Adhesive SEAM films and seams formed therefrom

Abstract

An adhesive seam film including an adhesive film composition, the adhesive film composition including, based on the total weight of the adhesive film composition 20 wt% to 95 wt% of one or more styrene-ethylene / butylene-styrene triblock copolymers, wherein the one or more styrene-ethylene / butylene-styrene triblock copolymer has a weight average molecular weight of 90,000 g / mol to 140,000 g / mol and an average bound styrene content of 18 wt% to 27 wt%, based on the total weight of the styrene-ethylene / butylene-styrene triblock copolymer; 5 wt% to 40 wt% of a white mineral oil, wherein the white mineral oil has a kinematic viscosity at 40C in the range of 15 mm2 / sto 100 mm2 / s; and 0 wt% to 40 wt% of a tackifier, wherein the tackifier has a weight average molecular weight of 500 g / mol to 5000 g / mol, a glass transition temperature of 50℃ to 100℃, and a softening temperature of 100℃ to 140℃.

Description

ADHESIVE SEAM FILMS AND SEAMS FORMED THEREFROMTECHNICAL FIELD

[0001] Embodiments of the present disclosure are generally related to adhesive seam films. More particularly, adhesive seam films include adhesive film compositions that include a styrene-ethylene / butylene-styrene triblock copolymer, a white mineral oil, and optionally a tackifier.BACKGROUND

[0002] Thermoplastic polyurethane compositions are commonly used in the apparel industry, such as in seamless adhesives, due to their desirable mechanical properties and durability. However, the use of thermoplastic polyurethane compositions may be cost prohibitive. Moreover, thermoplastic polyurethane compositions and other commonly used thermoplastic compositions may be in various forms, such as sprays or gels, that are difficult to work with and create unnecessary production delays.

[0003] Accordingly, a need exists for cost-effective thermoplastic compositions that may be formed into thin adhesive seam films.SUMMARY

[0004] Embodiments of the present disclosure are directed to adhesive seam films.

[0005] According to some embodiments, an adhesive seam film is provided. The adhesive seam film includes an adhesive film composition. The adhesive film composition comprising, based on the total weight of the adhesive film composition: 20 wt%to 95 wt%of one or more styrene-ethylene / butylene-styrene triblock copolymers, wherein the one or more styrene-ethylene / butylene-styrene triblock copolymer has a weight average molecular weight of 90, 000 g / mol to 140, 000 g / mol and an average bound styrene content of 18 wt%to 27 wt%, based on the total weight of the styrene-ethylene / butylene-styrene triblock copolymer; 5 wt%to 40 wt%of a white mineral oil, wherein the white mineral oil has a kinematic viscosity at 40℃ in the range of 15 mm2 / sto 100 mm2 / s; and 0 wt%to 40 wt%of a tackifier, wherein the tackifier has a weight average molecular weight of 500 g / mol to 5000 g / mol, a glass transition temperature of 50 ℃ to 100 ℃, and a softening temperature of 100 ℃ to 140 ℃.

[0006] In one or more embodiments, the adhesive seam film has a thickness of 30 μm to 150 μm.

[0007] In one or more embodiments, the adhesive seam film has a thickness of 50 μm to 100 μm.

[0008] In one or more embodiments, the adhesive film composition comprises 5 wt%to 30 wt%of the tackifier.

[0009] In one or more embodiments, the one or more styrene-ethylene / butylene-styrene triblock copolymers includes a first styrene-ethylene / butylene-styrene triblock copolymer having a first bound styrene content and a second styrene-ethylene / butylene-styrene triblock copolymer having a second bound styrene content, and the first bound styrene content is greater than the second bound styrene content.

[0010] In one or more embodiments, the adhesive film composition comprises 85 wt%to 95 wt%of the one or more styrene-ethylene / butylene-styrene triblock copolymers, 5 wt%to 15 wt%of the white mineral oil, and 0 wt%to 3 wt%of the tackifier.

[0011] In one or more embodiments, the adhesive film composition comprises 20 wt%to 55 wt%of the one or more styrene-ethylene / butylene-styrene triblock copolymers, 20 wt%to 40 wt%of the white mineral oil, and 15 wt%to 40 wt%of the tackifier.

[0012] In one or more embodiments, the adhesive seam film has a width of 5 cm to 40 cm.

[0013] In one or more embodiments, the adhesive film composition has a melt index of 35 g / 10 min to 80 g / 10 min, as measured according to ASTM D1238 at 190 ℃ and under 2.16 kg load.

[0014] In one or more embodiments, the styrene-ethylene / butylene-styrene triblock copolymer has a polydispersity of 1.0 to 1.3.

[0015] In one or more embodiments, the adhesive seam film is a mesh.

[0016] In one or more embodiments, the adhesive seam film is part of a multilayer composite comprising two or more films.

[0017] In one or more embodiments, the adhesive seam film is part of a multilayer composite comprising the adhesive seam film adhered to a fabric backing.

[0018] In one or more embodiments, the adhesive seam film is part of a multilayer composite comprising the adhesive seam film adhered to a release liner.

[0019] In one or more embodiments, the adhesive seam film is coated with a polymeric powder or dusting agent.

[0020] In another embodiment, a seam is provided comprising: a first section of fabric; a second section of fabric at least partially overlapping the first section of fabric to form a seam section; and the adhesive seam film as described above is located in the seam section adhering the first section of fabric to the second section of fabric.

[0021] In one or more embodiments, the adhesive seam film is disposed between the first section of fabric and the second section of fabric.

[0022] In one or more embodiments, the seam section includes stitches attaching the first section of fabric to the second section of fabric.

[0023] In one or more embodiments, the seam section is a stitchless seam section.

[0024] In another embodiment, a method of forming an adhesive seam film is provided comprising preparing an adhesive film composition; and extruding the adhesive film composition to form an adhesive seam film that has a thickness of 25 μm to 250 μm; wherein the adhesive film composition described above

[0025] In one or more embodiments, the adhesive film composition comprises 5 wt%to 30 wt%of the tackifier.

[0026] In another embodiment, a method of preparing a seam is provided comprising supplying a first section of fabric, a second section of fabric, and an adhesive seam film; situating the adhesive seam film between the first section of fabric and the second section of fabric to form a seam section, wherein the second section of fabric at least partially overlaps the first section of fabric; and heating the seam section such that the adhesive seam film adheres the first section of fabric and the second section of fabric, wherein the adhesive seam film compromises an adhesive film composition is described above.

[0027] In one or more embodiments, the adhesive film composition comprises 5 wt%to 30 wt%of the tackifier.

[0028] In one or more embodiments, the step of heating the seam section is performed by a hot iron or hot air.

[0029] Additional features and advantages of the embodiments described herein will be set forth in the detailed description which follows, and in part will be readily apparent to those skilled in the art from that description or recognized by practicing the embodiments described herein, including the detailed description, which follows and the claims.

[0030] DRAWINGS

[0031] FIG. 1 depicts an exemplary adhesive seam film, according to one or more embodiments shown and described herein;

[0032] FIG. 2 depicts an exemplary multilayer composite, according to one or more embodiments shown and described herein;

[0033] FIG. 3 depicts an exemplary multilayer composite with an adhesive seam film adhered to a fabric backing, according to one or more embodiments shown and described herein;

[0034] FIG. 4 depicts an exemplary multilayer composite comprising an adhesive seam film adhered to a release liner, according to one or more embodiments shown and described herein;

[0035] FIG. 5 depicts an exemplary adhesive webbing, according to one or more embodiments shown and described herein

[0036] FIG. 6 depicts an exemplary seam, according to one or more embodiments shown and described herein;

[0037] FIG. 7 depicts another exemplary seam, according to one or more embodiments shown and described herein; and

[0038] FIG. 8 depicts an exemplary seam with stiches, according to one or more embodiments shown and described herein.DETAILED DESCRIPTION

[0039] Reference will now be made in detail to various embodiments of adhesive seam films and seams formed therefrom.

