs. Even traditional particle functionalization using a single ligand appears to be an inadequate approach. However, by mimicking a complex, multi-step virus-target cell binding and recognition process, the inventors have obtained particles that can identify MCs and accumulate within them. This expands new options for drug delivery for the treatment of various diseases, including kidney disease.

[0062] The inventors have further fabricated adenovirus-mimetic block copolymer nanoparticles that effectively target glomerular mesangial cells due to sterically controlled sequential ligand-receptor interactions. Hetero-polyvalent NPs thereby not only exhibited precisely controllable physicochemical characteristics but also demonstrated excellent avidity to both target motifs, resulting in substantial AT1r binding in the picomolar concentration range and significantly increased mesangial cell uptake compared to non-functionalized NPs. Benefiting from these features, virus-mimetic NPs were able to selectively target mesangial cells even in the surrounding environment of off-target cells. Furthermore, hetero-polyvalent NPs exhibited the necessary in vivo robustness, resulting in efficient in vivo accumulation in the mesangial region with only minimal off-target deposition in the kidney. Notably, hetero-polyvalent EXPcRGD NPs thereby showed far better mesangial targeting compared to homo-functional cRGD or EXP NPs. The inventors were able to target the same distinct cell type in vivo using concepts inspired by two different viruses, and therefore conclude that mimicking viral infection patterns enables a highly effective targeting concept. Furthermore, successful mesangial cell targeting enables sophisticated treatment of mesangial-associated renal pathology because it dramatically increases drug delivery compared to all other approaches currently available.

[0063] The present invention is further described herein with reference to the following drawings.

[0064] All methods mentioned in the following drawings were carried out as described in detail in the examples. [Brief explanation of the drawing]

[0065] [Figure 1]Figure 1 shows viral-mimicking attachment and target cell recognition. (A) NPs (NPEXPAng-I) possessing EXP3174 and Ang-I on their corona attach to the cell membrane via EXP3174-mediated AT1R binding. Specific recognition is induced via enzymatic Ang-I processing and Ang-II-mediated internalization. (B) A flowchart illustrating triple target cell recognition of decision-executing NPs.

[0066] [Figure 2] Figure 2 shows the characterization of nanoparticles. (A) Assembly of ligand-modified NPs. (B) Molar concentrations of different NP species and ligand content normalized to PEG content, (C) size and polydispersity index (PDI), and (D) zeta potential of the resulting NP formulations. Results are shown as the mean ± SD of at least n=3 measurements.

[0067] [Figure 3] Figure 3 shows the in vitro interactions with AT1R and ACE. Interactions of ligand-modified NPs with their targets AT1R (A-D) and ACE (E-F), determined by intracellular calcium measurements. (A) Ligand affinity and (B) particle avidity for AT1R. (C) IC50 values ​​for free ligand and particle-bound ligand. (D) Dynamical measurement of AT1R inhibition by ligand-modified particles. (E) Michaelis-Menten dynamics of NPEXPAng-I and NAng-I. (F) Specificity constants (Kcat / km) for free Ang-I and particle-bound Ang-I, calculated based on ligand and NP concentrations. Results are shown as mean ± SD of at least n=3 measurements. The levels of statistical significance are indicated as **p≦0.01, ***p≦0.001, ****p≦0.0001, and #p≦0.0001 and x≦0.001 when comparing AT1R inhibition by NPEXP and NPEXPAng-I at different time points. ns: Not significant.

[0068] [Figure 4]Figure 4 shows the intracellular integration of NPEXPAng-I (red) in target rat mesangial cells (rMCs) (white) (pAT1R-rMCs) transfected with YFP-tagged AT1R (green) at different incubation times. Scale bar 20 μm.

[0069] [Figure 5] Figure 5 shows the uptake specificity of viral mimic NPEXPAng-I. (A) Ligand-mediated internalization of NPEXPAng-I, NPAng-I, and NPEXP in rMCs inhibited by free EXP3174 and captopril (see also Figures 11 and 12). (B) Uptake of NPEXPAng-I in AT1R and ACE-positive rMCs and HK-2 cells, as well as in AT1R and ACE-negative HeLa cells. Specificity of particle uptake in co-culture of targeted rMCs with off-target (C) NCI-H295-R cells or (D) HeLa cells, analyzed via flow cytometry. (E) CLMS image of particle uptake (red) in green-stained (CTG) rMCs (green) in co-culture with deep red-stained (CTDR) off-target HeLa or NCI-H295R cells (white). Scale bar 20 μm. (See also Figure 13). Results are shown as the mean ± SD of at least n=3 measurements. Levels of statistical significance are shown as **p≦0.01, ***p≦0.001, ****p≦0.0001, and #p≦0.0001, comparing NP uptake in cells with and without captopril or EXP3174 inhibition. ns: not significant.

[0070] [Figure 6] Figure 6 shows the distribution of NPs in mouse kidneys. (A) NPEXPAng-I fluorescence located in the renal glomeruli (white arrows). (B) Untargeted NPMeO in the control group does not accumulate in the renal glomeruli and lacks particle-associated fluorescence. Blue: DAPI staining of cell nuclei; Green: Tissue autofluorescence; Red: NP-associated fluorescence. From left to right, the rectangular sections are shown as magnified views.

[0071] [Figure 7] Figure 7 shows the evaluation of NP-related fluorescence detected in renal glomeruli, analyzed via fluorescence microscopy. (A) Images of renal glomeruli (dotted circles) from mice treated with different particle formulations. Scale bar 40 μm. See also Figure 14B. (B) Quantitative analysis of complete glomerular NP-fluorescence. (C) Comparison of particle-related fluorescence in extracortical and endocortical glomeruli. (D) Glomerular localization of NPEXPAng-I determined via CLSM and integrin-α8 staining of MCs (scale bar 20 μm). Results in (C) and (D) are shown as mean ± SD of at least n=120 fluorescence measurements from n=6 mice per NP sample. Levels of statistical significance are shown as ****p ≤ 0.0001. ns: not significant.

[0072] [Figure 8] Figure 8 shows ligand coupling to PEG-PLA block copolymers. (A) Lys-Ang-I and (B) EXP3174 were coupled to PEG5k-PLA10k terminated with a carboxylic acid or amine, respectively, using EDC / NHS or DCC / NHS chemistry. (C) Complete polymer functionalization as shown by quantification of molar concentration ligand and PEG content. (D) Absence of unreacted NH2 polymer terminal groups on the EXP3174-modified polymer was determined using fluorescamine. Student's t-test was performed using GraphPad Prism 6.0 to assess statistical significance. The level of statistical significance is indicated as ****p ≤ 0.0001, comparing the fluorescence of MeO- and EXP3174- with NH2-terminated PEG5k-PLA10k. See Example 1 for detailed methods.

[0073] [Figure 9]Figure 9 shows the maximum calcium signal and inhibition by NPEXP. rMCs were simultaneously stimulated with Ang-II and NPEXP, and the resulting intracellular calcium response was measured immediately for 1 minute. At the NPEXP concentrations used, the EXP3174 ligand did not inhibit the agonist-induced calcium signal during the assay duration. Therefore, the effect of EXP3174 on the Ang-II measurement was considered negligible. Results are shown as mean ± SD of at least n=3 measurements. See Example 1 for detailed methods.

[0074] [Figure 10] Figure 10 shows the time course of uptake of different particle formulations in AT1R-positive pAT1R-rMCs analyzed via CLSM. (A) NPEXP is not internalized in the cell line and is mostly located in the cell membrane and in the filipodia between cells, which form large clusters over time. Receptor binding is indicated by the co-localization of NP-associated fluorescence and receptor-associated fluorescence. (B) NPAng-I is internalized by cells, as indicated by their cytoplasmic localization. (C) NPMeO is not associated with cells due to the lack of an anchored ligand that enables specific targeting. Cells: white; AT1R-YFP: green; NP formulation: red. Scale bar 20 μm. See Example 1 for detailed method.

[0075] [Figure 11]Figure 11 shows that EXP3174 counteracts the reduced uptake of the Ang-I ligand due to steric hindrance caused by the long polymer chains on NPEXPAng-I. NPAng-I (gray) with a 20% Ang-I density was prepared using COOH-PEG5k-PLA10k with varying polymer densities, and their cellular uptake was analyzed using flow cytometry. Concurrently, NPEXPAng-I (yellow) was prepared using EXP3174-PEG5k-PLA10k with varying densities, and the effect of the second ligand on Ang-I steric hindrance was compared. Functionalization of the long polymer chains on NPEXPAng-I by EXP3174 counteracted the reduced uptake due to steric hindrance of the Ang-I ligand when unfunctionalized long polymers were added, significantly increasing particle internalization. Results are shown as mean ± SD of at least n=3 measurements. A two-way ANOVA using Sidac's multiple comparison test was performed using GraphPad Prism 6.0 to evaluate statistical significance. The level of statistical significance is indicated as ****p ≤ 0.0001. For detailed methods, please refer to Example 1.

[0076] [Figure 12] Figure 12 shows the specificity of NP uptake analyzed via CLSM. Cells were pre-incubated with free EXP3174 for 30 minutes before the addition of different NP formulations (NPEXPAng-I, NPAng-I, and NPEXP). Inhibition of the target receptor resulted in suppression of particle-associated fluorescence. Scale bar 20 μm. See Example 1 for detailed method.

[0077] [Figure 13]Figure 13 shows the uptake of (A) NPEXP and (B) NPAng-I in co-culture of target and off-target cells. NPEXP shows accumulation in rMC and NCI-H295R cells because these cells both possess AT1R. In contrast, co-culture of rMC and HeLa cells shows preferential accumulation of NPEXP in rMCs because HeLa cells express only small amounts of the receptor on their cell membrane (see [3]). NPAng-I shows higher specificity because it preferentially accumulates in target rMCs rather than off-target cells (HeLa or NCI-H295R cells) that lack ACE, and target rMCs possess the necessary machinery (ACE and AT1R) for their internalization. Cell nucleus: blue; off-target cells (HeLa or NCI-H295R): white; target cells (rMC): green; NP: red. Scale bar 20 μm. For detailed instructions, please refer to Example 1.

[0078] [Figure 14]Figure 14 shows the in vivo distribution of different NP formulations. (A) Renal distribution of NPAng-I and NPEXP in mouse kidneys. NPAng-I shows small NP-related fluorescence in the majority of glomeruli, in contrast to NPEXP, which did not accumulate in this region. Glomeruli are marked with white arrows for better visualization. From left to right, the square-cropped regions are shown as magnified views. DAPI staining of cell nuclei: blue; tissue autofluorescence: green; NP-related fluorescence: red. (B) Renal distribution of free dyes used to label NPs. CF647 was injected into mice as a control, and its distribution in the kidneys was evaluated. Strong fluorescence was detected in the tubular region without fluorescence in the glomeruli (marked with white circles). This demonstrates that the fluorescence observed for particle-samples originates from the particles themselves and not from leaked dyes that are freely filtered due to their low molecular weight. (C) Plasma retention of different NP formulations after 1 hour of circulation in NRMI mice. NP fluorescence in plasma was measured 1 hour after injection and normalized to fluorescence measured 5 minutes after injection (initial particle blood fluorescence). Untargeted NPs (NPMeO) exhibit the highest circulating time, attributed to the stealth effect conferred by their PEG-shell. Even when 40% of all polymers on the NPEXPAng-I surface are coupled to ligands, reducing the particle stealth effect, they can still exhibit blood retention consistent with untargeted particles. These show significantly higher fluorescence in plasma after 1 hour compared to particles functionalized by only one ligand (NPAng-I and NPEXP). NPAng-I, possessing a specific two-step virus-mimicking recognition mechanism, also shows significantly better blood retention than NPEXP, which commonly indicates targeted NPs. As a control, the free dye (CF647) used to label the particles was further injected into mice, which then rapidly disappears from blood circulation into its free filtration (6% of initial fluorescence after 1 hour). Results in (C) are shown as mean ± SD for at least n=6 samples. A Student's t-test was performed using GraphPad Prism 6.0 to evaluate statistical significance.The levels of statistical significance are indicated as *p≦0.05, ***p≦0.001, and ****p≦0.0001. ns: Not significant. See Example 1 for detailed methods.

[0079] [Figure 15] Figure 15 shows an exemplary in vivo use of the determination-executing nanoparticles of the present invention, comprising a first ligand for adhesion to target cells and a second ligand for recognition of the nanoparticles / internalization thereof into the target cells. The nanoparticles of the present invention can be used to target various target tissues, e.g., mesangium. The nanoparticles can be customized to target specific target tissues by selecting first and second ligands that target target receptors and / or molecules on the surface of target cells.

[0080] [Figure 16] Figure 16 shows cross-sectional kidney sections of animals treated with particles. A) Virus-mimicking particles show high accumulation in the renal corpuscle (indicated by round labels). B) Unmodified nanoparticles without the first and second ligands show no significant uptake into glomerular tissue.

[0081] [Figure 17] Figure 17 shows that adenovirus-mimetic NPs enter glomerular mesangial cells via a synergistic combination of passive and active targeting strategies. (a) Upon administration, NPs reach the glomerular region of the renal filtration system via afferent arterioles that subsequently branch into the glomerular capillary system. (b) Within the glomerular capillaries, NPs, due to their reticular structure, cannot pass through the renal filter but can extravasate through endothelial fenestrations, thereby reaching the mesangium located in the gaps. (c) Subsequently, virus-mimetic NPs can effectively infiltrate mesangial cells via initial binding to angiotensin II receptor 1 (AT1r) and subsequent αVβ3 integrin-mediated endocytosis. (AA: afferent arteriole; EA: efferent arteriole; MC: mesangial cell; PO: podoptera; FP: peduncle; ET: endothelium; BM: basement membrane).

[0082] [Figure 18] Figure 18 shows the characterization of adenovirus-mimetic NPs. (a) Particle design of hetero-polyvalent EXPcRGD NPs and homo-functional or non-functionalized NP species. (b) DLS analysis. All particle types were manufactured below a 60 nm size threshold without significant aggregation (PDI: polydispersity index). (c) Zeta potential measurements. Addition of COOH-PEG2k-PLA10k to the polymer mix resulted in a negative surface charge. (d) / (e) Quantification of ligand surface density of cRGDfK and EXP3174, respectively, after NP manufacturing. The final surface content was directly proportional to the amount of ligand-functionalized polymer added beforehand for both cRGDfK (R2=0.9957) and EXP3174 (R2=0.9871). Results are shown mean ± SD (n=3).

