Environment protection spinning thread wax ring and its producing method

Abstract

The present invention relates to an environment-protecting thread-spinning wax ring and its preparation method, belonging to the field of physical treatment technology of fiber and threads. It is made up by using (by wt%) 0.1%-99.9% of plant wax, 0.1%-99.9% of paraffin wax and 0%-99.8% of vegetable oil through the processes of mixing, heating and moulding. Its heating temperature is 60-110 deg.C.

Description

technical field

[0001] The invention discloses an environmentally friendly spinning wax ring and a manufacturing method thereof, belonging to the field of physical treatment of fibers, yarns, and threads, and in particular relates to a spinning wax ring used in textile processes such as knitting and wool weaving. Background technique

[0002] The spinning wax ring is used for the cotton yarn turned over on the yarn turning machine, so that the surface of the cotton yarn contains a certain amount of paraffin, and there is an extra layer of diaphragm between the cotton yarn and the contact object, which reduces the static electricity generated during the operation of the cotton yarn and reduces the workshop. Flying hair and thread breakage occur during knitting, so that the produced knitted fabric has fewer holes. The traditionally used spinning wax circle is made by adding high melting point paraffin wax to low melting point paraffin wax or industrial wax. Low melting point ...

Examples

Embodiment 1

[0022] The present invention is made up of 60% of vegetable palm wax and 40% of paraffin wax by weight percentage, wherein 19.5% of white paraffin wax, 20% of saponified wax and 0.5% of soft wax are used in 40% of paraffin wax, and the above components are mixed by weight percentage Put it in a pressure-free, non-sealed heatable container, heat it up to 60°C, pour it into the wax ring mold after it is completely dissolved, and take it out for packaging after cooling to room temperature.

Embodiment 2

[0024] The present invention is composed of 70% of vegetable palm wax and 30% of paraffin wax by weight percentage, wherein 9% of white paraffin wax, 20% of saponified wax and 1% of soft wax are used in the 30% of paraffin wax, and the above components are mixed by weight percentage Put it into a pressure-free, non-sealed heatable container, heat it up to 80°C, pour it into a wax ring mold after it is completely dissolved, and take it out for packaging after cooling to room temperature.

Embodiment 3

[0026] The present invention is composed of 60% of vegetable palm wax and 40% of paraffin wax by weight percentage, wherein 10% of white paraffin wax and 30% of saponified wax are used in 40% of paraffin wax, and the above-mentioned components are put into a pressure-free, Heat it to 110°C in a non-sealed heatable container, pour it into the wax ring mold after it is completely dissolved, and take it out for packaging after cooling to room temperature.

technical field

[0001] The invention discloses an environmentally friendly spinning wax ring and a manufacturing method thereof, belonging to the field of physical treatment of fibers, yarns, and threads, and in particular relates to a spinning wax ring used in textile processes such as knitting and wool weaving. Background technique

[0002] The spinning wax ring is used for the cotton yarn turned over on the yarn turning machine, so that the surface of the cotton yarn contains a certain amount of paraffin, and there is an extra layer of diaphragm between the cotton yarn and the contact object, which reduces the static electricity generated during the operation of the cotton yarn and reduces the workshop. Flying hair and thread breakage occur during knitting, so that the produced knitted fabric has fewer holes. The traditionally used spinning wax circle is made by adding high melting point paraffin wax to low melting point paraffin wax or industrial wax. Low melting point ...

Examples

Embodiment 1

[0022] The present invention is made up of 60% of vegetable palm wax and 40% of paraffin wax by weight percentage, wherein 19.5% of white paraffin wax, 20% of saponified wax and 0.5% of soft wax are used in 40% of paraffin wax, and the above components are mixed by weight percentage Put it in a pressure-free, non-sealed heatable container, heat it up to 60°C, pour it into the wax ring mold after it is completely dissolved, and take it out for packaging after cooling to room temperature.

Embodiment 2

[0024] The present invention is composed of 70% of vegetable palm wax and 30% of paraffin wax by weight percentage, wherein 9% of white paraffin wax, 20% of saponified wax and 1% of soft wax are used in the 30% of paraffin wax, and the above components are mixed by weight percentage Put it into a pressure-free, non-sealed heatable container, heat it up to 80°C, pour it into a wax ring mold after it is completely dissolved, and take it out for packaging after cooling to room temperature.

Embodiment 3

[0026] The present invention is composed of 60% of vegetable palm wax and 40% of paraffin wax by weight percentage, wherein 10% of white paraffin wax and 30% of saponified wax are used in 40% of paraffin wax, and the above-mentioned components are put into a pressure-free, Heat it to 110°C in a non-sealed heatable container, pour it into the wax ring mold after it is completely dissolved, and take it out for packaging after cooling to room temperature.