[0040] The disclosure should not be construed as limited to the embodiments set forth herein. Rather, these embodiments are provided so that this disclosure will be thorough and complete, and will fully convey the subject matter to those skilled in the art.

[0041] Definitions

[0042] Unless otherwise expressly defined, all technical and scientific terms used herein have the same meaning as commonly understood by a person of ordinary skill in the art. The terminology used in the disclosure herein is for describing particular embodiments only and is not intended to be limiting.

[0043] Unless otherwise expressly stated, it not intended that any method disclosed herein be construed as requiring that its steps be performed in a specific order, nor that any article set forth herein be construed as requiring specific orders or orientations to its individual components.

[0044] Unless otherwise expressly stated, it is intended that any composition or mixture disclosed herein may comprise, consist essentially of, or consist of the disclosed components.

[0045] As used herein, the singular form of a term is intended to include the plural form of the term, unless the context clearly indicates otherwise.

[0046] As used herein, numerical values are not strictly limited to the exact numerical value recited. Instead, unless otherwise expressly stated, each numerical value is intended to mean both the exact numerical value and “about” the numerical value, which encompasses a functionally equivalent range surrounding that numerical value, such that either possibility is contemplated as an embodiment disclosed herein.

[0047] As used herein, the terms “adhesion” or “bonding strength” refer to the ability of a material to adhere to another material, as determine by peel force.

[0048] As used herein, the term “peel force” refers to the force required to separate two layers of fabric from an adhesive seam film, which is situated between the two layers of fabric and bonded at 150 ℃ under 2kgf for 30 seconds as measured by an Instron tensile tester. The two ends of the fabric layers are mounted on the Instron tensile tested and pulled apart at 200mm / minute to separate the two layers of fabric from the adhesive seam film according to ASTM D3330.

[0049] As used herein, the term “resilience” refers to the ability of a material to return to its original shape when a load is removed, as determined using the ten cycle 100%stretch test.

[0050] As used herein, the term “ten cycle 100%stretch test” refers to the following process. In a first cycle, a 100mm long and 20mm wide film is mounted in the jaws of an Instron tensile tester and pulled to 100%extension at a rate of 500 mm / minute, and returns to its original length of 100mm and holds the film in that position for 30 seconds. The cycle are repeated 10 times. After the tenth cycle, the resilience is measured by determining the length of the deformed film and calculating the percent difference between the original 100mm length and the final length. For example, if, after 10 cycles, the film becomes 102 mm long due to permanent deformation, then it is considered to 98%resilience.

[0051] As used herein, the term “100%Modulus” refers to the determination of the measurement a load at 100%stretch using the ten cycle 100%stretch test.

[0052] As used herein, the term “elasticity” refers to the stretchiness of a material, as determined by measuring the load at 200%using the two cycle 200%stretch test.

[0053] As used herein, the term “elastic recovery” refers to the ability of a material to return to its original shape when a load is removed, as determined by measuring hysteresis using the two cycle 200%stretch test.

[0054] As used herein, the term “two cycle 200%stretch test” refers to the following process. In a first cycle, a 1 inch long and 1 inch wide film is mounted in the jaws of an Instron tensile tester and pulled to 200%extension at a rate of 10 inches / minute. The film is then held at that extension for 2 minutes. After the 2 minutes, the Instron returns the film to its original length of 2 inches and holds the film in that position for one minute. In a second cycle, the film is again pulled to 200%extension at a rate of 10 inches / minute. The film is then held at that extension for 2 minutes and the load on the film is measured (i.e., load at 200%) . After the 2 minutes, the Instron returns the film to its original length of 2 inches and holds the film in that position for one minute. After the second cycle, the hysteresis is measured by determining the length of the deformed film and calculating the percent difference between the original 2 inch length and the deformed length. For example, if, after two cycles, the film becomes 2.4 inches long due to permanent deformation, then it is considered to have 20%hysteresis.

[0055] As used herein, the term “surface tack” refers to the strength at which an adhesive seam film can stick to itself.

[0056] As used herein, the term “polydispersity” refers to a molecular weight distribution metric measured as the weight average molecular weight (MW) divided by the number average molecular weight (MN) .

[0057] As used herein, the term “weight average molecular weight” refers to the weighted sum of all the molecular weights in the population, where the weighting factor is the mole fraction of each molecule sum of the weight of all chains in the polymer divided by the total number of chains, as measured according to Gel Permeation Chromatography (GPC) using polystyrene standards.

[0058] As used herein, the term “number average molecular weight” refers to the statistical average molecular weight of all polymer chains in the sample and is the sum of the weight of all chains in the polymer divided by the total number of chains, as measured according to Gel Permeation Chromatography (GPC) and Size Exclusion Chromatograpy (SEC) using polystyrene standards.

[0059] As used herein, the term “glass transition temperature” refers to the temperature at which an amorphous polymer changes from a hard / glassy state to a soft / leathery state, or vice versa.

[0060] As used herein, the term “softening temperature” refers to the temperature at which a polymer flows under a load on heating.

[0061] As used herein, the term “melt flow rate” refers to a measure of ease of flow of a melted material through an orifice at a specified temperature and load, as measured according to ASTM D1238. The term “melt flow index” also may be used to refer to melt flow rate.

[0062] As used herein, the term “kinematic viscosity’ refers to the ratio of -absolute (or dynamic) viscosity to density -a quantity in which no force is involved. Kinematic viscosity may be obtained by dividing the absolute viscosity of a fluid with the fluid mass density. Kinematic viscosity may be obtained according to ASTM D445-2019a.

[0063] As used herein, the term “formed from” (including related terms such as “forming” ) refers to, with respect to an article (or component of an article) and an adhesive film composition, that the article (or component of the article) is extruded, molded, shaped, pressed, or otherwise made, in whole or in part, from the adhesive film composition under sufficient heating to enable such forming. As such, the term “formed from” (including related terms such as “forming” ) means, in some embodiments, the article (or component of an article) can comprise, consist essentially of, or consist of, the adhesive film composition; and, in other embodiments, the article (or component of an article) consists of the adhesive film composition because the article (or component of an article) is, for example, made by an extrusion process or a molding process.

[0064] Usefulness

[0065] As discussed hereinabove, thermoplastic polyurethane compositions are commonly used in the apparel industry, such as in seamless elastic tapes, due to their desirable mechanical properties and durability. However, the use of thermoplastic polyurethane compositions may be cost prohibitive. Moreover, thermoplastic polyurethane compositions and other commonly used thermoplastic compositions may be in various forms, such as sprays or gels, that are difficult to work with and create unnecessary production delays.

[0066] Disclosed herein are adhesive film compositions. Specifically, the adhesive film compositions disclosed herein include a styrene-ethylene / butylene-styrene triblock copolymer, a white mineral oil, and optionally, a tackifier. Advantageously, the styrene-ethylene / butylene-styrene triblock copolymer, white mineral oil, and optionally tackifier, help to achieve an adhesive film composition that may be used to form a thin adhesive seam film. Moreover, the adhesive film compositions may exhibit desirable adhesion or bonding strength, elasticity, elastic recovery, and / or surface tack.