[0083] [Figure 19] Figure 19 shows the AT1r interaction of adenovirus-mimicking NPs. (a) Intracellular calcium levels after AT1r stimulation of rMCs treated with free EXP3174 or particle-bound EXP3174. Both EXPcRGD NPs (IC50 = 276 ± 31 pM) and EXP NPs (IC50 = 552 ± 73 pM) effectively bound to AT1r, thereby inhibiting AT1r and resulting in lower Ca2+ influx upon AT1r stimulation by angiotensin II (ATII). This effect was even stronger than that for free EXP3174 (IC50 = 2.66 ± 0.9 nM), due to increased avidity from polyvalentity. (b) AT1r activity for rMCs treated with NPs without AT1r ligands. Neither the non-functionalized control NP nor the cRGD NP significantly bound to AT1r, and both produced maximum calcium levels upon ATII stimulation, confirming the specificity of the assay (M = molar concentration of either NP or EXP3174). The results are shown as mean ± SD (n=3).

[0084] [Figure 20]Figure 20 shows in vitro internalization of NPs by target mesangial cells. (a) CLSM analysis of rMCs stained with CTDR after incubation with EXPcRGD nanoparticles labeled with 0.05 mg / mL of AlexaFluor® 568. NP-related fluorescence (purple) was detected in the vesicle structure (gray) within the rMC cytosol. With increasing incubation time, endocytotic vesicles grew together in size, number, and intensity, showing fusion of vesicles into larger endosomes (scale bar 20 μm). (b) Flow cytometry analysis of NP uptake into rMCs. Hetero-multivalent EXPcRGD NPs showed substantially increased cellular uptake compared to control NPs and homo-functional NPs. (c) Flow cytometry results after 60 minutes of NP incubation. EXPcRGD NPs showed maximum cell association compared to all other NP types, but the addition of an excess amount of free cRGDfK (c=500 μM) sharply reduced the fluorescence signal to the level of EXP NPs, indicating αVβ3 dependence of NP uptake. Results are shown mean ± SD (n=3). ◇P<0.0001, ○P<0.001, ****P<0.0001 (AFU, arbitrary fluorescence units).

[0085] [Figure 21]Figure 21 shows TEM analysis of NP interactions with mesangial cells. (a) EXPcRGD NPs accumulated in numerous vesicular structures (black arrows) within rMCs. Vesicles of different sizes are present in both the outer and inner portions of the cell cytosol, indicating intracellular processing and fusion into larger endosomes. Furthermore, a significant number of NPs remain located on the cell membrane, suggesting that the particles underwent a stepwise process of initial cell binding and subsequent endocytosis (the image on the right shows a zoomed-in view of the black square on the left). (b) In contrast, EXP NPs accumulated only at the cell boundary, where they bound to distinct surface structures of rMC cells, indicating possible interactions with membrane-bound AT1r (the image in the upper left corner shows a zoomed-in view of the black square). (c) Control NPs showed only negligible interactions with rMCs, and gold-enhanced NPs were barely visible.

[0086] [Figure 22]Figure 22 shows the mesangial cell selectivity of EXPcRGD NPs in an in vitro co-culture assay. (a) CLSM analysis of CTG-stained rMCs (green) co-cultured with CTDR-labeled HeLa or NCI-H295R cells (gray) acting as off-target cells. Cell nuclei were stained with Hoechst 33258 (blue). For rMC / HeLa co-cultures (top row), NP-derived fluorescence (purple) could only be detected within the rMC region, indicating selective uptake of EXPcRGD NPs into target cells. Co-culture of rMCs with AT1r-expressing NCI-H295R cells resulted in a diverse NP distribution (bottom row). EXPcRGD NPs also bound to the surface of NCI-H295R cells, resulting in a diffused pattern around the cell boundary. However, efficient particle uptake into round endocytic vesicles was observed only in mesangial cells (scale bar 20 μm). Flow cytometry analysis of rMCs with both HeLa (b) and NCI-H295R (c) supported the CLSM results, as EXPcRGD NPs showed significantly higher cellular association with rMCs in both cases. Interestingly, the addition of an excess amount of free EXP3174 (c=1 mM) in (c) sharply reduced NP interactions with NCI-H295R cells, indicating that EXPcRGD NPs could no longer bind to NCI-H295R cells via AT1r. Results are shown mean ± SD (n=3). ****P<0.0001 (ns: not significant. AFU, any fluorescence units).

[0087] [Figure 23] Figure 23 shows that EXPcRGD NP exhibits strong intraglomerular accumulation in vivo. Transverse kidney frozen sections were imaged using a fluorescence microscope. To facilitate histological evaluation, cell nuclei were stained with DAPI (blue) and tissue autofluorescence was recorded (green). EXPcRGD NP (red) was found to accumulate almost exclusively in the cortical glomerular region (white circles), while fluorescence in the tubular region was negligible (images are shown as zoomed-in figures with white squares, from top left to bottom right).

[0088] [Figure 24] Figure 24 shows that EXPcRGD NPs exhibit significantly enhanced accumulation in mesangial cells. (a) Fluorescence microscopy analysis revealed that high fluorescence levels within glomeruli (white circles) were primarily detectable for EXPcRGD NPs. EXP NPs showed moderate accumulation in glomeruli, while control NPs and cRGD NPs produced no signal to a significant degree (scale bar 20 μm; calibration bar: values ​​from 0 to 65535 Gray). (b) Accurate quantification of intraglomerular fluorescence intensity was achieved by evaluating the integrated density per glomerular area for a sufficient number of glomeruli. This showed that EXPcRGD NPs exhibited significantly higher fluorescence intensity per glomerulus compared to all other particle types. Results are shown mean ± SD (n=60). ****P<0.0001 (AFU, arbitrary fluorescence units). (b) Antibody staining for the mesangial surface marker integrin α-8 showed that EXPcRGD NP-related fluorescence (red) co-localized with regions covered by mesangial cells (yellow), indicating that EXPcRGD NP was able to selectively infiltrate mesangial cells via endocytosis. Scale bar 20 μm.

[0089] [Figure 25]Figure 25 shows the synthetic concept for ligand-functionalized PEG-PLA block copolymers. (a) A hetero-bifunctional PEG polymer ((1)) with varying chain lengths (2kDa / 5kDa) was mixed with 3,6-dimethyl-1,4-dioxane-2,5-dione ((2)) to create NH2-PEG5k-PLA10k and COOH-PEG2k-PLA10k ((3)) via ring-opening polymerization. (b) Subsequently, NH2-PEG5k-PLA10k was covalently coupled to the carboxyl group of EXP3174 ((4)) via DCC / NHS chemistry to obtain EXP3174-PEG5k-PLA10k ((5)). (c) Furthermore, COOH-PEG2k-PLA10k was bonded to the lysine residue of cRGDfK((6)) via EDC / NHS chemistry to obtain the shorter cRGDfK-PEG2k-PLA10k((7)). (d) The coupling efficiency for the synthesized EXP3174-PEG5k-PLA10k was determined by comparing the molar concentrations of both PEG and EXP3174. The molar concentrations did not vary significantly, indicating successful functionalization. (e) The coupling efficiency for cRGDfK-PEG2k-PLA10k was also within a reasonable range, with only negligible differences in the molar concentrations of PEG and cRGDfK. Results are shown mean ± SD (n=3).

[0090] [Figure 26] Figure 26 shows gold-tagged NPs that enable enhanced TEM visualization. The NPs were labeled with gold by covalently bonding extremely small gold nanoparticles (diameter: 2.2 nm) to the carboxyl groups of PLGA, which was subsequently used to produce the NPs. After incubation of the rMC and the labeled NPs, the particle cores were enhanced with gold by depositing additional gold particles on the NP cores, thereby increasing the electron density of the sample and enabling visualization under a TEM microscope, at which point the NPs appeared as dark spots.

[0091] [Figure 27]Figure 27 shows (a) flow cytometry results and (b) quantification of αVβ3 expression by different cell types investigated by CLSM. For cytometric analysis, nonspecific binding sites were blocked with 2% BSA in DPBS, and 10⁵ cells were incubated for 1 hour with AlexaFluor® anti-CD51 / 61 antibody (AlexaFluor® mouse IgG1, κ isotype control (FC)) at a 1:20 dilution in 0.1% BSA in DPBS (serving as a nonspecific control). The cells then underwent multiple steps of DPBS washing and centrifugation. Finally, the samples were resuspended in DPBS and analyzed using flow cytometry as previously described (FACS Calibur, excitation: 633 nm, emission: 661 / 16 nm bandpass filter). Fluorescence levels derived from αVβ3 were thus highest for rMCs, while HeLa and NCI-H295R cells both showed negligible signals, both of which were significantly lower than those for rMCs. Results are shown mean ± SD (n=3). ****P<0.0001, **P<0.01, *P<0.05 (AFU, arbitrary fluorescence units). To confirm the flow cytometry results, rMCs were seeded in 8-well Ibidi slides (15,000 cells / well) and stained for αVβ3 integrin as described above. The cells were then washed with DPBS, fixed with 4% PFA in DPBS, and analyzed on a Zeiss LSM 710. The CLSM image shows a strong integrin signal co-localized with the rMC cell body, indicating substantial αVβ3 expression by mesangial cells. Scale bar 20 μm.

[0092] [Figure 28]Figure 28 shows the results of fluorescence imaging. A) Relative plasma fluorescence after NP injection. The control NP showed a maximum circulating blood value with nearly 50% residual plasma fluorescence 60 minutes after injection. In contrast to EXP NP and EXPcRGD NP, both of which showed acceptable residual concentrations, cRGD NP was rapidly cleared from the blood. Results are shown mean ± SD (n=3). ****P<0.0001, ***P<0.001, **P<0.01 (ns: not significant). B) Fluorescence imaging of kidney frozen sections after injection of free CF™ 647 fluorescent dye. Sections were stained with DAPI (blue) to visualize cell nuclei. After injection of comparable molar concentrations of the free dye, a strong fluorescence signal (red to white) may be detected in the renal tubular region, indicating free renal filtration of the low molecular weight dye. As expected, no glomerular accumulation was detected (white circles) (calibration bar: values ​​from 0 to 65535 Gray).

[0093] [Figure 29] Figure 29 illustrates the concept of synacigat delivery assisted by NPs. Hetero-polyvalent EXPcRGD NPs enter target renal mesangial cells via a previously described sequential recognition sequence. Following successful endocytosis, the NPs undergo endolysosomal degradation, resulting in synacigatate release (small dots). The CCGs then activate and stabilize mesangial sGCs, leading to enhanced NO-mediated cGMP production. Several profibrillatory pathways are inhibited via cGMP-mediated activation of protein-regulated kinases (PGK1-α), resulting in an overall reduction in profibrillatory remodeling of mesangial cells.

[0094] [Figure 30] Figure 30 shows an exemplary experimental setup. For all experiments, free synaciguat (c=2 μM) was compared to EXPcRGD NPs with or without the drug, with a concentration of 0.2 μM CCG. The amount of free synaciguat was selected in accordance with previous studies that showed potent effects in this concentration range.

[0095] [Figure 31] Figure 31 shows a Western blot analysis of the effects of synaciguat on drug targets. a) sGC stimulation and stabilization. Both free CCG and CCG-loaded EXPcRGD NPs resulted in a substantial increase in sGC levels during a 24-hour incubation, while control NPs lacking CCG showed no significant effect. b) PGK1-α activation. To assess PGK1-α activity, phosphorylation of its substrate, vasodilator-stimulated phosphorylated protein (VASP), was evaluated. Both free CCG and CCG-loaded EXPcRGD NPs resulted in a significant increase in the P-VASP / VASP ratio, while control NPs showed no detectable change (n=3;****P<0.0001;***P<0.001;**P<0.01;*P<0.05).

[0096] [Figure 32-1] Figure 32 shows the anti-fibrotic and anti-proliferative effects of synacigat-loaded NP. Mesangial cells were pre-incubated with free CCG or NP for 4 hours before 48 hours of incubation with 10 ng / mL TGF-β to induce fibrotic and hyperproliferative changes. a) MTT assay shows antiproliferative effect. Mesangial cells showed significant hyperproliferation upon TGF-β stimulation, but pre-incubation with free CCG or CCG-loaded NP significantly reduced this effect. b) Western blot analysis of both α-SMA and c) collagen I levels showed a dramatic reduction in both fibrosis markers for CCG or CCG-loaded NP compared to TGF-β control (n=3;****P<0.0001;***P<0.001;ns not significant). d) LSM analysis further supported the results from b), showing that mesangial cells exhibited significantly reduced α-SMA production upon pre-incubation with CCG or CCG-containing NPs. Scale bar = 2 μm. [Figure 32-2] Same as above. [Modes for carrying out the invention]

[0097] In the following, references are made to the examples given, not to limit the present invention, but to illustrate it. [Examples]

[0098] (Example 1) material and method cell culture The cell lines used in this study were cultured at 37°C and 5% CO2. rMCs, NCI-H295R, and HeLa cells were cultured in RPMI1640 medium (Sigma Aldrich) supplemented with 10% FBS, insulin-transferrin-selenium, and 100 nM hydrocortisone. HK-2 cells were maintained in DMEM-F12 (1:1) medium (Sigma Aldrich) supplemented with 10% FBS. pAT1R-rMCs were obtained by transfecting rMCs with a plasmid encoding AT1R with a YFP tag (CXN2-HA-AT1R-YFP) (see [4]) using the commercially available transfection reagent Lipofectamine 2000 according to the manufacturer's instructions. pAT1R-rMCs were cultured in RPMI1640 medium supplemented with 10% FBS and 600 μg / ml Geneticin (G418). The cell lines were characterized for their target AT1R and ACE expression, as previously shown [1, 3].

[0099] mouse Experimental procedures involving animals were carried out in accordance with national and institutional guidelines and approved by local authorities (Regierung von Unterfranken, reference number: 55.2-2532-2-329). The mice listed in the Key Resources Table were used in this study at 10 weeks of age. Only female mice were used in all experiments. These mice were maintained in a specific pathogen-free (SPF) containment facility under standard conditions (relative humidity of 50±5%, temperature of 21±1℃, air exchange >8AC / hour, and 12 hours:12 hours (L:D) of light).

