Adhesive sheet and electronic device

Abstract

Provided is an adhesive sheet having an adhesive layer. The adhesive layer includes a water-dispersible acrylic polymer and a pigment. The water-dispersible acrylic polymer is a polymer synthesized by emulsion polymerization using a reactive emulsifier having a radically polymerizable functional group.

Description

Adhesive sheets and electronic devices

[0001] The present invention relates to a pressure-sensitive adhesive sheet and an electronic device. This application claims priority to Japanese Patent Application No. 2024-105248, filed on June 28, 2024, the entire contents of which are incorporated herein by reference.

[0002] Generally, adhesives (also referred to as pressure-sensitive adhesives; the same applies hereinafter) are in a soft solid (viscoelastic) state at temperatures near room temperature and have the property of easily adhering to an adherend under pressure. Taking advantage of these properties, adhesives are widely used in a variety of applications, for example, for the purpose of joining, fixing, and protecting components within electronic devices, including mobile electronic devices such as smartphones. Furthermore, adhesive sheets having an adhesive layer containing a pigment such as carbon black are used for the purposes of preventing light leakage and anti-reflection from light sources such as backlight modules of liquid crystal display devices in electronic devices, and self-luminous elements such as organic electroluminescence (EL) devices, as well as for the purposes of concealing the adherend, adjusting the appearance of the adherend through the adhesive sheet, and adding design features. Patent Document 1 is an example of a document relating to this type of technology.

[0003] Furthermore, in recent years, there has been a demand for a reduction in the amount of organic solvents used in the production of adhesives, from the perspective of environmental considerations and reducing the use of petroleum resources. For example, the amount of organic solvent used can be reduced by adopting solventless adhesives such as active energy ray-curable adhesives, hot-melt adhesives, and emulsion adhesives. Among these, emulsion-type acrylic adhesives are preferred because they allow the desired properties to be suitably obtained by highly controlling the polymerization reaction of the acrylic monomer. Patent Documents 2 and 3 include technical documents disclosing adhesives containing water-dispersible acrylic polymers obtained by emulsion polymerization.

[0004] Japanese Patent Application Publication No. 2020-66655 Japanese Patent Application Publication No. 2007-154078 Japanese Patent Application Publication No. 2011-90193

[0005] It is also preferable to reduce the amount of organic solvent used in pigment-containing adhesives that can be used in electronic devices, etc. However, as a result of research by the present inventors, it was found that when adhesives containing pigments such as carbon black are formed using water-dispersible acrylic polymers instead of acrylic polymers synthesized by solution polymerization, as described in Patent Document 1, the appearance quality deteriorates when exposed to high temperatures during storage or use. Specifically, even if an adhesive containing a water-dispersible acrylic polymer and a pigment has a good appearance under normal temperature conditions after preparation, when exposed to high temperatures, pinholes and color unevenness occur due to air bubbles in the adhesive. The occurrence of such pinholes can impair the intended light-blocking properties and design properties, and may cause display defects when used in electronic device displays, for example. Since air bubbles causing pinholes were not observed in adhesives containing water-dispersible acrylic polymers that do not contain pigments, this is considered to be a problem unique to adhesives containing water-dispersible acrylic polymers and pigments.

[0006] Patent Document 3 describes that an emulsion-type acrylic pressure-sensitive adhesive for optical films was attached to a polarizing plate, which was then attached to an alkali-free glass plate, and the resulting product was subjected to a heat treatment at 80°C for 500 hours, and the heat durability was evaluated using an optical microscope to check for the presence or absence of bubbles with a maximum length of 200 µm or more and the number of bubbles that were generated. Because the pressure-sensitive adhesive described in Patent Document 3 does not contain a pigment, the heat durability evaluation is thought to be an evaluation of a phenomenon different from the occurrence of pinholes and the like in a pressure-sensitive adhesive containing a water-dispersible acrylic polymer and a pigment under a high-temperature environment.

[0007] The present invention has been made in view of the above circumstances, and aims to provide a pressure-sensitive adhesive sheet having a pressure-sensitive adhesive that contains a water-dispersible acrylic polymer and a pigment and that can maintain good appearance quality even when exposed to a high-temperature environment. Another related aim is to provide an electronic device that includes the pressure-sensitive adhesive sheet.

[0008] According to the present specification, a pressure-sensitive adhesive sheet having a pressure-sensitive adhesive layer is provided. The pressure-sensitive adhesive layer includes a water-dispersible acrylic polymer and a pigment. The water-dispersible acrylic polymer is a polymer synthesized by emulsion polymerization using a reactive emulsifier having a radically polymerizable functional group. The pressure-sensitive adhesive including the water-dispersible acrylic polymer and the pigment as described above can reduce the amount of organic solvent by using the water-dispersible acrylic polymer, and can maintain good appearance quality even when exposed to a high-temperature environment while obtaining the effects of containing the pigment (light-blocking properties, hiding properties, appearance adjustment, design properties, etc.).

[0009] In some embodiments, the PSA sheet has a light transmittance of 15% or less at a wavelength of 550 nm. PSA sheets having such a light transmittance are preferably used in various applications requiring light blocking properties, concealment of adherends, etc.

[0010] In some embodiments, the pigment includes inorganic particles. In embodiments using a pigment including inorganic particles, the effects of the technology disclosed herein can be preferably realized.

[0011] In some embodiments, the pressure-sensitive adhesive layer preferably contains carbon black as a pigment. By using carbon black as a pigment, light transmittance can be efficiently reduced, and a pressure-sensitive adhesive with high light-blocking properties can be preferably obtained. Furthermore, in embodiments using a pressure-sensitive adhesive containing carbon black, the effects of the technology disclosed herein can be preferably achieved.

[0012] In some embodiments, the content of the pigment in the PSA layer is within the range of 0.1 to 15 parts by weight per 100 parts by weight of the water-dispersible acrylic polymer. The technology disclosed herein can be preferably implemented in embodiments in which the pigment is used in an amount within the above range.

[0013] In some embodiments, the thickness of the pressure-sensitive adhesive layer is 1 μm or more and 100 μm or less. The thicker the pressure-sensitive adhesive layer, the more favorably the pressure-sensitive adhesive sheet can exhibit its adhesive properties, such as adhesive strength. Furthermore, a pressure-sensitive adhesive layer having a thickness greater than or equal to a predetermined value is likely to provide excellent light-blocking properties. Furthermore, a pressure-sensitive adhesive sheet having a pressure-sensitive adhesive layer limited to a thickness of 100 μm or less can be easily configured to be thin, which is advantageous in terms of reducing the thickness, weight, and space of the product to which the pressure-sensitive adhesive sheet is applied. On the other hand, in a thin pigment-containing pressure-sensitive adhesive layer, pinholes and the like tend to be noticeable if they occur. The pressure-sensitive adhesive sheet disclosed herein is less likely to develop pinholes and the like even when exposed to a high-temperature environment, and is therefore preferably applicable to a configuration having a thin pressure-sensitive adhesive layer such as the one described above.

[0014] In some embodiments, the PSA sheet is a substrate-less double-sided PSA sheet comprising the PSA layer. The effects of the technology disclosed herein can be preferably achieved in a substrate-less double-sided PSA sheet. Furthermore, since a substrate-less double-sided PSA sheet does not have a substrate, it can be made thinner, which is advantageous in terms of making products to which the double-sided PSA sheet is applied thinner, more compact, and more space-saving. Furthermore, a substrate-less double-sided PSA sheet can maximize the effects of the PSA layer, such as adhesive strength.

[0015] In some other embodiments, the PSA sheet is a substrate-attached double-sided PSA sheet comprising the PSA layer and a supporting substrate layer. Double-sided PSA sheets having a substrate are advantageous in terms of processability and handleability.

[0016] In some embodiments, the PSA sheet has a 180-degree peel strength of 5 N / 20 mm or more against a stainless steel plate. PSA sheets that satisfy this characteristic have good adhesive strength while exhibiting the effects of adding pigments, such as light-blocking properties and design properties, and are therefore preferably used in applications requiring adhesive strength above a certain level.

[0017] The pressure-sensitive adhesive sheet disclosed herein can be preferably used, for example, to bond components of electronic devices, including mobile electronic devices such as smartphones. For example, electronic devices have parts that are visible to the user, and excellent appearance quality is required. Furthermore, due to recent improvements in processing speed, the internal environment of electronic devices is prone to relatively high temperatures. The pressure-sensitive adhesive sheet disclosed herein can suppress the occurrence of pinholes and maintain good appearance quality even when exposed to a high-temperature environment, and can therefore be applied to visible parts of electronic devices to achieve a surface with good appearance quality.

[0018] As described above, the present specification provides an electronic device using any of the pressure-sensitive adhesive sheets disclosed herein, in other words, an electronic device including the pressure-sensitive adhesive sheet.

[0019] Fig. 1 is a cross-sectional view schematically showing one configuration example of an adhesive sheet; Fig. 2 is a cross-sectional view schematically showing another configuration example of an adhesive sheet; Fig. 3 is a cross-sectional view schematically showing another configuration example of an adhesive sheet; Fig. 4 is an exploded perspective view schematically showing a configuration example of a display device.

[0020] Preferred embodiments of the present invention are described below. Matters necessary for carrying out the present invention other than those specifically mentioned in this specification can be understood by those skilled in the art based on the teachings for carrying out the invention described in this specification and the common general technical knowledge at the time of filing. The present invention can be carried out based on the contents disclosed in this specification and the common general technical knowledge in the relevant field. Furthermore, in the following drawings, components and parts that perform the same function may be denoted by the same reference numerals, and redundant descriptions may be omitted or simplified. Furthermore, the embodiments shown in the drawings are schematic to clearly explain the present invention, and do not necessarily accurately represent the size or scale of the pressure-sensitive adhesive sheet of the present invention that is actually provided as a product.

[0021] As used herein, the term "adhesive" refers to a material that exhibits a soft solid (viscoelastic) state in a temperature range around room temperature and has the property of easily adhering to an adherend by pressure, as described above. The adhesive referred to here is generally a material having a complex tensile modulus E ＊ (1Hz) <10 ７ dyne / cm ２ The material may be a material having the properties satisfying the above (typically, a material having the above properties at 25°C).

[0022] In this specification, the term "water-dispersed PSA composition" refers to a composition in which at least a portion of the PSA-forming components are dispersed in water. The water-dispersed type also includes a suspended state and an emulsified state. The concept of the water-dispersed PSA composition includes what is called an emulsion-type PSA composition. In this specification, a PSA (layer) formed from a water-dispersed PSA composition may be referred to as a water-dispersed PSA (layer).

[0023] As used herein, the term "acrylic polymer" refers to a polymer containing more than 50% by weight of monomer units derived from an acrylic monomer as the monomer units constituting the polymer. The acrylic monomer refers to a monomer having at least one (meth)acryloyl group per molecule.

[0024] As used herein, "(meth)acryloyl" refers collectively to acryloyl and methacryloyl. Similarly, "(meth)acrylate" refers collectively to acrylate and methacrylate, and "(meth)acrylic" refers collectively to acrylic and methacrylic.

[0025] <Configuration example of pressure-sensitive adhesive sheet> The pressure-sensitive adhesive sheet disclosed herein may be a substrate-attached pressure-sensitive adhesive sheet having the pressure-sensitive adhesive layer on one or both sides of a non-releasable substrate (support substrate), or may be a substrate-less pressure-sensitive adhesive sheet (i.e., a pressure-sensitive adhesive sheet without a non-releasable substrate) in which the pressure-sensitive adhesive layer is held by a release film. The concept of pressure-sensitive adhesive sheet here may include what are called pressure-sensitive adhesive tapes, pressure-sensitive adhesive labels, pressure-sensitive adhesive films, etc. The pressure-sensitive adhesive sheet disclosed herein may be in the form of a roll or a sheet. Alternatively, it may be a pressure-sensitive adhesive sheet processed into various shapes.

[0026] Examples of the configuration of a double-sided adhesive substrateless pressure-sensitive adhesive sheet (substrateless double-sided pressure-sensitive adhesive sheet) are shown in Figures 1 and 2. The pressure-sensitive adhesive sheet 1 shown in Figure 1 has a configuration in which both surfaces 21A and 21B of a substrateless pressure-sensitive adhesive layer 21 are protected by release films 31 and 32, respectively, with at least the pressure-sensitive adhesive layer side being the release surface. The pressure-sensitive adhesive sheet 2 shown in Figure 2 has a configuration in which one surface (adhesive surface) 21A of the substrateless pressure-sensitive adhesive layer 21 is protected by a release film 31, both of which are release surfaces. When this sheet is rolled up, the other surface (adhesive surface) 21B of the pressure-sensitive adhesive layer 21 abuts against the back surface of the release film 31, so that the other surface 21B is also protected by the release film 31.

[0027] The structure of a PSA sheet according to another configuration example is shown schematically in Figure 3. This PSA sheet 3 is configured as a substrate-attached single-sided PSA sheet comprising a sheet-like support substrate 10 having a first surface 10A and a second surface 10B, and a PSA layer 21 provided on the first surface 10A side. The PSA layer 21 is fixedly provided on the first surface 10A side of the support substrate 10, i.e., without any intention of separating the PSA layer 21 from the support substrate 10. Before use, the PSA sheet 3 may be in a form in which the surface (adhesive surface) 21A of the PSA layer 21 is protected by a release film 31, at least the side facing the PSA layer 21 being a release surface, as shown in Figure 3.

[0028] The structure of a PSA sheet according to yet another configuration example is shown schematically in Figure 4. This PSA sheet 4 is configured as a substrate-attached double-sided PSA sheet comprising a sheet-like support substrate 10 having a first surface 10A and a second surface 10B, a first PSA layer 21 fixedly provided on the first surface 10A side, and a second PSA layer 22 fixedly provided on the second surface 10B side. Before use, the PSA sheet 4 may be in a form in which the surface (first adhesive surface) 21A of the first PSA layer 21 and the surface (second adhesive surface) 22A of the second PSA layer 22 are protected by release films 31, 32, as shown in Figure 4.

[0029] The technology disclosed herein can be preferably implemented in a substrate-less form from the viewpoint of reducing the thickness of the PSA sheet. Substrate-less PSA sheets are advantageous in that they can be easily thinned and can maximize adhesive properties such as adhesive strength. Alternatively, in an embodiment in which the PSA sheet disclosed herein is in a substrate-attached form, the presence of a substrate makes it easier to obtain excellent processability, handleability, and the like.

[0030] <Pressure-sensitive adhesive layer> (Water-dispersible acrylic polymer) The pressure-sensitive adhesive layer disclosed herein contains a water-dispersible acrylic polymer. In this specification, "water-dispersible acrylic polymer" refers to an acrylic polymer synthesized in a form dispersed in water, and more specifically, an acrylic polymer synthesized by emulsion polymerization. By using a water-dispersible polymer as a pressure-sensitive adhesive-forming component, it is possible to reduce the amount of organic solvent used, and ultimately to achieve organic solvent-free applications. In addition, water-dispersible acrylic polymers can be obtained by polymerizing acrylic monomers while highly controlling the reaction, and have the advantage of being easy to obtain desired properties due to the high degree of freedom in molecular design.

[0031] The water-dispersible acrylic polymer is typically contained as a base polymer in the pressure-sensitive adhesive layer. Here, the "base polymer" of the pressure-sensitive adhesive layer refers to the main component of the rubber-like polymer contained in the pressure-sensitive adhesive layer, and is not intended to be interpreted in any other limiting sense. The rubber-like polymer refers to a polymer that exhibits rubber elasticity in a temperature range around room temperature. Furthermore, in this specification, the "main component" refers to a component contained in an amount of more than 50% by weight, unless otherwise specified. Hereinafter, the water-dispersible acrylic polymer may be simply referred to as an acrylic polymer.