[0067] Accordingly, the adhesive film compositions may be used to form any article that requires a thin adhesive seam film. The adhesive film compositions are especially useful in seamless construction of performance apparel, intimate apparel, casual wear, and commodity undergarments.

[0068] The adhesive film compositions described herein the adhesive film compositions disclosed herein include a styrene-ethylene / butylene-styrene triblock copolymer, a white mineral oil, and optionally, a tackifier.

[0069] Styrene-Ethylene / Butylene-Styrene Triblock Copolymer

[0070] The adhesive film compositions disclosed herein comprise a styrene-ethylene / butylene-styrene triblock copolymer. The styrene-ethylene / butylene-styrene triblock copolymer is included to impart adhesion, elasticity, and surface tack to the adhesive film compositions.

[0071] In embodiments, the adhesive film composition may comprise, based on a total weight of the adhesive film composition, 20 wt%to 95 wt%of the styrene-ethylene / butylene-styrene triblock copolymer. In embodiments, the amount of the styrene-ethylene / butylene-styrene triblock copolymer in the adhesive film composition may be, based on a total weight of the adhesive film composition, greater than or equal to 20 wt%, greater than or equal to 25 wt%, greater than or equal to 30 wt%, greater than or equal to 35 wt%, greater than or equal to 40 wt%, greater than or equal to 45 wt%, greater than or equal to 50 wt%, greater than or equal to 55 wt%, greater than or equal to 60 wt%, greater than or equal to 65 wt%, greater than or equal to 70 wt%, greater than or equal to 75 wt%, greater than or equal to 80 wt%, or even greater than or equal to 85 wt%. In embodiments, the amount of the styrene-ethylene / butylene-styrene triblock copolymer in the adhesive film composition may be, based on a total weight of the adhesive film composition, less than or equal to 95 wt%, less than or equal to 90 wt%, less than or equal to 85 wt%, less than or equal to 80 wt%, less than or equal to 75 wt%, less than or equal to 70 wt%, less than or equal to 65 wt%, less than or equal to 60 wt%, less than or equal to 55 wt%, less than or equal to 50 wt%, or even less than or equal to 45 wt%. In embodiments, the amount of the styrene-ethylene / butylene triblock copolymer in the adhesive film composition may be, based on a total weight of the adhesive film composition, from 85 wt%to 95 wt%, from 87 wt%to 94 wt%, or from 89 wt%to 93 wt%, from 20 wt%to 55 wt%, from 25 wt%to 53 wt%, from 30 wt%to 50 wt%, from 35 wt%to 47 wt%, from 38 wt%to 45 wt%, from 40 wt%to 44 wt%, or any and all sub-ranges formed from any of these endpoints.

[0072] In embodiments, the styrene-ethylene / butylene-styrene triblock copolymer may have a minimum molecular weight (e.g., greater than or equal to 90, 000 grams per mole (g / mol) ) such that the adhesive film composition to impart elastic recovery to the adhesive film composition. The molecular weight of the styrene-ethylene / butylene-styrene triblock copolymer may be limited (e.g., less than or equal to 140, 000 g / mol) to allow the adhesive film composition to be made into a film or webbing. Accordingly, in embodiments, the styrene-ethylene / butylene-styrene triblock copolymer may have a weight average molecular weight of 90, 000 g / mol to 140, 000 g / mol.

[0073] In embodiments, the styrene-ethylene / butylene-styrene triblock copolymer may have a average minimum bound styrene content (e.g., greater than or equal to 18 wt%) such the styrene-ethylene-butylene-styrene separates into distinct rubbery and plastic phases in the adhesive film composition. The average minimum bound styrene refers to the weight percentage of the bound styrene of one or more species of styrene-ethylene-butylene-styrene out of the total weight of one or more species of styrene-ethylene-butylene-styrene. The weight percent of bound styrene content may be limited (e.g., less than or equal to 27 wt%) so that there is a balance of elastic phase and plastic phase in the adhesive film composition in order to develop elastic recovery. Accordingly, in embodiments, the styrene-ethylene / butylene-styrene triblock copolymer may have a bound styrene content of 18 wt%to 27 wt%, based on the total weight of the styrene-ethylene / butylene-styrene triblock copolymer. In embodiments, the bound styrene content of the styrene-ethylene / butylene-styrene triblock copolymer may, based on the total weight of the styrene-ethylene / butylene-styrene triblock copolymer, greater than or equal to 18 wt%, greater than or equal to 19 wt%, or even greater than or equal to 20 wt%. In embodiments, the bound styrene content of the styrene-ethylene / butylene-styrene triblock copolymer may be, based on the total weight of the styrene-ethylene / butylene-styrene triblock copolymer, less than or equal to 27 wt%, less than or equal to 26.5 wt%, or even less than or equal to 26 wt%. In embodiments, the bound styrene content of the styrene-ethylene / butylene triblock copolymer may be, based on a total weight of the styrene-ethylene / butylene-styrene triblock copolymer, from 18 wt%to 27 wt%, from 18 wt%to 26.5 wt%, from 18 wt%to 26 wt%, from 19 wt%to 27 wt%, from 19 wt%to 26.5 wt%, from 19 wt%to 26 wt%, from 20 wt%to 27 wt%, from 20 wt%to 26.5 wt%, or even from 20 wt%to 3260 wt%or any and all sub-ranges formed from any of these endpoints.

[0074] In embodiments, the styrene-ethylene / butylene-styrene triblock copolymer may have a polydispersity from 1.0 to 3.0 such that the adhesive film composition is able to flow so that it may be made into a film or webbing. In embodiments, the polydispersity of the styrene-ethylene / butylene-styrene triblock copolymer may be greater than or equal to 1.0, greater than or equal to 1.1, or even greater than or equal to 1.2. In embodiments, the polydispersity of the styrene-ethylene / butylene-styrene triblock copolymer may be less than or equal to 1.3, less than or equal to 1.2, or even less than or equal to 1.1. In embodiments, the polydispersity of the styrene-ethylene / butylene-styrene triblock copolymer may be from 1.0 to 1.3, from 1.0 to 1.2, from 1.0 to 1.1, from 1.1 to 1.3, from 1.1 to 1.2, or even from 1.2 to 1.3, or any and all sub-ranges formed from any of these endpoints.

[0075] Suitable styrene-ethylene / butylene-styrene triblock copolymers are available under the KRATON brand from Kraton, such as grade G1642 or MD1648 V or under the LCY brand such as LCY 7550U.

[0076] White Mineral Oil

[0077] The adhesive film compositions disclosed herein comprise a white mineral oil. The white mineral oil is included in the adhesive film composition to impart processability to the adhesive film composition to, for example, allow the adhesive film composition to be extruded so that it can be made into a film. The white mineral oil may also balance the viscosity and melt flow rate of the adhesive film composition at processing temperatures to allow the allow the adhesive film composition to be extruded so that it can be made into a film.

[0078] In embodiments, the white mineral oil may have a kinematic viscosity at 40℃ in the range of 15 mm2 / sto 100 mm2 / s. In embodiments, the kinematic viscosity at 40℃ may be less than or equal to 100 mm2 / s, less than or equal to 95 mm2 / s, less than or equal to 90 mm2 / s, less than or equal to 85 mm2 / s, or less than or equal to 80 mm2 / s. In embodiments, the kinematic viscosity at 40℃ may be greater than or equal to 10 mm2 / s, greater than or equal to 11 mm2 / s, greater than or equal to 12 mm2 / s, greater than or equal to 14 mm2 / s, or greater than or equal to 15 mm2 / s. In embodiments, the kinematic viscosity at 40℃ may be in the range of 10 mm2 / sto 100 mm2 / s, in the range of 11 mm2 / sto 95 mm2 / s, in the range of 12 mm2 / sto 90 mm2 / s, in the range of 14 mm2 / sto 85 mm2 / s, or in the range of 15 mm2 / sto 80 mm2 / s.