[0100] Polymer preparation: Block copolymer synthesis PEG-PLA block copolymer (COOH-PEG 2k -PLA 10k COOH-PEG 5k -PLA 10k NH2-PEG 5k -PLA 10k and MeO-PEG 5k -PLA 10k ) was synthesized via ring-opening polymerization of cyclic 3,6-dimethyl-1,4-dioxan-2,5-dione (lactide). In short, lactide was recrystallized from anhydrous ethyl acetate before use and dried under vacuum at 40°C for 12 hours at room temperature (rt). COOH-PEG 5k -OH, COOH-PEG 2k -OH, Boc-NH-PEG 5k -OH or MeO-PEG 5k -OH was used as a macroinitiator for ring-opening polymerization. These were dissolved in anhydrous DCM (0.3 mmol) and mixed with purified lactide (18 mmol). 1,8-Diazabicyclo[5.4.0]undeca-7-ene (DBU) (0.9 mmol) was added as a catalyst. Polymerization was quenched with benzoic acid (4.6 mmol) after 1 hour. The resulting polymer was precipitated in diethyl ether and incubated at 40°C for 12 hours (COOH-PEG). 2k -PLA 10k COOH-PEG 5k -PLA 10k and MeO-PEG 5k -PLA 10k (Regarding) or 35℃ (Boc-NH-PEG 5k -PLA 10k The mixture was dried under vacuum. To cleave the Boc protecting group, Boc-NH-PEG-PLA was dissolved in 50% (v / v) TFA / DCM and stirred at rt for 30 minutes. This was then diluted to 3 times the volume of DCM and washed three times with saturated sodium bicarbonate solution. The organic phase was dried over anhydrous sodium sulfate, filtered, and concentrated under reduced pressure. The resulting NH2-PEG 5k -PLA 10kThe solution was purified by precipitation in diethyl ether and subsequently dried under vacuum at 35°C for 12 hours.

[0101] Polymer preparation: Ligand coupling For the preparation of the Ang-I modified polymer (see also Figure 8), 14 μmol of COOH-PEG was used. 5k -PLA 10k The polymer was activated for 2 hours with a 25 molar excess of EDC and NHS in DMF. The reaction was then quenched for 20 minutes with the addition of 863 μmol of 2-mercaptoethanol, followed by the dropwise addition of 66 μmol of DIPEA and 17 μmol of Lys-Ang-I in DMF. After 48 hours, the resulting polymer was diluted in ultrapure water (Millipore) to a DMF concentration of less than 10% and dialyzed over 24 hours (with medium changes at 30 minutes, 2 hours, and 6 hours) using a 6-8 kDa molecular weight cutoff regenerated cellulose dialysis membrane to remove unreacted ligands and reagents. For the preparation of the polymer modified with EXP3174 (see also Figure 8), 96.4 μmol of EXP3174 was activated for 2 hours with equimolar amounts of DCC and NHS in DMF. Subsequently, the obtained urea byproduct was removed by centrifugation (5 minutes, 12,000 × g) and subsequent filtration using a 0.2 μm Rotilabo PTFE syringe filter. 27.6 μmol of NH2-PEG in DMF. 5k -PLA 10kAnd 17.5 molar excess DIPEA was added to the activated ligand and reacted for 20 hours. The ligand-modified polymer was purified to remove excess free ligand by precipitation in ice-cold 1:5 (v / v) diethyl ether:methanol and subsequent 24-hour dialysis in 10 mM borate buffer (pH 8.5) with 10% ethanol (with medium changes at 30 minutes and 6 hours), and then dialyzed against ultrapure water to remove buffer salts using a 6-8 kDa molecular weight cutoff regenerated cellulose dialysis membrane (Spectrum Laboratories) over 24 hours (with medium changes at 30 minutes, 2 hours, and 6 hours). The ligand-modified block copolymer was freeze-dried for 72 hours before ligand coupling confirmation. For this purpose, the polymer was solubilized in ACN at a concentration of 40 mg / ml and precipitated in stirred ultrapure water to create polymer micelles (final concentration 1 mg / ml). PEG content was quantified using a colorimetric iodine complex formation assay, and coupled Ang-I was quantified using a Pierce BCA assay kit according to the manufacturer's instructions, using a FLUOstar Omega microplate reader. EXP3174 was quantified using an LS-5S fluorescence plate reader, λ ex =250nm and λ em Quantitative fluorescence analysis was performed at 370 nm. NH2-PEG 5k -PLA 10k The absence of the unreacted NH2-terminal group was determined using fluorescein (see also Figure 8).

[0102] Polymer preparation: Fluorescent labeling of PLGA For in vitro and in vivo particle detection, fluorescently labeled PLGA was used in the particle core. For this purpose, TAMRA-amine (for CLSM) and CF6467-amine (for flow cytometry and in vivo experiments) were covalently coupled to carboxylic acid-terminated 13.4 kDa PLGA. Briefly, 5 μmol of acid-terminated PLGA was dissolved in anhydrous DMF and activated at rt for 2 hours with 129 μmol of DMTMM (25-fold excess). Then, 1 μmol of fluorescent dye dissolved in DMF was added dropwise to the PLGA and reacted at rt in the dark for 72 hours. The reaction product was diluted (DMF < 10%) and dialyzed against ultrapure water over 34 hours (with medium changes at 30 minutes, 2 hours, and 6 hours) using a 3.5 kDa molecular weight cutoff regenerated cellulose dialysis membrane (Spectrum Laboratories) under light shielding. The fluorescently labeled PLGA was then freeze-dried for 3 days.

[0103] NP preparation and characterization: Particle preparation For NP preparation, PEG-PLA block copolymer and 13.4 kDa PLGA were mixed in a mass ratio of 70:30 to a final concentration of 10 mg / mL in ACN. COOH-PEG was used for ligand-modified particles. 2k -PLA 10k The polymers modified with ligands were mixed appropriately so that 20% of the polymer constituting the NP structure was modified with Ang-I (NPAng-I) and / or EXP3174 (NPEXP and NPECPAng-I, respectively). The NPs were prepared to a final concentration of 1 mg / ml by bulk nanoprecipitation of the polymer mixture in vigorously stirred 10% DPBS (v / v) (pH 7.4). The particles were stirred for 2 hours to ensure evaporation of the organic solvent, and concentrated by ultracentrifugation at 756 g for 20 minutes using a 30 kDa molecular weight cutoff Microsep advanced centrifuge (Pall Life Sciences).

[0104] Preparation and characterization of NPs: dynamic light scattering and zeta potential The size and zeta potential of the obtained particles were determined in 10% PBS at a constant temperature of 25°C using a ZetaSizer Nano ZS (Malvern Instruments) equipped with a 633 He-Ne laser at a backscattering angle of 173° and Malvern Zetasizer software version 7.11, at concentrations of 1 mg / mL or 3.5 mg / mL, respectively. The cuvette position was set to 4.65 mm, and the attenuator was automatically optimized by the device. Disposable micro-cuvets (Brand) and folding capillary cells (Malvern Instruments) were used for size and zeta potential measurements, respectively.

[0105] Preparation and characterization of NPs: Particle quantification The particle PEG concentration was quantified using a colorimetric iodine complex formation assay and correlated with the gravimetric NP content determined via lyophilization. Briefly, particle samples were diluted in ultrapure water to PEG concentrations ranging from 5 to 30 μg / mL. Dilutions of MeO-PEG-OH in ultrapure water (0 to 40 μg / mL) were used as standards for the calibration curve. 140 μL of sample or standard was mixed with 60 μL of a 2:1 (v / v) mixture of 5% (m / v) barium chloride solution in 1N HCl and 0.1N iodine aqueous solution. The samples and standards were transferred to 96-well plates, and their absorbance at 535 nm was measured using a FUOstar microplate reader (BMG Labtech). The correlation between particle PEG content and precise polymer concentration was determined gravimetrically after sample lyophilization. The particle concentration in molar concentration was determined by a colorimetric iodine complex formation assay, and the particle mass and density (1.25 g / cm³) were also determined. 3 ), and the hydrodynamic diameter of the NP obtained via DLS measurements assuming a spherical particle shape were calculated. Ligand concentrations on the particle corona were quantified fluorescenceically for Ang-I and EXP3174, respectively, using the BCA assay as described above.

[0106] Intracellular calcium measurement To evaluate the AT1R interaction of different NP formulations, proportional measurement of Fura-2Ca 2+ The chelator method was used with AT1R-positive rMCs as previously described [1, 3]. For this purpose, rMCs were seeded in T-150 flasks (Corning) and incubated until confluent. Subsequently, they were trypsinized, centrifuged (200 g, 5 min), and resuspended in Leibovitz medium supplemented with 5 μM Fura-2, AM (Thermo Fisher), 0.05% Pluronic F-127, and 2.5 mM probenecid. Cells were incubated for 1 hour with gentle stirring (50 rpm) and photoprotected. The cell suspension was then washed with DPBS by centrifugation (2 ×, 200 g, 5 min, RT) and resuspended in Leibovitz medium supplemented with 2.5 mM probenecid at a count of 2 million cells / mL. To determine particle avidity and ligand affinity for AT1R (Figures 3A-C), 45 μl of rMC (90,000 cells / well) loaded with Fura-2 in suspension was incubated with 10 μL of different samples (NP, or free ligands ranging from 1 nm to 300 μM (ligand concentration)) in a 96-well half-area microplate for 30 minutes at rt. The cells were then stimulated with 45 μL of 300 nM Lys-Ang-II aqueous solution, and the resulting calcium signal was immediately recorded over 1 minute / well using a FLUOstar Omega microplate reader (BMG Labtech) with excitation at 340 / 20 nm and 380 / 20 nm and emission bandpass filters at 510 / 20 nm. To determine the dynamics of AT1R interaction (Figure 3D), the same procedure was used, but the samples were incubated with the cells for different durations (5–320 minutes). The maximum and minimum signal ratios were determined by stimulating cells with either 0.1% Triton-X 100 or 0.1% Triton-X 100 combined with 45 mM ethylene glycol-bis(2-aminoethyl ether)-N,N,N',N'-tetraacetic acid (EGTA), respectively. Intracellular calcium concentration was determined by stimulating cells with 225 nM K dThe values ​​were calculated after Grynkiewicz, assuming the values. Statistical significance was assessed using GraphPad Prism 6.0 via Student's t-test (Figure 3C) and two-way ANOVA with Sidac's multiple comparisons (Figure 3D).

[0107] Dynamic measurement of enzymes The Michaelis-Menten kinetics for NPAng-I and NPEXPAng-I were determined as previously described [1] using rabbit lung ACE (Sigma Aldrich) as a soluble substitute for the cell membrane-binding enzyme. Briefly, different concentrations of NP (corresponding to 10–120 μM Ang-I) were incubated with 18 μM of the enzyme for different durations (5, 15, 30, 60, 90, and 120 minutes) to convert Ang-I on particle corona to Ang-II, the ligand for AT1R activity. The resulting Ang-II was quantified by direct intracellular calcium assay. For this purpose, rMCs were loaded with Fura-2 dye as described above. Ten μL of the sample was then pipetted onto 96-well half-area plates, and 90 μL of Fura-2-loaded rMC suspensions (90,000 cells / well) were injected onto them. The obtained calcium signal was recorded immediately for 1 minute using a FLUOstar Omega microplate reader (BMG, Labtech) as described above. NPEXP was used as a control to eliminate interference from the EXP3174 ligand to NPEXPAng-I under the experimental conditions used (see Figure 9). rMCs (90,000 cells / well) were simultaneously stimulated with different NPEXP concentrations and Lys-Ang-II (400 nM), and the obtained calcium signal was recorded immediately for 1 minute. The measured calcium concentration was converted to pmol of the hydrolyzed product using free Lys-Ang-II at known concentrations ranging from 1 nm to 300 μM. The reaction rate (pmol / min) during a 15-minute incubation time was plotted against the substrate concentrations used in the assay using a GraphPad Prism 6.0 to determine the Michaelis-Menten constant (Km) for particle-based and ligand-based concentrations (Figure 3E). To calculate the specificity constant (Kcat / Km) used to compare different substrates for the same enzyme, the catalytic constant (Kcat) was obtained using the same software (Figure 3F). Statistical significance (Figure 3F) was assessed using GraphPad Prism 6.0 via two-way ANOVA with Tukey's multiple comparison test.

[0108] Cellular distribution of NPs: Confocal microscopy To determine the cell distribution of different particle formulations (Figure 4), pAT1R-rMCs were seeded at a density of 10,000 cells / well in 8-well μ-slides (Ibidi, Graefelfing, Germany) and incubated for 24 hours (37°C). These were then incubated for 15, 45, or 90 minutes with a pre-warmed NP solution (0.2 mg / ml) in Leibovitz medium (LM) supplemented with 0.1% bovine serum albumin (BSA). The NP was then discarded, the cells were thoroughly washed with DPBS, and then stained with 1× CellMask® Deep Red Plasma Membrane Stain for 5 minutes, followed by fixation with 4% paraformaldehyde (PFA) in DPBS for 10 minutes at rt. Images were acquired using a Zeiss LSM 700 microscope with a focal plane set to 1.4 μm using Zen software (Carl Zeiss Microscopy). To inhibit particle uptake and binding, cells were pre-incubated with 1 mM free EXP3174 or captopril before particle addition. Images were analyzed using Fiji software.

[0109] Cellular distribution of NPs: Flow cytometry Analysis of particle uptake via flow cytometry (Figure 5A) was performed as previously described [1]. Briefly, rMCs were seeded at a density of 30,000 cells / well in 24-well plates and incubated for 48 hours (37°C). Pre-warmed NP solution (0.7 mg / ml in LM supplemented with 0.1% BSA) was pipetteed onto the cells, washed with DPBS, and incubated at 37°C for 45 minutes. To confirm uptake specificity, cells were incubated with 1 mM captopril and / or EXP3174 for 30 minutes prior to particle addition. The particle solution was then discarded, cells were thoroughly washed with DPBS, trypsinized, and centrifuged (2×, 200 g for 5 minutes, 4°C). NP-related cell fluorescence was analyzed in DPBS using a FACS Calibur cytometer (Becton Dickinson). Fluorescence was excited at 633 nm and recorded using a 661 / 16 nm bandpass filter. The viable cell population was gated using Flowing software 2.5.1 (Turku Centre for Biotechnology), and the geometric mean of NP-related fluorescence was analyzed. Statistical significance (Figure 5A) was assessed via Student's t-test using GraphPad Prism 6.0.