[0032] The acrylic polymer is preferably a polymer of a monomer raw material (monomer component) that contains, for example, an alkyl(meth)acrylate as a main monomer and may further contain a secondary monomer copolymerizable with the main monomer, where the main monomer is a component that accounts for more than 50% by weight of the monomer composition in the monomer raw material.

[0033] As the alkyl(meth)acrylate, for example, a compound represented by the following formula (1) can be suitably used: CH ２ = C(R １ ) COOR ２ (1) Here, R in the above formula (1) １ is a hydrogen atom or a methyl group. ２ is a chain alkyl group having 1 to 20 carbon atoms (hereinafter, this range of carbon atoms is referred to as "C １－２０ From the viewpoint of the storage modulus of the adhesive, R ２ is C １－１４ alkyl(meth)acrylates in which R ２ is C １－１０ Alkyl (meth)acrylates, which are chain alkyl groups, are more preferred.

[0034] R ２ is C １－２０Examples of alkyl(meth)acrylates, which are chain alkyl groups, include methyl(meth)acrylate, ethyl(meth)acrylate, propyl(meth)acrylate, isopropyl(meth)acrylate, n-butyl(meth)acrylate, isobutyl(meth)acrylate, s-butyl(meth)acrylate, pentyl(meth)acrylate, isopentyl(meth)acrylate, hexyl(meth)acrylate, heptyl(meth)acrylate, 2-ethylhexyl(meth)acrylate, octyl(meth)acrylate, and isooctyl(meth)acrylate. Examples of alkyl (meth)acrylates include butyl (meth)acrylate, nonyl (meth)acrylate, isononyl (meth)acrylate, decyl (meth)acrylate, isodecyl (meth)acrylate, undecyl (meth)acrylate, dodecyl (meth)acrylate, tridecyl (meth)acrylate, tetradecyl (meth)acrylate, pentadecyl (meth)acrylate, hexadecyl (meth)acrylate, heptadecyl (meth)acrylate, octadecyl (meth)acrylate, nonadecyl (meth)acrylate, and eicosyl (meth)acrylate. These alkyl (meth)acrylates can be used alone or in combination of two or more. Suitable examples of alkyl (meth)acrylates include n-butyl acrylate (BA) and 2-ethylhexyl acrylate (2EHA).

[0035] The technology disclosed herein is ２ is C １－２０ alkyl (meth)acrylate (C １－２０ In some preferred embodiments, the above-mentioned C can be preferably carried out using an acrylic polymer in which the chain alkyl (meth)acrylate accounts for approximately 50% by weight or more of the monomer components. １－２０ The proportion of the chain alkyl (meth)acrylate in the monomer component may be approximately 75% by weight or more, approximately 90% by weight or more, or approximately 95% by weight or more. １－２０In an embodiment in which a secondary monomer is used, the upper limit of the proportion of the chain alkyl (meth)acrylate may be, for example, 99.9% by weight or less, 99.5% by weight or less, or 99% by weight or less (e.g., 98.5% by weight or less).

[0036] In some embodiments, the monomer component is R ２ is C ４－１０ alkyl (meth)acrylate (C ４－１０ It is preferable that the copolymer contains a chain alkyl (meth)acrylate. ４－１０ Examples of the chain alkyl (meth)acrylate include C ４－８ It is more preferable to use a chain alkyl (meth)acrylate, and from the viewpoint of adhesive properties, R １ is a hydrogen atom and R ２ is C ４－１０ alkyl acrylate (C ４－１０ It is more preferable to use a chain alkyl acrylate), ４－８ It is particularly preferable to use a chain alkyl acrylate. ４－１０ The chain alkyl (meth)acrylate may be used alone or in combination of two or more. ４－１０ The proportion of the chain alkyl (meth)acrylate is preferably about 50% by weight or more, more preferably 70% by weight or more, and even more preferably 80% by weight or more. ４－１０ The upper limit of the proportion of the chain alkyl (meth)acrylate is 100% by weight, and in some embodiments, from the viewpoint of obtaining good cohesive strength, it is appropriate to set it to approximately 95% by weight or less, and it may also be set to approximately 90% by weight or less.

[0037] In some embodiments, the monomer component is C ６－１０ It is preferable that the compound contains a chain alkyl (meth)acrylate. ６－１０ Examples of the chain alkyl (meth)acrylate include C ７－９ It is more preferable to use a chain alkyl (meth)acrylate, ８It is more preferable to use a chain alkyl (meth)acrylate. ６－１０ As the chain alkyl (meth)acrylate, a chain alkyl acrylate is preferably used. ６－１０ The chain alkyl (meth)acrylate may be used alone or in combination of two or more. ６－１０ The proportion of the chain alkyl (meth)acrylate is approximately 50% by weight or more (for example, more than 50% by weight), and may be 60% by weight or more, 70% by weight or more, or 80% by weight or more. ６－１０ The upper limit of the proportion of the chain alkyl (meth)acrylate is 100% by weight, and in some embodiments, from the viewpoint of obtaining good cohesive strength, it is appropriate to set it to approximately 95% by weight or less, and it may also be set to approximately 90% by weight or less.

[0038] Above C ６－１０ As the chain alkyl (meth)acrylate, 2EHA is preferably used. In the embodiment using 2EHA, the proportion of 2EHA is not particularly limited, and ４－１０ In the chain alkyl (meth)acrylate, the content is suitably more than 50% by weight, preferably 70% by weight or more, more preferably 90% by weight or more, and even more preferably 95% by weight or more (for example, 95 to 100% by weight).

[0039] The alkyl (meth)acrylate is ４－１０ When a chain alkyl (meth)acrylate is contained, other alkyl (meth)acrylate (R ２ is C ４ Less than or C １０ The alkyl (meth)acrylate may contain an alkyl group having a chain alkyl group longer than 100 nm. This allows a good balance between adhesion and cohesion. The alkyl (meth)acrylate may contain an alkyl group having a chain alkyl group longer than 100 nm. The alkyl (meth)acrylate may contain an alkyl group having a chain alkyl group longer than 100 nm. This makes it possible to achieve a good balance between adhesion and cohesion. The alkyl (meth)acrylate may contain an alkyl group having a chain alkyl group longer than 100 nm ... ２ is C １－３Alkyl (meth)acrylates, which are chain alkyl groups, can be preferably used. Specific examples include methyl acrylate (MA), methyl methacrylate (MMA), and ethyl acrylate (EA). Among these, MA is more preferred. The other alkyl (meth)acrylates can be used alone or in combination of two or more. The proportion of the other alkyl (meth)acrylates in the alkyl (meth)acrylates contained in the monomer component is preferably about 30% by weight or less, and may be, for example, about 20% by weight or less, or about 15% by weight or less. Furthermore, from the viewpoint of obtaining the effects of the other alkyl (meth)acrylates, the proportion of the other alkyl (meth)acrylates is preferably about 1% by weight or more of the total alkyl (meth)acrylates, and may be, for example, about 5% by weight or more, or about 10% by weight or more.

[0040] A minor monomer copolymerizable with the alkyl (meth)acrylate main monomer can be useful for introducing crosslinking points into the acrylic polymer or for increasing the cohesive strength of the acrylic polymer. Examples of the minor monomer include the following functional group-containing monomer components, which can be used singly or in combination of two or more: Carboxy group-containing monomers: ethylenically unsaturated monocarboxylic acids such as acrylic acid, methacrylic acid, carboxyethyl (meth)acrylate, carboxypentyl (meth)acrylate, and crotonic acid; ethylenically unsaturated dicarboxylic acids such as maleic acid, itaconic acid, and citraconic acid, and their anhydrides (maleic anhydride, itaconic anhydride, etc.); Hydroxyl group-containing monomers: hydroxyalkyl (meth)acrylates such as 2-hydroxyethyl (meth)acrylate, 2-hydroxypropyl (meth)acrylate, 3-hydroxypropyl (meth)acrylate, and 2-hydroxybutyl (meth)acrylate; and unsaturated alcohols such as vinyl alcohol and allyl alcohol. Amide group-containing monomers: for example, (meth)acrylamide, N,N-dimethyl(meth)acrylamide, N-butyl(meth)acrylamide, N-methylol(meth)acrylamide, N-methylolpropane(meth)acrylamide, N-methoxymethyl(meth)acrylamide, N-butoxymethyl(meth)acrylamide. Amino group-containing monomers: for example, aminoethyl(meth)acrylate, N,N-dimethylaminoethyl(meth)acrylate, t-butylaminoethyl(meth)acrylate. Epoxy group-containing monomers: for example, glycidyl(meth)acrylate, methylglycidyl(meth)acrylate, allyl glycidyl ether. Cyano group-containing monomers: for example, acrylonitrile, methacrylonitrile. Keto group-containing monomers: for example, diacetone(meth)acrylamide, diacetone(meth)acrylate, vinyl methyl ketone, vinyl ethyl ketone, allyl acetoacetate, vinyl acetoacetate.Monomers having a nitrogen atom-containing ring: for example, N-vinyl-2-pyrrolidone, N-methylvinylpyrrolidone, N-vinylpyridine, N-vinylpiperidone, N-vinylpyrimidine, N-vinylpiperazine, N-vinylpyrazine, N-vinylpyrrole, N-vinylimidazole, N-vinyloxazole, N-vinylmorpholine, N-vinylcaprolactam, and N-(meth)acryloylmorpholine. Silane-based monomers: for example, alkoxysilyl group-containing monomers such as 3-(meth)acryloxypropyltrimethoxysilane, 3-(meth)acryloxypropyltriethoxysilane, 3-(meth)acryloxypropylmethyldimethoxysilane, and 3-(meth)acryloxypropylmethyldiethoxysilane.

[0041] The functional group-containing monomers can be used alone or in combination of two or more. Among the functional group-containing monomers, carboxy group-containing monomers, hydroxy group-containing monomers, and cyano group-containing monomers are preferred because they can suitably introduce crosslinking points and improve cohesive strength as described above.

[0042] When functional group-containing monomer is copolymerized with acrylic polymer, the proportion of functional group-containing monomer in the total monomer components constituting acrylic polymer is not particularly limited.Usually, from the viewpoint of achieving a good balance between cohesion and adhesiveness, the proportion of functional group-containing monomer is preferably about 0.1 wt% or more, for example, it can be about 0.5 wt% or more, or it can be about 1 wt% or more.In addition, considering the adhesive effect of alkyl (meth)acrylate, in some embodiments, the proportion of functional group-containing monomer is preferably about 40 wt% or less, for example, it can be about 30 wt% or less, about 20 wt% or less, 10 wt% or less, 5 wt% or less, or it can be 3 wt% or less.

[0043] In some preferred embodiments, the monomer component constituting the acrylic polymer contains a carboxyl group-containing monomer. By including a carboxyl group-containing monomer in the monomer component, it becomes easier to obtain a pressure-sensitive adhesive sheet exhibiting good adhesive properties (such as cohesive strength). This can also be advantageous in improving the adhesion between the pressure-sensitive adhesive layer and the adherend. The carboxyl group-containing monomer can be used alone or in combination of two or more. Acrylic acid and methacrylic acid are preferably used as the carboxyl group-containing monomer.

[0044] When a carboxyl group-containing monomer is copolymerized with an acrylic polymer, the proportion of the carboxyl group-containing monomer in the total monomer components is not particularly limited. From the viewpoint of cohesive strength, etc., in some embodiments, the proportion of the carboxyl group-containing monomer is, for example, preferably about 0.1 wt% or more, more preferably about 0.5 wt% or more, even more preferably about 1 wt% or more, and particularly preferably about 1.5 wt% or more. Furthermore, from the viewpoint of adhesive properties such as adhesive strength, in some embodiments, the proportion of the carboxyl group-containing monomer is suitably about 15 wt% or less, preferably about 12 wt% or less, for example, it may be 10 wt% or less. In some preferred embodiments, the proportion of the carboxyl group-containing monomer in the total monomer components is 5 wt% or less, may be 3 wt% or less, or may be 2.5 wt% or less. Acrylic polymers with a limited copolymerization proportion of the carboxyl group-containing monomer are advantageous in terms of pigment dispersibility because the occurrence of locally high acidic components is suppressed, and a high-quality appearance with less color unevenness tends to be obtained.

[0045] In an embodiment in which the monomer component contains a carboxyl group-containing monomer as a functional group-containing monomer, the proportion of the carboxyl group-containing monomer in the total functional group-containing monomers (total functional group-containing monomers including the carboxyl group-containing monomer) used as a copolymerization component of the acrylic polymer is, from the viewpoint of effectively exhibiting the effect of copolymerizing the carboxyl group-containing monomer, suitably 30% by weight or more, preferably 50% by weight or more, more preferably 70% by weight or more, even more preferably 80% by weight or more, particularly preferably 90% by weight or more, for example, 95% by weight or more, 97% by weight or more, 98% by weight or more, or 99% by weight or more (for example, 99.9% by weight or more). The upper limit of the proportion of the carboxyl group-containing monomer in the total functional group-containing monomer is 100% by weight, and may be, for example, 95% by weight or less.

[0046] In some embodiments, the carboxy group-containing monomer preferably includes acrylic acid (AA). The use of acrylic acid facilitates obtaining good adhesive properties (adhesion strength, cohesion strength, etc.) and excellent polymer dispersion stability. In some embodiments, the content of acrylic acid in the monomer components is, for example, preferably about 0.1 wt% or more, more preferably about 0.5 wt% or more, and even more preferably about 1 wt% or more. Furthermore, from the viewpoint of adhesive properties such as adhesive strength, in some embodiments, the proportion of acrylic acid is suitably 10 wt% or less, for example, preferably 5 wt% or less, more preferably 3 wt% or less, or may be 2 wt% or less, or may be 1.5 wt% or less. In embodiments using acrylic acid as the carboxy group-containing monomer, the proportion of acrylic acid in the total carboxy group monomers is suitably 30 wt% or more, preferably 50 wt% or more (e.g., more than 50 wt%), and may be 60 wt% or more. Furthermore, the upper limit of the proportion of acrylic acid in the total carboxy group-containing monomers is not particularly limited, and in some embodiments, it may be 90% by weight or less, 80% by weight or less, or 70% by weight or less.

[0047] In some preferred embodiments, acrylic acid (AA) and methacrylic acid (MAA) are used in combination as the carboxy group-containing monomer. A PSA containing an acrylic polymer with such a monomer composition (i.e., copolymer composition) can provide a PSA sheet with higher performance (e.g., better repulsion resistance). The weight ratio of AA to MAA (AA / MAA) can be, for example, in the range of approximately 0.1 to 10, more preferably approximately 0.3 or more, even more preferably 0.5 or more, and particularly preferably 1.0 or more (e.g., greater than 1.0 or 1.2 or more). Furthermore, the weight ratio (AA / MAA) is more preferably approximately 5 or less, and may be, for example, 4 or less, 3 or less, or 2 or less. By having the AA / MAA ratio within the above range, there is a tendency for the effect of improving repulsion resistance to be sufficiently obtained, and after the PSA sheet is produced, there is a tendency for the adhesive properties to have excellent stability over time.

[0048] Furthermore, it is preferable that a silane-based monomer be copolymerized with the acrylic polymer. An alkoxysilyl group-containing monomer is preferably used as the silane-based monomer. The alkoxysilyl group-containing monomer is typically an ethylenically unsaturated monomer having at least one (preferably two or more, e.g., two or three) alkoxysilyl group in one molecule, specific examples of which are as described above. The silane-based monomer can be used alone or in combination with two or more. Copolymerizing the silane-based monomer can introduce a crosslinked structure into the adhesive containing the acrylic polymer through a condensation reaction of silanol groups (silanol condensation). This is advantageous in terms of suppressing the expansion of bubbles in the adhesive, thereby improving the appearance quality retention. The silane-based monomer is also called a silane coupling agent.