[0079] In embodiments, the adhesive film composition may comprise, based on a total weight of the adhesive film composition, 5 wt%to 40 wt%of the white mineral oil. In embodiments, the amount of the white mineral oil may be, based on a total weight of the adhesive film composition, greater than or equal to 5 wt%, greater than or equal to 6 wt%, greater than or equal to 7 wt%greater than or equal to 10 wt%, greater than or equal to 15 wt%, greater than or equal to 20 wt%, . In embodiments, the amount of the white mineral oil in the adhesive film composition may be, based on a total weight of the adhesive film composition, less than or equal to 40 wt%, less than or equal to 35 wt%, less than or equal to 30 wt%, less than or equal to 25 wt%, less than or equal to 20 wt%, or even less than or equal to 15 wt%. In embodiments, the amount of the white mineral oil in the adhesive film composition may be, based on a total weight of the adhesive film composition, from 5 wt%to 15 wt%, from 6 wt%to 15 wt%, from 7 wt%to 15 wt%, from 5 wt%to 10 wt%, from 6 wt%to 10 wt%, from 7 wt%to 10 wt%, from 10 wt%to 40 wt%, 15 wt%to 40 wt%, 20 wt%to 40 wt%, from 10 wt%to 35 wt%, 15 wt%to 35 wt%, 20 wt%to 35 wt%, from 10 wt%to 30 wt%, 15 wt%to 30 wt%, 20 wt%to 30 wt%, from 10 wt%to 25 wt%, 15 wt%to 25 wt%, or 20 wt%to 25 wt%, or any and all sub-ranges formed from any of these endpoints.

[0080] Suitable white mineral oils are commercially available under the HYDROBRITE brand from Sonneborn, such as grades 380, 100, and 550.

[0081] Tackifier

[0082] The adhesive film compositions disclosed herein optionally comprise a tackifier. The tackifier may be included in the adhesive film composition to impart adhesion and surface tack.

[0083] The adhesive film composition may comprise a minimum amount of tackifier (i.e., greater than 0 wt%) to impart adhesion to the adhesive film composition. The amount of the tackifier may be limited (e.g., less than or equal to 40 wt%) to ensure that the surface tack is below a certain threshold to allow for processing in equipment and handling. Accordingly, in embodiments, the adhesive film composition may comprise, based on a total weight of the adhesive film composition, 0 wt%to 40 wt%of the tackifier. In embodiments, the amount of the tackifier may be, based on a total weight of the adhesive film composition, greater than or equal to 0 wt%, greater than or equal to 5 wt%, greater than or equal to 10 wt%, greater than or equal to 15 wt%, or even greater than or equal to 19 wt%. In embodiments, the amount of the tackifier in the adhesive film composition may be, based on a total weight of the adhesive film composition, less than or equal to 40 wt%, less than or equal to 35 wt%, less than or equal to 30 wt%, less than or equal to 27 wt%, less than or equal to 25 wt%, or even less than or equal to 23 wt%. In embodiments, the amount of the tackifier in the adhesive film composition may be, based on a total weight of the adhesive film composition, for 0 wt%to 40 wt%, from 0 wt%to 35 wt%, from 0 wt%to 30 wt%, from 0 wt%to 27 wt%, from 0 wt%to 25 wt%, from 0 wt%to 23 wt%, from 5 wt%to 40 wt%, from 5 wt%to 35 wt%, from 5 wt%to 30 wt%, from 5 wt%to 27 wt%, from 5 wt%to 25 wt%, from 5 wt%to 23 wt%, from 10 wt%to 40 wt%, from 10 wt%to 35 wt%, from 10 wt%to 30 wt%, from 10 wt%to 27 wt%, from 10 wt%to 25 wt%, from 10 wt%to 23 wt%, from 15 wt%to 40 wt%, from 15 wt%to 35 wt%, from 15 wt%to 30 wt%, from 15 wt%to 27 wt%, from 15 wt%to 25 wt%, from 15 wt%to 23 wt%, from 19 wt%to 40 wt%, from 19 wt%to 35 wt%, from 19 wt%to 30 wt%, from 19 wt%to 27 wt%, from 19 wt%to 25 wt%, or even from 19 wt%to 23 wt%, or any and all sub-ranges formed from any of these endpoints.

[0084] In embodiments, the tackifier may comprise a minimum molecular weight (e.g., greater than or equal to 500 g / mol) to maintain viscosity below a certain threshold such that it may be made into a film. The molecular weight of the tackifier may be limited (e.g., less than or equal to 5000 g / mol) so that the tackifier is able to disperse in the adhesive film composition and associate with the other compounds in the adhesive film composition. Accordingly, in embodiments, the tackifier may comprise molecular weight of 500 g / mol to 5000 g / mol. In embodiments, the tackifier in the adhesive film composition may comprise a molecular weight of greater than or equal to 500 g / mol, greater than or equal to 1000 g / mol, or even greater than or equal to 2000 g / mol. In embodiments, the amount of the tackifier in the adhesive film composition may comprise a molecular weight of less than or equal to 5000 g / mol, less than or equal to 4000 g / mol, or even less than or equal to 3000 g / mol. In embodiments, the tackifier in the adhesive film composition may comprise a molecular weight from 500 g / mol to 5000 g / mol, from 500 g / mol to 4000 g / mol, from 500 g / mol to 3000 g / mol, from 1000 g / mol to 5000 g / mol, from 1000 g / mol to 4000 g / mol, from 1000 g / mol to 3000 g / mol, from 2000 g / mol to 5000 g / mol, from 2000 g / mol to 4000 g / mol, or even from 2000 g / mol to 3000 g / mol, or any and all sub-ranges formed from any of these endpoints.

[0085] In embodiments, the tackifier may comprise a minimum glass transition temperature (e.g., greater than or equal to 50 ℃) such that the adhesive film composition does not soften at the temperature of the environment or at the body temperature of the wearer. The glass transition temperature of the tackifier may be limited (e.g., less than or equal to 100 ℃) so that the adhesive film composition is able to flow at the temperature at which an adhesive seam film comprising the adhesive film composition is bonded to a fabric. Accordingly, in embodiments, the tackifier may comprise a glass transition temperature from 50 ℃ to 100 ℃. In embodiments, the tackifier in the adhesive film composition may comprise a glass transition temperature greater than or equal to 50 ℃, greater than or equal to 60 ℃, or even greater than or equal to 75 ℃. In embodiments, the tackifier may comprise a glass transition temperature less than or equal to 100 ℃, less than or equal to 90 ℃, or even less than or equal to 80 ℃. In embodiments, the tackifier in the adhesive film composition may comprise a glass transition temperature from 50 ℃ to 100 ℃, from 50 ℃ to 90 ℃, from 50 ℃ to 80 ℃, from 60 ℃ to 100 ℃, from 60 ℃ to 90 ℃, from 60 ℃ to 80 ℃, from 75 ℃ to 100 ℃, from 75 ℃ to 90 ℃, or even from 75 ℃ to 80 ℃, or any and all sub-ranges formed from any of these endpoints.