[0110] NP target cell specificity: Flow cytometry To evaluate NP uptake in different cell lines (Figure 5B), rMC, HK-2, and HeLa cells were seeded in 24-well plates at densities of 30,000, 50,000, or 100,000 cells / well, respectively, and incubated for 48 hours (37°C). Subsequently, pre-warmed NP solution (0.7 mg / ml in LM supplemented with 0.1% BSA) was added to the cells as described above and treated. Statistical significance (Figure 5B) was assessed using GraphPad Prism 6.0 via two-way ANOVA with Sidac's multiple comparison test.

[0111] Particle specificity in co-cultures of target and off-target cells was investigated via flow cytometry, as previously described [1] (Figure 5C-D). Briefly, CTG-stained rMCs (10 μM in serum-free medium, 30 minutes, 37°C) were seeded in co-culture with unstained off-target NCI-H295R or HeLa cells at densities of 10,000 and 75,000 cells / well in 24-well plates, respectively, and incubated for 48 hours. A warm NP solution at a concentration of 0.02 mg / ml in LM supplemented with 0.1% BSA was subsequently added over the cells and incubated at 37°C for 45 minutes. The particles were then discarded as described above, and the cells were processed for flow cytometry analysis. Statistical significance was assessed via Student's t-test using GraphPad Prism 6.0.

[0112] NP target cell specificity: Confocal microscopy To confirm the flow cytometry experiment, CLSM analysis of particle specificity in co-culture (Figure 5E and Figure 13) was performed as previously described [1]. Briefly, target CTG-stained rMCs (10 μM, 30 min, 37°C) were seeded in co-culture with CTDR-stained off-target HeLa or NCI-H295R cells (25 μM, 30 min, 37°C) at densities of 2,000 and 10,000 cells / well, respectively, and incubated for 24 hours. Subsequently, the cell nuclei were stained with Hoechst 33258 (5 μg / ml in DPBS) for 20 minutes, and a pre-warmed 0.02 mg / mL NP solution in LM supplemented with 0.1% BSA was pipetteed onto the cells and incubated for 45 minutes. The NP solution was then discarded, the cells were thoroughly washed with DPBS, and fixed with 4% PFA in DPBS for 10 minutes (rt). As described above, images were acquired and analyzed using a Zeiss LSM 700 microscope and Fiji software, respectively.

[0113] In vivo NP kidney distribution To evaluate the renal distribution of different NP formulations (NPEXPAng-I, NPAng-I, NPEXP, and NPMeO), 100 μL of 120 nM NP solution (equivalent to approximately 10 mg / ml of NP) was injected via jugular vein into 10-week-old female NMRI mice (Charles River) anesthetized with isoflurane inhalation and buprenorphine (0.1 mg / kg body weight) (n=6 for each particle sample). Additionally, as a control, 100 μL of the free dye (CF647) used to fluorescently label the particles was injected at the same concentration (approximately 50 μM) as that included in the particle samples. After 5 minutes, blood samples were collected via iv puncture, while the mice were still anesthetized. After 1 hour of particle circulation, the mice were anesthetized with ketamine / xylazine, final blood samples were collected, and the mice were sacrificed via perfusion fixation with 4% PFA. The kidneys were retrieved, transversely dissected, and cut. These were cryoprotected by placing them overnight in phosphate buffer (0.1M pH 7.4) supplemented with 18% sucrose and 1% PFA. They were then frozen in 2-propanol cooled with liquid nitrogen (-40°C) and embedded in Tissue Tek® OCT® Compound for frozen sections. The kidneys were sectioned into 5 μm sections using a CryoStar NX70 cryostat (Thermo Fisher Scientific) and transferred to Superfrost® Plus glass slides. For better visualization, cell nuclei were stained with DAPI (12.5 μg / ml in DPBS) before section imaging using an Axiovert 200M (Zeiss) fluorescence microscope and Zen software (Zeiss). Whole kidney images were acquired using a 10× objective lens (Figure 6). To quantify glomerular fluorescence, images were acquired using a 40× objective lens (average of 120 glomeruli per sample) and analyzed using Fiji software (Schneider et al., 2012). For better visualization, the "Red Hot" lookup table was applied to particle-related fluorescence. The area of ​​each glomerulus was quantified, and the fluorescence area was gated. Then, the integrated fluorescence density of each gated area was quantified and correlated with the total glomerular area.Statistical significance was assessed via Student's t-test using GraphPad Prism 6.0. To compare particle-associated fluorescence in the inner and outer cortex, the cortex was split into two equal sections, and glomerular fluorescence was analyzed as described above. Two-way ANOVA with Sidac's multiple comparison test was performed using GraphPad Prism 6.0 to assess statistical significance.

[0114] NP-related fluorescence in plasma was measured using a FLUOstar Omega microplate reader (BMG Labtech) with excitation and emission wavelengths of 640 nm and 680 nm, respectively. Fluorescence one hour after injection was correlated with the initial fluorescence of the sample obtained five minutes after injection.

[0115] immunohistochemistry To evaluate the glomerular localization of NPs, freshly cut 5 μm frozen kidney sections were washed with DPBS for 5 minutes, washed with DPBS supplemented with 0.1% sodium dodecyl sulfate (SDS) for 5 minutes, washed with DPBS for 5 minutes, and then blocked for 10 minutes with 5% BSA in DPBS supplemented with 0.04% Triton-X (m / v). The sections were washed again with DPBS (for 5 minutes) and incubated overnight at 4°C in a 1:200 solution of primary polyclonal goat anti-integrin-α8 antibody in DPBS supplemented with 0.5% BSA and 0.004% Triton-X (m / v). These were then washed in DPBS for 5 minutes and incubated with Cy2-anti-goat secondary antibody (1:400) and DAPI (12.5 μg / ml) in DPBS supplemented with 0.5% BSA and 0.04% Triton-X for 1 hour in the dark at rt. The frozen sections were washed with DPBS and ultrapure water, then mounted using Dako Faramount mounting medium, and analyzed using a Zeiss LSM 700 microscope and Fiji software as described above.

[0116] Quantification and statistical analysis Statistical analysis was performed using GraphPad Prism software 6.0. Statistical significance was assessed using Student's t-test or two-way ANOVA with Sidac or Tukey's multiple comparison test, as detailed in the methods section. The level of statistical significance and the number of "n" for each experiment are indicated in the text and figure captions.

[0117] (Example 2) Block copolymers enable the design of virus-mimicking particles. All materials and methods mentioned in this embodiment were as described in the previous embodiment.

[0118] For the development of virus-mimicking NPs, the inventors coupled ligands EXP3174 and Ang-I to poly(ethylene glycol) 5k-poly(lactic acid) 10k (PEG-PLA) block copolymer (Figure 8), which was then blended with poly(lactic acid-co-glycolic acid) PLGA for NP production via bulk nanoprecipitation, giving the particles sufficient in vivo stability. The remaining unfunctionalized polymer was PEG-PLA (COOH-PEG2k-PLA10k), which has shorter 2k PEG and 10k PLA blocks ending in a carboxylic acid (Figure 1A). Precise control of ligand density can be obtained by modifying the polymer with ligands before NP preparation. Particles were prepared so that 20% of their PEG chains were modified with Ang-I and a further 20% were modified with EXP3174 (NPEXPAng-I) (Figure 2B). Ligand density was maintained at a maximum of 40% to avoid steric hindrance and nonspecific interactions between ligands. For control, we assembled methoxy-PEG-terminated particles without ligands (NPMeO) and particles with either 20% Ang-I or EXP (NPAng-I and NPEXP, respectively) (Figure 1A). By combining polymers with longer ligands with shorter, unfunctionalized polymers for particle preparation, we were able to maintain the NP size below 80 nm and provide particles with the ability to pass through the endothelial window of mesangial capillaries (Figure 2C). Carboxylic acid-terminated block copolymers were selected as fillers to provide an ideal overall negative particle charge to avoid nonspecific electrostatic adsorption to the negative cell membrane (Figure 2D).

[0119] (Example 3) NPs recognize target receptors in vitro. All materials and methods mentioned in this embodiment were as described in the previous embodiment.

[0120] To confirm the ability of the particles to triple-check, the identity of the cells was first evaluated in vitro. Particle avidity to target receptors, which mediates primary adhesion and subsequent internalization, was investigated using a calcium mobilization assay, which showed that stimulation or silencing of Gq-coupled AT1R by an agonist or antagonist, respectively, affected cytosolic Ca 2+ This is because it results in either influx or inhibition. For this purpose, AT1R-positive rat mesangial cells (rMCs) were incubated with either a free ligand or an NP formulation at varying concentrations for a period of 30 minutes prior to stimulation with Ang-II, and the resulting calcium signals were recorded. As shown in Figure 3A, control experiments with free EXP3174 and Ang-II revealed high affinity for AT1R in the nanomolar concentration range (IC50 values ​​of 0.6±0.4 and 1.5±0.1 nM, respectively). Since receptor binding and activation occur only after enzymatic conversion to Ang-II by ACE present in the cell membrane, Ang-I exhibits lower affinity (IC50 0.9±0.6 μM).

[0121] Coupling to the linker results in affinity loss compensated by simultaneous high avidity polyvalent binding of several receptors (Figures 3B and 3C). Since their primary interaction is with ACE, particles containing only Ang-I (NPAng-I) exhibit lower avidity to AT1R (IC50 of 9.4 ± 0.4 nM) than particles containing EXP3174 (IC50 of 0.4 ± 0.1 nM). Nevertheless, particle binding of Ang-I results in a significant decrease in IC50 value compared to the free ligand, due to enhanced enzymatic cleavage at the NP interface and subsequent polyvalent binding. NPs modified with EXP3174, in contrast, exhibited avidity of the same order of magnitude as those with the free ligand. Surprisingly, particles NPEXPAng-I, possessing both ligands, showed a synergistic effect with respect to receptor binding, as they exhibited significantly higher avidity (IC50 of 0.2 ± 0.09 nM) against AT1R than any of the particles possessing only one type of ligand (Figure 3C). This demonstrates that these ligands do not interfere with each other's interaction, as both ligands target the same receptor in simultaneous agonist and antagonistic modes after enzymatic activation of Ang-I to Ang-II. Particles without any functionalization (NPMeO) elicited no response whatsoever, confirming that the assay was ligand-specific (Figure 3B).

[0122] To evaluate the dynamics of cell / particle interactions, intracellular calcium measurements were performed over a 5.5-hour period by incubating NP at concentrations corresponding to 10 μM ligand with rMC. The extent to which these free agonists could silence calcium signaling served as a measure of the completeness of each particle's binding to AT1R on the cell surface via their ligand at different time points (Figure 3D). Particles with only Ang-I on their surface showed slow receptor binding, because they first need to be activated into Ang-II-containing particles by cell membrane-bound ACE before they can interact with AT1R. Receptor binding reached a maximum of approximately 40% after 1 hour incubation and remained constant throughout the duration of the assay. This indicates rapid internalization of particles when a certain number of proligands are activated, and presumably not all Ang-I is converted to Ang-II. When Ang-II on the particle surface binds to the receptor, the particles are rapidly internalized (as they possess picomolar AT1R avidity [1]), meaning that not all proligands may need to be activated for NP internalization to occur. This phenomenon is avoided when EXP3174 is added as an adhesion factor on the particle surface. Very rapid and complete receptor blockade occurs after only 5 minutes of particle incubation (similarly for NPEXXAng-I and NPEXP). AT1R inhibition is maintained for almost the entire duration of measurement, decreasing to about 80% at the final point, likely due to receptor upregulation and recycling. Adhesion to the cell membrane by EXP3174 slows the recognition process and allows for higher activation from Ang-I to Ang-II, which can bind more efficiently to AT1R. Comparing NPEXXAng-I and NPEXP, there is a significantly higher initial AT1R inhibition in NPEXXAng-I, which becomes constant after 45 minutes of particle incubation. This is likely due to the combined effect of the two ligands, resulting in higher avidity against AT1R (Figure 3C).

[0123] A prerequisite for particle internalization is the ability of ACE to activate Ang-I to Ang-II. Therefore, the inventors investigated the enzyme kinetics of NPEXPAng-I to determine whether the presence of an antagonist on the particle surface interferes with the enzymatic reaction. The soluble form of ACE was incubated over varying periods with different particle concentrations, and the resulting Ang-II on the NP corona was quantified by performing a calcium recruitment assay. Interference of the EXP3174 ligand in the assay was evaluated by measuring the signal inhibition exhibited by NPEXP (Figure 9). The Michaelis-Menten constants (Km) determined for both NPAng-I and NPEXPAng-I (Figure 3E) yielded values ​​of the same order of magnitude for both particle formulations as for the free ligand (see [1]). Furthermore, the inventors determined the catalytic constant (Kcat) and calculated the specificity constant (Kcat / Km), which is a useful indicator for comparing the affinity of different substrates to the same enzyme (Figure 3F). Enzymatic activation of Ang-I on the NPEXPAng-I corona was not significantly different from that on NPAng-I, indicating that ACE is not sterically inhibited by the additional ligand EXP3174. Furthermore, the Kcat / Km values ​​calculated based on ligand concentration were equal for free Ang-I and particle-bound Ang-I. Moreover, when Kcat / Km is calculated based on NP concentration, the bound ligand is a significantly better substrate for the enzyme, which is a result of the binding of several ligand molecules on the particle surface to several enzyme molecules (Figure 3F).

[0124] (Example 4) Decision execution NPs are target cell specific. All materials and methods mentioned in this embodiment were as described in the previous embodiment.

[0125] After successfully establishing particle interactions with their individual targets, the next step was to determine whether NPs with antagonists and agonists on their corona still induce internalization by their target cells, and, if so, whether uptake follows specific ligand-receptor interactions. Since antagonists do not induce AT1R-mediated endocytosis, while agonists do, we investigated the cellular localization of NPEXPAng-I in rMCs expressing YFP-tagged AT1R (pAT1R-rMCs) via confocal laser scanning microscopy (CLSM). As shown in Figure 4, NPEXPAng-I-associated fluorescence was found inside the cells. This increased with longer incubation times and strongly co-localized with AT1R fluorescence.

[0126] Therefore, specific particle uptake mediated by AT1R exists. However, particles containing only the antagonist (NPEXP) are not internalized by the cell and are mostly located on the cell surface (Figure 10A). Particle fluorescence co-localizes with receptor fluorescence, demonstrating receptor-mediated adhesion. NPAng-I was also internalized by the cell (Figure 10B), so the enzymatically produced Ang-II mediates the cellular uptake of NPEXPAng-I. Unexpectedly, with increasing incubation time, there is a rearrangement of receptors on the cell membrane, from a more diffused, uniform distribution on the cell membrane (after 15 minutes) to a more concentrated clustering (at 90 minutes) (Figure 4), which strongly co-localizes with NP fluorescence. This provides further evidence that uptake is mediated by AT1R, because activation of GPCRs such as AT1R, which are internalized via clathrin-coated pits, promotes receptor clustering.