[0049] When a silane-based monomer is copolymerized with an acrylic polymer, the proportion of the silane-based monomer in the above-mentioned monomer components is suitably about 0.001 wt% or more, preferably 0.005 wt% or more, and more preferably 0.01 wt% or more. In some embodiments, the proportion of the silane-based monomer in the above-mentioned monomer components is suitably about 0.1 wt% or less, preferably 0.05 wt% or less, and may be, for example, 0.03 wt% or less. By using an appropriate amount of silane-based monomer, the effects of improving cohesion and improving appearance quality retention tend to be easily obtained.

[0050] Furthermore, for the purpose of increasing the cohesive strength of the acrylic polymer, copolymerization components other than the above-mentioned minor monomers can be used. Examples of such copolymerization components include vinyl ester monomers such as vinyl acetate and vinyl propionate; aromatic vinyl compounds such as styrene, substituted styrenes (α-methylstyrene, etc.) and vinyltoluene; cycloalkyl(meth)acrylates such as cyclohexyl(meth)acrylate, cyclopentyl(meth)acrylate and isobornyl(meth)acrylate; aryl(meth)acrylates (e.g., phenyl(meth)acrylate), aryloxyalkyl(meth)acrylates (e.g., phenoxyethyl(meth)acrylate), arylalkyl(meth)acrylates, and the like. Examples of other copolymerizable monomers include aromatic ring-containing (meth)acrylates such as (meth)acrylates (for example, benzyl (meth)acrylate); olefin-based monomers such as ethylene, propylene, isoprene, butadiene, and isobutylene; chlorine-containing monomers such as vinyl chloride and vinylidene chloride; isocyanate group-containing monomers such as 2-(meth)acryloyloxyethyl isocyanate; alkoxy group-containing monomers such as methoxyethyl (meth)acrylate and ethoxyethyl (meth)acrylate; and vinyl ether-based monomers such as methyl vinyl ether and ethyl vinyl ether. Examples of other copolymerizable monomers other than those mentioned above include monomers having multiple functional groups in one molecule (polyfunctional monomers).

[0051] The amount of copolymerization components other than the above-described secondary monomers is not particularly limited and may be appropriately selected depending on the purpose and application. For example, the amount is preferably 10% by weight or less of the monomer composition of the acrylic polymer, may be 3% by weight or less, or may be less than 1% by weight (for example, 0% by weight or more and less than 1% by weight).

[0052] Although not particularly limited, from the viewpoint of adhesion to an adherend, it is appropriate that the acrylic polymer is designed so that the glass transition temperature (Tg) of the polymer is −25° C. or lower. In some embodiments, the Tg of the acrylic polymer is preferably −40° C. or lower, more preferably −50° C. or lower, and may be −55° C. or lower. In some embodiments, from the viewpoint of cohesive strength, the Tg of the acrylic polymer is, for example, about −75° C. or higher, and may be about −70° C. or higher. The Tg of the acrylic polymer can be adjusted by the types and amount ratios of monomers used in synthesizing the polymer.

[0053] The Tg of an acrylic polymer can be determined by the Fox formula based on the composition of the monomer components used in synthesizing the polymer. The Fox formula, as shown below, is a relationship between the Tg of a copolymer and the glass transition temperature Tgi of a homopolymer obtained by homopolymerizing each of the monomers constituting the copolymer: 1 / Tg=Σ(Wi / Tgi) In the Fox formula, Tg represents the glass transition temperature of the copolymer (unit: K), Wi represents the weight fraction of monomer i in the copolymer (copolymerization ratio on a weight basis), and Tgi represents the glass transition temperature of a homopolymer of monomer i (unit: K).

[0054] The glass transition temperatures of the homopolymers used to calculate Tg are values ​​listed in publicly available documents. For example, for the monomers listed below, the following values ​​are used as the glass transition temperatures of the homopolymers of the monomers: 2-ethylhexyl acrylate -70°C n-butyl acrylate -55°C Methyl methacrylate 105°C Methyl acrylate 8°C Vinyl acetate 32°C Acrylic acid 106°C Methacrylic acid 228°C

[0055] For the glass transition temperatures of homopolymers of monomers other than those exemplified above, the values ​​described in "Polymer Handbook" (3rd Edition, John Wiley & Sons, Inc., 1989) shall be used. If multiple values ​​are described in this document, the highest value shall be adopted. If the value is not described in the Polymer Handbook, the value obtained by the measurement method described in Japanese Patent Application Publication No. 2007-51271 shall be used.

[0056] The acrylic polymer disclosed herein is synthesized by emulsion polymerization. The emulsion polymerization method is not particularly limited, and various monomer supply methods, polymerization conditions, materials used, and the like similar to those of conventionally known general emulsion polymerizations can be appropriately adopted. For example, the monomer supply method can be a batch feed method in which all monomer raw materials are supplied at once, a continuous feed (dropping) method, a divided feed (dropping) method, or the like. The monomer raw materials may be added dropwise in the form of an aqueous emulsion. The polymerization temperature can be, for example, about 20°C or higher (usually 40°C or higher), and is suitably about 100°C or lower (usually 80°C or lower).

[0057] The initiator used for polymerization can be appropriately selected from conventionally known polymerization initiators depending on the type of polymerization method. For example, azo initiators, persulfate initiators, peroxide initiators, substituted ethane initiators, carbonyl initiators, redox initiators formed by combining peroxides with reducing agents, etc. can be used. The polymerization initiators can be used alone or in combination of two or more. The amount of polymerization initiator used is not particularly limited as long as it is a normal amount. For example, it can be selected from a range of about 0.005 parts by weight or more (preferably 0.01 parts by weight or more) and about 1 part by weight or less (preferably 0.8 parts by weight or less) per 100 parts by weight of the monomer components.

[0058] The emulsion polymerization of the acrylic polymer disclosed herein is carried out in the presence of a reactive emulsifier having a radically polymerizable functional group. By emulsion polymerizing the monomer raw material in the presence of the reactive emulsifier, the reactive emulsifier can react and be incorporated into the acrylic polymer. By incorporating the reactive emulsifier into the acrylic polymer, the amount of free emulsifier is reduced, and even if bubbles are generated in the PSA, it is believed that the stabilization of the bubbles is suppressed. As a result, the amount of bubbles adhering to the pigment due to electrostatic interactions is also suppressed, and even if the PSA is subsequently exposed to a high-temperature environment, it is believed that the occurrence of appearance defects such as pinholes and color unevenness caused by the bubbles can be reduced. Note that the technology disclosed herein is not limited to the above considerations.

[0059] The reactive emulsifier may be, for example, an anionic surfactant or a nonionic surfactant having a structure in which a radically polymerizable functional group is introduced. The reactive emulsifier may be used alone or in combination of two or more. The type of radically polymerizable functional group possessed by the reactive emulsifier is not particularly limited, and may be, for example, an alkenyl group, an acryloyl group, a methacryloyl group, a vinyl group, a vinyl ether group (vinyloxy group), an allyl ether group (allyloxy group), or the like. Specific examples of the alkenyl group include a propenyl group and an isopropenyl group (CH ２ =C(CH ３ The concept of propenyl group here includes 1-propenyl group (CH３ -CH=CH-) and 2-propenyl group (CH ２ =CH-CH ２ -; sometimes referred to as an allyl group.

[0060] Examples of anionic reactive surfactants include polyoxyethylene (allyloxymethyl) alkyl ether sulfates (e.g., ammonium salts), polyoxyethylene nonylpropenyl phenyl ether sulfates (e.g., ammonium salts), alkyl allyl sulfosuccinates (e.g., sodium salts), methacryloxy polyoxypropylene sulfates (e.g., sodium salts), polyoxyalkylene alkenyl ether sulfates (e.g., ammonium salts in which the alkenyl group terminates in an isopropenyl group).When anionic reactive surfactants form salts, the salts may be, for example, metal salts such as sodium salts, or non-metal salts such as ammonium salts or amine salts.Examples of nonionic reactive surfactants include polyoxyethylene nonylpropenyl phenyl ether.

[0061] Commercially available reactive surfactants include those manufactured by Daiichi Kogyo Seiyaku Co., Ltd. under the trade names "Aqualon HS-05," "Aqualon HS-10," "Aqualon HS-1025," "Aqualon HS-20," "Aqualon KH-10," "Aqualon KH-1025," "Aqualon KH-05," "Aqualon BC-0515," "Aqualon BC-10," "Aqualon BC-1025," "Aqualon BC-20," "Aqualon BC-2020," "Aqualon RN-20," "Aqualon RN-30," "Aqualon RN-50," and Examples of such products include Aqualon AR-10, Aqualon AR-20, Aqualon AR-1025, and Aqualon AR-2020, ADEKA Corporation products under the trade names Adeka Reasop SE-10N and Adeka Reasop SR-1025, Kao Corporation products under the trade names Latemul PD-104, Latemul PD-420, Latemul PD-430, and Latemul PD-450, Sanyo Chemical Industries, Ltd. products under the trade names Eleminol JS-20 and Eleminol RS-3000, and Nippon Nyukazai Co., Ltd. product under the trade name Antox MS-60.

[0062] In this specification, "containing a reactive emulsifier" is used to mean containing the reactive emulsifier in a state after its radically polymerizable functional group has reacted. The reactive emulsifier in the technology disclosed herein is typically contained in the water-dispersible PSA composition or PSA layer in a form in which at least a portion of the reactive emulsifier is incorporated into the acrylic polymer as described above.

[0063] The amount of reactive emulsifier used in emulsion polymerization is not particularly limited. In consideration of polymerization stability and dispersion stability of the polymerization reaction product, in some embodiments, the amount of reactive emulsifier used is typically 0.1 parts by weight or more per 100 parts by weight of the monomer raw material, preferably 0.5 parts by weight or more, and may be 1.0 parts by weight or more, or even 1.5 parts by weight or more. Furthermore, the amount of reactive emulsifier used can be, for example, 10 parts by weight or less per 100 parts by weight of the monomer raw material. From the viewpoint of limiting the amount of free emulsifier, in some embodiments, the amount of reactive emulsifier used is typically preferably 5 parts by weight or less, more preferably 4 parts by weight or less, even more preferably 3 parts by weight or less, and particularly preferably 2.5 parts by weight or less. By appropriately setting the amount of reactive emulsifier used within the above range, it is possible to obtain the effects of containing the emulsifier while suppressing the stabilization of bubbles that may occur in the pressure-sensitive adhesive and preventing the occurrence of appearance defects such as pinholes.

[0064] During the polymerization, a chain transfer agent (which may also be understood as a molecular weight regulator or polymerization degree regulator) may be used as needed. Examples of chain transfer agents include mercaptans such as dodecyl mercaptan (dodecanethiol), lauryl mercaptan, glycidyl mercaptan, 2-mercaptoethanol, mercaptoacetic acid, 2-ethylhexyl thioglycolate, and 2,3-dimercapto-1-propanol, as well as α-methylstyrene dimer. Such chain transfer agents may be used alone or in combination of two or more. When a chain transfer agent is used, the amount used may be approximately 0.001 parts by weight or more, for example, approximately 0.005 parts by weight or more, or approximately 0.01 parts by weight or more, or approximately 5 parts by weight or less, for example, approximately 1 part by weight or less, or approximately 0.1 part by weight or less, per 100 parts by weight of the monomer components. By adjusting the amount of chain transfer agent used within an appropriate range, a desired polymerization rate can be obtained.

[0065] According to the emulsion polymerization, it is possible to prepare a polymerization solution (acrylic polymer emulsion) in the form of an emulsion in which an acrylic polymer is dispersed in water. Usually, from the viewpoint of dispersion stability, etc., a pH adjuster such as aqueous ammonia is added to the polymerization solution to adjust the pH to an appropriate range (for example, a range of about pH 6 to 9).

[0066] (Pigment) The pressure-sensitive adhesive layer disclosed herein contains a pigment. By incorporating an appropriate amount of pigment, the pressure-sensitive adhesive layer can be endowed with properties and functions such as light-blocking properties, concealment of the adherend, adjustment of the adherend's appearance through the pressure-sensitive adhesive sheet, and design properties. Pigments containing inorganic particles are preferably used. For example, inorganic pigments such as carbon black, graphite, activated carbon, ferrite (non-magnetic ferrite, magnetic ferrite, etc.), magnetite, molybdenum disulfide, chromium complex, copper oxide, manganese dioxide, zinc carbonate, zinc oxide, zinc sulfide, talc, kaolin, calcium carbonate, titanium oxide, silica, lithium fluoride, calcium fluoride, barium sulfate, alumina, zirconia, iron oxide, iron hydroxide, chromium oxide, spinel-type calcined pigment, chromate, chrome vermilion, Prussian blue, aluminum powder, bronze powder, silver powder, and calcium phosphate can be used. Black pigments such as aniline black, perylene black, titanium black, and cyanine black may also be used. The inorganic pigment includes all pigments that are mainly composed of inorganic materials, and is not limited to those that are composed only of inorganic materials. The pigments can be used alone or in combination of two or more.

[0067] From the viewpoint of light-shielding properties and reduced light transmittance, in some embodiments, black pigments such as carbon black, graphite, copper oxide, manganese dioxide, aniline black, perylene black, titanium black, cyanine black, activated carbon, ferrite (non-magnetic ferrite, magnetic ferrite, etc.), magnetite, chromium oxide, iron oxide, molybdenum disulfide, chromium complexes, etc. are preferably used. The black pigments may be used alone or in combination of two or more.

[0068] In some preferred embodiments, carbon black is used as a pigment. The use of carbon black can efficiently reduce light transmittance, resulting in a highly light-blocking adhesive. Carbon blacks commonly referred to as carbon blacks (furnace black, channel black, acetylene black, thermal black, lamp black, pine soot, etc.) can be used without particular limitation. From the perspective of maintaining appearance quality, it is preferable to use surface-modified carbon blacks having functional groups such as carboxy groups, amino groups, sulfonic acid groups, and silicon-containing groups (e.g., alkoxysilyl groups, alkylsilyl groups). Such surface-modified carbon blacks are also called self-dispersing carbon blacks, and they eliminate the need for or reduce the amount of dispersant added. The above carbon blacks can be used alone or in combination of two or more. Self-dispersing carbon blacks can be produced based on the methods described in, for example, Japanese Patent Application Publication No. 2017-171732 and Japanese Patent Application Publication No. 2018-30968 and the common technical knowledge of those skilled in the art. Commercially available products can also be used.

[0069] In some embodiments, the pigment may be selected from metal oxides such as titanium oxide (e.g., titanium dioxide such as rutile titanium dioxide and anatase titanium dioxide), zinc oxide, cerium oxide, aluminum oxide, silicon oxide, zirconium oxide, magnesium oxide, calcium oxide, tin oxide, barium oxide, cesium oxide, and yttrium oxide; carbonate compounds such as magnesium carbonate, calcium carbonate (light calcium carbonate, heavy calcium carbonate, and the like), barium carbonate, and zinc carbonate; aluminum hydroxide, calcium hydroxide, magnesium hydroxide, zinc hydroxide, and the like. Examples of inorganic materials that can be used include hydroxides; silicate compounds such as aluminum silicate, magnesium silicate, and calcium silicate; barium sulfate, calcium sulfate, barium stearate, zinc oxide, zinc sulfide, talc, clay, kaolin, titanium phosphate, mica, gypsum, white carbon, diatomaceous earth, bentonite, lithopone, zeolite, sericite, and hydrated halloysite; and organic materials such as acrylic resins, polystyrene resins, polyurethane resins, amide resins, polycarbonate resins, silicone resins, urea-formalin resins, and melamine resins. These can be used as non-black pigments, such as white. The non-black pigments can be used alone or in combination of two or more.

[0070] In some embodiments, one or more black pigments may be used in combination with one or more non-black pigments. In such embodiments, the ratio (weight ratio (A / B)) of the amount of black pigment A to the amount of non-black pigment B is not particularly limited. For example, the weight ratio (A / B) may be 0.001 or more, 0.01 or more, or 0.1 or more, and the weight ratio (A / B) may be 100 or less, 10 or less, or 1 or less.