[0086] In embodiments, the tackifier may comprise a minimum softening temperature (e.g., greater than or equal to 100 ℃) so that the adhesive film composition is able to flow at the temperature at which an adhesive seam film comprising the adhesive film composition is bonded to a fabric. The softening temperature of the tackifier may be limited (e.g., less than or equal to 140 ℃) so that an adhesive seam film comprising the adhesive film composition melts and flows at the temperature at which the film is bonded to a fabric. Accordingly, in embodiments, the tackifier may comprise a softening temperature from 100 ℃ to 140 ℃. In embodiments, the tackifier in the adhesive film composition may comprise a softening temperature greater than or equal to 100 ℃, greater than or equal to 110 ℃, or even greater than or equal to 120 ℃. In embodiments, the tackifier may comprise a softening temperature less than or equal to 140 ℃, less than or equal to 135 ℃, or even less than or equal to 125 ℃. In embodiments, the tackifier in the adhesive film composition may comprise a softening temperature from 100 ℃ to 140 ℃, from 100 ℃ to 135 ℃, from 100 ℃ to 125 ℃, from 110 ℃ to 140 ℃, from 110 ℃ to 135 ℃, from 110 ℃ to 125 ℃, from 120 ℃ to 140 ℃, from 120 ℃ to 135 ℃, or even from 120 ℃ to 135 ℃, or any and all sub-ranges formed from any of these endpoints.

[0087] The glass transition temperature and the softening temperature of the tackifier may vary based on the weight average molecular weight of the tackifier. Thus, the weight average molecular weight of the tackifier may be selected based on the desired glass transition temperature and softening temperature. As the weight average molecular weight increases, the glass transition temperature and the softening temperature will also increase. The softening temperature is the temperature at which the tackifier will bond with fabric to form a seam. For example, if bonding of the adhesive film composition to fabric is desired at a temperature of 100 ℃, then a tackifier with a weight average molecular weight near 500 g / mol may be selected. As another example, if bonding of the adhesive film composition to fabric is desired at a temperature of 140 ℃, then a tackifier with a weight average molecular weight near 5000 g / mol may be selected.

[0088] Suitable tackifiers are commercially available under the brand name PLASTOLYN from Synthomer, such as grade 290, under the brand name KRISTALEX from Synthomer, such as grade 5140; and under the brand name ESCOREZ from Exxon Mobile, such as grade 5300.

[0089] Other Additives

[0090] In embodiments, adhesive film compositions as disclosed herein may further comprise one or more optional other additives.

[0091] Suitable other additives may include conventional or commercially available plastics additives. Those skilled in the art of thermoplastics compounding, without undue experimentation, may select suitable additives from available references, for example, E. W. Flick, “Plastics Additives Database, ” Plastics Design Library (Elsevier 2004) .

[0092] Optional other additives may be used in any amount that is sufficient to obtain a desired processing or performance property for the material or component formed therefrom. The amount should not be wasteful of the additive nor detrimental to the processing or performance of the material or article formed therefrom.

[0093] Non-limiting examples of optional other additives may include one or more of antioxidants; nucleating agents; colorants (e.g., pigments and / or dyes) ; inorganic mineral fillers; mineral oils, flame retardants; glass beads, glass flakes, and glass fibers; impact modifiers; micas; slip and anti-blocking agents; ultraviolet light absorbers; and waxes.

[0094] Method of Preparing Adhesive Film Composition

[0095] In embodiments, a method of preparing an adhesive film composition may comprise combining a styrene-ethylene / butylene-styrene triblock copolymer, a white mineral oil, and optionally a tackifier, as disclosed herein, for example, a single screw extruder or a twin screw extruder.

[0096] The extruder may be operated at a temperature from 125 ℃ to 450 ℃, from 125 ℃ to 400 ℃, from 125 ℃ to 375 ℃, from 180 ℃ to 450 ℃, from 180 ℃ to 400 ℃, from 180 ℃ to 375 ℃, from 200 ℃ to 450 ℃, from 200 ℃ to 400 ℃, or even from 200 ℃ to 375 ℃, or any and all sub-ranges formed from any of these endpoints.

[0097] The extruder may be operated at a shear rate from 100 s-1 to 10000 s-1, from 100 s-1 to 5000 s-1, from 100 s-1 to 2500 s-1, from 500 s-1 to 10000 s-1, from 500 s-1 to 5000 s-1, from 500 s-1 to 2500 s-1, from 1000 s-1 to 10000 s-1, from 1000 s-1 to 5000 s-1, or even from 1000 s-1 to 2500 s-1, or any and all sub-ranges formed from any of these endpoints.

[0098] Operating the extruder at the temperatures and shear rates disclosed herein may ensure the flow and homogenous mixing of the styrene-ethylene / butylene-styrene triblock copolymer, white mineral oil, and optionally, tackifier. In some embodiments, the adhesive film composition may be pelletized after it is extruded.

[0099] Adhesive Film Composition

[0100] As described herein, the styrene-ethylene / butylene-styrene triblock copolymer, white mineral oil, and optionally tackifier help to achieve an adhesive film composition that may be used to form the a thin adhesive seam film. Moreover, the adhesive film compositions may exhibit desirable adhesion or bonding strength, elasticity, elastic recovery, and / or surface tack.

[0101] The ability to make a thin adhesive seam film from an adhesive film composition is dependent on the various properties of the adhesive film composition and the quantities and properties of the individual components in the adhesive film composition. Relevant properties of the adhesive film composition may include elasticity, elastic recovery, melt flow rate, adhesion, and viscosity. Relevant properties of the individual properties may include the molecular weight of the components.

[0102] Advantageously the selection and the amounts of the individual components of the adhesive film composition may be extruded into a thin adhesive seam film. The properties of the adhesive film composition harmonize to be able to be processed into a thin adhesive seam. Accordingly, changes to one or more properties may be offset by making responsive changes to one or more other properties. However, in some instances, if one or more properties is too far out of balance, changes to one or more other properties may not be sufficient to form a thin adhesive seam film. Thus, balancing of the quantities and properties of the individual components of the adhesive film composition may be important to achieving a thin adhesive seam film.

[0103] In embodiments, the adhesive film composition may have a peel force greater than or equal to 700 newton per linear meter (N / m) , to ensure sufficient bonding to various materials, such as nylon and polyester. In embodiments, the adhesive film composition may have a peel force greater than or equal to 700 N / m, greater than or equal to 750 N / m, greater than or equal to 800 N / m, greater than or equal to 850 N / m, or greater than or equal to 900 N / m. In embodiments, the adhesive film composition may have a peel force less than or equal to 1300 N / m, less than or equal to 1275 N / m, less than or equal to 1250 N / m, less than or equal to 1225 N / m, or less than or equal to 1200 N / m. In embodiments, the adhesive film composition may have a peel force in the range of 700 N / m to 1300 N / m, in the range of 750 N / m to 1275 N / m in the range of 800 N / m to 1250 N / m in the range of 750 N / m to 1225 N / m, or in the range of 900 N / m to 1200 N / m.

[0104] In embodiments, the adhesive film composition may have a melt index from 35 g / 10 min to 85 g / 10 min, as measured according to ASTM D1238 at 190 ℃ and under 2.16 kg load. In embodiments, the adhesive film composition may have a melt index of greater than or equal to 35 g / 10 min, greater than or equal to 37 g / min, or even greater than or equal to 40 g / min, as measured according to ASTM D1238 at 190 ℃ and under 2.16 kg load. In embodiments, the adhesive film composition may have a melt index of less than or equal to 80 g / 10 min, less than or equal to 78 g / min, or even less than or equal to 76 g / min, as measured according to ASTM D1238 at 190 ℃ and under 2.16 kg load. In embodiments, the adhesive film composition may have a melt index, as measured according to ASTM D1238 at 190 ℃ and under 2.16 kg load of from 35 g / 10 min to 80 g / 10 min, from 35 g / 10 min to 78 g / 10 min, from 35 g / 10 min to 76 g / 10 min, from 37 g / 10 min to 80 g / 10 min, from 37 g / 10 min to 78 g / 10 min, from 37 g / 10 min to 76 g / 10 min, from 40 g / 10 min to 80 g / 10 min, from 40 g / 10 min to 78 g / 10 min, from 40 g / 10 min to 76 g / 10 min, or any and all sub-ranges formed from any of these endpoints.