[0127] In the case of NPEXP, receptor rearrangement occurs on the cell membrane, which is a result of multivalent receptor binding facilitated by receptor migration on the cell surface. When NPEXP attaches to receptors on the cell membrane, the lack of their internalization can lead to receptor-particle mobility and even receptor binding on the cell membrane. Ligand-free particles (NPMeO) are not taken up by cells (Figure 10C), confirming that the specific targeting mechanism is essential for mediating high intracellular internalization.

[0128] Overall, the inventors demonstrate that the presence of adhesion-mediated antagonistic ligands linked to the particle corona does not interfere with subsequent particle internalization. Furthermore, including additional ligands on the particle surface compensated for loss of targeting due to steric hindrance of Ang-I ligands by the addition of more long polymer chains (Figure 11). To further confirm particle specificity and ligand-mediated internalization, cells were pre-incubated for 30 minutes before particle addition with free EXP3174 or captopril, an ACE inhibitor that suppresses particle-associated fluorescence, and analyzed by flow cytometry (Figure 5A) and CLSM (Figure 12).

[0129] Furthermore, the inventors tested particle internalization in different cell lines by flow cytometry (Figure 5B). HeLa cells that do not express ACE but express only trace levels of AT1R showed low particle uptake, which was nonspecific as it could not be suppressed by either captopril or EXP3174. In contrast, rMC and HK-2 cells expressing both targets were able to take up particles, as indicated by much higher particle-associated cell fluorescence. Pre-incubation of cells with captopril or EXP3174 significantly suppressed cell fluorescence, so internalization was also mediated by activated proligand binding to AT1R. Thus, particles exhibit high specificity for their target cells. Nevertheless, when NPs enter the body, they present both target and off-target cells simultaneously. Therefore, the inventors investigated whether NPEXPAng-I could distinguish between them.

[0130] Target cells (rMCs) were seeded with an excess of off-target NCI-H295R or HeLa cells, both of which lacked ACE and expressed high and low AT1R levels, respectively. These were incubated with different NP formulations, and each cell line was investigated for particle-associated fluorescence via flow cytometry (Figure 5C-D). NPEXPAng-I accumulated significantly more in target rMCs, demonstrating outstanding target cell specificity. NPAng-I also showed low accumulation in both off-target cells, indicating that specificity is conferred by Ang-I. In contrast, NPEXP bound to the cell surface in rMCs to the same extent as in NCI-H295R cells expressing high AT1R levels, demonstrating that a simple one-step recognition process is not sufficient to confer particle selectivity. CLSM imaging confirmed the flow cytometry findings (Figures 5E and 13), where NPEXPAng-I and NPAng-I fluorescence (red) were largely associated with targeted rMCs (green) but not with off-target HeLa or NCI-H295R cells (white), while NPEXP fluorescence was found in both rMCs and AT1R-expressing NCI-H295R cells. Taken together, these results demonstrate that NPEXPAng-I uptake is receptor-mediated and that initial cell adhesion via EXP3174 ligand does not reduce particle specificity to target cells conferred by the viral-mimicking recognition process.

[0131] (Example 5) NPs target MCs in vivo. All materials and methods mentioned in this embodiment were as described in the previous embodiment.

[0132] Since the complementary targeting ability and particle specificity of both ligands on NPEXPAng-I were demonstrated in vitro, the next step was to determine whether the virus recognition principle would result in higher in vivo MC accumulation. To that end, targeted particle formulations (NPEXPAng-I, NPAng-I, and NPEXP) (Figure 1A) and an untargeted particle formulation (NPMeO) were injected into NRMI mice, and frozen kidney sections were tested for particle-associated fluorescence (Figures 6 and 14A). As shown in Figure 6A, NPEXPAng-I fluorescence could be found uniformly across all glomeruli in the kidney section, and no fluorescence was found in other kidney structures such as the renal tubules. In contrast, for untargeted NPMeO, NP fluorescence was barely detectable in the kidney section (Figure 6B). This demonstrates that simple size-dependent targeting is not sufficient to achieve particle accumulation in MCs, which is because NPMeO is likely cleared from the mesangium due to a lack of specific cell interactions. Furthermore, NPEXP, a targeted NP that cannot mediate intracellular relocation, also exhibits very slight glomerular fluorescence (Figure 14A), demonstrating that particle uptake is important for achieving high MC accumulation. Moreover, NPEXPAng-I achieves a much stronger and more uniform glomerular distribution than NPAng-I lacking adhesion factors (Figure 14A), indicating that the enhanced target cell recognition principle in vivo is highly advantageous.

[0133] To quantitatively evaluate NP-related fluorescence and better distinguish differences between different particle formulations, glomerular images were acquired at higher magnification (Figure 7A). Quantitative analysis of glomerular fluorescence showed that the virus-mimicking particle with an enhanced recognition mechanism (NPEXPAng-I) produced 15 times higher fluorescence compared to the untargeted control particle (NPMeO), which showed only small fluorescence spots in some glomeruli.

[0134] Furthermore, NPEXPAng-I showed significantly higher accumulation than single-ligand targeted particles (7-fold and 5-fold higher than NPEXP and NPAng-I, respectively) (Figure 7B). The particle-related nature of the detected fluorescence was confirmed by the renal distribution of the free dye (CF647) used for particle labeling, which showed strong tubular fluorescence but no glomerular fluorescence due to its small size which allows it to be freely filtered (Figure 14B). To assess the glomerular distribution of NP, glomerular fluorescence in the outer and inner cortex was compared (Figure 7C). No significant differences existed between the two populations for all particle formulations. This indicates that the particles are uniformly distributed throughout the glomeruli of the renal cortex, which is an essential requirement for the treatment of glomeruli-related diseases. Finally, since other cells capable of internalizing NP were present in the glomeruli, separate from the MCs, specific antibody staining of the MCs using integrin-α8 as a marker was performed to elucidate particle accumulation in the MCs. As shown in Figure 7D, NPEXPAng-I fluorescence localizes to the inside of antibody-stained microclavus (MCs), confirming that the particles can not only reach the glomerular mesangium but also be taken up by the MCs.

[0135] Taken together, the results clearly indicate that size-mediated targeting is a necessary condition for reaching the mesangium, but insufficient to achieve particle accumulation in the MC. NP internalization appears essential to evade mesangial clearance, explaining why particles lacking this characteristic (NPMeO and NPEXP) yield the lowest glomerular fluorescence. Implementation of the virus-mimicking recognition principle (NPAng-I) increases NP specificity, resulting in particle uptake that subsequently leads to higher MC accumulation. However, promoting target cell recognition via initial virus-like cell adhesion (NPEXPAng-I) significantly enhances the targeting potential of NPs, which, as shown by in vitro studies, is a result of the combined effect of the two ligands.

[0136] Furthermore, enhanced functionalization of NPEXPAng-I does not result in a reduction in particle blood retention. Generally, NPs are coated with polymers such as PEG, which increases their circulation time and reduces plasma protein adsorption. Off-target cells expressing targeted receptors can bind to and interfere with NPs, thus counteracting the positive effects usually negated by ligand functionalization. Nevertheless, quantification of plasma NP fluorescence one hour after injection showed that NPEXPAng-I remained in circulation to the same extent as untargeted NPMeO and significantly longer than other targeted formulations (Figure 14C). This is likely due to higher particle specificity resulting from a more complex cell recognition process. Overall, these results demonstrate that it is possible to develop NPs that target MCs and accumulate in large quantities within MCs by closely mimicking viral binding and internalization and combining it with an optimal NP size.

[0137] (Example 6) material and method material Heterobifunctional hydroxyl poly(ethylene glycol)carboxylic acid (COOH-PEG) having molecular weights of 2000 and 5000 g / mol 2k / 5k -OH) and hydroxyl poly(ethylene glycol) Boc-amine (Boc-NH-PEG) having a molecular weight of 2000 g / mol 2k -OH) was purchased from Jenkem Technology USA Inc. (Allen, TX, USA), and contains methoxypoly(ethylene glycol) (MeO-PEG) with a molecular weight of 5000 g / mol. 5k-OH) and Resomer RG 502 (PLGA) were obtained from Sigma-Aldrich (Taufkirchen, Germany). EXP3174 (also known as losartan carboxylic acid) was purchased from Santa Cruz (Heidelberg, Germany), while cyclic RGDfK (cRGDfK) was obtained from Synpeptide Co. Ltd. (Shanghai, China). AlexaFluor® 568 Hydrazide (Alexa568), CellTracker® Green Dye (CTG), and CellTracker® Deep Red Dye (CTDR) were purchased from Thermo Fisher Scientific (Schwerte, Germany). Amine-functionalized spherical gold NP (Au) with an average diameter of 2.2 nm. 2.2 -NH2) was obtained from Nanopartz Inc. (Loveland, CO, USA). The GoldEnhance® EM Plus kit was purchased from Nanoprobes (Yaphank, NY, USA). The goat-derived integrin α-8 antibody was obtained from R&D Systems (Minneapolis, MN, USA). All other chemicals were purchased in analytical grade from Sigma-Aldrich unless otherwise stated. Ultrapure water was obtained from Milli-Q water purification systems (Millipore, Billerica, MA, USA). NCI-H295R (CRL-2128) and HeLa (CCL-2) cells were purchased from ATCC (Manassas, VA, USA). All cell lines were cultured in RPMI1640 medium containing 10% fetal bovine serum, insulin-transferrin-selenium (ITS) (1×), and 100 nM hydrocortisone.

[0138] Polymer synthesis COOH-PEG 2k -PLA 10k Boc-NH-PEG 5k -PLA 10k and MeO-PEG 5k -PLA 10kThe block copolymer was synthesized via ring-opening polymerization as previously described. Briefly, a heterobifunctional PEG polymer (1 equivalent) was mixed with 3,6-dimethyl-1,4-dioxane-2,5-dione (70 equivalents) and 1,8-diazabicylo[5.4.0]undec-7-ene (3 equivalents). The polymer mixture was stirred at room temperature (RT) for 1 hour until polymerization was quenched with benzoic acid (14 equivalents). The resulting block copolymer was precipitated in diethyl ether, isolated by filtration, and dried under vacuum. The molecular weight of the synthesized polymer was determined in deuterated chloroform at 295 K using a Bruker Avance 300 spectrometer (Bruker BioSpin GmbH, Rheinstetten, Germany).

[0139] cRGDfK-PEG 2k - For the preparation of PLA polymer, previously synthesized COOH-PEG 2k -PLA 10k This was covalently coupled to the lysine residue of cRGDfK, as previously shown. In short, COOH-PEG 2k -PLA 10k (1 equivalent) was activated at RT for 2 hours with 3-(ethyliminomethyleneamino)-N,N-dimethylpropan-1-amine (EDC) / N-hydroxysuccinimide (NHS) (25 equivalents), and then quenched with β-mercaptoethanol (BME) (30 equivalents). The activated polymer was reacted at RT for 24 hours with cRGDfK (3 equivalents) and N,N-diisopropylethylamine (DIPEA) (10 equivalents). After precipitation of the resulting cRGDfK-coupled polymer in diethyl ether / methanol (15:1 V / V)), free cRGDfK and excess reactants were removed by dialysis against millipore water (mpH2O).

[0140] EXP3174-PEG 5k -PLA 10kFor this purpose, Boc-NH-PEG 5k -PLA 10k The Boc protecting group was first cleaved. Briefly, the Boc-protected polymer was dissolved in dichloromethane (DCM) / trifluoroacetic acid (TFA) (1:1 V / V). After stirring for 30 minutes, the excess TFA was neutralized with a saturated sodium bicarbonate solution. The organic phase was washed with mpH2O, and then the polymer was isolated as described above.

[0141] The resulting NH2-PEG 5k -PLA 10k This was coupled to EXP3174 via the carbonyl residue of the imidazole component. EXP3174 (3.5 equivalents) was activated with N,N'-dicyclohexylcarbodiimide (DCC) / NHS (3.3 equivalents) at RT for 2 hours. After removal of the resulting dicyclohexylurea by centrifugation, NH 2- PEG 5k -PLA 10k (1 equivalent) and DIPEA (17.5 equivalents) were added, and the mixture was reacted at RT for 24 hours. The resulting EXP3174-PEG was obtained. 5k -PLA 10k The product was precipitated in methanol / diethyl ether (1:5 V / V), and the product was dialyzed against ethanol / 100 mM borate buffer pH 8.5 / water (1 / 1 / 8 V / V) for 24 hours, followed by dialyzation against mpH2O for 12 hours to remove unreacted EXP3174 and excess reactants.

[0142] PLGA labeling using fluorescent dyes For particle visualization, core-forming PLGA was covalently linked to a fluorescent dye before NP preparation. For this purpose, carboxylic acid-terminated PLGA was activated for 2 hours using 4-(4,6-dimethoxy-1,3,5-triazine-2-yl)-4-methylmorpholinium chloride (DMTMM) as a catalyst. The activated PLGA was then reacted with either AlexaFluor® 568 Hydrazide or CF® 647 amine at RT for 24 hours. Unreacted fluorescent dye was removed by dialyzing the labeled PLGA against mpH2O for 24 hours.

[0143] PLGA labeling using nanogold For electron microscopy analysis, PLGA was conjugated with nanogold nanoparticles. The PLGA was initially activated for 2 hours in EDC and NHS in DCM. After removal of DCM under reduced pressure, the activated PLGA was dissolved in DMSO and lyophilized monoaminogold nanoparticles (Au) with an average diameter of 2.2 nm. 2.2 It was mixed with (NH2). After stirring at RT for 24 hours, the gold-conjugated PLGA was precipitated in mpH2O, isolated by centrifugation at 2500g for 10 minutes, and freeze-dried.

[0144] NP preparation Block copolymer nanoparticles were prepared using a common solvent evaporation technique. Corresponding amounts of PEG-PLA polymer and PLGA were mixed in a ratio of 70 / 30 (m / m) and diluted in acetonitrile (ACN) to a final concentration of 10 mg / mL. cRGDfK-PEG was used to achieve the desired ligand surface density for hetero- / homo-functional NP species. 2k -PLA and / or EXP3174-PEG 5k -PLA 10k COOH-PEG, according to the calibration shown in Figure 18d / e 2k -PLA 10k The mixture was then added dropwise to 10% Dulbecco's phosphate buffered saline (DPBS) (7.5 mM, pH 7.4) which was vigorously stirred, and the mixture was stirred at RT for 3 hours to remove the organic solvent.