[0071] The particle size of the pigment is not particularly limited. In some embodiments, the volume average particle size of the pigment is approximately 3,000 nm or less, and may be approximately 1,000 nm or less. From the viewpoint of improving light-blocking properties, the volume average particle size of the pigment is appropriately approximately 500 nm or less, preferably approximately 300 nm or less, more preferably approximately 250 nm or less, and even more preferably approximately 200 nm or less, and may be approximately 150 nm or less (e.g., 120 nm or less). In some embodiments, the volume average particle size of the pigment is usually approximately 10 nm or more, and may be approximately 30 nm or more, 50 nm or more, 80 nm or more, or 100 nm or more (e.g., more than 100 nm). By using a pigment having an appropriate particle size within the above range, a pressure-sensitive adhesive layer with good appearance quality can be preferably obtained.

[0072] The volume average particle size of the pigment is the volume average particle size determined by the laser diffraction / scattering method, and specifically refers to the particle size at 50% of the integrated value in the particle size distribution measured for a pigment-containing dispersion using a particle size distribution measuring device based on the laser diffraction / scattering method (50% volume average particle size). As the measuring device, for example, a Microtrac MT3000II manufactured by Microtrac Bell or an equivalent can be used.

[0073] Although not particularly limited, in some embodiments, the average particle diameter of the pigment particles dispersed in the pressure-sensitive adhesive layer may be approximately 150 nm or less. The average particle diameter of the pigment particles dispersed in the pressure-sensitive adhesive layer here refers to the average particle diameter determined from the number-based particle size distribution obtained by TEM observation, specifically, measured using ultrathin frozen sections of the pressure-sensitive adhesive. A small average particle diameter of pigment particles in the pressure-sensitive adhesive layer tends to limit the amount of large-diameter particles, and the maximum diameter of particles present in the pressure-sensitive adhesive layer also tends to be small. Furthermore, limiting the amount of large-diameter particles with a relatively small specific surface area means that a certain amount of pigment particles in the pressure-sensitive adhesive layer has a predetermined or greater light absorption area. This makes it easier to achieve excellent pigment addition effects. For example, when the pigment is a black pigment such as carbon black, the pressure-sensitive adhesive layer can have excellent light transmittance reduction properties and, therefore, light-blocking properties. In some preferred embodiments, the average particle diameter is less than 130 nm, and may be approximately 120 nm or less, approximately 110 nm or less, approximately 100 nm or less, or 90 nm or less. The lower limit of the average particle size is not particularly limited, and is suitably about 10 nm or more. From the viewpoint of limiting the amount of small particles with low light absorption that cause diffraction and scattering, the average particle size is preferably about 50 nm or more, more preferably about 70 nm or more, and even more preferably about 80 nm or more, and may be, for example, 90 nm or more. The average particle size determined from the number-based particle size distribution by TEM observation is specifically measured by the following method.

[0074] [Measurement of Pigment Particle Diameter in the Pressure-Sensitive Adhesive Layer] A pressure-sensitive adhesive sample is rapidly frozen in a liquid nitrogen atmosphere, and then cut into approximately 100 nm thick ultrathin sections using an ultramicrotome (model "UC7" manufactured by Leica) in a frozen atmosphere at -30°C. TEM observation is performed on the obtained ultrathin sections using a transmission electron microscope (TEM; manufactured by Hitachi High-Technologies Corporation, accelerating voltage 100 kV). Image processing (binarization) is performed on one field of view (6 μm × 6 μm square) of a TEM image magnified approximately 3,000 times to identify particles, and the area fraction of each particle is calculated for all identified particles. The circle-equivalent diameter is then calculated from the area of ​​each particle. The circle-equivalent diameter refers to the diameter of a circle (perfect circle) having the same area as the area of ​​a single particle being measured. This operation is performed in four different fields of view in the TEM image (N=4), and the particles classified by circle equivalent diameter are histogrammed on a number basis to obtain a particle size distribution (number basis). The number used as the calculation basis for the particle size distribution is determined by counting the number of particles present in one field of view. From the obtained particle size distribution, the average particle diameter based on TEM observation (TEM average particle diameter) [nm] is determined. Note that when identifying particles, particles on the edge of the image are omitted during analysis. ImageJ, for example, can be used as image analysis software.

[0075] The form of pigment addition is not particularly limited. For example, the pigment is preferably blended into the PSA composition in the form of a dispersion containing the pigment. As such a dispersion, a dispersion in which at least a portion of the pigment is dispersed in water or an aqueous liquid containing water as a main component (typically, an aqueous dispersion) is preferably used. By blending a dispersion in which at least a portion of the pigment is dispersed into a PSA composition to form a PSA layer, a high-quality appearance with little color unevenness is likely to be obtained. The pigment dispersion is preferably used in the form of a dispersion that is liquid at room temperature (e.g., 23°C).

[0076] The content of the pigment in the pressure-sensitive adhesive layer can be set taking into consideration the dispersibility of the pigment in the pressure-sensitive adhesive layer, the thickness of the pressure-sensitive adhesive layer, the optical properties (light transmittance such as light-blocking properties) and design properties to be achieved, and other required adhesive properties. In some embodiments, the content (solid content basis) of the pigment (e.g., black pigment, more specifically, carbon black) in the pressure-sensitive adhesive layer is suitably approximately 0.01 parts by weight or more per 100 parts by weight of the acrylic polymer. From the viewpoint of effectively obtaining the effects of adding the pigment (e.g., light-blocking properties, design properties, etc.), the content is preferably approximately 0.1 parts by weight or more, more preferably approximately 1 part by weight or more, and may be approximately 3 parts by weight or more, or may be approximately 4 parts by weight or more. The content of the pigment in the pressure-sensitive adhesive layer may be approximately 5 parts by weight or more (e.g., more than 5 parts by weight), 7 parts by weight or more, or 9 parts by weight or more per 100 parts by weight of the acrylic polymer. Such a pressure-sensitive adhesive containing a large amount of pigment is suitable, for example, for applications requiring high light-blocking properties. In some embodiments, the pigment content can be about 30 parts by weight or less per 100 parts by weight of the acrylic polymer, and from the viewpoint of adhesive properties such as adhesive strength, it is preferably about 15 parts by weight or less, more preferably 10 parts by weight or less (e.g., less than 10 parts by weight), and may be about 8 parts by weight or less, about 6 parts by weight or less, or about 5 parts by weight or less (e.g., less than 5 parts by weight). The pigment content may be about 3 parts by weight or less, or about 2 parts by weight or less per 100 parts by weight of the acrylic polymer.

[0077] (Dispersant) The pressure-sensitive adhesive layer disclosed herein may or may not contain a dispersant. When a self-dispersing pigment such as the above-mentioned self-dispersing carbon black is used as the pigment, a dispersant may not be used. The dispersant is not particularly limited, and one or more suitable dispersants capable of dispersing the pigment well in the pressure-sensitive adhesive layer can be used from among known or commonly used dispersants. For example, one or more suitable dispersants exhibiting good pigment dispersion performance can be appropriately selected from the following anionic, cationic, nonionic, and amphoteric surfactants and polymeric compounds (which may be resins).

[0078] Examples of anionic surfactants used as dispersants include alkyl sulfates such as lauryl sulfate and octadecyl sulfate; fatty acid salts; polysulfonates; polycarboxylates; alkylbenzenesulfonates such as nonylbenzenesulfonate and dodecylbenzenesulfonate; naphthalenesulfonates such as dodecylnaphthalenesulfonate; naphthalenesulfonate-formalin condensates; alkyl diphenyl ether disulfonates such as dodecyl diphenyl ether disulfonate; polyoxyethylene alkyl ether sulfates such as polyoxyethylene octadecyl ether sulfate and polyoxyethylene lauryl ether sulfate; polyoxyethylene alkyl phenyl ether sulfates such as polyoxyethylene lauryl phenyl ether sulfate; polyoxyethylene styrenated phenyl ether sulfate; sulfosuccinates such as lauryl sulfosuccinate and polyoxyethylene lauryl sulfosuccinate; polyoxyethylene alkyl ether phosphates; polyoxyethylene alkyl phosphate sulfonates; polyoxyethylene alkyl ether acetates; and the like. When the anionic surfactant forms a salt, the salt may be, for example, a metal salt (preferably a monovalent metal salt) such as a sodium salt, potassium salt, calcium salt, or magnesium salt, an ammonium salt, an amine salt, etc. These anionic surfactants may be used alone or in combination of two or more.

[0079] Examples of cationic surfactants used as dispersants include alkylamine salts and quaternary ammonium salts. Specific examples include stearylamine acetate, trimethyl coconut ammonium chloride, trimethyl tallow ammonium chloride, dimethyldioleyl ammonium chloride, methyl oleyl diethanol chloride, tetramethyl ammonium chloride, lauryl pyridinium chloride, lauryl pyridinium bromide, lauryl pyridinium disulfate, cetyl pyridinium bromide, 4-alkylmercaptopyridine, poly(vinylpyridine)-dodecyl bromide, and dodecylbenzyl triethyl ammonium chloride. These cationic surfactants can be used alone or in combination of two or more.

[0080] Examples of nonionic surfactants used as dispersants include polyoxyethylene alkyl ethers such as polyoxyethylene lauryl ether, polyoxyethylene cetyl ether, polyoxyethylene stearyl ether, and polyoxyethylene oleyl ether; polyoxyethylene alkyl phenyl ethers such as polyoxyethylene octylphenyl ether and polyoxyethylene nonylphenyl ether; sorbitan fatty acid esters such as sorbitan monolaurate, sorbitan monopalmitate, sorbitan monostearate, and sorbitan monooleate; polyoxyethylene sorbitan fatty acid esters such as polyoxyethylene sorbitan monolaurate, polyoxyethylene sorbitan monopalmitate, polyoxyethylene sorbitan monostearate, polyoxyethylene sorbitan tristearate, polyoxyethylene sorbitan triisostearate, polyoxyethylene sorbitan monooleate, and polyoxyethylene sorbitan trioleate; polyoxyethylene glyceryl ether fatty acid esters; polyoxyethylene-polyoxypropylene block copolymers; etc. These nonionic surfactants may be used alone or in combination of two or more.

[0081] Examples of amphoteric surfactants used as dispersants include alkyl betaines such as alkyl dimethyl amino acetic acid betaine, amino carboxylates, alkyl imidazolines, etc. The above amphoteric surfactants can be used alone or in combination of two or more.

[0082] Furthermore, examples of resins (which may be polymeric compounds) used as dispersants include polyurethane resins; polyester resins; polyamide resins such as unsaturated polyamides; (meth)acrylic resins such as poly(meth)acrylic acid esters and (meth)acrylic acid-(meth)acrylate copolymers; polycarboxylic acids (salts) such as polyacrylic acid, amine salts and ammonium salts of polycarboxylic acids, and alkylamine salts; styrene copolymers such as (meth)acrylic acid-styrene copolymers and styrene-maleic acid copolymers; polyvinyl alcohol; polyvinylpyrrolidone; polysiloxane; polyalkylene oxide derivatives such as ethylene oxide-propylene oxide adducts; phosphate ester resins; long-chain polyaminoamide phosphates; and modified products thereof. These resins may be used alone or in combination of two or more.

[0083] The form of addition of the dispersant is not particularly limited, and the dispersant may be contained in the pigment dispersion before being blended into the pressure-sensitive adhesive composition, or may be supplied at the same time as the pigment is added to the pressure-sensitive adhesive composition, or before or after the pigment is added.

[0084] The content of the dispersant in the pressure-sensitive adhesive layer can be set within an appropriate range, taking into account the dispersibility of the pigment. In some embodiments, the amount of dispersant per 100 parts by weight of the pigment in the pressure-sensitive adhesive layer can be approximately 0.01 parts by weight or more (e.g., approximately 0.1 parts by weight or more), and is preferably approximately 1 part by weight or more, for example, approximately 2 parts by weight or more, for example, approximately 3 parts by weight or more, or approximately 4 parts by weight or more. In some embodiments, the amount of dispersant per 100 parts by weight of the pigment in the pressure-sensitive adhesive layer can be approximately 100 parts by weight or less, and is preferably approximately 60 parts by weight or less, and may be approximately 30 parts by weight or less, or may be approximately 10 parts by weight or less. By limiting the amount of dispersant used, it is possible to prevent or suppress deterioration in appearance quality retention due to the inclusion of the dispersant. From this perspective, in some embodiments, the content of the dispersant per 100 parts by weight of the pigment in the pressure-sensitive adhesive layer can be less than 5 parts by weight, less than 3 parts by weight, or less than 1 part by weight. The technology disclosed herein can be preferably practiced in an embodiment in which the PSA layer does not substantially contain a dispersant.

[0085] (Tackifier Resin) In some embodiments, the PSA layer may contain a tackifier resin. This can increase the adhesive strength of the PSA sheet. Examples of tackifier resins include rosin-based tackifier resins (including rosin derivative tackifier resins), petroleum-based tackifier resins, terpene-based tackifier resins, and ketone-based tackifier resins. These may be used alone or in combination of two or more.

[0086] Examples of the rosin-based tackifying resin include rosins such as gum rosin, wood rosin, and tall oil rosin, as well as stabilized rosins (e.g., stabilized rosins obtained by disproportionating or hydrogenating the rosin), polymerized rosins (e.g., rosin polymers, typically dimers), and modified rosins (e.g., unsaturated acid-modified rosins modified with unsaturated acids such as maleic acid, fumaric acid, and (meth)acrylic acid). Examples of the rosin derivative tackifying resin include esters of the rosin-based resins (e.g., rosin esters such as stabilized rosin esters and polymerized rosin esters), phenol-modified rosin-based resins (phenol-modified rosin), and esters thereof (phenol-modified rosin esters). Examples of the petroleum-based tackifying resin include aliphatic petroleum resins, aromatic petroleum resins, copolymerized petroleum resins, alicyclic petroleum resins, and hydrogenated versions of these. Examples of the terpene-based tackifying resins include α-pinene resins, β-pinene resins, aromatic-modified terpene-based resins, terpene-phenol-based resins, etc. Examples of the ketone-based tackifying resins include ketone-based resins obtained by condensation of ketones (e.g., aliphatic ketones such as methyl ethyl ketone, methyl isobutyl ketone, and acetophenone; alicyclic ketones such as cyclohexanone and methylcyclohexanone) with formaldehyde, etc.

[0087] Examples of tackifying resins that can be preferably used include rosin-based tackifying resins and terpene-based tackifying resins. Suitable examples of rosin-based tackifying resins include stabilized rosin esters and polymerized rosin esters. Suitable examples of terpene-based tackifying resins include terpene phenol-based resins.

[0088] The softening point of the tackifier resin used is not particularly limited. From the viewpoint of improving cohesive strength, etc., the softening point of the tackifier resin may be, for example, 80°C or higher, or may be 90°C or higher. In some embodiments, the softening point of the tackifier resin is preferably 100°C or higher, more preferably 120°C or higher, and even more preferably 130°C or higher. In some preferred embodiments, the tackifier resin may contain a high-softening-point tackifier resin having a softening point of 140°C or higher. The softening point of the high-softening-point tackifier resin may be 145°C or higher, for example, 150°C or higher, or even 155°C or higher. The use of the high-softening-point tackifier resin can favorably achieve both adhesion and cohesiveness. There is no particular upper limit for the softening point of the tackifier resin, but from the viewpoint of compatibility, low-temperature properties, etc., it is usually appropriate that the softening point be 200°C or lower, preferably 180°C or lower, more preferably 170°C or lower, and even more preferably 160°C or lower.

[0089] The softening point of the tackifier resin referred to here is defined as a value measured based on the softening point test method (ring and ball method) specified in JIS K5902 and JIS K2207.