[0105] In embodiments, the adhesive film composition may have a surface tack such that the adhesive film composition may be manually handled with ease.

[0106] As described herein, the adhesive film compositions may be used to form any article that requires a thin adhesive seam film. The adhesive film compositions are especially useful in seamless construction of performance apparel, intimate apparel, casual wear, and commodity undergarments.

[0107] Method of Forming Adhesive Seam Film

[0108] A method of forming an adhesive seam film may comprise preparing an adhesive film composition and extruding the adhesive film composition to form a film. The adhesive seam film may comprise an adhesive film composition according to one or more of the embodiments described herein.

[0109] For example, the prepared adhesive film composition or components thereof may be fed into an extruder and melt-mixed at a temperature greater than or equal to the melting temperature of the adhesive film composition. In embodiments, the adhesive film composition may be melt be melt-mixed at a temperature from 150 ℃ and 240 ℃ and for a time from 10 seconds (sec) to 120 sec. In embodiments, the adhesive film composition may be melt be melt-mixed at a temperature from 150 ℃ to 240 ℃, from 150 ℃ to 230 ℃, from 150 ℃ to 220 ℃, from 160 ℃ to 240 ℃, from 160 ℃ to 230 ℃, from 160 ℃ to 220 ℃, from 170 ℃ to 240 ℃, from 170 ℃ to 230 ℃, or even from 170 ℃ to 220 ℃, or any and all sub-ranges formed from any of these endpoints. In embodiments, the adhesive film composition may be melt be melt-mixed for a time from 10 sec to 120 sec, from 10 sec to 90 sec, 10 sec to 60 sec, from 20 sec to 120 sec, from 20 sec to 90 sec, 20 sec to 60 sec, 30 sec to 120 sec, from 30 sec to 90 sec, or even from 30 sec to 60 sec, or any and all sub-ranges formed from any of these endpoints.

[0110] The adhesive film composition may be extruded from the extruder to form the film.

[0111] Adhesive Seam Film

[0112] Referring now to FIG. 1, an adhesive seam film is shown at 50. The adhesive seam film 50 comprises a length l, a width w, and a thickness t. The adhesive seam film may comprise the adhesive film composition according to one or more of the embodiments described herein.

[0113] As described herein, the adhesive film compositions may be used to form thin adhesive seam films. In embodiments, the adhesive seam film 50 may have an appropriate thickness to provide minimal bulk in seamless construction and / or to achieve enhanced performance. For example, in embodiments, the adhesive seam film 50 may have a thickness t of 25 μm to 250 μm. In some embodiments, the adhesive seam film 50 may have a thickness t greater than or equal to 25 μm, greater than or equal to 30 μm, or even greater than or equal to 50 μm. In embodiments, the adhesive seam film 50 may have a thickness t less than or equal to 130 μm, less than or equal to 115 μm, or even less than or equal to 100 μm. In embodiments, the adhesive seam film 50 may have a thickness t from 25 μm to 130 μm, from 25 μm to 115 μm, from 25 μm to 100 μm, from 30 μm to 130 μm, from 30 μm to 115 μm, from 30 μm to 100 μm, from 50 μm to 130μm, from 50 μm to 115 μm, or even from 50 μm to 100 μm, or any and all sub-ranges formed from any of these endpoints. The thickness of the adhesive seam film 50 may be determined by measuring the adhesive seam film 50 thickness t with a thickness gauge.

[0114] In embodiments, the width w may be selected to conform to the width of the manufacturing equipment used to conform to the width of a fabric to which the adhesive seam film is to be applied, especially if the adhesive seam film is extruded directly onto the fabric. In embodiments, the width w may be further reduced after manufacturing by cutting or slitting the film, especially if the film is extruded on to a release liner. For example, in embodiments, the adhesive seam film 50 may have a width w from 5 cm to 40 cm. In embodiments, the adhesive seam film 50 may have a width w greater than or equal to 5 cm, greater than or equal to 10 cm, or even greater than or equal to 20 cm. In embodiments, the adhesive seam film may have a width w less than or equal to 40 cm or even less than or equal to 30 cm. In embodiments, the adhesive seam film may have a width w from 5 cm to 40 cm, from 5 cm to 30 cm, from 10 cm to 40 cm, from 10 cm to 30 cm, from 20 cm to 40 cm, from 20 cm to 30 cm, or any and all sub-ranges formed from any of these endpoints.

[0115] In embodiments the adhesive seam film 50 may be coated with a polymeric powder or dusting agent to ensure ease of manual handling. Examples of a suitable polymeric powders and dusting agents may include powdered polyethylene and powdered polypropylene.

[0116] In some embodiments, the adhesive seam film may be part of a multilayer composite comprising two or more films. For example, referring now to FIG. 2, a multilayer composite is shown at 100. The multilayer composite 100 includes a first adhesive seam film 102, a second adhesive seam film 104, and a third adhesive seam film 106. Each of the first adhesive seam film 102, the second adhesive seam film 104, and the third adhesive seam film 106 have a first surface 102a, 104a, and 106a, respectively, and an opposing second surface 102b, 104b, and 106b, respectively. The opposing second surface 102b of the first adhesive seam film 102 may be bonded to the first surface 104a of the second adhesive seam film 104. The opposing second surface 104b of the second film 104 may be bonded to the first surface 106a of the third adhesive seam film 106.

[0117] At least one film in the multilayer composite may be an adhesive film composition as described herein. In some embodiments, all of the films in the multilayer composite are adhesive seam films. In some embodiments, each film in the multilayer composite has the same composition as the other films in the multilayer composite. In some embodiments, each film in the multilayer composite has a different composition as the other films in the multilayer composite. In some embodiments, some of the films in the multilayer composite have the same compositions and some the films in the multilayer composition have different compositions.

[0118] In some embodiments, one or more films in the multilayer composite may enhance a specific property of the multilayer composite. For example, one or more layers of the multilayer composite may decrease surface tack to enhance the ease of handling of the multilayer composite. In some embodiments, the adhesive seam film may comprise one or more outer layers of the multilayer composite. In some embodiments, the adhesive seam film may impart increased peel force to the multilayer composite. In some embodiments, the inner layer of film may comprise a thickness greater than the thickness of the adhesive seam film. In some embodiments, the inner layer of film may impart elasticity and elastic recovery to the multilayer composite.

