Composite negative electrode material doped with nitrogen / phosphorus / boron elements and preparation process thereof

By constructing a boron-phosphate oligomer framework in the liquid-phase precursor stage and forming a nitrogen-phosphorus-boron supramolecular precursor gel under high shear conditions, the problem of boron loss during high-temperature heat treatment was solved, achieving high graphitization and uniform coupling of active sites, thus improving the high-rate performance and production consistency of lithium-ion batteries.

CN121894653BActive Publication Date: 2026-06-05NINGDE NORMAL UNIV
View PDF 3 Cites 0 Cited by

Patent Information

Application Number
CN202610356960.4
Authority / Receiving Office
CN · China
Patent Type
Patents(China)
Current Assignee / Owner
Filing Date
2026-03-23
Publication Date
2026-06-05
Estimated Expiration
2046-03-23

AI Technical Summary

Technical Problem

Existing technologies struggle to effectively suppress the loss of key catalytic elements during high-temperature heat treatment, making it difficult to achieve both high graphitization and high heteroatom retention rates. Furthermore, achieving uniform molecular-level coupling between the conductive network and active sites is challenging, impacting the high-rate performance and production consistency of lithium-ion battery anode materials.

Method used

By constructing a boron-phosphate oligomer framework in the liquid-phase precursor stage, volatile boron atoms are locked onto the thermally stable phosphate framework using POB covalent bonds. Under high shear conditions, a supramolecular precursor gel is formed with the nitrogen source melamine. Subsequently, during heat treatment, it is transformed in situ into a nitrogen-phosphorus-boron co-doped graphitized carbon coating layer, achieving molecular-level uniform coupling of the components.

Benefits of technology

The high-temperature retention rate of boron was improved, forming a highly conductive carbon framework and abundant active sites, which enhanced the fast-charging performance and electrochemical performance consistency of lithium-ion batteries and reduced the energy consumption of preparation.

✦ Generated by Eureka AI based on patent content.

Smart Images

  • Figure CN121894653B_ABST
    Figure CN121894653B_ABST
Patent Text Reader

Abstract

The application relates to the technical field of lithium ion battery negative electrode material preparation, and discloses a kind of composite negative electrode material doped with nitrogen / phosphorus / boron element and a preparation process thereof, comprising: adding boric acid in phytic acid aqueous solution, controlling the reaction to jump the dynamic viscosity of system to a specific interval, to generate boron-phosphorus ester oligomer;The oligomer is hot injected into the hot saturated solution of melamine under high shear state, and the pH value is adjusted to induce the generation of nitrogen / phosphorus / boron supramolecular precursor gel adsorbed on the surface of negative electrode active substrate;After drying and high-temperature heat treatment, it is in-situ converted into a nitrogen-phosphorus-boron co-doped graphitized carbon coating layer, the application utilizes the thermal stability locking effect of P-O-B bonding network in boron-phosphorus ester oligomer on boron atom, to inhibit the volatilization of boron at high temperature.
Need to check novelty before this filing date? Find Prior Art

Citation Information

Patent Citations

  • A silicon suboxide composite anode material for lithium-ion batteries, its preparation method, and the lithium-ion battery thereof.

    CN103474631B

  • Polyatom co-doped silicon-carbon composite negative electrode material, preparation method, application and battery

    CN117542992A

  • Core-shell structure graphite phase carbon nitride derivative and preparation method thereof

    CN120737430A