[0090] Some preferred embodiments include those in which the tackifier resin comprises one or more terpene-based tackifier resins (typically terpene phenol-based resins). The technology disclosed herein can be preferably implemented, for example, in an embodiment in which, assuming the total amount of tackifier resins to be 100% by weight, approximately 25% by weight or more (more preferably approximately 30% by weight or more) of the tackifier resins is terpene phenol-based resin. Approximately 50% by weight or more of the total amount of tackifier resins may be terpene phenol-based resins, or approximately 80% by weight or more (e.g., approximately 90% by weight or more) may be terpene phenol-based resins. Substantially all of the tackifier resins (e.g., approximately 95 to 100% by weight, or even approximately 99 to 100% by weight) may be terpene phenol-based resins.

[0091] In some other embodiments, the tackifier resin comprises a rosin-based tackifier resin. For example, assuming the total amount of tackifier resins to be 100% by weight, approximately 25% by weight or more (more preferably approximately 30% by weight or more) of the total amount of tackifier resins may be rosin-based tackifier resins, approximately 50% by weight or more of the total amount of tackifier resins may be rosin-based tackifier resins, or approximately 80% by weight or more (e.g., approximately 90% by weight or more) of the total amount of tackifier resins may be rosin-based tackifier resins. Substantially all of the tackifier resins (e.g., approximately 95 to 100% by weight, or even approximately 99 to 100% by weight) may be rosin-based tackifier resins.

[0092] In some embodiments, it is preferable to use a water-dispersed tackifier resin (also referred to as a tackifier resin emulsion) as the tackifier resin. In such embodiments, the PSA composition used to form the PSA layer contains the tackifier resin in the form of an emulsion in which the tackifier resin is dispersed in water. For example, by mixing an aqueous emulsion of an acrylic polymer with an emulsion of the tackifier resin, a PSA composition containing these components in a desired ratio can be easily prepared. It is preferable to use a tackifier resin emulsion that is at least substantially free of aromatic hydrocarbon solvents (more preferably, substantially free of aromatic hydrocarbon solvents and other organic solvents).

[0093] Such a tackifier resin emulsion may be prepared using a surfactant (emulsifier) ​​as needed. Surfactants that can be used in preparing the tackifier resin emulsion can be selected from one or more surfactants similar to those that can be used in preparing acrylic polymer emulsions. Anionic surfactants or nonionic surfactants are usually preferred. The amount of surfactant used is not particularly limited as long as it is an amount that allows the tackifier resin to be prepared in the form of an emulsion. For example, the amount can be about 0.2 parts by weight or more (preferably 0.5 parts by weight or more) and about 10 parts by weight or less (preferably 5 parts by weight or less) per 100 parts by weight (based on solids) of the tackifier resin.

[0094] When the PSA layer contains a tackifier resin, the content of the tackifier resin is not particularly limited. In some embodiments, the content of the tackifier resin (based on solid content) is usually about 1 part by weight or more per 100 parts by weight of the acrylic polymer, from the viewpoint of optimally exhibiting its use effect, and may be about 5 parts by weight or more, or may be about 10 parts by weight or more. In some preferred embodiments, the content of the tackifier resin per 100 parts by weight of the acrylic polymer is about 15 parts by weight or more, more preferably about 20 parts by weight or more, even more preferably about 25 parts by weight or more, particularly preferably about 30 parts by weight or more, and may be about 35 parts by weight or more. Furthermore, from the viewpoint of maintaining appearance quality, in some embodiments, the content of the tackifier resin per 100 parts by weight of the acrylic polymer is, for example, suitably approximately 60 parts by weight or less, preferably approximately 50 parts by weight or less, more preferably approximately 45 parts by weight or less, even more preferably 40 parts by weight or less, and may be 30 parts by weight or less, 20 parts by weight or less, or even 15 parts by weight or less. By limiting the amount of the tackifier resin added, the amount of additives such as emulsifiers that may be inevitably included in the tackifier resin can be reduced, thereby preventing or suppressing deterioration in appearance quality retention caused by such additives. Furthermore, by keeping the amount of the tackifier resin used within an appropriate range, the adhesive strength can be effectively improved. In other embodiments, the content of the tackifier resin per 100 parts by weight of the acrylic polymer can be approximately 10 parts by weight or less (e.g., less than 10 parts by weight), less than 5 parts by weight, less than 3 parts by weight, or less than 1 part by weight. The technology disclosed herein can be implemented in an embodiment in which the pressure-sensitive adhesive layer is substantially free of tackifier resin.

[0095] (Crosslinking Agent) In some embodiments, the pressure-sensitive adhesive layer contains a crosslinking agent. The use of a crosslinking agent can provide the resulting pressure-sensitive adhesive with appropriate cohesive strength. This cohesive strength suppresses the expansion of bubbles, even if they are generated in the pressure-sensitive adhesive layer, thereby improving the appearance quality retention. Aqueous crosslinking agents are preferably used as the crosslinking agent. The use of aqueous crosslinking agents is also beneficial in terms of eliminating organic solvents and being environmentally friendly. The term "aqueous crosslinking agent" encompasses both water-dispersible crosslinking agents and water-soluble crosslinking agents. Among these, the use of water-soluble crosslinking agents is preferred from the viewpoint of appearance quality retention. Furthermore, in this specification, unless otherwise specified, the term "crosslinking agent" refers to a crosslinking agent (also referred to as an external crosslinking agent) that is added (post-added) after the synthesis of the acrylic polymer. The pressure-sensitive adhesive layer may contain the crosslinking agent in a form after crosslinking reaction, a form before crosslinking reaction, a partially crosslinked form, or an intermediate or composite form thereof. The crosslinking agent is typically contained in the pressure-sensitive adhesive layer exclusively in a form after crosslinking reaction.

[0096] The type of crosslinking agent is not particularly limited, and can be appropriately selected from, for example, isocyanate-based crosslinking agents, epoxy-based crosslinking agents, oxazoline-based crosslinking agents, aziridine-based crosslinking agents, melamine-based crosslinking agents, peroxide-based crosslinking agents, urea-based crosslinking agents, metal alkoxide-based crosslinking agents, metal chelate-based crosslinking agents, metal salt-based crosslinking agents, carbodiimide-based crosslinking agents, hydrazide-based crosslinking agents, amine-based crosslinking agents, etc. The crosslinking agents can be used alone or in combination of two or more.

[0097] In some preferred embodiments, the crosslinking agent is selected from epoxy-based crosslinking agents, oxazoline-based crosslinking agents, carbodiimide-based crosslinking agents, hydrazide-based crosslinking agents, and aziridine-based crosslinking agents. These are multifunctional crosslinking agents having two or more functional groups that react with carboxyl groups or carbonyl groups. For example, in embodiments including an acrylic polymer having carboxyl groups, the crosslinking agent can form a crosslinked structure with good reactivity with the carboxyl groups of the acrylic polymer. Among the above crosslinking agents, carbodiimide-based crosslinking agents, epoxy-based crosslinking agents, and oxazoline-based crosslinking agents are more preferred, and epoxy-based crosslinking agents are particularly preferred. The use of a small amount of an epoxy-based crosslinking agent can effectively increase the degree of crosslinking, thereby limiting the impact of increasing the amount of crosslinking agent.

[0098] As the epoxy-based crosslinking agent, a compound having two or more epoxy groups per molecule can be used. Epoxy-based crosslinking agents having 3 to 5 epoxy groups per molecule are preferred. As the epoxy-based crosslinking agent, either water-soluble or water-dispersible types can be used, but water-soluble epoxy-based crosslinking agents are preferred. Specific examples of epoxy-based crosslinking agents include N,N,N',N'-tetraglycidyl-m-xylylenediamine, 1,3-bis(N,N-diglycidylaminomethyl)cyclohexane, 1,6-hexanediol diglycidyl ether, (poly)ethylene glycol diglycidyl ether, glycerol polyglycidyl ether, polyglycerol polyglycidyl ether, and the like. Examples of commercially available epoxy crosslinking agents include those manufactured by DIC Corporation under the trade name "Epiclon CR-5L" and those manufactured by Nagase ChemteX Corporation under the trade names "Denacol EX-313," "Denacol EX-512," "Denacol EX-810," "Denacol EX-821," "Denacol EX-830," and "Denacol EX-850."

[0099] As the oxazoline-based crosslinking agent, a compound having one or more oxazoline groups per molecule can be used. The oxazoline group may be any of a 2-oxazoline group, a 3-oxazoline group, and a 4-oxazoline group. An oxazoline-based crosslinking agent having a 2-oxazoline group can be preferably used. For example, a water-soluble copolymer or a water-dispersible copolymer obtained by copolymerizing an addition-polymerizable oxazoline such as 2-vinyl-2-oxazoline, 2-vinyl-4-methyl-2-oxazoline, 2-vinyl-5-methyl-2-oxazoline, 2-isopropenyl-2-oxazoline, 2-isopropenyl-4-methyl-2-oxazoline, or 2-isopropenyl-5-ethyl-2-oxazoline with another monomer can be used as the oxazoline-based crosslinking agent. Both water-soluble and water-dispersible oxazoline-based crosslinking agents can be used, but water-soluble oxazoline-based crosslinking agents are preferred. Commercially available oxazoline crosslinking agents include, for example, trade names "Epocross WS-500," "Epocross WS-700," "Epocross K-2010E," "Epocross K-2020E," and "Epocross K-2035E," manufactured by Nippon Shokubai Co., Ltd.

[0100] The carbodiimide crosslinking agent may be a low molecular weight compound or a high molecular weight compound having two or more carbodiimide groups. Commercially available carbodiimide crosslinking agents include the Carbodilite V series (aqueous solution type) such as "Carbodilite V-02," "Carbodilite V-02-L2," and "Carbodilite V-04," manufactured by Nisshinbo Chemical Inc., and the Carbodilite E series (aqueous dispersion type) such as "Carbodilite E-01," "Carbodilite E-02," and "Carbodilite E-04."

[0101] Examples of isocyanate-based crosslinking agents that can be used include polyfunctional isocyanate compounds having two or more functionalities. Examples include aromatic isocyanates such as tolylene diisocyanate, xylene diisocyanate, polymethylene polyphenyl diisocyanate, tris(p-isocyanatophenyl)thiophosphate, and diphenylmethane diisocyanate; alicyclic isocyanates such as isophorone diisocyanate; and aliphatic isocyanates such as hexamethylene diisocyanate. Both water-soluble and water-dispersible isocyanate-based crosslinking agents can be used. As the isocyanate-based crosslinking agent, so-called blocked isocyanate-type isocyanate-based crosslinking agents in which the isocyanate group is blocked may also be used. Commercially available products include the "Burnoc DNW" series manufactured by DIC Corporation, the "Aquanate" series manufactured by Tosoh Corporation, the "Takenate WD" series manufactured by Mitsui Chemicals, Inc., and the "Elastron BN" series manufactured by Dai-ichi Kogyo Seiyaku Co., Ltd.

[0102] The hydrazide-based crosslinking agent contains a hydrazino group (H ２ A hydrazino group-containing compound having two or more N-NH- groups can be used. Examples include polycarboxylic acid polyhydrazides such as oxalic acid dihydrazide, malonic acid dihydrazide, glutaric acid dihydrazide, succinic acid dihydrazide, and adipic acid dihydrazide, and hydantoins such as 1,3-bis(hydrazinocarbonoethyl)-5-isopropylhydantoin.

[0103] Examples of the aziridine crosslinking agent include trimethylolpropane tris[3-(1-aziridinyl)propionate] and trimethylolpropane tris[3-(1-(2-methyl)aziridinylpropionate)]. Either water-soluble or water-dispersible aziridine crosslinking agents can be used. Examples of commercially available aziridine crosslinking agents include trade names "ChemiTite PZ-33" and "ChemiTite DZ-22E" manufactured by Nippon Shokubai Co., Ltd.

[0104] In embodiments in which a crosslinking agent is used, the content of the crosslinking agent is not particularly limited. From the viewpoint of improving cohesive strength, etc., in some embodiments, the content of the crosslinking agent may be approximately 0.1 parts by weight or more, approximately 0.5 parts by weight or more, or approximately 0.8 parts by weight or more, relative to 100 parts by weight of the acrylic polymer. In some preferred embodiments, the content of the crosslinking agent may be approximately 1 part by weight or more, approximately 2 parts by weight or more, approximately 3 parts by weight or more, or approximately 4 parts by weight or more. Furthermore, in some embodiments, the content of the crosslinking agent may be approximately 15 parts by weight or less, approximately 10 parts by weight or less, approximately 8 parts by weight or less, or approximately 6 parts by weight or less, relative to 100 parts by weight of the acrylic polymer. By appropriately limiting the amount of crosslinking agent used, it is possible to preferably achieve both adhesiveness and cohesiveness. From the viewpoint of obtaining higher adhesive strength, in some preferred embodiments, the content of the crosslinking agent per 100 parts by weight of the acrylic polymer is approximately 5 parts by weight or less, or may be approximately 4.5 parts by weight or less, or may be approximately 3.5 parts by weight or less, or may be approximately 2.5 parts by weight or less, or may be approximately 1.5 parts by weight or less. In other embodiments, the content of the crosslinking agent per 100 parts by weight of the acrylic polymer may be approximately 1 part by weight or less (for example, less than 1 part by weight), or may be less than 0.1 parts by weight. The technology disclosed herein can be implemented in an embodiment in which the adhesive layer is substantially free of crosslinking agent.

[0105] In some embodiments, the pressure-sensitive adhesive layer may contain an acrylic polymer copolymerized with a silane monomer (silane coupling agent) and the crosslinking agent (external crosslinking agent). This allows for the formation of a favorable crosslinking structure within and between the acrylic polymer particles, resulting in a pressure-sensitive adhesive with favorable cohesive strength. In such embodiments, the ratio (weight ratio (C / S)) of the amount of crosslinking agent C to the amount of silane monomer S is not particularly limited. For example, the weight ratio (C / S) may be 1 or more, 10 or more, 30 or more, 50 or more, 80 or more, 100 or more, 120 or more, 150 or more, 180 or more, 200 or more, or 220 or more. The greater the weight ratio (C / S), the more effectively the crosslinked structure based on the crosslinking agent can be exerted. In some embodiments, the weight ratio (C / S) may be 1000 or less, 500 or less, 300 or less, 200 or less, 170 or less, 150 or less, 130 or less, 100 or less, or 70 or less. The smaller the weight ratio (C / S), the more favorably the effect of the crosslinked structure based on the silane-based monomer can be exhibited.

[0106] (Thickener) In some embodiments, the pressure-sensitive adhesive layer contains a thickener. The inclusion of a thickener can improve the coatability of the pressure-sensitive adhesive composition, facilitating the formation of a pressure-sensitive adhesive layer with good quality. As used herein, the term "thickener" refers to a component that, when added to an aqueous dispersion in which at least a portion of a pressure-sensitive adhesive-forming material is dispersed in water, increases the viscosity (thickening effect) compared to when the component is not added. The thickener is not particularly limited, and examples include polyacrylic acids, carboxylic acid copolymers, urethane compounds, polyvinyl alcohols, celluloses (e.g., hydroxycellulose), polyethers (e.g., polyethylene glycol), and the like. These can be used alone or in combination of two or more. For example, polyacrylic acids and carboxylic acid copolymers are preferably used. As the carboxylic acid copolymer, a copolymer containing a carboxyl group-containing acrylic monomer as a monomer unit is used.