[0145] The obtained NP dispersion was concentrated by centrifugation at 1250 g for 25 minutes using a Pall Microsep filter (molecular weight cutoff 30 kDa; Pall Corporation, NY, USA). To obtain the mass concentration of the prepared NPs, the PEG content was evaluated using a colorimetric iodine complex formation assay. The NPs were then lyophilized and analyzed gravimetrically to obtain the ratio of PEG content to NP weight. In the following experiments, this ratio was used to calculate the mass concentration for each NP species from the evaluated PEG content.

[0146] NP feature identification NP size and zeta potential were evaluated using the Malvern Zetasizer Nano ZS (Malvern, Herrenberg, Germany). Samples were measured in 7.5 mM DPBS using a 633 nm He-Ne laser at a 173° angle (25°C, RT) with either a PMAA semi-micro cuvette (DLS; Brand, Wertheim, Germany) or a folding capillary cell (zeta potential; Malvern, Herrenberg, Germany).

[0147] cRGDfK quantification The level of cRGDfK on the NP surface was evaluated based on arginine measurements. Briefly, 50 μL of NP sample (1 mg / mL) was mixed with 175 μL of a working solution consisting of 9,10-phenanthrenequinone (150 μM in ethanol) and 2N NaOH (6:1 V / V). After incubation at 60°C for 3 hours, one equivalent of the sample was mixed with one equivalent of 1N HCl and incubated for another hour at RT. Finally, fluorescence was measured using a Synergy® Neo2 Multi-Mode Microplate Reader (BioTek Instrument Inc., Winooski, VT, USA) with excitation wavelengths of 312 / 7 nm and emission wavelengths of 395 / 7 nm. Dilutions of cRGDfK (0–40 μg / mL) served as calibration. The molar concentrations of cRGDfK and the ratio of molar cRGDfK content to molar PEG content were determined and plotted against theoretical values ​​(Figure 18d).

[0148] EXP3174 Quantification To determine the surface level of EXP3174 on the fabricated particles, one equivalent of NP sample (1 mg / mL) was mixed with 10 equivalents of 0.2 M acetic acid. Dilution of EXP3174 in 0.2 M acetic acid (0–30 μM) served as calibration. Fluorescence of the sample and standard was measured using a Synergy® Neo2 Multi-Mode Microplate Reader (see above) (excitation 250 / 10 nm, emission 370 / 5 nm). The molar concentration of EXP3174 and the ratio of molar EXP3174 content to molar PEG content were determined and plotted against theoretical values ​​(Figure 18e).

[0149] Calcium mobilization assay To investigate AT1r binding of NPs, intracellular calcium levels were measured using fura-2 Ca 2+Measured using as a chelator. Briefly, rMC was incubated with 5 μM fura-2AM, 2.5 mM probenecid and 0.05% Pluronics F-127 in Leibovitz's L-15 medium at RT for 1 hour. The cells were then centrifuged (5 minutes, 200 g, RT) and resuspended in Leibovitz's medium. 45 μL of NPs or free EXP3174 at different concentrations were pipetted into a 96-well plate (Greiner Bio One, Frickenhausen, Germany), and then 45 μL of the rMC suspension (2×10 6 / mL) was pipetted. Hereinafter, the cells were incubated with the sample at RT for 45 minutes. After incubation, 10 μL of 30 nM AT II was added to each well to activate the un-inhibited AT1r and induce Ca 2+ influx into the cell cytosol as a result. The fluorescence signal during the first 30 seconds after injection was measured using a FluoStar Omega fluorescence microplate reader (BMG Labtech, Ortenberg, Germany) with excitation filters of 340 / 20 nm and 380 / 20 nm and an emission filter of 510 / 20 nm, respectively. The maximum ratio of Ca 2+ -bound Fura-2 to Ca 2+ -unbound Fura-2 was evaluated by incubating the loaded cells with 0.1% Triton-X 100 and measuring the fluorescence levels as described above. Similarly, the minimum ratio was achieved by incubation with 0.1% Triton-X 100 combined with 45 mM ethylene glycol-bis(2-aminoethyl ether)-N,N,N’,N’-tetraacetic acid (EGTA). The level of intracellular calcium per sample was calculated using the equation of Grynkiewicz et al. The half-inhibitory concentration (IC 50 ) was calculated using GraphPad Prism (San Diego, CA, USA) by applying a sigmoid dose-response equation (variable slope).

[0150] CLSM analysis For detailed analysis of NP-cell interactions, rMCs were seeded at a density of 15,000 cells / well in 8-well slides (Ibidi, Graefelfing, Germany) and incubated at 37°C for 24 hours. To facilitate visualization of the cell cytosol, rMCs were stained with CTDR (25 μM, 45 minutes, 37°C) in serum-free RPMI1640 medium prior to seeding. NPs were prepared using PLGA labeled with AlexaFluor® 568 and adjusted to 0.05 mg / mL in Leibovitz buffer supplemented with 0.1% BSA. Mesangial cells were incubated with 250 μL of NP at 37°C for 15, 45, and 90 minutes, washed in pre-warmed DPBS, and fixed in 4% paraformaldehyde (PFA) in DPBS for 10 minutes. After the final washing step, the fixed samples were analyzed using a Zeiss LSM 710 (Carl Zeiss Microscopy GmbH, Jena, Germany).

[0151] Flow cytometry To evaluate mesangial cell association of NP samples, rMCs were seeded at a density of 40,000 cells / well in 24-well plates (Greiner Bio One, Frickenhausen, Germany) and incubated at 37°C for 48 hours. NPs were prepared using PLGA labeled with CF(trademark) 647 and adjusted to 0.05 mg NP / mL in Leibovitz buffer supplemented with 0.1% bovine serum albumin (BSA). The α-adsorption of NPs into cells was evaluated. VTo confirm β3 dependence, 300 μL of free cRGDfK (c=500 μM) was added to the relevant cell samples for 15 minutes prior to NP incubation. Cells were washed with DPBS and 300 μL of pre-warmed NP solution was added at 37°C for 60 minutes. For each analysis of time-dependent uptake, cells were incubated for a period of 120 minutes, and NP was removed at 0, 15, 30, 45, 60, 90, and 120 minutes. Cells were washed with DPBS, trypsinized, and centrifuged at 200 g and 4°C for 5 minutes, followed by two further washing and centrifugation steps (DPBS, 200 g, 5 minutes, 4°C). Final samples were resuspended in DPBS and analyzed using a FACS Calibur cytometer (Becton Dickinson, Franklin Lakes, NJ, USA). NP-related fluorescence was excited at 633 nm, and the corresponding emission was recorded (661 / 16 bandpass filter). Flow cytometry data were analyzed using Flowing software 2.5.1 (Turku Centre for Biotechnology, Turku, Finland). The geometric mean of cell-related fluorescence was evaluated within the population of viable cells.

[0152] Transmission electron microscope To evaluate the cellular localization of NPs, rMCs were seeded in 24-well plates at a density of 12,000 cells / well and incubated for 72 hours. NP formulations containing PLGA conjugated to nano-gold were diluted in Leibovitz buffer containing 0.1% BSA and added at a concentration of 0.05 mg / mL (V=300 μL) for 45 minutes. After incubation, samples were washed with DPBS and prepared for electron microscopy analysis. Briefly, cells were fixed by RT with 2.5% PFA and 2.5% glutaraldehyde in 0.1 M sodium cacodylate solution (Caco buffer) for 60 minutes, washed with Caco buffer, and permeabilized with 0.1% Triton-X in DPBS for 10 minutes. After a washing step with mpH2O, the samples were enhanced with gold using the GoldEnhance® EM Plus kit (Nanoprobes Inc., Yaphank, NY, USA) according to the manufacturer's specifications, then washed again and post-fixed in a 2.5% sodium thiosulfate solution in mpH2O. Cells were stained with 0.5% osmium tetroxide and dehydrated in rinse concentrations of ethanol (50-99.5%). For counterstaining, 2% uranyl acetate was applied at a 70% ethanol concentration for 5 minutes. After embedding in Epon, 150 nm ultrathin sections were imaged using a 100 kV Zeiss Libra 120 electron microscope (Carl Zeiss NTS GmbH, Oberkochen, Germany) at magnifications of 6300 × and 12500 ×.

[0153] Co-culture experiment To evaluate the cell selectivity of the fabricated NPs, the inventors used a co-culture design previously implemented by the inventors. For flow cytometry analysis, rMCs were seeded with HeLa or NCI-H295R cells at densities of 10,000 and 75,000 cells / well in 24-well plates, respectively, and incubated at 37°C for 48 hours. To distinguish between cell types, rMCs were stained with CTG (15 μM, 45 minutes, 37°C) in serum-free RPMI1640 medium prior to seeding. The co-cultured cells were then incubated with NPs labeled with CF®647 at a concentration of 0.05 mg / mL (V=300 μL) for 45 minutes. Sample preparation and flow cytometry analysis were performed as described above. Furthermore, rMC-related fluorescence was excited at 488 nm and recorded using a 530 / 30 bandpass filter. During data analysis, the population of viable cells was further gated against stained rMC cells, and NP-related fluorescence was analyzed in terms of cell specificity.

[0154] For CLSM analysis, rMC cells were stained with CTG before seeding as described above. To visualize all cell types, HeLa or NCI-H295R cells were also stained using CTDR (25 μM, 45 minutes, 37°C). After CellTracker® incubation, rMCs were seeded together with HeLa / NCI-H295R cells at densities of 2,000 and 10,000 / 20,000 cells / well in 8-well Ibidi slides. After incubation at 37°C for 48 hours, cell nuclei were stained with Hoechst 33258 (5 μg / mL in DPBS) for 20 minutes. Cells were washed twice with pre-warmed DPBS, and NPs labeled with AlexaFluor® 568 were added at a concentration of 0.05 mg / mL (V=250 μL) at 37°C for 45 minutes. After NP incubation, the samples were treated as described above and analyzed using a Zeiss LSM 710 microscope.

[0155] in vivo cell targeting Animal experiments were conducted in accordance with national and institutional guidelines and approved by local authorities (Regierung von Unterfranken, reference no.: 55.2-2532-2-329). Female 10-week-old NMRI mice (Charles River, Sulzfeld, Germany) were used as the animal model. After analgesia with buprenorphine (0.1 mg / kg body weight), the mice were anesthetized with 2.5% isoflurane and injected via jugular vein with 100 μL of CF®647-labeled NP (c=120 nM). The mice were maintained under anesthesia, and after 5 minutes, an initial blood sample was taken via IV puncture. After 60 minutes, the mice were anesthetized with ketamine / xylazine, a final blood sample was taken, and the animals were sacrificed via perfusion fixation. Both kidneys were removed and immediately transferred to a solution of 18% sucrose and 14% PFA in phosphate buffer (0.1M pH 7.4). After 6 hours, the kidneys were washed with DPBS and cryoprotected at -80°C until further processing. For frozen sections, the organs were embedded in Tissue Tek® OCT® Compound (Sakura Finetek, Torrance, CA, USA), cut into 5 μm sections using a CryStar NX70 cryotome (Thermo Fisher Scientific, Waltham, MA, USA), and fixed on Superfrost® Plus glass slides (Thermo Fisher Scientific, Schwerte, Germany). For analysis of NP kidney deposition and glomerular fluorescence quantification, sections were rinsed in DPBS and blocked at RT for 10 minutes in 5% BSA supplemented with 0.04% Triton-X in DPBS. After further rinsing in DPBS, the samples were stained for the cell nuclei with 4',6-diamidine-2'-phenylindole dihydrochloride (DAPI) diluted 1:400 in 0.5% BSA and 0.04% Triton-X in DPBS. Following a final washing step in DPBS and mpH2O, respectively, the frozen sections were mounted using Mowiol mounting medium and analyzed on a Zeiss Axiovert 200M. Fiji software (Madison, WI, USA) was used for image analysis.The fluorescence intensity of glomeruli was evaluated by measuring the integrated density of the area exceeding a certain specific fluorescence threshold and dividing it by the glomerular area. To evaluate the exact cell position of NPs, kidney frozen sections were prepared as described above. After washing and blocking the sections, the samples were stained overnight at 4 °C with a goat-derived integrin α-8 antibody (diluted 1:200 in 0.5% BSA / 0.04% Triton-X in DPBS). Subsequently, the samples were washed with DPBS and stained at RT for 1 h with Cy2® donkey anti-goat and DAPI diluted 1:400 in 0.5% BSA / 0.04% Triton-X in DPBS. After the final washing step, the samples were mounted and analyzed with a Zeiss LSM 710.

[0156] (Example 7) Preparation of hetero-multivalent EXPcRGD NPs using a modular concept All materials and methods referred to in this example were as described in Example 6.

[0157] To create NPs with desired adenovirus-mimicking properties, the inventors implemented a modular design based on the synergistic combination of different biocompatible polymer components into hetero-multivalent particle species (Figure 18a). The overall polymer composition of the NPs was intended to be similar to the inventors' previous influenza A-mimicking NP design so that both targeting concepts could be appropriately compared. Thereby, the widely established poly(lactic-co-glycolic acid) (PLGA) forms a hydrophobic NP core that not only ensures enhanced structural integrity in aqueous media but also enables NP visualization via coupling of fluorescent dyes or nanogold. The poly(ethylene glycol)-poly(lactic acid) (PEG-PLA) block copolymer as the second component provides the structural flexibility required to implement the pursued virus-mimicking NP design. In the first step, longer (PEG 5k -PLA 10k ) or shorter (PEG 2k -PLA 10kPEG-PLA polymers having any of the PEG chains were synthesized via previously described ring-opening polymerization (Figure 25a). EXP3174 was intended to initially bind to mesangial AT1r as a freely moving ligand, thus providing a longer, and therefore more flexible, PEG chain. 5k -PLA 10k It was covalently coupled to the chain (Figure 25b). In contrast, the second ligand (cRGDfK) should not be able to interact with the surface-bound integrin unless the initial AT1r binding and subsequent spatial approach of the NP occur. In this regard, the second ligand (cRGDfK) was coupled to a shorter PEG. 2k -PLA 10k The surface densities of both cRGDfK and EXP3174 can be precisely adjusted by mixing a distinct amount of either ligand-functionalized or unfunctionalized PEG-PLA polymer with the PLGA before NP production via nanoprecipitation (Figure 18d / e).