[0119] In some embodiments, the adhesive seam film may be part of a multilayer composite comprising the adhesive seam film adhered to a fabric backing. For example, referring now to FIG. 3, a multilayer composite with the adhesive seam film adhered to a fabric backing is shown at 200. The multilayer composite with the adhesive seam film adhered to a fabric backing 200 may include the first adhesive seam film 102, the second adhesive seam film 104, and the third adhesive seam film 106 as shown and described with respect to FIG. 2. The multilayer composite 200 further includes a fabric backing 210. The opposing second surface 106b of the third adhesive seam film 106 may be bonded to the first surface 210a of the fabric backing 210. The fabric back 210 may comprise nylon, polyester, acrylic, polyurethane, olefin, neoprene, acetate, elastane, or a combination thereof. In some embodiments, the adhesive seam film may be part of a multilayer composite comprising the adhesive seam film adhered to a release liner. For example, referring now to FIG. 4, a multilayer composite comprising the adhesive seam film adhered to a release liner is shown at 300. The multilayer composite with the adhesive seam film adhered to a release liner 300 may include the first adhesive seam film 102, the second adhesive seam film 104, and the third adhesive seam film 106 as shown and described with respect to FIG. 2. The multilayer composite 300 further includes a release liner 330. The opposing second surface 106b of the third adhesive seam film 106 may be in contact with the first surface 330a of the release liner 330. In embodiments, the release liner 330 may comprise paper. The paper may be coated with a release material. The release material may decrease the force needed to remove the adhesive seam film from the release liner. The release material may comprise silicone.

[0120] In some embodiments, the release liner may be removable. In some embodiments, the multilayer composite comprising the adhesive seam film adhered to a release liner may comprise release liners on both surfaces of the multilayer composite. In some embodiments, the multilayer composite comprising the adhesive seam film adhered to a release liner may comprise a release liner on only one surface of the multilayer composite. In some embodiments, the release liner may be removed prior to using the multilayer composite.

[0122] In some embodiments, the adhesive seam film may be cut or slit to the desired width and then wound on a release liner as a roll. This roll may then be fed into an application machine and the application machine may then be used to apply the adhesive seam film onto fabric during apparel construction. The application machine may apply the adhesive seam film to fabric by unwinding the roll, bringing the adhesive seam film in to contact with the apparel, and removing and discarding the release liner.

[0123] Method of Forming Adhesive Webbing

[0124] A method of forming an adhesive webbing may comprise preparing an adhesive webbing composition and extruding the adhesive composition to form a webbing. The adhesive webbing composition may comprise an adhesive composition according to one or more of the embodiments described herein

[0125] For example, the prepared adhesive webbing composition or components thereof may be fed into an extruder and melt-mixed at a temperature and for a time the same or similar to that described herein with respect to the method of forming an adhesive film.

[0126] The adhesive webbing composition may be extruded from the extruder.

[0127] As the adhesive composition is being extruded from the extruder, a die with multiple die holes at the end of the extruder may rotate and the adhesive composition may pass through these die holes as a filament on a traveling wire. The rotation of the die with multiple holes will cause the filaments to lay on top of each other and fuse together as a webbing.

[0128] Adhesive Webbing

[0129] Referring now to FIG. 5, an adhesive webbing is shown at 60. The adhesive webbing 60 comprises a length l, a width w, and a thickness t. As shown in FIG. 5, adhesive webbing 60 comprise filaments 62 that may comprise the adhesive composition according to embodiments described and that are fused together to form the adhesive webbing 60. The adhesive webbing 60 may comprise the adhesive composition according to embodiments described herein.

[0130] The adhesive webbing 60 may have the same or similar thickness t and / or width w as described herein with respect to the adhesive film.

[0131] In embodiments, the use of an adhesive webbing may be desirable for applications where less fabric surface area needs to be bonded to an adhesive structure or applications where cost saving is desired.

[0132] In embodiments, similar to the adhesive film as described herein, the adhesive webbing 60 may be coated with a polymeric powder or dusting agent to ensure ease of manual handling. Examples of polymeric powders and dusting agents include powdered polyethylene and powdered polypropylene.

[0133] Method of Preparing a Seam

[0134] Referring now to FIG. 6, a method of preparing a seam comprises supplying a first section of fabric 440, a second section of fabric 460, and an adhesive layer 410; situating the adhesive layer 410 between the first section of fabric 440 and the second section of fabric 460 to form a seam section 450; and heating the seam section 450 such that the adhesive layer 410 adheres the first section of fabric 440 and the second section of fabric 460. As shown in FIG. 6, the second section of fabric 460 at least partially overlaps the first section of fabric 440. These steps may be performed in sequence. The adhesive layer 410 may comprise an adhesive composition according to one or more of the embodiments described herein. The adhesive layer 410 may be an adhesive film or an adhesive webbing.

[0135] Heating the seam section 450 may be performed using a hot iron or hot air. The seam section 450 may be heated to a temperature greater than or equal to 100 ℃, greater than or equal to 110 ℃, or even greater than or equal to 120 ℃. In embodiments, the seam section may be heated to a temperature less than or equal to 140 ℃ or even less than or equal to 130 ℃. In embodiments, the seam section may be heated to a temperature from 100 ℃ to 140 ℃, from 100 ℃ to 130 ℃, from 110 ℃ to 140 ℃, from 110 ℃ to 130 ℃, from 120 ℃ to 140 ℃, or even from 120 ℃ to 130 ℃, or any and all sub-ranges formed from any of these endpoints. In some embodiments, the seam section 450 may be heated to the softening temperature of the adhesive composition.

[0136] In embodiments, the seam section 450 may be compressed manually or by a compression machine. The seam section 450 may be compressed at a pressure of greater than or equal to 5 kilopascal (kPa) , greater than or equal to 15 kPa, or even greater than or equal to 30 kPa. In embodiments, the seam section may be compressed at a pressure of less than or equal to 200 kPa, less than or equal to 100 kPa, or even less than or equal to 50 kPa. In embodiments, the seam section 450 may be heated to a temperature from 5 kPa to 200 kPa, from 5 kPa to 100 kPa, from 5 kPa to 50 kPa, from 15 kPa to 200 kPa, from 15 kPa to 100 kPa, from 15 kPa to 50 kPa, from 30 kPa to 200 kPa, from 30 kPa to 100 kPa, or even from 30 kPa to 50 kPa, or any and all sub-ranges formed from any of these endpoints.

[0137] Seam

[0138] Referring again to FIG. 6, a seam is shown at 400. The seam 400 includes a first section of fabric 440, a second section of fabric 460, and an adhesive layer 410. The adhesive layer 410 comprises an adhesive film as described herein or an adhesive webbing as described herein. Each of the first section of fabric 440, the second section of fabric 460, and the adhesive layer 410 have a first surface 440a, 460a, and 410a, respectively, and an opposing second surface 440b, 460b, and 410b, respectively. At least a portion of the opposing second surface 440b of the first section of fabric 440 may be bonded to the first surface 410a of the adhesive layer 410. At least a portion of the first surface 460a of the second section of fabric 460 may be bonded to the opposing second surface 410b of the adhesive layer 410. The adhesive layer 410 is in the seam section 450. In embodiments, the adhesive layer 410 may be disposed between the first section of fabric 440 and the second section of fabric 460.

[0139] Referring now to FIG. 7, another seam is shown at 500, where the first section of fabric 540 fully overlaps the second section of fabric 560. The seam 500 includes a first section of fabric 540, a second section of fabric 560, and an adhesive layer 510. Each of the first section of fabric 540, the second section of fabric 560, and the adhesive layer 510 have a first surface 540a, 560a, and 510a, respectively, and an opposing second surface 540b, 560b, and 510b, respectively. At least a portion of the opposing second surface 540b of the first section of fabric 440 may be bonded to the first surface 510a of the adhesive layer 510. At least a portion of the first surface 560a of the second section of fabric 560 may be bonded to the opposing second surface 510b of the adhesive layer 510. The adhesive layer 510 is in the seam section 550. In embodiments, as shown in FIG. 7 the adhesive layer 510 may extend partially along the length of the first and second sections of fabric 540, 560. In other embodiments, the adhesive layer 510 may extend along the entire length of the first and second sections of fabric 540, 560.