[0107] In the embodiment in which the adhesive layer contains a thickener, the content of the thickener in the adhesive layer is appropriately set so as to obtain the desired viscosity characteristics.In some embodiments, the content of the thickener is suitably 0.01 parts by weight or more relative to 100 parts by weight of the acrylic polymer, and from the viewpoint of effectively obtaining the viscosity adjusting effect, it is preferably 0.1 parts by weight or more, more preferably 0.5 parts by weight or more, and even more preferably 0.8 parts by weight or more.In addition, in some embodiments, the content of the thickener is, for example, approximately 20 parts by weight or less relative to 100 parts by weight of the acrylic polymer, suitably approximately 10 parts by weight or less, preferably approximately 5 parts by weight or less, more preferably approximately 3 parts by weight or less, even more preferably approximately 2 parts by weight or less, and may be approximately 1 part by weight or less.

[0108] (Other Additives) The pressure-sensitive adhesive layer may optionally contain various additives within the range that does not significantly impair the effects of the present invention. Examples of such optional additives include pH adjusters, leveling agents, crosslinking aids, release adjusters, plasticizers, softeners, fillers, rust inhibitors, preservatives, mildew inhibitors, antistatic agents, antiaging agents, UV absorbers, antioxidants, light stabilizers, etc. As for such various additives, conventionally known ones can be used in the usual way, and since they do not particularly characterize the present invention, detailed explanations will be omitted.

[0109] (Pressure-Sensitive Adhesive Composition) The pressure-sensitive adhesive layer typically comprises a pressure-sensitive adhesive formed from a water-dispersed pressure-sensitive adhesive composition. A water-dispersed pressure-sensitive adhesive composition typically contains water or a mixed solvent or dispersion medium (aqueous solvent or aqueous dispersion medium) primarily composed of water as a dispersion medium. Typically, the proportion of water in the volatile components contained in the water-dispersed pressure-sensitive adhesive composition is, for example, approximately 90% by weight or more, preferably approximately 95 to 100% by weight. From the perspective of environmental considerations and eliminating organic solvents, in some embodiments, the water-dispersed pressure-sensitive adhesive composition is preferably substantially free of organic solvents. Here, "a pressure-sensitive adhesive composition substantially free of organic solvents" means that the amount of organic solvent in the pressure-sensitive adhesive composition is less than 1% by weight (e.g., less than 0.1% by weight). A water-dispersed pressure-sensitive adhesive composition can be prepared, for example, by mixing other components (such as a pigment dispersion) with an aqueous dispersion of an acrylic polymer. The aqueous dispersion of the acrylic polymer may be, for example, a polymerization reaction liquid obtained by emulsion polymerization, or a polymerization reaction liquid that has been subjected to treatment such as pH adjustment (e.g., neutralization), adjustment of the nonvolatile content, or adjustment of the viscosity, as necessary.

[0110] (Formation of Pressure-Sensitive Adhesive Layer) The pressure-sensitive adhesive layer disclosed herein can be formed by a conventionally known method. For example, a method can be employed in which a pressure-sensitive adhesive composition is applied to a surface (release surface) having releasability and then dried to form a pressure-sensitive adhesive layer. In a pressure-sensitive adhesive sheet having a supporting substrate, for example, a method (direct method) can be employed in which a pressure-sensitive adhesive composition is directly applied (typically coated) to the supporting substrate and then dried to form a pressure-sensitive adhesive layer. Alternatively, a method (transfer method) can be employed in which a pressure-sensitive adhesive composition is applied to a surface (release surface) having releasability and then dried to form a pressure-sensitive adhesive layer on the surface, and then the pressure-sensitive adhesive layer is transferred to a supporting substrate. For example, the surface of a release film described below can be preferably used as the release surface. The pressure-sensitive adhesive layer disclosed herein is typically formed continuously.

[0111] The pressure-sensitive adhesive composition can be applied using a conventional coater such as a gravure roll coater, die coater, reverse roll coater, kiss roll coater, dip roll coater, bar coater, knife coater, or spray coater. Alternatively, the pressure-sensitive adhesive composition may be applied by impregnation or curtain coating. From the viewpoints of promoting the crosslinking reaction and improving production efficiency, the pressure-sensitive adhesive composition is preferably dried under heating. The drying temperature can be, for example, about 40 to 150°C, and is usually preferably about 60 to 130°C. After drying, the pressure-sensitive adhesive composition may be further aged for the purposes of adjusting component migration within the pressure-sensitive adhesive layer, promoting the crosslinking reaction, and alleviating distortion that may exist within the pressure-sensitive adhesive layer.

[0112] (Thickness of Pressure-Sensitive Adhesive Layer) The thickness of the pressure-sensitive adhesive layer is not particularly limited. Depending on the application and intended use, a configuration having a pressure-sensitive adhesive layer with an appropriate thickness, for example, about 300 μm or less, can be adopted. From the viewpoint of avoiding excessive thickness of the pressure-sensitive adhesive sheet, in some embodiments, the thickness of the pressure-sensitive adhesive layer is preferably about 100 μm or less, more preferably about 70 μm or less, and even more preferably about 50 μm or less. In some preferred embodiments, the thickness of the pressure-sensitive adhesive layer can be about 35 μm or less, for example, about 25 μm or less, about 20 μm or less, about 15 μm or less, or about 10 μm or less (e.g., less than 10 μm). A pressure-sensitive adhesive layer with a limited thickness can effectively meet the demands for thinness and weight reduction. On the other hand, while pinholes and the like tend to be more noticeable in a thin pigment-containing pressure-sensitive adhesive layer, the pressure-sensitive adhesive sheet disclosed herein is less likely to develop pinholes and the like even when exposed to a high-temperature environment, and is therefore preferably applicable to configurations including such a thin pressure-sensitive adhesive layer. Furthermore, from the viewpoint of adhesive strength, etc., in some embodiments, it is advantageous for the thickness of the pressure-sensitive adhesive layer to be approximately 1 μm or more, and appropriately approximately 3 μm or more, preferably approximately 5 μm or more, more preferably approximately 10 μm or more, even more preferably approximately 12 μm or more, and may even be approximately 15 μm or more. By making the pressure-sensitive adhesive layer have a predetermined thickness or more, it is easy to achieve excellent light-blocking properties and concealment of the adherend. In some embodiments, the thickness of the pressure-sensitive adhesive layer may be 20 μm or more, 30 μm or more, or 40 μm or more. In a substrate-attached double-sided pressure-sensitive adhesive sheet having a first pressure-sensitive adhesive layer and a second pressure-sensitive adhesive layer on each side of the substrate, the first pressure-sensitive adhesive layer and the second pressure-sensitive adhesive layer may have the same thickness or different thicknesses.

[0113] (Light transmittance of pressure-sensitive adhesive layer) The light transmittance of the pressure-sensitive adhesive layer may vary depending on the purpose of adding the pigment (such as light-blocking properties or design properties). In some embodiments, the pressure-sensitive adhesive layer has a light transmittance at a wavelength of 550 nm (550 nm light transmittance) of approximately 80% or less. By incorporating a pigment into the pressure-sensitive adhesive layer, a pressure-sensitive adhesive layer with reduced light transmittance can be formed. The 550 nm light transmittance of the pressure-sensitive adhesive layer may be approximately 70% or less, approximately 60% or less, approximately 50% or less (e.g., less than 50%), approximately 40% or less, 30% or less, 20% or less, or 10% or less. In some preferred embodiments, the 550 nm light transmittance of the pressure-sensitive adhesive layer is less than 10%, may be 5% or less, 3% or less, 1.5% or less, 1.0% or less, or 0.1% or less. A pressure-sensitive adhesive sheet having a pressure-sensitive adhesive layer exhibiting the above-mentioned 550 nm light transmittance can exhibit excellent light-shielding properties and adherend concealment properties.In addition, in some embodiments, the lower limit of the 550 nm light transmittance of the pressure-sensitive adhesive layer may be 0.1% or more, or 0.3% or more, from the viewpoint of other properties such as productivity and adhesive strength.In some embodiments, the 550 nm light transmittance of the pressure-sensitive adhesive layer may be 1% or more, 3% or more, or 5% or more.The 550 nm light transmittance of the pressure-sensitive adhesive layer can be measured in the same manner as the 550 nm light transmittance of the pressure-sensitive adhesive sheet described in the Examples below.

[0114] (Gel Fraction of Pressure-Sensitive Adhesive Layer) In the pressure-sensitive adhesive sheet disclosed herein, the gel fraction of the pressure-sensitive adhesive layer is not particularly limited. The gel fraction of the pressure-sensitive adhesive layer may be, for example, 98% or less, 95% or less, or 90% or less. From the viewpoint of easily obtaining adhesive strength to an adherend (e.g., adhesive strength suitable for fixing a member), in some embodiments, the gel fraction of the pressure-sensitive adhesive layer is suitably less than 90%, advantageously less than 85%, preferably 80% or less (e.g., less than 80%), more preferably 77% or less, may be 75% or less, may be 73% or less, may be 70% or less, may be 65% or less, may be 60% or less, may be 55% or less, or may be 50% or less. Furthermore, the gel fraction of the pressure-sensitive adhesive may be 0%, and from the viewpoint of easily obtaining an appropriate cohesive strength, it is suitably 10% or more, and preferably 20% or more. From the viewpoint of increasing the crosslink density of the adhesive and suppressing the expansion of bubbles generated in the adhesive layer, in some embodiments, the gel fraction of the adhesive layer is suitably 25% or more, advantageously 35% or more, preferably 40% or more, or may be 45% or more, 50% or more, 60% or more, 65% or more, or 70% or more.

[0115] The gel fraction of the pressure-sensitive adhesive layer can be determined by wrapping a sample of weight W1 taken from the pressure-sensitive adhesive layer in a porous tetrafluoroethylene resin sheet, immersing it in ethyl acetate at room temperature for one week, drying it, measuring the weight W2 of the ethyl acetate-insoluble portion, and substituting W1 and W2 into the following formula: gel fraction [%] = W2 / W1 x 100. As the porous tetrafluoroethylene resin sheet, Nitto Denko Corporation's product name "Nitoflon (registered trademark) NTF1122" (average pore size 0.2 μm, porosity 75%, thickness 85 μm) or an equivalent product can be used.

[0116] <Support Substrate> In embodiments in which the PSA sheet disclosed herein is in the form of a single-sided or double-sided PSA sheet with a substrate, the substrate supporting the PSA layer can be a resin film, paper, cloth, rubber sheet, foam sheet, metal foil, a composite thereof, or the like. Examples of paper include Japanese paper, kraft paper, glassine paper, fine paper, synthetic paper, and top-coated paper. Examples of cloth include woven fabrics and nonwoven fabrics made from various fibrous materials, either alone or in combination. Examples of the fibrous material include cotton, staple fiber, Manila hemp, pulp, rayon, acetate fiber, polyester fiber, polyvinyl alcohol fiber, polyamide fiber, and polyolefin fiber. Examples of rubber sheets include natural rubber sheets and butyl rubber sheets. Examples of foam sheets include foamed polyurethane sheets and foamed polychloroprene rubber sheets. Examples of metal foils include aluminum foil and copper foil.

[0117] The term "nonwoven fabric" as used herein refers primarily to nonwoven fabrics for adhesive sheets used in the field of adhesive tapes and other adhesive sheets, and typically refers to nonwoven fabrics (sometimes referred to as "paper") produced using a general papermaking machine. The term "resin film" as used herein typically refers to a non-porous resin sheet, and is distinguished from, for example, nonwoven fabrics and woven fabrics (i.e., does not include nonwoven fabrics or woven fabrics). Such resin films may be non-foamed. Here, a non-foamed resin film refers to a resin film that has not been intentionally treated to form a foam. Specifically, a non-foamed resin film may be a resin film having an expansion ratio of less than 1.1 (e.g., less than 1.05, typically less than 1.01). The resin film may be a non-stretched film, a uniaxially stretched film, or a biaxially stretched film.

[0118] As the support substrate constituting the substrate-attached PSA sheet, a base film containing a resin film can be preferably used. The base film is typically a member that can independently maintain its shape (independent). The support substrate in the technology disclosed herein can be substantially composed of such a base film. Alternatively, the support substrate may include an auxiliary layer in addition to the base film. Examples of the auxiliary layer include a colored layer, a reflective layer, an undercoat layer, an antistatic layer, etc., provided on the surface of the base film.

[0119] The resin film is a film containing a resin material as a main component (for example, a component contained in the resin film at more than 50% by weight). Examples of resin films include polyolefin-based resin films such as polyethylene (PE), polypropylene (PP), and ethylene-propylene copolymer; polyester-based resin films such as polyethylene terephthalate (PET), polybutylene terephthalate (PBT), and polyethylene naphthalate (PEN); vinyl chloride-based resin films; vinyl acetate-based resin films; polyimide-based resin films; polyamide-based resin films; fluororesin films; cellophane; and the like. The resin film may also be a rubber-based film such as a natural rubber film or a butyl rubber film. Among these, polyester films are preferred from the viewpoints of handleability and processability, and PET films are particularly preferred.

[0120] A colorant can be contained in the resin film. This allows the light transmittance (light blocking property, etc.) of the resin film to be adjusted. Adjusting the light transmittance (for example, perpendicular light transmittance) of the resin film can also be useful for adjusting the light transmittance of a substrate containing the resin film, and even the light transmittance of a pressure-sensitive adhesive sheet containing the substrate. Conventionally known pigments and dyes can be used as the colorant. The color of the colorant is not particularly limited.

[0121] In some embodiments, a black colorant may be preferably used because light-blocking properties (e.g., vertical light transmittance) can be efficiently adjusted with a small amount of colorant. Specific examples of black colorants include those exemplified as black pigments that can be contained in the pressure-sensitive adhesive layer. While not particularly limited, in some embodiments, a pigment (e.g., a particulate black colorant such as carbon black) with a volume-average particle diameter of 10 nm to 500 nm, more preferably 10 nm to 120 nm, can be used. In other embodiments, the resin film may contain a white colorant such as titanium oxide. The amount of colorant used in the resin film is not particularly limited and can be adjusted appropriately to impart the desired optical properties. The amount of colorant used is typically approximately 0.1 to 30 wt % of the weight of the resin film, for example, 0.1 to 25 wt % (typically 0.1 to 20 wt %).

[0122] The resin film may contain various additives, such as fillers (inorganic fillers, organic fillers, etc.), dispersants (surfactants, etc.), antioxidants, antioxidants, UV absorbers, antistatic agents, lubricants, plasticizers, etc. The blending ratio of the various additives is usually about less than 30% by weight (for example, less than 20% by weight, typically less than 10% by weight).

[0123] The resin film may have a single layer structure, or a multilayer structure of two, three or more layers. From the viewpoint of shape stability, the resin film preferably has a single layer structure. In the case of a multilayer structure, at least one layer (preferably all layers) preferably has a continuous structure of the resin (e.g., polyester-based resin). The method for producing the resin film is not particularly limited and may be any conventionally known method. For example, conventionally known general film forming methods such as extrusion molding, inflation molding, T-die casting molding, and calendar roll molding may be used.

[0124] The supporting substrate may be colored by a colored layer disposed on the surface of a base film (preferably a resin film). In such a substrate having a configuration including a base film and a colored layer, the base film may or may not contain a colorant. The colored layer may be disposed on either one surface of the base film, or may be disposed on both surfaces. In a configuration in which colored layers are disposed on both surfaces of the base film, the configurations of the colored layers may be the same or different.

[0125] The colored layer may have a single-layer structure consisting of a single layer, or may have a multilayer structure including two, three, or more sub-colored layers. A multilayer colored layer including two or more sub-colored layers can be formed, for example, by repeatedly applying (e.g., printing) a colored layer-forming composition. The color and amount of colorant contained in each sub-colored layer may be the same or different. For a colored layer intended to impart light-blocking properties, a multilayer structure is particularly useful from the viewpoint of preventing pinholes and improving reliability in preventing light leakage.

[0126] The thickness of the entire color layer is usually about 1 μm to 10 μm, preferably about 1 μm to 7 μm, for example, about 1 μm to 5 μm. In a color layer including two or more sub-color layers, the thickness of each sub-color layer is usually preferably about 1 μm to 2 μm.