[0158] The inventors decided to prepare hetero-functional nanoparticles (EXPcRGD NPs) having 25% EXP3174 and 15% cRGDfK on their surface, thereby fully utilizing the ligand's receptor binding ability while preserving the structural integrity of the fabricated particles. The particles should be able to locate in target cells by binding to AT1r via sterically flexible EXP3174, then reduce the spatial distance to the cell surface, subsequently activate αVβ3 integrin via previously hidden cRGDfK, and ultimately initiate NP endocytosis (Figure 17c). When hetero-functional EXPcRGD NPs below a 60 nm size threshold, as well as homo-functional (EXP NP / cRGD NPs) and unfunctionalized, methoxy-terminated particles (control NPs) were fabricated, negative zeta potential values ​​were observed (Figure 18b / c). These features should not only facilitate successful exudation via endothelial fenestration (Figure 17a / b), but also prevent NP phagocytosis or widespread serum protein adsorption.

[0159] (Example 8) Hetero-multivalent EXPcRGD NPs exhibit excellent ligand affinity for target motifs. All materials and methods mentioned in this embodiment were as described in Examples 6 and 7.

[0160] The inventors tested EXP3174-mediated NP binding to AT1r expressed by rat mesangial cells (rMCs). q Activation of coupled AT1r by its primary ligand, angiotensin II (AT II), results in calcium influx into the cytosol, thus reducing intracellular Ca after AT II stimulation. 2+ The level can be used as a marker of AT1r activity after NP incubation. Since the ligand itself acts as a potent antagonist, low receptor activity indicates a high ratio of bound EXP3174. Figure 19 shows intracellular Ca25 of rMCs stimulated with AT II pre-incubated with NP or free EXP3174 for 45 minutes. 2+ Indicates the level. EXPcRGD NP(IC 50 =276±31pM) and EXP NP(IC 50 Both (=552±73pM) exhibit excellent AT1r avidity, which is highly effective inhibition of the receptor in the picomolar concentration range and the resulting minimal intracytosolic Ca 2+ This produces a level (Figure 19a). Furthermore, the inhibitory efficacy of the EXP3174-containing NP type was even higher than that of the free ligand (IC). 50 IC20 (=2.66±0.9nM). This strongly suggests that the EXP3174 functionalized particles were able to interact with the target receptor in a multivalent form, resulting in increased overall avidity. IC20 (IC20) of both EXPcRGD and EXP NPs. 50Since the levels were found to be within the same range, the inventors concluded that both combinations of EXP3174 and cRGDfK in one particle type did not significantly interfere with the binding ability of EXP3174 itself. Furthermore, the control NP and cRGD NP did not show interaction with AT1r and did not exhibit maximum Ca upon receptor stimulation. 2+ A signal was generated, confirming the assay's specificity for AT1r (Figure 19b).

[0161] After verifying the AT1r binding ability of adenovirus-mimicking EXPcRGD NPs, the next step was to investigate particle uptake into rMCs via cRGDfK-αVβ3 interactions. Therefore, we incubated mesangial cells with fluorescently labeled NPs and analyzed the cell distribution via confocal laser scanning microscopy (CLSM). To visualize the cell bodies, rMCs were pre-treated with CellTracker® Deep Red (CTDR). Figure 20a shows strong intracellular accumulation of AlexaFluor® 568-labeled EXPcRGD NPs in spherical structures representing endocytic vesicles. Over time, both the number and intensity of visible accumulations increased. Furthermore, the vesicles appeared to increase in size with longer incubation times. These findings support the idea that cRGDfK-functionalized NPs can bind to target cells and be uptaken into intracellular vesicles via integrin-mediated endocytosis. Over time, these endocytotic vesicles fuse with larger endosomes, further increasing in size and strength.

[0162] Based on the CLSM results, the inventors performed flow cytometry analysis of rMCs treated with NPs to determine cell-associated fluorescence over a 120-minute incubation period. As shown in Figure 20b, the level of NP-derived fluorescence was highest for EXPcRGD NPs over the entire incubation period compared to all other NP species. While EXP NPs and control NPs showed only moderate fluorescence signals, a considerable level of cell association was detected for cRGD NPs. Notably, while the respective fluorescence levels plateaued after approximately 60 minutes, cell association for EXPcRGD NPs increased further. This strongly supports the hypothesis of sequential interactions between EXPcRGD NPs and their target cells, resulting in a long-term increase in fluorescence levels compared to homo-functional cRGD NPs.

[0163] To investigate the effect of αVβ3 integrin on EXPcRGD NP cell uptake, an excess amount of free cRGDfK (c=500 μM) was added, and then rMCs were incubated with EXPcRGD NPs for 60 minutes. As a result, the level of cell-associated fluorescence decreased sharply to levels comparable to those of EXP NPs or control NPs (Figure 20c). Hetero-multivalent particles were apparently no longer able to target the required αVβ3 integrin and therefore could not substantially initiate endocytosis after AT1r binding.

[0164] To further validate the concept of integrin-mediated NP endocytosis, the inventors decided to utilize transmission electron microscopy (TEM), which enabled the evaluation of NP-cell interactions at much higher magnification levels. To increase electron density and thus enhance the resulting TEM visibility of the applied NPs, ultrasmall gold nanoparticles with an average diameter of 2.2 nm were covalently coupled to PLGA, which was then used for further NP production (Figure 26). To sensitize the gold cores of the particles, and thus visualize them and evaluate their precise locations, mesangial cells incubated with these gold-tagged NPs could then be enhanced with gold. This retrospective gold enhancement offers the substantial advantage that the physicochemical characteristics of the nano-gold-labeled NPs are not significantly different from those of unlabeled NPs, which is not the case for commonly used gold NPs.

[0165] Figure 21a shows the cell bodies of two mesangial cells incubated with gold-tagged EXPcRGD NPs. Numerous round vesicles filled with gold-enhanced NPs were detected within the cell cytosol. The distribution pattern showed a striking similarity to previously described CLSM results (Figure 20a), thereby strongly supporting ligand-mediated NP endocytosis. Furthermore, particle accumulation was observed at the cell boundary, indicating that these NPs were still bound to membrane-located surface structures. These findings further indicate that the applied EXPcRGD NPs interacted with the target cell in a stepwise process of pre-binding to AT1r and subsequent integrin-mediated endocytosis. In line with this assessment, EXP NPs without surface-bound cRGDfK were detected only at the rMC membrane, and no particle accumulation was found in endocytic vesicles (Figure 21b). Furthermore, cell-particle association for control NPs was minimal (Figure 21c). The specificity of the applied gold enhancement was demonstrated by the absence of gold accumulation in particle-free cells.

[0166] (Example 9) Ligand synergy results in enhanced mesangial cell selectivity in vitro. All materials and methods mentioned in this embodiment were as described in Examples 6-8.

[0167] Since it has been demonstrated that hetero-polyvalent EXPcRGD NP synergistically combines the key features of both of its surface ligands and presents them in a sterically controlled manner, we intended to demonstrate that this design can be practically utilized to increase mesangial cell selectivity. Accordingly, we implemented an in vitro-based assay in which target rMCs were co-cultured with a dominant number (5-10 times) of off-target cells that either lacked the target receptor or possessed only one of the two target receptors. HeLa cells did not express either AT1r or αVβ3-integrin to significant levels, but NCI-H295R cells showed high AT1r expression but low αVβ3 expression, so we selected them (Figure 27).

[0168] To distinguish between co-cultured cells in CLSM analysis, rMCs were stained using CellTracker® Green (CTG), while off-target cells were marked with CTDR. After 45 minutes of incubation with fluorescently labeled EXPcRGD NPs, the cell distribution of the NPs was evaluated. In the rMC / HeLa co-culture model, particle-derived fluorescence could be detected almost exclusively within the mesangial cell region. HeLa cells, in contrast, showed only weak interactions with the NPs, resulting in only slight fluorescence levels (Figure 22a). Therefore, we concluded that EXPcRGD NPs were selectively located in mesangial cells among HeLa cells due to differences in receptor expression on the cell surface. These findings were supported by flow cytometry analysis showing that cell-associated fluorescence of EXPcRGD NPs was significantly higher in rMCs than in off-target HeLa cells, while cell interactions for control NPs were minimal for both cell types (Figure 22b). In contrast, the rMC / NCI-H295R co-culture provided a diverse particle distribution. NP-related fluorescence could be found not only in rMCs but also within the regions covered by NCI-H295R cells. However, the distribution patterns differed significantly. Fluorescence among rMCs was found in round, vesicle-like structures, as previously observed, while NCI-H295R-related fluorescence was more diffuse and primarily amplified at the cell membrane (Figure 22a). Therefore, we concluded that EXPcRGD NPs accumulate in endocytic vesicles of rMCs but were only able to bind to AT1r present in the cell membrane of NCI-H295R cells and could not be taken up into the cytosol due to the absence of αVβ3 integrin. Furthermore, flow cytometry analysis showed that NP-related fluorescence was higher in NCI-H295R cells compared to HeLa cells, but EXPcRGD NP still showed a significantly enhanced signal in mesangial cells (Figure 22c).Notably, the addition of an excess amount of free EXP3174 (c=1mM) prior to NP incubation resulted in a sharp decrease in fluorescence levels for NCI-H295R cells, while cell-associated fluorescence for rMCs remained significantly higher. This observation further supports the view that EXPcRGD NPs can indeed utilize both surface ligands to target mesangial cells, thereby benefiting from a hetero-functional design.

[0169] In summary, our co-culture model demonstrated that hetero-multivalent EXPcRGD NPs are not only dominant in number, but also have the ability to effectively identify receptor-positive mesangial cells in the presence of off-target cells expressing one of the two target receptors.

[0170] (Example 10) In vivo accumulation of adenovirus-mimicking EXPcRGD NPs in mesangial cells All materials and methods mentioned in this embodiment were as described in Examples 6-9.

[0171] Both rMC binding and uptake studies successfully demonstrated that, through our viral-mimicking concept of sequential ligand-receptor interactions, hetero-polyvalent EXPcRGD NPs can selectively target mesangial cells in vitro. However, translating in vitro results into robust systems with sufficient in vivo efficiency has been a major obstacle in nanoparticle design, as many strategies fail to deliver the desired target specificity. Therefore, we decided to evaluate the ability of NPs to actually reach the mesangial region in vivo, which requires not only active enhancement of cell uptake but also appropriate passive accumulation in the target region. In this regard, fluorescently labeled NPs were injected into 10-week-old female NMRI mice. After 1 hour of NP circulation, the mice were sacrificed and the kidneys were extracted. Fluorescence analysis of the prepared frozen sections revealed that EXPcRGD NPs effectively accumulated in the glomerular region, while fluorescence in the renal tubular portion was negligible (Figure 23). In contrast, control NP and homo-functional EXP or cRGD NP showed considerably lower deposition in kidney frozen sections.

[0172] To quantify the observed differences, glomerular fluorescence levels were determined for all NP types by evaluating glomerular fluorescence intensity per unit area (Figure 24a / b). EXPcRGD NPs showed a more than 10-fold increase in fluorescence intensity compared to control NPs. Furthermore, glomerular accumulation of hetero-polyvalent NPs was significantly greater than for both homo-functional NP types. Notably, cRGD NP fluorescence was even lower than that of non-functionalized control NPs. We hypothesize that cRGD NPs were unable to reach the glomerular region because a majority of particles bind to αVβ3-expressing endothelial cells immediately after injection, and as a result leave the bloodstream before reaching deeper regions of the kidney. This hypothesis was further supported by the finding that the relative plasma levels of cRGD NPs after 1 hour of incubation were the lowest among all particle types (Figure 28a). In contrast, in EXPcRGD NPs, the shorter cRGDfK-functionalized PEG-PLA chain was shielded from premature presentation to αVβ3 integrin by the addition of the longer EXP3174-functionalized PEG-PLA chain. As a result, the hetero-multivalent particles avoided off-target deposition and thus successfully reached the glomerular region within the kidney. Antibody staining for the mesangial cell marker integrin-α8 further revealed that EXPcRGD NP-associated fluorescence in the glomeruli could be found almost entirely within mesangial cells (Figure 24c), which validated the hypothesis of exudation into the mesangial stroma and subsequent endocytosis (Figure 17a / b). To verify that the detected fluorescence in the mesangial region originated from structurally intact NPs, we further injected mice with a comparable dose of free fluorescent dye and analyzed the fluorescence deposition. While the intraglomerular signals for these samples were negligible, tubular cells showed very strong fluorescence levels (Figure 28b). This indicated that the low molecular weight dye was renally filtered, in contrast to the injected NP species. Therefore, we concluded that the intraglomerular fluorescence for all NP types originated from intact particles, since degradation would otherwise have resulted in an increase in tubular signals.

[0173] Therefore, the in vivo studies described herein successfully demonstrated the potential of the novel adenovirus-mimicking NP design of the present invention. Hetero-polyvalent EXPcRGD NPs accumulated effectively in the mesangial region of the glomerulus, while homo-functional or non-functionalized NP species did not accumulate in the same way. This strongly suggests that, in order to achieve a sufficient level of bioavailability, NPs must not only possess appropriate surface ligands but also present themselves in an organized form appropriate for their respective targeting strategies. Furthermore, NP accumulation in the mesangium also demonstrated the high effectiveness of adenovirus-mimicking systems for sterically controlled particle-cell interactions.

[0174] (Example 11) EXPcRGD NPs loaded with synacigat exhibit high efficiency. Nanoparticles (NPs) using either influenza A-mimicking or adenovirus-mimicking target cell recognition concepts were found to efficiently accumulate in mesangial cells in in vivo settings. In the next step, the experimental drug synaciguat (BAY 58-2667) was encapsulated within adenovirus-mimicking EXPcRGD NPs. Synaciguat (CCG) is a potent activator of soluble guanylate cyclase (sGC) and has been shown to significantly reduce mesangial fibrosis and reduce glomerular damage in diabetic animal models. By encapsulating CCG within our promising NP species, the cell-selective delivery of CCG to pathological mesangial sites can be significantly increased, resulting in enhanced therapeutic effects with minimized off-target effects (Figure 29).