[0140] In some embodiments, the seam section may include stitches attaching the first section of fabric to the second section of fabric. For example, referring to FIG. 8, the seam section 550 may include stitches 620. In some embodiments, the seam section is a stitchless seam section, as shown in FIGS. 6 and 7.

[0141] The first and second sections of fabric of the seam may each comprise nylon, polyester, acrylic, polyurethane, olefin, neoprene, acetate, elastane, and combinations thereof. Examples of olefins include polypropylene polyethylene, and combinations thereof. Examples of neoprenes include polychloroprene. Examples of elastanes includes spandex. Examples of spandex include  commercially available from DOW Chemical. In some embodiments, the first section of fabric and the second section of fabric may have the same compositions. In some embodiments, the first section of fabric and the second section of fabric may have different compositions.

[0142] In some embodiments, the multilayer composite comprising the adhesive seam film adhered to a fabric backing may be formed by extruding the film directly on to the fabric and bonding the adhesive seam film to the fabric to make the apparel waterproof. For example, waterproof apparel may be made by stitching or sewing with thread and then covering the holes created by the stitching or sewing with thread by bonding the holes and the surrounding fabric with the adhesive seam film.

[0143] EXAMPLES

[0144] Non-limiting examples of various embodiments of the disclosed invention are provided.

[0145] Table 1 below shows sources of ingredients of adhesive film compositions.

[0146] [Corrected under Rule 26, 02.04.2024]Table 1

[0147] The formulations of the Examples were compounded in a twin screw extruder at a temperature of 165 ℃ to 205 ℃. Pellets of the formulations of the Examples were then produced using a Brabender extruder with a film die attached to the end of the Brabender extruder at a temperature of 165 ℃ to 200 ℃.

[0148] The Example Adhesive Seam Films were situated between two layers of fabric and compressed at a pressure of 0.2MPa for 30 seconds at 150 ℃ using a press machine.

[0149] Table 2 below shows the formulations used to form and the certain properties of the Example Adhesive Seam Films.

[0150] Table 2

[0151] Every document cited herein is incorporated herein by reference in its entirety unless otherwise specified. The citation of any document is not to be construed as an admission that it is prior art with respect to any invention disclosed or claimed herein. To the extent that any meaning or definition of a term in this document conflicts with any meaning or definition of the same term in a document incorporated by reference, the meaning or definition assigned to that term in this document shall govern.

[0152] It will be apparent that modifications and variations are possible without departing from the scope of the disclosure defined in the appended claims. More specifically, although some aspects of the present disclosure are identified herein as preferred or particularly advantageous, it is contemplated that the present disclosure is not necessarily limited to these aspects.

Claims

An adhesive seam film comprising an adhesive film composition, the adhesive film composition comprising, based on the total weight of the adhesive film composition:20 wt%to 95 wt%of one or more styrene-ethylene / butylene-styrene triblock copolymers, wherein the one or more styrene-ethylene / butylene-styrene triblock copolymer has a weight average molecular weight of 90,000 g / mol to 140,000 g / mol and an average bound styrene content of 18 wt%to 27 wt%, based on the total weight of the styrene-ethylene / butylene-styrene triblock copolymer;5 wt%to 40 wt%of a white mineral oil, wherein the white mineral oil has a kinematic viscosity at 40℃ in the range of 15 mm2 / s to 100 mm2 / s; and0 wt%to 40 wt%of a tackifier, wherein the tackifier has a weight average molecular weight of 500 g / mol to 5000 g / mol, a glass transition temperature of 50 ℃ to 100 ℃, and a softening temperature of 100 ℃ to 140 ℃.wherein the adhesive seam film has a thickness of 50 μm to 100 μm.The adhesive seam film of claim 1, wherein the adhesive seam film has a thickness of 30 μm to 150 μm.The adhesive seam film of any of the preceding claims, wherein the adhesive seam film has a thickness of 50 μm to 100 μm.The adhesive seam film of any of the preceding claims, wherein the adhesive film composition comprises 5 wt%to 30 wt%of the tackifier.The adhesive seam film of any of the preceding claims, wherein the one or more styrene-ethylene / butylene-styrene triblock copolymers includes a first styrene-ethylene / butylene-styrene triblock copolymer having a first bound styrene content and a second styrene-ethylene / butylene-styrene triblock copolymer having a second bound styrene content, and the first bound styrene content is greater than the second bound styrene content.The adhesive seam film of any of the preceding claims, , wherein the adhesive film composition comprises85 wt%to 95 wt%of the one or more styrene-ethylene / butylene-styrene triblock copolymers,5 wt%to 15 wt%of the white mineral oil, and0 wt%to 3 wt%of the tackifier.The adhesive seam film of any of the preceding claims, wherein the adhesive film composition comprises20 wt%to 55 wt%of the one or more styrene-ethylene / butylene-styrene triblock copolymers,20 wt%to 40 wt%of the white mineral oil, and15 wt%to 40 wt%of the tackifier.The adhesive seam film of any of the preceding claims, wherein the adhesive seam film has a width of 5 cm to 40 cm.The adhesive seam film of any of the preceding claims, wherein the adhesive film composition has a melt index of 35 g / 10 min to 80 g / 10 min, as measured according to ASTM D1238 at 190 ℃ and under 2.16 kg load.The adhesive seam film of any of the preceding claims, wherein the styrene-ethylene / butylene-styrene triblock copolymer has a polydispersity of 1.0 to 1.3.The adhesive seam film of any of the preceding claims, wherein the adhesive seam film is a mesh.The adhesive seam film of any of the preceding claims, wherein the adhesive seam film is part of a multilayer composite comprising two or more films.The adhesive seam film of any of the preceding claims, wherein the adhesive seam film is part of a multilayer composite comprising the adhesive seam film adhered to a fabric backing.The adhesive seam film of any of claims 1-12, wherein the adhesive seam film is part of a multilayer composite comprising the adhesive seam film adhered to a release liner.The adhesive seam film of any of the preceding claims, wherein the adhesive seam film is coated with a polymeric powder or dusting agent.A seam comprising:a first section of fabric;a second section of fabric at least partially overlapping the first section of fabric to form a seam section; andthe adhesive seam film of any of the proceeding claims located in the seam section adhering the first section of fabric to the second section of fabric.The seam of claim 16, wherein the adhesive seam film is disposed between the first section of fabric and the second section of fabric.The seam of claim 16 or claim 17, wherein the seam section includes stitches attaching the first section of fabric to the second section of fabric.The seam of claim 16 or claim 17, wherein the seam section is a stitchless seam section.A method of forming an adhesive seam film comprising:preparing an adhesive film composition; andextruding the adhesive film composition to form an adhesive seam film that has a thickness of 25 μm to 250 μm;wherein the adhesive film composition is defined by one of claims 1-5.The method of claim 20, wherein the adhesive film composition comprises 5 wt%to 30 wt%of the tackifier.A method of preparing a seam comprising:supplying a first section of fabric, a second section of fabric, and an adhesive seam film;situating the adhesive seam film between the first section of fabric and the second section of fabric to form a seam section, wherein the second section of fabric at least partially overlaps the first section of fabric; andheating the seam section such that the adhesive seam film adheres the first section of fabric and the second section of fabric,wherein the adhesive seam film compromises an adhesive film composition defined by one of claims 1-5.The method of claim 22, wherein the adhesive film composition comprises 5 wt%to 30 wt%of the tackifier.The method of claim 22 or claim 23, where the step of heating the seam section is performed by a hot iron or hot air.