[0127] The thickness of the support substrate is not particularly limited. From the viewpoint of preventing the pressure-sensitive adhesive sheet from becoming excessively thick, the thickness of the support substrate can be, for example, approximately 200 μm or less (e.g., approximately 100 μm or less). Depending on the purpose and mode of use of the pressure-sensitive adhesive sheet, the thickness of the support substrate may be approximately 70 μm or less, approximately 30 μm or less, or approximately 10 μm or less (e.g., approximately 5 μm or less). The lower limit of the thickness of the support substrate is not particularly limited. From the viewpoint of the handleability and processability of the pressure-sensitive adhesive sheet, the thickness of the support substrate is usually approximately 2 μm or more, preferably approximately 3 μm or more, and may be, for example, approximately 5 μm or more.

[0128] The surface of the support substrate may be subjected to a conventionally known surface treatment such as corona discharge treatment, plasma treatment, ultraviolet irradiation treatment, acid treatment, alkali treatment, application of a primer, etc. Such a surface treatment may be a treatment for improving the adhesion between the support substrate and the pressure-sensitive adhesive layer, in other words, the anchoring ability of the pressure-sensitive adhesive layer to the support substrate.

[0129] <Release Film> In the technology disclosed herein, a release film (also referred to as a release liner) can be used during the formation of the pressure-sensitive adhesive layer, the production of the pressure-sensitive adhesive sheet, and the storage, distribution, and shaping of the pressure-sensitive adhesive sheet before use. The release film is not particularly limited, and examples that can be used include release films having a release treatment layer on the surface of a substrate (release film substrate) such as a resin film or paper, and release films made of low-adhesion materials such as fluorine-based polymers (polytetrafluoroethylene, etc.) and polyolefin-based resins (polyethylene, polypropylene, etc.). The release treatment layer can be formed by surface-treating the substrate with a release treatment agent such as a silicone-based, long-chain alkyl-based, fluorine-based, or molybdenum sulfide.

[0130] <Characteristics of the Pressure-Sensitive Adhesive Sheet> The total thickness of the pressure-sensitive adhesive sheet disclosed herein (which includes a pressure-sensitive adhesive layer and, in configurations having a supporting substrate, further includes a supporting substrate, but does not include a release film) is not particularly limited. The total thickness of the pressure-sensitive adhesive sheet can be, for example, approximately 500 μm or less, and may be approximately 300 μm or less. From the viewpoint of thinning and weight reduction, in some embodiments, the thickness of the pressure-sensitive adhesive sheet is usually approximately 200 μm or less, preferably approximately 100 μm or less, more preferably approximately 70 μm or less, and even more preferably approximately 50 μm or less. In some preferred embodiments, the thickness of the pressure-sensitive adhesive sheet may be approximately 35 μm or less, approximately 25 μm or less, approximately 20 μm or less, approximately 15 μm or less, or approximately 10 μm or less (e.g., less than 10 μm). The thickness of the pressure-sensitive adhesive sheet can be approximately 1 μm or more, for example, approximately 3 μm or more, preferably approximately 5 μm or more, more preferably approximately 10 μm or more, even more preferably approximately 12 μm or more, and may be approximately 15 μm or more. In some embodiments, the thickness of the pressure-sensitive adhesive sheet may be 20 μm or more, 30 μm or more, or even 40 μm or more. A pressure-sensitive adhesive sheet having a thickness of a predetermined value or more can have a pressure-sensitive adhesive layer with sufficient thickness, making it easier to obtain properties based on the pressure-sensitive adhesive layer (e.g., adhesive properties such as adhesive strength) and also tends to be easy to handle. In a substrate-less pressure-sensitive adhesive sheet, the thickness of the pressure-sensitive adhesive layer is the total thickness of the pressure-sensitive adhesive sheet.

[0131] The pressure-sensitive adhesive sheet disclosed herein has a pigment-containing pressure-sensitive adhesive layer, and therefore may have lower light transmittance than a transparent pressure-sensitive adhesive sheet. The light transmittance of the pressure-sensitive adhesive sheet may vary depending on the purpose of adding the pigment to the pressure-sensitive adhesive layer (such as light-blocking properties or design properties). In some embodiments, the 550 nm light transmittance of the pressure-sensitive adhesive sheet is approximately 80% or less, may be approximately 70% or less, may be approximately 60% or less, may be approximately 50% or less (e.g., less than 50%), may be approximately 40% or less, may be 30% or less, may be 20% or less, or may be 10% or less. In some preferred embodiments, the 550 nm light transmittance of the pressure-sensitive adhesive sheet is less than 10%, may be 5% or less, may be 3% or less, may be 1.5% or less, may be 1.0% or less, or may be 0.1% or less. Pressure-sensitive adhesive sheets exhibiting the above 550 nm light transmittance may exhibit excellent light-blocking properties. In some embodiments, the lower limit of the 550 nm light transmittance of the pressure-sensitive adhesive sheet may be 0.1% or more, or 0.3% or more, from the viewpoint of productivity, adhesive strength, and other properties. In some embodiments, the 550 nm light transmittance of the pressure-sensitive adhesive layer may be 1% or more, 3% or more, or 5% or more. The 550 nm light transmittance of the pressure-sensitive adhesive sheet can be measured by the method described in the Examples below.

[0132] The adhesive strength of the PSA sheet disclosed herein may vary depending on the intended use and the application location, and is therefore not limited to a specific range. From the viewpoint of obtaining good adhesion to the adherend, in some embodiments, the PSA sheet has a 180-degree peel strength (adhesion strength to SUS) against a stainless steel plate of approximately 3 N / 20 mm or more, preferably approximately 5 N / 20 mm or more, more preferably approximately 7 N / 20 mm or more, and may be approximately 9 N / 20 mm or more, approximately 10 N / 20 mm or more, approximately 12 N / 20 mm or more, or approximately 14 N / 20 mm or more. The PSA sheet disclosed herein can achieve an adhesive strength equal to or greater than the predetermined level by using a pigment-containing adhesive layer. The upper limit of the adhesive strength to SUS is not particularly limited, and may be, for example, approximately 30 N / 20 mm or less. The adhesive strength to SUS is the 180-degree peel strength against a stainless steel plate measured in accordance with JIS Z 0237, and can be measured specifically by the method described in the Examples below.

[0133] <Applications> The pressure-sensitive adhesive sheet disclosed herein has a pigment-containing pressure-sensitive adhesive layer and can maintain good appearance quality even when exposed to high-temperature environments. Therefore, it is suitable for a variety of applications in which the pressure-sensitive adhesive sheet attached to the surface of an adherend is visible, such as applications requiring the concealing properties of the pressure-sensitive adhesive sheet, applications in which a colored pressure-sensitive adhesive layer is used to impart design or color, and other applications requiring specific optical properties (such as light transmittance). For example, electronic devices have parts that are visible to the user and require excellent appearance quality. The pressure-sensitive adhesive sheet disclosed herein can be applied to visible parts of electronic devices to achieve a surface with good appearance quality. The pressure-sensitive adhesive sheet disclosed herein is suitable for applications such as joining components of electronic devices, including home appliances, office automation devices, and portable electronic devices such as smartphones, and for imparting optical properties (e.g., light-blocking properties) to the above-mentioned electronic devices.

[0134] Non-limiting examples of the portable electronic device include mobile phones, smartphones, tablet PCs, notebook PCs, various wearable devices (e.g., wristwear devices worn on the wrist like a wristwatch, modular devices worn on a part of the body with a clip or strap, eyewear devices including eyeglasses (monocular and binocular, including head-mounted devices), clothing devices attached to shirts, socks, hats, etc. as accessories, earwear devices attached to the ears like earphones), digital cameras, digital video cameras, audio equipment (portable music players, IC recorders, etc.), calculators (calculators, etc.), portable game devices, electronic dictionaries, electronic organizers, e-books, in-car information devices, portable radios, portable televisions, portable printers, portable scanners, portable modems, etc. Note that, in this specification, the term "portable" does not simply mean that a device is portable, but rather means that the device has a level of portability that allows it to be carried relatively easily by an individual (average adult). Examples of the electronic device include personal computers (desktop, notebook, tablet, etc.), televisions, etc. These devices may have built-in display devices such as liquid crystal or organic electroluminescence (EL) displays.

[0135] In some embodiments, the adhesive sheet can be used for the purpose of fixing a pressure-sensitive sensor to other members in an electronic device equipped with a pressure-sensitive sensor, such as the above-mentioned portable electronic device. In some embodiments, the adhesive sheet can be used for fixing a pressure-sensitive sensor to other members in an electronic device (typically a portable electronic device) equipped with a function that enables an absolute position to be specified on a plate (typically a touch panel) corresponding to the screen using a device for indicating a position on the screen (typically a pen-type or mouse-type device) and a device for detecting the position.

[0136] The pressure-sensitive adhesive sheet disclosed herein is also suitable for use in applications where it is disposed on the back surface of a display screen (display unit) such as a touch panel display in an electronic device such as a portable electronic device. By disposing the pressure-sensitive adhesive sheet according to some embodiments on the back surface of the display screen (display unit), it is possible to prevent a decrease in the visibility of the display screen regardless of the manner in which the electronic device is used. For example, by disposing the pressure-sensitive adhesive sheet on the back surface of a display screen (display unit) such as a touch panel display in the electronic device, it is possible to prevent light reflection through the display screen. The above-mentioned reflection can be caused by a metal member disposed on the back side of the display screen, but by using the pressure-sensitive adhesive sheet according to some embodiments, for example, to bond the metal member to the display unit, it is possible to simultaneously achieve bonding of the members and imparting light-blocking properties.

[0137] Materials (adherend materials) to which the pressure-sensitive adhesive sheets disclosed herein can be attached include, but are not limited to, metal materials such as copper, silver, gold, iron, tin, palladium, aluminum, nickel, titanium, chromium, zinc, etc., or alloys containing two or more of these metals; various resin materials (typically plastic materials) such as polyimide resins, acrylic resins, polyethernitrile resins, polyethersulfone resins, polyester resins (polyethylene terephthalate resins, polyethylene naphthalate resins, etc.), polyvinyl chloride resins, polyphenylene sulfide resins, polyetheretherketone resins, polyamide resins (so-called aramid resins, etc.), polyarylate resins, polycarbonate resins, and liquid crystal polymers; and inorganic materials such as alumina, zirconia, soda glass, quartz glass, and carbon. Among these, metal materials such as copper, aluminum, and stainless steel, and resin materials (typically plastic materials) such as polyimide resins, aramid resins, and polyphenylene sulfide resins are widely used. The above materials can be used as components for electronic devices and other products. The adhesive sheet disclosed herein can be used by being attached to a member made of the above-mentioned material. Furthermore, the above-mentioned material can be a material constituting a fixing object such as the pressure-sensitive sensor or display unit (e.g., a back surface member such as an electromagnetic wave shield or a reinforcing plate). The fixing object refers to the object to which the adhesive sheet is attached, i.e., the adherend. Furthermore, the back surface member refers to a member arranged on the opposite side of the front surface (viewing side) of the pressure-sensitive sensor or display unit in, for example, a portable electronic device, and can be, for example, a member constituting the support member 540 arranged on the back surface of the display device 500 shown in FIG. 5 (described below). The fixing object can have either a single-layer structure or a multilayer structure, and the surface (attachment surface) to which the adhesive sheet is attached (the attachment surface) can be subjected to various surface treatments. Although not particularly limited, an example of the fixing object is a back surface member having a thickness of 1 μm or more (typically 5 μm or more, e.g., 60 μm or more, or even 120 μm or more) and 1500 μm or less (e.g., 800 μm or less).

[0138] In some embodiments, the component or material to which the PSA sheet is attached may be optically transparent (a light-transmitting adherend). Since the adhesive surface of a PSA sheet attached to a light-transmitting adherend can be visible through the light-transmitting adherend, good appearance quality is desirable. The 550 nm light transmittance of the light-transmitting adherend may be, for example, greater than 50%, such as 70% or more. In some preferred embodiments, the 550 nm light transmittance of the adherend is 80% or more, more preferably 90% or more, and may be 95% or more (e.g., 95-100%). Such a material may be a resin film (e.g., a polyester resin film such as a PET film) disposed on the back surface of the image display unit of various devices, such as a portable electronic device. The PSA sheet disclosed herein may be preferably used in an embodiment in which it is attached to an adherend (e.g., a component) having a 550 nm light transmittance of a predetermined value or higher, as described above. The 550 nm light transmittance may be measured in the same manner as the 550 nm light transmittance of a PSA sheet.

[0139] In some embodiments, the pressure-sensitive adhesive sheet is used in a manner in which it is attached to a metal member. Examples of materials for the metal member include the metal materials exemplified above as the adherend material. Such metal members are, for example, members or articles having a surface (adhesive sheet attachment surface) formed from a metal material such as aluminum or stainless steel. Suitable examples include metal members such as stainless steel members and aluminum members. By attaching the pressure-sensitive adhesive sheet to an area of ​​the metal member surface that needs to be concealed, the area of ​​the metal member can be concealed. The pressure-sensitive adhesive sheet may cover the entire surface of the metal member, or may cover only a portion of the surface (e.g., a portion of the area that needs to be concealed). The metal member may, for example, be a member constituting the support portion 540 of the display device 500 shown in FIG. 5 (described below). The metal member is preferably one of the adherends of the pressure-sensitive adhesive sheet.

[0140] The pressure-sensitive adhesive sheet according to some embodiments can be preferably used in electronic devices (typically portable electronic devices) that require specific optical properties. For example, the pressure-sensitive adhesive sheet can be preferably used in electronic devices that include various light sources such as LEDs (light emitting diodes) or light-emitting elements such as self-luminous organic EL devices. For example, the pressure-sensitive adhesive sheet can be preferably used in electronic devices (typically portable electronic devices) that include organic EL display devices or liquid crystal display devices that require specific optical properties.

[0141] Fig. 5 is an exploded perspective view schematically illustrating an exemplary configuration of a display device. As shown in Fig. 5, display device 500 included in portable electronic device 400 includes display unit 520 configured from a cover member, an organic EL unit, etc., and support unit 540. Display device 500 is configured to further include an adhesive sheet 530. In this configuration example, adhesive sheet 530 fixes the members that make up display unit 520 and support unit 540. Note that support unit 540 is configured to include a substrate (a metal plate such as a stainless steel plate or an aluminum plate) and the like. The adhesive sheet disclosed herein is preferably used as a component of the above-mentioned display device.

[0142] The present specification discloses the following: [1] A pressure-sensitive adhesive sheet having a pressure-sensitive adhesive layer, wherein the pressure-sensitive adhesive layer comprises a water-dispersible acrylic polymer and a pigment, and the water-dispersible acrylic polymer is a polymer synthesized by emulsion polymerization using a reactive emulsifier having a radically polymerizable functional group. [2] The pressure-sensitive adhesive sheet according to [1] above, having a light transmittance of 15% or less at a wavelength of 550 nm. [3] The pressure-sensitive adhesive sheet according to [1] or [2] above, wherein the pigment comprises inorganic particles. [4] The pressure-sensitive adhesive sheet according to any one of [1] to [3] above, wherein the pressure-sensitive adhesive layer comprises carbon black as the pigment. [5] The pressure-sensitive adhesive sheet according to any one of [1] to [4] above, wherein the content of the pigment in the pressure-sensitive adhesive layer is in the range of 0.1 to 15 parts by weight per 100 parts by weight of the water-dispersible acrylic polymer. [6] The pressure-sensitive adhesive sheet according to any one of [1] to [5] above, wherein the thickness of the pressure-sensitive adhesive layer is 1 μm or more and 100 μm or less. [7] The pressure-sensitive adhesive sheet according to any one of [1] to [6] above, which is a substrate-less double-sided pressure-sensitive adhesive sheet comprising the pressure-sensitive adhesive layer. [8] The pressure-sensitive adhesive sheet according to any one of [1] to [6] above, which is a substrate-attached pressure-sensitive adhesive sheet comprising the pressure-sensitive adhesive layer and a supporting substrate. [9] The pressure-sensitive adhesive sheet according to any one of [1] to [8] above, which has a 180-degree peel strength from a stainless steel plate of 5 N / 20 mm or more.