[0175] In our experimental setup, CCG was initially encapsulated in hetero-polyvalent EXPcRGD NPs. The resulting NPs contained approximately 500–700 CCG molecules per NP (data not shown). In all subsequent experiments, administration of free synacigat at a concentration of 2 μM was compared to EXPcRGD NPs loaded with CCG at a concentration of approximately 0.5 nM (equivalent to 0.2 μM CCG) and to EXPcRGD control NPs without the drug (Figure 30). The concentration of free synacigatat was selected according to previous publications that demonstrated the anti-fibrotic effect of CCG within this concentration range. However, the CCG-containing NPs contained only 10% of the respective CCG amount in order to test the possible drug delivery effect.

[0176] To evaluate the effect of CCG-loaded EXPcRGD NPs on target sGCs, mesangial cells were initially incubated for 24 hours, and protein levels were assessed using Western blotting analysis. Interestingly, the total sGC levels gradually increased after incubation with both the free drug and the CCG-loaded NPs, indicating not only the previously shown activating effect of synaciguat on sGCs, but also a stabilizing effect (Figure 31). In contrast, NPs lacking synaciguat showed no significant effect on sGC levels.

[0177] Finally, the anti-fibrotic and anti-proliferative potential of NP-assisted CCG delivery was analyzed. Mesangial cells were initially incubated for 4 hours with either free CCG, CCG-loaded EXPcRGD NPs, or encapsulated, drug-free control NPs. After 4 hours, 10 ng / mL of transforming growth factor β (TGF-β) was added over 48 hours to induce fibrosis and hyperproliferative remodeling. While TGF-β administration resulted in a significant increase in mesangial cell proliferation, pre-incubation with both free CCG and CCG-loaded NPs significantly reversed this effect (Figure 32). Furthermore, Western blot and fluorescence microscopy analysis of the fibrosis markers α-SMA and collagen I revealed similar effects of CCG (loaded NPs) on inhibiting pro-fibrotic remodeling in mesangial cells.

[0178] In combination, these results revealed two main findings: 1. Both free synaciguat and NP-encapsulated synaciguat showed significant effects on their target enzyme sGC, resulting in marked activation of the described anti-fibrotic pathway (Figure 29). These results are consistent with previous findings regarding CCG and demonstrate the outstanding potential of the therapeutic agent in anti-fibrotic treatment. 2. Throughout all experiments, EXPcRGD NPs loaded with synacigat demonstrated comparable efficacy to administration of free CCG, even when the total amount of encapsulated CCG was only 10% of the free drug dose (0.2 μM vs. 2 μM). This demonstrates the remarkable potential of the described NPs to more efficiently deliver pharmaceutical agents to their intended intracellular targets.

[0179] References [1] Maslanka Figueroa, S., Veser, A., Abstiens, K., Fleischmann, D., Beck, S., and Goepferich, A. (2019). Influenza A virus mimetic nanoparticles trigger selective cell uptake. Proc. Natl. Acad. Sci. 201902563. [2] Sah E. and Sah H. Journal of Nanomaterials, Volume 2015, Article ID 794601. [3] Hennig, R., Ohlmann, A., Staffel, J., Pollinger, K., Haunberger, A., Breunig, M., Schweda, F., Tamm, ER, and Goepferich, A. (2015). Multivalent nanoparticles bind the retinal and choroidal vasculature. J. Control. Release 220, 265-274. [4] Inuzuka, T., Fujioka, Y., Tsuda, M., Fujioka, M., Satoh, AO, Horiuchi, K., Nishide, S., Nanbo, A., Tanaka, S., and Ohba, Y. (2016). Attenuation of ligand-induced activation of angiotensin II type 1 receptor signaling by the type 2 receptor via protein kinase C. Sci. Rep. 6, 21613.

[0180] Features of the present invention disclosed herein, in the claims and / or in the accompanying drawings may be materials for realizing the invention in various forms, both individually and in any combination thereof. The present invention provides, for example, the following items: (Item 1) Nanomaterials and nanoparticles comprising at least a first ligand and a second ligand, - The first ligand can mediate the attachment of the nanoparticles to target cells, - The second ligand can mediate the internalization of the nanoparticles into the target cells, Preferably, the nanomaterial includes polyethylene glycol (PEG), polylactic acid (PLA), poly(lactic acid-coglycolic acid) (PLGA), oxazoline-derived polymers, poly(amino acids), polysaccharides, phospholipids, sphingolipids, cholesterol, PEG-lipids, block copolymers, such as PEG-PLA or PEG-poly-caprolactone, inorganic substances, such as gold or qdot materials, and any combination thereof. Nanoparticles. (Item 2) The nanoparticles according to item 1, wherein the first ligand is a non-agonist agent that binds to GPCRs, such as angiotensin II receptor type 1 (AT1r), human neuropeptide Y1 receptor and CXC chemokine receptor type 4, and / or an agent that binds to glycoproteins and / or glycolipids on the surface of target cells, such as heparan sulfate, sialycoprotein, ganglioside and mannose receptors, preferably EXP3174 or telmisartan. (Item 3) The nanoparticles according to item 1 or 2, wherein the second ligand is any of the following: i) preferably an agent that binds to an integrin, e.g., αVβ3 integrin or αVβ5 integrin, selected from RGD, a cyclic RGD-peptide having the sequence of SEQ ID NO: 1, and derivatives thereof; ii) an agonist agent that binds to a GPCR, e.g., AT1r, preferably activated angiotensin-II; iii) an agent that binds to an ectoenzyme, e.g., regmine, membrane matrix metalloproteinase and angiotensin-converting enzyme (ACE), preferably angiotensin-I; and / or iv) an agent that binds to a transferrin receptor. (Item 4) A therapeutic agent, preferably a nanoparticle according to any of the preceding items, further comprising either pirfenidone or synaciguat. (Item 5) The nanoparticles according to any of the above items, wherein the first ligand and the second ligand are each coupled to the nanomaterial, preferably each being coupled to a block copolymer chain of the nanomaterial. (Item 6) The nanoparticle according to any of the above items, wherein the nanomaterial comprises more than one block copolymer chain, the first ligand is coupled to a first block copolymer chain of the nanomaterial, the second ligand is coupled to a second block copolymer chain of the nanomaterial, and the first block copolymer chain is longer than the second block copolymer chain, preferably at least 1.5 times the length of the second block copolymer chain, and more preferably at least 3 times the length of the second block copolymer chain. (Item 7) The first block copolymer chain comprises PEG in the range of 1k to 20k, preferably 1k to 10k, and / or PLA in the range of 5k to 40k, preferably 10k to 20k, and optionally the first block copolymer chain comprises PEG. 5k -PLA 10k The second block copolymer chain is PEG 2k -PLA 10k Item 6 is The nanoparticles described. (Item 8) The nanoparticles according to any of the above items, wherein the second ligand is enzymatically activated before the internalization of the nanoparticles into the target cells. (Item 9) The nanoparticles described in any of the above items, wherein the target cells are selected from mesangial cells, endothelial cells such as retinal endothelial cells, B cells, T cells, macrophages, dendritic cells, and tumor cells. (Item 10) Nanoparticles according to any of the above items, having a size of 5 nm to 1000 nm, preferably 10 nm to 150 nm, and more preferably 20 nm to 100 nm. (Item 11) Nanoparticles according to any of the above items, wherein the ratio of the first ligand to the second ligand is in the range of 2:1 to 1:2, preferably 1:1. (Item 12) Nanoparticles according to any of the above items, having particle avidity to a targeted receptor of 1 pM to 100 nM, preferably 50 pM to 1 nM. (Item 13) The nanoparticles according to any of the above items, wherein the nanomaterial contains PEG, and the nanoparticles have a ligand density of at least 5%, preferably at least 15%, and more preferably at least 25% ligand / PEG. (Item 14) Nanoparticles as described in any of the preceding items, for use as pharmaceuticals or diagnostic agents. (Item 15) Nanoparticles as described in any of the preceding items for use in methods of preventing or treating diseases selected from diabetic nephropathy, glomerulonephritis, glomerular VEGF A dysregulation, endothelial VEGF A dysregulation, diabetic retinopathy, rheumatoid arthritis, age-related macular degeneration, and cancers such as breast cancer. (Item 16) A method for preparing nanoparticles as described in any of items 1 to 13, a) Preferably, one or more nanomaterials comprising polyethylene glycol (PEG), polylactic acid (PLA), poly(lactic acid-coglycolic acid) (PLGA), oxazoline-derived polymers, poly(amino acids), polysaccharides, phospholipids, sphingolipids, cholesterol, PEG-lipids, block copolymers, e.g., PEG-PLA or PEG-poly-caprolactone, inorganic substances, e.g., gold or qdot materials, and combinations thereof, as well as a therapeutic agent, in any order; b) A step of preparing a block copolymer from one or more of the nanomaterials as needed; c) Preferably, one or more steps of coupling a first ligand and a second ligand to the nanomaterial by DCC / NHS coupling or EDC / NHS coupling; d) A step of providing a therapeutic agent, preferably a lipophilic therapeutic agent, if one has not already been provided in step a); e) Preparing and obtaining nanoparticles using the ligand coupled to the nanomaterial and the therapeutic agent, preferably by nanoprecipitation. Methods that include... (Item 17) The method according to item 16, wherein the obtaining step in step e) includes obtaining nanoparticles having a polydispersity index of 0.01 to 0.5, preferably 0.01 to 0.3, more preferably 0.01 to 0.1.

Claims

1. Nanomaterials and nanoparticles comprising at least a first ligand and a second ligand, - The first ligand is capable of mediating the attachment of the nanoparticles to mesangial cells, and the first ligand is EXP3174. - The second ligand is capable of mediating the internalization of the nanoparticles into the mesangial cells, and the second ligand is a cyclic RGD-peptide or angiotensin-I having the sequence of SEQ ID NO: 1, The nanomaterial comprises poly(lactic acid-coglycolic acid) (PLGA) and a block copolymer, wherein the block copolymer is PEG-PLA. If the nanomaterial comprises more than one block copolymer chain, the first ligand is coupled to a first block copolymer chain of the nanomaterial, the second ligand is coupled to a second block copolymer chain of the nanomaterial, and the second ligand is the cyclic RGD-peptide having the sequence of SEQ ID NO: 1, then the first block copolymer chain is longer than the second block copolymer chain. Nanoparticles.

2. The nanoparticle according to claim 1, wherein the second ligand is angiotensin-I, and the angiotensin-I is enzymatically activated before the internalization of the nanoparticle into the mesangial cell, and the enzymatic activation includes the conversion of angiotensin-I to angiotensin-II.

3. Nanoparticles according to any one of claims 1 to 2, further comprising a therapeutic agent.

4. The nanoparticles according to claim 3, wherein the therapeutic agent is either pirfenidone or synaciguat.

5. The nanoparticle according to any one of claims 1 to 4, wherein the first block copolymer chain is at least 1.5 times the length of the second block copolymer chain.

6. The nanoparticle according to any one of claims 1 to 5, wherein the first block copolymer chain is at least three times the length of the second block copolymer chain.

7. The nanoparticle according to any one of claims 1 to 6, wherein the first block copolymer chain comprises PEG in the range of 1 k to 20 k and / or PLA in the range of 5 k to 40 k.

8. The nanoparticle according to claim 7, wherein the first block copolymer chain comprises PEG in the range of 1 k to 10 k and / or PLA in the range of 10 k to 20 k.

9. The first block copolymer chain is PEG ５ｋ - PLA １０ｋ The second block copolymer chain is PEG ２ｋ - PLA １０ｋ The nanoparticle according to claim 7 or 8.

10. Nanoparticles according to any one of claims 1 to 9, having a size of 5 nm to 1000 nm.

11. The nanoparticles according to claim 10, having a size of 10 nm to 150 nm.

12. The nanoparticles according to claim 11, having a size of 20 nm to 100 nm.

13. The nanoparticle according to any one of claims 1 to 12, wherein the ratio of the first ligand to the second ligand is in the range of 2:1 to 1:

2.

14. The nanoparticle according to claim 13, wherein the ratio of the first ligand to the second ligand is 1:

1.

15. Nanoparticles according to any one of claims 1 to 14, having particle avidity to a targeted receptor in the range of 1 pM to 100 nM.

16. The nanoparticles according to claim 15, having particle avidity to a targeted receptor at 50 pM to 1 nM.

17. The nanoparticle according to any one of claims 1 to 16, wherein the nanoparticle has a ligand density of at least 5% ligand / PEG.

18. The nanoparticle according to claim 17, wherein the nanoparticle has a ligand density of at least 15% ligand / PEG.

19. The nanoparticle according to claim 18, wherein the nanoparticle has a ligand density of at least 25% ligand / PEG.

20. Nanoparticles according to any one of claims 1 to 19 for use as a pharmaceutical or diagnostic agent.

21. Nanoparticles according to any one of claims 1 to 19 for use in methods for preventing or treating a disease selected from diabetic nephropathy, glomerulonephritis, glomerular VEGF A dysregulation, endothelial VEGF A dysregulation, diabetic retinopathy, rheumatoid arthritis, age-related macular degeneration, and cancer.

22. The nanoparticle according to claim 21, wherein the cancer is breast cancer.

23. A method for preparing nanoparticles according to any one of claims 1 to 19, a) Providing one or more types of nanomaterials in any order; c) A step of coupling a first ligand and a second ligand to the nanomaterial in one or more steps; d) A step of providing a therapeutic agent if one has not already been provided in step a); e) Steps of preparing and obtaining nanoparticles using the ligand coupled to the nanomaterial and the therapeutic agent. Includes, The first ligand is EXP3174, The second ligand is a cyclic RGD-peptide or angiotensin-I having the sequence of SEQ ID NO: 1, A method wherein the nanomaterial in step a) comprises poly(lactic acid-coglycolic acid) (PLGA) and a block copolymer, wherein the block copolymer is PEG-PLA.

24. The method according to claim 23, wherein in step a), a therapeutic agent is provided in addition to the one or more nanomaterials.

25. The method of claim 23 or 24, wherein the coupling in step c) is by DCC / NHS coupling or EDC / NHS coupling, and / or the therapeutic agent provided in step a) or step d) is a lipophilic therapeutic agent, and / or the step of preparing and obtaining in step e) is by nanoprecipitation.

26. The method according to any one of claims 23 to 25, wherein the step of obtaining in step e) includes obtaining nanoparticles having a polydispersity index of 0.01 to 0.

5.

27. The method according to claim 26, wherein the step of obtaining in step e) includes obtaining nanoparticles having a polydispersity index of 0.01 to 0.

3.

28. The method according to claim 27, wherein the step of obtaining in step e) includes obtaining nanoparticles having a polydispersity index of 0.01 to 0.1.

Images