[10] An electronic device comprising the pressure-sensitive adhesive sheet according to any one of [1] to [9] above.

[0143] Several examples of the present invention will be described below, but it is not intended that the present invention be limited to those shown in these examples. In the following description, "parts" and "%" are by weight unless otherwise specified.

[0144] Example 1 Preparation of Acrylic Polymer 73 parts of ion-exchanged water and 0.07 parts of emulsifier E1 (trade name "Aqualon KH-1025", manufactured by Dai-ichi Kogyo Seiyaku Co., Ltd., an anionic reactive surfactant) were placed in a reaction vessel equipped with a thermometer, a stirrer, a nitrogen inlet tube, and a reflux condenser, and the mixture was stirred at 60°C for 1 hour under a nitrogen atmosphere. To this was added 0.1 part of a polymerization initiator (trade name "VA-057", manufactured by Fujifilm Wako Pure Chemical Industries, Ltd.), and then a monomer emulsion prepared by emulsifying 85 parts of 2-ethylhexyl acrylate (2EHA), 13 parts of methyl acrylate (MA), 1.25 parts of acrylic acid (AA), 0.75 parts of methacrylic acid (MAA), 0.035 parts of t-dodecanethiol (chain transfer agent), 0.02 parts of 3-methacryloxypropyltrimethoxysilane (trade name "KBM-503", manufactured by Shin-Etsu Chemical Co., Ltd.), and 1.88 parts of the above-mentioned emulsifier E1 (trade name "Aqualon KH-1025") in 30 parts of ion-exchanged water was added dropwise at 60°C over 4 hours to carry out polymerization. After further maintaining the temperature at 60°C for 3 hours, the mixture was cooled to room temperature and adjusted to pH 6.0 using 10% aqueous ammonia as a pH adjuster, thereby preparing an acrylic polymer emulsion containing a water-dispersible acrylic polymer.

[0145] (Preparation of Pressure-Sensitive Adhesive Composition) To the obtained acrylic polymer emulsion, 1 part of a thickener (trade name "Aron B-500", manufactured by Toagosei Co., Ltd., carboxylic acid copolymer) and 4 parts of Pigment P1 (trade name "Aqua Black 162", manufactured by Tokai Carbon Co., Ltd., self-dispersible carbon black aqueous dispersion, volume average particle size 110 nm) were added and mixed relative to 100 parts of the water-dispersible acrylic polymer, based on solids content. Ion-exchanged water and 10% aqueous ammonia were added to the obtained mixture to adjust the pH to 9.0 and the solids concentration to 40%, and the mixture was stirred at 2000 rpm for 5 minutes in a Mixer (manufactured by Thinky Corporation), followed by vacuum degassing at 2200 rpm for 5 minutes, to obtain a water-dispersible Pressure-Sensitive Adhesive Composition.

[0146] (Preparation of Pressure-Sensitive Adhesive Sheet) The pressure-sensitive adhesive composition was applied to the release-treated surface of a silicone-release-treated polyethylene terephthalate (PET) film (trade name "Diafoil MRF38", manufactured by Mitsubishi Chemical Corporation, thickness 38 μm) and dried at 100 ° C. for 3 minutes to form a pressure-sensitive adhesive layer with a thickness of 15 μm. The release-treated surface of a release-treated polyester film (trade name "Diafoil MRF25", manufactured by Mitsubishi Chemical Corporation, thickness 25 μm) was bonded to this pressure-sensitive adhesive layer. In this way, a substrateless double-sided pressure-sensitive adhesive sheet was obtained, both sides of which were protected by the two release films.

[0147] Examples 2 to 10 and Comparative Examples 1 and 2 The type of emulsifier, the type and amount of pigment, and the thickness of the adhesive layer were changed as shown in Tables 1 and 2. A pressure-sensitive adhesive composition for each example was prepared in the same manner as in Example 1, and a substrate-less pressure-sensitive adhesive sheet for each example was obtained in the same manner as in Example 1, except for using the pressure-sensitive adhesive composition. The materials used in the above examples and comparative examples are shown below. Emulsifier E1: Anionic reactive surfactant (trade name "Aqualon KH-1025", manufactured by Dai-ichi Kogyo Seiyaku Co., Ltd.) Emulsifier E2: Anionic reactive surfactant (trade name "Aqualon HS-10", manufactured by Dai-ichi Kogyo Seiyaku Co., Ltd.) Emulsifier E3: Nonionic reactive surfactant (trade name "Aqualon RN-20", manufactured by Dai-ichi Kogyo Seiyaku Co., Ltd.) Emulsifier E4: Anionic surfactant (trade name "Latemul E-118B", manufactured by Kao Corporation, non-reactive) Emulsifier E5: Nonionic surfactant (trade name "Emulgen A-60", manufactured by Kao Corporation, non-reactive) Pigment P1: Carbon black aqueous dispersion (trade name "Aqua Black 162", manufactured by Tokai Carbon Co., Ltd., self-dispersing type, volume average particle diameter 110 nm) Pigment P2: Carbon black aqueous dispersion (trade name "SA Black A4048", manufactured by Mikuni Shikiso Co., Ltd., using polymeric dispersant, volume average particle diameter 110 nm) Pigment P3: Carbon black aqueous dispersion (trade name "PSM Black C", manufactured by Mikuni Color Co., Ltd., using a nonionic dispersant, volume average particle diameter 130 nm)

[0148] Examples 11 to 16 In preparing the aqueous dispersion PSA compositions, the types and amounts of tackifier resins shown in Table 1 were further added. The aqueous dispersion PSA compositions for each example were obtained in the same manner as in Example 1, and substrate-less PSA sheets for each example were obtained in the same manner as in Example 1, except for using the PSA compositions. The tackifier resins used are as follows: Tackifier resin T1: terpene phenol resin (trade name "Tamanol E-200NT", manufactured by Arakawa Chemical Industries, Ltd., softening point 145°C) Tackifier resin T2: rosin ester resin (trade name "Superester E-865NT", manufactured by Arakawa Chemical Industries, Ltd., softening point 160°C)

[0149] Examples 17 to 25 In preparing the aqueous dispersion-type PSA compositions, the types and amounts of crosslinking agents shown in Table 2 were further added. The aqueous dispersion-type PSA compositions for each example were obtained in the same manner as in Example 12, and substrate-less PSA sheets for each example were obtained in the same manner as in Example 1, except that the PSA compositions were used. The crosslinking agents used are as follows: Crosslinking agent C1: Water-soluble carbodiimide-based crosslinking agent (trade name "Carbodilite V-04", manufactured by Nisshinbo Chemical Inc.) Crosslinking agent C2: Water-soluble epoxy-based crosslinking agent (trade name "Denacol EX-313", manufactured by Nagase ChemteX Corporation) Crosslinking agent C3: Water-soluble oxazoline-based crosslinking agent (trade name "Epocross WS-500", manufactured by Nippon Shokubai Co., Ltd.)

[0150] Example 26 An aqueous dispersion PSA composition was prepared using the same method as in Example 1. The PSA composition was applied to the release-treated surface of a silicone release-treated polyethylene terephthalate (PET) film (trade name "Diafoil MRF38", manufactured by Mitsubishi Chemical Corporation, thickness 38 μm) and dried at 100° C. for 3 minutes to form a 6 μm thick PSA layer. Two release films with this PSA layer were prepared and bonded to the first and second surfaces of a PET film (trade name "Lumirror 5A", manufactured by Toray Industries, Inc.) with a thickness of approximately 4 μm as a substrate layer, to obtain a substrate-attached double-sided PSA sheet with a total thickness of approximately 16 μm, having a PSA layer (thickness 6 μm) / PET film (thickness approximately 4 μm) / PSA layer (thickness 6 μm) structure and protected on both sides by the two release films.

[0151] Comparative Example 3 A substrate-attached double-sided PSA sheet according to this example was obtained in the same manner as in Example 26, except that the same PSA composition as the water-dispersed PSA composition of Comparative Example 1 was used.

[0152] <Reference Example> A water-dispersed pressure-sensitive adhesive composition was obtained in the same manner as in Comparative Example 1, except that no pigment was used, and a substrate-less pressure-sensitive adhesive sheet according to this example was obtained in the same manner as in Example 1, except that the pressure-sensitive adhesive composition was used.

[0153] <Evaluation Method> (Adhesion to SUS) Under a measurement environment of 23°C and 50% RH, a 50 μm thick PET film was attached to one adhesive surface of a pressure-sensitive adhesive sheet (double-sided pressure-sensitive adhesive sheet) to form a backing, and the sheet was cut to a size of 20 mm wide and 100 mm long to prepare a measurement sample. For the prepared measurement sample, under an environment of 23°C and 50% RH, the adhesive surface of the measurement sample was pressed against the surface of a stainless steel plate (SUS304BA plate) by rolling a 2 kg roller back and forth once. After leaving the sample under the same environment for 30 minutes, the peel strength (adhesion to SUS) [N / 20 mm] was measured using a universal tension and compression tester in accordance with JIS Z 0237:2000 at a tensile speed of 300 mm / min and a peel angle of 180°. The measurement results are shown in Tables 1 and 2. The universal tension and compression tester may be, for example, Minebea's "Tension and Compression Tester, TG-1kN" or an equivalent product. In the case of a single-sided PSA sheet, the PET film backing may not be required.

[0154] (550 nm Light Transmittance) The light transmittance [%] of the PSA sheet at a wavelength of 550 nm was measured using a commercially available transmittance measuring device in accordance with JIS K 7136:2000. The measurement results are shown in Tables 1 and 2. As the transmittance measuring device, a spectrophotometer manufactured by Hitachi Ltd. (device name "U4150 type spectrophotometer") or an equivalent device is used.

[0155] (Appearance Quality Evaluation) The pressure-sensitive adhesive sheet with a release film was cut into a size of 100 mm x 100 mm to obtain an evaluation sample. The release film (in the case of a double-sided pressure-sensitive adhesive sheet with a release film having two release films, the release film on the lighter release side) was peeled off from this evaluation sample, and the evaluation sample was held flat at the midpoint (a position about 50 cm away from the point light source) between a point light source positioned at a distance of about 100 cm and a projection screen, and the evaluation sample was placed so that the angle of the exposed pressure-sensitive adhesive layer surface of the evaluation sample was about 90 degrees with respect to the light from the point light source. The evaluation sample was placed with the pressure-sensitive adhesive layer surface from which the release film had been peeled facing the point light source. In a darkroom at 23°C and 50% RH, the point light source was turned on, and the image projected onto the screen through the evaluation sample was visually observed to detect visible pinholes (size 0.02 mm) present in the evaluation sample. ２ The presence or absence of pinholes (or more) was evaluated. For example, a "Xenon Lamp C2577" manufactured by Hamamatsu Photonics KK can be used as a point light source. For each example, 10 evaluation samples were prepared and the above evaluation was performed, and the number of samples in which visible pinholes were confirmed (NG number) was counted. A sample in which visible pinholes were confirmed was determined to be 5 or more (per 10 samples), and the sample was judged to have failed. The above appearance quality evaluation (evaluation before high-temperature treatment) was performed on the pressure-sensitive adhesive sheets of all Examples and Comparative Examples, and no samples had visible pinholes (i.e., NG number / 10 samples = 0 / 10 samples). After confirming this, the evaluation samples were stored at 80°C for one week, and then the above appearance quality evaluation (evaluation after high-temperature treatment) was performed. The results are shown in Tables 1 and 2. According to the above appearance quality evaluation method, bubbles equivalent to pinholes (pinholes of the above-mentioned visible size) can be visually observed even in uncolored pressure-sensitive adhesive sheets whose pressure-sensitive adhesive layer does not contain pigments such as carbon black.

[0156]

[0157]

[0158] As shown in Tables 1 and 2, in PSA compositions containing a water-dispersible acrylic polymer and a pigment, Examples 1 to 26, in which a reactive emulsifier was used during polymerization of the water-dispersible acrylic polymer, showed no pinholes or only a small number of samples with pinholes after one week of high-temperature treatment at 80°C, resulting in good appearance quality. On the other hand, Comparative Examples 1 to 3, in which a non-reactive emulsifier was used during polymerization of the water-dispersible acrylic polymer, showed pinholes after high-temperature treatment, resulting in poor appearance quality. As described above, the PSA sheets according to Examples 1 to 26 and Comparative Examples 1 to 3 showed no pinholes in the appearance quality evaluation before high-temperature treatment, and in the Reference Example, where no pigment was included, no pinholes were observed even when a non-reactive emulsifier was used. Based on these results, it is believed that in Comparative Examples 1 to 3, tiny bubbles of an invisible size were generated during PSA production, and that these tiny bubbles were stabilized (i.e., did not disappear) by the presence of the non-reactive emulsifier, attached to the pigment through electrostatic interaction, and grew (enlarged) in the high-temperature environment, for example by gathering together multiple bubbles, resulting in visible pinholes. The above results show that, in an adhesive comprising a water-dispersible acrylic polymer and a pigment, when the water-dispersible acrylic polymer contains a polymer synthesized by emulsion polymerization using a reactive emulsifier having a radically polymerizable functional group, it is possible to realize an adhesive that can maintain good appearance quality even when exposed to a high-temperature environment, and an adhesive sheet comprising such an adhesive.

[0159] Although specific examples of the present invention have been described above in detail, these are merely examples and do not limit the scope of the claims. The technology described in the claims includes various modifications and alterations of the specific examples exemplified above.

[0160] REFERENCE SIGNS LIST 1, 2, 3, 4 Adhesive sheet 10 Support substrate 10A First surface 10B Second surface (rear surface) 21 Adhesive layer (first adhesive layer) 21A Adhesive surface (first adhesive surface) 21B Adhesive surface (second adhesive surface) 22 Adhesive layer (second adhesive layer) 22A Adhesive surface (second adhesive surface) 31, 32 Release film

Claims

1. A pressure-sensitive adhesive sheet having a pressure-sensitive adhesive layer, wherein the pressure-sensitive adhesive layer contains a water-dispersible acrylic polymer and a pigment, and the water-dispersible acrylic polymer is a polymer synthesized by emulsion polymerization using a reactive emulsifier having a radically polymerizable functional group.

2. The pressure-sensitive adhesive sheet according to claim 1, which has a light transmittance of 15% or less at a wavelength of 550 nm.

3. The pressure-sensitive adhesive sheet according to claim 1 or 2, wherein the pigment comprises inorganic particles.

4. The adhesive sheet according to claim 1 or 2, wherein the adhesive layer contains carbon black as the pigment.

5. The pressure-sensitive adhesive sheet according to claim 1 or 2, wherein the content of the pigment in the pressure-sensitive adhesive layer is within the range of 0.1 to 15 parts by weight per 100 parts by weight of the water-dispersible acrylic polymer.

6. The adhesive sheet according to claim 1 or 2, wherein the thickness of the adhesive layer is 1 μm or more and 100 μm or less.

7. The pressure-sensitive adhesive sheet according to claim 1 or 2, which is a substrateless double-sided pressure-sensitive adhesive sheet comprising the pressure-sensitive adhesive layer.

8. The adhesive sheet according to claim 1 or 2, wherein the adhesive sheet is an adhesive sheet with a substrate, the adhesive layer and a supporting substrate.

9. The pressure-sensitive adhesive sheet according to claim 1 or 2, which has a 180-degree peel strength from a stainless steel plate of 5 N / 20 mm or more.

10. An electronic device comprising the adhesive sheet according to claim 1 or 2.